By P. L. Sibrell

The U.S. Bureau of Mines has tested cyanide leaching for recovery of palladium (Pd) from spent petroleum processing catalysts. Three different catalyst samples were supplied by a spent-catalyst processor. These catalysts consisted of a zeolite base and contained 0.4 to 0.7 pct Pd. During alkaline cyanide leaching, the catalysts exhibited ion-exchange properties due to their zeolite matrices. Hydrogen ions were released from the zeolite in exchange for sodium ions in solution, resulting in a significant decrease in solution pH. This could present a safety hazard because of the potential for release of toxic hydrogen cyanide gas. A pretreatment step where the catalysts were contacted with a 1.0M sodium hydroxide solution was found to prevent the pH shift from occurring. Following the sodium hydroxide pretreatment, two stages of leaching at 160 °C with solution containing 1 pct sodium cyanide and 0.1[M] sodium hydroxide gave at least 75 and up to 95 pct Pd recovery. The Pd was quantitatively recovered from the leach solution by thermal decomposition in an autoclave at 250°C for 1 h. The Pd content of the precipitate was over 50 pct. Thermal decomposition also decreased the total cyanide content of the barren solution to less than 0.2 mg/L. The catalyst leach residues passed the Federal Toxicity Characteristic Leaching Procedure and the California Waste Extraction Test, indicating that landfill disposal of the leach residues would be acceptable.

Jan 1, 2010

By R. E. Heithecker

The Zwolle oil field of Sabine Parish, La., is different from most oil producing areas of the State in that the oil is obtained from marl and chalkrock formations. The thickness of the reservoir rocks averages 500 feet; but production is not continuous throughout this thickness, as the oil apparently is localized in vertical and nearly vertical solution cavities and channelways or in porous zones of limited horizontal extent. The nature of the oil accumulation has caused two outstanding peculiarities of the field: (1) About 60 percent of the tests drilled were dry holes and (2) there were many instances of well interference. Commercial production was discovered in November 1928, after 17 years of prospecting in and around the present limits of the area now developed which has a length of about 22 miles and a maximum width of 4 miles. The field had produced 10,266,896 barrels of oil to January 1, 1934. The oil ranges in gravity from 400 to 420 A.P.I.

Jan 1, 1934

By Francisco Rumiche, Rolando Nuñez

El artículo presenta la metodología y resultados de una evaluación de la composición química, microestructura y propiedades mecánicas de tres aceros de puntas de excavación, comercialmente disponibles en el Perú, una de fabricante extranjero y dos de fabricantes nacionales. La microestructura de los tres aceros estaba constituida por martensita revenida con ciertos precipitados e inclusiones. La composición química de partida y las condiciones de fundición y tratamientos térmicos definen las propiedades finales de las puntas. En los tres casos el acero mantiene propiedades adecuadas y similares, con valores promedio entre 48 y 53 HRC para la dureza superficial, y entre 42 y 52 HRC para la dureza en el núcleo. La resistencia al impacto y al desgaste varía en los tres casos entre 12 y 25 J de energía absorbida en el impacto, y 0.82% a 0.98% de pérdida de peso debido a desgaste abrasivo.

Feb 28, 2018

By Alan D. Hartman

Instabilities in electric steelmaking furnace arcs cause electrical and acoustical noise, reduce operating efficiency, increase refractory erosion, and increase electrode usage. The U.S. Bureau of Mines is investigating methods to stabilize these arcs. To perform experiments to test new hypotheses, Bureau researchers designed and instrumented an advanced, experimental single-phase furnace. This report describes this furnace, which was equipped with high-speed data acquisition capabilities for electrical, temperature, pressure, and flow-rate measurements; automated atmosphere control; ballistic calorimetry; and view ports for high-speed cinematography. Precise environmental control and accurate data acquisition allow the statistical design of experiments and assignment of rigorous confidence limits when potential furnace or procedural modifications are tested.

Jan 1, 2010

By O. C. Blade

This report on the properties of aviation gasolines and aviation jet fuels produced in the United States during 1954 was made under a co-operative agreement between the American Petroleum Institute and the Bureau of Mines of the United States Department of the Interior. Analytical data are presented for 101 samples of aviation gasoline. Data also are given for 30 samples of aviation jet fuel. The analyses were made on samples typical of the manufacturers I 1954 production in their laboratories and the results submitted to the Bureau of Mines for compilation. The products of 19 manufacturers of aviation gasolines and of 15 producers of aviation jet fuels are represented.

