By S. R. Goodman, Hsun Hu

A study has hem made of the formation of annealing textures in an 18-8 austenitic stainless steel (Type 304L) from various deformation textures obtained by rolling at different temperatures. When the deformation texture is a mixture of the ferritic type and the brass type owing to the pres -ence of both martensitic ferrite and retained aus-tenite in the specimen, recrystallization takes place by the growth of the existing austenite phase. In a previous report,' it was shown that the rolling texture of austenitic stainless steel (Type 304L) changed gradually from the brass type to the copper type with increasing temperature of deformation above 200°C. These changes are similar to those in high-purity silver2,3 and electrolytic copper;4 a brass-type texture is favored at low rolling temperatures, whereas a copper-type texture is favored During the course of rolling -texture transition from the brass type to the copper type, the subsequent recrystallization textures change accordingly. The orientation relationship between the annealing textures and the various rolling textures, being consistent with previous observations on various fcc metals, can be described as [Ill] rotations of approximately 25 to 40 deg. Carhide precipitation may influence the annealing textures. at high rolling temperatures. Furthermore, the annealing textures in high-purity silver5 and electrolytic copper4 were found to depend entirely on the prior deformation texture. From a copper-type rolling texture a strong cube texture will form upon recrystallization, whereas from a brass-type rolling texture the annealing texture will be quite different from the cube orientation. In an earlier comm~nication,6 the formation of a strong cube texture in 18-8 austenite stainless steels (Types 304 and 304L) was reported briefly by the authors. The present paper constitutes the results of a complete study of the annealing textures obtained from a

Jan 1, 1965

By R. D. Pehlke, P. D. Goodell, R. W. Dunlap

The rate of dissolution of steel bars in molten pig iron has been measured experimentally in the temperature range 2300° to 2650° F. The rate of solution is shown to be a .function of bath composition, temperature, and stirring. A kinetic model based on carbon diffusion in the liquid phase has been derived to fit the experimental results. THE rate of scrap melting has long been an important variable in steelmaking operations. With the advent of the oxygen steelmaking process and the accompanying shorter heat times, the rate of scrap melting has now become one of the rate-limiting factors in steel production. As observed in commercial practice, the solution rate is influenced by the compositions of liquid and solid, the temperature, agitation, and time. However, no definitive work has been done on the Fe-C system, and there is very little information in the literature regarding the relative effects of these variables in steelmaking systems. A number of questions have been raised in regard to scrap utilization in basic oxygen steelmaking operations. Consideration has been given to the optimum size and shape of scrap, and to the use of preheated scrap as a means for decreasing the pig-iron requirement in oxygen blowing. The determination of an optimum scrap practice for a specific installation depends to a large extent upon the economics of the scrap market and also upon the behavior of scrap in the vessel. The present research was undertaken as a preliminary study in evaluating the behavior of steel in a pig-iron bath under various conditions of temperature, composition, and agitation, as might be encountered in oxygen converter operations or in any steelmaking operation where scrap behavior is an important process variable. Related studies have been carried out on non-ferrous systems. The solution rate of solid aluminum in a molten A1-Si alloy has been studied.' Furthermore, the increasing use of liquid metals has created considerable interest in studies related to dissolution of a solid in a liquid, or mass transfer taking place between a solid interface and a liquid metallic phase.2-10 In an effort to clarify the relative importance of factors influencing the dissolution of scrap in Fe-C alloys, this paper presents the results of a study of the rate of dissolution of a low-carbon steel cylinder in a molten Fe-C bath at various bath compositions, temperatures, and conditions of agitation. An attempt has been made to determine the mechanism of solution, and a model has been derived to fit the experimental results. The rate of heat transfer between the molten pig-iron bath and the solid-steel cylinder has also been studied. EXPERIMENTAL PROCEDURE A molten bath of pig iron (nominal composition 4.2 pct C, 0.5 pct Mn, 0.8 pct Si)* was held in a 200- *In view of the fact that the composition of the pig-iron bath was slowly changing with time because of steel dissolution and reaction with the surrounding atmosphere, intermittent samples of the liquid bath were taken throughout each experiment, Table 1. lb induction melting unit. The internal diameter of the furnace was 8-1/2 in. and the bath depth approximately 14 in. Cold-finished 1020 steel cylinders of 1/2-, 3/4-, 1-, 1-1/2-, and 2-in. diameters were cut into 1 -ft lengths for use as test specimens. One end of each bar was machined to fit a hand-driven, mechanical stirring device which rested on top of the furnace. This fixture permitted 7 to 8 in. of the bar to be immersed in the melt. The steel cylinders were cleaned to free the surface of grease and oxide. The rods, at ambient temperature, were immersed into the molten pig-iron bath. The melt temperatures studied in this investigation were 2300°, 2500°, and 2650°F. Different agitation conditions were achieved by operating with a) the power to the furnace, giving induction stirring; b) induction stirring plus mechanical stirring, using hand rotation with a chain and sprocket assembly at approximately 200 rpm; c) mechanical stirring alone with the power off; and d) the power off and no mechanical stirring resulting in minimum agitation, i.e., only that caused by natural convection currents in the bath. The samples were immersed in the melt for prescribed times ranging from 30 sec up to 6 min. Immersion times were measured with a stopwatch and temperature control of the melt was achieved by power adjustment following temperature measurement with an optical pyrometer. The measurements with the calibrated pyrometer were checked out to within less than 10°F with simultaneous thermocouple measurements. Following immersion, the bars were water-quenched and the diameters were measured with a micrometer at several positions on the reduced area, and by volumetric displacement. The dissolution rates calculated from the

