By P. W. Ramsey, E. J. Boyle, E. A. Anderson

Only a few zinc-rich alloys are in commercial use today, and these depend largely upon solid solution effects for their desirable properties. Typical examples are rolled alloys containing about 1 Per cent of copper, with Or without additions of elements such as magnesium, and die-casting alloys containing about 4 Per cent of aluminum with small amounts of magnesium and sometimes copper." A number of elements are capable of forming alloys with zinc, Which do not enter into solid solution except in limited degree. The Present Paper considers One such system, zinc-titanium, in which alloys having potentially useful properties in the rolled form were found. Zinc-titanium System The zinc-rich portion of the zinc-titanium diagram, as determined by standard methods in this laboratory,3 is shown in Fig. I. The portion of the diagram of significance in the present work extends from 0 to about 0.5 per cent titanium. Gebhardt4 places the eutectic at 0.45 per cent, but the evidence in favor 01 the composition given in Fig. I is considerable. The solid solubility of titanium in zinc is very low indeed and possibly places these alloys in a somewhat different category from the commercial alloys previously mentioned. Alloy Preparation All of the alloys used in this work were prepared with titanium metal of 98.9 per cent purity. In most cases high-purity zinc (99.99 per cent) was used but sufficient work was done later to show that zinc of about high-grade composition would yield approximately equal results. Best practice in alloy manufacture seemed to be to prepare a zinc-titanium hardener by adding about 4 per cent of titanium metal to molten zinc and holding under a boric acid cover, with frequent stirrings, at 750°C, until the titanium had dissolved. The desired titanium content could readily be obtained in the final alloy by adding the calculated amount 01 this hardener. The alloys proved to be quite stable in composition, unless overheated, and, with reasonable temperature control, required no cover or flux to prevent loss of titanium content by oxidatioll, Hot-rollig Tests Three alloys containing, by analysis, 0.05, 0.12, and 0.23 per cent titanium were selected for preliminary study. Slab cross sections a a marked grain refinement* (Fig. 2) in the two alloys of highest titanium content. Cast unalloyed zinc has a columnar grain structure similar to that shown for the alloy of lowest titanium content but without the scatter of small equiaxed grains at the center.

Jan 1, 1944

By James K. Stanley

When a plastically deformed mctal is heated to a certain temperature, it undergoes a complete change in microstructure, the consequence of which is a marked alteration of mechanical properties such as hardness, strength and ductility. This change in microstructure occurs by re-crystallization and is a process involving the formation and growth of strain-free nuclei in the deformed matrix. These nuclei continue to form with time and grow until a new grain structure replaces the cold-worked structure. The formation of the nuclei in the deformed sheet of I per cent silicon ferrite is illustrated in Fig. I. If a recrystallization is conducted iso-thermally, a nleasurement of the fraction of the matrix recrystallized plotted against time leads to an isothermal recrystallization curve, first established in 1942.1 Such recrystallization curves are shown in Fig. 4. These curves show that the recrystallization of a cold-worked metal is best considered as a rate process rather than a time independent process such as is suggcsted by the improperly named and misleading recrystallization diagrams involving deformation, temperature, and grain size.2-5 Any study of the rate of recrystallization resolves itself into a study of the component rates of nucleation and growth. The previous paper1 provided an account of the determination of the rates of nucleation; N, the number of nuclei formed per unit time per unit of unre-crystallized area, and growth, G, the radial growth in unit time, in the recrystallization of silicon ferrite (I per cent Si). A method was developed to furnish experimental data for evaluating the effect of the recrystallization variables on N and G. The mathematical analysis for the derivation of the isothermal recrystallization curve was developed for a two-dimensional case (in thin sheets where the diameter of the recrystallized grain is greater than the sheet thickness). The present paper is a continuation of the study of recrystallization of I per cent silicon ferrite begun in 1942.1 In this work the effect of the factors deformation, temperature, grain size, composition, and recovery is studied with respect to the rates of liucleation and grouth. At the same time it is shown how the cooperation of N and G affects the isothermal recrystallization curve. The study of these variables on N and G has a definite bearing on the mechanism of recrystallization and should lay a foundation for a rational theory on the subject. Procedure The procedure used in these experiments was essentially the same as that described previously but in certain details some changes were made in the interests of speed. With few exceptions, the procedure is the same for the study of all the variables. Where the procedure is different from standard manipulations attention is called to this fact.

Jan 1, 1945

By d&apos, John C. Entremont

Pure iron was inductively melted in small refractory crucibles and optical pyrometer and immersion thermocouple readings were simultmzeously taken. The resulting emissivities of the liquid iron surface obtained were found to be greatly affected by both the gaseous atmosphere and geometrical changes in the physical setup. Quantitative values for these effects are indicated. FOR many applications in both the laboratory and plant, optical pyrometry is still the best means of measuring temperatures in the incandescent range. A prerequisite in evaluating the correct temperature is a good value of the emissivity of the surface. To obtain the emissivity from the tabulated values of the literature can be very confusing and often far from correct. There are many reasons for these difficulties, and it is not within the scope of this paper either to enumerate or to discuss them all. Its purpose is to show quantitatively how several factors affect the apparent emissivities obtained from experimental measurements on liquid iron surfaces. The black body is the reference state for the quantitative values of emissivities and is defined1 as a body which absorbs all radiation incident on it, reflecting none; such a surface emits more radiation per unit area per unit time than any surface which reflects any radiation, and is given a value of unit emissivity. All bodies having reflective power thus have emissivities less than unity and are considered nonblack or grey bodies. The ratio of the radiant energy emitted by the flat, nonblack surface to that of a perfectly black surface of equal area and temperature is the emissivity of the surface. The above definitions are applied to flat, polished, opaque surfaces, very seldom encountered in actual measurements, and for this reason many authors have suggested that the word "emittance" be used for real bodies rather than emissivity. The emittance has reference to the material and its configuration rather than to its properties in the idealized state. Recent observations of molten iron in a small refractory crucible indicate that not only the configuration of its surface but the geometrical arrangement of its surrounding and the nature of the surrounding atmosphere have a pronounced effect on the emittance. Neglect of changes in such conditions may lead to errors as large as 40°C at 1600°C. Thus it is suggested that the term "apparent emissivity" be used and that it be recognized that its value pertains to a particular experimental arrangement only. As a result of not recognizing these differences in emissivities, which are obtainable from changes in the physical setup of an observation, many investigators have incorrectly quoted their values as those of the emissivities of particular materials rather than as an apparent emissivity for their particular arrangements. As a consequence, values of the emissivity of liquid iron ranging from 0.3 up to 0.55 are found in the literature. In an effort to establish an accurate optical temperature scale for liquid iron solutions in which de-oxidation studies were to be carried out, it was observed that the temperature relationship, obtained by simultaneously taking immersion thermocouple

