By L. W. Berger, R. I. Jaffee, D. N. Williams

The effects of hydrogen on the properties of binary Ti-A1 alloys containing 2.5, 5, and 7 pct aluminum and ternary alloys of the same compositions with added interstitial elements oxygen, nihrogen, and carbon were studied. Aluminum increases the apparent hydrogen solubility of the a-phase, resulting in a marked increase in resistance to impact embrittlement. In the Ti-5Al and Ti-7Al alloys, for example, the addition of 180 and 305 ppm hydrogen, respectively, did not cause embrittlement, while unalloyed titanium was embrittled by as little as 75 ppm. The role of aluminum in increasing hydrogen solubility of the a-phase probably accounts for the excellent hydrogen tolerance of a-ß alloys containing considerable amounts of aluminum. There is some evidence that aluminum retards the rate of hydride precipitation. If so, these alloys may be susceptible to slow-strain embrittlement. UNALLOYED a-titanium is extremely sensitive to small amounts of added hydrogen in that there is a marked decrease in notch properties. For example, as little as 100 ppm hydrogen is sufficient to lower the room-temperature notch-impact strength from over 100 to less than 20 in.-lb.' This loss of impact Strength has been associated with the Presence of hydride phase in the microstructure. Hydrogen in the amounts encountered in commercial practice

Jan 1, 1959

By P. D. Zemany, G. W. Sear, B. W. Roberts

Vanadium metal is embrittled by hydrogen at a temperature as low as 250°C when held in the presence of manganese metal and water vapor in a rough vacuum. It is established that the property changes are caused by the catalytic decomposition of water vapor at the vanadium surface and the diffusion into and solution in the vanadium of the resultant hydrogen. It is found that manganese is a necessary component of the catalyst. The manganese is transported in the vapor phase by an unknown molecule. A deuterium tracer experiment demonstates the role of water vapor in the embrittle-ment process. VANADIUM metal foils were observed to become embrittled' at a temperature of about 300 °C when held in the presence of manganese metal and a small amount of moist air, This paper describes the investigation to find the embrittling agent and an understanding of the relatively low temperature reactions that are involved. Experimental The vanadium metal foil used was prepared by cold-rolling and pack-rolling 32 mil sheet" in a series of steps down to 1 mil foil. The original observation was confirmed by sealing vanadium foils of 3 x 10 sq cm into individual Pyrex tubes with manganese powder† and a con- trol tube containing only the vanadium foil. These tubes were evacuated to 10 -5 mm Hg without baking and sealed. After heat treatment for 200 hr at 300°C, the control foil showed no change in duetility, whereas the foil contained in the manganese— containing tube was embrittled. The visual appearance of each was unchanged. A series of Pyrex sample tubes, about 2.5 cm diam and 25 cm long, were prepared, each containing a 3 x 10 sq cm piece of foil and 5 g manganese powder at the lower end of the tube. By reducing the time of anneal and the temperature of these samples, it was found that embrittlement could be created at 250°C in a time as short as 1 hr. Since the vanadium metal used here has been drastically cold-worked by rolling, it is assumed that it contains a maximum number of dislocations. To check the possible necessity of dislocations in this low temperature reaction, a vanadium foil sample was annealed in Vycor for 2 hr at 800°C to re crystallize and reduce the dislocation concentration. Metallographic examination showed grains which were not visible before annealing. The embrittlement procedure was carried out at 300°C and 3 hr. Upon checking the foil no embrittlement was observed. Further experiments demonstrated that about 6 hr at 300°C are required to create embrittlement in the foil. This delay in the onset of embrittlement in the vanadium foil suggests but does not prove that dislocation channels play a role in the embrittlement phenomena. If manganese metal is necessary for this low temperature embrittlement, do other elements in the transition metals group yield the same result? To check this qualitatively, a group of elements of similar atomic radii were obtained and sealed as before into Pyrex tubes with a sheet of vanadium foil. These tubes were annealed at 250°C for 6 hr and included (with radii)-2 A1 (1.4A), As (1.25A), Be (1.2A), Co (1.25A), Cr (1.45A), Cu (1.25A), Fe (1.25A), Ga (1.2A), Ge (1.25L%), Mn (1.3A), Ni (1.25A), Si (1.2A), Ti (1.45A), Zn (1.3A), air, H,O, 10 cm Hg of dry hydrogen, and MnO, powder. Upon testing the above sample foils for brittleness, only the manganese-containing tube yielded a brittle foil. Manganese Transport—To eliminate contact of manganese metal powder and vanadium foil, sample tubes were prepared with fritted glass barriers. The embrittlement reaction was still found to occur. Thus, the mode of transfer of manganese is certainly vapor transport. A vanadium foil was embrittled by this mechanism in an evacuated Pyrex tube for 8 hr at 300°C. By means of X-ray fluorescence analysis,' the amount of manganese added to the surface was established at 5 ±2 x 10 -6 g per sq cm. Since the average rate of manganese deposition is known, an effective average pressure of an assumed carrier compound can be computed. ___ P = M/T v2p mkT

