By G. Bitsianes

An experimental procedure was developed for studying magnetic roasting on a accurately-controlled laboratory scale. The loss-in-weight method was used and the course of reduction could be followed under a reducing gas atmosphere containing as many as five different components. Some important variables of the operation were checked on a marginal Mesabi iron ore containing porous and dense varieties of hematite as well as pure goethite. The conditions simulated were those for the grate roasting of a coarsely-sized ore burden. Temperature was maintained at 600°C; gas composition at 4.25% CO, 4.25% H2, 17.0% CO2, 15.0% H20, and 59.5% N2,, and gas flow rate at about 1,5 lineal feet per minute. The ore charge was composed of quarter-inch cubes. Under these conditions, the ore porosity was found to be one of the governing variables of the operation. Results showed that an ore size limitation existed as a function of this ore porosity. For efficient magnetic conversion, the size limit was 3/8 inch for very porous ores and about 65 mesh for very dense ores. An anomaly was noted in the weight losses incurred during actual magnetic conversion. For goethitic ores, these were generally about 13 per cent higher than could be accounted for theoretically. The effect was attributed to possible non-stoichiometric structures forming during the reduction process.

Jan 1, 1960

By D. L. Wood

This investigation was concerned with the aluminum-oxide particle dispersions, the mechanical properties, and the re-c,uystallization characteristics of some internally oxidized copper-aluminum alloys. Obserued hardness vaviations are in agreement with variations in oxide particle size revealed by electron metallographic studies. The increase in yield strength caused by internal oxidation is quite sensitive to matrix grain size and is accompanied by a loss of ductility, particularly at higher temperatures. Elevated temperature ductility is con-side,vably improved if major grain reorientation is accomplished by ve recrystallization prior to testing. The oxide particles offer a considerable restraint to softening during annealing after cold deformation. THE diffusion of oxygen under appropriate conditions into a suitable alloy causes solute oxide particles to be precipitated at an inward moving interface.1,2 Previous work has shown that the hardness

Jan 1, 1960

By Kenneth A. Gutschick, Robert S. Boynton

Lime has become a very general loosely used term that includes virtually all finely divided types of limestone as well as burned forms of lime. However, actually (and according to Webster) lime is only calcined limestone (known as quicklime, calcium oxide, or calcia). It also embraces the secondary product of quicklime-namely hydrated lime or slaked lime (calcium hydroxide). Fundamentally there are two basic types of limestone-high calcium and high magnesium (dolomitic). The dolomitic quicklimes and hydrated limes correspond to their "high calcium" counterparts in terminology. The only difference is that the dolomitic types are a combination of the elements, calcium and magnesium, whereas high calcium limes contain only 0.5 to 2 pct of magnesium. Both types, which are made through calcination at high temperatures, are shown chemically as follows: [ ] In the above reactions either type of limestone is burned (calcined) in furnaces known as lime kilns so that the carbon dioxide content of the stone is expelled as a gas. With high calcium limestone 44 pct of the weight of the stone is lost; with dolomitic limestone the loss is 48 pct. Also, both reactions are chemically reversible since quicklime absorbs carbon dioxide readily and in so doing transforms itself back to the original carbonate form. Most quicklimes correspond in size to the original rock, which varies from one to eight inches, depending upon the type of kiln employed. Slight shrinkage occurs during calcination. A few limestones when calcined will decrepitate (break down) into a fine powdery form; however, chemically it is the same as the pebble or lump-sized material. For some uses the lumps of quicklime are pulverized and packaged. Since quicklime has great affinity for moisture and carbon dioxide, it is perishable. When it absorbs moisture and CO2 slowly from the atmosphere, the resulting product is "airslaked." Consequently, it must be stored in dry, moisture-proof areas that are free from CO2. Because of its fugitive nature, it is usually consumed within a few weeks after manufacture. A more stable form of lime is hydrated lime-commercially made by adding water to the quicklime until the lumps break down into a fine, white powder. This product, which is usually packaged, can be stored more safely; and many of its uses are interchangeable with quicklime. The irreversible chemical reactions of hydrated lime for both high calcium and dolomitic types are: [ ]

