By N. A. D. Parlee, E. M. Sacris

OXYGEN solubility in liquid silver has been well studied.1-6 It has been established that the solubility follows Sieverts' law reasonably well5'6 up to po2

Jan 1, 1968

By H. E. Powell, A. A. Cochran, R. E. Coleman

Infrared spectroscopy, employing the internal reflection method in conjunction with solvent extraction techniques, was used to study surface reactions between aqueous potassium ethyl xanthate and both sphalerite and precipitated zinc sulfide, each activated with aqueous copper sulfate. It was determined that reactions occurring on the sphalerite and zinc sulfide surfaces produce the reaction products ethyl dixanthogen and cuprous ethyl xanthate, some of which are adsorbed on the mineral surfaces. As the pH of the xanthate solution increased from 5.6 to 11.0, the amount of cuprous ethyl xanthate on powdered sphalerite surfaces decreased and the amount of ethyl dixanthogen first increased and then decreased. It is generally accepted that the collector potassium ethyl xanthate will not float the mineral sphalerite (ZnS). However, Gaudin1 showed that sphalerite readily floats if activated with certain metal cations before exposure to the xanthate. Copper sulfate (CuSO4) was found to be the best activator for sphalerite. The over-all flotation reagent reaction, as given by Gaudin,3 is as follows: While this is the over-all reaction, the exact mechanism of the reaction and the intermediate compounds that may be formed are not yet known with certainty. Important work has been done in Russia by Plaksin

Jan 1, 1968

By M. S. Seltzer

High temperature steady-state creep rates have been determined jor lead sulfide single crystals whose defect concentrations were fixed by equilibration under controlled sulfur pressure. The activation energy of creep, Qc , for undoped lead sulfide, is a function 01 composilion, decreasing from 2.9 to 2.2 ev as the carrier concentration increases from 9 x 1016 to 8 1018 electrons cm-3 for lead excess crystals, and increasing from 1.7 to 2.3 ev as the concentration of holes increases from 4 x 1017 to 1 x 1018 cm-3 in sulfur excess material. For five different composilions, Qc for undoped and bismuth-doped crystals has been found to be equal to Qpb + Qs, the self-diffusion activation energies for lead and sulfur in PbS. It is well-established1 that high-temperature steady-state creep of pure metals is a diffusion-controlled process, where the activation energy of creep is equal, within experimental error, to the activation energy of self-diffusion. The relationship between the activation energy for steady-state creep and those for self-diffusion in binary compounds is more complicated, however, because two different diffusing species must be considered, and becayse the activation energies may be influenced by compositional variations and by foreign atom additions.2-4 In some cases experimentally determined creep activation energies are correlated with those for self-diffusion of the slower-moving species, but such agreement is by no means universal. Interpretation of experimental results is difficult because few investigations include measurements of creep rates and self-diffusion coefficients of both diffusing species on single crystals of similar composition and foreign atom concentration. The objective of this investigation, therefore, is to determine the influence of stoichiometric defects and foreign atoms on steady-state creep and self-diffusion for a well-characterized binary compound. Lead sulfide, a compound semiconductor which crystallizes in the NaC1-type structure, and whose homogeneity range includes compositions on either side of the 1:l atom ratio, was chosen for study in this investigation. The pressure-temperature-composition relations for PbS are available,5,3 and deviations from stoichiometry may be monitored by electrical measurements.7 Single-crystal specimens are available to allow observation of effects due to bulk phenomena without interference from grain-boundary effects. These crystals have been employed to determine steady-state creep rates under compressive stress for "pure" and bismuth-doped PbS as a function of sulfur pressure and temperature as well as crystal orientation and applied stress in order to establish the relationships between defect concentrations and creep rates. EXPERIMENTAL PROCEDURES Crystal Growth. Lead sulfide crystals, prepared by the Bridgman method, are grown in evacuated quartz crucibles, filled with almost equal atomic proportions of high-purity (99.999 pct) lead and sulfur, and heated to a temperature above the melting point of PbS (about 1127°C) so that the lead and sulfur react to form molten PbS. The crucible and melt are dropped through the hot zone of the crystal-growing furnace at the rate of 1 cm per hr. The maximum melting point of PbS is slightly on the lead-rich side of the 50:50 composition; hence crystals grown from a near stoichiometric melt are usually n-type semiconductors containing excess lead atoms. Typically the lead excess concentration in solid solution with the PbS is 3 x 1018 atoms cm-3. Crystals containing either 1/20 or 1/2 mole pct Bi2S3 were prepared by addition of the foreign atoms prior to crystal synthesis. Preparation of Specimens of Controlled Stoichiom-etry. Since it is difficult to grow crystals of desired composition, the process of crystal growth and control of stoichiometry are separated into two distinct operations. Equilibration of as-grown PbS to a desired composition is most easily accomplished by first annealing the n-type crystals under high sulfur pressure (about 1 atm) at temperatures above 700°C. This process serves to put excess lead precipitates into solution, yielding 0 -type crystals upon quenching to room temperature. Inter diffusion occurs readily in crystals so treated, and the methods described by Bloem may then be employed to obtain crystals of controlled stoi-chiometry. For the creep measurements made in this study, this involves heating crystals in mixtures of H2 and H2S The equilibrium constant for H2S is given by: Thus the sulfur partial pressure is obtained from knowledge of the H2/H2S ratio and Kh2S for the temperature in question. Fig. 1 shows the p-T-x diagram for PbS. It can be seen that, within the stability limits for single-phase lead sulfide, desired compositions may be obtained by equilibrating under a specified sulfur pressure and temperature. Characterization of Crystals. The principal methods for evaluating PbS crystals include measurement of electrical properties and mass-spectrographic analysis. The measured electrical parameters include Hall coefficient, conductivity type, and electrical resistivity Bloem7 has shown that there is a 1:l relation between the defect concentration and carrier concentration obtained. Hence, if the contribution to the carrier con-