Jan 1, 1959

By Robert L. Llewellyn

The Wharton No. 2 Mine of Eastern Gas and Fuel Associates is located about 60 miles south of Charleston, West Virginia in Boone County. Daily production is 6,000 T.P.D. on a two-shift basis. The Hernshaw Seam is mined by conventional equipment with one continuous miner in areas where conditions are suitable. The plant is on Cow Creek .Branch of Pond Fork, which in turn flows into the Little Coal River at Madison, West Virginia. When the mine was opened in 1948, plans were developed to build a dual Baum jig plant complete with mechanical and thermal drying, and because full production would not be reached for several years, it was decided to install only one Baum jig setup although the complete structure was erected. This phase of the plant was placed into operation early in 1949, The rated capacity was about 300 T.P.H. of 5" x 0 raw feed to the jig. Being a drift mine, the 10-ton mine cars are dumped at the Headhouse, crushed to 8" in a double roll crusher, conveyed 780 feet downhill to the picking .house where the +5" slate is removed by pickers. All coal is crushed to 5" and 5" x 0 is conveyed 150 feet to the cleaning plant. Further describing the plant growth, the second jig setup was installed in 1954 to clean the increased production. During this operating period, exhaustive tests had ,been run on the plant bleed which was an overflow from the large sludge tank located inside the plant, When the second jig addition was undertaken, 5-14' diameter and 12-8" diameter cyclones with a 9-disc filter were installed for the solids recovery and water clarification system, However, the circuit was not closed and a bleed of part of the overflows from the 8" diameter cyclones was still necessary, To comply with the State Water Commission regulations on stream pollution abatement, four pumps in series were installed to discharge the waste water behind the refuse pile.

Jan 1, 1959

Acclaimed as one of the most remarkable orebodies anywhere on account of its length and richness, the Oroya Shoot occurs on the eastern side of the Kalgoorlie gold mining district close to the contact of a fine-grained with a coarse-grained greenstone, and in association with sediments. In the same stratigraphic position on the synclinal flanks of a large drag fold there are a number of other flat ore pipes, smaller, but almost as rich in tenor. Although differing in control structure they are believed to be related genetically as all show a characteristic development of a bright-green ore known locally as "green leader". Folding and bedding structures have played an important part in formation of the ore shoots.INTRODUCTIONThe Oroya Shoot is the biggest individual bonanza of Kalgoorlie's Golden Mile. It has been stoped almost continuously over a length of 4,300 ft., and about 2,000,000 oz. of gold have been won from it. Naturally pillars are not left in the best sections of such an orebody and the detailed geology of stoped out portions can only be inferred from examination of adjacent workings.No mention is made in the literature of the actual makeup of the orebody although a few structures are shown on some of the old cross sections. A diagrammatic cross section, Fig. 1, adapted from Stillwell (1929) illustrates the form of the Oroya Shoot.Gustafson (1937) drew attention to the role of folding, previously unrecognized, in Kalgoorlie geology, and indicated that the Oroya Shoot is associated with a minor drag fold on the east limb of the Brownhill Syncline, itself part of a larger left hand drag on the Central Anticline. The latter in turn appears to be part of a regional right hand fold system as shown by Campbell (1953).

Jan 1, 1959

By R. D. Pehlke

THE impending commercial importance of iron-aluminum alloys has served as a stimulus for re- search on the preparation and properties of these alloys. However, the activities of the components of the binary system remain undetermined. The experimental determination of the thermodynamic properties of binary solutions of iron and aluminum has been hindered by the high liquidus temperatures

Jan 1, 1959

By Edward Cadwell

El presente texto señala la clasificación de combinación de minerales a través los desperdicios estériles y altos y concentrados bajos.