Jan 1, 1963

By C. R. Dodson, D. Goodwill, E. H. Mayer

The paper summarizes the historical background of the pressure-volume-temperature analyses of reservoir fluids, the errors involved in both the sampling and testing of reservoir fluids, the type of information required of a PVT determination, and the field conditions that limit the application of any one analysis. Particular emphasis is placed on the necessity for approximating as closely as possible the liberation sequence occurring in the producing formation, flow string, and surface separators. A combined differential and flash or "composite" liberation is suggested as the best means of approximating this liberation sequence. HISTORICAL BACKGROUND Petroleum reservoir engineering commonly is considered to be one of the newest fields of petroleum science, yet much work of a theoretical and intuitive nature was done many years before the modern techniques of reservoir analyses were developed. The period 1910-1924 saw considerable work in the field of reservoir behavior done by the U. S. Bureau of Mines. This work:.' although entirely theoretical, pointed out the importance of gas in the recovery of oil from the reservoir. The statement by J. 0. Lewis that 20 per cent or less of the oil originally in place in a pool was recovered from the ground under uncurtailed production conditions caused some operators to re-examine and modify their production methods. However, though these works showed methods of production that have subsequently resulted in greater oil recoveries, they in general went unnoticed, even though there was a fear that the nation's petroleum resources were being exhausted. The period 1924-1933 saw the industry take considerably more interest in reservoir behavior because of an unfounded fear of its inability to replace oil reserves, the possibility of government regulation, and the energy of one man, Henry L. Doherty. Doherty aroused heated discussions in the industry concerning conservation. To prove or disprove his theories the first experimental work on the reservoir behavior of petroleum was undertaken. The papers of Dow and Calkin,' Beecher and Parkhurst," and Mills and Heitheckere are classics although their experimental procedures were crude. These papers proved that the properties of petroleum in the reservoir are quite dissimilar to the properties measured at the well head. Gas dissolved in the oil phase was recognized as having considerable importance as had been predicted by the earlier theorists. Slightly later Miller and his co-workers assembled the first text correlating all the known data on the reservoir behavior of petroleum and used, these data to show the economic value of conservation. Quantitative application of pressure-volume-temperature analyses of reservoir fluids was given in the paper of Coleman, Wilde, and Moore"; this work showed that with sufficient laboratory and production data prediction of reservoir behavior was possible. The refined sampling and labora-

Jan 1, 1953

By Foster Fraas

That variations in the humidity of the air and in the moisture content of a mixture of broken solids being separated electrostatically cause trouble is not new.' Much of the reputation for unreliability commonly ascribed to the electrostatic separation processes is probably due to this one factor alone. Some operators dry thoroughly before separating; and while this is good in many instances, there are others in which it is not the remedy for trouble. Some mixtures behave best in very dry air and with the mixtures fed to the separator while hot to reduce the adsorbed water content. On the other hand, an overdried mixture on coming to equilibrium with more humid air, has been known to take up moisture selectively on one family of particles, as of coal in the presence of slate and clay, and give sharper electrostatic separation. From these observations it is concluded that there is a permissible moisture content for a particle and also for the atmosphere surrounding it, if in equilibrium, at which the particle will have a conductivity or cntact potential2-4 that is ideal for electrostatic separation. This permissible moisture content varies between a wide range of limits for the different materials that are are and with the kind of electrostatic separating process used. Water can be present as a result of adsorption and condensation from the atmosphere, as an accumulation before or during mining, or as a residue from a previous process step. The water may exist as a liquid film or as an adsorbed layer of vapor. If the water exceeds permissible limits it must be removed. Its state determines the method. Drying by evaporation is necessary for adsorbed water, for part of the liquid-film water (that is, up to several percent of the dry weight), and for free water in the internal structure. Large water contents may be removed by drainage Or filtration. At just what point mechanical removal should cease and drying by evaporation begin depends upon the method of mechanical removal and its cost. Particles can also be separated according to their differences in dielectric constant when suspended in a liquid of intermediate dielectric constant. Recovery of this liquid presents a a problem' Permissible Moisture The adsorbed moisture on the outer surface of minerals can be quickly removed or replaced. Accordingly, in speaking of adsorbed moisture contents, either that of the solid or that of the surrounding air may be considered, the two values being connected by a distribution coefficient which varies with the temperature. However, such a condition does not necessarily exist in processes where an initially dry material is suddenly introduced into an atmosphere having a partial pressure of water vapor or where a moist material is suddenly introduced into a dry atmosphere. Here the resultant differences in the