Jan 1, 1955

By Zhou Aiping, Lv Guozhi, Niu Liping, Wang Wenbo, Zhang Ting’an, Jiang Xiaoli

The current method used to produce sponge titanium utilizes a process cycle of magnesium metal and chlorine gas via the electrolysis of magnesium chloride. The primary issues are the high capital cost of the electrolysis process and the environmental regulations limiting high chloride concentrations. Thus, the authors have developed a conceptual method involving theelectrolysis of magnesium chloride as well as a reduction process which allows for a cycle of magnesium and chloride. In the new method, MgCl2 which was distilled during the titanium extracting process as raw material was directly pyrolyzed at elevated temperatures yielding high purity magnesium oxide and chlorine. The resulting magnesium oxide can be used in the production of magnesium metal. This work examines and compares the energy consumption and economic benefits of the Kroll method as well as the new proposed method. The results from the study demonstrated that in comparison to the traditional Kroll method, the new method provided considerable economic and environmental benefits.

Jan 1, 2014

By Patricia Negrini Siqueira Poveda, Leonardo G. A. Silva

Thermoplastic materials are sensitive to ultraviolet radiation (UV), which can cause structural changes, causing variation in mechanical properties and appearance. UV range between 250 and 400 nm is considered the most aggressive to polymers, and prolonged exposure to it results in breakage and/or crosslinking chains. Light stabilizer additives, blockers or absorbers are added to the polymers for protection in order to extend the life of the final product. The choice of the adequate light stabilizer additive system depends on factors such as resin final application, thickness, geographic location of exposure, presence of fillers in the composition, contact with chemicals, among others. This study evaluates different additive systems: conventional organic, inorganic nanotechnologyc base and the synergy between them when applied to polyethylene considering carbonyl index and UV/VIS results after aging by QUV chamber.

Mar 1, 2017

By Nicholas J. Grant, Rolf Nordheim, Bill C. Gissen

The system Cb-Re was examined in detail utilizing pure metals, careful melting techniques, and heat treatments. Metallographic and X-my methods were utilized for phase identification. In addition to soli-dus determinations, the composition limits and mode of formation of the intermetallic compounds 0 and X were determined. The binary constitution diagram Cb-Re has been the subject of a number of investigations.'-7 Two intermetallic phases have been described and tentative diagrams have been proposed. It was the aim of this investigation to obtain a complete and more accurate diagram through the use of purer alloys and improved techniques. The diagram worked out by Knapton7 was published after our experiments were concluded. EXPERIMENTAL METHODS The starting materials were Re powder of 99.95 pct purity, supplied by the Chase Brass and Copper Co., and Cb rondelles of 99.6 pct purity, supplied by the Electro Metallurgical Co. Typical analyses are given in Table I. The alloys were prepared from compacted Re powder and Cb rondelles; for critical compositions master alloys were used. The melts varied from 5 to 50 g and were melted nonconsumably in an Heraeus arc furnace, under ti-tanium-gettered laboratory grade argon. It was necessary to invert the buttons and remelt, followed by crushing and further remeltings, the number of which depended on the nature of the fracture of the alloy. The weight of each alloy was carefully checked after each melting operation. It was found that significant weight losses occurred only when loose Re powder was used. These losses amounted to a maximum of 3 wt pct in such instances, but did not occur after the charge was once molten, regardless of the composition. Typical loss of weight after 4 remelts, including crushing, amounted to 0.2 wt pct. Oxygen pickup during successive melting cycles did not appear to be significant, since the weight gain values never exceeded 0.01 wt pct. Control of the composition of the alloys was not too difficult; however, the problem of homogenization was a far greater one. Optimum alloying conditions were finally achieved by a combination of master alloy production and repeated crushing and remelting cycles. The compositions of the alloys utilized to determine the constitution diagram are listed in Table 11. The weight balance method was used ultimately as the sole analytical method, since repeated checks indicated that it was accurate to 0.2 pct, if the weight losses were small. The results were double-checked by a metallographic study of the homogeneity of the samples, since this was presumed to be the more serious factor. Heat treatments at 1200°C or lower were accomplished by sealing the specimens in Vycor tubes, heating in a Globar furnace, followed by air cooling. This was considered to be an adequate quench because of the very low temperatures involved. For temperatures of 1200" to 1900°, alloys were homogenized and heat treated in a tungsten-filament resistance vacuum furnace. From 1900" to 2750" a tantalum-tube resistance furnace was utilized, operating under a vacuum of 105 mm Hg. The temperature measurements up to 1200" were made by means of platinum-platinum 10 pct Rh thermocouples, with an accuracy of 5°C. For temperature measurements greater than 1200°C, optical pyrometers were used. They were calibrated against a standardized instru-