Jan 1, 1960

By Kenneth M. Ritchie

Mineral wool is a term applied to man-made fibers of silicate glass with useful properties resulting from their fibrous nature. In contrast with crystalline fibrous minerals such as asbestos, mineral wool fibers are amorphous, solid filaments produced by drawing from molten liquid and subsequent cooling. Chemically they are silicate glass with varying percentages of metallic oxides, especially those of aluminum, calcium, magnesium, iron, and in glass wool, sodium, potassium and boron. Other elements such as manganese, titanium, sulfur, etc., result from their presence in the raw materials used and are not purposely added. In the United States, mineral wool is a generic term and may be applied to rock, slag or glass wool. In Europe, glass silk and silicate cotton are products in the same category, but the term mineral wool is less commonly used. Current usage is to ignore the actual source and to differentiate products on a composition basis; thus rock and slag wools have about 35-45 pct of silica, while glass wool has 54 to 60 pct. Much mineral wool of slag origin is called "rock wool," and this practice is increasing, although wool made of slag from lead or copper refining is often referred to as "lead slag wool." Its greenish-gray to greenish-black dark color, due to 5-25 pct Fe (reported as FeO), distinguishes it from "white" wools made from iron, blast furnace slag containing only 1-2 pct FeO or Fe203. Most mineral wool is used for thermal insulation against heat and cold; sound absorption and isolation are probably the next most important uses. Both its thermal and acoustic values result primarily from the physical structure of the heterogeneous mixture of fibers and air which is the form in which the fibers are first obtained and handled. For this reason, within fairly wide limits, differences in chemical composition are relatively unimportant, and for most conventional applications all types are competitive in properties and value. Mineral wool intended for extreme conditions of high temperature, acid resistance and special purposes must have a chemical composition which will insure the desired properties. This may differ greatly from that of ordinary wools; for example one product approximately 98 pct Si02 and another consisting of 50 pct A1203 and 50 pct Si02 are produced and sold for high temperature service up to 2000°F or more. These are considerably more expensive to manufacture and their cost limits their use. Historical The manufacture of mineral wool consists fundamentally of a process which subjects molten material to shear and/or tensile forces that draw them into fibers. The liquids are cooled at a rate which solidifies them quickly. As a solid glass they are technically super-cooled liquids since they have no true melting point. The drawing out of glass into thin rods, filaments and tubes was known from very early times, and present day continuous production of glass filament for textiles was evolved gradually by adapting hand methods to automatic machinery. Rock and slag wool manufacture had a somewhat different development. Early explorers reported finding filamentous material

Jan 1, 1960

By H. S. Caldwell

This report describes work by the Bureau of Mines on the vacuum distilla¬tion of some of the more volatile metals such as cadmium, zinc, and magnesium from lead and tin. Evacuation within a distillation apparatus allows rapid diffusion of vapor away from the evaporation surface and prevents reaction of the vapor with residual gases. A reduction of pressure to several tenths of a millimeter makes possible practicable distillation rates, at temperatures for which the partial pressure of the metal vapor exceeds 10-3 atmosphere. The rate and selectivity of distillation depend primarily on the volatility and molal ratios of the alloy metals, and their chemical activity to each other. For very rapid evaporation or low concentration of the more volatile constituent, the rate is determined by the rate of diffusion of the evaporating metal, to the surface of the melt. Cadmium, zinc, magnesium, and tellurium were found to volatilize readily from both lead and tin. Tellurium appears to volatilize as an intermetallic compound rather than the pure metal. Antimony could not be removed from lead at 1,000° C.; the condensate was nearly all lead. Antimony, bismuth, and lead were removed from tin.

