By T. J. Koppenaal, M. E. Fine

A yield point effect attributed to short-range ordevi?g (SRO) occurs in Cu base Al. At at 296°K varies with heat treatment, decreasing as the annealing ternperature is raised .from 433Oto 598°K. Davies aid Cahn' observed a corresponding decrease in SRO. (523 °K anneal, measured at 77°K) is approximateZy proportional to the variations of A7 with strain rate and testing temperature are also Consistent with the idea that is associated with SRO. A preliminary investigation of the tensile properties of a Cu-Al single crystals showed the presence of a rather strong yield-point effect (drop in flow stress after initial yielding). The object of this research was to investigate its origin and behavior. a Cu-Al alloys are particularly interesting because diffuse X-ray scattering measurements by Davies and Cahn,' Houska and Averbach,' and Borie established the presence of short-range order. The degree of local order may be changed with heat treatment.' cottrel14 suggested that the presence of local order might result in a yield-point effect, and thus the possibility exists here for experimentally ascertaining the importance of short-range order with respect to yield points in these alloys. Since a 12 pct difference exists between the atomic sizes, elastic or Cottrell locking5 must also be considered. Further, Howie and swanne have shown that the stacking fault energy of copper is reduced by aluminum additions. The width of extended dislocations should thereby increase. hus the conditions appear attractive for Suzuki locking.' Finally, the possibility of stress-induced order at dislocations, schoeck locking,' must also be examined, EXPERIMENTAL PROCEDURE Alloys up to 14 at. pct Al were prepared by induction melting high-purity (99.999 pct) Cu and (99.996 pct) Al in a graphite boat under a dynamic vacuum of 5 X 10o mm of Hg. After homogenizing the ingots at 900°C for at least 24 hr under vacuum, they were rolled with intermediate anneals to strips 1.55 mm thick. Single crystals 10 in. long were grown by lowering strips, contained in a split graphite mold sealed in fused quartz at 5 X lo-' mm of Hg, through a single coil induction heater at a constant rate of 1/2 in. per hr. Tensile specimens 1.25 in. long were cut from the single crystal strips and reduced cross sections about 0.7 in. long and 3.0 to 3.5 mm2 in area were introduced by filing and abrading.8 To remove the worked portion about 10 pct of the cross-sectional area was removed by etching. Back-reflection Laue photographs of a filed and etched specimen were taken before and after annealing at 900°c for 24 hr. Small, well defined Laue spots were obtained with no visual difference in the two photographs. Further, specimens with and without the reduced sections began yielding at about the same stress. Hence, for our purposes, filing and abrading did not affect the structure of the specimens. Each single crystal specimen was annealed at 900° c in vacuum for at least 24 hr and furnace cooled; while cooling through the range of 250o to 200°c, the rate was about 55°C per hr. Orientations were determined by the usual back-reflection Laue

Jan 1, 1962

By J. C. Swartz

New measurements of graphite and cementite solubilities in ferrite have been obtained to resolve disagreements among previous data. To measure graphite solubility, specimens of iron were equilibrated with rarious carburizing atmospheres at temperatures be-twee~z 480" and 1435°C. The carbon activity of each atmosphere relative to graphite was taken from published data. After quenching from each equilibration treatment the concentration of carbon (typically 10 pprn by wt) was determined from the height of the Snoek peak in the internal friction spectrum. A few inclividual analyses by combustion support the reszdts of Smith on the solubility of graphite near the eutectoid temperature. Combination of these combustion and internal friction analyses determines In a, (at 0.01 wt pct) = 24,000/RT - 12.72, where a, is the activtity relative to graphite in ferrite at fixed cornposition. The same specimens were used to determine the solubility of self-stressed cementite precipitates. The results indicate solubilities of 6.3, 23.2, and 68 pprn carbon by wt at respectively 400°, 500". and 600°C. The once large discrepancy between the cementite solubility determined by internal frictiori and that calculated from flee energy data has been almost completely resolved. A recent study1 (hereafter designated I) on the solubility of cementite in a iron did not fully resolve the disagreement among previous data. The remaining disagreement is illustrated by the phase diagram in Fig. L The data of I are represented by the line labeled "stress-free" cementite. They determine a heat of solution of cementite of (14.8 * 0.2) kcal per mole which contrasts with the (20 * 1) kcal per mole derived from Smith's graphite solubility2 and the formation energy of cementite.3 Toward resolving this disagreement we have obtained new data on the solubilities of graphite and cementite. METHODS As in I the Snoek peak in the internal friction spectrum was used to measure the concentration of carbon dissolved in ferrite. This method relies on the relation C=kQ-1 [1] in which C is the concentration of dissolved carbon, Q-I is the Snoek peak height, and k is a proportionality factor which is a function of the peak temperature, polycrystalline texture, and other parameters characteristic of the ferrite lattice. To determine true heats of solution via Eq. [1], it is necessary to establish that k is independent of the temperature from which the specimen is quenched. Some evidence on this point is contained in a separate report.* Additional evidence is shown by the data points in Fig. 1. These represent the Snoek peaks of two specimens carburized to about 10 ppm C, copper plated, and quenched first from 888º then from 588°C. The copper plate was removed before each Snoek peak measurement. These data show that there is no detectable dependence of k on quenching temperature. The solubility of graphite was determined by repeatedly carburizing various specimens of iron wire with gas mixtures of known carbon activity relative to graphite. To cover a wide temperature range within the a phase boundaries it is desirable to use as low a carbon concentration as is compatible with reasonable precision. With the present internal friction apparatus the best compromise of these desires is a concentration near 10 wt ppm. The dashed line in Fig. 1 was used to approximate the activity of carbon* for

Jan 1, 1970

"Boston’s Central Artery passes beneath nine active railroad tracks carrying commuter and Amtrak trains into South Station, the City's busiest rail terminal. These railroad operations had to remain in service throughout the construction of the “Big Dig”. The solution was to jack the tunnel under the tracks, rather than build the tunnel by more conventional means.Jacking of utility pipes is fairly common, but jacking boxes as big as a highway had never been done in North America, until the Big Dig came along.Soil freezing was decided upon as a means of stabilizing the soil under the tracks. This allows the tunnels to be jacked into place without soil caving when the soil is excavated at the leading face of the advancing tunnel boxes. Hundreds of pipes were driven into the ground between the tracks. Inside the steel pipes were smaller plastic pipes. A freezing plant near the railroad tracks pumped refrigerated brine into the inner plastic pipes. The brine ran out the bottom of the inner pipe, flowed up to the top inside the outer pipe, and was re-circulated to the freezing plant and back again into the ground. Over several weeks the circulating brine drew the heat out of the soil little by little, and froze the ground outward from the pipes. Soil FreezingThe plan required the construction of jacking pits in which the tunnel boxes could be constructed, and from which they could be jacked forward to their final locations, as described in the accompanying article. Once the jacking pit was built and the tunnel box constructed inside the pit, crews made an opening in the headwall of the pit to allow passage of the tunnel sections, excavated about three feet of the frozen soil, pushed the tunnel box ahead, and repeated the procedure again and again."

