By P. Shahinian, R. L. Stegman, M. R. Achter

Creep strength has been determined as a function of oxygen pressure for nickel at 510" and 600°C. Creep-rupture life drops from its highest value at the ultimate vacuum of 10-7 torr to a high pressure plateau of nearly constant life which, at 600°C, commences at torr. This behavior is described in terms of a model that relates surface gas adsorption and the generation of fresh crack surfaces. In a calculation based a this model the predicted pressure beyond which the creep strength should not decrease further has been found to agree well with the observed value. The introduction of oxygen during creep in vacuum was found to cause a prompt rise of the creep rate. The magnitude of the environmental effect was much less than generally observed in fatigue and this is attributed to the diffarent crack morphologies in creep and fatigue. GASEOUS environments are known to affect creep resistance adversely1-5 but the effects have received less attention than the much larger ones in fatigue. At low temperatures it has been shown for nickel that the creep rates are faster and the rupture lives are shorter in air than in vacuum and that these environmental effects can be correlated with faster crack growth rates in the reactive environment.' In support of a mechanism of gas adsorption at the crack tip to explain the above effects, a calculation based on kinetic gas theory showed that surface coverage by gas was not as rapid as the exposure of fresh metal at the crack tip in the ultimate vacuum but was in air.7 In fatigue a number of investigations have demonstrated that the reduction of life with gas pressure usually follows a step curve with most of the reduction occurring in a transition range at intermediate pressures and little or no change at high and low pressure.8 There have been no studies, however, in which creep strength has been determined as a function of reactive gas pressure to see whether similar effects would be found. This investigation was undertaken to study the kinetics of the environmental effect in the creep of nickel. EXPERIMENTAL PROCEDURES The environmental creep apparatus was constructed to minimize many of the experimental conditions which can cause scatter in data. Dead weight loading is employed and weights are contained within the environmental chamber to eliminate bellows and the necessity for compensation for gas pressure changes. Elongation over the specimen gage length is recorded from a Riehle Model DV Controlled Environment Extensometer which provides readout to 2.5 x 10- in. Temperature is monitored and controlled from a thermocouple at- tached to the specimen gage length to +0.5oC or better. The freon trapped oil diffusion pump vacuum system included an auxiliary liquid nitrogen trap and, with a wide range variable conductance leak valve, pressures from the ultimate vacuum of 10"7 to l03 torr of any desired gas are obtainable. Pressure is measured by means of a hot filament ionization gage below 10"3 torr and a NRC Model 530 Alphatron Vacuum Gauge above 10-3 torr. The oxygen, which was leaked into the environmental chamber, was an Aviator's Grade of 99.5 pct purity with a dew point of -80°F. Analysis of the nominal 99.8 pct Ni showed the following percentages of major impurities: 0.02 C, 4.01 Mn, 0.005 Si, 0.01 Cu, 0.02 Fe, and 0.034 Mg. Cylindrical specimens were machined with a 0.180

