Search Documents

By M. Ahlers, Horace Pops

Slip features and formation of stress-induced mm-tensite have been studied in single crystals of fl phase Cu-Zn alloys in the composition range between 43 and 48 at. pct Zn. A phenomenological analysis is presented in which the glide planes and directions that me associated with the inhomogeneous shear in the martensite phase are predicted from the experimentally determined habit planes and macroscopic shear directions. It is shozun that the resolved shew component of the applied stress on the secondary shew system is a very important factor governing the formation of stress-induced martensite. A comparison is made between martensitic phases that form spontaneously upon cooling and those phases that arise from deformation. THE ß phase in Cu-Zn alloys is unstable and may transform spontaneously by a martensitic transformation1-3 during cooling. Thermoelastic and burst-type spontaneous martensitic phases have been observed3 in the composition range between 38 and 42 at. pct Zn. Martensite forms in alloys containing more than 42 at. pct Zn only by cold work below a temperature denoted as Md.4 Thus, alloys near the equiatomic composition can undergo a stress-induced transformation upon cold work at room temperature. Although data have been obtained concerning the effect of temperature5 and composition4 on the deformation of polycrystalline Cu-Zn alloys, it is rather surprising that few detailed studies6-8 on 6 brass have been conducted for single crystals where the stresses acting on crystallographic planes can be determined. A thorough understanding of transformation mechanisms requires knowledge of the role of stress and plastic strain. With this objective in mind we have made an investigation of the stress-induced rnartensite transformation in single crystals of 0 brass in the composition range between 43 and 48 at. pct Zn. Particular emphasis is given to the morphology and crystallographic features and a comparison is made between stress-induced and spontaneous martensite. I) EXPERIMENTAL PROCEDURE Master alloys having nominal zinc contents of 43, 45, and 48 at. pct were prepared from spectroscop-ically pure metals (>99.999 pct) in sealed quartz tubes under a partial pressure of helium. These alloys were cut into several pieces and converted into small rods by melting in quartz tubes. Subsequently, single crystals were grown from the rods by the Bridgman technique and homogenized for 3 hr at 820°C. Lattice parameter measurements were made from stress- relieved filings. Compositions, as determined from the reported variation of lattice parameter with atomic percent zinc,' indicated a zinc loss of less than approximately 0.25 at. pct. The single crystals were electroturned using a phosphoric acid electrolyte into tensile specimens each with a center section of 1 mm diam and 1 cm gage length. Cylindrical specimens approximately 3 mm in diam and 10 mm long and spark-machined rectangular blocks approximately 3 by 3 by 10 mm were prepared for compression studies. These blocks were stress-relieved and electropolished to eliminate any stresses introduced by spark machining. Crystal orientations were determined to an accuracy of ±2 deg primarily from back-reflection Laue photographs, and sometimes by the rotating single-crystal method. Figs. 1 to 3 show the location of the tension and compression axes within unit stereographic triangles. All specimens were deformed plastically at room temperature using an Instron machine, the crosshead speed being 0.02 or 0.05 cm per min. A hard steel hemisphere was placed at the upper end of the compression samples to achieve uniaxial loading. Trace normals of slip markings and habit planes of strain-induced martensite were determined to an accuracy of ±4 deg from the rectangular blocks by a two-surface analysis and from cylindrical specimens by measuring the angle between the tensile (or compression) axis and the tangent to the surface trace for different rotations about the deformation axis. Slip

