By P. R. Swann, R. M. Fisher, W. R. Duff

Observations by transmission electron microscoPy of the microstructures in quenched Fe-A1 alloys provide the basis for revision of the Fe-A1 phase diagram. The diagram is characterized by first-order transitions between the disordered ferromagnetic a! solid solution and the two ordered phases FeAl and Fe3Al. However, second-order transitions showing corre-luted fluctuations in the degree of order near the critical temperature occur between the paramagnetic a! and FeAl and the FeAl and FeAl phases. ELUCIDATION of the true nature of the Fe-A1 equilibrium diagram has proven to be an extremely challenging problem as evidenced by the fact that six quite different versions of the iron-rich portions have been published since 1958.&apos;-6 The most recent diagram shown in Fig. 1 was proposed by Rimlinger6 based on X-ray diffraction analysis and dilatometry. He shows the single-phase fields of the ordered phases of the types FeAl(L20) and Fe3A1(D03) and the disordered bcc Fe-A1 solid solution, a, separated from one another in every case by large two-phase regions. Thus, he implies that in Fe-A1 alloys ordering always occurs via a classical phase transition. In contrast to this view, theoretical studies3&apos;" have concluded that the transitions a — FeAl and FeAl — Fe3A1 should be second- or higher-order in character. A further revision of the Fe-A1 diagram of state is presented in Fig. 2 based on our previous8,9 and current observations by transmission electron microscopy of the microstructures found in quenched specimens. The average quenching rate was 50,000°C per sec and although this was sufficiently rapid to prevent Fe3A1-type ordering below -550°C it was not sufficient to suppress ordering of the type FeAl in the temperature range -650" to 800°C. However, ordering during the quench is easily recognized since the FeAl phase formed during holding at temperature rapidly develops large antiphase domains whereas FeAl formed during quenching has a very fine domain size, -50Å diam. Each symbol in Fig. 2 indicates the result of a micro-structural examination of specimens heat-treated (-1 hr) until equilibrium was established. The results will be discussed in the order of the points, A - Dl marked on both diagrams with reference to the phase fields, critical temperature, and "transition" ranges, respectively. The dark-field micrograph corresponding to point A is shown in Fig. 3 and was obtained using a 111 reflection of the Fe3A1 structure which reveals both a&apos;/4<111> and a&apos;/2<100> antiphase domain boundaries.10 The structure observed in this specimen is typical of single-phase Fe3A1 and shows no evidence for FeAl or any other additional phase. The dark-field micrograph shown in Fig. 4 corresponds to point B on the two diagrams. It was taken with a 100 FeAl reflection which reveals a/2(111) domains and exhibits the typical structure of single-

Jan 1, 1970

By D. J. Carney, E. C. Rudolphy

Large macroscopic nonmetallic inclusions were related to altered fireclay refractories by chemical and microscopic means. Pouring refractories are discussed as a source of these large inclusions. Nozzles and wells are major contributors. Use of alkali and titania contents as tracers is described. Recommendations are offered to minimize the sources of inclusions from pouring refractories. IN any attempt to improve the cleanliness of plain carbon and alloy steels, consideration must be given not only to the proper deoxidation practice to minimize inclusions, but also to sources of inclusions from pouring refractories. In some cases, the inclusions resulting from deoxidation may be minor in amount, yet a relatively dirty steel may be produced as a result of improper care in the pouring practices for the steel. The number of studies of inclusions resulting from pouring refractories has increased recently and some excellent reports on this subject have already been published.&apos;4 Some of these reports were reviewed briefly in a companion paper by M. P. Fedock.5 Mr. Fedock&apos;s contribution is a fine addition to the studies necessary to improve steel cleanliness for the ultimate benefit of all steel producers and consumers. In the interest of constantly improving cleanliness, the authors have been actively engaged for the past two years in experimentation to determine more closely the sources of inclusions in steel. One phase of this work was associated with efforts to define more closely the sources of macroscopic inclusions which have been experienced on occasional heats. The term "macroscopic inclusions" is defined in general as those inclusions which are visible to the naked eye or at low magnifications of the order of less than X25. These inclusions sometimes can be seen in the macro-etch tests of billets and slabs. This report summarizes a few of the field experiments and laboratory studies conducted at the South Works of the United States Steel Corp., which were made regarding nozzles, wells, and ingot scums, as well as inclusions occurring in steel products. The data in the present study, together with the data of Mr. Fedock concerning ladle erosion, should be of value in regard to future studies of inclusions arising from pouring refractories. The knowledge gained as a result of data collected thus far at South Works has been helpful in improving the cleanliness of the products and in pointing the way toward further improvements. Similarity of Large Inclusions to Refractories and Altered Refractories In the routine inspection of billet etch tests, occasional inclusions visible to the naked eye have been observed. These large inclusions most frequently occur near the top of the ingot and near the billet surface. When such material was encountered, careful examinations were made in an attempt to determine the origin of these inclusions. In a relatively few cases, examination revealed that the material was unaltered fireclay refractory of a type similar to that used for hot-top material, with only the surface of the inclusions having an altered appearance under the microscope. However, the great majority of these inclusions were completely altered-refractory material. The term "altered refractory" is defined

