Search Documents

By Arnulf Muan, W. C. Hahn

Activities of "FeO" in "FeO"-MgO solid solutions have been determined in the temperature interval 1100" to 1300"C by equilibrating oxide samples with pure metallic iron in atmospheres of known oxygen partial pressures. The end members "FeO" and MgO form a complete solid solution series. The system shoztls a considerable positive deviation from Raoult's law. A large amount of data has been accumulated during the past 50 years on stability relations existing among various crystalline and liquid phases in oxide systems of importance in metallurgical processes. By comparison, very little is known about the thermodynamic properties within the various homogeneous phases present in the systems, particularly the crystalline phases. The present paper deals with determination of activities as a function of composition in solid solutions of wüstite ("FeO") and periclase (MgO). Such solid solutions ("Magnesiowustites") have simple sodium chloride structure and are known to be continuous between the end members at elevated temperatures (> 1000°C) and strongly reducing conditions such as prevail in contact with metallic iron. Wiistite has a defect structure in which the ratio of oxygen to iron varies and never has as low a value as 1:1 corresponding to the simplified formula FeO. Within the range of stability of this phase, the composition changes between a maximum oxygen content of approximately 25.6 wt pct (corresponding to the formula FeO.83O) and a minimum oxygen content of approximately 23.2 wt pct (corresponding to the formula Fe0-96O). The activity data to be reported in the present paper are based on using as standard state the wüstite which is in equilibrium with metallic iron at a particular temperature, i.e., "FeO" of minimum oxygen content at each temperature. For sake of simplicity, the formula FeO will be used to represent the wustite phase in the remainder of this paper. Consider the reaction 2 FeO solid solution = 2 Femeta1 + Ozgas in which FeO dissolved in another oxide dissociates to metal and gas. The activity of FeO in the solid solution, relative to "pure FeO" in equilibrium with metallic iron as a standard state, is then expressed as Here Po, and po2 * are the partial pressures of oxygen of the gas phase in equilibrium with metallic iron and the oxide solid solution or "pure FeO", respectively. The equation holds only if the metal phase is essentially pure Fe. The oxide combinations used in the present investigation fulfill this requirement. Magnesia is so much more stable than FeO that for all practical purposes aFe = 1 in the metal phase present in all mixtures used in this investigation. I. EXPERIMENTAL METHOD 1. General Procedure. The experimental method used was analogous to that developed by Foster and Welch1 and used recently by Hahn and Muan.2 It consisted of four steps: a) Determination of the equilibrium between FeO and Fe. b) Determination of d-spacing change with composition in oxide solid solutions (FeO-WO). c) Equilibration of various members of the solid solution series with a metal phase and a gas phase of known oxygen partial pressure. d) Determination of compositions of solid solutions resulting from step (c) by means of data obtained in step (b). 2. Starting Materials. General Aniline and Film Corp. carbonyl iron powder, type HP, was used as the source of metallic iron. A representative analysis was as follows: Fe, 99.6 pct; C, 0.01 to 0.04 pct; 0, 0.1 to 0.3 pct; N, 0.00 to 0.05 pct. Other elements were present as traces only. Wiistite was prepared from "Baker Analyzed" Reagent grade Fe2O3 of reported analysis as follows: Assay (Fe2O3), 98.8 pct; insoluble in HC1, 0.02 pct; not precipitated by NH,OH, 0.02 pct; Zn, 0.003 pct. Production of wüstite was achieved by a two-step

Jan 1, 1962

By Robert J. Uffen

YOU will likely recall the accomplishments of the International Geophysical Year of 1957, with its polar expeditions, the discovery of the Van Allen radiation belts and the spectacular launchings of the first artificial earth satellites. Our know ledge of the exterior of the earth was greatly increased by this international, friendly, cooperative scientific investigation. The Inter-national Union of Geodesy and Geo-physics has now been joined by the new International Union of Geological Sciences in sponsoring a similar study of the earth's interior. The program will extend from January, 1962 until December. 1964, and is known as the International Upper Mantle Project. During the T.G.Y studies of the interior of the earth were relatively neglected, even though the same international •Cooperation in obtaining simultaneous world-wide observations, by similar instruments, is required to locate and study earth-quakes, for example, as it is to study the earth's upper atmosphere. The upper mantle is 1•emote from man, as it extends from a depth of about 10 km. to perhaps 1000 km., but its practical importance is great.

