By Robert K. Koch

Laboratory-scale studies on defluorination of natural and synthetic fluorspars by pyrohydrolysis at 1,500° C. were made to determine the feasibility of developing a process for producing hydrogen fluoride from siliceous fluorspars. It was found that the reaction (at 1,500° C.) is not promising for process development, even though a silica-free offgas can be generated. The primary difficulty is the low hydrogen fluoride content of the offgases; an HF content of 6 percent was the best achieved. Previous research by the Bureau of Mines has demonstrated that offgases averaging 27 percent hydrogen fluoride can be produced under carefully controlled conditions at 1,280° C. The lower temperature process is a better method for production of HF. However, charges in which the CaF to Si02 mole ratio varied from 0.4 to 2 could be processed with similar results. Also, combined alumina and ferric oxide contents up to 25 mole-percent did not noticeably alter the rate of defluorination. Therefore, virtually any natural siliceous fluorspar would respond in essentially the same manner when exposed to water vapor at 1,500° C.

Jan 1, 1962

By B. R. MacKay

Introduction During the past six seasons the writer has been engaged in semi-detailed investigations on the coal areas lying along the front of the Rocky mountains between the Brazeau river and the Smoky River Coal Reserve (see Map, Figure 1). The purpose of this paper is to present some observations pertaining to the stratigraphy and structure of the district, touching especially upon the lithological units into which the Lower Cretaceous sediments have been divided, the thicknesses of the formations at different localities, the number, thicknesses and horizons of the principal coal seams, and the structural conditions which exist in the various fields.

Jan 1, 1930

By John S. Stevenson

"Although we have no uranium- producing mines as yet in British Columbia, uranium, associated with gold and cobalt, has been found in two deposits in amounts such that the combined value of the metals not only warrants the further exploration of these deposits, but also encourages the search elsewhere in the Province for other similar deposits.Where uranium-bearing veins have been found in British Columbia, the uranium mineral is the crystalline variety of uranium oxide, uraninite, rather than the massive, non-crystalline variety, pitchblende, such as found in the Great Bear Lake deposit and in other similar deposits along the southwestern margin of the Precambrian shield.The principal occurrences of uranium known so far in British Columbia are associated with bodies of granodiorite and quartz diorite along the eastern side of the Coast Range belt of batholiths. In this part of the Province, interesting amounts of uranium occur on the Gem property in the Bridge River area and on the Victoria property south of Hazelton; and smaller amounts occur on the Red Rose, Rocher Debouze, Delta, and Ohio properties, also south of Hazelton. At the Gem and the Victoria, the uranium mineral, identified as uraninite, occurs in deposits that also contain abundant cobalt-nickel sulpharsenides, and molybdenite.At these properties, the uraninite occurs as clusters of small black crystals of sub-metallic lustre that may be seen upon careful -searching of a highly radioactive specimen with a hand lens. Under the microscope, the uraninite is seen to be in the form of cubes or modifications of cubes that may occur as individual grains widely scattered throughout the gangue or may be gathered into clusters of several grains. The grain size of the uraninite is in general small. Although a few clusters of grains are up to about 10 mesh in diameter, the individual grains, whether in clusters or widely disseminated, are rarely more than 400 mesh in diameter."

Jan 1, 1950

By H. S. Caldwell

Molten zinc, condensed from zinc vapor, was used by the Federal Bureau of Mines to leach aluminum from an aluminum-silicon alloy made by carbothermic reduction of silicious aluminum ores. Zinc requirements were minimized by re-fluxing condensed zinc in a low-pressure, Soxhlet-type distillation unit. The minimum ratio of zinc used to aluminum in the crude alloy was approximately 2:1. When the system pressure was reduced from atmospheric pressure to 100 microns or less, the rate of aluminum extraction increased by a factor of 20. Leaching rates were much higher when the zinc vapor was condensed directly on the crude alloy than when molten zinc was passed over the alloy in the absence of appreciable zinc vapors. Observations indicated higher extraction efficiencies from crude alloys containing greater amounts of iron. Complete extraction was obtained with negligible loss of zinc. Assuming complete removal of zinc, the aluminum products will contain 1 to 6 percent silicon and about 0.5 percent iron plus titanium. The leached crude-alloy residue is a highly friable spongelike material containing about 80 percent silicon, several percent iron and titanium, with the remainder aluminum. This extraction method has been patented (Patent 2,810,637) and assigned to the Government. Research and development investigations are continuing at the College Park Metallurgy Research Center.

