By Gábor Mucsi, József Faitli, Imre Gombköto, Sanjay Kumar, Zoltán Molnár, Balázs Ráczkevi, Ádám Rácz

"Generally, fly ash particles are very fine (< 100 ?m), mainly spherical and glassy materials form an outer shell on it. This paper deals with the laboratory investigation of ground fly ash based geopolymer. This material can be applied in many fields, mainly in the construction industry, e.g. non-structural elements, concrete, pavements and products, containment and immobilization of toxic, hazardous and radioactive wastes, advanced structural tooling and refractory ceramics, and fire resistant composites used in buildings, etc. The preparation of fly ash using high energy density milling is presented. Systematic experimental series were carried out in order to optimize the preparation process. The particle size distribution (LPSA) and structure of fly ash (FTIR) and the uniaxial compressive strength ,the permeability and structure of geopolymer product, furthermore the rheology of geopolymer paste were investigated. The product properties were studied as a function of the fly ash fineness. As a result of the investigation the relationship between the grinding circumstances, the ground material properties and the geopolymer characteristics was identified. It was found that the above mentioned physical properties of the geopolymer strongly depend on the grinding process."

Jan 1, 2014

By James C. Bayles

The ideal pressure-tube is obviously the one which combines the greatest strength with the least weight of material consistent with the uses for which it is designed or employed. The inside of the pipe is the first concern of the engineer. It should be cylindrical, smooth, and of the requisite capacity for the purpose in view. It should be in lengths as great as can be oonveniently handled, so that the couplings may be as few as possible. With the walls of the tube the engineer has no further occasion to concern himself than to make sure they are adequate to carry the internal and external pressures to which they will be subjected. It is as true of a pipe as of a truss, that when it is strong enough to give the requisite factor of safety, nothing is gained by having it stronger. Anything more than this means dead weight, which has to be paid for many times, first as material, and again and again in the costs of transportation and handling, until it reaches its place in the trench or on supports. In use it must be and remain tight against all leakage, and must sustain whatever is placed over or upon it, or suspended from it, without deformation or injury. Finally, in addition to meeting all the immediate requirements of service, it must possess qualities of durability which warrant a reasonable expectation of a long life of usefulness. The wise engineer no longer regards it as reasonable to depend upon mere bulk of its own material for the protection of a metal as readily impaired or destroyed by oxidation as iron or steel. The metal must have a coating which will be and remain impervious and indestructible. When all these conditions are met, we have as near an approach to the ideal tube as can be attained with the materials now available for their manufacture. Steel wed constructively, to the best advantage, meets these requirements most perfectly. Gold alone would do it better. If we search through the whole list of metals and alloys we find nothing available which so perfectly meets the requirements as a pipe material as steel. Mr. Hamilton Smith, Jr., in a paper on the expedients adopted on

Jan 1, 1891

By Arkady Senchenko, Yevgeny Zhagun, Yury Kulikov, John Starkey

"The paper contains description of a new project in Russia - gold-processing plant at Aleksandrovskoye deposit (start up in September, 2013). The paper includes a brief description of plant flowsheet, data for material composition and technological properties of ore, as well as information about the achieved parameters of ore processing over the first months of plant operation. The project is interesting because a new semiautogenous mill and a ball mill were purchased on the basis of SAGDesign Consulting Group recommendations after the testing of ore samples characterizing the deposit according to specific years of operation. The plant has relatively small design capacity - 750 000 tpa, but nevertheless is the biggest gold-processing plant in the territory of Zabaikalsky region. Major valuable component in the ore is gold, silver is recovered as a by-product. The ores are very hard to grind. The design grinding flowsheet includes a semiautogenous mill operating in closed circuit with a screen, and a ball mill operating in a closed circuit with hydrocyclones (SAB). Process technology includes gravity processing and flotation with subsequent cyanide leaching of concentrates. Mill operation analysis and conclusions about the compliance of the achieved values to target ones are shown, as well as the accuracy of SAGDesign method when applied to very hard ores of Aleksandrovkoye deposit are presented in this paper. Basic directions of technological flowsheet optimization are also given."

