Trans No. Place Date Vol. 1. Wilkes-Barre, Pa. May, '71 1 2. Bethlehem, Pa. Aug., '71 1 3. Troy, N. Nov., '71 1 4. Philadelphia, Pa. Feb., '72.. 1 5. New York, N. Y. May, '72 1 6. Pittsburgh, Pa. Oct., '72 1 7. Boston, Mass. Feb., '73 1 8. Philadelphia, Pa. May, '73 2 9. Easton, Pa. Oct., '73 2 10. New York N. Y. Feb., '74 2 11. St. Louis, Mo. May, '74 3 12. Hazleton, Pa. Oct., '74.. 3 13. New Haven, Conn. Feb., '75 3 14. Dover, N. J. May, '75 4 15. Cleveland, Ohio Oct., '75 4 16. Washington, D. C. Feb., '76 4 17. Philadelphia, Pa. June, '76 5 18. Philadelphia, Pa. Oct., '76 5

Jan 1, 1944

By F. Benard

Recovery of selenium and tellurium at Copper Cliff by the Ontario Refining Co. has been previously described by the writer.l During 1935 a new building was erected to house this operation and description of the new plant and process form the subject of this paper. The building, of modern steel and tile construction, covers an area of 5900 sq. ft. with a volume of approximately 165,000 cu. ft. The large monitored center bay is flanked by two smaller outside bays, one of which is devoted to the tellurium section. All equipment, ceilings and upper walls, are treated with aluminum paint, giving good illumination and facilitating good housekeeping, essential from a health standpoint in handling material of this nature. Equipment Layout and type of equipment conforms to the requirements of the process as described below. In the selenium section, storage tanks, neutralizing tanks and precipitators are of steel construction, lead-lined and arranged for gravity flow (Fig. 1). The neutralizing tanks are equipped with water-cooled lead coils for controlling solution temperature, agitation being accomplished with compressed air. The precipitators are provided with mechanical agitators, and sulphur dioxide is introduced into the solution through 1/2-in. lead pipes leading from a manifold attached to the cover of the precipitator. Each precipitator has internal cooling coils and an air-jet exhauster to carry off fumes. Neutralized solutions are filtered in a 29-plate wooden filter press using heavy cotton duck as a filter medium, forced feed being maintained by a Welmet centrifugal pump. Dilute solutions are concentrated by evaporation in a vacuum evaporator, constructed of cast hard lead. Heat is supplied by an outside steam chest operating under 15 Ib. steam pressure. The solution is circulated through the steam chest by a pump of antimoniallead at a rate approximating 400 cu. ft. per min. The evaporator is evacuated by a water-jet condenser that creates a vacuum of 26 in. of mercury under normal operating conditions. The capacity of the vessel is 60 cu. ft. and the rate of evaporation 25 cu. ft. per hour.

Jan 1, 1944

By H. I. Najarian

This paper is a companion piece to the description of the electrothermic process that begins on page 141. It will be confined to a brief story of the development. of the Weaton-Najarian vacuum condenserf at this plant, together with up-to-date design and operating data. The Josephtown smelter was designed primarily for production of zinc oxide. However, the development of a method for production of zinc metal had always been under consideration, and accordingly one of the original eight units of the elcctro-thermic furnaces built in 1930 was set up to produce metal. The design of this furnace was identical with that of the oxide furnaces except that in place of oxide tewels opening into oxide manifolds, conventional conical clay condensers—similar to condensers used in horizontal retort smelting—were installed around the periphery of the furnace and in several tiers vertically for condensing the zinc vapors. The early experimental work in trying to condense zinc out of the mixtures of zinc vapor and carbon monoxide gas from the electrothermic furnaces indicated that, while the gases from electrothermic smelting would condense in surface-type condensers, the formation of blue powder was excessive and condenser efficiency low. Furthermore, operating a large unit of electric furnace with several hundred small condensers, with attendant high labor cost and unfavorable operating conditions, did not appeal to us. We also realized that a single unit of surface condenser capable of condensing 12 torg tons of metal per day would be of huge dimensions and possibly difficult of control. So we took as our aim the development of a method whereby a single condenser unit of reasonable dimensions would condense zinc, in one step, from the large volume of gases that the electric furnaces produced. We set about searching for knowledge on zinc metallurgy and design of zinc condensers in particular. Our study of the prior art focused our attention on the oft-repeated statement by earlier experimenters, that the most efficient way to condense metallic vapors, such as zinc vapors, was to bring the vapors into "intimate contact" with molten metal; but the methods offered for securing this "intimate contact" in any practical manner left much to the imagination. We were handicapped by not having some-one on the Josephtown smelter staff who could lay claim to being an expert zinc metallurgist and could give guidance from actual experience on the practicability of various schemes that haunted our imagination. Laboratory Experiments However, we had an expert ex-steam engineer in the person of George I?. Weaton, manager of the Josephtown smelter, who had had long experience with steam-jet condensers and would reiterate his belief at every opportunity that the logical and the most efficient way to condense zinc would be with a jet-type condenser. We became intrigued by the possibilities of a zinc con-

