By J. D. Price, G. V. Woody

MANY producers of by-product coke have spent considerable time and given considerable thought to the use of a substitute for low-volatile coal as an admixture with high-volatile coking coal for charging high-temperature by-product coke ovens. Generally speaking, there are two principal reasons for this, one being occasioned by the lack, in certain localities, of low-volatile coal delivered at a cost sufficiently low to permit its use, and another being the desirability of finding a substitute product with a delivered cost lower than the cost of the low-volatile coal. It was for the first of these reasons that the Colorado Fuel and Iron Corporation was particularly interested in this subject. This paper deals with the experimental work and the results obtained by that company in producing and using low-temperature char. OVERCOMING DEFECTS IN COKE FROM COLORADO COALS Colorado coking coals are all of the high-volatile type and were all laid down during he Cretaceous period, which makes them something like 80 million or so years younger, geologically, than eastern coals. They behave, when coked alone, something like the Pittsburgh-seam coals. They make a very brittle, highly cross-fractured, fingery coke of fair shatter value but quite low in resistance to abrasion. Mixed with a low-volatile coking coal such as Pocahontas or certain Oklahoma coals, they make a coke that is equal to virtually any of the eastern cokes. The inferior quality of Colorado coke has long been recognized, and a considerable amount of time, effort and money has been spent upon investigations of means for improving its physical properties. While it has been found that some improvement in quality of coke can be secured by the adjustment and control of such variables as pulverization, moisture content, oven temperature and bulk density of charge, and through the addition of certain inert materials such as pulverized coke breeze, pitch, high-volatile noncoking or semicoking coal, the benefits so gained have been comparatively small. There are no low or medium-volatile coking coals available within a reasonable freight-cost distance. Therefore a substitute for low-volatile coal was developed through low-temperature carbonization-or, more correctly speaking, through the partial devolatilization-of high-volatile coals. The blending of this lower volatile char with the high-volatile coking coal distinctly improves the quality of coke made from Colorado coal. There is nothing especially new about this idea. In 1908 a Japanese patent was taken out by Kotaro Shimomura, whose claim was: The method of making a nonfingery coke out of bituminous coals, without using natural coals of low-volatile matter; according to which a certain coal is heated at a temperature between about 300°C. and about 600°C. so as to leave about 15 to 25 per cent volatile matter in the coal; this coal is mixed with the

Jan 1, 1944

By M. L. Samuels

In a recent paper the authors1 discussed the reactions to tempering of hypereutectoid steels quenched from 1000' C., as revealed by studies on changes in hardness, electrical resistivity, coercive force and metallo-graphic charaeteristics. The data, which related specifically to tempering temperatures of 550°, 650" and 710" C., for varying periods up to 125 hr., permitted the following important conclusions: 1. The rate of softening of the steels at the temperatures examined differed markedly although the steels were of "similar" general chemical composition. 2. The temperature of maximum softening spread over a range from about 650" C, to the eutectoid inversion. 3. The divergence in behavior was ascribed, at least in part, to a profound difference in tendency to graphitization on annealing at sub-eutectoid temperatures. 4. The mode of spheroidization of the cementite, as revealed by metallographic studies, also varied considerably in the different steels. The purpose of the present investigation is to pursue further the study of the difference in behavior of the steels on tempering over a wider range of temperature. To this end the following features have received particular attention: 1. Comparison of temperatures of maximum softening of the various steels when the quenched samples were tempered for 5 hi. and for 75 hr. followed by furnace cooling and by quenching in water. 2. Deterrnirlation of the effect of quenching temperature, prior to tempering, on the rate of softening. Quenching temperatures of 1000" and 850" C. were used in the investigations. 3. Examination of the microstructures obtained with the various heat-treatments employed.

Jan 1, 1938

By William Fink

SINCE so many different curves have been published for the solid solubility of zinc in aluminum, it seems desirable to definitely establish the correct curve by two or more independent methods. The curve published in part I1 was based entirely upon X-ray measurements because the other methods employed at that time were not satisfactory. The present paper (the seventeenth of this series on high-purity aluminum alloys) describes the determination of the solid solubility of zinc in aluminum by the measurement of electrical resistivity at temperature and by microscopic examination. Since the publication of our part I in 1932, an investigation of the solubility relations in the aluminum-zinc system has been reported by Schmid and Wassermann2, who obtained their solubility results from lattice-parameter measurements on heat-treated and quenched speci-mens. The diagram that they published is shown in Fig. 1. In this investigation they also found by X-ray measurements that the parameter of the gamma phase changed continuously with zinc content and at such a rate that it would be identical with that of the beta phase at 60 atomic per cent zinc. It was concluded therefore that the beta and gamma phases, from the point of view of structural relationship, are one single phase. They also suggested a gap of immiscibility between 270° and 350° C. The complete boundary in this region could not be deter-mined satisfactorily by the method employed and therefore was not shown in their diagram.

Jan 1, 1936

By M. L. Samuels

In a recent paper the authors1 discussed the reactions to tempering of hypereutectoid steels quenched from 1000' C., as revealed by studies on changes in hardness, electrical resistivity, coercive force and metallo-graphic charaeteristics. The data, which related specifically to tempering temperatures of 550°, 650" and 710" C., for varying periods up to 125 hr., permitted the following important conclusions: 1. The rate of softening of the steels at the temperatures examined differed markedly although the steels were of "similar" general chemical composition. 2. The temperature of maximum softening spread over a range from about 650" C, to the eutectoid inversion. 3. The divergence in behavior was ascribed, at least in part, to a profound difference in tendency to graphitization on annealing at sub-eutectoid temperatures. 4. The mode of spheroidization of the cementite, as revealed by metallographic studies, also varied considerably in the different steels. The purpose of the present investigation is to pursue further the study of the difference in behavior of the steels on tempering over a wider range of temperature. To this end the following features have received particular attention: 1. Comparison of temperatures of maximum softening of the various steels when the quenched samples were tempered for 5 hi. and for 75 hr. followed by furnace cooling and by quenching in water. 2. Deterrnirlation of the effect of quenching temperature, prior to tempering, on the rate of softening. Quenching temperatures of 1000" and 850" C. were used in the investigations. 3. Examination of the microstructures obtained with the various heat-treatments employed.

Jan 1, 1938

By A. D. S. Gillies

Diesel engine particulate matter pollution is a matter of concern currently in underground mines worldwide. A number of real-time Diesel Particulate Matter (DPM) monitors have been developed in recent years; two of these by the National Institute of Occupational Health and Safety (NIOSH) in the US. One, the D-PDM, is based on an adaption of the successful NIOSH?s Personal Dust Monitor (PDM) unit which is being taken up very successfully for mine respirable dust monitoring. The D-PDM measures all particulate matter within a sub-micron range as classified nominally at 0.8 micrometers by a purpose developed cyclone. The other, the FLIR Airtec, measures the Elemental Carbon (EC) component of DPM by a laser scattering approach. Both instruments have been evaluated underground in robustness and reliability testing in coal mines by the authors. Real time DPM monitors allow greater understanding of the sources and levels of DPM pollution in underground activities. They allow engineering evaluations to determine how conditions can be improved or mining personnel relocated to lower concentration levels. Studies are discussed that examine DPM concentrations from vehicles under varying ventilation conditions. Some of these concern tests undertaken during high activity longwall face moves. They focus on evaluating DPM during the various phases of the face Chock Shield moves. An initiative in some mines has been to limit the number of vehicles in the mining section or panel by the use of a Tag Board or Traffic Controller at the panel travel road entrance to manage exhaust DPM and gases. Diesel tags or tokens are used to control the number of vehicles entering a section or panel and so limit level of pollution. Summation of DPM levels from points monitored throughout a panel demonstrates increasing DPM levels from influence of additional equipment in series within the ventilation circuit. An alternative approach is to invest in underground continuous real-time monitoring of exhaust gases, DPM and section air quantity and integrate this information to determine whether an additional vehicle can enter without exceeding diesel target limit. This optimizes the access of diesel vehicles and replaces the existing manual tag board system. Real-time DPM monitoring allows the industry to pin-point high exposure zones such as those encountered where various vehicles work in areas of constrained or difficult ventilation. Identification of high DPM zones allows efficient modification of mine ventilation, operator positioning and other work practices to reduce underground miners? exposures.

