Search Documents

By Fred W. Shultz

The process engineer is familiar with the in any methods employed in the past for analyzing various materials. These include panning. eyeballing, and wet chemistry. Of those mentioned only wet chemistry has been and will continue to be a standard measure for the elemental content in a given material. However, wet chemistry, by the very nature of the method, can be excessively time-consuming and thus reducing obviously the number of samples that may be processed in a given period. The analysis by X-ray, in most cases, requires nothing more than assurance that the sample is in a suitable state for presentation to the X-ray spectrometer.

Jan 1, 1964

By Sumner M. Anderson

THE ENORMOUS contrast between the mineral economy of Cuba in 1963 and in 1958 was the result of the overall Political changed to which the total economy of the country was intimately lined. Creation of the Cuban Mining Institute (Instituto Cubano de la Minería) to direct all mining activities in the country was an early act of the new Government after the revolution on January 1, 1959. During the next 2 years, the Government confiscated foreign holdings,2 including Unite States investments exceeding $1 billion in value. Foreign mining and metallurgical technicians-predominately from Communist areas-were brought in to reorganize the mineral industries. On January 3, 1961, diplomatic relations between Cuba and the United States were severe and then on May 2, Cuba announced its full-fledged membership in the so-called Communist Bloc. Fifty-four international treaties assured Cuba of Communist economic support, technical and financial assistance, machinery, raw materials, and manufactures. The Soviet Union agreed to buy some Cuban mineral products, and Czechoslovakia stated that it would buy all mineral production offered for the next 20 years, but in both cases at prices said to be much lower than the world market. The mineral productivity segment of the mineral economy during and since the period of political metamorphosis, has withstood the political disruption better than has the economy as a whole, but with no direct measure of the magnitude of its cost. The overall economic record is marked with steady deterioration; the annual average per capita income has dropped from $374 in 1957 to $185 in 1963, when Cuba's deficit with the Soviet Union alone reached an admitted $1 billion.

Jan 1, 1964

THE problem of reaction rates in the open-hearth process is essentially that of trying to form a fairly clear picture of the "chemical mechanisms" in the bath. Quantitative data on reaction rates would perhaps not be of much practical importance even if they were available; however, what few approximate data there are can be used in combination with data given in Chapters 16 and 17 to sketch a picture of the "chemical mechanics" of the open-hearth process that is consistent with essentially all the present available evidence. The result may later be found incorrect in many details but even so it will illustrate certain useful methods for obtaining a clearer understanding of the process. Consistent with the treatment in Chapter 15, but in simpler terms, we may say that chemical reactions in general involve the following elements or steps : 1. The reacting molecules are mixed together in space in such fashion as to favor collisions among them. 2. Units of what is usually an intermediate molecular arrangement called an activated complex are formed at a certain rate, depending on temperature and concentrations. 3. .These activated complex units decompose into the reaction products (this step usually assumed to be so rapid as never to limit the over-all process). 4. In any of these steps, heat energy may have to flow into, or away from, the reaction zone to permit the reaction to proceed. 5. The products of reaction will usually have to move out of the way to permit further reaction. The temperature factor enters mainly through step 2, and its effect is very marked. (What is called temperature is really the mean energy content of all the molecules of the substance involved; at any one temperature a certain proportion of the molecules will have much higher energy content than the mean value.) Various reaction rates measured at around room tem-

