By Wayne S. Cavender

The geochemical association of arsenic and gold in epithermal precious metal deposits of the Basin and Range province is well documented, and in this paper I wish to discuss the evaluation and utilization of this element association for geochemical gold exploration. In 1961-62, I conducted an exploration program on lands controlled by Getchell Mine, Inc, and centered about the Getchell gold mine itself, Besides exploring for new gold deposits, the program was to evaluate these lands for potential deposits of any type; thus, a multi-phase program encompassing a number of exploration methods was conducted. I shall not elaborate on the process of designing the program or of integrating the various methods, but for gold exploration, geochemical methods were determined to have the best potential. This paper is based on that effort. Figure 1 shows the exploration area, which covers the northern half of the Osgood Mountains in eastern Humboldt County, Nevada. The Getchell $line is on the east flank of the range and is about 40 miles northeast of Winnemucca.

Jan 1, 1964

INCREASING realization that pouring and ingot-mold practices involve many factors of fundamental importance to ingot quality and general steel-mill operations has caused these phases of steelmaking to become major concerns of operators and metallurgists engaged in control of quality and costs. Methods of pouring steel from the ladle into the ingot molds have some direct effects on ingot quality. The mold itself governs solidification and dimensions of the ingot and in so doing exerts some very tangible influences not only on ingot quality but also on product yields and general steel-mill processing. In addition, practices are employed in the handling of molds during daily open-hearth operations that are important to quality and production costs. Therefore, pouring and mold practices must be considered highly specialized and important steps in steel-mill operations. MOLD DESIGN Mold design is difficult to discuss in a precise manner because it varies greatly throughout the industry, both in theoretical concepts and practical application, and few well developed data are available. Most ingot molds are designed to meet conditions peculiar to a given plant wherein quality standards are dictated by end-use requirements, which may differ considerably even for the same grade of steel. The mold designer must also consider the equipment available to process ingots and the product obtained from them. Such equipment, used for stripping, heating, blooming and finishing operations, is seldom, if ever, exactly the same in any two steel plants. Thus, pronounced contrasts in mold designs can be expected to continue, even among plants making strictly comparable types of product, particularly because some producers are just beginning to realize the benefits possible from specialized designs. Certain fundamentals are used in mold design but even these

Jan 1, 1964

By G. V. Raymor, James T. Waber, I. Rex Harris

The lattice parameters of a series of fcc alloys of cerium and thorium were measured at 93 " and 298OK. Lattice parameters were also estimated for 171OK. Substantial deviations, y, from Vegard's law were observed. Although y was negative at the two higher temperatures, it was positive and large at the lowest temperature. A variety of models, which have been proposed in the past, were considered, and the calculated values of y were compared with the observed values. The best agreement was achieved with values computed with Friedel's equation. THE purpose of this investigation was to determine the effect of temperature on the lattice parameter and on deviations from Vegard's law of Ce-Th alloys. A large negative deviation from Vegard's law was first observed independently by Weiner, Freeth, and Raynor' and Van vucht2 in the room-temperature lattice parameters of Ce-Th alloys that form a continuous series of solid solutions. This observation was confirmed by Evans and Raynor. The allotropy of unalloyed cerium was reviewed recently by Gschneidner, Elliott, and McDonald. In two subsequent papers,5" these authors reported the influence of various alloying additions on the y= transformation, which occurs below room temperature. Although other rare earths tend to stabilize the double-hexagonal phase, thorium, plutonium, and scandium as solutes tend to stabilize the normal fcc phase. With addition of sufficient thorium as a solute, there is evidence that the formation of is suppressed and it becomes possible to pass continuously with decreasing temperature from the room-temperature phase to the fcc a phase. Thus there is a closed loop which is similar in many ways to the y loop well-known in ferrous alloys. A closed field also occurs in the pressure-temperature "equilibrium" diagram of unalloyed cerium. Because of interest in the effect of thorium additions and their influence on the a and phases, lattice-parameter measurements were made at low temperatures on the fcc phase for a series of alloys ranging from 10 to 90 at. pct Th. The results obtained at three temperatures are shown in Fig. 1. Evans and Raynors analyzed the deviations from Vegard's law in Ce-Th alloys in terms of changes in the occupancy of the 4f electron level in cerium,