Jan 1, 2014

By Robert Roby

The Mouat copper-nickel deposit in Stillwater County, south-central Montana, was examined by Paul T. Allsman, an engineer of the Bureau of Mines, in 1939. Because of the strategic importance of nickel, a project was executed by John East, Jr., J. J. Naughton, and E. W. Newman, engineers of the Bureau, to further delimit some of the copper-nickel sulfide-bearing bodies that had been discovered by the Anaconda Copper Mining. Co. in 1937 and to investigate the central part of the deposit, which had not been drilled previously. This report is based largely upon the results of the. Bureau of Mines investigation and the results of exploration by the Anaconda Copper Mining Co. In addition, a brief description is given of some other copper-nickel sulfide-bearing deposits along tho Stillwater Complex.

Jan 1, 1949

By SHANTAE LEE, ELAHEH TALEBI, Frank A. Drews, W. Pratt Rogers

Fatigue in mining operations is a serious issue and a significant contributor to incidents and accidents. While mine operators are using or introducing new technology to monitor operator fatigue, there is little work that focuses on the subjective experience of fatigue and the use of fatigue monitoring technology. To investigate this issue, eight focus groups with a total of 44 operators of heavy haulage equipment working for two mining companies in the Mountain West of the USA participated in 1-h focus groups. The topic of the focus groups was the experience of operator fatigue and issues surrounding fatigue at the workplace. The results of the content analyses suggest that operators are well aware of the signs of fatigue, and that they understand the severity of these signs as well. In addition, they are aware of the effect of fatigue on driving performance and are using a wide range of methods to manage fatigue. Finally, based on participants’ assessment, current fatigue monitoring systems lack face validity and reliability and are perceived as not being effective. The results of this study emphasize the importance of a socio-technical systems perspective in the context of miner health and safety management. Only such a comprehensive perspective can result in improvements that are sustainable.

Jun 17, 2020

By Walter Hermülheim, Klaus-Dieter Beck

In German hardcoal mining approximately 1 or 2 cases of spontaneous combustion are recorded per 10 million tonnes of saleable output. In approximately every 20th spontaneous combustion case, CH, is ignited. By the example of a fire caused by spontaneous combustion on Friedrich Heinrich colliery, an overview on the measures taken for firefighting and explosion prevention is given. These measures comprise (in sequential order) - early fire detection by CO-monitoring, - gob-sealing measures against ventilation air leaks, - full-space inertization of the coalface subsequent to a CH,- deflagration, - installation of a target inertization of the caved-in gob under the protection of the full-space inertization, - re-opening of the fire zone and reestablishment of the ventilation-air current, - completion of the salvaging work with continued target inertization of the caved-in gob and further sealing measures (monolithic packing), - sealing of the coalface after salvaging. The measures described allowed gain of control of a safety- critical (because close to the face) gob fire caused by spontaneous combustion, in spite of a CH, deflagration, within few days only, and salvaging of equipment from that coalface and start-up of the follow-up coal-face on schedule. The measures taken as well as the experiences gained allow deduction of general safety criteria for fighiing of gobfires caused by spontaneous combustion, and for controlling the explosion risk. e.g. - warning and alert thresholds for early detection of fires, - criteria for spotting of the zone of fire, - rules for tightening caved-in gobs, - thresholds for the retreat of firefighting crews from the vicinity of the zone of fire, and for starting ineiization, - considerations for positioning of and strength requirements for stoppings with/without inertization, - flow-by-volume adjustment of inertization, - safety rules for work with respiratory apparatus in the inertized zone, - safety rules for the re-opening of zones of fire. The considerations end up in the conclusions that the duration in terms of months of the classic cycles of sealing, waiting, and reopening can nowadays be reduced to a few days only by purposeful combination of full-space inertization and locally confined tar- get inertization of the gob area. The earlier high risks incured by the mine resuce squads en- trusted with sealing of zones of mine fires under explosion hazards can be reduced by the method described, provided the safety regulations are conformed with. In this way, intertizing contributes substantially to reduction of down-time caused by mine fires, to preservation of recoverable parts of the deposit, and to improved safety of the fire-fighting crews.