Jan 1, 1968

By M. C. Flemings, F. R. Mollard

Two-phase Pb-Sn alloys, ranging in compositiotz from 12 to 26 at. pct Pb, were unidirectionally solidified in a convection-fvee system, with thermal gradients in the liquid of up to 480°C per cm. Plane front solidification Loas achieved in all alloys at sufficiently steep gradient and slow growth rate. Conditions causing breakdown of the interface to a cellular or dendritic structure were roughly as predicted by a sinlple constitutional supercooling criterion. Structures of alloys of near-eutectic composition, solidified with plane front, exhibited a lamellar structure; the alloys furthest from the eutectic exhibited a rod-like morphology. Assumptions used in a previous paper for calculations of solute redistribution in two-phase plane front growth are shown to be reasonable for Pb-Sn alloys. Results of calculations are in good agveement with experiment. These show that variations in growth rate during solidification of the composite produce marked changes in average composition of the solid. IN a previous paper, Part I,' conditions necessary for plane front solidification of two-phase alloys were discussed and calculations given on solute redistribution in this type of solidification. This paper, Part 11, describes experiments on Pb-Sn alloys, designed to check the assumptions of the analyses presented, and to demonstrate their applicability to a given alloy system (Pb-Sn). APPARATUS AND PROCEDURE General. A vertical crystal growing unit was built for the study as described below, and "normal solidification" employed throughout (i.e., the ingot was completely melted except for a portion near the bottom end and then solidification initiated). The furnace was designed to permit achieving very low interface velocities, and steep gradients, in essential absence of convection; it is sketched in Figs. 1 and 2. Simple heat flow considerations indicated choice of a small-diameter specimen (ingot) to achieve high thermal gradients; ingot size chosen was 0.3 cm in diam. The ingots were held inside silica tubes 0.06 cm wall thickness. The requirement for an essentially convection-free system was met by use of the vertical furnace with the heat source over the heat sink, as well as by use of the small diameter ingots. In addition, by selection of tin-rich Pb-Sn alloys, the diffusion boundary layer (lead-rich) was denser than the bulk liquid and would not cause convection. The only apparent driving force for convection in this system was the small transverse temperature gradient resulting from heat flow into the samples from the furnace. Such convection must have been small, however, since 1) no temperature fluctuations in the melt were noted in the recordings, which would have indicated turbulent convection, and 2) experimental results obtained and described below could not have been achieved in presence of significant convection. Ingot Preparation. Pb-Sn alloys ranging from 12 to 26 at. pct Pb were prepared from high-purity lead and tin (99.9999 pct pure metal). Each alloy was prepared by first melting the pure metals in the proper ratio in air, in a Pyrex container. The melt was then stirred thoroughly with a graphite rod and cast into a preheated graphite mold. Ingots were then prepared from these castings for use in the actual experiments; each ingot consisted of a rod of alloy, 15 cm long in a 25-cm-long transparent fused-silica tube, 0.3 cm ID and 0.06 cm wall thickness. One chromel-alumel thermocouple, made with 0.004-in.-diam wire and protected by a two-hole alumina tube, was inserted into each ingot. The 1.5 cm of the thermocouple nearest the bead were protruding from the alumina tube and were coated with a very thin layer of boron nitride paste which provided electrical insulation while allowing good heat conduction. The electrically welded junction size was about that of each wire and the cross section of the two wires represented about 0.3 pct of the sample cross section. Including the coating, the thermocouple cross section still represented less than 0.5 pct of the ingot cross