Jan 1, 1961

By W. E. Falck, A. Usubiaga, J. Spangenberg, P. Schepelmann, S. Šolar, D. Wittmer, F. Blanchard

The extraction and processing of mineral resources may be accompanied by environmental impacts. In spite of technological advancements, the enormous increase in production volumes within the last decades has induced sizeable environmental impacts along the life-cycle of products. Beside environmental impacts, social issues associated with mining need to be considered to ensure the social acceptability of mining activities. The project EO-MINERS aims at deploying Earth Observation (EO) tools to inform best practices in mining and to thus assist the global mineral resources industries in their transition to sustainable development. In order to facilitate the handling of complex sets of information requirements from a wide variety of stakeholders, a set of indicators was developed that will inform the process of EO tool and services development. The project strives to enable stakeholders outside the industry to meaningfully participate in decision-finding processes on mining-related issues by developing and providing EO products and services that fit the information requirements. The project has identified a wide range of such information requirements by stakeholders that could be potentially provided by EO tools. The applicability of the EO tools on the local level is tested on three mining sites.

Jan 1, 2011

By Suzana Souza da Silva Scardua

O desenvolvimento dos aços microligados representa um grande avanço tecnológico e oferece grandes vantagens econômicas para diversas áreas da engenharia. Nas últimas décadas houve um aumento expressivo na demanda mundial por tubos utilizados na construção de dutos para transporte de petróleo e gás. Neste caso são utilizados os aços ARBL (Alta Resistência e Baixa Liga) que combinam alta resistência e tenacidade necessárias para operar em altas pressões. Os tubos são produzidos a partir de placas laminadas e posteriormente soldadas atendendo a norma API 5L. Em componentes de geometria complexa, tais como juntas, acoplamentos e conexões, a laminação não é a técnica mais adequada. Para este fim, o processo de forjamento é uma alternativa, pois permite uma ampla faixa de dimensões e formas complexas com controle da microestrutura e propriedades mecânicas após tratamentos térmicos adequados. Para avaliar novas técnicas de processamento, foram fabricadas barras forjadas de um aço microligado com composição química similar à de um API 5L X70 comercial. O aço foi lingotado e forjado em barras quadradas de 35 mm de aresta. Em seguida foram retiradas amostras para tratamentos térmicos de têmpera a 920°C e 1.050°C e revenimento de 150°C a 650°C. Após analisar as microestruturas foi escolhida a similar à de um tubo comercial API 5L X70 para preparação de corpos de prova para ensaios de tração. Resultados preliminares mostram a possibilidade de obter aços com qualidade API através do forjamento.

Aug 7, 2018

By Percy Gillie

THE Tralee preparation plant, owned and operated by the Semet-Solvay division of Allied Chemical and Dye Corp., is located on the Virginian railway, near Mullens, Wyoming County, W. Va., and the mine, which is in the Winding Gulf district, produces coal exclusively from Pocahontas No. 3 seam. The property, comprising 4900 acres, is leased from the Pocahontas Land Corp. Prior to 1930 four separate mines were operated in this tract, some having been started about 1916. Plans for the preparation plant were formulated soon after World War 11. Construction began in the spring of 1948, operation early in 1950. The plant was designed to be operated with minimum labor. It was equipped for production of first quality graded sizes of coal for house heating and 3/8x0-in. slack suitable for high-standard metallurgical coke. In the beginning, a thorough investigation was made of the property by means of core drilling, prospect openings, and sections from shallow mines on the property, as well as sections and analyses from mines in the immediate vicinity. After the extent of desirable coal had been established and the average seam section and nature of overlying and underlying strata had been determined, it was decided to install a system of mining which would load the full seam and would clean the product mechanically. Pocahontas No. 3 seam is characterized by draw slate and bone and rock partings. It was not known what the washing difficulties and cleaning plant requirements would be for processing the raw product of full mechanical mining. Arrangements were made, therefore, through the courtesy of the property owner, to obtain a large sample from a section of the mine along the adjoining property line. The