Jan 1, 2003

By Frederic L. Kadey

Perlite, as a volcanic glass, has been recognized since the Third Century, B.C. (Langford, 1978). The precise details of discovery often become lost in antiquity, and the variations among the stories pertaining to the more recent discovery of perlite as a material of commerce are no exception. Credit in the United States is given to a dentist who, while experimenting with tooth enamels about 1941, discovered that perlite-the rock-intumesced when subjected to heat. At about the same time it is reported that the chief geologist of Silver and Barytes Ores Mining Co. attempted to put out a picnic bonfire on the shores of Milos Island, Greece by throwing beach sand on it. The ensuing pyrotechnic display immediately conjured up in that man's mind the possibility of a new use for the volcanic rock that constituted most of the island. Very little was done with this discovery either here or abroad until after World War II. Today the name perlite is applied to both the hydrated volcanic glass, generally of rhyolitic composition, and to the lightweight aggregate that is produced from the expansion of the glass after it has been crushed and sized. Petrologically, it is defined as a glassy rhyolite that has a pearly luster and concentric, onionskin parting. Occurrences of perlite are restricted to several Tertiary to Quaternary age rhyolitic belts that trend in a generally north-south direction around the world. Commercially suitable deposits generally occur as domes of several hundred feet in height, although glassy zones in welded ash-flow tuffs and others associated with dikes and sills also have been reported. Mining is by ripping and blasting from open pits. Because of weight considerations, perlite usually is shipped to the local market area for subsequent expanding. In the United States, New Mexico leads in production with Arizona, California, Nevada, Idaho, and Colorado following in approximately that order. The principal use for expanded perlite is as a lightweight insulating aggregate in cryogenics, in plaster, concrete, and in loose fill insulation. Expanded perlite is also used in horticultural applications, and after subsequent milling and classification, as a filter aid. The United States is the world's largest producer and consumer of perlite. Table 1 shows the world production of perlite and Table 2 shows the perlite mined, processed, expanded, and sold or used by producers in the United States. Geology Composition and Morphology Any discussion of perlite must take into consideration its dual nomenclature, for it is known by the same name as both the naturally occurring rock and, after processing and expansion, as the lightweight aggregate of commercial significance. In its naturally occurring form, perlite is a rhyolitic glass that contains from 2 to 5% combined water. While perlite also can occur as andesitic or dacitic glass, these latter types are of negligible commercial significance. Table 3 lists the chemical composition of a few typical perlites (Anderson, et al., 1956; Langford, 1979). What sets perlite of commercial significance apart from other volcanic glasses is the fact that under the proper conditions of preparation-crushing and sizing-it will, when rapidly introduced into a flame of sufficient temperature, expand or "pop." All of the elements of composition contribute to the expansibility of the rock. The role of the combined water, however, is the most significant because it is believed not only to produce a fluxing effect in the softening of the highly siliceous glass prior to expansion, but it is also responsible for the explosive force of expansion through volatilization during heating. The current theory of the origin of the water in perlite is now less con-

Jan 1, 1983

By S. A. Bradford

Internal-oxide precipitates in decarburized a iron alloys were studied by microscopic and X-ray methods. Diffusion of oxygen is primarily trans-granular, although large amounts of manganese or PhosPhorus cause preferred grain boundary dimsion at temperatures below 1450OF. Transgvanular internal oxidation follows the parabolic rate law with an apparent activation energy of 60 kcal per g-atom for decarburized rimmed steel and around 50 kcal per g-atom for higher alloy contents. The internal oxide is (Fe,Mn)0. Evidence was found for a miscibility gap in the FeO-MnO system. UNTIL very recently, the internal oxidation of metals was studied primarily as a scientific curiosity or, in a few cases, as a means of strengthening alloys by precipitation hardening. However, with the recent development of low-carbon enameling sheet steel, internal oxidation has become a problem of practical importance to the steel industry. For example, in 1961 it was reported1 that internal oxidation of steel can occur during decar-burization by open-coil annealing and will reduce the notch ductility of the sheet unless the process is carefully controlled. The present study was therefore undertaken to learn more about the rates and mechanism of oxygen diffusion and oxide formation in iron alloys. BACKGROUND The process of internal oxidation has been well-defined in the literature:',' oxygen dissolves in an alloy, diffuses inward from the surface of the metal, and reacts to form a precipitate with the alloying element that will provide the most stable oxide. he growth of the finely divided so-called subscale, i.e., the internal-oxidation zone, depends on the diffusion rates of both the oxygen and the reactive element.4 Investigators have generally found that increasing the temperature increases the size of the oxide particles, the rate of subscale growth, and the tendency to transgranular diffusion. With very few exceptions, the square of the thickness of the internal oxide layer is directly proportional to the reaction time. Given two conditions easily satisfied for iron systems— a) an oxygen solubility much less than the concentration of the alloying metal and b) an oxygen-diffusion rate to the oxide boundary much faster than that of the alloying element—then the general expression developed by Rhines and co-workers5 for the parabolic growth rate of the internal-oxide zone can be simplified to the following form: where Co and CM are, respectively, the solubility of oxygen and the concentration of the alloying element, DO is the diffusion coefficient of oxygen, O/M is the weight ratio of oxygen to metal in the precipitated oxide, and x is the thickness of the internal-oxide zone after an annealing time t. Both the oxygen solubility and diffusion coefficient can be approximately expressed as functions of temperature by Arrhenius-type equations: in which H and Q are, respectively, the heat of solution and the activation energy of diffusion. Consequently, the apparent activation energies calculated from Arrhenius plots are the sum of the heat of solution of oxygen in iron and the activation energy for diffusion of oxygen. The data, if not the interpretation, of Schenck et al.8 bear out the fact that oxygen diffuses in the atomic form. The general rate law for atomic diffusion is: the reaction rate being proportional to the square root of the pressure at low pressures. Benard and Moreau8 studied both the surface oxidation of Fe-Ni alloys and the gradual penetration of oxygen into the metal. They observed that oxide particles first form along grain boundaries and then grow to form continuous films that eventually envelop the grains. The parabolic rate law does not usually apply in these cases, especially at the higher temperatures. The oxide formed is wustite which gradually transforms into Fe3O4 and finally into Kennedy and coauthors8 examined Fe-Ni alloys with 26, 75, and 84 pct Ni oxidized at 800°C and

Jan 1, 1964

By L. S. Birks

The bainite transformation in a 3.5 pct Ni-1.25 pct Cr steel was studied under various conditions of cooling and stress. Several characteristics may be specified: 1) transformation in the bainite region (925° to 575°F) is very little affected by the manner of cooling from the austenitizing temperature at 1600°F to 575°F)tothe upper limit of bainite transformation at 925°F; 2) starting time for the bainite transformation is the same order of magnitude for either isothermal transformation or continuous cooling, but the rate of transformation is somewhat greater for isothermal transformation; 3) tensile stress accelerates both isothermal and continuous cooling transformation, and 32,000 psi stress changes the form of the isothermal transformation diagram to correspond in appearance to the continuous cooling diagram; 4) transformation for nonlinear, continuous cooling may not be determined directly from the linear, continuous cooling transformation diagram, but may be predicted by assuming first that the fractional amount of austenite transformed in a given small temperature interval depends on the approximate linear cooling rate during that temperature interval and then by summing stepwise over the whole temperature range. IN a previous publication' an X-ray spectrometer was described with which the X-ray diffraction from a specimen could be observed continuously under controlled temperature and tensile stress. This instrument has now been applied to a study of the austenite-bainite transformation in a Ni-Cr steel for both isothermal and continuous cooling conditions, with and without stress. Certain characteristics of the transformation lead to a method of predicting the amount of transformation to be expected at a given temperature for any type of cooling curve. Material and Specimen Preparation The steel chosen for the investigation was a Ni-Cr steel having the composition in the following percentages: 0.30 C, 0.27 Mn, 0.019 P and S, 3.50 Ni, and 1.25 Cr. In order to fabricate specimens suitable for the X-ray spectrometer, a 1/4 in. plate was ground down to 0.060 in. and then cold rolled to about 0.035 in. Next it was heat treated by quenching in oil from 1650°F and tempering at 1200°F for 1 hr. Then it was etched in dilute nitric acid to reduce its thickness to 0.014 in. and cut into blanks in the shape of flat tensile specimens 3 1/4 Vi in. long, 7/16 in. wide, with a notch % in. long and 7/32 in. wide; see Fig. 1. X-Ray Technique Since the X-ray spectrometer has been described in detail elsewhere,' only a brief outline of the principles will be repeated here. A focusing, pow- der-diffraction arrangement' was used, as shown schematically in Fig. 1, and the specimen was mounted vertically in a vacuum furnace (not shown in the figure). The X-rays, moving in a horizontal plane, enter and leave the furnace through beryllium windows. As shown in the figure, X-rays diverging from the line source A are diffracted by the specimen B and converge at the detector slit C. The detector D and the slit C may be set at the proper angle in the horizontal plane to receive X-rays diffracted by either the face-centered phase (austenite) or the body-centered form (ferrite, bainite, martensite). The specimen is heated by electrical conduction between connectors E, and E,, and a Pt—Pt-10 pct Rh thermocouple spot-welded to the center of the notched region on the side away from the X-ray beam indicates the temperature continuously on a Brown recorder. Temperature control is exercised manually with a variable transformer on the input to E,-E,. Any desired time-temperature relationship is easily obtained by first drawing the desired curve on the temperature recorder chart and then adjusting the variable transformer during the run so that the thermocouple

