Search Documents

By G. L. Smit

The Buffelsfontein Gold Mining Company is situated in the Klerks-dorp district of the Province of the Transvaal in the Republic of South Africa, approximately 100 miles west of Johannesburg. Gold production commenced in January 1957 and Uranium treatment of residue slimes as a by-product started in July 1957. The mining property is 5435 mining claims in extent, the equivalent of 7,988 acres or 12.5 square miles. The mine was initially exploited by the Pioneer Twin Shaft System, consisting of a 26 feet diameter down-cast shaft and a 22 feet diameter up-cast shaft, sunk in the north-west area of the mine to cater for the hoisting and ventilation requirements for a milling rate of 150,000 tons per month.

Jan 1, 1964

Bauxitic laterite of variable thickness and grade is best developed in the Darling Range but covers a large part of the southwest corner of Western Australia. Its limits are defined by the rainfall isohyets to which jarrah forest is confined. Within this broad belt there is an increase in arable land southwards concomitant with a thinning of the laterite layer.Bauxite quality and perhaps thickness as well are dependent on the type of source rock, and are influenced by topography. Economic deposits occur over a vertical range in altitude of about 1200 ft. Some bauxite orebodies appear shoot-like in character, and analogy is suggested with the ore shoots of syngenetic metalliferous deposits.The alumina is in the form of gibbsite enabling low temperature digestion in treatment.INTRODUCTIONAlthough the existence of bauxite in Australia has been known for many years it is only recently that exploitation has commenced of the two most important deposits, strangely at almost diagonally opposite tips of the continent (Fig. 1).Recognition of the importance of the bauxite in the southwest corner came about initially through the efforts of Western Aluminium N.L. which, with some outside financial help, tackled the early exploration with commendable foresight and courage. Subsequent investigations around the periphery of the original reserves (now held by Alcoa of Australia) were undertaken by several companies, including Bauxite Exploration Pty. Ltd.ORIGIN OF BAUXITEThe genesis of bauxite is stilI somewhat controversial.Owing to its common association with kaolin some investigators have been led to believe that it has been derived from the latter; others believe the process has been vice versa.From a recent study of the Arkansas bauxite region in the...

Jan 1, 1964

A field method combining solvent extraction and paper partition chromatography permits a simple and rapid semiquantitative estimation of gold in siliceous, argillaceous and sulphide ores. The method will facilitate the eyaluation of prospect samples in which the gold is too fine for separation by panning.Ethyl alcohol-hydrobromic acid mixtures are suitable for chromatographic development of the gold complex, and give clear reproducible definition of the gold zone. Substitution of commercial "methylated spirits" for the ethyl alcohol gives equally good definition, improving the potential of the method for field use.A batch of six samples in the range of 0·5 to 5·0 dwt/ton can be completed in two hours. The range may be extended by simple modification to higher or lower values.INTRODUCTIONIn a chromatographic method described previously (Lever 1958, Nevill and Lever 1959), gold from a standard volume of ore clamped between -plate glass was extracted by aqua regia on to the paper. After cautious drying the chromatogram was developed by an ethyl acetate-nitric acid-water mixture and gold was identified by spraying with stannous chloride solution. Sensitivity of the method in the low range was poor. The brown line obtained in the 1-3 dw/j ton range, caused by movement of gold in the reduced form, was not considered to be a satisfactory confirmation of the presence of gold. It was felt that the method would be improved by using a more elegant extraction and applying developing conditions which would produce a well defined purple line at all gold values. Iron was a limiting factor, and a method of eliminating its interference was needed.The method now developed overcomes these shortcomings, and gives a reliable result with a purple line for assay values of 0·5 dwtjton and over. Gold is dissolved from an...

Jan 1, 1964

By R. W. Stahl

Burning coal-mine refuse banks were surveyed in 15 States. The following characteristics were tabulated for 495 hanks: County; name, population, and distance of nearest town; size and status of bank; status and stage of fire; and topography. Ways of controlling fires were reviewed, the compacting and sealing method proving most satisfactory. Means for preventing refuse-bank fires by proper construction of banks are described.