Jan 1, 2012

By G. L. Simard, D. J. Salley, J. Chupak

DITHIOPHOSPHATES and xanthates are the principal collectors for sulphide minerals, and consequently any knowledge of mineral-collector systems of this type is of value. In the present investigation an attempt was made to obtain information on the interaction of a typical dithiophosphate with galena. In carrying out this study, radioiso-topes, so much discussed in the past few years,', ' were extensively employed. By using radioactive dithiophosphate synthesized from radioactive phosphorus, a rapid and sensitive analytical procedure G. L. SIMARD is in the Research Division, Stamford Research Labs., American Cyanamid Co., Stamford, Conn.; J. CHUPAK, formerly in the Research Division, Stamford Research Labs., is now at Camp Detrick, Frederick, Md.; and D. J. SALLEY is in the Research Division, Stamford Research Labs. AlME New York Meeting, Feb. 1950. TP 2815 B. Discussion (2 copies) may be sent to Transactions AlME before April 30, 1950. Manuscript received Oct. 17, 1949. was at hand. This permitted determination of such important quantities as the rate of uptake of dithiophosphate by the mineral, the amount existing at equilibrium on the mineral surface and in the solution, and the desorption of the agent from the surface. Such measurements were possible even on single crystals of galena. In addition the exchange of dithiophosphate between the solution and the sorbed phase was examined, a matter which could be accomplished only by the use of isotopes. It is desired to point out at this time that throughout this paper the term "sorption" has been employed to designate the uptake of agent by mineral, without implication as to the nature of the process by which the uptake was accomplished. Experimental Materials: Galena: The galena was from the Tri-State district. For studies on ground mineral four preparations were used during the course of the investigation. These were prepared from selected large crystals by wet grinding in order to reduce surface oxidation. Alcohol was chosen as a convenient medium for this purpose. The ground mineral was then fractionated by sedimentation in alcohol, dried by evacuation, and stored in a nitrogen-filled desiccator. Data on the preparations are tabulated in table I. The size analysis indicated that the areas of the preparations were of comparable magnitude, even though the absolute values may be somewhat incorrect. Dithiophosphates: Nonradioactive dithiophbsphate (di-isopropyl or di-secondary butyl) was obtained by purification of a commercial product. An aqueous acid solution of the agent was extracted with petroleum ether, the ether layer dried, and the dithiophosphate precipitated as ammonium salt with anhydrous ammonia. Several repetitions of this process resulted in a nearly colorless, flaky product of good purity. (General formula (RO,)PSSNH,). Radioactive dithiophosphate was synthesized by heating radioactive elementary red phosphorus* • For early experiments (1943 to 1944), the elementary red phosphorus was obtained from the cyclotron group at the Crocker Radiation Laboratory of the University of California. Berkeley, through the courtesy of Dr. Joseph W. Hamilton. For more recent work (1946 to 1949). the elementary radioactive Phosphorus has been supplied by the Oak Ridge National Labarotories on allocation from the U. S. Atomic Energy Commission. with sulphur at 270" to 300°C to produce radioactive P,S,. The latter was then treated with the desired purified alcohol (isopropyl or secondary butyl) at 60" to 80°C to form the dithiophosphoric acid derivative. Purification was effected in the same manner as for the nonradioactive material. The effectiveness of the purification method was established by the isotopic dilution method." The same technique was used to show that only negligible decomposition of neutral or of carbonate solutions of the dithiophosphate took place over a period of a day; this was true whether or not galena was suspended in the solutions. Procedures: Radioactivity: The activity of a solution was obtained by counting with a small glass-jacketed, silvered Geiger counter, using a conventional scaling circuit.' Crystals and other solids were counted under a bell-shaped, mica-window counter tube. Sufficient counts were made so that the probable error of counting was of the order of +I-3 pct. The specific activity in terms of counts per minute

Jan 1, 1951

By Arnulf Muan, Hobart M. Kraner

Ferromanganese alloys react with aluminu-silica brick in blast furnace hearths and cause the formation of new phases with low refractoriness and consequent failure of the refractory lining. The nature of these reactions is explained on the basis of petrographic observations, thermodynamic data, and Phase equilibrium considerations. Animproued hearth design resulted from these findings. The production of ferromanganese in blast furnaces presents many problems which are not encountered in the production of iron in the same furnaces. One of the most serious of these problems is the rapid failure of refractories caused by their reaction with the ferromanganese metal. The present paper describes such a "hearth attack", its symptoms, causes, and cure. Following an introductory discussion of operating practice in ferromanganese blast furnaces, results are presented of a petrographic examination of samples from a furnace which had to be shut down because of refractory failure. The causes of this failure are then analyzed on the basis of petrographic observations combined with thermodynamic and phase equilibrium data available in the literature. The latter type of data were subsequently used as a guide in recommending improvements in hearth designs which have since proven themselves successful in practical operations. I) FERROMANGANESE BLAST FURNACE PRACTICE It is considered good practice to blow in a furnace on iron and operate it in this way for a period of time preliminary to producing ferrornanganese. During this time, iron generally penetrates the bottom refractories six or more feet below the original working surface of the hearth. Not only does this metal pervade the joints to these depths, but the pores of the refractories are usually also filled by molten iron. The high throughput of the iron furnace provides ample heat to maintain a high temperature in the hearth refractories. This, together with a high ferrostatic pressure, causes porous clay brick of the hearth to shrink. During subsequent use of such a furnace in ferromanganese production, the iron in the pores of hearth brick if; replaced to some extent by ferromanganese. The replacement is usually not complete. This is probably due to the lower metal throughput and lower prevailing temperatures resulting from this in the brick of the hearth bottom. When the ferrornanganese furnace is banked—or when the temperature in the furnace falls due to a furnace delay—-manganese oxidizes even though the atmosphere is largely CO. Considerable expansion accompanies this oxidation of manganese from metal to oxide. The hearth refractories are then subjected to the disintegrating forces of the volume expansion. These forces may in extreme cases be large enough to lift the furnace off its mantle supports as was described in a previous paper.' When cooling takes place slowly, however, and the temperature remains at a fairly high level, the refractories undergo fluxing action by the MnO. This latter reaction and the reduction of SiO2 of the clay brick is the general subject of the present paper. The observations to be described herein were made on a ferromanganese furnace located at the Johnstown plant of Bethlehem Steel Co. The furnace was lined entirely with clay refractories and had operated on iron for 266 days and on ferromanganese for 96 days prior to being taken off because of a hearth wall failure. II) PETROGRAPHIC EXAMINATION AND CHEMICAL ANALYSIS The photograph reproduced in Fig. 1 shws a cross section of the upper part of an 18 by 9 by 4-1/2 in. bottom block removed from the blast furnace. This brick came from a depth of approximately 6 ft below the original working face of the bottom. It will be noted that the 4-1/2 in. dimension is almost the same as when the brick entered the furnace. Three characteristically different zones marked I, II, and III on the print of Fig. 1 are apparent. Results of chemical analyses of the original brick and samples from each of these zones are listed in Table I. Petrographically the various zones were characterized as follows: The central zone marked I was essentially un-reacted brick. The microstructure consisted of fine needles of mullite, and the pores in this entire area were filled with iron. This is characteristic of