Jan 1, 1964

By J. L. Ratliff, R. I. Jaffee, H. R. Ogden, D. J. Maykuth

An experimental program was carried out to improve the low-temperature ductjlity of tungsten through the combined use of dispersed oxides for grain-size control and Groups VII and VIII metal additions for matrix softening. Separate binary -alloy studies showed that increasing amounts of finely dispersed thoria or zirconia and critical amounts of rhenium, osmium, and iridium were effective in significantly reducing the ductile-to -brittle bend transition temperature of tungsten as well as in increasing its re crystallization temper - LIKE most of the high-melting point bcc metals, tungsten undergoes a marked transition from ductile to brittle behavior with decreasing temperatures. The material factors which influence the transition temperature include grain size, metal purity, and the presence of dispersed phases. ature and decreasing its recrystallized grain size. The beneficial effects shown by each of these additions on transition temperature and grain size in binary combinations appeared to be additive in tevnary combinations. Thus, combined additions of 2 to 8 vol pct thoria with 5 pct Re, 0.87 pct Os, or 0.30 pct Ir were effective in lowering the transition temperature of tungsten pom 2000 to 75"C, increasing its re crystallization temperature from 1600 to 1800°C, and decreasing its recrystallized gain size from 1175 to 6800 grains per sq mm. The mechanism by which these factors are operable in tungsten is not yet clearly understood. Nevertheless, it has become increasingly apparent that the interrelationship of grain size and matrix composition governs to a large extent the degree of low-temperature ductility which can be achieved. Though it is not possible to accurately assess the relative importance of these variables, the available evidence suggests that, at low temperatures, grain-size effects predominate over purity effects. This was indicated in recent studies by Allen, Maykuth, and Jaffee,' involving single crystals containing 20 to 40 ppm 0 and 1 to 30 ppm C. Thus, while each

Jan 1, 1964

By T. R. Madhavan

The development of contact angles on highly polished ?uraninite surfaces, using sodium oleate and dodecyl ammonium acetate as collectors, has been studied at different collector and hydrogen ion concentrations. It was found that sodium oleate in acidic media (up to a neutral: PH) and dodecyl ammonium acetate in neutral and alkaline media give good contact angles. It appears that the combined forms of these collectors, viz., oleic acid and free amine, are more important in effecting contact. W ITH the emergence of uranium as a strategic metal in the last fifteen years, considerable effort has been directed toward the commercial recovery of uranium from its ores. This has resulted in the development of a uranium technology. It is only in recent years, However, that fundamental data regarding the floatability and surface properties of uraninite and ?pitchblende have been elucidated by different methods. Contact-angle measurement is one of the important tools for tl1e evaluation of the conditions of floatability

Jan 1, 1964

By John C. Kleiber

From time to time since the initial installation of an experimental flotation section in 1940 (reference A), Permanente Cement Company has made efforts to beneficiate the low-grade limestone fraction which occurs in its deposit at Permanente, California, The encouraging results outlined in this paper are the result of Permanente's latest effort. This paper discusses the factors governing the selection of the flowsheet with particular reference to marketability of the sand tailing by-product. The process flow is outlined in detail, and operating statistics of the plant are presented. Finally, the problems encountered in the operation of Permanente's beneficiation plant are discussed as well as solutions sought and found.

Jan 1, 1964

By Louis A. Panek

Research on roof bolting has developed significant information with respect to the functions that can be performed by properly installed bolts and the methods that can be used to ensure that effective installation has been achieved. The present paper brings together results that are pertinent to the design of a bolting system for reinforcing horizontally stratified mine roof with vertical bolts. The design approach is based on the use of bolts to decrease the maximum bending stress within an arbitrary sequence of roof strata (such as shown by figure 1) in which the only loads are the weights of the individual beds. The use of rock bolts to achieve other objectives, such as to stabilize a fractured rock mass on the periphery of a mine opening (3), is excluded from consideration herein.

