By E. Klar, A. B. Michael

Differences in the electrical conductivities of copper powder sintered under reducing, selectively oxidizing, and neutral atmospheres are related to impurities in solution or as precipitated oxides. The precipitation of impurities as oxides during sintering in nitrogen is proposed for maximizing the conductivity of sintered copper. Conductivity equations for two-phase systems are summarized. Selected equations are applied to porous sintered copper and composite structures. A recent review of the influence of impurities on the electrical conductivity of copper by Gregory et al.1 emphasized that an impurity in solid solution has a much more pronounced effect on reducing the electrical conductivity than when present partly or wholly as a second phase. When impurities in solid solution can be precipitated as oxides, the copper is purified with respect to these elements and the conductivity is increased. Cast and wrought copper, therefore, frequently contain an intentional residual oxygen concentration to oxidize and precipitate impurities less noble than copper. Copper powders generally also contain impurities which can contribute to a reduction in the electrical conductivity of the sintered material. The most deleterious impurities commonly found in commercial copper powders which markedly decrease the electrical conductivity when in solid solution but which can be precipitated as oxides include iron, tin, antimony, arsenic, cobalt, and nickel. In addition to impurities, porosity in sintered copper also contributes to a reduction in the electrical conductivity. The work reported herein discusses the influence of impurities, sintering atmospheres, and porosity on the electrical conductivity of sintered copper. These are important factors for controlling the electrical conductivity of materials such as sintered copper electrical contacts. Several publications on the electrical conductivity of sintered copper and composite materials with random pores or obstacles have incorrectly considered the conductivity to be proportional to the volume fraction of conducting material. However, analyses and equations have been proposed, the earliest of which is perhaps Lord Raleigh's of 1892,' which more accurately describe the conductivity of two-phase systems. These equations which in many cases allow one to closely estimate the electrical conductivity of porous sintered materials and two-phase composites will be reviewed and related to the measured electrical conductivity of sintered copper, copper-graphite. and Ag-W composites. INFLUENCE OF IMPURITIES AND OXIDIZING, REDUCING, AND NEUTRAL ATMOSPHERES Zone-Melted and Leveled Copper. The electrical conductivities of an electrolytic copper and a lower-purity compacting grade of copper powder after consecutive treatments in reducing or selectively oxidizing atmospheres are compared in Fig. 1. The powder and drillings from the electrolytic copper ingot were melted and solidified in a graphite crucible under hydrogen. The vertical zone leveling technique of multiple passes in opposite directions was used to obtain a uniform distribution of impurities. The electrical conductivity was measured on machined specimens 3 by 0.10 in. diam of the zone-leveled material and after the same specimens were consecutively treated as follows: 1) heating in hydrogen at 1600°F for 3 hr; 2) heating in air in a sealed tube so that 0.04 pct 0 was introduced; heating was started at 1000°F for 1 hr and continued at 1800°F for 8 hr; the stepwise diffusion treatment was used to avoid loss of copper due to evaporation of copper oxide at higher temperatures; and 3) final heating in hydrogen at 1600°F for 3 hr. A L&N Kelvin Bridge, type 4306, and a test fixture with knife edges 2 in. apart were used to measure the room-temperature conductivity with an estimated accuracy of ±0.5 pct. In all cases the conductivity of the electrolytic copper was approximately 100 pct of IACS. The conductivity of the impure copper was 80 pct of IACS both in the cast state and after heating in hydrogen. However, after the heating in air, the conductivity of the impure material was 100 pct IACS. After again heating in hydrogen, the electrical conductivity decreased to 60 pct of IACS. This decrease is attributed both to the dissolution of impurities and observed intergranular cracks due to the phenomenon of hydrogen embrittle-ment in copper. These data show that the electrical conductivity of commercial copper as represented by a compacting type powder can be increased significantly by the precipitation of impurities as oxides through heat treatment in an oxidizing atmosphere. Sintered Copper Powder. A commercial compacting type of copper powder pressed to various densities was sintered either in nitrogen, dissociated ammonia, or dissociated ammonia followed by a selectively oxidizing atmosphere of air in sealed Vycor tubes so that 0.06 pct O was added to the material. The electrical conductivity was measured perpendicular to the pressing direction on as-sintered specimens of approximately 3 by 0.25 by 0.15 in. The fully dense material was obtained by zone melting and leveling

Jan 1, 1969

By E. J. Freeh, W. E. Horst, R. C. Kellner

A technique useful in the important area of process-model building is described. The procedure is illustrated in the development of a mathematical model to describe the unsteady-state process of batch ball-mill grinding. The influence of certain assumptions relative to model structure are quantitatively evaluated and reviewed.

