By Graham W. Mark

A chemical method of analysis for beryllium was developed recently in Bureau of Mines laboratories. In this method, quinalizarin (1-2-5-8 tetrahydroxyanthraquinone) in N/4 NaOH is used as a colorimetric titration reagent. This solution has a reddish-purple color, whereas the solution containing equivalent amounts of beryllium and the dye is rather blue. In the titration procedure, standard quinalizarin solution is added to the unknown beryllium sample and to two standard beryllium samples of different but known concentrations. Then adjustments in concentrations of BeO in the two known and of quinalizarin in all three are made until the red-violet shade of the unknown is halfway between that of the two knowns. The amount of BeO in the unknown is calculated from the known BeO content of the solutions between which it lies. It is extremely difficult to distinguish the slight differences in shade of these solutions without the use of a proper light filter, especially when the concentration is over 0.1 mg. of BeO, so a study was made of the transmission characteristics of quinalizarin in N/4 NaOH and of the corresponding beryllium complex to determine what filter would give the most contrast.

Jan 1, 1950

By W. S. Reid

R. H. McNAUGHTON*—The Smelt- ing Co. and Mr. Reid and his men at Selby are to be congratulated on the job they have done on sinter gas recircula-

Jan 1, 1950

By Whitman E. Brown, Louis J. Erck

L. A. ROE*—This paper is one of great value to the iron ore industry. The Humphreys spiral is a relatively new tool and gives promise of being quite useful in solving certain problems of iron ore beneficiation. Spirals have been tested on a martite ore at the Benson mine of Jones and Laughlin Steel Corp. in northern New York State. Our New York ore is considerably different, physically and mineralogically, than the one mentioned in this paper, and contains only 25 pct iron. This ore can be processed on spirals to give a concentrate containing 62 pct iron with an 85 pct recovery. On our particular ore we found operating difficulties when the spiral feed was coarser than 14 mesh. These were chiefly due to excessive "build-up" of locked middlings in the spiral circuit. In extreme cases these middling particles would accumulate to such an extent that the plant had to be shut down and the spiral surge tanks cleaned out. It is interesting to note that there exists a close relationship between the results of tabling a given iron ore and concentration of this same ore on Humphreys spirals. The size range of the ore must, of course, be within those limits acceptable to spiral concentration. Comparative tests on several of our mar-tite ores showed tabling results to be the same as spiral results. The authors make no mention of the use of a tailing stream splitter (now available from the spiral manufacturer) which is a useful tool in studying iron losses in the tailings stream. 011 our particular martite ore we found a considerable accumulation of fine-sized iron ore particles in the outside portion of the tailings stream. This fraction may be amenable to further treatment. E. H. ROSE*—The authors have concluded an interesting piece of work and this paper is an excellent factual account of a rapid and somewhat unusual transi-;ion in practice in the plant described. Perhaps it was modesty on their part which caused them so casually to limit to one sentence the fact that "several other methods of concentration on the fine ores representative of the Hill Trumbull group . . . failed to produce consistently an acceptable grade and recovery of finished product." The fact is that they were confronted by a difficult mineral-dressing problem and they are to be congratulated on their courage and persistence in staying with it until a satisfactory solution was evolved. A visitor to the plant might have been mildly astonished, as I was, to see one type of concentrator handling that part of the load early in the 1947 season, its experimental replacement by another a little later, and then in 1948 to see that both types had simply disappeared and their place taken by the spirals which were operating as placidly as though they had been there all the time. In working out economic methods of beneficiating Alabama red ore, most of which development is still ahead of us, it is likely that we also will pass through a period of successive disappointments, for we too have a problem where it is next to impossible either to "guess 'end right in the first place," or, because full-scale operating cost is such an important factor, to lay the ultimate answer on the line in advance by means of laboratory experimentation. Iron ore being what it is instead of what it used to be, it is encouraging to have the example the authors have given us today that a tough nut that will not crack on the first blow or the second is apt to do so on the third or fourth.