Jan 1, 1969

By G. H. Bishop

The kinetics of the inter granular penetration and embrittlement of [100] tilt boundaries in 99.998 pct pure nickel upon exposure to bismuth-rich Ni-Bi liquids have been determined in the temperature range from 700° to 900°C. The kinetics of penetration are parabolic in time at constant temperature over most of the temperature range. In a series of 43-deg bicrystals the rate of penetration is anisotropic with respect to the direction of penetration into the grain boundaries. In lower-angle bicrystals the penetration rate is isotropic. The rate of penetration decreases with tilt angle at 700°C. The activation energy for penetration in the 43-deg bicrystals is 42 kcal per g-atom independent of direction. It is concluded that the intergranular penetration and embrittlement in the presence of the liquid proceeds by a grain boundary diffusion process and not by the intrusion of a liquid film. This was confirmed by a determination that the kinetics of penetration and embrittlement were the same in the 43-deg bicrystals upon exposure to bismuth vapor under conditions such that no bulk liquid phase would be thermodynamically stable. WhEN solid metals are exposed to a corrosive liquid-metal environment, the grain boundaries are sites of preferential attack. Depending on the temperature, the composition of the liquid, and the composition, structure, and state of stress of the solid, a number of modes of attack are possible. This paper reports a study of the kinetics of intergranular penetration and embrittlement of high-purity nickel bicrystals upon exposure to bismuth which, together with an earlier study by Cheney, Hochgraf, and Spencer,&apos; demonstrates that there are at least two modes of intergranular attack possible in the Ni-Bi system. In the study by Cheney et al., columnar-grain specimens of 99.5 pct pure nickel were exposed to liquid bismuth presaturated with nickel in the temperature range 670" to 1050°C. They found that the majority of the boundaries, which were predominantely high-angle boundaries, were penetrated by capillary liquid films, the attack proceeding by a process which will be termed grain boundary wetting. This process occurs in a stress-free solid when twice the liquid-solid surface tension is less than the surface tension of the grain boundary,* i.e., when 2yLs < YGB In this case the penetration of the grain boundary by the liquid occurs at a relatively rapid rate, resulting in the severe embrittlement of a polycrystalline solid. Grain boundary wetting is a common mode of intergranular attack in systems in which the lower melting component is relatively insoluble in the solid, but the solid has an appreciable solubility in the liquid, for example, the Ni-Bi system, Fig. 1. In systems of this type at temperatures above the range of stability of any intermetallic phases, once the liquid is saturated with respect to the solid so that no gross solution occurs, chemical gradients are small, and surface tensions become major driving forces for attack, provided the solid is stress-free. The results of Cheney et al. appear to be typical of those encountered when grain boundary wetting occurs.&apos; Capillary films were observed in the boundaries after quenching from the exposure temperature. The mean depth of penetration increased linearly with time, and the activation energy for the process was found to be 22 kcal per g-atom. In a study of the Cu-Bi system Yukawa and sinott4 found that the depth of penetration of bismuth into high-purity copper bicrystals of orientations from 22 to 63 deg of tilt about (100) at 649°C ranged from 0.05 to 0.25 in. after a 12-hr anneal. This corresponds to a linear rate of 6 to 15 X 10~6 cm per sec. At the same reduced temperature of 0.68 the rate for the Ni-Bi system&apos; was 7 x lo-&apos; cm per sec. In another study of the Cu-Bi system, Scheil and schess15 determined the kinetics of grain boundary wetting in hot-worked commercial rod. While there were several complicating factors present in this study, there is general agreement with the above results. The kinetics of penetration were linear, the activation energy was 20 kcal per g-atom, and at 650°C the rate of wetting was 2 to 5 x 10-6 cm per sec. The rate of wetting in the A1-Ga system6 is somewhat

Jan 1, 1969

By P. B. Mee

The secondary re crystallization behavior of two vacuum-melted, nominally 3 pct Si-Fe alloys has been studied, one alloy being produced from pure electrolytic iron and semiconductor-grade silicon and the other from commercial-purity hot band. The vacuum-melted and vacuum-remelted alloys were found to develop {110}(hhl) and {lll)(hkl), respectively, on annealing in high vacuum and {100}(0kl) and {11l}(hkl), respectively on annealing in pure hydrogen of dew point, < — 60°C. H2S doping of the hydrogen or annealing in commercial argon was found to effect a reversal for the vacuum-remelted alloy from (111) to (100) secondary recrys-tallization, while prolonged vacuum annealing at 2 x 10-6 Tow resulted in a tertiary re crystallization from (111} to (110). The growth selection of the {lll}(hkl) component was found to be governed predominantly by the {111}/planar misorientation, the maximum deviation of the resulting secondaries being 5 deg. It is considered that the driving force for {111}(hkl) secondary recrystallization arises from the preferential lowering of ?111, possibly by phosphorus or nitrogen diffusion, just as oxygen and sulfur under certain conditions have been found to preferentially lower ?100. When heavily cold-rolled metals are annealed at high temperatures, primary recrystallization usually occurs rapidly and may be followed by considerable grain growth. However, in the presence of a fine dispersion of inclusions1"3 or with a strong matrix preferred orientation4&apos;&apos; the matrix may be stabilized and a secondary recrystallization may then be effected. Also, in vacuum-melted Si-Fe it has been shown possible to develop {100}(001) and {110}(001)6 surface energy driven secondary recrystallization textures. Further, it has been found that, on annealing very pure metals, grain growth normally ceases when a grain size approximately twice the strip thickness is acquired, due to the formation of V-shaped thermal grooves which result in an equilibrium being set up between surface and grain boundary stresses. If, however, a surface energy difference ??s, exists between adjacent grains (of the order of a few percent of the grain boundary energy ?b), then according to Mullins8 a secondary recrystallization may be effected, since the grains having lowest ?s would grow at the expense of their higher-energy neighbors. For clean bee metal surfaces ?110 should be lowest; however, for 3 pct Fe-Si (100) secondary structures have frequently been developed and have been attributed by Walter and Dunn9 to an alteration of the relative surface energies due to the preferential chemisorption of oxygen on (100) planes. Kohler,10 however, indicated that this reversal may be achieved by employing minute quantities of highly polar compounds in the annealing atmosphere, i.e., sulfur compounds, in par- ticular H2S being beneficial in (100) growth. This work has been verified by Kramer" using {100)/{110} bicrystals, while Mager12 demonstrated the importance of sulfur diffusion within the strip. Detert13 has intimated that carbon may be responsible for the preferential lowering of ?110 although no direct evidence has appeared yet to support this supposition. It must , be appreciated that the above-mentioned examples of surface energy driven secondary recrystallization were obtained with very pure vacuum-melted materials with oxygen contents (which is now known to be a critical factor") less than 35 ppm. During the course of a textural study on Si-Fe it has been found that under certain conditions (111) secondary recrystallization can be obtained by what is believed to be a surface energy growth selection mechanism. The purpose of the present paper is to briefly describe this result and to try and postulate the possible causes. EXPERIMENTAL Two vacuum-induction-melted, nominally 3 pct Si-Fe alloys were produced, one from pure electrolytic iron and semiconductor-grade silicon designated A and the other from commercial-purity hot band, designated B.