Jan 1, 1957

By O. P. Arora, M. Metzger, G. R. Ramagopal

The rates of grain boundary and general corrosion were surveyed by an approximate method. Quantitative differences between their variations with the strength or cupric ion content of the acid yielded large variations in their ratio, highly selective intergranular attack being observed only under specific chemical conditions. The boundary corrosion rate increased with the copper content of the aluminum; this was attributed to an autocatalytic effect similar to the one shown for general corrosion. High- purity aluminum in hydrochloric acid exhibits striking intergranular corrosion and other structure-dependent corrosion phenomena of fundamental interest. The behavior is highly sensitive to the metallurgical and chemical conditions, the significance of many of which has not been established. The features of the intergranular-corrosion phenomenon, first described by Rohrman,l are summarized in the remainder of this paragraph. Strong attack normally occurs only at high-angle grain boundaries.' Usually 15 to 25 pctHCl is used to obtain a high rate, but this has also been obtained with weaker (7 to 15 pct) acid either by adding cupric or ferric ion to the acid3-5 or by passing an anodic current (-0.1 ma per sq cm).2,3,5,6 The two latter corrosion conditions produce strong attack of low-angle boundaries after certain heat treatments 2-4,5,7 The susceptibility of high-angle boundaries is influenced by the grain-boundary segregation of iron atoms; this increases the slow (µ per month) attack in 10 pct HCl8 but diminishes the rapid (mm per month) attack in 20 pct Hc14 (the present and most previous investigations deal with rapid attack). That segregation of elements other than iron affects intergranular corrosion has not been demonstrated, although analysis of data for iron alloys indicated that at least one other element must be considered.9 Intergranular attack occurs over a wide range of purity although it begins to become obscured above several hundred parts per million (ppm) total im- purities by the severe general corrosion which accompanies the higher iron contents and which is associated with the presence of a second phase or an inhomogeneous distribution of the dissolved iron.4,6,10 The variation of intergranular-corrosion rate with heat treatment1'3-6'"10 can be explained in some cases in terms of the distribution of the iron impurity but is not in general adequately understood. The present work dealt with two questions not previously considered in detail. The first proceeded from the view that the extent to which a special behavior is associated with the boundaries is indicated not by the intergranular corrosion rate alone but by the ratio of the intergranular to the general corrosion rate. A comparison of the two rates was therefore made for one lot of aluminum in acids of varying strength and metallic ion content. The second question was the effect of the copper content of the aluminum. For general corrosion, it has long been known that copper ions introduced into the acid by corrosion of the solid solution are reduced on the aluminum as patches of elemental copper which enhance the corrosion rate by providing cathodes of lower hydrogen overvoltage than were originally present.''-'3 Since the copper patches remain themselves unchanged, their action is "catalytic", and since they are products of corrosion, the effect is "autocatalytic." This phenomenon is significant at copper levels much lower than previously suspected, even at those typical of high-purity aluminum, as the authors have shown in a previous paper.l4 The present work shows that copper content affects intergranular corrosion. With polycrystalline specimens, truly quantitative rate measurernents are not readily made for intergranular corrosion or for general corrosion in the presence of rapid intergranular attack, and previous work in this field has tended to be qualitative. The present study made use of a simple procedure which provided fair approximations to the quantitative corrosion rates and fitted the purpose of surveying the behavior over % wide range of conditions and displaying certain large effects. The approximations involved in this work were usually outweighed by the experimental scatter, which tends to be substantial in a system as sensitive as this one. I) EXPERIMENTAL A. Material. The material procured, Table I, represented three low copper (1 to 3 ppm) lots, two of "normal" copper content (21 and 22 ppm), and two

Jan 1, 1962

By E. J. Fasiska, H. Wagenblast

The dilalion of a ivon by interslilial carbon was measured by two independent techniques —dilatometric mesurements at 719 c and X-ray measurments of the urlil cell parameters a1 room temperature after quenching. The relative expansion per increase in cavbon content by both methods is (2.9 + 0.3) x 10-3 pev at. pcl C nrzd is temperature- independent within experimental error. This corresponds to (6.3 5 0.6) cu cm per g-atom for the partial gram-atomic volume of carbon in a iron-only slightly smaller than the atomic volume for iron in the same temperature vange. THE only previous quantitative study of the dilational effect of carbon dissolved in a iron was performed in 1934 by Burns1 which, at the time, generated some discussion of possible sources of experimental error.2 For a system of such widespread importance, we felt that a new investigation was merited. Both X-ray diffraction and dilation measurements were used to determine the expansion of the a iron lattice by dissolved carbon, avoiding as much as possible any previous experimental problems and deficiencies. The dilation method at solution temperature offers not only measurements which are free of residual strain but also, in conjunction with the room-temperature X-ray measurements, a method to detect any large temperature dependence of the partial gram-atomic volume of carbon. To insure that quenching strains did not affect the room-temperature X-ray measurements, wire specimens of constant carbon content but different diameter were examined for such an effect. SPECIMEN PREPARATION The material used for both experimental techniques was "Ferrovac E" iron received in the form of 19-mm-diam rod and stated as having the following impurity contents: C, Cr, Cu, Mn, P, and V, each in the range of 10 to 50 ppm; Co, O, Mo, S, and Si, 60 to 100 ppm; W, 200 ppm; Ni, 230 ppm; N, 4 ppm. The stock material was cold-swaged to 0.71 mm diam for the Debye-Scherrer X-ray camera specimens and portions were cold-rolled from 6.3 mm diam to 0.79- and 0.25-mm sheet for X-ray diffractometer and dilation measurements. The wires were annealed in wet hydrogen for 6 hr at 840°C and 15 hr at 720°C, and then quenched into 0°C water. A chemical analysis for carbon after this treatment gave 0.0046 + 0.0014 at. pct C. Three portions of these wires were subsequently held at 719°C in three different hydrogen + methane mixtures and then quenched, resulting in carbon concentrations of 0.0283, 0.0598, and 0.1067 at. pct C by chemical analysis. After carburizing, the wires were swaged to 0.48 mm and electroplated with silver to prevent carbon loss during subsequent heat treatment. The final heat treatment consisted of holding the wires at 72 1°C for 5 min in a He-2 pct H mixture followed by quenching into 0°C brine. The wires were held at room temperature for a few minutes to remove the silver plating using a phosphoric acid-hydrogen peroxide solution, and then stored in liquid nitrogen until the measurements were made. EXPERIMENTAL TECHNIQUE A) Dilation Measurement. The dilatometer consisted of a gas-atmosphere vertical tube furnace modified so that length changes of a ribbon-shaped specimen could be measured externally. This was done by installing a gas-tight mercury seal at the top of the furnace as shown schematically in Fig. 1. The specimen (21.0 cm long, 1.27 cm wide, and 0.25 mm thick) was suspended in the center of the furnace by 3-mm-diam quartz rods with the upper one passing through the cap of the mercury seal. Above the cap, the upper quartz rod was coupled to a lever exerting a load of about 25 g (-12 lb per sq in.) on the specimen and having a 10 times mechanical magnification. The vertical position of a marker at the other end of the beam was read with a traveling microscope with a precision of 0.01 mm. The temperature gradient of the furnace was meas-

