Search Documents

By J. A. Richardson

J. A. RICHARDSON[t]-Mr. Stuckey's account of the geology of the kaolins of North Carolina suggests that they exhibit some features similar to those of the Malay Peninsula. About one half of British Malaya (some 26,000 square miles) is occupied at the surface by igneous rocks, of which granite and its associated derivatives constitute fully 90 pct. The average granite is a biotic variety. It is predominantly potassic but carries, in addition, notable amounts of soda and lime so that albite and albiteoligoclase are generally common constituents of the rock. The minor derivatives from granite "magma" likewise include potassic and sodi-potassic members. Decomposition of the granitic rocks has led to the formation of kaolin in many localities, but, in general, the deposits are rather small and, at present, none is exploited commercially. True primary or residual kaolins (as defined by Stuckey; p. 48 Vol. 173, p. 2 TP 2219) have been developed from feldspar veins, pegmatites and from other granitic differentiates which cut through the larger masses of granite; they are usually small and narrow. Kaolin has been derived from aplite, quartz porphyry, quartz micro-porphyry, felsites and microgranites belonging to a complex known as the Chegar Perah-Pulai intrusion in northwest Pahang and southwest Kelantan. The bulk of the component rocks has been more or less strongly sheared. Kaolin-like end products have been formed from both sheared and nonsheared varieties. Kaolin has been formed also by the complete breakdown of trondjemite flanking the northwestern and western margins of the complex Bukit Ranjut syenite intrusion in northwest Pahang. These trondjemites range in composition from essentially quartz-free albiteplagioclasites to quartz-free microcline rocks; they are, in effect, the syenitic homologues of white sodic and potassic granite-aplites. The granites in Malaya have generally undergone more or less severe surficial weathering leading to the production of a spongy and rather cellular or a soft "mealy" material (sandy clay) down to depths of about 100 ft; in places the granite is strongly decomposed down to 150 ft. There has occurred, therefore, widespread partial kaolinization, but, in general, no extensive deposits of good quality kaolin seem to have been formed by these processes of decay. Frequently, the katamorphic processes of desilicification have advanced beyond the production of kaolin towards the formation of lateritic end products. The more important Malayan kaoiins seem to be confined to the western alluvial plains, particularly in areas either where granite crops out at surface, or where it forms the bedrock of the alluvium. There are numerous excellent examples around Gopeng and elsewhere in the Kinta Valley of Perak. Such kaolins belong to Stuckey's groups of secondary deposits, and, like them, these also may be bedded. Field observations have established the existence of what for want of a better name is referred to by the Malayan Geological Survey as "granite wash." It is believed that granite, undergoing extensive deeply penetrative and probably rather rapid destruction under humid tropical weathering (temperature around 90°F; rainfall about 100 in. per annum; high humidity) "flowed," was moved by "creep" and, in addition, probably slumped in large waterlogged masses of sandy clay from topographic salients onto the adjacent flats. Either during this period of transmigration or later when the sludged granite detritus, after having more or less come to rest, was attacked by flowing water, differential sorting and erosion took place with the result that the resorted debris was moved and later deposited as bedded alluvium. In this way, banded "granite wash" was produced comprising alternating bands of clayey sand (resorted granite sludge) and white

Jan 1, 1947

By A. W. Bethune, L. M. Pidgeon

The equilibrium vapor pressure of zinc has been determined over the systems: ZnS(s) + Fe(s) = FeS(s) + Zn (vapor) and ZnS(s) + 2Cu(s) = Cu2S(s) + Zn (vapor) by reacting the components in an evacuated tube containing a thin copper fiber, and allowing equilibrium to be established with respect to the brass formed and the zinc in the vapor phase. The composition of the brass formed was determined and equilibrium vapor pressure values obtained from existing data. Between 850' and 1000°C, values for the first reaction ranged from 8 to 58 mm Hg; for the second reaction from 1.8 to 22 mm Hg. THE direct reduction of metallic sulphides may be indicated by an equation of the form MS + X = XS + M [1] where X is some suitable reducing agent. In the case where M is a metal of relatively high volatility, the use of vacuum will displace the equilibrium to the right at comparatively low temperatures in the face of the usually unfavorable thermochemistry. For this technique to be feasible, MS, X, and XS, must of course be nonvolatile compared to M. In this regard, zinc becomes an obvious metal both from the point of view of its volatility and the fact that most commercial ore deposits of this metal occur as the sulphide, and its direct reduction would avoid the expensive roasting process necessary prior to present day reduction methods. Two reducing agents are of interest, namely copper and iron, with the former having the added attraction of being relatively easily regenerated by oxidation in the copper converter. The possibility of these reactions has been considered before. Imbert1 patented a process whereby zinc sulphide was reduced by either copper or iron. The process as described took place at atmospheric pressure and, at the high temperatures required, the system was molten, resulting in the formation of a matte with the consequent reduction in the activities of the reactants. Peterson2 did further experimental work on these reactions and, although promising results were obtained on a small scale, attempts to increase the size of the furnace led to excessive "blue powder" formation. The early workers failed to realize the large reduction in temperature afforded by the use of vacuum and its desirable results. More recently, the direct reduction of zinc sulphide by iron has been the subject of a thermody-namic investigation by Kelley,3 and Gross and War-rington' have studied the kinetics of the reaction in the temperature range 900" to 1000°C, their experiments being conducted using vacuum and indicating that the reaction would proceed practically to completion in 1 to 3 hr, depending on the temperature. A qualitative examination of the system ZnS-Cu carried out at this University indicated that 98 pct of the theoretical zinc in the charge could be recovered in 1 hr at 1000°C when operating under reduced pressure. The purpose of this research program was to study the equilibrium of the two reactions. During the investigation, reference to the experimental work of Schenk5 was found but, due to lack of detail in the report, it was felt that it would be desirable to continue the equilibrium measurements. Selection of Method The measurement of vapor pressure of metals presents obvious problems resulting from the high temperatures which must be employed. In the present case, the production of the "reaction pressure" introduces a further difficulty since a chemical reaction must proceed before any metal vapor pressure is produced, resulting in depletion of the re-