Jan 1, 1955

By J. W. Halley

THE effects of tin on steel have become increasingly important because of the necessity of using poorly detinned scrap, tin cans, and terne plate, in the open hearth. Since a tin can contains about 1.5 per cent tin, it would be possible to have up to 0.75 per cent tin in steel made with a 50 per cent scrap charge. In order to use tin-containing scrap, it is necessary to know the effect of tin on various grades of steel. The following investigation is by no means comprehensive but covers a number of steels in which tin content is important. PUBLISHED WORK A number of investigations of the effects of tin on rolling quality and physical properties have been published. It has been found that tin increases strength and hardness and reduces ductility and notched impact resistance. The decrease in ductility and notched impact resistance becomes more marked as the carbon decreases. McKimm1 found no change in Olsen ductility, Rockwell hardness, yield strength, tensile strength or elongation in cold-reduced strip containing up to 0.124 per cent tin. A tin content of 0.15 per cent gave difficulties in rolling and increased the hardness but 0.21 per cent tin showed no change in properties from material containing very little tin. No explanation of this contradiction is offered. Andrew and Peile2 investigated steels containing 0.01 to 0.25 per cent carbon and up to 0.63 per cent tin. They found an increase in tensile strength of from 100 to 200 lb. per sq. in. for each 0.01 per cent tin on normalized samples. The elongation and reduction of area were decreased and the notched impact resistance was reduced markedly. Quenched and drawn samples did not show embrittling if water-quenched from the draw temperature of 1148°F. (620°C.). They could find no evidence of tin under the microscope. Whitely and Braithwaite3 investigated the effect of tin on rail steel containing 0.55 to 0.06 per cent carbon. They found that 0.08 per cent tin caused a marked decrease in elongation, notched impact resistance and the degree of bend. The tensile strength was increased in some tests and not in others. Bolsover and Barraclough4 investigated the effect of tin up to 0.50 per cent on a 0.35 per cent carbon steel and on several alloy steels with from 0.30 to 0.40 per cent carbon. They found a comparatively uniform decrease in notched impact resistance with increasing tin on quenched and drawn samples. If the samples were quenched from the drawing temperature or reheated to the drawing temperature and quenched, the embrittling was much less severe. Steels containing molybdenum suffered much less embrittlement than other steels. EXPERIMENTAL WORK Effect of Tin on Low-carbon Rimmed Steel Increasing quantities of tin were added to four ingots of a heat of the following ladle analysis: carbon, 0.08 per cent; manganese, 0.39; phosphorus, 0.009; sulphur, 0.025.

Jan 1, 1942

By C. A. Bruch, J. F. Duffey

On the basis of metallographic and cooling-rate studies of 15 U-Zr alloys, a new version of the 6 phase region of the U-Zr phase diagram is proposed. IN several published diagrams of U-Zr alloy system:&apos; there is good agreement that at elevated temperatures complete solid solubility exists between y uranium and ß zirconium. Similarly, there is reasonably good agreement concerning the uranium-rich and zirconium-rich ends of the diagram. However, there is no agreement concerning the nature of the diagram at intermediate compositions and at temperatures below about 650°C. The early work of Saller et al.8 hows an intermediate phase, 6. In a later diagram by Saller and Rough&apos; shown in Fig. 1, the d phase field is drawn with dotted lines, indicating doubt that this phase exists. The diagram of Summers-Smith2 does not show the d phase. More recently Holden and Seymour&apos; have shown that in the composition range 40 to 60 wt pet Zr, the high-temperature ? phase, which is body-cen-tered-cubic, transforms to an ordered structure, 8. They found that the order-disorder transformation occurs between 595° and 610°C, and presented a diagram based on the study of four different alloy compositions. Most recently Saller et a1.5 presented a new diagram which differs with respect to the composition limits of the 8 field from the others proposed by these authors. The purpose of the present investigation was to determine the boundaries of the d phase field. Experimental Procedures and Results Alloys—Buttons, weighing 80 g of 15 different alloy compositions were prepared by arc melting Mal-linckrodt uranium and iodide-process zirconium in a water-cooled crucible. A controlled atmosphere of argon and helium was maintained in the furnace. Prior to making each button, a sacrificial button of zirconium was melted to increase the purity of the furnace atmosphere. Each alloy was then melted six times to improve its homogeneity. Subsequently the alloy buttons were jacketed in copper and hot rolled to slabs at 775°C. From these slabs, specimens were machined for chemical, thermal, and metallographic analyses, Table I gives both the estimated chemical composition of the alloys, and the values which were obtained by analysis. The oxygen contents varied from 0.013 to 0.032 pet, nitrogen from 0.0014 to 0.014 pet, and carbon from 0.0013 to 0.011 pet. The purity of the alloys ranged from 99.947 to 99.975 pet. Thermal Analysis—The specimens for thermal analysis were blocks 11/4 x 1/4 x % in. The bead of a calibrated thermocouple was placed between two of these blocks and molybdenum wire was wrapped around the assembly. Each assembly was sealed in a quartz capsule having an argon atmosphere. The capsule was placed inside a refractory crucible which was heated in a furnace. Using a method described by Smith,&apos; the emf of a differential thermocouple, with junctions inside and outside of the refractory crucible, was used to activate the

