By S. Floreen, R. M. Pilliar, H. W. Hayden

The fracture behavior of a 50 pct Cu-50 pct Fe mi-croduplex alloy, laminated composites of copper and iron and an extruded 50-50 Cu-Fe elemental powder composite was studied. Very low ductile-brittle transition temperatures were achieved in all cases, but for different reasons. In the microduplex alloy both the initiation and also the propagation of cleavage fractures appeared retarded by the very small in-terphase distances. In the composites, crack propagation through the sumples was prevented in most cases by delamination fractures perpendicular to the advancing cracks. These delaminations occurred at different regions and by different mechanisms in the various composites. In the extruded powder composite, de-lamination appeared to take place along preexisting flaws. In the crack arrest geometry of the laminated plates, delamination took place by localized shear fractures within the copper near the Fe-Cu interfaces. In this case delamination was enhanced by thicker laminate layers, and by having the resistance to shear failure of the copper sufficiently low compared to the toughness of the iron. BRITTLE fracture in engineering materials has long been a problem, and many different ways of preventing it have been considered. One method that has been of growing interest lately is to prevent crack propagation by the introduction of mechanical discontinuities into the structure. These discontinuities may act in several ways. They may simply act as crack stoppers. They may introduce secondary fractures such as de-laminations that deflect the initial crack into new, less damaging directions. Alternatively, they may subdivide a fairly large bulk sample that would have been loaded in plane strain, for example, into a number of subunits that are individually loaded in plane stress and thus are more resistant to fracture. Other mechanisms, or combinations of mechanisms, are also feasible. A number of methods exist for introducing mechanical discontinuities into a structure. Composites by their nature have discontinuities in structure, and numerous studies have shown that fracture propagation in materials of this type can be radically changed by suitable control of the composite parameters. Of particular significance to the present work are recent investigations of layered composites made by joining high strength steel sheets by various means.'-4 These studies have shown that through proper control of the mechanical properties of the bonds joining the sheets it was possible to introduce delamination fractures that markedly improved the overall toughness of the composites and in some cases completely prevented through-the-thickness fractures. Another technique for introducing structural discontinuities is simply to use a two-phase alloy. It has been recognized for many years that a small amount of a second phase may improve toughness either by homogenizing plastic flow and thus preventing localized stress concentrations that nucleate fracture, or by interacting with an advancing crack. In most of these studies of two-phase materials, the decreases in ductile-brittle transition temperatures produced by the second phase were relatively small. More recently, work on two-phase stainless steels having a very fine grain microduplex structure has shown that the presence of on the order of 40 to 50 pct of a tougher second phase may lower the ductile-brittle transition temperature of the brittle phase by approximately 300°F. 5-7 In these alloys delaminations were seldom observed. The tougher second phase appeared to minimize the ease of both the initiation and the propagation of cleavage fractures. These results show that both the composite approach and the microduplex alloy approach are effective methods of preventing brittle fracture. Therefore, it was of interest to compare the fracture behavior of a microduplex alloy with composites made from the two-phases that were present in the alloy. To simplify this comparison the 50 pct Cu-50 pct Fe system was selected for study. At low temperatures the equilibrium tie line phases in this system are essentially pure ferrite and pure copper. A 50-50 alloy was cast and hot worked to produce a microduplex structure. Two types of composites were studied; laminated structures prepared by roll bonding iron and copper sheets of the tie line compositions, and an extruded powder composite made from high purity elemental powders. The fracture behavior of these materials was then compared. EXPERIMENTAL PROCEDURE Alloy Preparation. The 50-50 Fe-Cu alloy and the components for the roll bonded composites were prepared by vacuum induction melting 30-lb heats using electrolytic grades of iron and copper as charge materials. A carbon boil was used to deoxidize the melts. Small additions of copper and iron were made to the iron and copper heats, respectively, to approximate

Jan 1, 1970

By V. Pasupathi, R. E. Hummel, J. W. Koger

Specimens of P1 brass were plastically deformed at room temperature to various degrees of deformation and subsequently cooled in order to transform them to low-temperature martensite. Deformation shifts Ms. A, , and the temperature of minimum resistivity to lower temperatures, and also decreases the temperature coefficient of electrical resistivity. These properties change rapidly up to about 15 pct reduction but vary very little with higher deformation. The possible relationships between martensite formed by deformation and the M, temperature of low-temperature martensite are discussed. Evidence is given that deformation martensite delays the formation of low-temperature martensite. BETA' brass undergoes at least two different types of martensitic transformations. One of these transformations (B1- B2) was first observed by Kaminski and ~urdjumov' and occurs when 81 brass with a zinc content between 38 and 42 wt pct (quenched from the single-phase region) is cooled below room temperature. Jollev and Hull' determined the structure of 0" from X-ray and electron-diffraction data as ortho-rhombic. Kunze came to the conclusion that the super-lattice cell of 0" is one-sided face-centered triclinic (pseudomonoclinic). The second martensitic transformation (B1-A1) occurs when the specimens are deformed at or somewhat above room temperature. This type of martensite will be called deformation martensite. Horn-bogen, Segmuller, and Wassermann4 determined the structure of deformation martensite to be bct. (An intermediate phase, az, occurs before the final phase appears.) At deformations higher than 70 pct, a, transforms into a.4 A critical temperature Md exists above which no transformation occurs during deformation and is estimated to be around 400°C in P1 brass.5 This martensite has elastic properties.6 When the sample is stressed, martensitic plates appear; when the stress is released, the plates disappear. The present paper studies the effect of deformation martensite on the formation of low-temperature martensite. The experiments involved samples of 8, brass which were plastically deformed by various amounts and were subsequently cooled below the transformation temperature. EXPERIMENTAL PROCEDURE The 13 brass investigated was made from 99.999 pct pure copper and 99.9999 pct pure zinc and contained 38.8 wt pct Zn. The specimens, consisting of foils 0.1 mm in thickness, were heat-treated at 8'70°C for 15 min in an argon atmosphere and then quenched into ice water. They were then deformed by cold rolling and subsequently cooled at a rate of 1°C per min. The martensitic transformation that occurred during cooling was followed by electrical resistivity measurements. The resistance measurement technique and its accuracy have been described in a previous paper. Because the transformation 81 —-8" occurs below room temperature, the samples were placed in a cryo-stat which contained isopentane as a cooling medium. The isopentane was cooled by liquid nitrogen pumped under pressure through a 15-ft coil of copper tubing which was immersed in the isopentane. The nitrogen flow was regulated by a temperature controller using two thermistors in the cooling medium. The cryogenic liquid could be heated with an immersion heater. The useful temperature range with this device was from +25° to approximately -155~C. EXPERIMENTAL RESULTS Resistivity Measurements. The following abbreviations are used in this paper to label the characteristic temperatures during the martensitic transformation. M, is the starting point of the martensitic transformation and is defined as that temperature where the resistivity vs temperature curve on cooling first deviates from a straight line. Mf is the temperature at which the martensitic transformation is completed. On reheating, the transformation from martensite to the parent phase starts at a temperature A, and ceases at a temperature Af. Fig. 1 presents five different resistivity vs temperature curves corresponding to the transformation of brass from Dl to 8" after different degrees of reduction in thickness. The following observations can be made from these curves. 1) With increasing degree of deformation the Ms temperature is shifted to lower temperatures. This shift ranges up to 35°C compared to the undeformed state. This is also indicated in Fig. 2, where AM, (the shift of Ms, compared to the undeformed state) is plotted vs the degree of deformation. AM, increases rapidly until a reduction of about 15 pct is reached. With higher deformations, no additional increase in AM, was found. 2) With increasing degree of deformation the temperature of minimum resistivity (M) is also shifted to lower temperatures. The shift, attains a maximum of about 61°C compared to the undeformed state. In Fig. 3, AM is plotted as a function of deformation. It can be seen that, as in 1 above, AM increases rapidly and no further shift of M occurs for deformations greater than 15 pct. 3) The temperature coefficient of resistivity, is given by the slopes (dp/dT) of the linear portions of