Jan 1, 1954

By Klaus Detert

Fifteen and 18 pct Ni maraging steel and several binavy and ternary alloys of the iron-rich corner of the Fe-Co-Ni system have been studied. After annealing in the austenite range, these alloys were deformed slightly by cold rolling and subsequently aged. Compavison of experimental measurements at various processing stages indicates that small degrees of deforn~ation (5 to 10 pct reduction in thickness) do not influence hardness and strength or the aging kinetics. Electrical resistivity and ductility are somewhat redu]ced and the coercive force is substantially lower when compared to identical samples which were not deformed. The results are explained in terms of retained austenite which transforms into martensite with the small amount of deformation. RECENTLY there has been increasing interest in maraging steel for applications in electric power generators requiring a high ratio of power to weight.' Fifteen pct Ni maraging steel has been investigated to evaluate its properties and performance for application as high-strength magnetic rotor steel,' and a thorough investigation of the precipitation and transformation processes in this alloy has been conducted in this laboratory.3 The influence of deformation, which preceded the aging treatment, was also studied. It was found that a small deformation in the order of 5 pct has a rather striking effect in reducing the coercive force. Other interesting effects on the properties caused by such deformation have led to the more detailed studies reported herein. EXPERIMENTAL METHOD The methods used to produce the samples from 15 pct Ni maraging steel have been described elsewhere.3 The general procedure of hot forging and cold rolling to sheet has been followed. The composition is included in Table I which also contains the composition of the 18 pct Ni maraging steel grade 250 studied. More data about the material and the processing of the 18 pct Ni maraging steel have been recently reported.4 The experimental alloys of binary and ternary Fe-Ni-Co alloys were made by levitation melting in an argon atmosphere and casting into rod-shaped ingots 7 mm thick weighing 20 g. From these ingots 25-mm-long rods were machined to study the phase transformation by a dilatometer. These rods were then cold-rolled to strips, 2.4 mm thick. Annealing for austenitizing was done in tube furnaces in an argon or helium atmosphere followed by cooling in the water-cooled portion of the tube. Aging was done in a salt bath containing a neutral blend of Alkali nitrates and nitrites. Vickers hardness was measured using a load of 50 kg for 15 sec. Tensile tests were carried out on a hard beam tensile tester at a strain rate of 5 X lo-' per sec using flat samples with a gage length of 37.5 mm and a cross section of 1.25 by 6.25 mm. Estimated sensitivity was 5 K x strain and 0.35 kg per sq mm stress. Magnetic saturation was determined on small cylindrical samples, 2.5 mm in length and diameter, by measuring the force exerted by the gradient of a magnetic field of 1000 oe per cm in a mean field of 11,500 oe. The measured values could be reproduced within *1 pct. Coercive force was measured by a precision-type magnetic field probe in a magnetic coil as described by Foerster.5 The magnetizing field was 1300 oe. The samples were 5 cm long, 1 cm wide, and 2.4 mm thick. he coercive force was measured to within +0.1 oe. Electrical resistivity was measured by using a potentiometer on flat strips with a gage length of 100 mm and a cross section of 2.5 by 0.5 mm. The accuracy of the measurement was 0.1 pct but the reproducibility of the measured specific resistivity among different samples was in the order of 1 pct. The method used to prepare the samples for electron transmission has been reported elsewhere.3 RESULTS Fig. 1 shows the influence of deformation after annealing on the resistivity, hardness, and coercivity. The samples were annealed for 30 min at 1000"C,

Jan 1, 1968

By Gregory Molinda

Extremely difficult ground conditions were encountered in the main belt entry in a room and pillar mine in West Virginia. Several generations of supplemental support, including cable bolts, cribbing, and Heintzmann jacks and beams failed to halt roof falls that threatened workers safety and the life of the mine. Polyurethane (PUR) was injected into 27 intersections in the roof and the results were monitored by borehole video camera. The mine had averaged 2-3 falls in the beltway per year and, since the roof injection, no roof falls have occurred. Pre- and post injection monitoring of test holes showed that stability can be achieved without filling all of the existing void spaces. Video logging showed that the project goal of building a beam from 2-6 ft into the roof was successful. Pre-injection monitoring of roof fractures uphole can delineate the zones to target for reinforcement, and avoid pumping PUR into large voids to little effect. Multiple-¬injection zones can be identified, and the entire intersection drill hole array can be optimized based on knowledge of the fractured zones. In addition, pre-monitoring can prevent excessive hydrofracturing in solid zones. Polyurethane injection is a proven method of rock stabilization in even the weakest, most broken ground. Optimization of the injection design by pre-injection video diagnostics can greatly contribute to the successful and efficient roof stabilization.

Jan 1, 2004

By J. J. Benitez

MIBC (methyl-isobuthyl carbinol) was previously shown to enhance significantly sylvite flotation when used at the stage of preparation of amine dispersions. In this paper Atomic Force Microscopy (AFM) is used to study the effect of MIBC on deposition of octadecylamine (ODA) on the surface of mica. The AFM images indicate that amino terminated, and therefore hydrophilic, deposits of ODA are observed on the mica surface in the ODA dispersions free of MIBC. In the presence of MIBC a methyl terminated (hydrophobic) monolayer is obtained on the mica surface. The transition between the monolayer and bilayer phases is due to the presence of MIBC. Experiments carried out in distilled water reproduced the results obtained from the brine. Working in pure water instead of brine simplifies the preparation conditions and the analysis by AFM.