Jan 1, 1959

By J. W. Halley

THE effects of tin on steel have become increasingly important because of the necessity of using poorly detinned scrap, tin cans, and terne plate, in the open hearth. Since a tin can contains about 1.5 per cent tin, it would be possible to have up to 0.75 per cent tin in steel made with a 50 per cent scrap charge. In order to use tin-containing scrap, it is necessary to know the effect of tin on various grades of steel. The following investigation is by no means comprehensive but covers a number of steels in which tin content is important. PUBLISHED WORK A number of investigations of the effects of tin on rolling quality and physical properties have been published. It has been found that tin increases strength and hardness and reduces ductility and notched impact resistance. The decrease in ductility and notched impact resistance becomes more marked as the carbon decreases. McKimm1 found no change in Olsen ductility, Rockwell hardness, yield strength, tensile strength or elongation in cold-reduced strip containing up to 0.124 per cent tin. A tin content of 0.15 per cent gave difficulties in rolling and increased the hardness but 0.21 per cent tin showed no change in properties from material containing very little tin. No explanation of this contradiction is offered. Andrew and Peile2 investigated steels containing 0.10 to 0.25 per cent carbon and up to 0.63 per cent tin. They found an increase in tensile strength 0f from 100 t0 200 lb. per sq. in. for each 0.01 per cent tin on normalized samples. The elongation and reduction of area were decreased and the notched impact resistance was reduced markedly. Quenched and drawn samples did not show embrittling if water-quenched from the draw temperature of 1148°F. (620°C.). They could find no evidence of tin under the microscope. Whitely and Braithwaite3 investigated the effect of tin on rail steel containing 0.55 to 0.60 per cent carbon. They found that 0.08 per cent tin caused a marked decrease in elongation, notched impact resistance and the degree of bend. The tensile strength was increased in some tests and not in others. Bolsover and Barraclough4 investigated the effect of tin up to 0.50 per cent on a 0.35 per cent carbon steel and on several alloy steels with from 0.30 to 0.40 per cent carbon. They found a comparatively uniform decrease in notched impact resistance with increasing tin on quenched and drawn samples. If the samples were quenched from the drawing temperature or reheated to the drawing temperature and quenched, the embrittling was much less severe. Steels containing molybdenum suffered much less embrittlement than other steels. EXPERIMENTAL WORK Effect of Tin on Low-carbon Rimmed Steel Increasing quantities of tin were added to four ingots of a heat of the following ladle analysis: carbon, 0.08 per cent; manganese, 0.39; phosphorus, 0.009; sulphur, 0.025.

Jan 1, 1942

By J. M. Markowitz

The movement of hydrogen in two-phase Zircaloy-2 under the influence of a thermal gradient was studied in specimens of cylindrical geometry. A gross displacement of hydrogen toward the cooler regions of the specimen was observed with consequent copious precipitation of 6-ztrconium (ZrH) there. The kinetics of the diffusion are analyzed and discussed. X HE temperature-gradient redistribution of hydrogen in a-Zircaloy-2 has been treated both theoretically and experimentally Hydrogen moves toward the cold side of the temperature gradient until a steady state has been established; tendency for further hydrogen movement because of temperature differences is nullified by the tendency to move in the reverse direction because of the concentration gradient. The steady state condition is described by the equation in which iV is the concentration of hydrogen at a point in the specimen corresponding to absolute temperature T, R is the gas constant,k is a constant of integration, and Q is a parameter called the heat of transport, characteristic Of the particular system. The value of Q has been determined for hydrogen in Zircaloy-2 by several investigators, using Eq. [11. There is considerable variation in the results, the cause of which has not been resolved; reported values lie in the range 3 to 6 kcal per mole. The physical situation for two-phase thermal migration is much more complex. The -phase boundary for the solubility of hydrogen in Zircaloy-2 ranges from a concentration of 25 ppm at 200°C to a maximum of about 600 ppm at 550°C.4a Thus, if the concentration of hydrogen in Zircaloy-2 is sufficiently great (>600 ppm), the specimen will be entirely two-phase, consisting of a matrix of a-Zircaloy-2 surrounding particles of zirconium hydride. At time zero, with a temperature gradient imposed, the relative amounts of hydride and a-phase in each infinite-simally thin isothermal section of the specimen can be determined from the phase diagram by the lever rule. Moreover, the concentration of hydrogen in the matrix phase varies from point to point, following the a solubility line. Over most of this temperature range (<450°C) 6 phase, Fig. 3, has a constant concentration.5 The diffusion rate toward the cold side should be governed by 1) the slope of the a solubility line and 2) the temperature gradient, The extra complication of two-phase thermal diffusion lies in the fact that migration of hydrogen would leave the a-phase concentration gradient unaffected, since it is fixed at any temperature only by the solubility; gross concentration changes would reflect only the relative amounts of matrix and hydride, which could vary continuously at every point. Migration of hydrogen out of a region would lead to dissolution of hydride, and

Jan 1, 1962

By A. V. Deforest, A. R. Anderson, C. W. MacGregor

ONE of the important problems in the design of structures and machine parts subjected to rapidly applied loads is the determination of the strength and ductility of the material itself under such conditions. Realizing the need for such information, many investigations have been carried out in the past. Most of these experiments have been made using notched bars in bending either with the Charpy or Izod impact machine. While yielding valuable data on the effect of notches in the energy absorption of the material and on the condition of heat-treatment, this form of test does not lend itself readily to a determination of fundamental stress-strain relations. For this and other reasons, more attention has been paid recently to the tension impact test. An extensive literature already exists on the subject and only those investigations somewhat closely related to the present paper will be mentioned. For a more comprehensive list, the reader is referred to the Symposium on Impact Testing of the A.S.T.M., 1938. The work of Mann,1 Clark and Dätwyler,2 Nádai and Manjoine,3 Winlock and Leiter,4 Deutler,5 and Brinkmann,6 however, deserve especial mention. In most of the previous investigations on the subject, when stress-strain relations were obtained under high rates of loading, it was the common procedure to determine stresses based on the original area and strains based on the original length. Stress-strain curves were then constructed by [P OL, plotting So = Ao as a function of eo = Lo] where A o and Lo refer to the original area and gauge length, respectively. At present there exists a paucity of true stress-strain data in the impact problem. The advantages of constructing so-called true stress-strain curves in order to reveal the fundamental physical properties of the material for the tension test were discussed recently by one of the authors&apos; It was shown that the true physical behavior of the material in the tension test could best be represented [by plotting the average true stress, S = P as a function of e = q&apos; = log o = log Log] where P, A, L, S, e, and q&apos; refer to the load, the cross-sectioned area while the load P is applied, the actual gauge length, the average true stress, the true strain and true reduction in area, respectively. Besides giving a better physical representation, the method has certain additional advantages in that the stress-strain curve so plotted becomes a straight line from the maximum load point to fracture. The construction of such- curves, however, while comparatively simple for the slow rates of loading customarily used in the tension test, presents certain difficulties for tensile impact in that both loads and diameters are required throughout the test. The continuous measurement of test-piece

