Search Documents

By J. C. Bradley

THE relation of annealing temperature to conductivity of copper wire has been determined. Conductivity hard was 98.26 per cent. After a 10-min. heating at 200°C. it was 98.69. By annealing 10 min. at 300° C. a large increase, to 100.93, occurred. Maximum conductivity, 101.15, was attained after a 500° C. anneal; thereafter it decreased to 100.53 after a 950° C. anneal. If copper is gassed the decrease is much more than this. Materials and Methods The work was done on high grade electrolytic copper, 99.942 per cent. copper plus silver, silver 0.0008 per cent. It was hot-rolled to >/4 in., then cold drawn to 0.080 in. The wire was cut into 25 5-ft. lengths and numbered 1 to 25 as cut. Four samples were tested hard. The others were wound into 5-in. diameter coils. For the 100° C. heating a coil was put into water, the water brought to boiling, and the wire kept at this temperature for 10 min. For the higher temperatures the coils were placed in envelopes of sheet copper, a little water added, and the envelopes sealed by folding over the edges twice, and hammering them together. This kept the air out very well. The envelope and wire 'were brought to the desired temperature; this was maintained for 10 min., then the whole was water-quenched.

Jan 1, 1927

By J. R. MacDonald

MINING literature contains very few descriptions of operations producing as little as 25 to 30 tons of ore per day. The purpose of this paper is to discuss the gradual development of a mining method for such a small-scale operation at the No. 2 mine of Central Patricia Gold Mines, Limited, and in doing so to review several systems of stoping applicable to narrow ve1ns. MAIN ECONOMIC FACTORS TO BE CONSIDERED (1) Overhead.-The outstanding feature of most mines operating on a single narrow vein is chat of small daily tonnage. The reason for this low output can be readily understood. The strictly limited ore-reserves present a condition unfavourable for a policy of large initial expenditures, with the result that the capacity of the plant provided must be governed by the? amount of ore in sight at the time when mill construction is planned. This is immediately reflected in the cost per ton, there being relatively few tons over which to distributed the more or less static charges, such as hoisting, heating, supervision, administration, pre-production expenses, and other write-offs. (2) Development.-In mining this type of orebody, the main factor contributing to high costs is unquestionably the small tonnage of ore made available by a given amount of development. Thus, for example, from the data tabulated below it can be seen chat, assuming a 12-in. vein and a drifting cost of $9.00 per foot, the development charge for this item alone would be 71 cents per ton. Add to this the charges for raising, cross-cutting, shaft-sinking, and pumping, besides charges arising from development in waste, and the figure will be very considerably higher than 71 cents.

Jan 1, 1941

One of the earliest and continuing challenges in driving sustainable development in large scale resource industry projects is around the issue of assessment û how do you measure the sustainability of a mineral operation? One of the key road blocks when confronted with this challenge is the temptation of technical folks to reach for a definition of sustainability or sustainable development. But definitions, by definition, have boundaries and limitations that serve to constrain thinking û they limit the thinking of what we can achieve with sustainability (it also acts as a barrier that constrains innovation). Rather than seeking definitions, better understanding of the core perspectives around sustainability and their application to the minerals industry provides a much more powerful platform from which to conduct assessments. But it is only when these perspectives are combined with the right framework and supporting techniques that the complex becomes doable. With the support of the perspectives and the framework, various assessment and measurement methodologies can be used; the challenge is communicating to stakeholders the sustainability character of the project in ways that are meaningful and to which people can connect. Assessment is not about finding the best or most accurate methods that fulfil strictly academic and possibly abstract requirements. The challenge is to help people understand what the impacts are, and what the value contributions will be, in a format and language that make sense in their world-view.

Jan 1, 2009

By Junhyun Choi, Allan Gomez-Flores, Chonbuk National University, Siyoung Q. Choi, Gahee Kim, Seungkon Kim

