By J. Chipman, N. J. Grant, H. L. Bishop

In a recent review1 of the iron-oxide activity of simple open-hearth type slags containing lime, magnesia, silica, and iron oxide, it was established that activity values were lacking in the range of slag composition most interesting to open-hearth operators. That is, laboratory experimental results were not available for simple slag compositions having basicity ratios ranging from about 1.5 to 4.0 and iron-oxide concentrations ranging from about 10 to 30 pct. However, in order to estimate iron-oxide activities for the range of slag compositions of interest to open-hearth operators, activity values were calculated using ionic concepts of slags by following the treatment of Flood and Grjotheim.2 A study of these data indicated that the desired slag compositions were probably not obtained due to the limited solubility of the basic constituents lime and magnesia. Thus, it was decided to make additional heats equilibrating molten carbon-free iron with slags containing MnO, P2O5, and A12O3 in percentages commonly found in open-hearth refining slags, and to examine the liquid slag field over a greater composition range than that of the simple slags studied previously. The ranges of the constituents used in the present study are summarized as follows: Metal Pct 0 0.070-0.201 PctMn 0.005-0.142 Slag Pet CaO 24.45-41.90 Pct MgO 3.23- 9.21 Pct MnO 1.13- 9.62 Pct FeO 20.08-48.7 Pet Fe2o3 2.23-10.14 Pct SiO, 3.51-28.50 Pct P2O5 0.23- 3.65 Pct A12O3 0.43- 3.38 The experimental procedure consisted of equilibrating the slag and metal in an induction furnace provided with a carbon-arc slag heater as described previously by Winkler and chipman.3 The data obtained were used to establish both the iron-oxide activity values and the activity coefficients for FeO and MnO in the open-hearth type slags. RESULTS AND DISCUSSION I) Iron-Oxide Activity of Open-Hearth Type Slags—The iron-oxide activities of various iron-oxide contents of the open-hearth type slags, as calculated from the oxygen content of the metal by the method of Taylor and Chipman, 4 are plotted against the molar ratio of bases to acids in Fig. 1. The data represent slag-metal studies carried out in the temperature range 1530" to 1700°C. For the purpose of this study, the constituents CaO, MgO, and MnO are assumed equal on a molar basis in their effect on the iron-oxide activity; and, PO2,5 is calculated as an equivalent to SiO2 and A12O3 on a molar basis. The total iron content of the slag is calculated to FeO and is represented by the symbol (FeO) The points presented in Fig. 1 represent the results of this investigation for iron-oxide slags containing between 1 and 8 mol pct MnO and less than about 2 mol pct each of A12o3 and PO2,5 The curved lines shown in Fig. 1 represent the results of the summary1 of the iron-oxide activities of simple slags of the system (CaO + MgO) - SiOz - (FeO),. The solid portions of the curved lines represent experimental data, and the broken portions represent iron-oxide activities calculated from ionic concepts of slags. The iron-oxide values of the open-hearth type slags of this study are in good agreement with the values of the simple iron-oxide slag system. Only a slight modification is indicated. The results of this study suggest that the line for 20 mol pct (FeO), should be lowered slightly in the basicity range 1.5 to about 3.

Jan 1, 1959

By Klaus Schwerdtfeger

The rate of formation of silicon monoxide from silica spheres has been measured at 1500°C in H2, H2-H2O, H2-He, H2-Ar, and CO-CO2 gas mixtures. Indications are that in the hydrogen-containing gases the reaction rate is mainly determined by convective diffz~sion. In the CO-CO2 mixtures the rate approches a constant value which is independent of sphere diometer (and gas velocity). This suggests that a surface reaction becomes rate controlling in CO-CO2 gas. WHENEVER silica is exposed at elevated temperature to a strongly reducing atmosphere there occurs, inevitably, a volatilization of silica by the formation of gaseous silicon monoxide. Because of the importance of this reaction in metallurgical processes and laboratory experiments, its kinetics were studied in the present work. EXPERIMENTAL The spheres made of vitreous silica were suspended by a molybdenum wire in the hot zone of a gas-tight high-purity recrystallized alumina furnace tube of 3.1 cm internal diam and 100 cm length. Molybdenum wire resistance heating was used. A purified H2, H2-H2O, H2-He, H2-Ar, or CO-CO2 gas mixture was passed through the tube, from top to bottom. The amount of silicon monoxide formed was determined by weighing the silica balls before and after the experiments. The silica balls were made from commercially available translucent fused quartz glass. In experiments with hydrogen-containing gases the silica stayed vitreous during the experiment, whereas in experiments with CO-CO2 mixtures, which were performed over longer times, the balls were always crystallized to cristobalite (as determined by X-ray examination) at the surface. Constant-pressure head capillary flowmeters were used to control the composition of H2-He, H2-Ar, and CO-CO2 gas mixtures. The oxygen and water vapor were removed from the gases containing hydrogen by passage through columns containing platinized asbestos (450°C) and an-hydrone. The CO was purified from O2 and CO2 by passing it through activated copper (200°C) and through ascarite. The H2-H2O gas mixtures were prepared by passing purified Hz through a mixture of oxalic acid dihydrate and anhydrous oxalic acid held at a constant temperature in a water bath. The equilibrium water vapor pressures of oxalic acid dihydrate-anhydrous oxalic acid mixtures were taken from the available data.1 The furnace system was checked for sufficient gas tightness at regular intervals. As an additional check, the H2O and CO2 contents were measured in the exit gas and were found to agree closely with the metered contents when H2-H2O or CO-CO2 mixtures were used. When purified H2 was used, H2O pressures found in the exit gas were always below 0.1 mm Hg. These contents originate either from an incomplete reoxidation of silicon monoxide in the cold part of the furnace or from small leaks which cannot be avoided. If the latter is the case, such small uncontrolled H2O contents decrease the partial pressure of SiO in equilibrium with SiO2 by less than about 7 pct, which is considered small in comparison to other experimental uncertainties. The temperature of the furnace was controlled automatically in the usual manner. The reported temperature was measured with a Pl-Pt/l0pct Rh thermocouple and was accurate to ± 5°C. TRANSPORT-CONTROL LED RATE OF REDUCTION The gaseous convective diffusion from the surface of a sphere can be predicted from the semiempirical relationship obtained by Ranz and Marshall2 in a study of the evaporation of water and benzene drops in air. The following equation applies:

Jan 1, 1967

By K. T. Aust

The relative interfacial energies of symmetrical tilt boundaries in silver of greater than 99.999 pct purity were measured as a function of orientation difference 0 between 9° and 36° about <001>. The results are in good agreement with the dislocation model of the grain boundary. The energy vs H curve may be represented by the Shockley and Read equation in the form Eoe (0.55—In 8). READ&apos; has indicated that an ideal experimental method of testing the predictions of the dislocation theory of the grain boundary would be to measure the interfacial energies of symmetrical tilt boundaries between face-centered-cubic grains that have a common <001> axis, as a function of orientation difference 0. The misfit H should be defined by a rotation of each grain through an angle of H/2 away from the boundary. Such boundaries might be expected, from geometrical considerations, to be made up of a series of edge dislocations, at least for small values of 0. Energy vs H relationships for tin&apos; and lead:&apos; were previously obtained for an asymmetrical tilt boundary separating two grains in which generally only one grain was rotated about a <001> specimen axis through an angle of H away from the boundary, the other grain remaining fixed. It is possible, however, that the boundary atoms in tin and lead may have attained a symmetrical position, in relation to the orientations of the grains on either side of the boundary, during equilibrium annealing. The two sets of measurements on silicon ferrite&apos; were somewhat better suited for comparison with theory, since the boundaries were symmetrical tilt boundaries in which the axis of relative rotation was <110> in the first series and <l00> in the second; but this alloy has a body-centered-cubic structure. Although the grain boundaries in silver" were symmetrically tilted, the axis of relative rotation was not a simple crystallographic direction, and it varied from boundary to boundary. Although the above measurements were in good agreement with the Shockley and Read equation,"&apos;: it appeared desirable to carry out experiments under the ideal conditions specified by Read.&apos; Consequently, the relative energies of symmetrical tilt boundaries in silver between grains that have a common <001> axis were measured. The technique of equilibrating grain boundaries in oriented tricrystals was used rather than the less satisfactory thermal groove method previously employed for silver bicrystals." Experimental Details and Observations The solidification and seeding techniques, described previouslyh for growing tricrystals of controlled orientations, were used to prepare tricrystal specimens from silver of greater than 99.999 pct purity. The silver was obtained from American Platinum Works, Newark, N. J., in the form of poly crystalline rods 10 cm long and 7 mm in diam. These rods were then cold worked by rolling or drawing them into suitably shaped blanks. Single crystal seeds and tricrystals were grown in a high purity graphite boat by means of a movable furnace with globar heating elements. The graphite boat was enclosed in a Vycor tube, which was first evacuated to about l00/u Hg and then filled with a static argon atmosphere. The maximum temperature outside the Vycor tube was 1250°C. A typical tricrystal specimen of silver is shown in Fig. 1. Grains B and C were grown from seed crystals with a <001> specimen axis or longitudinal direction parallel to the direction of growth and with another <001> direction perpendicular to the surface. Each of the two seed crystals was rotated 18" about the <001> specimen axis but in opposite directions away from the boundary. A symmetrical tilt boundary, therefore, separated grains B and C with an orientation difference 8 of 36" about <001>. Grain A in Fig. 1 was grown from the middle seed with a <110> direction parallel to the specimen axis and with a <001> direction inclined at 45&apos; to the surface of the specimen. The interfaces sepa-

Jan 1, 1957

By F. Paredes, W. R. Holman, R. W. Crawford

The diffusion coefficient for hydrogen in the ß titanium alloy containing 13 pct V, 11 pct CY, and 3 pct A1 was measured over the temperature range 20° to 500°C. Results fit the expression: D= 1.58 x lgs exp-------==-----) cm2,sec THE diffusion coefficient for hydrogen in the metastable ß-phase titanium alloy containing 13 pct V, 11 pct Cr, and 3 pct A1 was measured as part of an investigation of the effects of hydrogen on the mechanical properties of titanium alloys. Several theories on the mechanisms of hydrogen embrittle-ment include diffusion of hydrogen at ambient temperature as an important step in the embrittling process.&apos;-5 In hydrogen-contaminated a-ß titanium alloys, it has been postulated that the rate-controlling step may be the rate at which hydrogen diffuses from the ß phase to stress- or strain-nucleated brittle hydride platelets at the a-ß interface.&apos; However, embrittlement of the all-ß alloy investigated in this work may proceed by a different mechanism, since this alloy can be embrittled without the formation of detectable hydride platelets.6 Troiano has suggested that in this case the mechanism of delayed failure or embrittlement is similar to that proposed for high-strength steel, i.e., repeated crack initiation caused by a decrease in bonding energy as hydrogen diffuses to points of high tri-axial stress at the root of a notch. In both types of alloy the rate of embrittlement is believed to be controlled by diffusion of hydrogen in the ß phase. Accurate hydrogen-diffusion data in the vicinity of room temperature should therefore be of some assistance in understanding the mechanisms of embrittlement in these two classes of titanium alloys. Diffusion of hydrogen in pure titanium has been studied by Wasilewski and Kehl7 at temperatures above 500°C. Their measurements on diffusion in the ß phase were extended below the ß-a transformation temperature (882°C) to approximately 600°C. This was possible because of the 8 stabilizing effect of hydrogen. No results at lower temperatures have been published and there are no data in the literature on hydrogen diffusion in the ß -phase alloy used in this program. Hydrogen diffusion in metals is generally investigated by measuring the rate of transport of hydrogen past a solid-gas interface, i.e., by absorption, permeation, or degassing-rate measurements. These methods produce accurate diffusion data when bulk diffusion is the rate-determining step in the over-all process. However, at the lower temperatures of interest in hydrogen-embrittlement studies or under conditions where surface films are present, the measured rates may be surface-controlled and the calculated diffusion coefficients will be in error. Surface effects were eliminated in the present work by using a modification of the common welded-couple technique m which two bars with uniform but different compositions are joined before the diffusion anneal." The same type of step change in the initial concentration vs distance curve was produced by electrolytically hydrogenating thin-strip specimens which had been electrically insulated over half of their length. Concentration vs distance curves were determined, after appropriate diffusion-annealing treatments, by vacuum-extraction analyses of transverse samples sheared from the strips. Diffusion coefficients were calculated by the methods of Grube.M This technique was feasible because of the large concentrations of hydrogen which can be charged into p -phase alloys without the formation of hydrides15&apos;16 and because of the extremely low degassing rates observed when hydrogenated titanium alloys are heated in air. EXPERIMENTAL WORK The diffusion couples were cut from a 0.022-in.-thick mi ll-annealed sheet.* Strips 8 in. long by 1/2

