By P. A. Fisher, J. B. Wilson, D. J. Whitehead, C. J. P. Ball, A. C. Jessup

The properties of a new magnesium alloy ZT1 containing 3.0 pct Th, 2.5 pct Zn, 0.7 pct Zr are described. The alloy possesses good creep and fatigue resistance up to 650°F, is free from microporosity, and is readily sand-cast. ZT1 is shown to be superior to zinc-free Mg-Th-Zr alloys. THE advent of the jet engine created a demand for a light sand-casting alloy capable of being cast into large complex shapes and capable of resisting creep at temperatures up to 500°F. This demand has been largely met by alloys of the magnesium-cerium mischmetal-zirconium types, containing about 3 pct Ce mischmetal and 0.7 pct Zr, typified by Elektron magnesium alloys MCZ and ZREI, the latter alloy also having a zinc addition of 2.5 pct. These alloys utilize the valuable properties at elevated temperatures conferred by the addition of rare earth metals to magnesium, a fact which has been known for many years and discussed by several investigators.1-1 Murphy and Payne8 showed that the addition of the powerful grain-refining element zirconium to Mg-Ce mischmetal alloys produced alloys with attractive room temperature properties combined with good creep properties and castability. With the increasing power of modern jet engines the temperatures to which some of the magnesium parts are subject are likely to exceed the safe working range of the cerium-mischmetal-containing alloys, and at the beginning of the research considerable interest had been shown by aeroplane engine designers in a magnesium sand-casting alloy suitable for service at higher temperatures, e.g., 600°F and above. At an early stage in the development of this type of alloy a check on the fatigue properties at elevated temperatures indicated that, since the fatigue limit even at 108 eversals was appreciably higher than any permissible creep stress, the main emphasis of the research could be concentrated on creep behavior. The primary aim in developing the new alloy has therefore been to attain maximum creep resistance; but due consideration has also been given to other important properties such as castability, tensile strength, and cost. It is by now well established that it is not possible to correlate creep strength with other short time mechanical properties such as are obtained in tensile

Jan 1, 1954

By F. R. Cattoir, R. W. Kimball, C. T. Anderson

ONE of the principal impurities in all steels is sulphur. Sulphur-bearing, manganese-free steels exhibit hot shortness. Manganese is added to steel to improve the hot-working properties. If no sulphur were present in steel, it is probable that hot shortness would be nonexistent. This paper is the first of a series to be issued by this Laboratory reporting the measurements of hot forgeability tests and the physical properties of Fe-C alloys to which additions of various alloying elements have been made. The present paper describes the results- obtained by the addition of varying amounts of sulphur to Fe-C alloys. To obtain control over residual elements in the various charges melted in the arc furnace, it was considered advantageous to use sponge iron from one source as the melting stock rather than scrap metal having an unknown history. Small amounts of unwanted alloying elements might be introduced into the charge when scrap was used, thereby influencing the results of the various heats. A sponge iron having a high silica-lime ratio was used. Ore from Sunrise, Wyo., had been reduced to sponge iron and briquetted at the Bureau of Mines sponge-iron plant at Laramie, Wyo. The briquettes were 5 in. in diam and 2 to 3 in. in thickness, and weighed about 10 lb each. The chemical analysis of the sponge iron is as follows: C, 0.67 pct; Mn, 0.10; SiO2, 4.75; CaO, 1.4; P, 0.044; S, 0.72; MgO, 0.4; A12O3, 1.1; total Fe, 87.5; Fe metallic, 79.2; and reduction, 90.5 pct. Where a reducing agent was required, crushed graphite electrodes usually were used. The charcoal available contained 0.20 pct S. An analysis of the available coke showed it to contain 0.70 pct S. Where high sulphur heats were required, elemental sulphur additions were made to the ladle. Limestone of good quality was obtained locally and had the following analysis: CaO, 53.7 pct; MgO, 0.8; ignition loss, 42.4; R2O3, 0.2; SiO2, 3.0; and P2O5, 0.014. Melting Procedure Sponge iron was melted to produce metal stock for the experimental alloys in a silica-lined, three-phase, direct-arc, size ST, Moore Rapid Lectromelt furnace with a 500 kva rating. Fig. 1 shows this furnace installation. About 25 tons of sponge iron was melted in 75 heats, averaging 927 lb of sponge iron to the heat. An addition of carbon was required to complete the reduction of a portion of the iron oxide remaining in the sponge to prevent high losses of iron oxide in the slag and a low carbon content in the resulting metal. As reducing agents in preparing the melting stock, charcoal, coke, and a carbon product resulting from the thermal decomposition of natural gas were used. The quantity varied from 20 to 60 Ib per furnace charge, with an average of 38 lb. An average analysis of the metal obtained gave 0.52 pct C, about 0.01 pct Mn, 0.070 pct P, and 0.092 pct S. The average yield of metal was 647 lb with 241 1b of slag, the sponge-iron recovery being 70 pct. The metal obtained in melting the sponge iron was cast into pigs weighing about 20 lb each to facilitate recharging into the furnace for further refining. The pouring of the pigs is shown in Fig. 2. The average power consumption for the production of the 24 tons of metal obtained was 1704 kw-hr per ton.

