By J. B. Clark

An exploratory study of the 60 wt pct Mg and 80 wt pct Mg sections of the solid constitution in the magnesium-rich region of the Mg-Al-Ca-Zn system was undertaken. The objective of the investigation was to determine the general configuration of the phase fields with respect to the magnesium solid solution in this complex system. The 335°C (635°F) tetrahedron was selected for study because the solid constitutions of the bounding ternary systems—Mg-Al-Zn,1 Mg-A1-Ca,2 Mg-Ca-zn3—were well known and, at least in these ternary systems, diffusion was rapid enough at 335°C for equilibrium to be reached fairly rapidly. Metallography and powder X-ray diffraction were selected as the best corroboratory methods for determining the solid phase equilibria. A total of forty-six quaternary alloys on the 60 wt Mg and 80 wt Mg sections were prepared, annealed to equilibrium at 335°C, and the phases present identified. Singly sublimed (99.99 pct) magnesium, electrolytic (99.99 pct) zinc, high-purity (99.99 pct) aluminum, and USP calcium were alloyed in graphite crucibles under a chloride flux and chill cast into a split graphite mold. Alloy samples were sealed under argon in Pyrex vials and annealed at 335°C ± 1/2° for a minimum of 500 hr. At the conclusion of the anneal, the alloy samples were quenched rapidly in ice water. Standard metallographic procedures for magnesium alloys were used. Powder X-ray diffraction patterns were taken on a G. E. Camera with a diameter of 14.32 cm using nickel filtered copper radiation. The phase equilibria in the 60 wt pct Mg section of the 335°C (635°F) tetrahedron is shown in Fig. 1. The complex equilibria in the zinc-rich region were not accurately determined and are shown only tentatively with dotted lines. The equilibria of the three bounding ternary 335°C sections from pure magnesium to 60 wt pct Mg are also shown as though folded away from the tetrahedron. The 80 wt pct Mg section has the same configuration of phase fields as that shown in Fig. 1. Thus it is reasonable to conclude that in higher magnesium sections, the same relative configuration of phase fields is maintained though the relative proportions of the individual phase fields may change slightly as the magnesium solid solution is approached. Note that all the ternary phases present in these ternary diagrams enter into the quaternary equilibria with the exception of the phase of the Mg-Al-Zn system which becomes unstable with the addition of as little as 1/2 pct Ca. No quaternary intermetallic phases were found. No liquid phase was detected in any of the quaternary alloys annealed at 335°C suggesting that if a quaternary eu-tectic exists, it must lie between 335°C and 339°C, the temperature of the ternary eutectic in the Mg-Al-Zn system.

Jan 1, 1962

By D. L. King, B. A. Schepman

A number of unique thickener mechanism designs with the operating results achieved in various installations are discussed. These unusual designs include new types of raking arms, lifting devices, and feed-wells employed to obtain higher underflow densities and minimum operator control or improved overflow clarity. Several installations of large thickeners in which the underflow lines pass upward through the center to eliminate tunnels are reviewed. The location of the lines and pumps with the maintenance and operating records are included. Several types of automatic lifting device controls are used to provide storage in the thickener. Some of the installations employing underflow density controls are achieving excellent operating results. Thickeners or sedimentation basins are used in minerals beneficiation plants for three basic purposes. These are 1) Concentration, or to raise the density of a liquid-solids slurry. 2) Clarification, or removal of finely divided solids from a slurry. 3) Hydroseparation, or removal of a specific fraction of solids from a slurry. The concepts that control the size and configuration of basins used for these purposes are different. Likewise, different equipment is properly employed to accomplish these various objectives. The pattern of liquid and solids flow in the clarification zone of a sedimentation basin used for thickening or raising the density of a pulp normally is not critical. That is, the solids normally will drop or plunge to the bottom quite readily, and the liquid separates itself from these solids so as to overflow the basin in a relatively clear condition. When clarification or removal of finely divided particles is to be accomplished, the flow patterns in the basin are extremely important. The velocity of the incoming stream must be dissipated and the liquid flow distributed ]In the tank so that the feed is not divided into streams that flow directly to the overflow carrying the fine:ly divided solids that are to be removed. Similarly, the configuration of the arms that provide the raking and thickening of the pulp is not as important in basins primarily devoted to clarification. In thickening, the design of the arms and the manner in which the pulp is moved or worked, can contribute appreciably to the thickening process and achievement of a higher density underflow. THICKENING As the grade oi ore bodies throughout the world generally decreases, and chemical processes, hydro-metallurgy, and other more refined methods of minerals beneficiation are required, problems in thickening become more acute. Difficult operating conditions, previously encountered only occasionally in thickening metallurgical slurries, or clarifying process streams in the mill, are now the rule rather than the exception. Fig. 1 illustrates some of the different types of raking arms that are successfully achieving the desired goals in pulp thickening. The conventional raking arms consist of a relatively simple truss with the blades attached to the bottom chords. This design provides proper Concentration of many 'normal' slurries. A modificaiion of this design as shown in the center is being used with excellent results on large thickener basins where it is desirable to have a

Jan 1, 1962

By A. C. Rice

Investigation of a variety of mines to determine efficiency for rare- earth extraction has resulted in a solvent extraction technique wherein Primene 81-R,4 N-benzylheptadeeylamine (BHDA), and Primene JM-T give favorable extraction from sulfate solutions. Extraction from chloride, nitrate, and perchlorate solutions is negligible. Distribution coefficients for 10 rare-earth elements with Primene 81-R establish an extraction sequence beginning with lanthanum and proceeding through lutetium according to atomic number. Yttrium and ytterbium are exceptions in the extract ion sequence.