Jan 1, 1949

By Foster Fraas

INTRODUCTION THAT variations in the humidity of the air and in the moisture content of a mixture of broken solids being separated electrostatically cause trouble is not new.1 Much of the reputation for unreliability commonly ascribed to the electrostatic separation processes is probably due to this one factor alone. Some operators dry thoroughly before separating; and while this is good in many instances, there are others in which it is not the remedy for trouble. Some mixtures behave best in very dry air and with the mixtures fed to the separator while hot to reduce the adsorbed water content. On the other hand, an overdried mixture on coming to equilibrium with more humid air, has been known to take up moisture selectively on one family of particles, as of coal in the presence of slate and clay, and give sharper electrostatic separation. From these observations it is concluded that there is a permissible moisture content for a particle and also for the atmosphere surrounding it, if in equilibrium, at which the particle will have a conductivity or contact potential2-4 that is ideal for electrostatic separation. This permissible moisture content varies between a wide range of limits for the different materials that are separated and with the kind of electrostatic separating process used. Water can be present as a result of adsorption and condensation from the atmosphere, as an accumulation before or during mining, or as a residue from a previous process step. The water may exist as a liquid film or as an adsorbed layer of vapor. If the water exceeds permissible limits it must be removed. Its state determines the method. Drying by evaporation is necessary for adsorbed water, for part of the liquid-film water (that is, up to several percent of the dry weight), and for free water in the internal structure. Large water contents may be removed by drainage or filtration. At just what point mechanical removal should cease and drying by evaporation begin depends upon the method of mechanical removal and its cost. Particles can also be separated according to their differences in dielectric constant when suspended in a liquid of intermediate dielectric constant. Recovery of this liquid presents a similar problem. PERMISSIBLE MOISTURE The adsorbed moisture on the outer surface of minerals can be quickly removed or replaced. Accordingly, in speaking of adsorbed moisture contents, either that of the solid or that of the surrounding air may be considered, the two values being connected by a distribution coefficient which varies with the temperature. However, such a condition does not necessarily exist in processes where an initially dry material is suddenly introduced into an atmosphere having a partial pressure of water vapor or where a moist material is suddenly introduced into a dry atmosphere. Here the resultant differences in the

Jan 1, 1947

By C. W. Green-Halgh

The accuracy with which grade and tonnage of a mineral deposit may be calculated from diamond-drill assays is dependent upon: (1) the reliability of core and sludge samples and (2) the validity of methods used in grade and tonnage calculations. Limitations imposed by drilling and sampling preclude elaborate methods of computation. In adjusting core and sludge assays the importance assigned the core and sludge samples may be based on either the respective weights recovered or the respective volumes represented by each. Only when core and sludge recoveries arc poor do discrepancies between adjusted assays calculated by these two methods develop, in which case the "weight" method gives emphasis to the core sample and the "volume" method gives emphasis to the sludge sample. When the sludge suffers classification within the drill hole, the weight method gives more accurate results; when the sludge sample suffers no classification, the volume method gives more accurate results. Any drilling campaign offers a compromise between desired accuracy on the one hand and expediency, limited time, money. or facilities on the other. Since the determination of grade and tonnage is an approximation at best, a proper basis for their computation requires a knowledge of the limitations imposed by all phases of work upon which the calculations depend A rational basis for coordination of these phases of work requires determination of: (I) the degree of accuracy desired, as a function of the object of examination; (2) the degree of accuracy attainable, as a function of the limitations imposed in the drilling and sampling program; and (3) the validity of method to be used in calculating grade and tonnage from core and sludge assays. This paper presents results of a comparison made between two commonly used methods of adjusting core and sludge assays, the assumptions upon which these methods are based, and the interrelationship of the phases of work upon which these calculations are dependent. Object of Examination The Purpose of prospecting any mineral deposit is to secure sufficient samples from which Ore grade and tonnage may be calculated. Any mine examination, preliminary or formal, has a definite purpose, although its scope may be limited or broad. The type of examination to be conducted is dependent, therefore, 'pan the reason for instituting the investigation; its scope and thoroughness are directly related to economic considerations. It is highly desirable, therefore, that before starting a drilling campaign a complete understanding of the extent of examination and desired degree of accuracy be determined as a means of simplifying the drilling program and unifying the relative degree of

Jan 1, 1946

"Classification is an important aspect of mineral processing plants and if not operated efficiently can compromise both the throughput and recovery of the circuit. This paper discusses the benefits that can be obtained by operating the classification section efficiently. Since classification in most of the mineral processing plants is carried out using either hydrocyclones or screens the case studies involving the two classifiers were used in the discussion. Studies where optimising the classification circuit lead to improvements in the performance of the overall plant were included to show the benefits of paying attention to this area that is usually neglected. The data from the mill-float mill float, SABC, and Single Stage SAG mill circuit case studies have shown that the circuit throughput can be increased throughputs without compromising recoveries by optimising the classification circuit. On plants where the ore can be liberated at coarser sizes the experimental results have shown that replacing hydrocyclones with high frequency screens can lead to improved plant throughput with no detrimental effect on recovery. The discussion has included information on design and operational considerations for plants that have or intend to use hydrocyclones or screens that could make the classification circuit more efficient.INTRODUCTIONComminution is the process in which particles are reduced in size mainly by crushing and grinding. In most mineral processing circuits comminution is carried out to liberate the valuable minerals prior to subjecting the ore to a recovery process were values are concentrated or extracted (Mainza, Evertsson, Benzer, Tavares, Powell, Rule, Plint, …, 2013). Comminution is an energy intensive process and is usually achieved in stages. It is common to have a classifier after each comminution stage. The process is carried out in stages to minimize energy usage and to improve the efficiency of the process in meeting product specifications. Although comminution circuits have been advancing classification has remained a key component of the comminution circuit design (Mainza et al., 2013). Mainza et al. (2013) summarised the role of classification in mineral processing circuit as: to allow material in the equipment that can promote high operational efficiency, to improve material handling in the circuit, to minimize overgrinding of material to reduce energy consumption, and to provide the best quality product to enter the next stage of processing. Classification stages are employed in comminution circuits to ensure that high throughputs are processed without compromising the product quality or to produce a fine product at relatively low energy. If neglected classification can have detrimental effects on plant performance."