Jan 1, 2006

By Amitava Gangulee, Michael B. Bever

The order-disorder transition in Ag-Mg alloys in the range 17 to 26 at. pct Mg was investigated and some thermodynamic, electrical and mechanical properties of ordered Ag-Mg alloys were measured. A modification of the phase diagram is proposed on the basis of measured transition temperatures. The stability of the ordered structure is analyzed in terms of the quasichemical theory. Kinetic aspects of the order-disorder transition were also investigated. The energies of ordering at 273°K of Ag-Mg alloys were measured by liquid metal solution calorimetry. The electrical resistivities and the tensile Properties of the ordered alloys were measured. The exothermic energy of ordering increased with magnesium concentration up to the composition Ag3Mg; it is discussed in terms of the quasichemical theory. Pronounced order hardening was observed and can be explained by several strengthening mechanisms, which are particularly effective because of a change in crystal structure associated with the ordering transition. IN silver-rich solid solutions containing approximately 17 to 26 at. pct Mg, long- range ordering may occur during appropriate therma1 treatments. Clare-brough and Nicholas1 first detected such long-range order in the solid solution of composition Ag3Mg and suggested that the unit cell of the superlattice contained 256 atoms. x-ray2 and electron diffraction3 investigations confirmed the occurrence of long-range order, but indicated a shifted Ll2-type structure. On the basis of recent X-ray measurements the crystal structure of ordered Ag3Mg has been confirmed as type D023.4 The present paper is concerned with the order-disorder transition in silver-rich Ag-Mg solid solutions and some thermodynamic, electrical, and mechanical properties of the ordered alloys. The effects of short-range order on the properties of silver-rich solid solutions containing up to 26 at. pct Mg are discussed in a concurrent paper.5 1) EXPERIMENTAL PROCEDURES 1.1) Preparation of Specimens. Specimens of Ag-Mg alloys containing from 18 to 26 at. pct Mg were prepared in the form of 1.0-mm-diam wires as described in Section 1.1 of Ref. 5. Disordered specimens were prepared by annealing at 773°K for 1 hr and quenching into iced brine. Ordered specimens were prepared by annealing at 773°K for 1 hr and slowly cooling to room temperature over a period of 15 days. The specimens were stored at 78°K. 1.2) Resistivity Measurements. Electrical resistivi- ties were measured by a potentiometric method.' Equilibrium values were obtained at several temperatures. The kinetics of ordering were investigated by following the time-dependent changes of the resistivity of initially disordered specimens during annealing. The specimens were enclosed in copper capsules and immersed in salt pots; the heating up was accelerated by injecting preheated helium into the capsules. 1.3) Calorimetry. The energies of ordering of the alloys were measured in a tin solution calorimeter as the difference between the heat effects of additions of completely ordered and disordered specimens of the same composition. The procedure and the method of calculation have been described.6 Magnesium was used for thermal compensation in most calorimetric runs in order to improve the accuracy.677 1.4) Mechanical Tests. Tensile tests were carried out with wire specimens at room temperature as described in Section 1.5 of Ref. 5. Microhardness measurements were also made.? 2) RESULTS AND DISCUSSION The characteristics of the order-disorder transition of silver-rich Ag-Mg solid solutions will be discussed first. Some thermodynamic, electrical, and mechanical properties of the ordered alloys will then be considered and compared with the corresponding properties of dis-disordered alloys. 2.1) The Order-Disorder Transition. 2.1.1) Thermodynamic and Structural Aspects. The transition temperatures Tt were determined from discontinuities in the slope of the equilibrium resistivity vs temperature curves. Normalized curves for three compositions are shown in Fig. 1. The transition temperature increases with the magnesium concentration and reaches a maximum at the stoichiometric composition Ag3Mg. The transition temperature of the alloy Ag3Mg was measured as 665° ± 2°K and compares with published values of 660°,1 663°,8 and 66°k.3 In the slopes of the resistivity vs temperature curves of alloys containing 22.2 and 22.5 at. pct Mg, discontinuities were observed at two temperatures. Such upper and lower discontinuities indicate a two-phase field. A modified form of the published phase diagram9 is shown in Fig. 2. A two-phase field was found only on the low-magnesium side of the composition Ag3Mg. On the high-magnesium side, the existence of a two-phase field could not be established because of insufficient resolution, but such a field must be present. This part of the phase diagram can be made complete by a eutec-toid-type reaction a = (a' + ß). The existence of a boundary between the two-phase fields (a + ß) and (a' + ß) is also in accord with published lattice parameters.3 The crystal structure of ordered Ag3Mg (type Do23)

Jan 1, 1969

By E. G. Leonardon, C. Schlumberger, M. Schlumberger

Last year the authors presented a paper that discussed the various electrical measurements they perform in drill holes, which they name "electrical coring."' The object of the present paper is to give a brief account of the points of scientific interest that have been elucidated by further field work and laboratory research, as well as the economic results that have been attained recently. The practical examples given in this paper are drawn, for the most part, from the field work performed in Russian oil fields during the years 1931 and 1932. This is due to the fact that, thanks to the comprehensive cooperation of the Russian geologists and scientists, the authors are allowed to make public a large amount of recant information. In other countries in which the authors are engaged in similar work, the competition between private companies makes it imperative, for a considerable lapse of time, to avoid publication of the results obtained. The following points will be discussed successively, under separate headings: 1. Electrochemical phenomena in drill holes. 2. Stratigraphic correlations and tectonic studies. 3. Relations' between the productivity of oil horizons and their electrical resistivity. 4. Location of coal seams. 5. Summary and conclusions. Electrochemical Phenomena in Drill Holes Technical Publication 462l described the author's discovery concerning the existence of important differences of potential spontaneously gener-

Jan 1, 1934

By J. E. Coyne, L. E. Tanner, J. E. Boyd

In recent investigations of the isothermal transformations of the retained 0 phase in a titanium alloy having 13 pct V, 11 pct Cr, and 3 to 4 pct Al, there have been indications that the w transition phase is the initial decomposition product at temperatures below about 950°C (510 c).' This metastable phase, found in a number of titanium-base alloys rich in stabilizing elements and known to have an adverse effect on their ductility and toughness, is not easily observed by the usual experimental techniques. Since wis coherent with the /3 matrix,495 distinct interphase boundaries are not revealed metallographically. However, in some cases, an etching effect (i-e., a "mottled" /3 surface) poorly resolved by light microscopy has been found to correspond with the presence of w.6 X-ray diffraction examination has generally been the most suc- cessful means for identifying this phase and crys-tallographic determinations have been made.4'5 Dynamic elastic modulus7 and electrical resistivity measurementse have also aided in the identification of w. In the current study, the electron microscope was utilized to examine microstructures in aged Ti-13V-11Cr-3A1 that were unresolvable by light microscopy techniques. Using negative parlodion replicas (shadowed with chromium at 27 1/2 deg) examination was made of various transformation