Jan 1, 1964

By S. D. Strauss

The marketing of nonferrous metals and of the ores and concentrates from which these metals are recovered is a fascinating trade, international in character, sensitive to every change in the economic tide, and complex in its organization. Each individual metal has its own marketing mechanism; no two are exactly alike. The differences sometimes are a matter of tradition rather than of necessity, but usually they have developed because of the very nature of the problems of producing or consuming the individual metal. This description, because of limitations of space, can do no more than indicate the major aspects of the trade and touch lightly on the marketing structure of each metal. The dictionary states that a market is a "meeting of people for selling and buying." In the case of nonferrous metals this meeting may occur on a half-dozen different occasions between the time the ore has been first mined and the time the refined metal is available for use by industry; or it may not occur at all until after the metal itself has been rolled, drawn, stamped, cast, or forged into a useful semifabricated shape. To illustrate: A Chilean miner may sell his small ore production to a custom mill, which produces concentrates that are sold to an ore dealer, who finances shipments of the concentrate to a custom smelter, which buys them for conversion into blister, to be subsequently refined into electrolytic copper (sometimes by a refinery having no corporate ties with the custom smelter) and sold. Conversely, aluminum production is mostly by integrated concerns that mine bauxite, convert it to alumina, smelt that to produce aluminum, and then fabricate that into semifinished or even finished products before title to the material changes hands for the first time. Some nonferrous ores are not converted into metal at all but are sold by the miners or dealers directly to the ultimate consumers. A good example would be chrome ores used by the chemical industry. And of course a substantial part of the commerce in nonferrous metals is in scrap, which is the reconversion into useful form of metals that have long since been mined and smelted. Thus, one-third of all the lead used in the United

Jan 1, 1964

By M. H. Pilkuhn, H. Rupprecht

p layers on n-type substrates of GaAs were prepared by difhsion of zinc into these substrates. Experimental details about the diffusion technique will be presented. It will be shown that inhomogeneity in the substrate doping level and crystal shucture defects cause nonplanarity in the junction plane. These nonplanarities give rise to high threshold current densities. From incremental sheet-conductivity measurements the zinc profile is derived. Data about surface concentration and gradient of the zinc concentration at the junction are presented. Finally, some results of laser diodes, which were made of wafers with extremely planar diffusion fronts, are discussed. ThE investigations reported here are part of a program concerned with the materials aspect in the fabrication of GaAs laser diodes. This includes studies of the influence of crystal defects introduced both during the growth of the crystal and as a consequence of subsequent diffusion. Compared with the progress made in the investigation of structure defects, for instance by X-ray microscopy in materials like silicon, no similar results are known so far for the case of GaAs. The further progress in laser diodes will depend very much upon our knowledge of these structure defects and subsequently upon our ability to avoid them. Laser diodes of GaAs had been made mostly by diffusing an acceptor impurity, normally zinc, into an n-type substrate. This procedure was found more convenient than the inverse one for various technical reasons. We will follow this line and restrict ourselves to zinc diffusion only in this paper. DIFFUSION TECHNIQUES AND EXPERIMENTAL DETAIL In order to set a refgrence for our experiments, we used a standard procedure for the diffusion runs. The diffusions were carried out in a sealed quartz tube for 2-1/2 hr at 850°C. One milligram zinc arsenide (ZnAsz) per cu cm of the tube volume served as zinc source. Under these conditions the junction depth was between 25 and 30 p. It is assumed, according to the investigations of the zinc arsenide system by V. Lyons and V. ilvestri,' that ZnAs2 dissociates completely at 850°C into ZnsAsz and Asg. Since there is a condensed phase of ZnsAs2 in the tube at 850°C, the partial pressure of zinc is controlled by the pressure of the arsenic formed by the dissociation of ZnAs2. Due to the fact that the zinc partial pressure resulting from the dissociation of ZnsAsz is only a weak function of the partial pressure of arsenic, the amount of the initial ZnAs2 is not very critical. Experimentally, we found that the junction depth, as well as the surface concentration, was practically the same, if the ingots of ZnAs2 varied between 0.2 and 5.0 mg per cu cm. The wafers were oriented with the main faces in (100). Surface damage due to cutting and lapping was removed by a chemical-etch treatment in a rotating beaker (etch solution: HzSOr, H202, and HzO in a ratio 3:l:l). The GaAs substrate material was n type and doped with tellurium, selenium, silicon, or germanium. It was grown by means of horizontal or Czochralski techniques. After the diffusion process, junction depth and planarity were checked either by grooving with a