Jan 1, 1964

By R. E. Hanneman, A. N. Mariano

In conjunction with the need for accurate volumetric data in the Fe-V system for subsequent use in calculating the high-pressure diagrams, room- and high-temperature X-ray diffraction measurements have been carried out. No previous measurements have been published on lattice parameters or volume changes associated with the a transformation for Fe-V alloys. The existing literature on lattice-parameter data for the a and s phases has been reviewed by pearson1 with considerable uncertainty indicated in the data. In order to obtain a good estimate of ?Va-? for thermodynamic calculations of the a D ?(bee D fee) phase stability, high-temperature vacuum X-ray diffraction measurements were made on an Fe-V alloy of 0.92 wt pet V. The term ?Va-? is the difference of molar volumes of the limiting solubilities of the a and y phases at any given temperature; these values can be calculated readily from the appropriate lattice-parameter data. The equipment used was a commercially available MRC (Materials Research Corp.) high-temperature X-ray camera which was fitted to a Norelco diffractometer

Jan 1, 1964

By M. E. Wadsworth, K. J. Richards

The oxidation rates of tantalum in various partial pressures of carbon dioxide in the temperature range 700°to 950°C were measured with a thermo-gravimetric balance. Oxidation involved a surface -controlled reaction associated with the formation of a nonprotective layer of Ta2O5. Below about 720°C, there was a change in the rate-determining mechanism, and above 830°C the linear rate was preceded by a complex region of nonlinear oxidation behavior. The linear oxidation of tantalum has been explained quantitatively in terms of carbon dioxide adsorption, followed by a rate-controlling surface reaction. The initial adsorption has been expressed both as an equilibrium process and as a steady-state reaction. The enthalpy for chemisorption of CO, was determined to be -17.3 kcal per mole. The surface-controlled reaction had an activation enthalpy of 40.4 kcal per mole. A considerable amount of interest has been shown in recent years in the oxidation of tantalum and the nature of the oxide film produced. This interest is associated with the increasing demand in our technology for structural materials to withstand high temperatures and corrosive atmospheres. The low oxidation resistance of tantalum has severely restricted its application as a high-strength, high-temperature material. As a fundamental approach to the realization of the full poten- tials of this metal, the kinetics of the oxidation of tantalum in oxygen and air have been extensively studied; however, very little work has been reported on the effect of other gases, including carbon dioxide. According to Miller,' the only reported study of the reaction between tantalum and dry carbon dioxide is a restricted observation by O'Driscoll et al.2 at 8 atm absolute pressure and 500°C. Therefore, this study was made to investigate the reaction of tantalum with carbon dioxide. EXPERIMENTAL MATERIALS AND METHODS The vacuum-annealed tantalum used in this study was obtained from Fansteel Metallurgical Corp. as 0.025-mm-thick sheet stock. This material had less than 0.1 pct total impurities, and the maximum individual impurity concentrations were

Jan 1, 1964

THE refining period of an open-hearth heat blends imperceptibly into the finishing period, during which final adjustments are made in slag composition, in bath action and temperature, and in composition of the steel, in order to prepare it for casting into ingots. Operations must be governed by the consideration that alterations in the character of the heat during the finishing period must be held to a minimum. In a broad sense, the finishing and deoxidation period of a heat may be said to be- gin when the action of the last ore addition has ceased, and to end when the teeming of the ingots is completed. INGOT STRUCTLIRES A survey of the relative advantages and disadvantages of different types of ingot structure is required because deoxidation treatments during the finishing period control the amount of gas evolved during solidification and consequently determine the type of ingot structure. Four classes of ingots are recognized, de- pending upon the degree of deoxidation to which the steel has been subjected. These types are killed, semikilled, capped, and rimmed; typical examples of their structures are represented by ingots 1, 2, 5, and 7, respectively, of Fig 9-1. The actual ingots from which these cross sections were sketched were all poured to the same height (indicated by the dotted lines) in the same type and size of bottle-top molds. The eight drawings of the figure represent selected types of ingot structure in a continuous series from "dead killed" to "wild," resulting from variations in the total quantity of gas evolved, from none at all to copious amounts, during solidification of the steel in the mold. Killed and semikilled steels are adjacent at the "quiescent" end of the ingot structure series where only small amounts of gas are evolved. The term "quiescent" describes the action of the molten metal during and subsequent to the teeming of killed and semikilled steels. Capped and rimmed steels are adjacent at the