Jan 1, 1960

By J. Intrater, E. S. Machlin

In a study of grain boundary sliding in superpure Copper (99.999 pct),&apos; bicrystals of a specific shape were used, Fig. 1. That shape was adopted in order to minimize the deformation of grains on both sides of the boundary due to clamping. Another requirement was to obtain bicrystals with a rnicroscopically straight boundary, Fig. 2. Single crystals of predetermined orientation (growth axis parallel to <310>) were grown in a graphite mold from seed crystals. The apparatus for growing single crystals consisted of a vacuum system, argon purification train, vycor tube (in which a graphite mold was placed), a carriage for the induction coi1,and a Lepel (7-1/2 KW) high-frequency converter. The graphite mold was heated by induction and the charge in turn was heated by conduction. The induction coil was moved by means of a motor at a speed of 1 1/2 in. per hr. Single crystals of two different orientations were grown from the melt in one-half of a split graphite mold, Fig. 3(a). Two such crystals were then placed in contact with each other in another split mold, Fig. 3(b) using tapered inserts. The pair of crystals was then remelted starting 2 in. from the top to insure that the whole top portion of the crystals was maintained molten. By moving the induction coil

Jan 1, 1960

By Douglas Castleberry

The degree of fragmentation obtained in primary quarry blasting has always been a factor in the speed of digging&apos; the muckpile This paper will discuss a case history of increased production and associated lowered costs from increased fragmentation. The quarry under discussion is fairly new, located in Georgia, and is in the large operation .category. Loading is done by three yard shovels, and, primary crushing by a 48" x 60" haw crusher preceded by a 5&apos; wide feeder. The stone is a hard granite gneiss, of Los Angeles rating 22, and apparent specific gravity is 2.68. The product is shipped to points in that state for railroad ballast, concrete aggregate, and road building stone. Inasmuch as fairly large shovels and a large Jaw were to be utilized, initial drilling and blasting were pointed toward producing fairly large sized muck for this large equipment. This was following a concept somewhat in vogue for some years in the Southeast wherein many large equipment plants would tend towards larger fragmentation, and smaller equipped plants would conversely tend toward attempts at smaller sized rock piles for smaller shovels and crushers.

Jan 1, 1960

By A. S. Yue

It was deemed desirable to obtain an understanding of the vacuum desulfurization process. McKechnie1 has reported that the sulfur content of nickel- and cobalt-base alloys is reduced in vacuo. Keverian and Taylor2 have observed that vacuum melting causes desulfurization of iron-carbon-silicon alloys. Garnyk and samarin3 have desulfurized transformer steel by vacuum treatment. Experiments were conducted in order to investigate the desulfurization of liquid iron under reduced pressures, and to establish the effect of some alloying elements, and various crucible materials. A vacuum-induction furnace of 50-lb capacity was used. The charge was Armco iron. Silicon was added as 90 pct ferrosilicon, carbon as electrode graphite, and aluminum as high-purity aluminum metal. Magnesia and silica crucibles were used, their inside diameters were 5 1/2 and 5 3/8 in., respectively. The temperature was measured with an optical pyrometer and it was held at 1600 1 15°C. Samples were withdrawn with quartz tubes of 6 mm ID, without disturbing the furnace atmosphere. Pressures were measured with an alphatron gage. The experimental results are shown in Fig. 1. They indicate that: 1) Sulfur can be removed from liquid iron alloys by vacuum treatment; 2) The desulfurization is enhanced by the presence of silicon, carbon, and aluminum, all these elements increase the activity of sulfur dissolved in liquid iron;4 3) The pronounced effect of silicon indicates that probably a volatile silicon sulfide is formed, Alcock and Richardson5 have observed a similar phenomenon; 4) The same rate of desulfurization was obtained when the metal was contained in either magnesia or silica crucibles. Dr. J. Keverian has contributed many discussions and recommendations. M. S. Sutliff has helped in conducting the heats. The permission of General Electric Co. for this publication is gratefully acknowledged.