Jan 1, 1970

By Charles H. Grant

Some of the limiting factors relative to explosive crushing of rock and ways to overcome a few of these problems are presented. Relationships between borehole diameters, bench heights, and spacings, along with a review of the influence geometry has on energy as these are changed, are discussed. Efficiency in use of explosives and the decay of energy as it moves through rock and is absorbed and dissipated, is described, along with fragmentation as a function of spacings and energy zoning, etc. Communications are one of the major problems encountered. In an effort to provide a better understanding of the use of explosives, it is necessary to take a little different view of what explosives are, how to look at them as tools to fragment rock, and some of the problems encountered in doing so. First, take the explosive: although there are many factors involved, consider these as being reduced to only two — shock-strain imparted to the rock by the high early development of energy, and the gas effect which is a combination of heat, moles of gas formed, rate of formation of these gases which develop pressures, etc. First, consider shock energy by itself and assume there is no gas effect in the reaction. Fig. 1 illustrates a block or cube of rock, in the center of which is detonated an explosive charge which is 100% shock energy. Tensile slabbing would be seen on the surface and probably the cube of rock would generally hang together even though microcracks were formed. If the situation is reversed and an explosive whch has no shock energy and only gas effect (Fig. 2) is considered, the cube of rock would act as a pressure vessel and contain the pressure from the gas effect until it exceeded the rock-vessel strength; then the rock would break in a few large pieces. If these two kinds of energy are put together and the area of shock-strain around the explosive (Fig. 3) is considered, the two energies will be seen working together to furnish broken rock. The gas effect applies pressure to the microcracks formed from the shock energy to weaken the rock-pressure vessel and propagate these cracks to break the rock apart. It not only will be broken more finely, but will break apart at a lower pressure than the gaseffect case, since the shock energy has first weakened the rock vessel. Although tensile spalling from the shock-strain imparts momentum to the rock, the main source of displacement comes from the gas effect. The term "rock" is being used to mean any material to be blasted. These energies are absorbed by the rock in different ways. First, classify rock into two main categories: "elastic" and "plastic-acting." Elastic rock should be thought of as rock which can transmit a shock wave and is high in compressive strength, such as granite or quartzite. Since this elastic rock transmits a shock wave well, it makes good use of the shock energy from the explosive-forming cracks, etc., for the gas effect to work on. Plastic-acting rocks are rock masses which are relatively low in compressive strength and absorb shock energy at a much faster rate, thereby making poor use of the shock energy by not developing as extensive a cracked zone for the gas effect to work on. Rocks of this type are generally softer materials such as some limestones, sandstones, and porphyries. For the most part, the shockenergy part of the explosive reaction is wasted in plastic-acting rock, leaving most of the work to the gas effect. Since the ratio of gas effect to shock energy is different in different explosives, it is easy to understand why some explosives perform well in elastic rock and poorly in plastic-acting rock, and vice versa. Some of the most difficult blasting situations arise when mixtures of plastic-acting and elastic rock are encountered (Fig. 4). Fig. 4 shows an example of granite boulders cemented together with something like a decomposed quartz monzonite which is plastic-acting. The elastic granite boulders will transmit the shock-strain within itself, but when this shock tries to move through the monzonite to the next boulder, its intensity is absorbed by the monzonite and little shock-strain is placed on the adjoining boulder. In addition to this loss by absorbtion, shock reflection at the surface of the boulder will effect tensile spalling. The net effect is poor breakage of the boulders which do not have drillholes in them as they simply will be popped out with the muck. The same is true (Fig. 5) when layers and joints make

Jan 1, 1970

By L. D. Fetterolf

The New Jersey Zinc Zompany operates at Depue, Illinois, an integrated zinc smelting plant using tie vertical retort reduction process. The overall operation comprises green concentrate roasting, sintering, vertical retort smelting and metal refining. In the roasting operation, the fine concentrate is pelletized, the dried pellets fluidized and autogenously roasted with air in a “fluid column” with minimal formation of dust requiring recirculation. The roasted pellets and any associated roaster dust are agglomerated in a rotating drum and laid down, in combination with coal for fuel, on a Dwight-Lloyd sintering machine which converts to a semi-fused mass - a physical state more suitable for vertical retort smelting. The smeltins plant of 27 vertical retorts rated at 8 T zinc each per day on average requires the following major processing steps - mix preparation and briquettine, briquet coking, vertical retort reduction, vapor condensation and slab casting of metal. A portion of zinc production is converted to 99.99+ percent purity by boiling and fractional distillation in columns consisting of externally heated, superimposed trays of high-conductivity refractory.