Jan 1, 1964

By H. M. Thorne

Oil shale, a potential source of products presently obtained from petroleum, is found in many countries. The most extensive known deposits from the standpoint of potential shale oil in place are those in Brazil and the United States of America. Mining methods used for oil shale range from open-pit operations for shallow deposits to room-and-pillar and longwall techniques for deposits with thick overburdens. Oil shales from different sources vary greatly in the amounts and types of organic and inorganic constituents. By retorting, the organic material is converted to oil, gas, and coke. The largest percentages of oil are obtained from materials having the highest hydrogen content. Over 2,000 retorting systems have been patented, but only a few have been used industrially, and no single process seems best for all types of shales or economic conditions. Shale oils have different characteristics, depending on the source rock and method of retorting. They contain large quantities of olefinic hydrocarbons and more oxygen, nitrogen, and sulfur derivatives of hydrocarbons than most petroleums. Consequently, petroleum refining methods usually must be modified for shale oil. This is particularly true in catalytic processing. Hydrogenation, even under mild conditions, improves shale-oil refinability. Several byproducts may be obtained from both the retorting and refining steps,

Jan 1, 1964

By Michael Hoch, Seong Kwan Rhee

The ternary system Zr-Cr-0 was investigated at 1200°, 1500°, and 1700°C. The isotherms at these temperatures were determined by metallographic and X-ray diffraction analysis of carefully selected alloys. AS a part of a series of investigations1-4 of the ternary and quaternary phase diagrams on refractory metals and their compounds, the ternary system Zr-Cr-O was investigated at 1200°, 1500°, and 1'700°C. The binary diagrams Zr-Cr, Zr-O, and Cr-0 as reported by Hansen5 and Levin et a1.' and the existence of a ternary coompound ZrsCrsO (q-carbide structure a. = 11.96A) provided a good base for this investigation of the Zr-Cr-O phase diagram. MATERIALS The materials used and their suppliers were: Zirconium powder, 99.4 pct pure, Charles Hardy, New York; Zirconium dioxide, Fairmount Chemical Co., Newark, N.J.; Chromium powder, 99.85 pct pure, Fairmount Chemical Co., Newark, N.J.; Chromium sesquioxide, 99.86 pct pure, J. T. Baker Chemical Co., Pillipsburg, N.J. Though the materials used were not "hyperpure", the impurities present do not affect the results (lattice parameters, phase boundaries) within the experimental accuracy. EQUIPMENT AND PROCEDURE The detailed procedures and equipment used for this investigation were similar to those described elsewherel' "ith the exception that in this study an induction-heated argon-atmosphere furnace was used. The latter furnace was used to prevent the vaporization of chromium metal in samples in the higher temperature range (above 1200°C). The tungsten crucible was induct ion-heated in a vertical quartz tube filled with argon gas. The quartz tube was 1-1/2 in. in diameter and 10 in. long; it was connected at the top and bottom to water-cooled copper plates. The argon gas of a purity 99.995 pct was further purified by being passed through zirconium metal chips which were maintained at 800°C in a silica tube 1 in. in diameter and 30 in. in length. The furnace was flushed with argon gas for an hour before starting heating; during heating, a slight (3 cm oil) overpressure of argon was maintained in the system. Power was supplied by a 20-kw Ther-Monic Induction Generator. The samples rested on a tungsten-wire basket; the wire basket was connected to a tungsten wire which passed through the tungsten crucible lid, and entered the system on top through a Wilson-type seal. By pulling on the wire, the sample was removed from the crucible and dropped to the water-cooled copper base of the furnace. Because of the presence of argon gas, the cooling of the sample was even more rapid than in the vacuum furnace.' EXPERIMENTAL RESULTS AND DISCUSSION 1) Isothermal Section at 1200°C. The compositions investigated have been numbered within the phase diagram, Fig. 1, and all the pertinent information about the samples can be found in Table I. This table lists the composition of the samples, the phases present in the room-temperature diffraction patterns, the phases detectable in the microstruc-ture, and calculated lattice parameters of the a-zirconium phase. The shapes of the various phase

Jan 1, 1964

By Ernest E. Thurlow

The Geology Division of Northern Pacific Railway Company has adapted to its exploration efforts field procedures for geochemical sampling and semi-quantitative analysis which have been developed through research by the U. S. Geological Survey. The sampling is done in conjunction with reconnaissance geologic mapping on aerial photographs or during field checking of maps which have been prepared largely by photogeologic interpretation.. Stream sediment or soil samples are taken and readily soluble combined heavy metals are extracted with ammonium citrate followed by colorimetric titration with dithizone at the sample site. The effectiveness of this approach has been demonstrated both in positive and negative results, thereby assisting in the elimination of large areas of land from further immediate attention and in providing targets for followup exploration. An occasional sample is submitted for spectrographic analysis as a check on the possible presence of other elements of economic significance. Field laboratory procedures are also being implemented for determining molybdenum, mercury, and other metals which may be valuable in themselves or useful as pathfinder elements in outlining mineralized areas. A lead-zinc occurrence in Oregon and a copper deposit in Montana were readily detected and outlined by stream sediment and soil sampling and a heavy metal anomaly that lacks obvious interpretation has been found in northwestern Montana. Detailed mapping and additional sampling are followed by other exploration techniques if warranted.