Jan 1, 1962

By Martti Hagfors, Jussi Saavalainen

The underwater explosions has been used as a test method for the determination energy content of explosives. The test method is suitable for all kind of explosives; homogeneous, heterogeneous, wa-ter-resistant, no-water resistant, cap sensitive, booster sensitive, explosives with hard confinement, explosives without confinement etc. It is also the only test method by which shock, gas heave and to-tal energy values of the explosives can be measured separately. This feature makes it possible to use the test method to develop the explosives for different purposes; the military high explosives need more shock energy where as the gas heave energy is very important feature for the blasting and sea mine explosives.

Jan 1, 2010

By G. W. Birge, D. E. Wolfson, J. H. Lynch

This report presents all available 900 ° C BM- AGA carbonization and related data for coals from the principal beds of the southwest Virginia field in a form which permits ready comparison of product yields and properties of coals and cokes . Thirty- one channel samples from Buchanan , Dickenson , Russell , Tazewell , and Wise Counties were carbonized at 900 ° C in an 18 - inch - diameter retort . Blending properties of 10 of the coals were studied , and expansion of most of the coals and blends was measured in the Bureau of Mines sole - heated oven . Ash Most of the samples were chemically suitable for metallurgical use in coking blends , and their coking properties generally were satisfactory . content exceeded 10 percent in only three samples , and none of the coals contained more than 1.5 percent sulfur . Dry , mineral - matter - free fixed - carbon content of the coals ranged from 62.1 to 77.5 percent . Expansion behavior varied widely , ranging from 16.8 percent expansion to 27.6 percent contraction .

Jan 1, 1964

By A. P. Wang

Porous carbon adsorbents derived from inorganic materials templates such as zeolite and mesoporous silicate attracted considerable attention in the last decade and got great progress in re-cent years. However, so far almost all of templates used in the process were artificial porous materials; the porous carbons prepared by this method are very costly, which restricts the synthesis and application of templated porous carbons. In order to reduce the cost of templated porous carbons, natural inorganic porous minerals have been taken into consideration, which maybe possible and promising templates to prepare carbon adsorbents. In this work, we describe template process using tubular halloysite, rich mesoporous zeolite and low bulk density diatomite, as exemplars of the categories of inorganic porous templates which we have studied and discussed the effects of different templating structure on the resultant carbons. Two main carbon precursors, sucrose and furfuryl alcohol, were used respectively. The morphology of minerals and corresponding templated carbons were characterized using electron microscopy. The pore structures of minerals and templated carbons were characterised with nitrogen adsorption. The results showed that the morphology and pore structure of porous carbons are in good pertinence to those of corresponding templates. The morphology and pore structure of templated carbons could reflect those of corresponding templates at nanometer level. The templated carbons with high specific surface areas and rich mesopores can be prepared by using these three kinds of natural porous minerals as templates. The higher the surface area and pore volume of the minerals, the higher those of the corresponding carbons. The template carbons from halloysite possessed higher pore volume and mesoporosities. Based on the large mounts of experiment results, a model for the mechanism of resultant nanopores formation has been proposed. The nanopores of templated carbons are mainly composed of three kinds of pores: templated pores formed by removing mineral, hereditary pores formed by inheriting the pores of templates and nanopores formed during carbonization. These three kinds of pores have a close relationship with corresponding template.

