Search Documents

By B. S. W. Buffam

"The property of Aunor Gold Mines, Limited, is in Deloro township, Ontario, about 3 miles southeast of Timmins. It consists of a group of eleven claims between the Buffalo Ankerite and Delnite mines.In the autumn of 1909, two brothers, John A. and W. S. Mitchell, joined the 'gold rush' to Porcupine. By the time they arrived the township of Tisdale, in which the Hollinger and Dome discoveries had been made, was staked solid but they managed to locate four claims in the northern part of Deloro township. Sufficient surface work was performed to bring the claims to patent in 1915. Following the Porcupine fire the Mitchells left the north to follow the oil developments in southwestern United States. In 1935 because of the rise in the price of gold and the successful development of the l3uffalo Ankerite and Delnite mines, they returned to Timmins and organized Augite Porcupine Mines, Limited, which combined the original four claims in Deloro and two adjoining claims controlled by Montreal River International Silver Mines, Limited. There were few rock exposures on the property, and as the overburden was generally deep surface exploration was impracticable. A programme of diamond drilling was, there; fore, undertaken in an endeavour to locate the western extension of the orebearing formation of the Buffalo Ankerite mine. This drilling was started in August 1936, and 5 months later ore was intersected at a depth of 500 feet on the south boundary of the property."

Jan 1, 1954

By W. J. Farley

"The Sherritt Gordon mine is 100 miles north of The Pas in northern Manitoba. Copper-zinc ore was discovered on the property in 1922. Production began in 1931 and continued to June, 1932, when operations were suspended because of the low price of copper. Operations were resumed on August 1st, 1937, and have been carried on continuously from that time to the present (March 1947). The production of metals up to the end of 1945 was copper, 287,129,880 lb.; zinc concentrate (50 per cent) 104,419 tons ; gold, 79,388 oz.; silver, 2,529,974 oz.GENERALThe ore occurs in two deposits, the east and the west. Both are enclosed in gneisses that are highly metamorphosed sedimentary and volcanic derivatives. The rock beneath the deposits, and hence forming their footwall, is gneissoid quartzite; the hanging-wall rock is basic garnetiferous hornblende gneiss. Pegmatite commonly occurs along both foot- and hangingwall peripheries and as isolated blocks and fragments within the ore zone . These blocks and fragments are considered to be residuals of unreplaced host rock .The ore is relatively coarse grained and ranges from the massive to the disseminated type. The metallic sulphides composing these, named in the order of their abundance, are pyrite and pyrrhotite ( 2-1 ratio) , chalcopyrite, sphalerite (marmatite) , and minor chalmeriite; subordinate amounts of gold and silver are recovered . The insoluble content of the ore averages about 35 per cent.Another deposit known as the Bob Lake, much smaller and lower in grade but having very similar relationships, occurs about 3 ½ miles to the northeast of the main Sherritt Gordon ore masses.STRUCTUREThe Sherritt Gordon orebodies are of the replacement type, and lie within a pegmatite sill that has been intruded along a contact between quartzite and hornblende gneiss. The two main orebodies are intimately related, for the east deposit is an erosional remnant of the lower, easterly limit of an orebody once continuous with the west body. The ore lies along the southwest limb of an overturned syncline."

Jan 1, 1954

By O. F. Carter

"Coniaurum Mines, Limited, hold nineteen claims in Tisdale township, in the Porcupine district, adjoining the McIntyre mine on the east. They extend for over a mile along the strike of the Hollinger-McIntyre 'break'. The property has been explored extensively along the ore zone both laterally and vertically. Workings have been carried to a depth of 5,500 feet, and nearly 50 miles of lateral workings (drifting and cross-cutting) have been driven to date in development and in gaining access to the orebodies.Production started at the Coniaurum in June 1928 and has continued without interruption. To the end of 1946 the plant has treated 2,695,725 tons of ore, yielding gold having a value of $21,989,918.The Coniaurum is controlled by Ventures Limited of Toronto. Mr. John Redington, who has guided all operations since work began on the property in 1922, is Managing Director.GENERAL GEOLOGYAge and Types of RocksKeweenawan- Quartz diabase dykes.Algoman - Quartz porphyry intrusive; the veins are probably late Algoman.Keewatin - Lava flows.Brief Description of Rock Types.Diabase DykesTwo quartz diabase dykes traverse the property in a north-south direction, cutting all formations, including veins.Porphyry IntrusivePetrographically all porphyries in the Coniaurum are of the usual Porcupine type- quartz-feldspar with alteration advanced in most instances to the stage where the feldspars are completely dissolved, leaving a wellsheared carbonate and sericite matrix with embedded rounded quartz 'eyes'. Alteration is most extensive in the smaller bodies and in the narrow protuberances from the larger masses; the cores of the larger masses are generally much fresher, with more or less well defined feldspar phenocrysts."