Jan 1, 1997

By M. J. Hordon, M. A. Wright

ReCENT work has indicated that the substantial decrease in the rate of fatigue crack propagation for aluminum observed below a critical vacuum level can be attributed to the depletion of oxygen or water vapor from the vicinity of the fatigue crack opening.&apos; At reduced gas pressures, generally below 10-2 Torr with fatigue strain amplitudes in the range *1 to 2 x 10-3 and cyclic loading rates of 25 to 50 cps, estimated rates of oxide or hydroxide monolayer adsorption on newly formed crack surfaces can fall behind the actual rate of crack extension. Changes in the critical pressure required for the transition in fatigue behavior with changes in temperature, strain amplitude, and cyclic frequency can be interpreted from variations in the adsorption and crack growth rates.&apos;" Although the adsorption model generally appears to explain the enhanced fatigue resistance of reactive metals in vacuum, the specific adsorbing gas species and nature of the adsorption mechanism are uncertain. In addition to the direct dissociation and adsorption of O2 on the metal surfaces,3 the dissociation of H20 and subsequent adsorption of H ions have been advanced for aluminum alloys.4 The present note describes some measurements of the fatigue behavior of 1100 aluminum in reduced partial pressures of specific gases including O2, H2O, and H2 in order to provide additional experimental data. Cantilever-type specimens of 1100-H14 aluminum were fatigued in cyclic reverse bending at constant strain amplitude using a multispecimen vacuum apparatus and procedure described previously.&apos; After initial vacuum evacuation to 1 x 10-7 Torr, the appropriate gas species was bled into the system through a calibrated leak valve. The input rate was adjusted to maintain the desired pressure level under continuous evacuation, thus minimizing possible changes in gas composition during testing. High-purity input gases including 99.9 pct O2, 99.999 pct H 2, and water vapor from triply distilled H 2 O were used to provide residual pressures. Trace amounts of contaminant species were limited by passing the Oz and H 2 input gases through liquid-nitrogen-cooled copper coils prior to entry to the test chamber. Care was taken to repeatedly flush the gas lines and valves before testing to minimize the effect of adsorbed contaminants. Residual gas pressures in the range 10-6 to 5 x x3 Torr were monitored by an NRC ionization gage corrected for each gas species. In the higher-pressure range, 5 x 1CT3 to 5 x 10&apos; Torr, an NRC alphatron gage was used. In operation, eight simultaneous fatigue tests were conducted at a constant strain amplitude of *1.2 x 10 at cyclic bending rates of 25 and 50 cps to give an average fatigue life of 6.5x 105 cycles-to-fracture at standard atmosphere and 3.3 x 106 cycles in 1 x 10"7 Torr vacuum. Representative results for the effect of residual O2, H2O, and H2 contents on the fatigue life are shown in Fig. 1 for tests performed at 50 cps. It is apparent that the presence of either O2 or H2O gas in the system at partial pressures greater than 10"3 Torr was noticeably detrimental to the fatigue life. In contrast, the enhanced fatigue resistance typical of high-vacuum environments was retained with pure H 2 through the pressure range up to 1 Torr. For partial pressures of H2 gas above 1 Torr, the fracture life noticeably decreased. The critical Hz

