By A. C. Losekamp, R. M. Fincel, J. B. Conway

HIGH-TEMPERATURE thermal-expansion data for tungsten, rhenium, molybdenum, Mo-50Re, and W-25Re were obtained recently by means of a paired

Jan 1, 1965

By J. W. Leonard

This expanded and more detailed supplement to earlier published work1 is offered as a means to demonstrate the high empirical correlation which exists between the readily measured coal bench scale test parameters of volatile matter (d & a.f.), Hard-grove grindability index (HGI), Koppers cone bulk density (BD) and pulverization level (% passing a 1/8-in. screen) to the less readily measured full scale coke stability index. Thus, Fig. 1, 2 and 3 represent the correlated test data contained in Tables I, II and III respectively. Ninety-six coals are correlated so that 97% of the resultant cokes fall within two points and 100% fall within three points of the actual tested coke stability indices. The main generalizations which can be drawn from the correlation of these coals are as follows: 1) The coke stability indices for higher bulk density coals (46.0 BD to 50.6 BD) appear to be largely influenced by differing combinations of factors for coals above and below a pivotal point of approximately 36% to 37% volatile matter. Below this pivotal volatile matter coke stability index appears to be influenced largely as a result of changes to the coal volatile matter and pulverization level. While above this pivotal volatile matter coke stability indices appear to be dependent on the coal hardness, as measured by the HGI, and to some extent upon coal volatile matter. Pulverization appears to have little influence on the coke stabilities of the harder coals (52 HGI to 58 HGI) of greater than 36% to 37% volatile matter. 2) The coke stability indices for lower bulk density coals (41 BD to 45.9 BD) appears to be largely influenced by changes to coal volatile matter and pulverization level for softer coals above approximately 58 HGI. 3) The main empirical observation to be drawn from these results is that for coals above approximately 36% to 37% volatile matter the quantities of hard and soft constituents as measured by the HGI are important when defining coal rank for correlation to the coke stability index.

Jan 1, 1965

By Nicholas J. Grant, A. W. Mullendore, Paul Predecki

The Duwez technique of splat cooling in which a molten droplet of metal is accelerated and made to impact on a cold, highly conducting substrate was investigated.- An apparatus for producing "splat" was constructed employing an explosive powder charge to accelerate the molten metal. Transport of the molten metal just prior to impact with the substrate was studied by means of high-speed photography. The molten particles are small spherical droplets from about 1 to 50 µ diameter. The average cooling rates for aluminum, silver, and a gold alloy splatted on nickel substrates at room temperature were determined experimentally and were found to vary from 18 to 5 x 10' C per sec. The heat-transfer coeficients for pure aluminum and pure silver splats cooled on nickel substrates at room temperature were found to be 2.7 to 6.8 and 13.6 to 54.2 cal per sec sq cm 'C (2 to 5 x 104 and 1 to 4 x 18 Btu per hr sq ft OF), respectively. Solidification rates in pure aluminum and silver splats were calculated. "SPLAT cooling" is a term describing a technique for extremely rapid freezing and cooling of molten metals and alloys to room temperature or below. The technique was developed by Duwez et al.' in 1960, and after refinement2 consisted in transferring a few tenths of a gram of molten metal to near sonic velocity to strike a suitably placed cold copper surface. Upon impact, the metal spread into a thin nonuniform film called a splat, about 10-4 cm thick. The splat particles produced in this manner were thin enough in some areas to be suitable for transmission electron microscopy, without further treatment, and, together with X-ray data, yielded a variety of structures which would be classified as follows: 1) supersaturated solid solutions (increase in solubility limit), 2) metastable crystalline stoichiometric and non-stoichiometric intermediate phases ( in Au-20.5 at. pct Si and in Au-14 at. pct Sb, respectively), 3) amorphous alloys, 4) retained high-temperature phases, 5) alloys having equilibrium phases present, but with unusual, markedly altered structures. The crystalline phases present in splats were usually extremely fine-grained and had low dislocation densities. Present interest in splat cooling centers around a study of the unusual structures produced by the technique, their contribution to alloy theory, and the possibility of the development of new or unusual properties. In addition, the technique is being examined for the production of bulk quantities of new high-strength alloys for low- and high-temperature use. Although a number of alloy systems have already been investigated by the technique, relatively little is known about the mechanism of splat formation and the physical conditions encountered by the metal during solidification and cooling. The purpose of this work was: 1) to determine the velocity, shape, and size of the molten metal droplets just prior to impact with the cold substrate; 2) to try to estimate or measure solidification rates, heat-transfer coefficients, and cooling rates in splats. EXPERIMENTAL TECHNIQUE Splatting Apparatus and Procedure. An apparatus similar to the type originated by Duwez et a1.,2 but employing an explosive charge to accelerate the molten metal, was used. A "Ramset" fastening tool (a gun normally used for driving studs into concrete, steel, and so forth) was mounted vertically above a resistance-heated graphite crucible as shown schematically in Fig. 1. A splat product was produced by melting a few tenths of a gram of metal at the position shown in Fig. 1, and then exploding a powder charge in the breach. The shock wave thus generated traveled down the barrel into the furnace, ejecting the molten metal through the 0.06-in.-diameter hole at the bottom of the crucible. The ejected metal was impacted on a high-conductivity metallic substrate where it formed a splat. High-Speed silhouette Photography. In order to investigate the size and shape of the ejected, molten metal just prior to impact with the cold substrate, high-speed silhouette photographs were taken, and are shown in Figs. 2 and 3. These photographs were obtained with the aid of an Edger-ton, Germeshausen, and Grier microflash unit and a submicrosecond flash drive equipped with a variable time delay. Two types of triggers were

