By D. D. Gertenbach

"The successful commercialization of a pressure oxidation (POX) process for recovering metal values, including gold, copper, zinc, nickel and molybdenum, is the result of a carefully planned development program. The initial task involves developing one or more conceptual flowsheets, including the POX autoclave and downstream purification and recovery steps. A laboratory program is completed to determine the technical viability of the flowsheets, define the operating parameters for each step and provide information for an initial economic assessment of the process. The process is then confirmed during a continuous pilot plant program, providing engineering design data and other information for the commercial design. A well-thought-out development program has been shown to be critical for reducing the risk of commercializing POX processes. Experiences developing POX processes for refractory gold ores and copper concentrates are briefly discussed. IntroductionPressure oxidation (POX) has become a common commercial operation for processing sulfide-bearing feedstocks. These feedstocks include gold ores and concentrates; copper concentrates; nickel concentrates and mattes; zinc concentrates; and molybdenum concentrates. Drivers for the development and commercialization of POX processes include:• The high cost for pyrometallurgical processing of sulfide ores, much of which is attributed to environmental controls.• The motivation to implement safe and more environmentally attractive alternatives for sulfide ores.• The need to process increasingly difficult ores with complex mineralogy.• Improvements made over the last 25 years in POX equipment design and experience operating commercial POX plants.Although the capital and operating costs for commercial POX processing can be high, this technology is capable of rapid oxidation of most sulfides and arsenic minerals in the feed, with little noxious gases and environmentally stable iron arsenate and other iron compounds in the POX residue (Marsden and House, 2006).In POX operations, sulfides are oxidized to either sulfates or elemental sulfur in an autoclave at elevated temperature and pressure with oxygen gas. An example is the overall oxidation reactions of chalcopyrite when sufficient oxygen is present, shown in the following reactions:"

Jan 1, 2016

By M. SIDDARAJU, Rameshwar Sah, Satendra Kumar, Arvind Jaiswal

The study explores a novel process to sinter porous iron ore with improved productivity and quality. The iron ore is pre-processed with calcined lime to temporarily close pores, preventing water absorption during granulation. This enhances reaction kinetics and early slag formation during sintering, resulting in significant improvements in sinter productivity, product yield, and cold strength property.

Feb 28, 2022

By George D. Haley

This report will be given in two sections. The first sec¬tion outlines techniques and equipment to form almond shaped fluorspar briquettes by means of briquet presses, and the second section outlines techniques of the balling disc. PART I - BRIQUET PRESSES Fluorspar has been briquetted for a number of years and the so called "peach pit" briquet is known to many steelmen. Present production is estimated at over 100,000 tons annually. Slide 1 shows an assortment of various sizes and shapes of briquettes. It is possible to form fluorspar into almost any configuration of briquet. For safety on the melting floor, pillow type briquets are preferred. Ease of mechanical handling and durability of the product are facil¬itated by an almond shape. The dimensions of the almond can vary from 1-in. to 1-1/2-in. in length, from 13/16-in. to 1-in. in width and from 1/2-in. to 1-in. in thickness. The type of equipment to pro¬duce almond shaped fluorspar briquettes is shown in Slide 2. Here we have a Komarek-Greaves and Company 300 ton briquettor equipped with almond rolls. This machine is capable of producing fluorspar briquettes at a rats of 30 tons per hour with power consumption of 35 hp per ton par hour.

Jan 1, 1969

THE BULOLO gold-dredging operations were described at some length by Frank W. Griffin at the Oct. 11 meeting of the San Francisco Section. This enterprise is on the island of New Guinea, about 1800 miles north of Sydney, Australia. The area in which the present placers exist originally was German territory but later the location was taken over by Australians. Gold was discovered in 1923 by prospectors who required 8 to 9 days to pack into the country over severe mountain trails. In 1926 a rich discovery was made on Edie Creek and in 1927 the deposit on the Bulolo River was discovered.

