By William V. Kotlensky

PYROLYTIC graphite may be represented by a stack of overlapping, wrinkled sheets with the graphite basal planes more or less parallel to the deposition surface. Previous work1" has described two stages in the deformation above 2600°C produced by applying a stress parallel to the deposition surface. The first stage occurs at deformations less than about 15 pct and involves dewrinkling accompanied by basal-plane slip and basal-plane reorientation. The basal planes are not perfectly

Jan 1, 1965

By Rudecindo S. Silo

[The principal characteristics of the process is that when applied in medium or in great degree it only needs unelaborated raw materials such as sodium chloride and calcium carbonate, or of medium elaboration, as sulphur which is found in large quantity in the North of Chili; however, the may be also applied to small copper plants provided that low cost sulphuric acid is available as a substitute for sulphur, that is, in. those plats of small capacity where large additional installations are not needed for the regeneration of the leaching solution. The method itself comprises 6 stages, namely: crushing, leaching, washing; of solutions, precipitation, regeneration of the leaching solution and fusion.]

Jan 1, 1965

By R. Steinitz, L. Seigle, R. Resnick

THE rates of growth of the carbide phases MC and M2C in the Ta-C and Cb-C systems have been measured at various temperatures and the results used to estimate the rate of carbon diffusion within the inter metallic phases. Sheets of high-purity tantalum (50 ppm Cb, <25 ppm Ti, 10 ppm Fe, 5 ppm Cr, <50 ppm Mo, W, and all other metals, 15-75 ppm O2, 10-30 ppm N2, and 10-30 ppm C) approximately 1/4 by 1/2 by 0.020 in. were heated to temperatures between 1800" and 2700°C in a carbon resistor furnace under an atmosphere of argon plus sufficient methane to maintain an excess of carbon at the sample surface. The thicknesses of the carbide layers, illustrated in Fig. 1, were measured with a filar micrometer and plotted logarithmically as a function of time. Fig. 2 is a typical plot for the TaC phase. The points may be represented within experimental error by lines with slope equal to 1/2; therefore the growth of the layers may be described by the usual expression X = kt1/2, where X is the layer thickness, t is the time, and k is a temperature-dependent constant. From these data and compositions at the phase boundaries, it is possible to estimate values for the diffusion coefficients of carbon in each phase, assuming that layer growth occurs by carbon diffusion alone, and that the dif-fusivity is not a function of composition within each

Jan 1, 1965

By I. R. Kramer

I. R. Kramer (Martin Co.)—In a recent paper Nakada and Chalmers24 reported some observations of effects of surface conditions on the stress-strain curves of aluminum and gold single crystals. It is of interest to compare these observations with the results published previously in this journal and to comment on their general conclusions. In brief, Nakada and Chalmers concluded that the removal of the surface layer of a prestrained specimen lowered the stress-strain curve for aluminum but not that for gold. Further, they concluded that the surface work hardening of aluminum is confined to a depth not more than l0-3 cm. In our results25 published previously, it was pointed out that when prestrained specimens of aluminum and gold were polished to reduce the thickness upon reloading the initial flow stress decreased markedly. Further if a sufficient amount of metal was removed, the yield point failed to appear. With continued application of the load the stress-strain curve became coincident with that of the virgin crystal. We have found this behavior in some 100 determinations to hold consistently for gold, aluminum, and copper in both single and poly-crystalline specimens. The amount of strain required before the curves coincided depends upon the amount of metal removed but it is usually less than 0.01. This type of behavior is the same as that reported for metarecovery by other investigators.29 For aluminum specimens which have been prestrained and then heated to temperatures above 50°C we have consistently found that the stress-strain curve was typical of the orthorecovery28 type. In this case the stress-strain curve always lies below that of the virgin specimen. With respect to Ref. 24 the curves for aluminum are always below that of the virgin curves, while those for gold become coincident. This observation indicates at least for aluminum that the specimens must have been heated to a temperature high enough to cause recovery by an alteration of the internal dislocations. In addition, a recovery would be expected because of the removal of the surface work-hardened layer. Nakada27 had reported that, with his particular apparatus in which a perchloric acid polishing solution was used, the temperature of the specimen increased 65°C. The curves presented in Ref. 24 for gold do not permit one to detect the initial flow stress upon reloading after the surface-removal treatment. In fact, contrary to the method used by Nakada and Chalmers, the change in the stress-strain curve produced by a surface-removal treatment cannot be described in terms of a decrease in stress at strains much higher than that at the initial flow stress because of the coincidence of the curves at the higher strain values. With regard to the depth of the work-hardened surface layer, our data show for aluminum single crystals (7.5 by 0.3 by 0.3 cm) that the initial flow stress remained constant after 12 x 10-3 cm had been removed from the thickness. This depth was independent of the prior strain. For gold crystals this depth is somewhere between 10 x 10-3 and 20 x 10-3 cm. Y. Nakada (author&apos;s reply)— Kramer states,28 "for aluminum specimens which have been prestrained and then heated to temperatures above 50°C, we have consistently found that the stress-strain curve was typical of the orthorecovery28 type. In this case the stress-strain curve always lies below that of the virgin specimen." However, Cherian et a1.26 discovered that aluminum polycrystals annealed at 32" and 100°C showed the metarecovery behavior. They showed that the orthorecovery behavior did not appear until the crystals were annealed at 150°C. Kramer suggests28 that the drop in the flow stress of aluminum crystals after the surface removal by electropolishing24 may be due to the recovery caused by the temperature rise which may occur during the electropolishing.27 However, as indirectly stated in Ref. 24, the current density used in these electro -polishing experiments was 0.15 amp per sq cm. According to ref. 27, this current density should cause a temperature rise of only 40°C. This may cause the metarecovery but not the orthorecovery. Furthermore, as stated explicitly in Ref. 24, the surface removal was accomplished by chemical etching as well as by electropolishing. The results were the same for both electropolishing and etching. During the etching, the specimen temperature did not rise above 35°C. Some aluminum crystals were placed in water at 35° C for 30 min. These crystals did not show the decrease in flow stress. Therefore, it is quite clear that the flow-stress drop after the surface removal is not caused by a high-temperature recovery. However, as Kramer points out,28 it is quite possible that the internal dislocation structure may have been altered because of the removal of the highly work-hardened surface layer. However, how much this rearrangement contributes toward the flow-stress decrease is not known at present.