Jan 1, 1969

By Wilson R. G

The Bulli and Wongawilli Seams, the two principal sources of coking coal for the Port KKembla steelworks of Australian Iron and Steel Pty. Ltd., vary in rank and in type over the Southern and -South Western Coalfields. The Bulli Seam, ranging widely in type, produces coke varying from weak to strong. The Wongawilli Seam, more consistent in type, produces coke of more consistent strength, but considerably less strong than that from the best Bulli Seam coal. Plans of seam variation show the regional trends in rank and type for each sear. The strongest coke is derived from coal containing between 45 and 55 per cent vitrinite, m.m.f. This is obtainable from the Bulli Sean in a zone embracing Bulli and Appin Colleries.

Jan 1, 1969

By G. J. Wilson

Difficulties experienced in correlating vertical and lateral locations of subsurface features that are encountered in directional wells prompted critical review of the tangential method of computing directional surveys. Inherent discrepancies were indicated to cause small incremental but significantly large cumulative errors in computed vertical depth and horizontal departure. A radius of curvature method, developed for planning and analyzing directional wells, was studied as a means of more accurately calculating survey data. Errors incurred in the tangential method were not present in the radius of curvature method. Conflicting assumptions in calculating dog-leg severity by the tangential method were resolved by a new procedure that was derived from the radius of curvature method. Results of the investigation showed the radius of curvature method to be an improved method for computing directional surveys. Introduction Many improvements in directional drilling tools and techniques have been made in the past 10 years,&apos; but the method of computing survey data has remained virtually unchanged. While use of computers greatly aids the process of calculation&apos; and eliminates many human errors, manual and computer calculations are still made with the assumption that the wellbore consists of straight-line segments. This paper points out discrepancies in the method and presents an improved method in which the wellbore is assumed to be curved. Tangential Method The method presently used to calculate vertical depth, horizontal departure and direction coordinates with measured values of well depth, inclination angle and direction angle is termed the tangential method. This term stems from performing calculations with a series of straight-line segments, with each segment assumed to be tangent to the wellbore at a corresponding survey point. A segment is defined by inclination and direction angles measured at only the lower or deeper end. Consequently, a discrepancy or error is introduced for each segment. Errors are not of extreme magnitude, but cumulatively are significant due to the need to define as accurately as possible the vertical and lateral location of subsurface features such as pay tops, fluid contacts and fault cuts encountered in expensive directional well bores. In Fig. 1, the curved-line segment ab represents a portion of the actual borehole as viewed in the vertical plane. Points a and b are survey stations and +, is the inclination angle at point b. The curved-line segment ab is assumed to be the straight-line segment arb of a length equal to ab and tangent at point b to the curved-line segment. Lengths a&apos;c&apos; and c&apos;b are equal to a&apos;b cos +, and a&apos;b sin +,, respectively. Point a already has been fixed by calcillations performed with survey data obtained at point a, and calculated lengths m&apos;c&apos; and c&apos;b are projected as lengths from point a, rather than from point a&apos;. Point b1 is thus fixed and assumed to represent the actual point b. Calculated length ac" is shorter than actual length ac, and calculated length c"bl is longer than actual length cb. Since b1 is the point from which the next deeper segment will be projected, errors are cumulative. Cumulative error continues to increase as long as the inclination angle continues to increase. When the inclination angle decreases (Fig. 2), calculated length ac" is longer than actual length ac, and calculated length c"bl is shorter than actual length cb. These errors also are cumulative, but differences between calculated and actual lengths are opposite in mathematical sign to differences demonstrated in

