By Leonard D. Jaffe

IN recent years, the advantages of tempered martensite as a microstructure for steel parts have been well established. For parts that must not fracture brittlely when loaded at high rates, at low temperatures, or under conditions of combined stress, tempered martensite is especially desirable. One of the factors that determine whether a steel part will have a martensitic structure after heat treatment is the hardenability of the steel. Despite the large amount of recent research, there are still many unsettled basic questions concerning hardenability and its relation to chemical composition, and, indeed, considerable disagreement among investigators in the field. Much of the uncertainty that beclouds the existing knowledge of hardenability arises from the fact that hardenability is still a wholly empirical concept, and has not been quantitatively related to the more fundamental knowledge of isothermal decomposition of austenite. Hardenability is, essentially, a measure of the time required for small percentages of austenite to decompose, during continuous cooling, to pearlite, bainite, proeutectoid ferrite, or proeutectoid carbide. In the practical heat-treatment of steel, also, the decomposition of austenite is usually not isothermal but rather during cooling, or, in general, is not at a single constant temperature. Thus, both hardenability and practical heat treatment involve anisothermal decomposition of austenite. In a previous publication1 the author and his collaborators outlined the principles that govern the relations between isothermal and anisothermal decomposition of austenite, and reviewed the experimental information available in 1945. To avoid repetition, familiarity with that article (Paper 1) will be assumed, and attention given primarily to work carried out or published since 1945. The method generally employed was explained in Paper 1: anisothermal transformation is studied through investigation of the effect of holding austenite at one temperature upon its subsequent decomposition at another temperature. Both temperatures are below the stability range of the austenite. This paper is confined to studies in which only a small amount of transformation occurred at the first temperature. This is the only case of importance in practical heat treatment when an essentially martensitic structure is sought. MATERIALS AND PROCEDURE It was necessary to use different steels for the studies involving proeutectoid ferrite and for those involving proeutectoid carbide, because the two constituents have not been found to form in the same steel. Several steels were tried and rejected

Jan 1, 1947

By Enid C. Plante

To extend our knowledge of the flotation behavior of sulphide minerals, the response of the following minerals to ethyl xanthate as collector was studied by captive bubble and cylinder flotation tests: antimonite (Sb2S3), arsenopyrite (FeAsS), covellite (CuS), rnarcasite (FeS2), orpiment (As&.), pyrrhotite (FeS) and tetrahedrite (4CU2S, Sb2S3). Lollingite (FeAs2) was also exarnined to determine if its behavior could be correlated with that of pyrite or rnarcasite (FeS2. Experimental Method Mineral for Flolation and Contact Tests Mineral was prepared in the manner a1ready described1 and its behavior both freshly ground and "oxidized" was studied. Tests in which the mineral was allowed to oxidize for various periods showed that a uniform response to xanthate was reached in two days or less. Oxidation Products The soluble oxidation products from most of the above minerals were measured and their effect on the flotation of the mineral studied. The mineral samples were wet ground to minus-52 mesh and deslimed, and 20 g of this material placed in 200 ml of distilled water of a measured pH value, and CO2-free air bubbled through each suspension at a constant rate (about I bubble/sec) for 5 days. It has been shown1 that the size of the mineral is unimportant in the rate of formation , oxidation products and that probably the supply of oxygen to the mineral is the rate-determining step. At the end of 5 days the pH value of the 'supernatant liquid was measured again, the mineral filtered off and the soluble products determined. Methods for estimation of sulphur acids, ferrous and ferric iron and copper have already been described.l No satisfactory method was found for antimony. Arsenic was estimated as the arsenate.2 Flotation of "Unoxidized" Minerals with Ethyl Xanthate as Collector Fig I to 3, 4. 6, show the effect of alkali and cyanide as depressants for the minerals with 25 mg potassium ethyl xanthate per liter as collector at 35°C. Wark and Cox8 have shown that with ethyl xanthate as collector, galena, pyrite and chalcopyrite show a greater tolerance to cyanide and hydroxyl ions at room temperature than at 35°C Covellite (Fig I), marcasite (Fig 2) and pyrrhotite (Fig 3) behave similarly. The independence of the curves for pyrrhotite at 35°C with respect to cyanide