Jan 1, 1954

By J. N. Hobstetter, J. J. Becker

Deformed copper single crystals exhibited, upon annealing, a recrystallized twinned grain with a twin plane parallel to an active deformation plane, rotated approximately 22" about its pole, or else did not recrystallize at all. If extraneous deformation was not carefully removed, no simple orientation relationship was found. RECRYSTALLIZATION textures have been a subject of practical interest for many years, but any real understanding of their formation will have to start with a study of the recrystallization of carefully deformed single crystals. Some efforts have been made in this direction,'-' but much more experimental information is needed before a satisfactory picture of the crystallography of recrystallization can be formed. This paper reports a few results in copper single crystals. The crystals studied in this investigation were grown by the Bridgman method," and their orientations determined by the back-reflection Laue technique." Some specimens were simply deformed in compression, others were sheared, and still others tested in a rotating-grip device, in attempts to remove end constraints. The details of their deformation behavior are described elsewhere.' The deformed specimens were annealed and the orientations of the recrystallized grains were determined optically, as described by Barrett and Levenson.8 Compressed Specimens Specimen 17-A, whose orientation is given in Fig. 1, was compressed to a total of 19 pct. As observed before,' increasing deformation took place by increasing density of slip lines in initially formed clusters, with little if any formation of new slip clusters in unslipped areas. The specimen was then etched in nitric acid until its length had been reduced from 0.766 to 0.735 in. It was annealed at 1000°C, in increments of a few minutes. After 63 min, two small grains had appeared in the center, Fig. 2. They were found to be twinned with respect to each other (AB, Fig. 4). After 30 min more, the specimen was completely recrystallized. A typical view of it is given in Fig. 3. A summary of all orientations found is given in Fig. 4, in which the prominent grain G is in (001) standard projection, and the poles of the active slip planes after deformation are indicated by SP (primary slip plane), CrSP (cross-slip plane), and CnSP (conjugate slip plane). All the orientations found were related through seven orders of twinning. A "family tree" of these twins is given in Fig. 5. Furthermore, the BG twin composition plane lies close to the cross-slip plane

Jan 1, 1954

By J. S. Koehler, F. Seitz

THE dislocation theory of plastic flow originated in 1928, when Prandtl1 suggested that the internal damping of metals of plastic origin might arise from the motion of a crystalline imperfection. Following this, Dehlinger2 employed a similar imperfection in a theory of recrystallization. The first detailed theoretical discussions were those of E. Orowan3 and G. I. Taylor4 in 1934. The resulting theory was gen- eralized by J. M. Burgers5 in 1939. Mott and Nabarro, in England, and Seitz and Read,6 in the United States, started an extensive examination of the atomic theory of dislocations in the period between 1939 and 1941. However, this development was arrested by the mar and was not taken up again until after 1945. Since 1946, the field has been the object of very intense activity, particularly in the United States and England. Dislocations are beautiful and intricate imperfections; they are sufficiently complicated to account for the great variety of phenomena encountered in the field of plastic flow. Above all, the dislocation concept enables us to understand how a metal or other plastic solid can deform inelastically under very small stresses at temperatures far below the melting point. Suppose we attempt to shear a perfect crystal plastically. This can be done by sliding one entire atomic plane simultaneously through one atomic distance with' respect to the near-

Jan 1, 1954

By K. E. Nelson

The effect of thorium and zinc variations on the strength and 100-hr creep characteristics of Mg-Th-Zn-Zr alloys was investigated. Optimum resistance to creep at 650° and 700°F are attainable within a certain range of thorium and zinc contents. This range does not conform to that which develops maximum tensile properties. RAPID advances have been made during the last few years in the development of magnesium alloys for elevated temperature applications demanding high resistance to creep. The beneficial effect of rare-earth metals on the creep resistance of magnesium alloys has been emphasized by a number of publications1-13 and such alloys are now in commercial production. The use of thorium as an alloying ingredient in magnesium was mentioned by McDonald and also in two Alien Property Custodian patent applications.10,17 The initial observation of Sauerwald that thorium contributes still higher creep resistance to magnesium than is attainable with rare-earth metals has recently been substantiated.'" " In fact, it has been demonstrated that the useful temperature range of magnesium alloys is appreciably extended by the use of thorium. In all cases, it was observed that zirconium must be included in the alloys in order to render them fine grained and more readily castable. Several recent publications:2-27 indicate that a still further improvement in creep resistance and a further extension of the useful temperature range can be realized by the addition of zinc to alloys. The primary purpose of this paper is to present the results of a comprehensive study of the effect of zinc on the strength and creep characteristics of Mg-Th-Zr alloys. Compositions covering the range of thorium content from M to 6 pct and zinc content from 0 to 5 pct have been investigated. The creep characteristics at 650" and 700°F reported in this paper are based on results of tests of 100-hr duration. It is appreciated that creep tests of 100-hr duration might not yield adequate data for design purposes for parts with much longer expected life. However, for the purposes of the present discussion, it is felt that the combination of stresses and temperatures used in the 100-hr creep tests have yielded a clear representation of the compositional variation of creep resistance at the temperatures investigated. Creep tests of 1000-hr duration are now in progress on a few of the most promising alloys. Preparation and Testing of Alloys The alloys studied in this intensive investigation were prepared in 25 lb capacity mild steel crucibles. The thorium, zinc, and zirconium were alloyed and poured as described in earlier publications The thorium was introduced into the melt in the form of a Mg-Th hardener," the zinc added in the metallic form, and the zirconium alloyed in the form of the commercial hardener containing magnesium and 30 to 50 pct Zr.10, 26 Fluxing practices for melting and refining were the same as for magnesium-rare-earth metal-zirconium alloys. The melts were sampled for analytical determinations and poured into separately cast 1/2 in. diameter standard tensile bars. The test bars were given a precipitation treatment of 16 hr at 600°F in laboratory furnaces. It has been shown by other tests that a high temperature solution treatment followed by an aging treatment is unnecessary for the development of optimum properties in Mg-Th-Zn-Zr alloys. The selection of 600°F as the aging temperature was based on an attempt to achieve metallurgical stability without coalescence of the undissolved phases and the attendant loss in strength. The thorium, zinc, and zirconium contents of each melt were determined chemically. The zirconium contents are reported in two parts, "soluble" and "insoluble," referring, respectively, to the portions present in the alloy which are soluble and insoluble in dilute HCl acid. Distinction is being made between these two components of the zirconium content in the alloys because it has been found that only that portion of the zirconium content which is soluble in dilute inorganic acids affects the structure and properties of the alloys. The usual impurities consisting of copper, iron, manganese, and nickel were determined spectroscopically. The analysis for each melt is listed in Table I. A description of the methods of tension and creep testing has been detailed in earlier papers. The tests were performed with the cast skin re-