Jan 1, 1969

By S. Storchheim

MORE and more attention is being paid to the bonding of metals in their solid states. For a better understanding of this technique for joining metals and how it is affected by changes in temperature, pressure, and time at temperature and pressure, a detailed report concerning nickel to aluminum bonding has been published.' In order to broaden the knowledge accrued, some additional work concerning solid state joining of aluminum to copper and aluminum to zirconium was performed. The investigation of the Al-Cu system was considerably more extensive than the investigation of the Al-Zr system. For the A1-Cu system, not only were tensile sudies made but intermetallic penetration rate investigations also were carried out. The effect of temperature on intermetallic penetration rate for the A1-Cu system was determined at 11 tsi pressure, held 2 min. Procedure Apparatus: The hot pressing technique was the means of solid state reaction used and required the equipment depicted in Fig. 1. The following procedure was involved: The two metals to be reacted were placed in an aquadag-lubricated 18-4-1 tool steel die, 16 in. high by 1.440 in. ID, between punches of 1.366 in. diam made of the same material. A thermocouple well was located in the die body 3½ in. down from the top of the die, while another well was located centrally in the bottom punch 8½ in. from the bottom of the die. This die assembly was located in three cylindrical ceramic heating furnaces placed in tandem. Each furnace was controlled individually by a Variac power transformer. In turn, the die and furnaces were placed in a water-cooled stainless steel pot which could be evacuated. A cover, which contained a centrally located Wilson seal with an 18-4-1 1 in. diam ram running through it, was bolted on the pot. After sealing, the pot was evacuated by a roughing pump to 200 microns pressure, after which a diffusion pump was used to bring the pressure down to 5 to 15 u. At this pressure, the furnaces were turned on. As soon as they started to heat, out-gassing of the entire unit raised the pressure to 30 to 400 p. By the time the specimens were at temperature ready to be pressed, approximately 4/2 hr, the vacuum pumps had re-established the 5 to 15 u pressure. Once the desired temperature was reached, the required pressure was applied for a predetermined length of time to the 1 in. ram, through to the top punch, and to the specimen. When the time for keeping the specimen under pressure had elapsed, the pressure was released, the energizing coil current turned off, and the assembly allowed to cool. After cooling, the die was removed from the pot and the specimen was ejected. Specimen Preparation: Two different types of specimens were made for this investigation. One was for subsequent tensile testing, while the other was for determination of intermetallic alloy zone penetration into the parent metals. Tensile Bars—Commercially rolled copper pieces in. thick or zirconium sheet pieces 1/32 in. thick and 1.366 in. diam were placed between commercial 2-S aluminum rod 1 in. thick and 1.366 in. diam. This sandwich in turn was slipped into a 2-S aluminum sleeve 1.438 in. OD and 1.370 in. ID. This sleeve lined the couple up and prevented the aquadag lubricant from getting in between either the A1-Cu or Al-Zr interfaces. Immediately prior to the specimen assembly, the copper or zirconium was abraded on the flat surfaces with 320 grit silicon carbide paper, producing clean smooth surfaces. The aluminum was chemically cleaned just before assembly by: l—degrease in acetone, 2—distilled water rinse, 3—immersion for 3 min in 5 pct NaOH at 70" to 80°C, 4—distilled water rinse, 5—immersion for 2 min in 50 pct HNO3 solution at room temperature, 6—distilled water rinse, and 7—drying in a blast of gas. After the A1-Cu sandwiches were hot pressed and ejected, the specimens were machined such that the aluminum sleeve was removed, and the remaining aluminum was then threaded; the bar so produced was tested later for tensile strength. In all the instances where Al-Cu couples were tested, the specimens broke during the test at the Cu-A1 interface and never within the aluminum or copper. The ultimate tensile strength values at times showed considerable scatter for a set of given reaction conditions. Because of this, as many as three to five specimens were made for a particular set of conditions. The trend of the average tensile strengths obtained was not as conclusive as was the trend of the maximum tensile strengths, the latter values being obtained under optimum reaction conditions. Therefore, the values of ultimate tensile strength given herein are maximums.

Jan 1, 1956

By Amitava Gangulee, Michael B. Bever

The order-disorder transition in Ag-Mg alloys in the range 17 to 26 at. pct Mg was investigated and some thermodynamic, electrical and mechanical properties of ordered Ag-Mg alloys were measured. A modification of the phase diagram is proposed on the basis of measured transition temperatures. The stability of the ordered structure is analyzed in terms of the quasichemical theory. Kinetic aspects of the order-disorder transition were also investigated. The energies of ordering at 273°K of Ag-Mg alloys were measured by liquid metal solution calorimetry. The electrical resistivities and the tensile Properties of the ordered alloys were measured. The exothermic energy of ordering increased with magnesium concentration up to the composition Ag3Mg; it is discussed in terms of the quasichemical theory. Pronounced order hardening was observed and can be explained by several strengthening mechanisms, which are particularly effective because of a change in crystal structure associated with the ordering transition. IN silver-rich solid solutions containing approximately 17 to 26 at. pct Mg, long- range ordering may occur during appropriate therma1 treatments. Clare-brough and Nicholas1 first detected such long-range order in the solid solution of composition Ag3Mg and suggested that the unit cell of the superlattice contained 256 atoms. x-ray2 and electron diffraction3 investigations confirmed the occurrence of long-range order, but indicated a shifted Ll2-type structure. On the basis of recent X-ray measurements the crystal structure of ordered Ag3Mg has been confirmed as type D023.4 The present paper is concerned with the order-disorder transition in silver-rich Ag-Mg solid solutions and some thermodynamic, electrical, and mechanical properties of the ordered alloys. The effects of short-range order on the properties of silver-rich solid solutions containing up to 26 at. pct Mg are discussed in a concurrent paper.5 1) EXPERIMENTAL PROCEDURES 1.1) Preparation of Specimens. Specimens of Ag-Mg alloys containing from 18 to 26 at. pct Mg were prepared in the form of 1.0-mm-diam wires as described in Section 1.1 of Ref. 5. Disordered specimens were prepared by annealing at 773°K for 1 hr and quenching into iced brine. Ordered specimens were prepared by annealing at 773°K for 1 hr and slowly cooling to room temperature over a period of 15 days. The specimens were stored at 78°K. 1.2) Resistivity Measurements. Electrical resistivi- ties were measured by a potentiometric method.' Equilibrium values were obtained at several temperatures. The kinetics of ordering were investigated by following the time-dependent changes of the resistivity of initially disordered specimens during annealing. The specimens were enclosed in copper capsules and immersed in salt pots; the heating up was accelerated by injecting preheated helium into the capsules. 1.3) Calorimetry. The energies of ordering of the alloys were measured in a tin solution calorimeter as the difference between the heat effects of additions of completely ordered and disordered specimens of the same composition. The procedure and the method of calculation have been described.6 Magnesium was used for thermal compensation in most calorimetric runs in order to improve the accuracy.677 1.4) Mechanical Tests. Tensile tests were carried out with wire specimens at room temperature as described in Section 1.5 of Ref. 5. Microhardness measurements were also made.? 2) RESULTS AND DISCUSSION The characteristics of the order-disorder transition of silver-rich Ag-Mg solid solutions will be discussed first. Some thermodynamic, electrical, and mechanical properties of the ordered alloys will then be considered and compared with the corresponding properties of dis-disordered alloys. 2.1) The Order-Disorder Transition. 2.1.1) Thermodynamic and Structural Aspects. The transition temperatures Tt were determined from discontinuities in the slope of the equilibrium resistivity vs temperature curves. Normalized curves for three compositions are shown in Fig. 1. The transition temperature increases with the magnesium concentration and reaches a maximum at the stoichiometric composition Ag3Mg. The transition temperature of the alloy Ag3Mg was measured as 665° ± 2°K and compares with published values of 660°,1 663°,8 and 66°k.3 In the slopes of the resistivity vs temperature curves of alloys containing 22.2 and 22.5 at. pct Mg, discontinuities were observed at two temperatures. Such upper and lower discontinuities indicate a two-phase field. A modified form of the published phase diagram9 is shown in Fig. 2. A two-phase field was found only on the low-magnesium side of the composition Ag3Mg. On the high-magnesium side, the existence of a two-phase field could not be established because of insufficient resolution, but such a field must be present. This part of the phase diagram can be made complete by a eutec-toid-type reaction a = (a' + ß). The existence of a boundary between the two-phase fields (a + ß) and (a' + ß) is also in accord with published lattice parameters.3 The crystal structure of ordered Ag3Mg (type Do23)