Jan 1, 1969

By W. B. Morrison

Anderson, King, and Spreadborough present detailed evidence to show what ~aldwin~' has already pointed out, that, over a relatively small grain-size range (Ad"1/2 ^ 10 mm-'I2, d is average grain diameter), yield point data can fit a number of relationships. Part of the difficulty in obtaining data which reflect only the effect of change in grain size on yielding arises from the fact that in varying the grain size, even though great care is taken, other structural changes are almost certain to occur. In iron alloys, these changes may consist of variations in subgrain size, grain boundary ledge density, and degree of carbon and nitrogen segregation at grain boundaries, all of which are difficult to detect and which may affect yielding, primarily through their effect on dislocation generation. Because of the inherent inaccuracy associated with yield point measurements there is little point in using relatively complex equations to fit data, as was done by Anderson et mnl., rather than the simpler, widely used Hall-Petch equation. In compiling their table of data, it is surprising that they did not include results from certain low-carbon steels,31 in which, as illustrated in Fig. 2, the grain-size range is very much larger than in their Armco Iron. The very fine grains in these steels were obtained by a thermomechanical process. Examination by electron microscopy showed that the grains were separated by high-angle boundarie and contained only an occasional subboundary. The data from these steels obeyed the Hall-Petch equation, and it was shown quite conclusively that they did not fit a d-l or (1-lJ3 relationship. Obviously, a much wider range in grain size than used by Anderson et al. is desirable if we are to determine the true relation between lower yield stress and grain size.

Jan 1, 1969

By R. Stefanko

Rock bolting as a method of support continues to increase with applications in many other industries in addition to mining. Nevertheless, with nearly 55,000,000 roof bolts installed in coal mines alone last year, this remains as the single greatest use. While bolts have frequently supported ground where conventional timbering could not, there are relatively few design criteria; and trial-and-error procedures prevail. Furthermore, development of suitable instrumentation that is simple to install and readout, sensitive, durable, reliable, safe and economical in evaluating the effectiveness of a bolt over long periods of time lags behind. Therefore, the pull test continues to be the most popular method of evaluating the applicability of a certain type of roof bolt under specific installation conditions. At Penn State in the Department of Mining, research has been conducted for a number of years to measure bleedoff in carefully controlled laboratory experiments as well as in underground investigations.1,2,3,4 Unfortunately, most of the instrumentation developed has been primarily suitable only for research purposes, not possessing all of the aforementioned characteristics desirable for routine underground use. Other groups also have met with restricted success. Therefore, while relatively crude, the torque wrench continues to remain as the most widely used load measuring device. While both field and laboratory tests continue to be conducted, analytical analyses are attempted to discover the more important design parameters in order that more efficient anchorage might be devised.