Jan 1, 1944

By I. R. Kramer

[The final paper in the diffusion symposium was given by I. R. Kramer. The author called attention to the diffusion characteristics of chromium deposited on the surface of steel by treatment with chromium chloride and alloyed with the surface layer of the steel by thermal treatment. As the data cited were previously published in the paper " Chromizing of Steel," by I. R. Kramer and Robert H. Hafner (Metals Technology, October 1942, and in the Transactions, volume 154, 1943, pages 415-420), it is unnecessary to reproduce these data here. The following paragraphs are taken from the author's presentation.— Editor.] Aside from the well-known practical application of the diffusion phenomena to carburizing and calorizing, -diffusion also finds application in adding alloying elements to the surfaces of steel parts. The chromizing of steels is a process by which the surface of a low-alloy steel may be enriched with chromium to form a highly corrosion-resistant case; This chromized case differs from an electroplated coat in that it is a diffused layer integral with the base metal and has all of the properties of a high-chromium steel. Recently a method of chromizing has been developed in Germany by Daeves, Becker and Steinberg in which gaseous chromium chloride and hydrogen are passed over the steel at temperatures of 1650° to 1800°F. The chromium chloride reacts with the iron to give chromium and iron chloride. The chromium atoms are deposited on the surface and diffuse in as the iron atoms diffuse out, forming a layer rich in chromium. The principal role of hydrogen is to remove the carbon from. the surface of the steel. Of the two mechanisms, chemical reaction and diffusion, the one operating at the slower rate will determine the rate of formation of the layer. In this case, diffusion is slower and therefore any factors influencing its rate will affect the process. The rate of diffusion is influenced by the temperature and crystal structure of the parent metal. Depth-concentration studies show that the concentration falls off gradually for a considerable distance and then drops sharply at about 13 per cent chromium, the point coincident with the boundary of the gamma loop. The influence of the composition of the base metal upon diffusion is quite important. The depth of penetration of the chromium decreases as the carbon content increases and, of more importance, the chromized layer becomes brittle and is likely to spa11 if the carbon content is too high. It appears that in order to chromize successfully the carbon must be fixed by strong carbide-forming elements such as chromium or molybdenum, which decrease the diffusion of carbon. If this is not done, the carbon will diffuse from the interior faster than the chromium can diffuse inward, thus forming a carbide barrier. The corrosion resistance of the chromized layer is high, and these steels offer some unique advantages over other corrosion-resisting coating or alloys. While chromizing is not meant to replace stainless steels, it may serve in the saving of alloying elements. The chromizing process uses soft or low alloyed steels that can be easily hot or cold formed and since the chromized layer is soft and firmly adherent, chromized parts can be subjected to cold deformation without spalling or chipping and without loss of corrosion resistance.