Jan 1, 1970

The commonly used Stopes-Heerlen coal petrographic classification and nomenclature has over the years been subject to variable interpretations. This paper discusses the problem with specific reference to the inertinite maceral group. The effect of various interpretations of the Stopes-Heerlen system on maceral analysis is discussed and illustrated by means of comparative analyses conducted by a number of laboratories in Australia.An attempt is made to define the reflectance thresholds used by the authors to subdivide the inertinite group; the genetic and technological significance of these thresholds are compared.The difficulties of distinguishing structured and nonstructured macerals of the inertinite group are discussed in terms of possible improvements to the present StopesHeerlen system by extending the classification to include transitional maceral types.

Jan 1, 1970

Lead isotope measurements indicate that lead from the A.B.H. Consols mine and two transgressive veins in Browne's shaft is "Thackaringa" type and not "Broken Hill" type.

Jan 1, 1970

By M. K. Foster

Ten horizontal retort zinc blocks of a modified Hegeler design are in operation at Nueva Rosita, Coahuila, Mexico, and produce approximately 170 t of spelter daily, or 62 000 t/year. A block consists of two furnaces of 448 retorts each, making 8960 retorts as the plant complement. Each furnace block is fired with natural gas and air maintaining the combustion mixture in the furnace always slightly reducing. No attempt to recover energy through waste heat boilers is made. The spelter moves to market by rail and truck either in palletized bundles weighing approximately 1060 kg, as loose slabs weighing 26.5 kg each, or as 1088 kg ingots. At present 46% of the metal is exported and 54% is consumed domestically in Mexico. The present day trend toward equalized or alloyed spelter, as well as special shaped castings results in sales of 35% of the entire plant's production. Sulfuric acid is also produced by the Contact Process using vanadium pentoxide as the catalyst. The plant is basically a Monsanto contact system, producing approximately 68 t of 100% sulfuric acid daily. Both 98.5% sulfuric acid and 20% oleum are available. All of the acid made is consumed in Mexico. Shipments are made in 26,900 dm3 tank cars.

Jan 1, 1970

Standard petrographic profiles for many Permian seams from New South Wales and Queensland have been drawn up. The standard profiles of seams of the same age and from one or more coalfields were used to compile an idealized or type seam sequence for those coals in which more than half the seam profiles were similar to one another. A marked similarity existed between at least 7 of the 10 type seam sequences formed.The configurations of the vitrite-plus-clarite contents of the plies of 95 per cent of the seams could be formed from different arrangements of 3 basic sequences. These were...

Jan 1, 1970

By S. C. Gambrell

The practice of roof bolting in world-wide mining activities is very well known, having been used extensively for over 50 years. The theory of roof bolting, however, is extremely complicated, and only recently have investigators attempted to explain the theory. Discussions of the mechanics involved usually originate with actual experience gained in the use of roof bolts. The use of roof bolting in mines has grown dramatically during the period after World War II. Other scientific techniques have emerged in mining research in the same period. Included in these techniques is the study of rock mechanics, which has now developed into an impressive research effort. Various means of analysis have been utilized in rock mechanics, most of which reduce rock to an isotropic, homogeneous medium that could be easily analyzed. Because of the inherent nature of rock, direct research methods frequently are not certain to provide satisfactory results, whereas indirect methods must idealize a given set of conditions in order to be useful. One of the indirect research methods is the photoelastic technique, the theory of which is widely known and needs no elaboration. This technique has been used extensively to examine the state of stress around underground openings of various shapes in certain types of strata, and under various configurations (1,2,3,4,5). Much of the theory used now in the design of underground openings is based on photoelastic evaluation. Unless rigorously applied, how- ever, the photoelastic technique is at best a qualitative means of evaluation. It is useful, however, for unusual examples which can be more or less easily analyzed to obtain the overall state of stress which could not be determined by other means. Little work has been done in the photoelastic analysis of rock bolting, mainly because direct research techniques have proven useful.

