By W. A. Calhoun

This investigation of low-grade bauxites as potential sources of aluminum by caustic desilication and alumina extraction was undertaken by the Bureau of Mines to develop extractive methods for winning alumina from domestic deposits of low-grade bauxites. This report is the second of a series covering the work by the Bureau of Mines' Rolla, Mo., and Bauxite, Ark., laboratories. The first report published in the Journal of Metals, December 1951,3/ and dealt with kaolin and halloysite. The present investigation is concerned with low-grade bauxites only. The purpose of these investigations is to increase the domestic supply of aluminum ores. With eventual depletion of high-grade deposits, aluminous materials, such as low-grade bauxite, clays, shales, and high-iron laterites, will become our principal domestic sources of aluminum. The development of extractive processes for winning alumina from these low-grade materials is one of the many national security measures undertaken by the Bureau of Mines. A method has-been developed in the laboratory for successfully treating high-silica bauxites from domestic deposits. In this process the bauxite was calcined at 980° C. to form amorphous silica and alumina. The calcine was then leached by percolation with 15-percent sodium hydroxide solution at 940 to 96° C., removing 67 to 77 percent of the silica with a loss of 4.1 to 5.0 percent of the alumina. The sodium hydroxide in the spent liquor used in desilication was 95 percent recoverable, and comparable desilication results were obtained with 100-percent reclaimed liquor, The indicated cost of reagents, for sodium hydroxide and lime used in the desilication and regenera¬tion of spent liquor, was about $4.00 per ton of calcine treated.

Jan 1, 1954

By C. E. Cairnes

The Slocan mining camp in Kootenay district; British Columbia; has long been noted for the great number of its silver-bearing deposits; and for the success that has; in many instances; attended their development. The orebearing area lies east of Slocan lake and mainly within a radius of 6 to 8 miles of the mining town of Sandon. Within this limited area 135 or more properties have shipped ore in quantities of from 100 tons or less to more than 500; 000 tons; and with a total value in silver; lead; and zinc ranging from a few hundred dollars to well over $10; 000; 000. Of the three metals; silver has easily ranked first in value; with lead second and zinc third. Zinc production; however; made slow progress in the early years; and with . the exception of the Lucky Jim mine; and a few others where high-grade ore could be readily hand-sorted; was a detriment to the silver-lead ores until improved methods of separation enabled it to take an important place in the mineral production of the Slocan.

Jan 1, 1954

By J. W. Byrkit

Design features and operating methods at the new Ajo smelter are described in detail. Successful operation of a novel method of handling and charging wet concentrates to a deep bath type reverberatory furnace contribute to the daily production of 200 tons of anodes with good results from the standpoint of both metallurgy and economy. THE New Cornelia Branch of the Phelps Dodge Corp. is located at Ajo, Ariz. Large scale mining operations were started at Ajo in 1917, when a 5000 ton leaching plant was put in service to treat the copper carbonate ore that overlaid the sulphide ore-body. In 1924 a 5000 ton flotation plant was built to treat the sulphide ore and the leaching operation was abandoned a few years later. Changes in practice and additions to plant facilities have resulted in a gradual increase in the milling rate which now approaches 30,000 tons daily. Prior to the erection of the Ajo smelter, flotation concentrate was shipped by rail to Douglas, Ariz, where it was treated in the Phelps Dodge smelter. Construction of a one reverberatory furnace smelter to produce an average of about 200 tons per day of copper anodes at Ajo was started early in 1949. Initial heating of the reverberatory furnace was begun on June 21, 1950. Charging the furnace was started on july 8, and the first anodes were cast on July 14. Neither the anode furnace nor the reverberatory furnace has cooled since the initial firing. Fig. 1 is a photograph of the new smelter. Built primarily to eliminate the '300 mile haul of concentrate to the Douglas plant, the new smelter was designed to treat the Ajo concentrate, with a minimum of capital investment. A novel, and relatively simple, method of concentrate handling and furnace charging made unnecessary the installation and operation of expensive storage facilities and reclaiming equipment, and obviated the necessity of holding in storage large quantities of copper-bearing materials. (Patents are pending in the United States and abroad on the Ajo process.) In the selection and arrangement of equipment, consideration was given to the full utilization of all smelting facilities, reducing the amount of idle equipment to a minimum. The layout of the smelter is shown in Fig. 2. The important problem of internal transportation was minimized by arranging the reverberatory furnace, converters, and anode furnace in a compact group and providing storage bins inside the smelter building, within reach of overhead cranes, for fluxing materials and other supplies needed in the daily operation. This can be seen in the sectional view of the smelter given in Fig. 3. Incorporated in the design were many innovations in smelting equipment intended to facilitate operations and effect economies in maintenance expense and manpower requirements. Table I gives operating data of the entire plant. Metallurgy The metallurgical practice at Ajo is based essentially upon the use of a single, deep bath reverberatory furnace for smelting wet concentrate, without concentrate storage facilities. The large reservoir of slag and matte maintained in the furnace serves to equalize, to some extent, the day to day variations in the nature and grade of concentrate and permits