Jan 1, 1969

By A. U. Seybolt, V. A. Phillips

Binary iron alloys containing 1 pct of Al, Cr, Mn, Mo, Si, Ti, or V, and 0.4 pct C, 1 pct Cr steels with and without 1.2 pct A1 or 2.0 pct Ti additions, were ion-nilrided at 550° to 600° in N-H mixtures. Nitriding increased the inicrohardne ss of all the binary alloys except those containing manganese or molybdenutn, and also hardened the heat-treated steels if aluminum or titanium urns present. Transmission electron microscopy revealed particle formation in all casts where hardening occurred. Electron diffraction gare positive identifications for ALN, CrN, and a, Si3N4 in the binary alloys, and AlN and CrN in the aluminum- cold chromium-bearing steels, respectil&apos;uly. Cubic VN with a, = 4.13A was tentatively identified. Particles, apparently of CrN, also formed in the base steel but did not increase the hardness very much. Chromium and vanadium formed nitride platelets on {001}° matrix planes, while titanium gave clusters <15A diam. Aluminum nitride precipitated at grain and subgrain boundaries, and within the grains. Silicon gave profuse precipitates of several Morphologies at grain boundaries and cubical particles within the grains. No effect of the alloy carbides on nitride precipitation was observed in the heat-treated steels. THE nitriding of steel has been a well-established commercial process for about 40 years, but in spite of this comparatively long period of use there have been few studies aimed at understanding the process. Most studies, like the early but very competent work of Jones and organ&apos; and nones.&apos; were concerned with establishing the pertinent engineering variables of steel composition, gas composition, temperature, and time. As far as the present authors are aware, there have been no studies of the composition, size, shape, or distribution of the nitrides formed in the nitriding of steel. Noren and Kindbom3 did, however, examine a few nitrided steels by surface replica electron microscopy, and were able to show the presence of car-bonitrides and AlN and TiN nitrides. pitsch4,5 and Hrivnak6 examined nitrided pure iron by transmission electron microscopy. Baird7 found manganese nitrides in Fe-1.6 pct Mn when nitrided at 650°C, using the same technique. In the present work, emphasis was placed on transmission electron microscopy because of its inherently better resolution, using principally binary alloys of iron containing 1 pct of alloying element. In addition, a few simple 0.4 pct C steel compositions were examined to investigate possible carbonitride formation. It was not anticipated that all of the added elements would form nitrides under the conditions used, but it was considered desirable to obtain direct experimental evidence on this point. It would be considerably easier to ascertain the presence of alloy nitrides by examining appropriate binary alloys in preference to relatively complex steels. The work reported here could have been done using orthodox ammonia-nitriding procedures, but an operating ion-nitriding equipment was available, and was therefore used for specimen preparation. EXPERIMENTAL DETAILS 1) Materials. Binary alloys were made up from vacuum-melted electrolytic iron with 1 wt pct additions of Cr, Ti, V, Al, Mn, Mo, and Si of about 99.9 pct purity. In addition, three steels were similarly made up—a basis steel with 1 wt pct Cr and 0.4 wt pct C and two steels with further additions of 1.2 wt pct A1 or 2.0 wt pct Ti, respectively. The materials were vacuum-melted and cast as 11-lb heats into tapered square molds of about 2 by 2 in. average cross section. The castings were forged and hot-rolled to 11/4 in. rounds. Discs of 4 in. thickness by about 1 in. diam were machined from the rods. Some of these discs were hot-forged and hot-rolled to about 0.020 in. thick, sand-blasted, and then cold-rolled to about 0.003 in. thick. At this point, the surface was cleaned by light etching with HC1, then washed, dried, and vapor-degreased prior to nitriding. 2) Ion-Nitriding Procedure. The type of ion-nitriding equipment used here is similar to that described by Jones and Martin.8 Briefly, a mixture of nitrogen and hydrogen at 5 mm total pressure is placed in a vacuum chamber with a dc potential of 450 to 500 v applied between the work (cathode) and the grounded metal vacuum enclosure (anode). Nitrogen ions are accelerated to the work where a thin layer of Fe4N forms on the surface and thus sets up a nitrogen concentration gradient. This causes nitrogen atoms to diffuse into the surface layers of the alloy forming a finely divided dispersion of alloy nitrides, causing hardening of the surface. In the work to be reported here. the nitriding was carried out at 550° to 600°C to be consistent with commercial nitriding practice. The temperatures cited are those measured by a thermocouple located under a platform on which the work was sitting. Except where otherwise stated, the mixture used in nitriding the binary alloys contained -2.0 pct N, balance hydrogen. The nitrogen concentration in the nitriding gas mixture used for the binary alloys was purposely kept lower than normally used in nitriding steels. 10 to 20 pct, in order to minimize Fe4N formation. In this way only the alloy nitrides would be present as a second phase. However, in the case of steels which would contain a- carbide phase along with as

Jan 1, 1969

By R. K. Adams

The availability of digital computers costing less than $15, 000 makes them economically attractive as versatile research and experiment tools. Several such installations at Oak Ridge National Laboratory have shown that improvements in research productivity and experimental control accuracy can result from the proper application of a small digital computer. However, careful attention must be paid to several potentially expensive problems in 1) interfacing the experiment to the computer and 2) programming the computer. Two specific applications of very small computers to metallurgical testing and research are described. One is a system for data acquisition and precise temperature control associated with a thermocouple testing program, and the other is a system for pulse calorimetry determination of the specific heat of metals over wide temperature ranges and in the neighborhood of metallurgical transformations. The data acquisition system which uses a PDP-8/S computer monitors signals from up to 264 low-level thermocouple signals at two scanning speeds: 10 readings per second for long-term drift data, and 500 readings per second for transient data. The pulse calorimetry system which uses a PDP-8 computer accepts up to 6 signals of 0- to 10-v range and because of a larger analysis program, uses a bulk memory (magnetic disc) in addition to core memory.

Jan 1, 1969

By L. Rahnenfuhrer

"Hoisting equipment is a vital part of the operation of most producing mines. Safety and continuation of operation necessitates ultrasonic preventive maintenance inspection on a regular basis.Ultrasonic inspection of hoist shafting, brake linkage and draw bars will contribute to a safe operation and can prevent costly unscheduled shut-down time. With little dismantling, ultrasonic testing techniques can be applied to. determine the conditions of shafting and linkage in hoisting equipment, mining equipment and other miscellaneous mining equipment."