Jan 1, 2014

By Yasumasa Hattori

An extensive study including fluid dynamic calculations, cold model tests, pilot plant tests as well as measurements in a commercial flash furnace was carried out in order to develop a new Sumitomo flash smelting concentrate burner. The pressure measurements in the commercial burner indicated that the premixing of the concentrate and reaction air in a burner was insufficient. Pilot plant tests showed that enhancement of the premixing of the concentrate and reaction air is very effective for improving the burner performance. Using the additional pressure drop of the reaction air as an indicator of the premixing, a new type Sumitomo premixed concentrate burner was developed.

Jan 1, 2003

By B. L. Landrum, P. B. Crawford

The rise of a new laboratory model for studying tran-sient fluid flow problems, is described. The theory of he model is based on the analogy between the equa-ions which describe the flow of compressible fluids in porous media and the conduction of heal m solids. The "thermal model" is used to study the Iransient Pressure distributions during fluid displacement in five Standard well patterns. The studies indicate quantita-ively how die pressures change with lane at any poit in the reservoir. It was found that, in general, the equipressure contours are more radial about the wells early in the program than after steady-state conditions are established. In addition two studies of fractured five-spot patterns are presented to illustrate the opplicability of the model for a wide range of reservoir conditions. INTRODUCTION In reviewing the oil recovery techniques involving fluid displacement it was found that a very considerable quantity, if not all of the fluid within the pattern, mav be displaced (during a time-dependent or transient period rather than the usually applied steady-state conditions. Since the oil is displaced during a transient period, it was believed desirable to study the nature of the transients for several of the commonly used fluid displacement patterns. A literature review indicated fairly complete studies of the streamlines and isopotentials for steady-state: yet few data were available on the transient displacement process. Several simulated steady-state multiwell displacement programs were carefully mapped by Foster and Lodge on an electrical conducting sheet as early as 1875, hut the more recent work of Muskat provides the best source for steady-state phenomena having direct petroleum production applications. In order to study the transient phenomena a new lab-oratory model was developed which is based on the similarity of the equations that describe the flow of fluids and the conduction of heal. The equations describing heat flow were developed early in the nineteenth century. Regorous solutions tor most transient problems are in gcneral complex and usually limited to fairly restricted houndary conditions.2 the thermal model may be used to obtain approximate solutions for many transient problems without some of the restrictions required for analytical solution. The application of the analogy between heat conduc-. tion in solids. electrical flow and fluid flow, in a porous media has long been recognised. Techniques originally developed for the solution of heat conduction prol?lems have in many instances proved useful in ohtaining solutions to fluid flow prohlcms. Ir is not surpri5ing then that a heat conduction or thermal model might bf usefull in sludying transient fluid flow. As an example ol the problems suitable for the study with the thermal model, transient pressure distributions during fluid displacement programs are studied for the five-spot, line-drive, staggered line-diibe. seven-spot 211 two fractured patterns. A model was constructed of an iron plate of geometry similar to the reservoir patterns under study. The principle of mirror images as suggested by Bryan was employed in shaping the model. A temperature differential was obtained by soldering two sections of copper tubing to the plate at points analogous to the well location in the field. Hot and cold water was passed through the tubing. The temperature distribution, analogous to the pressure distribution in the field. was obtained a a function of time from thermocouplcs distributed over the plate.

