By F. George, W. Tice, M. Salkind

It was found that Al-A13Ni could be readily cold rolled perpendicular to but not parallel to the whiskers. Reductions of more than 98 pct were achieved without cracking by rolling perpendicular to the whiskers, whereas extensive edge cracking was noted after only 15 pct reduction when rolling parallel to the whiskers. The longitudinal and transverse tensile strengths were nearly doubled, and the longitudinal yield strength more than tripled by cold rolling 50 pct in a direction perpendicular to the whiskers. The whiskers exhibited some waviness (elastic bending) as a result of cold rolling, but at very high reductions (greater than 75 pct) whisker fracture and misalignment became significant. A fine dislocation substructure in the matrix consisting of cells attached to the whiskers was pro -duced by cold rolling. Most of- the substructure was readily removed by a 1-hr anneal at 500°C. Cold rolling was found to substantially reduce the thermal stability of the microstructure at 610°C but did not affect the stability at 500°C. FIBER and whisker reinforced composite materials promise significant improvements in properties over conventional materials. Before they find wide use, however, it will be necessary to understand the response of these highly anisotropic materials to common metalworking processes. Most of the nonmetal-lic fiber reinforced materials have very low elongations (a few pct or less) in the direction of fiber alignment. Thus, metalworking techniques such as rolling and forging would not be as broadly applicable to these materials. This investigation was initiated to determine how a composite system consisting of Al3Ni whisker reinforced aluminum responded to rolling, what changes in the microstructure occurred, and the effect of deformation on the mechanical properties. The composite material studied was produced by unidirectional solidification of the A1-Al3Ni eutectic alloy'-7 and consisted of 10 pct by volume of aligned whiskers of Alai in a matrix of aluminum. It should be pointed out that this system is not representative of all composite materials, and the results will therefore not be universally applicable. The A1-Al3Ni system is characterized by: 1) A strong fiber-matrix interfacial bond 2) A ductile matrix 3) A sufficiently low fiber content to allow significant plastic flow between fibers 4) Strong, completely elastic whiskers (tensile strength 400,000 psi, elastic modulus = 20 X 106 psi.1 These factors allow the material to be readily rolled perpendicular to the fibers. If the fiber-matrix bond were not strong, such a weak interface could fail during rolling. A measure of the ability of a composite to be rolled in the transverse direction can be obtained from noting the transverse tensile behavior. In the case of Al-Al3Ni,2 there is considerable ductility (15 to 30 pct). In the case of boron filament reinforced aluminum, for example, the transverse elongation is less than 1 pct,8 and the material could probably not be cold rolled as readily in that direction. EXPERIMENTAL PROCEDURE 3-in. diam ingots of A1-A13Ni eutectic were unidi-rectionally solidified in graphite crucibles. The starting materials consisted of 99.99+ pct pure nickel and aluminum, and the pure eutectic ingots were made with 6.2 wt pct Ni. The unidirectional solidification process (described in detail elsewhere1-3) consists of preparing a master heat of eutectic composition, remelting, and withdrawing the ingot vertically downward through the heat source at a controlled rate so that plane front solidification proceeds upward at a constant velocity. The resulting microstructure consists of 10 pct by volume of whiskers of very high aspect (length to diameter) ratio. The fiber lengths have not been measured because of the difficulty of detecting fiber ends9 but exceeds 104. There is some possibility that the fibers may be continuous within one grain. Flat sheet specimens 2¾ in. sq and approximately 0.2 in. thick containing whiskers parallel to the plane of the sheet and to one edge were used for this study. A1-A13Ni exhibits either a rod-like (high solidification rates) or a blade-like (low solidification rates) whisker morphology,1,3 and both types were studied. Rolling was accomplished using a two-high rolling mill at a speed of approximately 10 fpm. The rolling direction was either parallel to or perpendicular to the direction of growth (direction of whisker alignment). Reductions of from 0.002 to 0.03 in. per pass were used with the most common value being 0.005 in. per pass. Cold rolling of Al-Al3Ni to more than 98 pct reduction in thickness was accomplished with no intermediate anneals. In addition. a series of speci-mens was cold rolled 97 pct with a 1-hr, 500°C anneal in air after each 50 pet reduction. Tensile testing was accomplished using a Tinius-lsen four screw testing machine. Flat sheet specimens + in. wide and between 2 and 2; in. long with the thickness dependent upon rolling reduction, were used. The gage section was in. wide and 1 in. long. Strain was measured using a clip-on LVDT extensome-

Jan 1, 1970

By R. G. Ward, D. R. Gaskell

Using the maximum bubble pressure technique, the densities of iron silicates at 1410°C have been measured blowing helium, nitrogen, and argon. By ensuring equilibrium between the melt and the blowing gas with respect to oxygen potential and by minimizing tempcrature cycling of the furnace, iron precipitation in the melt has been prevented. Thus the previously reported effect of blowing-gas composition on the densities of the melts has been eliminated. Consideration of the oxygen densities of the melts gives an indication of the structural changes accompanying composition change. The density-composition relationship of iron oxide-silica melts in contact with solid iron has been the subject of several investigations1-7 and considerable disparities exist among the various results obtained. Of these investigations, all except one5 have employed the maximum bubble pressure method. In the most recently reported of these investigations1 the density-composition relationship obtained blowing nitrogen differed from that obtained blowing argon. The measured densities obtained under nitrogen were greater than those obtained under argon, the difference being a maximum at the pure liquid iron oxide composition and decreasing with increasing silica content. This observation rationalized the disparities existing among the results of the earlier investigations, showing that two lines, one for nitrogen and the other for argon, could be drawn to fit all the earlier results. No explanation for this phenomenon could be offered. Chemical analysis of rapidly quenched samples of melt for dissolved nitrogen, and direct weighing measurements, excluded solution of nitrogen in the melt from being the cause of the increase in density. The range of blowing gases was extended by Ward and Hendersons who measured the density of liquid iron oxide bubbling helium, nitrogen, neon, argon, and krypton. The measured density was found to decrease smoothly with increasing atomic number of the bubbling gas. The work reported here is a continuation of the program initiated by Ward and Sachdev7 to study the densities in multicomponent melts in which the iron oxide-silica system is the solvent. As such it is necessary to explain or eliminate the anomalous densities of iron silicates under different atmospheres, and the present rede termination was carried out towards this end. EXPERIMENTAL The maximum bubble pressure method of density determination was again employed and the experimen- tal apparatus used was essentially the same as that used by Ward and Sachdev.7 A molybdenum-wound resistance furnace heated an ingot iron crucible of internal diameter 1 in. containing a 2-in. depth of melt. The bubbling gas was blown through a 1/4 -in.-diam mild steel tube onto the end of which was welded a 2-in. extension of 1/4 -in.-diam ingot iron rod, drilled out to 5/32 in., and chamfered to an angle of 45 deg. The blowing tube was introduced to the furnace through a sliding seal and its position was controlled by a vertically mounted micrometer screw which allowed the depth of immersion to be determined with an accuracy of ± 0.01 cm. A Pt/Pt-10 pct Rh thermocouple was located below the crucible and temperature control was effected initially by means of an on-off controller and later by a saturable core reactor. The bubble pressure was determined by measurement of a dibutyl phthalate manometer using a cathetometer. PREPARATION OF MATERIALS Iron oxide was produced by melting ferric oxide in an inductively heated iron crucible in air. The liquid was quenched by pouring onto an iron plate. Silica was prepared by dehydrating silicic acid at 650°C for 12 hr. RESULTS Before any measurements of the density of a melt were made, the density of distilled water at room temperature was measured bubbling helium and argon. Both gases gave the density as 1.00 ± 0.01 g per cu cm which showed that the density of the manometric fluid (dibutyl phthalate) was not affected by contact with the blowing gas. With the furnace controlled by an on-off temperature controller an attempt was made to measure the density of pure liquid iron oxide by bubbling argon. The furnace atmosphere gas and bubbling gas were dried over magnesium perchlorate and deoxidized over copper turnings at 600°C. It was found that the pressure required to blow a bubble at a given depth increased slowly with time, and thus it was impossible to obtain a unique value for the density of the melt. Inspection of the blowing tube after removal from the furnace showed that rings of dendritic iron had precipitated from the melt onto the immersed part of the tube. This is shown in Fig. l(a) where the various "steps" correspond to different depths of immersion. The precipitation of iron was considered to be due to one or both of two possible causes: i) The composition of the liquid iron oxide is that of the liquidus at the temperature under consideration and can be expressed by the equilibrium

Jan 1, 1968

By C. Wildman

Prospectivity modeling of seafloor massive sulphide (SMS) deposits has been completed over the Kermadec Arc-Colville Ridge area using the GIS based weights of evidence and fuzzy logic modeling techniques. SMS deposits are the current equivalent of ancient onshore volcanogenic massive sulphide (VMS) ore deposits. These high-grade deposits are formed on the seafloor and commonly consist of a black smoker and metal rich sediment mound complex resulting from the discharge of hydrothermal fluids (up to 400°C) from fractures on the seafloor. Metal sulphides are continuously precipitated in response to mixing of high-temperature hydrothermal fluids with ambient seawater. Accumulation of metal sulphides has led to SMS deposits being potentially major sources of copper, zinc, lead and other metals such as gold, silver, which to date remain untapped. Modeling of SMS deposits was undertaken to illustrate the power of GIS modeling for seafloor resource evaluation and how it can be used to quickly identify and rank in terms of the most likely prospective areas of the seafloor where new SMS deposits might exist. The mineral deposit modeling was constrained by the mineral systems concept which defines those parts of a mineralisation system that are critical to the ore-forming process. The deposits are typically formed in extensional tectonic settings, including both submerged tectonic margins and sea-floor spreading. Volcanic vent systems and underlying dykes, stocks and sills are the sources of heat that are responsible for converting sea water drawn down through fractures in the oceanic crust into an ore-forming hydrothermal fluid. This fluid is then capable of leaching metals and elements from surrounding footwall rocks, which are then transported upwards via the convection of hydrothermal fluids. The ore materials are then precipitated within the black smoker field as massive sulphides due to the mixing of high-temperature (250-400°C), metal-rich hydrothermal fluids with cold (about 2°C) oxygen bearing seawater.