Jan 1, 2016

By Ernest L. Ohle

The newly opened Hayden Creek lead mine represents a variation from the usual Southeast Missouri type. Galena mineralization occurs in sandy dolomite cementing a conglomerate of granite boulders and in cracks in the boulders. The conglomerate occurs at the base of the Bonneterre formation on the slopes of two buried pre-Cambrian knobs. IN 1943 diamond drilling from the surface in an area 2 miles southwest of Leadwood, Mo., discovered a lead deposit of a markedly different character from the usual southeast Missouri type. Subsequent drilling of about 500 holes indicated several million tons of ore, and in 1950 a 701-ft vertical shaft was sunk into the orebody. This paper describes the geology of this interesting occurrence insofar as it is known from the drilling and the small underground exposure at the bottom of the shaft. Geology The location of the Southeast Missouri Lead Belt and of the Hayden Creek property are shown in Fig. 1. As shown here, there are two separate producing areas, one from which the larger tonnage has come, located near Bonne Terre, Flat River, Desloge, and Leadwood, and the other to the south around Fred-ericktown and including famous old Mine LaMotte. The best published description of Lead Belt geology is by Tarr.* In pre-Cambrian time in this area, an assemblage of granites and rhyolitic flow rocks was eroded to a mature topography. Sedimentation, beginning in the Upper Cambrian, filled in the valleys and gradually covered even the highest hills. The first formation deposited was the La-motte sandstone; it is successively overlain by the Bonneterre dolomite, the principal lead-prodbcing formation, then the Davis shale. the Derby-Doerun limestone, and a succession of Cambro-Ordovician cherty dolomites. Several of these formations may be found in direct contact with the pre-Cambrian as their deposition progressively overlapped the older rocks on the flanks of the igneous knobs and ridges. Immediately overlying the pre-Cambrian there is, not uncommonly, a thin basal conglomerate of granite or porphyry boulders, which is incorporated into the overlying sediments. Deposition of the lower part of the rock section was fairly continuous, and the Lamotte sometimes grades almost imperceptibly into the lower sandy Bonneterre. Since the sediments were deposited on an uneven floor, they tend to reflect the irregularities in that floor. Most of the steep dips found in the district, that is, dips in excess of 10°, are original dips and not caused by deformation. Such domelike structures in the sedimentary rocks around the igneous knobs have localized a considerable number of the orebodies in the district and particularly those in the Frederick-town area. Many of the larger orebodies, however, have no close relation to the pre-Cambrian topography. Most of the lead production has come from the lower 150 ft of the Bonneterre formation, where disseminated ore spreads laterally parallel to the bedding for great distances. Average stoping height is about 20 ft, but in a few places there are stopes over 175 ft high.

Jan 1, 1953

By Ernest L. Ohle

The newly opened Hayden Creek lead mine represents a variation from the usual Southeast Missouri type. Galena mineralization occurs in sandy dolomite cementing a conglomerate of granite boulders and in cracks in the boulders. The conglomerate occurs at the base of the Bonneterre formation on the slopes of two buried pre-Cambrian knobs. IN 1943 diamond drilling from the surface in an area 2 miles southwest of Leadwood, Mo., discovered a lead deposit of a markedly different character from the usual southeast Missouri type. Subsequent drilling of about 500 holes indicated several million tons of ore, and in 1950 a 701-ft vertical shaft was sunk into the orebody. This paper describes the geology of this interesting occurrence insofar as it is known from the drilling and the small underground exposure at the bottom of the shaft. Geology The location of the Southeast Missouri Lead Belt and of the Hayden Creek property are shown in Fig. 1. As shown here, there are two separate producing areas, one from which the larger tonnage has come, located near Bonne Terre, Flat River, Desloge, and Leadwood, and the other to the south around Fred-ericktown and including famous old Mine LaMotte. The best published description of Lead Belt geology is by Tarr.* In pre-Cambrian time in this area, an assemblage of granites and rhyolitic flow rocks was eroded to a mature topography. Sedimentation, beginning in the Upper Cambrian, filled in the valleys and gradually covered even the highest hills. The first formation deposited was the La-motte sandstone; it is successively overlain by the Bonneterre dolomite, the principal lead-prodbcing formation, then the Davis shale. the Derby-Doerun limestone, and a succession of Cambro-Ordovician cherty dolomites. Several of these formations may be found in direct contact with the pre-Cambrian as their deposition progressively overlapped the older rocks on the flanks of the igneous knobs and ridges. Immediately overlying the pre-Cambrian there is, not uncommonly, a thin basal conglomerate of granite or porphyry boulders, which is incorporated into the overlying sediments. Deposition of the lower part of the rock section was fairly continuous, and the Lamotte sometimes grades almost imperceptibly into the lower sandy Bonneterre. Since the sediments were deposited on an uneven floor, they tend to reflect the irregularities in that floor. Most of the steep dips found in the district, that is, dips in excess of 10°, are original dips and not caused by deformation. Such domelike structures in the sedimentary rocks around the igneous knobs have localized a considerable number of the orebodies in the district and particularly those in the Frederick-town area. Many of the larger orebodies, however, have no close relation to the pre-Cambrian topography. Most of the lead production has come from the lower 150 ft of the Bonneterre formation, where disseminated ore spreads laterally parallel to the bedding for great distances. Average stoping height is about 20 ft, but in a few places there are stopes over 175 ft high.

Jan 1, 1953

Using 5-p Ni powder and 0.018 ,u A1203, oxide dispersion strengthened nickel alloys were prepared by mechanical mixing of powders, followed by compaction, sintering and extrusion. Processing variables such as cooling of the powder during mixing, electrostatic discharging, mixing time, amount of oxide, and so forth, were studied to determine the effects on room-temperature tensile and high-temperature creep-rupture properties and on the reproducibility of alloys. MECHANICAL mixing of metal and metal oxide powders provides one of the simplest and most inexpensive methods for preparing dispersion strengthened metal-metal oxide alloys;" however, because of large differences in specific gravity, powder particle diameters and other variables, difficulties have been encountered in reproducing alloys and alloy properties. Using 5-p Ni powder and 0.018 p A1203, the following variables were investigated: a) Blending techniques b) Blending time c) Volume fraction of oxide for the selected pow- ders d) Sintering of compacts before extrusion Cooling of Powders During Blending— Cremens and Grant had indicated that dry ball milling of the powder mixture gave superior results over other procedures. When ultra-fine metal and oxide powders became available and comminution was unnecessary or offered little gain, the use of dry mixing in a Waring Blendor gave optimum results.' In the current study, observations of the powder mixtures indicated that considerable heat was generated due to the high speed of the Waring Blendor (15,000 rpm). This heating appeared to produce some degree of clustering and pelletizing. To minimize such agglomeration, a Pyrex cooling coil was installed in the mixing vessel. A double coil, water cooled, proved to be quite satisfactory, providing a fair degree of cooling along with good erosion resistance. Discharge of Electrostatic Charge—Electron-microscopy showed that agglomeration was minimized by the cooling procedure but was not entirely eliminated. It appeared that some of the ag- glomeration had to be explained on the basis of an electrostatic attraction due to the high-speed blending operation. These charges had the effect of promoting the growth of alumina clusters. At the end of the blending procedure such clusters had an effective size which was as much as 50 times that of the individual powder particles and were very tightly bunched. Several methods were utilized to try to discharge the electrostatic forces to minimize the clustering. One successful method, utilized in alloy 17, involved continuous exposure during blending to a radium source of 50 millicuries at a distance of 1.5 ft from the container. A number of other methods were noted to work equally well. Fig. 1 shows the more open oxide structure which results from such a treatment, permitting the matrix metal to penetrate into the cluster more effectively. The combination of powder cooling and discharging led to noticeably improved structures. Fig. 2 shows a cross and a longitudinal section in alloy M-17, one of the best alloys, illustrating the marked decrease

