Serrated plastic flow in stable austenitic alloys based on Fe/Ni has been shown to be related to the presence of carbon and/or chromium in the systems. Strength peaks and plateaus in the serrated-flow temperature region for a commercial alloy correlate with an increased dislocation content, arising, presumably, from enhanced multiplication as a result of a strong interaction between dislocations and solute atoms. The data generally support a mechanism controlled by migration of vacancies, with the energy for vacancy motion being modified by the presence of chromium. Chromium atom -dislocation interaction is responsible for effects above 500°C, whereas the defect interacting with dislocations between 200" and 500°C is suggested to be a carbon-vacancy Pair. ThE phenomenon of jerky flow, serrated flow, or the Portevin-le Chatelier (P-C) effect in austenitic stainless steels is usually attributed to substitutional at1,2 mospheres1,2 or to precipitates&apos;-4 which form at dislocations during plastic deformation. On the other hand, evidence exists which supports a direct inter-stitial-dislocation interaction mechanism for serrated flow in fcc Ni-C,5,6 Ni-H7-9 and in nickel-austenites containing carbon." The present work consists in a study of serrated plastic flow in stable austenitic al-loys. The effects of carbon and of chromium were investigated separately, and a commercial stainless steel with different levels of interstitial impurity concentration was studied in an attempt to delineate the combined effects of the alloying elements. EXPERIMENTAL TECHNIQUES a) Materials and Fabrication. A commercial AISI 330 stainless steel and several specially prepared aus-tenitic alloys have been studied. The experimental alloys were prepared by arc melting the constituents under purified argon. Analyses of the materials are given in Table I. The commercial alloy was obtained as 5/8 in. bar stock and rolled to 0.092 in. sq, with several intermediate anneals. At this stage some of the material was annealed in Pd-purified hydrogen at 1100°C to establish different levels of interstitial content. All other heat treatments were in vacuum (10-5 torr). The "pure" alloy ingots were swaged to 0.120-in. rod and annealed in Pd-purified hydrogen at 1100°C. The analyses for these conditions are also contained in Table I. Following the above treatment, the final wire sizes Table I. Chemical Analyses of Test Materials Hrin Hydrogen at Cr, Ni, Alloy 1lOO°C wt pct wt pct C, ppm* N, ppm* Type 330 As-received 14.78 33.25 430 300 Type 330 64 14.78 33.25 40 50 Type 330 200 14.78 33.25 27 21 Fe/35 Ni 72 - 35.10 <10 62 Fe/35 Ni 200 35.10 <I0 44 Fe/35 Nil15 Cr 72 14.95 34.94 <I0 61 Fe/35 Ni/15Cr 200 14.95 34.94 <10 45 Fe/35 Ni/C $ 35.OM 380 *Sensitivity: N t 5 ppm Ct10ppm. f Nominal Ni content. % A master NiC alloy was used in preparation of this material; courtesy of D.E. Sonon. were obtained by either swaging or cold drawing. The test results did not vary with these techniques. b) Specimen Preparation. Two sizes of specimen and two gripping systems were used. i) 0.070-in. wire with a chemically milled gage section: 0.75 in. long, 0.060 in. in diam. These were fastened into grips containing tapped grooves. ii) 0.050 in. wire, gage length 1.5 in. Ball bearings were welded to the ends of the wires and the gage length was taken to include all material between the welds. Socket-type grips were used with these specimens. With specimens of type ii), joining was performed in a specially constructed brass jig, under argon, and automatic timing was utilized in the procedure. No adverse effects of welding were noted. Specimens were encapsulated and solution treated for 1 hr at temperatures selected to produce the same average grain size, -50 µ. Annealing twin boundaries as well as normal crystal boundaries were counted. The temperatures used are listed in Table 11. Table 11. Specimen Size. Temperature of Heat Treatment and Resulting Grain Diameters for Test Materials Recrystallization Resulting Material Condition Temperature Grain Sue AISI 330 Not H purified 0.070 120O°C 45 to 55µ in, wire AlSl 330 H , pure, 0.070 in. 1150°C 45to55µ wire Fc/35Nil15Cr Pure, 0.070 in. wire 1000°C 45tossp Fe/Ni Pure. 0.070 in. wire 775°C 45 to 55µ Fe/Ni/C Pure, 0.050 in. wire 850°C 10 to 20p AlSl 330 Not purified, 0.050 1150CC 45to55p in. wire AlSl 330 ti, pure, 0.050 in. 1150°C 45to55p wire

Jan 1, 1970

By Xiaojie Gao, Shufeng Yang, Jingshe Li, Chengsong Liu

In the blast furnace process, the dust entrained in the blast furnace gas enters into the down-comer, flows through the gravity dust separator (to eliminate coarse particles) and then is collected in a bag-house. The powder collected by the baghouse is called bag dust, while both fractions are called blast furnace dust whose main components are C and Fe. The dust also contains small amounts of nonferrous metals such as Zn and Pb, which have some value. Also, due to the small particle size and low density the dust is easily suspended in air and so can endanger human health. Therefore it is necessary to develop a process to both treat the dust to recover the metal values and to dispose of the residue – preferably by recycling to the blast furnace itself via the sinter strand. These objectives will result in good economic, environmental and social benefits [1].

Jan 1, 2014

F. Lynwood Garrison, Philadelphia, Pa. (communication to the Secretary): I have been specially interested in Mr. Drake&apos;s valuable contribution to our knowledge of the Chinese coalareas, as I had occasion, about a year ago, to make a reconnoissance over some of the coal-fields in the Yangtse river valley. I noticed, as he appears to have done, certain peculiarities which may eventually prove to be characteristic of the Chinese coal-measures, at least in central and northern China. The most striking feature, perhaps, is the invariable proximity of the great granite masses to those coal-deposits which have an anthracite character. In common with all other anthracite areas elsewhere, the Chinese show evidences of profound stratigraphical disturbances. The sedimentary rocks are folded, faulted and dislocated in a manner similar to those of the Pennsylvania anthracite-regions. It would seem that the intrusive granite had much to do with converting the original bituminous into present anthracite. The action of the granite was probably direct as a conveyor of heat, and indirect as dynamic force in dislocating, overturning, and compressing the coal-measures. My stay in China was unfortunately cut short, so that I was unable to collect fossils, or to give this highly interesting and important subject more than passing attention. Cholnoky* and Richthofen are practically agreed that these granite eruptions took place during the Tertiary period—probably the Eocene. This profound tectonic movement has had a most important effect upon the geological conditions in central and northern China, and will be, I am sure, a potent factor in the economic development. Evidences of disturbances and metamorphism are very abundant in the anthracite-areas of the Yangtse valley. I noticed the coal in them, as did Mr. Drake in northern China, to be often flaky and " slickensided."

Jan 1, 1902

By L. Russell, van Wert

During an investigation in which the solubility relations of the phases in Muntz metal (60 per cent. copper, 40 per cent. zinc) were under study, certain phenomena that had no immediate connection with the main problem were observed, which were thought sufficiently interesting to study further. Because of lack of time, only a preliminary survey was made of two of these; namely, the cleavage structure developed under certain conditions in a 60:40 brass and abnormal grain growth in this alloy. Cleavage Structure in Heat-treated Muntz Metal Carpenter noted many years ago that cold-working a brass of the Muntz metal type, which had been quenched previously from within the beta field, results in a partial breakdown of the supersaturated beta solution and the precipitation of the solute (the alpha solution) in the cleavage planes of the beta grains. This manner of rejection of a solute from a metastable solid solution is not peculiar to this particular alloy, for among others, it occurs in the cold-working of certain austenitic steels; for example, the austenitic nickel steels. In these ferrous alloys, cold deformation produces a partial decornposition of the austenite, with the formation of martensitic "needles" and zigzags in the austenitic poly-hedra. It is interesting to note that while the two solid solutions— austenite and quenched Muntz metal— are metastable and in their mode of decomposition behave quite alike when deformed in the cold, the metastability of each results from a different cause; viz., that of the austenite from the fact that it is a supercooled solution (its solvent. gamma iron, at ordinary temperatures is below its normal stable range whereas the metastability of the quenched Muntz metal is the result of supersaturation. When a 60:40 brass is quenched from above 800" C.—that is, from within the field where the beta phase alone is stable—this solution is retained practically intact and the alloy so cooled is found to consist almost entirely of polyhedra of this solution with only a little alpha present ordinarily at the boundaries of the beta grains—the result of a slight