Jan 1, 1969

By Lulie H. Crump

U.S. supply and demand data for petroleum and natural gas liquids, by States and regions, were tabulated for the years 1960 and 1965. Estimates arcs provided of State-by-State quantitative data for the petroleum and natural gas liquids industry that can be integrated into State, regional, and national energy balances by source, form, and consumer sectors, and used for determination of interstate and interregional energy flows. Tables 1-4 show the estimated total supply of petroleum available for consumption and the supply&apos;s distribution among the major consumer demand sectors (household and commercial, industrial, transportation, and electricity generation). To obtain summary figures for the major proportion of refined products by States, individual tables were compiled for the six major products (tables 5-16). To enable comparison of petroleum data with those for other energy forms, conventional volumetric data in barrels were converted to their British thermal unit (Btu) equivalents. Interregional shipments of crude petroleum and theoretical flow patterns for petroleum products are shown in figures 1-4.

Jan 1, 1969

By J. R. Sturgul

Two problems which are common to nearly every branch of applied physics, including geophysics, are the ‘Dirichlet Problem’ and the ‘Poisson Problem.’ A numerical method for their solution is derived and a problem of heat flow in a plate is solved using a high-speed digital computer. The solution to this problem is presented in a form which illustrates the versatility of computer output.

Jan 1, 1969

By J. Szekely, Robert J. Fisher

A formulation is Presented and solutions are given for the problem of transient heat conduction in a sphere that undergoes a spatially uniform radiative heat exchange with its environment. The solutions were obtained by the numerical integration of the appropriate Partial differential equation and are Presented in a graphical form by Plotting a dimensionless average temperature against the Fourier number with the radiation number as a paranreter, for various initial sphere and environment temperatures. In addition to these numerical results asymptotic analytical solutions are also given. PROBLEMS involving the transient heating or cooling of droplets and particles frequently arise and are of importance in metallurgical operations. Spray refining, vacuum degassing, high-temperature gas-solid reaction systems, and pebble heaters are but few of the numerous examples that may be quoted. The practical interest in these problems from a design or operational point of view is to evaluate the change in the particle temperature with the time given its physical properties, initial temperature, and that of the environment. At the high temperatures encountered the principal mode of heat transfer between the particles and their environment is by thermal radiation; in case of vacuum degassing due to the very low thermal conductivity of the gas space the convec-tive components are negligible and radiation is the only heat transfer mechanism. Although much work has been done on transient heat conduction problems, the special class mentioned here, in which thermal radiation is specified at the bounding surface, received little attention to date. One contributory factor to this situation may be the nonlinearity of the radiation term in temperature, which in general precludes the use of analytical techniques and requires numerical or analog solution of the appropriate differential equations. In fact the only solutions of general nature that are available at present pertain to semi-infinite media and slabs.&apos;-3 The work on which the paper reports forms part of a program aimed at the theoretical and experimental study of transient radiative heat exchange between particles and their environment. The purpose of the present paper is to develop a formulation and solutions to the problem of transient heat conduction in a sphere that undergoes a spatially uniform radiative heat exchange with its surroundings. The solutions, obtained by the numerical integration of the appropriate differential equations, will be presented graphically, by plotting dimensionless parame- ters covering the range of variables relevant to metallurgical interests, thus affording a ready reference for design calculations. In addition to these results, approximate analytical solutions are also given which represent asymptotes, corresponding to extreme values of the variables mentioned. FORMULATION Consider a spherical particle of radius, a, initially at uniform temperature, Ti (T measured on the absolute scale), having a thermal conductivity, k, density, , specific heat, C, and thermal diffusivity, a. At time = 0 let this particle be exposed to an environment which is at a temperature T, and subsequently let there be a purely radiative heat exchange between the particle and the environment resulting in a spatially uniform heat flux at the surface. If in addition to the above we make the assumptions that the sphere is a gray body radiator, homogeneous, isotropic, and opaque, and that the physical properties are independent of temperature, conservation of heat in the sphere may be written as follows: The boundary condition contained in Eq. [3] states that the initial temperature of the sphere is considered uniform, equalling Ti, whereas Eq. [4] is readily obtained from symmetry considerations. Eq. [5] expresses the continuity of the heat flux at the surface of the sphere, or in other words the condition that the rate of heat exchange between the sur-

