By William G. Fricke

MaCROSEGREGATION, as distinct from microseg-regation, is often inverse in nature. That is, the eu-tectic solute elements, which are expected to be con-

Jan 1, 1970

By N. K. Bohidar

Evaluation of the stability of a structure under given boundary conditions requires accurate knowledge of the state of stress as well as the mechanism of failure at the critical state of stress. This paper represents a part of the research done by N. K. Bohidar during 1965-1968 for his Ph. D. research in Mining Engineering at the University of Utah. It summarizes the determination of internal stress and failure phenomena around cylindrical openings in viscoelastic media subjected to lateral restraint and vertical uniaxial load. The conditions of lateral restraint and viscoelastic nature of the media represent conditions associated with subsurface openings in rocks. The financial assistance provided to the project from the University of Utah Research (Uniform School Fund), W. C. Browning Scholarship Fund, Earth Science Research Fund, and D. C. Jackling Loan and Scholarship Fund is gratefully acknowledged. The authors also acknowledge the assistance of S. Siugh, W. Jones, and K. McCarter during the project.

Jan 1, 1970

By G. H. Keith

A vanadium-base alloy consisting of the following elements in weight-percent--molybdenum, 20; titanium, 10; carbon, 0.1; silicon, 0.5; and yttrium, 0.5--had exceptionally high strength at temperatures up to 1,200° C. This alloy was capable of fabrication to sheet of ~ 1 mm thickness by a combination of hot swaging and hot and warm rolling. In the warm-rolled condition at ambient temperature, its ultimate tensile strength was 1,205 MN/m2. The strength at 1,200° C was 150 MN/m2. Within the temperature range of 25° to 1,200° C, the ductility of the alloy as measured by elongation increased from 4 to >90 percent. Strengthening was achieved by both solid-solution and dispersed-phase mechanisms. Alloys of 20 percent molybdenum and 10 percent titanium were stronger than the other molybdenum-titanium alloy compositions tested. Strength was increased 15 percent in the temperature range of 25° to 800° C, with no accompanying loss in ductility, by the addition of 0.5 percent silicon. Workability was improved by additions of 0.25 and 0.5 percent yttrium.

Jan 1, 1970

By R. J. Fruehan, F. D. Richardson

Electrochemical measurements have been made of the activity of oxygen in copper and its alloys with silver and tin at 1100" and 1200°C. The galvanic cell used was Pt, Ni + NiO/solid ellectrolyte/[O] in metal, cermet, Pt The results do not support any of the equations so far designed for predicting the activities of dilute solutes in ternary solutions from activities in the corresponding binaries. If, however, a quasichemical equation is used with the coordination number set to unity, agreement between observed and calculated activities shows that this empirical relationship can be useful over a fair range of conditions. SEVERAL solution models have been proposed for predicting the activity coefficients of dilute solutes in ternary alloys from a knowledge of the three binary systems involved. Alcock and Richardson1 have shown that a regular model, and a quasichemical model,' in which the dissolved oxygen is coordinated with eight or so metal atoms, can reasonably predict the behavior of both metal and nonmetal solutes when the heats of solution of the solute in the separate solvent metals are similar. But when this is not so, neither model gives useful predictions unless coordination numbers of one or two are assumed. Wada and Saito3 subsequently adopted a similar model to derive the interaction energies for two dilute solutes in a solvent metal. Belton and Tankins4 Rave proposed both regular and quasichemical type models in which the oxygen is bound into molecular species, such as NiO and CuO in mixtures of Cu + Ni + 0. However, their models have only been tested on systems in which the excess free energies of solution of the solute in the two separate metals differ by a few kilocalories. Ope of the reasons why more advanced models have not been proposed is because few complete sets of data exist for ternary systems in which the solute behaves very differently in the two separate metals. For this reason measurements have been made of the activities of oxygen dissolved in Cu + Ag and Cu + Sn. Measurements on both systems were made by means of the electrochemical cell, Pt, Ni + NiO/solid electrolyte/O(in alloy), cermet,Pt [1] The activity of oxygen was calculated from the electromotive force and the standard free energy of formation of NiO, which is accurately known.5 Before investigating the alloys, studies were made of oxygen in copper to test the reliability of the cell and to check the thermodynamics of the system. Of the previous studies those by Sano and Sakao,6 Tom-linson and Young,7 and Tankins et al.8,7 have been made with gas-metal equilibrium techniques; those by Diaz and Richardson,9 Osterwald,10 wilder," Plusch-kell and Engell,12 Rickert and wagner,13 and Fischer and Ackermann14 have been made by electrochemical methods. EXPERIMENTAL The apparatus employed was the same as described previously,9 apart from slight modification. The molten sample of approximately 40 g was held in a high grade alumina crucible 1.2 in. OD and 1.6 in. long. The solid electrolytes were ZrO2 + 7½ wt pct CaO and ZrO2 + 15 wt pct CaO; the tubes 4 in. OD and 6 in. long were supplied by the Zirconia Corp. of America. They were closed (flat) at one end. In one experiment with Cu + O, both electrolytes were used in the cell at the same time. The reference electrodes inside the electrolyte tubes consisted of a mixture of Ni + NiO. They were made by mixing the powdered materials and pressing them manually into the ends of the tubes, with a platinum lead embedded in them. The tubes were then sintered overnight in the electromotive force apparatus at 1100°C. By sintering the powders inside the tubes (instead of using a presintered pellet9) better contacts were obtained between the electrolyte, the powder, and the platinum lead. Troubles arising from polarization9 were thus much reduced. The electromotive force was measured by a Vibron Electrometer with an input impedence of 1017 ohm; the temperature was measured with a Pt:13 pct Rh + Pt thermocouple protected by an alumina sheath. The couple was calibrated against the melting point of copper. The cermet conducting lead of Cr + 28 pct Al2O3, previously found to be satisfactory9 for use with Cu + 0 was also found satisfactory with Cu + Ag + 0 and Cu + Sn + 0. Superficial oxidation was observed, but it did not interfere with the working of the cell. The reaction tube containing the cell was closed at each end with cooled brass heads and suspended in a platinum resistance furnace. The tube was electrically shielded by a Kanthal A-1 ribbon which was wound round it, and the ribbon was protected by a N2 atmosphere between the furnace and the reaction tube. The cell was protected by a stream of high purity argon which was dried and passed through copper gauze at 450°C and titanium chips at 900°C. All the metals used were of spectrographic standard. Procedure. In studies of the system Cu + 0, be-

