By Stanley J. Gasior, Albert J. Forney, Joseph H. Field

Most bituminous coal mined near Eastern industrial areas requiring high-Btu pipeline gas is caking and therefore unsuitable for fixed-bed pres- sure gasification by present techniques. If the caking property of such coal can be destroyed, the resulting fuel can be gasified in a fixed bed at pressure with steam and oxygen as a preliminary step in making a high-Btu gas. To find a practical way to convert strongly caking coals of granular or small lump size to noncaking fuel was the object of this study. In previous work, strongly caking coals of 1/8- to 1½ -in. size were converted to a noncaking coal char by treatment in a static bed in about 3 hours1 and coal of 18-100 Tyler mesh in a fluidized bed in about 5 min.2 An inert gas such as steam, nitrogen, carbon dioxide or a mixture of all three with a small amount of oxygen was used in both studies. In our work a strongly caking bituminous coal from the Pittsburgh seam of 4-8 Tyler mesh size was converted to a noncaking form in free-fall in about 2 sec by dropping it through a countercurrent flow of steam containing 4% to 7% oxygen at 1150º-1200°F and 300 psig. This method should also be applicable to smaller-sized material.

Jan 3, 1965

By Gene Asai

Properties obtained for columbium carbide-carbon castings ranging in car-bon content from 12 to 17 weight-percent were compared with those of hot-pressed composites of similar composition. The properties were oxidation resistance in static air between 500° and 700° C, linear thermal expansion between 20° and 2,400° C, electrical resistivity between 20° and 1,500° C; microhardness between 20° and 1,500° C, and modulus of rupture between 1,300° and 1,800° C. CbC-C castings differed markedly from hot-pressed material with respect to microstructure, electrical resistivity, and modulus of rupture, but behaved quite similarly with respect to oxidation resistance, thermal expansion, and hot hardness. In oxidation resistance, thermal expansion, and hot hardness both materials were independent of carbon content. Both castings and hot-pressed composites oxidize rapidly in air above 600° C, have thermal expansion coefficients very similar to columbium metal, and the logarithm of the hardness decreases linearly with increasing temperature. The microstructures of hot-pressed composites contained varying amounts of graphite in a CbC matrix but did not contain significant amounts of a eutectic structure present in all castings, nor did they contain graphite needles which were present in the hypereutectic castings. The higher electrical resistivity of hypereutectic castings over hypereutectic hot pressings was attributed to the presence of highly oriented graphite needles in the castings. The modulus of rupture of castings was 1-1/2 to 2 times that of hot-pressed composites. Both materials displayed bend ductility above 1,800° C.

Jan 1, 1971

By M. L. Cunha

The lack of control of As and Sb compounds from copper smelters and converters has rendered some chalcopyrite containing arsenopyrite, stibnite and tetrahedrite minerals unusable for metal extraction. In the present investigation, we have studied the carbothennic reduction of Portuguese chalcopyrite mineral concentrate in the presence of lime/CaS04 and CaS04/Si02. Thermodynamic equilibrium calculations were performed to study the distribution of As and Sb between metal and the CaO-Si02-FeO slag phase. The phase equilibrium calculations also show the effect of oxygen partial pressure on the increase in the volume of the slag phase, which helps in lowering the copper metal formation temperature and facilitates a better separation between metal, matte and slag. The reduction reaction kinetics was studied between 850°C and 1100 °C, and the phases formed were identified by X-ray powder diffraction and scanning electron microscopy techniques. The importance of this research for using recycled matte, lean and rich minerals with As and Sb is also explained.

Jan 1, 2001

By Sergio N. Monteiro

Polymeric composites reinforced with natural fibers are increasingly been used in several engineering applications, from automotive parts to building construction elements. In addition to the relatively low cost, the natural fibers are also appraised by their renewable and biodegradable characteristics. Fibers extracted from the crust of coconut fruits, also known as coir fibers have been investigated for a possible use in composite materials. In the present work, the coirfiber/polyester matrix interfacial strength was evaluated by means of pullout tests. The variation of the pullout tensile stress vs. the embedded coir fiber length permitted to determine the critical fiber length and, thus, to calculate the interfacial strength. Observations by SEM complemented the results from pullout tests, indicating that coir fibers have a potential for application aspolymeric composites that could replace conventional materials such as wooden and gypsumpanels.