Jan 1, 1968

By S. S. Lau

The authors of the previous comment stated that Dorn and Rajnak33 and others34-40 concluded that "agreement with this function [(t'/tp) -f(Un/2Un) = T/Tc} may be used as a criterion for that (the Peierls) mechanism of deformation". In contrast, however, Dorn and Rajnak33 and others34-40 never made such a statement. In order to clarify the issues involved it is appropriate to recapitulate the conditions that must be satisfied in order to suggest that some deformation process might obey the Peierls mechanism: 1) Within permissible variations due to changes in the slope of the Peierls hill the T*/Tp - T/Tc relationship must be obeyed. Although some mechanisms, e.g.. solute atom stress field, recombination of dissociated partials in bcc metals, intersection of dissociated dislocations, and so forth, give about the same t* - T relationship, other mechanisms, such as cross slip, disruption of attractive junctions, climb, motion of jogged screw dislocations, and so forth, give distinctly different t*-T relationships. On this basis some distinction can be made of the various mechanisms. 2) An important feature of the Peierls mechanism concerns its physical origin based on the nucleation of pairs of kinks. The value of T* at 0°K increases with the density of dislocation (i.e. , cold work) for the intersection mechanism and it increases with the square root of the atomic fraction of solute atoms in the solute atom interaction mechanism. In contrast the value of t* at 0°k, for the Peierls mechanism which depends only on the line energy and the shape of the Peierls hills. is independent of cold working and the square root of the solute atom concentration. These differences have been employed by various investigators for elimination of a few other possible mechanisms. On the other hand it is not possible to eliminate all mechanisms, e.g., the recombination of dissociated dislocations in bcc metals, and so forth, on this basis alone. 3) Further discrimination between possible mechanisms is based on the activation volume. For the in-

Jan 1, 1968

The problems of using comparatively simple x-ray diffraction equipment for quantitative analysis are examined. Internal standard and direct calibration procedures based upon the measurement of integrated diffraction energy (diffractometer peak area) have been developed for the determination of quartz in Broken Hill dusts. By these methods an accuracy of ± 10 per cent of the true value can be obtained and this can be improved to ±2 1/2 per cent by statistical methods if necessary.Rapid analysis for the components quartz, muscovite, rhodonite, galena, fluorite, sphalerite, calcite, and garnet has been developed by adaptation of direct calibration procedures and use of maximum diffraction energies (diffractometer peak height). Until more is know!) about the pathological effects of multi-component dusts of the Broken Hill type it seems undesirable to fix theIr allowable concentrations in terms of the quartz content.

Jan 1, 1968

By J. Gurland, A. Gangulee

The cracking of silicon particles embedded in an aluminum matrix occurs progressively over the range of plastic deformation of the composite specimen. The fracture probability of the particles increases with increasing particle size and decreasing silicon contents. The crack orientation tends to be perpendiculay to the direction of the maximum tellsile strain. An example of a direct association between matrix slip and particle cracking is shorn. ALUMINUM-SILICON alloys of commercial compositions fail by ductile fracture in three stages:' I) initiation of cracks in the silicon particles, 2) growth of cracks into cavities, and 3) rupture of the aluminum matrix separating the cavities. The present work is concerned with the first stage: the initiation of cracks in the silicon particles. EXPERIMENTAL PROCEDURE Aluminum samples with 2.8, 6.1, 9.6, and 13.2 vol pet Si, respectively, were cast from commercial al- loys. Machined tensile specimens (2 in. gage length) were annealed in air at 1000°F for 100 hr, and then pulled at a strain rate of 0.025 per min. The grain size (average linear intercept) of the aluminum matrix was 0.24 and 1.6 mm in the 6.1 and 13.2 pet Si alloys, respectively. The particle size of silicon in alloys of one composition (6.1 pet Si) was varied by either modifying the castings with 0.15 pet Na or prolonging the annealing time. The average particle size was measured by linear and planar analysis, assuming spherical particles of uniform size. The particle sizes and compositions of all samples are tabulated in Fig. 8, together with the identifying symbols used in the graphs. The respective numbers of broken and unbroken silicon particles were determined from metallographically prepared longitudinal sections by counting a total of approximately 2000 particles per sample. EXPERIMENTAL RESULTS 1) Crack Initiation During Deformation as Function of Composition. Nominal stress-strain curves of four specimens of different compositions, but approximately equal particle sizes, are presented in Fig. 1. The fraction of broken particles, P (no. of broken particles/ total no. of particles), is shown in Fig. 2 as function of true stress and in Fig. 3 as function of nominal strain. The last point of each composition line in Fig. 2 rep-

Jan 1, 1968

By L. B. Pankratz

The Bureau of Mines conducted heat-content measurements above 298.15° K for dehydrated analcite (NaAISi2O6) to 1,000°K, kaliophilite (KA1Si04) to 1,800° K, and leucite (KAlSi206) to 1,800° K. Heat content and entropy increments were tabulated, and the heat content data, were given in equation form. A first order transition was noted for kaliophilite near 810° K with a heat absorption of 160 cal/mole. Leucite had a second order transition which became complete near 955° K. In this transition a crystal change occurred from tetragonal (low-temperature form) to cubic (high-temperature form).

