By R. L. Rickett, S. H. Kalin, J. T. Mackenzie

Aluminum killed low carbon steel, § which is now used extensively for severe deep drawing or other difficult forming operations, is unusual in that its grain structure, after cold reduction and box annealing in accordance with conventional continuous sheet or strip mill practice, often is elongated, although at times it is equiaxed. Since this unusual structure has been found superior for many, but not all, severe forming operations, recrystallization of the steel, both at constant temperature and on continuous heating, was investigated and compared with that of rimmed steel in the hope that something might be learned about the mechanism of, and the factors controlling, the formation of such elongated grains. In this structure, the grains are elongated both in the lengthwise direction of the strip and transverse to this direction, even though nearly all of the extension in both hot and cold rolling is in the lengthwise direction. The grains are thus roughly pancake-shaped, being longer and wider than they are thick, as observed also by Burns and McCabe,1 and as illustrated by the typical structures shown in Fig 1. Fig la, representing a conventional longitudinal section, shows the length and thickness of the grains, whereas Fig Ib shows their length and width as seen by examining a section parallel to the sheet surface. Both illustrate the very irregular grain boundaries usually associated with the elongated grain shape. A finer equiaxed grain structure in this same grade is shown in Fig Ic. Either the elongated or the equiaxed structure may be present in the annealed product, and in rare instances the two types may coexist in a single specimen, as shown in Fig 1 d. Isothermal Recrystalliza-tion of Rimmed and Alamimum Killed Steel An aluminum killed steel known to have an elongated grain structure after conventional processing (Steel B, Table l), was selected for the initial recrystallization studies; for comparison, a rimmed steel, A in Table 1, was used. Samples of each in the form of hot rolled strip 0.075 and 0.095 in. thick, respectively, were cold rolled on a small laboratory mill in steps of about 0.010 in. per pass to obtain total reductions of 40 and 60 pct. Small pieces of the cold reduced strip were heated in lead at selected constant temperatures for one of several periods of time, then cooled in air. Rate of heating in the lead was, of course, very fast. Hardness of the cooled specimen was measured and a longitudinal section examined metallographically. Isothermal recrystallization curves for these two steels at 1050°F, based on hardness of the air cooled specimens, are shown in Fig 2 in which the amount of recrystallization corresponding to each plotted point is indicated. The marked difference in the behavior of these two types of steel is evident. After a corresponding amount of cold reduction, the rimmed steel recrys-tallizes in a much shorter time than the killed steel and the shape of its recrystallization curve, (plotted on a logarithmic time scale), is very different. The curve for rimmed steel indicates that recrystallization is analogous to isothermal transformation of aus-i.enite in that it proceeds at a progressively faster rate up to some 50 pct recrystallization, then at an increasingly slower rate. For the aluminum killed steel, however, the start of

Jan 1, 1950

By Charles Prasky

ABOUT five years ago the Bureau of Mines began a study, at Minneapolis, of the various methods for beneficiating the low-grade manganese deposits of the Cuyuna range. Several samples of green carbonate slate from the Cuyuna range, containing about 7 pct Mn and about 28 pct Fe, were obtained for this study. The component minerals in the carbonate slate formation were so intimately associated that mineral dressing methods were not suitable for concentrating manganese to a ferrograde product. Although upgrading of manganese and iron minerals has been effected by flotation methods, it appears that manganese cannot be separated from iron except by chemical means. Because the flotation studies at Minneapolis were carried out simultaneously with the hydrometallurgical studies, only crude slate was available for process testing. An important economic consideration in selecting any one of the several chemical methods proposed for recovering ferrograde manganese is the availability of the chemical reagent. Fortunately, large tonnages of sulfur are available on the Cuyuna range in low-grade pyrite and pyrrhotite deposits that are readily concentrated by flotation to a suitable feed for a sulfide roasting furnace as indicated by a Bureau of Mines investigation in 195 0-1951.1 The roasted residue from the sulfide concentrates is a potential source of marketable iron oxide. Therefore, if these sulfide deposits were employed in recovering manganese, utilization of two heretofore unused mineral deposits would be accomplished. Laboratory investigations of several proposed leaching processes were made as a preliminary step in the investigation of hydrometallurgical methods for the treatment of Cuyuna carbonate slate using sulfur as a chemical reagent. From results obtained in the laboratory tests, these leaching processes did not appear entirely suitable for treating Cuyuna carbonate slate. The method developed at the North Central Experiment Station and selected for a more intensive pilot-plant investigation has been termed the differential high-temperature sulfatizing process. Essentially, this sulfatizing process consists of the following steps, described in the order in which the small-scale pilot-plant investigations were made. The first and perhaps most significant step in the process consists of a sulfate roast. Carbonate slate is roasted in an atmosphere of sulfur dioxide gas and air. The overall chemical reaction for converting manganese carbonate to a sulfate at a high temperature in a sulfur dioxide atmosphere follows MnCO8 + SO2 + 1/2 0, = MnSO4 + CO2 (H077°O = —64,180 cal per g mol) .' The need for concentrated sulfuric acid is avoided. Fine grinding is not essential. Removal of carbon dioxide from the slate during roasting produces a more porous structure and permits easier permeation by the sulfatizing gas mixture. The temperature limits for this conversion of manganese have been established as 600" and 850°C. Iron sulfate is unstable and is not formed at these temperatures; phosphorus is not converted to a water-soluble form; and polythionates are not formed. The second step in the process consists simply of a water leach of the sulfatized product. Manganese sulfate in the sulfatized product is dissolved in water. Iron, phosphorus, and calcium remain in the leach residue as water-insoluble products. The third and final step consists of the recovery of ferrograde manganese oxide from manganese sulfate leach solution. Water is evaporated from the leach solution, and impure monohydrate crystals of manganese sulfate are recovered. The moist crystals are formed into pellets or extrusions and thermally decomposed to produce a ferrograde manganese