Jan 1, 1949

By R. S. Dean. J. R. Long, T. R. Graham

Following the development of electrolytic manganese production by the Bureau of Mines, an extensive program was planned to study the character of this high-purity product and its possible utilization in various alloy combinations. Previous work reported in the literature concerning alloys containing substantial amounts of manganese dealt largely with material prepared from relatively impure grades of the metal, and in many instances the impurities thus introduced did not permit true evaluation of manganese as an alloying element. One phase of the Bureau's program included a general review of the system and the establishment of the physical properties of copper-manganese-zinc alloys, using electrolytic manganese, and with particular emphasis directed to compositions within the alpha solid solution area. A number of reports of the work on alloys in this system, giving specific data concerning the equilibrium system and some of its alloys, have already been published. One study' established the alpha solid solution area at various temperature levels and composition ranges up to 50 pct manganese. Other investigation reports presented the properties of selected alloys; namely, a 65 pct copper, I0 pct manganese, 25 pct zinc alloys;1 a sensibly white manganese brass composed of 70 pct copper, 20 pct manganese, 10 pct zinc,3 and a series of alloys with a constant copper content of 60 pct and 5 to 25 pct manganese, balance zinc.4 In these reports tensile properties as influenced by cold-working and subsequent annealing were given in detail. Additional data are now available on other alloys of the alpha region up to 50 pct manganese, and these, together with previously published information, are sufficiently complete to establish the relationship between properties and composition for this portion of the ternary system. The present report is a summary of the tensile properties of wrought alloys in the form of sheet and rod stock. The summary is necessarily limited to data for only one condition of cold-work and a single annealing temperature, since a complete exposition of all the data available would be too extensive for this presentation. Nevertheless, it is possible to make a reasonable approximation of the tensile properties in other conditions of cold-worki"g and annealing by a correlation of the data previously presented on specific alloys and the data given here.

Jan 1, 1947

By S. Torres, J. Álvarez, R. Castillo, R. Fuentes, C. Sandoval, R. Parra, Myakalwar A. K., M. Velázquez, J. Yáñez, D. Sbarbaro

Rapid analytical assessment in copper mining industry is a limiting factor for operational purposes and for the improvement of processes. The present work aims to review the analytical assessment in the copper industry utilizing emerging spectrochemical techniques such as laser induced breakdown spectroscopy (LIBS) and UV-Vis-IR Hyperspectral Sensing. LIBS is a plasma based spectroscopic method where the sample surface is irradiated by high power laser. The light emitted from the plasma contains atomic -molecular spectral information and can be detected using a simple CCD based spectrometer. UV-Vis-IR Hyperspectral Sensing is produced by the reflection of light from the sample’s rough surface in all directions and it can be collected by using an ellipsoid or paraboloid mirror arrangement. The electromagnetic radiation emitted by the samples in the UV-Vis, NIR and MIR region can be used for molecular characterization. The spectrometer splits different wavelengths through a CCD arrangement in 2D spatial and spectral dimensions, thus a hyperspectral cube of data is generated. Chemometric techniques such as principal component analysis (PCA), K- nearest neighbors (KNN), support vector machine (SVM) among others, can be applied to LIBS and Hyperspectral data for better classification and quantification purposes in copper ores. Real- time determination of elemental and mineral species used for online processing control will help to achieve the copper industry 4.0. INTRODUCTION The demand for copper mineral resources is intensely growing with the increase in population, per capita GDP, the development of new technologies and the increase in global living standard. With the rise in consumption of copper, it is important to optimize mining and metallurgical processes tending to the copper industry 4.0 (Ge, Song, Ding, & Huang, 2017). The real-time analytical assessment in the mining and metallurgical processes is a crucial part for allowing the global improvement in mining industry. The features considered for better analytical assessment are the instrumental automation and interconnection, real time results, low cost, quality in terms of accuracy and precision. Furthermore, improving recovery (extraction), timing and quality of final products avoiding environmental impacts. Some elements such as Cu, Fe, Ag, Au, Mo, S, As, Pb, Zn are important to be determined in the process control. Additionally, rapid mineral identification of few species such as CuFeS2, Cu4FeS5, FeS2, CuS, Cu2S, MoS2, Cu3AsS4, FeAsS, among other can be challenging.

Jan 1, 2019

By Thos. W. Gibson

The object of taxation is the raising of a revenue. Unless a tax accomplishes this, it is a failure. The right to take for public purposes a part of the moneys obtained from the carrying on of private enterprises is an attribute possessed only by a lawful government, and may indeed be called the supreme attribute of government. In free, democratic communities this power must of necessity rest upon the consent of the governed. Power implies obligation, hence it is obviously the duty of a government, in framing a system of taxation, to provide one which, while effective in producing a revenue, is also just and impartial. • It will be conceded that mines and mining property ought to bear a fair share of the public expenditure. The question is, upon what basis taxation should proceed. Two separate taxing principles are usually contended for: Taxation should be proportionate to the benefits received by the person or property taxed; taxation should be based on ability to pay. A third is sometimes added, taxation should have reference to the extent and value of the natural resources enjoyed. As applied to mining taxation, it is pointed out by those who support the fist mentioned basis that, mines being usually situated in rocky and hence sparsely peopled regions, mining companies are frequently obliged to construct roads, railways, telegraph and telephone lines, schools, water and sewerage systems, and many other amenities and conveniencea of civilization the cost of which in regions better suited for agriculture, and consequently more thickly populated, has either been defrayed locally, or can be spread over a sufficiently large taxable group of people to materially lighten the financial burden on the mine. The mining company, it is argued, having made these outlays, should receive credit for them and be relieved of taxation to a corresponding extent. There may be some force in this contention, but the situation is capable of relief without attempting to place taxation upon so unworkable a basis as the value of benefits received. Who is to be the judge of these benefits, and how are they to be valued? The very existence of a mining company and its ability to carry on business in peace and security depeind on the prevalence of law and order, which is a result of good government. The state provides protection against violence, and courts of law for