Jan 1, 1954

By W. W. Tyler, A. C. Wilson, L. B. Nesbitt

INVESTIGATIONS of thermal conductivity and impact strength of the titanium alloy RC-130-B and 316 stainless steel were undertaken because of interest in strong, nonmagnetic, commercially available alloys of low thermal conductivity for use in low temperature experiments. Measurements of electrical resistivity and thermoelectric power were also made for some of the samples studied. The titanium alloy designated as RC-130-B is manufactured by Rem Cru Titanium Inc. It contains 0.14 pct C, 3.99 pct Al, and 4.7 pct Mn. A general discussion of properties of the two phase Ti-4Mn- 4A1 alloys is given by Finlay and Vordahl.' The alloy is machinable and has a yield strength greater than 130,000 lb per sq in. at 0.2 pct offset. The 316 stainless steel sample used for both conductivity and impact strength measurements was obtained from the Allegheny-Ludlum Steel Corp. and is designated as Allegheny metal 18-8M, Type 316, Grade 316. The sample had received 25 pct minimum final cold reduction and had a Brine11 hardness rating of 255. Several impact tests were made on a sample of 316 stainless which had not received the 25 pct cold reduction. Also several data points are reported giving thermal conductivity and electrical resistivity for a sample of 304 stainless steel taken from stock. Figs. 1 and 2 give thermal conductivity and electrical resistivity data for the titanium alloy and for

Jan 1, 1954

By W. T. Irvine

"The Britannia ore deposits are approximately 20 miles north of Vancouver; and occur in a prominent ridge facing Howe sound. A large ironstained bluff first attracted the serious attention of early prospectors. This; upon investigation; proved to be the outcrop of a large copper orebody. The highest outcrops were 4; 300 feet above sea-level.The original discovery was made in 1888, but no real development took place until 1902. The first mining was done in what came to be known as the Jane orebody, and some production was obtained from this in 1905. Underground exploration led to the discovery of several other orebodies. The first main adit, the 1,050-foot level, was driven to tap the ore at an elevation of 3,300 feet above sea-level. During succeeding years, however, long adits were driven from points lower down on the mountain side. These, with connecting shafts, followed the ore to horizons well below sea-level. The lowest working has now reached to 880 feet below sea-level. The property has been in almost continuous operation since its original exploitation in 1905. Until the end of 1944, 732,414,420 pounds of copper and 261,125 ounces of gold had been produced from the mine."

Jan 1, 1954

By B. F. Decker, J. H. Keeler, W. R. Hibbard

Textures of hot-rolled, of cold-rolled, and of cold-rolled and annealed zirconium sheets were determined by use of an X-ray spectrogoniometer. All textures showed a tilt of the basal planes 240" from the rolling plane about the rolling direction. Deformation textures showed the [1010] direction to be approximately in the rolling direction. After recrystalliza-tion, the 111201 direction was approximately in the rolling direction. This texture was sharpened by annealing above the allotropic transformation. Textures of sheet produced by alternately cold rolling and then annealing were less strongly oriented than sheets that underwent severe deformation without intermediate anneals. THIS study of the deformation and annealing textures of high purity zirconium was carried out to supplement an investigation of zirconium and zirconium-base alloys. The spectrogoniometer method of pole figure determination was used and yielded more detailed and precise information than the photographic techniques used by previous investigators. Earlier investigations of the rolling textures of hexagonal metals titanium,1,2 beryllium," and zirconiumL having a c/a ratio slightly less than 1.6 disclosed a rotation of the basal planes from the rolling plane about the rolling direction so that the basal poles were inclined toward the transverse direction, and with one exception,& the [1010] direction was found parallel to the rolling direction. Similarly, hot rolling produced a spread of the basal poles in the transverse direction,2,3,5 With the [1010] direction parallel to the rolling direction. The textures of these metals after recrystallization differ somewhat from each other although still exhibiting the transverse rotation of the basal poles about the rolling direction. Zirconium" was found to have the [1120] direction in the rolling direction, beryllium" continued to have the [1010] direction in the rolling direction, and titanium' was shown to have the [1010] direction in the rolling direction (the cold-rolling texture) when annealed at 1000°F, changing to the [1120] direction in the rolling direction when annealed at 1500°F. It was suggested2 that the titanium retains the deformation texture after re-crystallization, and preferred grain growth at higher temperatures produces the second texture. Annealing above the allotropic transformation temperature did not appreciably change the high temperature recrystallization texture for titanium.' Coarsegrained zirconium showed more spread" in the transformation texture than in the recrystallization texture. The material used in this investigation was crystal-bar zirconium prepared by the iodide process. The major impurity was hafnium which was less than 0.3 pct. The composition obtained by spectro-graphic analysis is given in Table I. The hot-rolled specimen was prepared from a 50-g button of zirconium arc-melted in a water-cooled crucible under an argon atmosphere. This button was enclosed in a welded sheath of soft iron and the ensemble was rolled at 825°C. After each pass the sheath was put back into the furnace to allow it to return to the desired temperature. The zirconium ingot was reduced in this manner to a thickness of about 0.035 in., a reduction of approximately 90 pct. The sheet after removal from the sheath was alternately polished and etched to a thickness of 0.001 in. Cold-rolled specimens were prepared from crystal bar by a series of reductions of approximately 0.010 in. until the sheet reached a thickness of 0.010 in. after which it was cold-rolled to 0.001 in. thickness between sheets of alloy steel. The total cold reduction amounted to about 99.8 pct. Specimens were annealed in an evacuated Vycor or quartz tube. The transmission pole figures were obtained by the quantitative method of Decker, Asp, and Harker6 modified by Geisler7 using an X-ray spectrogoniometer with Cu Ka radiation. Unless otherwise specified all four quadrants were examined with 5" increments along the radius of the pole figure. Absorption corrections were made for changes in length of the X-ray path through the sample as inclination of the