Jan 1, 1964

THE primary interest in the subject of this chapter lies in the fact that various heats of steel made to the same chemical specification do not always have the same properties. The properties considered here, of course, are those inherent in the ingot immediately after solidification and not qualities imparted by variations in subsequent mechanical or thermal treatment. The expression "made to the same chemical specification" is used because some of the variations in properties are due to variations in chemical analysis within the specified ranges of those elements commonly specified and determined. Other variations in properties are due to variations in those constituents of steel (elements or compounds) that are not ordinarily included among the elements specified, thus not a part of the specified "composition." The term "constitution" is used to include not only the specified composition but also the nature and distribution of every element or compound contained in the steel entering the ingot mold ; also included are items such as aluminum oxides and nitrides, presence of soluble gases, and dispersion of nonmetallic particles. When it is considered that the constitution of steel is determined by the addition or absorption into the bath of all such constituents from whatever source, it follows that constitution is of necessity the final result of steelmaking practice. It is the agency through which steelmaking practice operates to control the properties of the steel. The term steelmaking practice is here used in the broad sense, meaning the control of all the materials entering the steel and of the conditions under which the process is carried out. Steelmaking practice, thus defined, establishes the chemical system within which the reactions between components must proceed in obedience to the laws of chemistry. Thus the chemical constitution of the steel is established and, through constitution, the properties of the metal are established. In the preceding chapters it has been shown how the constitu-

Jan 1, 1964

By Gary A. Kingston

This examination of Pacific Northwest (Idaho, Montana, Oregon, and Washington) ferrous scrap-industry operations, principally those in Oregon and Washington, points out factors influencing the supply and consumption of scrap materials, such as the complete dependence of steel ingot producers in these States on scrap as a metal raw material and the sizable quantity of scrap exported from Seattle and Portland to Japan. The pattern of the industry is presented as a movement of materials from their diverse sources to the consuming market. The geographic locations of the consuming industries in relation to the areas generating scrap materials and the movement pattern of the supply from source to destination strongly influences the cost of the commodity. The best measure of the scrap supply available in an area is experience in terms of how much scrap was withdrawn at a given price. Scrap availability is not finite, because the return of materials as scrap is secular and influenced by constantly varying market conditions. Steel ingot producers use 75 percent of the approximate 500,000 tons of scrap consumed in Oregon and Washington; steel foundries take 15 percent of the total; and iron foundries, ferroalloy plants, and other miscellaneous consumers utilize the remainder. Also, from 1955 to 1960 an average of about 200,000 tons has been exported annually from Oregon and Washington. The foreign exports are supplemented by lesser shipments to other steel producing States, principally in the western United States. From 1955 to 1960 the preferred and higher value heavy melting scrap grades accounted for about 60 percent of total withdrawals which varied between 600,000 and 950,000 tons annually. Total crap withdrawals from Oregon and Washington are projected to 1.8 million tons by 1985, 60 percent (1.1 million tons) of which will be heavy melting grades. No. 1 heavy melting scrap is most attractive to scrap consumers at $35 per ton or less. Price-supply relationships compared with projected scrap requirements indicate future prices possibly over $35 per ton. High prices over a long period could motivate the Pacific Northwest scrap consumers to produce steel from iron ore. However, technologic changes taking place at integrated steel plants could reduce scrap withdrawals from the Pacific Northwest, which might keep the scrap price sufficiently attractive to obviate production of competitive iron products by the Pacific Northwest scrap consumers.

Jan 1, 1964

By E P. Graham

Orebodies occur in an infinite variety of grades, shapes and sizes, and take many millions of years to grow. When extraction starts there is only one possible end -the mine sooner or later will run out of ore and shut down. If the mineral industry is to supply the ever increasing demands of modern civilizations, more and more metals must be found and mined. This will require a never-ending search for ore, and the development of every economic body, large or small. To justify the mining of a small orebody, it first of all must pay its way. If the size of the burden imposed by the capital cost estimates is not carefully worked out, an otherwise promising situation could be killed. The very nature of mining, as a transient industry, re-leases a steady stream of good used equipment, and the trained personnel to install and operate it. All manner of plans and layouts, which can be utilized at a new property, are available. Working these and other economies into the estimates will sometimes make enough difference to give a prospect the green light.