Jan 1, 1968

By R. Gibala

Internal-friction measurements on hydrogen-charged iron over the temperature range 4° to 300°K are reported. Two relaxation peaks, the hydrogen Snoek peak at 48 °K and the hydrogen cold-work peak in the range 145" to 2200K, are observed at 80 kc per sec. The effects of hydrogen-charging, aging, and deformation on the internal-friction results are determined and are used to show evidence of partitioning of hydrogen between solid solution and dislocations. The hydrogen-dislocation binding energy is estimated from the behaviors of the relaxation tiwzes and relaxation strengths of the Snoek peak and the cold-work peak. Its value is approxi,mately 6400 cal per mole. MANY investigators have demonstrated the usefulness of internal-friction measurements in determining the manner in which interstitial impurities interact with dislocations in bcc metals. Part of this success has resulted from the existence in bcc interstitial alloys of two anelastic relaxation peaks—the Snoek peak' and the cold-work or Koster peak2 (designated hereafter by SP and CWP, respectively). The SP has its origin in the redistribution of interstitials in solid solution among sites made energetically nonequivalent by an applied stress. The rate at which the redistribution occurs, measured by the relaxation time for the process, is related in a simple way to the diffusion rate of the interstitial in the free solution. The relaxation strength is proportional to the concentration of interstitial in solid solution. The CWP appears to have its origin in the relaxation of an interstitial-dislocation complex for which the relaxation time at a given temperature is much longer than that for the SP. The relaxation strength depends strongly on the concentration of interstitial and the amount of deformation at relatively low concentrations and deformations.2-8 From the dependence of the relaxation strength on interstitial concentration, the SP and CWP may serve as measures of the concentrations of interstitials in free solution and bound at dislocations, respectively. Thus their behaviors have been used to investigate interstitial-dislocation interactions in Fe-C, Fe-N, and several refractory metal systems.'-' However, the Fe-H system has not been studied extensively,? even though disputes in recent years over the mechanism of hydrogen embrittlement in steels involve argument over the extent to which lattice hydrogen and hydrogen-dislocation interactions play an important role.?-'' Previous work on Fe-H indicates the internal-friction behavior to be qualitatively consistent with that for other systems. Apparently, both a SP and a CWP are observed in the temperature ranges 30" to 50°K and 100°to 140°K, respectively (at 1 cps). However, there is neither sufficient nor accurate enough information to identify convincingly these peaks with their supposed counterparts in other systems. Nor have there been any attempts to make quantitative use of these peaks to study hydrogen diffusion, aging, or interaction processes. In this paper, an attempt is made to obtain more complete information on internal friction of hydrogen in iron than presently available. Internal-friction measurements in the range 4° to 300°K on hydrogen-charged iron show that the two peaks discussed above are in fact the hydrogen SP and CWP. Several effects of hydrogen charging, aging, and deformation on these peaks are observed and are used to determine the partitioning of hydrogen between solid solution and dislocation sites in iron. EXPERIMENTAL Materials. The starting material for this investigation was a high-purity iron supplied by National Research Corp. as a 1-in.-diam rod. The following analysis was given (inwt pct): C, 0.004; N, 0.0003; 0, 0.007; P, 0.002; S, 0.005; Si, 0.006; Mn, 0.001; Cu, 0.002; Ni, 0.005; Cr, 0.001; Mo, 0.001. After an initial vacuum anneal (-5 XTorr) at 700°C, the rod was cold-

Jan 1, 1968

By Paul Gemmill

Production was first recorded from the Pioche district in 1864, and it has continued to show an inherent ability to take on new life after periods of depression in the metal markets. Production from replacement leadsilver- zinc sulfide ore bodies in limestones of Cambrian age now accounts for several times the gross value of silver production from rich fissures in Lower Cambrian Quartzite. Aggregate production of some 6 million tons represents a gross value over $100-million. Future output is expected mostly to be from limestone replacement deposits of which the most productive are "channels" of ore up to several hundred feet wide and several thousand feet long with thicknesses from a few feet up to 50 feet. Such channels are restricted to the lowermost limestone bed of the district, about 250 feet above the basement quartzite. The "blotter-like" characteristic of this highly productive Jimesto~e bed in absorbing mineralization is believed to be, at least in part, due to lithology, including free carbon in the bed, which has created a unique set of conditions for delicately balanced mineralizing solutions that rejected any tendency to replace siliceous wall rock and were properly constituted for replacement of Limestone. All recognizable orogenic history is considered to be related to the Basin and Range faulting that created the mountain ranges. The faults developed after mid-Tertiary time and after widespread extrusives that are themselves involved in the faulting. Flat faults, formerly believed to be part of regional thrust faulting, are now interpreted as gravity slide faulting that can be shown to be large in magnitude and not simply local landslides. Large slide faults generally have concealed the great magnitude of mountain-bordering faults. Mineralization that accounts for ore is later than the faulting. Most faults are pre-mineral since they influence the shape of ore bodies, and some clearly have been offset by fault fissures containing ore. Post-mineral movement probably has been an important component of some large, initially pre-mineral faults. A single period of mineralization was begun by the introduction of large quantities of ironmanganese carbonate, and, in places, carbonate manganese with minor values in sulfides. Closely following the carbonate invasion, massive sulfides were brought in, usually replacing part of the carbonate body though in some places the massive sulfides replaced limestone that was not previously mineralized. Manganese mineralization is not a "halo" but leaks of manganese to higher formations and to the surface are the most significant exploration guides. The Pioche district is expected to be long lived with technological developments in ore treatment being important to the exploitation of low-grade manganiferous ores, while aggressive exploration is expected to find important quantities of bedded lead-silver-zinc ores of the massive sulfide type.