Jan 1, 1965

By W. R. Huff

Yield stress and plastic viscosity values, determined from shear rate-shear stress relationships, were found to be a linear function of coal concentration for coal-water slurries containing 40, 45, 50, and 55 weight-percent of powdered coal. In the laminar region, the flow is described by an equation derived from the fact that the square root of the shear stress varied linearily with the square root of the shear rate. In the turbulent region, the friction factor was found to be inversely proportional to the velocity to the 0.12 power.

Jan 1, 1965

By S. F. Ramseyer, E. A. Steigerwald

INFILTRATED structures represent composite materials which are capable of combining high-temperature strength with adequate low-temperature toughness and thermal shock resistance. Although copper- and silver-infiltrated tungsten structures are actually being used in rocket nozzle hardware, adequate understanding of the fracture mechanics of these composite systems is not available. Specifically the relative importance of the strength, ductility, and modulus of the infiltrant in determining composite properties is not known to the extent that optimum composites can be selected. The major portion of experimental effort in the area of composite strength has been devoted to fiber-reinforced systems1 or to systems where a discontinuous phase is imbedded in a relatively ductile matrix.2'3 In the case of high-temperature systems, which are composed of a relatively brittle matrix, such as tungsten or an oxide, a continuous phase exists for the propagation of a crack. The method by which the presence of a conjugate ductile continuous phase influences the gross properties of the composite represents an area which requires further investigation. This technical note presents results which evaluate the effect of infiltrant strength on the strength of the tungsten-base composite. A tungsten matrix and copper-base infiltrant were selected for the initial studies because of the ease of fabrication. Tungsten structures with nominally 20 and 30 pct porosity were evaluated. The porosity was controlled by varying the initial powder size and a ratio of open-to-total porosity greater than 95 pct was obtained by selective sintering cycles. The processing sequence involved hydrostatic pressing followed by a 72-hr presinter in hydrogen at 2000° F and a final sinter at 4000°F for 4 hr in vacuum. The 20 pct porous structure was obtained

Jan 1, 1965

By Thon T. Gin

The lithologic, mineralogic, and magnetic beneficiation characteristics of the iron formation at U. S. Steel's Atlantic City Ore Mine, Fremont County, Wyoming, have been determined. The iron formation averages about 30 percent Fe content, and varies from 125 feet to about 500 feet in thickness. It is composed of interbedded magnetite-rich quartzites, magnetite-quartz-amphibole schists, and amphibole-chlorite schists. Quartz, actinolite-tremolite, chlorite, and magnetite are the essential mineral constituents. These rocks are differentiated into four major ore types on the basis of their relative quartz and amphibole content. The iron content of the magnetic concentrate decreases and the silica content increases with decreasing grain size and increasing amphibole content in each ore type at the same fineness of grind. Criteria were developed to enable the mine operator to recognize the ore types and to blend them to produce a more uniform concentrator feed. This results in less variation in product quality and requires fewer changes in operating conditions-in the concentrator.