Jan 1, 2006

By F. Z. Utyashev

The present work considers the essence of fragmentation: on the level of a simple model as a material response to the curvature accumulated by it at large deformations. It is on this basis that the correlation between curvature and fragment sizes is determined. It is shown that at deformation the area of curvature center inevitably changes. It is revealed that a specific value of variation of center surface area, i.e. ^As parameter, is numerically equal to the value of curvature acquired by a material. Minimum sizes of fragments and grains depending on ^As have been estimated, and the dependence of this parameter on strain has been established. Besides, the present paper considers the effects exerted by curvature center geometry, material distortion, directions of deformation and thermal warming up in the localization zones on structure refinement when various techniques are applied.

Jan 1, 2006

By Robert W. Schaut

The use of micropiles is increasing for new construction and to retrofit distressed foundations in expansive soils. Typical micropiles in expansive soils have a lower section where the micropile grout is embedded in direct contact with the soil, and an upper section that is cased with rigid PVC pipe or other material to reduce the friction between the micropile and the surrounding expansive soil. In the upper cased section, the micropile grout is in direct contact with the inside of the casing. During construction, grout can flow upward into the annular space between the soil and the outside of the casing as the grout is tremied into the micropile. Thus, various interfaces may exist in a typical micropile, including soil-to-grout, grout-to-PVC, and soil-to-PVC. As the surrounding soil heaves, shear stresses are mobilized along the interfaces. The frictional characteristics of the interfaces are design variables that must be evaluated. For this study, an experimental program was conducted to evaluate the shear strength of the three interfaces listed above. Conventional direct shear testing was performed at a commercial testing laboratory. In addition, specialized testing was performed at Colorado State University (CSU). For the CSU testing, an interface testing protocol was designed using a modified triaxial cell to allow evaluation of the interface characteristics between rigid PVC and cylindrical specimens of grout or clay soil. It is shown that the shear strength of the soil-to-PVC and grout-to-PVC interfaces are similar, both of which are significantly lower than the shear strength of the soil-to-grout interface. This indicates that the use of a PVC casing in the upper portion of a micropile has a positive effect in reducing friction and the shear stresses resulting from expansive soil.

Jan 1, 2011

By J. L. Wyatt

THE smelting of ilmenite to produce a slag rich in titanium, with pig-iron as a byproduct, introduces new concepts in electric smelting metallurgy. Titanium slags are characterized by low electrical resistance, thereby requiring a different type of electric furnace operation, and power supply sources substantially different from those encountered in normal steel melting and siliceous ore smelting furnaces. This paper describes special apparatus for determining specific electrical resistivity of titanium slags, and reports the values obtained on slags encountered in the process of smelting ilmenite ores. In an induction furnace under conditions approximating normal furnacing operation, 25 general heats and 6 special standardization and comparison heats were run. Results indicate relatively low resistivity. Resistivity depends primarily on slag composition, and, to a lesser degree, on temperature. During the summer of 1947 a cooperative project between the National Lead Co. and the Bureau of Mines was conducted at Boulder City, Nevada, in the Electrometallurgical Laboratories of the Bureau. The project involved smelting of ilmenite ores in electric furnaces, and has been reported in detail.' The author participated as a member of the staff of the National Lead Co. during the entire campaign. One outstanding characteristic of the titaniferous slags, their apparently excellent and variable electrical conductivity, was considered sufficiently important to warrant further study. Although little electric smelting of iron ores has been done in the United States, a certain amount of information is available for comparative purposes. Personal experience in smelting siliceous iron ores in electric furnaces furnished further information for comparison. In general, silicate slags are relatively poor conductors of electricity. Current flow during smelting operations may be maintained through a floating layer of coke on top of the slag bath, or through a bath of molten iron, beneath the slag. Silicate slags are not sufficiently conductive to furnish a path for current passage when normal furnace voltages are used. Experimental smelting of a silicate iron ore was undertaken for comparative purposes. A fluid melt was not obtained until the FeO content was reduced to 15 pct. The resistivity increased as the FeO content decreased, FeO compounds being the most conductive of the various oxides in such a normal slag system. The converse appears to be true in slags containing large percentages of TiO2. It has been found that titanium slags become molten with FeO percentages in excess of 30 pct, and that the conductivity becomes generally better as the FeO con-tent of the slag diminishes. This phenomenon was demonstrated in the furnacing operations at Boulder City. During the initial smelting period furnace electrodes could be held immersed several inches in the slag, with tap selectors set for a no-load voltage of 70 v. As the FeO content decreased, the furnace electrodes would "walk up," until at one point in the process the tips would break the surface and arc on top of the slag. This was undesirable since direct arcing caused losses of important flux additions. The slag compositions under study at that time were such that losses due to surface arcing sometimes caused viscous slags to be formed. Forcing the electrodes into the slag bath by manual control to prevent surface arcing resulted in excessive power input and lack of control. Suitable low voltages were not available. Measurement of the electrical resistivity of titanium slags at various operating temperatures and slag compositions was undertaken. It was believed that this information would be of use in the design of electric furnaces suitable for smelting ilmenite, with voltages, electrode sizes, and electrode spacing adapted specifically to titanium slags.