Jan 1, 1962

By F. A. Forward, V. N. Mackiw

The paper relates to the laboratory and pilot plant studies that have been carried out by Sherritt Gordon Mines Ltd., Metallurgical Research Div., in developing the ammonia pressure leach process for extracting copper, nickel, cobalt, and sulphur from high grade nickel concentrate produced from Lynn Lake ores, and describes in some detail the chemistry of the process. IT is well known'.' 2 that copper, nickel, cobalt, zinc, ferrous iron, and a number of other metals combine with ammonia in aqueous solution to form complex ions of the form [Me(NH,)x]"+. The stability and solubility of these ions depend on the concentration of the metal ion in solution, on the amount of NH, present, and on the amount and type of anions present, e.g., OH-, C0;-, NO,, C1-, SO;-. If ammonia is partially or completely removed from such solutions, for example by boiling, the soluble ammines tend to decompose and the metals precipitate as basic salts. These properties of metal ammines have found practical application in the commercial recovery of copper, nickel, and cobalt from a variety of ores. In an operation formerly conducted at Kennecott"" the mill tailing containing 0.80 pct Cu as copper carbonate was leached by percolation with an ammonia-ammonium carbonate solution to dissolve the copper as the ammine. At Calumet and Hecla0-" With a mill tailing containing about 0.4 pct Cu as metallic copper, it has been found necessary to aerate the ammonia-ammonium carbonate leach solutions between stages to oxidize the solubilized copper. At Nicarol"-" where nickel and cobalt occur as oxides and silicates which are not soluble in ammonia, the ore is heated to decompose silicates and to selectively reduce the nickel and cobalt to metal, leaving the iron as Fe,O,, and is then leached with ammonia-ammonium carbonate solution accompanied by aeration to dissolve nickel and cobalt as ammines. In each of these leaching operations, the anion present is CO, and the metals can be precipitated from the leach solution as oxide (copper) or hydroxide and carbonate (nickel and cobalt) by boil- ing off NH, and C02 both of which are recycled to treat a subsequent ore charge. The products-—oxide, hydroxide, or carbonate—can be treated by conventional smelting, calcining, or electrolytic methods to convert them to refined metals. Thus the procedures mentioned utilize the properties of the ammines to extract copper, nickel, and cobalt from nonsulphide ores and separate them from the leach solutions. These processes have the advantage that they can be carried out in closed vessels at atmospheric pressure, that the leaching solutions are specific for the desired metals, that the metals can be recovered as relatively pure compounds by the boiling operation, and that the NH, and CO, can be recycled. Also, as the leach solutions after boiling and filtration are substantially free of metals, NH,, and CO,, they can be discarded, thus facilitating the control of the water balance in the leaching circuit. When, as is the case with Sherritt Gordon concentrates, sulphides are treated with ammonia solution in the presence of oxygen, the leach solution contains SO,--, and an entirely different set of conditions is encountered. The ammine sulphates (of nickel, for example) are more soluble than the carbonates and can be only partially decomposed by boiling. The SO, and NH, in the solutions can not be recovered by boiling. Thus, despite the more favorable leaching conditions resulting from high solubility of the ammine sulphates, the recovery of metals, NH,, and SO, from the solutions must be effected by other means. Sherritt Gordon Nickel Concentrate Treatment The Ni-Cu-Co flotation concentrate produced at Lynn Lake'" contains 12 to 16 pct Ni, 1 to 2 pct Cu, 0.2 to 0.5 pct Co, 33 to 40 pct Fe, 28 to 34 pct S, 8 to 20 pct insoluble, and less than 0.02 oz per ton precious metals. The nickel is present chiefly as pentlandite, the copper as chalcopyrite, and the iron as pyrrhotite and pyrite. Most of the cobalt is thought to be present in pentlandite, although it is known that a small amount occurs as Co-Ni-pyrite.

Jan 1, 1956

By A. A. Brant

In this presentation, concepts of the formation and evolution of the universe, the earth, and the cyclic civilizations of man are broadly outlined. The 5 billion or more years of the universe and the 4% billion years of the earth are contrasted to the 5000 years of modern society and the 100 years of objective scientific breakthrough. THE UNIVERSE Let us start back as far as possible, to the beginnings of this universe, some 5 billion or more years ago. This is a time interval that can be crudely underestimated by the moon-earth tidal friction effects that have increased the length of the day by about 1/1000 second per century — from a 5 to 7 hour day to its present 24 — and have moved the moon away at 5 inches per year to its present 240,000 miles. The oldest stony meteorites from interplanetary space give an age dating of some 4.6 billion years, approximating the time of formation of our earth. Further, certain stars pulsate, the period of pulsation being related to their absolute brightness. Measuring apparent brightness and comparing, gives the distance away. Thus Hubble and Shapley of Harvard, from 1925 on, were able to show that the universe reached as far as our telescopes could scan. The Doppler shift of the hydrogen red lines could only mean that the nebulae, or galaxies, were moving away away at velocities increasing with their distances, by 180 km/sec velocity increase for every million light year's distance. In short, the universe is expanding like an exploded bomb. Comparing the velocity increase per million light year's distance again indicates a zero time of some 5 billion years' Thus it appears that this universe had a finite beginning. Physical measurements and present theories permit some picture of our universe's birth. We know since Einstein that many forms of energy are equivalent, e.g., mass, and electromagnetic radiation, aspects of which are heat and light. Now with expansion, radiation density or equivalent mass decreases as a length factor to the 4th power, while mass as matter decreases at a length factor cubed. The temperature in outer space is now perhaps 100° absolute and the radiation mass equivalent is but 1/1000 the rarefied interstellar gas densities. Decompressing the universe to a starting point, however, raises temperature more rapidly than mass density, and results in a high radiation mass energy fraction, which since it is proportional to temperature to the 4th power suggests a zero point temperature of several billion degrees, brighter than any sun. "Let there be light and there was light," according to Genesis 1-3. Now what further initial conditions must there be to explain the relative abundance of the elements in the universe, which by spectral analyses of the earth's crust, stony meteorites, and the sun and stars is surprisingly uniform throughout. Some 55% of all cosmic matter is hydrogen, some 44% is helium and only 1% is made up of all the heavier elements in much the same proportions as on earth. These latter decrease logarithmically in abundance up to atomic weight 100, then level out. This consistent abundance distribution of elements in the universe may be generally explained by taking at Time Zero a hot neutron gas of density about 10-3 grams per cc, at a temperature of several billion degrees Centigrade, with a high radiation energy fraction. Generally neutrons break down into positrons and electrons within about ten minutes, but at the initial high temperature and radiation pressure would recom-bine. However, with rapid expansion and decrease of temperature and pressure, the neutron disintegration would run uncompensated and aggregation would result from neutrons and protons uniting in different degrees of complexity. The total calculated element aggregation time would be about one hour while the temperature still remained above one billion degrees. The element abundances formed would depend on density of the nuclear gas, simplicity of the atom formed, and the neutron capture cross section. Thus a higher density