Jan 1, 1965

By P. R. Gage, R. W. Bartlett

SILICIDE coatings on refractory metals are often applied by transporting a silicon halide vapor to a hot metal surface where dissociation or hydrogen reduction occurs. The subsequent chemical reaction to produce the coating requires diffusion of silicon or the refractory metal through the in situ silicide layer. This solid-state diffusion process step is often slower than the vapor-transport step and, therefore, rate controlling. This situation is analogous to the parabolic oxidation of metals in which the oxidation rate is controlled by diffusion through the oxide layer. The purposes of this study were to 1) measure the rate of formation of MoSiz and MoSi2 coatings under conditions such that the silicide diffusion process is rate controlling and lower silicide compounds are not formed and 2) determine by a marker experiment whether silicon or the respective refractory metals are the principal diffusing species in the disilicides.

Jan 1, 1965

By Martin H. Stanczyk

The Bureau of Mines studied continuous closed-circuit attrition grinding of a coarse commercial filler-grade kaolin to produce paper-coating-grade clay having a particle size analysis of at least 70 percent minus 2-micron equivalent spherical diameter (esd). The coarse clay, containing about 12 percent minus 2-micron-esd material, was ground in a Bureau-developed 10-inch-diameter attrition grinder in closed circuit with a 5-foot-diameter bowl classifier. In the best test, a finished product containing 82.7 percent minus 2-micron-esd material was obtained when grinding 20 pounds of raw clay per hour at percent solids with a 100-percent circulating load. Energy consumption was about 341 kilowatt-hours per ton of clay feed, or 487 kilowatt-hours per ton of minus 2-micron-esd material produced. Closed-circuit grinding gave some-what greater particle size reduction and lower energy consumption than either batch or continuous open-circuit grinding.

Jan 1, 1965

By K. M. Busen, J. Lindmayer

A heterojunction model is suggested for descrihzng the electronic conditions at oxide -semiconductor interfaces. Detailed study of the silicon oxide-silicon interface shows that the heterojunction model explains many experimental facts; however, it is necessary to assume that a transition layer exists at the interface. It will he demonstrated that ionic contrbution way also he present. Extended low-temperature heating stabilizes the oxide to a charge carrier density in the order of 10' cln-: determined by the heterojuncton model. OXIDIZED semiconductor surfaces are widely used, since they offer technological advantages and "passivate" the surfaces of semiconductor devices. However, it has been recognized that there are always n-type inversion layers formed in the silicon oxide-silicon system, which must be regarded as a definite disadvantage. An added complication is the "instability" of these inversion layers;' the inversion layer appears to vary with the processing and they change at temperatures as low as 100" to 200°C This paper will point out that the inversion layer is a result of the dissimilarity of the contacting materials and therefore must always be present. The dissimilarity is the essence of the heterojunction or electronic model and involves directly the structure of the materials involved. In addition, one finds the contribution from ions; this disturbance, however. can be eliminated for the case of silicon oxide-silicon interface. The strength of the inversion layer or channel will be expressed in terms of the density of elementary charges per square centimeter, N*, maintaining the channel. The next section contains the formulation of the heterojunction model by assuming a contact between two homogeneous materials. This calculation should not imply that silicon oxide is homogeneous; it serves only to point out the general properties of the electronic model. Following the electronic model, the practical case of the silicon oxide-silicon interface will be discussed. I) THE HETEROJUNCTION MODEL Contacting an oxide with a semiconductor, a work-function difference must be accommodated. Fig. 1 represents the oxide and the semiconductor before and after contact. When the contact has been made, one finds that qVi + qV, = A@; i.e., the work-function difference is distributed between the oxide and the semiconductor. Normally, the work-function difference appears on the wide-bandgap material, but in the present case the oxide is thin and far from being a single crystal. Accordingly, a significant fraction of the work-function difference must appear on the semiconductor. The work function of silicon2 is about 4.8 ev, but we shall not assign any particular work function for the oxide as it may vary. However, oxides usually have lower work functions and therefore the potentials must build up in the manner shown in Fig. 1. Such an argument predicts that the inversion layer must be n type, as opposed to the clean surface which is p type. Another important factor to be considered is that the oxide is disorderly and therefore contains many trapping levels. As a result, the charges in the oxide arise primarily from the change in trap occupation, while on the semiconductor side the space charge is composed of mobile free electrons. The consequence of this fact is that a change to another thermal equilibrium will require some time, dictated by the traps in the oxide. The conditions can easily be calculated on the semiconductor side. Assuming an intrinsic semiconductor, Poisson's equation is