Jan 1, 1954

By Merrill Horine

IT has been stated and accepted for many years that the automotive industry was the instigator, the principal sponsor for and the largest user of alloy steel and nonferrous alloys. The only universally recognized standard specifications and heat-treatments for these materials are those adopted by the Society of Automotive Engineers. It is this same auto-motive industry that has been the chief inspiration for and consumer of modern production machine tools. The production curve of steel ingots is more sensitive to fluctuations in automotive production than any other influence or group of influences. In every other important steel-con-suming industry, automotive materials and automotive processes are the outstanding features of modern progress. In this connection I need only mention the prefabrication of buildings, following the automotive system of straight-line, interchangeable mass production; the motorization of ships and railroads, employing automotive types of prime movers; the production of pressed-steel stoves, plumbing and furniture by methods originated in the automobile-body industry and the extensive use of rubber for the cushioning of all manner of machinery as pioneered by the automotive and tire industries. Dr. Jeffries has brought out this point in his address (p. 21), assuring us that the transportation industry is the largest user of these materials. In the transportation industry, or as we might more accurately express it, the transportation group of industries, the. automotive industry pre-dominates as a user of light alloys. One out of every four tons of aluminum produced is consumed by the automotive industry. Similarly, the automotive industry ranks first in the consumption of the following metallurgical materials: steel, 24.04 per cent; malleable iron, .57; alloy steels, 72.2; nickel, 30; lead, 39 per cent.

Jan 1, 1936

By W. J. Huff, G. W. Jones, I. Spolan, R. E. Kennedy

"INTRODUCTION Information on the exploeibility and ease of ignition of acetylene is important in connection with investigations by the Bureau of Mines and others seeking the causes of explosions in medium-pressure acetylene generators.A previous report 6/ gave preliminary results of an investigation made by this Bureau to determine the causes of these explosions. This report indicated the need of amending Federal specifications for ""1/4 by 1/12"" carbide to reduce the amount of fine sizes permitted under the specifications then in force. Tests described in the above report showed that certain sizes of carbide may, under certain conditions, attain excessively high temperatures when acetylene-water vapor mixtures are passed through carbides for extended periods.Federal specifications P-0-101, Amendment 5, June 28, 1944, are now in effect. These latest specifications permit a maximum of 7 percent of ""1/4 by 1/12"" carbide by weight to pass through a 0.0661-inch sieve and a maximum of 2 percent to pass through a 0.0555-inch sieve. Experience has shown that these specifications have insured a safer size range of carbide for medium-pressure acetylene generators.Although the improvement in the size range of the carbides has aided in the prevention of explosions, there have been explosions in which the carbide used at the time of the explosion met the latest Federal specifications."

Sep 1, 1945

By K. K. Kershner, J. G. Donaldson

This investigation was conducted to obtain data on optimum conditions for chloridizing metal sulfides . Salt- roasting galena at 450° C for 8 hours chloridized 75 percent of the lead ; in an equal time of treatment at 750° C , the process chloridized 42 percent of the zinc in sphalerite . Hydrogen chloride at 500° C completely chloridized galena in 15 minutes , and at 600° C converted all of the zinc in sphalerite to the chloride in 4 hours .

Jan 1, 1963

By Joseph A. DeCarlo

This publication presents a tabulation of oven-and beehive-coke plants in the United States as well as pertinent statistical data on the number, capacity, kind, and condition of the ovens. Coke is an essential raw material in pig-iron production and the coal-chemical materials produced during the coking process are used to manufacture fertilizers, paints, plastics, synthetic rubber, explosives, detergents, nylon, pharmaceuticals; dyes, and many other products necessary to the high standard of living in this country. In table 1 the oven-coke plants in the United States on December 31, 1959, are listed. This shows the name and address of the company, location of the plant, classification or type of ownership, number and type of ovens, annual coke capacity, and the coal-chemical materials produced. The "furnace" plants I are those owned by iron and steel companies and most of them are integrated with blast furnaces to facilitate transportation of raw materials for steel making. Furnace plants represented 87 percent of the total coking capacity and their average annual capacity was 1. 3 million tons. The "merchant" plants are those associated with chemical companies, gas utilities, as well as those that produce metallurgical, industrial, and residential-heating grades of coke and coal-chemical materials for sale on the open market. These coke plants are smaller than furnace plants and in 1959 their average coke capacity was only 520 thousand tons annually. On December 3l, 1959, there were 54 furnace and 20 merchant oven-coke plants in existence in the United States.