Jan 1, 1964

By R. D. Carnahan, J. E. White

ThE use of strain gages in the measurement of microplastic behavior of materials is well-known.'-3 Recently it has been suggested that similar techniques might be useful for determining stress relaation. It is the purpose of this report to comment on the use of strain gages in the measurement of strains in the vicinity of 10"6. We will also discuss observations of an anomalous anelastic behavior apparently associated with small temperature changes, which accompanies the unload portion of a load-unload microstrain test. The key to successful strain determinations at levels below 1 pin. per in. is a good gage-mounting technique and either precise ambient temperature control or a set of matched temperature-compensated gages. The importance of good mounting cannot be overemphasized, for example, as in the use of Eastman 910 contact cement. If the cement layer is not sufficiently thin and properly hardened, it is possible to observe anomalous negative stresses when small loads are removed, which relax back to zero in an orderly way with time. Such anomalous behavior, thought to be due to gage bonding, has been reported in microstrain experiments by Thomas and verbach' who observed a negative strain of -3 X lo-' upon unloading. This kind of behavior severely limits the over-all strain sensitivity which can be achieved in such tests. The relaxation of a small positive strain subsequent to unloading in a load-unload experiment is quite normal, however, and is to be expected. The occurrence of an apparent negative strain is also encountered in those instances where the elasticity of the bonding cement is exceeded—for example 0.5 pct or 5000 pin. for cured Eastman 910. An elastic strain of this magnitude can be encountered during load-unload type testing particularly in higher-strength materials (-150,000 yield strength). During the course of microplasticity studies on pure nickel and nickel alloys,' the authors have made the following observation. In a four-point bending test, two active gages are mounted one on each side of the beam as arms R1 and R z of a conventional strain-gage bridge circuit shown in Fig. l(a). This technique provides two advantages: the sensitivity is doubled because R1 and Rz experience opposite strains and temperature compensation is provided automatically because any ambient temperature change would cause both gages to see a strain of like sign whose signals would cancel in the circuit.

Jan 1, 1964

By E. S. Cheney

The sandstone-type uranium deposits of the Gas Hills occur in the arkosic, lower Eocene Wind River formation on the southern edge of the Wind River Basin. The d S34 values of pyrite cement associated with uranium mineralization are-significantly lighter than values for syngenetic-diagenetic pyrite nodules, therefore the H2S responsible for the precipitation of the epigenetic pyrite and uraninite was produced [t]epigenetically. These values are much lighter than the values of H2S from neighboring oil fields. The presence of biogenic pyrite in meta-igneous Precambrian cobbles indicates that these cobbles are not remnants of former; vein-type uranium deposits.

Jan 1, 1964

By Maurice E. Peloubet

This discussion of accounting will describe the statements and the information that the accounting system produces, from the point of view of those who use such systems rather than of those who prepare them and who do the detail and technical accounting work. In any well organized mine, quarry, or other enterprise exploiting a mineral deposit, no matter how small, some clerical and accounting work must be done. Miners and other employes must be paid, supplies must be purchased and issued, and various tax and information returns, which even the smallest enterprise must file, have to be prepared. In this chapter it is assumed that the enterprise has employes of this type and that they understand the fundamentals of record keeping and accounting. It would be impossible here to give sufficiently full explanations to enable a man with no previous clerical and accounting training to set up and operate an accounting and cost system for even the simplest extractive operation. Rather, we shall hope first, to tell the investor and the operator, from the chief engineer or president down to a subforeman, what to expect from the accounting statements and records and how to use this information in his daily work; and second, that it will enable the man with some knowledge of accounting or book- keeping, but with little or no experience in any extractive industry, to set up and operate a satisfactory system for a mine or other extractive enterprise. For readers who wish to go further, the bibliography at the end of this chapter contains many references. T he emphasis has, therefore, been placed on the statements to be produced and the purposes for which they are to be used rather than the underlying books and records. These are, with a few exceptions which will be described later, essentially what might be found in any industrial enterprise and would probably, in the extremely small enterprise, consist of handwritten journals, ledgers, analysis books, payroll books, and stores ledgers. In the larger enterprise, various types of mechanical accounting would be introduced in proportion to the complexity of the operation.