Jan 1, 1965

By D. C. Shelton

Eq. 4 and 5 on page 5 of the March 1965 issue of Transactions, and Eq. 12 on page 8 of the same issue should read respectively:

Jan 1, 1965

By Gareth Thomas

The analysis of Kikuchi pattersns of exct ovientalions from single cryslals and paired Kikuchi lines from single and overlapping crystals is shown to be useful and quanlitalve and is applied to Phase transfovnzcitions including ordering, spinodals, mavten-silic, and nuclealion and growth pyocesses. 112 pinciple, the analysis of exacl orientations enables the crystal system and the Bravais lattice of a crystal to he determined. The advantages of the davk-field imaging technigure for detecting vevy small precipitates are also described. ALTHOUGH Kikuchi electron-diffraction patterns were first observed nearly 40 years ago,' little systematic application seems to have been made of them, until fairly recently during electron microscopy, when their usefulness in contrast experimen and for determining exact orientations8'9 has been pointed out. With the availability of gonio-metric specimen tilting stages it has now become possible to make much wider use of diffraction patterns, particularly the Kikuchi pattern, which is the main subject of this paper. The treatment presented here is not exhaustive but it is hoped that it will stimulate more use of Kikuchi patterns during electron-microscopy investigations. The Kikuchi pattern is formed as a result of Bragg diffraction of the inelastically scattered electrons produced during the interaction of the beam and thick specimens, The important feature of these patterns is that they give an accurate representation of the symmetry of the crystal being investigated, so that it is possible to identify crystal systems and even the Bravais lattice. This means that new structures, e.g., formed in phase transformations, may be identified during normal electron microscopy, so that Kikuchi-pattern analyses considerably extend the uses of the electron microscope. Recent work has also shown that dark-field images are more informative than bright-field images, particularly, for observing small precipitates. The second part of this paper discusses some applications and advantages of dark-field imaging in studies of two-phase systems. 1) DIFFRACTION PATTERNS 1.1) Spot Patterns. Electron-diffraction spot patterns have their limitations because of the importance of the form factor on the intensities and shape of the reciprocal lattice points. Because of the extension of these points into relrods, reflections are possible over a large angular range (+5 deg) and the patterns from thin regions can be complicated because second-layer relrods intersect the reflecting sphere. Spot patterns can thus give only an approximate idea of the crystallography unless the foil is tilted into exact orientation. In this case the spot pattern is symmetrical, with equal numbers of spots on the positive and negative zone directions about the origin. Such cases are necessary for structural analyses and have been used recently to determine the crystal structure of the ordered Ta64C phase." Exact orientation means that the plane of the reciprocal lattice lies exactly normal to the incident beam as shown in Fig. 1(b). It should be noted that in exact orientations the angle of reflection is less than the exact Bragg angle 9 so that the reciprocal lattice points lie to the outside of the sphere, Fig. 1(b). This deviation is denoted by the parameter s and in the usual convention4 s is negative for exact orientations and, of course, zero at the exact reflecting position shown in Fig. l(a). In order to avoid secondary reflections from thickness relrods it is advantageous to work in thicker regions of foils. Diffraction from thick regions may also produce Kikuchi patterns and as dis-

Jan 1, 1965

By L. A. Dale, D. A. Dahlstrom

Closed-water circuits are justified today from two standpoints: economical operation and prevention of stream pollution. In today's modern preparation plant, it has been found very desirable to have the plant circulating water maintained at a relatively low solids concentration of around 3%. In so doing, bene-ficiation equipment can operate at a much higher efficiency. However, makeup water requirements would become excessive if the fines were to be removed from the preparation plant by bleeding a 3% solids concentration to a tailings pond. With the ever increasing percentage of —200 mesh coal, clay and slimes in the raw coal, coupled with the creation of these fines within the preparation plant, the need for water conservation for economy reasons becomes even more important. Because of stream pollution laws, tailings ponds have become very costly to operate and maintain, resulting in the necessity of employing an in-plant method of water recovery. Accordingly, the primary system employed in water recovery in the coal preparation plant today consists of a solids concentration device to thicken refuse solids while at the same time producing a sufficiently clarified effluent that can go back to the preparation plant for water reuse. The thickened product is then normally passed to a dewatering device that will produce a handleable solid that can be disposed of