Jan 1, 1960

By James A. Barr

Phosphate rock is a natural rock containing one or more phosphate minerals usually calcium phosphate, of sufficient purity and quantity to permit its use, either directly or after beneficiation in the manufacture of commercial products.1 The principal minerals in phosphate rock have the apatite structure which may be represented by the type formula: Ca10(X2) (PO4)6 where X represents the hydroxyl group (OH), chlorine or fluorine, either singly or collectively. The calcium may be partly replaced by sodium, magnesium, and other positive ions such as manganese, strontium, lead, uranium, cerium, yttrium and other rare earths. The PO4 radical may be partly replaced by small quantities of UO4, AsO4, SiO4, CO3, SO4, or Vo4. A typical commercial rock is usually a calcium phosphate containing 3 to 4 pct fluorine, the major impurities being limonite or other iron oxides, clay, aluminum phosphates and silica as quartz sand. A little vanadium is present in most of the domestic rock deposits (except the Tennessee Brown Rock), according to Jacob, Hill, Marshall and Reynolds! A little uranium occurs in the Florida leached zone, as will be brought out later. The chemical analyses are reported as P205, or tricalcium phosphate Ca3(PO4)2, the latter often designated by the trade name BPL (bone phosphate of lime). Commercial analyses usually report iron and alumina as oxides, lime as CaO and silica or insoluble. Colony3 examined many samples of apatite, staffelite, dahlite and American phosphorites and concluded that all have identical X-ray diffraction patterns. The phosphates in the phosphate rock have very minute crystalline structures. The mineral apatite Ca3(F.Cl) (PO4) 3 is the principal primary source of the element phosphorus, and occurs widely distributed in igneous rocks but rarely in a minable mass. Only about 12 pct of the world production of phosphate rock comes from primary apatites; the remainder is derived from secondary phosphorites. These phosphorites have been formed by the alteration of sediments by solutions containing phosphoric acid. Such solutions have come from the weathering or leaching of igneous rock containing apatite, bone deposits of prehistoric animals, marine life or guano deposits. These phosphorites are mostly alterations of phosphatic limestones. The sedimentary phosphate deposits are of marine origin and may have been enriched by subsequent solution of the more soluble calcium carbonate by waters containing carbon dioxide, by physical concentration by wave action, and by redeposition of the dissolved phosphate ions. Uses of Phosphate Phosphorus is the spark of life and is the structure builder and one of the main elements of plant food (fertilizer). Without phosphorus, life cannot exist. A "complete" plant food[t] in addition to phosphorus compounds contains potash, which acts as a catalyst to convert nutrients to useful forms, nitrogen to supply the growth element and many minor elements. The cycle of supply of phosphorus is from the apatite to solution and soil, absorption of plant life, decay and return to the soil or by animal life feeding on the plants. With insufficient supply of phosphorus in vegetation, life is not prolific. If crops are removed from

Jan 1, 1960

By Robert W. Smith

Computation of the thermodynamic properties of the reaction products in the deflagration of explosive gas mixtures has been a most valuable guide regarding the possible kinetic mechanisms of homogeneous combustion processes. Knowledge of the physically possible end states is indispensable for understanding observed deviations from equilibrium in heterogeneous combustion. However such information on dust flames is entirely lacking. To complement a Federal Bureau of Mines study of stationary graphite dust flames burning in pure oxygen,6/ this report gives examples, at atmospheric pressure and room temperature, of composition profiles in an idealized oxygen-dust flame, with both mass and enthalpy being preserved. Similar profiles can be obtained from the data of the paper for elevated temperature and pressure.