Jan 1, 1969

By Roy A. Koski

This paper describes variations in feed characteristics, preparation techniques, response to induration and product quality in pelletizing magnetite concentrates, earthy hematite ore fines, and specular hematite concentrates in grate kiln systems. The Cleveland-Cliffs Iron Company manages plants processing these various materials on the Marquette Iron Range in northern Michigan. The operations include the Humboldt Mining Company, Marquette Iron Mining Company, Empire Iron Mining Company and the Pioneer Pellet Plant. The combined output of the operations is approximately 9,000,000 long tons per year. The Humboldt Mining Company, owned by Ford Motor Company and Cliffs, produces pellets from a specular hematite concentrate. The Empire operation, which processes magnetite ore, is owned by Inland Steel Company, McLouth Steel Corporation, International Harvester and Cliffs. The Pioneer operation, which processes earthy hematite ores, is a joint venture of Republic Steel Corporation, McLouth Steel Corporation, Bethlehem Steel Corporation and Cliffs. The Marquette Iron Mining Company, owned by hones and Laughlin Steel Corporation, International Harvester, Wheeling-Pittsburgh Steel Corporation and Cliffs, produces pellets from specular hematite concentrate at the Republic Mine and Eagle Mills Pellet Plant. With the exception of the Eagle Mills plant, the operations employ the grate-kiln pelletizing system. Descriptions of the Empire, Pioneer and Republic operations, which have a combined capacity of 7,200,000 tons per year, are given in the paper.

Jan 1, 1969

By M. Gell, G. R. Leveran

The high- and low-cycle fatigue properties of the nickel-base superalloy, Mar-MBOO, in columnar-grained and single-crystal forms were determined at room temperature. It was found that the fatigue lives of these materials were greatly affected by the size of preexisting cracks in MC-type carbides contained in the micro structure. Most of the data falls on two curves given by: (zN)&apos;/A€= K, where Nf is the number of cycles to failure, Af is the total strain range, and K is a function of carbide size. No difference was observed in the fatigue behavior of the columnar-grained and single-crystal materials for the same MC carbide size. Matrix slip and crack initiation occurred at precracked MC carbides and, to a lesser extent, at micropores. Fatigue crack propagation was mainly in the Stage I mode, i.e., on cry stallo graPhic slip planes. The Stage I fracture in these materials was unusual in that distinct features were observed on the fracture surfaces. In high-cycle fatigue, these features resembled those commonly observed on the cleavage fracture surfaces of bcc and hcp materials. Yet, in this study, the cracks propagated slowly in a cyclic manner. In low-cycle fatigue, the Stage I facets contained equiaxed dimples, similar to those observed on the tensile fracture surfaces of ductile materials. These observations indicate that both local normal and shear stresses are involved in these Stage I fractures. A model is proposed to explain these results based on the weakening of the cohesive energy of the active slip planes by reversed shear deformation and the fracture of the bonds across the weakened planes by the local normal stress. RECENT developments in casting technology have produced cast nickel-base superalloys in columnar -grained and single-crystal forms.1&apos;2 The tensile and creep properties of the nickel-base superalloy, Mar-M200, cast in these forms have been shown to be superior to the corresponding properties of the conventionally cast polycrystalline material.lp2 This improvement in properties results, in part, from the elimination of grain boundaries in the single crystals and the alignment of the grain boundaries parallel to the stress axis in the columnar-grained castings. As part of a program to evaluate the fatigue properties of nickel-base superalloys cast in single-crystal and columnar-grained forms, a study has been made of the cyclic deformation and fracture of Mar-M2OO at room temperature. M. fiFl I .hininr Mpmher AIMF ic ^pninr Rocoarrh Accn^iata anH I) EXPERIMENTAL PROCEDURE The composition range of Mar-Ma00 in weight percent is: 8 to 10 Cr, 9 to 11 Co, 11.5 to 13.5 W, 0.75 to 1.25 Cb, 1.75 to 2.25 Ti, 4.75 to 5.25 Al, 0.01 to 0.02 B, 0.03 to 0.08 Zr, 0.07 to 0.12 C, bal. Ni. All of the castings met the above specifications. The castings were solutionized for 1 to 4 hr at 2250°F followed by aging at 1600°F for 32 hr which resulted in a 0.2 pct offset yield stress of 150,000 psi at room temperature. The microstructure of the material consisted of cuboidal, coherent particles of ordered, fcc Ni3(A1,Ti) (commonly designated y&apos;), approximately 0.3 p on edge, distributed in an fcc y solid-solution matrix. MC carbides together with shrinkage and gas micropores were also distributed throughout the materials. The MC carbides and micropores were located preferentially in the interdendritic interstices, as well as in the grain boundaries in the columnar-grained castings. The (100) direction of all the single crystals and the common (100) axis of the grains in the columnar materials were aligned within about 5 deg of the specimen axis. Fatigue testing was carried out in the high-cycle (HCF) and low-cycle (LCF) fatigue regions, with the major difference being gross yielding of the specimen occurred during the first cycle in the LCF region. This division also corresponded with the more usual one in which the life of a specimen in LCF is less than lo4 cycles and that in HCF is greater than lo4 cycles. The designs of the high-cycle fatigue and low-cycle fatigue specimens are shown in Figs. l(a) and (c), respectively. The gage sections of both HCF and LCF specimens were electropolished prior to testing. The HCF specimens were tested in an MTS, closed-loop, hydraulic fatigue machine at 10 cps in air. The specimens were cycled between a tensile stress of 5000 psi and a maximum tensile stress which ranged from 35,000 to 125,000 psi, Fig. l(b). The LCF specimens were cycled under strain control from zero to a maximum tensile strain, Fig. l(d), in a Wiedemann-Baldwin testing machine. The experimental procedure has been described elsewhere.3&apos;4 Both HCF and LCF tests were interrupted periodically in order to replicate the development of slip and cracking at the specimen surface. This was accomplished by placing plastic replicating tape around the gage section of the specimen while the specimen was in the mahine. The size of the MC carbides for all specimens was measured on a polished longitudinal section through the gage section after fatigue testing. The method of measurement consisted of carefully scanning the entire polished section in order to locate the largest MC carbides. Photographs were then taken of the six longest carbides oriented approximately normal to the