Jan 1, 1962

By K. T. Aust

The occurrence of annealing twins in high-purity aluminum resulted in the formation of grain boundaries having orientation relationships which correspond to a high density of coincidence sites. The results provide support for the coincidence site model and indicate that large-angle coincidence boundaries have lower free energies than large-angle noncoincidence boundaries. Observations are presented concerning the coherent structure of twin interfaces in aluminum and the importance of inter-facial energy in preferred orientation. RECENT experiments1 have shown that when an annealing twin is formed during grain boundary migration in zone-refined lead, a large-angle random boundary is replaced at the growth front by a large-angle coincidence site boundary. The coincidence site orientation relationships obtained by twinning were of the type considered by Kronberg and Wilson,2 Frank,3 and Dunn.4 On the basis of the theory of annealing twins advanced by Fullman and Fisher,5 these observations indicate that the energy of a coincidence site boundary is less than the energy of a random boundary by an amount which exceeds the energy of the coherent twin boundary. This energy difference between the coincidence and random boundaries must be at least about 5 pct since the ratio of twin boundary energy to grain boundary energy in zone-refined lead is 0.05 * .014.6 Fullman7 has found that the twin boundary energy in aluminum is about 21 i 5 pct that of a large-angle grain boundary. A twin boundary energy as large as this would be expected to exclude the formation of many coincidence site grain boundaries, especially those which have a relatively low density of coin- cidence sites. Therefore, if the coincidence site model is a useful interpretation of certain large-angle boundaries, then it would be predicted that only coincidence boundaries which separate adjacent crystals with a relatively high density of coincidence sites may be obtained as a result of twinning in aluminum. The present experiments provided a means of testing this prediction since annealing twins occurred during the growth of recrystallized grains into striated, melt-grown single crystals of zone-refined aluminum. EXPERJMENTAL PROCEDURE A striated single crystal of zone-refined aluminum, about 1 cm sq and 37 cm in length, was obtained during zone melting of aluminum of 99.996 wt pct starting purity in a graphite boat under helium atmosphere.8 A molten zone of 2 to 3 cm in length, which was maintained by induction heating. was passed along the length of the bar for eleven passes at a rate of 0.9 mm per min. An additional final pass was given at a rate of 0.2 mm per min. The center portion of the zone-melted bar was characterized by an electrical resistivity ratio between room temperature and 4.2° K of 8000 to 9000. Single crystals of 1 to 2 cm in length were removed from the center section of the zone-refined bar and electrolytic ally polished in a 2:l solution of methyl alcohol and concentrated nitric acid. The specimens were then chemically polished in Alcoa R-5 solution. X-ray analysis of the single crystals indicated the presence of striations or lineage substructure having misorientations as high as 2 deg. New, recrystallized grains were introduced into each striated crystal by the technique of artificial nucleation and growth, previously described.9 During the growth of the recrystallized grains at 300' to 600°C in argon, it was sometimes found that a

Jan 1, 1962

By Donald J. Knight

HEAT Treatment at 1500' F of a mild steel containing 0.1 pct C, in an atmosphere which is oxidizing to both carbon and iron, results in the progressive oxidation of the metal surface with little or no change in the carbon content of the underlying metal. Further heat treatment of the scaled metal in either a neutral atmosphere or in a vacuum may or may not result in the decarburization of the metal depending upon the physical nature of the scale. It is apparent that if a continuous layer of oxide is present on the steel surface, the reaction OScale + Cmetal Cogas cannot progress since the SO formed gas would be unable to leave the oxide/metal interface. Thus, in order for the reaction to progress, the oxide must be cracked or porous. Vacuum heat treatment at 1500" F of samples with a thick continuous oxide scale showed no decarburization of the steel. However, when cracks were introduced mechanically into the scale prior to the vacuum heat treatment notable decarburization of the metal resulted and a structure as shown by Fig. 1 obtained, i.e., reduction of the crack walls to ferrite. With reference to the diagram of Fig. 2, it would appear that a mechanism of the following type takes place. Carbon atoms arriving at an oxide/metal/void interface, such as 'A', Fig. 2(a), can combine with oxygen atoms from the scale and leave the reaction site as Cogas thereby reducing the oxide to metal. On a greatly magnified scale, Fig. 2(b),this will appear as a ferrite projection along the crack wall. Carbon atoms entering this projection can react with oxygen atoms at point 'C', which is a new interface, and so on leading to a progressive growth of the ferrite along the crack wall and to the surface, Figs. 2 (c) and 1. It would appear that the only means by which thickening of the ferrite film can take place is by a diffusion of oxygen through the ferrite film to react with carbon at the newly formed ferrite/ void interface. Since the diffusion rate of carbon is reportedly much greater than that of oxygen, and since there is a low probability factor of oxygen and carbon atoms arriving simultaneously at the same site on the ferritehoid interface, there will be a tendency for more rapid lengthening than thickening of the ferrite layer, as is observed.

