By C. Elbaum

If a thin layer of liquid gallium is spread on a surface of solid aluminum, the gallium penetrates high-angle grain boundaries at a very rapid rate and separation along these boundaries follows. An experiment was carried out to investigate this phenomenon. A well-annealed specimen of aluminum 99.994 pct pure, consisting of several large grains was used, Fig. 1. The dimensions of the sample were 25 mm wide by 2.5 mm thick and all the grain boundaries extended through the entire thickness of the plate. This sample was prepared by strain-annealing and, as can be seen in Fig. 1, contained one long, straight boundary. An examination of the crystal orientations showed this boundary to be a coherent twin boundary. The angular misorientations between the grains forming the other boundaries were all in excess of 20 deg. A thin layer of liquid gallium was spread on one side of the specimen at about 30°C (the melting point of gallium is 29.7"C). After the application of the liquid the temperature was lowered to about 27°C. The gallium remained liquid at this temperature and it can be seen from the A1-Ga phase diagram1 that the liquid was probably saturated with aluminum.

Jan 1, 1960

By R. V. Lundquist

A method was developed by the Federal Bureau of Mines for evaluating viscosity data from slurries obtained in leaching sinters from the lime soda sinter process for extracting alumina from aluminous silicates. The logarithm of the viscosity was observed to be a linear function with time. The slope of the plotted line provides a means for evaluating viscosity behavior in a lime soda sinter blurry and also a means for comparing gelation characteristics directly with other variables in the lime soda sinter process. This report presents one aspect of a continuing study by the Bureau of Mines on methods for treating siliceous aluminum ores. It is one of the many programs of the Bureau concerned with conservation, development, and use of our domestic minerals resources. Previous investigations of lime soda processes, both by the Bureau4-7/ and industrial concerns, have demonstrated that sintered materials containing CaO, Na2O, A1203, and S102 in various combinations exhibit a tendency to gel or set when mixed with water or other extraction solutions. Gelling prevents satisfactory recovery of alumina and in extreme cases prevents operation of an extraction plant.

Jan 1, 1960

By J. A. Berge, R. S. Mateer, R. G. Aspden

IN a study of the cold-rolling characteristics of iron-base alloys with 3 to 12 pct Al, the influence of aluminum content on the cold-rolling textures was evaluated. This work was undertaken to determine if binary iron-aluminum alloys possessed cold-rolling textures similar to other body-centered-cubic alloys and to contribute additional information on the effect of solute concentration on the cold- rolling textures. Gradual changes in cold-rolling textures with an increase in solute content have been observed in copper1 and in titanium.2 Iron-base alloys containing 3.0, '6.0, and 12.0 pct aluminum were vacuum-induction-melted in a magnesia crucible and permanent-mold cast. The materials used were high-purity electrolytic iron and 99.99 pct grade aluminum. Each ingot was 1 in. square in cross section by 12 in. in height. The bottom half of each ingot was soaked for 1 hr at 1000°C and rolled at 1000°C to a thickness of 0.055 in. with the long axis of the ingot parallel to the rolling direction. The strip was reheated between passes to maintain a rolling temperature of 1000°C.

Jan 1, 1960

By R. A. Wood, R. I. Jaffee, H. R. Ogden, D. N. Williams

Strain-induced porosity has been found to occur in titanium and other materials at tensile strains greater than the uniform elongation of the material. Porosity in titanium increases with increasing strain and temperature, being most severe at 300° to 800°F. Strain-induced porosity is believed to be a normal part of the mechanism of deformation in ductile materials. DURING the past few years there have been numerous references to the occurrence of voids in laboratory test specimens of metals subjected to strain.l-7 These voids have been referred to as intercrystalline cracking, strain-induced porosity, intergranular cav-itation, voids, and porosity. They appear to occur at grain boundaries or interfaces, and are generally associated with large amounts of strain and have been found mostly in creep specimens and to a lesser extent in tensile specimens. Because the phenomenon does not occur unless the material has been strained,

Jan 1, 1960

By Alla D. Mah

The work described in this report is part of a Bureau of Mines research program for obtaining heats of formation of inorganic oxides, carbides, and nitrides by combustion calorimetry. The heats of combustion of molybdenum subnitride (Mo2N) and chromium subnitride (Cr2N) were measured. The data were combined with previous determinations of the heats of formation of molybdenum trioxide and chromium sesquioxide to obtain the heats of formation of the two subnitrides from the elements at 298.15° K. The corresponding free energies of formation were estimated. The heat data were compared with those of nine previously studied nitrides.