Jan 1, 1961

By C. E. Drennan

Your Chairman and the Program Committee have limited the time allotted to me, and so, with your permission, I will omit the preliminaries, and wade right into my subject. I believe I am safe in taking for granted that you are all agreed that electricity is the most feasible means of transmitting the power used in coal mining. If you are not, then the papers read before the Association in previous years have failed of their object. If you are so convinced, the only question is as to the choice between alternating and direct current, and the voltage. Fundamentally, this is primarily a matter of dollars and cents. With the sole exception of your trolley locomotives, there is no part of your equipment that cannot be operated as well on alternating as on direct current. With your pay rolls at their present high level and the efficiency of the labor you employ at the stage it now occupies, I believe you will agree, first, that everything possible must be done to increase the tons of coal produced per man employed; and, second, that ample power at all times must be available at every machine so that every one of your men can really get out a day's work without any avoidable delay. Speaking Electrically, all this means is a machine instead of a man wherever it is possible for a machine to do a man's work, and full voltage at the machine always, so that there can be no excuse for the work not being done promptly and efficiently-and dependably. The real reason for the selection of one kind of current or the other can best be understood by considering the formula which determines the size of wire required for transmitting electrical energy. The size of the copper required, and, consequently; its weight and cost, depends upon four factors: 1. The amount of energy or power to be transmitted. 2. The distance to be covered. 3. The percentage of loss allowed. 4. The voltage at the receiving end of the line. These factors enter into the problem to different extents, and, briefly, the size of wire depends directly upon the amount of power and the distance transmitted, and inversely upon the percentage of loss allowed and the square of the voltage. From this it will be seen that, with the amount of power and the distance fixed, if the loss is to be cut in two, the wire must be doubled with a given voltage, while if the loss remains constant and the voltage is doubled, the wire may be cut in four; that is, reduced 75 per cent in weight and cost. Now, standard motors are designed and recommended by their builders to run within a range of 10 per cent under voltage to 10 per cent above voltage - 440-volt motor, then, should preferably not be operated on less than 400 volts

Jan 1, 1923

By James Terry Duce

The symposium on production for the year 1941 contains few papers on the foreign situation. Rigid censorship prevails in various countries, as the question of the volume of petroleum supplies has become one of great strategic importance. This is even truer than in the last war, owing to greater mechanization of armies. It has always been the policy of officers in charge of the symposium to refrain from publishing information that might possibly injure national or private interests. At the close of the war we hope again to publish full and accurate records of production abroad. Excerpts from Circular to AutHORs In order to facilitate interpretation of the data in this chapter, we print the fol-lowing excerpts from the Circular to Authors. The field is the unit in this tabulation. In cases of fields extending across State boundaries, such as Rodessa, it is suggested that each State author treat the section of the field in his State as a unit, and by a footnote indicate that the field extends into an adjacent State. Each space in Table I may represent one of four possibilities; either it is not applicable to the particular field, or the proper entry is not determinable, or the proper entry may be determinable but is not determinable from data available to the author, or the proper entry is determinable. When spaces are not applicable, leave blank; in spaces where the proper entries are determinable but not de-terminable from data available to the author, please insert y; in spaces where the proper entries are determinable by the author, make such entries. y implies a hope that in some future year a definite figure will be available. The entry of a zero is a positive declaration, and an important declaration where it is in order. Inability to determine precisely the correct entry for a particular space should not lead the author to insert merely y. Contributions of great value may be made by the author in many cases where entries are not subject to precise determination. In such cases the author should use his good judgment and make the best entry possible under the circumstances. For many spaces the correct entries represent the opinion of the author (for example, "Area Proved") and in such cases the entry need not be hedged to such extent as when the quantities are definite yet can be ascertained only approximately by the author. In cases under definite headings but where figures are only approximate, the author may use x. It is thought that the nearest whole numbers are sufficiently accurate for our purposes except as to percentage of sulphur in oil. If an author desires to report any other figures to tenths, he may do so. The quantity of gas produced should include, where possible, gas sold or otherwise marketed, and gas blown into the air, burned as flares or otherwise wasted. Segregation of these figures would be interesting if the authors can make such segregation. In any event, the figures should represent as nearly as possible the total quantity of gas removed from the reservoir.. Under the columns on "Depth," the average depth to the top of the productive zones and to the bottom of the productive wells, when