Jan 1, 2011

By Preston C. Holloway

Transformational roasting involves the heating of a material along with specific additives to induce mineralogical changes in the starting material. By controlling the chemical composition, roasting atmosphere, temperature and time of reaction, the mineral transformations induced during roasting can be engineered to control the distribution of valuable, or harmful, metals and to produce new mineral assemblages that are more amenable to conventional methods of metals recovery or to environmentally safe disposal. To date, this type of process has only been applied to the recovery of a limited number of metals, but current research is looking to expand the application of these techniques to the recovery of metals from a wider range of materials. An introduction to these techniques is presented along with preliminary results from their application to metals recovery from zinc bearing wastes, such as zinc ferrite leach residues and carbon steel electric arc furnace dust.

Jan 1, 2006

By A. J. Mortlock

Cobalt and nickel have been diffused at tracer concentrations in gold at several temperatures in the range from approximately 700° to 950°C. The diffusion penetration profiles were determined by a serial sectioning technique in which the gold is first anodized and then the anodic layer is dissolved in acid. In this ulay sections as thin as 250A could be removed reproduci-bly. In all cases, the region close to the specimen surface was characterized by irregular behavior in the sense that the logarithm of concentration was not linear in the square of the penetration distance. In sotne cases, there zuas an indication of the operation of very slow dijfusion in this region, while in others the apparent diffusion coejj'icient was negative. Possible reasons for this anomalous behavior are briefly discussed. In recent years it has been found that the region close to the surface of a metal can sometimes exhibit anomalously slow diffusion characteristics relative to the interior of the metal. One of the best examples of this fact is the work of Styris and omizuka,' who showed that the apparent diffusion coefficient for zinc in the region withi: about 1 p of the free surface of copper was about ,,,, that at deeper penetrations. This result is particularly interesting, because it is free from the possibly complicating effects of low solubility of the diffusing tracer in the solvent metal. In the case of diffusion under conditions of low solubilitjr, interpretaticn of the results in terms of lattice diffusion is difficult because of the enhanced short-circuiting produced by segregation to dislocations.2'3 Measurements by Duhl et 1. suggest that cobalt diffusing in gold may also show a near-surface effect of this type. Once again the solubility is high, so that this result could be of great interest. However, the technique used for analyzing the diffusion penetration zones by Duhl, viz. the counting of residual gamma activity in the specimen following sectioning, appears to have indicated a near-surface effect in a parallel experiment on the self-diffusion of gold reported at the same time. The latter result is known to be spurious, since Kidson5 has demonstrated that self-diffusion in gold does not show this effect. Duhl et 01. also reported some measurements on the diffusion of nickel in gold, but failed to give any data for the near-surface region. As the solubility of nickel in gold is high, such data would also be of special interest. We, therefore, decided to conduct another set of experiments on the diffusion of nickel and cobalt in gold, using a sectioning technique that allows the individual sections to be assayed for solute content and thus gives direct determinations of penetration profiles. Also, by sectioning with an anodizing/stripping tech- nique, very thin layers can be removed and the region close to the surface studied in detail. MATERIALS The gold specimens were supplied as single crystal disks $ in. in diam by a in. high by Monocrystals Co. of Cleveland, Ohio. The gold itself was of spectro-scopic purity, i.e., better than 99.99 pct pure. METHOD Specimen Preparation. One flat end face of each gold crystal was spark planed with a Servomet spark erosion machine set for minimum spark energy. Following this treatment the crystals were preannealed for 2 to 4 days at temperatures of either 400" or 700°C. The three crystals preannealed at 700°C showed signs of recrystallization. The spark-planed end face of each crystal was then coated with the appropriate amount of 63i or 60 radioactive tracer. This deposit was laid down in a simple plating bath containing the as-supplied solution of the radioactive isotope as well as sufficient ammonium oxalate to saturate the solution. Some ammonium oxalate remained undissolved on the floor of the bath for this purpose. During plating further additions of ammonium oxalate were sometimes required to allow the plating to continue satisfactorily, perhaps due to passivation of the undissolved oxalate already present. The thickness of the deposited layer was determined by comparison of the apparent surface activity of the plated specimen with that of a similar specimen having a weighable deposit of the isotope on its end face. Correction for self-absorption of the radiation was made in this calculation. Annealing. The deposited crystals were annealed in a hydrogen atmosphere in sealed silica tubes. During this heat treatment they were supported, active face down, on optically flat silica plates. The temperature was measured with calibrated Pt vs Pt-10 pct Rh thermocouples, and the tabulated values can be taken to be correct to Z°C. All the crystals showed evidence of recrystallization following these heat treatments, suggesting that initially they may not have been good single crystals or had suffered strain during delivery. Concentration Profile Analysis. After annealing, the crystals were sectioned by the anodizing-stripping technique.6 The anodizing involved suspension of the specimen with its cylindrical axis horiz6ntal by a gold wire in a 200-ml beaker containing 1 M Hg304. A cathode in the form of a strip of gold sheet, 2 in. wide and positioned to be in contact with the curved side of the beaker, completely encircled the specimen. An anodizing current of 30 ma, corresponding to a current density of 5 ma per sq cm on the surface of the specimen, was passed for times ranging from 5 to 150 min depending on the thickness of gold to be removed; the solution was stirred continuously during this process. Following this treatment, the specimen

Jan 1, 1969

By C. Altstetter

THE work herein reported is restricted to the carbides which occur in quenched and tempered AISI 43XX steels with carbon contents up to 0.40 pct and silicon additions of up to 3 pct. In view of the instability and extremely small size of the carbides formed at low tempering temperatures, the technique for successfully preparing specimens for X-ray diffraction will be outlined. The alloys listed in Table I were obtained through the courtesy of the United States Steel Corp. in the form of 1/2-in. rounds forged from 100 lb. induction furnace heats (except for 4337 which was a commercial heat). The stock was normalized and then swaged and drawn to 15 mil wire with anneals at 1200F between passes. The wire was austenitized for 45 min in evacuated vycor capsules and quenched into iced brine with simultaneous smashing of the capsule. Tempering was done in air with a water quench after tempering. The carbides were extracted in a simple cell using a solution of 1M KC1 and 0.5 pct citric acid with an initial current density of 0.1 amp per sq cm. One end of a short length of wire was immersed in the solution, and the current at constant voltage was noted as a function of time. After about an hour the current dropped sharply because of the decrease in specimen cross-section. At this point it was found that the dissolution could be stopped and that the very fine wire which then resulted was just large enough to permit handling of the extracted precipitate still clinging to it, yet so small that it diffracted and absorbed only a negligible amount of the X-radiation. This rod of residue with a convenient handle of undissolved wire was rinsed in distilled water. alcohol, and acetone. Then it was dipped in a thin solution of cellulose-acetate cement and dried in vacuum. The resulting specimen was straight, uniform in density, easily handled, but most important, was completely sealed and never exposed to air. Furthermore, the residue had never been subjected to strong acids or rough handling such as in the extraction-replica technique or in the complete extraction to a powdered residue. It was found that improperly coated specimens were pyrophoric, turning to oxide with a dull red glow as they were exposed to air and yielding patterns of Fe2O3 and Fe3O4. The steels containing 3 pct Si were especially difficult to prepare for this reason. The specimens were put in a 57 mm Straumanis camera with double pinholes or slits and irradiated with filtered-chromium radiation. Readable patterns were obtained in less than an hour. A preliminary finding of some note was that for both tempered and as-quenched specimens of steels 4337 and 4337 (1.5 Si). M23C6 patterns were found along with the patterns of other constituents of the residues. This result was somewhat surprising in that previous investigators had reported that this carbide did not appear in a 0.38 pct C, 0.48 pct Mo steel1 or in chromium steels of less than about 10 pct Cr.2 Although the total amount of carbide-forming alloying elements is less than 2 pct, due to their mutual interaction and the action of the plastic deformation in promoting equilibrium, this carbide was able to form even in the steel containing 1.5 pct Si. M23C6 was not detected in the 4337 (3.0 Si) steel and the lower-carbon steels were not investigated in this condition. It is very likely then that the steels studied herein underwent a fourth stage of tempering during the anneals at 1200°F. This result has significance in that even a small amount of undissolved M23C6 in a low-carbon, low-alloy steel would exert a large effect on its hardenability. Its presence would also influence the mechanical properties by decreasing the carbon content of the matrix. Annealing in vacuum for 1 to 4 hr in the austenite field removed all traces of MZ3C+ The results on carbide precipitation during tempering, summarized in Table I, are in agreement with those of Klingler et al.3 for the higher carbon steels. For the AISI 4337 steels it is noteworthy that in the steels with added silicon the E carbide persists to longer times and higher temperatures and that silicon delays the formation of cementite. The results for the lowzr-carbon steels parallel those of the higher-carbon grade. The appearance of E carbide in the AISI 4315 is significant. There is considerable disagreem-nt in the literature as to whether this carbide forms in the tempering of steels containing less than about 0.2 pct C. Following the detection of E carbide in a 0.18 pct C plain-carbon steel,4 its occurrence in a steel containing chromium and molybdenum should be expected. The fact that the low-carbon steels have the same carbide-precipitation sequence as the high-carbon steels has bearing on the larger problem of the exact tempering reactions in all steels. Following the suggestion of Roberts et al.,' the first stage has been generally assumed to result in a metastable equilibrium of c carbide and martensite of about 0.25 pct C. From this it was concluded that a steel having less than 0.25 pct C should then be under-saturated with respect to c carbide and should not precipitate this carbide upon tempering. In view of the experimental findings of c carbide in steels hav-