Jan 1, 1968

By M. Cohen, D. Caplan

The scaling characteristics of three Fe-Cr alloys have been investigated by determining their weight gain vs. time curves at 1600° to 2000° F. The scales formed thereby have been examined using the techniques of X-ray diffraction and spectrographic and metal-lographic analyses in an attempt to explain the discontinuities in the curves and to elucidate the mechanism of scaling. DESPITE the considerable number of investigations that have been carried out on heat resistant alloys, the characteristics of the scales formed at high temperatures are not fully known. The research reported here was undertaken in an attempt to ascertain the mechanism of scaling of the stainless steels. Scaling experiments were carried out first, the weight increase of the specimens being followed continuously with time. It was observed that, as well as showing the expected decrease in oxidation rate with time, the oxidation curves showed breaks corresponding to intermediate periods of accelerated oxidation, after which protectiveness again increased. This phenomenon was observed with austenitic stainless steels (types 302, 309, and 330) and with Fe-Cr alloys (types 410, 430, and 446), but only the latter are treated in this report. An examination of the scales was made using the techniques of X-ray diffraction and spectrographic and metallographic analyses in an attempt to obtain a correlation between the nature of the scales and the oxidation curves. A search through the literature revealed only a very few previous reports of such periods of accelerated oxidation. Dunn' found breaks in the oxidation-time curves of some Cu-Si alloys but saw no rational explanation of the phenomenon. Heindlhofer and Larsen2 attributed a discontinuity in the weight gain-time curve of iron at 1290°F to the formation of blisters, the subsequent cracking of which exposed an unprotected surface and permitted rapid oxidation until a new protective scale had been reestablished. They advanced no explanation, however, for what they termed the peculiar behavior of a 27 pct Fe-Cr alloy at 2000°F which gained weight very rapidly in between two periods of very slow weight gain. Portevin, Pretet, and Jolivet3 in describing breaks in the weight gain-time curves of Fe-A1 alloys suggested that they might be associated with the occurrence of localized and deeply oxidized areas on the specimens. Bandel4 in a general discussion of oxidation curves of heat resistant alloys considered that the discontinuities were due to a local disruption of the protective layer by the growth of iron-rich oxides. Day and Smith" in their report on the scaling of a large number of iron alloys noted but did not explain occasional relatively rapid changes in oxidation rate at higher temperatures. Chevenard and Wache6 found breaks, often two per specimen, in the oxidation curves of an 18-8 type alloy. They suggested that the cause might be a depletion in chromium of the surface layer of metal due to its selective oxidation, the resultant high concentration of iron and nickel in the scale leading to a poorly protective scale. McCullough, Fontana, and Beck' explained the breaks in the oxidation curves of types 304, 430, and 410 alloys as due to mechanical ruptures. Experimental Work Table I lists the chemical compositions of the materials used. Cylindrical specimens 1/4 in. in diam and 11/2 in. long were machined from cold rolled % in. rod. After a fine finish cut with a sharp tool, the specimens were abraded while still mounted on the lathe with Nos. 2, 1, 0, and 00 metallographic grade emery papers. A 3/64 in. hole was drilled at a distance of 1/8 in. from one end to permit suspension in the furnace. Specimen Nos. 1, 2, and 3 were tested with this surface preparation. All others, after being similarly prepared, were electropolished in a perchloric-acetic electrolyte, electrical contact being made by pressing a tapered platinum hook into the drilled hole. The specimens were then washed in hot water, rinsed with distilled water, rinsed with methanol, dried at 120°F, and weighed. Thereafter,

Jan 1, 1953

By B. C. Raynes

IN the early part of 1952, under the auspices of the U. S. Atomic Energy Commission, Horizons Inc. undertook an investigation dealing with the preparation of high purity thorium metal in order to develop an economically competitive production process for this metal based on a recovery of the metal by a fused salt electrolysis, since a survey of the literature of thorium chemistry indicated that electrolytic methods had not received much attention, despite the consideration that electrochemical production methods often offer attractive commercial potentialities. Thorium metal has been prepared by methods which fall into four general categories: 1) reduction of halides or double halides; 2) reduction of the oxide; 3) thermal decomposition of halides; and 4) electrolytic methods. Some of the important results obtained by various investigators since about 1900 in recorded attempts to prepare pure thorium metal are summarized in Table I. A bibliography of pertinent literature is included in this paper. Thorium is strongly electropositive and possesses a great affinity for oxygen and nitrogen. As a result the prospects for the production of high purity thorium from aqueous media or oxygen bearing compounds are remote. The most promising and profitable area of investigation for production of thorium metal lies in fused salt electrolysis. Thorium has been produced previously by this technique from halide salts in fused alkali chloride eutectic mixtures. Until recently, however, the lack of known large uses for thorium has inhibited the investigation of these methods. The basic problem in an investigation into fused salt production methods for thorium is to develop a suitable fused salt system for the economic preparation of thorium. The first portion of the work in these laboratories was a small scale investigation of the electrolysis of potassium thorium fluoride, KThF5, under a variety of conditions. High purity thorium was prepared in this manner, but the process did not appear to offer the simplest and most attractive continuous commercial operation. The work reported here relates to an all-chloride system employing thorium chloride as the cell feed. ThCL4 was produced as an anhydrous material stabilized in molten sodium chloride. This product, further diluted in NaCl, was subjected to electrolysis. The electrolytic process has been studied in cells capable of holding up to 50 lb total salt charge. Ductile, pure thorium metal has been reproducibly obtained in this operation. Considerable experimentation was carried out in the preparation of ThCL as a cell feed free from moisture, oxides, and other impurities. Thorium was cathodically deposited as a coarsely crystalline powder interspersed with residual bath salts. Aqueous procedures for separating and recovering the metal were developed. The thorium metal powder obtained has been evaluated with respect to its hardness, chemical purity, and certain other physical properties. Preparation of ThC1,—Thorium chloride, and the chlorides of some other metals (aluminum, beryllium, tantalum, zirconium, etc.) cannot be obtained from aqueous solution by direct heating and evaporation. Evaporation and heating of a solution of thorium chloride yields a hydrated salt or partially hydrated salt, and finally Tho,. Anhydrous thorium chloride is obtained by forming a hydrated ammonium chloride complex salt in acidified water solution, dehydrating this compound, and finally decomposing the double salt and subliming the ammonium chloride component. Various methods for the preparation of anhydrous thorium chloride, in accordance with this concept, were investigated as indicated in Table I1 from hydrated thorium chloride (ThCl, . 3H2O), and from thorium oxycarbonate (ThOCO,). In the method found most satisfactory for this work, thorium oxycarbonate was dissolved in an excess of concentrated HC1 to give a clear yellow solution. At least 2 mol NH,Cl were added to the solution per mol of contained thorium. Ammonium thorium chloride hydrate was crystallized from solution by cooling and saturation with HC1. The resultant complex, (NH,Cl),ThCl;xH,O, was dehydrated by evaporation at 130° to 150°C and thoroughly dried at about 250°C. The dried ammanium thorium chloride was then mixed with sodium chloride in proportions to form NaThCL or to produce a ThCL4-NaCl mixture with a given thorium content. The ammonium chloride was sublimed off at temperatures above 500°C in an inert atmosphere furnace to give an anhydrous chloride source electrolyte, essentially free of Tho, and of NKC1.