Jan 1, 1958

By Baoxiang Zhang, Jing Zhang

"As extruded Mg-9Zn-0.6Zr-2Er magnesium alloys were hot-rolled at 400°C, followed by solution treatment at 400 °c for 1. 5h and artificial aging at 200°C for 10h. Microstructures and tensile mechanical properties of the alloys after hot rolling, solution and aging treatment were examined respectively. Optical micrographs of the as-rolled and as-solution alloys showed fine grain structures, due to the formation of Er-and Zn-bearing compounds at grain boundaries which obviously improved the thermal stability of the alloy. Yield strength as high as about 335 MPa was obtained for the as-rolled alloy, showing that the mechanical properties of the alloy was greatly benefit from the grain refinement and dynamic precipitation of fine MgZn2 during hot rolling. Due to solution heat treatment, vast majority of the Mg-Zn phases dissolved into the matrix, and precipitated out again as fine dispersoid during the subsequent aging, resulting in an enhanced aging-hardening effect.IntroductionWith high specific strength and low density, magnesium alloy has stimulated significant interest for the applications in microelectronics, aerospace and automobile industries. Due to its HCP structure, magnesium alloys exhibit relatively poor strength and ductility. Great efforts have been made to improve the properties of magnesium alloys.Thermo-mechanical processing which combined with subsequent heat treatment can strengthen magnesium alloys due to the strain-hardening mechanism, homogeneous distribution of second particles and grain refinement [1, 2]. However, commercial wrought magnesium alloys have high tendency of grain growth at high temperature due to lack of effective solutions to stabilize the microstructure [3, 4, and 6]. But Magnesium-RE alloys containing high rare earth were reported to have remarkable thermal-stability, Rare earth (RE), such as Y, Nd, Yb, Gd, Ce, were known to form second-phase particles that have higher thermal stability combining with Zn and matrix in Mg[12-17]."

Jan 1, 2012

By GEORGE S. POPE

The purchase of coal by the Government under specifications depending on the heating value of the coal, its content of ash and of moisture, and other considerations, rather than upon the reputation or trade name of the coal, was based on the fuel investigations begun by the Technologic Branch of the United States Geological Survey in 1904. The plan was first adopted by the Treasury Department in 1906. Since then the plan, variously modified in form but the same in principle, has been gradually adopted by other departments until at present of the coal used by the Government, the total value of which approximates $8,000,000 annually, more than half is purchased under specifications. The Government publications dealing with the adoption by the Government of the specification plan, the number of contracts awarded on that basis, and the quality of the coal delivered under such contracts in the several fiscal years covered by the reports are given in publications listed at the end of this bulletin. Under the authority of acts of Congress making appropriations for analyzing and testing fuels belonging to or for the use of the United States Government, a laboratory is maintained at the headquarters of the Bureau of Mines, Washington, D. C., where samples represent- ing deliveries of coal purchased under specifications for Government use are analyzed and tested. At this laboratory more than 1,200 samples have been analyzed and tested in one month. With the complete equipment and the efficient force employed, the analytical work has been so perfected that the analyses and heating-value tests of the samples received are as accurate as may be reasonably expected in laboratory work of this nature. One of the serious drawbacks to the general adoption of the speci- fication method for the purchase of coal is the difficulty of obtaining at reasonable cost samples of coal that can be considered fairly repre- sentative of the commercial product delivered in wagons, railroad