Jan 1, 1962

By D. D. Howat, J. van der Colf

Selected members of the slag system were reduced in graphite crucibles in an argon atmosphere, and the physicochemical properties of the reduced derivatives of the slags were determined in inert crucibles. It was found that slags having magnesium aluminium titanate as the primary phase before reduction underwent an increase in liquidus temperature, accompanied by a change in the primary phase. No analogous behaviour could be detected for the slags having perovskite as the initial primary crystallization product. In most instances, the viscosity of the melt passed through an initial minimum, followed by an increase as the reduction time was extended. Increased MgO/CaO ratio. basicity, titania content, and reduction temperature all served to accelerate thickening. During reduction, the electrical conductivity of the slags tended to rise relative to the value for the unreduced melt.

Jan 1, 1979

By Derek J. Fray, John Chipman

THE solubility of graphite in y-iron has been determined by several workers'12 with reasonable agreement. With the increasing use of more complex steels, it is necessary to understand more fully the thermodynamics of the austenite phase. The activity of carbon in a number of alloys is known but the maximum solu- bility of graphite has only been measured by Sohnchen and piwowarsky3 for Fe-Ni and Fe-Si alloys. Recently, Chipman and Brush reviewed the published data on the activity of carbon in binary and ternary austenite and also obtained expressions for calculating the solubility of graphite in Fe-Ni, Fe-Co, and Fe-Si alloys. On comparing the theoretically derived solubilities with the limited results of Sahnchen and Piwowarsky, it was found that the agreement for Fe-C-Si was excellent but there was considerable discrepancy for Fe-C-Ni and no data for Fe-C-Co. It was therefore decided to measure the solubility of graphite in a series of Fe-Ni and Fe-Co alloys. The alloy samples were made up by induction melting a high-purity master alloy under an inert atmosphere in an alumina crucible and drawing the molten metal into four-bore alumina tubes. Using this technique, it was possible to form alloy rods approximately 2 in. long and 1/18 in. in diam. Sixteen lengths of fine rod could be made without solidifying the master alloy. These were then allowed to cool under the inert atmosphere before being sectioned. The samples were packed in a graphite crucible with spectroscopic graphite powder, together with a piece of pure iron foil. Dry hydrogen, which had been saturated with isopropyl alcohol at room temperature, was passed over the crucible at 1000°C for 72 hr. At the end of the 72 hr argon displaced hydrogen in the reaction tube and the crucible was quickly pushed to the water-cooled end. The samples were thoroughly cleaned of the adhering graphite and analyzed. The pure iron samples always contained 1.5 0.02 pct C, which compares favorably with the data of smith2 and

Jan 1, 1970

By E Garbarino, P Molina, V Badino

Given the ever increasing quantity of construction and demolition waste (C&DW), one of the most challenging issues presently facing policymakers and public administrators in Italy concerns how to organise and manage collection and recycling and to understand whether and to what extent recycled aggregate can complement natural building aggregates in a sustainable supply mix (SSM). The paper presents the results of a research aimed at analysing energy and environmental implications of the C&DW recycling chain in the administrative territory of Provincia di Torino in northern Italy. In respect of a population of about 2.25 million inhabitants, the annual production of C&DW in the area under study is 1.8 Mt. A combined geographical information system (GIS) and Life Cycle Assessment (LCA) model was developed, paying attention to the geographical location, land use, transportation network and avoided landfill: crucial issues for sustainable planning and management. Around 90 recycling plants were classified according to the size, typology (stationary, semi-mobile and mobile) and physical- mechanical characteristics of the recycled aggregate. Under different assumptions relevant to the delivery distance, and considering the typology and grade of recycled aggregate, as well as local availability of natural aggregates, it was possible to evaluate the geographical coverage of aggregates demand and to use LCA in order to identify and quantify energy and environmental indicators.

Jan 1, 2009

By Reginald Williams

THE amount or value of the precious metals consumed in dentistry is probably amazing to most people. It falls very little short of that which is consumed in jewelry. Inasmuch as the ultimate destination is in the human mouth, dental alloys enjoy some importance because life and health depend upon restorations made with them. Prosthetic dentistry has made wonderful progress in the last few years. The manufacturers who supply the metals also deserve commendation. This industry which deals with metals to go-into people's mouths is comparatively new. There is no literature on the subject, and little or no precedent by which to be guided. It was only by close cooperation with the dentist or prosthetic technician that desirable physical properties were produced, as-nearly as possible, in the metals which were available and permissible. It is true that there were and still are conflicting opinions among the dentists as to the physical properties they require. Sometimes they request the impossible, such as alloys which are exceedingly stiff and springy, yet will bend or adjust easily. Even in this latter instance, progress has been made by supplying methods of heat-treatment whereby metals may be softened or hardened at will. (Figs. 1 and 2.) The demands made upon manufacturers are extremely varied. They must supply metals of tensile strengths ranging from approximately 30,000 to 100,000 lb. per sq. in. and over. The latter metals must be workable and in many instances capable of extreme deformation. They must not be affected by mouth conditions, nor should they oxidize greatly when molten, at red heat, or during a soldering operation. In addition to physical, specifications, color demands must also be met. The firm of which I have the most, knowledge manufacturers 11,553 standard stock articles of precious metals, taking into consideration formulas, finenesses, grades, colors, gages, lengths, sizes and weights. If special demands are taken into consideration, the number would be in excess of 25,000. Wrought metals are manufactured in a great many alloys of different sizes and shapes, such as plate, bar, rod, wire, sheet, strip, mesh and foil. There are also other products of importance.

