Search Documents

By Harold W. Lipper

Helium production and shipment reached new peaks in 1.361. The Bureau of Mines produced 727 million cubic feet, 13 percent more than the 1960 record, and shipped 552 million cubic feet, 16 percent more than the 1960 record. Production exceeded demand for the third successive year, enabling the Bureau of Mines to add 174 million cubic feet to the volume stored underground for future use. At the end of 1961, the total volume of helium in underground storage in the Clifside gasfield was 44-7 million cubic feet. Contracts to implement a long-range helium conservation program were completed with four companies, obligating all the contracting authority of $47.5 million a year made available by the Congress. The four companies will finance, build, and operate helium extraction plants to recover from natural gas an annual average of 3.1 billion cubic feet of helium that would ordinarily be wasted when the helium-bearing natural gas is used for fuel.

Jan 1, 1962

By T. P. Meloy

The behavior of slime-sized particles in a flotation cell is neither well documented nor well understood. In general, slimes (or 'fines' as they will be alternatively called in this chapter) have been either ignored, eliminated, or treated empirically. Recently, however, some good experimental and theoretical work has been done that leads qualitatively to a clearer understanding of the problems involved. Fines are small particles that, owing to their smallness, behave differently from larger particles of the same material. The smaller the particle, the larger is its surface-to-mass ratio. The difference in the surface-to-mass ratio for a micron-sized particle and a centimeter-sized particle is 10,000 to 1. For our purposes we shall arbitrarily define any particle less than 10 µ 10-3 cm) as being a fine. This is generally considered the upper limit of colloidal-sized particles. Recently, the field of colloidal chemistry has successfully used the concept of the double layer to explain dispersion and flocculation of fine particles in a static system. Flotation, however, is a dynamic system due both to the turbulence of the liquid and to the coursing of the bubbles through the cell. Further more, a flotation system is a heterogeneous system in which there are a number of different types of particles which interact with one another. A further difficulty is that no two flotation systems are the same for minute quantities of a variety of common chemicals will alter the behavior of the system. These reasons make reproducible experimental results that can ex- plain fine-particle behavior difficult to obtain. In spite of these experimental difficulties, millions of tons of ore containing a large amount of fines are successfully floated every year. For example, at the Morning mill of American Smelting and Refining Co., a galena concentrate that was 42% -6 µ and a sphalerite concentrate that was 33% -9 µ were floated leaving a tailing that was 27% - 9 µ.l Ores that contain fines can generally be divided into two classes. In the first are those in which the valuable mineral tends to slime, such as galena and hematite. In the other class, one or more of the gangue minerals forms the slime; a typical example is barite. Though the problems due to the presence of fines are often the same in handling the two classes of ore, the method of handling them is different because of economic considerations. Nonmetallic mineral flotation is particularly affected by slimes, by either slime-coating effects or excessive reagent consumption. Though a given gangue mineral may not float under the conditions prevailing in the flotation cell, it may still be able to adsorb the collector. I£ it also slimes, a significant

Jan 1, 1962

By D. R. Miller

Internal friction and elastic modulus variations in electrorefined titanium, iodide refined titanium, and alloys of the latter material with oxygen, nitrogen, aluminum, and zirconium were investigated. No oxygen peak was detected with electrorefined titanium but, provided precautions were taken to prevent increases in background damping, an oxygen peak at about 410°C could be resolved with each of the other materials. An additional partially resolved peak was observed at 500°C in a Ti-N alloy. An anomaly in the variation of rigidity modulus with temperature was observed. Possible mechanisms for the formation of any oxygen peak have been discussed. PRATT, Bratina, and Chalmersl investigated the internal friction of commercial purity titanium and alloys of this material containing 1.5, 3.5, and 4.5 at. pct O. With commercial titanium the internal friction curve consisted of two components, a background which increased steadily with temperature and a peak at about 600" C which was due to grain boundary relaxation. In the Ti-O alloys, however, an additional internal friction peak was observed at 430" to 450°C and, since this peak increased in height as the oxygen content was increased, it was thought to be associated with the presence of oxygen. The diffusion of oxygen in titanium at temperatures between 300" and 500° C is believed to have marked effects in its tensile properties2'3 and the present internal friction measurements were undertaken to obtain further information on this diffusion, using material of higher purity than that of Pratt et d. and an apparatus of very much greater sensitivity. In the course of the investigation a number of important limitations on the work of Pratt et al. were revealed and results have been obtained which emphasize the need for ensuring that in this type of experiment, internal friction is independent of strain amplitude and that the values obtained are reproducible. 1) MATERIALS AND APPARATUS The basis material from which the majority of the specimens was prepared was iodide-refined titanium, the major impurities in which were oxygen and nitrogen—the metallic impurities being present at concentrations less than 0.001 at. pct. The hardness of this material after arc melting, forging, and swaging to rods 1/4 in. diameter was Dph = 110. Specimens 10 in. long and 0.020 in. (0.51 mm) diameter were prepared from these rods by further swaging and wire drawing and were finally annealed in vacuo (5 x 10-6 mmHg) for 24 hr at 800°C. The oxygen alloys were prepared from iodide-