Jan 1, 1960

By S. Weinig, J. Winter

The grain boundary adsorption of solutes as a function of bulk concentration and solution temperature was studied using internal-frictimz techniques. From the variation of the cor-responding energy of activation for the Phenomenon, the inter-actior2 energy between a solute atom and a high-angle boundary was calculated. Interaction energies in the range of 0.3 ev were obtained, and were used to obtain the actual concentration of solute at the grain boundary. In corroboralory creel, studies the direct grain boundary contribution to the total creep strain was measured. It was found that the interface creep varied with the type and magnitude of the solute adsorbed. Subscribing to the theory of their being energetically favorable sites at the grain boundary for solutes of both Positive and negative size deviations, ternaries were investigated in Which solutes of both types were present. A marked increase in the resistance to grain boundary creep was manifested. THE major difficulty which has been encountered in investigations of the grain boundary segregation of solutes has been the lack of a sufficiently sensitive method of measuring the amount of adsorbed solute at the boundary. For the general case of a high-angle boundary, no direct method of measuring the adsorption at the boundary has been found to date. Internal friction has been used in several studies of grain boundary adsorption1-3 and although it is somewhat indirect, it was demonstrated to have the necessary sensitivity. In this investigation the authors have used internal-friction techniques in conjunction with a study of the grain boundary contribution to the total creep strain. As both parts of the investigation were performed on the same specimens it was possible to combine a highly sensitive technique with a somewhat more direct method in order to obtain information about the adsorption phenomenon. From internal-friction studies the rate of increase of the activation energy was observed to be a function of the difference in size between the solute and solvent atoms. It was proposed that if Gibbs&apos; adsorption isotherm is considered, i.e., where r is the excess solute at the boundary, c is the bulk concentration, and ay/ac is the change in grain boundary energy with bulk concentration, then AH b/ac must vary in the same way as ay/ac and therefore In this way a relative measure of the grain boundary adsorption of solutes is directly obtainable from in-ternal-friction studies. If the previous work in the field of grain boundary adsorption of solutes is examined, certain apparent information is desirable if the phenomenon is to be understood. The most important questions that must be asked are as follows: 1) Is the adsorption of solutes at the grain boundary an equilibrium process? 2) Can the Mott model of the grain boundary be used as a basis of setting up an elastic interaction between the grain boundary and solute atoms? 3) Is it possible to obtain an exact measure of the excess solute at the grain boundary as a function of temperature and bulk concentration rather than merely a relative measure of the adsorption 4) Are the conclusions obtained from an indirect method such as internal-friction studies meaningful in considering gross grain boundary effects such as creep? EXPERIMENTAL PROCEDURE The material used in this investigation was Bureau of Mines "superpurity" titanium (79 Bhn—1500 kg

Jan 1, 1960

By Donald A. Brobst

The minerals barite (BaSO4) and witherite (BaCO3) are the chief sources of the element barium and its compounds needed for many industrial processes and products. Barite, the principal ore mineral, is found the world over and is abundant and widely distributed throughout the United States.3 Witherite is much less common than barite, though more desirable in many ways as a raw material for the production of barium chemicals. England is the chief producer of witherite. Witherite is not mined in the United States at the present time, but it has been mined with barite from a deposit at El Portal, California. Barite is also called barytes, tiff, cawk, or heavy spar. Ordinarily it is a heavy mineral that crystallizes in the orthorhombic system. It is colorless, white, or gray, and transparent to opaque. In some deposits barite is black, yellow, brown, red, green, or blue because of included impurities. The streak is white and the luster vitreous to resinous or pearly. The specific gravity of pure barite (65.7 pct BaO and 34.3 pct SO3) is calculated to be 4.5, but inclusions and impurities in natural barite may reduce this value considerably. Well-formed crystals are generally tabular and have three cleavages. The barite of many deposits, however, has an uneven fracture and an apparent cleavage caused by separation along planes between successively deposited layers. The hardness is 2.5 to 3.5 on Mohs&apos; scale. Commercially the terms "hard" and "soft" are used to refer to ease of grinding. Barite is relatively insoluble in water and acid, and thus can be used as a chemically inert material. Witherite, the natural carbonate of barium (77.7 pct BaO and 22.3 pct CO2), crystallizes in the orthorhombic system. The fracture is uneven and the luster is vitreous to resinous. The hardness is 3 to 3.5. The specific gravity of the pure mineral is calculated to be 4.29. It is transparent to opaque. The color is ordinarily white, gray, yellow, brown, or green. Geology and Distribution of Deposits Workable deposits of barite are widely distributed throughout the world in many geologic environments in sedimentary, igneous, and metamorphic rocks. Most deposits can be classified into three main types: (1) vein and cavityfilling deposits; (2) bedded deposits; and (3) residual deposits. 1. Vein and cavity-filling deposits are those in which barite and associated minerals occur along faults, gashes, joints, and bedding planes, and in breccia zones and solution channels. They also occur in various collapse and sink structures in limestone. Sharp contacts of the veins and cavity fillings with wall rocks are common. Barite cements fault and collapse breccia by replacement of the matrix or by filling voids. Large-scale replacement of the wall rocks beyond ore-controlling structures is rare. Barite in vein and cavity filling deposits is generally dense, "hard," and white to gray. Associated minerals are fluorite, calcite, ankerite, dolomite, quartz, and many sulfide minerals, especially pyrite, chalcopyrite, galena, and sphalerite. Gold, silver, and rare earth minerals occur with barite in some deposits in the western United States. Barite is also a gangue mineral in metallic ore deposits but production as a byproduct from such deposits will be affected by many economic factors. The host rocks are igneous, sedimentary, and metamorphic rocks of pre-Cambrian to