Jan 1, 1950

By D. A. Dahlstrom

Although the liquid-solid cyclone is a relatively recent innovation in the field of coal preparation, various authors have already indicated three distinct applications to operations encountered in the modern tipple. Driessen's articles and work at the Dutch State Mines exhibited its possibilities in the bene-ficiation of fine coal with apparently high efficiencies down to the 200-mesh fraction. l,2,3,4 Other publications point out its use as a recoverer, thickener, and preliminary dewatering agent of fine coal which in too many cases is being wasted due largely to former high operating cost limitations.M Finally, certain authors have emphasized the practicability of applying the cyclone to the elimination of coarse and fine solids from water slurries in the tipple in order to produce a water suitable for recycle purposes containing only minute particles far below the 200-mesh size.6 This would result in a closed water system for many cases, with its accompanying economic and operating advantages to locations where water quantity and quality problems are severe; better operation of washing equipment using a consistent water devoid of injurious fine particles; lowered maintenance costs due to the lesser abrasion resulting when the fine abraiding particles are removed; and the greater ease of disposing of refuse streams of reduced volume containing greater percentages of solids. While the three applications have been indicated to be feasible, only a meager amount of data is available on capacities and solid elimination eficiency as a function of design variables and cyclone friction loss. This information is essential for the optimum use and construction of the solid-liquid cyclone, and accordingly, work on the problem was initiated at Northwestern University. For the unfamiliar reader, briefly the cyclone consists of a cylindrical section mounted above a truncated cone. The feed nozzle enters the cylindrical ring tangentially with the underflow nozzle permitting discharge of the concentrated solids located at the apex of the cone. The overflow nozzle through which the clarified water exits is centered in the cylindrical section at the top of the cyclone. Half sections of experimental cyclones will be found in Fig la and 6. The feed slurry enters with a tangential velocity, thus creating a spiral pattern of high centrifugal force. The solid particles of sufficient size and gravity are ejected outward to the walls and spirally discharge to the underflow. Most of the water with uneliminated fine solids moves radially inward along the path of the outer

Jan 1, 1950

By James J. Dowd

The investigation to evaluate the reserves of coking coal in the United States suitable for the manufacture of metallurgical coke is being made by the Bureau of Mines in three parts: (1) To estimate known (measured plus indicated) recoverable reserves of all coking coal; (2) to study the carbonizing properties of coals and coal blends not now widely used for metallurgical coke making; and (3) to upgrade marginal coals through effective preparation. This is the second7j of a series of reports giving the results of studies by counties under part (1) of the investigation. This report covers Indiana County, Pa., which comprises parts of the Smicksburg, Punxsutawney, Elders Ridge, Indiana, Barnesboro, Latrobe, New Florence, and Johnstown Quadrangles. (See fig. 1.) A base map for each bed in each Quadrangle was made to the scale 1 inch equals 1,200 feet. Maps of mines, locations of drill holes, bed and total coal thicknesses, and the outcrop of the bed were plotted on the maps. With all available data plotted, isopach lines were drawn to limit areas of known unmined reserves in beds 0 to 14 inches thick, 14 to 28 inches thick, 28 to 42 inches thick, and over 42 inches thick. These areas of coal reserves also were divided into "measured" and "indicated" categories. All areas in each thickness range and in each category, mined-out areas, areas excluded from the estimate, and areas outside of the outcrop were measured by planimeter on the base maps. Estimates of total reserves 14 inches and more thick and maps for individual beds were prepared from these data.

