Search Documents

By H. C. Brown

SINCE 1934 the steel industry has been utilizing the spectrograph for supplementing wet chemical analysis in the production control of electric and open hearth furnaces. This means of control made great strides during the war years because of the general acceptance of the spectrograph and the increased emphasis that was placed on rapid control methods. However, in the post war era, with the demand still on increased production, it became apparent that a still more rapid and economical means of production control was needed. Since the spectrograph had been used mostly in the analysis of low alloying and residual elements, it also became apparent that equipment was needed to extend the spectrographic technique to the analysis of the high alloying elements in stainless steel. For these reasons, companies manufacturing spectrographic equipment were prompted to start development work on direct reading instruments. In June 1949, the Applied Research Laboratories of Glendale, Calif., announced that a direct method of spectrochemical analysis for stainless type steels had been developed. This paper will describe the use of the Applied Research Laboratories Production Control Quantometer in the quantitative control of stainless, silicon, and plain carbon steels being made at the Butler Pennsylvania Div. of the Armco Steel Corp. The Armco Butler Div. has one 70-ton electric furnace and six 150-ton open hearth furnaces. The electric furnace is employed in the making of all types of stainless steel and the open hearth furnaces are used for the production of silicon, wheel, and plain carbon steels. The ARL quantometer was purchased primarily for the purpose of controlling the steelmaking in the electric furnace, but its use has been extended for the analysis of final tests (ladle tests) on a number of different types of stainless, silicon, and plain carbon steels. Because of this additional work by the quantometer, substantial savings in manpower and time have been realized by the laboratory. In the analysis of a set of preliminary tests from the stainless steel furnace, approximately 40 min in laboratory time are saved due to quantometric analyses. Despite the fact that more specialty grades of stainless steel are being made in the electric furnace, the average tons per hour have been increased since the quantometer was put into operation. Specialty grades require more furnace time than regular commodity grades of stainless steel. The installation of the ARL production control quantometer was completed on March 13, 1952. By May 1, 1952, the instrument was calibrated for nickel, chromium, manganese, silicon, and molybdenum, which are the elements necessary for the production control of the stainless steel furnace. Within the following month, training of personnel on the quantometer was achieved and a study of the accuracy of the instrument showed that the results obtained were sufficiently accurate for control purposes. Therefore, on June 11, 1952, the quantometer was placed on production control for all types of stainless steels. Starting September 11, 1952, the instrument was gradually placed on ladle analysis (final tests) as the analytical curves were refined and additional curves were drawn. The quantometer has been relatively free of breakdowns since placing it on production control. The samples from only one stainless steel heat have had to be analyzed by wet chemistry because of instrument trouble. The previously existing heat-time record was also bettered by 15 min on a commodity grade of 18-8 stainless steel. Scope of Control In general, the quantometer determines all elements necessary for the production control of all types of stainless steel heats and for the ladle analysis of various types of stainless steel heats. It is also used in reporting final results for silicon, manganese, chromium, nickel, molybdenum, tin, copper, and aluminum on all silicon steel grades and manganese, chromium, nickel, molybdenum, tin, and copper on several plain carbon steel grades. Table I shows the elements and the concentration ranges of these elements in the various types of stainless, silicon, and plain carbon steel that are determined on the quantometer. A study of the results obtained on ladle test samples of stainless steel types 410, 430, 430 Ti, 446, 301, 302, 304, 304L, 305, and 17-7 PH will be discussed. Also included in the study are the results obtained on ladle test samples of a number of silicon steels. Apparatus In order to take full advantage of the potentials of the production control quantometer, the unit has been placed in an air-conditioned room with relative humidity control. The temperature is maintained at 73'22°F and the humidity at 45&5 pct. The air conditioning serves as a precaution to minimize the amount of adjustment and calibration needed during operation. It also reduces contaminating fumes and dust and thereby lessens the necessity for maintenance on the equipment. The quantometer is composed of three units: the high precision multisource unit, the 1.5 meter vertical spectrometer, and the console. The source unit supplies excitation conditions varying from spark-like discharges to arc-like discharges. The voltage to the source unit is supplied by a motor-generator

Jan 1, 1955

By J. H. Wernick

IN a study of the rate of decomposition of %-in. cubes of limestone, dolomitic limestone, and dolomite in a sweeping nitrogen atmosphere, Joseph, Beatty, and Bitsianes' found that the zone of calcination advanced at substantially a constant rate at a given temperature. The purpose of this paper is to show that their data indicate at least two processes occurring when the above carbonates decompose. It is suggested that there are two processes occurring consecutively, one the limiting process in a given temperature range and the other the limiting process over another temperature range. The data of Joseph and co-workers have been extended by use of the Arrhenius equation, Eq. 1, a relation beween the velocity constant k of a reaction and the absolute temperature T. d In k A ' dT Rr2 A is the activation energy in calories per mol (additional energy that must be added for an average molecule to react), and R is equal to 1.986 cal