Jan 1, 1962

By O. P. Arora, M. Metzger, G. R. Ramagopal

Single-phase aluminum containing 0.0001 to 0.06 pct Cu was studied in strong acid, mainly through observations of hydrogen evolution. The strong influence of copper was exerted almost entirely through the imposition after a certain delay time of an auto-catalytic localized-corrosiott reaction. Additions of cupric ion to the acid produced lower accelerations. The significance of the quantity and distribution of copper was discussed, and the implications for intergranular corrosion and neutral chloride pitting were indicated. AN investigation of intergranular corrosion in single-phase high purity aluminum exposed to hydrochloric acid indicated the copper content of the metal to have an influence on corrosion at lower levels than previously suspected.&apos; The work reported here was a closer examination of the action of copper but dealt with general corrosion to gain the advantage of having a continuous measure of corrosion through the volume of hydrogen evolved, the reduction of hydrogen ion to hydrogen gas being the principal or only cathode reaction in strong hydrochloric acid. Previous work on the hydrochloric acid corrosion of aluminum was sometimes insufficiently structure-conscious and the need for care in evaluating it arises from the low solubility of the iron impurity,&apos; and of some alloying elements, and the known or possible presence in many of the compositions studied of second phases leading to greatly increased corrosion rates.3 These increases are attributed to the presence of low hydrogen-overvoltage cathodes provided by the second phase.3&apos;4 For the present single-phase work, a few studies which used high-purity base material and small copper additions5-&apos; provide the essential information most unambiguously. The corrosion rate was shown to be increased markedly by the introduction into the acid of small quantities of the ions of copper (and of certain other metals) which cement on the aluminum and provide cathodes of low overvoltage.5 When there was sufficient copper in the aluminum, the same result was produced during the course of corrosion leading to a rate which increased with time as the reaction was stimulated by one of its products (autocatalytic reaction). In 2N (7pct) HC1, an accelerating rate was observed at 0.1 pct Cu but not at 0.01 pct.5,7 The present work dealt with corrosion rate and morphology and their correlation with the quantity and distribution of copper catalyst for copper contents from 0.0001 to 0.06 pct. PROCEDURE A lot of high-purity aluminum containing 0.0021 pct Cu, 0.001 pct Fe and 0.003 pct Si (Alloy A) was alloyed with copper to yield aluminum containing 0.014 pct Cu (B) and 0.06 pct Cu (C). Later it was found necessary to include the lower copper Alloy K which contained 0.0001 pct Cu, 0.0004 pct Fe and 0.0004 pct Si. The upper limit for any other element can be confidently estimated as 0.0005 pct. No element other than copper appears to be present in quantities sufficient to have an effect on general corrosion as great as the observed effect of the copper in A, B, and C. The only other heavy metal detected by spectrographic examination was silver (< 0.0001 pct). The acid was made up from a selected lot of 37 1/2 pct CP hydrochloric acid containing 0.1 ppm heavy metals (mainly Pb), 0.05 ppm Fe, and < 0.008 ppm As and from water distilled from 1 megohm-cm demineralized water and believed to have contained negligible quantities of heavy metals influencing corrosion. Acid strength was adjusted to within 0.05 pct HCl of the stated value by using precision specific gravity measurements. Test blanks 10 by 41 mm were sheared from 1.65-mm cold-rolled sheet. Edges were finished by filing. The blanks were annealed in air at 645°C for 24 hr in alundum boats and rapidly water quenched. The anneal is thought to have produced a substantially homogeneous solid solution—for iron, copper, or silicon, for example, the annealing temperature was 200°C or more above the solvus-and the quench is considered to have preserved the high-temperature structure except for the condensation of lattice vacancies into dislocation loops.&apos; The 0.06 pct Cu alloy did not appear unstable in respect to slow precipitation reactions at room temperature since two pairs of tests failed to show significant differences between specimens heat treated 3 1/2 years earlier and specimens heat treated 1 or 2 days before.

Jan 1, 1962

By R. P. Agarwala, M. S. Anand

Using residual activity technique, the diffusion of palladium, silver, cadmium, indium, and tin in alunzinum has been studied in the temperature range of 400" to 630°C. The diffusivities (in units of square centimeters per second) have been expressed as: IMPURITY diffusion in aluminum,1-9 silverand lead5 for cases of low solid solubility of the impurity in the host metal has yielded frequency factors in the range of l0-6 to l0-9 sq cm per sec whereas the activation energy is practically half the self-diffusion activation energy value. From the observed values of frequency factor, activation energy, and entropy of activation, it has been suggested&apos; that these solutes are not diffusing by vacancy or interstitial mechanisms but by a mechanism which should be consistent with such low values of the diffusion parameters (Do and Q). However in spite of extensive work on these types of systems, the mechanism of diffusion is still not well understood. The present investigation on the diffusion of palladium, silver, cadmium, indium, and tin in aluminum has been carried out to throw further light on the diffusion mechanism in systems, where the solid solubility is very low (except for the case of silver). The results are discussed on the basis of solid solubility and the structural changes involved owing to the presence of the solutes in aluminum solid solution. An attempt has also been made to apply the existing theories of charge5-8 and size8 difference between the solute and the solvent. EXPERIMENTAL PROCEDURE Specimens (1/2 in. diam by 3/8 in. high) were machined out of pure aluminum (99.995 wt pct) rod obtained from Johnson Mattheys. They were sealed under vacuum in quartz tubes and annealed at 620° C for several hours; the grains thus developed were sufficiently large to eliminate the possibility of diffusion along the grain boundaries. The flat ends were prepared carefully after polishing as described previously,10 Radioactive nitrates of cadmium, indium, and tin and chloride of palladium containing, respectively, cd115, 1n114, sn113, and pd103 were dissolved in distilled water and mixed with 30 pct acetone. By means of a micropipet a drop of this solution was placed on a smoothly polished and lightly etched surface of the specimen. Due care was taken to see that the solution spread uniformly on the surface of specimen without trickling down its sides. Radioactive silver was elec-trodeposited using a AgCN-KCN bath. The amount of sample deposited in all the cases was not more than 0.1 µ thick. The samples were then sealed in quartz tubes in vacuum. The cadmium samples were sealed in a purified argon atmosphere to avoid evaporation. The samples were then diffusion-annealed. The temperature of annealing varied between 400° and 630°C and was controlled to ±5°C. On heating to -400°C,the deposits of cadmium, indium, and tin, which were of the order of 0.1 p in thickness, were converted to their respective oxides. The contribution of oxygen present in the lattice of aluminum due to these oxides has been calculated and found to be less than 10 ppm in all cases. Oxide method has already been used by other workers11&apos;12 in diffusion studies without any controversy on the issue. However, in some of these investigations, metallic deposition was also tried. The diffusivities calculated from these measurements were found to agree very well with the diffusivities obtained by using the oxide method. Thus it is assumed that the measured diffusivities represent true diffusion coefficients. Since palladous chloride decomposes at about 500°C, the deposited samples which were to be diffusion-annealed below 500°C were heated in vacuum for a very short time at 500°C to allow the decomposition of palladous chloride to palladium metal. Time taken in decomposition of nitrates to oxides and chloride to metal was negligibly small as compared to the period of the diffusion anneals. The residual activity technique13 was used to study the diffusion profiles where thin layers from the specimen surface were removed by grinding it parallel to a flat surface on a 600-grade carborundum paper. The specimen was washed, dried, and weighed, the differ -ence of the weight being the measure of the thickness of the layer removed. After each such abrasion and weighing, the total residual activity on the surface of the specimens was measured by counting 0.656, 0.94,