Jan 1, 1964

By G. Venturello, C. Antonione, G. Della Gatta

Results from work on the effect of inferstitials on recovery and recrystallization of' very pure iron (99.995 pet) doped with nilrogen up to 400 ppm are reported. Nitrided specimens were obtained by heating the iron in a static atmosphere of NH3 + H2. The samples were cold-rolled 80 pet, subjected to a series of isochronal and isothermal anneals, and submitted to examination by X-rays, micrographs, and hardness tests. Small additions of nitrogen show a strong effect in reducing recovery of' the mechanical properties of high-purity iron. At the temperatures of. the experiments, this effect proved greater than in the case of carbon. At 400°C pure iron recovers more than 50 pet of the total hardness increase, carburized iron vecovers 25 pet, and nitrided iron only 10 pet. On the other hand. the addition of nitrogen has, similarly to carbon, a very small effect on recrystallization; the effect is, however, slightly higher than that of carbon. When the concentration Of nitrogen is above the solubility limit in a iron at the temperattue of the experiments, an increase in the frequency of nu -cleation is also observed. THE object of the present work is to improve knowledge on the effect of interstitials both on recovery and on primary recrystallization of pure iron. In fact. at present there are no available data on the effect of nitrogen on high-purity iron. The only work which at present can be somewhat related to this problem is a work of Leak et al.1 in which grain boundary internal friction at high temperature in the presence of increasing amounts of nitrogen is studied by a torsion pendulum. The present work is a continuation of a previous one2 on the effects of carbon. EXPERIMENTAL PART Preparation of the Material. Pure iron was prepared following the same methods used in the pre- vious work2 and was nitrided using controlled quantities of ammonia in an apparatus similar to that used for carburizing. The apparatus consists essentially of a gas-tight quartz tube containing the specimens. The tube, maintained at constant pressure by means of a mercury seal, is placed in a resistance furnace. For nitriding, the NH3 + H2 atmosphere with a suitable concentration of NH3 was introduced into the tube, which had been previously carefully evacuated and degassed by heating at 600°C. The hydrogen used was carefully purified by passing it through a palladium filter. The ammonia required was prepared with the following reaction: CaO + 2NH4CI —CaCl2 + H2O + 2NH3 by heating the mixture of CaO and NH4C1 in a glass flask and then collecting the ammonia in a graduated Hempel burette. For each nitriding program a given amount of NH3 prepared by this method was introduced together with the H2 into the tube previously evacuated. Nitriding of the sample was then performed at 570°C for 48 hr. After this, to ensure a homogeneous distribution of nitrogen, the samples were further heated for 72 hr at 800°C. With this method which uses a static nitriding atmosphere, carefully controlled conditions of purity are obtained. Contrarily, with the conventional continuous-flow methods, using large quantities of circulating gas, there is a greater risk of introducing impurities into the samples. Furthermore, the required nitrogen concentration in the specimen is easily predetermined and obtained. A plot of the relation observed between the initial concentration of NH3 in the gas and the quantity of nitrogen introduced into the iron samples is given in Fig. 1. The data refer to samples of 1.2-mm thickness and to the nitriding conditions previously described. Furthermore, as a comparison, the data relative to two 0.5-mm-thick samples are reported. The presence of a reservoir in the cold zone of the reaction bulb made possible the gradual dissociation of ammonia on the sample in the hot zone. Internal-friction methods were used to determine the content of nitrogen dissolved in the iron samples. Some analyses were also carried out with chemical methods. The following table, Table I, shows a comparison of data obtained with chemical and internal-friction methods. The correspondence between chemical methods and internal-friction