Jan 1, 1970

By J. D. Hunt, R. J. McDonald

It is proposed that extensive fluid motion occurs between the dendrites of a Partially solid casting and it is suggested the A segregates in steel castings are a direct result of this motion. The fluid flow arises because of density differences between liquid ahead of the dendrites and the interdendritic liquid. Experiments are described on a model system investigating this fluid motion. The importance of interdendritic fluid flow is discussed with reference to longitudinal segregation. SERIOUS macro segregation is often found in large killed steel ingots. Among the most common segregates are those known as A and V, Fig. 1. The A segregates are arranged over the surface of cones, the wide parts being at the base of the ingot. The A segregates are pencil like in shape and extend from the columnar into the equiaxed region. The V segregates are distributed over inverted cones but have a less well defined shape. They occur at the center of the ingot. Because of the commercial importance of macro inhomogenities these segregates have attracted wide-scale attention. The segregates contain alloying elements and impurities which depress the freezing temperature and are thus the last liquid to freeze. A number of explanations have been proposed to explain their presence. It has been suggested1'' that the segregates are the result of the equiaxed zone growing towards the columnar region together with the interaction of convection within the bulk liquid. It has also been proposed that the segregates are the result of nucleation and rapid growth ahead of the dendritic front.3 Neither of these explanations is completely satisfactory because A segregates are pencil shaped and are not found as continuous cones. In this paper an alternative mechanism is proposed, and experiments are described on a model system to determine whether the mechanism occurs in practice. It is thought that A and V segregates are not peculiar to steels but should occur in many other large castings. Fluid motion within the bulk liquid region of a casting has been extensively discussed. Little attention has been paid to fluid motion within the partially solid regions. The work415 that has been done has been mainly concerned with the fluid motion which results from the volume contraction on freezing. The volume contraction is used to explain various types of macro segregation. The present authors suggest that in many cases the fluid flow resulting from volume contraction will be small compared with that due to other causes. When the columnar region is growing, the liquid still remaining between the dendrites has a much lower temperature near the ingot walls than at the dendrite tips. The composition of the liquid in contact with solid will vary with temperature. The density of the liquid will thus vary both because of changes in temperature and composition. The layers of different density liquid will give rise to a slow but steady liquid flow through the interdendritic regions. If there is no density change with composition, the temperature gradient within the dendritic region should give rise to a downward flow between the dendrites, shown schematically in Fig. 2. When the liquid density changes appreciably with alloy concentration this motion could either be en-

Jan 1, 1970

By E. Gaucher, M. St-Amant

"Among the electromagnetic surveys performed by SOQUEM in the last three years, a certain number of the more instructive cases have been chosen to illustrate the theory of electromagnetism by field examples of: (a) The depth penetration of the TURAM as compared to the SLINGRAM (Ronka) method. (b) The limitations of the TURAM as compared to the SLINGRAM method when a conductor dips the wrong way, or when it is small in size. (c) The expression of a shallow-dipping conductor in a SLINGRAM survey. (d) The effect on the SLINGRAM survey of deep ditches or reef structures.(e) A comparison between the CRONE and the SLING-RAM method in the Abitibi clay belt, by means of field and model studies, indicating a usually better signal-to-noise ratio for the SLINGRAM method. From the above and from other experiments, different electromagnetic methods are now being used by SOQUEM, depending on field conditions."