By W. A. Backofen, G. Y. Chin, W. F. Hosford

The effect of machine stiffness on discontinuous flow and fracture of the 2024 aluminum alloy was studied in tension at 4.2OK. An increase of machine stiffness was found to decrease the amount of elongation and drop in load during discontinuous flow, thereby postponing fracture to larger strains and higher stresses. The possibility of utilizing stiffened tools in deformation processing to suppress shear fracture originating from unstable flow was indicated. The problem of nucleating discontinuous flow and the role of the effective mass of the system in discontinuous flow were also considered. AT low temperatures the plastic flow of metals is often discontinuous, with sudden load drops and elongations.1,3 Basinski1,4 has presented strong evidence that discontinuous flow, at least in aluminum alloys, occurs under nearly adiabatic conditions. During testing the load may drop suddenly and flow become localized when the thermal softening, due to heat generated in plastic straining, is greater than the strain and strain-rate hardening. This instability criterion is more easily satisfied at low temperatures because 1) the volume specific heat is reduced so that relatively large temperature increases are possible in straining, and 2) the flow stress is relatively temperature-dependent. The important role of adiabatic shear in ductile fracture processes has been emphasized,5-1 and consideration has already been given to the influences of thermal and mechanical properties on the tendency of a material to undergo adiabatic shear.17677 By focusing attention on how the mechanical loading system influences low-temperature discontinuous flow, additional insight into adiabatic shear and its effect on fracture may be gained. EXPERIMENTAL PROCEDURE Because of its low thermal conductivity, the 2024 aluminum alloy exhibits a highly consistent discon- tinuous-flow behavior at 4.2°K and was therefore chosen as the material for study. Machined specimens of 0.113 in. diam and 1.125 in. gage length were solution heat-treated at 490°C for 3 hr, quenched into cold water, and immediately immersed in liquid nitrogen until just before testing. Testing was done at 4.2°K by immersion in liquid helium at a crosshead drive rate of 0.03 in. per min. As normally used (hard-machine basis), the spring constant of the testing machine was k = 25,000 lb per in. By inserting beam springs in series with the specimen, this value could be lowered by a factor of about 100. Details can be found elsewhere.? As a result of variable machine stiffness, the actual strain rate ranged from about 3 x 10 5 to 3 x 10-4 per sec from one test to another, as well as within any one test. However, preliminary tests had established that the tensile curves were not altered significantly by this strain-rate variation. Fig. 1 shows a typical load vs plastic-elongation curve for a solution heat-treated 2024 aluminum alloy specimen pulled in the standard hard machine (k = 25,000 lb per in.) at 4.2"K. The elastic extension has been subtracted. Plastic flow proceeded smoothly from yielding at approximately 22,000 psi (load = 220 lb) to a strain of about 4 pct at which point the flow became discontinuous. The magnitude of the load drops as well as the plastic elongation per drop increased with increasing strain until the specimen finally broke abruptly. The load-elongation behavior of a sample tested with a relatively soft machine under otherwise identical conditions is given in Fig. 2. In general, there

Jan 1, 1964

By Reinhard Gertl, Maximilian Weithaler, Harald Kammerer, Juan Pablo Muñoz, Juan-Carlos Rueda

The Guillermo Gaviria Echeverri tunnel and its access roads project in Antioquia, Colombia is a mega infrastructure project that includes a road network with the longest tunnel in Latin America and several short tunnels, the latter being the focus of this study. The design of the project required careful consideration of several special factors, such as the tunnels’ steep slopes of up to 5%, high fire load of 100 MW, bidirectional operation, and short lengths that make it difficult to place ventilation equipment. The combination of all these parameters cause a challenging design problem for the ventilation systems and smoke control of the short tunnels. To address this challenge, a risk assessment study was conducted to support the design of a new and innovative ventilation strategy that deviates from relevant guidelines and standards, like the Austrian RVS [1][5][6] or the German EABT [8] in order to provide a customized solution for this particular project. This strategy resulted a cost-effective solution, that allowed a reduction in the number of required jet fans and at the same time reaches or reduces the risk level compared to traditional ventilation strategies.

Jun 13, 2023

By Larry A. Haas

The Bureau of Mines is investigating the use of complex gas mixtures, such as would be produced by coal gasification, for reducing iron oxide pellets. A semiempirical model was developed to predict a priori the reduction rate of an iron oxide pellet in a laboratory tube furnace with simulated coal gases at a total pressure of 1 atm. The model uses partial pressures of H2, CO, CO2, CH4 (methane), water vapor, and a temperature-dependent term to predict the rate of reaction. The reduction rate (weight loss per unit of time) was determined with a thermo-gravimetric apparatus (TGA) in the temperature range of 800° to 1,100° C. The ranking of the reductants, in order of decreasing reducing potential, is H2, CO, and CH4 at temperatures between 800° and 1,000° C; however, CH4 became a better reductant than CO at 1,100° C. Water vapor did not decrease the reduction rate as much as did CO2, Carbon deposition was observed at temperatures below 1,000° C with gas mixtures with high CO and low H2 concentrations. With low-Btu gas at 900° C, over 90 pct of the iron oxide was reduced to iron in less than 3 h. This com-pares with a reduction time of 1.5 h with medium-Btu gas and 1 h with reformed natural gases.