Jan 1, 1960

By S. Yukawa, M. J. Sinott

The low solubility of bismuth in copper and its segregation at copper grain boundaries with resulting embrittlement is well known.1-3 The heterogeneous diffusion of liquid bismuth into polycrystalline copper has also been studied.4 This work presents some further observations on these phenomena using high-resolution auto radiography to detect the presence of bismuth in copper polycrystalline and bicrystal specimens. The auto radiographs were made by the stripping film technique which produces an autoradiograph that is intact with specimen surface and can be examined simultaneously with the under-lying microstructure. The details of the technique have been described previously.3 In one series of experiments, high-purity copper was alloyed with 0.02 to 0.03 wt pct radioactive bismuth obtained from the Oak Ridge National Laboratory. Melting and casting was done under a

Jan 1, 1960

By Joseph L. Gillson

Bentonite, designating a distinct type of clay, is a young name in mineral nomenclature in the light of the age-old names of most other useful nonmetallics. The earliest references in literature are to "soap clay" (1873) "taylorite" (1888) and finally "bentonite" in 1897, from its occurrence in the Fort Benton series of rocks near Rock Creek, Albany County, Wyoming. Bentonite is a rock term and consists largely of montmorillonite clay. The latter name was proposed in 1847 for a plastic clay found at Montmorillon, France. A clay of apparently identical properties was described by Cronstedt of Sweden in 1788 and a number of other similar clays found in France were given other names in publications from 1853 to 1856. The mineral name montmorillonite was recognized by Dana in 1892. The recognition of "clay mineral" distinctions which led to the present-day classifications of clays by their chief mineral content, dawned in the early part of the twentieth century. Grim6 has aptly said: About 1924, Ross10 and some colleagues of the U. S. Geological Survey began a study of the mineral composition of clays that led to a series of monumental papers on the subject. By the early 1930's what has come to be known as the clay-mineral concept became firmly established in the minds of a great many people actively studying clay materials. The clay mineral concept designates the major clays as kaolins, montmorillonites and illites and by this concept bentonites are now defined as "fine-grained clays containing not less than 85 pct montmorillonite" and a wide variety of clays found all over the world are included in that classification. They could all properly be called "montmorillonite clays" but the common commercial name is bentonite. For a period of over forty years from the time of the earlier discoveries, bentonite was thought to be only the sodium type highswelling clay produced principally in Wyoming. By the clay mineral concept, non-swelling montmorillonite clays also became known as bentonite. In the trade there are two broad divisions-sodium bentonite, often called Wyoming or "western," which expands in water and carries sodium as its predominant exchangeable ion, and calcium bentonite often called "southern," which has negligible swelling and carries calcium as its principal exchangeable ion. There are many intermediate gradations. Properties The mineralogy and chemistry of the clays are so complex that the subject cannot be summarized briefly. The reader is referred to Chapter 12 of this volume in which the subject is treated at some length. Grim6 gave the formula for montmorillonite as (OH)4Si8AL4020.nH2O. He wrote: Montmorillonite is composed of units made up of two silica tetrahedral sheets with a central alumina octahedral sheet. . . . Exchangeable rations occur between the silicate layers. . . . The words "tetrahedral" and "octahedral" refer to the coordination number of the cations in the unit cell in the crystallographic lattice. Carroll5a stated: That the montmorillonite structure is the same as that of mica, but the layers are not held together by K+ ions; and water and other polar molecules, such as organic molecules, can enter between the unit layers and cause expansion. Ex-

Jan 1, 1960

By C. E. Birchenall, J. R. Stubbles

ThE equilibrium between lead, lead sulfide (PbS), and atmospheres of H2 and H2S has been determined previously by Jellinek and Deubel,' and SudO.' Blbem and Kroger3,4 used Jellinek's data to calculate the sulfur dissociation pressures of PbS crystals (of