Jan 1, 1944

The Institute maintains a dual relationship with students: (1) an individual relationship with a Student Associate; and (2) a relationship with local organizations of students, known as Affiliated Student Societies or Student Chapters. 1. The conditions of Student Associateship are set forth in Section 9, Article I, of the Bylaws of the Institute (see page 62 and following pages). During 1934, sundry amendments were made for the purpose of improving the student relationship. Postgraduate students are now eligible; and associateship can be maintained, with the payment of the regular dues of $2 per year, for 18 months following graduation in June. With his regular dues, each Student Associate is entitled to receive during the year his choice of MINING AND METALLURGY, METALS TECHNOLOGY, MINING TECHNOLOGY, PETROLEUM TECHNOLOGY, or two "classes" of Technical

Jan 1, 1944

By E. L. Jones

THE concentration of tin in the tailing from Sullivan ore has been de-scribed by H. R. Banks, superintendent of the Sullivan concentrator, in a paper presented at the annual meeting of the B.C. Division of the Institute in October, 1941(1). The reduction of the concentrate EARLY EXPERIMENTAL WORK Experimental work on the smelting of Sullivan tin concentrate was done in Trail. Preliminary tests in the laboratory indicated that the concentrate could be successfully treated in an electric furnace. A small electro-thermic pilot plant was built and, at the same time, reduction tests were made in an oil-fired reverberatory furnace. Both types of treatment gave satisfactory results. It developed that no fluxes, other than those already in the ore and in the ash of the reducing agent (either coke or coal), were needed. By using an excess of iron, a complete recovery of the tin in the slag was obtained, but with 20 to 30 per cent iron in the tin. A counter-current treatment was thus indicated, viz., the primary slag was first treated with hard-head (iron-tin alloy) from the refining and final slag smelting, producing tin with 2 to 4 per cent Fe. This secondary slag was subsequently treated with scrap iron to produce tin-iron alloy, and a final slag low enough in tin to waste. By following this line of endeavour, a tentative flow-sheet was drawn up and a successful operation was established. Without resorting to electrolytic refining, a metal comparable in purity to standard tin was produced. Metallurgical results and operating costs were found to be very similar with an electric furnace or a fuel-fired furnace. 'However, electric furnace smelting was chosen because the furnace required was smaller, and because some doubt existed as to the cleaning of the final slag in the reverberatory furnace reduction.

Jan 1, 1944

By M. G. Arthur

This paper is a theoretical analysis of fingering of water and coning of water and gas in homogeneous sand. Investigation of this idealized case illustrates the relative magnitude of the factors involved in actual conditions. The body of the report presents equations, example calculations, and charts that facilitate solution of such problems. Derivation of the equations introduced in this paper and a discussion of previously published equations are included in the appendix. Introduction Production of water from oil wells as a result of the pressure gradients established by flow of fluids through oil-~roducing sands is a common occurrence, which influences the cost of oil production, the degree of depletion and the efficiency of expulsion of oil from naturally occurring reservoirs. Control of water production and encroachment are important both in primary and secondary phases of of exploitation in order to produce oil and gas at lowest cost and in order to achieve the greatest ultimate recovery of the oil in the reservoir. Although many actual oil reservoirs present a multitude of variables that influence fingering and coning of water and gas, an inspection of the relationship and magnitude of the forces involved in the case of a homogeneous sand may indicate satisfactory methods of controlling water production. Application of equations relating the variables may indicate the geometric type of drainage that exists in a particular reservoir or in the vicinity of a particular well. A homogeneous sand body is assumed within the portion of the reservoir influenced by the well. Two geometric types of drainage are considered theoretically. The first is water fingering into an oil sand that is relatively thin compared with the lateral extent of the sand. This sand may represent the entire oil-producing reservoir or it may represent one interval in an oil reservoir, which is separated from other producing intervals by competent lithologic barriers to flow of fluids. For the condition of complete penetration of a well in such a sand body, it may be assumed that no flow occurs across bedding planes. A mathematical relation is developed between the limit of approach of a water finger to the well without being drawn into the well and the corresponding operating pressure drawdown. The second condition considered is that of water or gas entry into an oil well as the result of coning through bedding planes. The theory and graphical solution developed by Muskat' for the limit of approach of a water or gas cone to a well, without its entry into the well, related to the corresponding maximum pressure drawdown, is reviewed and amplified, Charts are presented, which facilitate graphical solution of the problem. A method is presented for the extension of this type of graphical solution to the case where gas and water coning occurs simultaneously~