Jan 1, 1965

By Nicholas J. Grant, Robert H. Kane, Bill C. Geissen

The platinum-rich section of the Ta-Pt Phase diagram was worked out by metallographic and X-ray techniques, using twenty alloys; solidus temperatures and solid solubilities were determined. Besides s phase, four intermediate stoi-chiometric phases were found: TaPt (high-temperatzrre phase, structure unknown); TaPt2 (ortho-rhomhic, new type); a TaPt3 (orthorhombic, TiCu3 type); ß TaPf3 (monoclinic, new type). TaPt2 and TaPt3 melt congmentlv; two eutectic, two beritec-tic, and one eutectoid reactions occur in the inuestigated range. THE Ta-Pt system was examined as part of a study of the phase diagrams and the intermediate phases of niobium and tantalum with Group VIII transition metals. Since the main scope of this work was the relation among the ordered close-packed phases occurring in the concentration range from AB to AB3 (A = Nb, Ta; B = Pd, Pt, and so forth), only the platinum-rich side of the diagram was worked out thoroughly, while spot checks were made to determine the approximate outline of the tantalum-rich portion. The system has not been thoroughly treated in the literature; Greenfield and Beck1 in their survey of refractory metal intermediate phases found a o phase between -18 and 37 at. pct Pt which coexists at higher platinum concentrations with an unidentified intermediate phase. Browning2 worked on the range between 55 and 100 at. pct Pt; however, this preliminary study did not cover temperatures >1500°C, and included no conclusive crystallo-graphic data. More recently, a study of the platinum-rich section of the Ta-Pt system has been carried out by Ray,3 while Hartley, Parsons, and steedly4 have studied the tantalum-rich section. The crystal structures of TaPt2, a TaPt3, ß TaPt3, and others have been reported in abstracted form by Giessen and Grant.5 EXPERIMENTAL METHODS The methods of alloy preparation and processing and of the metallographic and X-ray procedures follow very closely those described by Ritter, Giessen, and rant&apos; for other refractory metal-noble metal systems, and will not be repeated except where significant differences exist. Starting materials were: tantalum rod of 99.95 pct purity, supplied by National Research Corp., and platinum sponge 99.9 pct, supplied by The International Nickel Co. An oxygen analysis of the tantalum rod showed 30 ppm O; other impurities were C, N, Si, Nb, Mo, none of these exceeding 50 ppm, and 100 ppm W. Homogeneous buttons were readily prepared as follows: ingots of 5 g were weighed and arc-melted under welding grade argon, followed by two remelts after inverting the button. Between 40 and 100 at. pct Pt, weight losses during the first melt rarely exceeded 0.1 pct, in which case the alloy was rejected, and were nil on subsequent remelts. Since the vapor pressure of platinum far exceeds that of tantalum, the small evaporation loss could be assumed to consist of platinum; therefore, a corresponding amount of platinum was added on the second melt. Since it was confirmed on pure tantalum samples that no weight gain through oxygen or impurity pickup occurs (see Ref. 71, it could be assumed that the uncertainty in the composition did not exceed ±0.1 at. pct for the range 40 to 100 at. pct Pt. For the four control melts from 0 to 40 at. pct Pt, an error of ±0.5 at. pct was calculated. Microscopic examination of the whole buttons after melting showed no inhomogeneity other than local coring. This was eliminated by a homogenization heat treatment. A total of twenty-three alloys were prepared. Heat treatments were carried out in a tantalum