Jan 1, 1960

By L. Kaufman

An equation is derived relating AF a", the difference in free energy between austenite and martensite, to temperature and composition in the iron-chrmnium and iron-chromium -nickel systems. This equation is used to calculate at M,for low-carbon stainless steels. A method for utilizing the energetic equations to calculate M, in stainless steels is suggested. In addition, an explanation is given for the anomalous effect of chromium in forming a y loop concurrent with the lowering of M, in iron-base alloys. It has been demonstrated that the effect of alloying elements on the Ms temperature is strongly dependent upon the influence of the alloying element on the thermodynamic properties of the y and a phases. Notwithstanding the fact that alloying elements affect the Ms temperature by changing the lattice parameters, elastic constants, and inter-facial energies of the a and y phases, their primary role is a thermodynamic one. Thermodynamic analyses have been presented for the iron-carbon'-4 and iron-nickele systems in which equations are derived for Fa and FY, the free energies of the b.c.c. (or b.c.t.) and f.c.c. phases. These equations, which can be obtained with the aid of the equilibrium diagrams, can be used to help predict the Ms vs composition curves. This paper deals with a calculation of the thermodynamic properties necessary to compute AFffLY for iron-chromium alloys. In view of the lack of direct information concerning the activity of chromium in the a and y phases of iron, the regular solution approximationa,g was utilized to bridge the gap. After the necessary equations were derived for the iron-chromium system they were used to calculate AFff— Y for stainless steels by combining them with the previous results obtained for iron-nickel alloys. The results of these calculations offer a means of rationalizing the anomalous behavior of chromium in iron-base alloys. The latter depends on the regular solution approximation in contrast to the explanation offered by zener , which is based upon the "magnetic specific heat effect." THERMODYNAMICS OF THE IRON-CHROMIUM SYSTEM If y represents the atomic fraction of chromium in an iron-chromium alloy, then the free energy of the b.c.c. phase Fa, the f.c.c. phase FY, and the difference in free energy between the f.c.c. and b.c.c. phases of the same composition are given through [3] and Fmy represent the free energies of mixing of the a and y phases; while @era -' and uFea 4Y represent the difference in free energy between f.c.c. and b.c.c. chromium and iron respectively. The values of AEFe0ff4Y in the temperature range between 0" and 900K ( .

Jan 1, 1960

By K. Winterton, Carruthers. J.

"Attempts have been made to produce hardened structures of a pseudomorphic type in various carbon and alloy steels. In order to obtain martensite with a fine distribution of cementite, an initial structure of fine lamellar or nodular pearlite is required; this may be obtained by conventional means. This is followed by partial austenitization and quenching.Two methods have been tried to induce partial austenitization:(a) A resistance (direct current) heating method involving rapid entry into the austenite field.(b) A new method, described as the ""threshold"" technique, involving homogenization of temperature just below A 1, followed by entry into the austenite field; two furnaces are required.The resulting structures have been examined for microstructures, hardness, tensile, and impact values. The tensile properties are comparable with those obtainable by conventional treatment methods. Impact values are disappointing, but this is explainable from the nature of the manifold changes occurring."

Jan 1, 1960

By R. J. Linney

Reserve Mining Co. produces 5 million tons of iron ore pellets per year. The finished product runs about 65.50 pct Fe, with 7.75 to 8.00 pct SiO2. Less than 12 pct arrives at the blast furnaces smaller than % in. This plant was originally designed to produce 3.75 tons annually—not 5 million. To handle the increased tonnage a fifth fine crushing line was added, and some very minor changes were made. When production can be stepped up 33 1/3 pct without extensive additions or changes—within the short period of a year—basic engineering has been sound. Operators of the plant consider it the best design job they have seen or heard of, and competent authorities have said that start-up was quicker and easier than for any previous large-scale minerals beneficiation plant. One big advantage is the elbow room allowed. Generally speaking, there is an eternal conflict between operator and designer over space. The designer has his costs per cubic foot, and he is keenly aware that if he permits the number of cubic feet to rise unnecessarily, total costs will be too high. But this was a new operation, and on a large scale. There were no proven standards to go by. Realizing this, Reserve's engineers provided ample and efficient access to machinery, allowing extra space for unanticipated situations. In three years of production this planning has paid off handsomely. Gravity Flow Saves Time and Money: This plant is on a rocky hillside, the car dumper about 270 ft above Lake Superior. In locating buildings and placing machinery the designers mad= good use of gravity flow, at considerable financial savings. In the concentrator building from rod mills to filters, gravity carries the material between all stages of the operation except one—the closed circuit pumping of concentrate between cone classifiers and ball mills. Since no machine is located directly above any other, an observer can stand on the truck ramp adjacent to the offices and laboratory and see practically every phase of activity in the huge building. The first mill section started in August 1955. After a day's run several modifications were made on auxiliary chutes and launders where spillage had occurred. This procedure was followed for the first