Jan 1, 1954

Jan 1, 1954

Jan 1, 1954

By L. B. Berger

This information circular is a revision of I.C. 7238, Danger from Carbon Monoxide in the Home, by L. B. Berger and H. H. Schrenk, issued in April 1943. Each winter brings its toll of deaths and serious accidents from the deadly gas, carbon monoxide. Newspapers carry warnings to the public of the, dangers of this gas, and frequent news items report the finding of persons dead at unconscious from the effects of carbon monoxide, yet these accidents continue. Either these warnings are not read, or they are unheeded by people who feel that, "It can't happen to me." It can happen to you carbon monoxide is no respecter of persons.

Jan 1, 1954

By J. P. Nielsen, H. Margolin, E. Ence

The Ti-Ni phase diagram has been investigated up to 68 pct Ni with iodide titanium base alloys by metallographic, X-ray, and melting point methods, and from 68 to 90 pct Ni by examination of as-cast structures of sponge titanium base alloys. NVESTIGATION of the nickel-rich portion of the I Ti-Ni phase diagram was first reported by Vogel and Wallbaum in 1938.' This work was subsequently extended to lower nickel contents by Wallbaum' who indicated the possibility of a eutectic reaction for nickel contents below 38 pct. Long et al.3 studied the titanium-rich portion of the phase diagram and found eutectic and eutectoid reactions below 38 pct Ni. However, the temperature of the eutectic indicated by Long et al. was considerably lower than that suggested by Wallbaum. Long and his coworkers synthesized their alloys by powder metallurgical techniques and encountered oxygen and/or nitrogen contamination. Thus the diagram which was obtained did not represent binary alloying conditions. However from these results the features of the binary diagram were predicted. At Battelle Memorial Institute4 the Ti-Ni diagram was investigated up to approximately 11.5 pct Ni with sponge titanium alloys. The range of temperatures used was not sufficient to define the eutectoid temperature or composition. The data of Wallbaum2 and Long et al.8 were of particular interest for the present study, and although the work was originally concerned with the region below 40 pct Ni, the investigation was extended to higher nickel contents in an attempt to resolve the differences between these workers. Experimental Procedure Preliminary work on the Ti-Ni system was carried out with duPont Process A sponge titanium alloys to reduce the amount of subsequent work to be done with iodide titanium base alloys. The sponge titanium used contained 99.71 to 99.77 pct Ti, 0.1 pct Fe and 0.005 to 0.009 pct Ni. The iodide titanium obtained from the New Jersey Zinc Co. contained 99.9 to 99.95 pct Ti. Nickel used with sponge titanium was 98.9 pct pure. The high-purity nickel alloyed with iodide titanium was cobalt-free with approximately 0.05 pct C and was obtained through the courtesy of the International Nickel Co. The 15 g sponge titanium charges for melting were prepared by compacting in a die or by placing the weighed portions of nickel and titanium directly into the furnace. Iodide titanium charges were made by drilling holes in the as-received rod and inserting the nickel or by wrapping the nickel in sheet. Sponge titanium alloys containing from 0.2 to 90 pct Ni and iodide titanium alloys containing 0.2 to 68 pct Ni were prepared by these methods. In addition to these alloys several 1/2 1b sponge titanium alloys were supplied by the Allegheny Ludlum Co. The charges were melted in an arc furnace under an argon atmosphere. The procedures used were similar to those reported in the literature5,' and the furnace has been described.' Except for iodide titanium alloys with 40 to 68 pct Ni (see section on copper contamination), each alloy was melted for 1 min, then either turned over or broken before re-melting for an additional minute. Currents of 200 to 400 amp were used depending on the melting point of the alloy. Prior to heat treatment, alloys containing less than 14.5 pct Ni were hot-forged at 750°C. With the exception of alloys in the homogeneity range of the compound TiNi, alloys of higher nickel contents could not be hot-forged. Heat treatment of iodide titanium base alloys was carried out in argon-filled quartz capsules which were broken under water at the conclusion of heat treatment to quench the specimens. Temperatures were controlled to ±5oC and annealing times up to 48 hr were used. For melting point determination, specimens were placed in carbon crucibles which were in turn en-capsuled in argon-filled quartz capsules. The start of melting was determined by rounding of corners and by metallographic examination. Complete melting was considered to have occurred at that temperature at which the specimen assumed the shape of the crucible. Specimens were prepared for metallographic examination by mechanical polishing or by an electrolytic procedure." For alloys containing up to 80 pct Ni Remington A etch7 50 pct glycerine, 25 pct HNO,, 25 8 HF) was used. For higher nickel alloys aqua regia and Carapella's etch (5 g FeCl,, 2 ml HNO,, and 99 ml methyl alcohol) were employed. Specimens to be exposed for powder patterns were prepared by filing, by breaking specimens in a