Jan 1, 1932

By Liu Liching, Yan Hongjiu

"In China, the electromagnetic induction initiating system f or blasting engineering has been greatly developed in recent years. With this system, the total number of detonators that may be blasted in each round has been increased from 420 to 940 as a result of the invention of a powerful exploder, and the length of leg wires of a detonator has reached 12 metres. These developments make the new system suitable for blasting engineering of medium scale. Another attractive feature of this system is a set of testing instruments which have been invented that enable a final check of the system to be made before firing as in normal electric blasting. This paper reports on these developments.IntroductionThe initiating system for blasting explosives is one of the key factors to the success of blasting engineering, along with the progress of explosives and blasting technology. Today, we have initiating systems which may be divided into two groups: electric and non-electric. The earliest initiating system was non-electric. Many mines, as well as many projects where rock excavation was involved, were blasting non-electrically before the new nonelectric initiating system came into use in the 1970s. Electric and non-electric initiating systems are the two main initiating systems which are now being widely used, each having its advantages and disadvantages. In electric blasting, the blasting supplies and the blasting circuit can be checked before it is used or fired and, therefore, is regarded to be more reliable. In many large-scale blasting engineering where reliability of the initiation is of great concern, a checkable initiating system is preferable. The electric initiating system is not considered to be as safe as the non-electric initiating system due to its inability to choose proper ignition energy. Therefore, a non-electrical initiating system would be preferable where a hazard of stray currents or static electric energy exists. At this stage of development, one would say it would be advantageous to develop a new initiating system."

Jan 1, 1988

By Brad Sampson

Project Ownership ?Discovery Metals Limited ?ASX (DML), BSX (DML), AIM (DME) ?Market Cap AUD 195M ?Key assets ?Boseto Cu ?Dikoloti Ni The Boseto Copper Project ?Location ?Setting ?History ?Status ?Future

May 1, 2010

By Joseph Indeck, Seokbin Lim, Andrew Thompson

In the design of explosively driven penetration devices, understanding the impact conditions between the explosively propelled penetrator and the target is one of the most important steps in optimizing the performance of the device. These impact conditions are especially prevalent when a shaped charge jet impacts concrete, which is not an ideal target material. The specific impact conditions, including but not limited to the impact angle and jet properties, create a great deal of variability that affects the performance and penetration of the shaped charge. The large amount of impurities and voids in concrete, along with its heterogeneous nature and the general strength characteristics, make concrete a non-ideal material for shaped charge jet penetration. These material characteristics lead to a highly non-linear deformation behavior of the concrete target during a hyper-velocity impact.

Jan 1, 2011

By Anand Raman, Steve Dixon

"Industry practice for defining acid consumption is based on column tests. Freeport-McMoRan (FCX) has adopted a practice of leach operation using a defined pH or gpl acid in the raffinate based on the column test program. The acid consumption can be easily calculated using the leach operating parameters of SX-EW efficiency, lift height, bulk density, irrigation rate, primary leach cycle time, acid cure dose and acid concentration in the raffinate. The column leach test results and a column to heap efficiency factor are used to define the copper extraction. The maximum acid consumption will occur when zero acid is contained in the raffinate. The term Net Extracted Value (NEV) is to define the maximum extracted value relative to acid consumed.This paper presents the operating logic and method used to calculate acid consumption based on column tests and operating parameters.INTRODUCTIONIndustry practice for defining acid consumption is based on column tests. This may result in lower economic value if the tests are not designed to account for operating variables. A test program is described to assist in defining lift height and the influence of gangue on solution chemistry. A simple spreadsheet is presented that will use the leach operating parameters of SXEW efficiency, lift height, bulk density, irrigation rate, primary leach cycle time, acid cure dose and acid concentration in the raffinate to calculate the acid consumption for a proposed operation.A review of current leach operations solution chemistry will help to define acid consumption. This is recommended for all current leach operations.DISCUSSIONThe current practice at Freeport-McMoRan (FCX) is the use of column test results to define operating parameters. The monitoring of operational solution chemistry and copper production addresses any changes needed in operational parameters. This practice maximizes the value extracted from each tonne of ore leached."

Jan 1, 2008

By A. J. Hynes, Lutes. G. G., Ravenelle. J. -F.