Jan 1, 1960

By R. W. Kewish

The preparation of massive uranium metal containing very low concentrations of a number of light elements by bomb reduction of UF4, with calcium is described. Details of procedures are given for preparing high-purity ingredients for the bomb reduction. The as-reduced uranium metal contained, on the average, less than the following amounts of light element impurities, in ppm: Li, 0.1; Be, 0.1; B, 0.1; C, 25; 0, 70; Na, 1; Mg, 3; Al, 2; and Si, 7. Other impurities for which the metal was examined averaged, in ppm: Ca, < 10; V, < 10; Cr, 2; Mn, 6; Fe, 50; Co, < 5; Ni, 8; and Cu, 1. THE preparation of very high-purity uranium metal in massive form for research purposes is of great importance. Recently the kilogram-scale preparation of uranium metal containing less than 70 ppm of detected impurities was accomplished by Blumen-thal and coworkers by vacuum remelting of high-purity crystals of uranium obtained by fused salt electrolysis.1"3 Albert and coworkers4 have reported successful experiments in lowering the concentrations of certain impurity elements in uranium, notably iron, to a few ppm by the zone-melting method. The present paper describes the preparation of high-purity massive uranium metal by the bomb reduction of UF4, with calcium. Early in 1951 a program was undertaken at the Los Alamos Scientific Laboratory to prepare uranium metal of very high purity with respect to a number of the light elements. The methods considered for this purpose were 1) bomb reduction of a uranium halide with calcium, 2) electrolysis of fused salts, and 3) hot wire decomposition of UI4, The first of these processes had been used extensively at Los Alamos since 1943 (and still is used) for the production of uranium metal.5 In considering the three processes it was evident that either of the last two would require an extensive development program with no certainty of success. On the other hand, a study of available data showed that uranium metal of very high purity with respect to some light elements had occasionally been made in routine processing by the first method. It was therefore decided that an intensive study of the bomb-reduction process would be made to see if it could be improved to yield uranium metal with very low concentrations of light elements. DEVELOPMENT OF PROCEDURES The bomb-reduction process used at Los Alamos consists of reducing UF4 with calcium, using iodine as a booster. The reaction is carried out in a magnesium-oxide crucible enclosed in a steel bomb. Argon is used in the bomb to avoid objectionable side reactions which would occur in the presence of air. All ingredients for this bomb-reduction process were examined as possible sources of light elements. It was known that high-purity UF4 was required. The calcium used in the reductions was a source of carbon and magnesium. The magnesium-oxide crucibles were sources of boron, silicon, and magnesium. The iodine did not appear to be a source of any impurities. Pure UF4- The UF4 for bomb reduction is prepared from U3O3 , by successive reduction to UO2, with hydrogen and hydrofluorination of the UO2, with anhydrous HF. Since it was known that no impurities were normally introduced during the gas-solid reactions, effort was directed toward the preparation of high-purity U3O3. Of the many possible procedures for the purification of uranium solutions the following were investigated: 1) Precipitation of uranium peroxide. (Two procedures were tried. The first consisted of simultaneously adding hydrogen-peroxide and ammonium-hydroxide solutions to a uranyl-nitrate solution, containing citric and malonic acids, at such relative rates that precipitation was carried out at a constant pH of 1.5 The second consisted of simultaneously adding uranyl-nitrate, ammonium-hydroxide, and hydrogen-peroxide solutions to an aqueous solution