Jan 1, 1920

By Thos Gibson

THE object of taxation is the raising of a revenue. Unless a tax accomplishes this, it is a failure. The right to take for public purposes a part of the moneys obtained from the carrying on of private enterprises is an attribute possessed only by a lawful government, and may indeed he called the supreme attribute of government. In free, democratic communities this power must of necessity rest upon the consent of the governed. Power implies obligation, hence it is obviously the duty of a government, in framing a system of taxation, to provide one which, while effective in producing a revenue, is also just and impartial. It will be conceded that mines and mining property ought to bear a fair share of the public expenditure. The question is, upon what basis taxation should proceed. Two separate taxing principles are usually contended for: Taxation should be proportionate to the benefits received by the person or property taxed; taxation should be based on ability to pay. A third is sometimes added, taxation should have reference to the extent and value of the natural resources enjoyed. As applied to mining taxation, it is pointed out by those who support the first mentioned basis that, mines being usually situated in rocky and hence sparsely peopled regions, mining companies are frequently obliged to construct roads, railways, telegraph and telephone lines, schools, water and sewerage systems, and many other amenities and conveniences of civilization, the cost of which in regions better suited for agriculture and consequently more thickly populated, has either been defrayed locally, or can be spread over a sufficiently large taxable group of people to materially lighten the financial burden on the mine. The mining com¬pany, it is argued, having made these outlays, should receive credit for, them and be relieved of taxation to a corresponding extent. There may be some force in this contention, but the situation is capable of relief without attempting to place taxation upon so unworkable a basis as the value of benefits received. Who is to be the judge of these benefits, and how are they to be valued? The very existence of a mining company and its ability to carry on business in peace and security, depend on the prevalence of law and order, which is a result of good government. The state provides protection against violence, and courts of law for

Jan 4, 1919

By H. M. Chance

Recent research work has shown that coal can be produced, at reasonable cost, from almost all coal-mining districts containing not more than 3 to 8 per cent. of ash. From coal so produced, an abundant supply of coke, suitable for blast-furnace operation, can be made containing from 12 down to 6 per cent. or less of ash. These statements apply broadly to the Appalachian coal belt, including most of the mining districts in Pennsylvania, Ohio, West Virginia, Kentucky, Tennessee, and Alabama. The exceptions will generally be found among those coals carrying a prohibitive percentage of sulfur. Any gravimetric heavy fluid method of separation will effect a reduction in the percentage of sulfur, but this reduction may not be sufficient to produce, from coal unfit for metallurgic use, a product that can be so used. When a large part of the sulfur is in the form known as "organic sulfur, "or is present as very finely disseminated and homogeneously distributed pyrite, possibly it cannot be eliminated from the low-ash coal produced. When the sulfur exists as pyrite in distinct layers, bands, or nodules, or when it is finely disseminated but is irregularly distributed, often a low-ash coal low enough in sulfur to make good metallurgic coke can be produced from relatively impure coals. It has generally been assumed that the quality of coke on which blast furnaces must be operated depends on the geographic location of the furnace, and that the grade of coke on which a blast furnace must operate is that produced from the best coal obtainable by careful mining; or if the coal is prepared by washing, hand picking, or other means by which the foreign impurities are removed, that the grade of coke on which the furnace must operate depends on what has been termed the "inherent ash" of the particular coal. The term "inherent ash " is generally understood to mean the percentage of ash present after all removable (free) impurities, slate, fireclay, high-ash bony coal, and pyrite have been removed, and is usually applied to the percentage of ash present in run-of-mine coal from any mine after these impurities have been removed. Perfect washing, or perfect preparation, is understood to be attained when the percentage of ash in the washed coal is reduced to the percentage of inherent ash; that is, of ash that cannot be removed by the washing processes in common use. Wash-