Jan 1, 1970

By Freeman Bishop

Before Capitol Hill hearings, primary metal producers are often called "concentrated industries" because there are relatively few companies in each category and most of them are large corporations. Capitol Hill still looks on large companies as inherently wrong, but there are about as many arguments one way as the other. Encourage Imports? Now comes Assistant Attorney General for Antitrust Richard W. McLaren to say that imports of metals and other basic materials should be encouraged to create competition for the concentrated industries here at home. Cloakroom analysts are wondering how this ties in with President Nixon's cabinet task force studying the copper price structure. This is chaired by Dr. Hendrik Houthakker, a member of the White House Council of Economic Advisers who has also indicated that the use of imports to pull down prices may be one way to create less inflation.

Jan 1, 1970

By L. Valentik

Many attempts have been made during the last 40 years to evaluate the performance of gravity separation equipement, that is, the effectiveness with which light and heavy particles are separated. The most comprehensive treatment of the subject was made by Cerchar at the 1st International Conference on Coal Preparation held in Paris in 1950. The methods suggested by the Conference were accepted and very widely used in the last two decades. This paper discusses an improved method of evaluation in the light of the now-accepted standard presentation. The float-and-sink analysis of the product is presented on a Gaussian distribution curve, resulting in an easier visualization of the inherent difficulties of separation. The ogives of the distribution curve me then plotted, giving a quantitative measure of the deviation from perfect separation as an error distance instead of an error area. Illustrations of the new method are given both for gravel and for coal preparation, but the content is valid and applicable to other types of minerals which are separated by gravity methods. Many attempts had been made during the last forty years to evaluate the performance of heavy-media separation (HMS) equipment, that is, the effectiveness with which floats and sinks are separated.'-' The most comprehensive treatment of the subject was made by Cerchar at the 1st International Conference on Coal Preparation held in Paris. 6 The primary aim was the thorough understanding of the mechanism of separation and the unified presentation of data on gravity separation so that the evaluation and comparison of washery performance could be made from all over the world. No strict overall standardization has been achieved, but after the conference a more or less uniform presentation of performance was accepted, which, during the last two decades, has been very widely used. In this paper, illustration of the old methods and an improved method of evaluation will be given. HEAVY-MEDIA SEPARATION (HMS) PERFORMANCE CRITERIA In the ideal HMS process, all material lower in density than the specific gravity of separation (SGS) would be recovered as floats and all material of higher density would appear as sinks. In order to evaluate the misplaced material, the washery products are tested at the density at which the washing unit is operated. The original type of plot1,7, 8 is shown in Fig 1; this was developed primarily for coal cleaning units. The curve for raw coal represents the cumulative percentages of sink material. The refuse curve is also plotted as a cumulative sink, the percentages being expressed in terms of raw coal. This diagrammatic representation of the results of washing units has the merit of easy visual observance of the degree of separation obtained. The error areas (cross-hatched) are a measure of the amount of misplaced material and therefore they can be used to characterize the quality of separation. The ideal and actual separating performance between floats and sinks can be best seen from the partition curve developed by Tromp,2 where the ordinate is the percentage recovery of the sinks, and the abscissa is the specific gravity (Fig. 2). It can be seen from the shape of the curve that as the SGS is approached, the proportion of material reporting to the improper product increases rapidly. In fact, the SGS can be defined as the density of the material in the feed that is distributed equally between float-and-sink products. When the upper half of the curve is inverted, a shape similar to that of a Gaussian error distribution curve is obtained and therefore the analysis of gravity separation may be carried out by using the law of probability. The shape of the curve in Fig. 2 is determined partly by the density composition of the feed, and partly by the sharpness with which the unit separates floats from the sinks.9, l0