Jan 1, 1962

By E. H. Crabtree, J. D. Vincent

Probably no metallurgical process in the history of the mining industry has been responsible for such increased mineral production as has flotation. It has made possible the economic treatment of low grade and complex ores which, with the old methods of gravity concentration, would have been classed as worthless. Starting with the sulfide ores of copper, lead, and zinc, the process has been applied to almost all metallic and nonmetallic minerals. Today, the sulfides of the common metals not only can be readily recovered, but can be separated from each other. Thus, three or four mineral recoveries from the same ore, such as galena, chalcopyrite, sphalerite, and pyrite, are possible. Molybdenite is recovered initially with copper sulfides and the two are subsequently separated. Flotation of metallic gold and of native copper and graphite is being commercially practiced. The carbonates of some of the base metals, principally those of lead, can also be concentrated. Flotation of the oxides, silicates, phosphates, and other so-called non- metallic minerals represents the greatest advance in the art in the last few years. Today, commercial plants are successfully treating such minerals as feldspar, garnet, ilmenite, muscovite, cassiterite, cement rock, fluorspar, phosphate rock, sylvite, and a host of others. Flotation of the various types of iron ores along with other concentration methods is today the subject of a tremendous amount of investigation on the iron ranges. EARLY PATENT HISTORY OF FROTH FLOTATION Although what we call the froth flotation process as distinguished from bulk oil processes was not used commercially until 1905, many investigators had recognized its possibilities long before the twentieth century. The principal patents issued throughout the years give us a method of recording early flotation history. BULK OIL PROCESSES: In 1860, William Haynes patented (British Patent 488) a process for separating oil-wetted sulfide minerals from water-wetted gangue minerals by agitating the dry ground ore with oil and then the mixture with water. In 1877, the Bessel brothers patented (German Patent 42, Class 22) a process where a mixture of graphite ore was mixed with 1 to 10% oil; after adding water, the

Jan 1, 1962

By Henry M. Harris

Low-carbon shales from 65 deposits and 11 sources of coal-mine waste in western Oregon and Washington were tested in a rotary kiln for their suitability as raw material for expanded aggregate. Shales from 41 sources bloated enough to produce crushed, expanded aggregates, weighing less than 65 pounds per cubic foot in the preliminary tests. The samples were judged on the basis of processing qualities, physical properties, and size and uniformity of the source. Nine low-carbon shale deposits and three coal-mine waste sources were selected for more extensive bloating tests and for examination of the expanded aggregates in concrete shapes. Composite samples from these 12 sources and from 2 commercial operations, when processed for testing in concrete shapes, had bulk densities ranging from 37.S to 72.9 pounds per cubic foot. Damp-cured concrete shapes made with these aggregates had bulk densities ranging from S6 to 119 pounds per cubic foot, and all but three of the lightweight concretes had crushing strengths ranging from 3,270 to 6,810 p.s.i. Properties of the lightweight concretes were compared with those of concrete shapes made with commercial aggregates, and with sand and gravel.

Jan 1, 1962

By Lawrence H. Van Vlack, Otta K. Riegger

Periclase-type oxides were examined microscopically after being exposed to siliceous liquids. The rate of grain growth was found to be inversely proportional to the grain diameter. Grain growth proceeds more rapidly at higher temperatures, but is retarded by increasing liquid contents. aMag-nesiowiistites with higher MgO contents grow less rapidly than those with higher FeO contents. The growth rate is reduced by the presence of a second solid phase. The silica-containing liquid penetrates as a film between the individual magnesiowus tite grains. This is independent of time, temperature, amount of liquid, or the MgO/ Fe0 ratio. When present, olivine and spinel-type phases can provide a solid-to-solid &apos;&apos;bridge" between magnesioustite grains. THIS paper presents the results of a study of the microstructures of periclase type oxides in the presence of a silicate liquid. The purpose was to learn more about the effect of service factors such as 1) time, 2) temperature, and 3) liquid content upon A) grain growth, and B) liquid location among the solid grains. This study was prompted by the fact that periclase refractories are known to have very little solid-to-solid contact when the phases which are present are limited to periclase and liquid. Such a micro-structure gains industrial significance because it permits fracture during service when stresses are applied at high temperatures. The details of ceramic microstructures have not received extensive attention. This is in contrast to the extensive attention given to a) the phase relationships pertaining to refractory compositions, and b) the details of the microstructures of comparable metallic materials. A brief review will be made of the pertinent phase relationships and microstructural considerations in general, as well as of refractory compositions. a) Phase Relationships. This investigation was limited to those compositions in which (Mg, Fe)O was the solid phase. MgO and FeO form a complete series of solid solutions. Pure MgO has the name of periclase. The related FeO structure is called wustite. Both have the NaC1-type structure: however, wustite possesses a cation deficiency so that the true composition is Fe<10 even in the presence of metallic iron. The phase relationships involving solid (Mg, Fe)O and a silicate liquid are shown in Fig. 1. In this case. the liquid is saturated with (Mg, Fe)o. There-fore its SiOz content is below that encountered in orthosilicate liquids. As a consequence the liquid phase specie:; are primarily the following ions: and 0-&apos; plus occasional Fe+ ions. Two features are of importance: a) the liquid contains relatively small species and b) the liquid contains large quantities of the same species as the solid. viz., Fig. 2 shows the system, FeO-SiOz, which will be used in some of the discussions that follow. This diagram is the right side, vertical section of Fig. 1. Here, as pre\iously, the composition at the FeO end of the diagram is nonstoichiometric, varying from Feo.950 when the liquid oxide is in contact with the solid iron, to about Fe 0, when the solid oxide is in equilibrium with an atmosphere of equal proportions of CO and C02 at the solidus temperature. The Fe/O ratio will be maintained in wustite in the presence of SiO,. However, the FeM/Fe++ ratio in the liquid will be lower because of the effect OIF the SiO, on the activity of the FeO. With the addition of MgO to wustite, the over-all composition (IvZg, Fe)@, has a value of x lying between 0.9 and 1.0 when the COz/CO ratio is 1.0&apos;. b) Microstructures. In general, published attention to refractory microstructures has been directed toward the phase analyses that accompany compositional variations. This is illustrated by Harvey6 in his work on silica brick and by wells7 in his work on periclase brick. In each case, a series of altered zones is encountered which provides a sequence of phase associations. If due consideration is given to reaction kinetics, such an examination reveals phases that are compatible with equilibrium studies. Admittedly, however, it is often necessary to determine more complicated polycomponent systems to account for all the phases present.8 Relatively little attention has been given to microstructural geometry in ceramic materials. Certainly less attention has been given to this aspect of ceramic microstructures than to the size, shape, and distribution of the constituent phases in metals. Burke has pointed out that the grain size of oxides follows the same growth rules as for metals, viz.,