Jan 1, 1962

By T. J. Koppenaal, M. E. Fine

The critical resolved shear stress of aCu-A1 single crystals has been investigated as a function of composition, testing temperature, and strain rate. The strength, and its temperature and strain rate dependency increase markedly with aluminum content. The solid solution strengthening at 4.2°K is much larger than at room temperature. The activation energy for the low temperature dislocation cutting process increases from about 0.17 ev for a 0.5 at. pct A1 alloy to about 0.50 ev for a 14 at. pct A1 alloy. This result is attributed to an increase in the width of extended dislocations due to the known decrease in the stacking fault energy. In addition, the activation volumes at 4.2 and 77°K decrease with aluminum additions. Concerning the solid solution strengthening in the 296° to 373°K range, no definite conclusions are reached, but it is suggested that subgrains and cutting of subgrains are important. In a previous paper,' the authors reported that adding aluminum to copper produces two types of strengthening: a yield point effect and an increase in the lower yield stress. This behavior is illustrated in Fig. 1 by shear stress-shear strain curves of furnace-cooled single crystals of pure copper and Cu-14 at. pct A1. The yield point effect, At, was thoroughly studied previously1 and shown to be associated with short-range order. The present paper reports an investigation of the lower-yield stress in aCu-A1 single crystals as a function of composition, testing temperature, and strain rate. EXPERIMENTAL PROCEDURE Single cryski1 tensile specimens were prepared in the same manner as previously described.l Briefly,

Jan 1, 1962

By C. Z. Serpan, L. J. Wittenberg

The density of liquid plutonium was determined, by a pycnometm'c technique, from 664 to 788°C and exhibited a temperature dependence, which could be expressed as:. P= C17.63 - 1.52 x 10-"t] +0.04 g per cc where t = OC. These density values compare favorably with the values previously obtained by a technique utilizing Archimedes' principle. The apparatus and method were evaluated when the densities 0.f molten tin and bismuth were measured and found to be in agreement with accepted literature values. PLUTONIUM or an alloy of plutonium in the liquid state has been proposed as a fuel for a fast-breeder type nuclear power plant.' Since knowledge of the liquid density of plutonium is required for the proper design of such a system, this study was undertaken. In addition, the density and volume expansion coefficient of liquid plutonium are of interest for comparison with these same properties of the six allotropic modifications of the solid metal. Comstock and GibneyZ were first to report a value for the density of liquid plutonium. The value for only one temperature, 665"C, was calculated from data obtained by the radiography of the meniscus, Fig. 3. Recently, the density at a series of temperatures has been reported by Knight,3 who obtained his values by using a differential volumeter, and by 01-sen, Sandenaw, and Herrik, who obtained their values from measurements of the loss in weight of a tungsten bob immersed in the liquid. The density of liquid plutonium reported here was determined by a vacuum pycnometer method. In an evacuated system, the tips of calibrated tantalum pycnometers were lowered beneath the liquid sur-

Jan 1, 1962

The various functions of public relations are playing an increasingly important part in the activities of the many companies now engaged in oil exploration in Australia.Several of the larger exploration companies, notably West Australian Petroleum Pty.Limited, Ampol Exploration Limited, Caltex Oil (Australia) PtSr: Limited and Australian Oil and Gas Ltd. (and its American Associate Union-Kern), employ staff or consultant public relations specialists. In, most of the other companies now exploring in Australia, public relations are handled within the company, directed from the highest executive level.The object of public relations in.the oil industry is. to create in the public mind an impression favourable to the industry as a whole and'the company -or group of companies with which the public relations officer is associated.