Jan 1, 1960

By E. C. Harder, E. W. Greig

Bauxite is known mainly as the ore from which aluminum is smelted but it has large use also in the manufacture of artificial abrasives and in the production of a number of useful chemicals as well as of aluminous cement "ciment fondu." An important and growing use is in the manufacture of refractory products. Composition Dana and earlier mineralogists gave the mineral formula of bauxite as A1203.21120 and the composition as A1202, 73.9 pct; H2O, 26.1 pct. A specific mineral of this composition has, however, never been identified by either microscopic, chemical or X ray examination, and therefore it is concluded that bauxite is a rock consisting of one or more aluminum minerals together with impurities. The term is now used synonymously with aluminum ore and it embraces gibbsite (hydrargillite or alpha trihydrate), A1203. 3H20 (A1203, 65.4 pct; H2O, 34.6 pct); boehmite (alpha monohydrate), A1203•H20 (A1202, 85 pct; H2O, 15 pct) ; diaspore (beta monohydrate), A1203•H20 (A1203, 85 pct; H2O, 15 pct), and mixtures in various proportions of any two of them. Bauxite of the Mediterranean region in Europe is predominantly boehmite, as in France and Istria, subordinately a mixture of gibbsite and boehmite, as in Dalmatia, or of boehmite (or gibbsite) and diaspore, as in Greece. The bauxite of North and South America, tropical Africa, Asia, and Australasia consists largely of gibbsite, but boehmite in appreciable amount occurs in many places. Corundum (A1202) is not included un¬der bauxite, although gradations from bauxite to emery or corundum exist. All bauxite, irrespective of the aluminum minerals composing it, contains certain impurities in variable amount, including silica in the form of clay minerals (kaolinite, halloy site, and others) or quartz, iron oxide (as hematite or goethite), titania (as leucoxene or rutile), iron sulfide (as pyrite or marcasite), iron carbonate (siderite), and calcium carbonate (as calcite); the last three mentioned in minor amount and of local occurrence only. Bauxite belongs to a group of partly consolidated materials called laterites, formed by surface weathering. This group includes also impure siliceous, ferruginous, and phosphatic bauxite and siliceous and aluminous iron ores and manganese ores and nickel and chrome laterites. Phosphorus and manganese minerals locally form important impurities in bauxite deposits. Properties Gibbsite is white or light shades of gray, cream or pink. Its hardness is 2.5 to 3.5; specific gravity, 2.3 to 2.4; crystal system, monoclinic, crystals tabular parallel to 001, often fibrous, concretionary, stalactitic; luster, vitreous to pearly; generally translucent; cleavage, parallel to 001; disassociation temperature, approximately 300°C. Boehmite, a relatively new and important mineral described by J. Boehm15 in 1925, confirmed and named by J. de Lapparen64 in 1930, has some properties not yet definitely determined. It occurs in grayish, brownish, and reddish shades. Its hardness is between that of gibbsite and diaspore; specific gravity, 3.01 to

Jan 1, 1960

By H. J. Booss

THERE is a considerable lack of data on thermody-namic properties of hard-metal alloys. Only two papers 1,2 give mean values of specific heat in an unknown temperature range; more recently the author3 gave more detailed information on the mean specific heat in the temperature range from 20" to -190° C.. EXPERIMENTAL 1) Method—Experimental procedure followed a method suggested by Oelsen and coworkers.4 It requires samples of some 100 g of weight. The time of measurement is prolonged (30 min) but one run allows the measurement of a lot of positions on the heat-content curve. Results4 were found to be in good agreement with "best values" given by kelley,5 Kubaschewsky and Evans,6 etal.

Jan 1, 1960

By J. E. Hilliard, J. W. Cahn

In this paper it is suggested that the degree of contiguity (or contact) between adjacent grains be described by three parameters which can be rigorously determined from measurements on a random plane of polish. An expression is also derived for the number of contacts per unit volume and it is shown that this quantity can-not, in general, be estintated from measurements on a random plane. IN a recent contribution1 Gurland has proposed various parameters for describing the degree of contiguity (or contact) between grains of the same phase in an alloy. To relate these parameters to measurements on a random two-dimensional section, it was necessary in most cases to make some assumption about the form of the structure. Since Gurland was specifically interested in sintered carbide structures, he chose, quite reasonably, to assume that the grains were constant-size spheres and that all the intersections were flat areas of constant radius. Since, as we will show, the relationships between the parameters and the measurements are strongly dependent on the grain shape and size distribution, it is evident that these assump tions will not be satisfactory approximations for a