Jan 1, 1964

By M. R. Tek

A new method for correlating the data on multiphase flow through vertical pipe is presented. The correlation is based on a "two-phase f factor" concept which was developed and successfully applied to horizontal multiphase flow by Bertuzzi, Tek and Poettmann. Field data previously published on several flowing and gas-lift wells have been used as the basis for the developed correlation. The application of the method to actual two-phase flow problems indicate that this method is capable of predicting the pressure distribution in vertical multiphase flow strings well within the accuracy range usually desired for common engineering and design calculations. A new working chart developed for calculation of two-phase pressure gradients and a graphical step-by-step procedure for the computation of pressure distribution are presented along with an example problem. INTRODUCTION Multiphase flow through vertical pipe is encountered in many engineering installations. In petroleum, chemical process, nuclear engineering and many other industries, problems associated with simultaneous flow of two or more phases through vertical pipe have been of interest for a long time. This interest has increased considerably during recent years due to applications to new processes in petroleum production and refining and to problems of steam generation and heat removal from nuclear reactors. One prominent example of vertical two-phase flow is provided by the gas-lift process where oil, water and gas flow simultaneously. If the pressure profile in a gas-lift well can be predicted within reasonable accuracy, it would be possible to get good estimates of the power required to lift the oil, the optimum depth, the pressure and the rate at which to inject gas. Furthermore, the effect of production rate and tubing sizes on these quantities can be evaluated before any design decision is made on the installation and operation of the flow string. The majority of experimental work available in the literature deals with two-component systems where individual phase flow rates in and out of the pipe remain constant. The general problem of prediction of pressure drops in multiphase flow systems is very complicated. The co-existence of numerous flow patterns of widely different geometry and mechanism, conditions of surface instability and the nature of force fields acting upon the system are among the major difficulties commonly encountered. The classical approach of fluid dynamics which would be based upon the formulation and solution of Navier-Stokes equations has been found by many investigators completely devoid of any hope of success-—not only because of inherent nonlinearities but also because of insurmountable analytical difficulties standirng in the way of setting up the boundary conditions. The presence and effect of interfacial forces on mu1tiphase flow systems further complicate the theoretical approach. For these reasons, many investigators choose to adopt semi-empirical if not purely empirical approaches in order to obtain solutions of engineering utility. A prominent practical solution has been given by Poettmann and Carpenter' in the form of an empirical correlation. In their paper, total flowing densities of fluids and solubility effects of gas in oil have been taken into account for the correlation of field data covering a wide range of operating conditions for oil wells. They treated the gas. oil and water as a single phase of combined propcrties and correlated the multiphase friction factor as a function of the product (pvd), i.e., density X velocity X diameter of the flow string. However, because the product (pvd) is dimensional while the frictior factor is dimensionless, the generality of their result's is somewhat restricted. It seems that the omission 01 viscosity effect may be one of the reasons for the scatter of data as shown in their correlation chart. The concepts of the "two-phase f factor" and the "two-phase Reynolds' number function" were recently developed and successfully applied to correlate horizontal multphase flow by Bertuzzi, Tek and Poettmann.' Recently, two new methods of correlation by Tek and Chan' have been presented on simultaneous flow of liquid and gas through vertical pipe. These two methods of correlation and the working equations in field units necessary for their application are included in this paper. The extension of the conccpt of two-phasc Reynolds' number function successfully developed for horizontal flow into vertical multiphase flow systems, development and evaluation of working charts permitting calculation of two-phase pressure gradients and

By R. J. Stoehr, F. Howell

Since the ore mined in the Grants-Ambrosia Lake uranium area is taken from a water-saturated sandstone formation, part of the milling operation includes a drying process. The authors discuss the merits and disadvantages of two methods: natural drying and mechanical gas-fired drying; operating and cost data are included. In the Grants-Ambrosia Lake uranium area, approximately 7000 tons of ore are mined each day from a water-saturated sandstone formation. This ore is sampled and treated at four separate milling operations. Prior to the design and initial construction of the milling facilities, very little was known as to the physical properties of the ore which would be handled in the sampling and crushing facilities at the mills. All four mills initially were constructed without ore-drying facilities. As mining proceeded, it was determined that, even after drying the ore in place by use of drainage development underground, the moisture content of the ore as hoisted averaged approximately 18 pct. Actually, some of the mines produced ores which resembled cream-of-wheat in character and had a moisture content in excess of 24 pct. Each of the four mills had a differently designed sampling and crushing plant; therefore, the moisture content of the ores had varying adverse effects upon the operation of the plants. It was determined after some experience that most of the sampling and crushing facilities could not economically handle ore if the moisture content was greater than 10 pct—one operator considers 12 pct moisture as a maximum. In all of the plants, moisture content over 8 pct increases costs to some extent. In addition to the added sampling and crushing costs, some of the mills were located 15 to 20 miles from the mines and the high moisture content of the ores increased the haulage costs from the mine to the mill. It was generally conceded that it was necessary to employ some method to reduce the moisture content of the ore prior to sampling. Several methods were considered: 1) natural drying at the mine site, 2) mechanical gas-fired drying at the mill site, 3) mechanical gas-fired drying at the mine site, 4) radiant heating on concrete clabs, and 5) infrared shed drying. After preliminary investigation all possibilities but natural drying and mechanical gas-fired drying at the mill site were eliminated. NATURAL DRYING A cooperative feasibility study was conducted on the natural drying method. This study indicated the following: 1) During summer months May through September, ore piled 4-ft deep would dry from +20 to +10 pct HzO in 30 days with no mechanical turning. 2) In the first four days after piling a reduction of 5 to 7 pct total moisture content was accomplished by drainage and absorption of the water into the underlying ground on which the ore was piled, providing the ground surface absorption rates approached 10 gal per sq ft per day. After the first four days the decrease of moisture caused by drainage was practically nonexistent. 3) In the summer months drying by evaporation amounted to approximately 0.1 pct decrease in total moisture per day and mechanical turning of the ore could increase this as much as three times. 4) Climatic conditions of the area indicated that: a) Air temperatures averaged 64' May, June, July, August, September; 41" October, November, December, March, April; 31" January, February. b) Average rain fall was 10 in. with 40 pct of this occurring during July and August. c) Only on very rare occasions were there over five consecutive days with below freezing temperatures. d) The annual evaporation rate was approximately 75 in. On the basis of this study, two of the mill operations decided to attempt to meet the moisture specifications by natural drying supplemented by mechanical turning. The other two operations decided upon rotary gas-fired drying at the mill site. The natural drying method has been quite successful in practice. The ore running approximately 18 pct moisture is trucked from the head frame and piled in rows about 6 ft wide, 3 1/2 ft deep, 5 feet apart during the months of May through September. In approximately 30 days this ore will