Jan 1, 1928

By Rajendra K. Devala, Sukumar Bandopadhyay

In order to be able to design an adequate mine ventilation system it is necessary to understand how pollutant masses disperse into turbulent ventilation air streams. The mixing of gases and dusts with ventilating air, and dispersion of these pollutants in mine airways, are important flow or transfer problems. For the solution of such problems, the finite difference technique is often used. In this paper, numerical approximation schemes for the solution of the mass transfer problem have been developed using several explicit finite difference schemes. Results from these schemes have been compared with the analytical solution for spatial and time increments using the concept of Root Mean Square error. The comparison of various schemes reveals that the explicit finite difference schemes analyzed here give more accurate results at lower velocities, though the results are dependent on the spatial and time steps considered. At higher velocities the schemes tends to oscillate about the analytical solution. INTRODUCTION In mining, most of the mine air pollutants, such as respirable dust, methane, blasting fumes and diesel exhaust, are produced at the mine face and in haulageways. Injection of any of these pollutants in the mine ventilating air causes disturbances of the equilibrium state of the pollutant concentration of the ventilating air. The mixing of these gases and dusts with the ventilating air are typical examples of mass transfer processes. Pollutants are diluted by the stream of ventilating air flow along airways and discharged into the outside atmosphere of the mine through a return shaft. The dispersions of these pollutants in mine airways are important flow or transfer problems. Knowledge about pollutant sources, emission and transport of these pollutants are essential for ventilation planning and design to ensure good engineering control over air quality, quantity, and environmental conditions. Modeling of mass transfer phenomena in mine ventilation is largely based on extensive studies of turbulent dispersion in wind tunnels and the lower atmosphere of the earth. The general approach in the formulation of models lies in the recognition that these mass transfer phenomena can be conceptualized as a flow problem that can be solved by the general application of Taylor's theory (1954) of turbulent flow and diffusion with modification appropriate static and dynamic parameters. If the face zone is initially contaminated by a pollutant over a long section (e.g. instantaneous exposure of large gas accumulation, rapid methane release etc.), the process of decontaminating the mine workings can be regarded as displacement and diffusion of the tailing edge of the cloud of contaminates in the form of a semi-infinite gas body, for which a one-dimensional mass transfer equation is represented by: [at + u • ax = Ex ex2 + f (x,t)(1.1)] In Eq. (1.1), the term [~~] is the rate of growth of the concentration in the differential element, while a [(5xx )] is the net gain of material due to convective transfer. The two terms balance the total loss of material due to turbulent dispersion that is represented by [Ex . 21] and f(x,t), the source term for the pollutant in the roadway. Several cases of mass transfer that occur in mining can be identified and modelled using the conservative volume element method. The governing equation, along with the associated boundary and initial conditions, source terms and their solutions are detailed elsewhere (Bandopadhyay and Ramani, 1988, Devala, 1989). Only one mass transfer situation is presented (Figure 1) here for the present analysis. Mixed Evolution of Pollutant (multiple pulses) Typical examples of these situations are emission of pollutants from multiple diesel vehicles in the face area, and gas emission from standing pillars as well as from broken coal seam during coal cutting with a continuous miner. The mathematical statement of the problem along with the initial and boundary conditions are given below, Governing Equation: [do+u- =E d2c(1.2) ataxx dx2] Initial conditions:

Jan 1, 1993

By R. M. Asimow

Both smith1 and wells2 have shown that the dif-fusivity of carbon in austenite increases rapidly with increasing carbon concentration. Smith has shown, in addition, that part but not all of this increase can be attributed to the concentration dependence of the activity coefficient of carbon in austenite. From the work of Eshelby', it is known that, because of the image displacements, there is a uniform dilatation of the material in a body containing random centers of dilatation. It is thus tempting to explain the enhanced diffusivity as resulting from this apparent negative pressure caused by the interstitial carbon atoms.* That is, the activation free energy for diffusion is not directly a function of concentration if we consider that the alloy is subjected to a concentration-dependent pressure. To proceed with a quantitative solution, it is necessary to determine the activation volume AV for the diffusion process. An exact calculation of AV is quite a difficult problem and does not appear to have been solved as yet. A simpler procedure is to use the semiempirical, macroscopic theory of seyes' which relates the activation free energy AG to AV. Keyes has shown that for many types of diffusion processes the following relationship is valid Where p is the Gruneisen constant and x the compressibility. This relationship is based on the assumption that AG can be identified with strain-energy terms. In general there will also be contributions to AG due to a change in the energy of the valence electrons of the metal; thus the relation must be considered largely empirical. Surprisingly, for self-diffusion where it is well-known that the electronic contribution is quite important,' the Keyes relation works quite well for many systems. For interstitial diffusion where it might be expected that the relationship is on a firmer theoretical basis, the limited experimental data available is not in particularly good agreement as can be seen from Table I. However, it must be remembered that besides the uncertain basis of the Keyes formula there is considerable uncertainty in some of the experimental values of AV. The only real justification for using the Keyes formula in the present analysis is that it gives a result which satisfactorily solves the problem at hand and, further, there are no more reliable procedures for calculating AV available. The coefficient 3 in Eq. [I] is determined such that the room-temperature value for x is to be used. The activation entropy AS is estimated as 8.95 x 10"3 kcal per OK mole using the values in Table I1 and the Zener" relation AS = PAHIT, where p is a dimensionless thermal coefficient of Young's modulus which is to be evaluated at low values of T/T,, aH is the activation enthalpy, and T, is the melting temperature of the alloy. The resulting value of AG at 1000°C is 25.6 kcal per mole. The Gruneisen constant (p = 3cup/XC,), where p is the density, is evaluated from the room-temperature data in Table I1 after calculating C, from the relation. A value of p = 8.32 g per cu cm based on the value of a. in Table I is used. The result is C, = 5.0 x lo6 erg per g, H = 2.32, and AV = 3.41 cu cm per mole at 1000°C and infinite carbon dilution. It is assumed that the activation volume is not a function of carbon concentration. The theory could be refined to consider AV a function of concentration, but due to the uncertainties in the parameters there seems little justification for this. Carbon dissolved in austenite forms a nonideal solid solution, so that in writing an equation for. the diffusivity of carbon it is necessary to take into account the change in activity coefficient with concentration. The resulting equation is16