Jan 1, 1954

By G. R. Speich, D. J. Mack

The transformation of was studied by isothermal methods. At all temperatures, the ß transforms quickly to fine grained ß" which develops silver-rich striations. At higher temperatures the striations disappear, the final structure being Widmanstatten a in ß'. At lower temperatures, the striated ß" is consumed by pearlite nodules of a + ß' which in turn form the Widmanstatten a in ß'. The transformation is unlike any previously reported for a eutectoid. AS part of a general program of study on the eutectoid reaction, the Ag-Cd eutectoid seemed particularly attractive because the ß phase which undergoes the reaction is another of the typical "electron compounds," AgCd, having the disordered body-centered cubic structure. This work deals with the eutectoid which occurs at 50.5 wt pct Ag, and not with the eutectoid which has been reported at 42.9 pct Ag.' There has been no work reported specifically on the Ag-Cd eutectoid which was studied. The only information available on this eutectoid is that work done in the determination of the phase diagram. For the most part, the terminal portions of the diagram, Fig. 1, are well established; however, the region from 40 to 60 pct Cd is still somewhat in doubt. The X-ray evidence'..' in this region is in conflict with the results of thermal analysis. X-ray analysis3 does not show a polymorphic transformation at about 240°C as indicated by thermal analysis.1,5 Even the X-ray evidence, within itself, is confusing in this region of the diagram. One investigator2 reports the ß phase as hexagonal close-packed and has found three phases in the one-phase ß field. Other X-ray investigators"' ' report the ß phase as body-centered cubic. The authors believe that much of the confusion resulted from incomplete homogenization of the alloys. It was found that it takes almost a week to produce a completely homogeneous two-phase structure at 370°C. Another possible source of error is the volatilization of cadmium from the surface and cracks of the specimen during annealing with the possible formation of a cadmium-poor phase. The only metallographic data available on this eutectoid alloy are those of Durrant1 and Fraenkel and Wolff.5 his information is very limited. The phase diagram chosen as most nearly correct is that in the Metals Handbook," which is almost identical with the phase diagram suggested by Durrant.1 Materials and Procedure The alloy was prepared from high purity silver (999.5 plus fine) and high purity cadmium (0.02 Pb, 0.005 Cu, trace Fe). The metals were melted in carbon under a nitrogen atmosphere. Some cadmium was lost by volatilization but by remelting several times and adding cadmium a 200 g ingot of approximately eutectoid composition was obtained. Because the CdO fumes are quite toxic, the exit gas from the furnace was led through a water trap to condense the CdO. The ingot was homogenized at 650°C for 24 hr, no attempt was made to prevent decadmiumization. This resulted in a narrow decadmiumized rim on the ingot which was removed. Filings for analysis were obtained from cross sections of the ingot. Silver was determined by the Volhard thiocyanate method,? cadmium by difference. The ingot analyzed 50.8 pct Ag at the top of the ingot and 50.7 pct at the middle and at the bottom of the ingot. This alloy was only slightly hypo-eutectoid compared to the accepted value of 50.5 pct Ag and was used for the isothermal studies. It was felt that further attempts to adjust the composition might be futile because of the volatility of the cadmium. The ingot was sectioned to specimens approximately 3/4 x 3/4 x 1/8 in. These specimens were "austeni-tized" for 3 hr in air at 650°C to yield homogeneous ß and then quenched into a salt bath held at constant subeutectoid temperatures where the transformation