Jan 1, 1954

By J. P. Nowlan

"This paper is an attempt to outline the structural problems at the Cochenour Willans mine, in so far as their details have been tentatively worked out. It must be emphasized that there are considerable data that can be interpreted in more than one way, and that further work may modify or completely change some of the hypotheses presented herein. Certain features, however, are sufficiently constant to warrant reliance on them when searching for extensions of orebodies.As the individual ore shoots usually have relatively small dimensions, but are often very high grade, structural details are of more than usual significance in laying out a mining programme. An illustration of this is a small shoot recently located and mined as a result of studying a minor slip cutting off a part of high grade gold ore in No. 319 stope. The shoot, which is bounded on three sides by slips, and on the fourth by the original stoping, was roughly triangular in plan, 20 feet on the base, and 40 feet in length. The average width mined was 4.5 feet, but the gold obtained totalled over 1,800 oz.The property lies in Dome township, east of McKenzie island, and consists of an original group of thirteen claims acquired from the Cochenour Willans syndicate, plus one additional group of five claims obtained by purchase from the Kelson Red Lake Gold Mines, Limited, and one other claim that rounds out the southeast corner of the block.The claims of the original group were staked by W. M. Cochenour, Dan Willans, and Horace Young, during 1926 and 1927. The Cochenour Willans Syndicate was formed in 1928, and until incorporation of the present Company work was carried on at varying intervals by several different interests, including Ventures Limited, Hollinger Consolidated, who sank a shaft to open up the 150-foot level, and by the Syndicate itself. The first ore from the property was shipped to the Gold Eagle mill by the present Company in 1939, and amounted to 4,959 tons, from which 2,360 oz. gold was recovered. The first brick was poured in December, 1939, and production has been continuous since that date. To the end of June, 1946, gold having a value of $5,982,000 has been produced from 345,033 tons of ore treated."

Jan 1, 1954

By W. A. Haley

This is the second of a series of publications that describes the progress of mechanical longwall coal mining in the United States in which a German coal planer was employed.3/ Details of the equipment, a description of its operation, and the results obtained in mining the experimental panel were published in the preceding report. Experimental mining with the planer in the first panel showed an improvement in performance over conventional mining methods at the coal company's Stotesbury 11 mine. The work, which was begun on an experimental basis, soon proved successful, and the coal company purchased the equipment for continued use. Two panels, adjacent to the first, were developed and mined with the planer. Each of these panels was shorter than the preceding one because water seepage from a surface creek limited development. On completion of mining in the third panel, the planer equipment was moved by the cooperating company to a nearby mine operated in the same coal bed where a large area of coal suitable for planer mining is available.

Jan 1, 1954

By Franc R. Joubin

"Gold has been found in many parts of the Bridge River district of British Columbia; but it is from a relatively small area in the valley of Cadwallader creek that most production has come. The ore-bearing area measures 1/2 mile in width by 3 miles in length; and for convenience it is called the Cadwallader gold belt in this paper. In this belt are found the Bralorne and Pioneer mines and in addition several prospects under development.The gold of the Cadwallader gold belt occurs in quartz veins averaging about 3 feet in width and containing about ½ oz. of gold a ton. Except for a relatively small amount of silver, no other metals are produced from these veins. The ore-bearing veins occur in a variety of rocks. They occupy reverse faults and tension fractures belonging to a distinctive fracture system. Some of these structures are ore-bearing over lengths exceeding 5,000 feet and depths exceeding 3,700 feet. The production of the Bralorne mine (1932-1945) is 996,383 oz. gold and 190,709 oz. silver; that of the Pioneer mine (1930-1945) is 777,588 oz. gold and 135,698 oz. silver. These two mines have together distributed about $25,000,000 in dividends.The Bridge River district first attracted attention in 1863* when prospectors were attracted by its small but rich placer gold deposits. Most of the important lode deposits of the Cadwallader gold belt were discovered in 1897 (11). Many years of desultory development followed and it was not until 1928 and 1932 that the Pioneer and Bralorne mines, respectivdy, entered into profitable production."

Jan 1, 1954

Small scale' table concentration tests have many critics. Many metallurgists consider that such tests are of problematical value because of the difficulties involved in conducting and interpreting them.Many kinds of small-scale ore dressing tests are difficult to conduct, and there is, perhaps, good reason for thinking that table concentration tests are amongst the most difficuIt.Interpretation of results from small-scale tests is the responsibility of the metallurgists and engineers in charge, and it is often held that small-scale table concentration tests are particularly difficmlt to interpret.TESTING FOR TABLE CONCENTRATIONOn analysis it appears that the difficulties encountered in conducting small-scale table concentration tests are of three fairly distinct kinds. Firstly, there are difficulties due inherently to the smallscale nature of the operations; for example the smaller width of all mineral bands on the table and the less complete separation due to the shorter length of travel between the feed and discharge points.Secondly, there are the effects of batch operation owing to the fact that the mineral particles behave differently during the initial period when the sample is just beginning to spread over the table, the middle period when feed and discharge are even and continuous, and the final stage, when the last of the sample has been added and the table is beginning to empty itself.