Jan 1, 1964

By John W. Weeton, Donald W. Petrasek

Relatively few metal-metal systems exist that would permit the creation of fiber-metal composites consisting of mutually insoluble constituents. It is anticipated that most high strength-to-weight ratio and high -temperature fiber composites ultimately to be produced will utilize high-strength fibers embedded in a highly alloyed matrix. An investigation was conducted to determine the effect of alloying on the tensile Properties and micro-structure of tungsten-fibey-reinforced composites. Composites were made of tungsten fibers infiltrated with copper binary alloys that contain elements of varying solubility in tungsten. Room-temperature tensile tests were made on the composites, and a metallographic study of the microstructure of the fiber-metal-matrix interfaces was conducted. It was shown that, as the depth of penetration of some alloying elements into the fiber increased, a decrease in both tensile strength and ductility of the composite results. A notch effect, due to the formation of a brittle alloy zone with the tungsten fiber, was observed and gave rise to greater reductions in tensile properties and ductility behavior than would be Predicted by a law-of-mixture relation alone. In recent years, investigators have considered combining fibrous materials with relatively weak binder materials. The interest in fiber-reinforced composites results from the fact that fibers or wires may be exceedingly strong and exhibit mechanical properties superior to those of the bulk materials from which they are derived. For example, tungsten wires drawn to less than 1 mil in diameter may have strengths of over 600,000 psi,' while steel wires ranging from 10 to 3 mils in diameter may have strengths of the order of 300,000 to over 600,000 psi.2 Both metallic and ceramic whiskers are known to have very high strengths. For example, iron whiskers have been shown to have strengths of 1.9 million psi3 and sapphire whiskers have been reported to have strengths of the order of 1.7 million psi.4 If all or part of the strengths of such fibers could be retained, subsequent to the incorporation of the fibers in an engineering material, a superior material could result. In previous work done at the Lewis Research Center, McDanels, Jech, and weeton5 demonstrated the feasibility of fabricating metal-fiber—metal-matrix composites that utilized the full strengths of the fiber and matrix materials. Tungsten fibers were combined with a copper matrix by a liquid-infiltration method such that the tungsten fibers were uniaxially oriented parallel to the tensile axis of the composite. A linear relation was established that related the tensile strength of the composite with the volume percent of the fibers. Mutually insoluble constituents were selected for the study so that the strength of the composite could be quantitatively related to the strength of the individual constituents. The fact that there are only a few metals that are mutually insoluble with tungsten, e.g., copper, silver, gold, and zinc, and that these either have low melting points, high vapor pressures, or poor oxidation resistance, makes it necessary to utilize other metals that are soluble in tungsten, where high-temperature applications are ultimately contemplated. It was anticipated that, for most practical fiber-reinforced composite materials, it would be necessary to use a fiber and metallic matrix that would have varying degrees of solubility for each other. A logical extension of the earlier work was thus felt to be a study that would determine the effects of elements that had mutual solubility with the tungsten. Numerous investigators have found that tungsten fibers may be damaged by thermal treatments or contamination of the surface of the fiber by alloying elements.6-10 On the other hand, surface treatments may improve the strength of such fibers."-" Relatively little work with composites containing tungsten fibers have been reported. The work of parikh14 has shown that kinked, short-length tungsten, steel, and molybdenum fibers could str'engthen such matrices as silver, gold, and copper. Some of the combinations of fibers and matrices studied by