Jan 1, 1964

By Gilbert L. Eggert

The effects of reactor irradiation on age hardening in a Cu-2 wt pct Be alloy have been investigated in two neutron-energy ranges. During some of the irradiations, specimens were exposed to high-energy fission neutrons which passed through a boron-10 shield; during other bombardments, the boron-10 was omitted and specimens were irradiated in a reactor thermal column, or the fuel configuration was modified to increase the thermal-neutron flux at a location in the core. Differences in length, X-ray diffraction angle, and hardness indicated that low-energy neutron irradiation made a small contribution to changes in the measured properties. The influence of defects generated by knock-om with less than the Brinkman critical energy or by prompt (n,y) recoil is suggested as the cause of this effect. EXPERIMENTS designed to test the effects of reactor irradiation on the properties of age-hardening alloys have to the present time employed fluxes un-differentiated according to neutron energy. Billing-ton and Siegell in 1950 were the first to perform such an experiment and to compare the results with those obtained by thermal aging. These authors concluded that precipitation in a Cu-2 wt pct Be alloy was not enhanced by the radiation. However, 4 years later, Murray and Taylor,2 working with specimens of the same Cu-2 wt pct Be alloy, reported that an increase in density, hardness, and resistivity which followed reactor irradiation resembled changes associated with thermal aging at about 100°C. (It should be noted that these authors reported that higher aging temperatures caused a decrease in resistivity.) cupp3 reported hardness results similar to those of Murray and Taylor. Koppenaal4 showed that irradiation-enhanced precipitation and irradiation defect hardening were not simply additive but that they acted separately in an irradiated alloy. Kernohan et a1.,5 working with Ni-Be, offered evidence that beryllium was removed from solid solution by reactor irradiation and suggested that the mechanism was one of increased diffusion through the use of vacancies in the structure. piercy6 also found that more precipitate particles were formed by fission-neutron irradiation of a Cu-Co alloy which contained a small amount of particles before irradiation. He proposed that the additional particles were caused by an appreciable amount of diffusion during the final cooling of displacement spikes. The retrogression of extant precipitate particles found by Murray and Taylor2 and Boltax7 as well as piercy6 indicated that nuclei were dissolved within a high-energy spike region and, upon resolidification of the perturbed volume, new nuclei precipitate and grow by enhanced diffusion. Bleiberg et al.' and Konobeevski et al.' explained phase changes obtained by irradiating fissionable alloys in terms of retrogression and re-precipitation in regions of high-energy spikes. Parsons and Balluffi10 used electron microscopy to verify that crystallization did indeed occur in displacement spikes which were formed in amorphous germanium by fast-neutron irradiation. The concept that low-energy neutron irradiation might cause structure-sensitive property changes in semiconductors by atomic recoil associated with the (n, y) reaction was first proposed by Schweinler" and walker." This thesis was tested by Cleland and crawford" and found to be valid. Coltman et al.14 exposed a variety of pure metals to thermal-neutron irradiation at cryogenic temperatures and attributed the resulting resistivity changes to the action of defects created by (n, y) recoil. The present work was undertaken to extend the concepts of Schweinler," walker," and Coltman et al.I4 to the case of an age-hardening alloy and to determine whether or not the action of defects produced by thermal-neutron irradiation would en-hance age hardening. EXPERIMENTAL PROCEDURE Omeea West Reactor Irradiations.* Thermal-

Jan 1, 1965

By Amitava Gangulee, Michael B. Bever

The effects of changes in short-range order on some thermodynamic, electrical, and mechanical properties of the silver-rich Ag-Mg solid solutions have been investigated. The heats of formation at 273°K of several alloys after two different thermal treatments were measured by liquid metal solution calorimetry. Their electrical resistivities were measured at temperatures ranging from 4° to 773°k. Tensile tests and microhard-ness measurements were carried out at room temperature. An effective short-range order parameter and an effective interaction energy are defined. The measured changes in the properties are interpreted in terms of these quantities. The short-range order parameter is evaluated separately from calorimetric and X-ray data; the results are in fair agreement. Increasing short-range order lowers the resistivity of- the silver-rich Ag-Mg alloys but does not measurably affect the temperature dependence of the resistivity. Short-range order increases the yield stress of these alloys but does not affect the ultimate tensile stress. Changes in the effective short-range order parameter independently obtained from measured changes in the heat of formation, resistivity, and yield stress are in fair agreement. THE thermodynamic, electrical, and mechanical properties of solid solutions have been investigated as functions of composition in many alloy systems, but the effects of configurational variables, such as short-range or long-range order, on these properties have received much less attention. The silver-rich terminal solid solutions in the system Ag-Mg are well-suited for the investigation of the effects of order. The composition of these solid solutions may be varied over a range extending to about 27 at. pct Mg.1 Appreciable short-range ordering is likely to take place in these solid solutions; the degree of short-range order can be varied by suitable thermal treatments. In the alloy Ag3Mg long-range ordering is possible.2 This paper is primarily concerned with the effects of short-range order on some thermodynamic, electrical, and mechanical properties of the silver-rich Ag-Mg solid solutions.-The long-range ordering transition is the subject of a concurrent paper.3 1) EXPERIMENTAL PROCEDURES 1.1) Preparation of Specimens. Ag-Mg alloys containing up to 26.4 at. pct Mg were prepared by melting 99.99 pct pure Ag (obtained from Baker Chemical Co.) and 99.99 pct pure Mg (obtained from Eastman Chemi- cal Co. or Johnson Mathey & Co.) in graphite crucibles under molten potassium chloride. The solidified ingots were homogenized at 823°K for 10 days in evacuated Vycor capsules. A surface layer 6 in. thick was then removed by machining. The ingots were swaged into rods (2.5 mm diam) which were drawn into wires (1.0 mm diam). The wire specimens were annealed at 773°K for 24 hr in vacuum and either quenched into iced brine or cooled to room temperature over a period of 15 days. The average grain diameter (obtained from the linear intercepts) was about 0.1 mm. 1.2) Calorimetry. The heats of formation of the alloys were measured in a tin solution calorimeter as the difference in the heat effects of alternate additions of samples of an alloy and the mechanical mixture of its component elements. The additions were made from 273°K to the bath at about 623°K. The heat effect on addition of the alloys was approximately 5.5 kcal per g-atom. The procedure and the method of calculation have been described.4 1.3) X-Ray Diffraction. Short-range order parameters of two alloys were calculated from diffuse scattering intensities,' obtained with briquettes made from powdered specimens. A GE-XRD 5 diffractometer with filtered copper radiation was used. The absolute intensities were based on calibrations with paraffin. 1.4) Resistivity Measurements. The electrical resistivities were measured by a potentiometric method in which the potential drop across the specimen was compared with that across a standard resistance. For measurements below room temperature, the specimens were immersed in liquid helium (4°K), liquid nitrogen (78°K), dry ice and trichloroethylene (195°K), or ice and water (273°K). Measurements above room temperature were made on specimens held in a furnace under helium or in vacuum. The resistivity measurements were reproducible to ±0.5 pct or less. 1.5) Mechanical Tests. Tensile tests were carried out at room temperature with a Tinius-Olsen XY elec-tromatic Universal testing machine. Wire specimens (nominal gage length 1 in.) were used. The strain was measured with an extensometer, which had a sensitivity of 4 x 10-5; the strain rate was 10-3 min-1. Microhard-ness measurements were made with a square-pyramid indenter and a 100-g load.11 2) RESULTS AND DISCUSSION All measurements were made on two parallel sets of specimens, one quenched and the other slowly cooled from 773°K. The reported values are the averages of at least three measurements. In the range of magnesium concentration substantially below that of the composition Ag3Mg, quenched alloys have less short-range order than slowly cooled alloys. As the magnesium concentration approaches that of Ag3Mg, slow cooling develops long-range order. Quenching sup-