Jan 1, 1960

By G. L. Cook

The design of a dual-inlet system for a Consolidated model 21-103C mass spectrometer is described in detail. The system permits both high-mass and low-mass samples to be run by using a single instrument. The difficulties of using a single instrument for both purposes are given and a method of minimizing these difficulties through the use of the present design is discussed, After examining the experience of five years of use, the conclusions are that the bimodal operation is practical and the low-mass analyses had nearly the same precision as before the modifications to the instrument were made. In 1951, O&apos;Neal and Wier.5/ published the first description of the modifications made to a mass spectrometer so that the spectra of hydrocarbons with molecular weights up to 600 could be obtained. Further discussion of the equipment of O&apos;Neal appeared in 1953.6/ Also, Brown, Melpolder, and Young7/ described a parallel inlet system designed to reduce sorption effects at room temperature.

Jan 1, 1960

By H. B. Charmbury, D. R. Mitchell

Recovery of fine coal from solids reporting to wash water has become increasingly important. These solids range from about 28 mesh to 0 and constitute 3 to 7 pct by weight of the feed tonnage to a coal preparation plant. In the past they were usually wasted to streams, but present clean stream legislation makes it necessary to remove them from the wash water and, if economically possible, recover the associated coal as a saleable product. Where these solids are not wasted to streams or to slime ponds they are recovered by thickeners and filters. Since filter cake is often high in ash or sulfur, or both, it is not readily marketed or used. Common practice is to mix it with other plant products, generally slack or cleaned run-of-mine. Uniform blending is difficult, not only because the impurity is usually high, but also because during certain operating periods it is possible to get a concentration of this filter cake in a railroad or barge. At some plants filter cake has been derived from the froth flotation clean-up of Dorr thickener underflow. The operating circuits required for a froth flotation plant make this a comparatively high-cost treatment, and in the last few years experiments have been carried out with bulk oil methods. These also are quite expensive and lend themselves only to special situations. Table I gives some characteristics of thickener underflows for plants in the Pittsburgh area treating Pittsburgh seam coal. It will be noted that there is a concentration of impurities in the -200 mesh sizes.

Jan 1, 1960

By John C. Machisak

THIS CHAPTER of the Minerals Yearbook (Volume III) contains overall employment and injury experience for coal mines-bituminous, lignite, and anthracite; coke, petroleum and natural gas; and peat and slag plants; metal and nonmetal mines; sand and gravel operations; stone quarries; metallurgical plants, including metal mills and smelters; and nonmetal mills for 1959. Volume I of the yearbook contains injury experience and employment data in the metal, non-metal, sand and gravel, slag, and quarrying industries, and the milling operations and related plants. Volume II contains the injury experience and employment data in the fuel industries--coal, coke, petroleum and natural gas, and peat. Surveys conducted by the Bureau of Mines were the source of injury and employment data used to compile the tables and furnish information for the accompanying text. Response to the surveys was voluntary except that for coal mines. The Coal Mine Safety Act requires operators of coal mines to furnish the information requested.

Jan 1, 1960

By Donald R. Irving

THIS CHAPTER is new to the Minerals Yearbook and will appear regularly hereafter. Its purpose is to present statistics that reflect technologic trends in the minerals and metals industries (except fuels). Much useful information has been collected annually through the Bureau of Mines mineral commodity and employment and injuries canvasses. However, these data must be supplemented by further data to permit evaluation of the type, direction, and rate of technologic change, which are vitally important in long-term mineral planning. In addition to, and fully as important as, expanding the available data is the need to ascertain that the various items collected are obtained from identical reporting units, to enable direct comparisons to be made.