Jan 1, 1964

By J. L. Moriarty, Irving Johnson, H. M. Feder

The crystallization of ternary alloys has been studied as a coprecipitation phenomenon by measuring the substitutional carrying of trace metals with CeCd11 precipitating from liquid cadmium. The Doerner-Hoskins logarithmic distribution law has been found to apply in all cases; the coprecipitation coefficients obtained were: 1.48 (La), 1.06 (Th), 0.63 (Pr), 0.24 (Gd), 0.17 (Sm), 0.13 (U), 0.10 (Er), 0.09 (Sr). Li, Na, K, Ba, Y, Sc, and Zr were not measurably carried. It has been observed that coprecipitation was most extensive for those tracers which form with cadmium an intermetallic compmdnd isostructural with CeCd11 or closely related thereto. For these tracers an inverse relation between Solubility in cadmium and coprecipitation coefficient was noted. THE partition of impurities between the liquid and solid phases of a metal or a congruently melting intermetallic compound has been extensively studied by the methods of zone melting.' However, when the composition of a liquid alloy and of the solid phase crystallizing from it differ grossly, partition of an impurity cannot be investigated in this manner. Partition of the impurity under equilibrium conditions may be studied by investigation of the appropriate phase diagram and partition under nonequi-librium conditions may be studied by observation of coring in the solidified alloys.2 The nonequilibrium case is of special interest in metallurgical practice because many complex alloys are cooled too rapidly to permit the uniform diffusion of impurities throughout the crystallizing phase(s). With this in mind, the present study was undertaken to obtain quantitative data on the phenomenon of coprecipitation via substitutional solid solution in certain metallic systems. It will be noticed that rather than adopting metallurgical ter- minology we have chosen to refer to the partition of impurities during alloy crystallization as coprecipitation.3 In the terminology of coprecipitation the impurity is referred to as the tracer and the precipitating phase as the carrier. From aqueous solution, coprecipitation may occur as a result of adsorption on the surface of the carrier, by occlusion of the liquid within the crystals, or by solid solution of the tracer in the carrier. By slow cooling of liquid metallic solutions it is relatively easy to form large, regular crystals of the carrier; the effects of adsorption and occlusion may be minimized and the influence of substitutional solid-solution formation may be made to predominate. Previous studies of the crystallization of some intermetallic compounds4 and of copper, silver, and gold5 have shown that the coprecipitation or partition behavior of trace metals is entirely analogous to that observed in aqueous systems when ionic substitution occurs, e.g., coprecipitation of Ra++ with BaSo4. The precipitation of CeCd11 from liquid cadmium was chosen for study. This choice was influenced by the following consideration. If the relative atomic sizes of the tracer atom and the atom for which it substitutes determine the tendency to coprecipi-tate, then a lattice having a substitutional site of well-defined size would be desirable. In CeCd116 (structure type cubic BaHg117) the cerium atom is completely surrounded by a cage of twelve nearly equidistant cadmium atoms. Thus, atoms much larger or much smaller than cerium should be poorly accommodated in this cage. The choice of a lanthanide central atom allowed the testing of the size hypothesis with a number of lanthanide tracers which differed in size but not in valence or electro-negativity. EXPERIMENTAL The general technique of this investigation was to prepare a slightly undersaturated solution of carrier in liquid cadmium to which a tracer was added. The concentration of tracer was always so low that saturation over the entire temperature range investigated was never exceeded. The solution was cooled in a stepwise fashion. After each step a por-