Jan 1, 1965

By John E. Crawford

A year ago, if I had the pleasure of addressing you, I would have discussed ocean mineral resources from a promotional standpoint. I would have described exciting indications of mammoth tonnages of sea-floor industrial minerals. I would have attempted to fire your imaginations as to the potential of a nation having the technologic know-how to exploit its submerged boundaries. As a first step toward this capability, I would have solicited your support for a Bureau of Mines? program aimed at determining the industrial worth of marine minerals and devising techniques and hard- ware for their recovery. We still need your support, but recently we have ventured out of the realm of planning and into your Government's first program in marine mineral engineering. Today, I wish to describe what we have done within the framework of existing research problems and our possible goals. I will be brief so as to allow ample time for questions, and I can do this with confidence because our program is so new that I need not be chagrined at not having all the answers.

Jan 1, 1965

Recently discovered Carboniferous bentonites are variable in charadeI and thickness, but being altered aeolian, ash-fall tuffs, they are probably extensive. Most are the Ca-montmorillonite type without the natural swelling characteristics of the Wyoming deposits, but their situation, thickness, and response to beneficiation through cation exchange may give them some potential as sources of future economic deposits.INTRODUCTIONLoughnan and See (1959) gave an account of bentonites and fuller's earth deposits of New South Wales. The most likely potential industrial sources were those occurring in the uppermost formations of the Newcastle and Singleton Coal Measures (Permian) in the Hunter Valley and deposited during epochs not marked by strong contemporary vulcanicity.One feature of the record of known occurrences at that time was the absence of bentonites from the thick volcanic sequences of the Carboniferous, but since this paper appeared, many bentonite beds have been discovered by the writer in the Carboniferous facies formerly known as the "Kuttung Series".The purpose of this contribution is to report briefly on the occurrence, genesis, mineralogy, and economic potential of these deposits which augment possible sources of bentonite near major industrial centres on the eastern seaboard.The potential world demand for bentonite would increase markedly with the trend to pelletization in the steel industry, if its use in this field became more general. More detailed mineralogical studies will be presented in later publications.STRATIGRAPHIC DISTRIBUTIONBentonite occurs at irregular intervals throughout a thick sequence of dominantly continental, plant bearing strata...