In this study, to confirm the effect of depletion attraction on the flotation, we theoretically and experimentally investigate the effect of the depletion attraction force on flotation. While varying the concentration of the depletion agent (polyethylene glycol), three different systems are studied: pure malachite, pure silica, and a 1:1 mass ratio of malachite and silica binary system. We find that recovery increases significantly as the concentration of the depletion agents increases for all three systems, as the depletion agent facilitates the adsorption of the particle on the bubble surface. However, the recovery suddenly decreases in a certain concentration range, which corresponds to the onset of the decreased surface tension when high concentrations of the depletion agent are used. This non-monotonic overall recovery trend implies the surface adsorption of the depletant on a surface. The decreased surface tension of the air/water interface suggests that the recovery rate is lowered due to the adsorption of the depletion agent to the bubble surface, acting as a polymer brush. Based on our observations, we conclude that the depletion force can greatly improve particle adsorption, as predicted in the accompanying theory paper, while simultaneously the adsorption of the depletion agent on the bubble surface plays an important role because it hinders particle adsorption. We also perform experiments in the presence of a small amount of a collector, sodium oleate. An extremely small amount of the collector leads to the increase in the overall recovery, which eventually reaches nearly 100 percent. Nevertheless, the grade worsens as the depletant provides the force to silica particles as well as target malachite particles.

Jan 1, 2016

By E. W. Murbach

The oxidation of uranium carbide by oxygen at various pressures, and by air, has been investigated at temperatures up to 600°C. Arc-melted and cast uranium carbide displays oxidation behavior that appears to be dependent on its treatment after melting. ccReactive" uranium carbide, which results from exposure of freshly melted material to laboratory air, ignites in oxygen at about 275° to 350°C depending on pressure, and in air at about 350°C. The product of the initial oxidation appears to be UO2+.. Continued heating produces U30,. The initial oxidation rate is poportional, roughly, to the square root of the oxygen pressure. The activation energy determined for the initial oxidation reaction is 7.1 kcal, from 400° to 600°C in 10 mm of oxygen. AN investigation of low-decontamination methods for reprocessing uranium carbide reactor fuels is being carried out at Atomics International. One of the reprocessing cycles includes oxidation of the fuel at relatively low temperature (300° to 500°C) and reaction of the product oxide with carbon at elevated temperatures (above 1500°C) to produce uranium carbide. A number of small-scale experiments have been carried out in which uranium carbide was oxidized in air and oxygen at various pressures to measure reaction rates and to obtain other information concerning the oxidation process. In initial experiments with arc-melted UC, ignition was observed at about 275°C in oxygen or 350°C in air. However, similar experiments by Neymark' at 426°C in air showed no ignition. It was soon determined that the difference in oxidation behavior was due to the treatment of the UC following arc-melting. Neymark's experiments were carried out with freshly melted UC while those reported in the

Jan 1, 1963

By Howard C. Pettibone

Mine safety personnel reported occurrences of excessive "glove-fingering" and other problems with resin-grouted roof bolt installa tions. To study these problems, the Bureau of Mines designed a test plan to (1) obtain baseline information on several resin cartridges and (2) investigate the variables involved in the installation of a resin bolt. Three brands of resin representative of the industry in January 1983 were selected for cartridge evaluation. The installation variables selected for study were the method of installation, the hole depth, and the hole annulus. These variables were studied by installing a series of bolts in concrete blocks using different values for each variable. Results of the research show overspinning the resin may cause problems, but they can be avoided by using the spin times recommended by manufac-turers. Excessive glove-fingering is not a problem if the manufacturer-recommended installation procedures are followed.

Jan 1, 1987

By Jillian Spindura

This work investigates the carbothermic reduction of the complex sulphide mineral, pentlandite, in the presence of lime. The effects of change in temperature and the use of different carbon sources are studied and the role of these variables on the reducibility of pentlandite mineral is discussed. The microstructures of the heat-treated pellets are examined using X-ray diffraction and scanning electron microscopic techniques. The latter analytical method also allows any variation in the morphology and composition of the metallic phases formed, with temperature, to be considered. The kinetics of the reduction process is studied and the magnitude of the overall activation energy is determined from the plots of percentage reduction versus time.