Jan 1, 1962

By J. P. Capp

The Bureau of Mines conducted field-scale experiments in underground gasification of coal with oxygen-enriched air. A path about 140 feet long was linked at the rate of LO feet per day through a coalbed hydraulically fractured with a mixture of starch gel and sand. During the best gasification period, which extended for 2-1/2 days, 785,000 std. c.f. per day of 124-B.t.u. gas was produced. In other periods the heating value at times was almost 300 B.t.u. per std, c.f,, but sustained production of such gas was not achieved. During gasification, a total of 50 tons of coal was gasified and 114 tons of coal was carbonized. Approximately 12 million B, t .u. per foot of nominal path was recovered at the surface.

Jan 1, 1962

By B. A. Rose

Coal is being thermally dried in ever increasing tonnages today. Because of fire and explosion hazards, it is important that drying equipment be designed for maximum safety in operation. It is well then that we review dryer design and operation to bring out those features and operating practices which will provide maximum safety to equipment and personnel. This paper presents the author's views regarding the fundamental requirements for safety and explains the Heyl and Patterson approach to the meeting of those requirements in the design and operation of their dryer.

Jan 1, 1962

By John A. Brooks

The description of a phosphate flotation operation is repeat information for many people, except for variations in flow sheets. This paper is written to show the variations in flows, and to give enough. of the overall flows to allow anyone not familiar with the operation to be able to formulate a fair idea of the operations.

Jan 1, 1962

By Robert Hall

The Lynch Creek beryllium-tungsten prospect was investigated as part of the domestic beryllium resource studies by the Bureau of Mines. This prospect is in the Birch Creek mining district, Lander County, Nev., 9 airline miles south of Austin. A tungsten mine was operated intermittently from 1952 to 1957. Beryl was identified in the pegmatite dikes in 1960, and the lode claims were relocated. No beryl has been produced. Rocks in the area are Paleozoic sediments2 cut by pegmatite and aplite dikes and quartz stringers. Beryl occurs in random pockets, as disseminations throughout the dikes, and in occasional pockets in the quartz stringers.

Jan 1, 1962

The Geograph is a revolutionary seismic system involving special techniques in combining the use of FIT magnetic tape with shock wave echoes created by a weight dropping system.The idea of- weight dropping as a- source of seismic energy is not a new,.,oxie. Records 'indicate òa pos'sihle use of falling weights as early as .1929. 'Dr. Burton McCollum began his experiments in 1938, but it wasn't until 1951 that the method was first proven useful.The first weight dropping crew began commercial operations in Edwards and Sutton .Counties of West Texas in 1953. By 1962, more than '40 weight drop-ping.crews have come into existence with operations in the United States, Canada, Algeria, Iraq, Argent na,òSpanish West Africa, Tunisia, Qatar, Niger Morocco and Libya by most major oil companies and larger independent oil companies. .

Jan 1, 1962

By Merih Celasun

The literature in operations research centered on mineral exploration has been comparatively limited in view of the significant implications of mineral discoveries upon the national economies in general and mineral industries in particular. Much of what has been published is of somewhat unsure academic nature, indicating to a certain extent the scarcity of industrial applications. Mineral exploration activities present quite difficult operational and conceptual problems. The purpose of this paper is to discuss the principal characteristics of decision problems encountered in planning an exploration program, to indicate an optimization approach to a certain class of allocation problems, and to suggest directions for future research effort.

Jan 1, 1962

By Zoltan F. Oszter

The design of belt conveyors is a well-known procedure and related formulae can be found in any handbook dealing with materials handling. Belting and conveying equipment manufacturer's catalogues and design manuals offer a wide range of detailed information which can be applied to most of our conveying problems. The aim of this paper, however, is to investigate the design of a specific type of belt conveyor, namely the long horizontal, or nearly horizontal, type. (The undulating type, with moderate lifts and drops, can also be included in this category.) Most of the long overland conveyors carrying ore from pit to processing plant, or those carrying over-burden to the disposal area, fit this description. A critical appraisal will show that reasonably accurate results can be obtained when tl1e familiar horse-power formulae are applied to this type of conveyor. The progress and new developments in the design of belt conveyors, which have resulted from the extensive research done in the past decade, will also be explored.