Jan 1, 1969

By W. M. Courtis

In compliance with the suggestion in Mr. Emmons&apos;s paper on the Genesis of Certain Ore-Deposits (Trans. xv., 125), that facts should be accumulated for study and future compilation, I wish to put on record, before the data are lost, a section of the Animikie series of rocks and the vein-phenomena exposed by the explorations at the Duncan mine, Port Arthur, Thunder Bay, Lake Superior. This may serve as a supplement to my paper on this district (Trans. v., 473). I trust this information will not be without interest at. the present time. The recent discoveries of very rich silver-ores at Rabbit and Silver Mountains, on the same belt, have brought the district once more before the public; and a study of the facts here set forth may assist some fellow-engineer in the determination of the value of property offered for sale in this neighborhood. The vein at the Duncan mine was tested to a depth of over eight hundred feet by shaft and drifts, and to nearly a thousand feet with

Jan 1, 1887

By Paul H. Johnson

The CH Leaching process is a new, more sophisticated, form of gold, silver, uranium and sulfide copper heap leaching wherein each layer of a multi-layered heap is divided into a number of independent cells, each of which are successively formed and leached in the top layer of the heap to their maximum economic recoveries, and then rinsed and sealed from further leaching. Triangular earth berms form the outside walls of the heap and a gridwork of rock-filled berms on top of the bottom pad form independent under- heap solution storage zones. The high degree of solution recirculation and staging that occurs in this process produces a relatively small volume of very rich pregnant solution. The cellular heap design and its mode of operation result in a uniform, intensive, long-term leach for all of the ore particles in the heap. Besides improved metal recoveries, the process appears to have several cost and operating advantages. In the CR2MR process, sulfuric acid and a soluble sulfide are added to a gold and/or silver pregnant leach liquor to precipitate most of the contained silver, mercury, copper, etc. as sulfides at a pH below 2.5. The other product of the reaction is solubilized HCN. Following a liquid-solid separation step, cyanide is regenerated in the supernatant solution by raising the pH to a level above 9.0. This process regenerates a portion of the cyanide used in the leaching step, removes contaminant ion species (silver, copper, mercury, etc.) from the leach solution and, in a subsequent step, recovers the gold in an enriched form. It is believed that substantial cost savings may be experienced by the use of this process in some gold and/or silver leach systems.