Jan 1, 1996

By M. Neises, M. Roeb, C. Sattler, S. Stenger

"A two-step thermo-chemical cycle process has been developed and investigated. It is based on metal oxide redox pair systems, which can split carbon dioxide as well as water molecules by extracting oxygen atoms and reversibly incorporating them into their lattice. If concentrated solar radiation is used as the heat source, a promising method exists to produce synthesis gas from water and CO2. An easy way of operation is gained by the combination of a ceramic substrate as the absorber structure, which can be heated to high temperatures with concentrated solar radiation, and of a metal oxide coating which is capable to carry out the redox reactions. The performance and kinetics of a ferrite based redox material coated on ceramic substrates were investigated in a laboratory set-up. CO2 could be reduced with significant conversions. In addition, several side reactions were observed like the formation of carbon and like the Boudouard reaction.IntroductionThe search for alternative energy carriers and for processes able to reuse carbon dioxide stimulates the research for sustainable routes of alternative fuel production. In the scope of this search thermo-chemical processes combined with sources of concentrated solar energy have become more and more attractive. Ideally, the only raw materials for such processes are water (H2O) and carbon dioxide (CO2) enabling not only a process free of emissions, but also allow to reduce emissions of other processes by reusing CO2 to provide synthesis gas, which itself can be applied to produce chemical commodities or even better synthetic fuels like methanol or petrol.In contrast to the direct splitting of those raw materials, thermochemical cycles split water and CO2 in several steps and enable hydrogen (H2) and carbon monoxide (CO) generation at temperatures controllable by today’s technical equipment. One of the most interesting thermochemical cycles is a two-step process using metal oxide based redox systems. During the first step of this cycle (the regeneration step) the metal oxide is reduced setting some of its lattice oxygen free according to reaction (1). In the next step (the splitting) the reduced and activated material is oxidised by withdrawing oxygen from water and CO2 and at the same time hydrogen and CO is set free according to reactions (2a) and (2b) respectively."

Jan 1, 2011

By G. N. Carlson, C. H. Hazelroth, D. R. Dorrance

"Located on the north shore of the St. Lawrence River at Pointe Noire, Quebec are the agglomeration and ship-ping facilities of the Wabush Mines complex. Here, the specular hematite concentrate from the Scully Mine is received for further processing. Modern facilities for handling the ore, either to the 1plant or to stockpile, provide quick and efficient operation of the ore receiving station. Physical preparation of the ore for balling is accomplished with regrind ball mills, filters, bentonite crushing and drying facilities, pumps and related conveying circuits. Rotating table feeders deliver the reground and de-watered ore from storage bins to balling drums, where green ball or green pellet formation is achieved. The green balls are then conveyed to the indurating section. Three Dravo-Lurgi travelling grates, producing a total of 6,000,000 long dry tons of pellets per year, are used in the indurating phase of the operation. These grates, having 38 windboxes and firing at a temperature of 2,500°F, harden the pellets for shipment to various blast furnaces throughout the world."

Jan 1, 1969

By O Handayani, R Barr, E Isaaks

The mining industry has focused a great deal of attention recently on the impact of blast movement on grade control. Although the problem of blast movement and its contribution to dilution and ore loss is well known, solutions to the problem are less than satisfactory. Perhaps the most recent innovation is the application of blast movement monitoring (BMM) devices to quantify blast movement. These devices emit an electronic signal and are planted at surveyed locations within the preblast material. Following the blast, their new locations are found using an electronic scanner. The magnitude and direction of the blast movement is given by the vectors between the pre- and post-blast BMM locations. However, it’s not clear how the BMM vector data can be best used to minimise dilution and ore loss. One common solution is to displace preblast dig line polygons by distances indicated by the BMM vectors. However, studies of BMM vectors show that blast movement not only displaces material laterally but also mixes material internally within the bench (Thornton, 2009a).This paper presents a method for modelling the post-blast muck pile that accounts for displacement and internal dilution using simulated annealing. The preblast ore control block model is re-blocked to 1?×?1?×?1?m sub-blocks. Each sub-block is displaced by simulated BMM vectors conditional to post-blast surface topography and blast initiation sequence data in addition to BMM vector data. The displaced sub-blocks are aggregated into new ore control model blocks whose grades are calculated from the contained sub-blocks. New dig lines are then designed on the post-blast muck pile model using the new ore control block model grades. A case study based on actual data is provided.CITATION:Isaaks, E, Barr, R and Handayani, O, 2014. Modelling blast movement for grade control, in Proceedings Ninth International Mining Geology Conference 2014 , pp 433–440 (The Australasian Institute of Mining and Metallurgy: Melbourne).