Jan 1, 1962

By A. M. Gaudin, T. P. Meloy

Based on the equation for single fracture, a formula has been obtained for repeated fracture. Solution of this equation is obtainable analytically for a few examples and numerically for all others. Graphs of the size distribution equations have been obtained; they agree broadly with the experiments of others. In another paper1 we have considered a model and a comminution distribution equation for single fracture of brittle materials. Most comminuting devices, however, depend on the occurrence of repeated fracture. This is especially true of continuous cylindrical mills of the ball, tube, or rod type. But even in primary crushers there is some repetition of the breaking process, so that this paper should be of interest in connection with all comminuting devices. HALF LIFE AND PROBABILITY OF FRACTURE To facilitate the study of fracture it is useful to introduce the concept of the half life of a particle, In the ball mill, for example, we may start with 10,000 feed particles. The time, 7, by which one half of these particles have been broken is the half life of the feed under the prevailing experimental conditions. The probability of breakage bears an inverse relationship to the half life. In a ball mill, for instance, it can be shown that the

Jan 1, 1962

By J. Beland

The Rimouski-Matapedia region is along the southwestern extension of the central Siluro-Devonian synclinorium of Gaspe Peninsula. As in Gaspe about 30,000 feet of Siluro-Devonian strata rest on a "basement" of tightly folded Ordovician rocks. The central synclinorium is divided up into two northeasterly trending belts each of which is characterized by distinctive lithologies and patterns of folding. The northwestern belt is gently to moderately folded and includes lithologies which point to a stable environment. The southeastern belt on the other hand is tightly folded and the lithologies indicate a less stable environment. A marked angular unconformity separates the basement from the Siluro-Devonian cover near the north-western margin of the northwestern belt. At the southeastern margin of the southeastern belt the relationship of cover to basement has not been as-certained because of a fault. The northwestern belt has several features significant in the search for petroleum; the Silurian strata are exposed in broad open anticlines

Jan 1, 1962

By W. Rostoker, H. Nichols

The embrittlement by mercury of aluminum alloys in various states of anneal, cold work, and aging has been studied. It is shown that single phase and non-precipitation hardened structures irrespective of de,pee of prior cold work demonstrate some small measure of yielding before fracture occurs. Sub-yield-stress failure is confined to the aged state, and embrittlement is accentuated by small plastic prestrains. With large plastic pyestrains, embrittle~nent is progressively reduced. In previous work&apos; it was shown that the propensity of commercial aluminum alloys for embrittlement when wetted with mercury seems to be related primarily to the intrinsic strength in the normal un-wetted condition. The data from a large number of commercial alloys in various states of anneal, cold work, and/or aging gave a generalized relationship. At low strength levels, the wetted fracture strength increases proportionately to the increase in tensile strength; but above 65,000 psi normal ultimate strength, the trend is abruptly reversed, and the wetted fracture stress decreases proportionately to the increase in tensile strength. This paper will demonstrate that the simple character of this relationship between normal tensile strength and wetted fracture strength is fortuitous. It will be shown that structure and thermal-mechanical history are clearly relevant factors. The term brittle fracture has been used to connote the geometry of the fracture surface (transverse vs shear plane) or the negligible extent of preceding plastic strain. At its maximum effectiveness, liquid metal embrittlement can satisfy both criteria—fracture transverse to the axis of tension and without observable plastic strain. In this paper, brittle fracture will signify failure at stresses below the engi-