Jan 1, 1954

By Y. C. Liu, H. Margolin

Investigation of martensite habit plane in water-quenched Ti-Mn alloys was carried out in the range of manganese contents between 4.35 and 5.25 pct. On the basis of 22 measurements, the poles were observed to fall into two groups, indicating the existence of two habit planes. The Miller indices of the poles close to these two groups were found to be <334>ß and <344>ß. TITANIUM has an allotropic transformation at 882.1° ± 0.5C1 by which the high temperature ß (body-centered cubic) phase changes to a (hexagonal close-packed) phase. It is well known, as in the case of low carbon steel, that the unalloyed high temperature ß phase cannot be retained no matter how rapid the cooling rate. However, the addition of alloying elements usually lowers the transformation temperature continuously and stabilizes the ß phase to a temperature much lower than the allotropic transformation temperature in pure titanium. A typical example of this behavior is found with manganese-alloying of titanium. Fig. 1 shows the titanium-rich Ti-Mn equilibrium diagram as established by Battelle Memorial Institute.&apos; The addition of manganese lowers the ß transus line and the eutectoid reaction takes place at 550°C, the eutectoid composition being 20 wt pct Mn. However, upon quenching to room temperature from the ß field, the ß phase can be completely retained with much less manganese, see Fig. 2. If the composition is less than that required to stabilize the ß phase completely, a plate-like structure, similar to that of martensite in other alloy systems, appears as shown in Fig. 3. Much lower alloying content merely intensifies the amounts of these transformed structures, as shown in Fig. 4. This paper presents the results of an investigation of the habit plane of these martensitic structures in Ti-Mn alloys. Experimental Procedure Investigation of the pole of a given platelet was made using the two-surface method of analysis." In order that a given martensite trace on two surfaces be readily recognized both at low and high magnifications, it is desirable that only a small amount of martensite be present. From a review of the data obtained at Battelle Memorial Institute4 on quench hardening in Ti-Mn alloys and the results of Duwez" on transformation in Ti-MO alloys, it was decided that the most appropriate Ti-Mn composition for this study would be about 6 pct Mn. A group of alloys containing from 3 to 10 pct Mn was made to bracket this composition. The choice of the 6 pct alloy was apparently proper, since it was later learned that approximately 5.5 to 6 pct Mn is required to stabilize the ß phase on water quenching.

Jan 1, 1954

By H. Clare Horwood

"Three types of structures, the main shear zone, the north shear zone, and a series of hanging-wall fractures, contain all the orebodies so far discovered at the McKenzie Red Lake mine. Lenses and veins of quartz in these zones and fractures are the sources of the ore. The ore-bearing structures are unusual in that they are in a complex intrusive mass known as the McKenzie-Gold Eagle stock. They are believed to have been produced by compressive stresses from the south andsouthwest.The mine is on the northeast side of McKenzie island, in Dome township in the central part of the Red Lake area. The original discovery, the main shear zone, was made in 1928, about 3 years after the property was staked, by M. L. Bouzan who was in charge of prospecting and development work on the property. Subsequent diamond drilling and underground exploration led to the installation of a mill, which came into production early in 1935. The hanging-wall fractures were found branching out from the main shear zone during development work on the 350-foot level. The north shear zone was discovered in 1940.From 1935 when the mill began operation until the end of 1946 total production from the mine was approximately 269,349 oz. gold and 69,317 oz. silver, having a value of $9,679,739, recovered from 823,527 tons of ore.GENERAL GEOLOGYThe McKenzie-Gold Eagle stock has a total length of approximately 1 ½ miles and a width of about ½ mile. It was intruded into a complex synclinal fold in Timiskaming sediments. The sediments, which have been cut in only one place in the underground workings, are principally wellbedded greywackes. The stock is composed of large masses of diorite and granodiorite, a small mass of hornblende pyroxenite, and basic dykes of two ages. The diorite occurs as irregular masses in large measure surrounded by the granodiorite that it intrudes. It contains tabular crystals of andesine, having a maximum length of3/4 inch. The hornblende pyroxenite is an elongated lens or dyke in the diorite. The granodiorite masses occupy about two-thirds of the stock. Along its eastern side the main mass tends to become darker and more dioritic toward the diorite contact.Basic dykes of pre-vein and post-vein age are the youngest intrusive rocks at the mine."