Jan 1, 1964

By Niels Hansen

Dispersion-strengthened sintered aluminum products are normally manufactured from surface-oxidized aluminum powder, SAP,' or from atomized aluminum powder.' The powder-blending technique consisting in mechanical mixing of the constituents has been used in the manufacture of numerous dispersion-strengthening alloys, but has never been successfully applied to aluminum alloys. This technique may, however, be applicable if it is possible to produce an unagglomerated mixture of the constituents in the form of fine powders, and the present study was initiated to test this assumption in the aluminum/aluminum oxide system.3 Table I lists the two grades of aluminum powder and the aluminum oxide powder used in the manufacture of the alloys. MD 105 A is an aluminum powder with an average grain size less than 5 IJ., which is isolated from the MD 105 powder by centrifugal separation in cyclohexanol. The aluminum powders and the aluminum oxide were blended in a high-speed blender and then subjected to cold compaction and hot compaction at 550" to 600°C. Subsequently the compacts were hot-extruded with an extrusion ratio of 15 to 1. The alloys were evaluated by tensile testing at room temperature and at 400°C, microscopic examination, and heat treatment at 500°C followed by tensile testing at room temperature. For the purpose of comparison, a commercial SAP quality supplied by Swiss Aluminium Ltd. was tested in the same manner. The tensile data at room temperature and at 400°C are plotted in Figs. 1, 2, and 3 as a function of the weight percent of oxide. The oxide content

Jan 1, 1964

Jan 1, 1964

IN the early period of steelmaking, ingot structure and segregation were of no practical importance. Crucible melting required very small ingots that gave little segregation, and a small inserted hot top prevented pipe. As larger ingots were poured from bessemer converters and open-hearth furnaces, segrega- [ ] tion, piping, and gas evolution became increasingly important. The techniques of making semikilled and rimmed ingots were developed with little knowledge of the actual mechanism of the process. The first studies of solidification were made by the Brearleys1 and Gathmann,2- who used stearine to show the effects of shrinkage and mold shape. Fig 11-1 is a picture of a series of stearine ingots at various stages of solidification. These studies showed that the liquid solidifies at a nearly uniform rate from the sides and bottom of the mold and demonstrated the formation of

Jan 1, 1964

By Erle C. Donaldson

A study of subsurface waste disposal in the United States shows that in eight States a wide variety of industrial wastes are being injected into formations ranging in age from Precambrian to Recent. More than 30 wells ranging in depth from 300 to 12,000 feet are used for waste disposal into subsurface formations which include unconsolidated sand, sandstone, vugular limestone, and fractured gneiss.