Jan 1, 1970

By E. J. Rapperport, J. P. Pemsler

The thermodynamic activities of zinc in six solid solution Cu-Zn alloys ranging from 5 to 35 at. pct Zn were determined experimentally in the temperature range 400° to 600°C. This low temperature investigation was canducted in order to evaluate techniques developed to utilize the inherently high sensitivity of atomic absorption flocesses in the measurement of thermodynamic activities. Analytical expressions ,for the activity and actizlity coeflcient are given for the six alloys in the temperature ranges investigated. RELATIVELY few experimental methods are available for investigation of thermodynamic activities of alloys, especially in the solid state. The techniques most frequently used have been the electrochemical potential and the effusion methods, both of which have severe limitations in many instances. It is therefore desirable to expand the ability to perform such measurements in order to obtain new information as well as to provide an additional independent verification capability. In this work, we present a significant improvement in the spectrophotometric method for sensing small vapor pressures in static absorption cells. Similar techniques have been used previously;1"5 however, applications had been limited to relatively high pressures, often greater than 1 torr. Prior investigators have, for the most part, used broad spectral sources such as xenon or mercury lamps, and high intensity arcs. Hollow cathode sources were first suggested in 1956 6 and were used soon afterwards.4'5 These sources offer significant improvements in sensitivity and freedom from interfering spectral lines.'-' EXPERIMENTAL High purity zinc was obtained from Cominco Products, Inc., and copper from American Smelting and Refining Co. Both elements were of 99.999 pct purity. Copper-zinc alloys were vacuum melted in a high fired carbon crucible with each alloy pulled from the melt as a 4 -in. diam bar. The bars were swaged to -1/4 in. rods and vacuum annealed for 160 hr at 800° + 1°C. Samples for gross chemical analysis were taken at intervals along the length of the rods to ascertain the axial zinc gradient. Electron microprobe analysis of homogenized specimens indicated that the alloys had uniform compositions over their cross sections on a macro (200 p) and micro (1 u) scale to better than *1 pct (20) of the gross composition. This tolerance was determined by counting statistics, rather than assured composition fluctuations. All SiO 2 windows were high-ultraviolet-transmission grade to minimize intensity losses. Silica absorption cells were scrupulously cleaned consecutively in organic solvents, dilute HF, and distilled water before use. The empty cells were then flamed while under a dynamic vacuum, cooled, and removed to an argon-filled glove bag. Alloy pieces were cut and filed in the glove bag to produce fresh surfaces, and then loaded into the cells. The loaded cells were temporarily sealed, removed from the glove bag, reevacuated to 10-5 torr or better, and permanently sealed. The instrument used is schematically shown in Fig. 1. The spectral emission from a commercially made hollow cathode lamp (A) of a selected element is focused through an absorption cell (B) inside a well-controlled furnace (C). The intensity of the transmitted beam is measured using the spectrometer* (D) 'Techtron model AA4 atomic absorption spectrometer. which contains a grating (E) that disperses the light prior to impingement on the photomultiplier (F). The monochromator grating is adjusted so that only the wavelength of interest is measured. The power supply delivered an interrupted voltage to the lamp, causing a chopped radiation output to be transmitted. The detector read only the intermittent component of radiation incident upon it, so that all continuous noise signals (furnace radiation, and so forth) were eliminated. Three recording thermocouples contained in the muffle furnace were positioned along the length of the absorption cell: one at each end and one at the center. An effort was made to keep the ends of the cell several degrees hotter than the center to avoid window condensate. Appropriate thermal corrections were then necessary to relate cell pressure to radiation attenuation. Water-cooled heat shields, as shown in Fig. 1, were found to aid signal stability by protecting the hollow cathode and the photomultiplier from furnace radiation. The furnace had a 2-in. diam muffle, Kan-thal wound, with SiO 2 windows at its ends to minimize convective effects. The hollow cathode radiation was masked and focused to form a conic beam that was a maximum of { in. diam within the furnace. Thus, the 1.5 in. diam absorption cell easily contained the entire beam. The furnace was mounted on ball-bearing slides with positive positioning detents. This arrangement allowed the removal of the entire furnace assembly from the radiation path, position [I], Fig. 1, so that frequent sampling of the unattenuated beam intensity could be obtained. In all cases the beam intensity was kept constant to 0.1 pct as judged by readings taken immediately before and immediately after data collection. Only data for absorptions of less than 80 pct were utilized, as systematic deviations from linearity were found for greater absorptions.