Jan 1, 1941

By W. L. Fink, L. A. Willey

DURING the war there was introduced a new higher strength aircraft alloy designated 75S.1,2.3 The properties of this alloy assure extensive applications in both military and commercial aircraft. It is therefore important to understand its limitations as well as advantages. The properties of 75S alloy in the heat-treated tempers, like those of many other aluminum alloys, are affected by the rate of quenching. In general, low quenching rates tend to cause low strengths and to adversely affect the resistance to corrosion. Commercial quenching procedures are usually sufficiently rapid to permit the development of maximum properties. However, in the center of heavy sections, such as large rolled and extruded shapes, the quenching rates may not be rapid enough to develop maximum strength or resistance to corrosion. The investigations of 75S alloy described herein reveal the most critical range of temperature and the effects of quenching sheet and extrusions at different rates through that temperature range, on the tensile properties and resistance to corrosion. PROCEDURE Preparation of Specimens Sheet specimens (3 in. by 9 in.) were prepared from a commercial lot of 75S "as rolled" sheet (0.064 in. thick). The composition° was as follows: Weight Percentage Cu Mn Mg Zn Cr Al with Normal Impurities 1.64 0.16 2.58 5.66 0.27 Remainder The specimens employed for the determination of the time-temperature relations during quenching of sheet were prepared by the following procedure: the hot junction of a 28-ga. iron-constantan thermoelement (asbestos insulated) was brazed to a thin strip of aluminum which was in turn brazed into the end of a 3/16 in. i.d. by ¼ -in. o.d. by 30 in. long aluminum protection tube. Before brazing, the tube was flattened to 0.064 in. thickness over the junction and adjacent lead wires for a distance of 1 ½ in. The flattened end of the tube was fitted into a slot cut from one edge to the center of the 3 in. by 9 in. by 0.064 in. sheet and brazed into place. The brazed joint was dressed to the thickness of the sheet and the entire specimen buffed to approximately the brightness of "as rolled" material. Because of the brazing operations required, these specimens were prepared using 3S alloy. For the investigation of quenching rates in heavy sections, there were used 75S extrusions which had compositions similar to that of the sheet. The specimens consisted of 14 in. lengths of ¾ in., 2 in., 3 in. and 4 in. diam cylindrical rods and a roughly rectangular extruded section which was approximately 4 in. by 7 ½ in. Thermocouples were peened into the bottoms of 1/8 in. diam wells drilled into one end and parallel to the axis to a depth of

Jan 1, 1947

By E. A. Gulbransen, W. S. Wysong

The behavior of molybdenum and its surface oxides in oxidizing and reducing gas atmospheres and in high vacua at elevated temperatures is a question of scientific and technical importance. The use of molybdenum as a metal or as an important component in alloys in oxidizing atmospheres at elevated temperatures has been limited because of the unprotec-tive nature of its oxide film and the volatility of this oxide at moderate temperatures. This communication will present results of a vacuum microbalance studyl, 2 of the following problems: (I) the oxidation kinetics in the temperature range of 250°to 450°C; (2) the reduction with pure hydrogen of thin oxide films formed on molybdenum; (3) the volatility of the thin oxide films; and (4) the vacuum oxidation of molybdenum at high temperatures. Molybdenum is an interesting metal to study for the following reasons: (I) although the oxide-to-metal-volume ratio is greater than one, the metal is not considered protective; (2) the metal oxidizes readily at temperatures of 2 50°C and higher; (3) the oxides of the metal are reduced at temperatures as low as 500°C by pure hydrogen; (4) the oxide Moo3 melts at 795°C; and (5) the oxides of molybdenum are volatile at moderate temperatures. The following variables are studied in the oxidation kinetics: time, temperature, pressure, surface preparation, surface area, concentration of inert gas in the lattice, cycling procedures in temperature, vacuum effect and high temperature vacuum oxidation. The general interpretation of many of these factors has been previously discussed. Literature The oxidation of molybdenum has not been studied critically. Although many studies have probably been made on the kinetics of the oxidation process, none has been reported in the literature available to us. The crystal structures found in the oxidation of molybdenum have been studied by Hickman and Gulbransen." Their results showed that Moo2 is the oxide which is stable in contact with the metallic substrate throughout the temperature range 300 to 700°C. As the film thickens in the low temperature range, MoO3 becomes predominant on the surface. Above 400°C, Moos is no longer observed, MoO2 being the only oxide found. Hagg and Magneli6 have shown from an X ray study that the a-phase, orthor-hombic Moo3 is stable up to 1050°C. Two other phases, ß and ß with compositions close to MoO2.90 are also obtained. The formula for the 0 phase is not given but that of the ß phase is defined as Mo9O26 The 0&apos; phase is found to be built upon a monoclinic unit cell. A ?-phase is isolated from a preparation MoO2.75 heated for 17 hrs at 670°C. This phase is