Jan 1, 1965

By P. Bolsaitis, L. Skolnick

A model of metallic solutions is postulated which explains the energy of formation of alloys on the basis of changes in electron density around solute and solvent atoms and changes in pairwise interactions between atoms. The model is based on the Wigner-Seitz cell model of metals, with the electronegativities of the metals as the parameter for the electron-attracting power of the constituent atoms. In contrast to models based on the description of cohesive energy in terms of pairwise interactions only, which require an empirical, adjustable correction parameter to the Berthe-lot relations in order to predict negative energies of formation, the electron cell model accounts for both negative and positive energies on the basis of parameters of the pure components. Calculated heats of mixing based on published parameters of the pure metals are found to compare favorably to experimental values, despite the absence of any adjustable parameters in the model. THE formulation of an "exact" quantum mechanical model for the energy of cohesion of metals reduces ultimately to the many-body problem and for a complete solution would require the knowledge of wave functions and energy levels of all the particles in the system. The case of alloys is further complicated by the fact that the potential fields around the constituent atoms are different and the matching of boundary conditions in terms of the resulting wave functions is still an unresolved mathematical problem. It appears that in spite of the numerous investigations that have led to an elucidation of many properties of the metallic state, the formulation of the Hume-Rothery rules in 1931 marks the lone accomplishment toward simple, qualitative prediction of the energy of formation of alloys. More recently Friedel&apos;&apos; and Arafa have utilized the modern concepts of the electronic structure in metals in combination with the Hume-Rothery rules to arrive at quantitative estimates of the energy of formation of alloys with low solute contents. The relative success of the Hume-Rothery rules and Friedel&apos;s and Arafa&apos;s studies encouraged broaching the subject of formulation of a model based on realistic physical parameters and of conceptual and mathematical simplicity that could be applied to alloys regardless of concentration. On the basis of the free-electron theory, the cohesive energy of pure metals can be expressed as a function of "valence" (number of free electrons per atom), lattice parameter (or density), and the ioniza-tion energy. In addition to the electronic contributions to cohesion, one has to consider the pairwise exchange interaction energy between neighboring ion cores and the contribution from van der Waals forces. The energy changes upon alloying are viewed as resulting primarily from a redistribution of electron densities around the ions (a simplification of the more basic concept of a change of the wave functions of the electrons in the presence of a perturbing potential field). In addition there is a change in the pairwise interactions between neighboring ions which is usually the only factor taken into account in commonly used adaptations of the quasichemical theory. The electronegativities of the metals forming the alloy are used as the measure of the electron-attracting power of the ions in the alloy and the difference in electronegativities as the driving force for changes in electron energy on alloying. The interplay of pairwise interactions and electronic forces results in positive or negative energies of formation of alloys. Results obtained for systems to which the free electron model is best applicable are in good agreement with experimental values. 1) COHESIVE ENERGY OF METALS IN TERMS OF THE ELECTRON CELL MODEL The simplest physical model of a metal is that of a lattice of positive charges immersed in a sea of uniform, negative charge distribution represented by the

Jan 1, 1969

By J. F. Held

In a study of the influence of cold rolling on mechani cal properties of steel, it was found that the specific rolling procedure influenced crystallographic orientation. Properties developed by several rolling modes were determined and related to crystallographic orientation. Sanzples were cold-rolled various amounts on a laboratory mill. When palm oil was used as a lubricant, the crystallographic orientation was homogeneous throughout the thickness of the samples. Other samples were rolled without lubrication. Variations in intensity of the recrystallization texture components persisted throughout more than 50 pct of the volume of these samples. When the average plastic strain ratio, which is dependent upon crystallogvaphic orientation, was plotted as a function of percent reduction, a maximum was found at 40 pct in the samples which contained the observed texture variation. No maximum was found for the samples with the homogeneous texture distribution. Other mechanical properties, such as tensile strength and yield strength, were not influenced by the variation in crystallopaphic orientation. MECHANICAL properties of steel sheets depend, in general, upon the structural properties of the steel. For example, the Petch equation describes the relationship between yield strength and grain size. Other properties, such as hardness, vary with chemical composition. The plastic strain ratio, or R value, has been found to be dependent upon crystallographic orientation . In the course of investigating the effect of cold rolling on mechanical properties, it was found that a previously reported relationship between percent cold reduction and R value was not always observed. Published data had shown that the optimum cold reduction for best R values is 70 pct for aluminum killed steel.&apos; However, by altering the rolling conditions, the optimum reduction can be shifted to much lower values, or it can be moved to very high values. This paper describes the rolling conditions that lead to shifting of the optimum cold reduction. The effect of rolling conditions on the various structure parameters and the resulting mechanical properties are evaluated. EXPERIMENTAL PROCEDURE Samples of three low-carbon aluminum killed steels were cold-rolled various amounts on a 9-in.-diam 2-high laboratory mill. Hot-mill thermal practice and steel chemistries are listed in Table I. Steel A was rolled with palm oil lubrication and heavy reductions on each pass; i.e., a total reduction of 75 pct was ac- complished with a maximum of five passes. Steel B was rolled without lubrication, and light reductions were given on each pass. After approximately 75 pct reduction, it was necessary to use a small amount of light oil to achieve any additional reduction in thickness. Following cold reduction, the samples were box-annealed at 1300°F for 10 hr. The heating rate between 800" and 1300°F was 50°F per hr, and the cooling rate following the soak period was 50°F per hr. Tensile specimens were machined from the annealed material and these were used to measure yield strength, tensile strength, and the plastic strain ratio (R value). Recrystallization textures were determined by an inverse pole figure technique.*&apos;3 Integrated intensities of the (110), (002), (112), and (222) reflections were recorded for those planes lying parallel to the sheet surface. Examinations were made on both surfaces of each sample, and also at various levels beneath each surface to approximately 0.010 in. depth by etching techniques. RESULTS R Values. The R values obtained in steels A and B are shown as a function of percent cold reduction in Fig. 1. No optimum cold reduction was observed in steel A, rolled with palm oil lubrication. It is likely, however, that an optimum reduction would have occurred had higher reductions than 88 pct been employed. The optimum reduction in steel B occurred at 40 pct. The behavior in both of these steels is quite

Jan 1, 1968

By T. M. Geffen, J. L. Sanderlin, F. F. Craig, D. W. Moore

Scaled reservoir models have been used to study the effect of gravity on oil recovery performance in frontal-drive operations; namely, water, gas, or solvent flooding. The difference in density between the reservoir oil and the injected fluid causes their segregation, resulting in a non-uniform advance of the fluid front. In the laboratory flow tests, which simulated both five-spot and linear injection operations in flat reservoirs, the viscous, capillary, and gravity forces present in these operations were scaled. Dyed fluids were used so that the gross movement of the injected fluid could be observed. The studies covered a range of injection rates, formation thicknesses, and rock and fluid properties normally encountered in field operations. The results of the model tests indicate that the volume of the reservoir contacted by the injected fluid at its breakthrough into the producing well is less than that expected based on information which neglects gravity effects. This difference can often be as much as 80 per cent by gas or water injection in uniform sand bodies. Preliminary flow tests on a non-uniform sand body indicate that the uniformity of the flood fronts may in some situations be influenced to a much greater degree by permeability variations within the rock body than by gravity effects. The magnitude of fluid segregation due to gravity is controlled by the average injection rate, rather than day to day or week to week variations. INTRODUCTION One of the important factors controlling the oil recovery from a frontal-drive operation, such as water, gas, or solvent injection, is the volumetric sweep efficiency. This factor is a measure of the gross portion of the reservoir that is contacted by the displacing fluid. The volumetric sweep efficiency is influenced by gravity effects, well arrangements, and variations in rock permeability within the reservoir. The gravity effects are due to the displacing fluid being of different density than the reservoir oil. This causes the displacing fluid to move preferentially toward either the top or bottom of the formation. Non-uniform advance of the flood front can be caused by the relative positions of the injection and production wells. Variations in rock permeability also result in an uneven advance of the displacing fluid. Gas zones, representing paths of low resistance, may result in non-uniform movement of the injected fluid. The more uneven the advance of the displacing fluid, the lower is the volumetric sweep efficiency and thus the lower the oil recovery efficiency. The effects of well arrangement and permeability variations, upon the gross movement of the injected fluid have been the subjects of extensive investiga-ti0ns.1,2,3,4,5,6 Gravity effects have been recognized as being present in frontal-drive operations&apos;.&apos; but there has been little quantitative measure of their magnitude. Very likely the reason gravity effects have not been studied is that this problem does not lend itself to simple experimental or mathematical analysis. The development of reservoir modeling techniques has made possible a quantitative determination of the effect of gravity on fluid segregation and thus upon the oil recovery performance of frontal-drive operations. This paper presents a progress report on a laboratory investigation of gravity effects in fully liquid-saturated, horizontal, uniform as well as non-uniform systems. These results were obtained from scaled experiments on both linear and five-spot systems within the range of conditions normally encountered in secondary recovery operations. This study is concerned with the gross movement of the injected fluid to the time it first reaches the production wellbore. Therefore, it should be emphasized that the results of this paper can not be used to determine the effect of gravity segregation on oil recovery efficiency at abandonment conditions. MODEL SCALING The science of scaling models is relatively new as applied as petroleum production problems, Many of the scaling techniques have been adaptions of those used in basic studies of heat and fluid flow. There are