Jan 1, 1929

By van Wert, L. Russell

During an investigation in which the solubility relations of the phases in Muntz metal (60 per cent. copper, 40 per cent. zinc) were under study, certain phenomena that had no immediate connection with the main problem were observed, which were thought sufficiently interesting to study further. Because of lack of time, only a preliminary survey was made of two of these; namely, the cleavage structure developed under certain conditions in a 60:40 brass and abnormal grain growth in this alloy. Cleavage Structure in Heat-treated Muntz Metal Carpenter noted many years ago that cold-working a brass of the Muntz metal type, which had been quenched previously from within the beta field, results in a partial breakdown of the supersaturated beta solution and the precipitation of the solute (the alpha solution) in the cleavage planes of the beta grains. This manner of rejection of a solute from a metastable solid solution is not peculiar to this particular alloy, for among others, it occurs in the cold-working of certain austenitic steels; for example, the austenitic nickel steels. In these ferrous alloys, cold deformation produces a partial decornposition of the austenite, with the formation of martensitic "needles" and zigzags in the austenitic poly-hedra. It is interesting to note that while the two solid solutions— austenite and quenched Muntz metal— are metastable and in their mode of decomposition behave quite alike when deformed in the cold, the metastability of each results from a different cause; viz., that of the austenite from the fact that it is a supercooled solution (its solvent. gamma iron, at ordinary temperatures is below its normal stable range whereas the metastability of the quenched Muntz metal is the result of supersaturation. When a 60:40 brass is quenched from above 800" C.—that is, from within the field where the beta phase alone is stable—this solution is retained practically intact and the alloy so cooled is found to consist almost entirely of polyhedra of this solution with only a little alpha present ordinarily at the boundaries of the beta grains—the result of a slight

Jan 1, 1929

By Ben-Zion Weiss, Melvin R. Meyerson

Chromium diffusion coatings on commercial Armco iron lead to carbide precipitation at the grain boundaries in and below the coatings. High compressive stresses are introduced into the coating and, as a result, tensile stresses are introduced into the base material below the coating. In coated samples, fatigue cracks form at the grain boundaries below the coating after only a limited portion of the total lifetime (5 to 10 pct). Residual tensile stresses and a stress concentration caused by precipitated carbides seems to be responsible for early crack nucleation. Stage I of Propagation may be divided into two substages: I-a in which the crack Propagates along grain boundaries, and I-b in which the crack propagates along slip boundaries according to a shear mode. In uncoated samples, the cracks form at slip bands after 40 to 50 pct of the total lifetime. In coated samples the Propagation process takes longer than in uncoated samples because of the moderate rate of crack extension until the crack breaks through the coating. The chromium-diffusion coating causes little if any increase in fatigue life. CHROMIUM diffusion is one of the most popular processes used to apply coatings to iron alloys. This popularity stems from the fact that the diffusion treatment is comparatively easy to carry out, and it improves certain surface properties such as corrosion and wear resistance as well as some other properties. Very little effort has been devoted to the investigation of the effect of chromium-diffusion coatings on mechanical properties and particularly on fatigue properties. Since the chromium coating usually represents a small fraction of the total volume of the base material it is generally assumed that the macro properties are dependent principally on the base material rather than the coating. Insofar as fatigue is concerned, there are indications that the fatigue life of the chromium coating is not less than that of the basic material and the fatigue properties are generally not reduced by it.&apos; But chromium diffusion causes drastic structural and chemical changes in the region of the material surface2-4 which introduce additional residual stresses. Such changes must affect fatigue crack nucleation and may sometimes affect the initial stages of propagation. Furthermore, it is conceivable that the secondary stages of the crack propagation could be influenced by some irreversible structural changes in the core of the material, which stem from the long-time heat treatment at high temperatures required to apply the coating. This paper analyses the structural and compositional changes produced in commercial Armco iron by a chromium-diffusion coating and the effect of the coating on fatigue crack initiation and propagation. EXPERIMENTAL PROCEDURES The investigations were carried out with commercial Armco iron. The chemical composition of the iron, the number of specimens tested, the grain size produced during chromizing and heat treating, and the thickness and microhardness of the chromized layers are shown in Table I. Samples were chromized by a gas diffusion process. The temperature and time of the diffusion coating process were chosen according to a previous grain growth study. It had been found that at a temperature of 970°C and a holding time of between 3 and 9 hr there are practically no changes in grain size. To describe the grain size more accurately the ASTM method5 was supplemented by a statistical analysis of the mean volume diameter as outlined by Fullman6 and The The mean volume diameter was deter- mined from D = p/2m where D is the mean volume diameter, and m is the mean reciprocal value of grain diameters as seen on the micrograph. The shape and the size of the asymmetrical sample, see Fig. 1, were chosen so as to facilitate the study of fatigue crack initiation. Before coating, the samples were machined and the surface of the groove was polished. After chromizing, the two side surfaces were machined and polished so as to retain the coating only on the top surface of the groove. Residual stress in the chromized layer was measured on the top of the grooved section of the specimen after the diffusion process. The inclined incident X-ray beam procedure was used.9&apos;10 The computations were performed with the initial assumption of a zero surface normal stress component. An electron microprobe analyzer was used to obtain the relative amounts of chromium and iron con-

Jan 1, 1970

By W. D. Forgeng, P. F. Wieser

MnSi alloys containing from 2 to 24 at. pct Si have been investigated by metallographic and X-ray methods. Contrary to published data, the temperature of the ß-manganese to a-manganese transformation is lowered by the addition of silicon. The existence of two additional intermediate phases E and ( is demonstrated. E, ranging in composition from 12 to 15.5 at. pct Si, forms by a peritectoid reaction between ß manganese and the second new phase, (. The latter phase is homogeneous at silicon contents from 16.2 to 18 at. pct and forms peritectically from the 0 phase and liquid. The eutectic reaction occurs between the ( phase and MnsSi rather than the ß phase and Mn3Si. As a result of this investigation, a modification of the manganese-rich section of the MnSi equilihrium diagram is proposed. The binary diagram of Mn-Si, according to Hansen,&apos; Fig. 1, exhibits in the low-silicon region (below 24 at. pct Si) a peritectic transformation at 900°C of 0 manganese + Mn3Si to a manganese as determined by R. Vogel and H. Bedarff2 as well as a thermal effect at 980°C between 16.2 and 22.6 at. pct Si reported by the same authors. The nature of the latter transformation was unknown. K. Amark, B. Boren, and A. westgren3 reported indications that possibly four more phases existed in the range of 10 to 27 at. pct Si. The present investigation deals with the phase relations in the range of 2.1 to 17.7 at. pct Si. A few spot checks were conducted up to 23.84 at. pct Si. EXPERIMENTAL PROCEDURE Small experimental heats were prepared by induction melting in a vacuum furnace using argon as a protective atmosphere. The crucible was of commercial-quality magnesia. The furnace charge consisted of silicon metal and dehydrogenated electrolytic manganese. The typical analysis for these materials is shown in Table I. The molten alloy was tapped into 2-in.-square, 7-in.-long ingots. After visual inspection, a small quantity of alloy in the middle portion of the ingot was separated for use in this investigation.MnSi alloys containing from 2 to 24 at. pct Si have been investigated by metallographic and X-ray methods. Contrary to published data, the temperature of the ß-manganese to a-manganese transformation is lowered by the addition of silicon. The existence of two additional intermediate phases E and ( is demonstrated. E, ranging in composition from 12 to 15.5 at. pct Si, forms by a peritectoid reaction between ß manganese and the second new phase, (. The latter phase is homogeneous at silicon contents from 16.2 to 18 at. pct and forms peritectically from the 0 phase and liquid. The eutectic reaction occurs between the ( phase and MnsSi rather than the ß phase and Mn3Si. As a result of this investigation, a modification of the manganese-rich section of the MnSi equilihrium diagram is proposed. The binary diagram of Mn-Si, according to Hansen,&apos; Fig. 1, exhibits in the low-silicon region (below 24 at. pct Si) a peritectic transformation at 900°C of 0 manganese + Mn3Si to a manganese as determined by R. Vogel and H. Bedarff2 as well as a thermal effect at 980°C between 16.2 and 22.6 at. pct Si reported by the same authors. The nature of the latter transformation was unknown. K. Amark, B. Boren, and A. westgren3 reported indications that possibly four more phases existed in the range of 10 to 27 at. pct Si. The present investigation deals with the phase relations in the range of 2.1 to 17.7 at. pct Si. A few spot checks were conducted up to 23.84 at. pct Si. EXPERIMENTAL PROCEDURE Small experimental heats were prepared by induction melting in a vacuum furnace using argon as a protective atmosphere. The crucible was of commercial-quality magnesia. The furnace charge consisted of silicon metal and dehydrogenated electrolytic manganese. The typical analysis for these materials is shown in Table I. The molten alloy was tapped into 2-in.-square, 7-in.-long ingots. After visual inspection, a small quantity of alloy in the middle portion of the ingot was separated for use in this investigation.