Jan 1, 1924

By Sina Mostaghel, M. Guo, E. Klaffenbach

The current paper is focused on evaluating the behavior of copper in a copper production slag and the assessment of metal recovery possibilities. For this reason, thermodynamic calculations were carried out to determine the influence of parameters such as slag composition, temperature and oxygen partial pressure on recovery of non-ferrous elements. It was found that the formation of a solid face centered cubic (fcc) phase, mainly consisting of iron, limits the extent of reduction that can be achieved for an industrial process. However, it could be discovered that solubility of iron in the Cu-rich liquid alloy strongly depends on presence of other elements, particularly arsenic. As part of the results of this study, the solubility of Cu in the slag at onset of fcc phase formation is presented as function of temperature, oxygen partial pressure and concentration of MgO and CaO. It was concluded that lower temperature (1200°C) and higher CaO addition (16 mass-% in this study), would result in the highest achievable copper recovery from slag. INTRODUCTION Copper slag is produced as a by-product of the copper production process. The slag is still containing a high amount of copper and other valuable metals. This demands further treatment of the slag as a secondary source of metals. In addition, the physical/mechanical properties of slag allow its use in several applications such as hydraulic engineering, civil engineering, as an abrasive and many more. These applications help reducing the use of natural resources like rock and sand. By decreasing the content of heavy metals such as Cu, Pb, Zn and As in the slag, its application in abovementioned fields becomes more attractive as the probability of releasing these elements to the environment is further reduced. To develop a pyrometallurgical slag reduction process, it is necessary to understand what describes the end point of the reduction. This point is expected at maximum copper recovery without facing operational challenges. Existing literature provide some information on the effect of different parameters such as temperature or concentration of different slag formers, on solubility of copper and heavy metals in different phases. However, due to complexity of industrial slags, equilibrium experiments and accurate thermodynamic modelling are essential to be able to reliably predict the behavior of different elements in the system and determine the end-point of reduction.

Jan 1, 2019

By T. T. Read

A short time ago, one of the large steel companies courteously furnished the author with detailed records of the operations of a considerable number of iron blast furnaces over a period of two months. These will be made the basis of a subsequent study, but in beginning this study one of the first points requiring consideration was the probable error of the records, for what otherwise might be regarded as significant differences of performance under different conditions were perhaps really due to errors of observation, or failure to observe and record variations. If it is assumed, in blast-furnace records and calculations, that known quantities or factors are constant, .when as a matter of fact they are variable, the effects of these variations may erroneously be ascribed to some other cause. This is quite clearly expressed in the following quotation from E. Buckingham:l Theory always operates on an ideally simplified picture of reality because real phenomena are unmanageably complicated. The results obtained are not exactly true for any real phenomenon, though they may be for an ideal one; and the approxi-mation with which a theoretical equation, however obtained, represents the actual facts, always depends on the approximation in essentials between the ideal picture and its real prototype. The purpose of dimensional reasoning is to find out how some quantity which is involved in the phenomenon under consideration is related to certain others; or to find the relation connecting two or more quantities which vary, or may vary, simultaneously during the course of the phenomenon. Since we know that we must have a complete equation to start with, we begin by thinking the matter over, to see whether the quantities we have in mind are the only ones involved. Usually it is evident that they are not; so we next make a list of all the quantities we can think of which might under any circumstances be important. Upon considering this list, which is often a long one, it is usually evident that under the actual circumstances a number of these quantities may safely be ignored; so we cross them off the list and thus pass from our most general conception of the phenomenon to an ideal simpler one, in which these quantities are not involved at all.

Jan 1, 1926

By M. Cohen, R. T. Howard

It has long been realized among metallurgists that a fast, reliable method for the quantitative determination of the percentage of microconstituents in an alloy would be of great benefit in studies of equilibrium and transformation in the solid state. For example, Polushkinl has shown that the compositions of two coexisting phases in a binary system at a given temperature may be calculated very simply with the aid of two alloys lying in the two-phase field if the relative amounts of the two phases in each alloy can be determined. Recently, Grange and Stewart2 have traced the course of the austenite-martensite reaction in a series of commercial steels by making visual estimates of the percentage of martensite formed as a function of cooling temperature. The correlation of mechanical properties with structure, a subject of wide-spread current interest, is likewise dependent upon quantitative microanaly-sis. Yet, there are very few investigations described in the metallurgical literature, wherein methods of quantitative microscopy are employed. Usually, the relative amounts of the microconstituents are estimated in a qualitative or semiquantita-tive way. The authors were faced with this problem some time ago in studying the kinetics of austenite decomposition. Several aspects of this research could not be treated satisfactorily by other quantitative tools, such as specific volume,' magnetic,6 dila-tometric, electrical resistance7 or x-ray measurements.a It became necessary to find an impersonal quantitative method that could be applied to microstructures. Fortunately, it was noted that geologists and petrographers had coped with quantitative microscopy to a considerable degree in their attempts to evaluate the mineral contents of rocks. A number of excellent articles were found on this subject, and since they appear to be unknown generally to many metallurgists, the first part of the present paper is concerned with a review of the literature in some detail. With this survey as a background, the authors have adapted the so-called methods of point-counting and lineal analysis to metallography, as described in the second part of the paper. Austenite-martensite structures were selected for illustration not only because they are important in many ways, but because such fine intermixtures are notoriously difficult to estimate visually. Literature Survey Perhaps the earliest work on quantitative microscopic analysis goes back to Delesse9 (1848) who proved mathemati-