Jan 1, 1962

By J. P. Morgan, J. R. Dawson

A review of Jones & Laughlin's Vesta coal preparation plant flowsheet in 1959 indicated that, of the three sizes making up the company's metallurgical product, the -48-mesh fraction offered the greatest potential for improvement. Efforts to improve quality and yield were directed toward the use of froth flotation. After laboratory and plant tests were completed, it was decided that treatment of the entire -@-mesh fraction of the coal mix by flotation was a significant step forward in providing better coal quality and recovery. Reduction of ash in the metallurgical coal from 6.75 to 6.25% provided material savings at the coal washer, coke plant and blast furnace. The Vesta preparation plant of the Jones & Laughlin Steel Corp. is located on the Monongahela River, eight miles south of Brownsville, Pa. This plant is capable of cleaning 2400 tph of a mixture of Pittsburgh seam high volatile coals from the Vesta and Shannopin mines to produce a metallurgical coal of 6.75% ash and a steam coal containing 14% ash. Heavy media vessels are utilized to upgrade the coarse coal while launders and tables handle the -1/4-in. fraction of the raw coal feed. Cleaned -1/4-in. coal goes to boot classifiers where the 48 mesh material settles and is removed by bucket elevators. This 1/4x48 mesh material is then sent to centrifugal dryers for dewatering. As designed, the -48 mesh fraction overflows the boot as a 7 to 8% solids slurry and is recovered by cyclones and a thickener and then dewatered by filtration. The products of the heavy media circuit, the launder-table-boot-dryer circuit and the cyclone-thickener-filter circuit, are combined to constitute the shipped metallurgical coal. The Vesta-Shannopin mix is combined at Jones & Laughlin's Pittsburgh and Aliquippa Works with purchased low and medium volatile coals for the production of metallurgical coke. A review of the preparation plant flowsheet in 1959 indicated that of the three sizes making up the metallurgical product, the -48-mesh fraction, containing 16.7% ash, offered the greatest potential for improvement of coal quality. This fraction was considered low, averaging 55%, while the rejects averaged only 33% ash. It was evident that while the boot overflow fraction represented only 6% of the product mix, a reduction in ash to 6 or 7% would reduce the ash of the metallurgical coal by 0.5%. The original plant flowsheet handling the boot overflow (Fig. 1) consisted of ten 14-in. cyclones treating 70% of the overflow and producing a 48x150-mesh underflow and a -150-mesh overflow. The cyclone overflow was combined with the remaining 30% of the boot overflow to constitute the feed to a 150-ft thickener. The cyclone underflow and the 48x325-mesh thickener underflow were fed to vacuum disk filters for dewatering prior to combination with the coarse metallurgical coal. The thickener overflow stream containing the -325-mesh material was split, 40% being recycled directly to the plant water system and 60% being flocculated and clarified in an 85-ft thickener. The underflow of this thickener was pumped to waste. Efforts to improve quality and yield on the -48-mesh coal were directed toward the use of froth flotation early in the investigation. A review of the fine coal flowsheet indicated that three streams should be considered for treatment by froth flotation. These were the -325-mesh thickener overflow, the -150-mesh cyclone overflow and the -48-mesh boot overflow. Flotation of the thickener overflow was considered basically to improve recovery by upgrading the reject stream so that it could be fed to the filters along with the thickener and cyclone underflows. The overflow from the thickener contained 3.7% solids and had an ash analysis of 33%. Flotation of the cyclone overflow and boot overflow were considered to upgrade coal quality as well as yield. Treatment of the cyclone overflow, a 5.4% solids slurry averaging 27% ash, would eliminate the coal thickener and provide a feed of flotation concentrate and cyclone underflow to the filters. Treatment of the boot overflow would eliminate both the cyclones and thickener and feed only flotation concentrates to the filters. Flotation feed in this