Jan 1, 1965

By J. J. Cosgrove, J. E. Warren

A general model which approximates the effect of cross- flow has been developed to give a practical method for predicting the waterflood behavior of a stratified reservoir. The model is based on a modification of Dietz&apos;s theory and allows for variations in both the permeability and hydrocarbon pore volume. In the particular cases considered, it is assumed that the permeability can be characterized by a log-normal distribution and the hydrocarbon pore volume by a normal distribution. A simple graphical method which enables the practicing engineer to predict the behavior of a stratified system is presented The results obtained by the proposed method are compared with those obtained by the Dykstra-Parsons method. As a result of this study the following conclusions have been drawn: (1) The effect of cross-flow in a stratified system can be appreciable, particularly at very favorable or very unfavorable mobility ratios; (2) Under normal conditions, the effect of variations in the hydrocarbon pore volume can be neglected; and (3) The failure to use all of the available permeability data can lead to large errors in the prediction of the behavior of a stratified reservoir. INTRODUCTION Various methodshavebeenproposedto characterize and to predict the waterflood behavior of a stratified reservoir. Most of the methods assume that the reservoir is composed of discrete homogeneous continuous layers. With this model, the degree of stratification can be measured by several parameters based on core-analysis data. Among these are the Lorenz coefficient1 and the variation of a log-normal permeability distribution? The behavior of stratified systems is usually predicted by the Stiles, Dykstra-Parsons method or some modification of these. In both of these methods the reservoir is divided into discrete homogeneous layers with no cross-flow between layers. In the Stiles method the mobility ratio is assumed to be equal to unity while in the Dykstra-Parsons method it is allowed to take on any value. Other predictive methods have been proposed; method allows for cross-flow between the beds and a method by Schmalz and Rahme6 correlate.s the recovery directly with the Lorenz coefficient. In this new approach, which is essentially a continuous analog of Hiatt&apos;s method, the effects of both mobility ratio and cross-flow between the beds have been included. It is assumed that the permeability can be represented by a log-normal distribution and the hydrocarbon pore volume or porosity by a normal distribution. These types of distributions have been observed by several authors, 1,2,4 and most field data seem to confirm their observations; e.g., if these distributions are assumed and there is a 1:l correspondence between porosity and permeability samples, the commonly encountered linear relationship between porosity and the log of permeability is obtained. Since, in many field cases the permeability and poro sity data are truncated or cut-off at predetermined upper and/or lower values, the effect of discarding part of the data was investigated with the proposed method. A better technique for truncating the data is suggested. THEORY In the derivation of the method to be described in this paper the following assumptions are made: 1. Capillary forces are negligible per se; their effects are only manifest in the relative permeability curves. 2. The fluids are immiscible, incompressible and homogeneous. 3. The reservoir is horizontal and uniformly thick; it is initially liquid saturated i.e., connate water and oil. 4. The reservoir is composed of discrete layers, each having its own permeability, porosity and connate water saturation; each layer is homogeneous,

Jan 1, 1965

By A. G. Crocker

The positions of twin reflections in electron-dijjcraction patterns obtained from thin metal foils may he calculated for any twin in any crystal structure by means of an elementary application of vector algebra, General equations for the four classical orientation relationships are presented using the superscript and subscript notation of the tensor calculus, which is briefly described. As an example of the application of these expressions, the case of twinned rhomhohedral crystals, and hence as a special cased twinned cubic crystals, is examined. CONSIDERABLE interest has recently been shown in the interpretation of electron-diffraction patterns obtained from twinned regions of thin metal foils. In the present paper, it is shown that the necessary information may be obtained directly for all twins in any crystal structure by means of a very elementary application of vector algebra. The equations involved are most conveniently presented by making use of the very powerful superscript and subscript notation of the tensor calculus. The use of this notation will first be described and then applied to the problem of calculating diffraction patterns for any twinned crystal. Finally, as an example of the application of the method, the specific case of twinned rhombohedra1 crystals will be considered.