Jan 1, 1960

The implementation of NAFTA in January of 1994 was expected to have small but beneficial effects for the Mexican economy, mostly through increased investment flows. Mexico's mining industry was especially likely to benefit, as mineral investment funds would be diverted to the now safer Mexico and away from similarly endowed but more risky Latin American mineral economies. The results of the past two years have shown that it is governments and macroeconomic factors that influence investment flows, rather than the fine-tuning of trade flows through so called "free-trade" agreements.

Jan 1, 1996

By AIME AIME

ASIDE from the annual dinner-dance, the two outstanding social events of the Annual Meeting were the dinner- smoker on Monday night and the informal dance on Tuesday night, both of which were held at the Commodore Hotel. Approximately 400 attended the former event, compared with 570 a year ago, and about 250, people were attracted to the dance.

Jan 1, 1933

By J. R. Maxwell

The development, commercial installation, and operating performance of large capacity Maxwell Flotation Cells. Volumes ranging from 300 cubic feet to 2,000 cubic feet per flotation mechanism.

Jan 1, 1971

By Y. Suzuki, J. Nagao, Y. Ueda, K. Shimokawa

"A Ti- Ni intermetallic compound could be formed rapidly from Ti and Ni powder compact with SHS process. Microgravity experiments using a drop shaft are carried out, This report shows the effect of microgravity or high gravity on formability of an intermetallic compound. It is concluded that the specimen forms a porous and nearly amorphous alloy by rapid cooling under microgravity but with rapid cooling under high gravity after microgravity, the specimen forms a uniform and dense structure with better crystallinity.IntroductionTi - Ni inter1etallic co1pounds have been produced and have beco1e si1ilar to the a1orphous and porous structure as a result of the SHS (Self Propagating High-te1perature Synthesis) process under 1icrogravity. SHS process is being applied to the synthesis of cera1ics and inter1etallic co1pounds (1). The technique is characterized by a large a1ount of heat being emitted within a very short ti1e interval as regards the sistering reaction. One SHS process, acco1panying 1elting by a reaction was observed, and that was due to the quick heating of a Ni-Ti co1pact containing 50 ato1ic percent of Ti under a low pressure (2-4). In this report, we have researched the use a drop shaft which is 1ore effective during a short ti1e under 1icrogravity and high-gravity, so as to obtain high dense speci1ens with the exception of porous specimens (5). Mechanical properties of each specimen were esti1ated from these 1icro-structures with a discussion about the effect of changing gravity regarding 1elting and solidification of the Ti-Ni intermetallic comounds."

Jan 1, 1996

By Gust Bitsianes, Joseph H. M. Beaty

Successful blast-furnace operation depends upon securing an optimum balance between a number of important variables. This balance will vary somewhat from furnace to furnace in the same plant and with raw materials available in different plants. It is difficult to isolate the effect of any one variable unless it has a rather pronounced effect upon the efficiency of operation. The physical properties of iron ore and coke are known to affect the process, yet it is difficult to set up any definite yardstick by which these differences can be appraised. In recent years, whenever practicable, operators have taken steps to obtain better control over the absolute size and uniformity of size of the ore and coke. The size and physical character of the stone, however, have received comparatively little attention, emphasis being placed upon chemical composition, fluxing efficiency, and action as a desulphurizing agent. Since the stone occupies only about 10 per cent of the volume of the stock column, its influence upon permeability is less than that of the ore and the coke. The large pieces now used have a tendency to roll to the center and thus increase the permeability of this part of the stock column. Smaller pieces would be more effective in promoting the permeability of denser portions of the stock. The size and physical properties of blastfurnace stone are important also for reasons best understood by considering the results obtained by the crushing and the sizing of iron ore. Crushing ore to about 2 in. at Provo, Utah, and to about I in. in Alabama produced material somewhat less permeable to gases, even though sized. In spite of some sacrifice in permeability, the efficiency of the process was improved by crushing and sizing the ore, as indicated by a substantial saving in fuel and increased output. This saving in fuel is due in large measure to more thorough reduction of ore in the upper part of the furnace and to a corresponding decrease in the amount of carbon consumed prematurely above the tuyeres by the reaction CO2 + C = 2CO - 70,080 B.t.u. [I] The physical properties of stone, its size and rate of calcination are important because they influence the rate at which CO2 is released and the completeness of calcination before reaching a level in the furnace where the temperature does not exceed 1050°C. (1920°F.). Briefly, carbon dioxide from the limestone or from the reduction of ore may cause premature corn bustion of carbon above the tuyeres. Assuming that 1000 Ib. of limestone is used per ton of pig iron, about 435 Ib. of CO2 will be liberated during calcination of a good grade of stone. If all this CO2 from the stone were to oxidize carbon prematurely, about 120 lb, would be consumed above the tuyeres in a heat-absorbing reaction. The amount of carbon thus consumed when a