Jan 1, 1961

By C. Y. Ang, C. Wert

Quench aging of supersaturated solid solutions of nitrogen in columbium takes place in reasonable times in the temperature range 300&apos; to 500°C. Changes in internal friction, hardness, and electrical resistivity are found to accompany this change. THERE is practically no detailed information in the literature concerning interstitial solid solutions in either columbium or tantalum. The fact that both of these metals are used extensively commercially in both pure and alloyed states makes studies of their properties of value. While the plan is to study both these metals and their alloys extensively, so far only a small number of measurements have been made. This paper presents data obtained in the initial investigations of columbium. The principal interstitial impurities of columbium are likely to be hydrogen, carbon, oxygen, and nitrogen. The first of these, hydrogen, is outside the scope of internal friction measurements at present and nothing quantitative is known about the initial hydrogen content of the specimens. However, it is believed that it is completely absent after the preliminary heat treatments are carried out. The carbon content of the original samples is low and can be reduced still further during sample preparation. Oxygen is normally present to some extent in columbium and can also be added or removed easily. Nitrogen is also normally present in small amounts and can also be controlled within limits. Since it is not possible yet to remove all the nitrogen from columbium and since it is possible to remove essentially all the oxygen and carbon, initial measurements were made on the alloy system nitrogen in columbium. In this sense then, the alloys are true binary alloys. Little is known about the effects of nitrogen on the physical and metallurgical properties of columbium, so it was necessary to perform some rather elementary measurements on the specimens. These measurements are described briefly in the next section and are discussed in detail in later sections. Scope of the Work That internal friction is associated with diffusion of nitrogen in columbium has been known for some time. It is similar in nature to that for carbon and nitrogen in a-iron. In these latter cases, the information obtained from internal friction has been useful metallurgically.&apos; and it is not too much to expect useful information from similar studies on columbium containing nitrogen. The technique of internal friction measurements is adequately described by Ke2 At a frequency of 1 cps the internal friction peak for nitrogen in columbium occurs at 300°C and that for oxygen at 160°C." So that all the measurements will be meaningful metallurgically, the internal friction has been calibrated by making a measurement of the damping at the two peaks and a measurement of oxygen and nitrogen content by chemical analysis. A comparison of the two gives the following calibration factor: To go from damping capacity expressed in terms of 1/Q to weight percent of oxygen and nitrogen in solid solution in columbium, multiply the peak values of internal friction by about 4 and 3 respectively." Data from which these factors were calculated are presented in Table I. The increase of electrical resistance of columbium caused by the addition of oxygen and nitrogen as interstitial impurities has been quantitatively determined. At room temperature the percentage increase is small for small additions of impurities (<0.1 wt pct); as the temperature is lowered it becomes an increasingly larger factor of the total resistance. An empirical relation has been established to express the resistivity at — 195°C in terms of weight percent of oxygen and nitrogen in solid solution. It is easy to make supersaturated solid solutions of nitrogen in columbium and to observe aging phenomena. The optimum aging temperature, as in the case for carbon and nitrogen in a-iron, occurs at the temperature for which the time necessary for a single place-change in diffusion is about 1 to 10 millisec. This means for nitrogen in columbium that significant property changes should take place for this alloy at about 400" to 500°C in reasonable time intervals. Results of such aging experiments are

Jan 1, 1954

By D. T. Peters, J. C. Bisseliches, J. W. Spretnak

The pain boundary relaxation phenomenon in high-purity copper, 0FHC copper, and a precipitation-hardenable alloy o-fCu-2 uit pct Co has been studied by internal ,friction and elastic aftereffect techniques. The data were analyzed by assuming the broad distribution of relaxation times observed obeys a lognormal distribution law which enables calculation of the relaxation strength. Grain size had no effect on relaxation strength, although the peak width increased with increasing grain size and decreasing temperature. A double grain boundary peak was produced in high-purity copper by annealing to produce secondary recrystallization. The activation energy measured for 99.999 pct Cu is 37.5 * 3 kcal per mol and 46.5 kcal per mole for OFHC copper. A small peak in the Cu-Co alloy at about 220°C at 1 cps was deduced to be the grain boundary peak. Its height increased and its activation energy decreased with increasing aging time. Except for erratic peak positions the observations were consistent with the theory of pain boundary sliding. BEFORE the mechanism of the grain boundary internal friction peak in metals can be satisfactorily explained, the detailed characteristics of the relaxation process must be documented. Of interest are the effect of grain size on relaxation strength, the high-temperature background, and peak width and position. The effect on the grain boundary peak of a precipitate at grain boundaries and of the change in distribution of the particles with aging time must also be explained by any existing or forthcoming theory. The model which has received the most attention was proposed by KG&apos; and zener2 and proposes that the anelastic strain results from sliding of adjacent crystals at grain boundaries. The sliding is limited by the interlocking of grain corners. It follows, according to this model, that the relaxation strength is independent of and the relaxation time is proportional to the grain size. The proportionality between grain size, D, and relaxation time, t, has been confirmed by K&&apos; and Bisseliches . In this case, the internal-friction peaks of various specimens can be superimposed by plotting Q-&apos; as a function of the parameter vD exp H/RT where v is the frequency and H the activation energy. However, the data of Starr et 01.&apos; and Leak6 fit better to a parameter containing D to an exponent near two. A meaningful relationship is not always deducible from the shift of peak temperature with grain size. KG7 demonstrated that a twofold variation in grain size obtained by varying the amount of cold work followed by identical recrystallization anneals will cause a peak shift that is too large to be accounted for even by an exponent of two. Since the decreased grain boundary area existing with a larger grain size is exactly compensated for by an increased sliding distance, the relaxation strength should not decrease with increasing grain size. The height of the internal-friction peak has generally been observed to be rather insensitive to grain size as long as the average grain diameter does not approach the specimen diameter. Exceptions have been reported by Koster, Bangert, and Lang8 for copper, and by Leak6 for iron. The observations for copper could well have been confused by the presence df 0.3 pct0. The possibility that the peaks may simply be increasing in width with increasing grain size and that the relaxation strength, which is proportional to the area under the peak, may remain constant was not examined. his point has been checked in this investigation using high-purity copper. Atomic mechanisms to account for damping by sliding at grain boundaries have been proposed by KG7 and Mott. KG predicts the activation energy to be identical to that for self-diffusion. Mott&apos;s "island" model suggests the activation energy is nL where n is the number of atoms in an island and L is the latent heat of fusion per atom. Other authors have felt that a value equal to the activa-