Jan 1, 1969

By William E. Bonini

Gravitational field anomalies have been observed over many igneous intrusives of medium (4000 km2) to small (100 km2) size in outcrop area. These studies give good results because the residual anomalies can be separated from larger scale crustal anomalies and density contrasts usually are present. Although unique solutions are not possible, the analysis of the gravity anomalies can put limits upon the geologic interpretation of such bodies. Three examples in Montana, U. S. A. are discussed: (1) the Boulder Batholith, a late Cretaceous quartz monzonite series of intrusives of 4000 km2 outcrop area; (2) the Little Rocky Mountains, an up-domed area, in which an Eocene porphyry (130 km2) has intruded the Precambrian crystallines and lower Cambrian sediments; and (3) the Crazy Mountains, an Eocene diorite (100 km2), which has intruded the Paleozoic and Mesozoic sediments. In both the Boulder Batholith and the Little Rocky Mountains, intrusive rocks are less dense than the surrounding rocks and negative anomalies are found (40 and 28 mgal, resp.). In the Crazy Mountains, the intrusive is more dense than the surrounding sediments and a sharp positive residual anomaly of 42 mgal is observed. The analyses of the gravity anomalies predict that: (1) the thickness of the Boulder Batholith is on the order of 10 to 15 kms and is concave upward; (2) the Little Rocky Mountain syenite is not a simple laccolith, but is T-shaped and extends in depth to about 16 kms; (3) the Crazy Mountain diorite is not a simple small scale series of stocks, but a large connected body extending in depth 5 kms to the basement (although nothing can be said of it within the basement because there is little density contrast). The analyses of the anomalies place important limits on both the areal and depth extent of the intrusive bodies. Of all possible geophysical techniques, gravity studies offer the most promise in the determination of the shape in depth of intrusive bodies.

Jan 1, 1969

Laboratory induced polarization measurements were made on representative samples of concentrated sulphide ores from three environments in New South Wales Comparisons were made with the membrane polarization exhibited by an argillaceous sandstone. The sulphide samples showed a strong polarization effect, the magmtude of whIch depended directly on the conductivity of tlIe pore electrolyte.

Jan 1, 1969

By L. W. Holm

This study shows that in the presence of foam, gas and liquid flow separately through porous media representative of reservoir rock. These results were obtained by using tracer techniques to measure the flow of the gas and liquid comprising the foam. Foam does not flow through the porous medium as a body even when the liquid and gas are combined outside the system and injected as foam. Instead, the liquid and gas forming the foam separate as the foam films break and then re-form in the porous system. Liquid moves through the porous medium via the film network of the bubbles and gas moves progressively through the system by breaking and re-forming bubbles throughout the length of the flow path. The flow rates of the gas and liquid are a function of the number and strength of the films in the porous medium. There is no free flow of gas; i.e., no continuous gas phase. On the basis of these results, foam can be expected to improve a water flood or gas drive by decreasing the permeability of the reseruoir rock to a displacing liquid or gas. This improves the mobility ratio and thus the conformance of the flood. INTRODUCTION Foam is formed when gas and a solution of a surface active agent are injected into a porous medium either simultaneously or intermittently. During the past few years, several papers have been published on the subject of foam flow in Dorous media. Foam has been used successfully in the removal of capillary water blocks from producing formations.&apos;&apos;2 The use of foam in gas storage reservoirs to reduce gas leaks and to increase storage capacity has been considered in recent years. Foam has also been investigated as an oil displacing agent,3-5 and as an agent to improve the mobility ratio in a waterflood.6-10 However, the mechanism by which the gas and liquid phases comprising the foam flow through a porous medium has nor been described adequately. Normally, when two immiscible phases (gas and liquid) flow concurrently through a porous medium, each phase follows separate paths or channels. At given saturations of the two phases, a certain number of channels are available to each phase, and as saturations change, the number and configuration of the channels available for each phase also change. The effective permeability of each phase is a function of the saturation of that phase only, and the flow of each phase can be described by Darcy&apos;s law. When foam is present, the effective permeability of the porous medium to each phase is greatly reduced compaced with permeabilities measured in the absence of foam.6,11-13 Based upon the observed flow of surfactant solutions and gas in capillaries, it has been concluded that the gas and liquid may flow separately or they may flow combined as foam. At least four mechanisms have been postulated to explain how fluids flow with foam present: 1. A large portion of the gas is trapped in the porous medium and a small fraction flows as free gas, following Darcy&apos;s law.9 2. The foam structure moves as a body; the rate of gas flow is the same as the rate of liquid flow. 6,13 3. Gas flows as a discontinuous phase by breaking and re-forming films. Liquid flows as a free phase.12 4. A portion of the liquid and gas move as a foam body while excess surfactant solution moves as a free phase.14 It also has been suggested that different flow mechanisms exist for high quality (dry) foams made from dilute surfactant solutions and for foams made from more concentrated solutions. Studies conducted on the flow of foam through capillaries have shown that a plug-type flow occurs and that foam flows as a body.6,15 Fried also has described the flow of foam through porous media as

Jan 1, 1969

By Phillip J. Maddex

Transportation is a major part of yours in the industrial minerals industry. Whereas federal income taxes merely take 50 per cent of your firms profits, transportation cost may take 50 per cent of the gross realization - selling price plus transportation - on your product, f. o. b. customers plant.