Jan 1, 1964

By Rex B. McLellan

A simple model for dilute interslitial solid solutions is set up which enables a solubility equation for the equilibrium between the solid solution and the gaseous solute to be deduced. This solubility equation is used to estimate the partial thermody -namic functions of Ag-O and Fe-N dilute interstitial solid solutions from the measured equilibrium between these solutions and the gas phase. It is shown that the partial excess entropy of the solute atom in solution is a vibrational entropy which is due Principally to the oscillation of the interstitial atom and does not arise from electronic or elastic interaction between the solute atoms and solvent matrix. In this work measurements of the equilibrium between dilute solid interstitial solutions and a gaseous phase are used to deduce the important thermody-namic functions of the solid solution with the aid of a theoretical solubility equation formulated from a knowledge of the thermodynamic functions of the gas and a simple model for the solid solution. The quantity of principal interest which is deduced from the equilibrium data is the change in vibrational entropy occurring when a solute atom (u) is placed in an interstial site in the solvent (u) lattice. This paper forms part of a more general study in which the properties of condensed phases are deduced from measurements of the equilibrium between the condensed phase and a gas. Previous investigations have dealt with the equilibrium between krypton and liquid metals,' a pure metal and its vapor,' and dilute substitutional alloys and the vapor,3 and the subject has been popularly reviewed by McLellan.4 In the latter investigation3 the vapor pressures of very dilute Cu-Ag and Cu-Au alloys were measured with a Knudsen cell technique over a large range of temperatures and the analysis of the vapor-pressure data showed that the relative partial excess entropies were large and positive [ds= -Sudk = 30 for Au-Ag alloys and 150 for Cu-Au alloys; these values should be compared to unity, the value assumed for these exponentials in the quasi-chemical theory of solutions]. For many interstitial solutions experimental data is available for the equilibrium between the solution and a gaseous phase, and this can be used to deduce the vibrational entropies of the solute atoms in solution. The general method employed is to calculate the chemical potential of the solute atoms in the gas and equate this to pi, the chemical potential of solute atoms in the solid, which is deduced from a simple model set up for the dilute interstitial solution (in which the solute atoms act as bound oscillators in interstitial sites). This enables a theoretical solubility equation to be set up. In the case of Ag-O and Fe-N solid solutions the solubility c, is found to vary with temperature according to a relation of the type, where PU2 is the pressure of the O2 or Np molecules. Essentially, the theoretical solubility equation enables the parameter A(T), which gives the vibration entropy, and the parameter AH, which gives the energy of solution of a solute atom, to be estimated from the measured variation of solubility with temperature. The solutions treated are dilute enough to enable solute-solute interactions to be neglected so that the partial energy and excess entropy of solution E, and GS are not functions of composition and the configurational entropy is that of a random solution. Large positive values have been found for sxSu this quantity has not been given sufficient consideration in recent work on interstitial solutions and it is felt that the partial thermodynamic quantities of very dilute solutions should be understood before the thermodynamics of concentrated solutions can be fully appreciated. EXPERIMENTAL DATA 1) The Silver-Oxygen System. The measurements of Steacie and Johnson,= using silver foils, indicate that there is a pronounced minimum in the solubility vs temperature curve for O-Ag solutions. Eichenauer and Miiller6 have recently redetermined the solubility of oxygen in silver using a method developed in the investigation of metal-hydrogen systems.7 The solubility determinations were carried out on compact specimens of differing shapes and sizes and the results indicate a much lower solubility than was obtained by Steacie and Johnson with no minimum at 400°C. Subsidiary experiments showed that the erroneous results of Steacie and

Jan 1, 1964

Three main divisions of the. Proterozoic are recognised in the North- West of Western Australia. These are referred to, in order of decreasing age as the Mt. Bruce Supergroup, the Bresnahan Group and the Bangemall Group. The stratigraphy and distribution of each is described, their relative ages discussed and a brief geological history of the whole area is Presented.