Jan 1, 1969

By Nicholas J. Grant, Ulf Kalling, John Chipman

THE operation of a blast furnace is dependent to an important extent upon the sulphur content of materials charged and the desired limit of sulphur in the product. It has long been known that the blast furnace is the most efficient tool for desulphurization in common use and that this efficiency is associated with the strongly reducing conditions of the hearth and is enhanced by increased basicity and fluidity of the slag. The chemical reactions of desulphurization may be studied from the viewpoint of the ratio of the process or of the final equilibrium conditions. Both kinds of studies contribute to an understanding of the process and both are included here. A simple measure of the desulphurization power of a slag is given by the ratio: Pct sulphur in slag (Pet S) Pct sulphur in metal [Pct S] This ratio was used by Holbrook and Joseph',' to measure relative desulphurizing powers under controlled laboratory conditions. It was also used by Hatch and Chipman3 as a measure of the equilibrium distribution. For the latter purpose it would be preferable to employ thermodynamic activities rather than percentages, but until very recently this has been impossible for lack of data. Now, thanks to the work of Morris and Williams and Morris and Buehl," the effects of carbon and silicon upon the activity of sulphur in the metal are known. The confirmation of this work and its extension to include the effects of other elements by Sherman and Chipman and by Rosenqvist and Cox' make it possible to calculate the activity of sulphur in pig iron of any composition. Hence it is now possible to use data on the equilibrium distribution of sulphur to find its activity in the liquid slag and to approach an ultimate solution of the thermodynamic aspects of the problem. The rate of transfer of sulphur from metal to slag is the problem of major industrial importance and indeed the principal need for equilibrium data has been as a necessary adjunct to the kinetic studies. The rate of approach to equilibrium under laboratory conditions seems slow compared to the requirements of industrial practice, and it is clear that further laboratory studies of rates are needed. In the research reported below, the items which were investigated were the following: I—The role of mechanical stirring on the approach to equilibrium. 2—The role of MgO in desulphurization as compared to CaO. 3—The role of MnO in desulphurization. 4— The limiting reactions which constitute the slow steps in desulphurization. Experimental Procedure The experimental set-up and procedure previously described by Hatch and Chipman" were essentially followed with several small modifications. The graphite crucible containing the slag and metal charge was altered to provide considerably more active stirring and mixing of the slag and metal in the carbon monoxide atmosphere. For this purpose the crucible was machined to provide two deep cylindrical wells which were interconnected at top and bottom as shown in Fig. 1. A graphite screw with a flat thread and of shallow pitch (4 threads per in.) spinning at 600 to 800 rpm was used to lift the slag and metal over the partition between the two wells and throw them over into the second well, where the metal settled through the slag into the reservoir at the bottom. It was possible to see actual particles of slag and metal being thrown over the partition. In this respect, the stirring was more vigorous than used in the work of Hatch and Chipman. A charge of 400 g of wash metal was first melted, and 20 g of FeS was then added to yield a bath containing 1.65 pct S. Immediately 400 g of slag (as pure mixed oxides) was added and fused. The slag was generally fused in 1 hr * 10 min. Within 30 to 45 min after melting, the temperature was adjusted to 1525"C, and the first slag and metal samples were taken. The slag was picked up on the end of a cold Armco iron rod, whereas the metal was sucked into a silica tube. The wash metal composition was (in percent): 4.29 C; 0.022 S; 0.021 P; 0.38 Si. The slags used were of four fixed starting compositions covering a wide range of acid-base ratios shown in Table I. Deliberate variations in MgO were made in these slags to check the role of MgO in blast-furnace desulphurization. Changes due to additions and reactions were followed by analysis of samples. Additions of Mn and MnO were made to most of the heats to note the role of Mn and MnO on desulphurization. Three heats (62 through 64) were made in an open pot induction crucible (graphite) using a

Jan 1, 1952

By W. C. Ellis, E. S. Greiner, M. E. Fine

Discontinuous changes of Young's modulus, internal friction, coefficient of expansion, electrical resistivity, and thermoelectric power are evidence for a transition in chromium near 37OC. Although the X-ray diffraction pattern gives no clue, a difference between the thermal expansivity and the temperature dependence of the lattice parameter suggests a crystal-lographic change. Young's modulus data disclosed another transition near THE thermal dependence of a number of proper- ties of chromium indicates a transition occurring over a temperature range near room temperature. Bridgman' noted this first from a minimum in the electrical resistivity near 12°C. In a sample of greater purity, Sochtig' observed the minimum at 41 °C. Erfling3 reported an inflection in the thermal expansivity curve at 36°C. These temperature-dependence curves are reversible with no hysteresis being detected. No discontinuity or inflection has been observed in the heat capacity' or the paramagnetic susceptibility.' Likewise, no one has noted a change in crystal symmetry. In the present investigation Young's modulus, internal friction, coefficient of expansion, electrical resistivity, illustrated in Fig. 1, lattice constant, Fig. 2, thermal electromotive force, Fig. 3, and paramagnetic susceptibility, Fig. 4, were measured over an extended temperature range. The samples were prepared in two ways: (1) By cold pressing a sintered electrolytic powder compact,' and (2) by electroforming from an aqueous solution. The electroformed samples were prepared by R. A. Ehrhardt and G. Bittrich by plating on copper or nickel tubes from an aqueous solution according to the method of Brenner, Burkhead, and Jennings.' The pressed powder samples (method 1) were finally annealed at 1400°C in purified helium: the electroformed samples, packed in powdered chromium, were vacuum-annealed at 1000°C. From the composition of the original powder' the purity of the pressed powder samples is estimated to be 99.8 pct Cr. Spectrochemical analysis furnished by E. K. Jaycox, revealed only slight traces of impurities in the electroformed sample (less than 0.001 pct), neither iron nor nickel being detected. Chromium deposited by this method is reported to contain approximately 0.05 pct 0.- Methods and Data Young's Modulus: For measurement of Young's modulus, an annealed, pressed powder sample, 0.114 x0.237x1.845 in., and an electroformed sample, 0.10 in. od, 0.01 in. id, and 1.86 in. long, were prepared. The resonant frequencies of the rod samples in forced longitudinal vibration were measured at a series of temperatures from —192" to 200°C by a method previously de~cribed.6,7 Because the samples were nonferromagnetic, iron- silicon or molybdenum permalloy tips (0.013 in. thick) were soldered to the ends. The softening temperature of the solder limited the temperature of measurement. Young's modulus, E,, of chromium at temperature, T, may be calculated from the resonant frequency of the composite rod, f,; the thickness of the tips, t; the length of the chromium sample at 25°C, l,.; the density of chromium at 25°C, pc (7.20 g per cc);5 and the thermal expansivity, Al/l25. Modulus differences for two temperatures, ET and E, are accurate to +0.002x10" dynes per cm2. ET = 4PAlc+2tyf Young's modulus at 25°C, Fig. la, is 28.2~10" dynes per cm' (40.8xlO" si) in wrought chromium (upper curve). The modulus of the electroformed sample is apparently lower due to cracks. From the modulus measurements two transitions were observed: one with a critical temperature at 37°C, the other at —152°C. Internal Friction: The internal friction, 1/Q, was determined from the width, Af, of the strain amplitude-frequency curve at 0.707 times the strain amplitude at resonance;' the internal friction, 1/Q, then equals Af/f. Fig. lb shows a sharp peak in internal friction at 38°C. The internal friction of the electroformed sample had a similar maximum. Thermal Expansion: The expansivity measurements, shown in Fig. 2, covering the temperature range —195" to +400°C were made by D. MacNair in an interferometric dilatometer8 sing a sample consisting of three pyramids 0.25 in. high prepared from wrought electrolytic chromium. Below —120°C the experimental points deviated up to ±2x10 from the drawn expansivity curve in Fig. 2 because of decreased precision of the quartz wedge thermometer at low temperatures. Near 38°C the thermal expansivity curve, Fig. 2, goes through an inflection corresponding to a minimum in the coefficient of expansion, Fig. ld, and a relative volume decrease on heating. Electrical Resistivity: The variation of electrical resistivity with temperature measured by the po-tentiometric method is also shown in Fig. l. The resistivity of the wrought chromium (upper curve) at 20°C is 13.6 microhm-cm; of electroformed chromium (lower curve) 12.8 microhm-cm. The lower value reflects higher purity and agrees closely with a published value." A minimum at 40°C occurs in the resistivity curves of both samples. No conclusive evidence for a transition near — 150°C was observed, but the points, Fig. 1, appear to deviate from a smooth curve between —120" and —160°C.