Jan 1, 1955

By F. D. Rosi

The slip and twinning behavior in extended titanium crystals were studied in some detail. The formation and appearance of coarse kink bands are discussed. Their crystallographic geometry was determined by X-ray analysis. A phenomenological interpretation of the complexities in kink band development is also presented. The critical resolved shear stress, coefficient of shear hardening, and plane of fracture were determined for several crystals extended at room temperature. THE slip and twinning elements observed in the room-temperature deformation of titanium were enumerated in a previous paper1 in which considerations were advanced regarding the nature and selection of these elements and their effect on the known mechanical properties of this metal. The present study concerns the crystallographic, microscopic, and mechanical aspects of flow in relation to the slip and twinning elements, and includes a prediction of slip systems, nature of slip and twin markings, inhomogeneities of plastic flow, and stress-strain characteristics. Unless otherwise noted, arc-melted titanium sponge (99.77 pct) was used in these experiments. The method of production of crystals, their dimensions, and the surface preparation for micrographic examination have been reported.&apos; For obtaining stress-strain characteristics, only those crystals which traversed the entire width of the specimen and were at least 8 mm in length were used. Tensile deformation of the crystals was performed with conventional grips for sheet specimens and a constant-stress loading beam, designed after the method of Andrade and Chalmers.&apos; The specimens were loaded by allowing sand to flow from a reservoir into a bucket suspended from the longer end of a balanced 6:1 lever arm at a rate controlled to load the specimen approximately 2 kg per min. Strain measurements were made using the Baldwin SR-4, bonded, resistance-wire strain gage, Type A-8, which permitted a reading accuracy of 2 microinches per inch. The formulas used in the evaluation of shear stress and shear strain, as in deriving the coefficient of shear hardening, are given by Schmid and Boasv n terms of the original orientation and change in length of the crystal. For calculating the critical resolved shear stress, the standard equation was used. The crystallographic nature of the unpredictable slip observed in a number of specimens was determined by the single-surface X-ray method of analysis as described in ref. 1. Experimental Results Prediction of Slip System: It was reported&apos; that room temperature slip in titanium takes place predominantly on {10i0} and in a <1120> direction, giving three potential slip systems. Hence, it should be possible to predict the operative primary system in the manner used by Taylor and Elam&apos; for alu- minum (i.e., the one with the greatest component of shear stress in the direction of slip). The stereo-graphic construction in Fig. 1 shows that this is true. In all cases, slip was found to occur initially on the (0110) plane and, in a number of cases, in the [21f0] direction. (The direction of slip was not determined for all orientations.) It follows that duplex slip can be expected when two slip systems are geometrically equally favorable for slip, as demonstrated in Fig. 2. In both crystals slip took place simultaneously on the (1700) and (olio) prismatic planes, as indicated by Fig. 2a and b. In the case of crystal B the movement of the specimen axis with increasing extension was toward the (10i0) direction, which represents the stable end orientation resulting from alternate slip on the [2ii0] and [1120] directions. This is analogous to the duplex slip process in face-centered cubic metals." Unpredictable Slip: In a number of crystals whose orientations were well within the operation of a single slip system, secondary slip occurred on planes not predicted by the criterion of maximum shear stress. Examples are shown in Fig. 3. In addition to

Jan 1, 1955

By Harold Vagtborg

Equilibrium vaporization ratios were obtained for light hydrocarbons, nitrogen, carbon dioxide, and hydrogen sulfide in a reservoir fluid containing 35 mole per cent hydrogen sulfide. The data cover the range from 700 to 2500 psia at 154°F. The results of this study are compared with results obtained by other investigators on systems containing less hydrogen sulfide. When large amounts of hydrogen sulfide are present, the equilibrium vaporization ratios for ethane and heavier hydrocarbons are greater than the ratios for systems containing little or no hydrogen sulfide. Large amounts of hydrogen sulfide have the reverse effect on the ratios for methane. Routine PVT studies were performed on the reservoir fluid including flash and differential liberations of the dissolved gas. The pressure-volume relationships of the saturated fluid were also determined. It is shown that the use of published correlations on physical properties of reservoir .fluids can lead to gross errors when applied to systems containing large amounts of hydrogen sulfide. INTRODUCTION Equilibrium vaporization ratios for various components in naturally occurring crude oil and condensate systems have been reported in the literature.1,2,3,4 Recently, several papers have been published with emphasis on non-hydrocarbon components such as nitro- gen, carbon dioxide and hydrogen sulfide.5,6,7,8,9 The increased discovery of reservoir fluids having high concentrations of these non-hydrocarbon components, particularly hydrogen sulfide, has created a need for a further study of their phase behavior. Equilibrium vaporization ratios are known to vary with pressure, temperature, and overall composition of the system.&apos;" It was anticipated that ratios for systems containing large amounts of hydrogen sulfide would differ from the ratios for systems containing small amounts of hydrogen sulfide. Therefore, the present work was undertaken in order to obtain reliable equilibrium vaporization ratios for the reservoir-fluid in question. PROCEDURE The procedure followed was evolved after considerable experimentation on methods of handling the very sour crude. It was found that drying agents (e.g. CaCl2 and CaSO4) absorbed an appreciable amount of hydrogen sulfide from the gas used to prepare the recombined samples. The concentration of hydrogen sulfide dropped as much as 10 mole per cent in a single pass through a 3-ft drying tube. It was also found that when undried gas was agitated with mercury in the PVT cell, a black scum, believed to be mercuric sulfide, was formed and the hydrogen sulfide content of the gas dropped several mole per cent. Because composition changes during a run could not be tolerated, separation of the mercury and sour fluid was necessary. In order to effect this separation, a stainless steel piston, equipped with Teflon O-rings, was placed in the PVT cell between the mercury and the sour fluid. This piston had to be constructed in three parts because