Jan 1, 1964

By Irving Cadoff, Jack Medoff

THE linear thermal expansions of oriented single crystals of zinc were measured in the range from 20" to 416°C using a Leitz HTV optical lever differential dilatometer. The single crystals, supplied by Dr. J. J. Gilman, General Electric Research Laboratory, Schenectady, N.Y., were prepared from 99.999 pct-purity zinc, and were in the form of rods approximately 2 in. long by 0.15 in. in diameter having the following orientations: x = 1.5, 12, 20, 30, 37.5, 49, 60, 73, and 82 deg where x is the angle between the specimen axis and the (0001) plane of the crystal. From the family of expansion vs temperature curves, the instantaneous expansion coefficients were calculated at 100°C intervals, and Fig. 1 shows a plot of these derived coefficients for each orientation. Coefficients were obtained from the raw data using the chord-slope method. The curves in Fig. 1 indicate a positive temperature coefficient for low x, a negative temperature coefficient for high X, and an expansion coefficient invariant with temperature, amounting to about 43 x 106, for a crystal orientation of approximately 52 deg. From the available data, it is possible to arrive at the values for the axial thermal-expansion coef- ficients a, and a, by extrapolating the curve of the expansion coefficient vs orientation to zero and 90 deg orientations. More precise values for a, and a, are obtained if the instantaneous coefficients are plotted against the square of the cosine of the orientation angle, as shown in Fig. 2. The extrapolated terminal points of the best straight line through the data points of such a plot define the axial coefficients at that temperature. The theoretical justification for the linearity of this curve comes from inspection of a rearranged form of the general anisotropic equation for expansion: ax=a, + (a, -a,)cosZx [1I in which a, is the expansion coefficient in the "c" or [0001] direction and a, the expansion coefficient in the "a" or [ll50] direction. From Fig. 2, the axial coefficients at 100°C, for example, were found to be a, = 13.9 x 10'6 and a, = 62.4 x 10"6 per "C. In the same way, the coefficients were determined for 20", 200°, 300°, and 400°C. This data is summarized in Fig. 3. It is of interest to observe the common intersection of the curves in Fig. 3, which seems to bear out the earlier observation, from Fig. 1, of a

Jan 1, 1964

By L. U. Spellman

Atlantic Cement Company's new multimillion dollar, 10,000,000 barrel per year cement plant went into full operation in February, 1962, bringing into reality a new concept in the distribution of Portland cement. The Cerro and Newmont Mining Corporations, well established in the mineral extraction and dressing industry, backed the venture. To take advantage of the, economics inherent in single production units of large capacity, it was necessary to first find a market' capable of absorbing such large quantities. Cement can be economically shipped by rail and truck about 200 miles. Beyond' that radius from the producing facility the freight costs become prohibitive. No single marker area within that radius exists which could absorb such a large volume of cement. However, water transportation provides a relatively inexpensive method of transporting bulk products many times over such a distance. Thus, it was decided to locate the producing facility near a deep water port which had ready access both to the Atlantic Ocean and, just as important, a good source of raw material. An extensive feasibility study was made and the site at Ravena, New York on the Hudson River near Albany was chosen. Here, vast quantities of limestone in the foothills of the Catskill Mountains are found within a short distance of-the deep-water Hudson River.

Jan 1, 1964

THE solid nonmetallic inclusions present to some extent in all commercial steels have been variously designated. In early references they were usually called slag inclusions, and this terminology is still retained to some extent. On the premise that all nonmetallic matter produced in a metallurgical process is slag, this can be justified. We have come to think of slag, however, in a more restricted sense, and calling these particles slag inclusions is further objectionable because it fosters the erroneous concept that they are actually incorporated portions of furnace slag. Rarely is this true. The term sonims (coined from solid nonmetallic impurities) was proposed many years ago but never came into common use. In general, the term non-metallic inclusions seems to be satisfactory and adequate. NATURE AND CONS1lTUTION OF NONMETALLIC INCLUSIONS From the standpoint of origin, inclusions fall naturally into two classes: (1) those occurring as a result of reactions taking place in the body of molten or solidifying metal and (2) those resulting from mechanical incorporation of refractories or other materials with which molten steel comes in contact. The former are by far the more numerous and have been called indigenous, natural, or native inclusions. The latter are by their very nature sporadic in occurrence and have been called exogenous, accidental, adventitious, or foreign inclusions. They are often referred to as the "slag-stringer" type, though here also the material is not likely to be furnace slag. Substances Found in Inclusions. Nonmetallic inclusions are composed principally of oxides and sulfides but carbides and nitrides sometimes play an important role. In the case of indigenous inclusions the reactions by which these particles are precipitated from molten or solidifying steel may be caused by: (1) oxidation such as may occur during refining or during tapping and teeming, (2) deoxidation by added alloys, (3) change