Jan 1, 1950

By Thomas Fraser, David R. Mitchell

THE primary purpose of the loading plant is to transfer the finished product from the preparation machines to the railroad car, truck, or barge in which it is to go to market. Secondary purposes of the loading plant are: to prevent excessive degradation of sizes during loading, to reduce segregation as much as possible, and to prevent excessive quantities of very good or off-grade coal from entering any one car. Nonuniformity of consignments is one of the chief sources of complaints by consumers and coal merchants. A properly designed loading plant will do much to reduce complaints and insure uniformity, not only from shipment to shipment but also in each individual consignment along the length of the car and in cross section. DEGRADATION IN STORAGE, LOADING AND SHIPMENT The object in loading is not only to handle the coal without breakage and segregation, but also to produce a well-trimmed load that will ride to its destination without spillage o~ breakage en route. The small sizes present in a car-of prepared coal as received by the purchaser consist of: missed small sizes not screened out in the preparation plant, breakage during loading, and breakage caused by handling en route. For domestic sizes of anthracite shipped from the Pennsylvania anthracite field to Atlantic coast cities, the dealers' loss because of breakage in loading and shipment amounts to from 2 to 5 per cent and for anthracite shipped to Middle West cities, the loss is 8 to 9 per cent. This difference is in part because dealers in the Middle West rescreen their coal more thoroughly than is usual in the East. One dealer handling Illinois No. 6 coal shipped from southern Illinois mines to Chicago reports an average size loss of 10 per cent when lump coal is unloaded with a fork. This runs as low as 5 per cent for carefully loaded coal and as high as 15 per cent for carelessly loaded coal. An Ohio dealer estimates the degradation in loading and shipment of West Virginia coals consigned to Ohio cities as follows: Pocahontas lump

Jan 1, 1950

By Carl S. Westerberg

1,. C. McCABE*-—An increased derliand for coal in the west is to be expected because of the growth in population and industry during the past ten years. The author calls attention to the increased mechanical cleaning of Utah coal between 1938, when no cleaning was being done, and 194.7, when more than 24 pct of the production was cleaned. This is essentially the Period of most rapid growth of the Pacific Coast. area altliough the growth and, no doubt, the general trends in coal production and cleaning continued at a less accelerated rate during 1948. The Pacific southwest increased 37 pct in population between 1940 and 191.7 while the United States showed only a 7 pct increase in the same period. it has been estimated that there will be an additional 15 pct increase in population between 1947 and 1950. The conclusion that more coal and more mechanicak cleaning capacity will be required appears to be well founded. Mr. Westerberg discusses the cco- nomic advantages of coal cleaning reflected in freight savings, in lower cost per million Btu, and lowered ash and sulphur content. In view of the limited occurrence of coking coals in the west it would be interesting to know whether significant beneficiation in coking strength can be expected from mechanical cleaning of Utah coals. This has been demonstrated for some eastern and midwestern coals. One can readily agree to the desirability of recovering the fine coal that has heretofore been lost in washery slurry. The very cheapness of coal has Iridered

Jan 1, 1950

By A. L. Engel

Many western ores containing ;old, silver, and copper can be mined and concentrated at a profit only when the recovery of those metals is high and treatment costs are low. Usually, ores containing easily dissolved copper minerals, or copper minerals that become soluble to some extent through oxidation during treatment, present a real problem in cyanidation. Copper cyanide compounds are formed that tend to 'precipitate and that cannot yield regenerated cyanide and metallic copper on contact with zinc. This results not only in some loss of copper through solution in cyanide, but in excessive consumption of cyanide above the amount required for the extraction of Gold and silver. Any moans, therefore, of minimizing the: loss of cyanide while at the same time effecting high recoveries of the several values contained in the ore is of wide interest. A sample of typical low-grade ore of gold, silver, and copper, containing copper-sulfide minerals, was obtained from the MacLaren Gold Mines Co., Cooke, Park County, Mont., for laboratory investigation by flotation and cyanidation.

Jan 1, 1950

By J. B. Zadra

Much has been published by various investigators on the use of activated carbon for adsorbing precious metals from cyanide solution and pulp. For the benefit of the reader, a list of these earlier publications appears at the end of this report. The present paper deals only with a process for extracting gold from gold-laden carbon and re-use of the de-adsorbed carbon. At the Getchell mine, Redhouse, Nev., experiments have been in progress for several years concerning the use of activated carbon to adsorb gold from their slime circuit pulp. The experimental work has been successful. Their practice has been to ship the gold-laden carbon to a smelter for treatment, which meant the total loss of the carbon in addition to smelter and freight, charges, all of which proved costly and wasteful.