Jan 1, 1952

By H. R. Page, A. E. Jr Lee

From the inception of zinc retorting on a commercial scale in the United States in 1890,' the retort employed has undergone wide variations in its composition and manufacture, facilitating in part equally remarkable improvements in furnace capacities. The early day hand made clay retort was charged with carbonates or silicates or with coarse dead roasted concentrates mixed with a large proportion of charge fuel resulting in a relatively low zinc burden and fired 24 hr in direct coal fired furnaces. Its modern counterpart is fabricated in hydraulic presses from clay mixtures containing sizeable amounts of either silicon carbide or silica flour, charged with sintered flotation concentrates to more than three times the early day zinc burden and fired 24 to 48 hr in gas fired furnaces. This paper does not attempt to describe in detail the early day clay retort practice as it is well outlined in treatises by Ingalls,2 Lodin,3 Liehig,4 Hofman5 and others. A brief review of clay retort practice is presented together with a description of the major developments since 1912. Clay Retorts The Belgian type retort, both in the circular and elliptical forms, has been used almost exclusively. Typical dimensions of press made clay retorts around 1910 are shown in Table 1. Variations in these dimensions were used at different plants according to local conditions to a maximum inside diameter of 9 in. and inside length of 54 in. However, the effective heat penetration in a 24 hr firing cycle and the tendency of the retort to bend limited the retort size. Use of the elliptical vessel was an attempt to present a stronger cross-section resisting the tendency to bend and to increase the burden without increasing the depth of heat penetration. One exception to the 48-54 in. length was the 60 in. retort used as early as 1905 at Palmerton by means of supporting the last 12 in. at the butt end with a specially designed furnace back-wall. This backwall construction with the 60 in. retort had been developed and used at Bethlehem by G. G. Con-vers and A. B. DeSaulles. An attempt was made at Blende, Colo. to use even larger retorts of the Rhenish type based on European practice and requiring much higher furnace temperatures. Satisfactory plastic clays capable of withstanding these temperatures were not available, and the plant never operated successfully. PREPARATION OF BATCH Composition of the clay retort by weight was 40 to 50 pct raw clay and the balance "grog." Generally speaking the mix consisted of 7 parts plastic clay to 9 parts grog by volume. Principal source of the clay used was the Cheltenham vein—sometimes referred to as "St. Louis city clay." A typical analysis was A12O3-31.0 pct, SiO2-50.0 pct, Fe2O3-2.5 pct, MgO-0.3 pct, CaO-1.5 pct and loss on ignition 14.0 pct. At the smelter the clay was weathered whenever possible and then crushed to 0.08 in. or finer. Grog consisted of calcined adobies, cleaned retort scrap and cleaned refuse fire brick such as old furnace brick, blast furnace linings, and others. Saggers from ceramic plants and calcined flint clay were later used. The grog materials were ground to 0.12 m. or finer. Occasionally coke dust up to 10 pct of the mix was substituted for a part of the grog following European practice.² Particle size of the grog has a major influence on the retort properties—the larger the grain, the better can the retort withstand thermal shocks, resist bending at furnace temperatures and resist corrosion from slag; the smaller the grain, the lower the loss of zinc vapor through the retort walls. Grog forms the skeleton of the retort, and the clay shrinks around its grains to act as a binder. In the drying process, the grog has a stabilizing effect on the drying rate, decreasing shrinkage and giving up previously absorbed water to the surrounding clay to minimize the danger of cracking or checking.² Grog and clay were mixed through a horizontal pug mill with 10 to 20 pct water added, depending on whether the retort was to be formed by hand or mechanically, more water being required for the hand process. The batch or "mud" extruded from the pug mill was cut in convenient lengths for handling, stacked in piles or in special rooms, covered with wet burlap and allowed to "rot" or age from 1 to 8 weeks to increase plasticity. HAND MOLDING If the retort was to be molded by hand, the mud was repugged after the rotting period and given to the molders. Their molds consisted of 3 sheet iron or wood cylinders, each one third the retort length and defining the outer shape of the retort. Beginning with the bottom section, mud was placed in the form and tamped with a rammer

Jan 1, 1950

By John D. Janak

Thank you for inviting me to come here and be your keynote speaker. Texas also thanks you for being included as part of the Rocky Mountain Coal Mining Institute. We'll kind of think of Texas as Baja Rocky Mountains. I've always wondered why coal miners were the only people to go to the mountains in the summer time-and now I know why. The program committee should be given a big hand for selecting this RESORT. And the golf course is stimulating to say the least. This is a very beautiful location. I was asked to talk about CHALLENGES, OPPORTUNITIES and INNOVATIONS as they affect the coal industry. I am going to do that from a Texas perspective. But first, since Texas is the newest state to belong to the Institute, I would like to give you a little background on how our coal industry got started and where we are at today. The vast majority of our coal is called lignite-it has a little lower heating value than most other coals and ranks somewhere between buffalo chips and sub- bituminous. Lignite is found In three geological formations running Northeast to Southwest through South and East Texas. In-place reserves lying within 200 ft. of the surface total 14 billion tons. This slide shows the lignite formations with cur- rent mine operations colored in RED. Mines that are planned to be built in the next 10 years are shown in BLUE. Lignite was used mostly by settlers in Texas during the 1800s. It was used as a fuel to fire locomotives during the Civil War. Between 1900-1930, about 100 mines, mostly underground, were operating in Texas producing lignite for home heating and as a boiler fuel. Here are some slides showing underground access, [lie tipple used to process the lignite, and the underground workings. This is the "BIG LUMP COAL COMPANY" as shown here. The typical underground mine was 100-150 ft. deep and each miner produced 7-10 tons per day-all by hand. In 1926, the Texas Power & Light Company built the Trinidad Power Plant and began using lignite as a boiler fuel. The lignite was mined by the McAlester Fuel Company at the nearby Malakoff Mine. Here are some slides showing a stripping shovel at Malakoff uncovering lignite. The lignite was loaded into railcars in the pit for transport to the power plant. This is a picture of the Trinidad Plant which had two 20 MW units and one 32 MW unit. At the time, Trinidad was the largest power plant in the United States using lignite exclusively as a fuel. Trinidad operated until 1942 when it was converted to natural gas that was sold to the plant for 3 ½ ¢ per MMBT'U. The mine closed after having produced 7 million tons. Lignite was mostly forgotten about until 1953 when Alcoa started an aluminum smelter. Our Company formed a subsidiary called Industrial Generating Company to operate the power plant that furnished electricity to the smelter. We also operated the nearby Sandow Mine that supplied lignite as a fuel to the power plant

Jan 1, 1989

By M. Rieber

In July 1985, as the U.S. copper industry contracted and the Mexican industry expanded, a trans border pollution agreement was signed which included smelter air pollution control in the "Gray Triangle": Cananea, Nacozari and Douglas. Since then the Douglas smelter has been closed, a year earlier than initially required; though its new smelter is operating, S02 collection and acid disposal at Nacozari is yet to come; and the Cananea smelter has been un-touched. Nacozari and Cananea copper mining have expanded while a reduced U.S. copper industry has rationalized to a point of fragile profitability. As a paradigm of U.S. copper competitiveness, this paper attempts to explain the differential fortunes of copper in the two countries, to project the future of the smelter agreement as a function of acid disposal, and to consider the consequences of the politicized application of smelter pollution control in Arizona.

Jan 1, 1988

By W. F. Domis, F. von Gemmingen, F. Garofalo

The effect of rain size on the creep behavior of an austenitic iron-base alloy has been studied at 1300° F under conditions of constant stress. The average grain diameter varied between 9 and 190 p (ASTM 10.7-2). The subgrain size and apparent activation energy for creep were not found to depend in any systematic manner on gain size. Grain hozmdary serrations were observed in all specimens tested. The variation of the secondary-creep rate, 2,, with the pain diameter, 1, is given by: es = K(213m + 1 )/l.]; 1, is the grain diameter zohere is reaches a minimum. Results in the literature shoujthat 1,increases as the temperature increases. At low creep temperatures is is therefore proportional to 12, at intermediate temperatures <, exhibits a minimum, and at high creep temperatures is is proportional to 1/1. The dependence ofis on the stress, u, is given by: t, = A" (sinh acrln, a and n show little variation with 1. The dependence of A" on 1 is given by: A" = KA[(21k + 13)/1]. For 1 » >>lmn = 4, and at constant values 01- isat lozu stress levels, the steady-state stress is given by the Hall-Petch relation. The variation of c, with grain size is believed to he associated particularly with grain boundary generation of dislocations which becomes more important with increasing temperatures. SEEMINGLY inconsistent experimental findings have led to a certain amount of confusion concerning the effect of grain size on creep behavior. The confusion is attributed to a lack of test results obtained over sufficiently wide ranges in grain size, stress, and temperature. Experimental results presented in this paper and results available in the literature1-5 show a consistent behavior and lead to a unified concept for the dependence of secondary-or steady-state creep rate on grain size. In accordance with this concept, which is substantiated experimentally, secondary-creep rate should increase with increasing grain diameter at low creep temperatures, leading to greater creep strengths for fine-grained materials. At intermediate temperatures the secondary-creep rate should decrease to a minimum and then increase as the grain size is increased. At high creep temperatures the secondary-creep rate should decrease with increasing grain size, leading to greater creep strengths for coarse-grained materials. Whether a temperature is high or low for creep in a metal or alloy depends primarily on its melting temperature. MATERIAL AND TEST PROCEDURES The material tested was an austenitic iron-base alloy of the following composition (wt pct): C, 0.005; N, 0.017; Mn, 1.26; Ni, 14.21; and Cr, 17.18. Two 15 -lb ingots were forged and hot-rolled to 5/8-in.-diam bars which were then cold-rolled and cold-swaged to a diameter of 0.49 in. These were sectioned into 3-in.-long blanks and heat-treated at various temperatures to obtain different grain sizes. The procedures employed and the results obtained are summarized in Table I. The secondary treatment at 1400° F followed the primary treatment without intermediate cooling to room temperature. This final treatment was employed to minimize various effects arising from heating to different temperatures during the primary treatment, particularly differences in intragranular dislocation structure, segregation of interstitial atoms at grain boundaries, and density of grain boundary ledges. The intragranular dislocation structure was examined by electron transmission metallography after each of the treatments described in Table I. Isolated dislocations and a few tangles were observed but no evidence of subgrains was found after any of the treatments. No grain-size effect was evident on the density and distribution of dislocations. Stabilization of grain boundary structure is particularly important because, as will be discussed later, grain boundaries influence high-temperature creep behavior. Magnetic-permeability measurements after each treatment and