Jan 1, 1964

By S. Leber, R. F. Hehemann

This investigation describes the kinetics of alloying in a (Cb-15 wt pct W. 5 wt pct Mo, 1 wt pct Zr) powder-metallurgy alloy. The degree of homogeneity obtained in hydrostatic ally pressed and vacuum-sintered samples is described by composition distributions resulting from analysis of X-ray dvfraction line profiles. Sintering variables and degvee of powder dispersion were evaluated. The utility of single-value parameters obtained from composition distributions is disaissed. The spatial distribution of composition, as revealed by anodically tinted metallographic sarrzples, was used to provide diffision models based on a concentric-sphere geometry. Diffusion equations developed from these models were found to be in general agreement with experimental results. The powder-metallurgy method for the production of refractory metal alloys has the ability to produce an inherently fine-grained, fabricable structure. The more general use of this method is inhibited, in part, by the presumed difficulty in obtaining homogeneity on a microscale. The degree of homogeneity therefore is an important, but usually neglected, variable in specifying the quality of a powder-metallurgy alloy. Convenient techniques for measuring the degree of homogeneity are now available,' and have been used to develop a model describing the process of alloying in a simple binary mixture.' In this investigation, the process of alloy formation has been studied in a more complex system. PROCEDURE The columbium-based F-48 mixture was prepared from the constituent powders shown in Table I. The particle sizes tabulated were provided by the vendors of the individual powders. Standard laboratory techniques utilizing a jar mill were employed for blending. The blended powders were hydro-pressed into 1-in. diam rods which were then sliced into thin discs for vacuum sintering. All samples were given a preliminary treatment at 1700°C for 2 hr. Varying degrees of homogeneity were obtained using additional treatments at higher temperatures. The degree of homogeneity obtained by a specific sintering treatment was evaluated metallographi-cally using the anodic-tinting technique described by olff,' and quantitatively by the analysis of X-ray diffraction line profiles using the X-ray diffraction technique developed by udman.' The diffraction technique is strictly valid only for binary systems. However, the relatively small difference between the lattice parameters of tungsten and molvbdenum when compared with columbium permitted the treatment of the complex composition of F-48 as a (W, Mo)-Cb pseudobinary. Calculations were weighted in accord with the W-Mo ratio in the F-48 composition. The contribution of the 1 pct Zr was ignored since it could not even be detected in the blended powder. Two factors are required to convert an X-ray line profile into a composition distribution. The variation of these factors with composition is shown in Fig. 1. Curve A was used to convert angular posi-

Jan 1, 1964

By Koch DFA

An electrochemical study of the dissolution of gold in aerated cyanide solution has shown that the dissolution rate is determined b the nature of the surface. A passive film (probably a basic cyanide formed at .o.6 V vs a saturated calomel electrode inhibits both the ca.thodi reduction of oxygen. Some aspects of these retction mechcnisms are discussed together with the-"activating" effect of Thpllium.

Jan 1, 1964

By Frank L. Wideman

THE TREND towards larger quantities of waste in materials handled at metal and nonmetal mines (excluding fuels) continued. A gain of 10 percent from 1962 in the tonnage of waste removed in mineral operations reflects the kind of technological problems being encountered. Technology has a major role in the mineral industry in the task of supplying raw materials obtained from resources occurring beneath the surface of the earth and used in manufacturing commodities essential to modern living. Changes in technology are often brought about by such factors as variations in economic conditions, differences in physical properties of raw material and changes in mineralogical compositions of ore. Mining is usually begun on the richest and most accessible of known deposits, and when these are exhausted, is continued with leaner ores or with less accessible deposits that are either lying at greater depths or are more remote from markets. The increasing difficulties of extraction and depletion of reserves are offset by improvements in extraction technology, improved transportation, and exploration for new deposits. Although depletion has prevailed at many individual mines and in many districts, technology has been the means of providing for increasing demands of an expanding economy with adequate supplies of minerals despite either the changing character or decreasing grade of certain ores. This has been accomplished by various methods applicable to minerals. Among the implements of technology are utilization of lower grade or more complex refractory ores by mass mining, concentration, processing, recovery of byproducts, and mechanization. Better methods to find concealed deposits or to penetrate to greater depths also have been helpful in maintaining a supply of particular minerals.