Jan 1, 1962

By D. A. Bailey, F. L. Kadey

During recent years, expanded perlite has found extensive use in a wide variety of commercial applications. Specifications for a range of uses call for aggregates having different physical properties and requiring various types of processing. The mitre scopic examination of expanded aggregates in specially prepared thin sections has yielded important information regarding internal structure and can be a useful aid in evaluation of the product. Perlite is an acid volcanic glass containing from 2 to 5 pct combined water. When crushed and rapidly raised to a temperature of 1500° to 2100°F, the volatilization of the combined water, coincident with softening of the siliceous glass, causes the particles to expand or pop. Expansion of perlite to densities as low as 1-1/2 lb per cu ft has been achieved, although the normal range is from about 2.5 to 10 lb per cu ft. Low-density materials of this nature have found application in cryogenic insula- tions, insulating tile and board, plaster and lightweight concrete, soil conditioners, filter aids after comminution, and a host of other uses. The expansion of perlite may be controlled by a number of variables. Some of these are ore milling, furnace design, expanding temperature, use of preheating techniques, screen size distribution, and feed rate of the crude. For the specific intended uses, the art of perlite expanding has developed to the point that much is known about the effect of these variables on the end product. The requirements, however, for an aggregate to be used in plaster are different from those for an expanded perlite to be used in lightweight concrete or for cryogenics. In the study of perlite, many practical questions remain unanswered. One of the most important is, "why do some perlites make hard aggregates while others cannot resist crushing or compaction?" The usual tests and methods for evaluation of nonmetallic substances have been tried and have contributed their share to our knowledge. But chemical analyses, compaction resistance tests, screen analysis, etc., will reveal only a limited amount of information. The answers to these complex questions may well be found in an examination of the intemal structure of the expanded particle. Such questions and the ex-

Jan 1, 1962

By Allan T. Gwathmey, J. Bruce Wagner, Kenneth R. Lawless

Between 250°and 550°C in oxygen pressures of 10 to 760 mm Hg, the relative oxide thicknesses formed per unit time on the (100), (111), (110), and (320), decreased in this order. The predominant oxide orientation was (001)Fe3O4 and [110] Fe304 A small amount of a-Fe2O3 which exhibited a fiber pattern was observed in all oxides except those formed at 250°c in low oxygen pressures. IN order to understand the properties and behavior of thin films, particularly their role in oxidation reactions, there is needed more experimental information on their structure, composition, and kinetics of formation on clean surfaces of known geometry. The present study was undertaken to obtain such information for thin oxide films formed on single crystals of a body centered cubic metal, iron. Crystals in the form of spheres were used in order to expose all possible crystal planes to the reactant gases simultaneously. Using this procedure the relative rates of oxidation of all planes could be estimated, and those exhibiting, maximum or minimum oxidation rates could be selected for a more intensive study of composition and expitaxy. Since the three types of information were obtained from the same experiment using a single crystal substrate, any differences between rate, composition, and expitaxy on the several planes may be attributed to the influence of the substrate structure. EXPERIMENTAL The starting material for this study was Armco iron rods, 6 in. long and 3/8 or 1/2 in. in diam. The analysis was reported to be 99.8 pct Fe, with major impurities listed as carbon 0.018 pct, manganese 0.027 pct, phosphorous 0.005 pct, sulfur 0.029 pct, silicon 0.005 pct, and copper 0.11 pct. These rods were cleaned with ether and heated in an atmosphere of moist hydrogen at 950°C for three days. The purpose of this treatment was to decarburize the iron and to provide a consistent, uniform grain size for the growth of single crystals. Crystals in the form of rods, up to 1/2 in. in diam and 2 in. long, were prepared by a method similar to that reported by Leidheiser and Buck.2 Spherical crystals, 3/8 and 1/2 in. in diam and having a handle about 1/4 in. in diam by 112 in. long, were machined from the single-crystal rods. After machining, each crystal was etched in aqueous nitric acid to remove the cold-worked metal at the surface. Before each experiment, the crystal was polished mechanically with metallographic papers through number 4/0, and electropolished in a perchloric acid-acetic anhydride mixture by the method of Jacquet and Rocquet.3 The crystal was washed in running distilled water for at least 5 min. The excess water was blotted with a soft paper tissue, and the crystal was placed in an all-glass reaction vessel (See Fig. 1). The crystal was heated at 550°C in hydrogen for at least 8 hr prior to the oxidation in order to reduce any surface oxides and to help relieve any stresses in the metal. For the structure and composition studies, flat faces were cut parallel to (loo), (111), and (110) planes on the iron crystal spheres. The orientation of these faces was checked by a back-reflection X-ray diffraction technique. The faces were within 2 deg of the desired orientation. The flat faces were treated as described above except that prior to electropolishing they were given an additional polish on metallographic felt saturated with twenty-minute levigated alumina. After the crystal was heated in hydrogen for at least 8 hr, the temperature was adjusted to the desired value, and the hydrogen was evacuated. Commercial oxygen which had been purified by successively passing through tubes containing magnesium perchlorate, Ascarite and magnesium perchlorate was admitted to the desired pressure as measured by a mercury manometer. A resistance-wound furnace surrounded the oxidation chamber, and a temperature controller maintained the temperature within ±3°C. The furnace was provided with a small window for observing the crystal. The changes in thickness of the oxide films were followed by observing the interference colors. The oxidation was allowed to proceed until the desired oxide thickness was attained on a given crystal plane. The experiment was terminated by evacuating the oxidation

Jan 1, 1962

By J. D. R. Neilsen

The objective of the research conducted and presented herein was to determine the effect of pre-established free gas saturation on the sweep efficiency of an isolated inverted five-spot well pattern. The investigation concluded that the ultimate recovery of an isolated inverted five-spot may be slightly increased by establishing a free gas saturation prior to water flooding; however, of more significance is the extreme deviation of the pattern's performance after water break-through from that commonly obtained from developed well patterns. The rapid "water-out" characteristic common to both linear floods and floods conducted in developed well patterns was not evidenced in the isolated inverted five-spot. Instead, the wells continued to produce oil long after breakthrough until ultimate areal sweep efficiencies of four, five, and six hundred percent were obtained prior to the water-oil ratio becoming excessive.