Jan 1, 1951

By Fred D. DeVaney

DURING the past few years a radically new process for the magnetic roasting of iron ores has been investigated and developed by Pickands Mather & Co. and the Erie Mining Co. in the Erie laboratory at Hibbing, Minn. This process, originally devised by Dr. P. H. Royster of Washington, D. C., involves the use of a roasting technique quite different from older methods. It has now been demonstrated that iron-bearing materials can be roasted as effectively as by any previously known method, and at a much lower cost. The increasing shortage of highgrade iron ores in this country has accelerated the search for new methods that would permit low grade materials to be utilized. The concept of magnetically roasting low grade nonmagnetic ores such as the oxidized taconites and then separating such material magnetically has always had considerable appeal. The magnetic concentration idea is attractive because of the sharpness of the separations and cheapness of the method. Heretofore, however, the equipment and the processes available for the magnetizing-roasting -step have left much to be desired. The customary equipment available for reduction roasting has been: 1-multiple hearth furnaces, 2-rotary kilns, and 3-shaft type kilns. In addition, it is understood that some work has been done in magnetically roasting fine ores by a process using the FluoSolids principle, but little information on this process is available. The multiple hearth kiln has been used the most but first costs and operating costs have been high because of low capacity, high maintenance, and poor gas utilization. Magnetic roasting can be done in a rotary kiln, but the radiation losses are high and the conversion to magnetite is usually unsatisfactory because of poor contact between the gases and the solids. Of the shaft-type furnaces, probably the most efficient yet developed is that designed by E. W. Davis of the Minnesota Mines Experiment Station. This furnace was operated at Cooley, Minn., during 1934-1937 but was abandoned in 1937 because the operation was uneconomic. Heretofore the basic concept behind most magnetic roasting processes has been the idea of heating iron ore to a temperature of 800° to 1100 °F in a strong reducing atmosphere, preferably either carbon monoxide or hydrogen. Temperatures under 800°F were undesirable since excessive roasting time was required. Temperatures over 1100°F were avoided because of the danger of converting part of the iron to ferrous oxide which is nonmagnetic. In the new roasting process, the operation is carried on in a shaft furnace using a controlled atmosphere containing a low percentage of reducing gas. The temperature in the roasting zone is considerably higher than with the usual reducing gas and this speeds up the reduction time. Portions of the spent furnace gases are cooled and recirculated and this together with the good contact between ore and gas makes for high reducing gas utilization. High heat economy is secured by recuperating heat from the roasted ore by passing the cold reducing gases countercurrent to flow of ore. The heat transfer principle is similar to that employed in a pebble stove and to that used in the Erie Mining Co. furnace at Aurora, Minn., for pelletizing fine magnetite concentrates derived from taconite. The theory of controlled atmosphere during the roasting operation can best be appreciated by inspecting the equilibrium diagram of the Fe-C-O system shown in Fig. 1. An inspection of this diagram shows that in certain areas magnetite, Fe3O4, is the only stable form of iron. A further inspection of this table shows that if the proper ratio is maintained between carbon dioxide to carbon monoxide, such a gas will be reducing with respect to hematite, Fe2O3, and will be oxidizing with respect to both ferrous oxide, FeO, and iron, Fe. It should be kept in mind that the formation of ferrous oxide in a roasting operation is harmful, since this oxide is nonmagnetic; if it forms in any quantity, it will cause substantial loss of iron in the ensuing magnetic separation step. If a ratio of approximately three parts carbon dioxide to one of carbon monoxide is maintained, the resulting operation can be carried on at a relatively high temperature without fear of over-reduction. Specifically, most of the tests in the Erie furnace have been made at a temperature of 1500° to 1600°F, with an entrant gas containing approximately 5 pct carbon monoxide and 15 pct carbon dioxide, with the remainder largely nitrogen. It should be remembered that the ratios of carbon monoxide to carbon dioxide shown in Fig. 1 hold even though the bulk of the gas is an inert gas such as nitrogen. It may surprise many to learn that a gas containing as low as 3 pct carbon monoxide, and 12 pct carbon dioxide with the remainder nitrogen is an extremely effective reducing gas in the 1000° to 1600°F temperature range. The reducing gas is not limited to carbon monoxide, and mixtures of hydrogen and carbon monoxide may be used effectively, provided that a similar ratio is maintained between the reducing gases and carbon dioxide and water vapor. For a more detailed explanation of the theory involved, the reader is referred to U. S. patents 2,528,552 and 2,528,553. From a safety standpoint, the weak reducing gas used in the furnace offers an advantage. Its composition is such that it is well below the limits of explosion should air enter a hot furnace. This condition is not true with the usual reducing furnace, in which a gas rich in carbon monoxide or hydrogen is used. The general furnace design and method of operation may best be understood by an inspection of