Jan 1, 1950

By E. O. Wagner, V. F. Parry, J. B. Goodman

The low-rank coals containing 10 to 50 pct natural bed moisture represent over half of the tonnage reserve of the available solid fuels of the United States, but only about 2 pct of United States coal production is derived from these fuels. Increased utilization of these large reserves will result if the bed moisture can be removed at the mine in high-speed low-cost processes. This paper presents a theoretical and experimental study of the factors affecting high-speed drying of coal dusts. The time required to heat particles of coal is proportional to the square of their diameter, and it is calculated that the probable time in minutes is equal to 6D2. In other words, a 1/16 in. coal particle should be heated to drying temperature in 1.5 to 2.0 sec. Likewise, 1/8 in. particles should be heated in about 6 sec. The net heat required to dry subbituminous coal and lignite varies from 240 to 375 Btu per pound, depending upon the moisture removed, and this heat can be obtained from 42 to 61 cu ft of hot gases at 600°F. The necessary heat also can be obtained from 7.5 to 11 cu ft of gas at 2000°F. A description of the design and operation of a pilot plant for flash drying coal dusts is presented. This plant dries 1/16 in. by 0 coal dust in suspension in 1.5 to 2 sec with 600°F gas at a rate of 1300 lb per hour per square foot of column area and operates continuously at an efficiency of about 85 pct. The design and operation of another pilot plant for drying 1/8 in. by 0 coal dusts Is also described. This unit dries coal in the fluidized state using the sensible heat of gases introduced at 2000°F and processes coal at a rate of about 1500 Ib per hour per square foot of grate area at 85 to 90 pct efficiency. Over 90 pct of the bed moisture of low-rank coal dusts can be removed by the methods described. The heating value of lignite can be increased 45 pet and that if subbituminous coal 25 pct in a few seconds. The physical and chemical properties of coal dusts before and after drying are presented in the report, and it is shown that the bulk density of the dried coal is equal to that of the raw coal. This phenomenon makes it possible to ship 25 to 45 pct more heat in a railroad car with consequent savings in freight costs. Introduction For several years the Subbituminous Coal and Lignite Section of the Coal Branch of the Bureau of Mines at Golden, Colo., has been concerned with upgrading low-rank coals by removal of natural bed moisture. These fuels contain 10 to 50 pct total moisture, which reduces their industrial value considerably. In 1938, investigations were initiated in cooperation with the University of North Dakota to study drying of lignite by the Fleissner process with heat derived from high-pressure saturated steam. Two pilot plants were built, and two reports were published giving the results of this work.l,2 It was demonstrated that lump lignite and subbituminous coal