Jan 1, 1955

By J. O. McCaldin, P. Duwez

ALLOTROPIC transformations between 1000° and 1900°C have recently been reported for several metallic elements. Since the proposed transformations are based on limited evidence, it was decided to examine the elements in question as well as some refractory metals by thermal analysis with a photoelectric technique similar to that described by Hug-gins, Roll, and Udin.1 In this method, a lead sulphide cell was used to detect thermal radiation from an electric-resistance heated strip specimen. A thermocouple spot welded to the specimen was used to calibrate the temperature of the system under steady temperature conditions, and recording was accomplished with a cathode ray oscilloscope. In the method used by the present authors, the temperature calibration was omitted and the cathode ray oscilloscope was replaced by a recording galvanometer. This technique, in which electric current passing through the specimen heats it, will be referred to henceforth as Method 1. Another arrangement was required for those cases where the specimen could not be formed into a wire or strip suitable for resistance heating. In such cases the specimen was a sintered compact heated by thermal radiation from a hot tungsten strip, Fig. 1. The specimen was insulated from the heating strip with a thin layer of thoria powder or suspended on 0.004 in. tungsten wires. The take-up spring had just sufficient tension to prevent buckling of the heating strip due to thermal expansion. This technique will be called Method 2. Both methods were tested with specimens of iron and titanium and the well known allotropic transformations, a toy and ? to 8 in iron and a to in titanium, were very clearly detected. Fig. 2 shows one of the records obtained for titanium. For this particular experiment, the iodide titanium specimen was a square rod 0.080 in. on an edge and 3 in. long.

Jan 1, 1955

By Leendert de Witte

Conventional resistivity logs consisting of a short normal, a long normal, and one or more long lateral curves do not give data that allow a complete quantitative interpretation in beds thinner than 20 ft. Reservoir rocks usually exhibit zones of continuous homogeneity of quite limited thickness where the long lateral curves become useless because of adjacent bed effects and boundary phenomena. If the beds are 12 ft or thicker, the short and long normals may be used for qualitative interpretation, which can be streamlined by the application of simplified departure curves. For beds of a thickness less than twice the long normal spacing, this procedure breaks down. The combination of the limestone curve, the later-olog or guard electrode log, and the microlaterolog permit quantitative interpretation for beds that are at least 10 ft thick, provided the mud resistivity and the hole diameter are known with sufficient accuracy. For beds thinner than 10 ft, combinations of the microlaterolog with short spaced laterologs and pseudo laterologs appear to be promising. Interpretation of these curves again requires the application of simplified departure curves. Resolution of various possible combinations was analyzed using departure curve data calculated on the Whirlwind I computer at the Massachusetts Institute of Technology. A field example is shown using the microlaterolog-microlog combination, and the combination of a 6-in. modified laterolog plus a 6-in. pseudo laterolog. INTRODUCTION For the purpose of quantitative interpretation of resistivity logs in porous formations, we want to obtain two essential quantities from the logs, namely, the true resistivity of the undisturbed formation, Rt, and the resistivity of the part of the formation invaded by mud filtrate, Rt. The apparent resistivities of all conventional logging devices are functions of these two parameters and are also influenced by a third unknown parameter, the diameter of the invaded zone, d. It has been shown&apos; that from the normal curves alone it is impossible to arrive at a unique solution for the three unknowns, Rt, R1, and d1. In very thick homogeneous beds, if invasion is not too deep, we can obtain a fair approximation to Rt from the long lateral curves and then use the two normal curves to find Rt and d1 Even under the most favorable conditions, the resolution of this system is not very good. The short normal does not give a reasonable approximation to R1 unless invasion is very deep (dl>16 hole diameters). For very deep invasion, however, the long laterals no longer approximate Rt. For bed thickness between 20 and 40 ft, the long laterals are affected appreciably by the adjacent beds; and the curves are distorted by boundary anomalies to the extent that they lose their quantitative usefulness in most cases. For the same bed thicknesses, the normal curves still function reasonably well. Although it is impossible to find unique solutions Lor R1 and Rt using the normal curves alone, we can obtain a reasonable approximation for the ratio R1/Rt through the use of simplified departure curves. This fact was brought to our attention by A. J. de Witte, geologist with Continental Oil Co. As the magnitude of Rl/Rt is a major clue to the presence of oil in formations, this method can be used to good advantage for qualitative analysis and will be discussed in somewhat greater detail. With the aid of suitable bed thickness corrections, the analysis of the normal curves may be used for bed thicknesses larger than 12 ft. For thinner beds, the method rapidly loses its resolution; and we have to resort to different types of resistivity logs if we want to attempt to analyze the curves quantitatively. The inadequacy of conventional resistivity curves in thin beds is far more serious than generally realized. Fig. 1 shows a conventional E. S. with a 16-in. and 64-in. normal and a 16-ft lateral through a section of Lansing-Kansas City lime, in comparison to a guard electrode survey through the same section in a neighboring well. The porous zones, which show up as low resistivity breaks on the guard electrode log, are completely masked by adjacent bed effects and boundary anomalies on the conventional curves. Even the short normal shows most of the porous Zones only as Vague deflections and in many cases fails to register Their