Jan 1, 1952

By A. Akerman, C. P. O’Connor, N. Vayenas

"Stereolithography is a well-known rapid prototyping technique in the manufacturing sector. Essentially, it is a three-dimensional printing process that produces plastic prototype parts from standard CAD files. At present, Canadian mining companies are not fully aware of the potential of rapid prototyping techniques (RPTs) for their production and mine design systems. Mining engineers and geologists attempt to visualize and understand the characteristics and layouts of orebodies on computer models, and in cases where it is decided to develop physical models, the process is time-consuming, based on simplified constructions. RPTs, such as stereolithography, can facilitate engineers and geologists to quickly, and with satisfactory accuracy, visualize sections of orebodies and evaluate alternative ore extraction techniques using 3D solid models.The research discussed in this paper is carried out by the Laurentian University Mining Automation Laboratory (LUMAL) in collaboration with Inco Limited and the Integrated Manufacturing Technologies Institute (IMTI) of the National Research Council of Canada. The main objective with this research is to evaluate the applicability of state-of-the-art RPTs to underground hard rock mining systems. RPTs can play a significant role in accelerating the design and development process of mining systems."

Jan 1, 2006

By Helio Wiebeck, Vijay Rangari, Julyana Santana, Francisco Valenzuela-Díaz, Esperidiana Moura, Marcus Vinicius de S. Seixas

Closed-cell polyethylene (PE) foams have been extensively used in many applications such as packaging, transportation, sports, construction, and agriculture because of their variety of properties including light weight, chemical resistance, thermal and electrical insulation. The objective of this study is to evaluate the influence of electron-beamirradiation on the properties of LDPE/EPDMblend foams. The LDPE/EPDM blend (80/20 wt%) were prepared by melt extrusion, using a twin-screw extruder machine. The foam structure of LDPE/EPDM blends was obtained by melt extrusion process, using a special single screw for foaming with 1.5 wt% of foaming agent as blowing agent. The foam samples were irradiated by electron-beamat radiation dose of 25, 50, 75 and 100 kGy and submitted to heating in an oven at 100 °C. The specimen tests samples of irradiated and non-irradiated foams were submitted to mechanical tests, DSC, TG analysis and density measurement.

Mar 1, 2018

By N. Charue

An international prediction event was carried out within the framework of a 30-pile testing program organized in a sandy soil in Belgium (Limelette). That program called upon sev­eral testing methods: static load tests, Statnamic testing, and dynamic testing. This paper provides a summary of received predictions and results obtained from the static pile load tests, which were carried up to failure of the instrumented piles. The comparison between predictions is made using load-settlement curves with reference to the results of the static load tests. The predictions are based on a geotechnical approach using an extensive soil investigation program and a dynamic approach using the dynamic load test data.