Jan 1, 1962

By J. W. Downey, M. V. Nevitt

The phase boundaries for the 950" isothermal sections in the ternary systems Zr-Co-0 and `Zr-Ni-0 have been determined for the composition range from 50 to 100 at. pct Zr. The two systems show very similar phase relations, having no extensive solid solution phase fields. Each contains a ternary phase. These phases are apparently isostructural, but their structure has not been determined. Some aspects of the phase relations are discussed in terms of the alloying behavior of transition metals. THE work described in this paper is the outgrowth of a recent study of the occurrence of phases having the Ti2Ni-type structure (structure-type E9,) in certain ternary systems involving Ti, Zr, or Hf with another transition metal and O.", In the Zr-CO-0 and Zr-Ni-0 systems no Ti2Ni-type phases were found to occur. However, there are several interesting aspects of the phase relations in the two systems which have significance from the point of view of the alloying behavior of transition metals. The results of this investigation may also have some importance in studies of the oxidation of Zr-Co and Zr-Ni alloys. In both the Zr-Co-0 and Zr-Ni-0 systems only the 950" isothermal sections were investigated and, as a further restriction, the study was limited to the composition range from 50 to 100 at. pct Zr. A tentative Zr-Co binary diagram has been published by Larsen, Williams, and Pehin. In the composition range pertinent to the present work they report a eutectic at 980°C and 75.9 at. pct Zr, the products of which are the terminal solid solution based on /3 Zr and the compound Zr2Co, and a eutectic at 1080" and 64.8 at. pct Zr whose products are Zr,Co and ZrCo. The solid solution based on /3 Zr is shown to decompose eutectoidally at 826°C into a Zr and Zr2Co. The limits of solubility of Co in a and /3 Zr have not been established. The structure of Zr2Co is not identified in the publication just cited. Dwight has reported that ZrCo has the CsC1-type strcture. The Zr-rich portion of the Zr-Ni diagram has been determined by Hayes, Roberson, and Paasche." The phase relations are very similar to those of the ZrCo system. A eutectic reaction whose products are /3 Zr containing 2.9 at. pct Ni and Zr,Ni occurs at 961°c, and a eutectic between Zr,Ni and ZrNi is found at 985". The solid solution based on /3 Zr decomposes eutectoidally at 808°C. The solubility of Ni in a Zr is not known accurately but is believed to be very small. Smith, Kirkpatrick, Bailey, and Williams7 have found that Zr2Ni has a tetragonal structure of the A1,Cu-type and that ZrNi is orthorhombic. Domagala and McPherson8 have published a constitution diagram for the system Zr-ZrO,. At 950" their diagram indicates that the solid solution of 0 in 0 Zr is stable from 0 to 0.5 at. pct while the phase field of 0 in a Zr extends from 6 to 29 at. pct. These solubility limits were adopted in the present study and no binary Zr-0 alloys were made. No previous data on the phase diagrams of the ternary systems are known to exist. EXPERIMENTAL PROCEDURE The experimental details involved in the preparation of alloys in this laboratory by arc melting have been described in several previous papers"3 and they will not be repeated here. Information concerning the purity of the metals used is given in Table I. Oxygen was added in the form of reagent grade ZrO,. All of the cast specimens in both alloy systems were annealed in air-atmosphere tube furnaces at 950 3' for 72 hr and water quenched. The specimens were protected from oxidation by wrapping them in Mo foil and sealing them in quartz tubes that had been evacuated at room temperature to a pressure of 1 x 10B mm of Hg. The phase boundaries were determined by metallography, and identification of the phases was accomplished primarily by X-ray diffraction methods which employed a powder camera having a diameter of 114.6 mm. The diffraction techniques which are in use in this laboratory have been previously described.' An etchant that proved satisfactory for most of the alloys consisted of 5 pct by vol of AgNO

Jan 1, 1962

By Josef Intrater

A dilatometric determination of the a + ß region temperature limits was performed on vacuum melted Zircaloy-2. The temperature of transformation for a-a+ß and a+ß — ß on heating and cooling as a function of rate of heating and heat treating history was studied. The limits were found to be 815° to 830°C to 975° to 995°C on heating and from 960° to 930°C to 785° to 770°C on cooling. A 5° to 15°C increase was observed for a- a + ß with increased rate of heating and a 20° to 30°C decrease for ß - a + ß with increased rate of cooling. 1 HE transformation temperature for pure zirconium has been determined by many investigators1-5 using metallography, electrical resistivity measurements, and dilatometry. The effect of the rate of cooling on the transformation temperature of zirconium has been studied by Hayes and Kaufmann6 and Duwez,7 and the effect of alloying elements by pfei18 and McGeary.13 Since the development of Zircaloy-2, the limits of the a + ß region for that alloy have been also determined. The first reported temperature for the a — a + a transformation in Zircaloy-2 was 900°C and for a + ß - ß 1000C Subsequent studies by Picklesimer and damson" indicated the beginning of the transformation at 810°C, and the metallographic study by the Technology Group of the Special Materials Section at the Westinghouse Bettis plant1' suggested that 820°to 830°C is the temperature of transformation. The dilatometric investigation by the latter group yielded 830°C for the beginning of the transformation. Thomas and Forscher12 set the beginning of the transformation at 900 °C on heating and the end of the transformation at 870°C on cooling. The above investigators stated in their paper that the dilatometric curve exhibits features caused by a eutectoid reac-

Jan 1, 1962

By John H. Lichtblau

There are three parties to the oil imports controversy: the domestic oil producers, whose side has just been ably summarized by Mr. Jameson; the oil importers; and the public. Domestic producers and importers are both motivated by economic self-interests, that is by their natural and legitimate desire for profit maximization, in their respective positions. Thus, domestic producers, rightly, regard every barrel of imported crude oil (with the exception of some specialty crudes) as a displacement of a barrel of their own crude. Hence, the lower the import Level the better they like it. Conversely, U .S. refiners whose plants are located at the seaboard or at certain inland waterways generally welcome a higher level of imports because refiner profits are based primarily on the spread between the crude oil price and the refined products price, since crude oil represents by far the refiner?s largest cost factor. The relatively low cost of foreign oil means therefore higher profits to those refiners able to process such oil, This applies particularly to integrated companies whose own domestic oil production is insufficient, to meet their refinery requirements but who have developed ample low-cost foreign oil supplies.