Jan 1, 1948

By W. T. Lundy

THE forms in which sulphur is commonly found-native sulphur, sulphides of many metals and sulphates-are widely distributed throughout the world. The two first mentioned are the principal sources of sulphur. Substantial amounts of sulphur in some form are recovered from gases from industrial plants and from gases from smelters treating other minerals. In recent years, plants have been installed in the United States to recover sulphur in elemental form from sour gases."' The amount of sulphur so produced is small at the present time but undoubtedly will increase in the future. The recovery of sulphur from gases is not covered in this chapter, which is confined to: (1) native sulphur deposits of Texas and Louisiana; (2) those of Italy; (3) other scattered deposits of native sulphur; and (4) pyrites deposits found in many countries of the world.30 Sulphur, a nonmetallic element, occurs normally in well developed bipyramidal or tabular crystals of the orthorhombic system, as well as in stalactitic and earthy masses. The mineral has a distinctive yellow color, which may be dark and discolored by impurities; the streak is white; the luster is resinous; and the fracture is conchoidal to uneven. Sulphur is translucent to opaque; has a hardness of 1.5 to 2.5, a specific gravity of 2.05, and an atomic weight of 32.06.16 The molecular weight of the solid is expressed by the symbol SS and that of the liquid and vapor ranges from S2 to S8, depending on the temperature. Sulphur melts at a temperature between 2340 and 248°F, depending on its crystalline state, to a liquid of dark amber color, the boiling point of which is 832°F. The viscosity near the melting point is about that of water and increases to 50,000 times that of water at a temperature of 380°F, subsequently falling rapidly to a low figure at the boiling point. Crystallization changes slowly from rhombic to monoclinic above 205 °F and in cooling the transformation is reversed. The mineral is a very poor conductor of heat and electricity; it is insoluble in water and nearly all acids and is soluble in cold carbon bisulphide and carbon tetrachloride. It ignites in air at a temperature of 478°F, burning with a distinctive blue flame with evolution of sulphur dioxide.47

Jan 1, 1949

By M. Cohen, R. T. Howard

It has long been realized among metallurgists that a fast, reliable method for the quantitative determination of the percentage of microconstituents in an alloy would be of great benefit in studies of equilibrium and transformation in the solid state. For example, Polushkinl has shown that the compositions of two coexisting phases in a binary system at a given temperature may be calculated very simply with the aid of two alloys lying in the two-phase field if the relative amounts of the two phases in each alloy can be determined. Recently, Grange and Stewart2 have traced the course of the austenite-martensite reaction in a series of commercial steels by making visual estimates of the percentage of martensite formed as a function of cooling temperature. The correlation of mechanical properties with structure, a subject of wide-spread current interest, is likewise dependent upon quantitative microanaly-sis. Yet, there are very few investigations described in the metallurgical literature, wherein methods of quantitative microscopy are employed. Usually, the relative amounts of the microconstituents are estimated in a qualitative or semiquantita-tive way. The authors were faced with this problem some time ago in studying the kinetics of austenite decomposition. Several aspects of this research could not be treated satisfactorily by other quantitative tools, such as specific volume,' magnetic,6 dila-tometric, electrical resistance7 or x-ray measurements.a It became necessary to find an impersonal quantitative method that could be applied to microstructures. Fortunately, it was noted that geologists and petrographers had coped with quantitative microscopy to a considerable degree in their attempts to evaluate the mineral contents of rocks. A number of excellent articles were found on this subject, and since they appear to be unknown generally to many metallurgists, the first part of the present paper is concerned with a review of the literature in some detail. With this survey as a background, the authors have adapted the so-called methods of point-counting and lineal analysis to metallography, as described in the second part of the paper. Austenite-martensite structures were selected for illustration not only because they are important in many ways, but because such fine intermixtures are notoriously difficult to estimate visually. Literature Survey Perhaps the earliest work on quantitative microscopic analysis goes back to Delesse9 (1848) who proved mathemati-

Jan 1, 1948

By Robert T. Howard, Morris Cohen

IT has long been realized among metallurgists that a fast, reliable method for the quantitative determination of the percentage of microconstituents in an alloy would be of great benefit in studies of equilibrium and transformation in the solid state. For example, Polushkin1 has shown that the compositions of two coexisting phases in a a binary system at a given temperature may be calculated very simply with the aid of two alloys lying in the two-phase field if the relative amounts of the two phases in each alloy can be determined. Recently, Grange and Stewart2 have traced the course of the austenite-martensite reaction in a series of commercial steels by making visual estimates of the percentage of martensite formed as a function of cooling temperature. The correlation of mechanical properties with structure, a subject of wide-spread current interest, is likewise dependent upon quantitative microanalysis.3 Yet, there are very few investigations described in the metallurgical literature, wherein methods of quantitative microscopy are employed. Usually, the relative amounts of the microconstituents are estimated in a qualitative or semiquantitative way. The authors were faced with this problem some time ago in studying the kinetics of austenite decomposition. Several aspects of, this research could not be treated satisfactorily by other quantitative tools, such as specific volume,4 magnetic,5 dilatometric,6 electrical resistance7 or x-ray measurements.8 It became necessary to find an impersonal quantitative method that could be applied to microstructures. Fortunately, it was noted that geologists and petrographers had coped with quantitative microscopy to a considerable degree in their attempts to evaluate the mineral contents of rocks. A number of excellent articles were found on this subject, and since they appear to be unknown generally to many metallurgists, the first part of the present paper is concerned with a review of the literature in some detail. With this survey as a background, the authors have adapted the so-called methods of point-counting and lineal analysis to metallography, as described in the second part of the paper. Austenite-martensite structures were selected for illustration not only because they are important in many ways, but because such fine intermixtures are notoriously difficult to estimate visually. LITERATURE SURVEY Perhaps the earliest work on quantitative microscopic analysis goes back to Delesse9 (1848) who proved mathemati-