Jan 1, 1954

By C. A. Winkler, V. Hospadaruk

PREVIOUS papers from this laboratory have discussed the effect of chloride ion on the cathode polarization during electrodeposition of copper from copper sulphate-sulphuric acid electrolytes, in the presence and absence of gelatin. The steady state polarization'" was found to decrease sharply and pass through a minimum with increasing chloride ion concentration in the presence of gelatin. The minimum shifted to higher chloride ion concentrations and to higher polarization values with increase in current density or gelatin concentration, while an increase of temperature shifted the minimum toward lower halide concentrations and lower polarizations. Since these observations were made in acid-copper sulphate electrolytes that contained no other addend than gelatin, there was obviously the possibility that they were not applicable to deposition of copper from commercial electrolytes that contain a variety of other substances in relatively small amounts. In particular, it was of interest to determine whether the presence of arsenic, antimony, or bismuth in the electrolyte would materially alter the behavior. Experiments have now been made under a variety of conditions with systems containing these cations, and the results are summarized in the present paper. Experimental Polarization measurements were made at 24.5oC in a Haring cell in the manner described previously.' Electrolytes were made with doubly-distilled water, and contained 125 g per liter of copper sulphate and 100 g per liter sulphuric acid, both of reagent grade Eimer and Amend gelatin from a single stock was used throughout. Chloride ion was introduced as reagent grade sodium chloride, and arsenic, antimony, and bismuth by dissolving the chemically pure metal in hot concentrated sulphuric acid and adding appropriate amounts of the solutions to the electrolyte. Each cathode, of 1/16-in. thick rolled copper, was first etched in 40 pct nitric acid and washed thoroughly with distilled water. The surface was then brought to a standard condition4~9 by electrodeposition from an acid-copper sulphate electrolyte containing no gelatin, at a current density of 3 amp per sq dm for 30 min, followed by deposition at a current density of 2 amp per sq dm for l hr. As in previous studies, the cathode polarization eventually attained a steady-state value (15 to 75 min) such that further change in polarization did not exceed 0.2 mv per min. The polarization values recorded are those for the steady states. "Excess weights" were determined with arsenic and antimony present in the electrolyte, as the difference between the weights of the deposits obtained in the presence of these cations and those obtained in their absence, with the two cells connected in series. When gelatin was present along with the arsenic or antimony, it was also added to the electrolyte in the cell in series. Results and Discussion The results of the study are summarized in Figs. 1 to 6. From Fig. 1, top, it is evident that the presence of arsenic or antimony alone results in an increase of polarization, while bismuth alone causes a decrease. The presence of gelatin (25 mg per liter) rather drastically modifies all three cation effects, as indicated in the lower panels of the same figure. The addition of chloride ion, when no gelatin is present, causes comparable decreases in polarization in the presence of antimony and bismuth, but a relatively larger decrease when the electrolyte contains arsenic. It is interesting to note that the decrease in polarization brought about by addition of chloride when both arsenic and antimony are present parallels the behavior with arsenic alone, while the polarization in the electrolyte containing the cation mixture, without chloride added, corresponds to that for an electrolyte containing only the antimony cation. Similarly, the polarization at zero concentration of chloride in electrolyte containing arsenic and bismuth is that corresponding to an electrolyte containing arsenic alone. From Figs. 3a, 4a and 4b, it is clear that, in the presence of gelatin at a level of 25 mg per liter, the effect of chloride in the presence of arsenic and antimony, or a mixture of the two, becomes quite analogous to that observed in the absence of added cations. When both bismuth and gelatin are present (Fig. 5), the decrease in polarization with increased chloride concentration is virtually absent. This is perhaps a reflection of the large decrease in polarization brought about by the bismuth itself in the presence of gelatin. The shifts of the minimum in the polarization-chloride concentration curves brought about by changes of temperature (Fig. 3b), gelatin concentration (Figs. 3c and 4c) and current density (Fig. 3d) when the metal cations were present are all similar to the corresponding shifts observed in their absence." The approximately linear "excess weightv-anti-mony concentration relation recorded in Fig. 6 would seem to indicate that antimony is codeposited with copper to a considerable extent. On the other hand, only very limited amounts of arsenic appear to be adsorbed or codeposited.