Jan 1, 1964

By J. D. Meakin

J. D. Meakin (The Franklin Institute Laboratories)— In a recent paper Garofalo12 has shown that a number of experimental creep results can be represented by the empirical relation In this expression ? is the steady creep rate, s is the applied stress, and A is a constant at a given temperature; a and n are adjustable parameters. Garofalo has shown that Expression [6] approximates to a power function at low stresses and a simple exponential function at high stresses. Among the data used by Garofalo are the results we published for creep of copper." For these results we found that the best correlation was an exponential law with different parameters in the low-and high-stress region, respectively. That is, i = A exp qs where A and q have different values above and below a critical stress a,. In Ref. 13 are listed a variety of observations which support the proposal that different mechanisms are operative at stresses above and below a,, and it is not felt appropriate to repeat those observations here. The purpose of this note is to demonstrate that, although the representation used by Garofalo does fit the experimental data very well, this fit cannot be used to conclude that only one mechanism is rate-controlling. The argument is best made graphically and is illustrated in Fig. 9. The continuous curves 2 and 3 represent pairs of simple exponential functions which intersect at i = 10-5. The curve 2 closely resembles the copper results in that a change of slope of 2:1 occurs at i = 10-5; the two functions shown are in fact: e = 10-7 exp (1.150) and ? = 10-6&apos; exp (0.576s) For purposes of comparison, curve 3 represents two exponential functions with a change of exponent of 3:1 and curve 1 has the exponent 1.150 throughout. It is quite clear that a satisfactory straight-line fit is obtained on a Garofalo plot for all three curves. The curves represent processes which have either a single stress exponent or two ex- ponents in a ratio as high as 3:l. It must, therefore, be concluded that the ability to obtain a linear dependence between log i and log (sinh cyo) cannot be taken as evidence for a single activated process. In fact, to some extent the way the experimental points quoted by Garofalo lie about a best fit straight line on the log (sinh as) plot indicates that two processes are indeed occurring. This is seen in Figs. 7(c) and 8(c) of Ref. 12 where it is particularly evident that the experimental points deviate from the straight line in a manner similar to curves 2 and 3 of Fig. 9. It is, of course, recognized that the generally used exponential form is an approximation to the hyperbolic sine function which is not valid for exponents of less than 1.2, e.g., qs < 1.2. The only curve in Ref. 12 which is affected by this restriction is Fig. 6(b) where the deviation from a In ? vs s

Jan 1, 1964

By J. L. Lytton, T. E. Tietz

UNALLOYED arc-cast molybdenum sheet is typically supplied in the cold-rolled and stress-relieved condition, hereinafter denoted CRSR. Such processing eliminates the yield-point phe-

Jan 1, 1964

By Y. C. Liu

The orientation relationship between the dejormation and recrystallization textztres of binary Cu-P alloys of high phosphorus content was observed to he a ± 14-deg (110) rotation. According to the ori-ented-gvowth hypothesis, the same relationship should exist between a successfully flowing pain and the strained single-crystal matrix of alloys of corresponding composition. The orientations of thirty successfully growing grains were obtained in a Cu-1.0 at. pct P alloy. Both a conventional analysis and the more detailed analysis advanced in the present study demonstrate that the observed orientation relationship is not comparahle to that predicted by the oriented growth hypothesis. IT has been shown experimentally that the formation of recrystallization textures in metals may be explained on the basis of the oriented-growth hypothesis. This conclusion is based primarily on the results of cooperative experiments carried out by various investigators in aluminum. Beck and HU&apos; suggested that the orientation relationship between the recrystallization and deformation textures of aluminum is a 38-deg(111) rotation. A similar relationship, i.e., a 40-deg(111) rotation, was observed between the primary and secondary recrys-tallization textures.&apos; Since the secondary grains result from a process of selective growth, this naturally implies that the same mechanism is also responsible for the formation of the primary re-crystallization texture from the deformed matrix. Further evidence was provided by the experiments of Liebmann, Liicke, and Massing3 and Yoshida, Liebmann, and Lucke.4 They observed that grains which could successfully grow into strained aluminum single crystals invariably exhibited the same orientation relationships with their matrix. Thus, regardless of other opinions,5&apos;9 these results offered good evidence in favor of the oriented-growth hypothesis. In order to examine broader applications of this oriented-growth hypothesis, experiments should be carried out in metals other than aluminum. In a recent investigation on the recrystallization textures of binary copper alloys with phosphorus, arsenic, and antimony,7 it was found that the predominant recrystallization components were related to the deformation textures by a (110) rotation. The (110) rotational relationship is different from the (111) relationship generally proposed between the recrystallization and deformation components of other binary copper alloys. 1,8,9 Applying the observations made for aluminum, the oriented-growth hypothesis predicts that the orientation relationship of grains successfully growing into the strained single crystals of either one of these copper alloys should correspond to that observed in the textural study. Verification of this prediction would provide a critical test of general applicability of the oriented-growth hypothesis to the formation of recrystallization textures in fcc metals other than aluminum. The Cu-1.0 at. pct P alloy was selected in the