Jan 1, 1968

By Kenneth Blower

This paper gives a detailed coverage of the ore flow through the primary crusher, cobbing plant and concentrator, including equipment sizes, recoveries, reagent consumptions and product descriptions. Special features, such as rubber chutes, rubber-lined mills, pebble-mill grinding, steam-hooded filters and process control instrumentation, are also discussed.

Jan 1, 1968

By John F. Elliott, John P. Hager

The standard free energies of formation of the lowest stable sulfides of chromium, molybdenum, and tungsten in equilibrium with the corresponding metal hazle been determined by reacting the sulfide and metal with H2(g)/H2S(g) mixtures. The reaction is A method for estimating the standard ~nolav entropies and standard entropies of formation at 298°K of the sul-fides of refractory metals is presented. The standard free energies of formation of the lowest sulfides of the metals in group VIa of the periodic table are probably best determined with the reaction* is known with greater accuracy than is that property for any other sulfur-bearing compound or solution which might serve as a reference phase to establish the chemical potential of sulfur for the essential re- However, there still remain significant problems to the use of Reaction [I] in studying these sulfides. First, the equilibrium gas ratios (Ph2S/PH2) are very small, and with the most stable sulfides in the series the ratios tend to be at the limit of the range for precise chemical analysis (10-4); and second, the reaction rate for the formation or reduction of these sulfides appears to be relatively slow. A primary reason for the latter problem is that the gas phase near the equilibrium concentration has very little capacity for transport of sulfur. It is to be noted that the thermo-dynamic properties obtained from the experimental results by Eq. [I] apply for 1 g-atom of sulfur in the metal-saturated compound even though the exact composition of the compound has not been determined. The work reported here is a study of the standard free energies of formation of the lowest sulfides of chromium, molybdenum, and tungsten, and of copper, by Reaction [I]. In planning the experimental program, it was decided that the technique that has been used previously3"' could be used with modification and that an improved analytical method was needed for determining H2S in the gas phase. THE EXPERIMENT The once-through flow of gas was selected in preference to recirculating the gas, a) because of the low sulfur capacity of the gas, b) because of the relatively slow rate of reaction and the danger of the

Jan 1, 1968

By T. J. Neil, C. B. Manula, O&apos

This paper describes a simulation model developed to analyze truck haulage problems as they are found in the open pit mining and construction industries. The model, using a computer, cycles trucks between their assigned loading and discharge points over a measured haulage route. Required parameters for model operation include the number and type of operating trucks and loading units, maximum truck acceleration and velocity, a realistic vehicular deceleration rate, and the ratio of ore to total material loaded at each origin. Equipment performance characteristics, system profile characteristics, and service time distributions are also included. Records are kept of all waiting times at the loading and discharge points and of any truck interference on the haulroads (moving queues), and a current journal of ore and waste production is maintained. In the pursuit of reduced truck haulage costs, management is confronted with three particular problems in truck and shovel mines. 1) What is the best assignment of trucks to shovels in the system? 2) If new equipment is needed, which new shovels and trucks will operate most effectively in the system? 3) Are any physical changes in the haulage layout warranted to increase productivity? For small open-pit mines the answers to these questions may be obvious. However, for larger operations complex problems are encountered with production and system configuration relationships usually being unknown. The mining simulator discussed here was developed to aid management in evaluating alternative pit-haulage schemes to reduce the risk involved in the selection and assignment of equipment in open-pit truck and shovel mining systems. There are two fundamental differences between this model and other truck haulage simulators: one is a difference of degree, the other a difference of kind. This model can simulate more complex systems than previous models by allowing transportation of material from multiple mine faces to multiple mine destinations and by being readily adaptable to a wide variety of mine layouts. The second difference that characterizes the model is the standard simulation of truck movements. This technique enables each vehicle to perform according to its mechanical capabilities and the physical profile of the haul road. Among the similarities between other truck haulage simulators and this model are the recognition of the probabilistic nature of certain service times in the system and the use of a digital computer to operate the model. The computer inherits the staggering computational and bookkeeping work loads and provides a means for compressing the time scale by allowing several days' operations to be simulated in a matter of minutes. DISTRIBUTION SYSTEM Basic aspects of the system analyzed here may be brought into focus by referring to Fig. 1, a schematic of the typical open pit truck-shovel operation programmed into the simulation model. A single stage materials handling scheme is employed to transport both ore and waste. Loaded trucks are directed to a crusher or stockpile if ore is being mined, while overburden is conveyed to a waste dump. Each shovel has a given number of assigned trucks and has two associated haulage routes, one for waste and one for ore. Up to 5 shovels and as many as 10 trucks per shovel (or a total of 50 trucks) can be operated in the model. Essentially the model, using a computer, cycles trucks between their assigned shovels and the proper discharge points over measured haulage routes. Required input parameters for model operation include the number of shifts to be simulated, operating time per shift, number and type of operating trucks and shovels, maximum truck acceleration and velocity, a realistic vehicular deceleration rate, and the ratio of ore to total material loaded at each shovel. Equipment performance characteristics, system profile characteristics, and service time distributions are