Jan 1, 1964

By Raymond L. Orr

Calorimetric measurements have been made of the heats of solution of gold axd indium in a number of liquid tin-rich alloys at a temperature of 705°K. Relative partial molar enthalpies of gold were determined as a function of dilute solute concentrations in the binary Au-Sn system and in the ternary Ag-Au-Sn and Au-In-Sn systems. Relative partial molar enthalpies of indium were determined for dilute solute concentrations in the In-Sn, Ag-In-Sn, and Au-In-Sn systems. Through application of the interaction coefficient concept introduced by Wagner and more recently extended by Lupis and Elliott, ualues have been obtained for the Au-Au, Ag-Au, Au-In, and Ag-In enthalpy interaction coefficients in liquid tin. The results are inte@reted in terms of solute atom distributions through comparisons with the predictions of dilute solution models. INTEREST in the thermodynamic behavior of dilute liquid alloys stems from two primary sources. From a practical viewpoint, it is often of importance to know or to be able to predict the effect that one solute will have on the thermodynamic properties of the other solutes in a multicomponent system. Studies of dilute solutions may also be rewarding from the theoretical point of view. Some of the difficulties arising from the more complex interactions possible in concentrated solutions are avoided, leading to easier interpretations in terms of solutibn models and bonding energies. For example, in a binary alloy the limiting values of the partial molar properties of the solute represent the case for which each solute atom is completely surrounded by atoms of the solvent, and no other interactions are possible. Solute - solute interactions in dilute solutions are conveniently treated by the interaction coefficient concept of ~agner.&apos; Using a Taylor series expansion for the logarithm of the activity coefficient, In yi, of a component, i, in a solution consisting of dilute solutes with atomic fractions xi, xj, xk, and so forth, in a solvent, s, and neglecting the second- and higher-order terms, Wagner obtained the expression: Where Wheyz is the limiting value of yi in the pure solvent, s. The interaction coefficients, e:, e:, and so forth, are defined by: Since yi is related to the excess partial molar Gibbs energy of component i by GfS = RT In yi, E: is re- ferred to as the "Gibbs energy interaction coefficient". Lupis and Elliott~ extended Wagner&apos;s treatment to the relative partial molar enthalpy, aHi, and the excess partial molar entropy, qS. They defined the enthalpy interaction coefficient as: and the excess entropy interaction coefficient as: leading to expressions similar to Eq. [I]: The three interaction coefficients are related by? The self-interaction coefficients, E:,qf,and at, represent the effects of interactions between atoms of component i in solvent s; €3, q{, and 03 represent the effects of interactions between i and j atoms in solvent s; and so forth. From the Maxwell-type relationships between partial molar quantities, it may be shown1&apos;2 that e{ = ej, r}\ =tj), and ai - crj. Experimental determination of the interaction coefficients requires extremely precise measurements of the appropriate properties as functions of solute concentrations in very dilute regions. Few such data exist for intermetallic alloys, even for binary systems, because of experimental difficulties. This is especially true with respect to enthalpy data for dilute alloys. Examination of the compilation of data for binary alloys by Hultgren, Orr, Anderson, and ~elle~~ reveals that determination of limiting values of &fii(Xi =0) often requires extrapolations to infinite dilution from xi = 0.05 to 0.10. Direct measurements of the enthalpy interaction coefficient, qi, for multicomponent systems are virtually nonexistent. This quantity is of course subject to direct calorimetric measurement, but its determination must be limited to cases where high experimental precision is possible. The heats of solution of gold and indium in liquid tin can be measured with relatively high precision, which makes determinations of 73 involving these metals as the measured solutes experimentally attractive. This paper presents the results of such determinations of the Au-Au, Ag-Au, Au-In, and Ag-In enthalpy interaction coefficients in liquid tin. MODELS FOR DILUTE-SOLUTION BEHAVIOR Random-Solution Behavior. In the quasi-chemical treatment of solutions, only nearest-neighbor bonds are considered, and a composition independent value

Jan 1, 1967

By D. T. Peters, S. Floreen

The age hardening behavior of an Fe-8Ni-13Mo alloy was studied after the matrix had been varied to produce either ferrite, cold u~orked ferrite, or nzassive nzartensite. The aging behavior of the cold worked ferrite and murtensite structures were very similar. The martensite aging kinetics were much different from those observed in earlier studies of aging of maraging steels, even though the martensite wzatri.r had the same dislocation structure as those found in maraging steels. The results suggest that the previously observed precipitation kinetics of maraging steels ?nay have been controlled by the nucleation be-haviov, which in turn were dictated by the alloy compositions and the resultant identities of the precipitating phases. IT is well known that the rate of precipitation from solid solution depends not only on the degree of super-saturation, but also on the density and distribution of dislocations in the matrix structure. These imperfections often act as nucleation sites, and may also enhance atomic mobility. &apos;Thus, the presence of dislocations is important since the type and distribution of precipitates may be determined by them. The precipitate density and morphology in turn affects the mechanical properties of the alloy. A number of studies have been devoted to the precipitation characteristics in various types of maraging steels.&apos;-" These are iron-base alloys containing 10 to 25 pct Ni along with other substitutional elements such as Mo, Ti, Al, and so forth, that are used to produce age hardening. The carbon contents of these steels are quite low, and carbide precipitation is not believed to play any significant role in the aging reactions. After solution annealing and cooling these alloys generally transfclrm to a bcc lath or massive martensite structure characterized by elongated martensite platelets that are separated from each other by low angle boundaries, and that contain a very high dislocation den~it~.~~~~~~~~-~~ Age hardening is then conducted at temperatures on the order of 800" to 1000°F to produce substitutional element precipitation within the massive martensite matrix. Most of the aging studies to date have revealed several common traits in these alloys, regardless of the particular identity of the precipitation elements. Generally hardening has been found to be extremely rapid, with incubation times that approach zero. The agng kinetics, at least up to the time when reversion of the martensite matrix to austenite begins to predominate, frequently follow a AX/~~ = ktn type law, where x is hardness or electrical resistivity, t is the time, and k and n are constants. The values of n are frequently on the order of 0.2 to 0.5, which are well below the idealized values of n based on diffusion controlled precipitate growth models. Finally, the observed activation energy values are typically on the order of 30 kcal per mole, and thus are well below the nominal value of about 60 kcal per mole found for substitutional element diffusion in ferrite. The common explanation of these observations is that the precipitation kinetics are controlled by the massive martensite matrix structure. Thus, the absence of any noticeable incubation time has been attributed, after ~ahn," to the fact that the precipitate nucleation on dislocations may occur without a finite activation energy barrier. The low values of the activation energy are generally assumed to be due to enhanced diffusivity in the highly faulted structure. If this explanation that the precipitation kinetics are dominated by the matrix structure is correct then one should observe a distinct difference in lunetics between aging in a martensitic matrix and aging the same alloy when it has a ferritic matrix. Such a comparison cannot be made with conventional maraging compositions, but could be made with the alloy used in the present study. In addition, the ferritic structure of the present alloy could be cold worked to produce a high dislocation density so that one could determine whether ferrite in this condition would age similarly to martensite. EXPERIMENTAL PROCEDURE The composition of the alloy used in this study was 8.1 pct Ni, 13.0 pct Mo, 0.10 pct Al, 0.13 pct Ti, 0.012 pct C, bal Fe. The alloy was prepared as a 40 lb vacuum induction melt. The heat was homogenized and hot forged at 2100°F to 2 by 2 in. bar, and then hot rolled at 1900°F to $ in. bar stock. The aging lunetics were followed by Rockwell C hardness and electrical resistivity measurements. Samples for hardness testing were prepared as small strips approximately 2 by $ by 4 in. thick. Electrical resistivity was studied on cylindrical samples approximately 2 in. long by 0.1 in. diam. The method for making the alloy either martensitic or ferritic was based on the fact that the alloy showed a closed y loop type of phase diagram. At high temperatures, above approximately 24003F, the alloy was entirely ferritic. Small samples on the order of the dimensions described above remained entirely ferritic after iced-brine quenching from this temperature. In practice, a heat treatment of 1 hr in an inert atmosphere at 2500°F followed by water quenching was used to produce the ferritic microstructure. These samples were quite coarse grained and usually en-