Jan 1, 1962

By W. C. Leslie

The textures of cold-rolled and of annealed iron are compared with those of an iron-0.8 pct copper alloy in which the amount of precipitation after cold rolling was controlled. Previously published pole figures -for cold-rolled and for annealed iron are confirmed. The effects of precipztatiotz after cold rolling are to retain the cold-rolled texture after annealing, to inhibit the formation of the usual allnealing texture, and to produce elongated recrys-tallized ferrite grains. It is suggested that the inhibition of new textures by precipitation after cold rolling is a general phenomenon. A great deal of attention has been paid to the development of texture during the secondary or tertiary recrystallization of ferritic alloys, but very little work seems to have been done on the control of texture during primary recrystallization. If such control were attained, it might be possible to simplify the processing of oriented materials or to change the characteristics of current cold-rolled and an-nealed products. From previous experience, it seemed likely that texture could be controlled by recrystallizing a supersaturated solid solution. Green, Liebmann, and Yoshidal found that the formation of preferred orientation in aluminum (40 deg rotation about <111> relative to the deformed matrix) was inhibited when iron was retained in supersaturated solid solution in the strained aluminum. The authors attributed this inhibition to iron atoms in solid solution. There is, however, an alternative explanation. Green et al, took a highly supersaturated solution of iron in strained aluminum and heated it to an unspecified temperature for recrystallization. It is probable that precipitation occurred prior to and during recrystallization, and it is proposed that the inhibiting agent is this precipitate, rather than the iron atoms in solid solution. It is important to note that precipitation before cold work is ineffective; the effective precipitate is that formed after cold working and either before or during recrystallization. The location and distribution of the precipitate are critical. Precipitation in such a manner has been found to have profound effects upon kinetics of recrystallization and the microstruc-ture of the recrystallized alloys.2-4 It would be surprising, indeed, if this were accomplished with no change in texture. Because of the relative simplicity of the system, and because of previous experience,4-7 it was decided to determine the effect of precipitation on texture in an alloy of iron and copper. Bush and Lindsay5 found an unspecified change in texture in cold-rolled and annealed low-carbon rimmed steel sheets when the copper content exceeded 0.1 pct. MATERIALS In earlier work, the rate of recrystallization of a low-carbon steel was greatly decreased by 0.80 pct copper, and, after the proper treatment, the recrystallized ferrite grains were greatly elongated.4 Accordingly, it was decided to investigate the effect of precipitation on texture at this level of copper content. The iron and the iron-copper alloy were made from high-quality electrolytic iron and OFHC copper, vacuum-melted in MgO crucibles, cast, hot-rolled to 0.2 in., then machined to 0.150 in. The compositions are given in Table I. The plates were heated to 925°C and brine quenched, twice. This produced a ferrite grain size of ASTM 0 in the iron and ASTM 1 in the Fe-Cu alloy. Disk specimens were cut from the heat-treated plates, repeatedly polished and etched, then used to determine (110) and (200) pole figures by reflection. Despite the complication of large grain size, these pole figures strongly indicated a random texture. PROCEDURES The copper content in solid solution in ferrite before cold rolling and recrystallization, and hence, the amount that could precipitate during the recrys-tallization anneal, was controlled at three levels by heat treatment. The specimens as quenched from 925° C were presumed to have all the copper, 0.80 pct, in solid solution. Other samples of the quenched alloy were aged 5 hr at 700°C to retain about 0.5 pct Cu in solid solution.6 A third set of quenched specimens was reheated to 700°C, then slowly cooled in steps, to reduce the amount of copper in solid solution to a very low level. All specimens were cold-rolled 90 pct, from 0.150 to 0.015 in. thick. The rolling was done in one direction only, i.e., the strip was not reversed between passes, with a jig on the table of the mill to keep the short specimens at 90 deg to the rolls. The rolls were 5 in. in diameter and speed was 35 ft. per min. Machine oil was used as a lubricant. In a supersaturated alloy, the maximum effect of the copper precipitate on microstructure and on recrystallization can be developed by a treatment at 500°C, after cold rolling and before recrystallization.&apos;

Jan 1, 1962

By D. L. Wood, J. H. Westbrook

The tensile behaviors of the CsCl structure compound AgMg are extensively documented in terms of strain, strain rate, temperature, composition, and metallurgical processing treatment. The observations lend themselves to presentation in terns of three regimes of deformation behavior; 1) low temperatures where deformation is primarily by slip; 2) intermediate temperatures where the deformation mode is also slip but with the detailed behavior dominated by dislocation interactions with solute atoms; 3) high temperatures where defomation is primarily by diffusion controlled processes. Of all the material groups of potential interest as high-temperature structural materials, the inter-metallics have been the least studied, particularly with respect to their mechanical behavior. Moreover, the application and processing of intermetallics for uses which exploit their often unique physical properties have been impeded by a lack of understanding of their mechanical properties. Previous work in this area* has been largely *For a recent review, see Westbrook.&apos; exploratory, aimed on the one hand at the direct empirical development of materials of engineering utility and ,on the other at identification of the important parameters affecting the mechanical behavior of inter metallics. As a consequence, there has not been available, heretofore—for any inter-metallic—data, sufficient in extent or precision to provide an adequate phenomenological description of the effects of metallurgical variables on deformation behavior. Such documentation is prerequisite to intelligent application or processing design and is also necessary for testing present and future theoretical analyses of mechanical behavior. It was therefore an objective of the present investigation to document the deformation behavior of a simple ordered intermetallic over as wide a range as possible of all the usual metallurgical variables. The compound AgMg was chosen as the subject of this investigation because it met all of a group of desired criteria, namely: 1) congruent but moderate melting point; 2) simple crystal structure; 3) ordered structure persisting to the melting point; 4) broad solubilities for the component elements. The first and last criteria were expected to aid in the preparation of homogeneous single-phase specimens: the second and third to help simplify the