Jan 1, 1969

By T. K. Perkins, W. W. Krech

Jan 1, 1969

By Raul A. Deju

This paper shows how one can relate the chemical reactions between water and a silicate bed to the equations of flow. First the reaction mechanism is studied both theoretically and experimentally. Once the reaction mechanism is established, the equations of flow are solved and a solution (under physically reasonable side conditions) is obtained. Experiments to substantiate the solution are also presented.

Jan 1, 1969

By P. R. Sahm, T. V. Pruss, D. A. Gandolfo

Cb 3 Sn powders were hot-pressed to estahlish densi-fication conditions and assess the possible use of such compacts in multiphase structures with ceramic or magnetic inclusions. Superconducting transition temperatures, Tc, were measured as a function of powder particle size, pressing temperature, and second-phase admixtures. The highest transition temperatures were found in coarse powder (5 to 500 u) compacts and were only weakly depended on pressing temperatures up to 1200°C. Fine powders (below 5 p), however, both single-phase CbsSn and Cb3 Sn-composites, showed a stronger dependence on hot-pressing temperatures. While Al2 O3 phase admixtures did not affect T, much more, a Pronounced T, degradation was observed upon the addition of ferrimagnetic Fe2 Mno. 5 Zno.5 O4 powders. Likewise, critical current densities, Jc, at 4.2° K were lowered appreciably in the ferrite doped samples, whereas the neutral A1203 inclusiow gave slightly improved Jc values. MULTIPHASE structures in electronically active materials have recently gained in interest as pointed out by Galasso in a review article.&apos; In superconductors the most widely reported group are eutectic alloys which have been mostly investigated with respect to the proximity effect.2"4 In addition, "artificial eu-tectics", for example in the form of mercury-vycor glass sponge5 or fine niobium wires imbedded in a copper matrix,= have been prepared to attain higher critical fields and critical current densities. The idea was to enhance flux pinning phenomena by second-phase inclusions or ho1es. 7 Flux pinning should also be possible by the introduction of insulator inclusions into a superconducting matrix. Ceramic-metal combinations are most easily produced by hot pressing (= pressure sintering), as it permits an almost unlimited selection of material combinations. Cb 3 Sn has been prepared by vapor phase growths or in the form of thin films. Large compacts must be sintered,1° however, and normally present difficulties. At temperatures below 1350°C insufficient densities are obtained and at higher temperatures the loss of tin due to dissociation upsets the stoichiometry. Hot pressing is a natural approach to circumvent the problems, since one can obtain satisfactory densities despite low sintering temperatures. This work was mostly concerned with establishing conditions to hot press Cb3 Sn and Cb3 Sn multiphase structures (= composites), because no data are presently available, and to evaluate these with respect to their transition temperatures. However, a few measurements on critical current densities were also carried out, in particular to assess the value of ferrimagnetic inclusions. I) EXPERIMENTAL PROCEDURE The experimental procedure involved the preparation of feed material and powders, hot pressing, and evaluation of the resulting ingots. As no attempts were made to synthesize Cb3Sn from the elements during hot pressing, feed material had to be produced. For this purpose, a stoichiometric Cb-Sn powder mixture was compacted into a 3-cm-diam ingot (80,000 psi) and then inserted into a quartz tube and evacuated. Rf heating was employed. Above the tin melting point (230°C) liquid tin was forced out of the ingot, but was pulled back by capillary action after approximately 0.5 hr of continuous pumping at 700°C. Thus, it appears that evacuation at this temperature caused desorption of impurity gas creating wetting surfaces which, later on, favored alloying at relatively low temperatures. After a presintering period of 17 hr at 800°C, the quartz tube was tipped off and sealed into another such larger-diameter tube which, in turn, was connected to a pump system. This configuration permitted a temperature treatment at 1400°C, carried out for 65 hr, without collapsing of the glass walls or unfavorable chemical interaction of Cb3Sn with the quartz. The resulting material was

Jan 1, 1969

By James Paone

The Bureau of Mines conducted laboratory drillability studies on nine rock types using two mining-type percussive drills. Percussive-bit action was simulated by dropping a known weight on a rock sample to obtain a coefficient of rock strength for each rock drilled. While no single physical property of a rock is completely satisfactory as a predictor of penetration rate, coefficient of rock strength showed a better correlation with penetration rate than did other physical properties. Results also indicate that over the range of energies investigated, energy per unit volume in a given rock is independent of blow energy. A drillability index for the percussive system is proposed that utilizes the coefficient of rock strength test to determine energy per unit volume for a given rock which, along with the work rate of a given drill and the bit diameter, is used to predict the penetration rate as shown in the following equation: [R = 4P pD2 E, where R = penetration rate, in/min, P = work rate, in lb/min, D = bit diameter, in, and Ev = energy required to produce a given volume of rock, in lb/in3.] Laboratory tests indicate this method&apos;s potential as a simple and reasonably accurate method of predicting penetration rates with any percussive drill and bit combination.