Jan 1, 1964

By Robert E. Green, P. W. Kingman

Application of a constant geometry compression test to single crystals of aluminum of selected diameters from 1/4 to 1/64 in. showed the presence of a diameter-dependmt size effect. The most pronounced effects were found in those crystals oriented for single slip, while for specimens possessing orientations in the comers of the standard stereographic triangle virtually no size effect was exhibited. The yield stress of the crystals oriented for single slip was found to increase with decrease in specimen diameter, while the strain-hardening rate was found to be lower for the smaller specimens. The experimental results are in general agreement with those of other investigators obtained from lensile tests on copper and aluminum crystals. THE earliest systematic investigation of a possible size effect on the plasticity of metals was that of no,' who in 1926 performed tensile tests on cylindrical aluminum single crystals with diameters of 3 to 8 mm. Ono concluded that the gross stress-strain curve did not show a diameter dependence, but that the resistance to slip for strains of 0.1 pet and less appeared higher for 3-mm-diam crystals than for larger sizes. Later studies of aluminum by Maddin et al2 tentatively concluded that a size effect exists, but the conclusions were again open to question because of inconsistencies in the experimental data. Wu and Smoluchowski3 had previously shown that the slip system activated in a single-crystal sheet specimen of aluminum is a function of the specimen cross section in the slip direction, but no stress-strain data were obtained. Subsequently Fleischer and Chalmers4 studied the effect of the length of the slip direction of the primary-slip system on the stress-strain curve by testing aluminum crystals with geometrically dissimilar cross sections. In the course of this investigation a size effect was indicated in rather large crystals; however, the number of these tests was small. Other investigators have indicated that a size effect in aluminum is appreciable only for diameters of 0.5 mm or less.5, 6 Size-effect studies have also been carried out on copper crystals, the most detailed being that of Suzuki et a1.7 who performed tensile tests on specimens of many diameters ranging from 2 to 0.12 mm. Suzuki found a strong size dependence in the easy-glide region, both the extent of the easy glide and the hardening rate in easy glide were size-dependent, and the size effect was found to be orientation-dependent. Suzuki's results are in agreement with the less extensive observations of Pater-sonB and those of Garstone et al.9 A size effect was found by Rebstock using tubular copper crystals.'0 Size effects have also been noted in a brass,6, 11 in cadmium,12'19 and in hexagonal crystals.14 All the previously cited works have been entirely concerned with the variation of specimen cross section. The effects of specimen length and the change of specimen geometry which results from using progressively thinner specimens while maintaining the same specimen length have been largely ignored. A theoretical discussion of the effects of specimen length and geometry has been given by Hauser and Jackson,15 who predict a grip effect on easy glide as a function of specimen geometry provided that the specimen dimensions are large compared with the spacing between the slip bands, and by Fleischer and Chalmers,18 whose analysis of grip effects resulting from lattice rotation predicts an increase in easy glide with an increase in specimen length. A study of size and geometry effects in aluminum crystals by Kitajima and shimba17 indicated increasing amounts of easy glide in specimens of increasing length and identical cross section, and nearly identical stress-strain curves for specimens of different sizes having constant length-to-diameter ratios. Since the present study is primarily concerned with diameter dependence, the following factors were taken into account: specimen material, specimen geometry, testing method, range of sizes to be tested, and possible influence of surface and volume effects. Aluminum was chosen because of the present lack of conclusive results and the seeming possibility of size effects at relatively large diameters, the

Jan 1, 1964

By A. S. Joy

Vacuum flotation tests carried out according to the method of Schuhmann and Prakash1 have shown that the acid limiting edge of the flotation area for a Brazilian hematite, in the presence of dodecylamine, is a straight line of slope approximately unity. The flotation tests and the structure, surface ionization, and electrokinetic properties of this hematite have been fully discussed elsewhere. 2 The numbers of adsorbed H+, and OH- ions and collector molecules have been determined in the range of critical conditions defining the acid limit of the flotation area. The total amine adsorption is shown in Fig. 1 as a set of contours superimposed on the straight part of the flotation area. These were determined by spectro-photometric estimation of the complex formed between residual amine and the anionic dye Orange II.3 The ionic strength of the solutions was kept constant and at a value in sufficient excess of the amine concentration to ensure that the diffuse part of the double layer was populated predominantly by indifferent ions. Adsorption of H+ and OH- in the absence of amine was found by potentiometric acid-base titration in the presence of hematite.4 The form of the adsorption-titration curves suggested that the hematite surface behaves in an amphoteric manner, and that positively charged sites arise through loss of a hydroxyl ion, and negatively charged sites by loss of a hydrogen ion. On this basis, curves 8 and 9, shown in Fig. 2, were calculated from the titration curves. These show the variation of the numbers of positive (s +) and negative (s—) sites with pH. To distinguish between ionic and other modes of adsorption, zeta-potential determinations have also been made using the streaming potential technique. The influence of amine on the zeta-potential of the mineral over a wide pH range is shown in Fig. 3. The change in charge ?s, due to adsorption of amine ions in the Stern layer, was calculated by applying the Gouy-Chapman theory, as modified by Stem, to the results shown in Fig. 3. The validity of this treatment has been shown by Ottewill and Jaycock.5 The three full lines, Nos. (1) through (3), included in Fig. 2 show the relationship between ?s and pH at three amine concentrations. The general conclusion from the zeta-potential curves is that adsorption of amine causes a reduction in the negative charge on the surface. Comparison of the values shown in curves (1) through (3) of Fig. 2 with the - curve shows that the magnitude of the reduction is comparable with that of s - at any given