Jan 1, 1958

By R. I. Jaffee, F. C. Holden, H. R. Ogden

The effects of grain size and shape on alloys of titanium with nitrogen and aluminum have been determined. Increasing a grain size decreases strength and hardness and increases impact resistance. Quenching from the ß field produces subgrain markings delineating a plates in Ti-N alloys but not in Ti-AI alloys. This suggests a precipitation from the high nitrogen alloys. ALPHA titanium alloys are single-phase alloys with the hexagonal-close-packed structure of a titanium. If these alloys are worked and annealed within the a field, equiaxed structures result in which strength is derived from the solid solution of the alloying elements present. Strain hardening can be used to increase further the strength of a titanium alloys. This is the only other mode of strengthening the a type of alloy. Quenching from the ß field has been noted by many investigators to have little effect on the strength of iodide titanium and on commercial titanium. Ti-A1 alloys were found to be little different in hardness, whether annealed in the a field or quenched from the ß field.' These facts illustrate a characteristic of a titanium alloys: they are insensitive to heat treatments from the ß field. Underlying this heat-treatment insensitivity are the facts that the a-ß field is generally narrow in a titanium alloys, the transformation-temperature range increases with a-stabilizing content, and the a solubilities of the alloying elements are greater than the ß solubilities. When quenching is done from the ß field, there is no supersaturation of the alloying elements in the acicular transformation structure produced. Welds in a titanium alloys generally are ductile, because no transformation hardening occurs during cooling.1,2 Other desirable features of a alloys are: no thermal-stability problem, excellent toughness, and retention of strength at elevated temperatures better than a-ß or ß alloys of comparable room-temperature strength. The prime factors governing the properties of a titanium alloys are the amount and kind of solute present. This can change the a phase from a soft, tough material into a hard, brittle material with no apparent change in microstructure. Moreover, brit-tleness can exist over a wider alloy-content range, without change of phase, than in most other metals. The solutes for a titanium may be divided into interstitial and substitutional types. Oxygen and nitrogen dissolve interstitially in rather large amounts, extending well through the brittle range, and the transformation-temverature ranges are raised in the process.:' , carbon has a maximum interstitial solubility of about 0.5 pct at the peritectoid temperature, while at lower temperatures the solubility decreases to about 0.2 pct.3,5 Substitutional a solutes include aluminum and tin. Aluminum has a high a solubility of 25 pct Al, and increases the transformation-temperature range markedly.6,7 Tin has a high a solubility of about 20 pct, but has a relatively innocuous effect on the transformation-temperature range.' The choice between interstitial and substitutional solutes generally has been conceded to the substitutional solutes because of a belief that they do not have as adverse an effect on ductility and notch toughness. However, a recent investigation8 on the effect of hydrogen on titanium has shown that this element, which is not under compositional control, has a powerful detrimental effect on notch toughness. Hydrogen was shown to form a hydride which is practically insoluble (about 0.002 pct) in a titanium at room temperature, although the solubility at the eutectoid temperature of about 300°C is relatively high, about 0.16 pct. Limited data were presented on the effect of hydrogen on a alloys, where the same impairment of toughness as in unalloyed titanium is found. The work reported here describes the effects of interstitial and substitutional solutes on 1—the mechanical properties of high purity titanium free of titanium hydride and 2—the influence of structural variables on these properties. Nitrogen was selected as an example of an interstitial solute with high solubility and aluminum as a substitutional solute with high solubility. All compositions were well within the ductile range, since it was not intended to study the brittleness problem here, but to study only the factors influencing optimum mechanical properties. Procedures The alloys were prepared from iodide titanium as 1/2 Ib ingots double melted to insure homogeneity.

Jan 1, 1955

By W. M. McKewan

Magnetite pellets were reduced in flowing hydrogen at pressures up to 40 atm over a temperature range of 350° to 500°C. The rate of weight loss of oxygen per unit area of the reaction surface was found to be constant with time at each temperature and pressure. The reaction rate was found to be directly proportional to hydrogen pressure up to 1 atm and to approach a maximum rate at high pressures. The results can be explained by considering the reaction surface to be sparsely occupied by adsorbed hydrogen at low pressures and saturated at high pressures. PREVIOUS investigation1,2 have shown that the reduction of iron oxides in hydrogen is controlled at the reaction interface. Under fixed conditions of temperature, hydrogen pressure, and gas composition, the reduction rate is constant with time, per unit surface area of residual oxide, and is directly proportional to the hydrogen pressure up to one atmosphere. The reduction rate of a sphere of iron oxide can be described3 by the following equation which takes into account the changing reaction surface area: where ro and do are the initial radius and density of the sphere; t is time; R is the fractional reduction; and R, is the reduction rate constant with units mass per area per time. The quantityis actually the fractional thickness of the reduced layer in terms of fractional reduction R. It was found in a previous investigation2 of the reduction of magnetite pellets in H2-H,O-N, mixtures, that the reaction rate was directly proportional to the hydrogen partial pressure up to 1 atm at a constant ratio of water vapor to hydrogen. Water vapor poisoned the oxide surface by an oxidizing reaction and markedly slowed the reduction. The enthalpy of activation was found to be + 13,600 cal per mole. It was also found that the magnetite reduced to meta-stable wüstite before proceeding to iron metal. The following equation was derived from absolute reaction-rate theory4,8 to expfain the experimental data: where Ro is the reduction rate in mg cm-2 min-'; KO contains the conversion units; Ph2 and PH2O are the hydrogen and water vapor partial pressures in atmospheres; Ke is the equilibrium constant for the Fe,O,/FeO equilibrium; Kp is the equilibrium constant for the poisoning reaction of water vapor; L is the total number of active sites; k and h are Boltzmann's and Planck's constants; and AF is the free energy of activation. Tenenbaum zind Joseph5 studied the reduction of iron ore by hydrogen at pressures over 1 atm. They showed that increasing the hydrogen pressure materially increased the rate of reduction. This is in accordance with the work of Diepschlag,6 who found that the rate of reduction of iron ores by either carbon monoxide or hydrogen was much greater at higher pressures. He used pressures as high as 7 atm. In order to further understand the mechanism of the reduction of iron oxide by hydrogen it was decided to study the effect of increasing the hydrogen pressure on rebduction rates of magnetite pellets. EXPERIMENTAL PROCEDURE The dense magnetite pellets used in these experiments were made in the following manner. Reagent-grade ferric oxide was moistened with water and hand-rolled into spherical pellets. The pellets were heated slowly to 550°C in an atmosphere of 10 pct H2-90 pct CO, and held for 1 hr. They were then heated slowly to 1370°C in an atmosphere of 2 pct H2-98 pct CO, then cooled slowly in the same atmosphere. The sintered pellets were crystalline magnetite with an apparent density of about 4.9 gm per cm3. They were about 0.9 cm in diam. The porosity of the pellets, which was discontinuous in nature, was akrout 6 pct. The pellets were suspended from a quartz spring balance in a vertical tube furnace. The equipment is shown in Fig. 1. Essentially the furnace consists of a 12-in. OD stainless steel outer shell and a 3-in. ID inconel inner shell. The kanthal wound 22 in. long, 1 1/2, in. ID alumina reaction tube is inside the inconel inner shell. Prepurified hydrogen sweeps the reaction tube to remove the water vapor formed during the reaction. The hydrogen is static in the rest of the furnace. The sample is placed at the bottom of the furnace in a nickel wire mesh basket suspended by nickel wire from the quartz spring. The furnace is then sealed, evacuated, and refilled with argon several times to remove all traces of oxygen. It is then evacuated, filled with