Jan 1, 1959

Jan 1, 1959

By C. Crussard, R. Tamhankar

It is the policy of The Metallurgical Society to provide, in the TRANSACTIONS OF THE METALLURGICAL SOCIETY OF AIME, a prompt and accurate medium for publication of reports of significant new research in both the scientific and engineering aspects of metallurgy. Papers submitted to the Society are judged by competent reviewers accord-ing to established criteria for technical merit, accuracy, originality, and presentation. STAFF: Editor, Gerhurd Derge Carnegie Institute of Technology Schenley Park Pittsburgh 13, Pa. Editorial Assistant, M. A. Redmerski Staff Coordinator, James J. Burke THE METALLURGICAL SOCIETY: W. R. Hibbard, Jr., President; J. C. Kinnear, Jr., Past-President; John Chiprnan, Vice President; T. D. Jones, Treasurer; R. W. Shearman, Secretary. PUBLICATIONS COMMITTEE OF THE METALLURGICAL SOCIETY: A. W. Thornton, Chairman; Dennis Carney, John Chip-man, J. C. Fulton, J. H. Hollomon, H. H. Kellogg, A. E. Lee, R. Maddin, J. D. Sullivan, and D. Swan. Review and selection of manuscripts is under the supervision of the following Publications Committees: Extractive Metallurgy Division: T. B. King, Chairman; S. J. Dickenson, R. P. Hermsdorf, R. Schuhmann, Jr., and P. T. Stroup. Institute of Metals Division: Robert Maddin, Chairman, F. Lincoln Vogel, Jr., Vice-chairman, W. A. Backofen, R. W. Balluffi, J. H. Bechtold, M. B. Bever, R. S. Busk, C. G. Goetzel, Paul Gordon, C. D. Graham, .Jr., Robert F. Hehemonn, R. I. Jaffee, F. E. Jaumot, Jr., Irving R. Kramer, A. J. Lena, Harold Margolin, C. J. McHorgue, Russell A. Meussner, J. B. Newkirk, H. W. Paxton, G. E. Pellissier, I. S. Servi, Alan U. Seybolt, A. J. Shaler, and Jack Washburn. Iron and Steel Division: J. C. Fulton, Chairman; T. B. King, F. C. Langenberg, W. 0. Philbrook, and T. 0. Winkler. Published bimonthly by the American Institute of Mining, Metallurgical, and Petroleum Engineers, Inc., 29 West 39th Street, New York 18, N. Y. Telephone: PEnnsylvania 6-9220. Subscription $20 per year for non-AIME members in United States and North, South, and Central America; $25, foreign; $5 for AIME members. Single copies, $4.00, single copies foreign, $5.00. The AIME is not responsible for any statement made or opinion expressed in its publications . . . Copyright 1958 by the American Institute of Mining, Metallurgical, and Petroleum Engineers, Inc. . . . Registered cable address, AIME New York ... Indexed in Engineering Index, Industrial Arts Index, and Chemical Abstracts... Second class postage paid at New Yark, N. Y., and Ann Arbor, Mich. Volume 212, Number 6.