Jan 1, 1965

By Charles W. Merrill

The U.S. Treasury stocks of silver have been reduced at such a rapid rate to meet industrial and coinage requirements that they face exhaustion in 3 or 4 years. Alleviation of the silver problem will require increasing supply or reducing demand. This paper examines possible long-range resource development and research programs and improved secondary recovery. The possible reduction or elimination of silver in coinage and development and introduction of substitutes in the arts and industry are also discussed.

Jan 1, 1965

By W. F. Rogers, J. A. Stewart, P. J. Kalish, E. O. Bennett

Detailed descriptions are given of materials, apparatus and the experimental procedure used to study the effect of bacteria on sandstone permeability. The factors affecting permeability during injection of bacterial suspensions which have been investigated are: (I) concentration of bacteria; (2) core permeability and median pore size; (3) species of bacteria, mode of aggregation and relative size; (4) injection rate or pressure differential; (5) mean pressure; and (6) depth of penetration of bacteria. The investigation demonstrated that bacteria cannot reduce core pertneability to zero and that their effect on permeability is subject to definite limitations. Remedial or permeability restoration studies also were made. Acidization in combination with reverse flow war found to be an effective method for restoring permeability In cores partially plugged with bacteria. The relationship between the bacterial quantities in the laboratory tests and those found in field operations is discussed. The linear laboratory flow data have been translated into terms of field radial systems; these data indicate the most practical methods of maintaining injection rates in the presence of bacteria are to increase injection pressures or hydraulically fracture the formation. INTRODUCTION It has long been known that various bacteria flourish in the above-ground components of oil field water-injection systems. The presence of these bacteria has led to the suspicion that they might enter into the causes for reduction of injection well permeability, but only recently has an attempt been made to describe the effects quantitatively.1 Biocides are used in many cases without a firm knowledge as to whether the bacteria are killed, or if they are, whether the dead cells affect formation permeability. This project was undertaken as part of a study to determine the effect of bacteria, residual oil and precipitated solids such as iron sulfide or calcium carbonate on the permeability of sandstones and to learn whether any of these materials adversely affect brine injectivity in secondary recovery or disposal operations. This report deals with that portion relating to the effect of bacteria. MATERIALS CORES Three different permeability ranges of Berea sandstone cores were used in the study. The range of initial, absolute brine permeabilities kj were: high — 278 to 400 md: medium—130 to 162 md; and low—17.7 to 48.3 md. The permeability data for the cores used in the tests are included in Table 1. All cores were cut to a nominal 1 in. diameter. Following air permeability determinations, they were molded with an epoxy resin in 1.5 in. ID aluminum sleeves. The sleeves had drilled and tapped holes for intermediate pressure connections along the length of the cores. After molding, the high- and medium-permeability cores were trimmed to 4 in. in length and the low-permeability cores to 2 in. These lengths resulted in pore volumes of approximately 10.9, 10.4 and 4.4 ml, respectively, for the high-, medium- and low-permeability cores. Pressure-transmitting channels were drilled through the plastic into the core proper, using the sleeve holes as drill guides. Width and depth of channel penetration into the core proper were approximately 0.03 in. and 0.05 in., respectively. Three pressure taps were used with all cores; for the high- and medium-permeability cores the taps were spaced 1 in. apart; for the low-permeability cores the taps were spaced 0.4, 0.8 and 1.2 in. from the inlet end. Pore size distributions were calculated from restored-state capillary pressure curves for representative cores in each of the three permeability ranges. In each case the pore size range with the greatest percentage of the pore space included the very small pores up to 0.5 micron in radius. The median pore radii were in the 5.5 to 6 micron range for the high-permeability cores; in the 4.5 to 5 micron range for the medium-permeability cores; and in the 3.5 to 4 micron range for the low-permeability cores.