Jan 1, 1970

By W. C. Winegard, C. J. Simpson

BNINGESSNER et al.1 have shown that the solidification substructure in dilute cadmium alloys persisted after repeated deformation, recrystallization, and annealing treatments. On the basis of this and similar evidence, Whelan has suggested in a recent publication' that the solidification structure might affect the mobility of grain boundaries even after primary re-crystallization. This suggestion is important, since the technique used by previous investigators3-5 to fabricate grain growth specimens consisted only of casting, deforming, and recrystallizing prior to the grain growth anneal. Usually no attempt was made to homogenize samples with prolonged annealing. Experiments. To test the Whelan hypothesis, grain growth experiments were performed with samples in which the degree of solute segregation was altered by controlling the solidification rate of the alloys. The initial experiments were performed on the Pb-Ag system. Alloys containing 0.01 at. pct Ag were produced from 99.9999 pct Pb and 99.999 pct Ag. Cylindrical samples, 40 cm long and 12 mm in diam, were solidified in graphite-coated Vycor tubes by lowering them through a vertical furnace at varying rates with the furnace power settings constant. Six-centimeter sections were discarded from each end, and the 28-cm section from the center was cut into sections 25 mm long for grain growth experiments. These samples were deformed with the aid of a drophammer to a uniform thickness of 5.7 mm. After almost instantaneous recrystallization, the samples were given a grain growth anneal for various times at 260°C in a salt bath. Experimental results are shown

Jan 1, 1970

By R. R. French

The industrial minerals industry in the Atlanta, Ga., area was studied in order to better understand problems associated with exploiting mineral resources in and near metropolitan areas. A method for delineating the Atlanta urban area and its component parts was developed so that the factors affecting the location of the minerals industry could be viewed mere objectively in the urban context. Major attention is focused on the area's dominant crushed stone subindustry Demographic and socioeconomic analysis of the Atlanta, Ga., area shows that expansion of the metropolis and its environs will probably eliminate potential mineral resources from the mineral resource base in the area, and that the expanding metropolis will be the primary determinant of future mining sites. Competition for land is accentuated to varying degrees by the incompatibility of wining operations with residential and other environmental requirements. Areas of consideration are suggested to provide maximum development of land and resources for greatest economic benefits it minimum social cost. Further research is recommended to determine market locations in urban areas, optimum operating levels for industrial minerals plants, and alternatives to surface mining.

Jan 1, 1970

By R. A. Greenkorn, R. C. Smith

Hele-Shaw cells are used to model creeping flow through porous media (where Darcy&apos;s law is valid). The effects of inertia on flow about obstructions in a Hele-Shaw cell can be calculated by a perturbation method if one can determine a solution to Laplace&apos;s equation. Results of a computer solution for flow about circular, square and elliptical obstructions are presented. These results show that or a modified Reynolds number of less than I, the inertia terms are small; and for values of less than 3, the average streamline predicts the ideal flow. Therefore, the analogy might be used for studying flow in porous media up to a modified Reynolds number of at least 3. INTRODUCTION The nature of fluid flow in porous media is of interest in the fields of soil mechanics, ground water flow, petroleum production, filtration and flow in packed beds. Because it is very difficult to study the phenomenological behavior of flow in porous media, homologs and analogs are used to study flow characteristics. A Hele-Shaw model, made of two closely spaced plates - usually glass — is often used as an analogy to two-dimensional flow in porous media. Hele-Shaw2 showed experimentally that the streamline configuration for creeping flow around an obstacle located between two closely spaced parallel plates is the same as for two-dimensional, ideal flow about the same obstacle. Stokes7 verified these observations mathematically. The usual equation of motion for flow in porous media is Darcy&apos;s law. The form of the mathematical statement of Darcy&apos;s law is identical, within a multiplicative constant, to the expression for the average velocity over the plate gap in the plane of a Hele-Shaw model. These models may be used to describe flow in both homogeneous and heterogeneous porous media. In the mathematical proof of the Hele-Shaw analogy it is assumed that the convective terms in the Navier-Stokes equations are negligible and that the equations of motion degenerate to Laplace&apos;s equation, with pressure the dependent variable. Whenever a Hele-Shaw model is used as an analogy to flow in porous media, .the validity of this assumption is in question. Riegels5 showed that if convection is not neglected, the velocity distribution around a cylindrical obstruction in the flow field depends on a Reynolds number, the plate spacing, and a dimension characteristic of the obstacle. Riegels&apos; solution, a perturbation solution, uses the boundary condition that the flow rate into the obstacle averaged over the plate gap at any point on the obstacle is zero. The method requires that a solution to Poisson&apos;s equation for the perturbation pressure be found. Riegels evaluated this solution for the case of the cylindrical obstruction. His method may be simplified by eliminating the need for solving Poisson&apos;s equation for the perturbation pressure. Instead, an analytic expression for the perturbation pressure gradient is obtained (valid for arbitrary shapes) and used to eliminate pressure from the equations for the perturbation velocities. The results show, for symmetrical shapes, that if NRe < 1, the convective acceleration terms are small, and that the average velocities represent ideal flow up to at least NRe = 3, where: L is a characteristic dimension of the obstacle perpendicular to flow, b is the plate spacing, u is viscosity, v, is velocity of approach and p is density. THEORY* Incompressible fluid flow through a Hele-Shaw model and a porous medium are analogous because the equations for the average velocity components in two-dimensional flow are identical if:

Jan 1, 1970

By D. M. Urich

New plant construction for pyrolysis and agglomeration during 1969 has been relatively quiet in the North American scene. U.S. pellet capacity approximates 52 million long tons and that of Canada 25.3 million tons. The foreign scene, however, has been extremely active during 1969, and this is expected to continue for the next several years. Changes in sinter practice have not been reported, other than a few changes towards increased bed depths and the increased use of screening facilities to size the product more closely. Interest in the field of briquetting in fields other than iron ore is high with a new fluorspar briquetting plant under construction at Brownsville, Texas. Considerable research appears to be pointed towards solving the problem of reclaiming steelmill waste products (flue dust, BOF dust, mill scale) by means other than sintering.

Jan 1, 1970

By Gary A. Kingston

Chromium resources in the United States are estimated at 1.8 million tons of recoverable chromium contained in 22.5 million tons of chromite-bearing material. Additional resource is presumed existent in large, but as yet undetermined, quantities of material containing less than 10 percent Cr203. No domestic resources are being mined presently (1969). Excluding transportation charges to domestic consuming areas, the total 1.8 million tons of chromim is estimated to be available, in ore or concentrate, at costs up to $0.64 per pound; 63 percent of the total is available under $0.11 per pound; and 38 percent under $0.08 per pound. It is judged that transportation from the resource areas to the existing market centers would add nearly $0.05 to the cost of a pound of chromium contained in ore or concentrate. Technically effective beneficiation methods have been developed for much of the known domestic resource, and further development might reduce costs of processing these materials. However, at present, domestic chromium resources are noncompetitive with foreign sources.

Jan 1, 1970

By B. S. Hickman

Using primarily quantitative single crystal X-ray techniques studies have been made of the precipitation of the metastable w phase in alloys of titanium with Mo, Mn, Fe, Cr, and Nb. It is shown that, in agreement with earlier work on the Ti-V system, the composition of the w phase during aging approaches a constant; the value varies from one system to another in a systematic manner with the electron concentmtion. Results relevant to the mechanism of w precipitation during quenching and during aging are presented and discussed. Results are presented to confirm that the w phase is coherent and the nzorphology of the Necipitates is described and discussed. PRECIPITATION of the metastable w phase in alloys of titanium is of interest because of its severe embrittling effect and also because of the enhancement of the superconducting properties which accompanies precipitation.1 The general features of w phase precipitation have been discussed by cuillan and by Bagaratskii et d3 The work described in this paper forms part of a general study of w phase precipitation which was undertaken to elucidate various unknown or controversial features of the process, namely: i) What is the mechanism of formation of the phase ii) How does its composition, morphology, volume fraction, and particle size vary with the type and content of the alloying element and with the heat treatment conditions? iii) What is the relation between the w phase and the equilibrium a phase? In a previous paper4 the results of a detailed study of w phase in Ti-V alloys were presented. It was shown that: U During aging the composition of the w phase approached a saturation value of 13.5 to 14.0 at. pct V. ii) w precipitated as cube shaped particles and once precipitation was complete, particle coarsening did not occur. iii) a phase formed initially by direct conversion of w-phase precipitates. In this paper similar measurements are reported on Ti-Mo alloys and some more limited data given on the Ti-Cr, Ti-Fe, Ti-Mn, and Ti-Nb systems. The results i.1 the six systems are then compared. It has been shown previously by electron microscopy that the w precipitates as ellipsoids in both the Ti-Nb system,&apos; and in i-o.&apos; Blackburn and williamsz3 have reported the precipitates in Ti-Fe, Ti-Cr, and Ti-Mn are cubic, i.e., similar to the Ti-V system.476 EXPERIMENTAL METHODS 1) Specimen Preparation. Samples of the compositions shown in Table I were prepared by arc melting. High purity electron beam zone refined titanium (Materials Research Corporation Grade I—total impurity content =250 ppm) was used; the other source materials are given in the table. A commercial Ti-8 wt pct Mn alloy was used for studies of this system. After homogenization the materials were rolled or cut into strip approximately 1/4 in. by 2 in.; the strip was then heated at temperatures of 1200" to 1300°C for several hours by passage of a direct current through the strip in an ultra high vacuum system (<10-torr) and then quenched by admitting high purity helium and switching off the current. This treatment resulted in crystals up to 2 in. by 2 in. by A in., almost all of which had a [100] direction nearly perpendicular to the plane of the strip. The crystals were cut from the strip by spark machining and their composition checked by lattice parameter measurements supported by chemical analysis. 2) X-Ray Diffraction Methods. Lattice parameter measurements were made using a modification of the single crystal spectrometer described by ond. In this technique the crystal angles for reflection on either side of a highly collimated primary beam are measured. Generally the 400 CuK, or the 400 CuKp reflections of the bcc lattice were used. In the as-quenched crystals a precision of 1 in 105 was obtained, but due to line broadening the parameters in aged materials could only be measured to 1 in lo4. This accuracy was, however, quite adequate for the purposes of these experiments and enabled the composition of the p phase to be obtained to 10.1 pct in all systems except Ti-Nb where the lattice parameter change with composition is very small. The precipitation and growth of the w phase was examined using a single crystal goniometer attached to a Phillips diffractometer. The relative intensities and line shapes of b-phase and w-phase reflections