Jan 1, 1954

By R. B. Russell

SINCE Cahn&apos;s¹ paper on plastic deformation in orthorhombic (a) uranium an increasing amount of work is to be expected on orientation of single crystals and preferred orientation in this metal. It would seem desirable to have a table of angles between crystallographic planes (hkl) and (HKL). Table I shows these angles as distances from (loo), (0l0), and (00l), and in Fig. 1 as a standard (001) stereographic projection. Only the locations of poles whose diffracting planes produce Cu Ka reflections up to 0 = 70.5" (i.e. (154) ) are given." The relative reflection of these planes are represented by circle diameters. It is hoped that the projection may also be used in making inverse pole figures, originally suggested by Harris.&apos; Values of 4 were calculated from the expression hH kK 1L cos = hH/a²+kK/b²-lL/c² where the lattice parameters a, b, c, and the spac-ings d were taken from the work of Jacob and Warren." (They report a = 2.852 kX (2.8578 A), b = 5.865 kX (5.8768 A), c = 4.945 kX (4.9550 A).) The parameters reported by them may be subject to revision,4,5 accordingly the interplanar angles are listed to only the nearest tenth of a degree. References ¹R. W. Cahn: Acta Metallurgica (1953) 1, p. 49. ¹G. B. Harris: Philosophical Magazine (1952) 43, p. 113. 3C. W. Jacob and B. E. Warren: Journal ACS (1937) 59, p. 2588. 4J. S. Lukesh: Acta Crystallographica (1949) 2, p. 420. ³ J. Thewlis: Nature (1951) 168, p. 198.

Jan 1, 1954

By W. Rostoker, R. P. Elliott, B. W. Levincer

Phase equilibria in the Ti-Cr-Mo system have been investigated for alloys containing 100 to 40 pct Ti in the temperature range 550° to 1300°C. Five experimental isothermal sections and a surface of incipient melting are presented in addition to a summary projection of the space. Seven vertical sections have been constructed from the isothermal sections. A STUDY of the system Ti-Cr-Mo was undertaken as part of a program sponsored by Watertown Arsenal toward the development of titanium-base phase equilibrium diagrams of potential technical importance to alloy development. The scope of the investigation included the composition range contained by the titanium corner and the line of 64 pct Ti (all compositions are by weight) and the temperature range 550" to 1100°C. A surface of incipient melting was constructed from measurements on a large number of alloys. The system Ti-Cr has been established.&apos;-? The phase diagram is characterized by a wide miscibility field of the solid solution at elevated temperatures and a eutectoid reaction of the type: (15 pct Cr) + TiCr, (685C). The a solid solution has a very limited capacity for solution of chromium (< 0.5 pct Cr). The intermediate phase TiCr2 has at best a very narrow composition range. It has been shown that two allotropic modifications of this phase exist. However, this behavior does not appear to be perceptibly reflected in the form of phase boundaries of the type + TiCr,. In the system Ti-Mo,9-10 the phase is stabilized to successively lower temperatures with increasing molybdenum content. There are no known intermediate phases. The a solid solution is limited to less than 0.5 pct Mo. Because of the very extensive range of the phase, the ternary system was ideally suited to the determination of the phase boundaries by the parametric method of Andersen and Jette." A parametric surface was constructed to provide the necessary basis for the application of this method. Preparation and Treatment of Alloys More than 60 alloy compositions were prepared for the study of this system. Alloy buttons of 10 grams were arc-melted in a nonconsumable electrode furnace using inert atmosphere protection and a water-cooled copper crucible. The construction and operation of this type of melting unit have been adequately described elsewhere.&apos;&apos; To insure complete solution of alloy additions, the buttons were remelted alternately on top or bottom as many as five times. This was accomplished by a suitable mechanism for "flipping" over the ingots. Iodide titanium (99.97 pct Ti) was used as the alloy base. An especially high quality chromium (99.9 pct Cr) was obtained from the National Research Corp. Molybdenum sheet (0.005 in.) of 99.9 pct purity was used.

Jan 1, 1954

By M. E. Wilson, A. C. Lee

"The property owned by Senator-Rouyn Mines, Limited, is in Rouyn township about 17'2 miles southwest of the town of Rouyn. It adjoins the Chadbourne claims of Noranda Mines, Limited, on the south and the Bagamac property on the ·west. It includes seven claims-block 44, blocks 80 to 83 and blocks 96 and 97; the mine is wholly in blocks 44 and 82.Late in 1936 gold was discovered in an outcrop of rusty weathering carbonate rock near the north end of block 44, and the following year the present Company was organized to proceed with the development of the property. During 1937-38, 17,000 feet of diamond drill core were bored to determine the extent of the ore deposit at depth. From October 15th, 1940, to April 15th, 1941, the ore was hauled to the mill at the Arntfield mine for treatment. The mill on the Senator-Rouyn property started on April 25th, 1941, and has been in practically continuous operation since than time. To the end of 1946, 574,874 tons of ore, from which gold having a value of $3,836,450 was recovered, were treated in the mill.GEOLOGYThe rocks exposed at the Senator-Rouyn mine, except in the southern part of the property, are almost wholly quartz diorite, part of an irregular mass that extends west from the town of Rouyn along the north shore of Noranda lake and thence southwest across the Senator-Rouyn claims. In the northern part of the propertyt inclusions of rhyolite occur here and there in the diorite. In the southern part the predominant rock is dacite and in the east-central part of block 44 claim andesite. Dykes of andesite, quartz syenite, and later diabase also occur on the property.The andesite of the Abitibi volcanics is not exposed on the property, but has been intersected in three diamond drill holes, one on the eastern boundary of block 44 and two farther west within the block. This andesite is probably the western end of a band of pillowed andesite well exposed in the Larose claim to the east."