Jan 1, 1962

By M. E. Tyrrell

The purpose of the work leading to this report was two-fold: (1) To determine the properties of cemented tungsten carbide modified by the addition of one, two, and five percent of titanium diboride, and (2) to compare the properties of these mixtures when sintered, hot-pressed, and flash-welded (resistance-sintered). Minor additions of titanium diboride to mixtures of 94 percent WC and 6 percent Co decrease mechanical strength but increase oxidation resistance in proportion to the amount of the addition. One percent of titanium diboride increased the hardness by 2 Rockwell A units. Hot-pressing produced compacts with the highest density and the best mechanical strength, but losses of cobalt were high and grain growth was pronounced.

Jan 1, 1962

By Frank B. Fulkerson

Of the about 60 million pounds of aluminum used in the Pacific Northwest in 1960, 40 million pounds or two-thirds was used by 10 companies. One of these companies made airplanes and missiles; one manufactured roofing, siding, and tubing; three produced truck tractors, truck bodies, or truck trailers; two made architectural metal products; one made irrigation and industrial products; one was a general foundry; and one was a shipyard. These companies contributed to regional growth by developing markets outside the area; some have worldwide sales. Aluminum consumption increased at an average rate of 7 percent annually from 1954 to 1960. Airplane manufacture, formerly preeminent in aluminum use, no longer was in first place in 1960. By industrial group, the leading users were manufacturers of building products, 30 percent; airplanes and missiles, 22 percent; truck tractors, truck bodies, and truck trailers; 17 percent; general foundries, 5 percent; ships and boats, 4 percent; mobile homes, 4 percent; other transportation equipment, 3 percent; and irrigation equipment and all other products, 15 percent.

Jan 1, 1962

By H. Brandhorst, C. G. Dunn

THE main purpose of the present note is to provide further information on the effect of orientation on strain-induced grain boundary migration in sheet material. A secondary purpose is to draw attention to the presence of a possible (hkl) dependent surface energy driving force, when the two grains of a bicrystal specimen have different (hk2) planes at the gas-metal interface, and to suggest means of eliminating this effect from the strain effect. If two grains A and B of a bicrystal have specific surface energies ? A and ? B respectively, there exists a driving force for grain boundary migration equal to 2(? B - ? A)/t, where t is the thickness of the specimen.' When t is quite small and the residual strain energy densities €A and €B of grains A and B, respectively, adjacent to the boundary are nearly equal, it is possible that the surface effect may be larger than the strain effect. he difference € B - € A gives a driving force per unit area of grain boundary due to an applied strain.)2 However, with increasing t the surface effect decreases while the strain effect presumably remains constant. Therefore, at some sufficiently large value of t, it is possible to ignore surface energy driving forces.* On the other hand, the surface effect is eliminated for all value of t when both grains have the same (hkl) orientation or have identical values of surface energy. Although the previous study provided information on the effect of orientation on strain-induced erain boundary migration,' no orientations with the (100) plane in the plane of the sheet were included. The present paper provides information of this kind. A seed crystal reorientation technique4 was used to prepare a large bicrystal of silicon iron (3 1/4 pct Si) consisting of two (100) grains in the (100) [001] and (100) [Oil] orientations. After a cold rolling strain (7 pct reduction to 3/4 mm final thickness), small specimens were prepared as before2 and then annealed in hydrogen. The boundary migration was such that the grain in the (100) [011] orientation always grew. After overnight anneals at 1100° or 1000°C, none of the initial (100) [001] grain remained. An anneal of 30 min at 950°c, however, provided information on the start of boundary migration. Fig. 1 shows both the initial position (lower line) and the final position (upper curved line) of part of the boundary, as revealed by thermal grooves. In a different area, part of the final boundary was not revealed by thermal grooves; the rate of boundary migration presumably was too high for the growth front to be defined by the time dependent thermal grooving process. In another area there was a vacated intermediate position connected to the initial position of the grain boundary. This indicates that only part of the boundary

Jan 1, 1962

By F. H. Deily, Jean M. Quets, Milton E. Wadsworth, John R. 222-000-000-012 Lewis, D. S. Rowley, R. J. Howe