Jan 1, 1955

By D. J. Carney, E. C. Rudolphy

Large macroscopic nonmetallic inclusions were related to altered fireclay refractories by chemical and microscopic means. Pouring refractories are discussed as a source of these large inclusions. Nozzles and wells are major contributors. Use of alkali and titania contents as tracers is described. Recommendations are offered to minimize the sources of inclusions from pouring refractories. IN any attempt to improve the cleanliness of plain carbon and alloy steels, consideration must be given not only to the proper deoxidation practice to minimize inclusions, but also to sources of inclusions from pouring refractories. In some cases, the inclusions resulting from deoxidation may be minor in amount, yet a relatively dirty steel may be produced as a result of improper care in the pouring practices for the steel. The number of studies of inclusions resulting from pouring refractories has increased recently and some excellent reports on this subject have already been published.&apos;4 Some of these reports were reviewed briefly in a companion paper by M. P. Fedock.5 Mr. Fedock&apos;s contribution is a fine addition to the studies necessary to improve steel cleanliness for the ultimate benefit of all steel producers and consumers. In the interest of constantly improving cleanliness, the authors have been actively engaged for the past two years in experimentation to determine more closely the sources of inclusions in steel. One phase of this work was associated with efforts to define more closely the sources of macroscopic inclusions which have been experienced on occasional heats. The term "macroscopic inclusions" is defined in general as those inclusions which are visible to the naked eye or at low magnifications of the order of less than X25. These inclusions sometimes can be seen in the macro-etch tests of billets and slabs. This report summarizes a few of the field experiments and laboratory studies conducted at the South Works of the United States Steel Corp., which were made regarding nozzles, wells, and ingot scums, as well as inclusions occurring in steel products. The data in the present study, together with the data of Mr. Fedock concerning ladle erosion, should be of value in regard to future studies of inclusions arising from pouring refractories. The knowledge gained as a result of data collected thus far at South Works has been helpful in improving the cleanliness of the products and in pointing the way toward further improvements. Similarity of Large Inclusions to Refractories and Altered Refractories In the routine inspection of billet etch tests, occasional inclusions visible to the naked eye have been observed. These large inclusions most frequently occur near the top of the ingot and near the billet surface. When such material was encountered, careful examinations were made in an attempt to determine the origin of these inclusions. In a relatively few cases, examination revealed that the material was unaltered fireclay refractory of a type similar to that used for hot-top material, with only the surface of the inclusions having an altered appearance under the microscope. However, the great majority of these inclusions were completely altered-refractory material. The term "altered refractory" is defined

Jan 1, 1955

By B. M. Larsen

A discussion based on three commercial furnace tests and electrical analogue calculations is presented. It shows that while regenerator efficiency is mainly dependent on loading or relative amount of heat exchange surface plus the heat transfer coefficients as effected by flow velocity, the actual air preheat temperature can be high or low, largely independent of regenerator efficiency, mainly due to the diluting or unbalancing effects of cold air leakage into various parts of the furnace system. THERE are many signs of a renewal of interest in the heat regeneration aspect of the open hearth process, among them being the recent paper by Marsh,&apos; the introduction of auxiliary checkers in the stacks of the Isley furnace design, and a number of recent installations of two-pass checkers in new and old furnaces. However, there are also signs of yielding to the usual temptation of oversimplifying a problem. Faced with the job of obtaining better draft on a furnace, for example, a good designer always recognizes that focusing attention on some one factor, such as height of the stack or capacity of the exhaust fan, does not make his problem any easier; rather he must look at the whole system, including such items as valve resistances, bends in the flues, and flow resistance in the waste heat boiler; then he must make his design in relation to the available draft so as to avoid any serious bottleneck in the system. Yet this example is really much simpler than the problem of air preheating, and again, the latter problem is not really made easier by concentrating on air temperature in uptakes and on the more obvious methods for making this air as hot as possible. Also to be considered are such things as the total amount of air needed theoretically for complete combustion at any selected fuel rate, together with that needed for oxygen absorbed into the bath and for burning the combustible gases given out from the bath, plus some excess air. Furthermore, how does this total air requirement relate to the regenerator efficiency at various loadings? How much of the total air equivalent in stack gases will come from preheated air passed through the whole length of the incoming regenerator and how much from air leakage into various zones of the whole furnace system? Does the effect of leakage air differ depending on whether it leaks into the ingoing regenerator, the furnace above floor level, the outgoing regenerator, or the stack zone? Over a number of years we have in this Laboratory experimented with methods for measuring hot gas temperatures; we have measured, approximately, the efficiency of a few regenerators on commercial furnaces and we have developed an electrical analogue&apos; for calculations of regenerator efficiency. The whole problem is too complex to cover in one paper even with a more complete background of data than we possess, but we can attempt here to clarify certain aspects in a general way, hoping to assist specific plant studies on individual furnaces. Some of our earlier experience has been incorporated into chaps. 4, 19, 20, and 21 in the book "Basic Open Hearth Steelmaking,"" and on the assumption that this text is available to most readers, this discussion has been shortened by references to that book. The most recent design of a flowing-gas thermocouple which we are now using for measurement

Jan 1, 1955

By William J. Campbell

The columbite-tantalite mineral series was studied by various instrumental techniques to establish the relationship of density to composition. The samples used were carefully selected to obtain a mineralogical purity of at least 98 percent. Impurities were determined by optical microscopy, X-ray diffraction, and optical and X-ray spectroscopy. Each sample was analyzed by fluorescent X-ray spectroscopy for iron, manganese, columbium (niobium), and tantalum. The existence of a unique relationship in this isomorphous series permits a simple correlation of the intensity of a spectral line with the concentration of the analytical element.