Jan 1, 1954

By G. M. Potter

During investigation of the occurrence of manganese deposits in the western United States, the Bureau of Mines collected 2-ton samples of 4 ores from 3 properties in northeastern Nevada. Laboratory tests were made to determine the amenability of these ores to ore-dressing methods of concentration. The Caviglia-Vietti property is situated 11 miles southeast of Ely, White Pine County, Nev. The ore deposits are lenticular veins and irregular masses found in limestone fracture zones and along the contact of limestone and underlying shale. Two samples, of the ore were tested: Lot A, from the Vietti shaft, and lot B, from the. Caviglia shaft.

Jan 1, 1954

By J. E. Hawley

"The property of Francoeur Gold Mines, Limited, lies directly west of the Armfield mine in Beauchastel township, Abitibi district, and 12 miles west and slightly south of Noranda. The gold deposits are of particular interest because of their replacement character and close association with fault zones. The property was originally staked in 1923 following the discovery oi a mineralized zone near the eastern boundary. This became No. 1 orebody. Later discoveries in 1936 of No. 2 and No. 3 orebodies led to underground development and actual mining in July, 1938. A fourth orebody, No. 8, was found in 1939.The following is the production record up to December 31st, 1947:Beginning in September, 1944, ore was shipped to Noranda as siliceous flux, but late in 1946 milling of low-silica ore from No. 1 orebody was undertaken until operations were temporarily suspended in 1947.The four main ore deposits, Nos. 1, 2, 3, and 8, consist of siliceous ferrocarbonate and albite replacement bodies mineralized with fine pyrite and specularite in schistose fault zones in Keewatin volcanics. Barren to low grade quartz veins though present in some are uncommon, but small stringers of quartz are usually present wherever here and there visible gold is found. Nos. 1, 2, and 3 deposits lie in a major fault zone that extends completely across the property from west to east (over 7,000 feet) and dips N.40° to 50°, and are separated by intervals of 1,800 to 2,000 feet respectively. The fourth lies in a smaller fault zone striking east and dipping on the average 65°S.No. 1 orebody has been explored by mining to a depth of 500 feet, No. 2 to 400 feet, and No. 3 to slightly less than 300 feet . The greater part of No. 8 lies above a depth of 200 feet, but a raise has recently .been driven through from the west end of the 5th level of No. 1 to the 2nd level on No. 8 zone. Most of the ore of No. 8 zone above the 2nd level and of Nos. 2 and 3 above the 3rd levels has been removed."

Jan 1, 1954

By J. H. Frye, D. L. McElroy, E. E. Stansbury

The rates of growth of pearlite in high-purity Fe-C alloys have been measured as a function of the transformation temperature. These and other data have been correlated in terms of a derived rate equation. Activation energies for the growth were found to be 24,200 cal per mol of austenite for the 0.78 pct C alloy and 27,600 cal per mol for the 0.93 pct C alloy. Theoretical implications are discussed. AN excellent review of the the theoretical and experimental studies on the mechanism and kinetics of the eutectoid reaction has been presented recently by Mehl and Dube.' They have pointed out that these investigations have followed two lines of approach: 1—experimental studies and derivations of expressions for the overall transformation characteristics, and 2—derivation of expressions for the nucleation and growth rates in terms of fundamental processes. Investigations of the latter type have been concerned for the most part with the nature of the growth at the austenite-pearlite interface in plain carbon and alloy eutectoid steels. They discuss two theories of the rate of growth of pearlite from aus-tenite—those of Brandt and of Zener. Both derive rate equations which are based on the assumption that carbon diffusion is the controlling mechanism. Mehl and Dube,' Zener,2 and Brandts. " have attempted to calculate growth rates by use of these equations together with thermodynamic and diffusion data. The results are encouraging, but agreement is not so good as to constitute verification of the theories. Furthermore, it Is not clear how these equations are to be used to study the effect of alloying elements which apparently exert little influence on carbon diffusion, but markedly decrease growth rates. It is not clear whether or not the addition to iron of an alloying element which does not diffuse during transformation can alter the rate of growth of body-centered from face-centered cubic iron. That it can greatly decrease the overall transformation rate has