Jan 1, 1970

By B. I. Ferber

Sodium chloride aerosol was employed to determine respirator filter penetration in a manner suitable for use in Bureau of Mines approval and certification procedures. The aerosol was produced by an ultrasonic generator and treated to yield the proper conditions of relative humidity, particle size, and concentration. Respirator filters were exposed to the aerosol; filter penetration (down to 0.02 percent) was determined with a flame photometer. Results are comparable with those obtained in another laboratory using different equipment.

Jan 1, 1970

By W. R. Bull, J. R. Roos

A method is described whereby the true financial value of each constituent of each concentrate can be calculated. Each value is then compared with what this value would be in a perfect separation. The difference in each case represents the loss incurred by each aspect of an inefficient separation. The relative magnitudes of these losses indicate those avenues of plant investigation and research that offer the highest potential reward. The metallurgical efficiency of a concentration operation is difficult to express because there are two criteria of performance, namely, grade and recovery. Neither of these alone gives any indication of the effectiveness of an operation and, if they are combined in some formula, it must be empirical and unreliable because of many external factors. Since milling is an operation performed as one step in the most profitable overall method of producing a metal or other end product, the main objective of mill operation should be to make a maximum contribution to this maximum profit. When concentrates are sold to custom smelters, the income from the operation, and the costs, may be calculated. When concentrates are further processed by another division of the same company, and there is no formal financial relationship between, say, the milling and smelting divisions of the company, the mill superintendent&apos;s job is less well defined. But even so, if the mill superintendent works as though he were selling his concentrates, and uses reasonable, if fictitious, conditions of sale, then he can get a good indication of the effectiveness of his operation by calculating his "Economic Recovery". ECONOMIC RECOVERY This is a method used as a basis of operation by several mills and has been described in the literature. Very briefly, the "standard" of operation is taken as that of a mill separating the ore into perfectly pure concentrates with 100% recovery of each mineral in its respective concentrate. For example, a 4%Pb, 4% Zn ore (galena and sphalerite), would provide a lead concentrate weighing 4.62% of the feed and assaying 86.6% Pb and a zinc concentrate weighing 5.97% of the feed and assaying 67.1 % zinc. These perfect concentrates are (hypothetically) shipped to the appropriate smelters, freight and treatment charges and payments calculated, and the net return obtained. This is the optimum financial return for the operation of the mill and is used as the standard. Now the return for the actual, real-life, mill operation is calculated in the same way, and the ratio of the two is termed the Economic Recovery. Many additions and modifications may be made in any particular case. For example, if the zinc mineral is marmatite, the optimum grade of the zinc concentrate may be set lower than 67.1%. If silver is present, it will be recovered 100% in the lead concentrate in the perfect operation. Similarly, cadmium will be recovered 100% with the sphalerite. Mr. Weiss&apos; paper&apos; mentions a case where, because of extremely fine intergrowth between the valuable mineral, chalcocite, and pyrite, the optimum grade of copper concentrate was taken as 45% Cu instead of the theoretical 80%. Each operation will present its own possibilities in this way.

Jan 1, 1970

By R. K. Agarwal

Transforming from a mere novelty field of science to a well-recognized branch of engineering, the scientific discipline of rock mechanics continues to mature. The past decade has witnessed an unprecedented in- fusion of scientific research approach into mine design. In the preceding year alone, there were six national and international congresses which also indicated the increased interest, in rock mechanics and participation by scientific personnel with diversified backgrounds. It may be presumptuous to conclude that the time, effort and money spent thus far on procedures for mine structure design have necessarily resulted in the evolvement of design techniques; but certainly the prospects of evolving such techniques art: more promising at present than ever before.