Jan 1, 1959

By J. Doig, A. A. Bauer, F. A. Rough

AN investigation of the phase relationships between the 6 phases of the uranium-molybdenum and uranium-titanium systems was conducted by studying alloys ranging in composition from uranium-31.5 at. pct Mo to uranium-34 at. pct Ti. A ternary cut showing these phase relationships is presented upon the basis of thermal-analysis data obtained and upon the basis of metallographic and X-ray examination of heat-treated and quenched specimens. Isothermal ternary sections, inferred from phase relationships determined between the two 6 phases, are presented for the uranium-molybdenum-titanium system. In the compositional range investigated, a y-ura-nium solid solution exists at elevated temperatures. At about 900°C the 6-U2Ti phase, with limited molybdenum solubility, forms. Epsilon, a molybdenum-titanium-rich solid solution appears at the same temperature and appears in all phase regions that exist below this temperature except in the terminal 6-phase regions. The y phase is stable to approximately 660°C in titanium-rich alloys; the y and 6-U,Ti phases decompose at this temperature to a uranium in a peritectoid reaction. The y phase in molybdenum-rich alloys of the ternary cut studied decomposes in an apparent eutectoid reaction, at about 593°C, to the 6-uranium-molyb-denum and a-uranium phases. The e phase while present, presumably plays a negligible role in these reactions. Titanium was found to markedly decrease the stability of retained y in these alloys. Age-hardening characteristics developed in titanium-contain ing uranium-molybdenum alloys quenched from 900°C and aged at 500°C are ascribed to decomposition of Y to the a and E phases. INTRODUCTION Alloys of uranium with molybdenum, titanium, and zirconium, respectively, are of great interest because of their potential use as reactor fuels. As a result, this interest extends to the constitution of these alloys, particularly in view of their uniqueness of constitution. In these systems, alone, among known uranium-alloy systems, an intermediate phase forms by direct decomposition of the high-temperature y-uranium phase. As a prelude to possible future alloy development, an investigation has been undertaken of the phase relationships that occur between the intermediate phases of these systems. These phase relationships have already been reported for the intermediate 6 phases of the uranium-zirconium and uranium-titanium systems.' The results of an investigation of the phase relationships between the 6 phases of the uranium-molybdenum and uranium-titanium systems are reported here. The phase relationships that occur in the binary systems pertinent to this investigation are shown in Fig. 1. Phase nomenclature appearing throughout this report is as shown in these diagrams; the crystal structure of the phase is given in Table I. EXPERIMENTAL PROCEDURE Alloys were cast and fabricated to flat plate. Specimens were heat treated and examined metal-

Jan 1, 1959

By H. L. Armstrong

SOLID-STATE diffusion is an important technique in certain aspects of metallurgy, and especially the metallurgy of semi-conductors and semi-conductor devices. If the diffusion is carried out under constant conditions for a time, t, the concentration, C, of the diffusant at a depth, x, below the surface from which the diffusion is carried out is given by an expression of the form. C = Cof(x,Dt) [I] Co being a constant, and D the diffusion constant of the diffusant in the material and at the temperature

Jan 1, 1959

By M. J. Sinnott, J. C. Tobin

A technique for collecting and analyzing the small quantities of gases desorbed on heating metal powders has been developed. The gases collected from copper powders of various types of manufacture have been analyzed and found to contain H2O, CO2, and SO2. The quantities of gas evolved vary from 0.05 to 1.0 milliliter, under standard con-ditons of temperature and pressure, per gram of powder. The source of the gas has been traced to surface films on the powder. IN the powder-metal industry it is recognized that the presence of gases in the powders affects the processing and resulting properties of the sintered product. Several sources for these gases are possible; namely, chemical reactions with the sintering atmospheres, inclusion. of gases during compacting, dissolved gases in the metal powder, and sorbed gases on the metal-,powder surfaces.1, 2, 3 Since the quantities of the gases are relatively small, no direct attempt has been made to collect and analyze them nor to isolate their source. The work that has been done has been concerned with the dimensional stability of the product., its porosity, density, or mechanical and physical properties. Conclusions are drawn on the basis of studies of this type as to the probable effect of gases on these properties. 4, 5, 0 In the present investigation an attempt has been made to obtain quantitative data on the analysis and quantities of gases associated with copper powders manufactured in different ways. Apparatus was constructed to collect gases evolved from loosely packed powder samples on heating to various temperatures under a reduced pressure of helium. The powders were outgassed thoroughly in a vacuum prior to starting the collection operation in order to eliminate mechanically entrapped gases and to prevent the possible reaction of the powder with these gases. Experimental Procedures Materials—The major portion of the investigation was carried out on a single heat of water-atomized, oxygen-free, high-conductivity copper. A relatively coarse fraction of this powder, 20 to 100 mesh, was tested as a mixed powder and as various graded size fractions. The microstructure of this powder showed equiaxed grains and was clean and free from oxides and oxide eutectic. The particle size, as determined