Jan 1, 1984

By W. G. Lidman, H. J. Hamjian

&apos; I HE fabrication of many materials from powders involves a sintering process. A mass of powder will sinter because of the excess free energy over the same mass in the densified state caused by the higher total surface area of the powder. An understanding of the kinetics and mechanism of sintering should assist in improving the properties of such materials. The present investigation conducted at the NACA Lewis laboratory deals with the sintering of chromium carbide. Dry sintering (sintering at a temperature below the melting point) was divided into two stages by Shaler:&apos; the first stage, during which the particles preserve much of their original shape and the voids are interconnected, and the second stage, during which densification occurs and the pores are isolated. The mechanism of forming interfaces between particles, or welding together of particles, has been investigated by Kuczynski2 and may be described by any one or a combination of the following mechanisms: viscous flow, evaporation and condensation, volume diffusion, or surface diffusion. The mechanism by which pores are closed or eliminated (densification) during sintering, is of interest. Grain growth observed during sintering may be attributed to the variation in the surface energies of individual grains, causing some grains to grow at the expense of others. Grain boundary migration occurs presumably by a diffusion process, therefore the rate of grain growth would be expected to increase exponentially with increasing time and temperature. Thus, for practical sintering times of less than 1 hr, a certain minimum temperature may exist at which major structural and property changes will occur. Densification and kinetics of grain growth during sintering under pressure of chromium carbide were investigated to provide additional information which will aid in describing more accurately the sintering process and the mechanisms involved. This material was selected for this study because of the current interest in high strength, oxidation resistant refractory materials, such as carbides, which are sintered to produce solid, dense materials from powders. Sintering under pressure is a process where the heat and pressure are applied to the compact simultaneously, specimens for this work were prepared by sintering under pressure at different temperatures and for various time periods. Experimental Procedure Preparation of Specimens: Chemical analysis of the commercial chromium carbide used in this investigation was as follows: Cr 86.19 pct, C 12.14 pct, and Fe 0.2 pct. X-ray diffraction powder patterns gave characteristic diffraction lines of Cr3C2 crystal structure. Powder particle size was determined microscopically and the average initial particle size was 6 microns with 85 pct between 2 and 10 microns. Specimens sintered under pressure were formed in graphite dies3 heated by induction. Sintering temperatures were measured with an optical pyrometer by sighting into a 3/8-in. hole drilled 1 in. deep at the midsection of the graphite die. A load of approximately 1 ton per sq in. was applied to the powder. The die assembly was heated in 20 min to the highest temperature (2500°F&apos;) at which no increase in grain size could be observed, and less than 2.5 min were required to heat from this temperature to the maximum temperature (3000°F). Sintering temperatures and times for the specimens of this investigation are indicated in Table I. Analysis of Specimens: Specimens polished with diamond abrasives were etched to reveal the grain boundaries with a 1:1 mixture of 20 pct potassium hydroxide and 20 pct potassium ferricyanide heated to 160°F. Representative areas of each sample were photographed at 1000 diameters. The largest diameters of all well-defined grains were measured, but only the measurements of 15 of the largest grains were averaged in order to determine an index of grain size on the assumption that they were among the first to begin growth. Densities were determined from differential weighing of the samples in air and water. The reported density values are considered correct within ±0.01 g per milliliter. Results and Discussion Metal compacts have exhibited grain growth when sintered at temperatures about two-thirds of the absolute temperature of their melting point.&apos; Grain growth also occurs during the sintering of chromium carbide and is illustrated by the micrographs shown in Fig. 1. These micrographs were prepared from specimens sintered for 90 min at temperatures ranging from 1371°C (2500°F) to 1648°C (3000°F). Average grain size and density measurements of specimens investigated are presented in Table I. The relationship between grain size and sintering tem-

Jan 1, 1954

By P. -É. Boileau, S. Mandapuram, Shiping Ma, S. Rakheja

The absorbed power (PAbs) has been suggested as a better measure of human responses to whole-body vibration, since it relates to the cumulative energy dissipated by the body exposed over a given duration. Moreover, unlike the other measures, the PAbs can adequately account for the intensity of exposure. Although, the vast majority of off-road vehicles impose considerably severe vibration along the horizontal axes, the vast majority of studies on biodynamic response characterization consider only vertical vibration. Only a few studies have reported PAbs responses of the seated human body exposed to horizontal vibration and the major contributing factors [1]. This study aims to characterize the PAbs responses of seated human subjects to horizontal (uncoupled x- and y-axis) vibration as functions of the vibration intensity, subject mass, seat height and the, type of back support. Methods Experiments were conducted using a rigid seat with an adjustable backrest inclination and seat height. The seat was installed on a horizontal vibration simulator and the forces at the seat base and the backrest were measured by three-axis force plates. Two single-axis accelerometers were installed on the seat back and the platform, oriented along the axis of motion. The experiments were performed using three different seat heights (350, 390 and 410 mm), back support conditions (NB- no back support and sitting erect; Wb0- Upper body supported against a vertical back support; and WbA- back supported against an inclined backrest, while sitting relaxed) and three different magnitudes of broad band excitations in the 0.5-10 Hz frequency range (0.25, 0.5 and 1 m/s2 rms acceleration under x-axis and y-axis, applied independently). A total of 8 healthy adult male volunteers with total body mass ranging from 59.4 kg to 92 kg and aged between 21-51 years took part in the experiments. The subjects were seated with their hands in lap, and feet supported on the moving platform for each posture. Each measurement was repeated 2 times, while the data were analysed using a bandwidth of 50 Hz and frequency resolution of 0.0625 Hz. [ ] The data were analyzed to derive the absorbed power characteristics of the body at both seat pan and backrest interfaces, while the coherence among the measured forces and accelerations wer

