By Pengqi Zhang, Mingcheng Bing, Lixiong Shao, Shuxing Qiu, Qingyun Zhang, Shengfu Zhang

Coal desulfurization has been regarded as an effective pretreatment for clean fuel and less environmental pollution. The microwave irradiation was used to desulfurize the Nantong coal leached with H2O2 and NaOH. The results showed the desulfurization rate of the coal is very low by directly microwave irradiation, while the coal samples leached with H2O2 and NaOH by microwave irradiation could effectively improve the desulfurization rate. The optimum desulfurization conditions were obtained as 10-min irradiation time, 800 W irradiation power, particle size below 74 μm, 1:1 concentration ratio of H2O2:NaOH, in which the desulfurization rate reached 51.14% of the total sulfur content. Attenuated total reflectance Fourier transform infrared (ATR-FTIR) spectra of coals structure before and after treatment have shown the bands in both coals changed slightly except the relative intensity of some absorption ones. It can be found that most of FeS2 and –S–S– functional groups transferred after treatment, while –SH and –S=O– had almost no changing by ATR-FTIR spectra analysis. The structures of coal matrix would not be broken by microwave irradiation in reasonable the reaction conditions.

Mar 1, 2017

By Glenio F. Daniel, Vinícius O. Barbosa, André R. Gomes, Sergio N. Monteiro, Victor B. de Souza, Frederico M. Margem

Nowadays notorious technological growth is encouraging research natural materials in substitution to more usual synthetic ones. One of those initiatives is the vegetable fibers that have been studied for the replacement of glass and carbon fibers. This research addresses broadly the study of the natural fibers mechanics properties, but none study have been made with natural fabrics, such as the pure jute fabric used in Brazil to make ropes and carpets. This work aim to evaluate the mechanical behavior of jute fabric strips with different dimensions to be used as reinforcement into polymeric composites Lots of those fabric strips were subjected to tensile tests in order to obtain the tensile resistance for each strip size. The results obtained during the tests were satisfactory and indicated that 160 × 160 × 1 mm correspond to the best result and the perfect fabric strip for the composite reinforcement.

Mar 1, 2017

By Xiaolong Lin, Yuanbo Zhang, Tiancheng Nie, Guanghui Li, Zhizhong Li, Zhiwei Peng, Tao Jiang

The coal-based direct reduction process has gradually become the focus of research concerning direct reduced iron production due to its advantages, including high reduction rate, stable chemical composition, and good metallurgical properties of products. Based on coal-based reduction theory and briquetting technique, this paper reports the use of microwave energy for intensifying the reduction of carbon-containing briquettes mainly consisting of magnetite concentrate and biochar. The heating behaviors of the raw materials show that under the conditions of microwave power of 1250 W, N flow rate of 4 L min −1 and briquetting pressure of 400 N, the briquettes present the highest heating rate. The average heating rate reaches 35.16 °C min −1. When the briquettes are irradiated by microwaves at 1050 °C for 45 min, the metallization degree of the reduced briquettes reaches 93.58%.

Mar 1, 2017

By Bowen Li, Jiann-Yang Hwang, Mingsheng He, Huaguang Wang

Kyanite is one of the major high-alumina minerals for producing refractory ceramics. At high temperature, kyanite can be decomposed into mullite and amorphous silica. This change is an irreversible decomposition and provides potentials for fiber reinforcement of ceramic matrix. In this study, kyanite powder was compressed into a cylinder green body of ceramic and heated at 1150–1450 °C.The phase transformation of kyanite and sinterability were investigated by X-ray diffraction and scanning electron microscopy. The results showed that the phase transformation of kyanite started at 1150 °C when rising the temperature. At 1350 °C, kyanite is completely converted into mullite and silica. The compressive strength of the ceramics reached 73.3–134.8 MPa, while the bulk density was 1.95–2.47 g/cm3. The microstructure indicated the correspondence of the compressive strength to mullitization degree of kyanite.