Jan 1, 1965

By P. W. Davies, B. Wilshire

PREVIOUS investigations on the effect of stress changes on the high-temperature creep and fracture behavior of metals have been confined mainly to the testing of complex alloys.172 Most of these alloys are structurally unstable during creep because of such effects as recrystallization, overaging, and so forth, so that the results are of limited application. The only pure metals on which observations have been made appear to be lead3,4 and aluminum5 tested under conditions which allow rapid recovery to take place. The present work describes the effect of a single stress change on the creep and fracture properties of a metal in which recovery is very slow. A Ni 0.1 at. pct Pd alloy was used so that grain growth and recrystallization did not occur during creep testing. Specimens of this material were heat-treated to give a uniform grain size of 10 grains per mm. Creep tests were carried out at 500°C using Denison T.47 machines; details of the creep-testing procedure have been given elsewhere.&apos; All specimens were tested at a constant initial stress of 5 tpsi which gives, in an uninterrupted test, a minimum creep rate of ~10-3 pct per rnin and a life of -7000 min. Specimens were loaded under these standard conditions and after 1500 min, when secondary creep was well-established, the stress was changed to either 8, 7, 6, 4, 2, or 0 tpsi for a period of 180 min. After this time the original load was reapplied and the tests continued to fracture. The results are shown in Fig. 1. No detectable creep occurred during the period of reduced load, even at 4 tpsi, and on reverting to 5 tpsi the creep rate returned to its original value immediately. Increasing the stress to 8, 7, or 6 tpsi resulted in an instantaneous extension followed by a period of transient creep leading to a new steady creep rate. On returning from these higher stresses, the resulting creep rate at 5 tpsi was very low compared with the original value. Furthermore, the higher the stress during the stress change, the lower was the final creep rate. It is significant that the rupture life is comparatively unaffected by any of these stress changes.

Jan 1, 1965

By L. A. Geoffrion, R. H. Perkins, J. C. Biery

Densities of cerium metal and several lour-melting binary cerium alloys were measured over the range 25° to 800°C. A rolumeter, using NaK as working fluid, was used to obtain the data. The cerium, Ce-Co, Ce-Ni, and Ce-Cu alloys all exhibited an increase in density on melting, while a Ce-Mn alloy expanded on melting. FOR the proper design of a nuclear reactor, the change in density of the fuel with temperature must be known. This is especially important in a system utilizing molten fuel, such as LAMPRE (Los Alamos Molten Plutonium Reactor Experiment), since a relatively large change in density usually occurs during the solid-liquid transition. The fuel for LAMPRE is a Pu-2.5 wt pct Fe alloy with a melting temperature of 410°C. However, limitations in reactor design with this fuel have led to consideration of other plutonium-containing alloys for use in future generations of this type of reactor. Several ternary alloys containing plutonium and cerium as two components have satisfactorily low melting points. The system that at the present time appears to be most acceptable is Pu-Ce-Co; it exhibits little change in melting temperature with wide variation in plutonium concentration. Other alloys that have received some consideration contain nickel, copper, and manganese as the third constituent. The proposed fuel alloys are difficult to handle experimentally in the 25" to 800°C temperature range since they oxidize readily, react with many solvents, and contain a poisonous fissionable material. In addition, in this temperature range the alloys pass through the solid-liquid transition. Several techniques are available for measuring the densities and volume coefficients of expansion of solids or liquids. However, the only apparatus that appears suitable for measuring expansion coefficients over this temperature range and through the phase transition is a volumeter. In a volumeter, the indicating medium must be essentially inert to and insoluble in the material being studied. It must also possess a low vapor pressure over the operating temperature range, and its coefficient of expansion must be accurately known. One material that is satisfactory in nearly all of these respects is the alloy Na-78 wt pct K, which melts at -10°C and has a vapor pressure of 860 mm Hg at 800°C. This relatively high vapor pressure at 800°C requires an overpressure of an inert gas to prevent boiling. While a volumeter is capable of determining accurately the volume coefficients of expansion of materials, it cannot be used for absolute density measurements. Therefore, a density determination at a known temperature must be coupled with the volumeter measurements to give all the desired data. The weight-loss technique using immersion in bromobenzene at room temperature proved to be satisfactory. The preliminary work that was done on this experimental program involved developing and calibrating the equipment, and measuring the densities and volume coefficients of expansion of cerium and some low-melting binary cerium alloys. The complications that are caused with the introduction of plutonium into the system were avoided until the equipment was proved to be satisfactory and until experience was gained in its operation. It is this first phase of the experimental work that is described in this report. DESCRIPTION OF EQUIPMENT AND OPERATING PROCEDURE The NaK volumeter is shown schematically in Fig. 1. Basically, the equipment consists of two weld-sealed stainless-steel containers of nearly identical volume. One container holds a tantalum crucible and the specimen being measured; the other contains a tantalum crucible and a tantalum specimen used as a control reference material. To avoid temperature gradients, the bombs are located in a copper block inside the furnace. Stainless-steel capillaries of equal length and volume connect each stainless-steel container to a glass viewing capillary. The stainless-steel containers, stainless-steel capillaries, and a portion of the glass capillaries are filled with NaK (22 wt pct Na-78 wt pct K). The NaK/gas interface in the glass capillary is viewed with a cathetometer which is accurate to *0.5 mm. The cathetometer readings are used to calculate the volume changes of the samples during a run. This volumeter is basically the same as that described by F. Knight in Plutonium 1960. 2 However, changes in equipment design and operating procedure were made to eliminate some major operating difficulties. These changes are summarized below. 1) In filling the manometer with NaK, gas was frequently entrained in the system. Evacuation of the system before filling failed to eliminate the en-