Jan 1, 1947

By James S. Browning

For the past several years, USBM has conducted laboratory and continuous process development work on the weathered mica pegmatites ores of Alabama, Georgia, and North Carolina to determine the feasibility of recovering commercial-grade mica concentrates by flotation. The research has resulted in the development of two processes for flotation of mica: 1) an acid-cationic method for recovery of coarse mica and 2) an alkaline-anionic-cationic method for recovery of fine mica. The research indicated that the two processes may be effectively utilized separately or in combination for flotation of mica from weathered pegmatite ores. This report summarizes the process development work, and demonstrates the feasibility of producing commercial-grade concentrates with a high recovery of the contained mica. Mica mining in the United States is confined largely to pegmatites and schists in a few well-defined areas. The largest region extends from central Virginia southward through western North and South Carolina, northern Georgia, and east-central Alabama.'" Whereas in western North Carolina, these pegmatite dikes are weathered to only a shallow depth, they are deeply weathered in the Carolina Piedmont and in Georgia and Alabama. Particularly in Georgia and Alabama, mica is found in the decomposed slates and schists adjacent to the pegmatites, and in deeply weathered granites. Most flake mica is obtained as the major marketable product by crushing and milling pegmatites4 To a lesser extent, mica is produced as a byproduct of feldspar" and spodumene. Past research by U.S. Bureau of Mines (USBM) has developed two methods for mica flotation. One method utilizes acid-cationic flotation for recovery of mica.' This method requires thorough desliming of the ore with consequent fine mica losses. The other utilizes an alkaline-anionic-cationic process for recovering fine-size mica from pegmatite ores after desliming sufficiently to remove clay materials but not so drastically as to remove the fine mica.8-18 The latter process has also been successfully applied to a micaceous schist ore from California.' This report summarizes the results of these research studies. Both of the flotation processes developed by USBM have been adopted by the mica industry and are being commercially utilized separately and in combination for flotation of mica from weathered pegmatite ores. Description of Ores The weathered mica pegmatite ores used in the investigations were obtained from commercial mica operations in Alabama, Georgia, and North Carolina. The

Jan 1, 1971

By Leonard D. Jaffe

In recent years, the advantages of tempered martensite as a microstructure for steel parts have been well established. For parts that must not fracture brittlely when loaded at high rates, at low temperatures, or under conditions of combined stress, tempered martensite is especially desirable. One of the factors that determine whether a steel part will have a martensitic structure after heat treatment is the hardenability of the steel. Despite the large amount of recent research, there are still many unsettled basic questions concerning hardenability and its relation to chemical composition, and, indeed, considerable disagreement among investigators in the field. Much of the uncertainty that beclouds the existing knowledge of hardenability arises from the fact that hardenability is still a wholly empirical concept, and has not been quantitatively related to the more fundamental knowledge of isothermal decomposition of austenite. Hardenability is, essentiaily, a measure of the time required for small percentages of austenite to decompose, during continuous cooling, to pearlite, bainite, proeutectoid ferrite, or proeutec-toid carbide. In the practical heat-treat- ment of steel, also, the decomposition of austenite is usually not isothermal but rather during cooling, or, in general, is not at a single constant temperature. Thus, both hardenability and practical heat treatment involve anisothermal decomposition of austenite. In a previous publication1 the author and his collaborators outlined the principles that govern the relations between isothermal and anisothermal decomposition of austenite, and reviewed the experimental information available in 1945. To avoid repetition, familiarity with that article (Paper I) will be assumed, and attention given primarily to work carried out or published since 1945. The method generally employed was explained in Paper I: anisothermal transformation is studied through investigation of the effect of holding austenite at one temperature upon its subsequent decomposition at another temperature. Both temperatures are below the stability range of the austenite. This paper is confined to studies in which only a small amount of transformation occurred at the first temperature. This is the only case of importance in practical heat treatment when an essentially martensitic structure is sought. Materials and Procedure It was necessary to use different steels for the studies involving proeutectoid ferrite and for those involving proeutectoid carbide, beeause the two constituents have not been found to form in the same steel. Several steels were tried and rejected