Jan 1, 1959

By A. K. Chetin, W. W. Fitkin

"The reservoirs of Mississippian Mi-dale beds and Frobisher beds found in the Weyburn field lie at the north-western termination of a broad productive belt extending 120 miles along the northeastern rim of the Williston basin. These carbonates, and inter-bedded evaporites, originated during cycles of marine transgression and regression, and were deposited as rock types characteristic of shoal, lagoon, and basinward shelf environments. The Frobisher-Alida Beds, which form a secondary reservoir to the main Midale Beds of producing zone are composed of oolit1c, fragmental-bioclastic, vugular limestone capped by an impervious dolomitic mudstone. Production is controlled by localized structural features resulting from de-positional build-up. Excellent reservoir conditions are accompanied by an active water drive. The Frobisher Evaporite, consisting of massive primary anhydrite with dolomitic veinlets, forms the floor seal for the Midale beds oil accumulation. A significant facies transition into an oolitic, bioclastic, vugular limestone characterizes this unit. Beyond the depositional margin of the evaporitic facies, marked increases in porosity and permeability of the en-tire reservoir are noted. Carbonate units overlying the areal extent of the Frobisher Evaporite exhibit a greater degree of metasomatism, dolomitization, and more abundant secondary anhydrite.Porous carbonates comprising the producing zone of the Midale beds are divided into an oolitic, fragmental bioclastic, vugular limestone, and an overlying granular marly lime-stone unit, capped, by the Midale Evaporite. Oil is accumulated in a stratigraphic trap bounded above and be-low by primary anhydrite and truncated by the post-Mississippian erosional surface. Mississippian strata dip basinward from this erosional surface in a broad homocline exhibiting only minor irregularities. Rapid lateral and vertical porosity and permeability variations are common. Localized, separated, porous lenticles contain interstitial water in areas where the Midale beds are underlain by the Frobisher Evaporite. The major portion of the field, however, is capable of water-free production. Bottom and edge waters are found in certain portions of the field. Productive limits are tentatively defined around most of the present field perimeter. A large area along foe southern edge of the field remains open to future development. Probable ultimate remaining recoverable crude oil reserves, as of September 30th, 1958, were estimated by Mc-Daniel Consultants Ltd. to be in excess of 330 million barrels."

Jan 1, 1959

Earnings of engineers in the period 1956 to 1958 continued the upward trend observed in the previous survey interval, 1953 to 1956. The overall median (all graduates) was $6500 in 1953, $7750 in 1956 (a 19 pct upstep or about 6.5 pct annually), and $8750 in 1958 (up 13 pct from 1956 or 6.5 pct average yearly). The latter represents an increase from mid-1956 to mid-1958. For this same two-year span the Consumer Price Index rose 1.5 pct and the Average Gross Weekly Earnings for Production (Manufacturing) climbed close to 10 pct. Median earnings for the major classifications studied are presented in Table I. The increase in engineering earnings are not distributed equally among the various activity classifications or among the experience levels of the survey. Summary results of the changes of the median lines for the major divisions are presented in Table 11. Data in this table are approximations- dollars are rounded to the nearest $50 unit and percentages to the nearest full percentage.

Jan 1, 1959

By J. Chipman, T. P. Floridis

The equilibrium of gaseous H2O-H2, mixtures with liquid iron is used to establish the activity coefficient of dissolved oxygen as log f o = — 0.20 [%O]. Discrepancies in earlier work are explained or eliminated. Additions of cobalt, molybdenum, tungsten, and platinum increase the activity coefficient of oxygen whereas copper and gold decrease it. THE importance of dissolved oxygen as a refining agent in liquid steel has led to a number of studies of its thermodynamic properties. It is the purpose of this paper to examine the effects of a number of alloying elements on the activity of oxygen in the steel bath. As a preliminary to the study of the effects of alloying elements, it seemed desirable to examine certain minor discrepancies in the published data on the properties of oxygen in simple iron-oxygen solutions. The activity and free energy of oxygen in liquid iron were studied by chipman1 in 1933 by means of the reaction h2(g)+-o = H2O (g);K; = PH2O/PH2[% O] [1] The data were in fairly good agreement with calculations from results on the similar reaction CO (g) + O- = CO2 (g); K2 =P CO2/P CO [% O] [2] which had been obtained by Vacher and Hamilton2 as an incidental part of their study of the reaction of carbon with oxygen dissolved in the melt. It was found that the equilibrium ratio k1 was not a true constant but varied with the oxygen concentration in the manner shown in Fig. 1, which is copied from the original paper. This early observation has been refuted in subsequent work but is confirmed in the present paper, and an explanation of the discrepancy can now be presented. In Fig. 1, the two points on the extreme right were disregarded in drawing the