Jan 1, 1965

By H. E. Powell

Basic data were recorded on the decompositions that take place during thermal decomposition of siderite (FeC03). Both the naturally occurring and a synthetically prepared mineral were studied by differential thermal, thermo-gravimetric, X-ray-diffraction, and chemical (including gas) analyses. Thermal decomposition was studied in the media of dry air, moist air, dry carbon dioxide, dry helium, and dry carbon monoxide and at atmospheric and at reduced pressures. Results showed the thermal decomposition of FeC03 to be an extremely complex process, dependent on environmental factors and side reactions that cannot now be completely controlled. Therefore, full understanding of the reaction involved must depend on additional research with advanced evaluation techniques.

Jan 1, 1965

By Lawrie D. C

Finely ground beryl was decomposed by mixing with ground limestone and soda ash and heating at 900°C for 4-6 hr. The sintered mater:al was then crushed and leached by boiling under reflux with 5N sulphuric acid for up to 4 hr. The liquor containing Be, AI, Fe and other elements as sulphates, was separated from the residue which consisted mainly of silica and gypsum, either by filtration or bydecantation washing.The clarified leach liquor was first treated to remove Fe+++ by contacting with a primary amine-kerosene solution in 2 countercurrent stages. The iron free liquor was then passed to a 4-stage counter-current extraction unit where it was contacted with O·5M di- (2 ethyl hexyl) phosphoric acid (EHPA) in kerosene. Under the operating conditions, 99 per cent of the Be and 7 per cent of the Al was extracted.The Be and Al were stripped from the organic phase by sodium hydroxide solution of suitable concentration to form soluble "beryllate" and "aluminate" respectively. Most of the Be was subsequently precipitatedas Be(OH)2 by heating the alkaline solution to 90°C, the Al remaining in solution. After filtration and washing, the Be(OH)2 could be ignited directly to BeO at about 1000°C or used as a feed to further purification stages if required.A small counter-current extraction unit was operated continuously using liquor derived from the sintering and leaching stages. Dataobtained in batch laboratory tests were confirmed. A product obtained by ignition of the washed "beryllate" precipitate contained more than 99 per cent BeO.INTRODUCTIONIn 1958 an investigation was commenced into the recovery of beryllium oxide from beryl, as part of a programme to utilize mineral resources of South Australia. A survey of the literature indicated that little work had been done on direct solvent extraction of beryllium from aqueous liquors, so it was decided to apply the experience gained in this field in uranium processing to the current problem.Preliminary extraction tests on solutions of beryllium...