Jan 1, 1958

By R. W. Fountain, J. F. Libsch

ONSIDERABLE time and effort have been ex- pended recently in research designed to provide a better understanding of the solid state transformations leading to the permanent magnet qualities of many commercial alloys. The knowledge derived from these investigations has resulted in the development of new magnetic materials as well as improvements in some of the older materials. The permanent magnet qualities of the newer alloys having high residual inductions and high coercive force values, have been attributed to the precipitation of a second phase or an order-disorder transformation in a solid solution. The ternary Co-Fe-V alloys provide an interesting group of magnetic materials having a wide range of magnetic properties. The low vanadium alloys&apos; possess soft magnetic properties similar to the binary Co-Fe alloys, while at higher vanadium contents (about 10 pct) interesting permanent magnet properties are obtained.2,3 Previous work by Nesbitt&apos; on the ternary Co-Fe-V permanent magnet materials, resulted in the conclusion that the precipitation of a second phase, ?, was responsible for the permanent magnet qualities of these alloys. However, unlike the conventional precipitation hardening alloys, the ? phase, which is stable at high temperatures, is precipitated in the low temperature a phase upon aging. Recent work by Geisler and Martin"." has established that the order-disorder reaction inherent in the binary Co-Fe alloys is also present in the ternary Co-Fe-V alloys. On the basis of their investigation, it was proposed that ordering of the a phase is also a possible explanation of the mechanical and magnetic hardening in these alloys. Thus, it appears that the Co-Fe-V alloys are rather unique in that two solid state transformations are taking place which may account for the properties of these alloys. In view of these facts, the present investigation was undertaken to study the mechanism of mechanical and magnetic hardening in the 10 pct V-Co-Fe alloy with particular reference to the role of the ? phase; and to correlate the results of this study with other magnetic properties. In addition, the influence of increasing vanadium contents on the transformation of Co-Fe alloys was also undertaken to supplement the main objective of the investigation. Experimental Procedure The Co-Fe-V alloys used for study consisted of: 1—a commercial lot of Vicalloy I, a 10 pct V alloy, and 2—alloys prepared by powder metallurgy and containing 52 pct Co and 0 to 14 pct V, balance iron. The commercial alloy was received in the cast and forged condition and was used primarily for the detailed study of hardness, electrical resistivity, and magnetic properties of the 10 pct V alloy. The powder metallurgy alloys were prepared from electrolytic iron, commercial cobalt, and ferro-vanadium powders. The processing cycle was as follows: 1—Elemental powders were weighed and mechanically mixed for 24 hr. 2—Mixed powders were pressed at 60,000 psi into the form of bars 5/8 x 5/8 x 5 in. 3—Bars were sintered in an atmosphere of purified dry hydrogen for 24 hr at temperatures ranging from 1380" to 1340°C, depending upon the vanadium content. The as-sintered bars were cut in half; and one half was machined to 7/16 in. diam for thermal analysis. The remainder of the bar was hot forged to approximately 0.050 in. for X-ray diffraction analysis. Additional details of sample preparation are presented subsequently according to the type of test performed. Thermal Analysis Measurements One of the simplest and most widely used tools for determining phase relations as they change with temperature and composition is to study the rate of change of temperature of a material as heat is supplied or extracted at a constant rate. The thermal analysis method used in this investigation is the inverse-rate method described by Smith.&apos;

Jan 1, 1954

By Flavio Rojos-Tapia, Oscar Pereira-Cerda, Samuel Sánchez-Pino, Samuel Sánchez-Baquedano

"Pneumatic flotation was introduced to the Chilean Copper Mining Industry in 1993 by Ingeniería de Minerales S.A. (IDM). The technology is based on the designs of Dr. Rainer Imhof from Germany, who is the designer of several different types of pneumatic flotation cells, already sold through his Company Maelgwyn Mineral Service Limited (MMH). The company is represented by Ingenieria de Minerales S.A. (IDM) in South America.Pneumatic flotation, has been used in tough industrial applications .It has been successfully used for metallic ores such as copper sulphide and oxide minerals, copper slag, silica and silicates from iron magnetic preconcentrate (reverse flotation) and gold. It has also provided promising results when applied to molybdenum flotation. The latest applications, with ultrafine molybdenum particles in operating plants, is showing the V and G Cell (end model designed) as a real technological alternative to conventional flotation., The G Cell is an extremely high speed flotation machine with high selectivity which introduces the possibility of producing a final molybdenum concentrate with only one stage of cleaning. This is a completely new development in molybdenum flotation in the industrial circuit which has the potential to dramatically reduce the circulating load in the cleaning circuit. As a consequence the capital costs of future Molybdenum plants may also be reduced. The suitability of the G Cell will have to be determined on a case by case basis but it provides the metallurgist with an alternate flowsheet for consideration.The good performance of the G Cell can be explained by the high gas hold-up and very effective micro-turbulence which helps improve the attachment of solid particles to the bubbles. This technology may change our traditional concept of residence time in flotation. Additionally, the rotation phenomena introduced in the vessel of the G Cell ,creates radial separation forces which are critical to achieving a more rapid separation of the target minerals from the tailing. This results in a much reduced residence time requirement in the flotation machine. Some benefits associated with the use of the new G Cell are: less energy consumption, less maintenance costs, simple and reliable circuit to operate and a small area required for installing the circuits.As a result of the industrial experience in the Chile, the pneumatic flotation type G Cell can be regarded as a technology which must be considered as a replacement technology for the rougher and cleaner stages for fine particle flotation."