Jan 1, 1944

Abrahamson. Guy C., (S'43) Univ. of California, Berkeley. Calif. ' Abrego, Alfredo, (S'43) Texas College of Mines Metallurgy, El Paso, Texas. Adamec, Lew, (S'42) c/o Braden Copper Co., Ran¬cagua, Chile. Adams, Charles E., (S'42) Box 1527, Stockton, Calif. Adams, John W? (S'42) Asst. Petr. Engr., Vander¬ bilt Dist., Magnolia Pets. Co., Edna. Texas. Adams, Karl S., (S'43) Univ. of New Ha mpshire, Durham; N. H. Adamson, Charles R., (S'41) Univ. of Utah, Salt Lake City, Utah. Aguilar, Ruperto G., (S'43) Texas College of Mines, El Paso,. Texas. Almone, Francis M., (S'41) Univ. of Toronto, Toronto, Ont., Canada. Ainge, Ronald Farra, (S'43) Otago University, Dunedin, New Zealand. Akarun, Cevdet A., (S'44) Pennsylvania State College, State College. Pa.

Jan 1, 1944

Jan 1, 1944

By M. B. Ramachandra Rao

THE spontaneous polarization surveys dealt with in this paper were carried out near Guddadarangavvanahalli (lat. 14° I7' N.; long. 76° 24' E.) in Chitaldrug district, which forms part of the Chitaldrug schist belt. The occurrence of gold, copper, lead and antimony ores has been noticed for several years but efforts to exploit them have been unsuccessful, therefore some spontaneous polarization surveys were made in the hope of finding indications of workable ore bodies. The country examined has a rugged topography, with numerous hills on which there is little vegetation. The climate is generally dry, the average annual rainfall of the tract being about 25 in., of which 17 in. occurs during the southwest monsoon. The geological formations of the area pertain to an ancient schistose series known as the Dharwar system (Archean). Locally, the rock formations have been divided into three series1-the chloritic series (or the Chitaldrug formation), the clay series (or the G.R. formation) and the trap series (or the Jogimardi trap). The chloritic series includes a complex of altered ancient traps and volcanic agglomerates intermixed with some schists of sedimentary origin, all of which are highly metamorphosed. The lithological types of this series are mostly distinguishable as greenstone schists, calc-chloritic schists, slaty schists, ochery and calcareous micachlorite schists, with subordinate bands of secondary limestone. The clay series (G.R. formation) is made up of shaly and argillistic schists, lithomargic clays, sandstones and brecciated ferruginous quartzites. The Jogimardi trap is mostly of the nature of an epidiorite (hornblende diabase), which is distinctly intrusive in the form of large laccolithic and narrower dikelike masses. In addition to this trap, there are other minor intrusives such as the chalybitic trap, quartz porphyry and quartz reefs. The topographical and geological features of the area are noted on the map of Fig. I. The locations of some of the spontaneous polarization centers determined by the geophysical survey are indicated also. METHOD OF SURVEY AND APPARATUS EMPLOYED The spontaneous polarization surveys were carried out in the manner recommended by the Imperial Geophysical Experimental Survey.2 Preliminary reconnaissance was first carried out along a series of parallel traverse lines that were laid out over the area. The potential profiles obtained in these traverses were plotted* on a suitable scale and when any