"The Anomaly A area of the Clarence Stream gold deposits in southwestern New Brunswick contains mineralized structures that bear geometrical relationships to regional folding events. The four mineralized zones of Anomaly A (AD, MW, 93, and Murphy) are hosted by turbiditic graywacke, quartzose wacke, siltstone, and argillite sequences of the Kendall Mountain Formation. A regional scale structural analysis reflects at least four deformational events, three of which appear to control the folded geometry of Anomaly A (D2, D3, and D4). F2 and F3 folds are coaxial and are refolded into a dome and basin geometry by F4 folds. The mineralized zones are subparallel to axial surfaces of F2 folds. Structural analysis of a mineralized zone exposed at surface indicates that gold mineralization is hosted by a quartz-vein system that comprises veins generated during both D2 and D3. Threedimensional representations of Anomaly A created using drill-core data and ®GoCAD suggest that the quartz-vein system was emplaced in fault structures during D2 as well as within brecciated dilation zones during D3. Three of the four zones that make up Anomaly A have F2 hinge surfaces that can be linked through a geometry compatible with the style of F3 and F4 folds. The apparent continuity of these three zones indicates the potential for kilometer-scale mineralized structures at Anomaly A. Le secteur de l’Anomalie A du gisement aurifère Clarence Stream contient des zones minéralisées qui montrent des relations géométriques avec les épisodes de déformation régionale. Les quatre zones minéralisées de l’Anomalie A (AD, MW, 93, Murphy) sont comprises dans une séquence turbiditique composée de grauwacke, de wacke quartzitique, de siltstone, et d’argilite appartenant à la Formation de Kendall Mountain. Des quatre épisodes de déformation étudiés par l’entremise de cartographie structurale, trois semblent contrôler la géométrie de l’Anomalie A (D2, D3, et D4). Les plis P2 et P3 sont coaxiaux et sont replissés en dômes et bassins par les plis P4. Les zones minéralisées sont subparallèles aux plans axiaux des plis P2. Une analyse structurale effectuée sur une zone minéralisée exposée à la surface indique que la minéralisation aurifère est localisée dans un système de veines de quartz qui contient des veines générées durant D2 et D3. Des représentations en trois-dimensions créées avec le programme informatique ®GoCAD à partir de données de forages suggèrent que le système de veines est localisé dans des zones de failles D2 ainsi que dans des zones de dilatation associées avec D3. Trois des quatre zones qui forment l’Anomalie A possèdent des plans axiaux P2 qui peuvent être liés par l’entremise d’une géométrie qui respecte le style des plis P3 et P4. La continuité apparente de ces trois zones indique qu’une structure minéralisée pourrait s’étendre sur plusieurs kilomètres dans le secteur de l’Anomalie A."

Jan 1, 2008

By Carl C. Nesbitt

A process has been developed to recover and recycle metals from wastes of brass foundries which contain copper, zinc and lead in various quantities. Tests were conducted to evaluate several leachants, including sulfuric acid, ammonia, hydrochloric acid, cyanide and acetic acid, and to determine the optimum leaching conditions, such as air flow rate, initial copper ion concentration, temperature, and agitation strength. Sulfuric acid containing copper sulfate with dissolved oxygen is the most successful leachant. More than 99% of the copper and zinc originally present in the waste was dissolved, while only 0.5% of the lead entered the solution after 14 hours of leaching. The leaching mechanisms of copper, zinc, and lead are proposed. The copper and zinc can be recovered from the solution by electrolytic processing. The unleached residue may be converted to a lead carbonate which can be converted to litharge at 400-450°C and to massicot at temperature above 500°C by calcination.

Jan 1, 1995

By Miguel Tapia, al et, Milenko Gonzalez, Sergio Giglio

El Encierro es un yacimiento de tipo pórfido Cu-Au del Mioceno superior ubicado en la zona intermedia entre las franjas de El Indio y Maricunga, en el norte de Chile. Está emplazado bajo un extenso lithocap que presenta evidencias de mineralización de tipo epitermal de alta sulfuración y que fue explorado entre 1987 y 2010 por varias empresas. En 2016, AMSA firmó un contrato de opción de compra con Barrick con el objeto de comprobar la existencia de un sistema tipo porfídico en profundidad con potencial económico. Cuatro campañas de perforación desarrolladas entre 2015 y 2020 permitieron probar que debajo del lithocap se encuentra un sistema porfídico de Cu-Au con leyes que se incrementan por debajo de la cota 3,000 m.

May 10, 2023

New Bio-Adsorber with Activated Carbon and Nano Tube Carbon for Separation of Nickel and Cadmium

Sep 13, 2010

By N van Aarde, B A. Moore, S van der Merwe

Frequently materials handling operations are compromised by transfer chute problems ranging from high wear rates, blockages and ineffective loading of the downstream conveyor. This paper will present the design flow implemented to overcome problems in two case studies utilising discrete element modelling incorporating material characterisation.Material testing is relevant in achieving a valid discrete element method (DEM) simulation model and subsequently a valuable design tool for transfer chute assessment and design. It is well recognised that in the current growth and demand for mineral resources, leading to ever increasing conveyor capacities associated with export terminals and mineral processing facilities that transfer chutes are a key focus point. The successful performance of the transfer chute is also dependent on operating with a ærobust rangeÆ of material flowability and handling characteristics. This requirement is crucial in accommodating mineral ores from developing resources, which are often more friable and stickier than in past decades.This paper will include details of chute installations associated with iron ore and coking coal, from the DEM simulations through to the performance of the installed and commissioned plant.CITATION:Moore, B A, van der Merwe, S and van Aarde, N, 2013. Implementation of advanced transfer chute designs, in Proceedings Iron Ore 2013 , pp 445-450 (The Australasian Institute of Mining and Metallurgy: Melbourne).