Aug 18, 2014

By G. Włoch, E. Rudnik

The oxide fraction of industrial zinc ash was characterized in terms of chemical and phase composition, leaching behavior in sulfuric acid solutions, and leaching thermal effect. The waste product contained about 68 percent zinc (Zn), 7 percent chlorine (Cl), 2 percent aluminum (Al) and less than 1 percent other metals, such as iron (Fe), manganese (Mn), calcium (Ca) and silicon (Si). It consisted mainly of zinc oxide contaminated with metallic zinc and zinc hydroxide chloride. The dissolution of metals from the zinc ash was determined for solid-to-liquid ratios ranging from 100 to 500 kg/m3, acid concentrations of 10 and 20 percent, and temperatures of 20 and 40 °C. The best result — 130 g/dm3 Zn(II) at 95 percent zinc recovery — was obtained at a solid-to-liquid ratio of 200 kg/m3, sulfuric acid concentration RI SHUFHQWDQGLQLWLDOWHPSHUDWXUHRI ƒ& 7KH¿QDOVROXWLRQVZHUHFRQWDPLQDWHGPDLQO\E\0Q ,, DQG)H ,,, ions, but the presence of cadmium (Cd(II)) and lead (Pb(II)) ions enabled electrowinning of zinc of about 99 percent SXULW\DWKLJKFXUUHQWHI¿FLHQF\RI WR SHUFHQW /HDFKLQJRIWKHPDWHULDOZDVDQH[RWKHUPLFSURFHVVZLWKUHDFWLRQ heat of about 520 kJ/kg

By The Staff

BEFORE going into detail on the subject to be presented, a brief outline of the Company's earl y history would not be out of place. Prospecting and mining on a small scale was started in 1876 on the site of the present open pit at Thetford Mines. The property was purchased from the Crown in 1878 and Johnson's Company was incorporated in 1885. It is owned and operated today by descendants of the original shareholders. Many employees, through their fathers and grandfathers, have service records dating back three generations. The principal asbestos deposit at Thetford Mines is pear-shaped, with surface dimensions of about 2,200 feet in length by 1,300 feet in maximum . width. Its long axis strikes northeast and the dip is nearly vertical, but irregular in detail. It is known to extend to a depth 1,200 feet below the original surface, but its area at that depth has not been determined. Ownership of this deposit is divided among three active Companies: the Asbestos Corporation, Limited; Bell Asbestos Mines, Limited; and John-son's Company. Johnson's Company owns a section about 1,000 feet in length and 500 feet in width, bounded on the northeast by the King mine of the Asbestos Corporation and on the northwest by the Bell pit. On Johnson ground, there was originally a large outcrop o~ asbestos rock which dipped toward the south below overburden. This was mined until recently by open pit, the overburden being stripped off as far southward from the original outcrop as was economically possible. As the. pit was deepened, within side walls maintained at a maximum safe slope, its floor area, of course, became progressively smaller, and eventually the pit would have wedged out against the Bell property line. It became necessary, there-fore, to introduce some other method of mining before production became seriously curtailed by a shrinkage of the pit area.

Jan 1, 1941

By Claude W. Sill

In the course of a series of investigations on vanadium deposits of the western United States, the Bureau of Mines collected many hundreds of samples for chemical analysis. As uranium is often associated with these vanadium minerals, they were also analyzed for uranium, which was pound to be absent in a large percentage of the samples. Since the usual methods for determining uranium are laborious and time-consuming it is very desirable to have some simple qualitative test that can be applied prior to a quantitative analysis to determine whether uranium is present or absent and thus save the time and expense of applying the quantitative analysis to the large proportion of samples containing no uranium. To be acceptable, the test should be specific for cranium, sensitive enough to detect small amounts of uranium, and. simple enough to make it worthwhile to apply. The available methods for detecting uranium lacked one or more of the desired characteristics. Eventually, however, a method was worked out that satisfied all the requirements. This method is probably more specific and sensitive than the usual qualitative methods for uranium, and its simplicity and speed of application make it ideal for testing samples prior to quantitative analysis.