Jan 1, 1964

By D. R. Uhlmann, T. P. Seward, K. A. Jackson, J. D. Hunt

microscopic ohservations on alloys of organic trzaterials show that dendrite arms can melt off under normal conditiorzs of growth. This occurs because of the interactiorz of&apos; heat and matter fluxes during dendritic growth. The re melting occurs where the den-drite arms are joined onto the main deizclrite sterrz. Many detached crystals can be produced in this fashion. It is postulated that this remelting phenornenon occurs in metal alloys, giving rise to the equi-axed region in castings. Experiments peyformed orr castings of transparent materials support remelting as a primary source of detached crystals. Ob~ervations an equiaxed tones in metal castings are discussed in terms of this and other mechanisms. It is concluded that the partial remelting of dendrites is on important mechanisnl for producing the equiaxed regions in castings. THE freezing of a casting can be divided into three regions: a chill zone formed near the mold wall, a columnar region, and a third region, at the center of the casting, which is called the equiaxed zone. The origin of the grains that comprise the equiaxed region is the subject of this paper. We will first outline the mechanisms which have been proposed to account for the origin of the equiaxed region and discuss some recent experiments which cannot be explained by these theories. We will then present some microscopic observations of dendritic growth which have led us to conclude that the equiaxed zone in castings can arise from partial remelting of dendrites. This proposal is supported by observations on transparent castings. Finally, we will discuss several observations on metal castings which could not be explained previously, and which can be accounted for by the present proposal. Previous Mechanisms. Winegard and Chalmers3 pointed out that the molten central region of an ingot could be constitutionally supercooled, because of the solute layer at the growing interface. In this supercooled region, nucleation on particles could occur, giving rise to the equiaxed crystals. Another mechanism has also been suggested,4y5 that the nuclei originate in the chill zone then float or are carried by convection to the center of the casting, where they grow to produce equiaxed crystals. In this case, all the crystals nucleate immediately on casting, so this mechanism will be termed "big-bang" nucleation. Walker&apos;s Experiments. J. L. Walker has made observations on the solidification of nickel and Ni-Cu alloys which cannot be accounted for by either of the above mechanisms. In studying the grain size resulting from freezing of nickel at various undercoolings, walker6 found that at large undercoolings the grain size was small, due to mechanical nucleation, as discussed by walker7 and Horvay.&apos; At small undercoolings, the grain size was large, and the growth dendritic. In Ni-Cu alloys, however, for initial undercoolings starting from just below the melting point and extending for a hundred or so degrees of undercooling, fine grains were also observed. Samples were undercooled 200 Centigrade degrees without nucleating, and were then heated 130 Centigrade degrees so that the undercooling was 70 Centigrade degrees, and nucleated. The samples had a small grain size, indicating multiple nucleation. There were no heterogeneous nuclei in the liquid which could operate at the temperature of growth. Constitutional supercooling could not have been greater than the supercooling of the initial melt, since the temperature rose as the freezing continued. walker -as also shown that a Ni-Cu alloy which can be undercooled to below its solidus will produce typical columnar and equiaxed regions when cast into a cold mold. This alloy could not reach a temperature below its solidus by constitutional supercooling. It could not, therefore, have nucleated heterogeneously. Neither the big-bang mechanism nor the Winegard-Chalmers mechanism can account for the fine grain

Jan 1, 1967

By Anibal Gastañaga

La determinación del cuarzo es un problema dentro de la Higiene Industrial, puesto que este mineral se convierte en una de las enfermedades ocupacionales causadas por la inhalación de pequeñas partículas de cuarzo encontradas en el aire. En ese sentido, el presente texto señala la importancia y peligrosidad de los polvos del mineral a través de la determinación cuantitativa de cuarzo en los polvos industriales, ya que el riesgo de adquirir silicosis es proporcional a la concentración de cuarzo en los polvos ambientales. Existen tres métodos para la determinación cuantitativa de cuarzo: El método químico, el de difracción de rayos X y el petrográfico. El método que presenta mejores beneficios es el de N. A. Talvitie, puesto que se basa en la propiedad del ácido fosfórico, donde se forma complejos solubles en agua con los silicatos y óxidos metálicos, quedando el cuarzo prácticamente inalterado.

Aug 1, 1955

By E. J. Rapperport, E. D. Levine

The boundaries of the (a +ß) field in the Al-Li system were determined between 150°and 550°C utilizing quantitative metallography and lattice-parameter measurements. The solubility of lithium in aluminum decreases from 12.0at. pct Li at 550°C to 5.5 at. pct Li at 150°C. P Al-Li is saturated with aluminum at 45.8 at. pct Li and has this boundary value constant over the temperature range 150°to 550°C. THE solid solubility of lithium in aluminum has been determined by several investigators, 1-6 but, as shown in Fig. 1, there is little agreement among the various determinations. The earliest investiga-tions&apos;-&apos; are suspect because of the use of impure materials. Although high-purity materials were employed in more recent work,4&apos;5 the experimental techniques may have led to contamination of the specimens. Probably the best work has been that of Costas and Marshall,6 who obtained close agreement between results obtained by two independent phase-boundary techniques: electrical resistivity and mi-crohardness. No detailed studies of the solubility of aluminum in the bcc ß phase, Al-Li, have been reported. Cursory investigations1,2,6 have indicated only that the (a+ß) -p boundary lies between 40 and 50 at. pct Li and is relatively independent of temperature. The present work was undertaken in order to provide an independent check on Costas and Marshall&apos;s determination of the solubility of lithium in aluminum, to extend knowledge of this solubility limit to temperatures below 225°C, and to make an accurate determination of the solubility of aluminum in Al-Li. EXPEFUMENTAL Alloy Preparation. In view of the difficulties encountered in previous investigations of the A1-Li system, close attention was paid to the use of methods of alloy preparation and treatment that would minimize contamination. Aluminum sheet (99.99 + pct Al) was vacuum-induction melted in a beryllia crucible to remove hydrogen. Lithium (99.9 pct Li) was charged with pre-melted aluminum into a beryllia crucible, in a helium-filled drybox. The crucible was sealed in a Vycor tube and transferred from the drybox to an induction furnace. Melting of alloys was performed by induction heating in a helium atmosphere. Solidification was accomplished by means of a suction apparatus, shown in Fig. 2, in which the alloy was forced by changes of pressure into a 3/16-in. inside diam closed-end beryllia tube. This technique produced rapid solidification of a small portion of the melt, resulting in alloys with a high degree of homogeneity. Typical lithium distributions are presented in Table I. Transverse sections 1/8 in. long were cut from the alloy rods, and each section was split in half longitudinally. One half of each section was analyzed for lithium, and the opposing halves were employed for phase-boundary determinations. Lithium contents were determined by flame photometry with an accuracy of 1 pct of the amount of lithium present. Thermal Treatments. Homogenization and equilibration heat treatments were performed in electrical-resistance furnaces with temperatures controlled to ± 2OC. Calibrated chromel-alumel thermocouples were employed to measure temperature. Homogenization was performed in helium-filled l?yrex tubes for 1 hr at 565°C. The encapsulated specimens were then transferred directly to furnaces maintained at lower temperatures for equilibration. Equilibration times were 2 hr at 550°C, 8 hr at 450°C, 27 hr at 350°c, 90 hr at 250°c, and 285 hr at 150"~. These times were chosen on the basis of conditions employed by previous investigators. Alloys were quenched from the equilibration temperatures by breaking the capsules into a silicone oil bath. By performing all possible operations either in sealed capsules or in a helium-filled drybox, the specimens were given minimum exposure to the atmosphere. Quantitative Metallography. Metallography of Al-Li alloys is difficult because of the atmospheric reactivity of the ß phase. It was found possible, however, to prepare surfaces of good metallographic quality by preventing contact with moisture during preparation. Grinding through 4/0 paper was performed in the drybox. The specimens were then transferred under kerosene to the polishing wheel. Three polishing stages were employed: 25-p alundum with kerosene lubricant on billiard cloth, 1-µ diamond paste on Microcloth, and 1/4-p diamond paste on Microcloth. Between stages the samples were cleaned by rinsing in trichloroethylene and buffing