Jan 1, 1954

By P. D. S. St. Pierre

IN recent years the use of high sulphur fuels and charges in steelmaking has necessitated rapid methods of slag control in order to insure the production of high quality steel. Several systems of control have been discussed in the literature, and of these the method described by Philbrook, Jolly, and Henry' has received the most attention recently. In their process the hydrogen ion concentration of an aqueous slag suspension is determined under controlled, but arbitrary conditions. The basicity of the slag may then be derived from a previously established pH-V ratio curve. Thus, by measuring the pH, some indication of the V ratio is gained, from which significant properties of the slag may be deduced. Philbrook et al. made no claims as to the theoretical justification of their treatment, but simply offered it as a rapid means of slag control. Encouraging results caused others to study the method and publish their findings.2-5 Although there was fair agreement on the efficacy of the method, no common parameter was evolved against which pH readings could be plotted. The results of the various determinations were related to such V ratios as CaO/SiO2 and CaO/ SiO2 + P2O5 by some,'-3 while others" plotted against "excess lime." Rivet,' however, found a simple proportionality between the hydrogen ion concentration and the sulphur content of the molten steel beneath the slag. Since slag control in North American practice is largely directed toward the efficient removal of sulphur from steel, Rivet's approach to the problem had the advantage of connecting directly a property of the slag with the impurity being removed. In view of the diversity of parameters used it seemed probable that some fundamental point was being overlooked in seeking a relationship. Examination of the literature revealed that much emphasis had been laid on experimental detail but scant attention paid to the fundamental aspects of the hydrolysis of the aqueous slag suspension. Consequently the present investigation was undertaken with the object of rectifying this deficiency and deriving, if possible, a parameter of general application. Petrographic studies on several matured Canadian open-hearth steel slags have shown that their major constituents are dicalcium and tricalcium silicates set in a complex matrix of iron oxides and ferrites. These phases are shown in Figs. 1 and 2. Free lime is frequently encountered in slags, but is not an equilibrium phase since on continued heating it dissolves forming silicates or ferrites. Thus, it appeared that a study of the hydrolysis of the major phases in steel slags would be profitable. The experimental technique used in the present work was a modification of that described by the other workers.'- Electrical conductivity measurements were also made on the suspensions, since Smith et al." had claimed advantages for this method in their paper on slag control. Experimental Procedure The compounds studied in this investigation were prepared in the laboratory by heating purified oxides

Jan 1, 1954

By W. T. Read, W. Shockley

THE subject of this chapter is the application of the dislocation theory to two problems of physical metallurgy where the theory has been able to give definite predictions that subsequently have been verified by experimental observations. Much of the history of dislocation theory has consisted of the explanation of already established results on the basis of ad hoc assumptions. Scattered bits of fundamental theory were formulated as needed-in particular explanations. The result had the appearance of a hodgepodge of ingenious ideas and exciting but possibly artificial speculations. The review article by Koehler and Seitz in this volume gives an excellent picture of the breadth, diversity, and flexibility that have made dislocation theory attractive to speculative theorists, although occasionally bewildering to others. Since 1950, there have been two developments, which have helped to establish dislocation theory, on the one hand, as a systematic coherent body of theory and, on the other, as a means of making predictions that can be tested experimentally and thereby guide experiment into more fruitful channels. The first and easier of these developments has been the systematic derivation of the classes and properties of dislocations from fundamental crystallographic concepts. An example of one phase of this development is the rigorous treatment of