Jan 1, 1970

By H. R. Babitzke

As part of a continuing project to develop refractory metal alloys for high-temperature structural applications, the Bureau of Mines applied solid solution and precipitation strengthening techniques to improve the properties of columbium alloys. The purpose was to investigate the effects of hafnium, tungsten, and boron on the formability, strength, and oxidation resistance of columbium. The experiment was of factorial design with two replications which called for 72 ingots of 36 basic compositions, weighing 150 grams each. Hafnium, tungsten, and boron were evaluated at 3, 3, and 4 levels, respectively. Values of alloy content are all in atomic percent. The highest strength observed was 29,000 psi at 1,200° C for alloys Cb-15Hf (No. 3), Cb-7.5Hf-5W-2B (No. 14), and Cb-15Hf-5W-2B (No. 15). At 1,200° C, the ternary alloy Cb-15Hf-5W (No. 6) which has shown good properties in previous Bureau of Mines investigations was the most resistant to oxidation For boron additions, the alloys oxidized more readily with increasing amounts of this element. The fabricability of the alloys high in boron became increasingly difficult, resulting in an inadequate number of alloys required for a complete statistical analysis for all the tests. As a result of the decrease in ductility, an insufficient quantity of tensile samples were available for a proper analysis for the high-temperature strength data.

Jan 1, 1970

By F. F. Aplan

Pollution control will be of utmost importance in the 1970's. In this area, the mineral process engineer has a special competence to understand and remedy many pollution situations. There is an old adage that goes, "Build a better mouse- trap and the world will beat a path to your door." Would that it were so, but the reality of the situation is such that, just as a supplier must sell his machine, a professional man must sell his competence. It is a sad but true fact that mineral processing engineers have not done a very good job in selling their extensive competence in the control of a broad range of pollution problems. Recently one of our students visited a paper pulp mill where he was shown a foam fractionator used to remove paper pulp fibers from plant discharge waters. "Foam fractionator hell, that's a flotation cell!'' was his comment. Ah so, it would appear that large numbers of technical people consider themselves experts on "foam fractionation" Or is it that we have been very remiss in demonstrating the usefulness of our equipment and processes and our professional competence to solve, these pollution problems?

Jan 1, 1970

By Richard W. Greene, Joel S. Hirschhorn

MATERIALS containing very large amounts of porosity, in the order of 50 to 90 vol pct, are extremely difficult to evaluate according to conventional mechanical behavior tests. This is usually a consequence of their low strength and brittleness, and the difficulty of preparing standard test specimens. A simple fatigue test has been developed and used successfully on porous nickel sheet materials requiring no specimen preparation; it could also be used for configurations other than sheet or plate. Samples of the sheet. 2 in. sq and about 0.025 in. thick, are placed in a vessel that is evacuated to about 50 f Hg by a mechanical pump. Distilled and deairated water is allowed to enter the vessel thereby filling the porosity (virtually all the porosity in these nickel ma-

Jan 1, 1970

By Raymond D. Daniels, Frank E. Rizzo, James D. Gerber

ThIS discussion describes a method for the addition of small amounts of oxygen to columbium (niobium) in an accurate and reproducible manner. The method is based on the complete reduction by columbium of a carefully weighed amount of another metal oxide. The equilibrium Pq associated with Cb-CbO mixtures is extremely low, e.g., 10"25 atm at 100O°C, and the pressures over Cb-0 solutions are even lower. The equilibrium Pq associated with a given metal-metal oxide mixture can be easily obtained, with the aid of a Richardson-Jeffes chart.' Although columbium should effectively reduce almost any metal-metal oxide combination, the proper choice of a metal-metal oxide system is complicated by the low rate of oxygen transport in the gas phase at low oxygen pressures and the difficulty in reducing any columbium suboxide formed during the reduction of the oxygen source material. Thermodynamically, oxide formation on columbium will be avoided so long as the oxygen partial pressure over the columbium is below the equilibrium pressure associated with the mixture Cb-CbO. The logical choice of a source for oxygen would appear to be a mixture of Cb-CbO, since oxide formation would be precluded by nucleation difficulty. But calculations using the kinetic theory of gasses indicate that, for a temperature of 900°C, the reaction would proceed too JAMES D. GERBER, formerly Research Assistant, University of Oklahoma, Norman, Okla., is Research Metallurgist, Air Force Weapons Test Laboratory, Kirtland Air Force Base, N. Mex. FRANK E. RIZZO, Junior Member AIME, formerly Assistant Professor of Metallurgy, University of Oklahoma, is Associate Professor of Metallurgy, University of Texas at El Paso, El Paso, Tex. RAYMOND D. DANIELS, Member AIME, Professor of Metallurgical Engineering, University of Oklahoma, is an NSF Fellow, Institute de MBtallurgie Structurale, Universite de euch:tel, Neuchitel, Switzerland. Manuscript submitted October 28, 1968. IMD