Jan 6, 2006

By D. Govender

Theoretical flotation models suggest that there is a positive relationship between bubble-particle collision rates and turbulent kinetic energy dissipation. Fine particle flotation performance is generally enhanced by increased collision frequency and hence higher energy dissipation. Contrarily, increased turbulence in the rotor-stator region is related to higher detachment frequency of the coarser size range. Therefore, the optimal modes of recovery for the ?fine? and ?coarse? size classes are diametrically opposed. Industrial applications have previously confirmed that applying greater power to flotation slurries yields significant improvements in fine particle recovery. However, recovery of the coarser size class favors a different flotation environment. An improvement in the kinetics of the fine and coarse size classes, provided there is no adverse metallurgical influence on the intermediate size ranges, is obviously beneficial to the overall recovery response. Managing the local turbulent kinetic energy dissipation, and hence the power imparted to the slurry, offers the benefit of targeting the particle size ranges exhibiting slower kinetics. FLSmidth recently introduced the practical implementation of this concept. In principle, it decouples flotation regimes where fine and coarse particles exhibit preferential recovery. In the case of naturally aspirated machines (Wemco®), it is referred to as Hybrid Energy Flotation? and incorporates at least three phases: ? Standard flotation machines (standard energy input, rpm, rotor size/type) at the beginning of the row, where flotation is typically froth phase limited and operational, and set-up parameters have a limited influence on the recovery. ? Higher-powered flotation machines (high rpm, high power rotor size/type) at the end of the row to improve fine particle recovery. ? Lower-powered flotation machines (low rpm, low power rotor size/type) to enhance coarse particle recovery. In evaluating the effect of turbulent kinetic energy on flotation performance, the spatial distribution and its effect on size denominated recovery needs to be evaluated. The mean energy dissipation rate is a measure of the bulk energy input, but CFD-based models offer a more introspective view of flotation sub-processes. A CFD-based flotation model is used to highlight the effect of turbulent dissipation energy on attachment and detachment rates. Preferential collection zones for ?fine? and ?coarse? particles are predicted for both forced air and naturally aspirated machines. Keywords: CFD-based model, attachment, detachment, energy dissipation, hybrid energy flotation?, forced air, naturally aspirated

Sep 1, 2012

By Manuel Pérez-Tello

An experimental study on the oxidation of chalcopyrite (CuFeS2), pyrite (FeS2), covellite (CuS) and chalcocite (Cu2S) particles was conducted by means of differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA) techniques. Oxygen concentration in the process gas was set to 40 and 70% by vol. and a heating rate of 40 °C/min was used. Response variables included: the temperature of incipient reaction, the total exothermic heat of reaction, particle mass, morphology, and mineralogy of the reacted particles. Based on the experimental data and phase stability calculations, reaction mechanisms were proposed to represent the behavior of the particles during oxidation. The reaction mechanisms were verified by X-ray diffraction (XRD) analyses of the oxidized particles, and by thermochemical and mass balance calculations to reproduce the DSC and TGA thermograms. Overall kinetic models were developed to represent the evolution of the exothermic heat of reaction for each mineral as a function of time. Experiments conducted with copper concentrate particles containing the minerals studied suggest that the reaction mechanisms for the individual minerals can be used to represent the oxidation behavior of the copper concentrate particles.