Jan 1, 1968

By A. H. Larson, L. G. Twidwell

The influence which Au, Ag, Sb, Bi, Sn, and Cu have, both individually and collectively, on the activity coefficient of sulfur in liquid lead at 600"C zuas studied by circulating a H2S-Hz gas wlixture over a specific lead alloy until equilibrium was attained. Subsequently, the H2S concentration in the equilibrium gas mixture and sulfur concentration in the condensed phase were deterruined. The elements gold, silver, and antinzony (above 8 at. pct) increased the activity coefficient of sulfur. Bismuth had no apparent effect. Tin (above 3 at. pct) and copper decreased the coefficient. The influence of an individual element, i, on sulfur is best reported as the interaction parameter, riS, which is defined as The values o these first-order interaction zus are: ESzu = —55.0. These interaction parameters are used to predict the activity coefficient of sulfur in six fouv-component alloys and one seven-component alloy. Comparisons are made with direct experimental determinations. INTERACTIONS in dilute solution have been studied by many investigators. Most of the experimental work has been confined to solute-solvent interactions in simple binary systems and solute-solute interactions in ternary systems. Dealy and pehlke"~ have summarized the available literature on activity coefficients at infinite dilution in nonferrous binary alloys and have calculated from published data the values for interaction parameters in dilute nonferrous alloys. Interaction parameters are a convenient means of summarizing the effect of one solute species on another in a given solvent. Only a few investigators have studied interactions of the nonmetallic element sulfur in a metallic solvent. They are as follows: Rosenqvist,~ sulfur in silver; Rosenqvist and Cox,4 sulfur in steel; chipman, sulfur in alloy steels; Alcock and Richardson,% ulfur in copper alloys; Cheng and Alcock,&apos; sulfur in iron, cobalt, and nickel; Cheng and ~lcock,&apos; sulfur in lead and tin. The only reported work on the Pb-S system in the dilute-solution region is that of Cheng and Alcock.&apos; Their investigation involved a study of the solubility of sulfur in liquid lead over the temperature range 500" to 680°C. The results may be summarized by the following relationship: S (dissolved in lead) + Pb(1) = PbS(s) log at. %S = -3388/T + 3.511 Experimentally, it was found that Henry&apos;s law was valid up to the solubility limit of sulfur in lead, i.e., at 600°C up to 0.43 pct. Their investigation did not include the study of sulfur in lead alloys. More accurate calculations could be made in smelting and refining systems if activity coefficients of solute species could be accurately predicted in complex solutions. One of the objectives of this study was to compare the experimental data with the values calculated from the equations derived from models for dilute solutions proposed by wagner9 and Alcock and Richardson. A temperature of 600°C was chosen as the experimental temperature to attain reasonable reaction rates and to minimize volatilization of the condensed phase. EXPERIMENTAL Materials. The Pb, Au, Ag, Sb, Bi, Sn, and Cu used for preparation of the alloys were American Smelting and Refining Co. research-grade materials. All were 99.999+ pct purity except the antimony and tin which were 99.99+ pct. The initial alloys prepared for this study consisted of twenty-one binary alloys, eleven ternary alloys, and one six-component alloy. The constituent elements were mixed for each desired alloy and were placed in a crucible machined from spectrographically pure graphite. The crucible was placed in a vycor tube which was evacuated with a vacuum pump and gettered by titanium sponge at 800°C for 8 to 12 hr. After the gettering was completed, the chamber containing the titanium was sealed and removed. The remaining sample chamber was placed in a tube furnace at 800°C for 2 hr and quenched in cold water. The final operation consisted of homogenization of the alloy for 1 to 2 weeks at a temperature just below the solidus for the individual system. The resulting master alloys were sectioned into small pieces and a random choice made for individual equilibrations. Cobalt sulfide (Cogs8) used to control the gas atmosphere in the circulation system was prepared by passing dried HzS for 24 hr over a Co-S mixture heated to 700°C in a tube furnace. This material was then mixed with cobalt metal to give a two-phase mixture which, when heated in hydrogen to a particular temperature, produced a desired H2S/H2 gas atmosphere in the circulation system. A Cu2S-Cu mixture also used in this study was prepared in a comparable manner. Apparatus for Equilibrium Measurements. The experimental technique of this study required apparatus

Jan 1, 1967

By K. A. Jackson, G. A. Chadwick, A. Klugert

The diffusion field ahead of a lamellar interfnce is analyzed using an electrical analog. A self-consistent solution is obtained for the shape of the interfnce and the diffusion field by an iterative process. The solutions presented here are for a 50-50 eutectoid or eutectic, The shape of the interface is found to he independent of growth velocity and lamellar spacing, and to depend on the relative values of interfacial free energies at the phase houndaries . The mode of growth of lamellar eutectics and eutectoids has been a subject of much interest for many years.1-4 Mehl and Hagel 1 have shown photomicrographs taken by Tardif when he attempted to determine experimentally the shape of an advancing pearlite interface; the results are completely ambiguous. Brandt&apos; and schei13 have made approximate calculations of the composition ahead of a lamellar growth front. The shape of the advancing front and the composition distribution ahead of the front are difficult to calculate because one depends on the other. It is the purpose of the present paper to describe a method by which this calculation has been done. Lamellar-eutectic growth usually occurs under conditions where the growth is fairly rapid, and the interface temperature is close to the eutectic temperature. The growth rate is usually determined by heat flow. Eutectoid growth, on the other hand, can best be studied by quenching to some temperature, and allowing growth to proceed isother-mally. In both cases the growth is believed to be controlled by diffusion* rather than by the atomic kinetics of the transformation. This being the case, a single treatment of the diffusion equation will apply to both cases, provided the region of the interface in a eutectic may be considered to be isothermal. If a part of the interface could appreciably change its thermodynamic driving force by advancing ahead of or lagging behind the mean interface, then the two cases would not be similar. Eutectics normally grow in temperature gradients of the or-der of a few degrees per centimeter. The normal eutectic spacing is the order of a few microns. Part of the interface would have to extend many lamellar spacings ahead of the mean interface before it experienced sensibly different conditions. The interface temperature is usually a few tenths of a degree below the eutectic temperature so that temperature differences of the order of one-thousandths of a degree (a displacement of one lamellar spacing) would be unimportant. Protrusions large compared to the mean spacing do occur when one phase only grows into a eutectic liquid. This is usually a dendritic type of growth, and easily distinguishable from the lamellar mode of growth. A single treatment of lamellar growth will apply equally well to both eutectic and eutectoid decomposition. At the interface, which as shown above is essentially isothermal, the difference between the equilibrium eutectic temperature Teu and the actual interface temperature Ti, can be divided into two parts: 1) the composition varies across the interface, so that the local equilibrium temperature is not Teu; and 2) the interface is curved, so that the local equilibrium temperature is depressed according to the Gibbs-Thompson relationship. This undercooling can be written as Teu-Ti =?T = mAC(x) + a/r(x) [1] where ?C(X) is the departure of the composition at a point x on the interface from the eutectic composition, see Fig. 1, r(x) is the local radius of curvature at a point x on the interface, m is the slope of the liquidus line on the phase diagram, and a is a constant given by where s is the interfacial free energy, TE is the equilibrium temperature, and L is the latent heat of fusion. The calculations in this paper will be made only for the case where the phase diagram is symmetric, that is, the eutectic occurs at 50 pct, the liquidi have the same magnitude slope m at the eutectic temperature, and C,, the amount of B rejected when unit volume of a freezes, see Fig. 2(a), is the same for both phases. As shown in Fig. 2(b), the composition ahead of the a phase will be rich in B, the composition ahead of the ß phase will be rich in A. The composition at the phase boundary is the eutectic composition. The difference between the local liquidus temperature and the actual tempera-

Jan 1, 1964

By W. A. Backofen, D. Lee

Tlze condition of superplasticity or neck-resistanl flow that results front high strain-rate sensitivity has been observed in isothermal tension tests on several titanium alloys and one of zirconium hi general, il was associated with reasonably fine-grain micro-structures being stvained in the transformation range at rates below i - 10 -3 sec-&apos;. The metallographic mean-free path, L, was measured at room temperature after rapid cooling from the temperature of test-ing. The flow stress of Ti-GAL-4V at 950°C was proportional to La at different constanl <; the value of a decreased with increasing. E but at E< 1.5 x 10-4 sec-1 it varied only from 0.9 to 1.25. The findings were interpreted to mean that viscous boundary shear is the rate-controlling process of deformation at high levels of strain rate sensitivity in these materials. Elongation of over 1000 pet could be obtained, but a1 temperatures so high and rates so low that any practical application of the full effect would probably be difficult. As the transformation range was narrowed, by turning from Ti-6AL-4V to Ti-5Al-2.5sn to nomznally pure titanium, the allowable temperature varialion was correspondingly reduced. Superplasticily was not found in Armco iron, presumably because the transformation range was too narrow to allow the developtnenl of a reasonably stable microstructure for isolhermal lesting. THE work represented by this paper grew out of a recent study of texture hardening in a(hcp) titanium and zirconium-alloy sheet,&apos; of which part has now been published.2 It was found that, with heating, the tensile plastic-anisotropy index, R,* was decreased from well above 1 towards 1 as the temperature range for the a(hcp) -ß(bcc) phase change was entered. The clearest example of that trend is illustrated with previously unpublished data in Fig. 1. It might have been thought that such a development resulted simply from introduction of the cubic and therefore plastically less anisotropic phase. However, the accompanying change in the index of tensile strain-rate sensitivity, m = a log a/a log E, was rapidly upwards, to a high of 0.85 in some cases (also illustrated in Fig. 1). At the same time, the total tensile elongation rose to a maximum and the flow strength dropped away as R (and m) approached 1. Taken together, the observations cannot be understood as resulting from the presence of cubic phase, per se. It has been concluded instead that they reflect the largely noncrystallographic deformation which characterizes superplasticity. As demonstrated in other recent work? a necessary condition for super-plasticity is strain-rate sensitivity of flow stress sufficiently high that m is above a lower limit of -0.3. The origin of large m has been traced, in turn, to grain size so small that a substantial amount of viscous deformation is introduced by such processes as Nabarro-Herring diffusional flow4 and/or grain boundary shear.5,6 Because of problems in the processing of titanium and zirconium alloys—problems of high strength, limited ductility, and excessive springback, originating largely in slip resistance-it was natural to wonder if something useful might be done with superplasticity in those materials. Therefore experiments were made for more closely identifying and generally bounding the phenomenon with temperature and strain-rate limits, before attempting to decide about its exploitation. The results are being reported here. EXPERIMENTAL Materials. The two of primary interest were the titanium alloys of nominal composition (in wt pct) 5A1-2.5Sn and 6A1-4V. Others were a 4A1-1/4O2 titanium alloy, titanium of commercial purity (RC-70), Zircaloy-4. and Armco iron. All were received as annealed 3/16 in. thick sheet, except RC-70 which was & in. thick, and tested in that condition. Details of transformation temperature and grain size are given in Table I. The results of dilatometry for the measurement of transformation temperatures were unsatisfactory. Data were finally obtained by metallographic examination of each specimen after test, to determine from the amount of transformed 4 where the specimen had been heated in relation to the critical temperatures. Results were in reasonable agreement with information from the supplier. Strip tensile specimens were of full sheet thickness and taken along the rolling direction, except for those