Jan 1, 1965

By A. J. Boyer, T. R. Meadowcroft

An experimental determination has been made of the efject of surface diffusion on the vapor pressure obtained in a Kwudsen cell. The results show that a knife-edge orifice in a molybdenum lid may give erroneous results for the vapor pressure of silver. when a correction suggested by winterbottom and Hirth is made, the results become meaningful. Experimental work with cylindrical orifices in molyhdenz~m lids and knife-edge orifices in ceramic lids shows that good vapor-pressure results may he obtained when the orifice is designed so that ejfusion is the only significant source of weight loss. THE Knudsen effusion cell technique has been used by many investigators to study relative and absolute vapor pressures over metals and alloys at elevated temperatures. As a result of this interest, some theoretical studies have been made of geometric factors affecting effusion from the orifice of a Knudsen cell. A review of these studies has been made by Margrave.1 Recently, Winterbottom and Hirth2 have suggested that a physical effect, that of condensation, surface diffusion, and re-evaporation, may seriously affect Knudsen cell measurements, especially when a knife-edge orifice is used. Inasmuch as many of the present vapor-pressure data have been obtained using knife-edge orifices. it was felt that an experimental evaluation of the effect of surface diffusion on Knudsen cell measurements would be of value both in the design of the cell orifice and in establishing realistic estimates of the limits of error for existing data. The experimental program was in two sections. Firstly, measurements of the vapor pressure of silver were made in cells with cylindrical and conical orifices in which the surface-diffusion contribution to the weight loss should be negligible. These results were correlated with existing data to give a reliable measure of the real vapor pressure of silver. Secondly, measurements made using knife-edge orifices were corrected using the surface-diffusion theory of Winterbottom and Hirth2 and were then compared to the real values. The experimental arrangement is shown in Fig. 1. The balance was an Ainsworth RV-AU-1 automatic recording microbalance capable of measuring weight changes of ±0.02 mg on a total load of up to 100 g. The temperature was measured by an optical pyrometer signted on the bottom of the suspended crucible. The temperature readings were calibrated in a separate experiment in which pyrometer measurements were made while at the same time thermocouple readings were taken of the temperature at the inside top and bottom of the crucible. The range of reproducibility with this technique was ±4°C. A constant voltage source maintained a temperature of ±2°C at 1200°C over 10 hr. Silver of 99.99 pct purity was used in nonporous alumina crucibles. Lids of molybdenum, tantalum, or magnesia were cemented to the crucible using a sodium silicate cement. Table I shows the characteristics of the lids used. The vapor pressure is obtained using the basic Knudsen formula:

Jan 1, 1965

Hatches Creek has been inactive since 1961, but with better metal prices, interest in the field is reviving.The mixed gravity concentrates which were unsalable in 1951 have been experimentally separated into salable wolfram, scheelite, and bismuth-gold concentrates, and a flow sheet incorporating magneticseparation and flotation has been developed.

Jan 1, 1965

By F. A. Jerabek, H. L. Hartman

This study presents results of investigations in a small model of segregation in discharged fill slurry, the quantity of solids escaping in the drain liquid, and the relationship of solids to slurry concentration and discharge rate. Compressibilities of fine fill material, in dry and wet states and individual size fractions, are compared. Two terms are frequently used in describing the hydraulic placement of fill material underground: hydraulic stowing is mostly associated with the underground flushing of coarse-sized fill material, such as coal washery refuse; while hydraulic backfilling refers to placement of small-sized fill material, e.g., sand or classified mill tailings, mainly in metal mines. Characteristically, in backfilling, only a few hours may elapse between the time the material is hoisted as ore and redeposited as fill underground. Hydraulic filling was first used about 100 years ago to control subsidence in coal mines. It was subsequently adopted in many mining operations all over the world, but its basic concepts have never been adequately studied and analyzed. This is not surprising, when one considers the number of variables involved in the hydraulic backfilling operation. Recently, much work has been done on the problems of transportation of slurries in pipes. Comparatively less research work has been done concerning the physical properties of fill material (compressibility, cementation, permeability, etc.). Very little work has been done on the problems of fill placing, distribution, and segregation of fill material discharged in the mine void. It is the purpose of this paper to explore two of the basic, lesser known aspects of filling: segregation and compressibility in discharged fill slurry. Difficulties in observing the behavior of hydraulic fill slurry during the pouring operation underground, and insufficient knowledge to conduct any kind of meaningful theoretical analysis, suggest experimental model studies. The tests described in the following sections were conducted in the Rock Mechanics Laboratory of the Department of Mining at Penn State.