Jan 1, 1962

By J. A. Elias, R. H. Heyer, J. H. Smith

Plastic anisotropy determined by the ratio of width strain to thickness strain in tensile specimens of low-carbon steels is strongly related to crystallographic preferred orientation. Using(222) Pole figures, a method was developed which permits rapid Predictions of plastic anisotropy for any crystallographic texture or orientation. The method is applied to low-carbon steel sheets in which four different crystallographic orientations were produced by variations in cold rolling and annealing treatments. AnISOTROPIC behavior of metal sheets during plastic deformation has long been evident. A familiar example is earing in cup type draws. During tension testing of sheet specimens, anisotropy results in a difference in width strain as compared with thickness strain. Carpenter and Elam1 observed this phenomenon in single crystals of aluminum for both sheet and rod samples. Lankford, Snyder, and Bauscher2 made tension tests on sheet samples of aluminum-killed low-carbon steel to determine the ratio of the width-to-thickness strains, and showed that this ratio was related to drawing performance. Burns and Heyer3 calculated theoretical ratios of width strain to thickness strain for two specific orientations of the bee system, using <111> as the operative slip direction. These calculated values were in fairly good agreement with the ratios determined by tension tests of low-carbon steel sheets in which these preferred orientations existed. The high degree of plastic anisotropy of silicon steel sheets could also be predicted from their crystallographic structure by these calculations. The present study has been made to show that the anisotropy observed in plastic tensile straining is strongly orientation dependent and can be adequately predicted for many orientations and textures. PLASTIC STRAIN RATIO R In the region of uniform elongation of a tension test specimen the plastic deformation may proceed at different rates in the width and thickness directions. Such anisotropy has been described in the past by the plastic strain ratioR:

Jan 1, 1962

By Henning E. Soderberg

Yesterday, air pollution was somebody else&apos;s problem -- today, it is everybody&apos;s problem. The coal industry with thermal coal drying, is aware of their problem and the necessity of doing an acceptable job; however, there is much to be said as to how good a job is required and what performance limits should be set up. American Air Filter Company has been one of the pioneers in the solution of the thermal coal dryer dust problems, Because of high moisture content, products of combustion and occasional temperature surges, only wet collection has been considered as the practical approach. Our first installation goes back some 12 years with a total to date of 29 Individual wet collectors, each, fabricated of suitable corrosion-resistant material, at 14 operating plants. To eliminate a potential air pollution problem, a performance requirement of not more than approximately one-quarter (1/4) grains per cubic foot in the dust collector discharge was used. In nearly all installations, operating performance surpassed requirements, but discharge stacks were not entirely free of discoloration. However, plant nuisance and air pollution complaints were eliminated. This satisfactory performance was accomplished by medium priced wet dust collectors operating at a 4-6" W.G. pressure drop with cater drain requirements of about 1 gallon of drain water per 1000 cubic feet of air exhausted.

Jan 1, 1962

By R. W. Fountain, John Chipman

The solubility of nitrogen in Fe-B alloys (0.001 to 0.91 pet B) is determined by the Sieverts&apos; technique for temperatures of 950° to 1150°C. The activity coefficient of nitrogen is decreased by boron. The three-phase equilibrium between ? iron, BN, and gas is established and also the four-phase equilibrium between iron, BN, Fe2B, and gas. The above equilibria are calculated for a iron. The relation of these data to hardenability and strain aging of boron-treated steels is discussed. BORON additions are known to enhanbe the hardenability of heat-treatable steels and to assist in the control of strain aging in sheet steel for deep drawing. The increase in hardenability is explained by the theory that adsorption of boron on austenite grain boundaries reduces their free energy and thus retards ferrite and upper bainite nucleation.l,2 Digges and Reinhart3 have shown that the full effectiveness of boron in commercial steels is achieved only when strong nitride formers such as titanium and zirconium are also present. The influence of nitrogen on eliminating the boron contribution to hardenability was also demonstrated by Shyne and Morgan.4 These workers prepared Ni-Mo steels containing either nitrogen or boron or nitrogen plus boron. The nitrogen-plus-boron steels showed the lowest hardenability which was attributed to the presence of stable nucleating particles, presumably nitride. Morgan and Shyne5-7 have shown that boron in the amount of 0.007 pet will completely eliminate strain aging due to nitrogen in low-carbon, open-hearth steels. In addition, by proper control of the boron additions, a rimming steel can be produced. Since the effectiveness of boron on hardenability and eliminating strain aging is influenced by the amount and distribution of the nitrogen in the steel, the present study was. undertaken to determine the influence of boron on the solubility of nitrogen in iron. EXPERIMENTAL PROCEDURE The solubility of nitrogen in Fe-B alloys was measured by the method of Sieverts, which consists of determining the amount of gas dissolved by the metal in a constant volume system. The apparatus employed in this investigation and the experimental details have beendescribed previously.B AMcLeodgage was added to the apparatus to allow measurements at very low pressures. The alloys were melted at reduced pressure in a basic-lined induction furnace using electrolytic iron and ferroboron. Ferroboron was added after the primary deoxidation of the iron with carbon. Since it was difficult to attain a constant low level of oxygen by this procedure, silicon was added after the carbon deoxidation and prior to the ferr obor on addition. The alloys were castas 2-in. sq ingots, heated in argon at 1050loC, and forged to 1/4-in. plate. After forging, 1116 in. was machined from each side of the plate to remove any possible contamination, and it was then cold-rolled to 0.010-in. sheet. The sheet was cut into approximately 1/4-in. squares and pickled in an inhibited H2SO4 solution to ensure a clean surface. In the case of the boron alloys, a hydrogen treatment could not be used for surface cleaning because boron losses resulted. The composition of the alloys is given in Table I. For a solubility determination, a 75-g sample was inserted in a quartz tube and sealed in place in the apparatus. The entire system was evacuated at room temperature and leak tested for 24 hr. If no leaks were observed, the system was heated to the temperature of measurement and again leak tested for 24 hr. If no leaks were detected, the hot volume and solubility determinations were begun. The hot volume was determined at a constant temperature for each run by admitting successive amounts of argon and recording pressure vs volume, which, in all cases, resulted in a straightline relationship. The argon was then removed and the procedure repeated with nitrogen. Successive additions were made until the desired nitrogen content of the metal and equilibrium pressure of the system were obtained. The