Jan 1, 1913

By A. B. Kinzel

SINCE the exposition of the behavior of certain iron alloys by Sykes1 involving the existence of an austenite loop and the discovery of such a loop in the chrome iron system by Bain,2 there has been much conjecture both on his part and on the part of metallurgists in general as to the exact shape and location of this loop. In previous work commercial steel has been used and the microscope has been employed to locate the critical points so that the position of the loop has been quite approximate. Numerous attempts have been made to measure the critical points of the carbon-free alloys but all of these for one reason or another have failed. A satisfactory method for studying these phenomena, is presented here. MATERIAL The first difficulty in this study was to obtain pure chromium-iron alloys. This has been overcome by melting in a vacuum electrolytic iron and chromium analyzing 99.84 Cr, Fe and C. A pure magnesite crucible was used and the melt allowed to solidify in the crucible. A typical analysis is chromium, 10.10 per cent., carbon, 0.006 per cent., silicon and manganese nil. To overcome the problem presented by segregation, ingots were made into wire 0.04 in. in diameter. This was accomplished by hand-forging the ingots into rods, using an oxyhydrogen flame for heating, in order to avoid carbon. Subsequently the rods were swaged too wire, the heating being carried out in hydrogen. Thus local segregation was eliminated although differences in analysis between portions 50 ft. apart were noted. An electric-resistance method was first tried to determine the critical points, but due to the physical defects in the wire this failed. Bain had previously shown the presence or absence of critical points in a qualitative way by observing the sag in a catenary. The author has devised the following method which gives an accurate determination of the critical points from expansion-temperature curves of suspended wire, a special telescopic dilatometer being used for the purpose.

Jan 1, 1928

By A. B. Kinzel

SINCE the exposition of the behavior of certain iron alloys by Sykes1 involving the existence of an austenite loop and the discovery of such a loop in the chrome iron system by Bain,2 there has been much conjecture both on his part and on the part of metallurgists in general as to the exact shape and location of this loop. In previous work commercial steel has been used and the microscope has been employed to locate the critical points so that the position of the loop has been quite approximate. Numerous attempts have been made to measure the critical points of the carbon-free alloys but all of these for one reason or another have failed. A satisfactory method for studying these phenomena is presented here. MATERIAL The first difficulty in this study was to obtain pure chromium-iron alloys. This has been overcome by melting in a vacuum electrolytic Eton and chromium analyzing 99.84 Cr, Fe and C. A pure magnesite crucible was used and the melt allowed to solidify in the crucible. A typical analysis is chromium, 10.10 per cent., carbon, 0.006 per cent., silicon and manganese nil. To overcome the problem presented by segregation, ingots were made into wire 0.04 in, in diameter. This was accomplished by hand-forging the ingots into rods, using an oxyhydrogen flame for heating, in order to avoid carbon. Subsequently the rods were swaged to wire, the heating being carried out in hydrogen. Thus local segregation was eliminated although differences in analysis between portions 50 ft. apart were noted. An electric-resistance method was first tried to determine the critical points, but due to the physical defects in the wire this failed. Bain had previously shown the presence or absence of critical points in a qualitative way by observing the sag in a catenary. The author has devised the following method which gives an accurate determination of the critical points from expansion-temperature curves of suspended wire, a special telescopic dilatometer being used for the purpose.

Jan 1, 1928

By A. B. Kinzel

Since the exposition of the behavior of certain iron alloys by Sykesl involving the existence of an austenite loop and the discovery of such a loop in the chrome-iron system by Bain,2 there has been much conjecture both on his part and on the part of metallurgists in general as to the exact shape and location of this loop. In previous work commercial steel has been used and the microscope has been employed to locate the critical points so that the position of the loop has been quite approximate. Numerous attempts have been made to measure the critical points of the carbon-free alloys but all of these for one reason or another have failed. A satisfactory method for studying these phenomena is presented here. MateRial The first difficulty in this study was to obtain pure chromium-iron alloys. This has been overcome by melting in a vacuum electrolytic iron and chromium analyzing 99.84 Cr, Fe and C. A pure magnesite crucible was used and the melt allowed to solidify in the crucible. A typical analysis is chromium, 10.10 per cent., carbon, 0.006 per cent., silicon and manganese nil. To overcome the problem presented by segregation, ingots were made into wire 0.04 in. in diameter. This was accomplished by hand-forging the ingots into rods, using an oxyhydrogen flame for heating, in order to avoid carbon. Subsequently the rods were swaged to wire, the heating being carried out in hydrogen. Thus local segregation was eliminated although differences in analysis between portions 50 ft. apart were noted. An electric-resistance method was first tried to determine the critical points, but due to the physical defects in the wire this failed. Bain had previously shown the presence or absence of critical points in a qualitative way by observing the sag in a catenary. The author has devised the following method which gives an accurate determination of the critical points from expansion-temperature curves of suspended wire, a special telescopic dilatometer being used for the purpose.