Jan 1, 1954

By D. J. Blickwede

WHEN iron is dipped in molten zinc at temperatures in the range 840" to 930°F, the two metals react to form layers of Fe-Zn compounds which adhere to the iron. At the galvanizing tem- perature, the successive layers are:&apos; y (Fe5Zn21), 61 (FeZn;), and 5 (FeZn13), in conformity with the Fe-Zn constitution diagram. There is no quantitative information in the literature on the rates of growth of the individual alloy layers over the temperature range 840° to 930°F. Rather all the past experiments have studied the loss in weight of iron as a function of galvanizing

Jan 1, 1954

By I. Cadoff, J. P. Nielsen

The Ti-C phase diagram exhibits a peritectic point at 1750°C and 0.8 pct C, and a peritectoid point at 920°C and 0.48 pct C. The maximum solubility of carbon in a titanium is 0.48 pct. The 6 region containing the Tic compound (20 pct C) extends to 11 pct C at the peritectic temperature. THE interest in the Ti-C alloy system stems from the fact that carbon occurs as an impurity in titanium alloys when graphite electrodes or graphite crucibles are used in their melting. Since titanium-base alloys are still in the development stage, some virtue may be found in carbon addition to titanium. The Tic compound is currently emerging as an important powder metallurgy base constituent similar to the WC compound. Ehrlich&apos; identified the phases and structures present in the Ti-C system. The peritectoid region of the phase diagram was investigated by Jaffee et al." A preliminary diagram based on theoretical considerations was proposed at the outset of this research." The Tic compound has been investigated extensively and has been reported on in a large number of papers. Experimental Procedure Arc-melted alloys of 24 compositions in the range 0 to 20 wt pct C were investigated using metallography, X-ray diffraction, and, for the liquidus and solidus regions, incipient and complete melting. All alloys were prepared from iodide titanium (New Jersey Zinc Co., 99.95 pct Ti minimum) and spectroscopic grade carbon (National Carbon Co.). To prevent carbon spattering during arc melting the carbon was encapsulated in titanium. For alloys containing less than 1 pct C the powder was inserted into a capsule formed by drilling a hole in the as-received rod. For higher compositions, capsules were formed from titanium sheet. Arc Melting: The charges were melted in the copper-hearth cold electrode furnace shown in Fig. 1. This furnace is similar in principle to the all-metal unit adapted for titanium melting at Battelle Memorial Institute.&apos; The transparent pyrex walls giving unlimited visibility during operation and the multiple-

Jan 1, 1954

By R. M. Brick, F. L. Vogel

THE elementary mechanism of deformation in the body-centered cubic metals has been a subject of dispute for many years. If the problem were merely that of designating the crystallographic plane or planes of slip, the solution would have appeared long ago. However, there must be greater differences in the deformation behaviors of the body-centered and face-centered types than the differences in their lattices would suggest. The lines of slip formed on the polished surface of a strained face-centered cubic metal conform to glide over a single plane of the crystal. Slip in body-centered cubic iron, however, is frequently observed as curved and forked lines which could not possibly define a single plane of atoms. This alone is sufficient reason to expect different modes of deformation to operate in the two lattice types. The literature in this field now has generally accepted the proposition that {110), {112), or (1231 planes will act as slip planes in iron. It is essential that the experimental evidence supposedly supporting this proposition be critically examined. Taylor and Elam1 in 1926, using relatively small single crystals, determined the operative slip systems by measurements of the distortion of a grid engraved on the specimens prior to deformation. Their results indicated that shearing had taken place in the close-packed direction on a plane adjacent to or coinciding with the plane of maximum shear which contained the slip direction. This led the authors to propose a theory of noncrystallographic or banal slip. The authors considered an alternate rationalization of banal glide. Slip on two (1101 planes or possibly two {112} planes containing the same <1ll> direction could produce the wavy slip lines. By employing plane segments of varying widths, the integrated plane could take any position in the <111> zone. They rejected this explanation, however, feeling that the preponderance of evidence was against it. Taylor&apos; continued the investigation of the plasticity of the body-centered cubic lattice on ß brass. He reasoned that the resistance to shearing of a given plane in the zone of the slip direction was a function of the angle between the glide plane and the closest (110),: P F=—cose sine cos(X —?) [1] where F is the resistance to shear; P, the axial load at yielding; A, the cross sectional area; e, the angle between slip direction and load axis; x, the angle between plane of maximum shear containing the slip direction and the (101) pole; and ?, the angle between observed glide plane and the (101) pole. Differentiating Eq. 1 and rearranging, dF — = tan(x-?) d? [2] F which expresses the variation of the shear resistance with the angle $. Integrating this equation between the limits 0 and ? yields In F/F0 = ?0?tan(x— ?) d? [3] Here, F, is the resistance to shear of the (110) plane and F is the resistance to shear of a plane $ degrees from the (110). Thus, the variation of shear resistance with $ can be calculated from an experimentally measured x vs $ relationship. Fahrenhorst and Schmid8 sed several methods, none of them involving direct observation, to determine the glide system in ferrite. They determined the variation of critical resolved shear stress with