Jan 1, 1965

By R. B. Falk, F. E. Luborsky

Small iron particles in mercury pow by diffusion of iron atoms through the mercury. Iron particles, with diameters about 200Å, have been stopped from gvowing in size, even up to the boiling point of mercury, by the addition of a third metal. The metal additives were classified according to whether they produced 1) negligible inhibition, 2) some inhibition, or 3) marked inhibition of the growth rate. Metal additives which resulted in a marked inhibition of iron-particle growth form a stable monolayer on the iron particles. Only those metals which may form compounds with iron showed this pronounced effect. The one exception was manganese. Metal additives which resulted in no inhibition of growth, showed no evidence for adsorption and could not form compounds with iron. None of the added metals, even those which strongly inhibited particle gvowth and thus had adsorbed on the particle surface, actually formed any compounds with iron at room temperature at the concentrations required for complete inhibition of growth. ThE stabilization of the size and shape of metallic particles dispersed in liquid metals has important technological implications in "homogeneous" nuclear reactor systems and in elongated particle magnets and is directly related to the problem of corrosion by liquid metals. Growth in these par-ticulate systems may occur by diffusion of atoms from surfaces of high energy, corresponding to a small radius of curvature, to surfaces of low energy or large radius of curvature. Thus, small particles dissolve and large particles grow to increase the average diameter of the particles. reenwood' has analyzed this diffusional growth of a system of particles containing a distribution of sizes and has obtained reasonable agreement with data on the growth of uranium particles in liquid sodium and UPb3 particles in liquid lead. Greenwood concluded from his analysis that the chief factors promoting stability of dispersed particles growing by a diffusion mechanism are large mean radius, high density, and low molecular weight with low values of the solute diffusion coefficient, the solubility, and the interfacial tension. In the case of elongated particle magnets the system of interest is that of iron particles dis- persed in mercury. Previous work,2 concerned with "spherical" particles in mercury, has indicated a diffusional growth mechanism similar to that discussed by Greenwood. It has also been shown3'4 that the addition of certain metals to Fe-Hg dispersions results in the formation of a monatomic layer of adsorbed atoms on the iron particles. In this paper we will show that this adsorbed layer provides the decrease in the iron-atom flux through the mercury necessary for size stabilization. The general features of the stabilization of the iron particles in mercury through the formation of this "coating", with many different metals, will be described. EXPERIMENTAL RESULTS Iron particles in mercury were prepared by elec-trodeposition,2, 4 and measurements2, 4 of coercive force HCi) and saturation induction (Is) were used to follow changes in size and composition during thermal aging in the mercury in the presence of relatively small amounts of an added metal. In Fig. 1 is plotted the aging behavior of spherical particle samples in the presence of some of the added metals to be discussed. The iron particles have an initial average diameter of 180Å. Each sample was aged for 20 min at each temperature in succession in the presence of a twofold to threefold excess of added metal over that required to form a monolayer on the iron particles. These are the same samples used previously3 to study the adsorp-

Jan 1, 1965

The Red Lake greenstone belt is an irregular mass of lavas sedimentary rocks and intrusives which is approxiately 35 miles long 18 miles wide and 7 miles deep. Basaltic volcamcs are the oldest rocks w1thm the belt. They are believed to have been laid down on an ancient crust which is at least 3 billion (3 x 109) years old and was composed partly of sediments. The basaltic rocks are overlain by acid volcanics and sedimentary rocks which have been complexly folded and are preserved as a down-folded remnant of younger rocks within the older crust. The volcanics and sedimentary rocks of the greenstone belt have been cut by intrusives with a wide range of composition. The emplacement of the intrusives and the accompanying regional metamorph-ism which terminated the orogenic activity in this area are believed to have occurred approximately 2.4 billion years ago. The basalts and many of the basic and ultrabasic intrusives undoubtedly had their source in the sub-crust or mantle. At least some of the granitic intrusives are believed to have had