Jan 1, 1944

By C. J. P. Ball

Prior to 1939 the bulk of the magnesium metal produced outside of the united Stater was extracted directly from the ore and ifi the United States from magnesium chloride obtained as a by-product from the treatment of natural brines. A typical brine is one containing about 0.25 to 0.75 per cent bromine, 11 to 14 per cent sodium chloride, 9 to 11 per cent calcium chloride and 3 to 10 per cent magnesium chloride. The state of Nevada was known to possess large deposits of magnesite ore (MgCOs, the carbonate of magnesium), in Gabbs Valley, near Luning, approximately 350 miles north of Boulder Dam. Deposits mined in Europe were supplying magnesite giving 97 per cent MgCOs with about I per cent each of silica, lime and oxides of iron and aluminum. parts of the Luning de-posits Were almost equally rich, and the general average was of sufficiently high grade for production of magnesium. power to the amount of 200,000 kw. was available immediately from Boulder Dam, and water from Lake Mead, and it was this combination of available power, water, and ore that led to the initial proposal to erect a magnesium reduction plant in southern Nevada to reduce the magnesite ores from Gabbs. The extraction of magnesium metal from these magnesite deposits had been considered by the I. G. Farbenindustrie of Germany as far back as 1929. Mine and Oxide Plant The mine and oxide plant of Basic Magnesium Incorporated are perched upon the oride slope of the Paradise Range, at an altitude of 5000 ft., overlooking the 30 mile desert panorama of Gabbs Valley, Nevada. , Ore Occurrence The Gabbs magnesite ores occur in a thick series of flat, westerly dipping dolomites of Upper Triassic age. The mag-"esite bodies are exposed in steep canyon "areas encircling the north and east edges of a northerly projecting tongue of a roughly elliptical stock of granodiorite, which intrudes the dolomite. The magnesite mineralization is considered to be a a of calcium by magnesium through the agency of hydro-thermal solutions associated with the intrusion of the granodiorite. The ore bodies are of very irregular shape and distribution. Incomplete evidence points to deep pipelike replacement shapes that mushroom out erratically at various elevations. A wide latitude in the degree of magnesium replacement is reflected in a variance of quality from pure magnesite to magnesitic dolomite. The, ore is a massive crystalline mag-nesite. Though some differences in characteristics occur between ore bodies, in general the ore is a medium-grained carbonate varying in color from white, through all shades of gray, to black. Recrystallized dolomite, which encloses and occurs as

Jan 1, 1944

Jan 1, 1944

By Raymond D. Sloan

Dropping from third position among the oil-producing states of the nation in 1942, Oklahoma ranked fourth in 1943 with a total output of 121,431,ooo bbl., a decline of 11.9 per cent from the previous year's total of 137,792,000 bbl. Production ranged from a maximum of 346,900 bbl. daily in February to a low of 322,800 bbl. daily in October, and at the close of the year was averaging 330,000 bbl. daily from 52,096 wells, or an average of 6.3 bbl. per well. The state's well, average at the close of 1942 amounted to 6.7 bbl. At the turn of the year, it appeared reasonable to assume that Oklahoma's producing rate would continue its downward trend during 1944 unless reversed by greater than normal discoveries. To Jan. I, 1944, Oklahoma has produced 5,188,466,-ooo bbl. of crude oil. Development and Exploration A total of 1287 wells was drilled in 1943, representing an increase of 77 wells, or 6.4 per cent over the preceding year's total of 1210. Of the wells completed, 587 (45.6 per cent) were oil wells with an average initial production of 319 bbl.; 127 (9.9 per cent) were gas wells with an average initial of 8,639,000 cu. ft.; and 573 (44.5 per cent) were dry. A total of 333 wildcats was drilled (25.9 per cent of all wells), an increase of 13 (4.1 per cent) over the 1942 total of 320. Of the*wildcats drilled, 46 (13.8 per cent) were oil wells with an average initial production of 235 bbl.; 27 (8.1 per cent) were gas wells with an average initial of 8,249,-ooo cu. ft.; and 260 (78.1 per cent) were recorded as failures. Reconditioning of wells throughout the state led to a total recompletion of 230 wells. Of these, 131 were oil wells with a combined initial production of 8360 bbl., 31 were gas wells with a total initial of 211,950,000 cu. ft., and 68 were abandoned. The 46 successful wildcats opened 33 new producing areas, one of which produced from three separate horizons, and led to the development of production in new horizons in 11 old pools. While none of the 1943 discoveries have as yet developed into what might be termed major pools, the West Moore pool, in Cleveland County, and the West Edmond pool, in Oklahoma County, are the two outstanding new areas opened to production. The West Moore pool, sec. 29, 10 N., 3 W., discovered in December 1943, was completed for an initial production of 248 bbl. of oil in 3 hr. through small tubing chokes in the second Wilcox sand from 8787 to 8800 ft. One well was drilling in this area at the close of the year. The West Edmond pool, an April discovery in sec. 32, 14 N 4 W., is producing from the Hunton lime at a depth of approximately 6950 ft., the world's deepest Hunton lime pool. To the end of the year, 15 oil wells had been completed, with no gas wells and no failures. Accumulated production to Jan. I, 1944, amounted to 474,300 bbl. of 41" gravity oil. There were 29 active operations in the field at the end of the year. The West Edmond and West Moore pool discoveries established the first commercial production west of the Granite Ridge,