Jan 1, 1970

By Brian F. Dyson

The surface tensions at 1550°C of some Fe-S alloys (in the range 0.008 to 0.052 wt pct S), Fe-Sn alloys (0.31 to 48.4 wt pct Sn), Fe-P alloys (0.038 to 2.38 wt pct P), Fe-Cu alloys (2.15 to 22.8 wt pct Cu), and Fe-1 pct C-S alloys (0.005 to 0.076 wt pct S) along with the surface tension of the base iron have been measured by the sessile-drop method. A mean value of 1754 dynes per cm was found for the surface tension of the base iron. Sulfur was found to be highly surface-active, the surface-tension results being in quantitative agreement with existing data. Tin and copper were found to be less surface-active than sulfur while phosphoms was completely nonsurface-active. The surface tensions of Fe-1 pct C-S alloys were found to be lower than those of the Fe-S alloys containing the same sulfur content. This was shown to be a mmzifestation of the increase in the thermodynamic activity of suZfur by carbon. It is only in recent years that attempts have been made to measure the surface tension of liquid iron of known high purity.1-3 Earlier measurements4-7 were made on liquid iron containing variable amounts of what are now known to be surface -active solutes. The exact value of the surface tension of liquid iron is still, however, open to some doubt. Halden and Kingery&apos; reported a value of 1720k 34 dynes per cm at 1570°C, Kozakevitch and Urbain8 gave 1790k 25 dynes per cm at 1550°C, while Van-Tszin-Tan et al. obtained a value of 1865k 37 dynes per cm at 1550°C. The first systematic investigation into the effect of controlled solute additions on the surface tension of iron was made by Halden and Kingery.&apos; They showed that sulfur and oxygen were highly surface-active, whereas nitrogen was only slightly active, and carbon inactive. A subsequent investigation by Kingery indicated that two other group-6B elements, selenium and tellurium, were also surface-active. This highly surface-active nature of sulfur and oxygen has recently been substantiated by Kozakevitch and Urbainla and Van-Tszin-Tan et al. l1 Kozakevitch and Urbainl2 have also conducted an experimental survey of the effects of a number of metals on the surface tension of liquid iron. Their surface-active nature was, in all cases, less than that of the group 6B elements. The present investigation was undertaken to study in more detail the surface tensions of dilute Fe-S alloys and to measure the surface tensions of binary alloys of iron containing phosphorus, copper, and tin. The effect of sulfur additions on the surface tension of Fe-1 pct C alloys was also determined. EXPERIMENTAL PROCEDURE The sessile-drop method was employed in the present investigation. An apparatus was built similar in principle to that described by Humenik and Kingery.lS It consisted of a horizontal silica tube, which could be evacuated to pressures less than 10-5 torr, with its central portion surrounded by a water jacket within which was a high-frequency coil. This generated heat in a tantalum susceptor placed inside the silica tube, which in turn radiated heat to the specimen mounted on a recrystallized alumina plaque. Temperatures were measured by an optical pyrometer and photographs of the molten drop were taken on a fixed-focus plate camera giving a magnification of X2. Surface-tension values were determined from the resultant drop using the method described by Baes and Kellogg.l4 The high vapor pressure of molten iron made it necessary to conduct all the experiments under a 1/4 atm of argon (greater than 99.995 pct purity). The analysis of the base iron used in the investigation is given in Table I. Each sample was approximately 3 g in weight and had a hemispherical base to ensure a uniform advancing contact angle on melting. The iron alloys were prepared individually in the sessile-drop apparatus by drilling a hole in the top of each sample and adding the required amount of solute, the drops being analyzed after the experiment. This method of preparation had the advantage of ensuring a consistent minimal contamination by oxygen due to refractory attack and also allowed surface tension to be measured at the same time. Every precaution was taken to ensure that the specimen was not contaminated by grease when it was introduced into the apparatus, the samples being cleaned in acid, dried in alcohol, and rinsed in petroleum ether. All handling was done with tweezers. Once the specimen had been placed inside the susceptor, the furnace was evacuated and the Sample leveled. The furnace was then degassed at approximately 1000"C before the argon was introduced. In every case the surface tension was determined at 1550" C.

Jan 1, 1963

By A. J. Mortlock

Cobalt and nickel have been diffused at tracer concentrations in gold at several temperatures in the range from approximately 700° to 950°C. The diffusion penetration profiles were determined by a serial sectioning technique in which the gold is first anodized and then the anodic layer is dissolved in acid. In this ulay sections as thin as 250A could be removed reproduci-bly. In all cases, the region close to the specimen surface was characterized by irregular behavior in the sense that the logarithm of concentration was not linear in the square of the penetration distance. In sotne cases, there zuas an indication of the operation of very slow dijfusion in this region, while in others the apparent diffusion coejj&apos;icient was negative. Possible reasons for this anomalous behavior are briefly discussed. In recent years it has been found that the region close to the surface of a metal can sometimes exhibit anomalously slow diffusion characteristics relative to the interior of the metal. One of the best examples of this fact is the work of Styris and omizuka,&apos; who showed that the apparent diffusion coefficient for zinc in the region withi: about 1 p of the free surface of copper was about ,,,, that at deeper penetrations. This result is particularly interesting, because it is free from the possibly complicating effects of low solubility of the diffusing tracer in the solvent metal. In the case of diffusion under conditions of low solubilitjr, interpretaticn of the results in terms of lattice diffusion is difficult because of the enhanced short-circuiting produced by segregation to dislocations.2&apos;3 Measurements by Duhl et 1. suggest that cobalt diffusing in gold may also show a near-surface effect of this type. Once again the solubility is high, so that this result could be of great interest. However, the technique used for analyzing the diffusion penetration zones by Duhl, viz. the counting of residual gamma activity in the specimen following sectioning, appears to have indicated a near-surface effect in a parallel experiment on the self-diffusion of gold reported at the same time. The latter result is known to be spurious, since Kidson5 has demonstrated that self-diffusion in gold does not show this effect. Duhl et 01. also reported some measurements on the diffusion of nickel in gold, but failed to give any data for the near-surface region. As the solubility of nickel in gold is high, such data would also be of special interest. We, therefore, decided to conduct another set of experiments on the diffusion of nickel and cobalt in gold, using a sectioning technique that allows the individual sections to be assayed for solute content and thus gives direct determinations of penetration profiles. Also, by sectioning with an anodizing/stripping tech- nique, very thin layers can be removed and the region close to the surface studied in detail. MATERIALS The gold specimens were supplied as single crystal disks $ in. in diam by a in. high by Monocrystals Co. of Cleveland, Ohio. The gold itself was of spectro-scopic purity, i.e., better than 99.99 pct pure. METHOD Specimen Preparation. One flat end face of each gold crystal was spark planed with a Servomet spark erosion machine set for minimum spark energy. Following this treatment the crystals were preannealed for 2 to 4 days at temperatures of either 400" or 700°C. The three crystals preannealed at 700°C showed signs of recrystallization. The spark-planed end face of each crystal was then coated with the appropriate amount of 63i or 60 radioactive tracer. This deposit was laid down in a simple plating bath containing the as-supplied solution of the radioactive isotope as well as sufficient ammonium oxalate to saturate the solution. Some ammonium oxalate remained undissolved on the floor of the bath for this purpose. During plating further additions of ammonium oxalate were sometimes required to allow the plating to continue satisfactorily, perhaps due to passivation of the undissolved oxalate already present. The thickness of the deposited layer was determined by comparison of the apparent surface activity of the plated specimen with that of a similar specimen having a weighable deposit of the isotope on its end face. Correction for self-absorption of the radiation was made in this calculation. Annealing. The deposited crystals were annealed in a hydrogen atmosphere in sealed silica tubes. During this heat treatment they were supported, active face down, on optically flat silica plates. The temperature was measured with calibrated Pt vs Pt-10 pct Rh thermocouples, and the tabulated values can be taken to be correct to Z°C. All the crystals showed evidence of recrystallization following these heat treatments, suggesting that initially they may not have been good single crystals or had suffered strain during delivery. Concentration Profile Analysis. After annealing, the crystals were sectioned by the anodizing-stripping technique.6 The anodizing involved suspension of the specimen with its cylindrical axis horiz6ntal by a gold wire in a 200-ml beaker containing 1 M Hg304. A cathode in the form of a strip of gold sheet, 2 in. wide and positioned to be in contact with the curved side of the beaker, completely encircled the specimen. An anodizing current of 30 ma, corresponding to a current density of 5 ma per sq cm on the surface of the specimen, was passed for times ranging from 5 to 150 min depending on the thickness of gold to be removed; the solution was stirred continuously during this process. Following this treatment, the specimen

Jan 1, 1969

By R. P. Agarwala, M. S. Anand

Using residual activity technique, the diffusion of palladium, silver, cadmium, indium, and tin in alunzinum has been studied in the temperature range of 400" to 630°C. The diffusivities (in units of square centimeters per second) have been expressed as: IMPURITY diffusion in aluminum,1-9 silverand lead5 for cases of low solid solubility of the impurity in the host metal has yielded frequency factors in the range of l0-6 to l0-9 sq cm per sec whereas the activation energy is practically half the self-diffusion activation energy value. From the observed values of frequency factor, activation energy, and entropy of activation, it has been suggested&apos; that these solutes are not diffusing by vacancy or interstitial mechanisms but by a mechanism which should be consistent with such low values of the diffusion parameters (Do and Q). However in spite of extensive work on these types of systems, the mechanism of diffusion is still not well understood. The present investigation on the diffusion of palladium, silver, cadmium, indium, and tin in aluminum has been carried out to throw further light on the diffusion mechanism in systems, where the solid solubility is very low (except for the case of silver). The results are discussed on the basis of solid solubility and the structural changes involved owing to the presence of the solutes in aluminum solid solution. An attempt has also been made to apply the existing theories of charge5-8 and size8 difference between the solute and the solvent. EXPERIMENTAL PROCEDURE Specimens (1/2 in. diam by 3/8 in. high) were machined out of pure aluminum (99.995 wt pct) rod obtained from Johnson Mattheys. They were sealed under vacuum in quartz tubes and annealed at 620° C for several hours; the grains thus developed were sufficiently large to eliminate the possibility of diffusion along the grain boundaries. The flat ends were prepared carefully after polishing as described previously,10 Radioactive nitrates of cadmium, indium, and tin and chloride of palladium containing, respectively, cd115, 1n114, sn113, and pd103 were dissolved in distilled water and mixed with 30 pct acetone. By means of a micropipet a drop of this solution was placed on a smoothly polished and lightly etched surface of the specimen. Due care was taken to see that the solution spread uniformly on the surface of specimen without trickling down its sides. Radioactive silver was elec-trodeposited using a AgCN-KCN bath. The amount of sample deposited in all the cases was not more than 0.1 µ thick. The samples were then sealed in quartz tubes in vacuum. The cadmium samples were sealed in a purified argon atmosphere to avoid evaporation. The samples were then diffusion-annealed. The temperature of annealing varied between 400° and 630°C and was controlled to ±5°C. On heating to -400°C,the deposits of cadmium, indium, and tin, which were of the order of 0.1 p in thickness, were converted to their respective oxides. The contribution of oxygen present in the lattice of aluminum due to these oxides has been calculated and found to be less than 10 ppm in all cases. Oxide method has already been used by other workers11&apos;12 in diffusion studies without any controversy on the issue. However, in some of these investigations, metallic deposition was also tried. The diffusivities calculated from these measurements were found to agree very well with the diffusivities obtained by using the oxide method. Thus it is assumed that the measured diffusivities represent true diffusion coefficients. Since palladous chloride decomposes at about 500°C, the deposited samples which were to be diffusion-annealed below 500°C were heated in vacuum for a very short time at 500°C to allow the decomposition of palladous chloride to palladium metal. Time taken in decomposition of nitrates to oxides and chloride to metal was negligibly small as compared to the period of the diffusion anneals. The residual activity technique13 was used to study the diffusion profiles where thin layers from the specimen surface were removed by grinding it parallel to a flat surface on a 600-grade carborundum paper. The specimen was washed, dried, and weighed, the differ -ence of the weight being the measure of the thickness of the layer removed. After each such abrasion and weighing, the total residual activity on the surface of the specimens was measured by counting 0.656, 0.94,