Jan 1, 1963

By T. Toda, R. Maddin

A study has been made of the microstructure and mechanical properties of splat-cooled aluminum-base gold alloys with gold concentration from 0.25 to 5.0 wt pct. These alloys have been quenched from the liquid state by a torsion-catapult technique, which has made it possible to pepare specimens suitable for mechanical property measwements. From the electron micrographs it has been shown that the solid solubility of gold in aluminum can be extended to 2.5 wt pct (0.35 at. pct) by splat-cooling, while the maximum equilibrium solubility is known to be less than 0.3 wt pct (0.04 at. pct). The very fine grain size (several tenths of a micron), the extended solid solubility, and the fine dispersion of a second phase (AuAl2) contribute concurrently to a substantial strengthening effect. In Al-5 wt pct Au splat-cooled specimens of less than 50 thickness, the yield strength is 17 kg per sq mm or 6 times as large as the strength of bulk specimens. For the Al-1.0 to 2.5 wt pct Au solid solution obtained by splat-cooling, the yield strength reaches 7.5 kg per sq mm after an aging treatment (for 10 hr at 200°C), while it is 3.7 kg per sq mm for the corresponding bulk specimens. A great deal of research has been done in recent years on the structure and the properties of metals and alloys rapidly quenched from the liquid state.&apos; The term "splat-cool" has been used with the meaning of a rapid quenching from the liquid state., The splat-cooling techniques have produced large numbers of new structures, which are expressed in terms of metastable phases,3 concentrated solid solutions,4 amorphous phases,5&apos;6 new phases,7 and so forth. Nearly all previous studies have concentrated on the physical properties; i.e., crystallography, structure, electrical resistivity, magnetism, and so forth, of the splat-cooled metals and alloys. The mechanical strength of splat-cooled metals and alloys has hardly been investigated except for some recent work by MOSS&apos; on A1-V alloys. The principle common to all experimental techniques developed to obtain very rapid quenching rates is based on the heat transfer by conduction. Liquid must be in good thermal contact with a substrate of high heat conductivity. Both of the published devices known as the "gun" and the "piston and anvil" techniques suffer from certain shortcomings. For example, the specimen obtained by the gun technique is very small and flaky, and hence inadequate for mechanical properties measurements. On the other hand if the material is forced to yield a continuous speci- men by the piston and anvil technique, it is probable that some plastic deformation occurs during the quench. A novel method for rapid quenching of a liquid metal or alloy, the "torsion-catapult", has been devised by Roberge and Herman9 at the University of Pennsylvania. In the apparatus the melt is thrown out of a curved furnace by a catapult and impinges on a copper substrate. The apparatus has the advantage of producing a continuous foil which is relatively large in size and of a quality suitable for the measurements of mechanical properties. The quenching rate is estimated to be of the order of l05 to l06 ºC per sec, (comparable to rates achieved by the piston and anvil technique). In selecting an alloy to be studied we were made aware of the fact that gold was believed to be "insoluble" in in and consequently age hardening in the A1-Au system appeared to be interesting. Quite recently Heirnendahl13-15 revealed that the solid solubility, as determined by transmission electron microscopy, was 0.3 wt pct Au at 640°C and 0.25 wt pct Au at 600°C, decreasing with decreasing temperature. In an A1-0.2 pct Au alloy after quenching from a solution treating temperature of 600°C the yield stress was 2 kg per sq mm, and it increased up to 6 kg per sq mm after aging for 1 to 10 hr at 200°C. The precipitation occurred in the form of platelike particles mainly on (100) matrix planes. The intermediate phase n&apos;, the equilibrium phase n (AuAl2), and lattice relationships between both precipitates and the matrix were also investigated by electron microscopy. One of the purposes of the present research is to determine whether or not the solid solubility in this system, in which gold has a very small solubility in

Jan 1, 1970

By W. A. Backofen, G. Y. Chin, W. F. Hosford

The ductile fracturing process was studied in single-crystal and poly cvystalline aluminum deformed in tension over a temperature range from 295° to 4.2°K. At temperatures as low as 77°K, the fracture of "inclusion-free" material, including zone-refined aluminum, was by rupture (-100 pct RA). At 4.2 OK, fracture was brought on by adia-batic shear. Metallographic examination did not disclose any voids or slip-band microcracks, thus negating for inherently ductile metals any mechanism of void nucleation by vacancy condensation or of cracking due to dislocation pile-ups. In Izigh-purity aluminum not treated to be inclusion-free, fracture at temperatures as low as 45°K was of the double-cup type and a result of void formation. The reduction-of-area decreased as temperature was lowered, corresponding to the earlier appearance of voids. Such behavior was rationalized in terms of a larger increase, with decreasing temperature, in the .flow stress relative to the strength of the inclusion-matrix interface. Evidence for low-temperature adiabatic shear was found in discontinuous flow at 4.2"K, in the transition to a localized shear fracture at low temperatures, and in the suppression of shear fracture with an elastically hard pulling device. A simple analysis for the initiation of adiabatic shew permitted a general correlation of the various contributing factors. It has been pointed out that the duration of shear depends upon effective mass and elastic stiffness of the deformation system. IT has long been recognized that fracture* may Throughout this paper, the term "fracture" is taken to mean any process that results in the separation of a material into two (or more) parts. Thus rupture as it may be encountered in a tension test leading to 100 pct reduction-of-area is included in this category. occur in a ductile mode, and that the process can be of great practical as well as general interest. Much information about ductile fracture has also been accumulated over this period, but only recently has an understanding of mechanism begun to appear. Ludwik,&apos; in 1926, first reported fracture in a tensile specimen starting with a central crack in the necked section. Since then, other studies have disclosed that such cracks may form by the coalescence of voids nucleated in this region where hydrostatic tension is highest.2-4 Rogers and Crussard et al.&apos; have emphasized void formation and reori-entation along localized shear bands as a mode of crack propagation. pines6 has considered the tensile rod as a bundle of fibers joined by weak interfaces, which subsequently separate to allow individual fiber contraction. The notion of cavity growth and coalescence by purely plastic processes was discussed by Cottrell: who added that the tensile reduction-of-area ought not to be sensitive to temperature. On the other hand, it has been observed that the reduction-of-area is greatly increased if tests are carried out at high temperaturesa or under high hydrostatic pressure.&apos; Fracturing anisotropy in wrought products lends support to the idea of void formation from preexisting flaws strongly aligned by earlier processing.&apos;&apos;-l2 There is evidence that many voids result from the fracturing of inclusions or separation at the inclusion-matrix interface Another possibility is that voids grow out of pore volume produced in the initial solidification and never fully removed in later working. In general, a structure 3f particles, pores, and weak interfaces can be expected, at least in materials of engineering interest. Vacancy condensation has been suggested as an alternative mechanism of void formation for materials considered to be inclusion-free.13 Yet experience has shown that tensile reduction-of-area increases with purity, to the extreme of rupture as so often observed in single crystals. Adiabatic shear has an important bearing on ductile fracture. It occurs when the decrease of flow stress, as a result of local temperature rise from heat generated during straining, becomes larger than the increase due to strain and strain-rate hardening. As demonstrated by experiments on punching of plates,14 a large temperature rise may be brought about by rapid straining. Adiabatic flow as a result of the high strain rate reached in an ordinary tensile specimen just prior to separation may account for the cone formation in cup-and-cone fracture;14 evidence of such local heating has been presented.15 For geometrical reasons, however, pure sliding along the conical surfaces is unlikely, and separation under tensile forces is probably an important accompanying feature of the shear.7 In deformation processing operations, a high shear-strain rate may exist at boundaries between plas-