Jan 1, 1965

By R. Taggart, D. H. Polonis, W. C. Gallaugher

In the Ti-Cu system, the a' phase can be produced over a wide range of alloy composition witJwut the retention of measurable amounts of the ß or ? phases. This paper reports on the decomposition of this hexagonal martensite phase front the standpoint of solute corzcentratiorz, tempering temperature, and coherency strain condition. The mechanism of precipitation during tempering comprises localized precipitation which is followed by discontinuous precipitation if sufficient coherency strains are present. The localized precipitation process in hypoeutectoid alloys is described by the generalized Johnson-hiehl equation and an activation energy of 46,000 cal per mole. In hypereutectoid alloys the corresponcEing activation energy is 51,000 cal per mole. The rate-controlling process has been proposed as the difision of copper along a' platelet interfnces. SEVERAL investigations have been reported concerning the kinetics of decomposition of the mar-tensitic a' phase in titanium binary alloys.' In the Ti-Mo system,' two modes of a' decomposition have been observed in the presence of /3 phase; one of these involves the precipitation of fine a from a', and the other involves diffusion across the a'-ß interface. In studies of the Ti-Cr system, Rostoker2 did not detect the formation of TiCr2 during tempering. In Ti-Ni alloys,3 the intermediate phase Ti2Ni has been found to precipitate directly from a' along the interfaces between plates. With the exception of the study of Ti-Ni alloys the previous investigations of tempering phenomena in substitutional martensites are mainly qualitative and do not present a detailed description of the precipitation processes. The following limitations restrict the correlation of the microstruc-tural processes and reaction kinetics during tempering in most binary-alloy systems. 1) A mixture of at least two phases characterizes the constitution of quenched alloys. 2) Difficulties have been encountered in obtaining uniform structures throughout quenched samples. 3) The reaction products, and in particular their morphology. have not been clearly resolved. 4) The martensitic a' phase forms over only a limited composition range for most titanium-base binary alloys. Gomez and polonis4 showed that the Ti-Cu system provides an excellent basis for investigating the tempering of a' over a range of composition without the complication of retained P or the transition w phase. In the present work the effects of solute concentration, tempering temperature, and coherency strain conditions are considered with reference to the over-all precipitation process in quenched alloys of the Ti-Cu system. Both microstructural observations and kinetic data are correlated to define the rate-controlling processes which govern the observed localized and discontinuous precipitation reactions. An earlier paper5 was devoted to a discussion of the modes of heterogeneous nucleation of Ti2Cu from the martensitic a' structure. The present paper will therefore emphasize the progress of the tempering reaction beyond the initial stages. EXPERIMENTAL METHODS The Ti-Cu alloys for this study were prepared by conventional arc-melting procedures. Chemical analysis revealed that the alloy buttons contained approximately 0.02 wt pct 0, 0.04 wt pct N, and within 0.1 wt pct of the intended copper concentration. The progress of the tempering reaction was followed by means of electrical-resistance measurements utilizing a Kelvin double bridge, microhard-ness readings with a 400-g load, and X-ray dif-fractometry patterns to reveal line-broadening effects. Metallographic specimens examined at magnifications greater than X1000 were shadowed with germanium to reveal fine structural details. Direct carbon replicas were prepared for the electron-microscopy studies. EXPERIMENTAL RESULTS Property Changes. The changes of microhardness that accompany the precipitation of Ti2Cu from a' are shown in Figs. 1 and 2. As the solute concentration increases the peak hardness, for a given tempering temperature, increases. In alloys of given composition the time to reach the peak hardness agreed with the time to attain maximum X-ray diffraction peak breadth, as shown in Fig. 3. The maximum hardness and the maximum line breadth increased with lower tempering temperatures, and the time to reach the maximum also increased. The a' peaks broadened during the initial stages of tem-

Jan 1, 1965

By B. Ramaswami

INTERNAL oxidation occurs readily in silver due to the rapid diffusion of oxygen in silver.' It has a marked effect on creep in polycrystalline silver2 and raises the critical resolved shear stress in single crystals of silver.3 However, the effect of oxygen on the work-hardening parameters of silver is not known. It is the aim of this paper to describe the effect of internal oxidation on the work-hardening characteristics of single crystals of silver and an Ag-0.1 at. pct A1 alloy. The materials used were: 99.99 pct Ag from Handy and Harman and 99.993+ pct A1 from Alcoa. Single crystals, 6 mm by 6 mm in cross section of silver and Ag-0.1 at. pct A1 of mo.5 orientation, i.e., the orientation with the Schmidt factor m = 0.5. were grown by the Chalmers technique.4 One set of specimens, referred to herein as oxidized specimens, was annealed at 940°C for 24 hr in a muffle furnace, in air, and furnace-cooled to room temperature. Another set of specimens, referred to as nonoxidized specimens, was annealed in oxygen-free helium at 940°C for 24 hr and furnace-cooled over a period of 7 hr to room temperature. The annealed single crystals were tested at room temperature in a floor-model Instron testing machine. The results are presented in Figs. 1 and 2. A

Jan 1, 1965

By Albert W. Deurbrouck

This report describes the preparation characteristics of 23 coal samples collected from nine of the more significant coalbeds of Fayette County, W. Va. In 1963 almost 5.4 million tons of medium to high volatile B coals of excellent quality for metallurgical and steam markets were produced in Fayette County. Of the 23 coal samples collected 11 would require some upgrading to pro-vide metallurgical quality products, 11 were acceptable as received, and 1 was a noncaking coal. Cleaning these coals to metallurgical standards would require only the removal of the sink 1.58 specific gravity material which would be quite easy as very little near-separating-gravity material was present at this gravity.