Jan 1, 1955

Jan 1, 1955

By J. F. Peters

The term solution loss is discussed and defined. Examples are given showing that solution loss may either have a favorable or unfavorable effect on blast furnace performance. A theory is advanced explaining the contradictions encountered during earlier studies of the problem. MANY papers have been written and numerous theories advanced concerning the chemical reactions in the iron blast furnace. Richards, discussing the utilization of fuel in the blast furnace, said: "All the carbon burnt in the furnace should be first oxidized at the tuyeres to CO and all the reduction of oxides above the tuyeres should be caused by CO, which thus becomes CO,. This dictum is not Gruner&apos;s own words, but expresses their sense, and from the point of view of the present discussion, it is the correct principle upon which to obtain the maximum generation of heat in the furnace from a given weight of fuel." Richards also said the cubic feet of wind per pound of coke does not express how efficiently a furnace is running, but it will be shown later where Howland paid much attention to this figure. Richards pointed out a shortcoming of Grun-er&apos;s discussion in that Richards claimed there is not enough CO generated in a good working blast furnace to possibly combine with the oxygen of the ore, so some of it must be reduced by solid carbon. Mathesius2 made two important contributions. First, he wrote the direct and indirect reduction equations showing the heats of formation in each case and stressed that the indirect reduction reaction produces heat while direct reduction absorbs heat. Secondly, he substantiated Richards&apos; conclusion that there may be a deficiency of CO gas and that some direct reduction is required, but he pointed out that "direct reduction in the hearth has often been confused with direct reduction in the stack, which more correctly should be termed &apos;premature combustion&apos;." Then he said that "as this carbon is consumed partly by economical (direct reduction in the hearth) and partly by wasteful reactions in ever varying proportions, it is evident that the relation of this total carbon gasified above the tuyeres to the fuel consumption of a furnace cannot possibly have a direct bearing on the economy of furnace operation. The premature combustion of carbon (CO2+C?2CO) must therefore in all cases be considered a detrimental reaction." Johnson3 discussed this whole problem. Through experience Johnson found that when departure from Gruner&apos;s ideal working is considerable, the fuel economy is poor, and when the quantity of blast goes up, the fuel economy goes up in the same proportion. Johnson said that the wind per pound of coke is a measure of fuel economy, which will be shown to be wrong. Howland4 established the fact from operating data that there was no relationship between the coke consumption of a furnace and the percentage of coke burned at the tuyeres. But some of his calculations have led to questionable conclusions, such as "it is practically impossible to obtain low coke consumption unless we keep our wind low." Howland made an important contribution when, in his concluding paragraphs, he reached certain negative decisions as to why one coke works better than another. He said the reason one coke works better than another in a blast furnace is not because: 1—there is any difference in the percentage gasified at the tuyeres, or 2—there is any difference of wind required per pound of coke. Korevaar5 propounded a new theory on combustion which disagrees with Gruner because "as far as we can see, this is sufficient proof for the invalidity of Gruner&apos;s ideal, for if it was valid, the Low coke consumption should always be accompanied by a higher percentage of carbon burned at the tuyeres. This not being the case, we must deliberately give up our belief in Gruner&apos;s ideal." The part in italics will be proved to be wrong. Martin" contended that there was not enough reducing capacity in the blast furnace unless solution loss occurs. He came to a series of conclusions, such as: 1—The greatest efficiency of the blast furnace may not be attained when the reduction is performed entirely by carbon monoxide as demanded by Gruner&apos;s definition of the ideally perfect working of the blast furnace. 2—The so-called solution loss reactions, which should more properly be termed direct reduction reactions, promote furnace efficiency. 3—In modern blast furnace practice, the carbon consumption of the process is determined primarily by the carbon needed for reduction purposes, any thermal deficiency created by the reduction process being balanced in practice by the use of blast heat. From a practical standpoint further discussion of the theory of chemical reactions is of little moment. There is however one phase of the general theory of chemical reactions which is very important and that is the combustion of coke in the blast furnace. The purpose of this paper is to show that the reaction

Jan 1, 1955

By J. Chipman, H. R. Larson

The data previously reported for the quantity as a function of oxygen pressure at 1550°C have been used to compute the activities of Fe, FeO, Fe2O3, and COO in slags of the ternary system. Activities of the first three have been obtained also for two quasi-ternaries involving fixed CaO:SiO2 ratios. IN a previous paper1&apos; the authors reported the results of an investigation into the effects of oxygen pressure on the composition of various simple slags analogous to some of those which are found in steel-making practice. The ratio of ferric iron to total iron was studied at 1550°C in iron oxide melts to which lime, magnesia, lime-plus-silica, and other oxides were added. The oxygen pressures involved those of air, carbon dioxide, and carbon dioxide plus carbon monoxide in several proportions. Although very low oxygen pressures could not be used, the slag-metal equilibrium studies of Fetters and Chip-man&apos; permitted extending the results to slags in equilibrium with iron. For the ternary system CaO-FeO-Fe,O, the oxygen pressure-composition relationship has been determined from zero percent lime to lime saturation over an oxygen pressure range from air to that represented by equilibrium with liquid iron. Lime and silica were added to iron oxide in the ratios 0.54, 1.306, and 2.235 to form three quasi-ternary systems which were also studied over the entire region of liquid melts at 1550°C. Ternary Gibbs-Duhem Equation Wagner" has developed a method by which the activities of two components of a ternary system can be calculated if&apos; the activity of the third component is known throughout the composition range being considered. The fundamental form of the Gibbs-Duhem equation for ternary systems is N, d In a, + N2 d In a, + N3 d In a3 — 0. Wagner has developed a usable form of this equation by introducing the term y = N3/(N3 + N1) and rearranging the equation to give (? In a1/?N2)x = -y/(1-N2)2 (? In a2/?y) x2 N2/1-N2 (? In a2/?N2) y To apply this equation to the slag system CaO-FeO-Fe,O,, the activity of one of these components must be known. However, the only activity which is known from the experimental data is the activity or pressure of oxygen in the gas phase with which the slag is in equilibrium. The activity of oxygen in the slag can be defined as the square root of the oxygen pressure. In order to use oxygen as one component, the composition of the slags must be converted to the basis Fe-O-CaO. Oxygen, exclu-sive of that contained in CaO, then becomes com-ponent 2 in Eq. 1, Fe is selected as 1 and CaO as 3. Then y = Ncao/(Ncao + NFe). Eq. 1 then becomes (? In a fe/? Nx) y = -y/(1-No)2 (? In ao/?y) xp - No/ 1- No (? In ao/ O No) y. In order to evaluate Eq. 2, the boundary conditions must be known. The obvious choice of a standard state for iron is to assign slags in equilibrium with iron an activity of one. Then In a,., or log aFe, which is substituted for convenience, is determined by integrating along a line of constant y from the slag in equilibrium with iron to the composition at which log a,, is to be determined. Mathematically this can be expressed as log aFe (Nlog y) = log a&apos;Fe + (? log a Fe/? No) dNo where the primes indicate equilibrium with liquid iron and a&apos;Fe = 1. When Eq. 3 is integrated along a line of constant y, the following is obtained: log a Fe (No, y) = - y No ?/ No ? y ( log ao/(1- No)2) No d No - No/1-No d log ao. Lime-Iron Oxide Slags Iron Activity: The oxygen pressure of lime-iron oxide slags is shown in Fig. 1 as a function of j, de-fined as j = Fe+++/(Fe++ + Fe +++) for various constant mol percentages of lime. The j values at 0 to 60 pct lime were then determined for oxygen pressures of 1, 10-1, etc. to 10-" atm. For purposes of calculation, the line for zero percent lime was extrapolated to