Jan 1, 1968

By A. H. Larson, L. G. Twidwell

The influence which Au, Ag, Sb, Bi, Sn, and Cu have, both individually and collectively, on the activity coefficient of sulfur in liquid lead at 600"C zuas studied by circulating a H2S-Hz gas wlixture over a specific lead alloy until equilibrium was attained. Subsequently, the H2S concentration in the equilibrium gas mixture and sulfur concentration in the condensed phase were deterruined. The elements gold, silver, and antinzony (above 8 at. pct) increased the activity coefficient of sulfur. Bismuth had no apparent effect. Tin (above 3 at. pct) and copper decreased the coefficient. The influence of an individual element, i, on sulfur is best reported as the interaction parameter, riS, which is defined as The values o these first-order interaction zus are: ESzu = —55.0. These interaction parameters are used to predict the activity coefficient of sulfur in six fouv-component alloys and one seven-component alloy. Comparisons are made with direct experimental determinations. INTERACTIONS in dilute solution have been studied by many investigators. Most of the experimental work has been confined to solute-solvent interactions in simple binary systems and solute-solute interactions in ternary systems. Dealy and pehlke"~ have summarized the available literature on activity coefficients at infinite dilution in nonferrous binary alloys and have calculated from published data the values for interaction parameters in dilute nonferrous alloys. Interaction parameters are a convenient means of summarizing the effect of one solute species on another in a given solvent. Only a few investigators have studied interactions of the nonmetallic element sulfur in a metallic solvent. They are as follows: Rosenqvist,~ sulfur in silver; Rosenqvist and Cox,4 sulfur in steel; chipman, sulfur in alloy steels; Alcock and Richardson,% ulfur in copper alloys; Cheng and Alcock,&apos; sulfur in iron, cobalt, and nickel; Cheng and ~lcock,&apos; sulfur in lead and tin. The only reported work on the Pb-S system in the dilute-solution region is that of Cheng and Alcock.&apos; Their investigation involved a study of the solubility of sulfur in liquid lead over the temperature range 500" to 680°C. The results may be summarized by the following relationship: S (dissolved in lead) + Pb(1) = PbS(s) log at. %S = -3388/T + 3.511 Experimentally, it was found that Henry&apos;s law was valid up to the solubility limit of sulfur in lead, i.e., at 600°C up to 0.43 pct. Their investigation did not include the study of sulfur in lead alloys. More accurate calculations could be made in smelting and refining systems if activity coefficients of solute species could be accurately predicted in complex solutions. One of the objectives of this study was to compare the experimental data with the values calculated from the equations derived from models for dilute solutions proposed by wagner9 and Alcock and Richardson. A temperature of 600°C was chosen as the experimental temperature to attain reasonable reaction rates and to minimize volatilization of the condensed phase. EXPERIMENTAL Materials. The Pb, Au, Ag, Sb, Bi, Sn, and Cu used for preparation of the alloys were American Smelting and Refining Co. research-grade materials. All were 99.999+ pct purity except the antimony and tin which were 99.99+ pct. The initial alloys prepared for this study consisted of twenty-one binary alloys, eleven ternary alloys, and one six-component alloy. The constituent elements were mixed for each desired alloy and were placed in a crucible machined from spectrographically pure graphite. The crucible was placed in a vycor tube which was evacuated with a vacuum pump and gettered by titanium sponge at 800°C for 8 to 12 hr. After the gettering was completed, the chamber containing the titanium was sealed and removed. The remaining sample chamber was placed in a tube furnace at 800°C for 2 hr and quenched in cold water. The final operation consisted of homogenization of the alloy for 1 to 2 weeks at a temperature just below the solidus for the individual system. The resulting master alloys were sectioned into small pieces and a random choice made for individual equilibrations. Cobalt sulfide (Cogs8) used to control the gas atmosphere in the circulation system was prepared by passing dried HzS for 24 hr over a Co-S mixture heated to 700°C in a tube furnace. This material was then mixed with cobalt metal to give a two-phase mixture which, when heated in hydrogen to a particular temperature, produced a desired H2S/H2 gas atmosphere in the circulation system. A Cu2S-Cu mixture also used in this study was prepared in a comparable manner. Apparatus for Equilibrium Measurements. The experimental technique of this study required apparatus

Jan 1, 1967

By J. O. Brittain, E. P. Lautenschlager, D. A. Kiewit

Compression tests were run in the temperature range of 700° to 900°C ox 0&apos; phase NiAl intermetal-lic alloys of several grain sizes. At these temperatures the minimum strengths were observed at the stoichiometric composition. While significant increases in strength occurved in both the low-nickel (vacancy) and high-nickel (substitutional) regions, the highest strengths were found in the high-nickel region. During deformation serrated flow was sometimes observed in the low-nickel alloys. After deformation transgranular cvacking and deformation striations were observed in all compositions tested. AS part of a general investigation of the properties of NiAl inter metallic compounds, a preliminary study of the role of point defects upon plasticity was made by high-temperature compression tests on ß&apos; NiAl specimens of several grain sizes and compositions. ß&apos; NiAl is an intermetallic compound having a CsCl structure and a rather wide range of composition from A1-45 at. pct to 60 at. pct Ni.1 According to Bradley and Taylor2 and to cooper,&apos; it possesses a defect lattice in which departures from stoichiometry in the direction of decreased nickel content lead to the presence of vacant nickel sites (although Cooper&apos;s work indicates that a small amount of substitution also occurs) whereas departures on the high-nickel side lead to substitution of nickel on aluminum sites. NiAl forms congru-ently from the melt at approximately 1650°C,1 and thus has a higher melting point than either of its component elements. Up to this time, although this and other high-melting intermetallic compounds have been suggested for elevated-temperature usage,4 only the hardness4 and a few tensile-strength measurements5 have been reported for NiAl at high temperatures. In the present investigation the effects of composition upon the compressive-strength properties in a range of 700° to 900°C have been measured for NiAl of several grain sizes. EXPERIMENTAL PROCEDURES The alloys were made as described elsewhere6 from an A1-46.8 at. pct Ni master alloy furnished by the International Nickel Co. with additions of high-purity nickel and aluminum. The charges were vacuum-induction-melted in A12O3 crucibles with small amounts of helium added to the atmosphere to suppress vaporization. They were cooled slowly from the melting temperature to achieve uniform grain size. In order to refine the as-grown grain size a special rolling technique was developed. Alloys were packed into 0.10-in. wall-type 302 stainless-steel tubes which were partially filled with magnesium oxide to prevent bonding between the alloy and the steel jacket. The ends of the tubes were closed by hot forging, and the packets were then hot-rolled. The alloys with greater than 50 at. pct Ni were rolled at 1100°C, but it was found necessary to increase the temperature to 1350° C before alloys with less than 50 at. pct Ni would roll without cracking. With these temperatures, reductions as high as 48 pct were achieved in a single pass. The rolled alloys will hereafter be referred to as "fine grained" whereas the as-grown material will be designated "coarse-grained&apos;&apos;. The compression specimens were made by cutting square cross-sectional pieces, approximately 3/16 by 3/16 by 1/2 in., with a water-cooled diamond cut-off wheel from the as-grown or the rolled alloys. Specimens were ground to their final dimensions by polishing through 3/0 grit silicon carbide papers. The final shape was a rectangular parallelepiped of square cross section having a height-to-width ratio of 3:1. Compression testing was carried out in a compression rig of our own design mounted on an In-stron Floor Model. The specimen chamber could be heated to 1000°C and was controlled within ±2°C. The compression rig was enclosed within a bell jar and was maintained at a 50 µ of mercury vacuum throughout the duration of the test. The test cham -ber was heated from room to test temperature within 15 min. Specimens were then held at the test temperature 30 min prior to testing. Previous experiments indicated that no grain growth would occur within this time. An Instron Variable Crosshead speed unit was used to adjust for small variations in specimen lengths in order to have a constant initial strain rate, €, for all specimens of a group. For the fine-grained specimens the strain rate was changed rapidly at constant temperature by a factor of 10 with the speed lever on the Instron. For a given € the compression data was analyzed in terms of true plastic strain (E) and true compressive stress (0).