Aug 12, 2013

By David Weiss

There is significant interest in magnesium alloy castings because of their low density and high strength-to-weight ratio. Lightweight, structural materials are in demand for aerospace components, hand tools, electronics enclosures and have found increased use in automobiles. Increased use of magnesium will depend on the resolution of a number of materials issues and development of more robust and economical casting processes. Most magnesium components are produced via high-pressure die-casting. High levels of porosity generally prevent die-castings from being used for structural applications. Structural castings are usually produced using sand casting, a relatively expensive casting process. Some work has been done on development of lower cost structural casting processes, such as lost foam casting, permanent mold casting or low-pressure casting. New programs are also emphasizing improvements to the die casting process. Research and cost reduction needs are discussed with respect to current programs and future components.

Jan 1, 2006

By Bai-ru Xia, Cang-qin Jia, Qi-wu Huang

Limit Analysis Theorems has revealed to be a powerful tool for the development of numerical models aiming the determination of the load bearing capacity of structures reached by plastic collapse. This work presents a numerical formulation for the computation of strict upper bounds of the collapse loads of rigid-perfectly plastic mechanical systems, derived within the kinematical theorem framework. A key advance of this present method is that the problem is described only in terms of nodes and discontinuities connecting those nodes rather than element or bodies. The alternative approximation procedure to the traditional finite element method might involve discretization of a given body using a suitably large number of nodes laid out on a grid, with the failure mechanism comprising the most critical subset of potential discontinuities interconnecting these nodes. Potential discontinuities which interlink nodes laid out across the problem domain are permitted to crossover one another, giving a much wider search space than when such discontinuities are located only at the edges of finite elements of fixed topology. Highly efficient interior point method solvers can be employed when certain popular failure criteria are specified (e.g. Mohr-Coulomb). By adopting this processing approach it is possible to solve very large problems which normally exceed the memory capacities of a single computer. The developed numerical tool reveals to be robust and versatile, able to solve a wide range of 2D problems. Velocity singularities are automatically identified and visual interpretation of the output is straightforward. Several numerical examples including rock slope are studied by the new method, and the results are very close to those calculated by using analytical method and FEM.

Jan 1, 2015

By S. Floreen

Seven iron alloys ranging from 5 to 12 pct Ni and 5 to 14 pct Cr were studied. All alloys transformed to bcc massive martensites. Tempering increased the strengths , probably because of relief of residual stresses generated by the martensite transformation. The major strengthening mechanism appeared to be solid-solution hardening by nickel and chromium. Studies of the work-hardening behaviw, of the effects of prior austenite grain size, and of the effects of changing strain rate and test temperature gaue results very similar to iron or low-alloy steels. Increasing nickel contents markedly improved the toughness at subzero temperatures. Studies of the flow properties did not, however, indicate the reason for the beneficial effect of nickel on toughness. The marine atmosphere corrosion resistance of the alloys was improved primarily by chromium additions, but increasing nickel contents were also beneficial at low levels of chromium. J\ number of maraging and PH stainless steels are strengthened by precipitation hardening in a low-carbon Fe-Ni-Cr martensite matrix. To some extent the resultant properties of these steels must depend upon the properties of this matrix. The present study therefore was conducted to evaluate the transformation characteristics and mechanical properties of a series of Fe-Ni-Cr martensitic ternary alloys. A limited evaluation of the corrosion resistance of the alloys in marine atmosphere was also made. ALLOY PREPARATION Seven 100-lb air induction melts were prepared using electrolytic iron, nickel, and chromium metal additions. The initial Fe-Ni charge also contained 0.05 wt pct graphite to produce a carbon boil during melt down. After melting of the base charge, the heats were refined with 0.1 wt pct additions of manganese, silicon, aluminum and titanium and poured into cast-iron molds. The ingots were homogenized at 1250°C and uni-directionally hot-rolled to 2-in. plate. They were then homogenized another hour at 1250°C, and unidirection-ally hot-rolled to %-in. plate at a finishing temperature of approximately 1050°C. The compositions of the heats are given in Table I. Two additional heats were prepared as 40-lb vacuum-induction melts using electrolytic iron, nickel, and chromium metals, and commercially pure molybdenum chips. A carbon boil, and 0.1 wt pct additions of aluminum and titanium were again employed, but manganese and silicon were not added. The heats were converted to %-in. plate using the procedure described above. The compositions of these heats are included in Table I.