Jan 1, 1942

By James Terry Duce

The symposium on production for the year 1940 contains few papers on the foreign situation. It is probable that the foreign part of next year's symposium will be even shorter. This is due to rigid censorship in various countries, as the question of the volume of petroleum supplies has become one of great strategic importance. This is even more true than in the last war, owing to greater mechanization of armies. 'It has always been the policy of officers in charge of the symposium to refrain from publishing information that might possibly injure national or private interests. At the close of the war we hope again to publish full and accurate records of production abroad. Excerpts from Circular to Authors In order to facilitate interpretation of the data in this chapter, we print the following excerpts from the Circular to Authors. The field is the unit in this tabulation. In cases of fields extending across State boundaries, such as Rodessa, it is suggested that each State author treat the section of the field in his State as a unit, and by a footnote indicate that the field extends into an adjacent State. Each space in Table I may represent one of four possibilities; either it is not applicable to the particular field, or the proper entry is not determinable, or the proper entry may be determinable but is not determinable from data available to the author, or the proper entry is determinable. When spaces are not applicable, leave blank; in spaces where the proper entries are determinable but not de-terminable frod data available to the author, please inserty; in spaces where the proper entries are determinable by the author, make such entries. y implies a hope that in some future year a definite figure will be available. The entry of a zero is a positive declaration, and an important declaration where it is in order. Inability to determine precisely the correct entry for a particular space should not lead the author to insert merely y. Contributions of great value may be made by the author in many cases where entries are not subject to precise determination. In sucli cases the author should use his good judgment and make the best entry possible under the circumstances. For many spaces the correct entries represent the opinion of the author (for example, "Area Proved') and in such cases the entry need not be hedged to such extent as when the quantities are definite yet can be ascertained only approximately by the author. In cases under definite headings but where figures are only approximate, the author may use x. It is thought that the nearest whole numbers are sufficiently accurate for our purposes except as to percentage of sulphur in oil. If an author desires to report any other figures to tenths, he may do so. The quantity of gas produced should include, where possible, gas sold or otherwise marketed, and gas blown into the air, burned as flares or otherwise wasted. Segregation of these figures would be interesting if the authors can make such segregation. In any event, the figures should represent as nearly as possible the total quantity of gas removed from the reservoir. Under the columns on "Depth," the average depth to the top of the productive zones and to the bottom of the productive wells, when

Jan 1, 1941

By R. D. Nelson, J. C. Shyne

The ß and a ß transformations in plutonium were studied with particular emphasis on the transformation kinetics and microstructure. Significant observations are: 1) The kinetic data show conclusively that the ß — a transformation in high-purity plutonium can proceed isothermally with no athermal component. 2) Plastic deformation of the stable (3 phase retards the subsequent (3 — a transformation. 3) Plastic deformation of the stable a phase accelerates the a — ß transformation; the acceleration is attributed only to residual stresses. 4) The a and a?a volume changes occur anisotroPically in textured plutonium. 5) An apparent crystallogvaphic relationship exists between the parent and the product phases of the and (3 — a transformations. 6) Both applied uniaxial compressive stresses and uniaxial tensile stresses raise the starting temperature for the ß — a transformation. 7) A given uniaxial tensile stress favors the a — ß transformation more than an equivalent applied uniaxial compressive stress opposes the transformation. These observations of the (ß —a and a — ß phase changes in plutonium are consistent with known mar-tensitic transformations. ThIS paper elucidates some of the characteristics of the a— ß and ß —a transformations in plutonium. Because considerable conjecture exists about the mechanisms by which the phase transformations occur in plutonium, experiments have been performed to provide indirect information concerning the mechanisms responsible for the a —ß and ß -a transformations. Indirect information is of particular value in the study of plutonium because of the experimental difficulties presented by the metal. Single crystals have not been produced in any of the allotropes. The large density results in high X-ray and electron-absorption factors and consequently complicating X-ray and electron diffraction. The kinetics of ß — a and a — ß transformations of plutonium and the behavior of the transformations under a variety of conditions have been investigated in detail. Information about the mechanisms of the allo-tropic transformations of plutonium was obtained indirectly from three sources: 1) the effect of plastic deformation of the stable parent phase upon the transformation kinetics; 2) the behavior of the metal transforming under applied stresses; and 3) the microstruc-tural and crystallographic features between parent and product phases. PHASE-TRANSFORMATION CHARACTERISTICS In characterizing solid-state phase transformations in metals and alloys, it is useful to define several types of transformations. An aim of the present work was to identify the low-temperature transformations in plutonium by type, i.e., as martensitic or nonmar-tensitic. Practical definitions for these terms follow. The terms commonly used to categorize phase transformations lack universally accepted definitions. This confusion arises doubtlessly because some terms specify crystallographic or morphological character while other words have a kinetic or a thermodynamic connotation. For example, martensitic specifies certain definite crystallographic restrictions. Unfortunately, martensitic is sometimes used in an ill-defined way to imply kinetic characteristics. Further confusion attends the use of such expressions as nucleation and growth, diffusional, and massive. From time to time new systems of phase-transformation nomenclature are suggested; unfortunately none of these has gained general acceptance.1,2 The authors of the present paper have no intention of entering the controversy. We recognize that some readers may object to the nomencliture used here. For exampie, the terms military and civilian have recently been used in much the same way as martensitic and non-martensitic are used in this paper. This paper is intended to describe several specific details of the low-temperature phase transformations in plutonium. The authors have found it useful to identify these transformations as martensitic; the term was chosen as the best available to describe the experimentally observed features of the transformations studied. A martensitic transformation is one that occurs by the cooperative movement of many atoms; the rearrangement of atoms from parent to product crystal structure occurs by the passage of a mobile semico-herent growth interface. The geometric features characteristic of a martensitic transformation are a specific orientation relationship between the product and parent phase lattices, a specific habit-plane orientation for the growth interface, and a shape change with a specifically oriented shear component. There is no alloy partition between the parent and product phases in a martensitic transformation. Martensitic transformations may display either athermal kinetic behavior or thermally activated isothermal kinetic behavior. Some martensitic transformations occur isothermally, although more commonly martensitic transformations are athermal. Isothermal martensitic transformations are suppressible by rapid cooling. In athermal martensitic transformations, nucleation and growth are not thermally activated and the transformations are essentially time-independent. Nucleation, growth, or both can be thermally activated in isothermal martensitic reactions. Transformation of the parent phase into a marten-