Jan 1, 1964

By P. R. Gage, R. W. Bartlett

At high temperatues and reduced oxygen pressuves, molybdenum silicicles oxidize to form SiO(g) vathev than a passivating SiO2 film. This is a sevious problem for low-pressure applications of sili-cide-coated rejvactory tnetals. As oxiclalion pvoceeds, the higher oxidntion potential of silicon initially suppresses oxidation of molybdenum and silicon is depleted near the surface. Eventually, silicon depletion causes secondary passivation (SiO2) mid an active to passiue transition in oxidntion behavior at moderately low pressures. At very low pressures, silicon depletion continues until steady-state oxidation of both silicon and rnolyhdenum can proceed at rates propovtional to their initial stoicliiorrzetvies. Ohsel-vations of &apos;oxidatiou-rate belzcriliov at temperatures from 1101° to 1700°C and oxygen pressures from 10-7 to 1 at in were made using thermogravimetn&apos;c, X-ray diffraction, and elect?*on-rtric?ro/,vobe techniqrres. The experimental results are in good agreement with calculated lirnits for the various types of behavior that were based on tlievtnochernicnl atzd dffusion rate data for the Mo-Si system. A protective oxide film normally forms during the oxidation of elemental silicon. However, at elevated temperatures and reduced pressures this film is not present and oxidation is rapid. wagnerl has shown that this behavior occurs because SiO(g) is more stable than SiO2. The behavior of the silicides at high temperatures is similar but more complicated. Molybdenum and several silicide compounds are involved and the chemical activity of silicon, or the equivalent silicon vapor pressure, can vary considerably in these phases. Also, diffusion in the silicides resulting from reactions in which a higher silicide is reduced to a lower silicide, or molybdenum containing dissolved silicon, must be considered. EXPERIMENTAL AND ANALYTICAL METHODS Isothermal oxidation experiments were conducted using hot-pressed MoSi2 and Mo5Si3 wafers. Each experiment was conducted at a fixed oxygen pressure by controlling the flow of oxygen in and out of the furnace chamber. Most of the experiments were conducted in a molybdenum-wound tube furnace. Special construction features, including use of a high-purity dense A12O3 refractory tube, permitted operation in high vacuum to 1500°C. Higher temperatures could be obtained at higher working pressures and with a sacrifice of tube lifetime. Temperature was measured with three Pt 6 pct Rh/Pt 30 pct Rh thermocouples and controlled with a proportional controller. Weight changes were monitored with a quartz spring balance. The few experiments, at higher temperatures and low pressures, were conducted in a cold wall vacuum chamber using induction heating with direct susceptance of the sample. Because of the variable levitation effect of the induction coil on the sample, weight changes could not be monitored continuously in these experiments. All samples representing both experimental methods were weighed before and after oxidiation and examined with a microscope and analyzed by X-ray diffraction. The analytical treatment assumes equilibrium at interfaces and uses existing thermodynamic data. For convenience, equilibria are expressed as chemical potentials or as vapor pressures of the gases involved. The resulting differences in equilibrium vapor pressure between adjacent interfaces and between the surface and external atmosphere drive diffusion processes in the solid and gas boundary film, respectively. These diffusion processes govern the rate of oxidation. A bibliography of the sources of thermochemical data for the reactions pertinent to the Mo-Si-O system is given in Table I. Reactions are listed with the sources of free-energy data referenced. Since all of these reactions involve one or more gas species, usually oxygen, a plot of the product-gas chemical potential, -RT In Pg, vs absolute temperature for each reaction is given in Fig. 1. These curves can be used to determine equilibrium vapor pressures or to compare the stability of different compounds in the various gases: O2, Si, SiO, and Moo3,. The data of Table I and Fig. 1 were used to determine the analytical results presented in this paper. EXPERIMENTAL RESULTS The weight changes for three MoSi, samples oxidized at 1500°C are plotted against time in Fig. 2. The treatments were identical except for the indicated variance of oxygen pressure and each curve represents one of three characteristic types of behavior that were observed. The upper curve is an example of passive oxidation, which is defined as

Jan 1, 1965

By David Cornell, D. L. Katz

Procedures for computing turbulent flow of gas in steady state near the well bore and a graphical method for predicting unsteady state laminar flow at distances from the well have been combined to compute pressure gradients in gas reservoirs. Methods are discussed for predicting single and multiple transients at constant flow rate in an infinite reservoir, predicting constant How rate. in a finite reservoir, reproducing and interpreting back pressure test data, and prediction of the behavior of a closed-in gas well. An example of the graphical method is given for a single transient and the results are compared to a published analytical solution. A typical calculation of the pressure gradient in a reservoir and the production of gas is made .starting with data from a hack pressure test. INTRODUCTION The calculation of pressure gradients throughouse a ga-reservoir at any point in its production history is a complex problem involving turbulent flow near the well bore and unsteady state flow of the gas from the reservoir. The problem is complicated further by the variety of boundary conditions that may be imposed upon the flow. Such boundary conditions include finite or infinite reservoirs. constant or variable rates of production, constant or varying bottom hole pressures, complex initial pressure distributions throughout the reservoir, and pressure maintenance through cycling. In addition to these problems there are the practical difficulties associated with natural gas reservoir analysis These might include: (1) variation. in the permeability and porosity throughout the formation. (2) variations in the thickness of the formation, (3) communication of the producing formation with other producing zones. (4) radial variations in permeability due to influx of drilling fluid. acidizing. or the buildup of liquid in the formation around the well, (5) partial penetration of the producing zone. (6) water flood, and many others. These problems will be considered eventually. In the mean- time, it is necessary to present methods of handling the case of radial flow through a homogeneous, regular, producing stratum to a single well uncomplicated by other factors. The idealized case of steady state, radial flow from a natural gas reservoir was studied by Elenbaas and Katz5 and by Mac-Koberts.&apos; An analysis of the unsteady flow of gases through porous media has been made by Aronofsky and Jenkins&apos; for the one dimensional laminar case with the boundary conditions of constant downstream pressure and uniform initial pressure. Solutions for the partial differential equation for unsteady state radial flow of liquids through porous media have been given by Van Everdingen and Hurst" for the constant bottom hole pressure and constant production rate cases for laminar flow in a reservoir initially at a constant pressure. The analogous heat transfer equation has been treated by Perry and Berggren9 for the case of quenching a cylindrical hole in an infinite medium to a constant temperature. The back pressure curve, which involves the variation of the bottom hole pressure as it is determined by the behavior of the reservoir as a whole. has been studied by Rawlins and Schellhardt,10 Binck-lev,&apos; Baumel and Breitung,&apos; and others. No complete. adequate treatment has been given for the unsteady state, radial flow of gases into a cylindrical hole from a porous medium with or without the presence of turbulent flow and for any set of boundary conditions. If one relies only on analytical solutions of the basic equations, a new solution must be obtained for each new boundary condition. Furthermore, the complexity of the mathematical expressions for boundary conditions other than the very simple cases limits the use of analytical solutions. Graphical methods exist, however. that are general in nature, accurate, and readily employed. The analysis of steady and unsteady, laminar and turbulent, radial flow for various boundary conditions with application to specific natural gas well problems by means of graphical procedures forms the content of this paper. STEADY STATE RADIAL FLOW EQUATION FOR LAMINAR AND TURBULENT FLOW A steady state radial flow equation for laminar and turbulent flow through unconsolidated sands has been given by Muskat as discussion of the work by Elenbaas and Katz.5 This equation is based on the properties of unconsolidated