Jan 1, 1967

By A. J. Shaler, J. Prieto Isaza, John Wulff

TANTALUM metal has a number of unique properties which give it widespread application in modern technology and in research. In electronic apparatus involving high temperatures in vacuo some of the refractory metals become brittle. Tantalum retains its ductility at elevated temperatures, and this property, together with its low vapor pressure and its ability to absorb gases, make it important in this field. Its chemical inertness in the presence of acids, halogens, and other corrosive media, makes it useful in chemical apparatus and in neuro and orthopedic surgical applications. As an addition to tungsten carbide in steel-cutting grades of cemented-carbide tools, the carbides of tantalum and of its sister element columbium have found considerable use. The present-day method1 of manufacturing tantalum is to sinter a powder compact of the metal in vacuo. Because tantalum- columbium alloys are difficult to work and since tantalum ores almost always contain columbium, the two metals must be separated chemically, the products of the separation being generally in the form of potassium tantalum fluoride and potassium columbium oxyfluoride. These salts are used in fused-salt electrolytic baths from which coarse metallic powder is deposited as a sponge at the cathode. Finer powder can be made from the coarse product or from tantalum scrap by first submitting it to an embrittling heat treatment in hydrogen and then crushing it. The fine hydrogen- containing powder may subsequently be degassed in vacuo at a high temperature. Prompted by the success of others2,3 in the magnesium reduction of titanium and zirconium halides, one of the authors under- took4 an investigation of the thermo- chemistry of the reaction between solid magnesium and gaseous tantalum penta-chloride, a subject which had not previously been studied. He found that the heat of formation of tantalum pentachloride is approximately 364,250 cal per mol at temperatures lower than the melting point of magnesium. A value of 83 units was found for the standard entropy at these temperatures. With these values, it was shown that magnesium and tantalum pentachloride are capable of reacting exothermically at temperatures less than the melting point of magnesium, and that no great violence is to be expected when these substances are heated together. The exothermic nature of the reaction indicated that the process should be efficient and should not require much externally applied energy. Tantalum pentachloride is not commonlv made commercially, and any process using it therefore involves the subsidiary problem of producing and handling this substance. A series of experiments was carried out in which dried chlorine saturated with carbon tetrachloride was passed over heated tantalum, either in the metallic state or combined

Jan 1, 1947

By W. Petruk

Imaging is a fundamental requirement when characterizing minerals, ores and related products. Images are used for presentation, texture analysis, characterization, image analysis, identification, etc. The image mode that is utilized is dependent upon the application, mineral properties and available instruments. Different instruments produce images that display different features; in order of increasing complexity they are: hand specimens, a non-polarizing microscope, polarizing optical microscope, scanning electron microscope (SEM), low vacuum SEM, microprobe, secondary ion mass spectrometer, staining, cathodoluminescence, tomography and others. Image analysis uses images produced with either an optical microscope or a SEM, but the SEM images are superior in this application.

Jan 1, 2001

By R. Boom, L. Holappa

In the present paper, microstructure changes of solid-state reduction of industrial chromite pellets and lumpy ore were investigated with SEM/EPMA. To simulate the reactions in the packed bed zone of the Submerged Arc Furnace (SAF), carbon monoxide was used as the reducing agent, with the presence of graphite in proximity to chromite. The experiments were carried out at 1500 °C. Scanning electron microscopy was used to observe and analyse the structure and composition changes of the chromite samples. It was found that reduction of lumpy ore generally took place slower than that of pellet. In all samples, chromite reduction proceeded faster in the outer part of the sample than in the centre part. The reaction mechanism is discussed on the basis of experimental results and earlier investigations. The possibilities to optimize the FeCr production process are also discussed.

Jan 1, 2007

By S. J. Parry, D. M. Evans, D. L. Buchanan

The reef is a PGE-enriched sulphidic zone, stratigraphically associated with and overlapping the C1d chromitite layer, that was formed by magmatic processes at the 1e-1d subunit boundary. Two distinct patterns of PGE enrichment are related to the presence or absence of Cr2O3 oversaturation during sulphide liquation that occurred during a complex sequence of changes at this boundary

Apr 1, 1996