Jan 1, 1959

By E. F. Thomas

THE late George S. Rice was active in the inves--I- tigation of bumps, particularly in the last ten years of his career as chief mining engineer of the U. S. Bureau of Mines. Since most of his investigation was carried out in Great Britain, continental Europe, and—to a lesser extent—Canada, his thinking on prevention was influenced considerably by the experience of those countries. It is not surprising, therefore, that when he was called upon a few years before his retirement to investigate bumps in the U. S. and suggest ways to prevent them, he turned to longwall mining. A longwall method had been most successful in combating the bump hazard in mining coal under deep cover, especially in Great Britain, but the prevailing method there at the time was advancing longwall mining, which he knew was uneconomical under U. S. mining conditions. For this reason he proposed a modified retreating longwall system that he believed included the best features of the advancing method. As brought out by Rice,' if the cover is 2000 ft and 50 pct of the coal is extracted, the static load on the remaining pillars will be about 4000 psi, which exceeds the ultimate crushing strength in most instances. If the pillar coal is overloaded before a pillar line is established, then the abutment zone preceding a line of extraction is no place to split pillars or extract them by any method other than an open-end system. Rice therefore advocated open-end mining, preferably by longwall, but he was willing to compromise with long-face mining if the longwall method was not acceptable. Rice's system was put into operation in a mine in Harlan County, Kentucky,3 but subsequent experience has shown that it did not take into account two important factors—avoidance of pillar-line points and maintenance of adequate development in advance of the pillar-line abutment area. For ten years after Rice's retirement the USBM did little investigation and research on bumps, chiefly because so few were occurring that there was not much cause for alarm. But in 1951 there were three occurrences involving fatal injuries, and the Bureau began a statistical survey in that year. C. T. Holland, head of the department of mines at Virginia Polytechnic Institute, was retained as a consultant. The resulting study' of 117 case histories brought out these important conclusions: 1) Almost invariably the bump occurred in a locality affected by the abutment zones of one or more pillar lines. 2) In most cases the locality of the bump was influenced by the abutment zones of more than one pillar line. The term pillar-line point has been used for many years in the Appalachian region for such a situation. Point is used in the geographical rather than the mathematical sense. 3) In pillar-line extraction the following practices are safest in preventing bumps: a. The mine layout should provide for pillars of uniform size and shape along the extraction line. b. The mine layout should be planned so that no development need be done in the abutment zone of a pillar line. c. The layout should permit open-end extraction of pillar lines from the next goaf, so that it will not be necessary to resort to pocket mining, splitting pillars, or any practice that will involve driving in the direction of the goaf within the abutment zone. d. Pillars should be large enough to support area without undue roof and floor convergence before establishment of a pillar line. These are, of course, generalities, and while they are useful in laying out areas where bumps can be expected, they are of limited help in many mines that were committed to a system of mining before it was realized that they were subject to bumps. Under such conditions it becomes necessary to choose between the following alternatives: 1) Abandon the territory, except for pillars that offer no extraction problems. 2) Through experience select the pillars that are most heavily loaded, and, by augering, induce bumps from a safe vantage point so that impinged loads are relieved. This method was first developed at the Gary, W. Va. mines of U. S. Steel Corp. and later adapted to mining thick coal beds at Kaiser Steel's Sunnyside mine in Utah. No scientific method is available to determine where to drill within a loaded pillar. Although this method of unloading has worked very successfully at Gary—with one exception—

Jan 1, 1959

By G. Derge, R. E. Grace

A S detailed studies of mass transport in hetero- geneous systems are made, a knowledge of the chemical diffusion coefficients in various liquid and solid phases is necessary to understand the kinetics of any total reaction. For example, in zone refining some information must be available about the diffusion coefficients of various species in the liquid and solid regions near the moving interface. In liquid-liquid reactions, of which slag-metal reactions are of particular interest to metallurgists, the diffusion coefficient of a transferring species must be known accurately in both phases in order to predict a transfer coefficient for the over-all process. Diffusion data for various elements in liquid iron and iron-carbon alloys have been roughly deter-