Jan 1, 1954

By G. S. Farnham, D. A. Scott

Partition of certain elements, particularly nickel, was determined for slowly cooled steels, the greater number containing from 0.30 to 0.35 pct C. Approximately 3 pct of the nickel, 18 pct of the manganese, 33 pct of the molybdenum, and 35 pct of the chromium occur in the carbide phase. Partition of one element is not much affected by the presence of another. THE object of this investigation was: 1—to determine the partition of nickel between cemen-tite and ferrite in a medium and high carbon series of annealed steels; 2—to evaluate the effect of chromium and/or molybdenum or both on the partition of nickel in medium carbon annealed steels; 3— to determine the partition of chromium between ferrite and carbide in a series of medium carbon annealed steels; and 4—to study the chemistry of the carbides formed in an AISI 2330 steel during both isothermal transformation, and quench and draw experiments at 1150°F (620°C). The partition of alloying elements between ce-mentite and ferrite in annealed steels has been the subject of many investigations, a summary of which has been given by Austin1. However, there is no satisfactory data available concerning the partition of nickel. It has generally been assumed that virtu- ally all of the nickel concentrates in the ferrite phase in annealed steels. Two investigators"." have reported the finding of nickel in extracted carbide residues. Recently, it has been shown4 that nickel substitutes up to 40 pct for iron in the lattice of cementite produced by the low temperature carburization of iron-nickel powders. In addition to the lack of data on nickel partition, the literature also fails to make reference to the effect of other elements on the nickel content of the carbide in nickel-bearing steels. The partition of molybdenum between ferrite and carbide has been reported"-&apos; for hypoeutectoid steels, isothermally transformed at 1300°F (705°C) and

Jan 1, 1954

By D. J. Carney, R. L. Stephenson

A sampling technique has been developed for procuring a sample of sinter representative of the entire depth of the sintering bed. The sampling method involves the use of an open-bottom metal basket that rides on the grate of the sintering machine and when removed contains a sample of the sintered product. Additional data have been obtained to indicate that the tumbler test is a suitable means of measuring sinter strength. IN the last few years additional sintering facilities have been installed in both the Pittsburgh and the Chicago district of the United States Steel Co. Since the construction of these sintering plants made possible the use of higher percentages of flue-dust sinter in our blast-furnace burdens, it became important to study means of controlling the quality of sinter to obtain optimum results in the blast furnace. For controlling an operating process, it is necessary first to establish standards by which the quality of the product can be judged. For sinter, it appeared that an important property was its strength or its resistance to degradation during transportation and charging into the furnace. Consequently work was undertaken to establish a standard for sinter strength that could be used both for controlling sintering-plant operations and for correlating sinter quality with blast-furnace performance. The first problem in setting up a standard was that of procuring a sample that would be representative of the sinter made under any particular set of conditions at the sintering plant. Since the United States Steel Co. sintering plants discharge the finished sinter either into a large pit or onto a rotary cooler, the sinter becomes inseparably mixed with material sintered 2 hr before or 2 hr afterwards. For this reason the exact identity of the sinter is lost. A sample selected as the cooler is discharged, or as the sinter is removed from the pit, cannot be said to be truly representative of the sinter made at any specific time. Sampling The first attempt to procure a sample that would be representative of a specific sinter mix and of specific operating conditions was made by stopping the Dwight Lloyd sintering machine and removing an entire pallet full of sinter. This method, however, proved very difficult to perform and interfered considerably with the operation of the plant. To overcome this difficulty, a sampling method was devised by technologists at South Works enabling them to secure, without interrupting the sintering operation, a sample of about 1 cu ft of sinter, representative of sinter for the full depth of the sintering bed. The South Works method involves the use of a steel-frame-work basket. A typical basket is shown in Fig. 1. The basket has been used both with and without crossbars along the bottom. As long as the crossbars are in the same direction as the grate bars on the sintering machine they do not interfere with the sintering process. The basket is set on an empty grate of the Dwight Lloyd sintering machine before it passes under the swinging feed spout, see Fig. 2. When the basket is removed after it has travelled the length of the sintering machine, it contains the sample. Just before the basket is removed, the sinter is scored and chipped to facilitate removal of the sample from the sinter bed. A view of the basket after its removal is shown in Fig. 3. Although the sampling method was originally designed for use on a Dwight Lloyd sintering machine, it can also be used on the Greenawalt type of machine. When used on the Greenawalt-type machine, the basket is placed on the sintering grate before the charging car passes over it, and finally it is removed just before the pan is dumped. Testing After a method of obtaining a representative sample of sinter had been developed, the next step was to select a method of measuring its strength. The irregular shape and size of the sinter pieces precluded the use of a simple compression test for determining strength; consequently, the shatter test and tumbler test were investigated. To perform the shatter test, a sample of sinter, approximately 5 lb, is dropped from a hinged-bottom box at a height of 3 ft onto a steel plate. The broken sinter is sieve-analyzed after a specified number of drops. The tumbler test is performed with the use of a standard ASTM coke-tumbling drum. The drum is 3 ft in diam and is equipped with two lifter bars diametrically opposite one another on the inner periphery of the drum. The drum is rotated at a speed of 24 rpm for 200 revolutions, and after tumbling the sample is sieve-analyzed. To express as single numbers the results of sieve analyses after shattering or tumbling, the method suggested by R. E. Powers1 was employed. This method involved plotting the size of the sieve openings on a logarithmic scale and the cumulative per cent larger than each sieve on a probability scale as described by J. B. Austin.&apos; By interpolating from the plotted data, which in most cases approximated