Jan 1, 1969

By A. R. Krause, C. Laird

In order to establish whether or not there is a real temperature effect in fatigue (independent of environment) , poly crystalline copper and Cu- 7.9 A1 alloy have been cycled at 298° and 7° K in vacuo and the fatigue lives compared with those in air and in liquid nitrogen. The lives of both copper and the alloy were found to be highly temperature-dependent in the absence of environment. This result casts serious doubt on the validity of the cell structure hypothesis for stage I crack propagation as presently formulated, because it predicts that there should be no such tempevnture dependence. On the other hand, the plastic blunling process is consistent with the result. Effects of environment aside, the homogenization of slip which accompanies testing at low temperature, and at low strains, seems to be the main cause for increased fatigue life. At high strain amplitudes, the fatigue lives of wavy slip materials, typically copper, are independent of temperature.&apos; It is well-known, however, that low-strain lives greatly as as the temperature of testing is decreased. By contrast, the lives of planar slip materials, such as Cu-7.9 pct A1 alloy, increase to an even greater extent with decreasing temperature throughout both the high and low strain ranges.1&apos;2&apos;5 The mechanism of this temperature effect is associated with the earliest stages of fatigue failure,&apos;" crack nucleation, and stage I growth,"&apos; which is slow propagation along slip bands to the depth of a few grain diameters. Such life behavior has been interpreted on at least two different bases. On the one hand, those interested in the temperature effect at high strain amplitudes1 believe that stage I growth occurs by the plastic blunting process of crack propagation.7&apos;9 They explain the effect in planar slip materials by the homogenization of slip* which accompanies fatigue testing at low temper- atures and serves both to delay crack nucleation and to decrease the rate of stage I propagation. On the other hand, Holt and Backofen,2 who have studied the effect in low strain fatigue, believe that stage I growth can be interpreted by a cell structure hypothesis.10-12 They have challenged2 the conclusion that there is a real temperature effect in this regime of fatigue testing and have interpreted the increased fatigue lives almost entirely in terms of the "environmental-protective&apos;&apos; effect of the liquid nitrogen and helium baths used to obtain low temperatures. This interpretation by Holt and Backofen2 may offer a means of discriminating between these two mechanisms as currently formulated and used to explain stage I growth. On the basis of the plastic blunting process applied to stage I crack propagation,7* the low strain fatigue lives of both wavy and planar slip materials should be increased with decreasing temperature. This follows because both materials show increased slip homogenization in this strain regime."13 Consequently, crack nucleation in intensified bands will be delayed and the linking of such small cracks into larger stage I cracks will be difficult. In addition, the blunting process required to lengthen a stage I crack from the order of 2 to 10 (where the strain concentration of the crack begins to overcome the slip homogenization property of the material) will also be retarded. These delays will give rise to longer lives in both kinds of material. In contrast to the blunting hypothesis, no temperature dependence has been predicted on the basis of the cell structure hypothesis, because it is well-known that materials cycled at low temperature show no differences in type of dislocation structure for a given strain amplitude.18"20 If the lives of wavy and planar slip materials do show a temperature dependence when the environment is eliminated as a variable, then it is questionable whether cell structures per se have a fundamental role in fatigue fracture. Accordingly, specimens of copper and Cu-7.9 wt pct A1 have been cycled at 298° and 77°K in vacuo and the fatigue lives compared with those in air and in liquid nitrogen, in order to establish whether or not there is a real temperature effect in low strain fatigue. Since it is difficult to measure the strains in specimens when cycled in vacuo, S-N curves have been used as the basis of comparison. In studying the influence of temperature on fatigue life in ordinary environment, Holt and Backofen2 used the superior basis of E-N curves. However, they also published S-N curves and thus established the relationship between E-N and S-N curves. This relationship is used to support the S-N comparison reported in the present investigation. EXPERIMENTAL Materials. The copper employed in this investigation was of 99.99 pct purity and the cu-7.9 pct A1 was prepared from metals of the same purity. The stock, of 3 in. initial diam, was reduced in size by rolling