Jan 1, 1943

By Joseph H. M. Beaty, Gust Bitsianes

Successful blast-furnace operation depends upon securing an optimum balance between a number of important variables. This balance will vary somewhat from furnace to furnace in the same plant and with raw materials available in different plants. It is difficult to isolate the effect of any one variable unless it has a rather pronounced effect upon the efficiency of operation. The physical properties of iron ore and coke are known to affect the process, yet it is difficult to set up any definite yardstick by which these differences can be appraised. In recent years, whenever practicable, operators have taken steps to obtain better control over the absolute size and uniformity of size of the ore and coke. The size and physical character of the stone, however, have received comparatively little attention, emphasis being placed upon chemical composition, fluxing efficiency, and action as a desulphurizing agent. Since the stone occupies only about 10 per cent of the volume of the stock column, its influence upon permeability is less than that of the ore and the coke. The large pieces now used have a tendency to roll to the center and thus increase the permeability of this part of the stock column. Smaller pieces would be more effective in promoting the permeability of denser portions of the stock. The size and physical properties of blastfurnace stone are important also for reasons best understood by considering the results obtained by the crushing and the sizing of iron ore. Crushing ore to about 2 in. at Provo, Utah, and to about I in. in Alabama produced material somewhat less permeable to gases, even though sized. In spite of some sacrifice in permeability, the efficiency of the process was improved by crushing and sizing the ore, as indicated by a substantial saving in fuel and increased output. This saving in fuel is due in large measure to more thorough reduction of ore in the upper part of the furnace and to a corresponding decrease in the amount of carbon consumed prematurely above the tuyeres by the reaction CO2 + C = 2CO - 70,080 B.t.u. [I] The physical properties of stone, its size and rate of calcination are important because they influence the rate at which CO2 is released and the completeness of calcination before reaching a level in the furnace where the temperature does not exceed 1050°C. (1920°F.). Briefly, carbon dioxide from the limestone or from the reduction of ore may cause premature corn bustion of carbon above the tuyeres. Assuming that 1000 Ib. of limestone is used per ton of pig iron, about 435 Ib. of CO2 will be liberated during calcination of a good grade of stone. If all this CO2 from the stone were to oxidize carbon prematurely, about 120 lb, would be consumed above the tuyeres in a heat-absorbing reaction. The amount of carbon thus consumed when a

Jan 1, 1943

By J. Kortnik

Mining has always been, and still is, an activity which is vital for the development of mankind. This is because a predominant proportion of industrial products and energy is produced from raw materials that are excavated using mining methods. The need for environmental protection and the close proximity of urban settlements and mines in Slovenia have necessitated ever stricter requirements for the excavation of raw materials and the introduction of more environmentally-friendly mining methods. This is achieved by implementing a closed eco-technological cycle of raw material excavation within the scope of mining methods. In surface mines, this means prompt reclamation of the degraded surfaces, and in underground mines the use of methods with minimized impact on the surface and on underground water. In underground mines, mining methods with backfilling installed according to the multi-barrier disposal system are the only ones that allow the possibility of implementing a closed eco-techno-logical cycle of excavating raw materials. Various industrial waste materials are also included in the backfilling material in order to improve its strength properties. Backfilling consisting of several different waste materials is produced in the form of a composite. Before backfilling consisting of waste material composites can even begin to be used in mines, an environmental impact assessment of its suitability for mines needs to be made. In order to make such an assessment, a pressure leaching cell and an open diffusion cell were made, i.e. a pressure leachate test and a sorption test were developed. The two cells and the developed tests will enable the study of the influence of backfilling on the environment if installed in an underground mine. The pressure leachate test performed with the use of the pressure leaching cell simulates leaching from a consolidated backfill during the seeping of underground water into the backfilling material under pressure. The sorption test performed in an open diffusion cell simulates the flow of eluate leached from the backfilling material through the rock/geotechnical barrier. The two tests were developed in such a manner that they are performed either in succession immediately after one another, but they can also be performed separately at a certain time interval. The paper presents an assessment of the suitability of backfilling made of different waste material composites. Keywords: environmental impact assessment, multi-barrier disposal system, waste material composites, pressure leachate test, sorption test, pressure leaching cell, open diffusion cell, eco-technological cycle, mining methods with backfilling.