Jan 1, 1965

By S. M. Wu, R. L. Stone, T. D. Tiemann

The dissolution of silica from quartz in sodium hydroxide solutions was investigated by statistical methods. A second-order predicting equation was developed with 28 experiments expressing the dissolution of silica as a function of the variables quartz size, time, temperature and sodium hydroxide concentration. With this equation a comprehensive picture of the dissolution reaction was gained which included the effect on extraction of each variable and their interactions, fractional extractions, reaction rates and activation energies. A previous investigation of the extraction of silica from low grade siliceous iron ore by digestion in sodium hydroxide solutions presented the extraction as a function of time, temperature and sodium hydroxide concentration.&apos; The present paper is an outgrowth of the previous work and develops by a mathematical analysis the functional relationship between the extraction of silica and time, temperature, sodium hydroxide concentration and particle size. Relatively pure quartz was used in this study in order that the basic quartz-sodium hydroxide reaction could be studied without the influence of other constituents that are commonly found in iron ores. The functional relationship between the dissolution

Jan 1, 1965

By W. C. Winegard, A. Galibois, C. J. Beingessner

The effects of solutes on the distribution of two-dimensional configurations of grains in zone-refined tin have been studied. When solutes with partition coefficients (ko) greater than unity are added, three-sided pains become more prevalent and the growth law changes. It is shown by electron-Probe micro-analysis that a solute buildup occurs ahead of a moving grain boundary when ko > 1. It has been found recently1, 2 that solutes with partition coefficients greater than unity have a larger retarding effect on grain growth than solutes with k, less than unity. ko is defined as the ratio of the concentration of solute in the solid to the concentration of solute in the liquid with which the solid is in equilibrium. Niessen and winegard2 have suggested that this effect is probably due to the complex shape changes which occur during the process of grain growth and that no theory based on single boundary motion3-5 can explain the results. They suggested that the dissociation of the unstable fourfold junction was delayed in alloys where ko was greater than 1 because the boundaries at the junction had to move into a region of high solute concentration. If indeed this mechanism were correct, it was felt that not only would the dissociation of fourfold junctions be affected by the solute buildup ahead of the boundaries, but the collapse of three-sided grains would be impaired. These combined effects would naturally lead to a modification in the distribution of the number of sides per grain seen on a two-dimensional section. The present investigation was undertaken to test these hypotheses by examining the grain-growth process in detail. EXPERIMENTS The Distribution of Grain Configurations in Zone-Refined Tin as Seen on a Two-Dimensional Section. Following the method of Bolling and Winegard,6 zone-refined tin was cast into button-shaped specimens and, subsequently, plastically deformed under a drop hammer at room temperature. The resulting flat coin-shaped samples were annealed at 200°C, some for 50 sec and others for 100 sec. The specimens were then examined to determine the distribution of the number of sides per grain, i.e., the num- ber of crystals adjacent to any particular grain in the section. For simplicity, the grains were classified as three-sided, four-sided, and so forth; this concept is schematically illustrated in Fig. 1. As indicated by smith,&apos; it was necessary to examine every grain within an enclosed area to obtain a proper distribution of the relative frequency of each type. The distributions for the two annealing times are illustrated in Fig. 2. The total number of grains examined is also indicated on the figure. It is evi-