Jan 1, 1965

By G. P. Airey, R. F. Mehl, T. A. Hughes

The coarsening of cementite particles in a ferrite matrix has been studied in a series of steels with 0.15 pct C only and 0.15 pct C plus 1 pct Ni, Mn, and Cr, respectively. Two initial states were employed: quenched nartensite, and quenched and cold-rolled martensite. A series of tempering temperatures between 500&apos; and 700" and tempering times of up to 190 hr were used. The structures were studied by replica and transmission electron microscopy. Particle size distribution curves were determined. From the average size value coarsening curves were obtained. These were plotted in accordance with the Wagner analysis assuming diffusion control. A discussion of the significance of the results is given. L HE reactions occuring upon the tempering of martensite have long engaged the attention of metallurgists. The latter stages, when cementite particles coarsen in a ferrite matrix, have been studied both qualitatively and quantitatively. Studies of such coarsening processes have recently been spurred by the publication of the Lifshitz-Wagner theory1, and the extension of this to the a Fe-Fe3C system by Oriani3 and by Li, Blakely, and einold. Following Wagner the coarsening process is often designated as "Ostwald Ripening". The only quantitative data on the rate of coarsening, except for the work of Hyam and uttin,&apos; in the a Fe-Fe3C system are those of Bannyh, Modin, and odin&apos; for a commercial eutectoid steel and those of Heckel and ereorio" using a pure eutectoid steel. The data of Bannyh, Modin, and Modin have been employed by 0riani3 to derive the a Fe-FeE interface energy. The reaction is one of the most important ones in steel and is worthy of detailed study. This is the purpose of the present study. Laboratory heats were prepared; these were steels with approximately 0.15 pct C, selected so that the num ber of carbide particles would be relatively small and thus so that the overlapping diffusion fluxes would be minimized, presumably a desirable circumstance.&apos;-3 In addition to Fe-C alloys, comparable heats containing 1 pct of Ni, Mn, and Cr, respectively, were included with a view of appraising the effect of alloying elements. This report includes an account of the micro-structures observed, primarily with the electron microscope, and of kinetic data and their interpretation. MATERIALS AND TREATMENT The alloys were prepared from electrolytic iron ("Plastiron") and high-purity graphite; these were melted in a zirconia crucible using a vacuum furnace. The alloy steels were made by adding electrolytic nickel, electrolytic manganese, and "vacuum grade" chromium, respectively, under a partial pressure of argon. Each melt was poured into a mold within the vacuum furnace and cooled in the mold. The ingots were 2 in. in diam. and 8 to 10 in. long. The analysis of the alloys is given in Table I. These ingots were hot-rolled to strip 0.1 in. thick, then cold-rolled to 0.05 in. and each alloy split into two batches. One batch was austenitized at 1200 for 1 min, quenched in cold brine, then cold-rolled to 0.02 in.; samples given this treatment are hereinafter designated as "worked". The other batch was cold-rolled to 0.025 in., austenitized at 1200" for 1 min, and quenched in cold brine; such samples are hereinafter designated as "quenched". These two batches were then tempered, as below. The purpose of the treatment given the first batch was to provide an initial structure of cold-worked martensite, with the expectation that the additional defect structure created by cold work would encourage a higher rate of nucleation of cementite on tempering and hence a more uniform distribution of cementite particles. Individual specimens were sealed in evacuated quartz or Pyrex tubes, then tempered in a muffle furnace. The temperature control was better than 3&apos;C at 700. Tempering treatments wer: performed at 400°, 500°, 550°, 600°, 65o°, and 700C for time periods between 15 min and 190 hr. PREPARATION OF SPECIMENS Specimens for optical and replicalelectron microscopy were mounted, polished conventionally, and etched with 2 pct nital. For electron microscopy, single-stage "formvar" replicas were made, dry-stripped and rotary-shadowed with chromium at an angle of 30 deg. Carbide extraction replicas were prepared from electropolished specimens usirig the method described by Smith and uttin.&apos; Thin foils for electron transmission microscopy were prepared by chemical thinning in an H202-HF bath prior to electropolishing in a chromium trioxide-acetic acid solution. The most

Jan 1, 1969

By P. T. Chiang

Chemical etching methods for the simultaneous revealing of the tellurium or selenium Phase and the chalcogenide grain boundaries of the alloy systems are given. A tellurium eutectic was found Present in zone-melted ingots. Similarly, a selenium monotectic was present in ingots. In general, the second phase (tellurium or seleniumn) occubies three different sites; viz., along the chalcogenide grain boundaries, as inclusions within the chalcogenide grain, and on the undersurface of the ingot. The detection limit for the tellurium phase is about 1 u in width. THERMOELECTRIC materials based on Group V (bismuth, antimony) and Group VI (selenium, tellurium) elements have aroused considerable interest in recent years in the practical application of thermoelectric cooling. In many cases, a small amount of excess tellurium (or selenium) was added to the material to optimize its thermoelectric properties. Then the question immediately arises as to the number of phases present in the resultant alloy. In the binary systems of Bi-Te, Sb-Te, and Bi-Se, the congruent melting compositions have been reported to be non-stoichiometric and are represented by Bi~Te respectively. It is to beexpected and known that Bi2Te3 and SbzTe3 crystallize from the melt with an excess of bismuth and antimony in the lattice and that tellurium forms a eutectic.~&apos; The same could be assumed to take place in the pseudo binary systems of (Bi,Sb)zTe3 and Bi2(Se,Te)3 as well as in the system studiedby puotinen5 and other workers. Likewise, BiaSe3 crystallizes from the melt with an excess of bismuth in the lattice and selenium forms a monotectic.~ Therefore, in practice, alloys solidified from the melt often contain a second phase (tellurium or selenium) in one region or another of the solid mass even without the addition of excess tellurium (or selenium). ~u~~recht&apos; studied the thermoelectric properties of (Bi,Sb)2Te3 alloys with excess tellurium and simultaneous additions of selenium. He mentioned that the materials show two phases because of the considerable excess of tellurium or selenium. However, he did not report as to how the tellurium or selenium phase was identified. It is generally believed that the presence of an excessive amount of tellurium or selenium phase in the alloy would adversely affect its thermoelectric properties and its uniformity. Consequently, there is a need for a simple method for the identification of the tellurium and selenium phase. The quantity of the second phase present is usually too small to be detected either by chemical analysis or by normal X-ray techniques. This investigation was therefore carried out, first, to devise a simple metallographic method for the identification of the tellurium or selenium phase coexisting with the chalcogenides and, second, to determine the distribution and specific location of the tellurium or selenium phase in the ingots. EXPERIMENTAL PROCEDURE The starting materials used for the alloy preparations were 99.999 pct pure bismuth, antimony, and tellurium and 99.997 pct pure selenium. The bismuth and antimony were obtained from Consolidated Mining and Smelting Co. of Canada Ltd., while the selenium and tellurium were obtained from Canadian Copper Refiners Ltd. The tellurium was purified further in the laboratory by zone refining. The elements were pulverized in a stainless-steel pestle and mortar. The amounts for the desired composition were weighed out each time on an analytical balance to make up a 100-g sample. Then the sample was introduced into a Vycor ampule (19 by 150 mm), pumped down to a vacuum of 10"5 Torr for 15 min, and sealed off. The ampule was then heated in a horizontal resistance furnace at 800" to 900°C for about 20 hr. During this period the assembly was rocked back and forth several times to ensure good mixing. At the end of the heating period, the ampule was quenched in cold water and then transferred to the zone-melting apparatus described in a previous publications to grow large-size aligned polycrystals. The background and ring-heater temperatures were adjusted to make the freezing solid-liquid interface slightly convex to the liquid. The recorded temperature gradient in the vicinity of the freezing solid-liquid interface was around 15°C per cm. The ampule was moved horizontally at a speed varying from 0.4 to 2 cm per hr so that the ring heater would cover the whole ingot length from end to end. A single zone-melting pass was used for the Bi-Te, Sb-Te, and Bi-Sb-Te ingots. Two passes in the forward and reverse directions were carried out for the Bi-Se and Bi-Se-Te ingots. Six passes in the forward and reverse directions were performed for the Bi-Sb-Se-Te ingot. The zone-melted ingots were found to contain several large crystals, with their basal planes (0001) approximately parallel to the growth axis. Samples of bismuth and antimony tellurides coated with a layer of tellurium, and bismuth selenide coated with a layer of selenium, were prepared for comparison in phase identification. These coatings were made by dropping a piece of the zone-melted ingot into some molten tellurium or selenium under argon atmosphere and allowing them to cool slowly to room temperature. The metallographic specimens were prepared by