Jan 1, 1959

By J. L. Walter, W. R. Hibbard

A GREAT deal of work has been done on the rolling of single crystals of iron. Barrett and evensoon studied end orientations of heavily cold-rolled iron crystals and found that some crystals maintained a sharp single orientation during rolling. Others rotated into two or more orientations, and some fragmented and approached the entire polycrystalline texture depending on the original orientation of both the normal and rolling directions. Barrett, Ansel, and Mehl2 studied iron-silicon alloys and found that the addition of silicon to the iron had little effect on heavily rolled polycrystalline material. Dunn3 has extensively studied the cold-rolling and recrystallization of silicon-iron single crystals. Dunn found that for single crystals having initial orientation between (110) [001] and (111) [112], the principalcomponent of the cold-rolled texture is (111) [112]. Koh and Dunn4 studied the cold-rolled textures of single crystals having initial orientations in the range (001) [110] to (111) [IT01 and found that these are stable end orientations. They also found that all orientations having a [110] direction parallel to the transverse direction rotate to either the (001) [110] or the (111) [112] stable end orientation except for orientations near (112) [11], which divide and produce a final texture consisting of (001) [110]and (111) [112] components. Crystals having a (111) <112>-type texture re-crystallized to a (120) [001] or (110) [001]-type texture. Crystals having orientations with a range of (001) to (335) in the rolling plane and [110] in the rolling direction recrystallized5 to a wide spread of the initial orientations resulting from a multiplicity of 30-deg rotations about several (110) poles. The present study was undertaken to relate other orientations of crystals of silicon-iron to their cold-rolling and recrystallization textures, so that one might rationalize polycrystalline recrystallization data on the basis of the known deformation texture and the behavior of single crystals in these orientations. PROCEDURE Samples were obtained from a cylindrical ingot of 3 pct silicon iron prepared as follows: Armco iron was melted with high-purity silicon flakes under an atmosphere of argon to minimize oxidation. The alloy was poured into a special mold to form an ingot which consisted partially of large columnar crystals. Plates were cut from the columnar portions of the ingot with the longitudinal direction parallel to the columnar axes and ground to 0.040 in. thick. The plates were heavily etched to a thickness of 0.032 in. to remove the cold-worked surface. Orientations of seventeen crystals were determined by Laue back-reflection techniques keeping the mean columnar axis as the reference direction. The plate was then cut in two, parallel to the columnar axis. One portion of the plate was rolled at room temperature parallel to the columnar axis to a reduction in thickness of 84 pct. The remaining portion of the plate was rolled also at room temperature across the columnar axis to a reduction of 66 pct, at which point the crystals began to separate at the boundaries. After rolling, nine individual crystals were removed from the strip by cutting along the crystal boundaries with a jeweler&apos;s saw. Fig. 1 shows the original orientations of the six crystals that were straight-rolled and of the three crystals (4, 7, and 8) that were cross-rolled. Each rolled crystal was carefully etched to approximately 0.002 in. thick. Textures of the cold-rolled crystals were determined by use of the diffractometer with a non-integrating sample holder. The pole figures were made for the (200) poles using molybdenum Ka radiation and were plotted by an automatic stereographic projection recorder.&apos; Spurious poles were determined by rerunning portions of the pole figures using strontium oxide to filter out the Ka radiation. The central portions of the pole figures have not been determined. The pole figures were completed to about 55 deg from the periphery at which point the sample holder interfered with passage of the beam. Following the determination of the cold-rolled