Jan 1, 1954

By J. P. Hammond, C. J. McHargue, S. E. Adair

Cold-rolled sheet textures have been determined for binary solid solutions of aluminum, columbium, tantalum, and zirconium in titanium. An alloy containing 3.8 pct Al had a (0002) [10101 texture, whereas alloys with the other elements had rotated (0002) [10101 textures similar to that of iodide titanium. THERE have been relatively few studies of the effect of alloying on deformation textures. A second element may be present in the base metal in solid solution and/or as a second phase. The literature offers no satisfactory explanation for the effects of solid solution alloying on textures noted thus far. For example, there is no satisfactory explanation of the difference in the textures of copper and a brass. The most complete study of the effects of solid solution alloying on deformation textures has been that of Brick, Martin, and Angier.¹ These investigators reported that the copper texture was retained by alloys of copper with up to 30 pct Ni, less than 5 pct Zn, less than 2 pct A1 or Co up to the limit of solubility. Copper containing more than 5 pct Zn, more than 2 pct Al, or the maximum soluble concentration of tin, silicon, or manganese showed the deformation texture of a brass. Bakarian² reported that additions of 0.20 pct Ca to 99.98 pct Mg or 2.0 pct Mn plus 0.15 pct Ca to magnesium resulted in entirely different textures than for the pure magnesium. The texture obtained for high-purity magnesium sheet showed the basal plane to be concentrated parallel to the rolling plane. The texture obtained for the alloy containing 0.20 pct Ca had the basal planes concentrated in elliptical areas whose centers were tilted 15" from the center of the pole figure toward the rolling direction. This split basal orientation was even more pronounced in the alloy containing 2.0 pct Mn and 0.15 pct Ca. Fuller and Edmunds" studied the rolled sheet textures in a zinc alloy containing 1 pct Cu and 0.01 pct Mn. The basal pole figure of this alloy contained a region of strong concentration not found in the pole figure for pure zinc.' In the above cases, results were discussed in terms of possible changes in slip and/or twinning systems and critical shear stresses. However, there were no experimental data to relate these speculations with the observed textures. It has been suggested that the deformation textures of titanium, zirconium, and beryllium could be directly ascribed to their low c/a ratios. The complex deformation mechanisms of titanium" also have been suggested to be characteristic of hexagonal close-packed metals with low c/a ratios. The purpose of this investigation was to study the cold-rolled sheet textures in binary titanium-base a alloys in which the c/a ratios were greater than, less than, and about the same as the c/a for iodide titanium. The annealed textures of these alloys will be reported in a subsequent article. Materials and Methods The chemical analyses of the metals used in this investigation are given in Table I. The alloys were prepared as 15 g buttons on a water-cooled copper block in a vacuum arc-furnace. The furnace was evacuated to pressures of the order of 10.' mm Hg, flushed with 99.98 pct pure argon, and melting was carried out in 0.2 atm pressure argon. Each button was remelted until radiographs and chemical analyses indicated complete solution of the solute elements. All buttons were forged and homogenized 72 hr at 500°C. The buttons to be rolled were ground and etched to sizes and shapes suitable for the rolling

Jan 1, 1954

By H. G. Iverson

As a part of the program of investigation of domestic sources of manganese ore, mining engineers of the Bureau of Mines examined and sampled three properties in the vicinity of Winnemucca, Nev. As the ores were too low grade for direct production of ferromanganese, they were tested for their amenability to concentration by ore-dressing methods. Two samples of ore were procured by examining engineers of the Bureau of Mines from several outcrops in the Pollard Canyon area, Pershing County, about 30 miles southeast of Winnemucca. The manganese occurs in relatively small lenticular bodies as secondary replacement deposits in chert and quartzite. The first sample represented average run -of -mine ore as exposed in the Pollard Canyon deposits. Sample 2 was composed of hand-sorted, high-grade ore.

Jan 1, 1954

By R. G. Dressler

The design and operation of the Koppers powdered-coal gasifier and its auxiliaries at Louisiana, Mo., are described. This unit was designed to convert 1 ton of coal per hour with oxygen and superheated steam into synthesis gas - primarily carbon monoxide and hydrogen. The first run was made on May 4, 1949. After this, 44 short runs (less than 8 hours each) and 1 long run (lasting 11 days) were made. Total gasification time was 420 hours. The gasifier was not cooled down during the year when these runs were made. After an initial period of test operations and equipment proving, during which 12 runs were made, the effect of numerous variables on gasifier performance was studied. The long run was made primarily to check the equipment in sustained operation. Detailed data from these runs are presented.