Jan 1, 2008

By Robert M. Grogan

Fluorspar is the commercial name for fluorite, which is the mineral having the composition CaF2, calcium fluoride. Its valuable properties are due to its content of fluorine, and it is the only important commercial source of that element. The name is derived from the Latin fluere, to flow, because the mineral melts easily and is a good flux. History The mineral has been known since Greek and Roman times, when it was used for drinking cups and ornamental slabs. Various peoples including the Chinese and the American Indians have carved ornaments from large crystals. Its usefulness as a flux was known to Agricola, who wrote about it in 1546.1 Mining began in England about 1775 15 and at various places in the United States during the period 1820 to 1840.28 Substantial production was achieved first in the period 1888 to 1900 in consequence of the development and widespread adoption of the basic open hearth method of making steel, in which fluorspar is used as a flux. After that, production and usage was stimulated by growth in the steel, aluminum, chemical, and ceramic industries and accelerated by World Wars I and II. The organic fluorides called "Freons" entered the picture in 1931, and the use of anhydrous HF as a catalyst in the manufacture of alkylate for high octane fuel blends began in 1942. The development of the froth flotation process in the late 1920&apos;s, a differential flotation scheme for separating fluorspar from galena, sphalerite, and other minerals in the 1930&apos;s, and the application of heavy-media concentrating methods to the treatment of low-grade ores in the 1940&apos;s were outstanding technological contributions that enabled increased production of fluorspar concentrates. Composition and Properties Fluorite in its purest form contains 51.1 pct calcium and 48.9 pct fluorine. Substitution of small percentages of cerium and yttrium for calcium have been noted.4 Mechanical inclusions of gases and fluids such as petroleum and water, and of other solid minerals such as pyrite, marcasite, and chalcopyrite are common. The fluorspar of commerce contains attached and admixed mineral impurities, chiefly calcite, quartz, barite, celestite, and various sulfides. It is interesting that the purest commercial form in which the mineral is sold, acid grade concentrate, contains a minimum of 97 pct CaF2, and as such is of comparable purity to many reagents used in chemical laboratories. Fluorite has a marked tendency to occur in large, well-formed crystals sometimes six to ten inches on a side. It crystallizes in the isometric system, frequently forming cubic and octahedral crystals or combinations thereof. The mineral also occurs in massive and in earthy forms, and in crusts or globular aggregates with radial fibrous texture. Crystalline fluorspar exhibits a great array of colors, from colorless and water clear to yellow, blue, purple, green, rose, red, bluish and purplish black, and brown. The colors are often arranged in alternating bands parallel to cube faces. They may be altered by exposure to X-rays, heat, ultraviolet light, and pressure, and are caused by a variety of factors including the presence of trace impurities and displaced ions in the lattice. Sometimes the changes induced by X-rays can be reversed by ultraviolet radiation. The mineral has a hardness of 4, and is the model of that hardness on the Mobs scale.

Jan 1, 1960

By Frank C. Aplleyard

The two calcium sulfate minerals-gypsum and anhydrite-occur in many parts of the world, and gypsum has long been of economic importance in the family of industrial minerals. Gypsum, the dihydrate form of calcium sulfate (CaSO4•2H2O) and anhydrite, the anhydrous form (CaSO4) are frequently found in close association, and it is seldom that a calcium sulfate deposit will consist exclusively of one mineral or the other. Although known gypsum deposits are extensive, anhydrite makes up the largest part of total calcium sulfate reserves. However, it has very minor economic use, and most of the following discussion will be devoted to gypsum. Calcium sulfate is one of the principal constituents of evaporite deposits, and when pure, has the following composition: [Sulfur Combined Lime Trioxide Water (CaO) (SO,) (H2O) Gypsum 32.6% 46.5% 20.9% Anhydrite 41.2% 58.8% -] Deposits of pure gypsum or of pure anhydrite which are large enough to be considered commercial have never been found because of both the metastable relationship between the two minerals, and the presence of impurities such as calcium or magnesium carbonates, chlorides, other sulfate minerals, clay minerals, or silica. As a result most mine production of gypsum will range between 85 and 95% pure. Often it is used as mined, although in certain cases, one or more forms of mineral beneficiation are employed to upgrade the product. End Uses The largest use for gypsum is based upon the unique property which calcium sulfate has of readily giving up, or taking on, water of crystallization. With the application of a moderate amount of heat in a process known as calcining, gypsum is converted to plaster of paris (the hemihydrate of calcium sulfate, CaSO4 ½ H2O) which when mixed with water will set or harden as the calcium sulfate returns to the dihydrate form. This semifinished product, usually called stucco, is then manufactured into a large variety of plasters, wallboard, and block for construction use, or into plasters for industrial applications. About 75% of the gypsum used in the United States is calcined for these purposes. Uncalcined uses of gypsum are principally as a retarder for portland cement, as a soil conditioner, as a mineral filler, and other minor industrial applications. About 25% of the gypsum mined in the United States goes into these markets; however, in less developed countries where construction and other industrial uses may be quite limited, the use of uncalcined gypsum for portland cement retarder may well be the dominant-if not the only-market for the mineral. It has often been noted that calcium sulfate constitutes the world&apos;s largest reserve of sulfur, and minor use of both anhydrite and gypsum has been made to produce sulfuric acid or other sulfur compounds such as ammonium sulfate. However, because sulfur is readily available at lower cost from other sources, use of calcium sulfate has been limited to only a few locations where it could compete economically. No such use is reported in the United States at this time. Mineralogy Anhydrite, CaSO4 because of its geologically rapid conversion to gypsum, and relatively high solubility (about 0.2 g per 100 g H2O) is not often found outcropping in climates wet enough to support abundant vegetation except on steeply dipping slopes or other places where hydrated material is continuously removed. Anhydrite rock is most often light to bluish gray in color, and under the microscope, varies

Jan 1, 1983

By John L. Halls

INTRODUCTION In this section, it is assumed that the reader is an engineer with sufficient training in underground mining work, preferably with budgetary control, to understand the mining methods outlined in other sections of this handbook. The mining-method descriptions are not repeated herein; only sufficient information is provided to enable the reader to comprehend the development of the costs presented. All costs are in 1977 US dollars, except where explicitly stated otherwise. CAPITAL INVESTMENT The capital investment in the underground mining portion of any mining property includes the following: 1) The development of original access involving adits, shafts, declines, etc. It includes the necessary equipment for transporting men, materials, and rock. 2) The purchase of mine equipment including loaders, underground haulage equipment, fans, pumps, electrical distribution, surface facilities associated with the underground mine, etc. 3) Sufficient preproduction mine development to assure steadily increasing production after startup. De- pending upon the mining method used, the preproduction development should provide a supply of three months to one year of ore that is developed and is ready to be stoped. Underground development also includes excavations other than shaft stations, loading pockets, sumps, etc., which usually are associated with the means of access and are excavated by the contractor. These excavations could include a crusher cavern, an ore- storage pocket, and underground workshops that may or may not be included by the shaft-sinking contractor. Portions of these could be delayed until after production begins, but it is preferable to complete them during the development phase, so there is no interference with the production buildup. 4) The staff and labor costs for all phases from inception through final production. 5) The provision of mine-surface equipment and facilities strictly applicable to the underground portion of the operation. The required facilities include a changehouse with a lamp room, a first-aid station, compressors, an electrical substation, workshops, a ware- house, water pipelines to the concentrator, water storage tanks, explosive storage, etc. A concrete-batch plant, a sand-fill plant, and boilers for heating may be required. 6) Other direct and indirect costs. 7) Engineering, design, and procurement costs. 8) Contingency allocations. 9) Contractor&apos;s fees, startup costs, and owner&apos;s costs. Original Access As part of a study for the US Bureau of Mines, Dravo Corp. conducted an extensive literature research survey covering underground operations in the United States between 1963 and 1973. Table 1 is compiled from the section of that study pertaining to the types of access to underground mines. Table 1 does not include distances attributable to the deepening of existing shafts, nor does it include shafts bored by raise drills or downhole machines that need existing underground workings for the disposal of the cuttings. During the period under review in the report ( 1963 through 1973). concrete-lined circular vertical shafts were the predominant means of providing the first access to a new underground mine; these shafts accounted for 80% of the original access in terms of the number of accesses completed, and 75% in terms of the total verti- cal linear distances. The inside diameters of the conventional circular shafts ranged from 3.7 to 7.0 m (12 to 23 ft). Most (72% ) of these conventional shafts were for production,

Jan 1, 1982

By George D. Graffin.