Jan 1, 1965

By R. F. Hehemann, D. J. Cometto, G. L. Houze

The w transformation in the Zr-Nb system was studied using X-ray diffraction, dilatometric, re-sistornetric, hardness, and metallographic techniques. w forms in a diffusionless, completely reaersible manner on quenching and in a diffusion-controlled manner- on aging. The temperature at which w begins to form on quenching was determined as a Junction of composition and was found to decrease with increasing solute content. w formed bv aging establishes a metastable equilibrium with an enriched ß phase. The ß/w + ß transus has been determined for this metastable equilibrium and employed to rationalize retrogression and reversion phenomena observed in these alloys. The decomposition mechanism is discussed in terms of a gradual or continuous transformation from ß to the w state. BETA- stabilizing alloying elements lower the MS temperature of the martensitic bcc (ß) to hcp (a&apos;) transformation in zirconium and titanium alloys. In certain titanium alloys, a lower symmetry modification of the martensitic structure, termed (a"), also has been reported.1,2 These martensitic transformations are suppressed when the amount of the ß-stabilizing element exceeds a critical level. However, the high-temperature ß phase cannot be quenched to room temperature without change. At alloy contents just above the critical level, |ß trans-forms to the w phase when cooled rapidly.3-6 The amount of w in quenched alloys is reduced by increasing alloy content, and this phase virtually disappears above a critical composition.5 In addition to the transformation during cooling, w also can be formed by aging ß at temperatures below approximately 500°C, and significant alloy enrichment of retained 13 accompanies the isothermal transformation.1-8 The structure of LC is closely related to that of the ß from which it forms.9-15 The bcc (ß) lattice can be generated using a hexagonal cell with three atoms located at (000) and ±(2/3, 1/3, 1/3). This cell has an axial ratio of 0.612 and is oriented with respect to the cubic cell such that (0001)H (111)C and [1120]H [101]C. Consequently, there are four possible orientations of the hexagonal cell, associated with the four (111) planes of the bee lattice. Formally w can be obtained from 0 by allowing the two atoms at the ±(2/3, 1/3, 1/3) positions to approach the coordinates ±(2/3, 1/3, 1/2) and there are four equally probable orientations of w for each 0 grain. In titanium alloys w retains the cubic axial ratio of 0.612" and hence also can be indexed as triply cubic, but this is not the case for aged Zr-Nb alloys where w is clearly hexagonal with an axial ratio of 0.622." The lattice parameters and atomic positions of w depend on thermal history and alloy content. The atomic positions (000), ±(2/3, 1/3, 1/2) provide reasonable agreement between calculated and observed diffracted intensities for w in the fully aged condition.10,14 In the quenched condition, on the other hand, the atoms appear to be displaced from the central plane12,13,15 and assume positions ±(2/3, 1/3, Z = 0.42-0.48) rather than ±(2/3, 1/3, 1/2). This results in a structure with trigonal rather than hexagonal symmetry. The readily detectable parameter and axial-ratio changes of w in Zr-Nb alloys make this system especially attractive for studying the structural changes that occur in the formation and aging of w. Particular attention in this investigation has been directed to the relationship between the structure of w in the quenched and aged conditions, and to certain aspects of the reaction kinetics. MATERIALS AND PROCEDURE Zr-5, 12, 17.5, and 25 pct Nb alloys were prepared by a double arc-melting practice, encased in stainless-steel cans and hot-rolled to 1/8-in.-thick sheet.* Charged weights have been employed for the niobium contents and interstitial analyses are reported in Table I. Dilatometric, X-ray diffraction (filtered CuK, and MoK, radiation), metallographic, and hardness techniques have been employed to follow the transformations during isothermal and quench-aging heat treatments. In quenched specimens, the electrical resistivity also was studied. Betatizing was conducted for 1 hr at 900°C. With the exception of the isothermal dilatometric studies, samples were

Jan 1, 1965

Coal research and related activities in 1964 by the Bureau of Mines resulted in many advances in the production, preparation, and utilization of this valuable natural resource. Mining research during the year was marked by work on hydraulic mining, coalbed degasification, mine drainage control, mine sealing, strip-mine rehabilitation, and quenching of mine-refuse fires. Bureau research continued to produce information leading to increased safety in underground mining. Such research included roof and rib control via bolting and bonding, pressure monitoring of coal and mine rock during mining operations, and development of safety devices for detecting conditions leading to roof falls. Other safety work was continued on methane detectors, coal-dust suppression, and mine ventilation equipment and techniques. Mine explosion and explosives research, mine equipment and materials, safety rule modernization, and safety education and training of mine workmen were continued. Coal storage and preparation work in 1964 ranged from freezeproofing of lignite for rail shipment, through washability studies of coals and washing equipment, to research on new ways to remove ash and sulfur from coal. Electric power production, which accounts for a major portion of the market for coal, received further study. Unique power generation systems, including coal-burning gas turbine and megnetohydrodynamic generators, were intensively investigated. Conventional power systems were improved through continuation of work on furnace performance, powerplant stack gas purification, and engineering and boiler water service.

Jan 1, 1965

By Wallace W. Key

Mineral raw materials produced in California, other States, and foreign countries were purchased for consumption in quantities valued at over $60 million at 800 of the 1,200 chemical plants operating in California Fn 1960, according to questionnaires completed by company officials. These and other data received from mineral consumers, producers, dealers, and Government agencies formed the basis for this the first of a series of reports designed to present the intricate features and relationships controlling mineral raw material supply and demand in California industries. The results of this study indicated certain changes in use patterns of minerals in chemical manufacturing; a shift in requirements from metals to nonmetals, from inorganics to organics, from natural to synthetic materials, and from distant to local sources of supply.