By Persifor Frazer

"The nebular theory is a noble speculation supported by plausible argument, and the verdict of science on the whole subject cannot be better expressed than in the words of Newcomb :—'At the present time we can only say that the nebular hypothesis is indicated by the general tendencies of the laws of nature, that it has not been proved to be inconsistent with any fact, that it is almost a necessary consequence of the only theory by which we can account for the origin and conservation of the sun's heat, but that it rests on the assumption that this conservation is to be explained by the laws of nature as we now see them in operation. Should any one be skeptical as to the sufficiency of these laws to account for the present state of things, science can furnish no evidence strong enough to overthrow his doubts until the sun shall be found growing smaller by actual measurement, or the nebulæ be actually seen to condense into stars and systems.' " Leibnitz2 is credited by Cuvier3 (who associates with him Descartcs) with " amusing their imaginations " by conceiving the world to be an extinguished sun or vitrified globe upon which the vapors, condensing in proportion as it cooled, formed the seas, and afterwards deposited the calcareous strata. Whiston4 believed the earth was crested from the atmosphere of one comet and deluged by the tail of another. The heat which remained from its origin excited the whole antediluvian population, men and animals, to sin, for which they mere all drowned in the deluge, except the fish, whose passions were apparently less violent. De Maillet5 held that the globe had been covered by water for many thousand years. The terrestrial animals were originally inhabitants of the sea, and man himself began his career as a fish. He adds it is not uncommon to meet with fishes in

Jan 1, 1905

By Claudio Sulca, Fernando Salas

Como parte de la política de mejora continua de nuestra compañía y de nuestro proceso de gestión de activos, uno de nuestros principales objetivos es lograr que nuestros activos alcancen y superen las horas de operación y ciclo de vida estimados en nuestro plan de negocios, asegurando la confiabilidad y buscando un equilibrio con los costos de reparación y costos horarios de rendimiento. Uno de los procesos importantes para lograr este objetivo es el proceso de monitoreo de condiciones, el cual asegura la salud y confiabilidad de los activos.

Sep 30, 2022

By H. F. Ramstad, F. D. Richardson

The equilibria (a) SiOz +Hz =SiO +H20 and (b) Si + SiO, = 2Si0 have beet1 studied at temperatures of 1425"to 1600°C ad 1310°to 1485°C respectively. The stattdard free energy changes for the tzrro reactions are given by the equatiotts Combination of the results for both equilibria leads to tiotz removes certain anomalies in existing high-terlzperature data for equilibria involving silica and silicon in iron. In many metallurgical processes and in many laboratory investigations silicon monoxide undoubtedly plays an important role. It is unfortunate therefore that wide differences exist between the results obtained by different investigators1-7 in their studies of such equilibria as In an attempt to put our knowledge of SiO on a surer basis, an exhaustive study has been made of equilibria [I] and [2] at temperatures ranging from 1300" to 1600°C. Reaction [I] was studied by measuring the amounts of silica which could be condensed from streams of Hz or Hz + HzO which had previously been brought into equilibrium with silica at temperatures ranging from 1425" to 1600°C. Reaction [2] was studied by measuring the material that could be condensed from streams of Hz or argon which had been brought into equilibrium with mixtures of silicon and silica at temperatures ranging from 1310" to 1485°C. EXPERIMENTAL Materials. The silicon was "superpure" grade and contained less than 0.1 pct impurities. The silica was prepared from pure mineral quartz; this was crushed and treated with concentrated hydrochloric acid to remove particles of iron, washed with water, and finally dried at 120°C. For the hydrogen + silica reaction, the silica was sized to —20+100 mesh. For the silicon + silica reaction, the two materials were ground to a fine powder in an agate mortar. The hydrogen and argon were commercial oxygen-free gases. The gas streams were controlled with capillary flow meters and the volumes were measured by wet gas meters. After passing through the meters, the gases were partially dried by silica gel. The hydrogen for the HZ + SiOz reaction was then passed through palladised asbestos at 300°C and dried with magnesium perchlorate. The efficiency of oxygen removal was checked throughout the experiments by passing the gas over an electrically heated strip of nichrome, used as an indicator as described by Rathman and de itt.' When mixtures of HZ + Hz0 were required, the partial pressures of water vapor (1.8 to 22 mm) were obtained by passing the hydrogen through oxalic acid dihydrateg' lo held at various controlled temperatures, O.l°C, by means of a water bath. The hydrogen for the Si + Si02 reaction was purified by passing it over a mixture of 3 parts of magnesium to 5 of lime heated to 600°."l1 u The argon for this reaction was passed through titanium powder (-3/16 in. + 100 mesh) heated to 900°C. The nitrogen used to prevent the reaction products escaping from the condenser (see later), was deoxidized by copper or iron at 600°C. All these gases were finally dried with magnesium perchlorate. Furnace, Temperature Contr01, and Measurement A molybdenum resistance furnace was used for both sets of experiments. The reactions were conducted inside a high-grade alumina tube, 36 in. long and 1 in. in diam as indicated in Fig. 1. With this arrangement an even temperature zone (2"C) 4 cm long was satisfactorily obtained. The temperatures were kept constant by means of a proportional controller actuated by a Pt-Pt 13 pct Rh thermocouple. This was placed between the two alumina tubes, so that the temperature at the junction was 1400" to 1450°C. Up to 1485"C, the temperatures were measured with Pt-Pt 13 pct Rh thermocouples. For higher temperatures an optical pyrometer was used, this being sighted (through the glass window 1 in Fig. 1) on the end of the alumina tube, that held the SiOz or Si +SiOz mixture, 10 in Fig. 1. The optical pyrometer was recalibrated whenever a change was made in any part of the apparatus situated in the hot zone. Successive readings with the optical pyrometer were reproducible to within 1"C. Equilibrium Apparatus and Procedure. Hydvogen and Silica Reaction. The apparatus is shown in Fig.