Jan 1, 1985

By Xun Zhang, Hang Qiu, Andrea R. Gerson4, Shaomin Lei, Yubiao Li, Yu Meng, Zhenyu Pei, Min Lin

Efficient separation of trace muscovite from the surface/interface of quartz grains was accomplished during oxidizing calcination and catalytic pressure leaching of the hydrothermal quartz. Experimental results suggest that 98.97% or more of the muscovite was separated when quartz sand was calcined at 900 °C for 5 h and then leached by hydrochloric acid and ammonium chloride solutions as substitutes for leaching agents containing fluorides. The chemical processing techniques show high selectivity in purifying quartz sand by transforming mineral muscovite into active structures during oxidizing calcination, and then dissolving the active substances during catalytic pressure leaching

By S Hapugoda, A Edenton, L Lu

The blast furnace cohesive zone has a profound impact on hot metal productivity and quality, fuel consumption, operational stability and the lining life of the blast furnace. The high temperature properties of ferrous burden materials determine the configuration and location of the cohesive zone and have therefore attracted particular attention. While numerous standard testing methods are in use to assess the quality of ferrous burden materials for the blast furnace, these simple tests are generally conducted under fixed conditions, which often represent the extreme situations encountered by the burden materials in the blast furnace. Furthermore, none of these simple tests provides information on the high temperature properties of the burden materials, such as their softening and melting properties. CSIRO is equipped with a fully computerised testing facility to characterise the high temperature properties of ferrous burden materials under realistic conditions similar to those encountered in the blast furnace. This paper will first review the CSIRO softening and melting test method and then discuss the softening and melting properties of a variety of blast furnace burden materials, including sinter, pellets and lump ore, and their implications for blast furnace operation.

Nov 8, 2021

By Hsu-Hui Hsing

In several previous studies from this laboratory (1-4) the autophobicity concept of Zisman and co-workers (5, 6) has been extended to gas phase adsorption processes. Low molecular weight alcohols adsorb on silica or alumina to yield novel isotherms in that monolayer adsorption occurs at low relative pressures indicative of strong bonding, but subsequently multilayer adsorption is quite sparse and diminishes with molecular weight of the alcohol. Such isotherms fit no standard classification scheme, however, in the vacinity of monolayer coverage alcohol isotherms give an excellent fit to the Langmuir or B. E. T. , Type I model (7). Monolayer adsorption is relatively irreversible and it is thus possible to prepare these chemisorbed layers and perform subsequent adsorption studies thereon. All indications are that the adsorptive properties on such films is radically different from that on the underlying alumina (4, 8) and in one study finite contact angles for hydrocarbon fluids were observed. One perennial conceptual difficulty is that there is no observed upper bound to the adsorption isotherm which would be necessary for autophobic adsorption to occur. The cause for this has been studied, and it is currently believed that adsorption is complicated by reversible capillary condensation at contact points between powder particles. The evidence for this is that large particle powders give less "apparent" adsorption at high relative pressures and in one very tedious study adsorption on planar sheets, oxidized aluminum displayed similar reduced uptake at high relative pressures when compared with high specific surface area powders (3).

Jan 1, 1974

By Douglas E. Wolfe, Jogender Singh, Robert Miller, Dong-Ming Zhu, Jeff Eldridge

This paper discusses microstructural changes produced by two novel approaches using electron beam physical vapor deposition (EB-PVD) in which periodic strain fields/microporosity was incorporated within the large columnar grains of Zr02- 8wt.%Y2O3 (8YSZ). The traditional columnar microstructure of partially stabilized zirconia has been slightly modified to produce a lower thermal conductive thermal barrier coating (TBC) by periodically interrupting the condensing vapor resulting in microstructural modifications with diffuse or sharp interfaces and morphological changes on the sub-micron scale without changing the composition of the TBC. These microstructural modifications resulted in a 20-30% reduction in the thermal conductivity, 28-56% increase in hemispherical reflectance, improved oxidation cyclic life (over 100%), and better strain tolerance as compared to standard ZrO2-8wt.%Y2O3 deposited on platinum-nickel-aluminide and CoNiCrA1Y bond-coated MAR-M-247 test samples. The TBC with tailored microstructures were examined by various techniques including scanning electron microscopy (SEM), x-ray diffraction (XRD), steady-state laser heat flux technique, and hemispherical reflectance.

Jan 1, 2004