Jan 1, 1970

By M. J. Stewart, F. Weinberg

PREVIOUS investigations into convective flow in molten metals have examined systems in which the length-to-height ratio of the enclosure is large, usually using long graphite boats.&apos;&apos;2 In normal castings this ratio is generally small and it is not possible to extrapolate the results of previous work to casting configurations. The present investigation was undertaken to examine liquid flow in systems of low length to height ratio. The apparatus used for the experiments is shown in Fig. 1. The molten zone of tin is contained in an aluminum mold of inside dimensions 6.4 by 6.4 by 0.31 cm. A heating block containing a resistance coil is attached to one end of the mold and a cooling block is attached to the other end. These are used to produce a wide range of temperature differences across the mold. The mold is contained in a stainless steel tank which is heated from the outside by resistance heaters to give the required operating temperature during the experiment. Temperature measurements in the molten tin are made with an iron-constantan thermocouple PT equal to 5 atm. The phase diagram derived by us was the same as that found by Krivsky and Schuhmann, except for a similar discrepancy in one boundary line representing the gas composition in equilibrium with SO a. The vapor pressures of the pure components can be neglected at 1700°K, 1 atm and 2500°K, 5 atm. There-fore, in these cases PT is essentially the total pres-sure in the system. This is valid for all the diagrams presented by Krivsky and Schuhmann except for the one at 2500°K and 0.01 atm, where the vapor pressure of silicon is comparable to PT.6 This work was supported in part by the American Iron and Steel Institute. &apos;C. E. Wicks and F. E. Block: Thermodynamic Properties of 65 Elements, U S. Bur Mines, Bull. No. 605, 1963. R. P. Elliott: Constitution of Binary Alloys, 1st supplementary, McGraw-Hill Book Co., New York, 1965. 3W. A. Krivsky and R. Schuhmann, Jr.: Trans. TMS-AIME, 1961, vol. 221, pp. 898-904. 4M. F. Ancey-Moret, M. Olette, and F. D. Richardson: Mem. Sci. Rev. Met., 1964, vol. 61, pp. 169-76. 5J . F. Elliott and M. Gleiser: Thermochemistry for Steelmaking, vol. 1. Addison-Wesley, Reading, Mass. 1960. 6 J.Drowart, G. De Maria, and M. G. Ingraham: J. Chem. Phys., 1958, vol. 29, p. 1015. probe of 0.4 mm diam inserted into the open top of the mold. Radioactive sn113, in the form of a small sphere, was gently lowered into the molten tin at point A in Fig. 1 THERMOCOUPLE> WATER ARGON END HEATER QUENCH ARGON Fig. 1—Apparatus for detecting liquid flow. Point A indicates position the tracer was introduced.

Jan 1, 1970

By W. H. A. Timm

Lake Dufault Mines, Limited, is located ten miles north of Noranda, Quebec, Canada. Following discovery of a copper-zinc orebody late in 1961, metallurgical investigations of diamond drill core were conducted by Lakefield Research Limited during 1962 and 1963. These were followed by pilot-plant tests in May and June of 1964, utilizing underground development ore. Milling operations commenced on August 16, 1964, and reached rated capacity of 1300 tpd by October 1, 1964. Since that time, tonnage was gradually increased to a maximum of 1400 tpd and since January 1, 1968, gradually decreased to the present rate of 1100 tpd due to an increase in the hardness of the ore. The ore milled from start-up until January 1968, was mainly massive sulfides, consisting of a complex mixture of iron, Copper, zinc, and minor amounts of lead sulfides with important associated values in gold, silver and cadmium (average specific gravity of 3-8). From January 1968 until the present, the ore being processed is described geologically as a boxwork of sulfide stringers of chalcopyrite, pyrite, and pyrrhotite with some local dissemination in siliceous rhyolite (average specific gravity 2.9) supplemented by the massive copper-zinc ore. The limited size of the orebody and the mining method employed (open stoping by blasthole and slash benching methods) would have