Jan 1, 1962

By E. Miller, J. M. Eldridge, K. L. Komarek

Activities of magnesium in liquid Mg-Sn alloys have been determined between 5 and 90 at. pct Sn and 990" and 1290°K by an improved isopiestic method wherein tin specimens, heated in a temperature gradient and contained in crucibles of special geometry, were equilibrated with magnesium vapor in a closed titanium system. The crucibles were designed so that the equilibrium compositions of the specimens were satisfactorily preserved on termination of the experimental runs by quenching. The activity values are in excellent agreement with those predicated on the phase diagram and allowed a delineation of the solidus curve of the compound Mg2Sn near its melting point. EQUATIONS have been recently derived relating the chemical potentials of the components to the liquidus and enthalpy data for binary systems exhibiting one congruently melting compound.' The liquidus curve of the Mg-Sn system between the eutectics was carefully redetermined and the thermodynamic properties thus calculated were in reasonably good agreement with values derived from electromotive-force measurements of an,' but differed greatly from the iso-piestically determined values of Ashtakala and Pid-geon.3 The present study was initiated: a) to resolve the discrepancies; b) to develop a method for measuring activities in systems having volatile (and possibly highly reactive) components; and c) to use the method in a general investigation of the thermodynamic properties of the homologous series of Mg-Group IVb systems, i.e., Mg-Pb, Mg-Sn, Mg-Ge, and Mg-Si. This paper describes the results for the Mg-Sn system. An isopiestic technique, originally developed by Herasymenko 4 and adapted for alloys having a component of high reactivity and low volatility,5-8 was modified in this study by using crucibles designed to preserve the equilibrium composition of highly volatile liquid specimens on quenching from high temperatures. Tin specimens, contained in tightly covered graphite crucibles and heated in a temperature gradient, were equilibrated with magnesium vapor of fixed pressure from a magnesium reservoir kept at constant temperature in a previously evacuated and sealed titanium tube. During equilibration magne-

Jan 1, 1967

By Henry Fay

THE erosion of guns is a complex problem which can be solved only by a detailed study of all the factors involved. In the present paper it is proposed to submit the results of observations and experiments which have extended over several years. Certain facts have been established and preliminary reports have been published.' Conclusions have been reached since then which, it is believed, are worth presenting for the purpose of promoting discussion, and with the hope that ultimately the whole truth will be known. The particular phase of the problem which will be presented here is the hardening of the inner surface of the gun tube. It has been known for a long time that after firing a large caliber gun for some time, the surface of the metal becomes hard and brittle, cracks, and wears away.2 The character of this phenomenon may be learned by an examination of some results which are typical, obtained from a detailed study of a 12-in. gun. The gun was trepanned and rings representing various sections of the gun were cut out for examination. The first ring represented the metal at the muzzle end, and the other rings were removed at approximately 120, 240, 325 and 337 in., respectively, toward the breech end. The appearance of the surface of the metal in the different sections is shown in Fig. 1. The greatest amount of wear and maximum amount of hard surface layer was found in section marked E, which is nearest the powder chamber and at the beginning of the rifling; the maximum amount of cracking in D; the maximum amount of copper deposition in C. Section B showed heat cracks on both lands and grooves, and section A showed heat cracks on the driving edge of the lands only. There was much flow of metal in both sections E and D, and there was progressively less effect noticeable toward the muzzle end. The polished cross-section of these same pieces is shown in Fig. 2. The