Jan 1, 1969

By J. Brett, S. Friedman

A study of the diffusion of nickel into both fibrous and recrystallized 0.065-in.-diam silica-alumina doped tungsten wire at 1200°C has been conducted. The diffusion profiles were determined by chemical dissolulion of successive circumferential layers and spectro-photometric determination of nickel in the etchant. It was shown that the diffusion of nickel into tungsten is markedly structure-sensitive. No significant amount of nickel could be introduced at 1200°C into tungsten which had first been recrystallized at temperatures of 2300°C, leading to an upper limit estimate for the bulk diffusivity of nickel in tungsten of 10-11 sq cm per sec at 1200°C. However, nickel did diffuse into initially fibrous wires, caused re crystallization, and was alsays present at the advancing recrystallization front. The accumulation of nickel in an initially fibrous region ceases when the recrystallization front arrives. The characteristics of the resulting diffusion profiles are explained in terms of the relation between diffusion processes and micro structural changes. WHILE it is well-known that the presence of nickel and certain other metals causes low-temperature recrystallization of the cold-worked fibrous structure of doped tungsten,&apos;&apos;&apos; the character of the phenomenon is not well understood. Recently it was shown that the recrystallization reaction can be induced at low temperatures by the presence of solid nickel on the surface of doped wire, but not by exposure to nickel vapors.3 Once recrystallization was initiated, a continued source of nickel was required for propagation of the recrystallization front. The phenomenon appeared to be a complicated solid-state reaction since, in addition to the change in structure of the tungsten from fibrous to equiaxed grains, diffusion of nickel from the surface into the recrystallized and fibrous structures was occurring with possible chemical reaction between nickel and tungsten at the surface and interaction of nickel with the dopants which ordinarily stabilize the fibrous structure within the wire. The objective of the present work was to study the diffusion of nickel into fibrous and recrystallized tungsten structures in order to clarify the relationship of the diffusion process to nickel-induced recrystallization. Studies of interdiffusion in the Ni-W system4"7 have been principally concerned with the mobility of tungsten in nickel. Information on diffusion of nickel in tungsten is meager, and there seem to be no studies of the mobility of nickel in tungsten which elucidate the structural aspects of the phenomenon. The present experiments were designed to determine the diffusivity of nickel at 1200°C in fibrous tungsten, in large-grained tungsten prerecrystallized at high tem- perature, and in tungsten recrystallized at 1200°C due to the presence of nickel. Although the concentration profiles were determined in these experiments, unexpected changes in boundary conditions or complex diffusion paths complicated the analysis of these profiles so that the interpretation could not be readily expressed in terms of simple diffusivities. EXPERIMENTAL PROCEDURE The experiments were conducted on Sylvania 0.065-in.-diam silica-alumina doped commercial tungsten wire, hereafter designated as ordinary doped wire. A special lot of 0.065-in.-diam silica-alumina doped low-nickel wire was also used. Impurity analyses of the wire are given in Table I. The experimental design is shown in Fig. 1. All heat treatments were conducted in vacuum. Two groups of ordinary doped wire were prepared for diffusion with nickel. One group in the as-received (fibrous) condition was elec-tropolished, nickel-plated, and annealed at 1200°C for 20 and 40 hr, or was exposed to nickel vapor at 1200°C for 20 and 40 hr. The second group was recrystallized to an equiaxed grain structure at 2300°C for 3 hr, electropolished, nickel-plated, or exposed to nickel vapor for anneals at 1200°C for 20 and 40 hr.