Jan 1, 1962

By Colin C. Harris, Nathaniel Arbiter

The flotation operation can be analyzed in terms of three groups of variables. The first, largely independent of control by the operator, embraces the fixed physical and chemical properties of the ore minerals. The second includes all chemical and physical effects imposed on an ore after mining that influence its floatability. These can be either purposefully or accidentally applied. The third embodies the flotation-machine characteristics which realize the potential floatability of selected ore minerals in terms of grade and recovery levels. The machine effectiveness thus depends not only on its own contribution, but on the prior influence of all other variables on floatability. HISTORICAL DEVELOPMENT From the earliest days, flotation mills used many types of machines. Hoover 20 in 1914 mentioned as then important the Potter-Delprat tank for gas generation by acid, the DeBavay cones for skin flotation, the Elmore mixer and separation chamber for vacuum flotation, and his own modification of the Mineral Separation cell for the agitation froth process. Less important at the time were the MacQuisten tube and the Hyde cell. By 19274~ scores of machines had been developed and dozens had found their way into mills. From then on, however, under the scrutiny of competitive tests, many fell into disuse. Taggart in 19454~ classified processes broadly as skin flotation and froth flotation, dividing machines for the latter into the three categories: bubble column, pulp body, and combination.* Under &apos;bubble column&apos; he listed all pneumatic, cascade, and subaeration cells; and under &apos;pulp body&apos; those cells in which gas was generated by boiling, chemical action, and pressure reduction, as well as the agitation-froth type. At that writing skin flotation, the cascade machines, and all pulp body and combination machines were said to be extinct, leaving pneumatic and subaeration types dominant (u. S. practice). The process of elimination has continued to the present, with almost all pneumatic cells succumbing to the pressure of competition from subaeration machines. The only new machines to appear in recent years have been double-impeller types f and these have met with only limited acceptance.

Jan 1, 1962

By Harry A. Lipsitt, Rollins E. Hook, Attwell M. Adair

A necessary condition for a uniaxial stress distribution in compression testing is that the specimen end surfaces make full contact with the apparatus compression plates. In addition all compression surfaces must be machined perpendicularly to the loading axis. In general this condition is not sufficiently fulfilled in a simple apparatus. Therefore on application of the load the compression plate may first touch the specimen at one point only. This may cause crumbling of the specimen if the material under investigation is brittle (e.g., ionic crystals). It also precludes a precise study of the beginning of deformation as the effective cross sectional area is unknown. In addition a complex stress state is set up which renders quantitative work impossible, e.g., on dislocation density and arrangement as a function of stress. To overcome these difficulties a "self-adjusting" upper compression plate is required. A simple and reliable method of achieving this is shown in Fig. 1: A steel hemisphere is placed on the specimen. As soon as the compression plate (which no longer needs precise machining) makes contact with this hemisphere the load is uniformly distributed over the whole specimen surface, and a homogeneous uniaxial state of stress results. An advantage of the method is that the loading is always central, even when the specimen surface is not parallel to the compression plate (Fig. 1, dashed line). Therefore to a first approximation a uniaxial state of stress is maintained if the misorientation of the specimen end surface is small. Two typical stress strain curves of identically prepared sodium chloride crystals are shown in Fig. 2; curve 1 was taken without and curve II with the hemisphere under otherwise identical conditions. The improvement in the accuracy of defining the beginning of elastic and plastic deformation is clearly indicated. The writer wishes to thank the Deutsche Forschungsgemeinschaft for financial support, and Professor P. Haasen for providing facilities for this work.