Jan 1, 1968

By F. E. Pawlek, J. K. Gerlach

The chloridizing roasting of ores is applied when metal sulfides and oxides are to be converted into soluble or volatile compounds. The chlorine required is either obtained from the admixed chlorides of sodium or calcium or added in the gaseous state. In the first part of the investigations the reaction rate of the chlorides of sodium or calcium with gas mixtures of SO,-0, or SO ,-O2 ,-SO , was measured. The rate for reactions with gas mixtures SO2-O2 is ThE chloridizing roasting of ores is applied when metal sulfides and oxides are to be converted into soluble or volatile compounds. At present the process is mainly applied to produce nonferrous metals which occur in pyrite cinders in small concentrations. Thereby the nonferrous metals are converted into water-soluble, acid-soluble, or volatile compounds whereas all the iron remains as insoluble oxide. The chlorine required is either obtained from the admixed chlorides of sodium or calcium or added in the gaseous state. The reactions occurring during the roasting process can be divided into two groups: solid-solid reaction and gas-solid reaction. The reactions between solids proceed by means of solid-state diffusion and are therefore of low velocity. The heterogeneous reactions between solids and gases of the roasting atmosphere5 are high-velocity processes and determine the velocity of the chloridizing roasting. These gas-solid reactions shall be the subject of the paper presented. In order to investigate the still little-known processes which occur during the chloridizing roasting 6-&apos; the complex reaction is split into several partial steps. First the reactions of NaCl and CaCl, with gas mixtures of SO2 and 0, have been investigated at temperatures between 500" and 600°C by measuring the weight increase of the samples. The gas mixtures used in this series of experiments had first variable compositions, then the amount of SO 2 had been increased. Furthermore the influence of Fe 2 O3 admixtures upon these reactions, the behavior of pure Fe 2 O3 with the gaseous reactants, and the chlorination of the sulfides of lead, copper, nickel, and zinc have been investigated. FORMATION OF GASEOUS CHLORINE Pyrite cinders are never completely roasted and therefore contain still a small amount of sulfide sulfur. When heated again in air, this sulfur is converted into SO,. Accordingly the formation of chlorine can first be described by the reactions: dependent on the composition of the gas phase. If more than 1 pct SO 3 is added to the roasting gas, the reaction rate is determined only by the concentrations of the SO,. In the second part the reactions between chlorine and metal sulfides are discussed. The rate of formation of gaseous chlorine is higher by me order of magnitude than is the reaction rate between ZnS and chlorine. The reaction rate of NiS and PbS lies considerably below that of ZnS. The conversion rate of both pure Fe 2 O 3 and Fe 2 O 3 containing NaCl or CaCl2 when reacting with SO2-O2, mixtures with and without SO3 portions was measured at temperatures of 500", 550°, and 600°C. The weight increase of pressings was determined by means of a spiral balanceg and the reaction rate calculated therefrom according to Eqs. [ll to [31 and [5] to [7]. The prepared samples were suspended on a platinum filament in a vertically mounted tube of mullite (ID 4 cm, length 110 cm) which could be heated by a resistance tube furnace. The platinum filament was tied to the lower end of the spiral balance. A supremax glass tube (length 70 cm) was mounted gas-tight on top of the reaction tube. The unit was sealed up at its top by a ground-in stopper which was holding the spiral balance with the sample. The spiral balance therefore hung outside the high-temperature region of the furnace. Fig. 2 shows the experimental arrangement schematically. While lowering the sample into the reaction tube pure nitrogen was flowing through the reaction zone providing a protective atmosphere. After the sample had reached the reaction temperature within approximately 1 min, the protective gas was replaced by the sulfur dioxide-oxygen reaction mixture. It took about 30 sec until the mixture filled the tube homogeneously. A Ni/NiCr thermocouple placed in the center of the furnace where the sample hung during the measure-

Jan 1, 1968

By J. O. Brittain, E. P. Lautenschlager, D. A. Kiewit

Compression tests were run in the temperature range of 700° to 900°C ox 0&apos; phase NiAl intermetal-lic alloys of several grain sizes. At these temperatures the minimum strengths were observed at the stoichiometric composition. While significant increases in strength occurved in both the low-nickel (vacancy) and high-nickel (substitutional) regions, the highest strengths were found in the high-nickel region. During deformation serrated flow was sometimes observed in the low-nickel alloys. After deformation transgranular cvacking and deformation striations were observed in all compositions tested. AS part of a general investigation of the properties of NiAl inter metallic compounds, a preliminary study of the role of point defects upon plasticity was made by high-temperature compression tests on ß&apos; NiAl specimens of several grain sizes and compositions. ß&apos; NiAl is an intermetallic compound having a CsCl structure and a rather wide range of composition from A1-45 at. pct to 60 at. pct Ni.1 According to Bradley and Taylor2 and to cooper,&apos; it possesses a defect lattice in which departures from stoichiometry in the direction of decreased nickel content lead to the presence of vacant nickel sites (although Cooper&apos;s work indicates that a small amount of substitution also occurs) whereas departures on the high-nickel side lead to substitution of nickel on aluminum sites. NiAl forms congru-ently from the melt at approximately 1650°C,1 and thus has a higher melting point than either of its component elements. Up to this time, although this and other high-melting intermetallic compounds have been suggested for elevated-temperature usage,4 only the hardness4 and a few tensile-strength measurements5 have been reported for NiAl at high temperatures. In the present investigation the effects of composition upon the compressive-strength properties in a range of 700° to 900°C have been measured for NiAl of several grain sizes. EXPERIMENTAL PROCEDURES The alloys were made as described elsewhere6 from an A1-46.8 at. pct Ni master alloy furnished by the International Nickel Co. with additions of high-purity nickel and aluminum. The charges were vacuum-induction-melted in A12O3 crucibles with small amounts of helium added to the atmosphere to suppress vaporization. They were cooled slowly from the melting temperature to achieve uniform grain size. In order to refine the as-grown grain size a special rolling technique was developed. Alloys were packed into 0.10-in. wall-type 302 stainless-steel tubes which were partially filled with magnesium oxide to prevent bonding between the alloy and the steel jacket. The ends of the tubes were closed by hot forging, and the packets were then hot-rolled. The alloys with greater than 50 at. pct Ni were rolled at 1100°C, but it was found necessary to increase the temperature to 1350° C before alloys with less than 50 at. pct Ni would roll without cracking. With these temperatures, reductions as high as 48 pct were achieved in a single pass. The rolled alloys will hereafter be referred to as "fine grained" whereas the as-grown material will be designated "coarse-grained&apos;&apos;. The compression specimens were made by cutting square cross-sectional pieces, approximately 3/16 by 3/16 by 1/2 in., with a water-cooled diamond cut-off wheel from the as-grown or the rolled alloys. Specimens were ground to their final dimensions by polishing through 3/0 grit silicon carbide papers. The final shape was a rectangular parallelepiped of square cross section having a height-to-width ratio of 3:1. Compression testing was carried out in a compression rig of our own design mounted on an In-stron Floor Model. The specimen chamber could be heated to 1000°C and was controlled within ±2°C. The compression rig was enclosed within a bell jar and was maintained at a 50 µ of mercury vacuum throughout the duration of the test. The test cham -ber was heated from room to test temperature within 15 min. Specimens were then held at the test temperature 30 min prior to testing. Previous experiments indicated that no grain growth would occur within this time. An Instron Variable Crosshead speed unit was used to adjust for small variations in specimen lengths in order to have a constant initial strain rate, €, for all specimens of a group. For the fine-grained specimens the strain rate was changed rapidly at constant temperature by a factor of 10 with the speed lever on the Instron. For a given € the compression data was analyzed in terms of true plastic strain (E) and true compressive stress (0).