Jan 1, 1964

By W. Zieman

"The low consumption of reagents can probably be attributed to a good clean type of ore. The cyanide level is kept at 0. 8 lb/ ton of solution and the lime at 1. 8 to 1.9 lb per ton of solution (pH 12. 2 to 12 .3). Experience in cutting down the lime level in half produced troubles in the presses, in the refinery and resulted in higher cyanide consumption. Finally the residue increased under these conditions, High lime always seems to prevent the trouble from occurring.A survey at one mine of the taxable work, performed in the mine shops for use in the mine, showed that under the new regulations, this had increased some 30 times what it was before the new rules came into effect on June 14, 1963.A water softener idea is incorporated at Lamaque with the crude addition of 100 lb of lime per shift to a spare agitator to precipitate the bicarbonates as carbonates from the water before it enters the mill. The lime titration of the softened water is about 0,2 to 0.3 lb per ton of solution (pH 11). This water is used mainly on the filters as washes."

Jan 1, 1964

By W. F. Hosford

A quantitative explanation is offered for the peculiar curled grain shapes found in the microstructures of drawn wires of bcc metals and compressed aluminum specimens. It is shown that once an [011] fiber texture is developed, the slip system are so oriented that further slip tends to produce plane strain rather than axially symmetric flow of individual grains. With plane -strain flow, however, compatibility of neighboring grains can be maintained only by a bending of grains about one another. PROBABLY the most obvious microstructural feature of heavily worked metals is the distorted shapes of grains. In the course of deformation, the shape change of each grain must be compatible with that of neighboring grains; otherwise holes would be formed at grain boundaries. In analyses of poly-crystalline deformation by Taylor and subsequent workers it was assumed that grain boundary compatability was maintained by each grain undergoing the same shape change as the polycrystalline aggregate in which it is imbedded. According to this assumption, when simple tension or compression is applied to a random polycrystal or to one with a fiber texture, each grain ought to deform with axially symmetric flow. Initially equiaxed grains should become cigar-shaped during wire drawing and pancake-shaped during compression. While microstructural observations of deformed metals are generally in accord with such a picture, certain striking exceptions may be noted. Peck and Thomas5'8 found that grains in heavily drawn tungsten, iron, and niobium (columbium) wires become shaped like ribbons curled about the wire axis, Fig. 1. At a suggestion from the author, they rationalized the development of these micro-structures by considering the orientation of the slip systems in the [011] texture formed by the wire drawing. It is shown in this paper that marked departure from axially symmetric flow of grains is also observed when polycrystalline aluminum is severely compressed. Again the explanation must lie in the orientation of the slip system in the [011] texture, which is formed in fcc metals by compression.' THEORY A simple quantitative argument will be presented to show that the development of these microstructures is a result of flow on the combination of slip systems for which the minimum amount of mechanical work is expended in producing a unit tensile (or compressive) strain. First it must be realized that the macroscopic strains of a crystal resulting from slip are given by: where d dy, and dc, are normal strain increments parallel to the x, y, and z reference axes; are crystallographic shear-strain increments on slip systems

Jan 1, 1964