Jan 1, 1969

Parallel lenticular orebodies occurring at the C.S.A. mine of Cobar Mines Pty. Ltd. are mined by mechanized cut and fill stoping over the full strike length. Access is provided for each stope lift from an inclined drive adjacent to the orebody. Mobile drill jumbos mounting hydraulically-operated booms are used for drilling upholes which are subsequently charged with ANFO explosive.Close control of drilling has been found essential for good back conditions and to ensure optimum fragmentation.Broken ore is transported from the face to the main ore pass by rubber-tyred, diesel-powered, load-haul-dump units. Initially, the units trammed ore to the main pass via the incline drive. As the stopes advanced and the lead distances increased, stope passes were developed in the wall rock and raised concurrently with each stoping lift. The passes terminate in drawpoints and production loaders are used to transport ore from the drawpoints to the main ore pass system.Two parallel ore pass systems have been developed to cater for both copper and copper-zinc ores. These systems terminate above a 48 in. by 60 in. jaw crusher. The crushed ore is conveyed to a traversing rock box and thence to one of two crushed ore bins adjacent to the main hoisting shaft. A loading station conveyor is interlocked with the winder to provide automatic ore hoisting.All phases of ore handling have been mechanized as completely as possible. Results to date indicate this policy has been vindicated but highlight the need for tight operating control and close liaison between operating and maintenance personnel.

Jan 1, 1969

By William F. Lawrence

Research performed by the West Virginia University Coal Research Bureau under the sponsorship of the U. S. Bureau of Mines has demonstrated that coal-ash can be converted into mineral wool insulation of a quality equal to commercial grade mineral wool. An unexpected benefit has been gained due to the discovery that the usual and costly fluxing agents employed when using conventional raw materials are not required when producing mineral wool from coal-ash. Because coal-ash sources are commonly located close to mineral wool marketing areas and because mineral wool is seldom shipped far as a result of its low weight and high volume, the use of coal-ash may offer the mineral wool producing industry profitable opportunities. Moreover, coal-ash produced from experimental limestone based air pollution control processes also yields high quality mineral wool which may aid in retarding corrosion of metals contacted by the wool. In addition, internal fluxing effects and possible sulfur oxide utilization could provide economic advantages to the use of these "modified" ashes.

Jan 1, 1969

By H. P. Whaley

This paper introduces Wabush Mines, including its ownership, physical assets, capacity, goals and achievements. It is to be followed by four papers which will present the detailed story. Wabush Mines, the largest supplier of iron ore to the Canadian steel industry, was brought into production in 1965. The ore is mined and concentrated in Wabush, Labrador, Newfoundland and pelletized at Pte. Noire, Quebec. Annual capacity is over 6,000,000 tons of high-grade iron ore pellets.

Jan 1, 1969

By A. M. McKim, J. S. Ambler

"The iron ore of the Scully Mine is upgraded from 36 per cent Fe to 66 per cent Fe through single-stage crushing, wet autogenous milling, sizing by vibrating screens and two-stage spiral separation, followed by a process in which the concentrate is dried and then further improved by high-tension separators. The capacity of the concentrator is 17,000 long tons of concentrate per day. Discussion of the operation will recognize the special problems encountered in handling preponderantly fine ore, relate issues of interest regarding wear and review mechanical innovations found to be advantageous at Wabush. The modern trend toward big equipment, thoroughly instrumented, has been the theme of design. Effects on availability must be a consideration in this choice, and sectionalizing of circuits to minimize these consequences is as important as streamlined maintenance."