Samples of synthetic magnetite were reduced in hydrogen-water vapor atmospheres in the temperature range 450o to 900oC. The reaction was always surface controlled, indicating the final products of reaction are nonfirotective. Three separate cases have been identified from the kinetic results: Case I, reduction of magnetite to iron below 570°C; Case II, reduction of magnetite to iron above 570°C; and Case 111, reduction of magnetite to wustite above 570 oC. In Cases I and 111 the kinetics have been explained by the formation of oxygen anion vacancies in the magnetite surface followed by associated diffusional processes. In Case 11 the observed kinetics have been related to the concentration of iron cation vacancies in the wustite layer formed, followed by associated steady-state diffusional processes. The concentration of cation vacancies in the wustite is maintained constant by the magnetite-wustite equilibrium. THE reduction of the oxides of iron has been a subject of study and interest for many years. However, few attempts have been made to interpret the results in terms of the mechanism of reduction of an iron oxide by either hydrogen or carbon monoxide. Stalhane and Malmberg' using CO, H2, and CO-Hz mixtures, developed the rate expression: where m = mass of oxide reduced, t = time, k = a constant, s = surface area, P = partial pressure of of CO or H,, and P, = partial pressure of the reducing gas at equilibrium. The rate of reaction per unit area was proportional to the difference between the partial pressure of the reducing gas and its pressure at equilibrium. Hansen, Bitsianes, and Joseph2 studied the reduction of pellets of hematite to magnetite with mixtures of CO-CO,. They concluded that below 450°C the reaction proceeded according to a model in which CO reacts with the hematite surface producing an oxygen ion vacancy. The rate controlling step was then assumed to be oxygen ion diffusion through vacancies resulting in the formation of magnetite. They derived an expression giving the rate of reduction proportional to the cO/CO, ratio. Recently McKewan3 published results for the reduction of magnetite spheres in atmospheres below 570°C. He explained his results by an equation of the form where K, is the equilibrium constant for wustite-iron equilibrium attributed to the formation of wustite as an intermediate in the reduction of magnetite. According to McKewan, Kp is an equilibrium constant for H, -HO adsorption in which oxygen is deposited on the surface from the H,Oand subsequently acts as a poison for reduction by hydrogen. Sample Preparation and Experiments. In this work the authors used the same apparatus and experimental procedure employed in the hydrogen reduction of magnetite. Sintered disk samples weighing approximately 1.5 g and measuring 1.2 cm in diameter and 0.25 cm in thickness were prepared by a method described previously.4 Partial pressures of hydrogen and water vapor were controlled by bubbling hydrogen through a series of flasks containing distilled and deionized water maintained at constant temperature in an oil bath. The total flow rate of the reacting gases—hydrogen and water vapor—was approximately 0.5 liter per min. The entire external system was maintained at a temperature above the oil bath to prevent condensation of water vapor. This was accomplished by wrapping electrical resistance elements over all surfaces. The glass column containing the weighing system-a McBain balance suspended from a gold chain-was enclosed in an aluminum tube heated by nichrome resistance wire enclosed in an insulating material. The temperature of the glass column was held constant by means of a series of thermocouples connected in parallel to a Leeds and Northrup temperature controller. This was necessary since variations in temperature resulted in expansion and contraction of the glass column and could be readily observed with the cathetometer. The spring extensions were measured through a window with a gaertner cathe-

Jan 1, 1962

By E. C. Rudolphy, M. E. Potter, J. R. Mitchell

The effects of 0.006 to 0.20 pet Sn ml the hot workability and the annealed mechanical properties were investigated for Types 302, 410, and 430 stainless steel. The hot workability of these steels was not significantly affected by their tin content within the range studied, although some effects on mechanical properties were noted. Apart from the effect of tin, optimum hot-working temperatures and V-notch Charpy impact transition temperatures for these grades were determined. HIGH tin residuals in some heats of stainless steel have been blamed for the poor hot workability, particularly during secondary mill rolling. However, very little quantitative information has been available. Previous work1"6 with carbon steels indicates that tin increases tensile strength and hardness but de- creases tensile and impact ductility. Halley,7 in reviewing the sources and effects of residual elements in carbon and alloy steels, concluded that much of the surface checking (hot shortness) encountered in rolling was caused by copper, and that tin, arsenic, and antimony combined with copper to form low-melting constituents which further increase the steel's sensitivity to hot shortness. These elements had little effect in the absence of copper. A more recent paper by Langenberg and Johnson8 concluded that tin reduces hot workability but that researchers disagree concerning the amounts which will cause trouble. They state that laboratory investigations with small ingots seem to indicate a higher tolerable level of tin than do statistical studies of mill data, and also that statistical analysis of mill data indicate that small amounts of residual tin are detrimental to the surface quality of stainless sheet. The accumulative increase in the general level of tin and other tramp elements in steelmaking materials will present greater problems to steelmakers in the future. The purpose of the present study was to obtain quantitative information on the specific effects of tin on the hot workability and mechanical properties of such common stainless steels as Types 302, 410, and 430.