Jan 1, 1954

By R. V. Lundquist

Leaching manganese-bearing materials with NaOH to remove caustic-soluble silica has been demonstrated as a method for upgrading manganese. Those materials containing opaline varieties of silica respond most readily. Spent leach liquors are regenerated by treatment with lime to precipitate calcium silicate and to reactivate the NaOH for leaching. ALL of our larger domestic deposits of manganese are very low grade, but estimated tonnages in these deposits are large enough to constitute a potential strategic reserve of manganese for emergency periods, provided these ores can be upgraded sufficiently to meet industrial specifications. Many types of processes have been suggested for upgrading these ores, several have been studied in pilot plants, and a few have attained limited commercial production for special purposes. The hydrometallurgical process to be described below proposes a leaching operation for removing caustic-soluble silica and other gangue minerals and consequently upgrading a manganese ore or flotation concentrate to a commercially acceptable moduct. It is known that some forms of silica and some silicate minerals are soluble in NaOH solutions under suitable conditions. This new process proposes to use NaOH for removing the soluble materials from manganese ores or concentrates and, as a result, upgrade the manganese content. Since spent leach liquors are not efficient leaching agents the liquor must be treated with lime to precipitate calcium silicate and reactivate the NaOH. Experimental Procedure Manganese-ore samples ground to —35 mesh were leached in iron containers into which the ore sample and appropriate NaOH solutions were placed. Flotation concentrates were already ground to —200 mesh. The slurries were then placed on a hot plate or into a pressure digester and stirred continuously during the period of digestion. Where the- digestion was performed at atmospheric pressures, water lost by evaporation was replaced at regular intervals to maintain approximately a constant volume of slurry. In the pressure digester, volume changes were not controlled. After digestion, the slurry was allowed to cool enough for easy handling, but it was filtered hot, 50" to 70°C, on a Buechner filter. Filtration under these conditions was satisfactory. The resulting filter cake was washed and dried. In most instances, a single leach would not produce maximum extraction of silica from the ore sample; consequently, the dried tailing was treated again in the same manner with a fresh solution of NaOH to obtain an additional extraction of silica. This procedure was repeated a number of times to get the maximum extraction of silica. Usually three or at most four stages of leaching were adequate for this purpose. This leaching procedure was used for obtaining the data reported in this paper on the effects of NaOH concentration, pulp dilution, temperature, and time of digestion on the efficiency of extraction of silica from the ore sample. The experimental procedure does not match industrial methods. consequently tests for counter-current leaching were set up. Data from these tests are not yet complete, but in a qualitative way they indicate that thickeners between stages of leaching will be satisfactory and that the quantity of silica in a leach liquor moving forward to a new solid has only a minor effect on the quantity of silica extracted from the new solid. A pilot plant is now being designed for operation in the near future to test and evaluate the merits of this process.

Jan 1, 1954

By L. J. Erck, T. E. Ban

A discussion of laboratory procedures used to determine pellet quality and to simulate handling and firing conditions. Strength-temperature relationships in pelletizing; effect of chemical additives on agglomeration; and crushing, abrasion, and impact resistance of the pelletized products are discussed with respect to five different iron ore concentrates. IN most routine experimental work on products and processes, method:; of operation and product evaluation are established from accurately controlled laboratory tests. With particular emphasis on the pelletization of fine iron ore concentrates, standardized procedures of laboratory production and product testing have been established at Cleveland-Cliffs Iron Co. Research Laboratory at Ishpeming, Mich. A program of this nature was used for investigating the agglomeration characteristics of various iron ore concentrates. The factors which control the process were studied and subsequently controlled for these investigations. Pelletizing as applied to iron ore agglomeration involves the preparation of spheroidal masses from a fine moist concentrate, followed by high-tempera-ture firing to produce a final product. The preparation of moist spherorids is generally designated as balling. This produces the so-called green pellets or balls. After, these have been fired they are called pellets. Balling is accomplished by rolling moist concentrates in a revolving drum until small spheroids form by a snow-balling action. These balls are then heated in a shaft furnace, or a modification of this device, to a temperature high enough to cause agglomeration within the individual balls while they descend countercurrent to hot oxidizing gases. By this process the lour strength balls are converted through various chemical and physical-chemical processes into hard pellets. With correct balling and firing, the pellets are strong, resist abrasive action and handling treatments, and provide a suitable blast furnace and open hearth feed. In 1950 Tigerschiold and Ilmoni developed a working hypothesis to explain the formation and stability of green pellets.' Their work was presented on the basis of geologists' discoveries concerning the soil-water system and C. V. Firth's early postulates of green pellet formation.' Fundamental reactions oc-curing within fired pellets have been described by Cooke and Ban, who showed the microstructure changes caused by different firing temperatures." All these investigators have provided scientific clarifications of agglomeration by the pelletizing process and have opened avenues for greater development. Mineral grain growth and ceramic bond formation are the two basic phenomena imparting coherency to particles within a fired pellet of iron ore. Each of these is established by the transfer of thermal energy to the mineral particles. Grain growth mechanisms are chiefly physical reactions wherein smaller particles consolidate into larger ones, with resulting decrease in surface energy conforming with the second law of thermodynamics. Ceramic bond formation is a chemical reaction usually between basic and acid metallic oxides of the gangue and ore minerals. CaO, MgO, A1203, and FeO of Fe3O4, react in varying proportions with SiO, or Fe2O3, to form a great series of compounds or amorphous solid solutions. These product bond iron mineral particles together by a bridging action or by direct reaction with the surfaces of the particles. The result of the grain growth-ceramic bond formations is a consolidated, coherent compact of gangue and iron minerals formerly held together by much weaker bonds of interstitial water and forces common to dry, unconsolidated particles.4 With respect to iron ore agglomeration, these high temperature bonding reactions have been described by Schwartz, who referred to the bonds in sinters," and by Cooke and Ban, who referred to the bonds in fired pellets." The extent of the bonding phenomena and the consequent strength of fired pellets is governed by