Jan 1, 1968

By A. Hansson, G. E. Tardiff

WHILE it is generally known that cold-worked low-and medium-carbon steels exhibit substantial increases in tensile rupture ductility with increased deformation velocity172 (up to the von Karman limit), the observations for annealed or normalized steel do not permit simple generalization. Various investigators, for example, have reported both small increases1,3 and small decreases4,5' in rupture ductility with increased rates of deformation of normalized low-carbon steel. The purpose of the present note is to report on the dependence observed for strain-aged steel since preliminary work here indicates that strain aging results in the development of a consistent type of behavior that is understandable in the light of current knowledge of the lower yield dynamics for steels which deform inhomogeneously.6 This realization throws additional light on the influences responsible for the behavior of normalized steel. The results presented here were obtained for a 0.21 pct C, 0.012 pct N sheet (0.012 in. thick) steel which was received in a temper-rolled condition (approximately 3 pct reduction in thickness after process annealing); the as-received material had a spherodized structure with a ferritic grain size of ASTM 8. The material was selected for testing after 6 months room temperature aging, at which time the static lower yield and ultimate tensile strength measured 79 and 82 kpsi, respectively. ASTM 2-in. reduced section, 1/2-in.-wide specimens were used in smooth bar tests and 3/4-in.-wide specimens containing two 60-deg opposed edge notches (root radii = 0.002 in.) were used in notched bar tests. To facilitate strain measurement, the smooth bars were blued with ink and marked at 0.1-in. intervals along the gage length; the notched