Jan 1, 1965

By R. H. Schnitzel

Internal-friction peaks have been observed in tungsten single crystals at about 300° and 400°C. The characteristics of these peaks are similar to interstitial peaks observed in other bee metals; therefore, the origin of these peaks appears to he the Snoek mechanism. The interstitial responsible for the peak at about 300°C has not been identified. Carburizing increases the magnitude of the peak at about 400°C; consequently, it appears reasonable to suppose that the specific interstitial associated with this peak is carbon. The activation energies associated with the 300° and 400°Cpeaks are about 35,000 and 45,000 cal per mole, respectively. INTERNAL - friction peaks resulting from the stress-induced diffusion of interstitials (Snoek relaxation peaks) have been frequently observed in bee metals.1-5 Attempts to detect Snoek relaxation peaks in tungsten have, however, not been fruitful.' Failure to find Snoek peaks in sintered tungsten can perhaps be attributed to one or more of the following difficulties: a) the relatively low purity of the sintered tungsten; b) the lack of extensive metallurgical knowledge about tungsten-interstitial alloys, such as suitable interstitial dosing and quenching procedures; and c) the inconsistency of some of the interstitial analyses of tungsten, which reflects itself in one's inability to be sure of the nature of the specimens. This present investigation did not overcome all of these difficulties for successful tungsten internal-friction measurements. Some of these difficulties still persist and new difficulties were encountered during the course of this investigation. Nevertheless, the use of electron-beam tungsten single crystals having somewhat greater purity levels than sintered tungsten combined with appropriate carburizing and quenching procedures permitted a reasonable attempt to be made. As a consequence, internal-friction peaks were observed in these tungsten single crystals at about 300° and 400°C. These peaks were found to be unstable, since they annealed rapidly away during a sequence of internal-friction measurements. Hence, it was necessary to construct an apparatus having a faster heating rate to study some of the details of these peaks. From the behavior of these peaks as well as our knowledge of similar peaks in other bee metals, one can reasonably conclude that these peaks are caused by residual interstitial impurities within these crystals. Further investigation of these peaks after the application of various metallurgical treatments lent credence to this supposition. EXPERIMENTAL TECHNIQUE The internal friction of tungsten single crystals was measured using two different pieces of apparatus both of which are of essentially the same conventional design, namely the KE type of torsion pendulum. The important difference between these two types of apparatus was in the attainable heating rate and method of protection of the specimen from atmospheric contamination. The apparatus designated "number 1" was enclosed in a vacuum chamber which was heated by an externally mounted furnace. It had a slow rate of heating which was estimated to be about 4°C per min from room temperature to about 350°C and then about 1°C per min to 600°C. The internal friction of tantalum was measured with this apparatus and the established Snoek peaks were found.' These tantalum peaks in the temperature range from room temperature to 400° C served as a check for the apparatus. The apparatus designated "number 2" having a faster heating rate than number 1 was not elaborate. It consisted of a mounted nickel tube to which split heating elements were attached. Argon was used as the protective atmosphere. The measured heating rate was about 12° to 15°C per min whereas the cooling rate was somewhat slower at about 10° C per min because of the increased difficulty encountered in stabilizing the temperature. No surface oxidation of the specimen was noted after any test. This apparatus was also checked with the known peaks of tantalum.1 The preparation of the single-crystal specimens for internal-friction measurements consisted of centerless grinding the crystals from an approximate 0.200 in. diameter to 0.030 to 0.040 in. in diameter, and then electropolishing them to about 0.020 in. in diameter. Single crystals processed in this manner are designated as being in the virgin condition. Since the length of crystal varied from 3 to 9 in., the test frequency varied from about 1 to 2 cps. The frequencies of measurement, axial orientations, and chemical analyses for the various crystals are listed in Table I. The controlled addition of carbon into tungsten is a difficult problem. Attempts to find the critical conditions necessary for an equilibrium treatment were not fruitful. Therefore, a simple nonequi-librium method was used. The addition of carbon to these crystals consisted of appropriately combining three treatments—carburizing to achieve a case, annealing to partially dissolve the carbon into the

Jan 1, 1965

By J. L. Eakin

The Bureau of Mines determined agents that are effective in foaming heavy brines and oil from gas wells in severe concentrations of sodium chloride, in severe concentrations of calcium chloride, or in moderate oil-brine mixtures. Dynamic foam tests were designed to select the more effective foaming agents. Numerous foaming agents were tested in concentrated simulated brines, in oilfield brines having varied concentrations of ions, in heavy natural brines, and in a commercial brine generally used as a reservoir pressure-balancing fluid. Several agents were detected that could perform efficiently in the field under the most severe saline conditions. Agents that promote foaming in oil-brine mixtures were also determined.