Jan 1, 1954

By Katherine Mather

This paper is an attempt to put together petrographic, physical, and chemical data about the large and varied group of rocks generally called limestones. Results of the properties of these rocks on their performance as concrete aggregates are discussed. CRUSHED stone classified as limestone comprises about 70 pct of the crushed concrete aggregate and roadstone produced in this country, and the product has amounted in the recent past to about 97 million tons per year, valued at more than $123,-000,000.' Therefore an evaluation of the properties of rocks classified in these statistics as limestones and an ability to predict their behavior as aggregate in portland cement concrete are matters of considerable economic consequence to producers and consumers of aggregate. This paper is an attempt to put together petrographic, physical, and chemical data about the large and varied group of rocks generally called limestones. It also points out certain results of the properties of these rocks on their performance as concrete aggregates. The problems encountered in efforts to explain the behavior of limestones, dolomites, and related rocks as concrete aggregate lie on the frontiers between the ignorance of the geologists and the ignorance of the engineers. The mineral composition and textures of the rocks have not been adequately explored and described, and the effects of mineral composition and texture on the performance of aggregates have been worked out in only a few cases. There are instances of unsatisfactory performance and some generalizations of those experiences. There are many more examples of satisfactory performance than of unsatisfactory, but there is practically no published information as to why a particular aggregate was satisfactory in a specific use. There are all too few investigations of undeteriorated concrete; more is known about the pathology of concrete than about its normal structure and aspect. As part of the investigation of aggregates, the classification of rocks is not an end in itself, but is a step toward recognition of properties expected to influence the behavior of aggregates in their intended use. Rock of any type may perform well or poorly as concrete aggregate, depending on the physical condition of the rock, its physical and chemical properties as compared to those of the matrix in which it is placed, and the circumstances under which the concrete is exposed. Some classification and descrip- tion of the limestones is necessary to distinguish subgroups whose members will probably behave in similar ways and to evaluate the group as a whole. The group name, limestone, includes and tends to conceal the identity of rocks that have a very great range in chemical and mineralogical composition, structure and texture, conditions of deposition, subsequent history, and suitability for use as concrete aggregate. All the rocks classified as limestones include one or both of the most abundant rock-form-ing carbonate minerals, calcite and dolomite, as major constituents. Carbonate rocks is a more descriptive and more accurate group name than limestone, which has generally been used to include dol-omitic or magnesian limestones and dolomites as well as calcitic limestones. Classification and Description of the Carbonate Rocks The question of names to be applied to the carbonate rocks may appear academic, but it is of practical importance as long as there are specifications for aggregate that result in acceptance or rejection of rocks by name and as long as failure to make distinctions among the carbonate rocks leads to misunderstandings of their properties and of what may be expected of them in performance. Materials included in production statistics as limestone and tested for concrete aggregate as limestone range in fact from calcareous shale and calcareous or dolomitic sandstone and argillaceous limestone and dolomite to calcitic limestone and pure dolomite and to rocks close to calcitic and dolomitic marble. To take a simple example: consider two manufactured coarse aggregates, both dense and unweathered, one composed principally of crystalline calcite and the other of crystalline dolomite, but both known as limestone. If each is used as coarse aggregate in a standardized concrete mixture with the same fine aggregate used in both cases, made into concrete specimens, and tested in accelerated freezing-and-thaw-ing, the test results will probably be quite different, because of the differences in internal bond and thermal properties between the two aggregates. As long as both aggregates are called limestone, the test results cannot be explained, or used except in a very limited way; if the aggregates are distinguished as limestone and dolomite and the consequent differences in texture and thermal properties are recognized, the results are reasonable. Classification of the carbonate rocks used as aggregate should be based on structure and on composi-