Jan 1, 1955

By A. B. Dyes

In the operation of a water-driven reservoir, a free gas saturation can he established by maintaining production rates fast enough to cause the reservoir pressure to decline below the bubble point. The benefit of such a procedure on the displacement efficiency of the oil by water is illustrated for two types of sandstone samples from one reservoir. Those rock samples showing the poorest recovery to water drive in the absence of a free gas saturation give the most improvement in the presence of a free gas saturation. Employing one type of reservoir fluid (low .shrinkage) the benefit of evolved gas on oil displacement is calculated at several reservoir pressures below the bubble point. This demonstrates the presence of air optimum pressure for water displace,rnent which is .several hundred pounds per .square inch below the bubble point. Displacement of oil at the optimum pressures results in the removal of 7 to I? per cent more oil than would be obtained by displacement at the bubble point pressure. In some instance. this magnitude of increase may be worthy of consideration in establishing the maximum efficient rate of production from many water-driven fields. INTRODUCTION For many years the belief that the use of gas could be combined with that of water to result in a better recovery operation than the use of either of these phases alone has been prevalent in the oil industry. This is evidenced by the several field trials which have employed the injection of gas and water in combination.1.2.v In most cases the small amount of any additional recovery, in combination with the limited knowledge available on the older reservoirs, has left uncertain the influence of gas on recovery in these earlier attempts to combine the use of gas with water. Research studies in recent years have demonstrated through laboratory. floods the magnitude of the benefit of the presence of gas on the displacement of oil from sandstones by water.5,6,7,8,9,10,11 In addition, studies of the distributions of the phases which are present during the displacement process have developed concepts concerning the mechanism by which this benefit is obtained."." It now remains for the engineer to incorporate these findings into the general technology of reservoir operations. It is the purpose of this paper to illustrate that the production of a water-driven reservoir at pressures below the bubble point is one such operation whereby improved oil displacement efficiency can be obtained as a result of gas evolution. The establishment of a gas saturation by evolution of dissolved gas was one of the techniques used by several investigators in the laboratory studies. The possibility of obtaining the benefit of gas evolution in water-driven reservoirs by producing at pressures less than the bubble point has 3150 been pointed out previously." The desirability of this operation has undoubtedly

Jan 1, 1955

By A. M. Gaudin, D. W. Fuerstenau

IN concentration of certain ores by soap flotation, prevention of quartz flotation is desired; the contrary is true in treatment of some oxide iron ores. Experimental study of the flotation of quartz goes back at least a quarter of a century.&apos; Clean quartz does not float with fatty acids or soaps but does float when activated by one of many metallic salts. Control of pH is important. Broadly speaking the problem of quartz flotation has been approached from the empirical side, as was the related topic of flocculation or dispersion of quartz suspensions.&apos; Empirical studies indicated the existence of critical relationships between the additions of collector and activator. These additions were not stoichiometric for the formation of soaps of the activator cation.