Jan 1, 1962

By Vittal S. Bhandary, B. D. Cullity

Swaged iron wire has a cylindrical {001} <110> texture. The texture is also cylindrical after re-crystallization in the absence of a magnetic field, but <111> and <112> components are added to this texture when recrystallization occurs in a field. The mecizanical properties in tension and in torsion are not greatly altered by these changes in texture. AS shown in a previous paper,1 cold-worked wires of the two fcc metals copper and aluminum can be made relatively strong in torsion and weak in tension, or vice versa, by proper control of preferred orientation (texture). The deformation texture can be controlled by selection of the starting texture (texture before deformation), because certain initial orientations are stable during deformation. The present paper reports on similar work performed on bcc iron. In this case it was clear at the outset that there was no hope of controlling the deformation texture, which is one in which <110> directions are aligned parallel to the wire axis. (1t has usually been regarded as a fiber texture, but Leber2 has recently shown that it is a cylindrical texture of the type {001} <110>. In either case, <110> directions are parallel to the wire axis.) There is general agreement on this texture among a large number of investigators, which in itself suggests that the starting texture has no influence on the deformation texture. More direct evidence was produced by Barrett and Levenson,3 who reported that iron single crystals of widely varying initial orientations all had a single <110> texture when cold-worked into wire. Thus <110> is a truly stable end orientation for iron and probably for other bcc metals as well. Under these circumstances attention was directed to the possibility of controlling the recrystallization texture. This texture is normally <110> in iron,4 just like the deformation texture. However, it is conceivable that this texture could be modified by a proper choice of the time, the temperature, and what might loosely be called the "environment" of the recrystallization heat treatment. In the present work the environmental factor studied was a magnetic field. The effect of heating in a magnetic field ("magnetic annealing") on recrystallization texture has been investigated by Smoluchowski and Turner.5 They found that a magnetic field produced certain changes in the recrystallization texture of a cold-rolled Fe-Co alloy. The texture of this material is normally a mixture of three components, and the effect of the field was to increase the amount of one component at the expense of the other two. Smoluchowski and Turner concluded that the effect was due to magnetostriction. With the applied field parallel to the rolling direction, the observed effect was an increase in the amount of the texture component which had <110> parallel to the rolling direction. In the Fe-Co alloy they studied, the magnetostriction is low in the <110> direction and high in the <100> direction. Thus nuclei oriented with <110> parallel to the rolling direction will have less strain energy than those with <100> orientations and will therefore be more likely to grow. In a later paper on the same subject, Sawyer and Smoluchowski6 ascribed the effect to magneto-crystalline anisotropy and made no mention of magnetostriction. In the papers of Smoluchowski et al. the intensity of the magnetic field was not reported but it was presumably large, inasmuch as it was produced by an electromagnet. In the second paper6 it is specifically mentioned that the specimens were magnetically saturated. But if magnetostriction has a selective action on the genesis of stable nuclei during recrystallization, that selectivity must depend only on differences in magneto-strictive strains between different crystal orientations and not on the absolute values of those strains. Thus the saturated state does not necessarily produce the greatest selectivity, because the relative difference in magnetostrictive strains between different crystal directions may be larger for partially magnetized crystals than for fully saturated ones.7 In the present work the specimens were subjected to relatively weak fields (0 to 100 oe) produced by solenoids. MATERIALS AND METHODS Armco ingot iron rod (containing 0.02 pct C and 0.19 pct other impurities) was swaged from 0.25 in. in diam. to 0.05 in., a reduction in area of 96 pct. The mechanical properties in tension and torsion were measured as described previously.&apos; Textures were measured quantitatively with chromium or iron radiation and an X-ray diffractometer,8,1 and

Jan 1, 1962

By F. Claisse, R. Angers

Self-diffusion in iron has been measured during rapid a-r transformations using a variant of the Kryukou and Zhukhovitskii diffusion method. The study was performed by thermally cycling iron foils (1 to 6 cpm) through the transformation (=910°C). Some foils have been subjected to over 1000 cycles and some have spent more than 15 pct of their total diffusion time in the process of transformation. The experimental results show that the a-r transformation has no measurable effect on self-diffusion in iron. The study is completed by a quantitative analysis of mechanisms which can affect the diffusion rate during the transformation. The analysis confirms the experimental results. SINCE diffusion is an important factor in many solid-state transformations, it is of interest to study how it is affected by the stresses generated during these transformations. Clinard and Sherby1&apos;2 were the first to make a study along these lines. They measured diffusion coefficients in Fe-FeCoV couples subjected to slow thermal cycling (1.5 cph) through the a-r transformation range. They found an enhancement of diffusion by a factor of about two. The purpose of the present paper is to report measurements of the self-diffusion coefficient of iron during much more rapid thermal cyclings (1 to 6 cpm) through the a-r transformation (-910°C). These more rapid cyclings produce higher strain rates during the transformation and should emphasize any possible influence of transformation upon diffusion. EXPERIMENTAL Iron foils, 25 to 35 µ thick, were cold-rolled from 99.92 pct pure iron and annealed in pure helium for 2 hr at 870°C; the resulting grain diameter was about 150 µ. Specimens 0.5 by 8 cm were cut from the foils and I7e55 was vapor deposited on one of their surfaces. A 38 gage alumel-chrome1 thermocouple was spot welded in the middle of one of the specimen long edges, Fig. 1. Two 38 gage chrome1 wires were also spot welded along the same edge on each side of the thermocouple; they were placed 2.5 cm apart and used for electrical resistance measurements. In order to prevent twisting and crumpling, the specimens were pinched between two quartz plates 0.1 by 1 by 7 cm and the assembly was close fitted into a 1 cm ID quartz tube. Four holes were drilled through the tube to let the 38 gage wires out: these were connected to the recording equipment by means of extension wires. 20-gage nickel wires fixed at both ends of the specimens were used to thermally cycle the foils by Joule heating. The above described device was placed in a 2.7 cm ID quartz tube which in turn was placed in a tubular furnace. Either a pure helium atmosphere or circulating hydrogen was used during the experiments. Specimens were subjected to thermal cycles between a minimum temperature To and a maximum temperature Tm at rates ranging from 1 to 6 cpm. This was obtained by maintaining the furnace at a constant temperature near the minimum temperature To and periodically passing an electric current through the specimen. Cooling was achieved by heat losses to the surroundings. The forms and periods of cycles were varied from one specimen to another; however, each specimen was subjected to one type of cycle only. The temperature and electrical resistance variations of the specimens were recorded as a function of time. The temperature curves were used for diffusion calculations while the electrical resistance curves were used to monitor the transformation and to determine its starting point and its approximate duration. Diffusion was measured by the method developed by Kryukov and zhukhovitskii3 and modified by Angers and Claisse.4,5 In this method a metallic foil is coated on one side with a radioactive isotope and the activity is measured periodically on both sides during the diffusion anneal. The following equation then holds: where: I1 Activity on the surface on which the deposit is made. I, Activity on the opposite surface. t Diffusion time. B Constant. D Diffusion coefficient. d Foil thickness including the deposit. G(t) A function of time; it is a second order correction term which is given graphically in Refs. 4 and 5. The diffusion coefficient D is found by plotting ln[(Il - I2)/(I1 + I,)] -G(t) against t; the resulting slope m leads to an accurate calculation of D through Eq. [2]. The effect of the a-r transformation on diffusion is expressed by the ratio DT/DU where:

Jan 1, 1970

By R. H. Gautschi, F. C. Langenberg

Rare-earth additions were made to laboratory heats of Type 310 stainless to observe their effect on as-cast ingot structure, nitrogen and sulfur contents, and nonmetallic inclusions. Lanthanum had a grain-refining effect in 30-lb ingots, but results with 200-lb ingots were inconsistent. Cerium, lanthanum, and misch metal lowered the sulfur content when the sulfur exceeded 0.015 pct and the rare-earth addition was greater than 0.1 pct. The rare-eardh content in the metal dropped very rapidly within the first few minutes after the addition. The size, shape, and distribution of nonmetallic inclusions was not changed in 30-lb ingots, but changes were noticed in larger ingots. RARE-earth* additions have been made to austenitic Cr-Ni and Cr-Mn steels to improve their hot workability. The high alloy content of these steels often results in a considerable resistance to deformation and inherent hot shortness at rolling temperatures, particularly in larger ingots. Rare earths in the metallic, oxide, or halide form are usually added to the steel in the ladle after deoxidation although they can be added in the furnace prior to tap or in the molds during teeming. The literature- indicates that the effects of rare-earth treatments on these stainless steels are not consistent, and sometimes even contradictory. Since no mechanism has been presented which satisfactorily accounts for the claimed improvements, the effects of rare earths are a qualitative matter. The work described in this paper was initiated to expand the knowledge of the effects of rare-earth additions on melting variables such as ingot structure, chemical analysis, and nonmetallic inclusions. REVIEW OF LITERATURE Ingot Structure—Rare-earth additions to stainless steels have been reported to cause a change in primary ingot structure in that there are fewer coarse columnar grains. However, the results are inconsistent. While one investigation1 has shown a large reduction in coarse columnar crystals, another2 has been unable to observe this effect, particularly when small ingots were poured. Post and coworkers3 observed ingot structures for a number of years and found that the columnar type of structure is not definitely a cause of any particular trouble in rolling or hammering, provided the alloy is ductile. Knapp and Bolkcom4 found rare-earth additions to be quite effective in preventing grain coarsening in Type 310 stainless steel. Chemical Analysis—Many effects of rare-earth treatment on chemical analysis have been claimed in the literature. Russell5 observed that some sulfur is removed by rare-earth metals, and that a high initial sulfur content improved the efficiency of sulfur removal. Lillieqvist and Mickelson6 report that rare-earth treatment causes sulfur removal in basic open-hearth furnaces, but not in basic lined induction furnaces. Knapp and Bolkcom found no sulfur removal in acid open-hearth and acid electric furnaces, probably because the acid slag can not retain sul-fides. snellmann7 showed that sulfur could be lowered apprecfably with rare-earth additions; however, a sulfur reversion occurred with time. Langenberg and chipman8 studied the reaction CeS(s) = Ce(in Fe) + S(in Fe), and found the solubilit product [%Ce] [%S] equal to (1.5 + 0.5) X 10-3&apos;at 1600°C. Results in 17 Cr-9 Ni stainless were about the same as those in iron. Beaver2 treated chromium-nickel steels with 0.3 pct misch metal and observed some reduction in the oxygen content. He also noted an inconsistent but beneficial effect of rare earths when tramp elements were present in amounts sufficient to cause difficulty in hot working. It is not known whether rare earths reduce the content of the tramp elements or change the form in which these elements appear in the final structure. No quantitative data are available concerning a possible effect of rare-earth treatment on hydrogen and nitrogen contents. However, Schwartzbart and sheehan9 stated that additions of rare earths had no effect on impact properties when the nitrogen content was low (0.006 pct), but served to counteract the adverse effects of high nitrogen content (0.030 pct) on these properties. Knapp and Bolkcom4 analyzed open-hearth heats in the treated and untreated conditions and found the nitrogen content (0.006 pct) to be unaffected. These two results lead to the speculation that rare-earth additions can reduce the nitrogen content to a certain level. Decker and coworkers10 have observed that small amounts of boron or zirconium, picked up from magnesia or zirconia crucibles, increased high-tem-

Jan 1, 1961

By F. V. Lene, E. J. Westerman

The recrystallization behaviors of two extruded and cold-drawn experimental sintered aluminum powder alloys, containing 1.75 and 3.0 pct Al2O3 by weight, were compared with that of extruded and cold-drawn commercially pure alumirzum. The kinetics of recrystallization of the alloys are described semiquantitatively. For the alloy containing 1.75 pct A l203 the rates of nucleation and of growth were also semiquantitatively determined. THE most striking property of aluminum alloys strengthened by a dispersion of Al2O3, the so-called SAP alloys, is their stability at elevated temperatures. One of the manifestations of this stability is their resistance to recrystallization after they have been cold worked. Most of the commercial grades of either the Swiss SAP or of Alcoa&apos;s Aluminum Powder Metallurgy Products have not been recrys-tallized after cold working, even when they are heated for a long time at a temperature near the aluminum melting point. Lenel, however, observed that the dispersion strengthened aluminum alloys with a larger spacing between the oxide particles than that of most commercial grades would recrys-tallize.1 It appeared to be of interest to further investigate the mode and kinetics of recrystallization of these alloys, and to compare their recrystallization behavior with that of commercially pure aluminum. Because homogeneous deformation of these SAP alloys in tension did not provide sufficient cold work to induce recrystallization, they were cold worked by wire drawing; the nonuniformity of this deformation unavoidably complicated the interpretation of the recrystallization studies. EXPERIMENTAL DETAILS Extrusions—Two types of sintered aluminum powder extrusions were used in this study. One type, designated AT-400, was produced from Reynolds atomized aluminum powder consisting of spherical particles averaging 3µ in diam and containing 1.75 wt pct of Al2O3. This powder was very similar to the R3M powder from which extrusions were previously prepared with an average spacing of 0.9µ between oxide particles.2 The second type, designated MD 2100, was produced from Metals Disintegrating Co. flake powder containing 3.0 wt pct of Al2O3, with an average flake thickness of 0.8µ. The average spacing between oxide platelets in MD 2100 extru- sions was 0.45µ.2 Powder compacts of 3/4-in. diam were extruded at 1000°F into 0.097-in. diam (AT-400) and 0.093-in. diam (MD 2100) wires by methods previously described.3 In order to compare the recrystallization behavior of sintered aluminum powder extrusions with that of wrought commercially pure aluminum 3/4 in. rod stock of 1100 F aluminum was extruded at 1000°F into 0.102-in. diam wire. Wire Drawing—Tungsten carbide dies were used for the AT-400 and 1100 F alloys. They had an included angle of about 15 deg and reduced the wire area approximately 7 pct per pass. Steel dies with an included angle of 11 to 13 deg and an average reduction per pass of 10 pct were used for drawing the MD 2100 alloy, because drawing this alloy through the carbide dies produced overdrawing defects. Heat Treatment—The cold-drawn wires were cut into small samples, and the deformed ends were etched off. The samples were each wrapped tightly in a single layer of aluminum foil, and individually isothermally annealed in a lead bath. Metallography—The modes and kinetics of recrystallization were determined by metallography. Mounted and polished specimens were anodized in a solution of 1.8 pct HBF4;4 examination under polarized light clearly revealed their grain structures. The recrystallized grains were generally much larger than those of the unrecrystallized matrix, and could clearly be distinguished because they alternated between maximum and minimum light reflection when the microscope stage was rotated, while the unrecrystallized matrix had a comparatively homogeneous "salt and pepper" structure. The fractional recrystallized volumes of the dispersion hardened alloy wires were determined by cutting and weighing of recrystallized and total transverse areas on photomicrographs. The recrystallized grains in the 1100 F alloy were too small to be cut out individually; therefore a combination of cutting and lineal analysis was used in this case. RESULTS AND DISCUSSION Modes of Recrystallization—The modes of recrystallization of the three alloys varied widely. In the 1100 F alloy nucleation and growth started in the region midway between the center and the surface;