Jan 1, 1964

By W. G. Fischer

Basic laboratory tests on trona and the surrounding shales initiated the Rock Mechanics program. The stress-strain curve, modulus of elasticity, Poisson's ratio, the uniaxial rock strength, Mohr's envelope, the biaxial stresses at failure, and creep were investigated. A series of underground problems were then approached using this information and various field measuring devices, most of which were developed by the Bureau of Mines. Initially, stress concentrations near mine openings were evaluated using the stress relief technique. This required an accurate determination of the pre-mining stress field. Later, stress concentrations associated with the cave line were studied. After about 30 stress reliefs over an appropriate time interval the effects of one type of mining could be compared against another. The microseismic technique was used to investi- gate a possible application of warning devices near the cave line. A study of mine reorientation was made. Problems related to the shape and size of pillars and barriers were studied. The effectiveness of roof bolting patterns was examined. Control of roof stresses was attempted. A new system of mining in heavy ground has been developed using the information secured in the Rock Mechanics program. Without this system, mining in more than one instance would have been next to impossible. Indeed, from this one discovery alone, the Rock Mechanics program has paid off in improved safety as well as in dollars. The Westvaco trona* mine is located near the town of Green River in the southwestern corner of Wyoming. It is owned and operated by FMC Corp. on land leased from the US Government, the State of Wyoming, and the Union Pacific Railroad. A conventional room and pillar system is being used, (Fig. 1) with complete removal of the pillars during final mining. Return air bleeders surround

Jan 1, 1964

By Roger A. Gregg, Barry J. Piearcey

MANY of the nickel-base superalloys developed recently for use in the as-cast condition exhibit a massive "white-etching" constituent1 in the inter-dendritic regions. Commercial alloys in this category are SM 200,* IN 100, INCO 713, and Nicrotung. The appearance of a similar microconstituent in nickel-rich Ni-A1-B alloys has been reported by Schijbel and Stadelmaier. Their investigation revealed that this constituent was the binary eutectic of the terminal nickel-base solid solution and the inter metallic based on Ni3A1. This binary eutectic is degenerate and NhA1 is the major phase. At lower temperatures the eutectic composition lies within the NkA1 phase field and under equilibrium conditions is single-phase NisAl. Taylor and F&apos;loyd3 have shown that in Ni-Al-Cr alloys containing at least 8 at. pct Cr, liquid compositions which solidify by the eutectic reaction in the nickel-rich portion, precipitate nickel-base solid solution and NiAl rather than nickel-base solid solution and NkA1 in the binary Ni-A1 system. Since the nickel-base alloys contain chromium in excess of 8 at. pct and are further alloyed with one or more of the elements titanium, cobalt, molybdenum, or tungsten, it is possible that the eutectic could contain NiAl rather than NisAl. In addition, Benson4 has reported that in low-nickel austenitic high-temperature alloys, which possess Ni/(Al + Ti) atomic-weight ratios <18.0, the Ni (Al, Ti) phase may precipitate from the melt during solidification. Since SM 200 and similar high-temperature materials were developed from alloys which were designed for solution treatment, the appearance of a eutectic would indicate that the limit of solid solubility has been exceeded. The purpose of this note is to confirm that the massive white constituent in the complex nickel-base alloys investigated is based on the binary eutectic Ni + NbAl and that the limit of solid solubility need not be exceeded to produce it, in common with other observations of cast alloys. Successive polishing of a sample of SM 200 showed that, in agreement with Schobel and Stadelmaier, particles of the constituent were spherulitic and in particular were a) situated between cored dendrite arms, Fig. 1, and b) nucleated at the surface of dendrites, Fig. 2. The Ni/(Al + Ti) atomic-weight ratios for the nickel-base alloys which were observed to contain the massive eutectic constituent in the interdendritic regions are 12.1 (Nicrotung), 9.2 (IN loo), 19.5 (INCO 713), and 14.5 (SM 200). However, the results of X-ray analysis of these alloys in the as-cast condition failed to reveal the presence of the Ni (Al, Ti) phase. An electron microanalyzer was therefore employed to analyze the composition of this constituent in SM 200. The results of analyses of representative particles are as follows5: 8.4 at. pct Ti, 8.8 at. pct Co, 5.5 at. pct Cr, 0.9 at. pct W, 12.8 at. pct Al, and 63.6 at. pct Ni. Assuming that

Jan 1, 1964