Jan 1, 1954

By P. W. Gilles, B. D. Pollock

THE pioneering work of Steinitz1 and Steinitz, Binder, and Moskowitz2 has shown conclusively the existence at high temperature of two additional phases in the molybdenum-boron system and thus brings to a total of six the number of structures appearing in this system. To the structures Mo2B, MOB, and Mo2B5 they have added MO3B2, a new -MOB form, and have shown that MOB,, which has the same range of composition as Mo2B5, is only a high temperature structure of the latter. This solid solution, interestingly enough, includes neither of the compositions corresponding to the stoichiomet-ric compounds, MOB, or Mo2B5, but rather at all temperatures has intermediate values of composition. These workers have also, in the course of their work, measured melting points, transition temperatures, eutectic and peritectic points in the system and have shown that Mo3B2, because of its dispro-portionation at low temperature to Mo2B and MOB, is stable only in a limited high temperature range. During the course of the present work on the vaporization properties of the molybdenum-boron compounds, a few transition temperatures were observed. When the report of the other workers appeared, it was decided to repeat, in part, their study of the system. As a result, considerable evidence has been obtained that substantiates the specific kinds of melting processes they report as well as the general features of their diagram. However, a marked difference was found between the temperatures they report and the ones observed in this study, with the latter being higher. The purposes of this paper are to present the evidence obtained in this laboratory that verifies their diagram of the system, to give some important temperatures in the system, to compare them with those previously published, and to seek an explanation of the difference. Samples The metal starting material was 400 mesh molybdenum powder with a purity stated by the manufacturer to be 99.9 pct. The initial treatment, designed to remove volatile contamination, consisted of heating in a vacuum for 10 min to a temperature of from 800" to 1000°C during which a loss of 0.3 to 0.4 pct occurred. An assay following this treatment showed it to be 99.4 pct pure, with the principal impurity probably being oxygen. The boron starting material was obtained from the Cooper Metallurgical Laboratories and the Fair-mount Chemical Co. as 325 mesh powder with manufacturers' analyses of 99 pct or better. Initial treatment consisted of heating in molybdenum in a vacuum at about 1700°C for 10 min. During this time a loss of 3.5 pct occurred. An assay following this treatment showed the different samples to have purities ranging from 95.5 to 99.0 pct with iron and carbon as the principal impurities. Following the initial treatment, the elements were combined to form stocks of Mo2B and MOB by heating pressed mixtures in a vacuum to 1100" to 1200°C to accomplish reaction and to 1500" to 1900°C for a few minutes to evaporate the more volatile impurities. Analysis of the two compounds for boron by a modification of the method of Blumenthal3 and for molybdenum by the lead-molybdate method indicated them to have purities greater than 99 pct. The individual samples to be studied had compositions in the Mo2B-MOB range and consisted of mixtures of the stock compounds. Procedure As is usually the case in high temperature work the selection of containers for the samples posed some problems. For vapor pressure studies tantalum crucibles, allowing little contact with the pressed samples, were used and some of the observations made during these experiments are pertinent to the study of the phase diagram. Most of the experiments, however, were performed in graphite containers, as were those of the previous authors. Two kinds of spectroscopic grade graphite crucibles were used. One was a % in. cylinder, 3/4 in. high, containing seven 3/16 in. holes drilled 1/2 in. deep into which were packed samples of the different mixtures weighing 250 to 500 milligrams. The other, consisting of separate crucibles, was prepared by drilling 3/16 in. holes, 1/2 in. deep into 1/4 in. graphite rods % in. long. The 7/8 in. cylinder was heated directly by induction while the small crucibles were packed in a tantalum heating element for induction heating. All heating was done in a high vacuum system in which the pressure was generally less than 1x10-5mm and never rose above 2x10-5mm when the samples were hot. The general pattern of the heating in graphite was to heat rapidly to a temperature somewhat below the desired one, then to raise the temperature slowly. The samples were held for 2 to 5 min at the maximum temperature, which in all cases was far higher than that needed to produce reaction. The short time was employed to reduce possible contamination by the crucible material and to reduce composition changes that would occur because of vaporization. After examination following the heating, the samples were reheated to a higher temperature. Temperatures were measured with a Leeds and Northrup disappearing filament optical pyrometer, certified by the National Bureau of Standards, by sighting through a window at the top of the vacuum

Jan 1, 1954

By J. L. Taylor, P. Duwez

The phase boundaries in the ternary system Ti-Cr-Al have been established at 1800° and 1400°F for alloys containing more than 60 pct Ti. The martensite transformation temperature has been measured for the titanium-rich alloys. THE studies of binary alloys of titanium with the transition elements which have been published so far1-0 ndicate clearly that the solubility of these elements is always much greater in the high temperature body-centered cubic form of titanium (ß phase) than in the low temperature hexagonal form. In this category of alloying elements are iron, nickel, chromium, manganese, vanadium, molybdenum, tungsten, columbium, and tantalum. Although studies of the nontransition elements have been rather limited, early work on titanium binary alloys'" has shown that most of them were not very soluble in the a form, with the exception of aluminum, for which the solubility in a is about 25 pct.13, 12 In addition to this large solubility in a, aluminum is also soluble in ß titanium to the extent of about 35 pct and the transformation temperature from ß to a is raised with aluminum content. This effect is also typical of aluminum, in contrast with that found for the transition elements which lower the ß to a transformation temperature. Therefore, it may be anticipated that tprnarv titanium alloys with aluminum and any one of the transition elements will constitute a class of ternary alloys having characteristic features absent in alloys involving two transition elements. Chromium was chosen as a typical transition element for the present study because ternary alloys of Ti-Al-Cr commercially produced have been found to possess very interesting physical properties (MST-3 pct A1-5 pct Cr of Mallory-Sharon).'" Binary Systems The binary systems Ti-A1 and Ti-Cr have been established recently by several investigators. The data used in this investigation were taken from the complete diagram of Bumps, Kessler, and Hansen." This diagram agrees quite well with earlier investigations." For the Ti-Cr system, the phase boundaries at 1800" and 1400°F were taken from refs. 6 and 7. The binary system Cr-A1 has been studied recently by Bradley." This system is rather complex and contains not less than seven intermediate phases. The present study was limited to the titanium corner of the ternary system (less than a total of 40 pct Cr plus Al) and none of the phases present in the Cr-A1 binary alloys were found in the ternary alloys investigated. Experimental Technique Microscopic observation and X-ray diffraction measurements were used to identify phases and de-