Jan 1, 1969

By H. Biloni, R. Morando

The surface structure and substructure of Al-Cu alloys solidified as conventional ingots and under particular conditions such as those used by Bower and Flemings are studied. The influence of lampblack coating on the mold walls is especially considered and the results compared with those obtained in copper and graphite molds where no coatings exist. When high heat extraction conditions exist the observations show that mechanism of copious nucleation is responsible for most of the chill zone. When the heat extraction through the mold walls is low, a coarse grain structure with dendritic morphology arises, with a size that depends on the degree of convection present, analogous to that analyzed by Bower and Flemings. In both cases the effect of the convection on the macroscopic and microscopic appearance is discussed. The ingot macrostructure consists of one or more of three zones: "chill zone", "columnar zone", and central "equiaxed zone". The mechanism of the columnar-equiaxed transition has been subject of considerable interest and at present at least three theories exist about the formation of the equiaxed region: 1) the constitutional supercooling theory1 maintains that the equiaxed crystals nucleate after the columnar zone has formed, as a result of the constitutional supercooling of the remaining liquid; 2) chalmers2 pointed out, however, that there were several objections to this proposal, and that consideration should be given to the possibility that all the crystals, equiaxed as well as columnar, originated during the initial chilling of the liquid layer in contact with the mold; 3) Jackson et aL3 and O&apos;Hara and ~iller~ suggested that a remelting mechanism of the dendrite arms is responsible for the formation of the equiaxed region. After the work of Cole and Bolling and other authors6 it became evident that convection (natural, reduced, or forced) plays a very important role in the transition from columnar to equiaxed and on the size of the resultant equiaxed structure. Until recently the accepted explanation of the chill zone was that it occurs as a result of copious nucleation in the liquid layer in contact with the mold walls.798 The columnar region is a subsequent result of the growth of favorably oriented grains and, as a result of a selection mechanism studied by Walton and Chalmers,9 elongated grains with marked texture are formed. Recently, however, Bower and Flemings" using an ingenious laboratory experiment introduced the idea that the "copious nucleation" mechanism is not responsible for the formation of the chill zone and that the presence of convection, introducing some form of "crystal multiplication", plays a decisive role in the formation of the chill zone. Unfortunately, it is important to consider that for their conclusions Bower and Flemings extrapolated the results obtained in their special experiments to the case of conventional ingots, and that these authors only analyzed the macrostructures of the specimens. Let us consider the work by Biloni and chalmers" concerning predendritic solidification. These authors were able to show that a study of the segregation substructure of A1-Cu gives information about the nucleation and growth of crystals formed in contact with a cold surface. A spherical predendritic region characterizes the first part of every grain nucleated in contact with the surface as a result of the chill effect. The aim of this paper is to elucidate through the observation of the segregation substructure the conditions under which (in the Bower and Flemings type of experiments and in conventional ingots) either the nucleation or the multiplication mechanism gives rise to the structure in contact with the mold walls. I) EXPERIMENTAL TECHNIQUES The experiments were performed on two alloys: Al-1 wt pct Cu and A1-5 wt pct Cu. The purity of the aluminum was 99.99 pct and the copper 99.999 pct. The results obtained with both alloys were similar. In the Bower and Flemings type of experiments the apparatus employed to obtain rapid solidification against a surface was similar to that used by those authors. The liquid was drawn by partial vacuum into the thin section mold cavity. Plate casts were 5 cm wide and usually 7.5 cm high. The thicknesses of the cast were 0.1 and 0.3 cm. Two different materials were used for the mold, copper and nuclear-grade graphite. The internal mold surfaces were polished and left uncoated for some experiments. In other experiments, the copper or graphite surface was coated with a thin film of lampblack material. In some of these particular experiments one of the mold walls was left with an uncoated region (usually in the form of a cross). The conventional ingots were cast in graphite or copper molds. In different experiments the mold walls were sometimes uncoated or coated with lampblack material. The results obtained in conventional and Bower and Flemings copper molds were compared with those obtained with copper molds coated with a very thin film of graphite; the results obtained were essentially similar. The size of the conventional ingots was 5 cm diam and 7 cm high in all cases. The cast surfaces produced by the Bower and Flemings type of experiments and conventional methods were observed macroscopically and microscopically without any metallographic preparation. As Biloni and Chalmers showed," the observation of the chill surface can give considerable information about the structure and segregation substructure.

Jan 1, 1969

By K. R. Carson, J. Weertman

An attempt is made to ascertain the mechanism of tangle and cell formation and its dependence upon dislocation-interstitial carbon interactions. The strain-hardening behavior of single crystals of 3.25 pct Si-Fe was determined at 300° and 425°K and under conditions of both continuous and interrupted tensile strain. Significantly enhanced hardening was observed in crystals deformed at the elevated temperature, and it was further accentuated by interrupted straining. Transmission electron microscopy was used to study the resultant dislocation structures. Strain aging was found to aid tangle and cell formation at 425°K, but at both temperatures embryo tangles formed solely from primary glide dislocations, presumably by a process involving cross slip and "mushrooming". IN the course of plastic deformation all bcc metals and alloys develop a dislocation structure characterized by loose-knit groups of tangled dislocations. With increasing strain the tangles become more tightly knit and grow larger; finally a three-dimensional cellular substructure is formed:1 This process has been observed with the transmission electron microscope.&apos;-l7 However, most investigations were confined to the study of nearly pure polycrystalline metals at relatively low temperatures. At intermediate temperatures, 0.17 to 0.14 Tm where T, is the melting temperature in degrees absolute, the mobility of interstitial impurities such as carbon is high enough to permit migration to nearby glide dislocations but is still low enough so that a significant drag force is exerted.18,19 it is also in this temperature range that a hump occurs in the curve of work-hardening rate vs temperature for iron. Analogous plots for tantalum" and columbiumzo show a definite upward trend in the work-hardening rate. Keh and Weissman1 have pointed out that this behavior may be explained solely on the basis of changes in the dislocation configuration: at low temperatures the dislocations tend to be relatively straight and uniformly distributed, but at intermediate temperatures tightly knit tangles and cellular substructure appear. The interference of these tangles with glide dislocations causes the observed increase in the work-hardening rate. This explanation appears reasonable, yet one might ask what factors cause tangle formation to be so favorable at intermediate temperatures. It seens likely that the strong dislocation-interstitial interactions which are known to occur in this temperature range are at least partly responsible," with the magnitude of the effect being proportional to the interstitial concentration. The purpose of the present work is to study the relationship between tangle formation and strain hardening in a bcc metal in the temperature range 0.17 to 0.4 Tm. Particular emphasis was placed upon a study of the effects of interstitial-dislocation interactions. Single crystals of 3.25 pct Si-Fe containing about 200 ppm of C in solid solution were used in the investigation for the following reasons: 1) The mobility of interstitial carbon in 3.25 pct Si-Fe is negligible at 300°K but increases rapidly at slightly elevated temperature22. Hence, differences between the flow curves and dislocation structures of crystals deformed at 300°K, 0.17 T,, and crystals deformed, say, at 425°K, 0.24 Tm, should be appreciable because of the enhanced dislocation-carbon interactions at the elevated temperature. This effect was accentuated in some samples by interrupted straining, thereby introducing a certain amount of aging. 2) Near room temperature, slip in suitably oriented 3.25 pct Si-Fe single crystals is largely confined to the (110) planes.23&apos;24 Dislocation structures formed under conditions of single glide are the least complicated and their method of formation is the most easily discernable. 3) Dislocations in Si-Fe can be tightly locked with carbon atmospheres by a low-temperature aging treatment. The subsequent thinning of samples to foil thicbess causes little or no rearrangement in the dislocation structure.25 EXPERIMENTAL PROCEDURE Large single-crystal sheets of 3.25 pct Si-Fe were donated by Dr. C. G. Dunn of the General Electric Research Laboratory, Schenectady, N. Y. The orientations of the sheets were determined and slabs 1.0 by 0.25 by 0.05 in. were cut such that the desired tensile axis corresponded to the long dimension. The slabs were mechanically polished and subsequently decar-burized by heating at 1000°C for 3 days in a flowing wet-hydrogen atmosphere. A carbon content of about 200 ppm was introduced by heating at 805°C for 25 min in a flowing atmosphere of dry hydrogen containing heptane vapor. Shaped copper tools were then used to spark-machine at 0.125 by 0.50 in. gage length onto each slab. Vacuum annealing at 1225°C for 2 days followed by a quench into the cold end of the furnace to retain carbon in solid solution concluded the soecimen preparation. Continuous tensile flow curves for crystals of severa1 orientations Were obtained both at 300&apos; and 425°K. A strain rate of 6.67 x 10-4 Per set was used in these and all other tests. Crystals oriented for single glide, B and D in Fig. 1, were subjected to a 3.5 pct plastic elongation to insure uniform slip along the gage length; they were then immediately subjected to interrupted strain cycling as indicated in Fig. 2(a). Each cycle consisted of unloading to 1.5 kg per sq mm, holding