Jan 1, 1960

By John B. Myers

Vermiculite is the commercial name used to describe a micaceous mineral that expands appreciably when heated. This process, called exfoliation, results in a light weight material. The light weight material is also called vermiculite, or more exactly, expanded vermiculite. Practically all uses of vermiculite are for the expanded material. Composition and Properties Vermiculite, in its natural state, has the characteristic micaceous habit and a perfect basal cleavage and readily splits into thin laminae, which are soft, pliable, and inelastic. The monoclinic crystal faces are often marked by triangular lines at 60° and 120°. The hardness varies from 1.5 to 2 or more, depending on the composition. The specific gravity varies from 2.2 to 2.7; specific heat 0.2; fusion temperature 2,000° to 2,500°F; luster pearly to greasy; color amber, bronze, brown, dark green, and black. Feel is like talc and sometimes soapy when wet. When heated quickly at elevated temperatures, vermiculite exfoliates by expanding at right angles to the cleavage into long wormlike pieces (the name vermiculite is from the Latin vermiculari, to breed worms). This important characteristic of expansion is believed to be a mechanical separation of the layers when the contained water is converted to steam. The increase in bulk volume of commercially prepared material is 8 to 12 times, but individual flakes may expand as much as 30 times. There is no expansion parallel to the cleavage. Vermiculite may also be expanded by several chemical processes such as soaking in hydrogen peroxide, weak acids and other electrolytes. The color changes during expansion. Heat-treated material changes to a light golden bronze or cream color depending on composition. The conditions of heating affect color. Heating in an oxidizing atmosphere produces reddish colors and heating in a reducing atmosphere produces dull gray colors. The iron is generally not oxidized during chemical expansion. Vermiculite is hydrated magnesium-aluminum silicate. Although there has been much research on the chemical and structural composition, there is not yet complete agreement on the exact formula and composition. This is to be expected since vermiculite is not a mineral of fixed composition and different workers have examined different varieties. It has been proposed that vermiculite is not a single species but a family of related minerals. This has also resulted in many names for the particular vermiculite found in a certain deposit. All of this difficulty arises from the very nature of its crystal chemistry. Unlike most minerals, certain crystal structure properties and the chemical composition can be changed by the ordinary forces of nature or in the laboratory. This would suggest that vermiculite be thought of more as a variable mineral rather than a group of related species. It was stated on page 261 of this volume in the chapter on Clay Minerals by H. H. Murray of the Georgia Clay Co., that vermiculite is an equidimensional, expandable clay mineral. Gruner (ref. 14, Chap. 12) showed that the structure consists of a layer made up of two silica tetrahedral sheets with a central magnesium, iron octahedral sheet separated by two layers of water molecules and adsorbed magnesium and calcium ions. Mathieson and Walker,2a in a recent publication, agree that vermiculite must be regarded as a true clay mineral. The characteristic properties of the mineral, such as high cation ex-

Jan 1, 1960

By P. K. Koh

Isothermal salt bath annealing of 0.014-in. thick 3 pct Si-Fe sheet was conducted at temperatures ranging from 927" to 1260°C in order to investigate the grain-growth behavior. Within the temperature range studied normal grain growth did not take place; instead nucleated grain growth prevailed. The nucleation frequency was found to increase with the annealing temperature, with corresponding decrease in grain diameter of ultimate secondaries after long-time annealing. Large secondaries grown by low-temperature isothermal annealing are essentially of (110)[001] orientation, and the (110)[001] texture is strong. The relatively small secondaries grown by high-temperature isothermal annealing also have orientations near (110)[001] as an average but widely scattered; thus the amount of (110)[001] texture is found to decxease with isothermal annealing temperature. Grain growth and texture development at various annealing temperatures can be described by families of sigmoidal curves with the time axis. ThE cube-on-edge (110)[001] texture and predominating large secondaries in fully annealed 3 pct Si-Fe are customarily produced by a 1100°C annealing of a primary recrystallized sheet. On annealing the primary recrystallized sheet above the temperature at which secondary recrystalliza-tion starts May and turnbull&apos; have demonstrated that secondary grains decrease in size as the temperature is increased. The phenomenon was attributed to a decrease in the (G/N) ratio where G is the growth rate of secondary grains and N is their nucleation frequency. In addition, the growth of grains in orientations rather far from (110) [0011 occurred. The present investigation is devoted to detailed rate studies of the same phenomenon. Mi-crostructure, magnetic anisotropy, and texture data were obtained on strips of 3 pct Si-Fe isothermally annealed for various lengths of time in a BaC12 salt bath at temperatures ranging from 927&apos; to 1260°C. The texture results are reported elsewhere.2 EXPERIMENTAL PROCEDURE Commercial 0.014-in. cold-rolled silicon-iron strip (3.16 pct Si), prepared by two stages of cold rolling with an intermediate short anneal, was given a decarburizing 3-min anneal at 800°C. Metallo- graphic studies indicated complete recrystallization. In order to provide a protective atmosphere and to obtain a rapid rise to an elevated temperature, a BaC12 and NaCl fused salt bath was used to heat samples isothermally at temperatures from 927" to 1260°C for various lengths of time. Torque magnetometer measurements were made on 1-in.-diam disc specimens before and after annealing, since magnetic torque curves supply information on textures and texture changes. Surface layers of the strip samples were polished and etched to reveal the grain structure. The diameters of grains were measured from micrographs at X100. The average value of diameters of matrix grains was established. Individual grains in the micrograph were cut out separately along grain boundaries. These grains were classified either as matrix grains or growth grains. The percent weight of growth grains in the cut-out patterns was reported as percent growth. Manv of the individual grains in the annealed samples were large enough to be X-rayed with a 5-mil beam for Lauegrams. Complete (110) pole figures were obtained for the primary recrystallized structure and short-time annealed structure with CoKa radiation at 30 kv in the back-reflection range, such as (220) for (110) poles, as described recently by Newkirk and ~ruce.~ Both the X-ray optics and the technique for pole figure differed slightly from those adapted previously.4