Jan 1, 1965

By G. P. Airey, R. F. Mehl, T. A. Hughes

The coarsening of cementite particles in a ferrite matrix has been studied in a series of steels with 0.15 pct C only and 0.15 pct C plus 1 pct Ni, Mn, and Cr, respectively. Two initial states were employed: quenched nartensite, and quenched and cold-rolled martensite. A series of tempering temperatures between 500&apos; and 700" and tempering times of up to 190 hr were used. The structures were studied by replica and transmission electron microscopy. Particle size distribution curves were determined. From the average size value coarsening curves were obtained. These were plotted in accordance with the Wagner analysis assuming diffusion control. A discussion of the significance of the results is given. L HE reactions occuring upon the tempering of martensite have long engaged the attention of metallurgists. The latter stages, when cementite particles coarsen in a ferrite matrix, have been studied both qualitatively and quantitatively. Studies of such coarsening processes have recently been spurred by the publication of the Lifshitz-Wagner theory1, and the extension of this to the a Fe-Fe3C system by Oriani3 and by Li, Blakely, and einold. Following Wagner the coarsening process is often designated as "Ostwald Ripening". The only quantitative data on the rate of coarsening, except for the work of Hyam and uttin,&apos; in the a Fe-Fe3C system are those of Bannyh, Modin, and odin&apos; for a commercial eutectoid steel and those of Heckel and ereorio" using a pure eutectoid steel. The data of Bannyh, Modin, and Modin have been employed by 0riani3 to derive the a Fe-FeE interface energy. The reaction is one of the most important ones in steel and is worthy of detailed study. This is the purpose of the present study. Laboratory heats were prepared; these were steels with approximately 0.15 pct C, selected so that the num ber of carbide particles would be relatively small and thus so that the overlapping diffusion fluxes would be minimized, presumably a desirable circumstance.&apos;-3 In addition to Fe-C alloys, comparable heats containing 1 pct of Ni, Mn, and Cr, respectively, were included with a view of appraising the effect of alloying elements. This report includes an account of the micro-structures observed, primarily with the electron microscope, and of kinetic data and their interpretation. MATERIALS AND TREATMENT The alloys were prepared from electrolytic iron ("Plastiron") and high-purity graphite; these were melted in a zirconia crucible using a vacuum furnace. The alloy steels were made by adding electrolytic nickel, electrolytic manganese, and "vacuum grade" chromium, respectively, under a partial pressure of argon. Each melt was poured into a mold within the vacuum furnace and cooled in the mold. The ingots were 2 in. in diam. and 8 to 10 in. long. The analysis of the alloys is given in Table I. These ingots were hot-rolled to strip 0.1 in. thick, then cold-rolled to 0.05 in. and each alloy split into two batches. One batch was austenitized at 1200 for 1 min, quenched in cold brine, then cold-rolled to 0.02 in.; samples given this treatment are hereinafter designated as "worked". The other batch was cold-rolled to 0.025 in., austenitized at 1200" for 1 min, and quenched in cold brine; such samples are hereinafter designated as "quenched". These two batches were then tempered, as below. The purpose of the treatment given the first batch was to provide an initial structure of cold-worked martensite, with the expectation that the additional defect structure created by cold work would encourage a higher rate of nucleation of cementite on tempering and hence a more uniform distribution of cementite particles. Individual specimens were sealed in evacuated quartz or Pyrex tubes, then tempered in a muffle furnace. The temperature control was better than 3&apos;C at 700. Tempering treatments wer: performed at 400°, 500°, 550°, 600°, 65o°, and 700C for time periods between 15 min and 190 hr. PREPARATION OF SPECIMENS Specimens for optical and replicalelectron microscopy were mounted, polished conventionally, and etched with 2 pct nital. For electron microscopy, single-stage "formvar" replicas were made, dry-stripped and rotary-shadowed with chromium at an angle of 30 deg. Carbide extraction replicas were prepared from electropolished specimens usirig the method described by Smith and uttin.&apos; Thin foils for electron transmission microscopy were prepared by chemical thinning in an H202-HF bath prior to electropolishing in a chromium trioxide-acetic acid solution. The most

Jan 1, 1969

By G. A. Vissac

The drying of fine coal involves special techniques, which are discussed and analyzed. Types of dryers employing these techniques are described. Calculations are presented for new methods of dealing with the entrained dust that is always present in fine coal drying operations. NEW conditions, new requirements, and new methods have increased the demand for more efficient and more economical methods of drying fine coal. Dewatering of larger sizes may reduce the surface moisture to 8 or 9 pct. It is more difficult, however, to dewater sizes below 1/4 in., and some filter cakes still contain as much as 20 or 25 pct moisture. Increased freight rates and stricter consumer specifications have resulted in a demand for further reductions in moisture content. This can be obtained only by heat drying. Most modern methods of heat drying disperse or spread the mass of coal to be dried, in an atmosphere of dry hot gases. The more intimate the contact between coal particles and hot gases, the quicker and more efficient the drying operation will be. Two different techniques are generally employed, using either a fluidized condition or an entrained condition of the coal to be dried. Fluidized Condition Fluidization of a body of sand was defined and explained by Fraser and Yancey in a paper published in 1926.&apos; This condition was artificially obtained and maintained by proper regulation of the rate of air flowing through the sand body. "The sand bath &apos;boils&apos; uniformly on the surface," they write, "and feels like a fluid." The fluidization technique was also described and analyzed by Steinmetzer2 in connection with the operation of an air cleaning table. His main conclusions are as follows: "Fluidity is, for the particles involved, the possibility of motion with minimum friction. . . . Then fluidity requires the introduction of various forms of energy capable of neutralising frictions. Two solutions can be used— air and/or mechanical motions (such as the shaking motion of the carrying deck of the air table). The combination of mechanical and air energy will give the widest margins of size ratios and of bed thickness, translated in capacity per unit area of the carrying table." Richardson and Langston3 have indicated results obtained with a dryer working with a fluidized bed. They used a vertical tube type of dryer, however, without the assistance of any mechanical energy, and without any lateral motion of the fluidized bed. The capacity of such a dryer is too limited for practical applications, since the speed of the acceptable air currents is held to the speed of fall of the particles involved. Capacities as low as 182 Ib of coal per hr per sq ft of dryer area are indicated. As stated by Richardson: "A basic limitation to a fluidised bed dryer is that the velocities of the gas must be held within a definite range; with velocities of 10 ft per second, all coal minus 6 mesh in size will be entrained, and the operation is then similar to that of a Flash dryer." A fluidized bed must be virtually static. The coal particles simply kept in suspension offer a minimum resistance to the flow of gases, insuring the most favorable conditions for rapid evaporation of surface moisture. However, very wet fine coal, i.e., over 12 pct of surface moisture, will be delivered in the forms of mud balls, or as a soggy, sticky mass, almost impossible to disperse, sticking and acting as a wet blanket on the deck. Strong currents of gases and wide deck perforations will be required to punch holes in the wet mass and gradually loosen and fluidize it. The mechanics of fluidizing a bed of coal in a gas medium for the purpose of obtaining the most efficient drying condition are entirely similar when the fluid used is water and the purpose is to break up and distend a bed of coal to be cleaned so that perfect stratification according to densities will be insured. Purely mechanical energy is used in the basket-type jig, water pulsations in the piston and in the Baum-type jigs. A combination of mechanical motion and of air pulsation offers the most efficient and favorable conditions. Entrained Condition The most critical factor to be considered in the design of a dryer employing the entrained condition technique is the speed of the hot gases to be circulated in the drying column. With insufficient gas velocity, excessive amounts of the largest sizes will drop to the bottom of the dryer column without being thoroughly dried. On the other hand, high gas velocity will cause degradation, dust losses, and high power consumption. Figs. 1 and 2, reproduced from Hanot,4 show the relative importance of speed and temperature for various sizes of particles. It can be seen, for instance, that to maintain in unstable equilibrium particles of 1/4-in. size in a gas current at 500°C, a speed of 30 meters per sec, or 6000 fpm, will be required. For % -in. particles an almost prohibitive speed of 45 meters per sec, or 9000 fpm, will be necessary. In practice, maximum gas velocities of 3000 fpm are recommended; since power increases as the cube of the velocity, it can be seen that beyond certain limits such dryers would not be economical. If the particles were moving at the same speed as the hot gases they would remain in the same

Jan 1, 1954

By P. T. Chiang

Chemical etching methods for the simultaneous revealing of the tellurium or selenium Phase and the chalcogenide grain boundaries of the alloy systems are given. A tellurium eutectic was found Present in zone-melted ingots. Similarly, a selenium monotectic was present in ingots. In general, the second phase (tellurium or seleniumn) occubies three different sites; viz., along the chalcogenide grain boundaries, as inclusions within the chalcogenide grain, and on the undersurface of the ingot. The detection limit for the tellurium phase is about 1 u in width. THERMOELECTRIC materials based on Group V (bismuth, antimony) and Group VI (selenium, tellurium) elements have aroused considerable interest in recent years in the practical application of thermoelectric cooling. In many cases, a small amount of excess tellurium (or selenium) was added to the material to optimize its thermoelectric properties. Then the question immediately arises as to the number of phases present in the resultant alloy. In the binary systems of Bi-Te, Sb-Te, and Bi-Se, the congruent melting compositions have been reported to be non-stoichiometric and are represented by Bi~Te respectively. It is to beexpected and known that Bi2Te3 and SbzTe3 crystallize from the melt with an excess of bismuth and antimony in the lattice and that tellurium forms a eutectic.~&apos; The same could be assumed to take place in the pseudo binary systems of (Bi,Sb)zTe3 and Bi2(Se,Te)3 as well as in the system studiedby puotinen5 and other workers. Likewise, BiaSe3 crystallizes from the melt with an excess of bismuth in the lattice and selenium forms a monotectic.~ Therefore, in practice, alloys solidified from the melt often contain a second phase (tellurium or selenium) in one region or another of the solid mass even without the addition of excess tellurium (or selenium). ~u~~recht&apos; studied the thermoelectric properties of (Bi,Sb)2Te3 alloys with excess tellurium and simultaneous additions of selenium. He mentioned that the materials show two phases because of the considerable excess of tellurium or selenium. However, he did not report as to how the tellurium or selenium phase was identified. It is generally believed that the presence of an excessive amount of tellurium or selenium phase in the alloy would adversely affect its thermoelectric properties and its uniformity. Consequently, there is a need for a simple method for the identification of the tellurium and selenium phase. The quantity of the second phase present is usually too small to be detected either by chemical analysis or by normal X-ray techniques. This investigation was therefore carried out, first, to devise a simple metallographic method for the identification of the tellurium or selenium phase coexisting with the chalcogenides and, second, to determine the distribution and specific location of the tellurium or selenium phase in the ingots. EXPERIMENTAL PROCEDURE The starting materials used for the alloy preparations were 99.999 pct pure bismuth, antimony, and tellurium and 99.997 pct pure selenium. The bismuth and antimony were obtained from Consolidated Mining and Smelting Co. of Canada Ltd., while the selenium and tellurium were obtained from Canadian Copper Refiners Ltd. The tellurium was purified further in the laboratory by zone refining. The elements were pulverized in a stainless-steel pestle and mortar. The amounts for the desired composition were weighed out each time on an analytical balance to make up a 100-g sample. Then the sample was introduced into a Vycor ampule (19 by 150 mm), pumped down to a vacuum of 10"5 Torr for 15 min, and sealed off. The ampule was then heated in a horizontal resistance furnace at 800" to 900°C for about 20 hr. During this period the assembly was rocked back and forth several times to ensure good mixing. At the end of the heating period, the ampule was quenched in cold water and then transferred to the zone-melting apparatus described in a previous publications to grow large-size aligned polycrystals. The background and ring-heater temperatures were adjusted to make the freezing solid-liquid interface slightly convex to the liquid. The recorded temperature gradient in the vicinity of the freezing solid-liquid interface was around 15°C per cm. The ampule was moved horizontally at a speed varying from 0.4 to 2 cm per hr so that the ring heater would cover the whole ingot length from end to end. A single zone-melting pass was used for the Bi-Te, Sb-Te, and Bi-Sb-Te ingots. Two passes in the forward and reverse directions were carried out for the Bi-Se and Bi-Se-Te ingots. Six passes in the forward and reverse directions were performed for the Bi-Sb-Se-Te ingot. The zone-melted ingots were found to contain several large crystals, with their basal planes (0001) approximately parallel to the growth axis. Samples of bismuth and antimony tellurides coated with a layer of tellurium, and bismuth selenide coated with a layer of selenium, were prepared for comparison in phase identification. These coatings were made by dropping a piece of the zone-melted ingot into some molten tellurium or selenium under argon atmosphere and allowing them to cool slowly to room temperature. The metallographic specimens were prepared by