Jan 1, 1950

By S. A. Herres, A. R. Elsea

Temper brittleness refers to the loss in the notched-bar impact resistance encountered in most medium- or low-alloy steels when they are tempered within the temperature range of 700 to ll00°F or slowly cooled from a higher tempering temperature. Temper brittleness is important because it impairs the service properties of otherwise suitable steels over the range of hardnesses obtained at medium tempering temperatures and because it is impractical to cool pieces of large section rapidly enough from higher tempering temperatures to prevent temper brittleness. The problem of temper brittleness has always been closely associated with ordnance manufacture because armor plate and gun steels require good shock resistance and are often heat treated in heavy section. However, it is now realized that many brittle failures in structural alloy steel parts are attributable to temper brittleness, and there is little question that it contributes to the low impact resistance of alloy steels used in the hot-rolled or normalized condition which are slowly cooled from the hot-rolling or normalizing temperature. Recently Hollomonl has presented a comprehensive summary of the literature on the subject and an excellent description of the manner in which temper brittleness affects the notched-bar impact resistance and other mechanical properties of steel. Carpenter and Robertson2 have given a good analysis of the probable mechanism of temper brittleness, which is similar in many respects to the precipitation-hardening phenomenon. Fig 1 is their diagram illustrating the response to tempering of a susceptible steel. Three changes are recognized as the temperature of tempering a previously quenched steel is raised: (1) pre- cipitation occurs more rapidly and to a greater extent and the notched-bar impact value falls to a minimum; (2) coalescence of the precipitated particles begins to be effective and the impact values for both rapidly cooled and slowly cooled specimens increase; (3) the precipitate goes back into solution at higher tempering temperatures and the impact values of specimens cooled rapidly enough to retain the solution increase, while reprecipitation occurs in slowly cooled specimens and their impact values decrease again. No change must proceed to completion before the following one begins and there is overlapping in temperature ranges. Although there have been a large number of experimental investigations of temper brittleness, insufficient evidence has been accumulated to permit definite identification of the precipitate wnich causes temper brittleness nor have the specific effects on it of various alloy elements and impurities in steel been definitely established. This lack of evidence is largely a result of the lack of a suitable measure for temper brittleness. Temper brittleness is evidenced by an increase in the temperature of brittle failure of notched-bar impact specimens, but most of the data are in the form of an arbitrary susceptibility ratio of the room-temperature impact value for specimens quenched from a high tempering temper to that of similar specimens furnace cooled from the temper. It is obvious that this numerical ratio is dependent upon the type of specimen used and the specific conditions of testing rather than the characteristics of the steel. In general, manganese, chromium, and nickel alloy steels are most susceptible to temper brittleness and molybdenum has heen used to decrease

Jan 1, 1950

By Lowell B. Moon

Concern over possible wartime shortages finally resulted in passage of the Strategic Materials Act in 1939. As authorized by one section of this legislation, the Bureau of Mines proceeded to investigate deposits of seven strategic minerals with the objective of developing tonnages of low-grade material that could be mined in an emergency. During the war, the size of the program and the number of strategic minerals were increased, and the objective was the more immediate one of aiding production. Since the war, the size of the program has been reduced, but the number of minerals on the strategic list continues to be large. The objective has returned to that of 1939. In the course of the program, more than 10,000 examinations were made and about 1,300 projects were run on deposits of 33 different commodities. A considerable contribution to war production was made in six of the commodities investigated, and a minor contribution was made in twelve others. Substantial reserves have been indicated in 19 minerals. Private interest is currently active in some of the deposits developed in 14 commodities.

Jan 1, 1950

At an early stage of the examination of most prospects, samples are taken; and the sample values obtained play an important part in determining the subsequent history of the prospect. It is, therefore, important that. eveJJy effort should be made to interpret asfully as possible the meaning of the observed results. In this connection, it is suggested that examination of the assay values of mine samples by simple statistical methods may bring to light information of considerable value, which might otherwise be missed.Although expert statisticians may derive more information from the available data, those who are, like the writer, less proficient mathematically, may also benefit by applying quite simple statistical methods. At least they will develop a useful habit of thought bywhich they become aware at all times that sampling results only provide estimates of the truth, but that an assessment of the precision of such results may be possible. The object of this paper is to provide some evidence of. the truth of these statements, by theuse of a few very elementary statistical calculations.General.The idea that any mine sample is subject to error from a variety of causes is a very familiar one. Doubt always exists with regard to the representativeness of a perfectly cut sample, and other errors may arise through imperfections of sample cutting, crushing, splitting and assaying. Some causes of error may give rise to "constant" errors, others may cause variable but one-sided "systematic" errors, and others again may bring about variable results without any tendency toward bias on the average. In statistical language, mine sample values are subject to errors which may have either assignable causes or chance causes. The former are those which can be isolated, or should be capable of isolation, while the latter are those remaining when all assignable causes have been removed. A single constant assignable cause brings about bias in all results, and one or more than one variable assignable cause brings about variation between individual results and perhaps an overall bias. The system of chance causes that would remain if all assignable causes were removed would cause variation between individual results but no overall bias. There is no sharp practical line of distinction between the two types of cause) of error; nor is it ever possible by any method of statistical analysis to be certain that there are no assign...