Jan 1, 1965

By W. H. McFarland

The mechanical properties have been determined for a large number of alloy-free martensitic steels with carbon contents ranging from 0.08 to 0.20 pct and with manganese contents of about 0.4 to 0.5 pet. These steels were tested 1) as water-quenched, 2) after quenching, temper rolling, and tinning, and 3) after tempering treatments which involved temperatures from 400o to 1300oF and times from 1 min to 8 hr. The majority of these tests represent steel from commercial-size coils, i.e., strip 32 in. wide, coil weights up to 20,000 16, and steel thicknesses from 0.0055 to 0.024 in. As a result of these treatments, it has been shown that as-quenched low-carbon alloy-free steels can be produced with tensile strengths ranging from 140,000 to 220,000 psi and tensile elongations from 3.0 to 4.0 pet in 2 in. The tensile strength of the as-quenched martensites can be represented by the equation, tensile strength (ksi) = 119 + 560 (wt pet C). The response to tempering of these steels is related to previous work by Muir, Averbach, and Cohen and by Grange and Baughman. Strain aging of low-carbon martensite has also been investigated. If low-carbon steels are defined as those steels with a maximum carbon content of 0.2 pet, it is found that the literature on low-carbon, alloy-free martensites contains little data on the mechanical properties of these steels. However, the following facts concerning low-carbon alloy-free martensites seem firmly established:'-' 1) The major factors in controlling the strength of the martensite appear to be a) fine structure, b) the internal strain resulting from the transformation, and, particularly, c) the amount of carbon in solid solution. 2) In low-carbon steels, the martensite is auto-tempered and is in the form of needles with only minor amounts of internal twinning, whereas the martensite in high-carbon steels forms as plates which are internally twinned on a fine scale. 3) Care must be taken in comparing the results of work that has been done on low-carbon steels with varying amounts of alloying elements to data on plain carbon steels. As has been noted by Irvine, Pickering, and Garstone,6 alloying elements generally lower the martensite start temperature and, thereby, decrease the amount of auto tempering obtained during the quench. This makes it difficult to

Jan 1, 1965

By Robert Parker

Measurements of the latent heat of transformation from a to 0 titanium were made using a pulse-heating technique. Rapid heating was accomplished electrically by discharging a low-inductance capci-tor hank through a thin-strip specimen. Both high-purity titanium and titanium containing 2700 ppm of 0 were studied. An electrical-resistivity technique and a plot of energy input us temperature rise were used to monitor the phase change. It was concluded that: 1) the latent heat of transformation is 800 i 48 cal per mole; 2) phase change occurred in less than 200 sec; and 3) the percentage phase change that occurs is linearly a function of the energy available for phase change. In addition, this experiment provides a simple and inexpensive method for determining specific heat of electrical conductors over large temperature ranges. The chief advantages of this technique over past pulse-heating experiments are: 1) static measurements of capacitor-bank voltage capacitance and specimen resistance can be made quickly and accurately to determine the energy supplied to the specimen; 2) the specimen is heated so rapidly (10 µ sec) that there is no appreciable heat loss during the heating. THE purpose of this paper is to illustrate the use of the capacitor bank as a tool for basic experimental investigations and to determine the rapid phase-change kinetics of titanium. The capacitor provides a number of unique properties: 1) rapid heating rates in the order of l09oC per sec can be obtained; heating rates as slow as l04oC per sec are available by merely adding a given amount of inductance to the circuit; 2) the energy input can be precisely determined and can be varied from several joules to millions of joules, depending on the bank capacitance and voltage; 3) the specimen can be heated uniformly through the thickness and length or non-uniformly, as desired; 4) the apparatus is simple and inexpensive and can be easily altered; 5) the form of the specimen can be wires, sheets, foils, rods, and cylinders; 6) there is great precision in the timing of events; 7) this technique may be readily used in conjunction with rapid cooling.