Jan 1, 1944

By Richard M. Foose

FIVE miles southwest of Mt. Holly Springs, Cumberland County, Pennsylvania, the Philadelphia Clay Co. has been mining and milling a white clay since 1896; for use in white cement, as a filler in rubber, pigment and paper, in the manufacture of insecticides, and for other minor purposes. Until late in 1942, when the mine was abandoned because of labor shortage, combined underground mining and surface stripping produced approximately 30,000 tons of clay a year, of which 10,000 tons were refined in the mill. GEOLOGY Lower Cambrian Antietam quartzite and the Montalto quartzite, stratigraphically older, trend N.55°E. and make a sharp 1600-ft. anticlinal ridge of the South Mountains. The Tomstown dolomite overlies the Antietam quartzite on the southeast flank of the anticline, which is displaced near its crest by a steeply dipping oblique fault. Erosion of the less resistant Tomstown formation has resulted in a narrow valley at an elevation of 700 ft. Directly on top of the Antietam quartzite and at the base of the Tomstown formation is a zone of sandy white clay, lenticular along the strike of the formations, ranging in thickness from 10 to 300 ft. within a mile. All of the formations dip steeply to the southeast, from 65° to vertical. The clay crops out at an elevation of about 1000 feet. ORIGIN AND CHARACTER The uppermost part of the Antietam formation is sericitic and schistose at many places, and at all these places weathering is in an advanced stage. The clay is the residual product of weathering of this sericitic quartzite or sandy schist. The crude clay has the physical aspect of a sandy kaolin, but there are large areas in the clay formation that are low in free silica, and commonly the 30 ft. adjacent to the Antietam quartzite is notably free of silica. The overlying Tomstown dolomite has been weathered almost completely to a mixed yellow and brown clay, which carries a zone of nodular and chunky limonite and manganese ore, 4 to 12 ft. thick, about l00 ft. from the contact with the white clay. In mining, this zone is an important "marker," indicating where the white clay may be expected in an advancing tunnel. The contact of the white clay formation with the yellow and brown clay of the Tomstown formation is relatively sharp, although the line of contact is irregular and therefore responsible for the lenticular character of the white clay formation. Following is an analysis of the refined clay containing less than one per cent of moisture when dried at 212°F.: Si02, 67.05 per cent; A1203, 22.27; Fe203, 0.40; CaO, 0.00; Ti02, 1.05; MgO, 0.52; Na20, 0.04; K20, 0.88; ignition loss, 7.65; total, 99.86.

Jan 1, 1944

The present paper records a chapter in the history of the development of an electrolytic manganese industry in the United States.l A relatively large pilot plant at Boulder City, Nev., for the production of electrolytic manganese was conceived as part of the national defense program to make this country independent of foreign importation of manganese ore. The first authorization, in November 1940, however, was for a plant of only several hundred pounds capacity. Improvements in process and subsequent additions to some sections authorized by subsequent appropriations have enabled the plant to produce as much as 2000 lb. of manganese a day for substantial periods of time. Since in pilot-plant operation frequent changes are made in the flowsheet, the electrolytic manganese plant was constructed so that equipment could be rearranged with a minimum of expense and time. Several different kinds of the various ¦ types of equipment were installed for many of the operations, so that the one most suitable for the process might be chosen. Pilot-plant operations were begun in November 1941 and have been continuous except for brief shutdowns for installation of new equipment. More than one-half million pounds of manganese have been produced. The improvements in process, selection of equipment, and operational procedure developed are recorded here. Development of the Process The work of early investigators on the electrolysis of manganese solutions has been reviewed by Shelton. Until the method of continuous production of manganese by electrolysis was perfected by SheltonZm4 and coworkers, no practical procedure had been devised. The method as originally developed by the Bureau of Mines will be described here only briefly. The manganese dioxide ore was reduced in a rotating kiln-type furnace at 650°C. in an atmosphere of "city" gas. The calcine was leached with spent electrolyte and enough sulphuric acid to produce a neutral leach solutioil containing 2 5 grams manganese per liter as manganese sulphate and zoo grams per liter of ammonium sulphate. Arsenic was removed from the solution by the addition of 0.0j gram iron per liter as ferrous sulphate followed by oxidation with manganese dioxide, and aeration, which precipitated the iron as ferric hydroxide. The solution, free from iron