Mar 1, 2017

By Shigeru Ueda, Shin-ya Kitamura, Shohei Koizumi, Xu Gao

Steelmaking slag was confirmed to be a useful fertilizer for paddy growth as it efficiently supplies Ca and Si to soil water. In addition, supplement of Fe from slag fertilizer has been expected to suppress the H2S generation in paddy soil, especially for the degraded paddy soil. However, on the basis of our previous research, the Fe dissolution ability changed with slag brands, and even some brands could dissolve Fe under paddy soil pH, the supplying ability were not high. To improve Fe dissolution, we found that among various kinds of Fe-rich mineralogical phases in slag, the CaO–SiO2–FeO glassy phase showed highest water solubility of Fe. Because the CaO–SiO2–FeO glassy phase was a quenched molten phase, its dissolution behavior may depend on chemical composition, and this is important for controlling slag composition to produce fertilizer which can easily release Fe. Therefore, in this research, the CaO–SiO2–FeO glassy phase of various CaO/SiO2 ratio, Fe2+/T–Fe ratios, and FeO contents were synthesized, and the dissolution behaviors of Fe as well as other cations from these synthetic glassy phases into an aqueous solution at pH of 5 were investigated. The result showed that the dissolution ratio of Fe increased significantly by increasing Fe2+/T–Fe ratio. An increase in FeO content of glassy phase also increased the dissolution of Fe. In addition, the Fe dissolution ratio showed a local maximum with increasing CaO/SiO2 ratio.

Mar 1, 2017

By Heric Henrique Souza e Silva, Johne Jesus Mol Peixoto, Natalia Barros Barony, Itavahn Alves da Silva, Weslei Viana Gabriel, Carlos Antonio da Silva, Varadarajan Seshadri

In this work the circulation rates have been determined in a 1:7.5 scale physical model of RH reactor (Ruhrstal Heraeus) and using oil/water and oil/zinc chloride solution to simulate steel melt/slag in the prototype with the objective of evaluating the influence of density and viscosity on the entrainment of oil simulating slag. A technique based on strain gage bridge and particle image velocimetry was developed to assess the circulation rate, as the usual tracer method is not feasible due to the presence of chloride ions in ZnCl2. The critical velocity and critical diameter of oil drops for slag (oil) entrainment in water/oil and ZnCl2/oil systems were estimated using equations from the literature. Due to the difference in density, the ZnCl2/oil system, showed a critical velocity that is 28% higher than the silicone oil/water system while the maximum size of the entrained droplets was about 65% lower than that for water/oil system.

Mar 1, 2017

By Dachun Liu, Xuepeng Li

Smelting-acid leaching process is a way to treat high-content arsenic containing copper dust. However, smelting makes a low recovery of valuable metals and acid-leaching produces large amounts of arsenic-iron slag. Arsenic sulphuration volatilization at low temperature was studied, followed by pressure leaching to selectively recover Cu, Zn, and In from copper smelting dust while minimizing arsenic contamination.

Mar 1, 2017

By Gisele Azimi, Jason Tam, Adrian Lambert

Many advanced technologies in modern society require the use of rare earth elements (REEs). Since these technologies are dominating the world, the demand for REEs is increasing fast. Finding new sources for them is highly of interest. One secondary source of REEs is phosphogypsum (PG), a by-product of the phosphate fertilizer industry. Microwave treatment is investigated as a method to enhance hydrometallurgical recovery of REEs from phosphogypsum, with results showing a 30% improvement in leaching efficiency.

Mar 1, 2017

By Muhammad A. Imam, Ramana G. Reddy

This study provides a reasonable evaluation of the Mg-B binary system. Magnesium and Boron (Mg-B) alloys were investigated to determine their thermodynamic properties employing solid state electrochemical cells based on CaF2 electrolyte represented as –Pt; Ar= MgþCaMgF4 f gCaF2 k kf½Mg B alloy þ CaMgF4 g=Ar; Pt+ Investigations were performed over the temperature range of 773–873 K to measure the electromotive force (EMF), which was used to derive the partial Gibbs Free energies of the alloys in the composition range of XB = 0.07 to 0.95. The activities of Mg were also calculated from partial Gibbs Free energies. The activities of Mg in MgB2, MgB4, and MgB7 were expressed as a function of temperature respectively, ln aMg = 4.27–9.32 × 103/T, ln aMg = −7.54 + 6.67×103/T, and ln aMg = 4.93–19.57 × 103/T, where T is the temperature in K. From this expression, the activity of Mg for these intermediate phases can be extrapolated at a higher temperature to get the accurate phase boundaries for the Mg-B system.

Mar 1, 2017

By Wei Lv, Xuewei Lv, Senwei Xuan, Chenguang Bai, Kai Tang

The contact angle between six iron ores and water were determined by the capillary pressure method with cyclohexane as the perfect wetting liquid. The factors influencing the contact angle were discussed, and a relationship between the content of oxy–hydroxides and the contact angle of iron ores was obtained. The results show that the ore F has the lowest contact angle but the ore D get the biggest, which are 32.09° and 78.16°, respectively. The volume fraction of oxy–hydroxides is linearly dependent on the contact angle. The contact angle decreased with increasing the volume fraction of Fe2O3*H2O.