Jan 1, 1962

By S. Wiederhorn

The energy and force of interaction between a crack and a slip band have been calculated. When the distance between the crack and the slip band is greater than the dislocation spacing of- the slip band, the force on the cgrack is perpendicular to the slip band. The energy needed to propagate a crack against this force can be lawe enough to pevmit crack propagation parallel to noncleavage planes. SEVERAL recent experiments have demonstrated the occurrence of crack-slip band interaction in ionic crystals having a NaC1-type structure. Stokes, Johnston, and Lil have studied the nucleation and growth of cracks in MgO. From their observations, they conclude that slip bands have the ability to halt and stabilize cleavage crack nuclei. Gilman2 has shown that a crack, propagating along a (100) cleavage plane in a previously deformed LiF crystal, tends, at certain points within the crystal, to switch to (110) planes. He reasons that plastic deformation reduces the cohesive energy of the (110) planes below that of the (1130) planes, making possible (110) crack propagation. Keh3 has demonstrated that when indentations are made in MgO, crkcks form along (110) planes at the indentations. Gilman2 attributes the formation of these cracks to plastic cieformation. There is some doubt as to the formation of cracks on (110) planes. Kuznetsov4 in his discussion of crack propagation in rock salt, shows that splitting along (110) planes requires 1.76 times as much energy as splitting along a stepped (100) surface. Therefore, the observed (110) cracking in LiF and

Jan 1, 1962

By H. P. Leighly

WORNER1 briefly studied the embrittlement of titanium by mercury. He found that mercury will wet the titanium surface at 400°C in vacuo, if the specimen had been heated previously to 700°C to dissolve the oxide coating. Subsequent exposure to the atmosphere causes the mercury film to recede rapidly. Bending of the titanium specimen even after the mercury film has receded results in a brittle fracture. For the study of the embrittling effect of mercury on titanium, specimens 2 by 12 by 0.051 in. were cut from RC-130-A sheet, an alloy having a nominal 8 pct Mn content and a mixed a-ß structure. The specimens were stressed horizontally at a predetermined value after which a plastic ring having a cavity 1/2 in. diam by 1/2 in. deep was placed on the specimen. The cavity was filled with mercury and a hole was drilled in the specimen through the pool of mercury. If the stress level was high enough, fracture occurred instantaneously with the drilling. By repeating the test at different stress levels, the threshold stress can be determined. Mercury embrittlement causes a drastic reduction in the ultimate tensile strength of this alloy from 132,000 psi to about 15,700 psi. The drilling of the hole, in the absence of mercury, does not change the tensile properties. Fig. 1 shows the typical fractures observed as a result of the embrittlement of this alloy by mercury. The central portion of the fracture was brittle represented by the jagged region which appears to have occurred on the shear planes at about 45 deg to the stress axis. Ductile fracture, which is perpendicular to the stress axis, occurred near the specimen edges accompanied by a reduction of the specimen thickness. Examination of the fracture reveals that only in the brittle region does mercury wet the