Jan 1, 1965

By W. D. Haentjens, A. P. Pipilen, M. Weintraub, A. A. Orning

W. D. Haentjens (Barrett, Haentjens and Co., Hazleton, Pa.) — The authors are to be complimented on undertaking a project which has little available experimental data. There are so many variables in the hydraulic transport of solid materials that it is difficult to correlate the experimental information from one series of tests into usable data involving other materials or even similar materials but of different size consists. The friction data is of particular interest to those involved in pipeline design. Most such pipelines, however, involve portions which are not level and the effect of sloping or vertical lines might also be considered in extensions of this test work. Pump manufacturers are concerned about criticism resulting from the stated amount of degradation occurring in a pump. The amount of degradation is affected somewhat by pump design and this should be taken into consideration. The pump which was loaned for this work was a modification of a standard medium duty slurry pump. This modification was for maximum particle size, however if minimum degradation is the object, then other design changes would be indicated. Although there is a tendency to be less concerned with degradation in industrial applications, it is nevertheless an important factor in many uses and further studies should be made. In particular, the amount of degradation could possibly be segregated into more classifications, rather than charge some losses to the pump which apparently are occurring in other handling. It seems difficult to evaluate the degradation which occurs in handling the coal into the pump sump and in removing it from the line into the tank. Each handling, of course, contributes some degradation, as does the screening operation itself. These are all charged to the pump, or to the pipe line and pump together; and, although they may be small, they could possibly be evaluated. It is interesting to note the verification of the old rule of thumb of maximum particle size equal to approximately one-third of the pipe size. Our experience has shown size distribution to have an effect on the flow characteristics and if this data is available for the tests which were run, it would be interesting supplementary information. A. P. Pipilen, M. Weintraub and A. A. Orning (Authors' Reply) — In this paper the authors have attempted to outline some of the major factors affecting a rational design for a solids-liquid transport system. They are grateful to Mr. Haentjens for pointing out several other equally important considerations. Pump manufacturers, in general, should be complimented on the strides that have been made in decreasing particle degradation within the pump. Considerable research and a great deal of mathematical analysis is required before pump design in this field can become a science rather than an art, for each system requires a different set of compromises. As Mr. Haentjens indicates, maximum-particle-size handling capability may be inconsistent with minimum degradation; even more important, the rotor profile for the most efficient transfer of energy to the fluid may have to be compromised to reduce particle breakage, for, whenever particle density differs from fluid density, the two phases will have different trajectories. Some evidence of this geometric factor is provided by a cursoy analysis in the Bureau of Mines Report of Investigations now in preparation, where it is indicated that, for the pump used, degradation decreased when the tangential velocity was decreased and when the radial velocity was increased. This relation, itself, is probably a function of particle size and concentration. Some data on particle size distribution, as requested by Mr. Haentjens, will be provided in the Report of Investigations referred to above in addition to that already presented in Table II of the original paper. However, in the limited number of tests it is difficult to distinguish between cause and effect, for not only did the particle size distribution alter the flow characteristics, but, through the medium of degradation, the operating conditions rapidly altered the particle size distribution.

Jan 1, 1965

By G. E. Rennick

A siphon-type laboratory airlift well was designed and operated by the Bureau of Mines to study the concurrent flow of air and oil in small-diameter pipes. Glass flowstrings ranging from to 1 inch in diameter and from L4 to 64 feet in length were equipped with various-sized air-entry jets. Liquid holdup volumes were used to correlate vertical-flow data, and empirical equations for computing gas requirements were derived. The effect of flowstring length on flow efficiency, oil- and gas-production rates, and gas-oil ratios was relatively minor at all flowing pressures. Air-jet sizes and flowstring diameters, however, had a marked effect on flow efficiency and oil- and gas-production rates. The small air-jet sizes increased maximum flow efficiency and its associated flowing pressures but decreased oil- and gas-production rates. An increase in flowstring diameter increased maximum flow efficiency with its associated flowing pressure and also increased the production rates of oil and gas.

Jan 1, 1965

By L. S. Darken, H. A. Wriedt

In a previous paper,1 an experimental study of nitrogen dissolved in a cold-rolled ad heat-treated, low-carbon steel at 300° to 450°C yielded the equilibrium solubility relations and the concentrations of the two types of deject sites involved. In this paper, the probable identities of the defects that absorb nitrogen are restricted from the available evidence to screw dislocatioms for B sites, and to either micro crack surfaces or edge In a previous paper.' we reported an experimental study of the excess nitrogen solubility in a low-carbon steel produced by a combination of plastic deformation and nonrecrystallizing heat treatment. The concentrations of the defect sites that absorb the excess nitrogen were measured in terms of their capacities for nitrogen. Also measured were the equilibria of nitrogen distribution among the sites. Several problems and questions arise from these measurements. We should like a physical identifi- dislocations for A sites. The concentrations of these defects in experimental steel specimens are estimated from the concentrations of defect sites. finally, the influence of chemical composition upon the nitrogen-trapping defects—the relative numbers generated in deformation, the relative numbers surviving as temperature is raised, the apparent numbers observed, and the distribution equilibria-is discussed. cation of the defects involved and of the two kinds of nitrogen-absorbing sites, called A and B types, upon those defects; the concentrations of the defects themselves could then be computed. We should also like to know how exclusively the findings apply to the "X steel" used in the experiments and to what extent they apply to cold-rolled steel given no subsequent treatment. By considering the data already given, together with results from a few specific tests which will be reported as they are invoked, we are able to eliminate some interpretations altogether and to secure an acceptable though limited interpretation from among the remaining possibilities.

Jan 1, 1965