Jan 1, 1945

By G. Guiglionda, A. Deschamps, F. De Geuser, M. Langille, B. J. Diak

"Increased demand for light-weighting in passenger vehicles has created a need for strong, light, ductile materials to be used in body-in-white applications. The AA6xxx-series of aluminum alloys are suitable candidates meeting most requirements but can fall short of the formability demands of designers, necessitating an understanding of what controls the formability in this alloy series. This work examines the effect of copper alloying in AA6xxx on the pre-ageing and natural ageing responses of the microstructure and mechanical properties. The changes in microstructure observed by differential scanning calorimetry and hardness testing are related to the work-hardening and strain-rate sensitivity parameters for these alloys measured by tensile testing. An observed asymmetry in the measured strain-rate sensitivity associated with increasing versus decreasing strain rate changes suggests that a different mechanism operates for the two conditions. It is postulated how this asymmetry in strain-rate sensitivity will impact the necking and ductility behaviour of these alloys.INTRODUCTION The widespread use of AA6xxx series alloys in the form of sheets has provided the need for a more thorough understanding of the complex interactions between composition, processing, resulting microstructure and ultimately, the mechanical properties of the alloys. Conventional industrial practices involve the production of rolled AA6xxx sheet (typically 1 mm thick) to be used for body-in-white (BIW) applications for auto body panels (Hirsch, 2004, 2014). The final metallurgical step prior to the shipment of these panels to manufacturers involves a solution heat treatment (SHT) reverting the ageing products of the alloys into solid solution and the product is then shipped to the customer. During this shipping time and while sheets are waiting to be used, the natural ageing (NA) process occurs whereby the strength of the alloys increases resulting in reduced formability. This can result in a product that is unable to meet the formability demands of the automotive manufacturer. As a result, industry has moved towards performing pre-ageing (PA) treatments to prolong the “shelf-life” of the material prior to it having insufficient formability. Once formed into BIW panels, the parts are then painted and subsequently undergo the paint curing heat treatment which consists of a short period of time at medium temperature, typically 20 minutes at 170–190°C. This short artificial ageing (AA) treatment, known as the paint bake (PB), provides additional strength and improved dent resistance for the material, but reduced formability. The PB result is strongly dependent on the PA treatment performed prior to the forming operation. Furthermore, the addition of copper (Cu) to a base Al-Mg-Si composition is known to increase the alloy’s strength. The goal of this work is to study the effect of Cu on strength, strain hardening, and strain-rate sensitivity (SRS) of these alloys, to understand the strength-formability compromise, for two separate heat treatment schedules; one including and one excluding the PA treatment, both followed by NA."

Jan 1, 2018

By Fazel G. Jahromi, Ahmad Ghahreman

"Several studies were performed on the atmospheric leaching of copper sulfide minerals in the presence of activated carbon and a new catalyst, AF 5. AF 5 is a carbon based catalyst with similar properties to those of activated carbon however much better mechanical properties. The activated carbon surface chemistry has been investigated in various studies; however the connection of the surface chemistry of activated carbon and AF 5 with the sulfide minerals during the atmospheric leaching process is not well-understood yet. Based on the surface analysis, AF 5 showed higher surface area than activated carbon (AC). Adsorption and oxidation of copper, arsenic and iron ions in the presence of different activated carbon were investigated. Adsorption properties of both catalysts were similar and 18-24% of iron, 12-18% of copper and 10% of arsenic adsorbed on the catalysts surface form 5 g/L Fe(III) and Cu(II) and 2 g/L As(III) at 80°C. In oxidation experiments, both catalysts reduced Fe(III) and Cu(II) ions and re-oxidized the reduced species in the presence of oxygen and oxidized As(III) ions. The addition of oxidizing ions can enhance the oxidation process kinetics and increase the catalytic capability of carbon.INTRODUCTION Hydrometallurgical processes of copper sulfide concentrates are under development and various different methods have been proposed to increase the atmospheric leaching rate of copper sulfide minerals. These methods include using different media, reagents, and catalysts. Among different methods, leaching of the copper sulfide minerals in the chloride media has some advantages over sulfate media. Smaller scale of operation, increased leaching rates, and lower sulfate formation are some of the benefits of the chloride leaching media over other similar media. Moreover, using ferric and cupric ions as oxidants and utilizing activated carbon as a catalyst has been proven to enhance the leaching rate of copper sulfide minerals effectively. Activated carbon (AC) and AF 5 (micro porous carbon based catalyst) are two of the most efficient and practical catalysts in copper sulfide leaching processes. AC can enhance the copper recovery of enargite in chloride media from 69% to 92% after 96 hours of leaching under the similar conditions (Jahromi & Ghahreman, 2016). It has been shown that AC at acidic pH can generate hydrogen peroxide in the presence of oxygen which can leach copper minerals (Ahmumada et al., 2002)."

Jan 1, 2017

By Harry H. Power

WORK of the Committee on Education of the Petroleum Division has been under way for approximately-one year. Although some progress has been made, further activities of the Committee are necessary in order to discuss mutual problems more thoroughly by a unified group interested primarily in this field of specialization.