Jan 12, 1916

By G. H. Kesler, C. E. Dryden, J. H. Oxley

Rates of heat- and mass-transfer from rods to recirculating air were determined within a one-quarter-scale model of a metals deposition bulb. The dependence of local and averaged rates of transfer upon outlet geometry, number of rods, position upon a rod, and airflow rate was established for flow patterns created by radial and tangential air inlets. The results are given a qualitative interpretation in terms of rates and distribution of metal deposition in a prototype deposition bulb. IT is well known that a number of metals can be prepared from volatile compounds containing them by causing dissociation of their compounds to occur at heated surfaces. Examples of such metals include silicon, titanium, zirconium, and aluminum, which can be prepared from their halides. While the ability to prepare high-purity metals by this technique is of importance in itself, the rate of deposition of metal also is important in considering the commercial potential of such a process. If the over-all process of deposition is broken down into separate steps of transport of materials to and from the heated deposition surface and establishment of chemical equilibrium at the surface, as was described in a recent paper,1 then since surface temperatures are usually high and surface equilibrium is attained very rapidly, the rate-controlling step can be considered as either that of transport of reactants to the surface or of transport of products other than deposited metal away from the surface. These two transport steps are related through the reaction stoichiometry. It can be shown1 that the rate and distribution of metal in such a transport-controlled process are determined by the over-all and local mass-transfer coefficients in conjunction with the equilibrium conversions at the hot surfaces. The rate relationship is: w = [KA(y a-y s)] B.E where the bracketed group is the rate of arrival of the reactant at the surface of area A as determined by the mole fraction driving force (y a - y s) and the convective transport constant K. The factor B is the weight fraction of metal in the reactant, and E is the equilibrium fractional conversion to metal. Numerical values of y, and y, are fixed by the vapor composition and the equilibrium compositim of reactant at the surface; and E can be determined by thermodynamic calculations or by experiment. However, values for the convective coefficient K are available generally only for systems of simple geometry, such as cross-flow past a rod or sphere or parallel flow past a flat plate or through a tube. Often it is necessary to work with systems of more complex geometry and in which the vapor flow may not be uniform or exactly parallel or perpendicular to the surface. It is possible, of course, to establish working correlations for these more complex systems by direct experiment; but the experiments usually are costly in both time and money. To circumvent this objection and to aid in arriving at an understanding of the relationships and interactions of the process variables, it is helpful to construct a model of the flow system in which air, water, or other convenient fluids can be substituted for the process vapors and with which mass-transfer measurements or analogous he at-transfer measurements can be made upon a simulated deposition surface. By this means, a large number of measurements can be made in a reasonable time, and the correlation of these results can be applied to the prototype system. Examples of the application of these techniques are to be found in the literature (e.g., Ref. 2). It is the purpose of this paper to illustrate these techniques by description of a model study which was done at Battelle Memorial Institute. The work to be described was of a preliminary nature; the investigation subsequently was extended to develop quantitative relationships among the significant dimensionless transport, geometric, and flow parameters. This more detailed study will be the subject of a future paper.

Jan 1, 1962

By J. J. Jonas, G. Gagnon

SHG zinc was extruded in the temperature range 110" to 350°C and the strain rate range 0.05 to 5 sec-1 The strain rate/flow stress/temperature results were analyzed using a power sinh stress relationship. When temperature changes due to the heat of deformation and to heat losses are neglected, the exponent of the sinh function of the stress is 5.6, and the apparent activation energy of deformation is 28 kcal per mole. When these changes are taken into account, the exponent decreases to 4.7 and the activation energy to 23 + 2 kcal per mole. The corrected stress exponent and activation energy are in very good agreement with published values obtained from creep experiments, and suggest that the hot extrusion of zinc is controlled by a mechanism involving self-diffusion. When the extrusion and creep data are compared using a Zener-Hollomon parameter and either a sinh or an exponential stress term, an appreciable offset is observed, which may be due to the difference in impurity content. For a given set of extrusion conditions the ram speed, maximum pressure, and initial temperature can also be correlated using a Zener-Hollomon parameter and a sinh pressure term. THE deformation of metals at temperatures over about one-half the absolute melting temperature has been extensively studied at creep strain rates. By contrast, relatively little work has been carried out on the behavior of metals at hot working strain rates. Most of the latter investigations have been performed using simulative methods, such as hot torsion and hot compression, in which the friction conditions and temperature rise during deformation may differ appreciably from those existing under industrial conditions. Recently, however, Wong and Jonas1 used a scaled-down industrial process to determine the stress and temperature dependence of the strain rate during the extrusion of aluminum. In such tests, the effects of friction and adiabatic heating are closer to those produced in industrial operations. Also, with regard to the testing of materials of limited ductility such as zinc, hot compression and hot torsion do not permit the attainment of true strains as large as the deformations usually applied commercially. The present study was undertaken to investigate the extrusion behavior of Special High Grade (SHG) zinc. The detailed objectives were: 1) to establish the stress and temperature dependence of the strain rate with and without a consideration of adiabatic heating, 2) to study the pressure and temperature dependence of the ram speed, and 3) to investigate the microstruc- tural changes occurring during the deformation. The last aspect of the investigation will be covered in a separate paper. The treatment described below differs from that of Wong and Jonas in that the adiabatic temperature rise during deformation is taken into account, and the calculation of the mean equivalent strain rate is based on the redundant as well as on the homogeneous work. EXPERIMENTAL PROCEDURE Rods from two shipments of continuously cast SHG zinc* were used in the investigation. The composition *Supplied by courtesy of Cominco Ltd. range of the impurities present, as given by the supplier, was: Pb: 0.0013 to 0.0023 pct, Fe: 0.001 pct max Cd: 0.0001 to 0.0006 pct, Cu: 0.0002 to 0.0005 pct, Ti: 0.0001 pct max; thus, by balance, zinc valued from 99.9963 to 99.9966 pct. The as-received rods were machined into billets having a nominal diameter of 1.56 in. and a nominal length of 1½ in.; longer billets up to 4 in. in length, were also used to investigate special aspects. The as-machined rods were annealed at 400°C for 24 hr and slowly cooled. This treatment produced a columnar grain structure, with a grain size of about $ by 2½ cm which was appreciably larger than the as-cast one. A 150-ton, direct extrusion, vertical press was used. Ram displacement and force were recorded continuously against time. A constant flow control valve permitted the maintenance of a range of preselected ram speeds up to in. per sec. The selected speed was held constant, irrespective of the required force, as long as the load developed was below the maximum available. Strain gages were used to determine the force; the gages were calibrated before and after each testing period with a 200,000-lb capacity load cell. Further details of the experimental equipment can be found in Ref. 2. The billets were preheated for 90 min in the extrusion container, which was well insulated so as to minimize temperature gradients. This period was sufficient for the billet to reach a uniform temperature at all temperatures between 110" and 350°C. A square-shoulder die having a 0.290-in. diam central hole was used. The extrusion ratio was 30 to 1. This is equivalent to a reduction in area of 96.7 pct, an elongation of 2900 pct, and a true strain of 3.4. The ram speed was varied over two orders of magnitude from 0.0027 to 0.26 in. per sec. The ram was water-cooled during most of the tests, although some experiments were conducted with a preheated, uncooled ram. All extrusions were run without lubricant, which resulted in conditions of sticking friction. EXPERIMENTAL RESULTS Stress Dependence of the Strain Rate Neglecting Adiabatic Heating. The maximum force required to extrude is given in Table 1 for each of the five initial