Jan 1, 1965

Jan 1, 1965

By Gilbert L. Eggert

The effects of reactor irradiation on age hardening in a Cu-2 wt pct Be alloy have been investigated in two neutron-energy ranges. During some of the irradiations, specimens were exposed to high-energy fission neutrons which passed through a boron-10 shield; during other bombardments, the boron-10 was omitted and specimens were irradiated in a reactor thermal column, or the fuel configuration was modified to increase the thermal-neutron flux at a location in the core. Differences in length, X-ray diffraction angle, and hardness indicated that low-energy neutron irradiation made a small contribution to changes in the measured properties. The influence of defects generated by knock-om with less than the Brinkman critical energy or by prompt (n,y) recoil is suggested as the cause of this effect. EXPERIMENTS designed to test the effects of reactor irradiation on the properties of age-hardening alloys have to the present time employed fluxes un-differentiated according to neutron energy. Billing-ton and Siegell in 1950 were the first to perform such an experiment and to compare the results with those obtained by thermal aging. These authors concluded that precipitation in a Cu-2 wt pct Be alloy was not enhanced by the radiation. However, 4 years later, Murray and Taylor,2 working with specimens of the same Cu-2 wt pct Be alloy, reported that an increase in density, hardness, and resistivity which followed reactor irradiation resembled changes associated with thermal aging at about 100°C. (It should be noted that these authors reported that higher aging temperatures caused a decrease in resistivity.) cupp3 reported hardness results similar to those of Murray and Taylor. Koppenaal4 showed that irradiation-enhanced precipitation and irradiation defect hardening were not simply additive but that they acted separately in an irradiated alloy. Kernohan et a1.,5 working with Ni-Be, offered evidence that beryllium was removed from solid solution by reactor irradiation and suggested that the mechanism was one of increased diffusion through the use of vacancies in the structure. piercy6 also found that more precipitate particles were formed by fission-neutron irradiation of a Cu-Co alloy which contained a small amount of particles before irradiation. He proposed that the additional particles were caused by an appreciable amount of diffusion during the final cooling of displacement spikes. The retrogression of extant precipitate particles found by Murray and Taylor2 and Boltax7 as well as piercy6 indicated that nuclei were dissolved within a high-energy spike region and, upon resolidification of the perturbed volume, new nuclei precipitate and grow by enhanced diffusion. Bleiberg et al.' and Konobeevski et al.' explained phase changes obtained by irradiating fissionable alloys in terms of retrogression and re-precipitation in regions of high-energy spikes. Parsons and Balluffi10 used electron microscopy to verify that crystallization did indeed occur in displacement spikes which were formed in amorphous germanium by fast-neutron irradiation. The concept that low-energy neutron irradiation might cause structure-sensitive property changes in semiconductors by atomic recoil associated with the (n, y) reaction was first proposed by Schweinler" and walker." This thesis was tested by Cleland and crawford" and found to be valid. Coltman et al.14 exposed a variety of pure metals to thermal-neutron irradiation at cryogenic temperatures and attributed the resulting resistivity changes to the action of defects created by (n, y) recoil. The present work was undertaken to extend the concepts of Schweinler," walker," and Coltman et al.I4 to the case of an age-hardening alloy and to determine whether or not the action of defects produced by thermal-neutron irradiation would en-hance age hardening. EXPERIMENTAL PROCEDURE Omeea West Reactor Irradiations.* Thermal-