Jan 1, 1969

By H. Biloni, R. Morando

The surface structure and substructure of Al-Cu alloys solidified as conventional ingots and under particular conditions such as those used by Bower and Flemings are studied. The influence of lampblack coating on the mold walls is especially considered and the results compared with those obtained in copper and graphite molds where no coatings exist. When high heat extraction conditions exist the observations show that mechanism of copious nucleation is responsible for most of the chill zone. When the heat extraction through the mold walls is low, a coarse grain structure with dendritic morphology arises, with a size that depends on the degree of convection present, analogous to that analyzed by Bower and Flemings. In both cases the effect of the convection on the macroscopic and microscopic appearance is discussed. The ingot macrostructure consists of one or more of three zones: "chill zone", "columnar zone", and central "equiaxed zone". The mechanism of the columnar-equiaxed transition has been subject of considerable interest and at present at least three theories exist about the formation of the equiaxed region: 1) the constitutional supercooling theory1 maintains that the equiaxed crystals nucleate after the columnar zone has formed, as a result of the constitutional supercooling of the remaining liquid; 2) chalmers2 pointed out, however, that there were several objections to this proposal, and that consideration should be given to the possibility that all the crystals, equiaxed as well as columnar, originated during the initial chilling of the liquid layer in contact with the mold; 3) Jackson et aL3 and O&apos;Hara and ~iller~ suggested that a remelting mechanism of the dendrite arms is responsible for the formation of the equiaxed region. After the work of Cole and Bolling and other authors6 it became evident that convection (natural, reduced, or forced) plays a very important role in the transition from columnar to equiaxed and on the size of the resultant equiaxed structure. Until recently the accepted explanation of the chill zone was that it occurs as a result of copious nucleation in the liquid layer in contact with the mold walls.798 The columnar region is a subsequent result of the growth of favorably oriented grains and, as a result of a selection mechanism studied by Walton and Chalmers,9 elongated grains with marked texture are formed. Recently, however, Bower and Flemings" using an ingenious laboratory experiment introduced the idea that the "copious nucleation" mechanism is not responsible for the formation of the chill zone and that the presence of convection, introducing some form of "crystal multiplication", plays a decisive role in the formation of the chill zone. Unfortunately, it is important to consider that for their conclusions Bower and Flemings extrapolated the results obtained in their special experiments to the case of conventional ingots, and that these authors only analyzed the macrostructures of the specimens. Let us consider the work by Biloni and chalmers" concerning predendritic solidification. These authors were able to show that a study of the segregation substructure of A1-Cu gives information about the nucleation and growth of crystals formed in contact with a cold surface. A spherical predendritic region characterizes the first part of every grain nucleated in contact with the surface as a result of the chill effect. The aim of this paper is to elucidate through the observation of the segregation substructure the conditions under which (in the Bower and Flemings type of experiments and in conventional ingots) either the nucleation or the multiplication mechanism gives rise to the structure in contact with the mold walls. I) EXPERIMENTAL TECHNIQUES The experiments were performed on two alloys: Al-1 wt pct Cu and A1-5 wt pct Cu. The purity of the aluminum was 99.99 pct and the copper 99.999 pct. The results obtained with both alloys were similar. In the Bower and Flemings type of experiments the apparatus employed to obtain rapid solidification against a surface was similar to that used by those authors. The liquid was drawn by partial vacuum into the thin section mold cavity. Plate casts were 5 cm wide and usually 7.5 cm high. The thicknesses of the cast were 0.1 and 0.3 cm. Two different materials were used for the mold, copper and nuclear-grade graphite. The internal mold surfaces were polished and left uncoated for some experiments. In other experiments, the copper or graphite surface was coated with a thin film of lampblack material. In some of these particular experiments one of the mold walls was left with an uncoated region (usually in the form of a cross). The conventional ingots were cast in graphite or copper molds. In different experiments the mold walls were sometimes uncoated or coated with lampblack material. The results obtained in conventional and Bower and Flemings copper molds were compared with those obtained with copper molds coated with a very thin film of graphite; the results obtained were essentially similar. The size of the conventional ingots was 5 cm diam and 7 cm high in all cases. The cast surfaces produced by the Bower and Flemings type of experiments and conventional methods were observed macroscopically and microscopically without any metallographic preparation. As Biloni and Chalmers showed," the observation of the chill surface can give considerable information about the structure and segregation substructure.

Jan 1, 1969

By K. R. Carson, J. Weertman

An attempt is made to ascertain the mechanism of tangle and cell formation and its dependence upon dislocation-interstitial carbon interactions. The strain-hardening behavior of single crystals of 3.25 pct Si-Fe was determined at 300° and 425°K and under conditions of both continuous and interrupted tensile strain. Significantly enhanced hardening was observed in crystals deformed at the elevated temperature, and it was further accentuated by interrupted straining. Transmission electron microscopy was used to study the resultant dislocation structures. Strain aging was found to aid tangle and cell formation at 425°K, but at both temperatures embryo tangles formed solely from primary glide dislocations, presumably by a process involving cross slip and "mushrooming". IN the course of plastic deformation all bcc metals and alloys develop a dislocation structure characterized by loose-knit groups of tangled dislocations. With increasing strain the tangles become more tightly knit and grow larger; finally a three-dimensional cellular substructure is formed:1 This process has been observed with the transmission electron microscope.&apos;-l7 However, most investigations were confined to the study of nearly pure polycrystalline metals at relatively low temperatures. At intermediate temperatures, 0.17 to 0.14 Tm where T, is the melting temperature in degrees absolute, the mobility of interstitial impurities such as carbon is high enough to permit migration to nearby glide dislocations but is still low enough so that a significant drag force is exerted.18,19 it is also in this temperature range that a hump occurs in the curve of work-hardening rate vs temperature for iron. Analogous plots for tantalum" and columbiumzo show a definite upward trend in the work-hardening rate. Keh and Weissman1 have pointed out that this behavior may be explained solely on the basis of changes in the dislocation configuration: at low temperatures the dislocations tend to be relatively straight and uniformly distributed, but at intermediate temperatures tightly knit tangles and cellular substructure appear. The interference of these tangles with glide dislocations causes the observed increase in the work-hardening rate. This explanation appears reasonable, yet one might ask what factors cause tangle formation to be so favorable at intermediate temperatures. It seens likely that the strong dislocation-interstitial interactions which are known to occur in this temperature range are at least partly responsible," with the magnitude of the effect being proportional to the interstitial concentration. The purpose of the present work is to study the relationship between tangle formation and strain hardening in a bcc metal in the temperature range 0.17 to 0.4 Tm. Particular emphasis was placed upon a study of the effects of interstitial-dislocation interactions. Single crystals of 3.25 pct Si-Fe containing about 200 ppm of C in solid solution were used in the investigation for the following reasons: 1) The mobility of interstitial carbon in 3.25 pct Si-Fe is negligible at 300°K but increases rapidly at slightly elevated temperature22. Hence, differences between the flow curves and dislocation structures of crystals deformed at 300°K, 0.17 T,, and crystals deformed, say, at 425°K, 0.24 Tm, should be appreciable because of the enhanced dislocation-carbon interactions at the elevated temperature. This effect was accentuated in some samples by interrupted straining, thereby introducing a certain amount of aging. 2) Near room temperature, slip in suitably oriented 3.25 pct Si-Fe single crystals is largely confined to the (110) planes.23&apos;24 Dislocation structures formed under conditions of single glide are the least complicated and their method of formation is the most easily discernable. 3) Dislocations in Si-Fe can be tightly locked with carbon atmospheres by a low-temperature aging treatment. The subsequent thinning of samples to foil thicbess causes little or no rearrangement in the dislocation structure.25 EXPERIMENTAL PROCEDURE Large single-crystal sheets of 3.25 pct Si-Fe were donated by Dr. C. G. Dunn of the General Electric Research Laboratory, Schenectady, N. Y. The orientations of the sheets were determined and slabs 1.0 by 0.25 by 0.05 in. were cut such that the desired tensile axis corresponded to the long dimension. The slabs were mechanically polished and subsequently decar-burized by heating at 1000°C for 3 days in a flowing wet-hydrogen atmosphere. A carbon content of about 200 ppm was introduced by heating at 805°C for 25 min in a flowing atmosphere of dry hydrogen containing heptane vapor. Shaped copper tools were then used to spark-machine at 0.125 by 0.50 in. gage length onto each slab. Vacuum annealing at 1225°C for 2 days followed by a quench into the cold end of the furnace to retain carbon in solid solution concluded the soecimen preparation. Continuous tensile flow curves for crystals of severa1 orientations Were obtained both at 300&apos; and 425°K. A strain rate of 6.67 x 10-4 Per set was used in these and all other tests. Crystals oriented for single glide, B and D in Fig. 1, were subjected to a 3.5 pct plastic elongation to insure uniform slip along the gage length; they were then immediately subjected to interrupted strain cycling as indicated in Fig. 2(a). Each cycle consisted of unloading to 1.5 kg per sq mm, holding