Jan 1, 1962

By A. S. Yue

The movphology of the Mg-32 wt pct Al eutectic has been studied as a function of freezing- rate and temperature gradient. At slow freezing rates a lamellar eutectic was formed; whereas, a rod-like eutectic was generated at fast rates. The inter-lamellar spacing increased as the freezing rate decreased in aggreement with theoretical predictions. Lamellar faults, morphologically similar to edge dislocation models in crystals, were responsible for the subgrain structures in the eutectic mixture. A linear increase in fault density with freezing rate was observed. Fault concentl-ations of the order of 10 per sq cm for a range of freezing rates from 0.6 to -3.0 x 10 cm per sec were estimated. The transformation from lamella?, to rod-like morphologies was determined experimentally to be dependent on the freezing rate and independent of the temperature gradient. Moreover, the number of rods formed per- unit cross-sectional area increased exponentiallv with increasing freezing rote. BRADY&apos; and portevin2 classified eutectic structures into lamellar, rod-like, and globular according to the morphology of the solid phases present. Although this classification is quite descriptive, very little has been reported on the details of the mechanism by which the eutectic structures are formed. Recent work by Winegard, Majka, Thall, and chalmers3 and by chalmers4 on lamellar eutectic solidification suggest that the maximum thickness of the lamellae decreases with increasing rate of solidification due to inadequate time for lateral diffusion. scheilS and Tiller&apos; have shown theoretically that the lamellar widths indeed depend on the solidification rate. However, there has been no experimental evidence to support the theory. Chilten and winegard7 have studied the interface morphology of a eutectic alloy of zone-refined lead and tin. They found that the lamellar width decreased as the freezing rate increased in agreement with the theoretical predictions of scheils and Tiller.&apos; More recently, Kraft and Albright&apos; have investigated the microstructures of the A1-CuA12 eutectic as a function of growth variables. They observed lamellar faults present in the lamellar eutectic, similar to edge dislocation models in crystals. Furthermore, Kraft and Albright reported that they could not designate which extra lamellar was responsible for the formation of a lamellar fault even under electron microscopic magnification. In this paper, the morphology of the Mg-A1 eutectic structure is described. The effects of freez- ing rate on the interlamellar spacing and on the lamellar fault density are presented in detail. The transformation from lamellar to rod-like eutectics is discussed in terms of the freezing rate and the temperature gradient. EXPERIMENTAL PROCEDURE The experimental details of alloy preparation, the decanting mechanism and the determinations of the freezing rate and the temperature gradient have been reported elsewhere. Measurements of plate-edge angles were made with a microscope. The true angles used to determine the interlamellar spacings were determined by a two surface analysis technique.&apos;&apos; Since the decanted interface structure does not represent the true eutectic morphology on the solid,g all measurements were made from an area in the solidified bar behind the interface. Measurements of the apparent interlamellar spacings between the two phases of the eutectic were made on a photographic negative by means of a calibrated magnifier. Each value listed in Table I represents the average of thirty measurements on one negative. In general, these measurements are approximately equal with an error of less than pct. The average rod diameter for each specimen was also measured on a magnified photomicrograph. Each value of the diameter represents the average of fifty measurements. RESULTS AND DISCUSSION The experimental observations and their discussion to be presented here are restricted to the morphology of the eutectic structure and to the effects of the freezing rate and the temperature gradient on the solidification of eutectics. INTERLAMELLAR SPACING It has been shown previouslyg that the micro-structure of the decanted interface and the longitudinal section of the Mg-A1 eutectic is characterized by the presence of both lamellar and rod-like morphologies. The lamellae become more regular as the freezing rate is decreased. A three-dimensional photomicrograph representing a perfect lamellar morphology is illustrated in Fig. 1. The lamellae of the top and longitudinal sections of the specimen are regularly spaced while those in the transverse section are not quite straight and parallel. Their parallelism is slightly distorted because fault lines producing a discontinuity are present. A method for calculating the interlamellar spacings A, is described in Appendix 1. The true

Jan 1, 1962

By D. I. Bardos

The occurrence of Laves phases (AB,) in various binary alloy systems has been reviewed in recent papers.13 Iron forms Laves phases with Sc-, Ti-, V- and Cr-group elements. However, two of the corresponding Laves phases with cobalt, namely MoCo, and WCo,, are missing. Nickel forms binary Laves phases with Sc and Y, but not with any Ti-, V-, or Cr-group element. These conditions are schematically illustrated in Table I. That electron concentration is a significant factor in determining which type of Laves phase is formed in a given case was recognized long ago by Laves and Witte,4 This concept has been more recently applied to Laves phases formed by transition ele-ments. It now appears that the average electron concentration (average number of electrons per atom outside of the closed shells of the component atoms) may be an important factor also in determining whether or not a Laves phase can occur at all in a given system. As shown in Table I, in the transition element systems considered Laves phases are absent at electron concentrations of 8, or larger (to the right and below the double line in Table I). These absences clearly cannot be accounted for on atomic size considerations, as evidenced by the many inconsistencies apparent in Table 11. While the ideal radius ratio for Laves phases is 1.222, in the systems which do have Laves phases the ratios of CN 12 radii range from 1.10 to 1.46. The consistent absence of Laves phases at RA/RB< 1.10 might be attributed to the low values of these radius ratios. However, Table II shows that absences also occur irregularly throughout the radius ratio range covered. In a previous paper7 it was concluded that, in transition element systems forming u-phases, silicon may act as an acceptor of electrons, thus stabilizing the u-phase at electron concentrations higher than