Jan 1, 1967

By Donald W. Scott, Nathaniel Arbiter, A. C. Richardson

This paper describes the application of amine flotation to a specific problem—that of increasing the grade of magnetite concentrates derived from an iron ore requiring extremely fine grinding for mineral liberation. Experiments conducted on an iron ore from Wisconsin had shown that concentrates containing 60 to 62 per cent iron and 12 to 14 per cent silica could be produced by magnetic separation. The residual silica occurred as quartz and hornblende, either entrained or locked with magnetite. Most advantageous utilization of the concentrate, however, necessitated that the silica content be reduced to about 5 per cent, equivalent to an iron content of 67.5 per cent. It had been demonstrated that tabling of the magnetic concentrate removed sufficient quartz and hornblende to yield an acceptable concentrate, but disadvantages inherent in tabling dictated that flotation be investigated as a substitute. The goals set for the flotation investigation were: (I) the production of concentrates of about 68 per cent iron content from the magnetic concentrate; (2) an iron recovery of about 85 per cent of that in the feed to flotation; and (3) minimum reagent cost. Both batch and continuous flotation tests were employed; the former, to establish the procedure and the latter to verify it. Although the data were obtained on a specific ore, and with a commercial application in view, it is believed that they have a bearing on other problems where amine flotation is being used or is anticipated. Samples Two samples, designated "(minus 100-mesh magnetic concentrate" and "minus 150-mesh magnetic concentrate," were used for the batch experimental work. They differed only in the degree to which the crude ore was ground prior to magnetic separation. They were stored moist in steel drums in quantities sufficient for all the experimental work reported. This procedure had the advantage of allowing all tests to be made on common samples, but had the disadvantage that the individual flotation samples, because of the difference in storage time, were subject to various stages of surface alteration. Previous work had indicated that common samples were desirable for the batch studies, and it was decided that if these data appeared sufficiently promising the effect of surface alteration could be checked best by continuous tests. The size distributions and the assays of the samples are given in Table I. The minus 150-mesh magnetic concentrate, on which most of the flotation tests were made, assayed 60.9 per cent iron, 13.3 per cent silica, and 0.016 per cent phosphorus. The minus 325-mesh portion represented 78.I per cent of the sample by weight, and assayed 67.9 per cent iron. Thus, the insoluble, mainly silica, was concentrated

Jan 1, 1947

By Donald W. Scott, Nathaniel Arbiter, A. C. Richardson

This paper describes the application of amine flotation to a specific problem—that of increasing the grade of magnetite concentrates derived from an iron ore requiring extremely fine grinding for mineral liberation. Experiments conducted on an iron ore from Wisconsin had shown that concentrates containing 60 to 62 per cent iron and 12 to 14 per cent silica could be produced by magnetic separation. The residual silica occurred as quartz and hornblende, either entrained or locked with magnetite. Most advantageous utilization of the concentrate, however, necessitated that the silica content be reduced to about 5 per cent, equivalent to an iron content of 67.5 per cent. It had been demonstrated that tabling of the magnetic concentrate removed sufficient quartz and hornblende to yield an acceptable concentrate, but disadvantages inherent in tabling dictated that flotation be investigated as a substitute. The goals set for the flotation investigation were: (I) the production of concentrates of about 68 per cent iron content from the magnetic concentrate; (2) an iron recovery of about 85 per cent of that in the feed to flotation; and (3) minimum reagent cost. Both batch and continuous flotation tests were employed; the former, to establish the procedure and the latter to verify it. Although the data were obtained on a specific ore, and with a commercial application in view, it is believed that they have a bearing on other problems where amine flotation is being used or is anticipated. Samples Two samples, designated "(minus 100-mesh magnetic concentrate" and "minus 150-mesh magnetic concentrate," were used for the batch experimental work. They differed only in the degree to which the crude ore was ground prior to magnetic separation. They were stored moist in steel drums in quantities sufficient for all the experimental work reported. This procedure had the advantage of allowing all tests to be made on common samples, but had the disadvantage that the individual flotation samples, because of the difference in storage time, were subject to various stages of surface alteration. Previous work had indicated that common samples were desirable for the batch studies, and it was decided that if these data appeared sufficiently promising the effect of surface alteration could be checked best by continuous tests. The size distributions and the assays of the samples are given in Table I. The minus 150-mesh magnetic concentrate, on which most of the flotation tests were made, assayed 60.9 per cent iron, 13.3 per cent silica, and 0.016 per cent phosphorus. The minus 325-mesh portion represented 78.I per cent of the sample by weight, and assayed 67.9 per cent iron. Thus, the insoluble, mainly silica, was concentrated

Jan 1, 1947

By J. H. Waxweiler, L. C. Ikenberry, R. J. Bendure

Carbon which is present as insoluble carbides in austenitic stainless steels can be measured quantitatively by dissolving the steel in iodine-methanol and analyzing the residue for carbon. Severe sen-sitization was observed in Type 302 due to precipitation of only 0.003 pet carbon. Both cold work and the presence of delta ferrite caused a marked acceleration in rate of carbide precipitation. Carbide precipitation rates in 17-7 PH were stzulied for the austenite conditioning and also the aging heat treatment. CARBON and its compounds exercise a major influence on the properties of stainless steels and their response to thermal treatment. Sensitization in 18-8 type stainless steels has been the subject of numerous investigations throughout the years. Bain, Aborn, and utherford," and Binder, Brown, Frankss all studied the effects of heating austenitic stainless steels in the temperature range of 1000° to 1500°F. The primary purpose of most of these studies was the investigation of susceptibility to in-tergranular attack in acids due to these sensitizing heat treatments. Intergranular precipitation of carbides was always associated with intergranular attack but it was recognized2 that severe attack could occur with but minute quantities of precipitated carbide. Mahla and ielsen utilized the electron microscope to make a significant contribution in illustrating the appearance and method of growth of chromium carbides during sensitizing heat treatments. However, as they stated, their studies of residues could not be used to obtain a quantitative measurement of the amount of carbon which was actually precipitated. The aim of the present investigation was to devise a relatively fast, simple method for the quantitative measurement of carbides in stainless steel. EXPERIMENTAL WORK The initial investigations were made to determine the best means of separating carbides from the matrix. A number of dissolving media were tried using both chemical and electrolytic attack. Qualitative examination of the extracted residues by X-ray diffraction indicated that solution in iodine-methanol would furnish a good means of separation. Consequently, further work was pursued along this line. The method is quite simple. The sample in the form of millings or nibblings is dissolved in iodine-methanol solution at room temperature (6-g iodine, 25-ml methanol per g of sample). The insoluble residue containing the carbides is separated by suction filtration through an ultra-fine glass filter disc. This is a very fine filter medium that will retain particles as small as 0.1 to 0.2 p in diameter. After washing with methanol and drying, the filter disc and residue are placed in a conventional combustion carbon-tube furnace and the carbon determined gravimetrically. Using this technique it was found that reproducible insoluble carbon values were obtained. However, since such small amounts of insoluble carbon were obtained on Type 302 after sensitizatipn at 1250°F and 1500°F, the values were confirmed by a second method. In the second method the sample was dissolved with copper potassium chloride and filtered through a millipore paper. This treatment dissolves the matrix but leaves undissolved practically all of the carbon irrespective of how it is present in the steel. The amount of insoluble carbon present as chromium carbide is determined by calculation from the analysis of the residue for chromium and iron. The derivation of the formula used for this calculation is discussed later. The values obtained by the indirect copper-potassium-chloride method were in agreement with those obtained by the iodine-methano1 method. See Table I. It should be pointed out that the sensitivity of the direct combustion method is not too high when the amount of carbide present is small. This is due primarily to inherent blanks and to analytical errors such as weighing. For this reason it cannot be stated with any degree of certainty that there is a significant difference between values of 0.002 and 0.005 pct. Having confirmed that the iodine-methanol extraction gave a quantitative measurement of the precipitated carbides in Type 302, exploratory tests were conducted on Armco 17-7 PH stainless steel. Samples from commercial Heat 54807 were solution annealed at 2000°F, water quenched and heated at 1250" and 1500°F, and water quenched. The analysis of Heat 54808 is as follows:

Jan 1, 1962

The Enquirer of October 13, 1835 carried a letter signed "G," calling attention to the great number of Virginians who were leaving the state and to the lack of enterprise shown in not developing the ample natural resources available. He mentioned coal in particular and in closing said: "Besides the coal mines owned by individuals, the Black Heath company of colliers are carrying on extensive operations. Owing to the derangement of the currency, and the immense expenses incurred in boring and sinking new shafts, I understand that their dividends have not yet been so large, as they may be confidently expected in future.-Another company, under the title of the Midlothian Coal Mining Company, is now about being organized by the Messrs. Wooldridges of Chesterfield, for the purpose of establishing an extensive coal business. Having examined the lands embraced in the charter and the principles upon which the company is designed to be organized, I am persuaded that more productive stock can no where be found. The charter embraces a space nearly equal to a mile square, adjoining the mines of the Black Heath company, those of Mr. N. Mills, and those of Stone Henge, which space must contain coal of great thickness of excellent quality, as the strata of coal of those other mines pass through it; exhibiting a field so extensive, that centuries may elapse before it is exhausted. A shaft has been sunk on these lands, from which a very large quantity of the best coal is being raised. The terms of the charter require the Proprietors to sell one-half of these lands and mines, from the sale of which they will appropriate $100,000 as permanent capital, to purchase hands and engines, and to sink other shafts to work the property and thus going into operation with such decided advantages, as to produce a profit as great as a reasonable man should desire. Here is an opportunity for investing capital, which I think should satisfy the wishes of many Virginians who speak of emigrating. Will they not embrace it?-I have confined my remarks to the coal mines, because they are in the heart of our State, and their operations are familiar to many who can verify the statements. I might extend them to the other mineral treasures of our State; but if I do so, they must be reserved for another number, this being longer than I intended, and perhaps longer than you can conveniently find room for in your crowded columns. G." In January 1828 the Tuckahoe Canal Company was authorized to construct a canal along Tuckahoe Creek, from the James River up the stream about five miles; later this was amended to allow the use of the stream with a depth of water of two feet, no tow path was required, or provided: A toll of one cent per bushel was collected and the canal company made large profits. The service was so poor that in December 18, 1835, John G.,

Jan 1, 1942

By R. R. Bryan

SINCE the first applications of cyanidation to silver ores about 1906, treatment of ores in the Pachuca district has been entirely by straight cyanidation. Until about the year 1921, Real del Monte removed a sulphide concentrate (largely pyrite) by tabling in the cyanidation grinding circuit. The ores milled prior to the year 1935 were dry ores, ideal for cyanidation, and yielded 90 pct of the silver and 92 pct of the gold. Since 1934 there has been a notable increase in the refractivity to cyanidation of the average ores received by the mill. Tonnages of the former amenable ores have gradually been replaced by tonnages of more refractory ones, so that present average recoveries have fallen to 83 pct of the silver and 90 pct of the gold. During this period there has also been an increase in the content of base metal sulphides' in many of the ores although this increase is not always directly related to the increased refractivity. Since March 1950, the Cia. de Real del Monte has been developing a flotation treatment for some-of its ores before cyanidation. Suitability for flotation is judged not only by the base metal content, but also by the amount of additional recovery of silver and gold made possible by the combined treatment. Selection and segregation of ores most suitable for flotation before cyanidation is a difficult problem for the mines, and the best that can be done is a compromise that leaves much to be desired. Development of Pre-cyanidation Flotation at Real del Monte Much laboratory work has been done on flotation of ores from the Pachuca district, however, the data could not supply reliable information on the many factors connected with the economics of low-base metal-high silver ores. Pilot plant operations would be required. Pilot plant facilities were made available in March 1950, when it became necessary to close down Loreto's 100 ton per day selective flotation plant because of exhausted ore supply. The results of the 100-ton pilot plant tests indicated that a large part of our tonnage of cyanidation ores could be profitably treated by flotation, and a tonnage of 1100 tons per day was selected as the maximum tonnage of ore that the mines were likely to deliver, and because this tonnage fitted with the grinding capacity of this circuit. Equipment was ordered for the production of a single flotation concentrate. The conception of flotation before cyanidation, at that time, was the production of a single concentrate to be shipped to the lead smelter. The 100-ton pilot plant was immediately increased to 350 tons by installing additional flotation cells.. This. plant was operated continuously until the 1100ton plant was put in operation in January 1951. In July 1950, an increase in the quotation for zinc called for an investigation- of the possibilities of producing a zinc concentrate, and laboratory tests on the tailings from the 350-ton plant indicated that a

Jan 1, 1952