Jan 1, 1949

By Eugene N. Cameron

Graphite is the hexagonal form of crystal-line carbon. It is found in nature locally as tabular crystals but occurs mostly as disseminated flakes, foliated, platy, or fibrous masses, or microcrystalline compact to earthy material. Graphite is characterized by its gray to black color, metallic luster, black streak, perfect basal cleavage, softness (H = 1-2) and unctuous feel. It is sectile and flexible and has a specific gravity of 2.1 to 2.3. It is an excellent conductor of heat and electricity and is inert to ordinary chemical reagents. It melts at a temperature of about 3500°C and vaporizes at a temperature of about 4500°C. In the presence of oxygen it oxidizes to CO2 in the temperature range 600° to 700°C, but it is stable at ordinary temperature and markedly resistant to chemical weathering. Although some natural graphite is nearly 100 pct pure carbon, most contains mechanical impurities of various kinds; quartz, biotite, muscovite, pyrite, iron oxides, and feldspars are the most common. Commercial graphite products have a wide range of graphite content, but the better grades contain 80 pct graphite or more. Both natural and manufactured (artificial) graphite are used in industry. Natural graphite products are divided into two broad categories based on grain size. Graphite composed of visible crystals is called "crystalline" graphite, whereas graphite so fine-grained that it is not visibly crystalline is termed "amorphous." The distinction is arbitrary, for all natural graphite is crystalline, and all gradations between the two commercial categories are known. Within the two categories the terminology used in industry is confusing and not entirely consistent. Crystalline graphite comes from two principal types of sources. The first consists of rocks containing disseminated flakes of graphite. This source yields the "flake graphite" of industry. The second comprises vein deposits of graphite, of which those in Ceylon are the most important and furnish the Ceylon graphite of industry. Amorphous graphite comes from any of a variety of sources, including some of those that yield crystalline graphite. Manufactured graphite is made by electric furnace processes, mostly from petroleum coke. Occurrence and Distribution of Graphite Deposits GENERAL Graphite is widely distributed in nature, occurring in igneous, sedimentary, and metamorphic rocks, and even in nickel-iron meteorites. Graphite deposits of economic interest, however, occur mostly in metamorphic terranes. Five principal geologic types of deposits are recognized: 1. Deposits consisting of flake graphite disseminated in metamorphosed siliceous sediments. 2. Deposits consisting of flake graphite disseminated in marbles. 3. Deposits formed by thermal or dynamothermal metamorphism of coal or other highly carbonaceous sediments. 4. Vein deposits of the Ceylon type. 5. Contact metasomatic or hydrothermal deposits in marble. DEPOSITS IN METAMORPHOSED SILICEOUS SEDIMENTS Deposits consisting of flake graphite disseminated in metamorphosed siliceous sedi-

Jan 1, 1960

By A. V. Deforest, A. R. Anderson, C. W. MacGregor

ONE of the important problems in the design of structures and machine parts subjected to rapidly applied loads is the determination of the strength and ductility of the material itself under such conditions. Realizing the need for such information, many investigations have been carried out in the past. Most of these experiments have been made using notched bars in bending either with the Charpy or Izod impact machine. While yielding valuable data on the effect of notches in the energy absorption of the material and on the condition of heat-treatment, this form of test does not lend itself readily to a determination of fundamental stress-strain relations. For this and other reasons, more attention has been paid recently to the tension impact test. An extensive literature already exists on the subject and only those investigations somewhat closely related to the present paper will be mentioned. For a more comprehensive list, the reader is referred to the Symposium on Impact Testing of the A.S.T.M., 1938. The work of Mann,1 Clark and Dätwyler,2 Nádai and Manjoine,3 Winlock and Leiter,4 Deutler,5 and Brinkmann,6 however, deserve especial mention. In most of the previous investigations on the subject, when stress-strain relations were obtained under high rates of loading, it was the common procedure to determine stresses based on the original area and strains based on the original length. Stress-strain curves were then constructed by plotting [So = ooT as a function of eo =o] where A o and Lo refer to the original area and gauge length, respectively. At present there exists a paucity of true stress-strain data in the impact problem. The advantages of constructing so-called true stress-strain curves in order to reveal the fundamental physical properties of the material for the tension test were discussed recently by one of the authors? It was shown that the true physical behavior of the material in the tension test could best be represented by plotting the average true stress, [S = P] as a function of [e = q&apos; = log A-le = log Lo] where P, A, L, S, [e], and q&apos; refer to the load, the cross-sectioned area while the load P is applied, the actual gauge length, the average true stress, the true strain and true reduction in area, respectively. Besides giving a better physical representation, the method has certain additional advantages in that the stress-strain curve so plotted becomes a straight line from the maximum load point to fracture. The construction of such curves, however, while comparatively simple for the slow rates of loading customarily used in the tension test, presents certain difficulties for tensile impact in that both loads and diameters are required throughout the test. The continuous measurement of test-piece