Jan 1, 1962

By C. H. Li, R. D. Carnahan, R. J. Stokes, T. L. Johnston

When silver chloride deforms by pencil glide at temperatures of 26ºand 72°C, grain size has no effect upon the proportional limit and the material necks down to a knife edge under tension. At -196ºC, deformation takes place on fewer slip systems to produce straight slip traces, the flow stress becomes sensitive to grain size and fracture occurs by cleavage from an intergranular source without any reduction in area. THERE are significant differences between the appearance of the slip bands formed in silver chloride and in the alkali halides at room temperature. The bands in sodium chloride, e.g., are fine and geometrically straight, whereas in silver chloride they are coarse and wavy.&apos; Such differences in the slip behavior prompted us to inquire what the effects of grain boundaries might be on the mechanical properties of these solids. As an introduction to a general study of ionic poly-crystal behavior, we have investigated the effect of grain size on the stress-strain relationships in silver chloride at different temperatures. We have chosen silver chloride chiefly because polycrystals can be easily prepared free from cracks and macroscopic voids by conventional techniques. Moreover, as we shall see, the slip behavior can be readily modified by changing the temperature. It will be shown that the effect of grain size on the yield stress of silver chloride is strikingly dependent upon the temperature of deformation and that this temperature effect comes about through a change in the number of slip systems which operate at the onset of plastic flow. EXPERIMENTAL PROCEDURES Polycrystalline tensile specimens were made by recrystallizing cold-rolled AgCl sheet. Thirty-gram quantities of AR grade silver chloride powder were melted in a low heat capacity furnace, cast into cylindrical forms 3/4 in. in dim and approximately 1 in. in length and then extruded with a 16:l reduction ratio into rods 3/16 in. in dim. Extrusion temperatures were varied from room temperature to 350°C. In order to impart various degrees of cold&apos;work to the extruded rod. All extrusions were then cross rolled to sheet 0.040 in. in thickness at room temperature and machined to form tensile specimens having a gage length of 0.750 in. with a width of either 0.250 or 0.145 in.* Annealing was carried out in an air oven at 200°C for periods up to 20 hr. specimens having average grain diameters ranging from 0.024 to 0.40 mm were prepared by varying the extrusion temperature and annealing time in the conventional manner. To obtain specimens with grain sizes larger than 0.40mm, lightly deformed thin prisims of silver chloride single crystals (supplied by Harshaw Chemical Co.) were recrystallized. Grain size determinations were made by an intercept method and revealed that the grains were equi-axed. Laue back-reflection X-ray patterns showed little tendency to form a preferred orientation texture. Specimens which were to be used for the slip band studies were polished by immersion in fresh boiling concentrated NH,OH for 60 sec. They were then etch polished for 10 sec on each side by hand lapping on a stationary velveteen lap wetted with a dilute Hypo solution (5 g of Kodak Acid Fixer in 100 cc H20). Finally the specimens were rinsed in warm water and alcohol, blown dry and carefully mounted in the tensile machine for testing. Tensile tests were performed at three temperatures, namely, 26º, -72º, and -196°C. A screw-driven hard tensile machine was used at a constant strain rate of 0.006 in. per in. per min. Loads were determined with a light- proof ring fitted with A-18 strain gages and extensions were measured with a 0.0001 in. dial gage. Constant level baths of alcohol with dry ice and liquid nitrogen were used to maintain the two lower test temperatures. EXPERIMENTAL RESULTS Reproducibility—In view of the light sensitivity and reactive nature of silver chloride, it was necessary to determine whether reproducibility depended upon either exposure to light or to the condition of the surface. However, during the course of the work it became clear that variation of laboratory lighting

Jan 1, 1962

By F. Weinberg

In developing a mechanism for the solidification of metals from the melt, it has been proposed that solidification proceeds by the growth of platelets parallel to close packed planes. The evidence for this is based primarily on observations of decanted interfaces of lead1,2 and tin on which platelets 1 to 10 µ thick4 were observed. In recent observations of decanted eutectic alloys, 5,6 it was found that the eutectic structure on the decanted surface was markedly different than that of the bulk material, with the surface structure extending approximately 10 µ behind the interface.&apos; This suggested that, at least for these experiments, a residual liquid layer 10 µ thick had been left on the decanted interface, which solidified subsequent to decanting. If a similar thickness of residual liquid was left on the decanted surfaces in the lead and tin observations referred to above, then it is questionable to what extent the observed platelets can be related to the solid-liquid interface before decanting. The purpose of the present investigation was to measure the thickness of the residual liquid layer on a decanted surface of tin, using relatively standard decanting procedures. The technique used was to add approximately 200 ppm of Tl204 (PI) to the melted portion of a high purity (99.999 pet) bar of tin, which was being progressively melted from one end, and then decant during melting. Since only the melt contained the radioactive tracer, the activity emanating from the decanted surface could be used as a measure of the thickness of the residual liquid layer. Progressive melting was carried out in the same fashion as single crystal growth, namely, in a horizontal graphite boat, in an argon atmosphere, using a moving furnace. The decanting was done in two ways; 1) removing the furnace and suddenly dropping the melt end of the boat, and 2) suddenly jerking the solid away from the liquid by the action of a falling weight (estimated peak acceleration 3 x 105 cm per sq sec), using a split graphite container. In all cases the melt was vigorously agitated by bubbling argon through it. The activity of the decanted surface was measured through an aperture 1.5 cm by 0.5 cm in a lead shield with an Anton tube geiger counter. Assuming that the active layer on the surface had the same concentration of Tl204 as the decanted liquid, the thickness of the layer could be determined from the measured activity of the decanted material, and the relationship between activity and material thickness. The latter was determined by rolling some of the decanted material into foil and measuring the activity of multiple layers of the foil. The activity At of material of thickness t (in mm) was determined to be A, = Ao(1 - e-22.5t) where Ao is the activity of the bulk material. The results of the measurements of the thickness of the residual liquid layer for six decants are given in Table I. The variation in t is attributed to variations in the decanting procedure and the rate of melting, the latter being difficult to control because of the vigorous agitation of the liquid. The rate of melting was in the order of 2 cm per hr, estimated from the position of the solid-liquid interface during melting. The results indicate that a residual liquid layer of the order of 10 µ in thickness is left on the decanted interface in agreement with the observation on eutectic alloys referred to above. If the mixing of the liquid during melting is not complete, as was