Jan 1, 1970

By Stephen D. Cramer

A nondestructive procedure for measuring electrodeposit porosity has been developed which records the location and number of deposit defects including pores, pits, and voids. The procedure involves the passage of an X-ray beam through the deposit-substrate system onto suitable film. The defects are recorded as images on the film. Variables studied included intensity and spectra of the X-ray beam, composition and thickness of deposit and substrate, film type and developing procedure, and limits for detecting defects. At an X-ray tube voltage of 40 kv, pores several mils thick were easily detected in copper-nickel specimens more than 20 mils thick. To illustrate the utility of the procedure, the effect of substrate oxidation and of current density on electrodeposit porosity was briefly studied.

Jan 1, 1970

By J. David Lowell

On a low desert ridge six miles south of Cairo lie the remains of the world's earliest known mining town, Maadi of predynastic Egypt. Copper artifacts, including ingots and an ax head which was spoiled in casting, indicate that copper ore was smelted in Maadi, and radio- carbon dating has placed the activity at least as early as 3300 B.C. This is the oldest documented date for the use of smelted copper, the first industrial metal used by man. Copper was mined and smelted almost as early in Asia Minor and on the island of Cyprus, but the greatest development of the budding copper industry was in Egypt, where specific historical records show that about 10,000 tons of copper metal were produced in the period from 1850-1580 B.C. Contrast this production of 35 tons per year with the present world production of about 7 million tpy.