Jan 1, 1965

By E. M. Boatman, S. J. Pirson, R. L. Nettle

More than a decade ago some theoretically derived relationships were proposed that permitted the prediction of the relative ability of reservoir fluids (oil, gas, water) to flow simultaneously within the porous structure of rocks. While many successful predictions of fluid-flow ratios from wells have been made from electric logs, the theoretical deductions have not been subjected to laboratory verifications. For the relative permeability to liquid and gas, simultaneous flow of water and air was used, employing the familiar external-gas-drive technique. While in the process or water desaturation, the resistivities of the test cores (Woodbine sand) were measured. Their permeabilities varied from 10 to 280 md. The laboratory results indicated the need for changing the values of exponents in the theoretically derived formulas, whereas the form of the functions of resistivities and saturations remained as derived by theory. For the relative permeability to oil and water, the three-core dynamic technique was used on six cores. In this case it was found that the formulas were valid with but slight modification as derived by theory, to a sufficient degree of accuracy for engineering use and for well productivity prediction from electric logs. INTRODUCTION Conventional quantitative well log interpretation generally stops after reasonable values for formation porosities and water saturations have been established. Yet such in formation is insufficient to predict either the outcome or the desirability of well tests and completion, let alone the economic aspect of producing oil- and gas-bearing sections which might have been established by conventional log analysis. To give an engineering answer to such questions, it is necessary to predict the expected fluid flow ratios, the productivity index and the ultimate recovery from potentially productive wells. This problem requires in part for its solution a determination of the relative permeability characteristics of the potentially producing formations, both to oil (or water) and gas, and to oil and water.

Jan 1, 1965

By R. C. Buehl

A pyrometallurgical process for recovering manganese from open-hearth furnace slags or low-grade manganiferous iron ores is described. The slag or ore is smelted in a blast furnace to produce spiegeleisen; the speigeleisen is then blown with air in a basic converter to give an oxide slag. This slag product contains 60 to 75 percent manganous oxide and may be considered a synthetic manganese ore. In the smelting operations coke rates for five test periods ranged from 3,255 to 4,130 lb per ton of spiegeleisen. The recovery of manganese in the spiegeleisen varied from 60 to 76 percent. Recovery increased to 83 percent when the open-hearth slag feed to the blast furnace was diluted with a high-? grade iron ore sinter to facilitate smelting. In blowing the spiegeleisen a cyclic procedure was developed that gave nearly 90 percent recovery of manganese in the slag product (synthetic ore) yet prevented excessive contamination of the slag by phosphorus and iron. The overall recovery of manganese was about 75 percent when iron ore sinter was used with the open-hearth slag in the smelting step. The metal remaining after oxidizing the manganese from the spiegeleisen contained approximately 3.5 percent phosphorus. It was refined in a basic converter by blowing with air in the presence of lime" A high--grade iron and a basic phosphate slag were produced.

Jan 1, 1965

By W. E. Anable

The Bureau of Mines studied the purification of commercially available yttrium by melting it in a 100-kw electron-beam furnace. Button-scale melts were made to determine the ultimate purification that could be attained by melting yttrium at 1,733° to 1,770° C at low pressure (0.05 to 0.1 micron) for 1 to 120 minutes. In addition, numerous melts were made to study the effect of doping yttrium with carbon, 17 selected metallic additions, and 3 compounds. Except for nickel and zirconium, the metallic impurities in yttrium were lowered significantly on extended treatment; silicon was lowered only slightly. The nonmetallic impurities} oxygen, nitrogen, and carbon, were not lowered except on short exposures. In isolated instances, the oxygen content was lowered from 5,860 ppm to about 5,000 ppm. In most instances the carbon con-tent was lowered from 545 to about 220 ppm in 20 minutes and then increased again. It was concluded that yttrium cannot be purified by direct heating or by the doping technique employed.

Jan 1, 1965

By V. Koump, T. F. Perzak, R. G. Olsson

Jan 1, 1965

By Richard F. Hewlett

This report describes how a limited number of preliminary exploration drill-hole assays from a mineral deposit can be used to design grid spacing that is both economic and efficient for subsequent evaluation drilling of that deposit. Relationships between desired precision of the estimate of grade of ore and drilling cost are used to determine the economic drill-hole spacing. The statistical concept of precision in estimating grade of ore is used to determine the efficient drill-hole spacing. Assay data from approximately 50 known copper deposits were studied, and the relationships of the statistical parameters of these deposits were computed. Drilling requirements for various precisions of the estimates of grade of ore were computed for some of these known deposits to serve as guides for drilling future copper deposits. The effect of various geologic factors on the trend in grade of ore and, therefore, on the drilling requirements is shown for certain deposits.

Jan 1, 1965