Jan 1, 2006

By John Birkinbine

In a former paper* attention was directed to the various forms of pumping machines employed for permanent work in mining and metallurgical processes. The following is simply a collection of memoranda of work done of a temporary character, and is presented by way of comparison with other work of similar nature. In close proximity to the charcoal fnrnace at Pine Grove, Cumberland County, Pa., is a large deposit of superior hematite iron ore, which has been worked for a number of years, and from which many thousand tons of ore have been taken by open pit workings. In July, 1874, the furnace was blown out and operations at the bank suspended, the machinery for draining being removed except a plunger pump, 18 inches in diameter and 66 inches stroke, operated by a steam-engine by means of rods. The pit was allowed to fill with water, and no steps towards its reclamation were taken until November, 1877. At that time the pit was a pond of water at the base of the mountain, having an area of about four acres and a depth of seventy feet. As the pumps, rods, etc., had been submerged for over three years, and partially buried by the mud washed down from the banks, and as it was determined to change the location of the pump for future operations and drive it by water-power, a temporary pumping apparatus was determined upon for reclaiming the pit and keeping it drained until the permanent arrangements could be completed. By opening an old adit about 10 feet of the water was removed, and the area decreased to three acres. The inflow of springs was found to be 250 gallons per minute, and the amount of water contained in the pit was computed to be 45,000,000 gallons. As the inflow would undoubtedly increase while the water sank in the pit, provision was made for removing at least 60,000,000 gallons, at the rate of 1,500,000 to 2,000,000 gallons per day. The company determined to employ a Heald and Cisco centrifugal pump driven by an oscillatinig engine by means of a belt. Steam was supplied by four plain cylinder boilers, each 36 inches diameter

Jan 1, 1879

By H. A. Guess

Introduction. History and Production Statements. Southeast Missouri is the oldest of the large producing districts of the United States. The first recorded production from disseminated ores was in 1869, although for many years prior to that time lead had been milled from shallow pockets, and steady growth in production has been shown ever since, the greatest increases being during the past five years. The production by years for each of the operating companies from 1869 to 1907, inclusive, is given in Table I. In Table 11. is given the production by years from 1908 to 1912, inclusive, for the district as a whole, showing the tonnage of crude ore mined, yield in concentrates, average assay of concentrates; yield in metallic lead both per ton of crude ore and in total; also approximate value of the yearly production. It is interesting to note that the production for the 5-yr. period 1908 to 1912, inclusive, is practically equal to the total previous production, viz., the 39-yr. period 1869 to 1907, the summary being as follows:

Jan 1, 1915

By C. M. McCulloch

As part of the Bureau of Mines methane control program, the Pittsburgh coalbed was studied in Washington and Green Counties, Pa., and in Marion and Monongalia Counties, W. Va., where this coalbed is now being mined at its greatest depth. The coalbed thickness appeared to be structurally controlled; the bed was generally thinner near the axes of anticlines and thicker near the axes of synclines. The overburden isopach shows a similar relationship. Most of the clay veins in coal occur in the synclinal troughs, generally under sandstone roof. Cleat orientations measured in 18 underground mines showed that face cleats are perpendicular to the axial trends of the folds, and the butt cleats are parallel to the axial trends, indicating structural control of the cleat. Measurement and analysis of surface joint orientations provide a method for predicting the cleat orientations of the coalbed, but linears measured from infrared photographs and photoindex sheets helped only to determine regional trends. The results of these investigations provide a geologic framework for rational planning for underground mine development to use the best available technology to cope with methane emissions, coalbed discontinuities, and related ground support problems.

Jan 1, 1975

By R. J. Wysor

MoRe than two years ago, in making efficiency tests on our hot-blast stoves, I was surprised to discover a marked difference in temperature as indicated by a pyrometer inserted near a stove on blast, and the regular recording instrument situated near the bustle pipe. A special hole was then provided at the junction of the hot-blast main and the bustle pipe, and portable pyrometers with bare fire ends were used, both at this point and in the stove necks. I had occasion to make a number of such tests on various stoves on the same, furnace, the difference in temperature as shown by the two pyrometers varying chiefly with the temperature of the blast, and the distance of the stove from the furnace. However, this difference was always great, often averaging above 100" F., for the entire period of a stove on blast. Later, experiments were made with similar results on another group of stoves. The pyrometers used were properly standardized and checked against each other before and after each test. However, there was still a slight doubt as to the accuracy of the results obtained, as subsequently explained. But I have obtained corroboration of the magnitude of heat losses from blast-furnace hot-blast mains from two independent sources. I have learned from H. A. Brassert, Superintendent of Blast Furnaces, South Works, Illinois Steel Co., that he has recently done some experimental work similar to my own, and found temperature drops of the same order of magnitude. Also, C.,R. Lyle, of the Armstrong Cork Co., has made some interesting theoretical calculations, based on the thermal conductivity of fire brick, for the particular conditions of several of our tests; and his theoretical interpolations, all facts being considered, check our actual observations fairly well. I understand that Mr. Lyle expects to publish the results of his investigations. Method of Conducting the Tests The location of the pyrometer fire ends is shown in Fig. I, a plan of Bethlehem Steel Co.&apos;s "G" blast furnace, hot-blast stoves, and main. Bare fire ends were used at both positions "A" and "B," being inserted