Mar 1, 2017

By S. Chama, P. Chishimba, Tina Chanda Phiri, J. Machona, S. Parirenyatwa, G. Kaluba, Y. R. S. Hara, D. M. Musowoya

The investigation focuses on leaching of copper (2 wt%), cobalt (0.5 wt%) and iron (2.4 wt%) from complex tailings material from the Democratic Republic of Congo. The highest recovery of copper and cobalt into the leach solution were 78 and 10%, respectively, under direct leaching with sulphuric acid. Higher recoveries (90% for copper and 96% for cobalt) were attained when the material was pre-reduced with coal for 1.5 h in the temperature range of 700–950 °C. The increased recoveries were due to metallisation of all the copper and cobalt which is in the silicate matrix. The effects of pre-reduction temperature and sample to carbon weight ratios were analysed and found to be important in; (i) achieving high recoveries of copper and cobalt and (ii) decreasing the amount of iron in the leach solution. The samples were characterised by atomic absorption spectroscopy and scanning electron microscopy (SEM) techniques.

Mar 1, 2017

By Leiv Kolbeinsen, Vincent Canaguier, Ingeborg-Helene Svenum

The syntheses of stoichiometric iron chromite and chromites with chosen impurity content have been developed using the induction skull melting technique. The aim for this synthetic material is to obtain pure samples to study the carburization by methane-hydrogen gas mixtures. For each synthesis, the parameters influencing the skull melting experiment have been considered. The product phases have been analyzed using X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM), Energy-Dispersive X-ray Spectroscopy (EDS) and X-ray Photoelectron Spectroscopy (XPS). The synthetic material was subsequently pelletized and sintered in argon. The use of excess iron was found to improve the quality of the final product as well as to help the melting. The difference in magnesium content between first and last solids formed seem to indicate a segregation phenomenon, while no evidence could support a similar trend for aluminum substitution in chromite.

Mar 1, 2017

By Uday Pal, Shizhao Su, Thomas Villalon

Compared with the current Hall–Héroult process for smelting aluminum, the Solid Oxide Membrane (SOM)-Based electrolysis process brings various advantages such as simplified design, lower cost, lower energy use, and many other environmental bene fits. However, the state-of-the-art SOM electrolysis process is limited by the solid oxide membrane’s stability and its compatibility with the molten salt and the electrode materials. This work will identify cost-effective molten salt compositions and membrane materials/architecture along with electrodes and current collectors that are all chemically compatible and provide optimum electrochemical properties for efficient aluminum oxide electrolysis.

Mar 1, 2017

By Bora Derin

This study is a collection of both newly published and/or presented works on impurity capacity predictions in molten melts which were carried out by Derinetal. Some sulfide capacity prediction results of iron oxide containing ternary silicate melts and industrial lead and copper slags using the Reddy-Blander model and some impurity capacity predictions of multicomponent oxide and salt melts obtained using a Artificial Neural Network Approach are discussed.

Mar 1, 2017

By Chengyi Ding, Xuewei Lv, Senwei Xuan, Jie Qiu, Yun Chen, Kai Tang

Isothermal reduction kinetics of CF2 by 30% CO and 70% N2 at 1123, 1173 and 1223 K was investigated by TGA in this study. The reduction rate analysis indicated that reduction of CF2 comprises three stages during the whole reduction process, Apparent activation energy of samples CF2 reduction is 34.37 kJ/mol. The ln-ln analysis implied the reduction of CF2 was expressed initially by a 2D subsequently by 3D shrinking layer reaction.

Mar 1, 2017

By Mostafa Maazouz, Jeff Blackwood, Mauricio Gordillo, Sang Hoon Lee, Micah Ledoux, Liang Zhang

To meet rising requirements for the low-damage ultra-fine process with the focused ion beam (FIB) in the materials science and semiconductor industry, the advanced ion column and corresponding advanced applications as a solution are developed and demonstrated. Novel high-speed high kV milling, low kV cleaning and imaging capabilities have enabled the creation of impeccable ultra-thin structures such as TEM samples and nanometer scale structures. Minimizing Ga+ induced sample damage is achieved through the optimized final cleaning at 500 eV ion landing energy with the new ion optics, which utilizes close control of the ion dose, beam incidence angle, spot size, pattern algorithm and imaging performance. Newly introduced process solutions achieve the improved process throughput. Initial demonstration is performed on the latest 14 and 10 nm scale FinFET device. Validation of the thinnest <0.8 nm thick ion damage layer on the <7 nm thick lamella structure was confirmed through TEM analysis.