Jan 1, 1960

By Reno H. Sales

The syngenetic, metamorphic water, and source bed concept theories of ore deposition proposed by Anton Gray, C, Lo Knight and others, to explain ores in sedimentary rocks, are challenged on the basis of a survey of the literature and personal observation, A hydrothermal origin for the Northern Rhodesian Copperbelt deposits is indicated by the presence of post-Roan age igneous rocks and post-gabbro mineralization, the wide distribution of ore in the various Lower Roan lithologic types, and the zoning of the copper-iron sulphlde minerals and minor elements The proposal by Gray and Knight that igneous rocks are not favorable as guides to nonferrous metal deposits, and Gray&apos;s hypothesis that the redistribution of connate waters and their dissolved metals by metamorphic processes was responsible for the emplacement of ores, are rejected as contrary to field evidence, The absence of exposed potential igneous source rocks is shown to be an invalid argument for the proponents of any syngenetic hypothesis, The common association of ore deposits with calc-alkaline intrusive rocks and their derivatives is, however, demonstrated to be convincing evidence that an exploration program based upon a magmatic theory of origin, would have found most of the important known non-ferrous metal deposits of the world, It is urged that prospecting be continued on the sound basis of accumulated knowledge of the lithologic and structural facts surrounding known ore deposits.

Jan 1, 1960

By J. B. Gayle

The removal of coal particles from a slurry by flotation is made possible by the formation of stable aggregates with air bubbles of suitable sizes. The formation of such aggregates is theoretically possible only for certain favorable combinations of the solid-liquid-gas interfacial tensions. Because interfacial tensions involving solid phases are not conveniently measurable, a related variable, the contact angle, frequently is used as a measure of the floatability of various materials. Zero angles indicate nonfloatable substances, and large angles indicate substances having a high degree of floatability. During a study of contact angles for coal and substances related to coal in their similarity of response to various physical and chemical treatments, particularly flotation, carbonization, and oxidation, the reproducibility of replicate determinations taken within a 4-hour period was found to be much better than that for comparable results taken over a longer period of time. Consideration of possible causes for these differences led to an investigation of the effects of temperature variations on contact angles. References to literature revealed only a small amount of information, some of it apparently conflicting. Specifically, Sutherland and Wark4/ found that temperature variations "within limits" did not appreciably influence the angles measured for galena conditioned with potassium ethyl xanthate. On the other hand, McGlashan and McLeod5/ presented preliminary data showing that for sphalerite conditioned with potassium ethyl xanthate the angle is maximum at 25° to 35° C., depending on the pH of the system.

Jan 1, 1960

By C. A. O’Malley, F. W. Kinsey

This paper deals with an experimental study in the use of a preagglomerated burden as a means of increasing the production of sinter. The effect of a wide range of sinter burden was studied, including concentrates produced by a flotation process. Some of the important characteristics of a sinter bed are discussed along with the strength and reducibility of the sintered product. In recent years the use of sinter in blast furnaces has become increasingly important across the country—largely because of the demand for more hot iron from existing plant capacity and the increasing amount of fines in the burden materials available to the blast-furnace operator. In many instances, unfortunately, the demand for sinter has been so great that little time has been available to give the proper

Jan 1, 1960

By Kennedy G. L, Evans D. G

The development of the carbonization of brown coal briquettes to produce a hard char suitable for use in place of imported hard coke has continued in Victoria, and an experimental carbonization plant has recently been commissioned at Morwell by the Gas and Fuel Corpora.tion to assess the prospects for the commercial production and marketing of hard char in Victoria. The char offers advantages in its very low ash content and its uniform lump size, while the indications are that it could be marketed at a price competitive with that of imported hard coke. The hard char is unique amongst metallurgical fuels in combining a high reactivity with high physical strength, and research by the University of Melbourne into its utilization in foundry cupolas for melting iron has shown how modifications could be made to take advantage of these properties. An 18 inch experimental cupola has been built to test in practice the predictions made from this fundamental research.INTRODUCTIONSteady development has continued in Victoria from the promising laboratory researches at the University of Melbourne which were reported to the 1955 Annual Conference of The Institute (Worner, 1956). This work had shown that a hard lump char could be produced by the high temperature carbonization of standard industrial briquettes by careful control of the heating conditions, and that the special briquetting techniques adopted in Germany were unnecessary with Yallourn brown coal. Continuation of this research has led to the refinement of carbonization techniques and has increased the strength of the char until it has equalled that of conventional metallurgical cokes.

Jan 1, 1960