Jan 1, 1955

By M. L. Leonardi

THE Searles Lake orebody is located in the north- west corner of San Bernardlno County. It is a dry lake bed with an exposed salt surface covering an area of 12 square miles. Recoverable mineral values are contained in the mother liquor below the surface of the lake. Stratification in the lake bed has separated the brine into two bodies which dlffer in composition. Although liquor is processed from both bodies, this paper will discuss only the upper structure brine. Fig. 1 illustrates a typical cross-section of the two commercial orebodies. The orebody is composed of a porous salt deposit 70 to 90 ft deep. The upper structure is separated from the lower orebody by a 12 to 16-ft thick impervious mud seam, as shown in Fig. 1. These salt structures are composed of 55 pct solid-phase salts and 45 pct voids which are filled with the original mother liquor. The brine wells are drilled to the separating mud seam and cased to wlthin 10 ft of the bottom. This is done to draw the brine horizontally from the bottom of the structure. It is pumped with multistage centrifugal pumps Into the plant at the rate of 3 milllon gal per day. The first process that was successful was developed by Charles P. Grimwood for the recovery of potash. The first evaporator unit was built in 1916. In the early twenties, Dr. Morse worked out a process for the recovery of borax. This made the cycle more efficient, as the end liquor could be sent back to the evaporators rather than being sewered. In 1926 the American Potash & Chemical Corp. was formed as a new company, and the entire plant was remodeled. The plant at that time produced only potash, borax, and boric acid. Since then the American Potash & Chemical Corp. has added processes for the production of USP boric acid, refined potash, sulphate of potash, soda ash, salt cake, lithium concentrates, Pyrobor (Na2B4O7) bromine, phosphoric acid, and lithium carbonate. The main plant cycle may be depicted as a closed cycle, see Fig. 2. The raw material, brine, enters the cycle to be mixed with the end liquor, known as ML2, from the pentahydrate borax crystallizers. The mixture of these two forms evaporator feed. Evaporator feed is pumped to the evaporators where it is concentrated, with respect to potash and borax. In the same operation water vapor, sodium chloride, salt trap salt, and clarifier salt are removed from the cycle, see Fig. 3 for potash plant product. The evaporators produce a concentrated liquor which contains approximately 19.5 pct KCI. This liquor is diluted as it enters the potash plant to keep all salts, except potash (KCI, 97.0 pct) in solution. Here the moist potash leaves the cycle at 100°F. The end liquor, known as ML1, is pumped to the borax pentahydrate crystallizers, where crude borax pentahydrate is crystallized and removed as solid phase. The ML2 is sent back to pan feed to be reconcen-trated, see page 207. Note that the only water to leave the cycle is in the form of vapor and moisture in the solid phase products crystallized. Thus there is a constantly cycling volume of liquor to which brine is added. Since the volume of liquor cycled does not increase, the brine is, in effect, evaporated to dryness. This would be true if there were no liquor losses. But, as in all processes, there are always unavoidable and accidental losses which reduce the volume of cycling liquors. The losses must be made up with brine. The concentration process is the beginning and the end of the cycling liquors. In this process there are three evaporator units of the triple effect counter-current type, that is, there are three pans in each unit and the heat flows in one direction while the liquor flows the other way through the evaporator pans, see Fig. 4. During the evaporation process a great deal of sodium chloride, burkeite, some sodium carbonate monohydrate, and a little lithium-sodium phosphate are crystallized. The volume of these salts is so great that they must be removed as they are formed or the process would come to a standstill. Brine and recycled mother liquor No. 2 enter the third effect evaporator pan from the evaporator feed storage tanks, see Fig. 5. A steady flow of liquor is removed from the bottom of the No. 3 pan and is pumped through the No. 3 cone of the salt trap, a clear liquor being returned to the NO. 3 pan. A portion of this clear liquor is pumped to the second effect pan. This process is repeated in each pan. The liquor from the No. 2 pan is pumped through the No. 2 salt trap cone and returned to the No. 2 pan.

Jan 1, 1955

By N. K. Chen, R. Maddin

Single crystals of molybdenum were extended at temperatures from 1300° to 2500°C. It was found that with increasing temperatures, the yield becomes more pronounced and the number of slip bands for equal amounts of elongation decreases. Slip at high temperatures fragments the structure. OTHER than the investigations on sodium and potassium by Andrade and Tsien,&apos; the researches of Steijn and Brick&apos; on a iron single crystals at low temperatures are about the only studies of the influence of temperature on glide of body-centered cubic single crystals. The effect of test temperature on glide has been rather widely investigated with hexagonal crystals" and less widely with face-centered cubic crystals. ~~ a result of these studies it can be said that, in general, the onset of plastic flow as measured by the initial rate of strain hardening becomes more abrupt with increasing temperature, and the value of the yield decreases with increasing temperature. Strain hardening, however, is markedly affected by changes in temperature except at very low and very high temperatures where the strain hardening rate becames constant. In the present investigation it is shown that temperature affects the glide of molybdenum single crystals in much the same manner as crystals of other classes, it., for comparable strains the number of slip bands decreases with increasing temperature; shear along the slip bands increases with increasing temperature; the yield becomes more pronounced with increasing temperature of test; and the strain hardening approaches a constant at very high temperatures. In addition, it is shown that, in agreement with the work of Tsien and Chow, Qlip occurs on (110) planes in <Ill> directions. It is further shown that slip at high temperatures fragments the structure into either irregular sized cells or bent atomic planes which are roughly aligned in crystallographic directions. Experimental Procedure Single crystals 3 mm in diameter by about 25 mm long were prepared using the technique previously described.&apos; The furnace in which the crystals were grown served as the extension apparatus for the tension tests. It consisted of a 4 in. water-cooled brass tube 20 in. long which was continuously evacuated at the bottom. Two water-cooled copper electrodes held the specimen by means of spherical collets secured in place in the electrodes by set screws. These electrodes served also to transmit power and stress to the specimen. The lower electrode was clamped to a stand, while the upper electrode was fastened to one side of a lever arm flexibly supported at the top through a slightly offset pinion. A metal bellows operating elastically was attached to the upper electrode to affect a vacuum seal and allow freedom of motion. The level of the arm was adjusted by rotating a graduated nut. Rotation of the electrode was prevented by a key fitted into a groove. After the specimen was mounted and the vacuum secured, the lever arm was adjusted so that the bellows was at its relaxed position. This insured that the total weight of the specimen, the upper electrode, and the downpull of the vacuum were balanced by the horizontal beam. Since the specimen was heated by its own resistance, expansion of the specimen proceeded freely by this arrangement. During the time of heating the specimen, the beam was maintained in a horizontal position by turning the nut at the top. By graduating the lever arm and using a known dead weight on the lever arm to supply a tensile stress, the graduated nut could be read to 0.0001 in. extension. Since

Jan 1, 1955

United Engineering Trustees, Inc C E Reistle, Jr (to Oct &apos;55), A B Kinzel, &apos;56, Andrew Fletcher, &apos;57, Philip Kraft (from Oct &apos;55 to &apos;59) The Engineering Foundation W M Peirce, &apos;56, A M Gaudin, &apos;58 Engineering Societies Library Board Frank T Sisco, &apos;58, C H Behre, Jr Engineering Societies Personnel Service Board of Directors E J Kennedy, Jr, E H Robie Advisory Committee, Milwaukee F T Agthe Special Survey Committee C M Cooley American Standards Association Mining Standards Board E R Borcherdt, &apos;55, Otto Herres, &apos;55, J K Richardson, &apos;56, E W Bullard, &apos;56, Alternate