Jan 1, 1941

By B. M. Larsen, L. S. Darken

SOME years ago we collated all laboratory data then available to us on the distribution at equilibrium of manganese and of sulphur between metal and simple slags, and used the results in setting up an equation, which proved to be in accord with determinations of the distribution ratio of manganese and of sulphur between liquid steel and open-hearth slag, over a wide range of operating conditions. We now present an outline of our calculations and inferences on these two closely related questions, which are of especial importance because of the advisability of conserving manganese wherever possible. In general, our results show that in the open-hearth furnace equilibrium between metal and slag, with respect to both manganese and sulphur, is substantially attained during the finishing period of the heat, or in about a half hour to an hour after any additions were made. This implies that the end result will be identical whether manganese is added as alloy or metal to the liquid steel or as oxide to the slag. The proportion of total manganese retained by the steel is favored: (I) by use of the minimum amount of lime, consistent with other operating limitations, required to give a lime-silica ratio of about 2.4, which usually corresponds to a minimum practical slag volume; (2) by a high concentration in the slag of MnO relative to FeO; (3) by high operating temperature. Absorption of sulphur by the slag from the liquid metal is favored: (I) by large slag volume; (2 by a high concentration of active (or "free") lime and of manganese oxide dis) solved in the slag; (3) by low concentration of silica, iron oxide, and phosphate dissolved in the slag. DISTRIBUTION OF MANGANESE BETWEEN SLAG AND METAL AT EQUILIBRIUM On the basis that the distribution of manganese between liquid steel and slag is controlled by the reaction [FeO + Mn = MnO + Fe [A]slag metal slag metal] the distribution at equilibrium, at a given temperature, is expressed by the equilibrium constant for this reaction, which is defined as [K" aMoO aFeI1 dFec) aMn] where a is the activity of the molecular species denoted by the subscript. The activity of each of the several components, although it is not known precisely, is approximately equal to the concentration of each component expressed as its mol fraction; that is, as the ratio of the number of mols of the given component to the total number of mols of all the molecular species present in the metal or slag, as the case may be. Moreover, since the activity, or concentration, of iron in the liquid metal is in fact substantially constant, the term [afe] may be combined with K" to give a new constant K&apos;. Making these changes,

Jan 1, 1942

By N. S. Dalal, V. Castranova, K. Van Dyke, V. Vallyathan

"IntroductionInhalation of crystalline silica is often associated with the development of pulmonary disease (Ziskind et al., 1976). Recently, it has been proposed that freshly sheared silica .may have surface properties that make it more reactive with lung tissue than aged silica, and that this unique reactivity ·of freshly crushed silica enhances its pathogenicity. A recent study in our laboratory strongly supports this theory (Vallyathan, et al., 1988a; 1988b). We found that grinding of silica cleaves bonds in a silica tetrahedral lattice generating reactive free radicals sites on the surface of the silica particles. The presence of surface radicals on freshly ground silica was monitored by electron spin resonance (ESR) spectroscopy. The ESR signal generated from fresh silica in air is characteristic of Si-0 and Si radicals. Evidence, i.e., the ESR signal after the addition of a spin trap (DMPO) and its sensitivity to ethanol, indicates that these silicon-based surface radicals can react with water to form hydroxyl radicals (OH). Results also indicate that these surface radicals make fresh silica more cytotoxic than aged silica; i.e., fresh silica causes more membrane damage as evidenced by hemolysis and lipid peroxidation. Therefore, the presence of reactive sites on the surface of freshly cleaved silica may play a significant role in its pathogenicity.If surface· free radicals are related to cytotoxicity, then screening dusts for the existence of such radicals may predict their relative pathogenicity. Since an ESR spectrometer is not available to many laboratories, the objective of this study was to develop a quick and simple technique to monitor the existence of reactive surface sites on dust. The technique chosen was the measurement of chemiluminescence using a liquid scintillation counter; i.e., an instrument which·would be accessible to most investigators."

Jan 1, 1989

By F. E. Bash

CONSTANTAN is an alloy of copper and nickel that is extensively used, under a number of trade names, as a resistance wire with a low temperature coefficient of resistance, and one of the elements of base-metal thermocouples, iron usually being the other thermoelement, although for low-temperature work copper is also used. Before the war, constantan was imported, in common with many other technical necessities. Since it required considerable time to receive the constantan after it was ordered, fairly large stocks were kept on hand; but after the beginning of the war no more was imported acid the stocks of foreign material were exhausted about the same time that the steel and munition manufacturers began to need great quantities of it for thermocouples for the heat treatment of steel. To meet this demand, the International Nickel Co. began manufacturing constantan that met all the requirements of the users of resistance wire but did not give the same electromotive force against iron as the German material and consequently could not be used with instruments calibrated for a definite e.m.f.-temperature relation. It so happened that all the constantan made had an e.m.f. lower than that necessary to meet the specifications of the Leeds & Northrup Co. for whom this investigation was carried out. If some had been higher and some lower, good wire could have been obtained by a, process of selection, but as it was no wire at all could be procured. To remedy this situation, a thorough investigation was started with the close cooperation of the International Nickel Co. and the Electrical Alloys Co. The specifications to which the constantan had to conform were that it should give an e.m.f. of 47.40 millivolts. against pure iron at 1500° F. (816° C.) with the cold-junction temperature at 0° F., or a proportional e.m.f. at temperatures near 1500° F. The method of checking a wire was as follows: It was first welded to a piece of iron wire; Armco iron was found to be satisfactory but iron with greater than 0.1 per cent. carbon would give a lower e.m.f. against the same piece of constantan than pure

Jan 9, 1919

By W. R. Ingalls

In reviewing the history of the metallurgy of zinc, I shall pass hastily over what is only of antiquarian interest. That has been excellently treated by Dr. Bernhard Neumann in "Die Metalle" (1904) and has been described briefly in my "Production and Properties of Zinc" (1902), in my "Lead and Zinc in the United States " (1908), and in other metallurgical works of more or less the same date. In this present monograph, I have it in mind to confine myself mainly to technical practice, especially to that of the last 75 years, prior to which period advance was slow and of no great moment. The ancients made brass by the cementation process, i.e., embedding copper in a mixture of calamine and carbon and heating, whereby zinc oxide was reduced and zinc was vaporized and combined with the copper. Zinc was isolated by some of the alchemists, who named it and knew something of its properties, but made no use of it. Long before then, however, zinc was produced in India. Later it was produced in southern China. Possibly the Chinese obtained their knowledge from India. The Chinese in remote places still produce small quantities of zinc. I have seen photographs of their furnaces; or pots, for they hardly deserve the dignity of being called furnaces. I imagine that they are the same that were used centuries ago, for I cannot conceive of anything more primitive. Anyway, it is certain that the idea of a commercial production of zinc in Europe was imported from the Orient, where the metal was known in commerce as Speauter and Spiauter, whence speltrum and finally our term spelter. Tutanego and Tuteneague are other old names. Dr. Isaac Lawson went to China about 1730, expressly to discover the method of its production. What connection there was between Isaac Lawson and John Champion we do not know, but the latter obtained in 1739 a patent for a process of distillation downward and at some time between 1740 and 1743 erected a works at Bristol and actually began the manufacture of spelter. A production of 200 tons per annum is mentioned. In about the year 1766, Rishop Watson visited the Champion works and saw the process in operation, which previously had been