Jan 1, 1954

By Walter J. Johnson

The coals in northern Wyoming and Montana are free-burning and non-caking and range from lignite to bituminous C in rank. Strip and underground mining are employed to supply railroad, utility, industrial, and domestic fuel. The market area includes Iowa, Nebraska, Minnesota, North and South Dakotas, Wyoming, Montana, the Pacific Northwest, and western Canada. THE larger producing coal mines in northern Wyoming are located in the Powder River Basin lying between the Black Hills region of South Dakota, eastern Wyoming, and the Big Horn Mountains in north central Wyoming, see Fig. 1. The mines are located particularly in the area along the route of the Chicago, Burlington & Quincy Railroad from Gillette, Wyo., to a point approximately 15 miles northeast of Sheridan, Wyo. Fig. 2 is a graph of coal production in the state of Wyoming from 1918 to 1951. Across the Big Horn Mountains lies the Big Horn Basin, situated between the Big Horn Mountains and the Rocky Mountains proper. Mining in the Big Horn Basin is almost entirely confined to a small area known as the Gebo Field, near the town of Kirby, which is located on the Chicago, Burlington & Quincy Railroad. This paper will describe present operating areas, making only brief reference to the history of mining and marketing primarily because of the large area to be discussed. The coal beds presently mined in the Powder River Basin are all of Tertiary age and are of Fort Union and Wasatch formations of Paleocene and Eocene ages, see Fig. 3. The Fort Union formation, consisting of 2000 to 3200 ft of alternate sandstone, shale, and coal, is divided from oldest to youngest into the Tullock, Lebo Shale, and Tongue River members. Most of the mineable coal is in the Tongue River member, which is 500 to 800 ft thick. The Carney coal bed, varying from 7 to 20 ft in thickness, is considered the base of the Tongue River member. About 85 ft above the Carney is the Monarch bed, ranging from 18 to 42 ft in thickness. At approximately 210 ft above the Monarch is what is locally known in the Sheridan district as Dietz No. 3 bed, which varies from 12 to 30 ft in thickness. One hundred feet above the Dietz No. 3 is Dietz No. 2 bed, which is 7 to 12 ft thick. At about 100 ft above the Dietz No. 2 is Dietz No. 1 bed, 7 to 15 feet in thickness. Two hundred and fifteen feet above Dietz No. 1 is the Smith bed, approximately 5 ft thick. One hundred twenty-five feet above the Smith is the Roland bed, which is estimated to be approximately 13 ft thick. The Roland bed is considered the base of the Wasatch formation, which in the Powder River Basin is 1000 to 3500 ft thick and is composed largely of shale, sandstone, and coal. The foregoing measures are the only ones above the Tongue River member that have been mined in the Sheridan field. To the east of the Sheridan field, particularly in the area of Gillette, the Roland bed is considerably thicker and is considered the thickest and most extensive coal bed in Wyoming, reaching a maximum thickness of 106 ft. From 125 to 225 ft above the Roland lies the Arvada bed, average thickness 9 ft. Three hundred seventy-five to four hundred feet above the Arvada is the Felix bed, which reaches its maximum thickness of 30 ft near Echeta on the Chicago, Burlington & Quincy Railroad. East of the Powder River the bed averages more than 10 ft in thickness, but it thins in a northwesterly direction. The highest mineable coal in the Powder River field is the Healy bed, about 400 ft above the Felix bed and exposed only in the highest parts of the area where much of it has been burned along the outcrop. Where it has not been burned, the thickness at most of the outcrops is 10 to 15 ft.

Jan 1, 1954

LIMA (PERU) Established May, 1952 James S Young, Honorary Member of Section (Legion of Honor Member) Bernard T Colley, Honorary Member of Section (Legion of Honor Member) Edward H Robie, Honorary Member of Section (Secretary of AIME) Carl W Westphal, Chairman Ernesto A Baertl, 1st Vice-Chairman Pierre L Garrigue, 2nd Vice-Chairman Walter E King, Secretary-Treasurer Avenida Santa Cruz 331 San Isidro, Lima, Peru Daniel M Rodriguez, Assistant Secretary Alberto E Brazzini, Assistant Treasurer Robert P Koenig, Section Delegate Irving L Barker, Special Representative

Jan 1, 1954

"The Waite-Amulet, an important copper-zinc mine, lies astride the Duprat-Dufresnoy township boundary about 8 miles northwest of Noranda, Quebec. It is an amalgamation of two properties, that of the former WaiteAckerman- Montgomery Mines to the north and that of Amulet Mines, Limited, to the south. This amalgamation took place in 1933. The description that follows is confined to the Amulet section.Ore was first discovered on the Amulet property in the autumn of 1924. The C Shaft and Upper A orebodies were found in 1925 and the F orebody in 1929, the latter by diamond drilling under a swamp. Under the present management, Lower A ore body was discovered by diamond drilling at a depth of 700 to 1,200 feet in 1938, and new ore was found from the old C Shaft workings between 1943 and 1945.From April 15th to October 20th, 1930, 60,291 tons of ore was produced from the Amulet. During the second half of this period, the ore averaged 4.2 per cent copper, 16.3 per cent zinc, and 0.02 oz. gold and 3.35 oz. silver per ton. Due to the prevailing low prices of metals, there was no further production until July, 1937. Output was greatly accelerated in 1940 when the newly found Lower A orebody assumed the main burden of production. Up to January 1st, 1946, mill reports indicate the treatment of the following ore: GENERAL GEOLOGYFig. 1 shows the geology of the entire property. To the east is the Lake Dufault granodiorite stock and to the west the Flavrian Lake granite mass. Around the granodiorite and separating the Waite from: the Amulet section is an older diorite intrusion. The ore occurs in a series of lavas that form a broad anticline pitching eastward at a relatively low angle into the Lake Dufault intrusives. There are several steep east-west faults. The late Powell diabase dyke is shown, also the general areas of strong dalmatianite alteration, a type closely associated with the sulphide mineralization."