Jan 1, 1955

By P. Pietrokowsky

lntermediate phases in the binary metal alloy systems Ti-Zn, Ti-Hg, Zr-Zn, Zr-Cd, and Zr-Hg have been investigated by X-ray powder diffraction methods. Gamma-TiBHg and Zr3Hg have a beta tungsten structure; TiHg and ZrHg are analogous to ordered AuCu (L l0 type); delta-TixHg and ZrHg, are isomorphous with ordered AuCu,, (L l2 type); ZrZnz is face-centered cubic (C 15 type); TiZna crystallizes in a C 14 type structure; and Zrll-, occurs in cubic and tetragonal modifications in which a random distribution of atoms exists. Additional information for the intermediate phase TiZn, is presented. THE physical metallurgy of titanium and zir-conium when alloyed with elements in subgroup 11-B of the periodic table has received comparatively little attention in the literature. Laves and Wallbaum&apos; reported the existence of several intermediate phases in the system Ti-Zn. They identified TiZn as a CsCl (B 2) structure and described TiZn, as an ordered Cu,Au (L 1, type) crystal structure. Gebhardt&apos; investigated very limited zinc-rich regions in the systems Ti-Zn and Zr-Zn. Phase relationships in these partial constitution diagrams were deduced from the results of thermal analysis and metallography, X-ray results being inconclusive. The first zinc-rich intermediate phase in either system was not identified. More recently, Anderson, Boyle, and Ramsey" have had occasion to refer to a partial Ti-Zn phase diagram (unpublished data) covering the region 0 to 10 atomic pct Ti, wherein two intermediate phases corresponding approximately to TiZn,, and TiZn,, were indicated. The metals used in this investigation and typical analyses as determined by the suppliers are given in Table I. The iodide-process zirconium which was used was not hafnium free. Experimental Methods Alloy Preparation: The relative ease with which titanium and zirconium combine with other elements places extensive restrictions on the methods by which alloying can be achieved. The direct current electric arc melting procedure was found to be unsatisfactory for preparing these binary alloys and for this reason solid state diffusion methods were utilized. The iodide process titanium and zirconium rods were filed by hand. Fines were subjected to a magnetic separation and classified as to size as either finer than 200 mesh or coarser than 200 but finer than 80 mesh. Powder mixtures of various binary combinations of titanium and zirconium with zinc and cadmium were compacted in a 12 mm diameter die and then placed in Vycor or quartz vials which were evacuated and sealed. The mercury alloys were prepared in a similar manner; the proper weight of liquid mercury being placed in a vial with minus 200 mesh titanium or zirconium. These ampoules were then heat treated at various temperatures and times depending on the characteristics of the particular alloy system. Upon completion of the heat treatment the ampoules were cooled rapidly and the specimens weighed. The loss in weight varied from 1 to 3 pct (except as noted in the text) and for this reason the calculated compositions were accepted as a fair measure of the actual alloy compositions. X-Ray Dif raction Techniques: Powder diffraction experiments were conducted at room temperature with a 143.2 mm Debye-Scherrer X-ray camera in which the film was placed in the Straumanis arrangement. When copper radiation was used, a nickel filter was employed, and for the cobalt target a filter of iron oxide was used. In both cases, the /i? filter was placed between the X-ray target and the powder specimen which was mounted on a glass fiber. The lack of information based on optical metallography placed reliance on the results obtained from the X-ray experiments for determination of

Jan 1, 1955

By J. E. Shelton

This presentation covers the results of laboratory studies conducted by the Bureau of Mines Mineral Dressing Section, Northwest Electrodevelopment Laboratory, Albany, Oreg., on alluvial sands from Dismal Swamp, Bear Valley, and Cascade, Idaho. The search for radioactive minerals has led to the reexamination of alluvial deposits; in the process of this reappraisal the frequent presence of minerals bearing columbium and/or tantalum was toted. Because of increased demand for these metals by the defense industries and because these industries depend upon foreign sources for their supply the domestic alluvial black sands are being considered, as a possible domestic source. However, utilization of these alluvial deposits depends upon development of methods of concentrating these valuable minerals. The primary objective of the test work was the study of the effect of attrition scrubbing, sizing, magnetic, electrostatic, and gravity separa¬tion as methods for concentrating and recovering the columbium and tantalum-bearing minerals, samarskite, euxenite, ilmenorutile, and columbite.

Jan 1, 1955

By P. R. Perry

This publication is a compilation of tested methods for the analyses of titanium tetrachloride, titanium sponge, and various intermediate materials and products. They are presented in concise form without the detail usually found in publication of new methods because many of them are modifications of well known procedures. The Electrometallurgical Experiment Station, Boulder City, Nev., has been developing titanium production methods since 1945. Most of this development was on a modified Kroll Process but also included work on sodium reduction and electrolytic methods. During these years a large variety of samples were analyzed. Most of the analytical problems were solved using published methods or modifications of the same. At the start, there were no published procedures for analyzing titanium sponge using spectrochemical methods. A great deal of study was given to testing several of the well known techniques, and some of them, such as direct sparking of the metal, proved to be completely unsatisfactory. Solution-spark techniques were finally tried, and satisfactory procedures were developed for some of the more common impurities. These spectrochemical methods were then put into routine use for several months before their publication.2/ Some new modifications have been made, and techniques have been developed to determine other impurities found in titanium sponge and tetrachloride. All spectrochemical methods used in 1954 are included in this publication.

Jan 1, 1955