Jan 1, 1953

By J. T. Norton, Pekka Rautala

The phases and equilibria in the W-Co-C system have been studied by X-ray diffraction methods, metallographic technique, and thermal analysis. In addition to the 7 phase, two double carbides, called 8 and have been revealed. The compositions correspond to CO3 W6C2 and Co3-W10C4. The reactions leading to these phases have been explained and tentative diagrams of stable and metastable equilibria proposed. The basic reactions in sintering cobalt cemented tungsten carbides are discussed. THE W-Co-C system is of fundamental importance in practical carbide manufacturing as well as for the understanding of the sintering mechanism. Surprisingly little is known about this system, for the probable reason that all the important alloys are of two-phase structure and that the diagram Co-WC has been treated as a quasi-binary. This obviously is incorrect, because WC decomposes before melting. One ternary phase, 7, of composition Co3W3C has long been known. It was first studied by Adelskold, Sundelin, and Westgren,1 although the isomorphous iron-tungsten carbide was known earlier. There have been in the literature several reports of two 7 phases.&apos; " Also the 7 phase has been considered unstable by Takeda4 and Westgren.1 The Co-WC diagram has been studied by Wyman and Kelley5 and a quasi-binary diagram has been published by Sandford and Trent.2 Takeda has published a tentative Co-W-C diagram, considering both metastable and stable equilibria. However, the lines of two-fold saturation are shown only partially and it seems impossible to complete the diagram without violating the phase theory. Therefore it seemed desirable to examine the system in more detail. Experimental Procedure The alloys used in the present investigation were made of powders of tungsten, tungsten monocarbide, cobalt, and carbon and were of the grade used in manufacture of commercial cemented carbides. The powders were ground and mixed in small stainless steel ball mills, using balls of the same material. Benzene was used as a dispersing agent. The mixing period was 1 hr, since this was shown to give suffi- ciently good mixing of the powders without too great a contamination from the mill. After ball milling, the specimens were pressed in cylindrical or rectangular dies. No paraffin or other lubricant was used and the small compacts had sufficient green strength to be handled without difficulty. Several sintering furnaces were employed. The most satisfactory arrangement was a vacuum furnace based on the Arsem principle which employed a graphite helix as the resistance heating element. Specimens were placed on graphite stands and there was generally a slight carburization or decarburiza-tion of the specimen surface, depending on the carbon content of the alloy. The evaporation of the cobalt at a sintering temperature of 1400°C was not significant, but became severe at 1500°C and higher. The sintering time was 1 hr at 2000°C and 2 to 4 hr at lower temperatures. It was not possible to quench the specimens, but the cooling rates were rather fast, greater than 300°C in the first minute. In the system under investigation, the reactions are sluggish, and it is believed that the high temperature structures are satisfactorily retained. The principal method of investigating the sintered specimens was X-ray diffraction by the Norelco recording spectrometer. Approximate determinations of the phase boundaries were made by the disappearing phase method. Ternary Phases To study the phase formation in W-Co-C system, a series of specimens was sintered at 1400°C. In this experiment two ternary phases, called here ? and k were formed in addition to the well-known 7 phase. The 7 phase, which has been completely described by Westgren: showed a range of homogeneity from 7 to 20 pct C and from 38 to 48 pct Co. At 1400°C the 7 phase was found to be in equilibrium with monotungsten carbide, 8, tungsten, 8, #?, and liquid. The boundaries toward #? and liquid were difficult to determine and appeared to be very temperature sensitive. The other boundaries are believed to be well fixed. The homogeneity range of 7, as measured in this work, is considerably smaller than the one

Jan 1, 1953

By J. Chupak, D. J. Salley, G. L. Simard

DITHIOPHOSPHATES and xanthates are the principal collectors for sulphide minerals, and consequently any knowledge of mineral-collector systems of this type is of value. In the present investigation an attempt was made to obtain information on the interaction of a typical dithiophosphate with galena. In carrying out this study, radioiso-topes, so much discussed in the past few years,&apos;, &apos; were extensively employed. By using radioactive dithiophosphate synthesized from radioactive phosphorus, a rapid and sensitive analytical procedure G. L. SIMARD is in the Research Division, Stamford Research Labs., American Cyanamid Co., Stamford, Conn.; J. CHUPAK, formerly in the Research Division, Stamford Research Labs., is now at Camp Detrick, Frederick, Md.; and D. J. SALLEY is in the Research Division, Stamford Research Labs. AlME New York Meeting, Feb. 1950. TP 2815 B. Discussion (2 copies) may be sent to Transactions AlME before April 30, 1950. Manuscript received Oct. 17, 1949. was at hand. This permitted determination of such important quantities as the rate of uptake of dithiophosphate by the mineral, the amount existing at equilibrium on the mineral surface and in the solution, and the desorption of the agent from the surface. Such measurements were possible even on single crystals of galena. In addition the exchange of dithiophosphate between the solution and the sorbed phase was examined, a matter which could be accomplished only by the use of isotopes. It is desired to point out at this time that throughout this paper the term "sorption" has been employed to designate the uptake of agent by mineral, without implication as to the nature of the process by which the uptake was accomplished. Experimental Materials: Galena: The galena was from the Tri-State district. For studies on ground mineral four preparations were used during the course of the investigation. These were prepared from selected large crystals by wet grinding in order to reduce surface oxidation. Alcohol was chosen as a convenient medium for this purpose. The ground mineral was then fractionated by sedimentation in alcohol, dried by evacuation, and stored in a nitrogen-filled desiccator. Data on the preparations are tabulated in table I. The size analysis indicated that the areas of the preparations were of comparable magnitude, even though the absolute values may be somewhat incorrect. Dithiophosphates: Nonradioactive dithiophbsphate (di-isopropyl or di-secondary butyl) was obtained by purification of a commercial product. An aqueous acid solution of the agent was extracted with petroleum ether, the ether layer dried, and the dithiophosphate precipitated as ammonium salt with anhydrous ammonia. Several repetitions of this process resulted in a nearly colorless, flaky product of good purity. (General formula (RO,)PSSNH,). Radioactive dithiophosphate was synthesized by heating radioactive elementary red phosphorus* • For early experiments (1943 to 1944), the elementary red phosphorus was obtained from the cyclotron group at the Crocker Radiation Laboratory of the University of California. Berkeley, through the courtesy of Dr. Joseph W. Hamilton. For more recent work (1946 to 1949). the elementary radioactive Phosphorus has been supplied by the Oak Ridge National Labarotories on allocation from the U. S. Atomic Energy Commission. with sulphur at 270" to 300°C to produce radioactive P,S,. The latter was then treated with the desired purified alcohol (isopropyl or secondary butyl) at 60" to 80°C to form the dithiophosphoric acid derivative. Purification was effected in the same manner as for the nonradioactive material. The effectiveness of the purification method was established by the isotopic dilution method." The same technique was used to show that only negligible decomposition of neutral or of carbonate solutions of the dithiophosphate took place over a period of a day; this was true whether or not galena was suspended in the solutions. Procedures: Radioactivity: The activity of a solution was obtained by counting with a small glass-jacketed, silvered Geiger counter, using a conventional scaling circuit.&apos; Crystals and other solids were counted under a bell-shaped, mica-window counter tube. Sufficient counts were made so that the probable error of counting was of the order of +I-3 pct. The specific activity in terms of counts per minute