Jan 1, 1944

By E. H. Rose

THE question is often pondered whether the flotation process is still an art or has become a science. The fact is that flotation is a science in so many variables that only art can blend them. It is demonstrable that no less than one hundred variables are involved in any flotation operation, most of them immeasurable on a routine basis. The behavior of every one of them is always governed by orderly and unchanging law, as no man can doubt. There is nothing truly indefinite about that behavior; the only indefiniteness is in our knowledge of it, either in general or from hour to hour in the circuit. In dealing with a simultaneous equation in, say, one hundred variables, all not only affecting the outcome to some degree but many influencing each other as well, it is small wonder that the mineral-dressing profession presents a case history of debate and controversial opinion. The statement of the subject of this symposium-a symposium on flotation machines-seems to delimit and define the matters to be considered and at least the general nature of the conclusions sought. Nevertheless, in such a meeting it is not possible to meditate upon all the variables that do in one way or another affect performance of flotation machines. To attempt it would be much like trying to operate a hundred-ring circus. Perverse variables being what they are, one could expect the elephant in ring 36 to squirt a trunkful of water at the tightrope performer in ring 37 to ruin that artist's act, just as our learning to depress pyrite in the early 1920's ruined the act of the formerly faithful old Callows. HONEST DISAGREEMENTS Selective flotation dates from 1922 or 1923, when several plants established their regular flotation operations on a selective basis. Since then, two decades of efforr have gone into the development of better and better flotation machines. Many have come and gone. The competition has simmered down to perhaps a dozen machines, each one of which is staunchly defended by some operators as being the best for their particular jobs, and as scornfully dismissed by at least a few others elsewhere as being positively the poorest for theirs. These disagreements are honest disagreements, honestly arrived at after plenty of sweat. In many a flotation plant, one machine has been tried out against another under conditions as fair as they could possibly be made. Sometimes the results are on a par but more often one machine shows a consistent and unmistakable margin of superiority over the other. In equally honest and enlightened tests, machine A may win over machine B in one place, and machine B over machine A by as great a margin in another. This paper purposes to identify some of the more prominent reasons why this is so,

Jan 1, 1944

By P. W. Ramsey, E. J. Boyle, E. A. Anderson

Only a few zinc-rich alloys are in commercial use today, and these depend largely upon solid solution effects for their desirable properties. Typical examples are rolled alloys containing about 1 Per cent of copper, with Or without additions of elements such as magnesium, and die-casting alloys containing about 4 Per cent of aluminum with small amounts of magnesium and sometimes copper." A number of elements are capable of forming alloys with zinc, Which do not enter into solid solution except in limited degree. The Present Paper considers One such system, zinc-titanium, in which alloys having potentially useful properties in the rolled form were found. Zinc-titanium System The zinc-rich portion of the zinc-titanium diagram, as determined by standard methods in this laboratory,3 is shown in Fig. I. The portion of the diagram of significance in the present work extends from 0 to about 0.5 per cent titanium. Gebhardt4 places the eutectic at 0.45 per cent, but the evidence in favor 01 the composition given in Fig. I is considerable. The solid solubility of titanium in zinc is very low indeed and possibly places these alloys in a somewhat different category from the commercial alloys previously mentioned. Alloy Preparation All of the alloys used in this work were prepared with titanium metal of 98.9 per cent purity. In most cases high-purity zinc (99.99 per cent) was used but sufficient work was done later to show that zinc of about high-grade composition would yield approximately equal results. Best practice in alloy manufacture seemed to be to prepare a zinc-titanium hardener by adding about 4 per cent of titanium metal to molten zinc and holding under a boric acid cover, with frequent stirrings, at 750°C, until the titanium had dissolved. The desired titanium content could readily be obtained in the final alloy by adding the calculated amount 01 this hardener. The alloys proved to be quite stable in composition, unless overheated, and, with reasonable temperature control, required no cover or flux to prevent loss of titanium content by oxidatioll, Hot-rollig Tests Three alloys containing, by analysis, 0.05, 0.12, and 0.23 per cent titanium were selected for preliminary study. Slab cross sections a a marked grain refinement* (Fig. 2) in the two alloys of highest titanium content. Cast unalloyed zinc has a columnar grain structure similar to that shown for the alloy of lowest titanium content but without the scatter of small equiaxed grains at the center.