Jan 1, 1944

By W. K. Hitchcock

Anecdotal evidence suggests that re-entering a sealed heating poses a significant hazard, whereby the original heating is rejuvenated at an accelerated rate forcing withdrawal and re-sealing of the area. Bulk-scale laboratory experiments using a two-metre column confirm these mine site observations. A high volatile bituminous coal from New South Wales, Australia was allowed to develop a significant hot spot before being inerted with nitrogen and allowed to cool. Air was then allowed back into the coal after the nitrogen was turned off and a hot spot developed almost immediately at the same location as the original hot spot before it quickly migrated towards the air source within a day. Two more re-entries were simulated. Each successive re-entry developed a broader hot spot and took longer to reach thermal runaway. These results clearly show the behaviour that can be expected when trying to recover a section of an underground coal mine that has been sealed due to a spontaneous combustion event.

Jan 1, 2009

By R Ayothiraman

Tunnel excavation may induce adverse effects on nearby existing structures/foundations in urban areas. Accurate prediction of tunnelling effects on pile foundations of nearby structures in the urban environment poses a major challenge during design. Several studies have been undertaken to understand the mechanisms of the soil-tunnel-pile interaction, which focused only on influence of tunnelling on nearby existing building and foundations. However, effect of pile loading on existing tunnels did not receive enough research attention so far. So it is essential to measure the response of existing tunnel-lining due to loading on newly constructed pile to assess to the safety against the additional forces/moment caused by pile loading and to evaluate the critical distance for the proposed construction of any structures from the tunnel location. This paper presents result of three-dimensional (3D) finite element analysis carried out in ABAQUS to investigate the effects of pile loading on existing tunnels embedded in cohesive soil. It is found that the effects on tunnel lining depend on horizontal separation distance between pile and tunnel as well as location/elevation of pile tip with respect to tunnel location.

Mar 8, 2011

By Angelina Anani, Nilufer K. B. Akbulut, Sefiu O. Adewuyi

Crucial information about safety, design and operation from ground movement data can be utilized in underground mines. Communicating the information and exploring new findings can be a challenge, however, in a decade where there is an ever-increasing volume and velocity of data due to advancements in mining technologies. This challenge escalates for geotechnical data as they are multidimensional, depending on the space and the rate at which they take place. To tackle this challenge, geotechnical engineers should focus on using simple yet compelling visualization of rock mass data in 3D. Competent visualizations of ground conditions as a trigger action and response plan (TARP) could ease the communication of safety concerns and the exploration of rock mass displacement and strain surrounding an opening at an underground mine. Therefore, this study focuses on using scientific visualization methods by rendering geotechnical data over the surface of a 3D mesh model to display TARP levels. The study was conducted at the East Decline of the San Xavier (SX) Underground Mine, a laboratory mine operated by the University of Arizona. The project aims to produce visualizations that optimize the use of geotechnical data in near-real time.

Sep 1, 2025

By G K. N Subasinghe

Metallurgists operating Knelson Concentrators (KC) often rely on manufacturerÆs recommendations for selecting operating parameters, such as fluidising water flow rate and cycle time. Recent studies have shown that these parameters are not only dependent on the machine parameters but also on the feed characteristics, such as size distribution of the gold and gangue particles and the composition of its constituent minerals. It is known that a particle entering a KC initially traverses a circular path within the bowl. For a particle to maintain a given orbit, the required centripetal force must be supplied by external means. It has been argued that this centripetal force, which is dependent on the mass of the particle, its radial position and the rotational speed of the bowl, is provided by the fluid drag force created by inwardly moving fluidising water and the BagnoldÆs force created by the particle/particle collisions. Depending on the fluidising water flow rate, one of two situations can occur where the porosity of the bed increases or decreases, which influences the amount of material retained within the bowl. The amount of material of a given size and density retained in the bowl is thus dependent on the extent of the centripetal force provided. Based on the above concept, a criterion that can be used to predict the amount of material recovered in the bowl has been derived and validated by experimental data. It may also be construed that this criterion demarcates the transition of the bed from a packed-bed state to a fluidised state. By identifying the transition values for the different constituent mineral particles in the feed, it is possible to estimate the optimal fluidising water flow rate that would maximise gold recovery while minimising gangue recovery. In addition, the kinetics of gangue displacement by incoming heavy mineral particles were also studied using synthetic mineral mixtures. The experimental data suggests that this process follows first order kinetics and that the build-up of heavy mineral reaches a maximum. A model has been proposed to predict the optimal batch cycle time for a KC in terms of the feed characteristics and machine operating parameters.

Jan 1, 2006