Jan 1, 1954

United Engineering Trustees, Inc James L Head, &apos;55, E C Meagher, &apos;56, Gail F Moul¬ton, &apos;57 Advisory Committee to Real Estate Committee Cleveland Dodge, Herbert Hoover, Paul D Merica The Engineering Foundation W M Peirce, &apos;56, A M Gaudin, &apos;58 Research Procedure Committee A M Gaudin, March &apos;54 Engineering Societies Library Board Frank T Sisco, &apos;54, E M Wise, &apos;56, James L Head, ex officio Engineering Societies Personnel Service Board of Directors E J Kennedy, Jr, E H Robie

Jan 1, 1954

By J. Washburn, R. Drouard, E. R. Parker

Temperature dependence of the rate of recovery in zinc single crystals after a simple shear deformation at low temperature was investigated. Some tentative suggestions regarding the annealed and strain-hardened states of a crystal are discussed. RECOVERY may be defined as the gradual return of the mechanical and physical properties of strain-hardened metal to those characteristic of the annealed material; an increase in temperature increases the rate of recovery. The annealing process in strain-hardened polycrystalline metals is complicated by the inhomogeneity of strain which always exists in aggregates. Polygonization in bent regions of the crystals and growth of new almost strain-free grains starting at points of severe local distortion1-:&apos; make it almost impossible to isolate and study the recovery process. Homogeneously strained single crystals, however, do not polygonize or re-crystallize and hence they can be used advantageously to study recovery. In such crystals strain hardening is completely removed by recovery alone. Since recovery is a process whereby certain lattice disturbances introduced by plastic flow are gradually reduced, a knowledge of the rate and temperature dependence of this process for various conditions of prestrain might be helpful in formulating a model of the strain-hardened state. For simplicity it seemed desirable to limit the type of prestrain to the simplest obtainable, i.e., simple shear strain. In the experiments to be described, recovery was studied by observing changes in the stress-strain curve of prestrained zinc single crystals held for various times at temperatures above that employed for straining. Single crystals were grown from the melt by a modified Bridgeman technique from Horse Head Special zinc 99.99 pct pure, and from spectrographically pure zinc 99.999 pct pure. They were grown as 1 in. diameter spheres and acid-machined&apos; to the final specimen contour. The test section was a cylinder about 1/8 in. high and 3/4 in. in diameter. The conical sections adjacent to the test section were cemented into the grips so the load could be transmitted to the crystal as uniformly as possible. The specimens were oriented so that in testing the maximum shear stress was applied along one of the slip directions, [2110], in the (0001) plane. Details of the production and testing of such specimens have been presented.&apos; Each test was carried out according to the following schedule: 1—The crystal was strained at — 50°C until it reached a maximum shear stress, ,,,. The strain rate was approximately 5 pct per min in all cases. 2—After straining, the crystal was unloaded before the temperature was changed. Unloading required about 3 min. 3—The temperature of the specimen was then increased from — 50°C to the temperature, T, of recovery. This change in temperature was completed in a time of less than 2 min. The specimen remained at temperature, T, for a time, t, which differed for the various specimens. 4—Thereafter the temperature was again reduced to — 50 °C in approximately 3 min. 5—While at —50°C, the stress-strain curve after recovery was obtained. 6—The specimen was then unloaded and annealed for 1 hr at 375 °C in a helium atmosphere to bring about complete recovery. Cooling to room temperature after anneal required 90 min. 7—The same crystal could be re-used for another test because the plastic properties after annealing closely duplicated those of the original crystal. The specimen was immersed during the test in a bath of methyl alcohol which, through a system of tubes, could be pumped through either of two heat exchangers to regulate the temperature; this was accomplished by circulating the liquid through coils immersed in a bath of acetone and dry ice for cooling or in a bath of warm water for heating. Test temperatures were thus maintained constant within ±1°C. The — 50°C temperature was low enough so that no measurable recovery occurred during unloading and reloading. The stress-strain curve continued after recovery along a path below, but approximately parallel to, the path of a curve obtained in an uninterrupted test. Fig. 1 shows some of the results from a specimen of 99.999 pct Zn. The amount of downward displacement of the curve due to recovery was a