Jan 1, 1937

By J. H. Hamilton, J. R. Lewis, J. H. Dismant, W. M. Fassell

RECENTLY this laboratory undertook the task of preparing some low carbon metallic cobalt by the carbon reduction of precipitated cobalt oxides. The oxides came in two lots and had the compositions given in Table I. Industrially, cobalt rondels&apos; are made by the carbon reduction of cobalt oxide in small reverberatory furnaces at temperatures near but not above 1050 °C. This is a slow and tedious small batch process but does give cobalt metal which is low in carbon (1 pct C). Inasmuch as these cobalt oxides were relatively low in copper and iron it was decided to reduce them with petroleum carbon in a small three-phase electric arc furnace of about 3 to 5 Ib of metal capacity. It was hoped such a procedure would save considerable time and perhaps also indicate an improved commercially feasible process. The furnace was preheated by using small pieces of carbon electrodes to maintain the arc until a temperature of 1500°C was reached. The broken pieces of electrodes were then removed and 500 g of the cobalt oxides and 60 to 100 g of petroleum coke added. At the end of the reduction reaction, a high lime flux was added to the furnace to facilitate the removal of sulphur. Due to the fineness of the cobalt oxide powder used and also to the presence of chlorides there was considerable dust lost in charging the furnace. This was overcome by preparing briquettes composed of the cobalt oxides, charcoal, and a little bentonite to serve as a binder. The results obtained are summarized in Table 11, which shows that the cobalt metal produced in the arc furnace was high in carbon varying from 2.5 to 3.5 pct. This, of course, is much too high. For certain uses, such as in the preparation of permanent magnets, the carbon content of cobalt must be low. It was necessary therefore to find an effective method of reducing the carbon content of the cobalt that had been prepared in the arc furnace. Van Arkel3 recommends the use of Co2O3 as a means of removing carbon from cobalt. Experiments by the authors indicate that carbon is removed with difficulty by this method. Other methods used, including lancing of the molten high carbon cobalt with a jet of oxygen, proved to be ineffective. The method finally used makes use of the fact that cobalt metal is decarburized by carbon dioxide at the temperature of the molten metal. Two methods were used: 1—carbon dioxide was bubbled up through the molten cobalt, and 2— molten cobalt was maintained in a carbon dioxide atmosphere. In the first method the gas was introduced below the surface of the molten metal by means of a quartz tube. A high frequency induction furnace was used to keep the cobalt molten in both of these experiments. This kept the metal somewhat agitated and no doubt was an important factor in hastening the decarburization &apos;process by the second method. Both methods gave satisfactory results as shown in Table 111. An interesting observation in connection with this &apos;work was that a small sample of carburized cobalt metal could be decarburized by heating it with an acetylene torch adjusted to give an oxidizing flame. This may have been due to the presence of carbon dioxide in the products of combustion. Samples of molten high carbon steel were decarburized by the same method and it is suggested that nickel and perhaps manganese can be decarburized in a similar manner. Additional work, including rate studies and other theoretical aspects of this problem, is in progress in this laboratory.

Jan 1, 1953

By C. G. Dunn

The measurement of interfacial teusions or grain boundary energies in metals is an important metallurgical problem, especially since it bears on growth and nucleation processes. Statistical methods of measuring equilibrium grain boundary angles, which relate interfacial tensions, have been used by some investigators1&apos;2 but more direct methods would be preferred. A direct way, based on a simple extension of a successful method of growing single crystals of silicon ferrite to predetermined orientations in flat specimens,3 is to produce three-grain specimens in such a way that the equilibrium common grain boundary will be perpendicular to the surface of the specimen. The angles to be measured then appear as the grain boundary angles in the surface of the specimen. The method of producing a single crystal specimen with a predetermined orientation is basically the same as that employed by Yoshida and Fuji-wara4 in their work on aluminum wires. The specimen, prior to any single crystal transformation, must have a matrix which will support the growth of a crystal of the desired orientation. Growth may occur through exaggerated grain growth or, if the matrix is strained a critical amount. by normal recrystallization. In either case the matrix must have stability at the temperature used to effect the transformation, this stability appearing as a long induction period for exaggerated grain growth or for the formation of recrystallization nuclei. Additional control is gained by using a high temperature gradient through which the specimen is moved at a suitable rate. To obtain the desired orientation, the specimen is fed a short way into the furnace producing one or more crystals in the hot end. After the specimen is removed from the furnace, the orientation of a crystal is determined, so that this crystal may be reoriented by properly deforming a narrow piece of the matrix between the end crystal and the rest of the specimen. This part of the specimen in the case of silicon ferrite is preferably held at red heat during the reorienting process. Fig 1 shows a specimen which is ready to be transformed into a single crystal through growth of a reoriented "seed" crystal. When the method just described is applied to the production of a three-grain specimen two crystals are grown first side by side in one end, the specimen is then reversed and the third grain grown from the opposite end. A suitable group of grains each of different orientation is one where all three grains have the same crystallo-graphic plane in the plane of the specimen. Fig 2 shows a photograph of a three-grain group prepared as described. The notches are introduced in the open ends of the grain boundaries to anchor them during the final annealing operations which ultimately should bring the grain boundaries to the lowest energy configuration. Two-grain groups with different crystallographic planes in the plane of the specimen can be similarly prepared and treated. If the two grains have different surface (gas to metal) energies per unit area, the equilibrium condition leads to a curved grain boundary.* * This feature of the problem was pointed out by J. c. Fisher. References 1. Cyril Stanley Smith: Grains. Phases and Interfaces: An Interpretation of Microstructure. Trans. AIME 175, 15. Met. Tech. TP 2387, June 1948. 2. D. Harker and E. Parker: Grain Shape and Grain Growth. Trans. A.S.M. (194,5) 34, 156-195. 3. C. G. Dunn, A. Seddon, and R. Wylie: Unpublished Work, 1946-1947. 4. Takeo Fujiwara: A Method of Producing A Long Single-Crystal Wire of Aluminum with any Desired Crystallographic Axis. Jnl. of Sci. Horoshima Univ. A, (1939) 9, No. 3, 227.