Jan 1, 1964

By A. W. Schillinger

Drilling was not entirely satisfactory in the search for native copper in the Osceola amygdaloid footwall, for oreshoots mined were more continuous than drilling indicated. The Geophysics Dept of Michigan Technological University developed a portable induced polarization drill hole probe with a 3-electrode configuration and a sampling radius of 5 ft ±. A 20 ma current of alternately reversed polarity is pulsed at 3.5 sec intervals and readings are taken every 2 ft. Potential is read during the "on" cycle for resistivity determinations. During the "off" cycle, after 10 ms delay, the 1P potential is sampled for 10 ms and recorded. Resistivity (ohm-ft) and "S" values (mv/v) are plotted on semi-log paper. A lithologic log is plotted based on resistivity and anomalous S values noted. The low resistivity amygdaloid contains sills of high resistivity basalt. Verified by core logs, contacts between amygdaloid and basalt could be picked to ± 0.5 ft from resistivity alone. Lithologic logs of long-steel holes, based on resistivity, then replaced sludge logging. An S value of 30 mv/v was established as the lower limit of diagnostic 1P effects in mineralized amygdaloid and 50 mv/v as a threshold value for ore. Of 914 footwall zones drilled, 315 were probed yielding 203 anomalies. Success increased from 34% for drilling to 72% for drilling and probing. As checked by mining, 46 probe results were 78% correct. Failures were due to the instrument not detecting copper or to the misinterpretation of an anomaly. No false anomalies were found. During the past ten years, the Calumet Div. of Calumet &Hecla, Inc has conducted extensive exploration and mining in the footwall of the Osceola amygdaloid lode in the native copper district in Michigan&apos;s Upper Peninsula. In an attempt to delineate more clearly the extent and nature of high-grade footwall copper mineralization, 876 diamond drill and long steel holes aggregating slightly more than 47,000 ft have thus far been drilled from the accessible hanging-wall workings in the Osceola No. 6, 13, 14 and 15 shafts. Early in this program it became obvious, through inspection of footwall workings in progress, that due to the erratic and bunchy occurrence of the native copper in the footwall zone, the exploration drilling was failing to outline completely the extent of the oreshoots. Early drilling re-

Jan 1, 1964

By E. M. Porbansky

DURING the investigation of the electrical transport properties of copper, it became necessary to prepare large single crystals of the highest obtainable purity. In an effort to meet these demands, single crystals of copper have been grown by the conventional pulling technique—as has been used for the growth of germanium and silicon crystals.&apos; Low-temperature resistance measurements made on these crystals show that, as far as their electrical properties are concerned, they are generally of significantly higher purity than the original high-purity material. The use of these pure single crystals with very high resistance ratios has made possible the acquisition of detailed information regarding the electron energy band structure of copper2-&apos; and has stimulated widespread effort on Fermi surface studies of a number of other pure metals. It is the purpose of this note to describe our method of preparing very pure copper crystals by the Czochralski technique. Precautions were taken to prevent contamination of the melt from the crystal growing apparatus. A new fused silica growing chamber was used to prevent possible contamination from previous groqths of other materials such as germanium, silicon, and so forth. A new high-purity graphite crucible was used to contain the melt. This crucible was baked out in a hydrogen atmosphere at -1200°C for an hour, prior to its use in crystal growth. Commercial tank helium, containing uncontrolled traces of oxygen, was used as the protective atmosphere. A trace of oxygen in the atmosphere appears to be necessary for obtaining high-purity copper single crystals. A 3/8-in-diam polycrystalline copper rod of the same purity as the melt was used as a seed. The copper rod was allowed to come in contact with the melt while rotating at 57 rpm. When an equilibrium was observed between the melt and the seed (that is, the seed neither grew nor melted), the seed was pulled away from the melt at a rate of 0.5 mils per sec. As the seed was raised, the melt temperature was slowly increased, so that the grown material diminished in diameter with increasing length. When this portion of the grown crystal was -1 in. long and the diameter reduced to less than 1/8 in., the melt was slowly cooled and the crystal was allowed to increase to - 1-1/4 in. diam as it was grown. By reducing the diameter of the crystal in this manner, the number of crystals at the liquid-solid interface was decreased until only one crystal remained. Fig. 1 shows a typical pulled copper single crystal. The purity of the starting material and the crystals was determined by the resistance ratio method: where the ratio is taken as R273ok/R4.2ok. The starting material, obtained from American Smelting and Refining Co., was the purest copper available. Most of the pulled copper crystals had much higher resistance ratios than the starting material. The highest ratio obtained to data is 8000. Table I is an example of the data obtained from some of the copper crystals. Note that Crystal No. 126 had a lower resistance ratio than its starting material and this might be due to carbon in the melt. The melt of this crystal was heated 250" to 300°C above the melting point of copper. At this temperature it was observed that copper dissolved appreciable amounts of carbon. The possible presence of carbon at the interface between the liquid and the crystal will result in reducing conditions and negate the slight oxidizing condition required for high purity as discussed below. The possible explanations of the improvement in the copper purity compared to the starting material are: improvement in crystal perfection, segregation, and oxidation of impurities. Of these, the latter seems to be most probable. A study of the etch pits in the pulled crystals showed them to have between 107 and 108 pits per sq cm. The etch procedure used was developed by Love11 and Wernick.10 The resistivity of the purest copper crystal grown was 2 x 10-10 ohm-cm at 4.2oK; from the work of H. G. vanBuren,11 the resistivity due to the dislocations would be approximately 10-l3 ohm-cm, which indicates that. the dislocations in the copper crystals would contribute relatively little to the resistivity of the crystals at this purity level. Segregation does not seem likely as the reason for purification of the material, since the resistivity of the first-to-freeze and the last-to-freeze portions are approximately the same, as was observed on Crystal No. 124. On most of the crystals that were examined, the entire melt was grown into a single crystal. If the