Jan 1, 1969

By Hsun Hu, R. S. Cline

The annealing behavior and the mechanism of re-orientation during recrystallization of iodide titanium cold-rolled 94 pct have been studied in detail. Results indicate that recrystallization occurs by the nucleation and growth of new grains, as in other common metals. Recrystallization nuclei form by the coalescence of subgraim, and the change in texture as a result of recrystallization is largely due to selective growth among the nuclei formed. The annealing of titanium is characterized by a wide range of overlap of the various stages of the annealing process, which may be responsible for a range of activation energies observed, and for the apparently gradual change in the annealing texture as a function of time or temperature. The deformation and recrystallization characteristics of titanium and zirconium are very similar. In cold-rolled strip, the deformation texture consists of two symmetrically oriented components, each having the basal plane laterally tilted at about 30 deg from the rolling plane and the [1010] direction parallel to the rolling direction. Upon annealing for recrystallization, the change in texture can be described, for simplicity,* as rotations around [0001].2&apos;6&apos;8 According to McGeary and Lustman,&apos; recrystallization occurs in zirconium through normal growth of the subgrains, which they called "domains", without the nucleation of new grains; and the magnitude of rotation around the [0001] axis increases gradually during the progress of recrystallization. If these conclusions were true, the mechanism of recrystallization in zirconium would be basically different from that in most metals, since it is commonly known that recrystallization with reori-entation always involves the migration of high-angle boundaries. In an attempt to clarify the situation, the mechanism of reorientation during recrystallization in iodide titanium cold-rolled 94 pct was studied in detail. The structural and textural changes upon annealing at various temperatures were examined by optical and transmission-electron microscopy, X-ray pole figures, pole density distribution measurements, and micro-beam techniques. EXPERIMENTAL PROCEDURE Material and Specimen Preparation. An iodide titanium crystal bar was are-melted and solidified in a cold-hearth crucible under a purified argon atmosphere. The solidified ingot had dimensions of approximately 3 by 1/2 by 3 in. One face of the ingot was somewhat uneven, but was as clean and shiny as the remaining parts of the ingot. Large grains with a Widmanstatten internal structure were clearly shown on the shiny surfaces, indicating the occurrence of P — a transformation upon rapid cooling from the melt. Analysis of the are-melted ingot indicated C 0.033, N 0.010, H 0.013, 0 0.002 in weight percent, and traces of iron, copper, and silicon as detectable impurities. The ingot was cold-rolled -40 pct to 0.300 in. thick with a reduction of 0.005 in. per pass. The defects on the uneven side of the ingot were then removed by machining. This reduced the thickness to 0.285 in. The piece was then recrystallized by annealing at 800°C for 1 hr in a fused silica boat charged into a fused silica tube furnace under a vacuum of 10~5 mm Hg. To refine the grain size, the recrystallized metal was again cold-rolled 40 pct to 0.170 in., then annealed at 700°C for 1 hr. These treatments yielded a strip with a uniform equiaxed grain structure, having a penultimate average grain diameter of 0.04 mm and a hardness of approximately 90 Dph. Final rolling reduced the thickness from 0.170 to 0.010 in., corresponding to a reduction of 94 pct. The strip was rolled in both directions by reversing end for end between passes. Surface lubrication was provided by oil-soaked pads attached to both rolls. Specimens of 1 in. length (for X-ray examinations) and +in. length (for hardness and microstructure examinations) were cut from the rolled strip, and a width of & in. was cut from the edges of each specimen by a jeweler&apos;s saw. These specimens were then etched in a solution of 10 cu cm HN03, 5 cu cm HF, and 50 cu cm H,O to 0.008 in. thick to remove the surface metal, as well as the distorted metal at the saw cuts, prior to annealing or measurements. To minimize any surface reaction with the atmosphere, all specimens were kept in an evacuated desiccator. Isothermal Anneals. All annealing treatments were conducted in vacuum in a fused silica tube furnace as described earlier. The temperature of the furnace was controlled to within *2"C. The specimen was placed in a fused silica boat, then pushed into the hot zone of the furnace. It took about 5 to 6 min for the specimen to reach the furnace temperature. After the specimen was held at temperature for a desired length of time the boat was pulled to the cold zone of the furnace; the heating-up period was excluded from the isothermal annealing time. Thus, the uncertainty in annealing time is higher for very short anneals, but negligible for long anneals.

Jan 1, 1969

By J. Steininger

The Hallimond tube flotation of sphalerite and pyrite with sulfhydryl collectors has been found to be inhibited near neutral pH in the presence of copper salts. Alkalimetric titration studies of the reactions between collector and activator indicate that this effect is apparently related to the formation of basic copper collector complexes. The conditions of formation of these compounds and their stability are in good agreement with the depression observed in flotation experiments. The general procedure employed in the flotation of zinc sulfide minerals requires activation of the mineral surface by heavy metal ions, usually copper, which react more easily than zinc with the common short-chain ionic sulfhydryl collectors.&apos; Commercially, zinc flotation is carried out under alkaline conditions (pH 7 to 10.5), but small-scale experiments indicate that zinc sulfide minerals can also be activated and collected under acid conditions. Selectivity, however, becomes poor at low pH and undesirable materials such as pyrite, silicates and carbonates tend to report in the float. Several years ago, Wark and Sutherland~, measured the contact angles of air bubbles on copper-activated sphalerite immersed in various sulfhydryl collector solutions. When represented, as in Fig. 1, on pH-sodium cyanide diagrams, the results are characterized by &apos;islands&apos; of non-contact near neutral pH and