Jan 1, 1962

By David T. Peterson

Calcium metal was found to deoxidize thorizcm at 1000° to 1200° C. The reaction kinetics were determilled and related to the diffusion coefficients of oxygen in thorium. The solubility of oxygen in thorium, the minimum oxygen concentration, and the diffusion coefficient were determined from 1000° to 1200°C. This firocess results in the lowest oxygen concentrations zohich have been reported for thorium metal. FOR many years it has been known that calcium metal will reduce thorium oxide to thorium metal. This reaction has been the basis for several methods of preparing thorium metal. From the equations giv-by Kubaschewski and vans, ' AF" for the reaction Cao, + Tho,(,) - CaO(,, + Th(,) was calculated and found to be -3.4 kcal at 1000°C, -2.5 kcal at llOO°C, and -2.0 kcal at 1200°c. Thorium is very slightly soluble in liquid calcium, and the solubility of calcium in solid thorium is very low. Consequently these metals would be in essentially their reference states. If thorium containing oxygen were equilibrated with liquid calcium between 1000° and 1200°C, the oxygen content of the thorium would have to be below the solubility limit in thorium. Oxygen is one of the impurities most difficult to remove from thorium and is the most abundant impurity in metal prepared by almost all known methods. Fortunately, oxygen does not have a large influence on the properties of thorium because the solubility in solid thorium is very low. EvenT in thorium containing 100 ppm of 0, particles of thorium oxide can be observed in the microstructure. In view of the incompatibility of thorium oxide and liquid calcium and the low solubility of thorium oxide in thorium, the deoxidation of thorium by this method was investigated. For thorium containing an amount of oxygen well in excess of the solubility limit, the reaction should proceed in the following sequence. The oxygen content of the thorium matrix near the surface would be depleted by the diffusion of oxygen to the surface. At the surface, the oxygen would react with calcium to form calcium oxide. To maintain equilibrium within the thorium, thorium oxide would dissolve to keep the matrix saturated. Consequently, the thorium-oxide particles would disappear first at the surface and then the particle-free rim would grow in thickness. If the rate-controlling step were the diffusion of oxygen through this layer of thorium which was growing in thickness in direct proportion to the amount of oxygen removed, the well known parabolic time law should be observed. If the oxygen concentration at the surface of the thorium and at the inner surface of the deoxidized rim were known, the diffusion coefficient of oxygen in thorium could be calculated from the parabolic rate constant. EXPERIMENTAL PROCEDURE The thorium metal used in this study was prepared by calcium reduction of ThF, by the method described by Wilhelm.' The analysis of this metal is given in Table I. The carbon was determined by combustion, the oxygen by the HC1-insoluble residue method, nitrogen by the Kjeldahl method, and the other elements by emission spectroscopy. A section of this ingot was hot rolled at 600°C to 1/4 and 1/8-in. thick plates. Specimens approximately 7/8 in. square were cut from these plates, and all surfaces of the specimens were cleaned and smoothed by filing with a clean file. Individual specimens were placed in 1-in. diam by 2-in.-long tantalum capsules. Approximately 1 g of clean, high-purity calcium was placed in the capsules and an end closure arc-welded in place. The tantalum capsules were sealed in Inconel crucibles to protect the reactive metals from oxidation. The entire loading procedure was done in a glove box filled with pure argon. The loaded crucibles were placed in a muffle furnace, controlled within 2OC of the desired temperature, for a measured length of time. After the specimen had cooled to room temperature, it was sectioned perpendicular to the large faces and through the mid-point of two of the sides. The sectioned specimen was mounted and polished through Linde A abrasive. The rim which was free of thorium-oxide particles could be clearly observed microscopically as mechanically polished. Twenty measurements of the thickness of the rim were made at equally spaced points far enough from the end of the

Jan 1, 1962

By D. F. Walsh

A study of damping capacity was made on a number of magnesium-base alloys, commercial types and experimental compositions. Hardness and tensile properties were determined, and the microstructure of each alloy was examined. Alloys of low yield strength, in general, possessed high damping ability. A correlation was established between damping capacity and composition.

Jan 1, 1962