The first use of graphite is lost in the mists of time. It was used by primitive man to make drawings on the walls of caves and by the Egyptians to decorate pottery. As early as 1400 A.D. graphite crucibles were being made in the Haffnerzell district of Bavaria. Through the Middle Ages graphite was confused with other minerals, especially galena and molybdenite. Two common names that are still used for the mineral are "Plumbago," meaning leadlike, and "Black Lead." The latter name implied that graphite is either composed of lead or at least contains a large percentage of it. Gessner is credited with having recognized it as a separate mineral in 1565, but its composition was not determined until 1779, when Scheele demonstrated that graphite oxidized to carbon dioxide, thus proving its carbon constitution. In 1789, Werner named it "graphite" from the Greek word "graphein," meaning to write. The United States has long relied on foreign countries for its graphite supplies. This reliance has been due more to the lack of suitable domestic graphites than to any particular preference for buying minerals overseas. Ceylon (now Sri Lanka) graphites were imported as early as 1820, and Madagascar graphites have been imported since the properties on that island were opened up about a hundred years later. Mexico has long supplied the United States with most of its requirements for amorphous graphite. Physical Properties and Classification Graphite is found in laminated, flaky aggregates disseminated in schistose rocks. It also occurs in veins and exhibits a foliated or fibrous structure. Graphite is a black lustrous mineral that crystallizes in the hexagonal system, with rhombohedral symmetry. The crystals have tabular form and are six-sided; the faces are commonly striated. The flakes have perfect basal cleavage and are opaque. When well crystallized, the flakes have a black metallic luster while the amorphous material is black and earthy, with a microcrystalline compactness. The flakes feel greasy. Graphite is an excellent conductor of heat and electricity. It melts at approximately 3550°C at a triple point under 1250 psi. It sublimes between 3300-3500°C at 14.7 psi. At 3726°C a second triple point occurs at approximately 100,000 atmospheres. Thermal oxidation in the presence of oxygen begins at 300°C and the rate increases with temperature. The three forms of carbon (charcoal, graphite, and diamond) are distinguished by chemical and physical tests. The specific gravity of charcoal is 1.3 to 1.9, of graphite 2.266 g/ cm3 (crystal density), and of diamond 3.5. Graphite has a hardness of 1 to 2 (Mohs&apos; scale). Natural graphite can be divided into three classes: disseminated flake, crystalline vein (fibrous or columnar), and amorphous. Flake graphite is a lamellar form found in metamorphic rocks, such as marble, gneiss, and schist. Each flake is separate, having crystallized as such in the rock. Crystalline vein graphite is found in the form of well defined veins or as pocket accumulations along the intrusive contacts of pegmatites with limestones. The graphite of such deposits is of two types, foliated and columnar. The important Sri Lanka (Ceylon) deposits are vein type. Amorphous graphite is commonly found as minute microcrystalline particles more or less uniformly distributed in feebly metamorphic rocks, such as slates and shales, or in beds consisting practically entirely of graphite. The latter usually are metamorphosed coal seams and carry as much as 80-85% graphitic carbon, while the former, being altered carbonaceous sediments, commonly range from 25 to 60%

Jan 1, 1983

By D. R. Uhlmann, T. P. Seward, O. Chalmers

A magnetic field has been used to damp out liquid convection during the solidification of castings. Ingots of Al-2 pct Cu were poured from various sperheats (10" to 65°C) into a room-temperature graphite mold located between the poles of an electromagnet. The effect on ingot structure of varying the strength and time of application of the magnetic field was investigated, and the results are interpreted in light 01- current theories of ingot structure. In the solidification of alloy systems, thermal gradients in the melt and differences in density of the constituents are expected to produce convective motion in the liquid. The thermal convection caused by temperature gradients should be present during the freezing of both alloys and pure materials, while the solute convection caused by density differences should be of concern only for alloys. The possible influence of this natural convection on the structure of castings has been discussed by Ruddle,&apos; Chalmers, and Tiller. More recently, an experimental investigation of such effects was carried out by Cole and Bolling. These workers took stationary molds containing lead- and tin-based alloys and. using a brine solution. quenched them from various superheats above their respective liquidus temperatures. When grids were placed across the mold diameter to suppress convection, the grid region was later observed to contain a larger percentage of columnar grains than other parts of the casting or than similar castings poured without the grids present. From thermocouple measurements, they found the temperature in the grid region to be higher than that in the region outside the grids throughout the freezing process, and concluded that convection should be an important mode of heat transfer in normal castings. In addition to such convection arising from thermal gradients or differences in density of the constituents, a further source of convective motion, which we shall call "momentum convection", may be particularly important in small (laboratory-size) castings. By this term we refer to the convective motion produced in the initial pouring process, a motion which is damped out as the linear momentum and angular momentum of the liquid are dissipated. Besides these sources of convection, which are present to some extent in all castings. external influences may also be effective in producing convective motion. Examples of such "forced" convection which have been discussed in the literature include stirring the melt, shaking the mold, rotating the mold, and so forth The purpose of the present study was to examine the effect of convection on the structure of castings poured into a cold mold. In this work, a magnetic field was employed to damp out the convective motions within the liquid, and hence control the extent of con- The effect of a magnetic field on convective currents in a conducting liquid is to induce eddy currents which oppose and damp out the convective motion. vection. The technique of magnetic damping was previously used by Utech and F1emings" in their study of convective effects on impurity banding and other substructure in alloy crystals grown unidirectionally from the melt. In their investigation, fields as small as 200 gauss were found to be effective in damping the convection currents which influence the banding. I) EXPERIMENTAL TECHNIQUE In the present study, alloys of A1-2 wt pct Cu were poured into a room-temperature graphite mold. The mold, in the shape of a circular cylinder, 2 in. ID, 2-3/4 in. OD, 5 in. inside height, and 5-1/2 in. outside