Jan 1, 1964

By Ronald Gibala

THE Au-Ni alloy system is one of many binary systems in which the supersaturated solid solutions may exhibit a multistaged precipitation behavior during aging. In addition to the equilibrium phase separation, which was studied extensively years ago in the range 400" to 600",&apos; there exists at least one earlier stage of precipitation, i.e., preprecipitation, which occurs below 300°C in quenched alls.-This note reports on some effects of composition on the preprecipitation in Au-Ni alloys as determined from resistivity measurements. The kinetics of the preprecipitation were studied in alloys of 15 to 85 at. pct Ni which were water- were found in alloys which after various quenching-and-aging treatments were slowly heated and cooled (1Z"C per hr) between room temperature and about 300°C. Two such heating-cooling curves for a 40 pct Ni alloy are shown in Fig. 2. Similar effects were observed in other 15 to 50 pct Ni alloys. These curves are characterized upon heating by two changes in slope indicated by A and B in the figure and upon cooling by a resistivity hysteresis of approximately the size of the original decrease in resistivity after the aging treatment. The inflection at B generally falls at about the same temperature for all heating curves for a given alloy and appears to be a critical temperature (T,) for the preprecipitation for that alloy. The values of T, for most of the 15 to 50 pct Ni alloys fall in the range 200" to 220°C. The position of the inflection at A depends upon the heat treatment prior to the heating-cooling run and perhaps the heating rate, which was held constant in these runs. The preprecipitates grown in by the appropriate aging treatments seem to decrease in size as the alloys are heated from A to T,, dissolve at T,, and do not reappear after cooling below T,. When similar heating-cooling treatments were performed on 60 to 85 pct Ni alloys, an entirely different behavior was observed. Typical results are shown in Fig. 3 for an 85 pct Ni alloy. In these

Jan 1, 1964

By Milan Lipensky

This paper discusses the longwalling practices used at the San. Francisco Mine of Compania Minera Autlan in Mexico, in. the mining of a sedimentary, manganese deposit. Bethlehem. Steel Company is a part owner of this property. The San. Francisco Mine is located approximately 580 miles west of Mexico City, on the outskirts of the town of Autlan, in the State of Jalisco. The ore is shipped from the port of Manzanillo 120 miles southwest of Autlan. The mining method is a variation of the longwall retreat system, using friction. props that, until recently, had been used only in coal mining operations of Europe and the United States. However, due to the structure of the ore body and the modified longwall system that is practiced, there exists some unusual variations, such as: .1) friction props set by a mechanical two-step lifting device, 2) drilling and blasting, against the friction props, 3) a highly fractured and undulating, volcanic tuff roof; 4) displacement faults-up to 5 meters, and 5) a relatively stable, irregular floor.

Jan 1, 1964

By C. M. Bartley

Canada has been a producer of sulphur in various forms for about 100 years, Pyrites, as a source of sulphur dioxide for the manufacture of sulphuric acid, were being mined in the 1860&apos;s. Smelter gas, for the same purpose, has been recovered since 1928. Between 1935 and 1943, and from 1952 to the present, elemental sulphur has been produced in Canada from two raw material sources and by several methods. This paper attempts to present a view of the current status of the elemental sulphur industry in Canada based on the sour gas fields of Alberta and British Columbia. Production from this source has increased rapidly in the past 12 years to make Canada one of the major sulphur producers of the world. The present industry in Canada relies mainly on sour gas sulphur and it is expected that it will continue to grow in the future. However, before describing current activity relating to sour gas it may be of interest to outline briefly the early pyrite activities, the roots of the sulphur industry in Canada.