Jan 1, 1964

By H. I. Aaronson, C. Laird

Although the past results of X-ray experiments indicate that the broad faces of 0&apos; plates are coherent with their matrix, dislocations lying in arrays have frequently been observed at these boundaries by transmission electron microscopy. Critical experiments employing the latter technique have been carried out in order to determine the origin of these dislocations. It is concluded that 8&apos; plates are essentially coherent with the matrix at their broad faces throughout the aging temperature/time envelope studied. Virtually all of the dislocation arrays observed are deduced to have been formed by plastic deformation accompanying transformation. The proportion of dislocations arising from convexity of the plates is shown to be negligible by comparison with that from plastic deformation. At the higher aging temperatures, a[001] dislocations appeared in moderate numbers. These dislocations were traced directly, however, to the ledgewise dissolution of 0&apos; occasioned by the formation nearby of 0 crystals. On the other hand, since there is a parametric difference normal to the broad faces of the ?&apos; plates, mismatch dislocations do form at their edges. A previous conclusion that these dislocations have Burgers vectors of type a[001] was confirmed directly. The edges of 0&apos; plates were observed to develop octagonal shapes when growing, but circular shapes during dissolution. 1 HIS paper presents the results of an investigation of the interfacial structures of plates of the transitional phase, 8&apos;, formed in an A1-4 pct Cu alloy. In a companion paper, Part 11, the effects of these structures upon the migration kinetics of a:?f boundaries are reported. This work is pa.rt of a general program designed to establish the basis of precipitate morphology. The present authors in Al-Ag,1 and whitton2 previously in U-C alloys, have used transmission electron microscopy to examine directly the vander Merwe3-6 networks of dislocations anticipated7 to compensate the small amount of lattice misfit normally founda at the broad faces of Widmanstatten plates. Since the broad faces of 0&apos; plates are considered to be perfectly coherent with the corresponding habit planes in the a matrix,&apos; no dislocations should be present at these faces. Many reports have been published, however, giving evidence to the contrary.10-18 The primary objective of this investigation was therefore to ascertain the nature of these dislocation structures. An attempt to do this is described in the first three sections of this paper. Inspection of the matching of the a and 8 &apos; lattices at the orientations of the 0:0&apos; boundary corresponding to the edges of 0&apos; plates raises the possibility that these edges may be made up of rather closely spaced edge- type misfit dislocations oriented so as to be sessile with respect to the lengthening or shortening of the plates. Since this structure should severely inhibit migration of the plate edges (Ref. 7, Part II), a situation not originally anticipated,&apos; an experimental determination of the interfacial structure of the edges of 8&apos; plates was clearly in order, and is reported in Section III. Those aspects of the experimental procedure applicable to both Parts I and I1 are presented in the next section. Specific procedures applicable to individual aspects of each investigation, and also the relevant surveys of the literature, are then individually reported in the appropriate sections. I) GENERAL EXPERIMENTAL PROCEDURE The material used in both parts of these studies was the same as that of a previous investigation:" strips of A1-3.93 pct Cu, 0.009 in. thick, prepared as before, solution-annealed at 548°C for 6 hr, and quenched. Details of subsequent aging, and in some cases deformation treatments, are given in the Experimental Procedure sections of the individual parts of both papers. Specimens of the heat-treated strips were electro-thinned as beforeLg and examined in a Philips EM 200 microscope equipped with a goniometer stage. A commercial hot stage, of the grid-heater type and capable of * 30-deg tilt about one axis in the plane of the specimen, was also used for kinetic studies. The usual precaution of calibrating for the additional heat supplied by the electron beam was taken.19 A 16-mm cine cam-I era mounted outside the viewing window was frequently used to record the transformations. Conventional selected-area diffraction and dark-field viewing techniques were used to identify the precipitates in the foils. Normal bright-field images corresponding to two-beam diffracting conditions or dark-field images were employed to characterize the dislocations observed at the interfaces of the precipitates. The application of these techniques to the study of an interphase boundary, and the interpretation of the images,20&apos;21 has been fully described in a previous paper.&apos;

Jan 1, 1969

By R. M. Hudson

The removal of nitrogen from a nitrogenized low-carbon sheet steel that contained 0.011 wt pct N was determined during heat treatment in Hz-N, mixtures. TIze process followed a first-order rate law; that is, plots of the logarithm of nitrogen content in steel were linear with the time of treatment at a given temperature. The rate of removal increased with an increase in temperature from 900" to 1300°F. By 1400°F the rate in dry hydrogen had decreased to a value intermediate between the rates at 1200" and at 1300°F; in wet (2.47 vol pct water vapor) hydrogen the rate at 1400°F was less than the rate at 1300°F and nearly the same as the rate at 1200OF. The rate at a given temperature increased as the 3/2 power of hydrogen concentration in the atmosphere. While wet atmosplzeres were generally more effective than the corresponding dry atmosplzeres, the effect of water vapor was much less pronounced than the influence of hydrogen content. NITROGEN is the principal agent in the strain aging of ferrite, the effect of carbon being secondary.&apos; To eliminate the return of the yield point after straining and aging, it is claimed2 that the amount of nitrogen in solution in steel must be reduced to 0.0002 wt pct. Strong nitride-forming elements (titanium, vanadium, zirconium, and aluminum) can act to eliminate strain aging by combining with nitrogen. It is extremely difficult to decrease the nitrogen content in commercial steels to the low level required by conventional coil annealing because of the poor contact between the strip surface and the reactive atmosphere. However, a variety of gas-metal reactions can be effected by use of the open-coil annealing method,3 in which the metal surface is fully exposed to the atmosphere. With this possibility in mind, the Applied Research Laboratory has studied the influence of time, temperature, and atmosphere composition on the removal of nitrogen from low-carbon sheet steel. MATERIALS AND EXPERIMENTAL WORK Samples from a commercial nitrogenized low-carbon steel (0.010 in. thick) in the cold-reduced condition were used. The chemical composition of this steel is given in Table I. The gas mixtures used are listed in Table 11. The moisture content in the "wet" annealing atmospheres was controlled at a +70°F dew point (2.47 vol pct water vapor) by passing the gas mixture through a glass tube packed with a solid mixture of 10 pct anhydrous oxalic acid and 90 pct oxalic acid dihydrate held at 127°F; this technique has been described previously.4 For "dry" atmospheres, the gas mixtures were passed through a cold trap immersed in liquid nitrogen. A hinged-top Hevi-Duty electric furnace was used with a Vycor-glass furnace tube. When the furnace was at the desired temperature, the gas mixture was passed through the furnace at a flow rate between 1.1 and 1.2 cfh; coupons (size 3 by 3/4 in.) of the steel were pulled into the center of the Vycor-glass

Jan 1, 1964

By J. E. Campbell, G. D. Calkins, N. M. Ewbank, M. Pobereskin, A. Wesner

GRINDING for size reduction affects the economics of many processes and products. It is essential as the first step in many industrial processes and is also a finishing step for materials with properties depending on particle size, such as talc, cement, and silica sand. Intermediate and fine grinding are vital operations in the U. S. cement industry, which is producing more than 250 million bbl of cement per year.&apos; Wear of the grinding media is a large part of the grinding operation cost. Problems encountered in grinding cement are so complex that evaluation of efficiency and economy of grinding media is difficult.2 It has been especially difficult to evaluate the relative effectiveness of different types of balls because there are no good testing techniques. Many other industrial operations can be evaluated on a laboratory scale with reasonable accuracy. This does not hold true for evaluation of grinding balls. The consistent results obtained in a laboratory test under a given set of conditions are not always borne out in field application. Rough evaluations of the effectiveness of various compositions and types of grinding balls have been made in the field by using a full charge of one type in a mill and comparing the production record with another run using another type of ball. This method is time-consuming and not very precise, as the second run may not have been carried out under identical conditions. Laboratory-scale tests, on the other hand, have yielded inconclusive results, and many investigators have turned their attention to the development of a field testing technique. Field testing small sample lots of grinding balls has been impractical because it is difficult to identify and recover the test specimens from the grinding mill, and individual groups of balls that have undergone different heat treatments can not be separated.".4 To overcome these difficulties, previous investigators have identified the balls by distinctive marks, notches, and drilled holes, but this procedure has three serious drawbacks: 1) Grinding characteristics and quality of the steel balls may be affected. 2) Physical markings may be worn away in the grinding process, especially during a prolonged run. 3) Recovery from the bulk of the charge will be extremely difficult because the markings are hard to see and may be masked by a coating of the product. To circumvent these difficulties, a radioactive-tracer technique was proposed for recovery and separation of steel grinding balls and subsequent evaluation of the various compositions of the balls. The proposed technique involved five basic operations: 1) Thermal-neutron irradiation activation5 of each group of test grinding balls to a different level of specific radioactivity. 2) Addition of groups of radioactive steel-ball specimens into a ball tube mill. 3) Recovery of radioactive steel-ball specimens from the bulk of the mill charge. 4) Separation of the various groups by their specific radioactivity. 5) Evaluation of actual grinding ball wear. Before any physical tests were performed, required neutron irradiation intensity and time were calculated. Probable composition of the steels to be used was ascertained. An examination was made of the radioactive nuclides8 to be formed which would contribute measurably to the radiation level immediately after irradiation and during the test operation. The radioisotopes formed, their types of radiation, and their half lives are listed in Table I. Of these radioisotopes only iron-59 and chromium-51 were significant for the actual wear test. The intensity of radiation that could be detected by a Geiger counter when the test was completed was the basis for the minimum activation level established. The intensity of radiaton that could be safely handled at the beginning of the test was the basis for the maximum activation level, although this was not considered a major problem. Ten groups of grinding balls of various composition and/or surface or heat treatment were to be tested. One group was designated for the minimum irradiation time. The remaining groups were designated for irradiation periods that increased by increments of 33 pct from that of each preceding group. This difference was considered enough for separation and identification of the groups by comparison of specific activity. Potential Hazards: Possible radiation hazards that might be encountered during this experiment were evaluated for the three important phases: 1) the radiation hazard of placing balls and removing them from the mill, 2) contamination of the product cement by radioactive material worn from the balls, and 3) contamination of the steel by the radioactive balls left in the mill. The radiation intensity expected from the whole group of radioactive balls was calculated to be 250 milliroentgen per hr at 1 ft. This meant the balls would require special shielded packaging and warning labels on the shipping containers. In a radiation field of 250 mr per hr a man can work for 1 hr without exceeding maximum permissible weekly exposure. Since the balls could be dumped into the mill in a matter of seconds, relatively little radiation exposure was anticipated at this stage of the operation. If the weight loss in the balls was 7.7 pct per month and the cement feed through the mill was