Jan 1, 1950

By A. B. Needham

In November 1940, the Bureau of Mines started exploration of the Three Blacks manganese properties - Black Diablo. in Pershing County and Black Eagle and Black .Rook in Lander County. The purpose was to determine possible reserves of manganese in the deposits. It is reported that a small amount of manganese was mined from the Black Diablo during World. War 1. No mining except that necessary for assessment work had been done on the Black Eagle. Shipments were being made from the Black Rock deposit to a concentrator at Vain, Nev., while the Bureau's development work was progressing. The Black Diablo deposit consists of one patented claim owned by the Charleston. Hill National Manes Co. Mary L. Clough of Winnemicca, Nev., president. The deposit is about 20 miles by a gravel and dirt road southwest of Golconda, a town on U. S. Highway 40 and the Southern Pacific Railway, Pershing County, Nev. The deposit lies at an elevation of about 5,600 feet on the east flank of the north-south trending Sonoma Range. The property was leased by Messrs. Hollis Chatwin, T. E. Chatwin, and R. H. Richards of Salt Lake City and Mammoth, Utah. The lessees installed a crusher and erected an ore bin below the open cut on the deposit and mined and, shipped about 5,000 tons of about 30 to 52 percent manganese ore to the Columbia Steel Co., Provo, Utah.

Jan 1, 1950

By Herbert Clark Hoover, Lou Henry Hoover

Jan 1, 1950

By L. C. Armstrong

Twice in the past two years and in two widely separated localities—ane near Williamsville, Mo., and the other in the Allard Lake district of Quebec— the Contract Drilling Division of the Longyear Company has experienced perplexing difficulties in drilling granitoid igneous rocks. The rocks in both places are characterized by appreciable amounts of feldspar intimately inter-grown with quartz particles of microscopic dimensions. The disappointingly slow rate of advance and the exceptionally high bortz loss, obtaining during the life of these two projects, are ascribed largely to the resistance to abrasion of these two minerals when arranged in this intergrown pattern. Whether all intergrowth-bearing igneous rocks would offer extraordinary resistance to bit progress cannot be stated with assurance on the strength of these experiences alone. More data on diamond drilling this sort of material in a number of localities are needed before any generalizations can be made safely. It should be pointed out that the lack of time and funds made it impossible for the writer, or other persons interested in correlating the details of bit histories with the kinds of rocks drilled, to be present during the performance of the contracts. However, the records kept in the normal course of drilling are deemed complete enough to be reportworthy. This information is presented here together with the findings made in studies of the rocks involved, with the thought that it may attract the comments of others who may have encountered similar refractory drilling conditions. A pooling of knowledge on the problem would be of material aid in devising more efficient cutting tools and procedures for penetrating this kind of rock. Drilling Blastholes in the Williamsville Granite Due to the unsatisfactory perform- ance of pneumatic percussion drills in boring blastholes on a construction contract near Williamsville, Mo., tests were made with a diamond drill. The poor progress achieved and the excessive loss of diamonds, however, soon led to the abandonment of these trials. The diamonds, in all of the bits tried, lost their cutting edges and acquired a polish after being in service for distances ranging from a few inches to a few feet. Coring bits containing surface-set, whole-stone bortz in a tungsten powder matrix were employed. The cost assignable to bortz wear averaged $7.17 per foot. This item of expense is several times the amount normally expended in diamond drilling in firm, unfractured, granitic rocks. Diamond-impregnated, tungsten carbide bits also were used without success. The diamond wear was at the rate of $0.98 per foot, but the diamond chips became too polished for further duty in less than a foot of drilling. The Williamsville granite is pink and medium-grained. In the hand specimen, it has a fresh, sound appearance; it is seemingly composed almost entirely of interlocking grains of feldspar and quartz and has no discernible features suggesting a greater durability than is usually found in rocks with this composition and texture. Microscopic examination, however, reveals a predominance of feldspar grains with more or less regularly distributed and sharply angular masses of quartz (see Fig 1). The pattern assumed by the two minerals in this mode of occurrence is referred to as a "graphic intergrowth," as it bears some resemblance to the cuneiform characters of ancient Persian writing. The other principal constituents are quartz-free feldspars (microcline and orthoclase) and quartz. All of these constituents are in nearly equidimensional grains, ranging up to about 3 mm in length. There are also