Jan 1, 1954

By P. H. Floyd

This report presents the results of laboratory beneficiation tests on a sample of scheelite ore and a sample of low-grade scheelite flotation concentrate from the Sangdong mine, Korea. Sangdong was the foremost producer of tungsten concentrates on two occasions - during part of World War II and in 1953. It was also a significant producer of bismuth concentrates. Resources are very extensive and could support a 5,000-ton annual output of tungsten concentrates for many years. Located in the eastern part of South Korea near the 37° latitude, Sangdong has been a vital source of dollar income for the Republic of Korea in recent years. Its shutdown in March 1954 came about as a result of the great decline of tungsten prices and the fact that a sales contract with the United States Government had been terminated, In addition to establishing new markets, the problem of reopening Sangdong will be related to cost reductions and improving mill recoveries. Large quantities of offgrade scheelite concentrates were produced in the past and shipped to the United States for further beneficiation. Other low-grade concentrates and middlings have been stockpiled or discarded at the mine plant.

Jan 1, 1954

By W. D. Walker

All pipelines used to transport liquid fuels over coal mines are potentially hazardous; however, this publication deals only with dangers in transporting gasoline. Since transporting gasoline by this method is an established practice, the hazards connected therewith should he recognized by coal-mine operators and pipeline companies so that every known precaution may be used to reduce and keep the hazards to a minimum. The purpose of this paper is to direct the attention of coal-mine operators and employees, pipeline-company officials, and other interested persons to the explosion and fire hazards that arise from seepage of gasoline into underground mines. A hazard is not only presented in an individual mine when gasoline enters underground workings; but, in cases where mines are interconnected, a hazard exists in mach such mine.

Jan 1, 1954

By L. J. Boucher

The beneficiation process at Northampton is described and reasons are given for installing a flotation plant. The economics of running the plant, the difficulties of operation, and subsequent remedial action are discussed. CEMENT rock from a quarry operated by the Northampton plant1, 2 of the Universal Atlas Cement Co. has a relatively low average CaCO³ content. To meet specifications required for cement manufacture it was formerly necessary, over succeeding years, to add increasingly larger amounts of high-lime, low-alumina rock, which was obtained from a quarry operated by the company at a point along the New Jersey-New York state border, 79 miles from Northampton. Previous to 1940, 8 pct of total kiln feed consisted of high-lime rock. From 1940 to 1943, this figure jumped to 13 pct. Today it would be necessary to use 18 pct of this high-lime to meet current specifications. Increasing transportation costs made this an expensive operation. In addition, this high-lime rock quarry was contaminated with granite and high magnesia pockets. As there was no available high-lime rock in the Lehigh Valley, it was decided in 1936 to install a pilot plant where experimental work was done on processing local cement rock with flotation and burning the resulting product in a small kiln. This plant was in operation for six months and at the end of that period a suitable method of flotation had been established. From these studies it was also found that if the proportion of shipped-in rock rose slightly above 10 pct it became economically advisable to use the flotation process. It is the object of this paper to present briefly the operation of the flotation system at the Northampton plant. It seems advisable to comment on the raw material used in this process. The Northampton quarry lies geologically in what is known as the Jacksonburg formation of Trenton limestone.' In Pennsylvania this extends in a southwesterly direction from Portland, through Nazareth, Bath, and Northampton and across the Lehigh River to Ormrod. This argillaceous limestone was formed from marine deposits laid down during the early Ordivician period when a shallow sea covered most of Pennsylvania. Carbonaceous matter in the original deposit formed graphitic carbon under later metamorphic forces. From this graphite the cement rock of the Lehigh Valley derives its dark color. Most of the graphite must be removed before lime flotation can proceed. The quartz in this rock is desirable from the chemist's point of view, as it furnishes him with a form of silica necessary in the calcining process, but its abrasive properties damage pumps and piping. Aluminum silicates of potassium, sodium, iron, and magnesium are found in the form of sericite. Cal-cite averages from 69 to 76 pct. Iron in the form of iron pyrites is also present and has no deleterious effect. Talc is present in minute quantities. The

Jan 1, 1954

By Charles T. Holland

ANALYSIS of 117 occurrences of bumps in coal mines shows that 67.6 percent are associated with pillar-line points.4 Slabbing and splitting pillars, development, and other unfavorable milling practices in abutment areas may be a contributory or the primary cause of bumps. The cure for pillar-line bumps is to recognize areas that can be expected to become highly stressed and to project the mining plan and operations to eliminate such areas insofar as possible. If such areas cannot be eliminated, then the mining plan and operations should be projected to avoid the necessity of disturbing these areas before the stresses have been dissipated.