Jan 1, 1950

By F. D. Rosenthal, F. J. Dunkerley, G. J. Mills

Activities, free energies, and heats and entropies of mixing of liquid Pb-Zn alloys have been obtained by the electrode-potential method between 400° and 650°C. The large positive deviations observed from Raoult&apos;s law are in agreement with the phase diagram, which indicates a wide immiscibility field. A vapor-pressure method was used to extend the activity measurements to 900°C, allowing the maximum of the immiscibility gap to be estimated by thermodynamic calculation. Data on the mono-tectic and eutectic points compare favorably with previously existing work. SEVERAL long-standing methods have been in use for the study of phase diagrams from measurement of the activities of the component metals.&apos; The use of thermodynamic analysis for interpreting equilibria data is comparatively recent, however. Such analysis is usually undertaken by first evaluating the principal thermodynamic functions as, for example, the enthalpy, entropy, and free energy of the alloy constituents. These, in turn, quite often can be correlated with the interatomic potential energies and atomistics of the system, from which a clearer understanding of the causes leading to deviations from ideal behavior is gained. The present study of liquid Pb-Zn alloys is concerned with a determination of these quantities by electrode-potential and vapor-pressure measurements, using these values in calculations involving phase equilibria and to obtain a theoretical insight into an alloy system exhibiting strong positive deviations from ideal metallic solution. A considerable portion of the previously reported work is based on thermal analysis. Supplemented by optical studies of solid alloys, these techniques have revealed the essential nature of the immiscible mixtures that are formed. It is difficult, however, using the phase-

Jan 1, 1959

By P. A. Studemeister

"A trondhjemite stock intrudes a volcanic sequence that has massive sulphide lenses and that is metamorphosed to the greenschist facies at Gutcher Lake, 25 km north of Wawa, Ontario. The stock is 4 km2 in plan and is partly enveloped by an aureole of chlorite-epidote-amphibolehornfels up to 1 km wide. Within this contact aureole, biotite is partly pseudomorphosed by chlorite;epidote and hornblende are mottled by chlorite, calcite, plus quartz; albite has 0% An to 8% An; and hornblende porphyroblasts have actinolite rims. The stock has chlorite pseudomorphous after biotite; and feldspar is mottled by white mica plus calcite and has a clear rim of albite. Fractures filled with quartz, calcite, ankerite, chlorite, white mica, pyrite, and native gold cross-cut the stock and its hornfels aureole. These gold-bearing veins are enveloped by foliated rocks with quartz, calcite, white mica, and chlorite that grade outward from the veins into trondhjemite or hornfels.The stock, emplaced into a submarine volcanic series, emanated heat that caused seawater to convect and formed a contact aureole of hornblende hornfels. The stock eventually intruded its aureole and this culminated with regional metamorphism to the greenschist facies. Regional metamorphism hydrated the stock and its hornfels aureole. Native gold precipitated with quartz along fractures from metamorphic flu ids in response to cooling and wallrock hydration. exploration for this type of gold deposits should focus around felsic intrusions that have albite and that have contact aureoles retrograded by regional metamorphism."

Jan 1, 1985

By Charles S. Barrett, Robert F. Mehl, Dana W. Smith

The Widmanstatten figures found in the steels have been long recognized and in some aspects carefully studied,&apos; especially as they occur in cast hypoeutectoid alloys. Aside from the practical importance of the structures obtained in the steels by various heat treatments, a study of the characteristics of these figures is interesting because of the rich opportunity the system affords to obtain new data on the mechanism of segregation from solid solutions. This opportunity is twofold: first, by changing composition within the austenite range the proeutectoid precipitate may be changed from that of ferrite to that of cementite, thus offering the same opportunity for changing the type of precipitate while maintaining the same basic lattice as that afforded by the Cu-Zn alloys;2 and second, the eutectoid inversion leads upon drastic quenching to the formation of martensite, a Widman-statten figure of unique interest from the crystallographic viewpoint, particularly in comparison with those formed on slow cooling.3 We have, therefore, two types of structure to study: that formed on slow cooling of hypoeutectoid and hypereutectoid alloys, and that formed on quenching hypoeutectoid, eutectoid, and hypereutectoid alloys. For each of these types of structure we require the crystallographic plane in the mother austenite along which the precipitate forms (we shall see that the precipitates in these alloys are invariably platelike in form), and also the orientation of the precipitate upon this plane. Some of these

Jan 1, 1933