Jan 1, 1970

By George S. Ansell, Thomas E. Davidson

It has been known for a considerable period of time that the ductility of even quite brittle materials can be enhanced if they are deformed under a superposed hydrostatic pressure of sufficient magnitude. The response of ductility to pressure, however, has been shown to vary considerably between materials. Prior work has shown that the effects of pressure upon the tensile ductility of Fe-C materials depend upon the amount, shape and distribution of the brittle cementite phase. In this current investigation, the effects of pressure upon the fracture mechanisms in a series of annealed and spheroidized Fe-C materials were examined. It was observed that the principal effect of pressure is to suppress void growth and coalescence, retard cleavage fracture and to enhance the ductility of cementite platelets in pearlite. Based upon the observed effects of pressure upon the fracture mechanisms, a proposed explanation for the enhancement in ductility by pressure and for the structure sensitivity of the phenomena is presented and discussed. THE effect of superposed pressure upon the tensile ductility of a variety of metals has been well documented.&apos;-&apos;&apos; Some of the results from several investigators are summarized in Fig. 1 where tensile ductility in terms of true strain to fracture (ef) is plotted as a function of the superposed pressure. As can be seen, a pressure of sufficient magnitude can significantly enhance the ductility of metals. However, Fig. 1 also demonstrates that the response of ductility to pressure and the form of the ductility-pressure relationship varies considerably between materials. Several explanations have been offered for the observed enhancement in ductility by a superposed pressure. Although no experimental evidence was provided, Bridgman13 and Bobrowsky10 proposed that the observed effect was due to the prevention or healing of microcracks or holes. Bulychev et a1.14 observed that cracks and voids in initially prestrained copper were healed in the necked region of a tensile specimen upon further straining while under a superposed pressure. Also, pugh5 observed that large cavities were suppressed in copper fractured in tension while under pressure. A second proposal has been forwarded by Beresnev et at al.6 This proposal is based upon the hypothesis that a material fails in a brittle manner because the normal tensile stress reaches a critical value before the shear stress is of sufficient magnitude to cause plastic flow. Since a superposed hydrostatic pressure will increase the ratio of shear to normal tensile stress, a sufficiently high hydrostatic pressure should favor plastic flow while retarding brittle fracture. Galli15 reported that a superposed pressure shifts the ductile-brittle transition temperature of molybdenum. This was explained based upon the reduction of the normal tensile stress by the superposed pressure. Pugh5 explained the occurrence of the observed pressure induced brittle-to-ductile transition in zinc in the same manner. Davidson et al.12 proposed an explanation for the enhancement of ductility by pressure based upon the effects of pressure upon the stress-state-sensitive stages of various fracture propagation mechanisms. Basically, they proposed that pressure will retard cleavage and intergranular fracture by counteracting the required normal tensile stress or will suppress void growth. They observed suppression of intergranular fracture and void growth in magnesium by pressure. Davidson and .Ansell16 reported ductility as a function of pressure for a series of annealed and spheroidized Fe-C alloys. Fig. 2, from this prior work, demonstrates that the effect of pressure upon ductility is structure sensitive in terms of the amount, shape and distribution of the brittle cementite phase. As shown in Fig. 2, in the absence of cementite or when the cementite is in isolated particle form (spheroidized), the ductility-pressure relationship is linear and the slope decreases with increasing carbon content. In the annealed carbon-bearing alloys wherein the cementite is in the form of closely spaced platelets (pearlite) or in the form of a continuous network along prior aus-tenite boundaries (1.1 pct C material), ductility as a function of pressure is nonlinear (polynomial relationship) in which the slope increases with increasing pressure. At the highest pressures studied (22.8 kbars), the slope of the curves for these materials tends to approach those for the spheroidized material of the same carbon content. In this current investigation the change in fracture mechanisms as a function of pressure for the materials shown in Fig. 2 has been examined. The possible connection between the observed effects of pressure upon the fracture mechanisms and the effect of pressure upon ductility is discussed.

Jan 1, 1970

By J. O. Wheeler

"DEFINITION OF THE REGION, ITS BOUNDARIES, AND PHYSICAL AND GE'OLOGICAL CHARACTERISTICSTHIS PAPER concerns the Western Cordilleran region, embracing most of British Columbia, the southern half of Yukon Territory and the southwesternmost part of the District of MacKenzie. It excludes Vancouver Island and the Queen Charlotte Islands, which are discussed in a background paper on the Pacific Continental Shelf. The region is bounded on the south by the northwestern United States, on the west by the continental shelf and Alaska, on the north by the front of the Ogilvie Mountains, on the northeast by the axis of the MacKenzie Mountains and on the east by the Rocky Mountain Trench.The region is dominated by two mountain chains that con tain icefields and glaciers: the St. Elias, Coast and Cascade Mountains in the west; the Selwyn, Pelly, Cassiar, Omineca and Columbia Mountains in the east. The Intermontane region between these mountain chains consists of lower mountains and plateaus. In the mountains, the region above the timberline and many of the steep valley-walls provide good exposures of rock, but these areas are subject to rockslides and landslides and in winter to snow avalanches. Much of the Western Cordillera was covered by ice-sheets at various times during the Pleistocene epoch. Consequently, the larger valleys in the mountains and much of the Intermontane region contain much glacial drift and alluvium and only limited exposures of rock. This same terrain in the Southern Cordillera, however, is the most favourable for agriculture. Parts of the region, particularly in the two mountain chains, are heavily forested. Elsewhere, the forest cover is less, with grassland prevailing in the south and tundra in the north."

Jan 1, 1970