Jan 1, 1950

By Joseph C. Mead, Alan Stanley

The MacIntyre Development of the National Lead Co. is located at Tahawus, N. Y. The operations involve the mining and concentrating of a titaniferous iron ore to produce an ilmenite concentrate and a magnetite concentrate. Construction of the MacIntyre plant was commenced during the summer of 1941,when world conditions threatened to cut off the supply of Indian ilmenite. An open pit mining operation was developed and the crushing and milling equipment put in operation in July 1942. A general description of the operation was given in the Adirondack Issue of Mining and Metallurgy for November 1943. The metallurgy of the mill operation was described by Mr. Frank R. Milliken,* Plant Manager, National Lead Company, MacIntyre Development, and presented at the AIME New York Meeting, February 1948. The magnetite concentrate produced in the milling operation was too fine (minus 20 mesh) to be used directly in iron blast furnace operation, and most of the magnetite had to be stockpiled in 1942 and 1943. In 1943, the Defense Plant Corp. built a Greenawalt sintering plant at Tahawus, N. Y., to put the magnetite concentrate in a more suitable form for use in the iron blast furnace. The Greenawalt sintering plant consists of three 10 by 25 ft sintering pans designed to produce 1800 gross tons of sinter per 24 hr. The vacuum to each pan is produced by two Greenawalt fans in series, pulling approximately 30,000 cu ft of air per minute at 50 in. water gauge vacuum. The plant started operation in August 1944. The present plant production averages 25 tons per operating pan hour (approximately 224 lb per operating hour per square foot of grate area) of plus 1 in. sinter. Raw feed to the plant consists of 61 pct magnetite, 4 pct anthracite coal culm, and 35 pct minus 1 in. return fines which are conveyed to a pug mill where the materials are mixed thoroughly and water added to give the mixture 5.5 to 6 pct moisture. The mixed prepared feed is conveyed to two 4 by 10 ft vibrating screens where the minus 1 in. plus 5/8 in. return fines are screened out and discharged into a surge bin for use as a hearth layer. The minus 5/8 in. prepared feed is discharged into another surge bin for use as prepared feed. A charge car, electrically operated, having a capacity of one charge of prepared feed and several charges of hearth layer, lays a thin layer of plus 5/8 in. return fines and 9½ in. depth of prepared feed into the pans. A fluffing roll and a vibrator on the car fluffs and spreads the prepared feed into the pans. An ignition car, electrically operated, ignites the top of the bed with a 30 sec flash burn. The 9½ in. bed sin-ters in approximately 13 min. Dumping the pan, and recharging and igniting the bed requires 2 min. To improve the quality of the ilmenite concentrate produced in the mill and to reduce the amount of titanium dioxide lost in the mill tailings and in the magnetite product, extensive research work and pilot plant operations have been done on grinding the crude ore to minus 65 mesh size (rather than to minus 20 mesh) and concentrating it by a combination of magnetic separation (for magnetite recovery) and flotation (for ilmenite re-covery). These tests have proved successful in increasing ilmenite re-covery and grade. With the development of the ilmenite flotation process to a stage where a full scale flotation plant was in the design stage, the problem arose of handling the 65 mesh magnetite concentrate that would be produced. In order to study and solve the problems of handling and sintering the 65 mesh magnetite in the sinter plant, a pilot sinter plant was secured from John E. Greenawalt. The effect of using 65 mesh magnetite in the sintering operations was then studied on the 2.4 sq ft test pan, operating under conditions as similar to the large plant as could be set up in the laboratory. A series of tests were run in the test pan on present sinter plant feed that had been mixed in the plant pug mill. An average production and an average quality of sinter produced in this series