Jan 1, 1968

By F. E. Pawlek, J. K. Gerlach

The chloridizing roasting of ores is applied when metal sulfides and oxides are to be converted into soluble or volatile compounds. The chlorine required is either obtained from the admixed chlorides of sodium or calcium or added in the gaseous state. In the first part of the investigations the reaction rate of the chlorides of sodium or calcium with gas mixtures of SO,-0, or SO ,-O2 ,-SO , was measured. The rate for reactions with gas mixtures SO2-O2 is ThE chloridizing roasting of ores is applied when metal sulfides and oxides are to be converted into soluble or volatile compounds. At present the process is mainly applied to produce nonferrous metals which occur in pyrite cinders in small concentrations. Thereby the nonferrous metals are converted into water-soluble, acid-soluble, or volatile compounds whereas all the iron remains as insoluble oxide. The chlorine required is either obtained from the admixed chlorides of sodium or calcium or added in the gaseous state. The reactions occurring during the roasting process can be divided into two groups: solid-solid reaction and gas-solid reaction. The reactions between solids proceed by means of solid-state diffusion and are therefore of low velocity. The heterogeneous reactions between solids and gases of the roasting atmosphere5 are high-velocity processes and determine the velocity of the chloridizing roasting. These gas-solid reactions shall be the subject of the paper presented. In order to investigate the still little-known processes which occur during the chloridizing roasting 6-' the complex reaction is split into several partial steps. First the reactions of NaCl and CaCl, with gas mixtures of SO2 and 0, have been investigated at temperatures between 500" and 600°C by measuring the weight increase of the samples. The gas mixtures used in this series of experiments had first variable compositions, then the amount of SO 2 had been increased. Furthermore the influence of Fe 2 O3 admixtures upon these reactions, the behavior of pure Fe 2 O3 with the gaseous reactants, and the chlorination of the sulfides of lead, copper, nickel, and zinc have been investigated. FORMATION OF GASEOUS CHLORINE Pyrite cinders are never completely roasted and therefore contain still a small amount of sulfide sulfur. When heated again in air, this sulfur is converted into SO,. Accordingly the formation of chlorine can first be described by the reactions: dependent on the composition of the gas phase. If more than 1 pct SO 3 is added to the roasting gas, the reaction rate is determined only by the concentrations of the SO,. In the second part the reactions between chlorine and metal sulfides are discussed. The rate of formation of gaseous chlorine is higher by me order of magnitude than is the reaction rate between ZnS and chlorine. The reaction rate of NiS and PbS lies considerably below that of ZnS. The conversion rate of both pure Fe 2 O 3 and Fe 2 O 3 containing NaCl or CaCl2 when reacting with SO2-O2, mixtures with and without SO3 portions was measured at temperatures of 500", 550°, and 600°C. The weight increase of pressings was determined by means of a spiral balanceg and the reaction rate calculated therefrom according to Eqs. [ll to [31 and [5] to [7]. The prepared samples were suspended on a platinum filament in a vertically mounted tube of mullite (ID 4 cm, length 110 cm) which could be heated by a resistance tube furnace. The platinum filament was tied to the lower end of the spiral balance. A supremax glass tube (length 70 cm) was mounted gas-tight on top of the reaction tube. The unit was sealed up at its top by a ground-in stopper which was holding the spiral balance with the sample. The spiral balance therefore hung outside the high-temperature region of the furnace. Fig. 2 shows the experimental arrangement schematically. While lowering the sample into the reaction tube pure nitrogen was flowing through the reaction zone providing a protective atmosphere. After the sample had reached the reaction temperature within approximately 1 min, the protective gas was replaced by the sulfur dioxide-oxygen reaction mixture. It took about 30 sec until the mixture filled the tube homogeneously. A Ni/NiCr thermocouple placed in the center of the furnace where the sample hung during the measure-

Jan 1, 1968

By Clarence O. Babcock

Model pillars of limestone, marble, sandstone, and granite having length to diameter ratios of 3:1, 2:1, 1:1, and 0.5:1 were broken in axial compression to determine whether lateral end constraint affected the breaking strength. Steel rings bonded to the ends of the model pillars with epoxy provided, during the loading cycle, a lateral end constraint of about 17 to 30 percent of the average axial stress. The effect of this constraint was to increase the breaking strength of the rock as compared to cylindrical pillars without constraint. The percentage increase in breaking strength varied with rock type and increased as the length to diameter ratio decreased. The maximum increase in breaking strength was 35 percent for marble pillars having a length to diameter ratio of 0.5:1. A theory was developed which relates the expected constraint to the physical properties of the ring and rock.

Jan 1, 1968

By K. A. Jackson, J. D. Hunt

The discussion by Tammann and Botschwar of the transition from eutectie grouth to denrdritic plus eu-tectic growth is reviewed and applied to metallic eutectic systems. Using expevimental data on the geowth rate of the Pb-Sn eutectic, and an extrapolalion of dendritic growth rate in tin and Sn-Pb alloys , qlcantitatice prerlictiotls of the extent of the eutectic region in tin-vich Sn-Pb alloys are made. There are no experimenta1 measuvements available for detailed comparison with these predictions. EUTECTIC structures form over a small range of compositions. The theory of lamellar growth presented by Jackson and Hunt' indicates that it is in principle possible to have eutectic growth over almost the complete range of compositions between the two solidus lines. This does not occur in practice. Alloys far from the eutectic composition grow dendritically followed by a eutectic as shown in Fig. I. The transition from a eutectic to a dendritic plus eutectic interface cannot be predicted from constitutional undercooling arguments because constitutional undercooling always exists ahead of the eutectic interface.' Reasonable predictions can, however, be made using arguments originally put forward by Tammanl. and Botschwar.3 These and later workers'"*6 carried out extensive experimental investigations of the extent of the eutectic range in organic materials. They concluded that the structure formed, eutectic or dendrites plus eutectic, depended on which structure grew faster at the given undercooling. This is, of course, equivalent to the structure which grows with the smallest undercooling at a given growth rate. In this paper, we will discuss these ideas briefly and then apply them to predict quantitatively the range of eutectic growth in tin-rich Pb-Sn alloys. The temperature dependence of the growth rates of dendrites and eutectic for a typical metal alloy of eutectic composition is shown schematically in Fig. 2(a). The growth rate for the eutectic increases more rapidly with undercooling than those of the dendrites because of the short diffusion path maintained in the eutectic, see Fig. 1. For an alloy off the eutectic composition on the A-rich side, the growth rates shift as shown in Fig. 2(b). The liquidus temperature of the a phase increases, that of the 3 phase decreases, and the temperature of zero growth rate for the eutectic does not change. The curves, particularly the dendritic ones, change shape as well, but for our purposes the principal effects occur because of the change in liquidus temperatures.3-6 In an isothermal system, only a dendrites will grow above TE, Fig. 2(b). If the temperature is below TE, and both phases have nucleated, a dendrites will grow ahead of the eutectic at