Jan 1, 1960

By A. J. Griest, A. P. Young, P. D. Frost

A study was made of the effect of ß grain size on the tensile ductility of a-ß titanium alloys haet treated to strengths in the range 165,000 to 180,000 psi. It was concluded that the primary cause of $ embrittlement is the large grain size which is obtained so rapidly in many a-ß titanium alloys when heated into the ß field. It was also found that grain-boundary a and acicular intragranular a in the microstructure are not necessarily detrimental to the tensile ductility if the prior ß grain size is sufficientlv fine. BETA embrittlement occurs in a-ß alloys when the finish hot-working or stages of the subsequent heat treatment have been done at temperatures in the ß field. In order to avoid this embrittlement, for-gings must be finished at temperatures under the ß transus. For better workability, it would be desirable to forge at temperatures in the ß field. For this reason, research has been conducted to determine the cause of ß embrittlement. Although ß grain size has been considered as a possible contributing factor to ß embrittlement, only limited research has been done to evaluate its effect. The effect of addition elements on ß grain growth in unalloyed titanium has been studied by Liu.&apos; Complete mechanical property data, however, were not obtained for correlation with grain size. Ogden and coworkers2 have investigated the effect of both a and ß grain size and grain shape in Ti-Cr-Mo alloys. Their data indicated that tensile ductility was relatively insensitive to ß grain size at annealed strength levels (140,000 psi ultimate). No study has apparently been made to determine the relationship between ß grain size and ß embrittlement in a-ß alloys heat treated to high strength (180,000 psi ultimate). The high-strength condition is that in which ß embrittlement is particularly severe. Beta grain size is not easily varied through the use of a range of annealing times and temperatures in the ß field, because of the rapidity with which ß grain growth occurs. Short-time heating techniques are needed to obtain the smallest ß grains. EXPERIMENTAL PROCEDURE In this research, the experimental procedure was as follows: 1) Tensile and microimpact specimen blanks were resistance heated to produce a range of ß grain sizes. 2) The tensile and microimpact blanks were then solution-treated in the a-ß field and aged to produce predetermined ultimate tensile strengths in the range 165,000 to 180,000 psi. Tensile and impact ductility were then correlated with a grain size for constant strength levels. Materials—The alloys Ti-6A1-4V, Ti-4A1-4Mn, and Ti-16V-2.5Al are representative of the heat-treatable a-ß types in which ß embrittlement can be severe. The compositions and ß transi of the heats studied are given in Table I. The Ti-16V-2.5Al heat was melted and fabricated to 1/4 in. round at Battelle; the other alloys were obtained as 1/4 in. round rolled from commercial heats. The micro-structures of the as-rolled alloys were fine a-ß mixtures. This structure is typical of titanium alloys hot-worked extensively in the a-ß field. Resistance-Heating Treatments to Establish ß Grain Size—For direit resistance heating, a 1/4-in.-diam s~ecimen was heated with a 3000-watt transformer rated for 1000 amp with adjustable secondary voltage. The apparatus included a spray quench fixture. Both heating and quenching periods could be automatically controlled. For temperature measurements, 28-gage Chromel-Alumel wires were tack-welded to the specimen at its midpoint. A high-speed recorder-controller was used to control the heating cycle.

Jan 1, 1960

By D. M. Baird

"THE Island of Newfoundland lies on the extreme eastern edge of the continent of North America and at the extreme northeastern end of the Appalachian geological province. Its belonging to the Appalachian province is shown in the geological history of the region and in the rock types and structures.Geosynclinal sedimentation in early and middle Palaeozoic times was interrupted by Taconic and, more profoundly, by Acadian, mountain building activity. Mid-Palaeo-zoic intrusions range from masses of serpentinized ultrabasic rocks to granite batholiths. A Carboniferous overlay of continental and shallow, drying sea types covers the earlier developed complex. Local basins in these times were filled with products of the erosion of tl1e earlier rocks, and, locally, grew the right kind of vegetation to make thin, discontinuons seams and pockets of coal. Post-early Pennsylvanian history is one of erosion and pene-planation with renewal of movement along many of the older fault systems."