Jan 1, 1969

By Klaus Schwerdtfeger, Leo Zwell

The equilibrium between Ir-Fe or Rh-Fe alloys, iron oxide (wüstite or magnetite), and CO2-CO atmospheres has been determined at 1200°C. The data are used to derive the activities in these binary solid solutions. Both systems show negative deviations from Raoult&apos;s law. The lattice parameters are given for the investigated Ir-Fe and Rh-Fe alloys. IRIDIUM and iron form a continuous series of fcc solid solutions at elevated temperatures.&apos; Rhodium-rich Rh- Fe alloys have fcc structure.&apos; In the medium concentration range an ordered bcc phase is stable at temperatures up to about 1300°C. Phase relations in iron-rich alloys are not well-known. No thermody-namic data are available for these alloys. EXPERIMENTAL METHOD The experimental method used was to measure the equilibria between a gas phase of known CO2/C0 ratio, the alloy, and iron oxide (wüstite or magnetite). In one series of experiments the alloys of known composition were heated in CO 2-CO gas mixtures. After treatment (usually 1 day) the sample was quenched to room temperature and its surface examined visually to determine whether an oxide tarnish had formed. The procedure was repeated at slightly higher CO 2/CO ratios until the CO 2/CO ratio of incipient oxidation was found. Subsequently, the CO 2/C0 ratio was lowered again in small increments until the tarnish was reduced. In other experiments mixtures of alloy and iron oxide powders were pressed into pellets and equilibrated with the CO2-CO gas phase. In order to ensure that equilibrium was attained, two specimens with different starting iron content were heated side by side; in most cases, equilibrium was approached in one pellet by reduction of iron oxide and in the other pellet by oxidation of metallic iron. The sample was quenched to room temperature, and the composition of the equilibrated alloy was determined by X-ray measurements of lattice parameters and comparison of these values with calibration curves obtained from alloys of known composition. The oxides present in the specimens were identified by comparison of their diffraction patterns with those in the ASTM Card File. It may be expected from the noble character of iridium and rhodium that no appreciable amount of iridium or rhodium is dissolved in wiistite and magnetite under the present experimental conditions. The activity of iron in the alloy is then equal to that established in the iron oxide by the COrCO atmosphere. The activities of iron in wüstite and magnetite, as a function of oxygen pressure, were taken from the work of Darken and Gurry,

Jan 1, 1969

By John W. Wagner, Robert K. Willardson

Single crystals of Pbl-xSnXTe have been grown from The melt under liquid B2O3 using the Czochralski technique. The PbTe-SnTe crystals were grown from near-stoichiometric melts and from melts with slight deviations from sloichiometry. Crystal growth rates ranging from 1 mm per hr to 1 cm per hr were employed, the latter being generally used. Several investigations were performed to characterize the single crystals grown In this study. The phase diagram of the PbTe-SnTe system was examined. X-ray analyses verified the single-crystal character of the crystals, and powder pattern lattice parameter determinations showed that Vegard&apos;s law was followed within the limits of the experimental error. The as-grown crystals were p-type with apparent carrier concentrations of -8 x 1018 to -8 x 1020 carriers per cu cm. Hall coefficients, resistivities, and carrier mobilities were determined as a function of composition. Dislocations were revealed by an electrolytic etch, and the crystals were found typically to contain 2 to 4 x 105 dislocations per sq cm. Microhardness measurements were performed; no maximum in the Vickers hardness us composition curve was seen. Mass spectrometry was used for impurity analyses, and the crystals were found to contain 1 to 2 x 1017 total p-type impurities per cubic centimeter. Distribution coefficients were calculated for the major impurities which were Na, Mg, Al, Si, Cl, and Zn. RECENTLY interest has been stimulated in the preparation and characterization of many alloys of the binary compound semiconductors. This interest is due primarily to the almost unlimited possibilities of adjusting the semiconducting characteristics of these materials by varying the alloy compositions. One alloy system which has been receiving extensive investigation is the PbTe-SnTe system, since these alloys show promise of being useful as emitters and detectors of electromagnetic radiation in the spectral range of 8 to 14 µ. This paper reports on the growth of PbTe-SnTe single crystals by the Czochralski technique and investigations of the general properties of these crystals. The phase diagram of the PbTe-SnTe system was investigated so that specific alloy compositions could be attained. I) CRYSTAL GROWTH The PbTe-SnTe single crystals were pulled from the melt using the Czochralski technique. Generally, the crystals were grown from near-stoichiometric melts, although special growth runs were made from both lead-rich and tellurium-rich melts. Growth of single crystals from up to 5 pct lead-rich melts presented no problems; however, melts with tellurium in excess of -1 pct caused volatilization problems which generally made crystal growth impossible. All melts were prepared from high-purity materials as follows: 1) lead— 6 N— Cominco (Cominco Products, Inc., Spokane, Wash.); 2) tin—5N—Cominco; and 3) tellurium— 5N+— American Smelting & Refining Co., Plainfield, N.J. No further purification of materials was undertaken in this study. The elements were reacted at -1000°C in a vacuum-sealed silica tube for a few hours, a gentle rocking action being used to ensure thorough reaction. The cast ingots were then transferred to a silica crucible for crystal growth. A schematic diagram of the growth apparatus is shown in Fig. 1. The Vycor tube is sealed at both ends by O-ring flanges so that a vacuum or a positive pressure may be maintained in the growth chamber. The pull rod and crucible may be rotated; all crystals produced in this study were grown with the crucible sta-

Jan 1, 1969

By Hugh Boyd

Jet pulverization is a relatively new tool for fine grinding. It is not yet in general use in the mining and ore dressing fields, since most of the requirements in these areas have been for relatively coarse particle sizes. As the need for finer grinding increases - because of different ores, new products, and new values being sought - jet pulverization will, increasingly, be properly used.

Jan 1, 1969