Jan 1, 1961

By A. J. Shaler

The subject of the mechanism of sintering has received much attention in the past few years, particularly since the beginning of the series of AIME seminars in powder metallurgy of which this paper introduces the fourth. In the first of these, F. N. Rhines1 brought together and discussed the available experimental data on the sintering of pure metallic powder, and succeeded in bringing to a sharp focus the attention of workers in this field on the established observations which a satisfactory theory must explain. Several other authors3,5,6 have, in the last few years, studied the phenomena that occur when cold metallic powders, loose or in the form of compacts, are first brought to elevated temperatures. Some workers&apos; in the field of friction have recently studied the adhesion of solid metal surfaces when they are brought into close contact. These researches have indicated that several separate mechanisms operate simultaneously, at least during the first part of the sintering process. Some of them have been called transient mechanisms4 because they are in general not absolutely necessary to sintering. Powders may be so prepared and so treated that these transient phenomena do not take place during subsequent sintering. This does not mean, of course, that their industrial and scientific importance is any less than that of the steady-state phenomena. The latter are changes that go on during sintering no matter how the powders are made or treated; they cannot be divorced from sintering. One way to analyze the process of sintering into its component parts is perhaps to distinguish between these transient and steady-state phenomena. Some of the transient phenomena have been studied in the past few years. Huttig3 has shown that, when the temperature of metallic powder is slowly raised, the following events generally occur in order: (1) physically adsorbed gases are desorbed; (2) there is an atomic rearrangement of the surface, a sort of two-dimensional "surface-reciystallization"; (3) there is a breakdown of chemically adsorbed surface compounds; (4) there is a recrystalliza-tion in the volume of the metal. All these changes are shown by Huttig and his coworkers to be completed fairly rapidly at lower temperatures than those generally used in sintering and are therefore not a part of the mechanism whereby the density of a mass of powder continues to change after long heating at an elevated temperature. But the first and third of these changes release gases in quantities which may or may not help to control the steady-state mechanisms, depending on when the voids become isolated from the outside of the compact. Among the phenomena studied by Steinberg and Wulff,8 there is the effect on sintering of residual stresses arising from the pressing operation. They found that the lateral surfaces of a green compact of iron are under a longitudinal residual tension-stress of the order of magnitude of half the yield-point for solid iron. If the outside surface is in tension, the core must be under longitudinal compression. When the compact is heated, the surface residual stress is thermally relieved first, and the compact therefore initially expands in the direction of its axis. This is a transient phenomenon, if for no other reason than the possibility of sintering unpressed powders, as demonstrated by Delisle,9 Libsch, Volterra and Wulff10 and others.1 The subject of recrystallization is dealt with further in a separate section, in view of its prominent place in sintering literature. It, too. is one of these transient phenomena. Among the steady-state parts there may be distinguished the attraction between particles and its consequences, the spheroidization of voids in the compacts, and the densification or swelling of the compact. There is considerable evidence4,7 showing that cold metallic surfaces, when brought to within a few interatomic distances of one another, are attracted to each other by forces of the order of many thousands of pounds per square inch. A calculation, discussed in greater detail in another section, shows that this force changes but slightly when the temperature of the surfaces approaches the melting point. Actual measurements of forces of adhesion of this magnitude have been made by Bradley12 on some nonmetals, but none has yet been made on cold or hot metals. This force is of sufficient magnitude to cause some plastic deformation in powder compacts, as will be shown below. A second force of steady-state nature is due to the surface tension, which probably has the same origin as the force of attraction between surfaces.164 A paper by Udin, Shaler, and Wulff1,3 gives the results of precise direct measurements of its value for solid copper. The demonstration of the tendency for the surface tension to shrink a pore was long ago given by Gibbs.17 He showed that its effect on a curved surface between two phases is equivalent to a pressure perpendicular to that

Jan 1, 1950

By M. M. Leighton

INASMUCH as the arrangements for the preparation of the review of progress and new developments in the field of industrial minerals (non-metallics) were not made until early December, the writing of this review could not be completed in time to appear in this issue and will, therefore, appear in the February issue. However, we desire to call attention to the steadily increasing importance of this group of mineral substances. The recent book, "Industrial Minerals and Rocks," published by the Institute, lists 47 principal varieties of nonmetallic minerals to which may be added several more of lesser importance. Because of the wide variety of uses to which many of these industrial minerals are put, it is difficult to classify them into categories, but to mention a few examples which indicate the widespread industrial employment of these minerals and their products, one may cite: the use of limestone, gravel, sand, clay products, lime, cement, and gypsum in the construction industry; fluorspar, lime, salt, borax, and sulphur in the chemical industry; diamond, corundum, emery, garnet, flint, quartz sand, tripoli. and diatomite in the abrasive industry; fluorspar, limestone, and magnesite in the metallurgical industry; clay, feldspar, fluorspar, flint, chalk, and limestone in the ceramic industry; and asbestos, gypsum, mica, vermiculite, magnesia, diatomite, and rock wool in the heat, sound and elec-

Jan 1, 1940

By R. Augsten, K. K. Feng, K. C. Cheng

"Methane emission and the desorption characteristics of vertical borehole coal samples of Greenhills multiple seams in the vicinity of Elkford, British Columbia were investigated. Three vertical boreholes at depths of 335 m, 380 m and 395 m were drilled along the west wall of an active open pit mine and 44 core samples from various coal seams were obtained for desorption studies.The results are presented in three tables and illustrated with six figures. The methane content was found to increase significantly at depths greater than 200 m. The adsorption equation by Kim and the properties of the coal have been used to predict the methane content and these were compared with the measured values by the direct method.IntroductionThe coalification of plant material in the sedimentary rock produces different ranks of co al and gases of various composition. The gas mixtures are retained in coal beds and rock strata under pressure. The gas content in a coal bed varies considerably depending on the rank of coal and the depth of overburden. The gas content is defined as the volume of gases adsorbed in a unit weight of coal materials. The net amount of gases remaining in a coal seam depends on the difference in the rate of generation of methane by geo-thermal heat and the rate of diffusion of the gases out of the coal bed through sedimentary cover. The major factor that causes the change in rank and the liberation of gases is the temperature, which is governed by the thermal conductivity of sedimentary cover and the heat flux through the underlying rocks. The rate of diffusion of the gases out of the coal is governed by the porosity of the overlying rocks and the degree of fracture. The measured values of gas content in major North American coal beds are from zero up to 24 cm3 per gram of coal(1,2). A gas content of 2.5 to 9 cm3/g is considered ""gassy"" and that of 9 cm3/g or higher is considered ""very gassy"" for underground mining(3). Normally, the gas mixtures released from bituminous coal in Canada contain 90 to 98% methane and the remainder is made up of CO2, N2, 02, H2, He and other hydrocarbons(4)."

Jan 1, 1984

By K. C. Hong, R. B. Jensen

The problem of determining the optimum set of steam volumes and cycle lengths for a single well undergoing multicycle steam stimulation in order to maximize the cumulative discounted net income has been formulated mathematically and programmed for a digital computer. The mathematical fonnulation of the problem and the method for its solution are discussed in this paper. The oil production performance during each stimulation cycle was simulated by either a constant percentage or a harmonic decline. Using simple analytical expressions for production performance, the cumulative discounted net income and cumulative time of operation were related to the pertinent process and cost parameters and two principal process control variables (cycle length and steam injection volume). The discrete maximum principles was used to transform the equations for cumulative time of operation and cumulative discounted net income into a set of simultaneous equations. The simultaneous equations then were solved by trial and error on a digital computer to determine the set of cycle lengths and stem injection volumes that gives maximum cumulative discounted net income over the project life. INTRODUCTION Steam stimulation is a process for improving the oil recovery rate from wells producing high-viscosity crudes. The process is applied on an individual well basis and is executed in a series of cycles, each consisting of three phases: steam injection, soaking (steam condensation), and production. Significant increases in production rate following the stimulation operation result from heating the reservoir around the wellbore. As heat is removed with produced fluids and dissipated into nonproductive formations, the production rate declines, usually to near the prestimulation value. Typical production responses are given in case histories reported by Owens and Suter,l and are depicted in Fig. 1. Duration of the production phase is equal to the time for the oil production rate to decline to some specified value and is called the cycle length. (Cycle length is defined as the producing portion of the cycle and does not include the downtime required for steam injection and soaking operations.) Termination of the production phase coincides with the start of steaming for the next cycle. The process is continued, cycle by cycle, until it becomes unprofitable. Models 2-4 have been developed to simulate behavior of a single well during one cycle of steam stimulation and have been used to investigate the effects of system and operating conditions on the production responses. However, these investigations have not shown how the models can be used to determine a most profitable set of operating conditions for a multicycle stimulation project. Perhaps these models are too complicated mathematically to be adapted readily to an optimization study. This paper presents a method for optimizing a multicycle steam stimulation project based on simple production performance models. First, the performance of a steam-stimulated well during each cycle was simulated by either a constant percentage or a harmonic decline model. Using these simple analytical expressions for production performance, the cumulative discounted net income (before tax) and cumulative time of operation for each cycle were related to the pertinent process and cost parameters and two process control variables—the cycle length and the steam injection volume. Finally, the profit function to be maximized was formed. The analogy between the above problem and problems of optimizing multistage decision processes that have been reported extensively in the chemical engineering literatures5-10 in recent years has led this investigation to the use of the discrete maximum principle.5-7 This principle was used to transform the equations for cumulative discounted net income and cumulative time of operation into a set of simultaneous equations characterizing the optimum operating conditions in terms of the two control variables. These equations

Jan 1, 1970