Jan 1, 1954

By W. J. Houk, F. C. Hull

To clarify interpretations of grain structures and to assist in calculations of spatial grain size distributions, plane distribution curves have been determined for random sections through four regular polyhedrons approximating the shapes of metal grains. The characteristics of the distribution curve for the average metal grain are predicted. IT was realized early in the history of metallurgy that metals are polycrystalline aggregates and that the size and shape of crystals affects the properties of the material. Reaumur1 in 1722 employed the microscope to examine the fractured surfaces of steel and of white and gray cast iron and suggested a polyhedral arrangement of the crystals. The first extensive investigation of the form of crystal grains was carried out by Desch.2 He examined the disintegrated grains from a ß brass sample and noted that the number of faces per grain ranged from eleven to twenty and that the number of edges per face varied from three to eight and the maximum occurred at five. While it has been found practical to examine isolated grains only in exceptional cases, it is always possible to make a plane section through the metal and examine the shape of the grain sections on the plane of polish. Desch2 tried to determine the relation between the form of a polyhedron and that of its plane sections for comparison with distribution curves of numbers of sides per grain section of actual metal samples. The polyhedrons investigated were the rhombic and pentagonal dodecahedrons and the orthic tetrakaidecahedron. However, the frequency distributions of the number of sides of plane intersections were not sufficiently characteristic to decide which polyhedron most closely approximated the average grain in a metal. Determination of Statistical Shape of Grain in Space Scheil3 was interested in the problem of calculating the distribution of grain sizes in space from the easily measured distribution of grain section sizes on the plane of polish. Assuming that the grains were spheres and using the plane distribution curve for a sphere shown in Fig. 1, he employed a successive subtraction method to calculate the spatial distribution. In order to evaluate the accuracy of these calculations, Scheil and Wurst4 determined the actual distribution of grain sizes in space in their sample of ingot iron by polishing off successive layers and following every individual grain in a series of micrographs. From curves of mean radius of intersection of a given grain vs thickness of metal removed in polishing, Scheil and Wurst attempted to derive the statistical shape of a grain in space. Their calculated plane distribution curve for this shape is compared with the distribution curve for a sphere in Fig. 1. A table of values based on this curve was prepared for calculating spatial distributions of grains. The calculated and measured spatial distributions of their sample then agreed much better than when a spherical shape had been assumed. In the present paper, an attempt has been made to learn something about the average metal grain by studying in detail the effect of the shape of regular polyhedrons on the plane distribution of areas and shapes of areas produced by random sections through them. From the data presented below, it can be concluded that the plane distribution curve for the average metal grain differs in three fundamental respects from the curve derived by Scheil and Wurst. Polyhedrons Selected for Study The polyhedrons selected for the statistical study are illustrated in Fig. 2 and consisted of a cube, a figure formed by cutting off the corners of a cube at the midpoints of the original edges, a tetrakaidecahedron, and a pentagonal dodecahedron. The length of edge on any one figure is a constant. For the above models the edge lengths were 3.50, 4.00, 2.00, and 2.08 in., respectively. A cube was selected for one of the polyhedrons because of its simple geometry, because it is a form that by repetition can completely fill space, and because it represents a convenient degree of departure from compactness beyond which the shape of

Jan 1, 1954

By P. M. Aziz, I. Markson, C. S. Barrett

The abnormal after-effect in twisted wires that occurs when untwisting is interrupted by etching con be brought under control and used to study the mechanical properties of thin surface films and how they are effected by reagents and heat treatment. Results are given of studies of oxide films on high purity aluminum. IF a wire is subjected to plastic deformation by torsion and then released, it untwists in the normal after-effect, but under certain circumstances the untwisting is abruptly lessened or reversed by the application of an etchant to the wire.1,2 This abnormal after-effect may occur, for example, if there is a coherent oxide film on the surface of the wire which is removed by the etchant. Following a suggestion of A. H. Cottrell that predicted this effect, it is attributed to dislocations that had piled up beneath the oxide layer and represents the rapid release of residual stresses caused by these dislocations. When the layer is removed, the stress relief may be by escape of piled-up dislocations from the metal, or by an activation of latent sources of dislocations located at the surface, together with rebalancing of elastic stresses to compensate for the loss of stressed material, as in a residual stress analysis determination, these mechanisms acting singly or in combination.&apos; The slower the attack of the reagent, the more gradual is the stress relief and the smaller the change in strain rate when the reagent is applied. A study has been made of the factors that influence the magnitude of the normal and abnormal after-effects with the object of developing techniques suitable for a quantitative investigation of the influence of various surface films on dislocations in wires, and of the rate and extent of the attack on the films by different reagents. It was found that reasonable sensitivity and reproducibility could be achieved if a suitable choice of variables was made and if these variables were held constant through a series of experiments. The method was then applied to a study of oxide films produced and treated in different ways on the surface of high purity aluminum wires, and to a study of the damage to these films caused by various reagents. Experimental Procedure The material used throughout this work was prepared from 99.9968 pct Al. This high purity aluminum was melted, cast into 1/2 in. diameter ingots, and then swaged and drawn without intermediate annealing to 0.040 in. diameter wire. A sketch of the apparatus employed for twisting is shown in Fig. 1. The test wires were mounted into the apparatus by cementing one end of the wire to the beaker and the other to the tube with laboratory wax of high melting point. The length of the wire between the waxed joints was 4.2 & 0.2 cm. Extreme care was taken during mounting to avoid cold-working the wire. The wire was twisted through 335" in 2 to 4 sec by rotating the pinion on the gear box until the vertical post on the rotating table, which was initially touching the horizontal stop, was arrested by the stop. All the tests were conducted with apparatus and reagents at the same temperature (about 25°C). In all tests, except those where the duration of the initial torque was investigated, the torque was applied for a period of 2 min. At the end of this time the table was rotated back a few degrees away from contact with the stop and the wire allowed to untwist. The after-effects were measured by reflecting a beam of light from the mirror shown on the apparatus. After the wire had untwisted for 6 min, a reagent was carefully poured into the beaker and thereby applied to the surface of the wire.. In some tests the liquid in the beaker was removed after a few minutes and replaced by an-

Jan 1, 1954