Jan 1, 2002

By G. Smith

This paper describes the allure of diamonds over time and highlights the magic and mystery of famous diamonds. Consideration is given to the effectiveness of marketing in the diamond industry. It is concluded that diamonds are held as cherished possessions, valued far above their real market price, retained as valued heirlooms, and widely used as a form of highly liquid currency. In order to sustain value, both from an investment and jewellery perspective, demand has been stimulated to keep pace with growing global supply while the illusion that ?diamonds are forever? has been fostered to ensure that most diamonds, once sold, do not re-enter the market.

Jan 1, 2003

By J. M. Schaekers

In the first part of the article, the authors give a broad overview of the chemistry and some engineering aspects of bioleach processes, eventually leading to the important and critical issue of the stability of arsenic-containing residues, especially those derived from bioleaching of sulphidic gold ores. In the section ?Factors affecting arsenic stability? they give an excellent summary of the factors normally affecting the stability of such residues. This is followed by some valid comments on the suitability of a single leach test to evaluate the long-term stability of solid waste streams. However, they fail to mention that, up till now, no tests procedure has been accepted by either environmentalists or the mining/processing industry as a valid method to test the long-term stability of solid wastes. Their own method is no exception, although, like many others, it is useful to identify potential problems with solid wastes considered for disposal.

Jan 1, 2001

By J. du Plooy

Mintek has implemented a training scheme that provides students with the experiential training requirement for the National Diplomas in Chemical Engineering and Extraction Metallurgy. This note describes the main features of the scheme and the course content, and our view of future developments in this area.

Jan 1, 1998

By H. G. Denkhaus

Please allow me the temerity to reply to your reply to my contribution as follows: A fracture is brittle if plastic deformation is absent or, conversely a fracture is ductile if plastic deformation is present. Consequently, brittleness is specified by the degree of plastic deformation at fracture. This is the generally accepted definition. If other material properties (e.g. the quorient or the product of the uniaxial compressive and tensile strengths) under certain conditions are influenced by brittleness, or brittleness by them, these should not be called brittleness. If the one or the other author does that, he simply uses imprecise language. Even your remark, that ?Inyang and Pitt (1990) stated that the ratio of the compressive strength (sc/st) is directly proportional to brittleness?, confirms that the two quantities are not considered the same. For example:? The well known definition that a material is linear?elastic if the strain is directly proportional to the stress?does not mean that stress (measured in MPa) and strain (measured in %) are the same thing.

Jan 1, 2003

By D. François-Bongarçon

When it comes to sampling theory, a bad sampler is a bad sampler, no matter what, and a sampler is either bad or good. It also is of critical economic importance to tell and understand the difference, especially in a metallurgical plant. In this paper, the grand principles of Sampling Theory are first recalled, then the most popular types of sample cutters for plants are critically reviewed. It is concluded that the industry has a lot of progresses to make in that direction, although improvements usually pay for themselves very quickly.

Jan 1, 2002

The increasing global demand for rough materials forces almost every mine to look at the mechanisation in their processes. This will not onlyimprove performance but with safety issues becoming more and more prevalent, the need for the introduction of mechanisation technologies to mining applications is essential. Ongoing developments are occurring in almost every field, ranging from basic developments to specialised mining. Mechanical tunnelling and shaft sinking have set the standards regarding safety, profitability and environmental protection. Different machine types and working principles have been developed to suit the geological and hydrological requirements of tunnelling projects worldwide. Continuous activity in research and development leads to constant optimisation of tunnelling performance.

Jan 1, 2008

By S. K. Kawatra

It is common in coal-cleaning operations to produce a fine waste stream which contains a considerable amount of coal, but which is not economical to recover both because it is mixed with large amounts of difficult-to-remove clay slimes, and because the fines are often heavily oxidized. Conventional froth flotation machines cannot produce an acceptable product from such material in a single stage of flotation, and even flotation columns often have difficulty cleaning this type of feed. A new type of flotation column was designed specifically to deal with these problems, and was installed and tested in a coal-cleaning plant in Ohio. The feed coal contained 39.8% ash as fine clay, and 2.83% total sulfur, and was 80% passing 176 micrometers. The coal was a thickener product which had oxidized for some time, and was very difficult to float. However, using the new column it was possible to recover up to 85% of the calorific value in a product containing less than 11% ash, and up to 60% of the calorific value in a product of less that 8% ash. The bulk of the pyritic sulfur was rejected from the coal as well. Multistage flotation tests showed that the flotation column was able, in a single stage, to produce the best froth flotation product that it was possible to recover from this coal.