Jan 1, 1969

Jan 1, 1969

THE increased demand for titanium alloys with improved high-temperature creep strengths has stimulated interest in silicon as an alloying addition to titanium. Silicon is a potent solid-solution strength-ener and, if added in sufficient concentration and properly heat-treated, can also dispersion-strengthen titanium by eutectoid decomposition.&apos; However, better understanding of the nature and distribution of the resulting silicide dispersion in more highly alloyed titanium matrices is necessary for the development of useful titanium alloys which utilize the latter strengthening mechanism. This note describes the chemical and crystallographic characteristics of the silicide phase as it occurs in a typical high-temperature near-a titanium alloy matrix. Several Ti-6A1-3Sn-3Zr a11oys containing various amounts of silicon ranging from 0.1 to 1.0 pct were melted as 10- to 20-lb ingots and processed into 1/2-in.-diam bar stock. The microstructures of specimens annealed at various temperatures were conveniently summarized by the (Ti-6Al-3Sn-3Zr)-Si pseudobinary phase diagram illustrated in Fig. 1. Comparison with the Ti-Si equilibrium diagram indicates the substitutional solutes (Al-Sn-Zr) increase the eutectoid temperature and decrease the a terminal solubility. Annealing at temperatures sufficiently high to dissolve the silicon in a ß solid solution and cooling rapidly enough to preclude coarsening generally produced a uniform dispersion of fine silicide particles, whereas annealing at temperatures near but below the ß transus produced relatively coarse silicide particles. Annealing in the limited a, plus 3 region produced a duplex coarse and fine silicide array. Several a-annealed specimens were examined by X-ray diffraction to determine the crystallographic identity of the precipitate phase. Copper Ka X-ray diffraction patterns of bulk specimens which contained 0.5 and 0.8 pct Si were virtually identical to that of the silicon-free Ti-6Al-3Sn-3Zr base alloy except for a slight shift in some of the high-angle diffraction lines. Apparently the silicide volume fraction was too low to be detected in bulk specimens. X-

Jan 1, 1969

By S. J. Aparo

Phosphate mining and beneficiation in the State of Florida are presently being carried on by 12 different mining companies with a total of 21 mining and flotation plant locations. Their combined production of both washer rock and flotation concentrate was approximately 28,000,000 long tons in 1968. This accounted for 70-72% of the total U. S. production and close to 30% of the world&apos;s output of this mineral. From this extensive activity in the Florida phosphate field, one basic flow sheet for beneficiation of the ore has developed over the years as the most commonly employed. In fact, all of these plants with the exception of two beneficiate Florida pebble phosphate using a basic operation as illustrated in Figure I. The two plants which differ from this general approach are not using raw matrix as feed. In one instance, +14 mesh pebble is ground in a rod mill to release free silica which is subsequently removed in a cationic froth flotation circuit using an amine acetate blend and kerosene. This technique generally results in a 4-7 BPL unit upgrading of the feed pebble. The other exception to the standard flow sheet illustrated in Figure I is an operation which is beneficiating tailing piles. In this case, the material is first subjected to cationic froth flotation in order to upgrade the feed to a point comparable to normal matrix. Thereafter, after, the phosphate is floated in an anionic rougher circuit followed by cationic flotation of the silica in a cleaner circuit.

Jan 1, 1969

By Robert H. Holgers

Eveleth Taconite Co. was chartered on July 29, 1963, and is 85% owned by Ford Motor Co. and 15% by Oglebay Norton Co. The latter also serves as managing agent. The location of the company&apos;s facilities is depicted in Fig. 1. The Thunderbird mine is located midway between the cities of Eveleth and Virginia, Minn. (Fig. 2). The Fairlane plant and General Office are located approximately 10 miles south on the St. Louis River near the community of Forbes (Figs. 3 and 4). The crude ore and the finished pellets are transported by a common carrier railroad, the Duluth, Missabe & Iron Range Railway Co. The facilities are also serviced by the Duluth, Winnipeg & Pacific Railway Co. Pellets are hauled year around by the DM&IR to its docks 60 miles south in Duluth, Minn. Ford Motor Co. consumes its share of the high grade pellets at its Rouge plant in Dearborn, Mich., and Oglebay Norton Co. sells its share in the open market. HISTORY Following six months of preliminary engineering by the initial staff of Eveleth Taconite Co. and the Western Knapp Engineering Div. of Arthur G. McKee & Co., the project was approved by Eveleth&apos;s board of directors on Apr. 17, 1964. On May 1, 1964, contracts were awarded to McKee for the mine, coarse and fine crushing and concentrating facilities, and to Allis-Chalmer for the pelletizing facilities. The pre-production surface overburden stripping contract was awarded to Skubic Brothers Co., Virginia, Minn. Ground-breaking ceremonies were held at the Thunderbird mine on

Jan 1, 1969