Jan 1, 1916

By H. R. Barnhurst

It would be a difficult matter to trace from the beginning the very few improvements made in the burning of fuels prior to 1860. Donbtless the crossing of the sticks of wood in building a mood fire early appealed to our savage ancestry as a means of expediting its effectiveness for their crude culinary purposes. Stones and andirons came later in assisting the admission of air to the under part of the fuel bed, while beacons and cressets, utilized metal bars as supports for the same purpose. It is probable that Tuba1 Cain owed his success to the use of bellows making possible the use of mixed fuel and charge upon a hearth. With the development of working in cast iron, grate bars came in, and they are still with us doing duty in every household and almost every art where heat is a factor. Little was done beyond these crude methods prior to 1860. With the advancement of knowledge came the fuel-gas producer, a natural child of the retorts employed in supplying illuminating gas. It is only within the last 15 years that the conclusion became general that complicated systems for saving heat would not remedy deli-. ciencies in its primary development, and within that time there has been great advancement in the means of producing initially a fire of high effciency, so that to-day we are moving rapidly toward both high development and high absorption, with the resultant of high efficiencies. In studying the subject of the availability of pulverized coal as a fuel, it may occur to ask, why has this not come up earlier? This, question would be naturally prompted by recalling the fact that Thomas Crompton&apos;s English patents upon his methods were issued to him nearly 40 years ago. A conclusive answer to this, however, is that Crompton at that time had very crude facilities for making what was at best a very imperfect pulverization of the coal, arid the expense of preparation mas very great. He does not seem to have been aware of the advantage of a thorough drying of the coal in the

Jan 1, 1914

By G. S. Adisoma

To address the problem of grade estimation in a general three-dimensional shape and the uncertainty associated with the estimate, the technique of jackknifing/block kriging short-cut is proposed. A new estimator called jackknife kriging is introduced first. Through the jackknife variance, a confidence limit for the reserve grade estimate can be calculated. Unlike the kriging variance, which is more a measure of data configuration and is independent of data values, the jackknife variance reflects the true variability of the data. This approach provides a simple way to set a confidence level for global estimation of resources.

Jan 1, 1995

This paper presents the results of research aimed at proposing new solutions in the area of belt conveyor elements. Many factors, such as energy consumption costs, and operating costs of belt conveyor elements, including belts, idlers and drives have an impact on the operational costs of conveyors. The paper presents special tests of new materials for the bottom cover of an energy-saving belt conveyor, which decrease rolling resistance. It also presents large-scale in-situ tests of a high-output belt conveyor for the purpose of simultaneous measurements of various types of conveyor belts (standard vs several energysaving types) under typical operating conditions of a lignite surface mine. Improvements in materials used for the bottom belt covers, supported by specially developed comprehensive tests of the new types of belts have provided valuable results of various proposed solutions. Since the tests of belts were done at exactly the same time and in the same operating conditions, direct comparison of the results is valid and should lead to a substantial decrease in the conveyors? drives? energy consumption, which will improve the effectiveness of belt transport and minimize its negative influence on the environment.

Aug 1, 2013