Jan 1, 1962

By T. Leser, A. W. Jenike

The problems of caving and underground subsidence can be considered as the failure of a highly compacted rock and its subsequent flow in the form of broken rock. The problem is complex because the propagation of failure and flow have to be considered simultaneously; the yield strength of the virgin rock and the broken rock are different; and, while under certain conditions it is sufficient to consider the virgin rock as homogeneous, the density and the yield function of broken rock are both pressure and time dependent. A study of the failure and flow of solids with a pressure dependent yield function has been published recently by Jenike.&apos; In this paper the density of the broken rock is assumed to be only time dependent and the consequences are examined in the case of one-dimensional vertical subsidence into an initial cavity. The following describes an attempt to develop a tool which, in combination with other tools, may lead to mathematical solutions of real problems of caving and subsidence. STATEMENT OF THE PROBLEM An underground cavity of horizontal cross section 4 = 1 and height 6 is assumed to exist at some depth below the surface. At the time t = 0 rock above the cavity fails and completely fills out the cavity with expanded broken material. With passing time the broken rock consolidates and subsidence proceeds continuously upuard in a vertical shaft. The phenomenon is one-dimensional (see Fig. 1). The problem consists of finding the displacement and the velocity with which the frlmt of the subsidence (wave front) moves upward as a function of the time and of the rock properties. DIFFERENTIAL EQUATIONS CONTROLLING THE PHENOMENON With the assumptions that the broken rock is a continuum and that the subsidence occurs continuously, we can apply the one-dimensional differential equation of contitiuity (conservation of mass) and the equation of preservation of momentum The latter equation is replaced by an assumed relation based on experience, which takes care of the

Jan 1, 1962

By Roy L. Wilfong

The thermal decomposition of the ammonium sulfate, carbonate, nitrate, oxalate, and sulfate salts of praseodymium, neodymium, and samarium was investigated thermogravimetrically in the temperature range 25° to 1,500° C. Each salt was decomposed at a heating rate of 2.5° C, per minute. The pyrolytic sequences have been identified and the temperatures of formation of inter-mediates, the minimum oxide formation temperatures, and values for loss on ignition have been determined. The nonstoichiometric ranges between Pr6011 and Pr203 and the extent of these ranges have been determined for oxides derived from the carbonate, nitrate, and oxalate salts of praseodymium. The alum and sulfate salts of praseodymium produced the sesquioxide without forming the intermediate non-stoichiometric oxides. The temperature limits of formation and regions of stability for the alums and sulfates were better defined than were those for the carbonates, nitrates, and oxalates. The minimum oxide formation temperature increased in the order of samarium, neodymium, and praseodymium irrespective of the anion.

Jan 1, 1962

By J. H. Brophy

Experimental evidence in recent years shows that nickel coated hydrogen reduced tungsten powder can be sintered to 98 pct of theoretical density at 1100°C. New data indicate that the sintering rate is the same for nickel contents ranging from 0.125 wt pct (mon-atomic layer) to 5.0 wt pct Ni coated on 0.561. tungsten powder. Nickel tungsten made by coreduction from oxides sinters in a kinetically similar way, but the rate tends to increase with higher nickel contents. The activation of sintering can be accomplished with a minimum amount of nickel if coated powder is used. Transverse rmpture strength was found to increase in specimens containing 0.25 pct Ni as density increased during the initial stage of the carrier-phase sintering process. Upon the onset of grain growth in the final stage, strength was found to decrease. With increasing nickel contents up to 4 pct, strength increased. Maximum strengths in three-point loading were observed at 73,000 psi for 0.25 pct Ni and 93,000 psi for 5 pct Ni. These were comparable to that of massive tungsten recrystal-lized in the presence of nickel and tested in the same way. The results were sensitive to the mode of powder treatment and ductility was negligible in all cases. The study and application of sintered bodies of nickel and tungsten is not new; however, the analysis of the mechanism by which small additions of nickel increase the sintering rate of tungsten promises to Contribute new information regarding sintering theory in general. Initial experimental evidence was presented by the authors showing that nickel-coated hydrogen-reduced tungsten powder may be sintered to 98 pct of theoretical density at 1100°C in 16 hr.&apos; Simultaneously, a kinetic analysis of the process showed that it took place in two distinct stages. In the first stage, nickel evidently served as a carrier phase through which tungsten atoms could move. This stage was kinetically similar to the &apos;solution-precipitationo step postulated when the carrier phase is liquid3 although in the nickel tungsten case, there is no evidence of the existence of a liquid phase either in equilibrium phase relationships or in mi-crostructures at the temperatures under consideration. In the present work, new data for nickel-coated tungsten powder are offered in support of the proposed mechanism, and a more explicit study of the second stage of densification is presented. Concurrently, the sintering kinetics of these coated powders are compared to Ni-W powder made by coreduction of oxides. In this way the present work can be compared to earlier results in nickel activated sintering of tungsten in which the coreduction process was emplyed. The ultimate utility of such an activated sintering process will be determined to some extent by the mechanical and physical properties of the final prod-

Jan 1, 1962