Jan 1, 1958

By J. B. Hess, C. S. Barrett

TO reach equilibrium between different phases in cobalt-rich alloys requires prohibitively long annealing cobalt-richalloystimes when temperatures are below about 700°C. The fact that a transformation from face-centered cubic to close-packed hexagonal readily tered takes place at temperatures below this in the cobalt-rich solid solutions is not an indication that thermally activated processes occur at an appreciable rate, for the transformation is well established as martensitic in nature. Wide divergence between heating and cooling experiments and high sensitivity to prior heat treatment make it difficult to judge temperatures of equilibrium between the phases.&apos; One object of the present work was to see if the information object of on the relative stability of phases could be gained by substituting plastic deformation for thermal agitation. Procedures were worked out that led to the determination of a diffusionless type of phase diagram, which represents the temperature of of phase equal stability for phases of the same composition, and the technique was applied to the Co-Ni system. Another object of the work was to see whether or not deformation would generate frequent stacking faults when these were thin lamellae of quentstackingfaultsa phase having higher free energy than the parent phase. The alloys were prepared in 80 to 100 g melts from cobalt (with metallic impurities estimated spectrochemically as follows: Ni, 0.05 pct; Fe, 0.001 pct.; Mg, Si, Cu, Cr, Al, < 0.001 pct) and Mond Car-bony1 nickel (with Fe, 0.05 pct; Si, 0.003 pct; C, 0.61 pct.; Cu, 0.001 pct; Co, Cr not detected, < 0.01 pct). The metals were melted in pure Al2O3 crucibles. An atmosphere of argon, that had been purified by passing over hot magnesium chips, was used for the alloys that, by analysis of the portions of the ingots actually used, were found to contain 15.3, 25.7, and 35.0 pct Ni, and vacuum melting (after degassing) was used for those containing 29.4 and 31.5 pct Ni. After induction melting the alloys were allowed to solidify in the crucible, and slices % in. thick x ½ in. in diam were annealed 12 hr at 1350°C for homogenization. These same specimens were used throughout the series of experiments, with annealing treatments of 4 hr at 900°C in purified hydrogen followed by furnace cooling, alternating with the deformation and X-ray tests discussed below. Results Spontaneous transformation was observed on cooling to room temperature in all alloys containing 29.4 pct Ni or less and by cooling the 31.5 pct alloy to — 195°C but was not observed in the 35 pct alloys after cooling to —195°C. These results are in satisfactory agreement with the cooling experiments of Masimoto.4 From these data it is clear that the temperature of beginning transformation M,,, drops to 20°C with the addition of about 30 pct Ni. The test for spontaneous transformation was metallographic. Specimens were thermally polished by annealing 10 hr in hydrogen at 1350°C, then furnace cooled; if trans- formation had occurred there were relief effects visible on the thermally polished surfaces. These markings were narrow straight lines, usually resolvable at high magnification as clusters of fine lines that resembled slip lines. It was concluded that they resulted from displacements on (111) planes, for the number of directions in individual grains often reached but never exceeded four, and lines could always be found parallel to the thermally etched (111) boundaries of annealing twins. The markings were thus consistent with the idea that the transformation occurs by (111) plane displacements (Shockley partial dislocations moving on (111) planes). This was further confirmed by X-ray tests for stacking disorders. Using an oscillating crystal technique previously employed to detect strain-induced faulting in Cu-Si alloys," streaks indicative of the stacking faults were looked for and found on X-ray films of the spontaneously transformed 25.7 pct Ni alloys, as expected by analogy with Edwards and Lipson&apos;s results on pure cobalt." The streaks were much intensified after rolling at room temperature. Transformation induced by plastic strain was investigated as a function of alloy composition and temperature of deformation. A series of tests was made to determine suitable straining and X-raying techniques. Filing was found inferior to abrasion in converting cubic samples to hexagonal, and abrasion was less effective than peening in producing smooth unspotty Debye rings in the X-ray patterns. Because the diffraction lines were broad, Geiger-counter spectrometer records of filings were less sensitive in revealing small amounts of transformed material than X-ray patterns recorded on films in a small diameter camera. After these exploratory tests the following methods were adopted. Specimens that had been annealed at least 4 hr at 900°C and furnace cooled were mounted in a block of aluminum, brought to temperature, and peened thoroughly with a mullite pestle preheated to the same temperature. The specimens were then quenched to room temperature. In peening, a circular area of % in. diam was given 500 blows. A few control tests showed that an additional 1000 blows did not detectably change the proportions of the phases present. The amount of transformation was judged by X-ray reflection patterns from the peened surface, using the innermost four lines of the cubic and the hexagonal patterns with filtered CoKa radiation,

Jan 1, 1953

By A. Totani, S. Nakajima, H. Okazaki

The phase diagram for the SnTe-SnSe system has been studied in the temperature range from 300° to 900°C by differential thermal and quenching techniques. The X-ray measurements were made on quenched specimens. High-temperature diffraction was also made to study the phase transition in SnSe. The system is proved to be of a eutectic type in which no intermetallic compound exists. The eutectic point is at the composition SnTeo.55 Seo.45. the eutectic temperature being 755°C. Solid solubility limits are SnTeo.6Seo.r and SnT eo. 3s Seo.6s at the eutectic temperature, and change almost linearly to SnTeo.aaSeo.lz and SnTeo.18 Seo.az as temperature decreases to 300°C. It was shown that the SnSe phase has a phase transition of the second order at about 540°C and that the transition temperature decreases with increase of the SnTe content. THERMOELECTRIC properties of tin telluride (SnTe) and tin selenide (SnSe) have been studied extensively in recent years. The variation of physical properties with composition could be of interest if these compounds form an appreciable crystalline solution. The purpose of present investigation is to confirm the formation of crystalline solution or intermetallic compound, if any, and to establish the phase diagram for this system. The crystal structure of SnTe is NaCl type with a cubic unit cell1 (a = 6.313A). The crystal of SnSe having an orthorh2mbic unit cellz (a = 11.496, b = 4.1510, and c = 4.4437A) is isomorphous with tin sulfide (SnS) which has a distorted sodium chloride structure. It has been known that SnSe has a phase at at 540°C; the transition has been assumed to be of the second order. As far as we know, only two studies on the SnTe-SnSe pseudobinary system have been reported. The conclusion obtained in these papers is that, in the composition regions near SnTe and SnSe, the system forms a crystalline solution of the SnTe structure and the SnSe structure, respectively, and that, in the intermediate region, both phases coexist. However, neither the variation of the solid solubility vs the temperature nor the liquidus and solidus were investigated. Hence present writers have attempted to determine the phase diagram of the system by differential thermal analysis (D.T.A.) and X-ray diffraction. EXPERIMENTAL Sample Preparation. Starting materials, SnTe and SnSe, were prepared by the direct fusion of commercially available high-purity (99.999 pct) elements. Stoichiometric amounts of each couple Sn-Te or Sn-Se were weighed into a clear fused silica ampule. After evacuation to a pressure below 10-3 mm Hg, the am- pule was sealed, and annealed at 900°C for 5 hr. The melt was quenched in water. X-ray analysis confirmed the formation of a single phase of SnTe or SnSe. The other samples, SnTel-,Sex were synthesized from these SnTe and SnSe by mixing them in the required ratio, followed by annealing at 900°C and quenching. These samples were used directly for D.T.A. For X-ray measurements, samples were annealed at 700°, 600°, or 500°C for 100 hr or at 300°C for 150 hr, and then quenched in water. It was found that the lattice constants of the SnTe phase annealed for 150 hr at temperatures above 500°C did not differ from those annealed for 100 hr at the same temperatures. However the X-ray phase analysis showed that at 300°C the annealing for 150 hr was necessary to attain a true equilibrium state. D.T.A. The solid-liquid equilibrium temperature was determined from D.T.A. measurements. The sample was sealed in an evacuated silica tube and molybdenum powders sealed in an another tube were used as a reference material. The sample and the reference tube were placed in a nickel block and were heated from room temperature to 900°C at a rate of 3°C per min and then cooled down at the same rate to 600°C. Thermocouples for these measurements were Pt-Pt. Rh (10 pct) and the error of temperature measurements was within + l0C. D.T.A. curves were obtained on a two-pen recorder and an automatic controller (PID type) was used for the program of heating and cooling. When temperature reaches the solidus from the low-temperature side, there appears an endothermic peak. The solidus temperature was determined by extrapolation of the straight portion of the starting flank of this peak to the base line. In a similar way, the liquidus temperature was determined from an exothermic peak on D.T.A. cooling curve. In the case of supercooling, if any, its degree can be estimated from the magnitude of the abrupt temperature rise. X-Ray . X-ray powder patterns were taken by a diffractometer using CuK, radiation. Since the SnSe crystal is cleaved easily, the powders become flaky when SnSe-rich samples are ground in an agate

Jan 1, 1969