Jan 1, 1954

By C. W. Sill

[In the original Norris and Fay method for determining selenium, selenious acid is reduced by an excess of standard thicsulfate in accordance with the following reaction: H2Se03 + 4Na2S203 + 4HC1 = Na2SeS406 + Na2S406 + 4NaC1 + X20. (1) The excess thiosutfate is then back-titrated with standard iodine solution. The disadvantages of ouch a method are obvious. On an unknown sample, the quantity of thiosutfate required would be difficult to determine; a definite excess is required, but large back titrations would be undesirable. Inasmuch as thiosulfate is decomposed by acid, considerable error may be introduced in this method, the amount depending on the acidity, temperature, concentration of excess thiosulfate, duration of contact between thiosulfate and acid, and other factors, In a critical study of the Norris and Fay method, Coleman and McCrosky3/ show that the method is accurate to less than .1 part per thousand if the excess of this sulfate Is not greater than 5 ml. of 0.1 N solution (in 1.0 ml. of 0.x4 N sulfuric acid) whether the titration is made at 0° or 20°C. A greater excess produced unsatisfactory values at either temperature. Coleman and McCrosky regulated the excess thiosulfate by adding 5-ml. portions of thiosulfate solution followed by the addition of 1 to 3 drops of 2.5 percent potassium iodide in the presence of starch. If a starch-iodine blue color formed locally around the drops of potassium Iodide, the reduction of selenious acid was not complete. On stirring the solution, the local blue color fades and another 5-ml. portion of thiosulfate is added. When addition of potassium iodide fails to produce a local blue color, reduction of selenious acid is complete, and the excess thiosulfate is then back-titrated with standard Iodine solution. The number of equivalents involved in the reduction of selenious acid by either thiosulfate or iodide is the same, and therefore no correction need be made for the potassium iodide. This procedure is much better than the original Norris-Fay titration, but acidity and time would stilt be rather critical factors subject to variation with individual technique. Also, the method still requires the lose of two standard solutions, a rather undesirable factor from the standpoint of routine application.]

Jan 1, 1954

By R. F. Domagala, M. Hansen, D. J. McPherson

On the basis of metallographic analysis, incipient melting data, thermal analysis work, and X-ray diffraction, phase relationships in the 0 to 50 atomic pct alloy content were carefully resolved. Phase relationships in the higher alloy content regions were outlined. A single intermediate phase, peritectically formed, of the form ZrX2 was established in each system. A eutectic and a eutectoid were found in the zirconium-rich region of both systems. Appreciable solubility of molybdenum and wolfram was found in ß zirconium, but only a slight solubility in a zirconium. PREVIOUS work on these systems was limited to X-ray investigations of the intermediate phases1, 2 and preliminary surveys of the zirconium-rich alloys." The diagrams presented were determined principally by metallographic, thermal analysis, and incipient melting techniques. In accordance with the Atomic Energy Commission contract requirements, phase relationships up to 50 atomic pct molybdenum or wolfram were carefully resolved, while only a limited amount of work was done to outline the 50 to 100 atomic pct alloy region. A description and analysis of the metals used in the preparation of alloys for this study are included in Table I. A "low-hafnium" zirconium crystal bar, produced by the decomposition of a volatile iodide onto a hot filament, was employed for these studies. Westinghouse "Grade 3" crystal bar was used for all alloys. The zirconium, as received, was coated with corrosion product from a standard autoclave test by which its grade designation is determined. This was removed by a sand-blasting and HF-HNO, pickling technique developed by the Atomic Energy Commission. The bars were cold rolled to approximately 1/32 in. sheet, pickled for iron removal, sheared to 1/4 in. squares, washed with acetone, and stored for furnace charge. Molybdenum sheet. 0.003 in. thick, 0.001 to 0.005 in. wolfram wire, and M in. wolfram rod crushed to granular form, from Fansteel Metallurgical Corp., were used as alloying stock. Melting Procedure A nonconsumable electrode arc furnace identical to that described in detail by Hansen et al.4 was used. The source of power for melting Zr-Mo alloys was a 400 amp dc welding generator, while a 900 amp dc generator was used for preparing Zr-W alloys. Electrode tips of the same material as the alloy addition were employed in both systems, i.e., molybdenum tips were used for Zr-Mo alloys, and wolfram tips for Zr-W alloys. This precluded any possible electrode contamination during arc melting. Ingots of 20 to 30 g of Zr-Mo alloys were melted under high purity helium in the cavity of a copper block insert in a spun copper crucible. Homogeneity was insured by remelting all ingots four to six times without opening the furnace. Due to the large difference between the melting points of wolfram and zirconium, direct melting of the charged metals as above generally yielded ingots containing unmelted wolfram particles. This was overcome, after many variations in technique, by melting a pure wolfram charge at high power levels (700 to 900 amp) and slowly adding zirconium to form a master alloy. Such master alloys were sectioned and remelted several times, then crushed to serve as melting stock for alloys of lower wolfram content. Master alloys containing 26, 50, 52, 70, and

Jan 1, 1954