Jan 1, 1944

By Paul T. Allsman, E. W. Newman

TRENCHING, sampling, and core drilling in Stillwater and Sweetgrass Counties, Mont., by the Bureau of Mines have delimited over 5,000,000 tons of chromite ore containing more than 20 per cent chromic oxide. The Benbow and Mouat-Sampson mines have been developed and are fully equipped for mining and milling 500 tons and 2000 tons a day, respectively.

Jan 1, 1944

Jan 1, 1944

By C. O. Tarr, G. V. Smith, R. F. Miller

Metallurgists have long recognized that the Fe3C type of carbide is not a stable phase in steel and that, given sufficient time, it will decompose with formation of graphite, at least at temperatures below about 205o°F.l This slow graphitization has never been of much concern to users of hypoeutectoid steels, for in such steels it occurs only during prolonged exposure at elevated temperature. In I935, Kinzel and Moore2 reported complete graphitization of the carbide of a 0. I5 per cent carbon steel that had been in service for about 26,000 hr. at a temperature of about IIOO° to 12oo°F. In discussing this paper, both Mathews and Sauveur reported graphitization of slightly hypereutectoid steels. In an extensive investigation of graphitization of high-purity iron-carbon alloys, Wells1 produced graphite at 7oo°C. (I29o°F.) in an alloy containing as little as 0.13 per cent carbon, and showed that graphite may precipitate either directly from austenite or from decomposition of Fe3C, also that the rate of graphitization tends to increase with increase of temperature, at least up to a certain point, and with the presence of graphite nuclei. Jenkins, Mellor and Jenkinson,3 studying the structural changes in carbon steels ranging from 0.17 to 1.14 per cent carbon during stress-rupture tests at elevated temperature, observed graphite in an aluminum-killed 0.40 per cent carbon steel after fracture in 4340 hr. under a stress of 17,900 lb. per sq. in. at 840°F. and in many of the steels after stress-rupture test at 12oo°F. Unstressed samples of 0.60, 0.86 and I.I4 per cent carbon steels graphitized almost completely in 360 hr. at I200°F., while samples of 0.90 and 1.10 per cent carbon steels were somewhat graphitized, and steels containing 0.24, 0.40 and 0.57 per cent carbon showed no sign of graphite. Their results indicate that graphite precipitates the more readily the higher the carbon content, though this tendency is influenced to some extent by deoxidation practice, and that graphitization is accelerated by plastic deformation. In a recent study of the graphitization of 0.4 and 0.6 per cent carbon steel strip, made by M. A. Hughes,4 it was found that at I2oo°F. graphite appeared after 72 hr. in aluminum-killed but not in silicon-killed steel, and that the rate of graphitization was increased by slow cooling from I6oo°F. and by cold-working prior to annealing. In creep tests of normalized 0.15 per cent carbon steel killed with 2.5 Ib. of aluminum per ton, at the U. S. Steel Corporation laboratory at Kearny, spheroidization and some graphitization were found after 3000 hr. at Iooo°F. under a stress as low as 1500 lb. per sq. inch. .

Jan 1, 1944