Jan 1, 2003

By Craig M. Sams

"Variable speed mill popularity has grown during the last 10 years with almost every SAG mill fitted with a variable speed drive. In addition, many of today’s larger ball mills are running a variable speed drive for various reasons. In the past, motor suppliers, especially gearless drive suppliers, have considered mills as being an overpriced rotor. This has lead to mills demanding more torque than what a motor can generate. This paper identifies the reasoning of what has happened and how to mitigate the mismatch in the future. Technical and economical issues are discussed, allowing mill operators to make an informed decision of which path to take in deciding what motor to put on a mill.INTRODUCTIONIt has been generally accepted in the past that motor suppliers and specialists in engineering companies understand the workings of a SAG mill or a ball mill and although there is a fair knowledge within the industry, in regards to mill torque requirements, the advent of variable speed drives in ball mills has shown the writer that a complete understanding of the mill torque requirements are not fully understood.This paper will discuss two aspects of mill torque requirements, (operating torque at various charge levels and start up torque), and how it relates to specifying the proper motor torque requirements.MILL OPERATING TORQUEMill operating torque at a given charge level and density in a mill is essentially constant throughout the entire speed range. For the purpose of this paper, we will take a 38’x 22.5’, 20’ EGL, SAG mill and provide the power draw at variable speeds but fixed loading conditions.The power draw and mill torque of this mill at 8% ball charge and 28% total loading (Highlighted) is shown below as Figure 1, at variable speeds."

Jan 1, 2007

By E. W. Filer, R. P. Smith, L. S. Darken

The solubility of nitrogen gas in purified iron and low alloy steels is determined for the y region (930° to 1350°C). The diffusivtiy of nitrogen is estimated from the rate of approach to equilibrium. The investigation of aluminum-killed steels, held in nitrogen, discloses precipitation of aluminum nitride, the solubility of which is determined. ALTHOUGH several investigations of the solu-bility of nitrogen gas in y iron have been reported, all have made use of the method adopted by Sieverts in his classic work, whereby the solubility is determined by the pressure or volume change of the gas. The agreement between different investigators* is rather poor, particularly as compared to the self-consistency of results of several individual investigators. The present report represents a portion of our investigation of the equilibrium of nitrogen and nitrogenous atmospheres with iron and steels. The method adopted in this temperature region (910" to 1400°C) consists of holding the specimen in gaseous nitrogen, quenching (or cooling), and determining the nitrogen content by direct analysis (solution in acid followed by distillation and titra-tion of the ammonia).** Up to 1050°C a 20 in. vertical wire-wound (Kan-thal) furnace was used; this was wound in three sections so that by proper adjustment of relative currents, and use of a modulator1 and a commercial controller (using a chromel-alumel control couple), a zone almost 6 in. long could be maintained uniform within a few tenths of a degree. Since the temperature coefficient of the nitrogen solubility is low, the full precision was not utilized and a variation of l° to 2" was tolerated; a variation of a similar amount also occurred occasionally between the beginning and end of the experiment. At higher temperature a vertically mounted, tubular Globar furnace and control unit was used; the zone of uniformity (l° to 2"C) was here limited to about 2 in.; fluctuations with time were comparable to those in the wire-wound furnace. Reported temperatures were measured by use of a platinum-platinum-rhodium thermocouple, which was frequently com- pared with a similar standard couple which was calibrated at the gold and palladium points and also compared with one certified by the Bureau of Standards; error from this source is believed to be less than 1 "C. Nitrogen gas from a commercial cylinder was mixed with slightly over 1 pct H by use of a gas mixer described previously.' This mixture was passed over hot copper and through ascarite and phosphorus pentoxide to remove oxygen and water vapor. The purified gas contained 1.05 pct H. This procedure was adopted to prevent the formation on the specimens of oxide film, which is well known to be nearly impervious to nitrogen; its success was attested by

Jan 1, 1952