Jan 1, 1949

By W. Robert Power

Stone is considered by many to be the premium material for beauty and durability in all kinds of construction. Its use dates to the dawn of civilization and only buildings made of stone have survived from ancient times. The use of stone relative to other materials declined from the beginning of the present century reaching a low point in the third quarter, but there has been a resurgence in the use of stone in construction during the past decade, due probably, to new techniques for producing stone, a greater recognition of its beauty and durability, and greater affluence among consumers. The aesthetic appeal of stone is attested to by the many attempts to simulate it in synthetic materials. Today, natural stone is considered by many to be the ultimate in aesthetic appeal, durability, and ease of maintenance. Consumption of dimension stone has increased dramatically during the past decade. The US Bureau of Mines reported that the total value of US consumption in 1978 was $1 13 million and that total imports were valued at $65 million in 1979 (Anon., 1980). In 1989 consumption of domestic dimension stone was valued at $208.3 million and imports at $525 million. This dramatic increase occurred after demand had decreased at an average rate of 2.5% in the two decades prior to 1978 (Anon., 1980). More than half of the imports come from Italy, but production of dimension stone has increased worldwide spectacularly. Meaningful statistics on dimension stone are hard to acquire. The finished piece of stone is a highly value-added product, but stone may be sold as rough blocks, sawed slabs, or finished product. The same piece of stone may therefore be sold and reported three or more times. Furthermore, although the quantity of stone is most commonly reported in tons, stone cladding is more often sold by the surface area and at the same price for different thicknesses. By any measure, however, the production and consumption of dimension stone has increased dramatically during the past decade. A significant indication of the resurgence of stone was the introduction of two new trade publications during the 1980s. Stone World (Tradelink Publishing Co., Inc., Oradell, NJ), introduced in 1984 is published monthly and Dimensional Stone (Dimensional Stone Institute, Inc., Woodland Hills, CA), introduced in 1985 is published monthly. Both magazines provide useful information on new technology, market trends, producing areas and companies, and other information not previously available.

Jan 1, 1994

By Leonard D. Jaffe

In recent years, the advantages of tempered martensite as a microstructure for steel parts have been well established. For parts that must not fracture brittlely when loaded at high rates, at low temperatures, or under conditions of combined stress, tempered martensite is especially desirable. One of the factors that determine whether a steel part will have a martensitic structure after heat treatment is the hardenability of the steel. Despite the large amount of recent research, there are still many unsettled basic questions concerning hardenability and its relation to chemical composition, and, indeed, considerable disagreement among investigators in the field. Much of the uncertainty that beclouds the existing knowledge of hardenability arises from the fact that hardenability is still a wholly empirical concept, and has not been quantitatively related to the more fundamental knowledge of isothermal decomposition of austenite. Hardenability is, essentiaily, a measure of the time required for small percentages of austenite to decompose, during continuous cooling, to pearlite, bainite, proeutectoid ferrite, or proeutec-toid carbide. In the practical heat-treat- ment of steel, also, the decomposition of austenite is usually not isothermal but rather during cooling, or, in general, is not at a single constant temperature. Thus, both hardenability and practical heat treatment involve anisothermal decomposition of austenite. In a previous publication1 the author and his collaborators outlined the principles that govern the relations between isothermal and anisothermal decomposition of austenite, and reviewed the experimental information available in 1945. To avoid repetition, familiarity with that article (Paper I) will be assumed, and attention given primarily to work carried out or published since 1945. The method generally employed was explained in Paper I: anisothermal transformation is studied through investigation of the effect of holding austenite at one temperature upon its subsequent decomposition at another temperature. Both temperatures are below the stability range of the austenite. This paper is confined to studies in which only a small amount of transformation occurred at the first temperature. This is the only case of importance in practical heat treatment when an essentially martensitic structure is sought. Materials and Procedure It was necessary to use different steels for the studies involving proeutectoid ferrite and for those involving proeutectoid carbide, beeause the two constituents have not been found to form in the same steel. Several steels were tried and rejected