Jan 1, 1969

By David W. James, Howard Jones, George M. Leak

Conditions are described for producing, by primary recrystallization, a matrix suitable for the growth of large grains near (110)[001] orientation in silicon iron strip by secondary recrystallizaliun in a steep temperature gradient. The orientation distribution of these large grains is expressed in terms of rotational deviations about the cross-rolling direction, the rolling direction, and the normal to the sheet, the deviational spread increasing in that order. With the aid of cowplenientary published data on the orientation dependence of growth rate, it is shown that this observation is consistent with the oriented-growth theory of recrystallization lextures. It is conclutled that growth-rate and orientation-distribution data obtained in a steep thermal gradient should be used with caution to account for isothermally Produced recrystallization textures. SEVERAL authors have reported methods of growing large grains by re crystallization of a small-grained matrix in silicon iron 1- B and pure a cr The present study was a preliminary in the growth of single crystals and bicrystals for surface relaxation," grain boundary mobility, and grain boundary diffusion studies. The method was to control the growth of a seed crystal into a suitable primary re crystallized matrix by feeding through a steep temperature gradient. The driving energy for growth derived from the grain boundary energy released as the seed crystals grew into the matrix. Thus, stability of the matrix against normal grain growth was considered to be essential for success. It was known that the manganese sulfide dispersion present in commercial silicon iron performs this function during secondary recrystallization to the (110)[001.] texture.12 Hence commercial, rather than high-purity, material was used throughout. The paper describes the growth conditions for grains large enough to be used as seed crystals for further growth into single crystals. The orientation distribution of the seed crystals is analyzed and its significance for the theory of recrystallization textures is discussed. EXPERIMENTAL PROCEDURE Strip material was supplied by the Steel Co. of Wales, Ltd. The chemical analysis in weight percent was Si, 2.90; C, 0.015; Mn, 0.059; P, 0.011; S, 0.027; Ni, 0.032; 0, 0.009; Fe, balance. A gradient furnace of similar design to one described previously4 was loaned from B.I.S.R.A. It consisted essentially of a vertical water-cooled copper slot projecting downwards into the hot zone of a molybdenum furnace. Hydrogen was passed through the furnace to protect both heating element and specimen from oxidation. Strip specimens up to 8 cm wide and 0.2 cm thick were sealed into the furnace at the mouth of the copper slot. A coating of light oil on the strip surface maintained the seal during translation of a specimen. The maximum temperature gradient in the region just below the copper slot was 500°C per cm over 1 cm, with the hottest point controlled at 1175°C. Several large grains would usually grow by secondary recrystallization from the primary matrix when a specimen was immersed in the hot zone for about 30 min. A back-reflection X-ray camera was constructed to facilitate rapid and accurate orientation determinations of the large grains produced. It was possible to reproduce a standard geometry, with regard to strip and camera, without the tedium of careful alignment on each occasion. Specimens, typically 4 cm wide and 75 cm long, were cut with the longitudinal axis parallel to the rolling direction of the original strip. The surfaces were cleaned by immersion alternately in a hot aqueous solution containing 2 pct hydrofluoric acid plus 10 pct sulfuric acid and in cold 10 pct nitric acid. The nitric acid etch was just sufficient to reveal the grain structure. Rolling and annealing treatments to prepare the matrix (discussed below) were followed by growth of seed crystals in the gradient furnace. The matrix was transformed to a single crystal by growth of a selected seed crystal connected to the matrix by a thin neck. 4,5 Growth was promoted by controlled feeding into the gradient furnace. Several single crystals of controlled orientation were grown successfully from seed crystals by twisting the interconnecting neck in a reorien-tation jig.4 EXPERIMENTAL RESULTS AND DISCUSSION Growth Conditions. A suitable matrix for growth of large grains was prepared starting from primary re-crystallized strip 1.9 mm thick. This was cold-rolled in two stages each being followed by a recrystallization anneal at 800°C for a few minutes. Such treatment gave the required growth matrix only if the two cold-reduction stages were each performed in several passes and in the following ranges: the first, 30 to 70 pct; the second, 10 to 50 pct. Immersion in the temperature gradient otherwise resulted in an equiaxed