Jan 1, 1960

By J. Chipman, T. Fuwa

The effects of various elements on the activity coefficient of carbon in liquid iron have been studied by two experimental methods: 1) equilibration with controlled mixtures of CO and CO2; 2) the solubility of graphite in the melt. Activity coefficient of C is increased by Al, Co, Cu, Ni, P, Si, S, and Srz. It is decreased by Cr, Cb, Mn, Mo, W, and V. THE thermodynamic properties of the iron-carbon binary system have now been fairly well established, although some uncertainty remains with respect to the exact location of some of the phase boundaries. The activity of carbon in ferrite and in austenite has been measured in the classic researches of R. P. smith&apos; while similar measurements by Richardson and ~ennis, and by Rist and chipman3 have established the values of the activity of carbon in liquid iron up to 1760°C. On the other hand, our knowledge of the effects of alloying elements on the activity of carbon in dilute solutions is restricted to Smith&apos;s experiments on systems Fe-C-Mn and Fe-C-Si in the austenitic range and to some more recent experiments of schwarzman4 in the a range. In addition there have been a number of determinations of the effects of various elements on the solubility of graphite in liquid iron, and from these the corresponding effect in saturated solution may be obtained. The purpose of the present study was to extend the investigation of the liquid system to include the effects of alloying elements upon the activity coefficient of carbon, principally in dilute solutions. Equilibrium measurements were made on the reaction C + co, = 2 CO (g) The prepared mixture of CO and CO,, diluted with argon, flowed over the surface of the liquid metal which, after several hours&apos; exposure to the gas, was quenched and anqlyzed. As in the earlier experiments, the principal experimental difficulty was in the deposition of carbon on the parts of the furnace at temperatures slightly below that of the metal bath. In order to minimize this difficulty, the ratio (Pco)2 /PCo2 was restricted to values not much higher than 100 atm, and correspondingly the carbon concentration in the metal seldom exceeded 0.30 pct. EXPERIMENTAL METHODS The method and apparatus were essentially the same as used by Rist and Chipman.3 The gaseous mixture consisting of highly purified CO, CO,, and argon, each controlled by a flowmeter, was led into the furnace and passed over the surface of the liquid-iron melt which was heated and stirred by high-frequency induction. One slight modification was made in that a molybdenum susceptor was placed outside the crucible for the sake of uniformity of temperature and to combat the tendency of carbon to precipitate on the crucible wall. Pure alumina crucibles approximately 25 mm ID were used. The charge consisting of about 30 g was made up of electrolytic iron, the alloying element to be added, and enough graphite to supply slightly more or less than the anticipated equilibrium carbon concentration. All metals used were of high purity. Metallic chromium, columbium, and vanadium were from special lots supplied by the Electro Metallurgical Co. Tin, copper, molybdenum, tungsten, cobalt, and nickel were of purest commercial grades. The electrolytic iron, after being cut to the proper size for charging, was prereduced by hydrogen at 850° to 1000°C to remove surface oxidation. The oxygen content of the reduced material was 0.002 pct. This treatment made it easy to control the carbon content of the initial melt. The charge was melted under the gas mixture to be used for the entire run. In some earlier melts the charge was melted under a stream of argon, but in this case some alumina was reduced from the crucible, and the aluminum thus absorbed in the melt was subsequently oxidized with the formation of a solid film of alumina on the surface of the melt. AS another safeguard against film formation, overheating of the bath was carefully avoided. All runs were made at a temperature of 1560°C. Under experimental conditions a charge of pure iron picked up 0.17 pct C in 3 hr and 0.23 pct C in 6 hr under an atmosphere for which the equilibrium concentration of carbon is 0.27. It is clear that the time required to reach equilibrium from an initially carbon-free melt would be very great. For this reason each experiment was started with a melt of known carbon concentration not far above or below the expected equilibrium value, and each melt was held at temperature for a period of at least 5 hr. Under such circumstances it was possible to chart the approach to equilibrium from both high-carbon and low-carbon materials. Temperature was controlled by frequent optical observation and adjustment and the metls were timed in such a way that the final 2 hr occurred during a time when electric power was steady; for example, 2 to 4 pm or after 11 pm. In melts containine volatile metals such as copper, tin, and mangane\e the time of holding was decreased somewhat in

Jan 1, 1960