Jan 1, 1950

By Herbert Clark Hoover, Lou Henry Hoover

GEORGIUS AGRICOLA was born at Glauchau, in Saxony, on March 24th, 1494, and therefore entered the world when it was still upon the threshold of the Renaissance ; Gutenberg's first book had been printed but forty years before ; the Humanists had but begun that stimulating criticism which awoke the Reformation; Erasmus, of Rotterdam, who was subsequently to become Agricola's friend and patron, was just completing his student days. The Reformation itself was yet to come, but it was not long delayed, for Luther was born the year before Agricola, and through him Agricola's homeland became the cradle of the great movement ; nor did Agricola escape being drawn into the conflict. Italy, already awake with the new classical revival, was still a . busy workshop of antiquarian research, translation, study, and publication, and through her the Greek and Latin Classics were only now available for wide distribution. Students from the rest of Europe, among them at a later, time Agricola himself, flocked to the Italian Universities, and on their return infected their native cities with the newly-awakened learning. At Agricola's birth Columbus had just returned from his great discovery, and it was only three years later that Vasco Da Gama rounded Cape Good. Hope. Thus these two foremost explorers had only initiated that greatest period of geographical expansion in the world's history. A' few dates will recall. how far this exploration extended; during Agricola's lifetime. Balboa first saw the Pacific in 1513 ; Cortes entered the City of Mexico in 1520; Magellan entered the Pacific in the same year ; Pizarro penetrated into Peru in 1528 ; De Soto landed in Florida in 1539, and Potosi was discovered in 1546. Omitting the sporadic settlement on the St. Lawrence by Cartier in 1541, the settlement of North America did not begin for a quarter of a century after Agricola's death. Thus the revival of learning, with its train of Humanism, the Reformation, its stimulation of exploration and the re-awakening of the arts and sciences, was still in its infancy with Agricola. We know practically nothing of Agricola's antecedents or his youth. His real name was Georg Bauer (" peasant "), and it was probably Latinized by his teachers, as was the custom of the time. His own brother, in receipts

Jan 1, 1950

By H. E. Lee, P. C. Feddersen

846 . . . Metals Transactions, Vol. 185 T. J. WOODSIDE*—In the paper it was stated that many of the A. S. and R. plants probably used a process patented by Roscoe Teats in 1930. I might describe

Jan 1, 1950

By D. Turnbull, A. M. Turkalo

It is well known that if copper that has been severely cold-worked by rolling (70-98 pct) is heated to high temperatures a small number of large grains are formed at the expense of the fine grained structure that appears upon primary recrystallization. Dahl and Pawlek,' Cook and Mac-Quarie,2 Ward,3 and Boas and Bowles4 have studied this phenomenon in copper. It has been reported as taking place with measurable velocities in the temperature range 700-1080". Boas and Bowles have reported that the time necessary for the transformation is of the order of days at 700°C. According to Ward3 the number of secondary grains which appear in OFHC copper decrease with increasing perfection of cubical alignment after primary recrystallization; also the perfection of cubical alignment increases with decreasing grain size prior to the final reduction. In this investigation two heats, A and B, of especially high purity copper (99.999 pct) supplied by the American Smelting and Refining Co., were used. The behavior of samples prepared from the two heats was qualitatively very similar providing that the grain sizes established prior to the final reduction were about the same. We observed that in specimens prepared from bars which were relatively coarse grained prior to final reduction secondary recrystallization took place at a rapid rate at temperatures as low as 500°C. This is about 200-300°C lower than the temperature necessary to obtain fairly rapid transformation in OFHC copper. A 0.22 in. thick rectangular bar of lot B was cold-reduced 60 pct by straight rolling and given a penultimate annealing treatment at 250°C. Following this it was cold-reduced 90 pct and heated to various temperatures in the range 450-1040°C. The specimens were about 8 mils thick

Jan 1, 1950