Jan 1, 1967

By H. M. Davis, T. S. Jones

A methodfor accelerating the reduction of a metal oxide by carbon monoxide is to incorporate in the reduction system a nonreducible oxide which has a strong affinity for carbon dioxide and will remove it from the product gases. The effectiveness of this method was investigated by veduction experiments on specially prepared powder mixtures of SrO-ZnO ("active&apos;.) and SrCO3-ZnO (reference). Measurements at 750o and 677°C showed that the rate of reduction of ZnO by CO was as much as an order of magnitude greater in the presence of SrO. Under the experimental conditions at least as much CO2 as generated by veduction was absorbed when SrO was present. Enlzancernent of the veduction rate by SvO resulted from modification of&apos; gaseous djfitsion processes. THE specific question posed in this investigation was whether the reduction reaction CO + ZnO - Zn(g) + COa [1] could be accelerated by incorporating strontium oxide into the oxide charge undergoing reduction. Provided the strontium oxide was active enough, it could remove carbon dioxide from the product gases of ( 11 and form strontium carbonate, thus modifying Reaction [ 1] to CO + ZnO + SrO = Zn(g) + SrCO3 [ 2] This study of the comparative rates of Reactions [ I] and [2] can be considered as a particular case of a general scheme for increasing the rates of reduction of metal oxides by carbon monoxide. The limits of applicability of this scheme are indicated in the simple thermodynamic analysis presented in the appendix. This analysis primarily dictated the choice of the system, CO-ZnO-SrO, employed in this investigation. In addition, it was thought that a study of this scheme by use of the CO-ZnO-SrO reaction system would be of special interest in view of indications in the literature1-3 that the gaseous reduction of zinc oxide is prone to rate control by diffusion in the gas phase. The distinction should be pointed out between this and other efforts to increase the rates of reduction reactions through the use of addition agents. Additions of a wide range of chemicals have been tried with de- grees of apparent success varying from slightly negative to highly positive. The reasons for making additions have included the use of salts to produce effects akin to catalysis,4, 5 the alteration of the microstruc-tural details of the reduction process (including solid-state diffusion),6-8 and the conversion of an en-dothermic reaction into one that is exothermic or autogenous.9-12 The means used to attempt alteration of the enthalpy change has commonly been to incorporate lime into the charge, so that heat is generated by reaction with either of the reaction products, carbon dioxide or water. The use of lime in this way makes endeavors such as that of Edstrom and Wiberg similar to the present one. Furthermore, the basic principle behind the present work has previously been set forth.13 However, a detailed investigation of the type of reaction described in this work does not appear to have been conducted. EXPERIMENTAL PROCEDURE From both conceptual and physical standpoints, Reaction [2] is to be considered as the sum of two reactions:

Jan 1, 1968

By Richard P. Hight

Abrasives include the substances, natural or artificial, that are used to grind, polish, abrade, scour, clean, or otherwise remove solid material, usually by rubbing action but also by impact (pressure blasting for example). They do not include abrasive tools, for instance, lathe tools and files--or polishing agents such as waxes, which act by filling pores. Detergents and cleaners whose action is chemical rather than physical are omitted al- though some chemical-action polishes and cleaners may also contain solid abrasives, for example, many automobile and metal polishes. General Considerations The most important physical properties of materials that qualify them for use as abrasives are hardness, toughness (or brittleness), grain shape and size, character of fracture or cleavage, purity or uniformity. For making bonded abrasive products such as grinding wheels, additional important factors are stability under high heat and bonding characteristics of grain surfaces. The economic factors of cost and availability are always important. No one single property is paramount for any use. For some uses extreme hardness and toughness are needed, as in diamonds for drill bits; for others, the factors of greatest importance are hardness and ability to break down slowly under use, to develop fresh cut- ting edges when grains become worn-for example: in garnet for sandpaper neither highly cleavable or friable grains nor extremely tough grains are wanted. For still other uses, great hardness is objectionable; for example, abrasives for dentifrices and for glass-cleaning soaps. For the most efficient use in the more critical applications, the different types of abrasives are rarely completely interchangeable; thus, while crushed quartz and garnet are both used in sandpaper, the papers are not at all interchangeable in their use applications. In the last analysis, the choice of a high grade abrasive depends upon the quality and quantity of work done by the abrasive per unit of cost. Initial cost of an artificial abrasive may be much greater than that of a natural abrasive but the artificial abrasive may do so much better work than the natural one, and do it so much faster that the ultimate cost will be less. It is for this reason that artificial abrasives have largely replaced natural abrasives. Abrasive Value Mineralogical hardness or "scratch" hardness as expressed in Mohs&apos; scale is an important property in evaluating abrasive materials, but, as noted before, it is only one of several essential properties. The mineral hardness of pure crystal almandite garnet is about 7.5, but if the crystal is crossed by incipient fracture planes, or if it contains inclusions of other minerals, the apparent or useful hardness may be much lower. While the quartz grains in a sandstone have a hardness of 7, the bond holding the grains together may be so weak that the stone is valueless as a commercial abrasive. In artificially bonded wheels and stones, the hardness, strength, and character of the bond are fully as important as the hardness of the abrasive grains. Thus, in an overall consideration of abrasive hardness of loose abrasive grains, both "scratch" hardness and toughness must be considered. In naturally or artificially bonded abrasive stones, bond characteristics are a third factor, which is most important. The problem of abrasive hardness is further complicated by the inadequacies of methods of testing hardness and of expressing relative values. The Mohs&apos; scale is inadequate both because the methods of testing are very crude and

Jan 1, 1975

By Richard P. Hight

Abrasives include the substances, natural or artificial, that are used to grind, polish, abrade, scour, clean, or otherwise remove solid material, usually by rubbing action but also by impact (pressure blasting for example). They do not include abrasive tools, for instance, lathe tools and files-or polishing agents such as waxes, which act by filling pores. Detergents and cleaners whose action is chemical rather than physical are omitted although some chemical-action polishes and cleaners may also contain solid abrasives, for example, many automobile and metal polishes. General Considerations The most important physical properties of materials that qualify them for use as abrasives are hardness, toughness (or brittleness), grain shape and size, character of fracture or cleavage, purity or uniformity. For making bonded abrasive products such as grinding wheels, additional important factors are stability under high heat and bonding characteristics of grain surfaces. The economic factors of cost and availability are always important. No one single property is paramount for any use. For some uses extreme hardness and toughness are needed, as in diamonds for drill bits; for others, the factors of greatest importance are hardness and ability to break down slowly under use, to develop fresh cutting edges when grains become worn-for example: in garnet for sandpaper neither highly cleavable or friable grains nor extremely tough grains are wanted. For still other uses, great hardness is objectionable; for example, abrasives for dentifrices and for glass-cleaning soaps. For the most efficient use in the more critical applications, the different types of abrasives are rarely completely interchangeable; thus, while crushed quartz and garnet are both used in sandpaper, the papers are not at all interchangeable in their use applications. In the last analysis, the choice of a high grade abrasive depends upon the quality and quantity of work done by the abrasive per unit of cost. Initial cost of an artificial abrasive may be much greater than that of a natural abrasive but the artificial abrasive may do so much better work than the natural one, and do it so much faster that the ultimate cost will be less. It is for this reason that artificial abrasives have largely replaced natural abrasives. Abrasive Value Mineralogical hardness or "scratch" hardness as expressed in Mohs&apos; scale is an important property in evaluating abrasive materials, but, as noted before, it is only one of several essential properties. The mineral hardness of pure crystal almandite garnet is about 7.5, but if the crystal is crossed by incipient fracture planes, or if it contains inclusions of other minerals, the apparent or useful hardness may be much lower. While the quartz grains in a sandstone have a hardness of 7, the bond holding the grains together may be so weak that the stone is valueless as a commercial abrasive. In artificially bonded wheels and stones, the hardness, strength, and character of the bond are fully as important as the hardness of the abrasive grains. Thus, in an overall consideration of abrasive hardness of loose abrasive grains, both "scratch" hardness and toughness must be considered. In naturally or artificially bonded abrasive stones, bond characteristics are a third factor, which is most important. The problem of abrasive hardness is further complicated by the inadequacies of methods of testing hardness and of expressing relative values. The Mohs&apos; scale is inadequate both because the methods of testing are very crude and