Jan 1, 1949

By W. R. Hibbard

The increased strength of a polycrystal-line metallic aggregate compared with that of its individual crystals generally has been associated with complex stress distributions at the grain boundaries resulting from atomic irregularity between grains. This disregistry, together with the necessity for adjacent crystals to deform compatibly regardless of the single crystal crystallo-graphic strain mechanism, complicates this mechanism so as to increase the metal's resistance to deformation. Although Taylor1 has shown from purely mechanical considerations the requirement for at least five active slip systems to absorb the complexities during the homogeneous deformation of polycrystalline face-centered cubic metals, experimental studies by Barrett and Levenson2 indicate that this is feasible only in a qualitative sense because of deviations from homogeneous deformation. Seitz and Read in their review3 state: " Unfortunately . . . present knowledge of the grain boundary influence is not sufficient to complement the work in single crystals and provide us with a good foundation for treating polycrystals." The purpose of this investigation was to attempt to clarify the gap between single crystals and crystalline aggregates by an analysis of the effects of dcformational stresses. Some of the results were described by C. H. Mathewson in his 1943 Campbell Memorial Lecture.zl Previous Investigations Since the performance of single crystals deformed under pure stresses has been relatively thoroughly investigated, the most significant researches are concerned primarily with deviations from single crystal behavior of large grained specimens. Qualitative grain boundary effects involving the observed amount of slip werc reported by Carpenter and Elam5 in 1921. Individual crystals in a two or three grained aluminum specimen deformed by tension acted in the normal manner described by Taylor and Elarn4 except for marked modifications at the grain boundaries. There the power to withstand deformation was considerably increased, leaving a ridge on the specimen where decreased slip occurred, often noticeable yi in. from the boundary. Adcock,6 Yamaguchi,' Seumel, Hirstg and others have also reported this phenomenon as a qualitative trend. Yet attempts by O'Neill'o and Ljunggrenll to measure a difference in hardness at grain boundaries in undeformed specimens were unsuccessful. Miller12 measured quantitatively the reduction in slip near the boundary between the single crystal and polycrystalline areas of zinc specimens. These effects consisted of two parts: I. Next to the polycrystalline interface thc distribution of stresses was so altered

Jan 1, 1949

By C. R. Ince

The term "differential flotation" is used to denote a flotation operation in which separation is effected between two or more minerals of the same class; e. g., lead sulfide from zinc sulfide, pyrite from blende, chalco-pyrite from pyrite, chalcopyrite from blende. At present, so far as published work shows, there seem to be two theories as to the mechanics of differential flotation. The earlier and more generally accepted theory is that the so-called depressing agents alter the surface of one or more of the sulfides in the ore, either by chemical action or adsorption, so that it is no longer amenable to flotation, but that these depressed sulfides can be revived, after the unaffected sulfide has been floated, by reagents which react chemically with the altered surface and make it amenable to flotation. More recently, Professor Taggartl has advanced the theory that slime adsorption is an important factor in differential flotation. He believes that, with the proper use of a class of agents, which he calls dispersion agents and which include practically all the depressing agents, one can cause the slime to adsorb differentially on sulfide surfaces. A gangue-slime coated sulfide surface will act as a gangue particle and will not float. If, subsequently, an agent that will remove the gangue-slime coating is added, the sulfide again assumes its original surface and can be floated as an ordinary sulfide. This is the basis of the slime theory of differential flotation. Timber Butte mill at Butte, Mont., is a typical lead-zinc flotation concentrator. Neihart ore, chosen for investigation in this work, is one of the custom ores treated at that mill. Practice at Timber Butte mill in February, 1928, was as follows: A combined lead-zinc concentrate was first made using 0.2 Ib. per ton on the ore of potassium xanthate and 0.03 lb. per ton of Cleveland Cliffs oil after 1.5 lb. per ton of lime and 1 lb. per ton of calcium chloride has been added just before the ball mill. The concentrate was then thickened to 70 per cent. solids. Potassium cyanide to the amount of 0.3 lb. per ton and zinc sulfate in the quantity of 0.5 Ib. per ton were added to the thickened pulp and the whole

Jan 1, 1930

By C. R. Ince

THE term "differential flotation" is used to denote a flotation operation in which separation is effected between two or more minerals of the same class; e. g., lead sulfide from zinc sulfide, pyrite from blende, chalcopyrite from pyrite, chalcopyrite from blende. At present, so far as published work shows, there seem to be two theories as to the mechanics of differential flotation. The earlier and more generally accepted theory is that the so-called depressing agents alter the surface of one or more of the sulfides in the ore, either by chemical action or adsorption, so that it is no longer amenable to flotation, but that these depressed sulfides can be revived, after the unaffected sulfide has been floated, by reagents which react chemically with the altered surface and make it amenable to flotation. More recently, Professor Taggart1 has advanced the theory that slime adsorption is an important factor in differential flotation. He believes that, with the proper use of a class of agents, which he calls .dispersion agents and which include practically all the depressing agents, one can cause the slime to adsorb differentially on sulfide surfaces. A gangue-slime coated sulfide surface will act as a gangue particle and will not float. If, subsequently, an agent that will remove the gangue-slime coating is added, the sulfide again assumes its original surface and can be floated as an ordinary sulfide. This-is the basis of the slime theory of differential flotation. Timber Butte mill at Butte, Mont., is a typical lead-zinc flotation concentrator. Neihart ore, chosen for investigation in this work, is one of the custom ores treated at that mill. Practice at Timber Butte mill in February, 1928, was as follows: A combined lead-zinc concentrate was first made using 0.2 lb. per ton on the ore of potassium xanthate and 0.03 lb. per ton of Cleveland Cliffs oil after 1.5 lb. per ton of lime and 1 lb. per ton of calcium chloride has been added just before the ball mill. The concentrate was then thickened to 70 per cent. solids. Potassium cyanide to the amount of 0.3 lb. per ton and zinc sulfate in the quantity of 0.5 lb. per ton were added to the thickened pulp and the whole

Jan 1, 1929