Mar 1, 2017

By I. Moscoso, R. Padilla, M. C. Ruiz

Antimony and arsenic are impurities in copper concentrates found normally as stibnite (Sb2S3), tetrahedrite (Cu12Sb4S13) and enargite (Cu3AsS4). When copper concentrates contain appreciable amounts of As and Sb, they must be removed before smelting to avoid environmental pollution. Oxidizing volatilization roasting at 500–700 °C has been used to eliminate these impurities. However, only a fraction of Sb volatilizes in those conditions; thus, a more effective process to eliminate antimony from concentrates is needed. In this study, the chloridizing roasting of Sb2S3 using CaCl2–O2 was investigated to remove the antimony from concentrates. XRD analysis of calcines indicated that the overall reaction could be written as: Sb2S3 þ3CaCl2 þ6O2 ¼ 2SbCl3 þ3CaSO4 Temperature and oxygen partial pressure have a significant effect on the rate of reaction. An estimated conversion of about 90% was obtained at 750 °C, 5.4% oxygen in 20 min. High oxygen concentrations arrest the advance of the reaction forming various antimony oxides including Sb6O13, Ca5Sb5O17 and Sb2O4.

Mar 1, 2017

By Beatryz C. Mendes, Márcio Sampaio S. Moreira, Rita de C. S. S. Alvarenga, Juliano Correa

Over the last decades, modern technology to build wood structures have been substantially developed. Building solutions for floor systems of wood-concrete mixed T-beams with wood web and concrete flange stand out among these technologies. This work describes an experimental investigation of the performance of bond connectors made of round steel bars for wood-concrete mixed elements. Symmetric three-member specimens were built. The middle member was made of concrete and the other two were made of wood. The first kind of connector consisted of steel bar designed as straight pins with head, normally driven through the wood. The second kind consisted of arc-shaped connectors directly embedded into the wood or bonded using epoxy adhesive. The specimens were then tested in compression. The compressive strength and the force-displacement curve were obtained, in order to evaluate the failure mode and obtain the stiffness in the ultimate (Ku) and serviceability (Ks) limit states. The stiffness values were calculated in the interval corresponding to the secant straight line between, respectively, 10–40 and 10–70% of the ultimate strength. The obtained results indicate high strength and ductile failure mode for all of the cases. Bond stiffness gains were verified when using the arch-shaped connectors.

Mar 1, 2017

By José Palacios, Mario Sánchez, Fernando Parada

As an alternative method of reducing the large amount of slag generated during metallurgical processes in the primary copper production, it is to use the remaining iron in the slag as feed material for the iron and steel industry. The slag is generated during copper concentrates smelting in ratios ranging from 2 to 5 ton per ton of produced copper, and it contains 42–45% of iron. However, copper, sulfur and other detrimental elements affecting iron properties need to be reduced prior to use the slag in steel production. Therefore, some laboratory experimental run has been conducted to reduce copper by slag oxidation followed by leaching and recovering the dissolved copper by SX-EW, and smelting the solid with coke to produce a metallic phase containing 98% iron and 0.9% molybdenum. In further reducing steps, copper content is lower down and a molybdenum rich iron phase is obtained. Recovery of iron from copper slags considering reduction and control of harmful elements for iron properties was studied.

Mar 1, 2017

By Mao Chen, Baojun Zhao, Xiangfeng Cheng, Zhixiang Cui, Leonel Contreras, Anh Nguyen

Smelting is an important process in copper production to produce matte and slag.The slag,containing about 1–12% Cu can be further processed to recover the copper contaminated, but recycle of the slag concentrate reduces overall productivity and efficiency of the operation. The best solution is to minimize the copper loss to the slag. The entrained matte droplets in copper smelting slag may originate from a few sources. The present study aims to investigate possible copper matte loss mechanisms by visualization of room temperature experiments and high-temperature examination. It is believed that the gas bubbles from the matte phase disperse the matte droplets into the slag causing entrained matte in slag. Analyses of quenched slags from industrial operation and laboratory experiments confirmed that matte droplets in the slag are extensively associated with the gas bubbles. Water model is used to simulate the procedure and the bubble behaviors at the liquid-liquid interface are observed experimentally with a high-speed camera.

Mar 1, 2017