Jan 1, 1983

By A. Hultgren, B. Herrlander

The original aim of the present investigation was to study the mechanism of cracking on hot-deforming red-short steels. During the microscopical examination of hot-deformed soft steels attention was directed to various patterns of so-called veining in the ferrite, as related to variations in the deformation procedure and the heat-treatment of the steels. Later, a hot-short steel of higher carbon content was also studied. Historical Storey1 suggested in 1914 that veining developed during the gamma-alpha transformation from the growing together of several alpha nuclei within the same gamma grain. Rawdon and Berglund2 found that in soft steel, forged somewhat below A3, the ferrite showed profuse veining, while usually there was very little veining after forging at very high temperatures. They emphasized the similarity between the pattern of veining formed by deformation about 600°C and that of slip lines formed by deformation at room temperature. They also suggested a relation between the gamma-alpha transformation and veining. They became convinced from etching and from the slip-line pattern in cold-deformed material, that the orientation within any ferrite grain showing veining was uniform. In recrystallized alpha grains veining was absent. Veining did not appear materially to affect the properties of ferrite. Independent of veining, continuous networks, attributed to preexisting delta and gamma grain boundaries were sometimes found, the former only in cast steel. Those networks were usually connected with small inclusions. Ammermann and Kornfeld3 confirmed that recrystallized ferrite grains showed no veining. In soft steel annealed between A1 and A3 there was veining only in the ferrite grains formed during cooling. Electrolytic iron deformed at 880&apos; was free from veining. Bannister and Jones&apos; considered veining in ferrite to be a manifestation of microscopical and sub-microscopica~ inclusions. NorthCOtt,5,6 in studies on veining in steel and other metals and alloys, attributed veining to oxide inclusions. It could generally be removed by annealing in hydrogen, a suggestion earlier made by Rawdon and Berg1und. TrittOn (discussion in ref. 5) emphasized the importance of perfect polishing for bringing out veining by etching, and thought the veins or subboundaries were produced during the gamma-alpha transformation, when it was rapid, as a result of the volume change and contraction during cooling. Slight distortion would not allow projecting parts of a growing crystal to join up with atomic symmetry. Hanemann and co-workers showed that veining in ferrite consisted of ridges

Jan 1, 1948

By L. D. Jaffe, J. H. Hollomon

The effect of tempering temperature and time upon the properties of quenched steel is clearly a subject of great practical importance, as well as of considerable theoretical interest. It would be very desirable to be able to predict the properties of a quenched steel when given any selected tempering cycle, with a minimum of experimental work upon that heat or even type of steel. Two problems are involved: one consists of relating the structure obtained to the physical properties, and will not be discussed here; the other, with which this paper deals, involves the relations of time, temperature and composition with the structure obtained 011 tempering. Indentation hardness is perhaps the most convenient quantitative measure of the tempered structure, or of what might be called the "degree of tempering." Undoubtedly, it is not an exact measure, and in some cases (as when temper-brittleness occurs) pieces of the same quenched and tempered steel may have widely differing properties at the same hardness. However, hardness has the advantage of being simple to determine and is certainly the most widely used indication of the degree of tempering. Moreover, for fully quenched steels that are not temper-brittle and do not contain retained austenite when quenched, it appears that, in general, if the hardness of the steel is the same, the tensile and impact properties will also be identical, whether a high or a low tempering temperature is used. The tempering charts available in the metallurgical literature usually give the hardness as a function of tempering temperature for only one tempering time. However, in practice, tempering times frequently vary, and a method of converting tempering curves for one time to tempering curves for some other time would be very valuable. It is also advantageous, in determining the tempering treatment necessary for a given part, not to have to temper samples at several temperatures for the time used for the commercial tempering operation. A more satisfactory procedure would be to employ times of the order of 10 to 30 min., rather than 5 or 10 hr., and if possible to use only one temperature. Furthermore, it is frequently desirable, for reasons such as temper-brittleness,* to obtain a given hardness with short times at relatively high temperatures, and it would be convenient to be able to compute without tests the time required to produce this hardness. Remarkably few quantitative studies of the hardness of quenched steel tempered over wide ranges of temperature and time

Jan 1, 1945

By L. Nastac, Y. Xuan

"The metal-matrix-nano-composite (MMNCs) in this research work consists of an A356 alloy matrix reinforced with 1.0 wt. % SiC 50 nm diameter nanoparticles that can be dispersed within the molten alloy matrix via ultrasonic stirring technology (UST) and induction melting and stirring processing. The necessary ultrasonic parameters to achieve the essential cavitation for adequate degassing and refining of the A356 alloy as well as the optimum fluid flow characteristics for uniform dispersion of the nanoparticles into the A356 alloy matrix have been investigated in this study by using computational fluid dynamics (CFD) modeling with a magneto-hydro-dynamics (MHD) model and an UST cavitation model.The MHD model accounts for turbulent fluid flow, heat transfer and solidification, electromagnetic field as well as the complex interactions between the solidifying alloy and nanoparticles by using ANSYS Maxwell and ANSYS Fluent Dense Discrete Phase Model (DDPM) and a particle engulfment and pushing (PEP) model.INTRODUCTIONAluminum matrix nanocomposites can offer outstanding properties, including low density, high specific strength, high specific stiffness, excellent wear resistance and controllable expansion coefficient, which make them attractive for numerous applications in aerospace, automobile, and military industries field (Bozic, 2010, De Cicco, 2009, Elshalakany, 2014, Goh, 2006, Jia, 2013 and 2015, Liu, 2014, Reihani, 2006, and Su, 2010).As shown in literatures (Aki, 1999 and Mussert, 2002), it is highly advantageous to use nano-sized ceramic particles to produce metal matrix nano-composites (MMNCs) since similar ductility and higher strength with the metal matrix can be achieved. Currently, there are several fabrication methods of MMNCs, including mechanical alloying with high energy milling (Chen, 1997) , ball milling (Filho, 2003), nano-sintering (Groza, 1999), spray deposition, electrical plating, sol-gel synthesis, laser deposition, etc. The mixing of nano-sized ceramic particles is normally lengthy, expensive, and energy consuming.Ultrasonic Stirring Technology (UST) has been extensively used in purifying, degassing, and refinement of metallic melt (Jian, 2005, Khalifa, 2008, Eskin, 2002, Xu, 2004, and Meek, 2006) mainly because introducing the ultrasonic energy into a liquid will induce nonlinear effects such as cavitation and acoustic streaming. SiC nanoparticles are widely used as reinforcement particles due to their relatively good thermal and chemical stability. Ultrasonic vibration can improve the wettability between the reinforced nanoparticles and the metal matrix (Lan, 2004, Cao, 2008, and Yan, 2011), which will assist to distribute the nanoparticles more uniformly into the metal matrix. Ultrasonic cavitation in liquids causes high speed liquid jets of up to 1000 km/h. Such jets press liquid at high pressure between the particles and separate them from each other (Hielscher, 2005)."

Jan 1, 2016