Jan 1, 1994

By Michael Perch, Charles C. Russell

Nearly 75 per cent of the total coke production in the United States in 1940 was consumed in blast furnaces. In 1939 the percentage was 69.9, and in 1938 it was 61.3. To produce a net ton of pig iron 1757 lb. of coke was required in 1940 and 1760 lb. in 1939. These figures indicate how dependent the production of pig iron is upon the production of coke. The rate of iron production is in some measure influenced by the physical and chemical characteristics of the coke. Blast-furnace operators believe that the physical properties of coke profoundly influence the operation of the furnace. Although it is true that coke of a wide variety of physical properties is used in American blast furnaces, the periodic fluctuation of these properties is one of the causes of irregularity of blast-furnace operation. The purpose of this paper is to present a broad picture of the physical properties of by-product coke that are generally considered to be important by coke-oven and blast-furnace operators. Effects of the kind of coal used, the preparation of the coal, the rate of coking, and other factors will be considered. Of all these variables, the kind of coal used is by far the most important. In this discussion use will be made of the method of coal classification by rank' standardized by the American Society for Testing Materials. Although this method of classification has been an American stand¬ard for several years, it has not been given the attention it deserves, especially in connection with the selection of coal for production of coke. Despite the fact that many producers of blast-furnace coke are limited to some particular source or sources of coal, a good understanding of the principles involved in setting up the standard method of classification may lead to a better appreciation of the causes of changes in coke characteristics. Furthermore, where it is necessary to select new coals as a substitute for the original supply, this method of classification can be of great assistance. The data presented have been gathered from many sources, but no attempt has been made to cover the vast literature. Instead, some of the more important data have been selected to show how coals and their carbonization affect some of the physical properties of coke. It must be emphasized that generalizations concerning the behavior of coking coals are presented and that individual coals may vary widely from the specific behavior depicted. Nevertheless, it is believed that the data illustrate certain typical behaviors. Neither was it possible to cover completely all the factors involved; for example, the macroscopic constituents of coal are believed to have important effects on the physical properties of coke, but since there is little information available for such study, and since vitrain, clarain, and durain are neither

Jan 1, 1944

Geochemical projects in progress or recently completed in the Bureau of Mineral Resources, Geology, and Geophysics (BMR) cover a wide range of topics and include research projects, regional studies, and prospecting programmes. However, in these notes emphasis is given to projects which are directly relevant to mineral exploration.FIELD INVESTIGATIONSStream sediment sampling, rock and soil sampling, and geobotanical surveys have been used by the BMR in a number of areas, partly in attempts to locate specific zones of mineralization, and partly to investigate the effectiveness of the various methods under different conditions of climate and topopraphy and in different geological settings.Stream sediment sampling has been most successful in the Territory of Papua and New Guinea. For example, in the South Sepik area, zones of disseminated su1phide mineralisation were found to give rise to anomalies with peak values of up to 1,000 p.p.m. copper, compared with background values of about 40 p.p.m. (Dow et al., 1968). By contrast, the results of rather limited work in the Northern Territory and in the Kimberley district of Westen Australia were inconclusive.Rock and soil sampling, on the other hand, was successfully used in a number of areas in Northern Australia, particularly at Rum Jungle and Tennant Creek.Rum Jungle area In the Rum Jungle area, where uranium and base metal mineralization is mainly associated with a Lower Proterozoic black slate sequence, samples, of c-horizon soil or weathered 'rock are generally collectedfrom the bottom of drill holes, usually 15 to 20 ft deep, bored with a power-operated auger.Surface sampling indicates that such a technique would probably have shown up all the major geochemical anomalies delineated by deep sampling, but the latter gives slightly more consistent and slightly

Jan 1, 1970