Jan 1, 1965

The Bureau of Mines has reviewed those portions of the "Tariff Schedules of the United States Annotated 1963" that are of interest to the minerals industry. This study shows to what extent rates of duty were altered (increased or decreased), and provides a bridge where possible from the old Schedule A classification sys tem to the new TSUS system of statistical reporting of import data. In general the new tariff has corrected previous classification defects and inconsistencies, but the rates of duties have not been materially changed.

Jan 1, 1965

By Sabri Ergun

NEW theoretical data are presented for the intensity of X-rays diffracted from randomly oriented aromatic and alicyclic molecules and diamondlike structures such as are found in coals, cokes, and carbonaceous materials. Data have been computed using the Debye interference function. Computations for the smaller molecules have been made with the Univac 1204 computer: those for large structures, with either the IBM 704 or Bendix G-20 computer. A brief theoretical introduction of the Dobye interference function is given, and an outline is made of the treatment of experimental data so that the experimental interference function can be obtained.

Jan 1, 1965

By James R. Kerr

This study reviews the sulfur and suliuric acid industries in Eastern United States with emphasis on patterns of consumption and marketing. Output of sulfur in the East is relatively small, and most of the area&apos;s sulfur requirements are met by gulf coast Frasch sulfur. Over the long ten recovered elemental sulfur from sour natural gas and petroleum may become the East&apos;s major source of sulfur. In 1958 sulfuric acid manufacture consumed over 80 percent of the area&apos;s sulfur requirements. The leading uses for sulfuric acid were the manufacture of superphosphates and chemicals. Over the years, unit requirements for sulfur and acid in many major markets have been reduced through improved technology, but new markets always have been developed to keep the industry vital and growing.

Jan 1, 1965

By Robert E. Green

Experiments were performed in order to investigate the influence of magnitude of driving force, recouery, and previous heat treatment on grain boundary migration in deformed aluminum crystals. The frequency of occurrence of strain-free grains possessing Preferred crystallographic orientations was studied both as a function of heat treatment and as a function of amount of deformation of the matrix crystal. Aluminum of such composition as to exhibit precipitation-hardening behavior was used. CONSIDERABLE work has been devoted to the factors influencing grain boundary migration in metals.1&apos;52 Aust and Rutterl-9 have studied grain boundary migration into matrix crystals containing a striation substructure, which provided a thermally stable driving force during the course of the migration experiments. These authors state that, while variations in the striation pattern were sometimes observed, it was possible to obtain reasonably uniform and reproducible striation structure by careful control of the solidification conditions. Admittedly, this source of driving force is a unique one and has served well in numerous experiments. However, although the striation substructure provides a thermally stable driving force, the subject of its reproducibility from crystal to crystal is questionable. In fact, Aust and Rutter3 attribute the scatter shown in some of their experimental points and several anomalies in boundary migration rates to variations in the substructure driving force along a single specimen. A further limitation on striation-induced driving force is that the driving force cannot be varied over wide ranges in a controlled manner. More often used as a source of driving force is the strain energy stored in a crystal during plastic deformation. This type of driving force has the disadvantage that it is not thermally stable due to recovery taking place simultaneously with the grain boundary mobility measurements. On the other hand, this strain-induced driving force is very reproducible from crystal to crystal since it is very easy to grow single crystals possessing the same purity and crystallographic orientation and then to strain them identically. In order to measure grain boundary migration rates two different methods are primarily used. Most often the technique employed is the heat-cool-etch method1&apos; which involves thermal cycling, while the other technique, developed by Graham and Cahn11 using an X-ray diffractometer and goniometer furnace, involves continuous heating only. Thus the influence of thermal cycling vs continuous heating is a factor to be considered in grain boundary migration rate measurements, particularly in cases where the source of driving force is the strain energy stored in the deformed matrix, and recovery is likely to occur. Numerous recent investigations have shown that extremely small impurity additions to zone-refined metals exert a marked effect on grain boundary migration rates1-5, 9, 12-27 and a few have considered the effect of the distribution of impurities.28-35 The concentration of impurities and their distribution as influenced by heat treatment must also be taken into account in migration-rate studies. In the present article consideration is given to the influence of the magnitude of driving force, recovery, and previous heat treatment on grain boundary migration rates. In order to vary the driving force over a large range it was necessary to use as a source of driving force the energy stored in the matrix crystal during plastic deformation. A majority of the investigations were performed on aluminum specimens which were of such compositions as to exhibit precipitation-hardening behavior.

Jan 1, 1965