Jan 1, 1970

By R. E. Cech, T. D. Tiemann

It has been shown that hydrogen may be made to serve as a rapid and eflicient reducing agent for Cu, Ni, Co, and Fe sulfides if a scavenging agent for hydrogen sulfide is intimately mixed with the sulfide particles being reduced. Accelerated reduction kinetics are demonstrated for nickel sulfide. Copper, nickel, and cobalt sulfides, when treated at certain temperatures in a combined reducing agent-scavenging agent system, are converted to voluminous masses of fibrous metal product. Studies have been carried out to determine the conditions which lead, on the one hand, to irregular poly crystalline fibers and, on the other, to long single crystal filaments a few microns in diameter. A mechanism is proposed to account for the formation of single crystal filuments. The sulfide minerals of Cu, Ni, Co, and Fe are an important source of these metals yet there has been comparatively little scientific effort devoted towards understanding reduction mechanisms of these minerals. This may be, in part, due to the fact that the most convenient reducing agents for carrying out such studies, viz., hydrogen and carbon, do not react appreciably with sulfides. We have found that the reaction of hydrogen with metal sulfides can be markedly accelerated by placing a scavenging agent for hydrogen sulfide in close proximity to the metal sulfide. A brief series of experiments demonstrating relative reduction rates is reported in this paper to illustrate the effect. With the reduction process thus accelerated we have observed an unusual type of reduction behavior on some of the sulfides investigated. Under certain conditions the metallic product of the reduction reaction takes the form of filaments growing outward from the sulfide particles. The present paper deals largely with efforts to classify the various types of growth forms observed. This study has shown that filamentary growths from sulfides take a much greater variety of forms than has heretofore been reported by Ercker,1 Hardy,2 and Nabarro and Jackson3 in their reviews of metallic growths from copper and silver sulfides. THERMODYNAMIC CONSIDERATIONS The thermodynamics for hydrogen reduction of metal sulfides is quite unfavorable. For the sulfides considered here equilibrium constants typically range from 10-3 to 10-5. These low equilibrium constants impose severe kinetic limitations on reduction since hydrogen sulfide must be transported out of the system at concentrations of only a few hundred ppm. Unless extremely high gas flow rates are employed the atmosphere surrounding any sulfide particle will always be essentially in equilibrium with the sulfide. If, however, one places an efficient scavenging agent for hydrogen sulfide in close proximity to the metal sulfide particles the concentration of H2S near the metal sulfide will be held to a very low value. This would permit the reduction reaction to proceed with little or no inhibition from a buildup of reaction product gas. It is well known that calcium oxide is capable of removing hydrogen sulfide from a hydrogen gas stream of low dew point.4 If a sufficient quantity of calcium oxide is mixed with the metal sulfide particles the reaction: CaO+H2S=CaS+ H2O [l] will substitute moisture in place of hydrogen sulfide in the gas stream and this will not affect, in a direct manner, the reaction: MeS +H2=Me + H2S [2] A convenient method of considering the thermodynamics of the combined reducing agent-scavenging agent system is to consider the atmosphere when the partial pressure of hydrogen sulfide is the same over both the metal sulfide and the scavenging agent, i.e., pH2S (1) =pH2S (2). As a consequence: pH2O (1) pH2(2) =K1K2 The chemical driving force for reduction will depend inversely upon the moisture content of the gas and will be 0 when, in the system, pH2O = pH2.K1K2. Table I lists values of the equilibrium constants for reduction and H2S scavenging reactions for a number of sulfides at several temperatures. Data are taken from Rosenqvist4,5 and Kelly.6 The equilibrium constant products calculated from this data show that the limiting level of gaseous reaction product has been increased by a factor of 10' to l04 as a result of substituting a reducing agent-scavenging agent system for a simple reducing agent system. One possible side effect which must be considered is the possibility that the moisture evolved in the scavenging reaction might cause the atmosphere in the system to be sufficiently oxidizing to favor the formation of oxide rather than metal. This possibility was examined by comparing the equilibrium constant products listed in Table I with equilibrium constants for hydrogen reduction of the respective metal oxides. It was found that for copper, nickel, and cobalt the combined reduction-scavenging reactions could not develop a sufficiently high oxidizing potential in the

Jan 1, 1970

Jan 1, 1970

By Fathi Habashi

OXIDE ORES can be divided into two groups: 1) Simple oxides (Table 3.1). 2) Complex oxides. Those ores containing minerals composed of two oxides; an acid oxide (Cr2O3, Nb2O5, etc.), and a basic oxide (CaO, FeO, MnO), as shown in Table 3.2.

Jan 1, 1970

The C.S.A. copper-lead-zinc mine, located 7 miles north of Cobar in central-western New South Wales, is the largest known mineral ocurrence in the Cobar mining field. The generally discordant orebodies occur within a strike width of 600 ft and an overall strike length of 1200 ft. They are enclosed by the steeply westdipping, west-facing sediments of the Cobar Group, and comprise lenticular steeply north-pitching and eastdipping zones of sulphide mineralization which range in composition from massive pyrite-sphalerite-pyrrhotitegalena to less massive pyrite-pyrrhotite-chalcopyrite varieties.The thinly bedded siltstones, shales, and greywackes enclosing the mineralization appear to have derived some of their constituents from volcanic sources. They have been metamorphosed to the greenschist facies of regional metamorphism. At least two stages of deformation and folding have occurred. The first stage folded the rocks on a south pitching fold axis into their present configuration, and superimposed a strong axial plane cleavage which subsequently guided the emplacement of the mineralization. The second stage of deformation is considered to have controlled the zonal distribution of the orebodies.

Jan 1, 1970