Jan 1, 1968

By W. G. Brissenden

"ALTHOUGH I SHOULD FIRST REVIEW the state of the mining art as it is today, because of the shortness of time I will confine myself to a re-view of the more important advances in that art which have been made in the past two to three decades. Then, a look at the opportunities and the challenges which now present themselves will be more meaningfulFirst, some of the more impor-tant developments in underground mining:(1) The recognition that good ventilation, visibility and working conditions are essential preliminaries to efficient production has resulted in their incorporation as a matter of practice in modern mine planning. (2) The introduction of the car-bide bit and the re-introduction of the airleg drill, and the resulting sharp rise in productivity, were early postwar developments. (3) The recovery of the coarser fraction of mill tailings for use as mine backfill also is an important cost-reducing development of recent years -and this has led to cemented backfill, which, al-though more expensive, meets certain specific needs and has tremendous potential. (4) Great strides have been made in improving explosives' materials and explosives' accessories. Millisecond-delay electric blasting caps, which improve fragmentation and reduce the seismic effect of blasting, and the development and •application for underground use of explosives are but two among many such improvements. (5) Trackless mining methods, using quarry-type equipment in some instances and specially de-signed low-headroom trucks, loaders and carrier-mounted drills in others have been successfully applied. (6) Dual-purpose load-haul units are now in use loading and hauling from open stope drawpoints, and smaller versions of this type of unit are in use in cut-and-fill and other types of stopes."

Jan 1, 1968

By R. H. Landshof, Reynold Q. Shotts, James A. Redding

GENERAL INTRODUCTION by R. Q. Shotts The sizing of coal particles is one of the most important beneficiation operations performed from the time coal is broken at the face until it is delivered to the customer. Indeed, in many cases it may be virtually the only such operation performed in that interval, although it is most often accompanied by some comminution. Sizing, as the term implies, is a separation of the broken coal particles into arbitrary groups, each group containing particles within restricted mass, volume or size limits. Size itself is not a rigidly defined property, but is actually determined more by the operating principles of the sizing device than by unique properties of the particles themselves. Particle size cannot be uniquely defined independently of particle shape. Taggart l says, "In fact, it is not possible to state the size of a single irregular body by means of a single dimension; such possibility exists only for regular polyhedra and their limit, the sphere." In view of the scarcity of regular polyhedra among coal particles, even though most appear to approximate a cube, we actually define size in terms of a surface opening through which the particle barely will or will not pass, or of two openings, the smaller of which retains all particles of the group under study and the larger of which passes all of them. Alternatively, size is expressed in terms of rate of settling of particles in a fluid under closely controlled conditions. Historical Sketch2-Taken from Coal Preparation, 2nd Ed. "Sizing is the process of separating mixed particles into groups of particles all of the same size or into groups in which all particles range between certain definite maximum and minimum sizes. In coal preparation, sizing is generally accomplished by passing the coal over screens. Separation by differential settling in air or water currents has been adapted to the special field of separating very fine sizes, and these processes are in commercial use to a relatively small extent in the coal industry. Separation with screens is a very old industrial practice. Agricola described the use of screens for ore treatment in the middle ages. In the literature of the British coal industry references were made to the screening of coal as early as 1589, but the practice of extensive sizing for the market did not become general until the last half of the nineteenth century. "In America, the practice of sizing developed first in the Pennsylvania anthracite region, beginning with the use of rakes in the mine working places to recover coarse coal. The mining procedure left the fines in the mine.

Jan 1, 1968

By Edward K. E. ] [Williams

Conditioning is any treatment of an ore with or without reagents which affect its floatability. While it can start in crushing or grinding circuits and continue into the flotation circuit, conditioning will refer here only to reagent treatment in an agitated tank designed for the purpose. Such treatment is often unnecessary with sulphide ores and collectors or with amines,* but it has long been recognized as essential with fatty acid collectors in the flotation of non-sulphide minerals, The requirements can be extremely variable, depending upon ore alteration, the presence or absence of slimes, and 1 the minerals to be separated. The study described here was concerned with the recovery of oxidized molybdenum minerals from an ore containing the element in both sulphide and oxidized form. Flotation of the iron minerals with which the oxidized molybdenum was associated was the basis for the process. Recovery and optimum concentrate grade without desliming depended upon a twenty to thirty minute conditioning of the pulp with flotation reagents at forty to fifty percent solids and at high turbulence. The objective in the study was the determination of design and operating criteria for conditioners in order to permit scaling-up of the results without repeating the entire study on a larger scale.

Jan 1, 1968