Jan 1, 1951

By J. H. Swisher

In measuvements of the solubility of nitrogen in fer-rilic Fe-P alloys, tile nitrogen solubility is found to be Less in pIrospliorus-bearing alloys than in pure iron. The reduction in solubility is about 20 pct in a 1.0 wt pct P alloy at 1300°C and about 30 pct in a 0.23 wt pct P alloy at 440°C. Diffusion coefficient measurements at 1150 and 585°C show that phosphorus also decreases the nitrogen diffusivity in iron. In previous work on the Fe-P-N system, phosphorus was found to reduce the nitrogen solubility in liquid iron slightly.&apos; Indirect evidence for similar behavior in a Fe at low temperature was obtained by Dickenscheid and Brauner.&apos; These authors found that phosphorus reduces the height of the internal-friction peak due to dissolved nitrogen. The results of Dickenscheid and Brauner were confirmed by J. C. Swartz of this Laboratory in a single internal-friction experiment using the same specimen stock as in the solubility measurements described below. In the present investigation, the solubility of nitrogen in a fer rite-stabilized Fe-1.0 wt pct P alloy was measured in the temperature range from 800" to 1300°C. Additional experiments were performed in the temperature range from 440° to 585°C, using an Fe-0.23 wt pct P alloy and NH3-H2 gas mixtures. EXPERIMENTAL The experiments were performed in a vertical tube furnace wound with platinum wire. For experimental temperatures of 800°C and above, a mixture of 5 pct Hz in N2 was used as the reacting gas. The gas mixture was prepurified from oxygen by passage over platinized asbestos at 450°C, and subsequently over anhydrone to remove water. Flow rates of the gases were measured with capillary flow meters. The temperature was measured before and after each experiment with a Pt/Pt-10 pct Rh thermocouple. The specimens used for the high-temperature solubility measurements were in the form of rectangular plates, 0.534 by 1.6 by 3.8 cm. The specimens were cleaned in trichloroethylene and annealed for 2 hr in hydrogen at the beginning of each experiment. In measuring the nitrogen solubility, the specimens were held in the reacting gas until equilibrated, then cooled in a water-cooled copper block at the bottom of the furnace. The time needed for equilibration at 1150°C was determined by measuring the average nitrogen content of the 1.0 pct P alloy as a function of reaction time. As will be described, the nitrogen diffusivity in the alloy at 1150°C is only slightly less than its calculated diffusivity in pure iron. At temperatures other than 1150°C, the reaction time used in measuring the nitrogen solubility was about twice the calculated equilibration time for pure iron at the same temperature. With a few exceptions, the procedure for the low-temperature solubility measurements was the same as that described above. The compositions of the NH3-H2 gas mixtures were determined by collecting gas samples from the gas train and analyzing them for NH3 by titration with HC1. The specimen thicknesses were less than those used for the high-temperature experiments, eg., 0.124 and 0.051 cm for measurements at 585° and 440°C, respectively. Nitrogen concentrations were obtained by chemical analysis, using the Kjeldahl method. The Fe-P alloys were made by adding ferrophos-phorus to electrolytic Plastiron (Type 104 A). Commercial ferrophosphorus, containing 3 pct Mn and 0.35 pct Si as the major impurities, was first purified by melting under an FeO slag. In a separate heat, the electrolytic iron was melted and vacuum-carbon-deoxidized prior to making the ferrophosphorus addition. The principal impurities and their concentrations in weight percent in the 1.0 pct P alloy are as follows: Mn, 0.01; Si, <0.01; C, 0.01; 0, 0.003; and N, 0.0012. The impurity levels in the 0.23 pct P alloy are con-

Jan 1, 1968

By Rex B. McLellan, M. L. Rudee, T. Ishibachi

A modelfor dilute quasi-regular interstitial solid solutions is proposed in which the solute atoms can occupy both the octahedral and tetrahedral interstices in the bee solvent lattice. The distribution function, according to which the solute atoms are apportioned between the two kinds of sites, is calculated. The partial thermodynamic functions of the solution are calculated from the distribution function. It is shown that such a solution model can explain the deviation from linearity of the Arrhenius plot of the temperature variation of the diffusivity of carbon through a iron. The published difiusivity data is analyzed to obtain numerical values for the distribution function. Finally it is shown from the numerical values of the distribution function that the possibility of dual-site occupancy will have a negligible effect on the solution thermodynamics for this system. DeSPITE the large amount of experimental data available on the thermodynamics and diffusion kinetics of dilute solid solutions of carbon in a iron, many of the elementary properties of these solutions are not understood due to real or apparent discrepancies in the experimental data. Basically there is a lack of agreement between the solubility and diffusion data obtained by anelastic damping techniques and by bulk chemical thermodynamic methods. SPecifically the heat of solution of cementite in ferrite estimated from thermodynamic measurement1, 2 is about twice as high as that determined from anelastic damping measurements.3 Furthermore the diffusion coefficient D of carbon in a iron in the range -40" to about 150°C (covering about ten orders of magnitude) determined from anelastic damping techniques is such that an Arrhenius plot of In D vs 1/T is linear. However in the range of about 300o to 850°C where mass flow measurements of D have been made (covering about four orders of magnitude), although the data merges with the low-temperature data, the Arrhenius plot departs from linearity. The object of this paper is to present a more refined model of dilute ferrite solutions in which the solute atoms can occupy two kinds of interstitial sites. The experimental data is analyzed in the light of this model and it is believed that thereby some of the anomalies can be resolved. snoek4 explained the room-temperature internal-friction peak (usually referred to as the Snoek peak) in iron as the stress-induced ordering of interstitial carbon and nitrogen atoms occupying the octahedral (0, 0, 1/2) interstices in the bee lattice. From the consideration of a hard-sphere lattice model the (0, 1/4, 1/4) tetrahedral interstices are larger than the octahedrons but their symmetry would not produce the strain dipole necessary to give rise to the Snoek peak. Thus the presence of the Snoek peak is direct evidence that the octahedrons are occupied. Since the publication of Snoek&apos;s explanation, most workers have assumed that all of the carbon and nitrogen in the a solid solution was located in the octahedral sites. This assumption of universal octahedral occupancy has been implicit in the theory of wert5 for interstitial

Jan 1, 1965

By M. S. Burton, J. E. Ritter

The sessile-drop technique was employed to study the effect of atmosphere and alloy additions of titanium and chromium on the surface tension and contact angle of nickel on sapphire substrates at 1500oC. Shear tests were conducted on the solidified sessile drops. The liquid-gas surface tension of pure nickel on sapphire was found to be 1747 ergs per sq cm, with a contact angle of 109.6 deg. The surface tension and contact angle were not affected significantly by the four atmospheres, vacuum, impure argon, pure argon, and pure hydrogen. Small additions of titanium and chromium decreased the contact angle and for the same alloy content, contact angles were lower in pure argon than in pure hydrogen. On the basis of shear-test results , the most probable cause for adhesion in the Ni-Al2O system is the formation of NiO:Al2O3 spinel at the interface; in the titanium alloy-Al2O3 system adhesion is thought to be due to a mechanical interlocking effect; in the chromium alloy-Al2O3 system adhesion is believed to be the result of solid-solution formation involving Cr2O3 and Al2O3 at the interface. In the last few years there has been considerable interest in reinforcing metals with ceramic whiskers. It has been postulated that, by reinforcing nickel with sapphire whiskers, high-temperature strengths su- perior to those of the best current nickel alloys can be achieved.&apos; To fabricate a whisker-metal composite having optimum density and strength, understanding of wettability and adherence in the system is of prime importance. Although there has been some previous research in this a a need for further studies has been cited4-8 to understand better the effects of impurities, alloys additions, and atmosphere on the wetting and bonding of metals to metal oxides. The purpose of this research was to investigate the factors involved in the wetting and adherence of nickel/nickel alloys to sapphire (single-crystal a Al2O3). Sessile-drop experiments were conducted in vacuum, impure argon, pure argon, and pure hydrogen, to determine the effect of atmosphere on the contact angle of the metals on sapphire, and the liquid-gas surface tension of pure nickel. The solidified sessile drops were sheared from the sapphire substrate to measure the bond strength between the metal and ceramic. The alloy additions chosen were titanium and chromium since both enhance the wetting of nickel on sapphire.2, 3c Also, titanium is commonly used when brazing metal-to-ceramic seals to improve adherence. Since chromium forms an oxide that is completely soluble in sapphire, it was thought that the oxide could serve as a transition phase to promote bonding between the Ni-Cr alloy and sapphire. I) EXPERIMENTAL APPARATUS AND PROCEDURE The sessile-drop apparatus was a horizontal furnace, with an induction-heated, cylindrical molybdenum susceptor in a water-cooled Pyrex chamber. This apparatus was patterned after that of Williams and Nielsen.7 A flat Pyrex window at each end of the furnace allowed temperature measurements to be made at one

Jan 1, 1968