Jan 1, 1970

By E. F. Draskovich

In 1984 a high temperature heat recuperation system was installed in the pellet plant of the National Steel Pellet Company located in Keewatin, Minnesota. The system is similar to those of Cleveland Cliffs Empire and U.S. Steel's Minntac operations. It recovers hot process air from the cooler by induced flow, and directs it to an intermediate zone between the drying and preheat zones on the grate machine. This system recently underwent further modifications in April 1985, following initial operation in 1984. The M. A. Hanna Company, which manages the property, developed the design criteria and made the subsequent recommendations for modification through its research facility in Nashwauk, Minnesota.

Jan 1, 1986

Roasting treatments were investigated to remove arsenic from a nickel concentrate. The main arsenic minerals and their proportions in the concentrate were niccolite (NiAs)-50%, gersdorffite (NiAsS)-40% and arsenopyrite (FeAsS)-10%. Thermal analysis showed that gersdorffite and niccolite began decomposing when heated above 640 and 830°C respectively. The maximum roasting temperature was limited by agglomeration of the concentrate above 900°C. A small vibrated bed reactor was used to investigate the effects of temperature and gas flowrate, the latter to sweep away evolved arsenic. At 900°C, 24% of the original arsenic remained in the concentrate. SEM examination of the calcine showed that the residual arsenic was associated with the calcium in the gangue minerals. Additions of sulphur (either as elemental sulphur or from pyrite) facilitated the decomposition of the arsenic-containing minerals, decreased reaction with calcium in the gangue and produced calcine containing 4-6% of the original arsenic. Treatment with chlorine during roasting was effective in reducing the arsenic content to similar levels. Generation of chlorine in the bed by sulphation of CaC12 also produced encouraging results. Arsenic, Nickel Concentrate, Roasting, Chlorine, Sulphur, Gersdorffite, Niccolite

Jan 1, 2005

By Stanley A. Bunk, Desmond J. Bruyns

The purpose of roasting gold ores is to release for extraction, typically by cyanidation, the small particles of gold which are surrounded by refractory stone. The roasting simply opens up passages for the penetration of solution into the interior of the ore particles. This is accomplished by the removal by volatilization or formation of volatile oxides of certain constituents such as sulfur, arsenic or antimony. Temperature is an important parameter. High temperatures tend to form a dense iron particle rather than a "spongy" calcine. The dense iron particles result in lower gold recoveries. High temperature can cause melting of some components which also results in gold encapsulation. Roasting of refractory gold ore concentrates has been practiced for decades. Multiple hearth, rotary kiln and muffle reactors were first used for roasting. Fluid bed roasting provided a low capital cost, low maintenance technology with better process control and soon became the favored technology. The first fluid bed concentrate roasters were commissioned in the late 1940's. Early fluid beds were "bubbling" type. Environmental considerations did not significantly impact on the design. Feedstocks were highly exothermic and reaction rates were relatively rapid. Roasting today must compete with other technologies for treatment of refractory ores. Ore bodies which are not