Jan 1, 1959

By S. B. Twiss, P. R. Basford

The relationship between areas of iron powders, briquettes, and sintered compacts and tensile strength has been determined. It has been found necessary to distinguish between two types of areas which exist in such powders—a macroscopic area due to the shape and size of particles and a microscopic area due to pores and cracks in the surface. Only the macroscopic area, specifically the area due to particle irregularity, contributes to tensile strength; the microscopic area cannot be forced into contact with adjacent particles ond does not participate in bond formation. Of the two methods of area measurement employed in this study—permeability to liquids and gas-phase adsorption—only the former is useful for determining the roughness factor. A measure of this roughness, (area measured by permeability to liquid) -f- (orea of powder with the same size distribution, but made up of spherical particles), is shown to be uniquely related to tensile strength at constant density. The other important factors in determining the strength of sintered-metal compacts are the density and presence or absence of surface oxide. THE manufacture of metal parts by the process of powder metallurgy is an important and rapidly growing industry. Progress has been rapid and continuous, largely because of the excellent research in the field. Nevertheless, the process remains inherently complex and empirical. Several investigators have shown that the properties of the final compact must depend on many variables; namely, shape,&apos; size distribution,"-" nd compositiona of the original particles, the pressure necessary to compress to the desired density, the density of the compact, the time and temperature of sintering, and so on. Through the application of some new techniques to the study of powders and compacts, and the correlation of a number of observations of known variables, the present paper attempts to clarify and simplify the underlying theory of the powder-metallurgy process. Any theory must start with the obvious fact that the strength of a compact, its most useful property, is due to the formation of welded areas between adjacent particles, and attempt to deduce what effect other variables will have on (a) the area and (b) the intrinsic strength of these welds. Such welded areas can be demonstrated by electron micrographs, as in Fig. 1. It was believed that (a) could be most directly studied by means of surface-area measurements on the original powders and on the compacts made from them; the area decrease should be related closely to the welded area. A representative group of eleven iron powders from commercial sources, and made by a variety of processes, was chosen for this study. In addition to the surface-area measurements, correlations were established between the tensile strength and all the known variables which might possibly affect it. The results are quite unexpected. They indicate that the situation is much simpler than the authors had anticipated. The strength of the sintered compact is determined, indeed, by no more than three variables; viz., the irregularity of the original particles, the density of the compact and, in exceptional cases, the amount of surface oxide. All three had been recognized previously as having some effect on the tensile strength, but in the absence of the special techniques and interpretations to be developed here, there could be no suspicion that they were the only relevant variables. Materials and Methods Material—All the iron powders were commercial products obtained from the Amplex Division of Chrysler Corporation. Powders A, B, C, and J were very pure electrolytic iron. Powder D was made from oxidized scrap reduced by heating with an excess of cast iron. Powder E was a high-grade iron ore reduced by hydrogen. Powder I was prepared by atomizing molten cast iron in an air blast, quenching the droplets in cold water, and crushing the coarse powder. Mill scale (oxide) is added and the mixture heated to reduce the high carbon content. The other powders were all prepared by reduction of iron oxides, such as mill scale. They

Jan 1, 1959

By A. J. Terrones

THE classical papers on contact metasomatic deposits by Lindgren on the Clifton-Morenci district,&apos; by Barrell on Marysville, Mont.,&apos; and by Gold-schmitt on the Oslo district, Norway,&apos; laid the foundation for understanding of the importance of separating the metamorphic process from the subsequent metasomatic stage. Knopf&apos; made a big step forward by recognizing that sulfide ore minerals are invariably younger than silicates and by further stressing the importance of structural control" in ore finding. Some years later Harrison Schmitt" fought the idea that contact metasomatic deposits are erratic, irregular, bunchy, economically marginal, and of small size, concluding that these descriptions have little factual basis. He emphasized the importance of detail mapping and careful geological study as fundamental requirements for a better understanding of these deposits. This article presents a comparative description of the structural features at the Magistral, Antamina, Morococha, Vilca, Ferrobamba, Katanga (Quibio), Tintaya, and Huarca contact deposits (Fig. 1). Further, it will describe how these structural features controlled the emplacement of the intrusives, their shape, distribution of metamorphic and metasomatic halos, and sulfide deposition in post-skarn structural channelways. Finally, the modifications introduced by a superimposed hydrothermal stage recognized at some localities will be discussed. Primary exploration and careful sampling of recognized structural targets were instrumental in outlining the copper ore potential at the Antamina and Tintaya districts, thus proving the benefits and reward of careful geological examinations in this type of deposit. The Magistral District: This district lies in the Province of Pallasca, Department of Ancash, in northern Peru, at 8o 16&apos; S and 77" 47&apos; W. High to medium grade copper orebodies in garnetite, bordering a quartz monzonite stock, are exposed at the bottom of a glaciated valley in the western slope of the Andes at 4250 m (14,000 ft)* elevation.

Jan 1, 1959

By M. E. Wadsworth, R. L. Pearson

THE dissolution of UO, in carbonate solutions can occur only il the tetravalent uranium is oxidized to the hexavalent state. The carbonate system is of particular interest because it provides a means whereby the oxidized uranium may be dissolved by forming the complex ion UO,(CO3)3-1. In the presence of oxygen the over-all reaction may be written UO+1/2O,4CO3T+2HCO2UO,(CO4)11+H2O [1] UO, was used in this study because it could be obtained in high purity and also because it is representative of the most refractory of the primary uranium minerals. The mineral ulrichite is the natural counterpart of the synthetic UO, used. The kinetics of the leaching of UO, should be similar for any of the uraninite type minerals. A pressurized system was used not with the hope it could be extended to commercial systems as a primary purpose but simply to provide the means whereby important temperature and pressure parameters could be varied for the evaluation of the kinetic processes. The importance of such pres-

Jan 1, 1959