Jan 1, 1964

By W. D. G. Hunter

Since 1945 the world&apos;s iron ore industry has experienced radical change. This transformation is reflected in new levels of production, consumption and trade, in shits in the location and size of markets, in the tapping of far distant sources of iron ore, and in the emergence of new export centres catering on an increasing scale to ore deficient, importing countries. Within the broad framework of shifting supply/demand relationships, certain operationally meaningful adjustments can be singled out for special mention: 1. The iron and steel industry has undergone vigorous and aggressive expansion, during the post-war period, not only in the capitalist world and among the socialist bloc, but in backward regions as well. New countries have been added to the list of steel producers, while new facilities have been relocated by established steel makers. 2. Overall demand for iron ore has risen rapidly, arid has flowed different channels.

Jan 1, 1964

By W. E. Newell

The basic principles and assumptions involved in D. L. White&apos;s solution5 for ultrasonic wave amplification in piezoelectric semiconductors are summarized. If the gain per unit length is maximized at each frequency without regard to the drift-field power density, the gain increases linearly with frequency. Therefore it would seem that very high gain is possible for frequencies in the hundreds of megacycles. However, with present materials the resulting drift-field power density is so large that cooling would be a major problem. For this reason it is more realistic to judge the capabilities of an ultrasonic amplifier in terms of the gain that is possible with a specified power density. In this case the gain at high frequencies does not increase but decreases more rapidly than l/f. The calculation of the gain us frequency at a fixed power level involves the repeated solution of a cubic equation and is therefore tedious. For the purpose of comparing different materials, sufficient accuracy can be obtained from an approximate solution which may easily be plotted as three straight lines on logarithmic graph paper. This method is used to compare the Performances of CdS, CdSe, ZnO, and GaAs. At a power density of 10 watts per cu cm, the first three give maximum gains of 60 to 80 db per cm in the vicinity of 60 megacycles. At the same power density, GaAs has a maximum gain of about 7 db per cm near 150 megacycles. Although an increase in mobility usually increases the gain for a specified power density, it is shown that there is an optimum mobility above which the gain decreases. An approximate expression for the optimum mobility is established. It is well-known that the interaction between charged particles and an electromagnetic wave can be used to amplify the electromagnetic wave. In the conventional traveling-wave tube, electrons in a vacuum are caused to move at a velocity slightly greater than the wave velocity, thereby coupling energy into the wave.&apos; In principle, the same effect would be evident in a solid except that repeated collisions prevent the electrons from attaining a velocity greater than that of an electromagnetic wave. However, the drift velocity of electrons can be made to exceed the velocity of an acoustic wave in a solid. In 1956, weinreich2 noted that the deformation potential provided one means of coupling energy from drifting electrons into an acoustic wave, but the effect was too small to be of any practical importance. It was not until 1961 that White and Hutson demonstrated that the piezoelectric effect provided a strong enough coupling to give appreciable amplification of an ultrasonic wave and awakened wide interest in electron-phonon interactions. Qualitatively the effect may be described as follows. An acoustic wave propagating through a piezoelectric material is accompanied by an electric-field wave. If the vibrations are properly oriented with respect to the crystal axes of a piezoelectric semiconductor, the local electric fields are axially directed and cause bunching of the charged carriers. If the drift velocity of these carriers is less than the velocity of sound, they tend to be dragged along by the acoustic wave. This electroacoustic effect results in a net potential appearing across the material and in attenuation of the acoustic wave. On the other hand, if the drift velocity exceeds the velocity of sound, energy is coupled from the carriers to the acoustic wave and amplification results. Related effects which are being investigated include ultrasonic amplification in semimetals6-&apos; and semi-conductor, and current saturation in piezoelectric semiconductors.&apos;4-17 There are various problems which hinder the immediate application of ultrasonic amplification in a practical device. First, there are the traditional problems encountered in the design of acoustic delay lines: attenuation in the electromechanical transducers, reflected waves (which can lead to self-oscillation in an amplifying device), mechanical tolerances necessary to maintain phase coherence, and so forth. Second, there is the problem of selecting the best material from among the various piezoelectric semiconductors as they become available in single-crystal form with a wide choice of characteristics. This paper deals with the second problem and shows that the most realistic way of comparing materials is in terms of the gain which can be obtained without exceeding a

Jan 1, 1964