Jan 1, 1967

By H. R. Peiffer

Recently artin has indicated that the recovery of resistivity at 145°C following elongation of molybdenum at room temperature was the result of the annihilation of vacancies. The activation energy for this process was, according to Martin, 1.26 ev. This energy seems to be a reasonable one for the activation energy for the diffusion of vacancies in molybdenum. However, impurity atoms such as carbon, nitrogen, and oxygen4 have an activation energy for diffusion in molybdenum of the same order of magnitude (i.e., 1.45, 1.15, and 2.09 ev, respectively). Cottrell and Churchman have already correlated the return of impurity atoms to dislocations in cold-worked iron with the return of the upper and lower yield point. According to cottrel16 the diffusion of carbon atoms to dislocations results in the return of the yield point. As the carbon atoms become trapped by dislocations, Bhatia has shown that a decrease in the electrical resistivity is to be expected. Cottrell and Churchman were able to correlate experimentally the decrease in electrical resistivity with the return of the yield point. Since one would expect strain aging to occur in molybdenum, an experiment was performed to determine whether the resistivity recovery at 150°C for molybdenum cold-worked at room temperature can be correlated with the return of an upper and lower yield point. For this experiment 3/16-in. tensile bars of Climax molybdenum, 99.961 pct pure, were used. The specimens were annealed at 1000° C for 1 hr in an argon atmosphere and then were elongated up to 10 pct on a Baldwin-Lima-Hamilton FGT

Jan 1, 1959

By A. Kurkov

Flotation process is based on the formation of primary collector-based supramolecular associates at the mineral surface and within the pulp. Supra molecular chemistry allows studying within a common framework, all kinds of molecular associates, from dimers to large assemblies, resulting from spontaneous association of a large number of interacting components of the flotation system, where the collective action of non covalent bonds can have an important role. Self-organization of supra molecular assemblies in the flotation process can be controlled by modifying the chemical structure of the collector, the nature and arrangement of functional group in it, by introducing secondary agents (SA) into the process, to adjust the interaction between the collector and the surface and to control the hydrophobicity of the adsorption bed. This offers broad opportunities to build supramolecular assemblies to improve the efficiency of flotation. Besides, the more complex is the system, the weaker are the interactions, that determine its behavior. This powerful factor still is not employed deliberately to control the flotation process. Organophosphorus compounds (OPC) - dialkyl phosphoric acids whose radicals contain ethoxylated groups ? are considered as nanocompounds, that can be used in building supramolecular assemblies. The presence in an OPC molecule of functional groups (P=O, P (O) O-, P (O) OH), ethoxylated groups, and aromatic rings is the basis for the formation of stable supramolecular associates. Gross formula: C54H94KO16P. Molecular weight is 1069.39. Phosphoryl anion has a regular tetrahedral structure with the angle of 109.5°. Lengths of -P-O- bonds in a PN molecule are 1.7345Å; length of the hydrocarbonic radical C42-C72 = 33.942Å. In an alkaline environment, PN is in the form of the anion, in an acidic environment ? in the form of the polycation due to protonation of the oxygen in the EO group. Chem Office software suite was used to generate three-dimensional images of an OPC molecule in acidic and alkaline environments, to reveal the OPC geometry (bond lengths, valence angles, aliphatic radical length), to identify the collector's binding sites with the mineral surface, to find the most stable and energy-efficient molecular conformations of an OPC molecule and its complexes with minerals under various conditions. Mechanisms of interaction between OPCs and the mineral surfaces are different. In ores whose minerals are dominated by ionic bonds (fluorite), the interaction mainly involves the anionic form of the collector; in ores, whose minerals are dominated by covalent bonds - the oxygen of the phosphoryl group (donor-acceptor interaction) and the oxygen of the ethoxylated groups. This difference is responsible for the formation of spatial associates with different surface layer structures. Introduction of supramolecular chemistry concepts into the analysis of flotation phenomena and mechanisms can become an effective tool for better understanding the flotation process and offers new means of consistently improving its effectiveness.

Sep 1, 2012

By David Deglon, Martin Harris, Mehdi Safari

"This study investigates the effect of energy/power input on the flotation of a platinum ore in a pilot-scale oscillating grid flotation cell. Oscillating grids generate near ideal hydrodynamic environments, characterised by turbulence which is relatively homogeneous and isotropic. Secondary rougher feed and primary cleaner tail streams were floated in a pilot-scale oscillating grid flotation cell at power inputs from 0 to 2.5 W/kg, using 0.50 and 1.50 mm bubbles. From this study one may conclude that the effect of energy/power input on the flotation rate is strongly dependent on the particle and bubble size. Flotation rates generally increase with increasing particle size and decreasing bubble size. Increasing energy input generally leads to an increase in the flotation rate for finer particles and an optimum flotation rate for intermediate & coarse particles. Optimum conditions for intermediate/coarse platinum ore particles are using small bubbles at low energy inputs, or large bubbles at higher energy inputs. These results suggest that higher energy inputs are generally beneficial for the flotation of platinum ores as these consist predominantly of finer particles (-75 µm) and most industrial flotation applications operate with larger bubbles (1.0-2.0 mm).INTRODUCTIONThere is a considerable body of experimental and theoretical evidence to suggest that energy/power input plays an important role in flotation kinetics, particularly in the finer particle sizes where flotation efficiency is poor (Deglon, 2005). A number of excellent studies into the effect of energy on flotation kinetics have been carried out in impeller stirred cells (Ahmed and Jameson, 1985; Deglon, 2002; Pyke et al., 2003; Newell and Grano, 2006). Investigations using this type of cell have a number of limitations. The impeller influences particle suspension, bubble break-up and agitation in the cell. In addition, turbulence is highly inhomogeneous and anisotropic, with power intensities near the impeller orders of magnitude higher than those found elsewhere in the cell (Deglon, 1998; Koh and Schwarz, 2003; Schubert, 1999, 2008). These limitations have resulted in the development of novel cells for the investigation of energy input."

Jan 1, 2016