Jan 1, 1962

By J. M. Markowitz

The movement of hydrogen in two-phase Zircaloy-2 under the influence of a thermal gradient was studied in specimens of cylindrical geometry. A gross displacement of hydrogen toward the cooler regions of the specimen was observed with consequent copious precipitation of 6-ztrconium (ZrH) there. The kinetics of the diffusion are analyzed and discussed. X HE temperature-gradient redistribution of hydrogen in a-Zircaloy-2 has been treated both theoretically and experimentally Hydrogen moves toward the cold side of the temperature gradient until a steady state has been established; tendency for further hydrogen movement because of temperature differences is nullified by the tendency to move in the reverse direction because of the concentration gradient. The steady state condition is described by the equation in which iV is the concentration of hydrogen at a point in the specimen corresponding to absolute temperature T, R is the gas constant,k is a constant of integration, and Q is a parameter called the heat of transport, characteristic Of the particular system. The value of Q has been determined for hydrogen in Zircaloy-2 by several investigators, using Eq. [11. There is considerable variation in the results, the cause of which has not been resolved; reported values lie in the range 3 to 6 kcal per mole. The physical situation for two-phase thermal migration is much more complex. The -phase boundary for the solubility of hydrogen in Zircaloy-2 ranges from a concentration of 25 ppm at 200°C to a maximum of about 600 ppm at 550°C.4a Thus, if the concentration of hydrogen in Zircaloy-2 is sufficiently great (>600 ppm), the specimen will be entirely two-phase, consisting of a matrix of a-Zircaloy-2 surrounding particles of zirconium hydride. At time zero, with a temperature gradient imposed, the relative amounts of hydride and a-phase in each infinite-simally thin isothermal section of the specimen can be determined from the phase diagram by the lever rule. Moreover, the concentration of hydrogen in the matrix phase varies from point to point, following the a solubility line. Over most of this temperature range (<450°C) 6 phase, Fig. 3, has a constant concentration.5 The diffusion rate toward the cold side should be governed by 1) the slope of the a solubility line and 2) the temperature gradient, The extra complication of two-phase thermal diffusion lies in the fact that migration of hydrogen would leave the a-phase concentration gradient unaffected, since it is fixed at any temperature only by the solubility; gross concentration changes would reflect only the relative amounts of matrix and hydride, which could vary continuously at every point. Migration of hydrogen out of a region would lead to dissolution of hydride, and

Jan 1, 1962

By R. W. Heckel

The conzpaction of metal powders is analyzed through density-pressure curves as a three-stage process — die filling, individual particle motion, gross compact deformatim. The densification occurring during each of these stages is evaluated quantitatively. The amount of densification in the first and second stages is primarily a function of particle geometry. The densification taking place in the third stage is dependent mainly upon the material. AT the present time the densification of powders during compaction is usually described by terms such as "compactibility," "compressibility," and "compression ratio." Schwarzkopfl has proposedthat compactibility be defined as the minimum pressure needed to produce a given green strength, while compressibility be used to indicate the extent towhichthe density of a powder is increased by a given pressure. Compression ratio is generally defined as the ratio of the compact density obtained at a given pressure to the apparent density of the loose powder. 13alshina found that the pressure imposed on a compact affects the relative volume of the compact according to the following relation: hP= - LV + C [ll where: P is the applied pressure, V is the relative volume of the compact, Ratio of the specific volume of the compact to that of the material without porosity. Lisa constant described as the modulus of pressing and is determined by the slope of a plot of h P vs V, and C is a constant which is determined by the intercept of a plot of InP vs V. Several drawbacks of the Balshin analysis may be noted from Fig. 1, which is a plot of pressure (loga-

Jan 1, 1962

By H. A. Stoess

The Minerals Industry makes heavy demands for and on its Material Handling equipment. It also gives progressive management the opportunity for considerable savings, ad consequently increased profits. In some cases, cost of Materials Handling amounts to 40°/o of the total cost of the ultimate product. Handling costs are hidden in overhead, indirect labor, excessive maintenance, productive workers performing handling tasks, and, a great many more. Even though Materials Handling is the oldest occupation of mankind, it is only within the past twenty years that it has emerged as a specialized field. While this industry has made full use of all types of mechanical and vibratory conveyors, pneumatic conveyors in their proper application can be a distinct asset. me use of pneumatic conveyors by this industry however is limited- to a certain extent by the particle size of your products through the various phases of manufacture, as well as their bulk density. However, with increasing knowledge of the fluidization of dry materials, their use is becoming more wide spread.

Jan 1, 1962

Dr. F. L. Stillwell. Segnit&apos;s article puts forward the views that the rocks associated with the Broken Hill lode are simply highly metamorphosed sediments, tbat metasomatism on a large scale was not an important factor at Broken Hill and that the rocks and lode were contemporaneously metamorphosed.In particular, the garnet quartzite, the most abundant rock in the limited section of the mine examined by Segnit, is described by him as a simple, metamorphosed manganiferous sediment.These views, while consonant with those of H. F. King (1958), are drastically opposed to those of myself and others e.g. Gustafson et al. (1950, p. 1383) who state that the most extensive hydrothermal alteration in the district is in and close to the zinc lodes in the Zinc Corporation and New Broken Hill Consolidated Ltd. mines. Segnit&apos;s conclusions conflict with 1. the absence of any manganiferous sediment in the Broken Hill district except in close proximity to the lode,2. the clear cut metasomatism of the dolerite dykes which indicates that the ore is younger than the dykes and therefore post-metamorphism, and 3. the petrofabric study of den Tex (1958) which provided independent evidence that the ore in its present form post-dates all events of a diastrophic nature in the area.The original sediments of the district were mudstones and calcareous sandstones with 2 to 5 per cent CaO. These have been converted by high grade metamorphism into sillimanite gneisses and quartzites characterized by the presence ...

Jan 1, 1962