Jan 1, 1993

By J. R. Kadambi, E. Kucukal, J. Furlan

"Hydrocyclone separators are used in various industrial applications, including mining milling and tailings systems, in order to separate or classify solid particles and liquid droplets from multiphase systems. The flow within a hydrocyclone commonly used in the mineral processing industry was investigated numerically and experimentally using Particle Image Velocimetry (PIV) and refractive index matching techniques. The computational simulations were performed using a commercially available CFD package, STAR CCM+. Two turbulence models were used in the numerical calculations: the k-? model and the Reynolds Stress Model (RSM). In both cases, the first order discretization scheme was unable to resolve the flow characteristics accurately due to the high levels of numerical dissipation. PIV measurements were taken at various spatial locations along the cyclone. Both the numerical simulations and PIV data demonstrate that tangential velocities tend to increase when going radially inward from the cyclone wall towards the vortex finder, and reach a maximum value before they begin to decline rapidly and eventually become zero at the wall. The results also demonstrate the utility of non-axisymmetric approaches in cyclone flow simulations for a greater understanding of the fluid mechanics. The computational results were validated globally using pressure and flow rate readings at the boundaries and locally by comparison to the PIV velocity vector maps and profiles. The comparisons demonstrated good agreement between the two models.IntroductionHydrocyclones are devices used to separate and classify solid particles or liquid droplets from liquid-solid or liquid-liquid systems. Versatile in application, they have been widely used in many industrial applications including the food, oil, power generation, chemical and mineral processing industries since 1891, when the first hydrocyclone was introduced by Bretney (Park, 2003). Hydrocyclones have a relatively simple design with no moving parts, which leads to an efficient separation process."

Jan 1, 2016

By Afrânio Márcio Costa

Placas lingotadas continuamente, não obstante atendam a requisitos como composição química, conteúdo de inclusões, aspectos macro e micrográficos, podem ser desclassificadas por falta de conformidade dimensional. Contrações térmicas, de solidificação e de transformações de fases são partes intrínsecas do processo e são afetadas por alterações na taxa de extração de energia da placa durante o processo. Este conjunto de contrações determina o Fator de Contração de operação, o qual é utilizado para determinar as dimensões do molde que irão resultar na largura especificada, onde o presente estudo determinará o fator de contração dos aços peritéticos. As variáveis identificadas que influenciam no fluxo de calor primário foram: frequência de oscilação, superaquecimento, velocidade de lingotamento e viscosidade do pó fluxante. Identificou-se que o resfriamento secundário e a conicidade utilizado no molde, também são critérios determinantes para obtenção de larguras especificadas. Assim sendo, uma equação de regressão foi desenvolvida para o Fator de Contração.

Aug 17, 2017

By I. Javandel, P. A. Witherspoon

The finite element method was originally developed in the aircraft industry to handle problems of stress distribution in complex airframe configurations. This paper describes how the method can be extended to problems of transient flow in porous media. In this approach, the continuum is replaced by a system of finite elements. By employing the variational principle, one can obtain time dependent solutions for the potential at every point in the system by minimizing a potential energy functional. The theory of the method is reviewed. To demonstrate its validity, nonsteady-state results obtained by the finite clement method are compared with those of typical boundary value problems for which rigorous analytical solutions are available. To demonstrate the power of this approach, solutions for the more complex problem of transient flow in layered systems with crossflow are also presented. The generality of this approach with respect to arbitrary boundary conditions and changes in rock properties provides a new method of handling problems of fluid flow in complex systems. INTRODUCTION Problems of transient flow in porous media often can be handled by the methods of analytical mathematics as long as the geometry or properties of the flow system do not become too complex. When the analytical approach becomes intractable, it is customary to resort to numerical methods, and a great variety of problems have been handled in this manner. One such method relies on the finite difference approach wherein the system is divided into a network of elements, and a finite difference equation for the flow into and out of each element is developed. The solution of the resulting set of equations usually requires a high speed computer. When heterogeneous systems of arbitrary geometry must be considered, however, this approach is sometimes difficult to apply and may require large amounts of computer time. The finite element method is a new approach that avoids these difficulties. It was developed originally in the aircraft industry to provide a refined solution for stress distributions in extremely complex airframe configurations. 27 Clough has recently reviewed the application of the finite element method in the field of structural mechanics.6 The technique has been applied successfully in the stress analysis of many complex structures.l, 27, 28 Recognition that this procedure can be interpreted in terms of variational procedures involving minimizing a potential energy functional7 leads naturally to its extension to other boundary value problems. In the field of heat flow, there recently have been introduced several approximate methods of solution that are based on variational principles.2-4, 17 By employing the variational principle in conjunction with the finite element idealization, a powerful solution technique is now available for determining the potential distribution within complex bodies of arbitrary geometry. In the finite element approximation of solids, the continuum is replaced by a system of elements. An approximate solution for the potential field within each element is assumed, and flux equilibrium equations are developed at a discrete number of points within the network of finite elements. For the case of steady-state heat flow, the technique is completely described by Zienkiewicz and Cheung.33 Since the flow of fluids in porous media is analogous to the flow of heat, Zienkiewicz et al. have employed the finite element method in obtaining steady-state solutions to heterogeneous and anisotropic seepage problems. 34 Taylor and Brown have used this method to investigate steady-state flow problems involving a free surface.25 The work of Gurtin has been instrumental in laying the groundwork for the application of finite element methods to linear initial-value problems.12 As a result, Wilson and Nickell have recently

Jan 1, 1969