Jan 1, 1969

By A. D. Zunkel, A. H. Larson

Equilibrium arsenic contents of Pb-As alloys in contact with PbO-As2O3 slags containing less than 30 mol pct As2O3, were determined at 650°, 700: and 750 C in an inert at?rzosphere. In this temperature range, the arsenic content of the alloy increased with increasing temperature in the single-phase liquid slag region and decreased with increasing temperature in the two-phase slag region and the single-phase solid-solution slag region. The PbO-As2O3 phase diagram below 22 mol pct As2O3 was determined by thertrzal analysis and by application of a log ?As2O3/?PbO vS log XAs2o3 /x3pbO plot determined from the equilibrium actiuity data. The resulting phase diagram was not well-defined since the eutectic temperature was not detected in the thermal analysis experiments, although a region of terminal solid solubility of As2O3 was found. Results from the phase diagram determination are compared with an existing diagram in the literature. THIS experimental investigation is an extension of a study by the authors1 on the slag-metal equilibria in the systems concerned with commercial lead refining processes such as softening and dross fuming. The first part of this investigation was a study of the slag-metal equilibria in the Pb-PbO-Sb2O3 system. The only experimental work previously done on the Pb-PbO-As2O3 system was by Pelzel2,3 in which the phase diagram for the PbO-As2O3 system was determined below 50 wt pct As2O3 and the equilibrium constant for the reaction 3Pb + As2O3 + 3PbO + 2As was determined as a function of temperature. No slag-metal equilibrium data have been determined. It is due to the scarcity of information regarding the Pb-PbO-As203 system that this work was undertaken. This paper describes the determination of the slag-metal equilibria in the Pb-PbO-As203 system by equilibrating Pb-As alloys with PbO-As2O3 slags in an inert atmosphere, the effect of 1 wt pct additions of bismuth and copper on the slag-metal equilibria, and the PbO-As2O3 phase diagram both by thermal analysis and the use of the slag-metal equilibria data. EXPERIMENTAL Materials. The materials used in this investigation were analytical reagent-grade and assayed as follows: 1) 99.8 pct PbO (0.014 pct insoluble in CHJCOOH, 0.02 pct not precipitated by H2S, 0.1 pct CaO, and 0.08 pct SiO2); 2) 99.95 pct As2O3; 3) 99.99 pct Pb; 4) 99.0 pct As; 5) 99.99 pct Cu; and 6) 99.97 pct Bi. Room-temperature X-ray patterns revealed no detectable impurities in any of these materials. Apparatus for Equilibrium and Thermal-Analysis Determinations. The resistance-heated crucible furnace used in this investigation employed nichrome elements and was mounted so that it could be raised to surround the reaction tube during each experiment and, subsequently, lowered. A schematic diagram of the apparatus is shown in Fig. 1. Each charge was heated in a 3+-in.-OD by 31/2-in.-high 416 stainless-steel crucible placed in a 41/4-in.-1D by 18-in.-long fused-silica reaction tube which was closed at one end. On a shoulder around the crucible was placed a 3: -in.-OD by 12-in.-long open-end fused-silica condenser tube. The open end of the reaction tube was covered by a water-cooled brass cap with ports for 1) admitting an inert atmosphere to the system through a stopcock, 2) introducing a stainless-steel, motor-driven, paddle stirrer into the crucible, 3) evacuating the system with a mechanical vacuum pump, and 4) sampling the melt with Vycor sampling tubes. The brass cap was fitted to the open end of the reaction tube with a silicone gasket and collar clamp. The furnace temperature was controlled by a Barber-Coleman Capacitrol controller and a chromel-alumel thermocouple. Due to the corrosiveness of the melt, the controlling thermocouple also served as the measuring thermocouple. The temperature of the melt was calibrated against the controller temperature and was checked periodically during each test with a Vycor-enclosed calibrated chromel-alumel thermocouple. The temperature measurement and control can be considered accurate to ±3°C. Procedure. The charge placed in the crucible for each experiment consisted of 1000 g of Pb-As alloy and 300 g of PbO-As2O3 slag. The crucible was then placed in the reaction tube, the condenser tube was placed on the shoulder of the crucible, the silicone gasket and brass cap were fitted on the open end of the reaction tube, and the entire system was evacuated and filled with argon ten times. After the last flushing, a positive argon pressure of 1 psig was impressed on the system. The furnace was then raised to sur-

Jan 1, 1968

By G. R. Speich

The interlarnmelm spacing, growth rate, and degree of segregation that accompany cellular precipitation in four Fe-Zn alloys containing 9.7, 15.2, 23.5, and 30.5 at. pct Zn have been determined in the temperature range 400" to 600°C. The chemical free-energy change for the reaction was calculated from the available thermodynamic data and the known compositions of the phases. The fraction of the chemical free-energy change for equilibrium segregation that is converted into interfacial free energy decreases from 0.43 to 0.08 as the magnitude of this free-energy change increases from 35 to 270 cal per mole. At constant temperature the cellular growth rate is proportional to the cube of the dissipated free energy. At 600°C newly 100 pct of the equilibrium segregation is achieved during cellulm precipitation whereas at 400°C only 85 pct of the equilibrium segregation is attained. During cellular growth, mass transport of zinc occurs by grain boundary diffusion; excess zinc remaining in the a! phase after the completion of growth is removed slowly by volume diffusion. A modified Cahn theory of cellular precipitation predicts the observed interlamellar spacing within a factor of two. In cellular precipitation reactions such as pearlite formation or discontinuous precipitation, the basic problem is to predict the variation of growth rate G, interlamellar spacing S, and degree of segregation P with composition and temperature. To accomplish this we need three independent equations relating these quantities. One of these equations comes from the diffusion solution. To obtain two additional independent equations, some assumptions must be made. cahnl has suggested recently that two plausible assumptions are 1) that growth rate is proportional to the dissipated free energy and 2) that the spacing which occurs is that which maximizes the dissipated free energy. According to the first assumption, this spacing also maximizes the growth rate and the rate of decrease of free energy per unit area of cell boundary. The present work was undertaken to test these assumptions. To test the first assumption it is necessary to study a cellular reaction over a wide range of supersatura-tions to establish a relationship between G and the dissipated free energy at constant temperature. This is possible only in discontinuous precipitation reactions since in pearlite reactions constituents other than pearlite form if the composition of the parent phase deviates even slightly from the eutectoid composition. The Fe-Zn system was chosen for study because 1) discontinuous precipitation proceeds to completion over a wide temperature and concentration range, 2) the degree of segregation within the cell can be measured by lattice parameter measurements,2 and 3) the thermodynamics of this system have recently been determined by Wriedt.3 In this system the cells consisting d alternate lamellae of a and r phases form from supercooled iron-rich a phase. The a phase within the cells is bcc as is the original a phase, cia, but has a different orientation and a slightly lower zinc content than the original a phase. The r phase has a zinc content of about 70 at. pct and a crystal structure isomor-phous with T brass. EXPERIMENTAL PROCEDURE Four Fe-Zn alloys with 9.7, 15.2, 23.5, and 30.5 at. pct Zn were prepared from carbonyl-iron powder (400 mesh, 99.8 wt pct Fe) and zinc powder (200 mesh, 99.99 wt pct Zn). The powders were ball-milled together and cold-pressed under 60,000 psi to discs $ in. thick by $ in. diam. The cold-pressed discs of the alloys with 9.7 and 15.2 at. pct Zn were sealed in evacuated silica capsules and heated slowly to 1100°C over a period of 1 week (3 days at 600°C, then 3 days at 80O°C, then 1 day at 1100°C). The alloys with 23.5 and 30.5 at. pct Zn were treated similarly except that the final homogenization temperatures were 1000" and 85O°C, respectively, to prevent melting. The alloys were quenched in iced brine from the final homogenization temperature. Specimens of each alloy were subsequently aged in salt pots at temperatures of 400°, 450°, 500°, 550°, 600°, and 650°C for times that varied from a few minutes to several hundred hours. At a late stage of this work, an alloy containing 11.2 at. pct Zn was prepared by vapor-impregnation of iron foil with zinc vapor at 890°C. This alloy proved useful for electron microscope studies because it was free of porosity. The homogenization and aging conditions were based on the recent Fe-Zn phase diagram of Stadelmaier and Bridgers4 rather than the earlier diagram of ansen.5 They consist of a homogenization heat treatment in the homogeneous a field followed by an aging treatment in the two-phase a + r field. The aged specimens were metallographically polished and etched in 2 pct nital and the radius of the largest cell in the microstructure determined. This radius plotted vs time gave a straight line whose slope is the boundary migration rate or growth rate G of the cell. To determine the interlamellar spacing, specimens were examined by surface-replica and thin-section electron microscope techniques. Because of the irregular nature of the lamellae within the cell, the average interlamellar spacing S .of the cell was measured by the method of Cahn and Hagel,6 where S is defined by:

Jan 1, 1969