Jan 1, 1969

By A. D. Zunkel, A. H. Larson

Equilibrium arsenic contents of Pb-As alloys in contact with PbO-As2O3 slags containing less than 30 mol pct As2O3, were determined at 650°, 700: and 750 C in an inert at?rzosphere. In this temperature range, the arsenic content of the alloy increased with increasing temperature in the single-phase liquid slag region and decreased with increasing temperature in the two-phase slag region and the single-phase solid-solution slag region. The PbO-As2O3 phase diagram below 22 mol pct As2O3 was determined by thertrzal analysis and by application of a log ?As2O3/?PbO vS log XAs2o3 /x3pbO plot determined from the equilibrium actiuity data. The resulting phase diagram was not well-defined since the eutectic temperature was not detected in the thermal analysis experiments, although a region of terminal solid solubility of As2O3 was found. Results from the phase diagram determination are compared with an existing diagram in the literature. THIS experimental investigation is an extension of a study by the authors1 on the slag-metal equilibria in the systems concerned with commercial lead refining processes such as softening and dross fuming. The first part of this investigation was a study of the slag-metal equilibria in the Pb-PbO-Sb2O3 system. The only experimental work previously done on the Pb-PbO-As2O3 system was by Pelzel2,3 in which the phase diagram for the PbO-As2O3 system was determined below 50 wt pct As2O3 and the equilibrium constant for the reaction 3Pb + As2O3 + 3PbO + 2As was determined as a function of temperature. No slag-metal equilibrium data have been determined. It is due to the scarcity of information regarding the Pb-PbO-As203 system that this work was undertaken. This paper describes the determination of the slag-metal equilibria in the Pb-PbO-As203 system by equilibrating Pb-As alloys with PbO-As2O3 slags in an inert atmosphere, the effect of 1 wt pct additions of bismuth and copper on the slag-metal equilibria, and the PbO-As2O3 phase diagram both by thermal analysis and the use of the slag-metal equilibria data. EXPERIMENTAL Materials. The materials used in this investigation were analytical reagent-grade and assayed as follows: 1) 99.8 pct PbO (0.014 pct insoluble in CHJCOOH, 0.02 pct not precipitated by H2S, 0.1 pct CaO, and 0.08 pct SiO2); 2) 99.95 pct As2O3; 3) 99.99 pct Pb; 4) 99.0 pct As; 5) 99.99 pct Cu; and 6) 99.97 pct Bi. Room-temperature X-ray patterns revealed no detectable impurities in any of these materials. Apparatus for Equilibrium and Thermal-Analysis Determinations. The resistance-heated crucible furnace used in this investigation employed nichrome elements and was mounted so that it could be raised to surround the reaction tube during each experiment and, subsequently, lowered. A schematic diagram of the apparatus is shown in Fig. 1. Each charge was heated in a 3+-in.-OD by 31/2-in.-high 416 stainless-steel crucible placed in a 41/4-in.-1D by 18-in.-long fused-silica reaction tube which was closed at one end. On a shoulder around the crucible was placed a 3: -in.-OD by 12-in.-long open-end fused-silica condenser tube. The open end of the reaction tube was covered by a water-cooled brass cap with ports for 1) admitting an inert atmosphere to the system through a stopcock, 2) introducing a stainless-steel, motor-driven, paddle stirrer into the crucible, 3) evacuating the system with a mechanical vacuum pump, and 4) sampling the melt with Vycor sampling tubes. The brass cap was fitted to the open end of the reaction tube with a silicone gasket and collar clamp. The furnace temperature was controlled by a Barber-Coleman Capacitrol controller and a chromel-alumel thermocouple. Due to the corrosiveness of the melt, the controlling thermocouple also served as the measuring thermocouple. The temperature of the melt was calibrated against the controller temperature and was checked periodically during each test with a Vycor-enclosed calibrated chromel-alumel thermocouple. The temperature measurement and control can be considered accurate to ±3°C. Procedure. The charge placed in the crucible for each experiment consisted of 1000 g of Pb-As alloy and 300 g of PbO-As2O3 slag. The crucible was then placed in the reaction tube, the condenser tube was placed on the shoulder of the crucible, the silicone gasket and brass cap were fitted on the open end of the reaction tube, and the entire system was evacuated and filled with argon ten times. After the last flushing, a positive argon pressure of 1 psig was impressed on the system. The furnace was then raised to sur-

Jan 1, 1968

By G. R. Speich

The interlarnmelm spacing, growth rate, and degree of segregation that accompany cellular precipitation in four Fe-Zn alloys containing 9.7, 15.2, 23.5, and 30.5 at. pct Zn have been determined in the temperature range 400" to 600°C. The chemical free-energy change for the reaction was calculated from the available thermodynamic data and the known compositions of the phases. The fraction of the chemical free-energy change for equilibrium segregation that is converted into interfacial free energy decreases from 0.43 to 0.08 as the magnitude of this free-energy change increases from 35 to 270 cal per mole. At constant temperature the cellular growth rate is proportional to the cube of the dissipated free energy. At 600°C newly 100 pct of the equilibrium segregation is achieved during cellulm precipitation whereas at 400°C only 85 pct of the equilibrium segregation is attained. During cellular growth, mass transport of zinc occurs by grain boundary diffusion; excess zinc remaining in the a! phase after the completion of growth is removed slowly by volume diffusion. A modified Cahn theory of cellular precipitation predicts the observed interlamellar spacing within a factor of two. In cellular precipitation reactions such as pearlite formation or discontinuous precipitation, the basic problem is to predict the variation of growth rate G, interlamellar spacing S, and degree of segregation P with composition and temperature. To accomplish this we need three independent equations relating these quantities. One of these equations comes from the diffusion solution. To obtain two additional independent equations, some assumptions must be made. cahnl has suggested recently that two plausible assumptions are 1) that growth rate is proportional to the dissipated free energy and 2) that the spacing which occurs is that which maximizes the dissipated free energy. According to the first assumption, this spacing also maximizes the growth rate and the rate of decrease of free energy per unit area of cell boundary. The present work was undertaken to test these assumptions. To test the first assumption it is necessary to study a cellular reaction over a wide range of supersatura-tions to establish a relationship between G and the dissipated free energy at constant temperature. This is possible only in discontinuous precipitation reactions since in pearlite reactions constituents other than pearlite form if the composition of the parent phase deviates even slightly from the eutectoid composition. The Fe-Zn system was chosen for study because 1) discontinuous precipitation proceeds to completion over a wide temperature and concentration range, 2) the degree of segregation within the cell can be measured by lattice parameter measurements,2 and 3) the thermodynamics of this system have recently been determined by Wriedt.3 In this system the cells consisting d alternate lamellae of a and r phases form from supercooled iron-rich a phase. The a phase within the cells is bcc as is the original a phase, cia, but has a different orientation and a slightly lower zinc content than the original a phase. The r phase has a zinc content of about 70 at. pct and a crystal structure isomor-phous with T brass. EXPERIMENTAL PROCEDURE Four Fe-Zn alloys with 9.7, 15.2, 23.5, and 30.5 at. pct Zn were prepared from carbonyl-iron powder (400 mesh, 99.8 wt pct Fe) and zinc powder (200 mesh, 99.99 wt pct Zn). The powders were ball-milled together and cold-pressed under 60,000 psi to discs $ in. thick by $ in. diam. The cold-pressed discs of the alloys with 9.7 and 15.2 at. pct Zn were sealed in evacuated silica capsules and heated slowly to 1100°C over a period of 1 week (3 days at 600°C, then 3 days at 80O°C, then 1 day at 1100°C). The alloys with 23.5 and 30.5 at. pct Zn were treated similarly except that the final homogenization temperatures were 1000" and 85O°C, respectively, to prevent melting. The alloys were quenched in iced brine from the final homogenization temperature. Specimens of each alloy were subsequently aged in salt pots at temperatures of 400°, 450°, 500°, 550°, 600°, and 650°C for times that varied from a few minutes to several hundred hours. At a late stage of this work, an alloy containing 11.2 at. pct Zn was prepared by vapor-impregnation of iron foil with zinc vapor at 890°C. This alloy proved useful for electron microscope studies because it was free of porosity. The homogenization and aging conditions were based on the recent Fe-Zn phase diagram of Stadelmaier and Bridgers4 rather than the earlier diagram of ansen.5 They consist of a homogenization heat treatment in the homogeneous a field followed by an aging treatment in the two-phase a + r field. The aged specimens were metallographically polished and etched in 2 pct nital and the radius of the largest cell in the microstructure determined. This radius plotted vs time gave a straight line whose slope is the boundary migration rate or growth rate G of the cell. To determine the interlamellar spacing, specimens were examined by surface-replica and thin-section electron microscope techniques. Because of the irregular nature of the lamellae within the cell, the average interlamellar spacing S .of the cell was measured by the method of Cahn and Hagel,6 where S is defined by:

Jan 1, 1969