By N. P. Haran

A detailed study was undertaken to beneficiate sub-grade iron ore sample from Kenojhar District, Orissa, India containing 57% Fe (T), 7.7% SiO2, 4.8% Al2O3, 4 % L.O.I. 0.4% TiO2,1.3 % Mn and traces of S(T) to make it suitable for the user industry. The mineralogical study indicated that it predominantly consists of haematite with subordinate amounts of goethite and clay. Quartz, Cryptomelane / Psilomelane, Pyrolusite, Gibbsite, Feldspar and Muscovite mica were present in very minor to trace amounts. The Denver grind ability tests indicated, that the sample could be categorized as ?medium soft to medium.? The Bond ball mill work index was determined to be 14.19 kwh per short ton. The beneficiation process involved classification followed by tabling of the classified sand, ground to minus 48 mesh size. The table slimes were subjected to Wet High Intensity Magnetic Separator (WHIMS). The developed process yielded a composite concentrate from tabling and WHIMS operations assaying 65% Fe(T), 2% SiO2, 1.8% Al2O3, 2% Mn and 0.9% LOI with a recovery of 60.1% Fe (T), amounting to 52.5 wt.% yield. To meet the size specifications for pellet making, it was further ground. Dewatering studies were also carried out on the ground combined concentrate and rejects. The thickener area of ground combined concentrate using 0.02 kg/t of Sufloc A 1115 flocculant was 0.02 m2/tonne of dry solids per 24 h. And for the combined rejects using 0.12 kg/t of flocculant, it was 0.035 m2/tonne of dry solids per 24 h. The moisture content, in the pressure filtration cake, in the ground combined concentrate product was 10.0%, and productivity was 506.7 kg/m2h. Thus, by thickening and filtration of process products, 90% of water used in the process could be recovered. The study highlights the development of a simple and cost effective flowsheet with almost complete water recovery for a subgrade iron ore sample. Keywords: tabling, WHIMS, thickener, filtration

Sep 1, 2012

Taknar polymetal (Cu-Zn-Au-Ag-Pb) deposit and concentration flotation plant are located in the northeast of Iran. The flotation feed contains Chalcopyrite, sphalerite and pyrite with 4, 4 and 8 percent respectively. Cu and Zn contents are 1.26 and 3.5 present. Pyrite decreases the quality of base metal concentrates and increases the amount of sulfur compounds produced in the base metal extraction processes. Therefore, depression of pyrite is essential in the concentration of base metal sulfides by flotation. For flotation tests, 4 mixed collector systems, MIBC (20g/t), lime and tow depression systems (sodium cyanide (60g/t)-zinc sulphate and dextrin (300g/t)-zinc sulphate) were used as collector, frother, pH regulator and pyrite-sphalerite depressants in the chalcopyrite flotation stage, respectively, and SIPX, MIBC, lime and copper sulphate (as activator) were used in sphalerite flotation from first stage tailings. The results have shown that, sodium cyanide is a suitable depressant for pyrite and sphalerite in the first stage of flotation. Compared to dextrin as depressant, chalcopyrite recovery was decreased approximately 1.83%. In addition, when sodium cyanide was used as pyrite depressant, copper sulphate consumption raised approximately 90 g/t for activation of sphalerite. From Environment and HSE points of view, dextrin is natural, biodegradable, and non-toxic while cyanide is very high toxic. Keywords: sequential flotation, Cu-Zn massive sulphide, pyrite depressant, dextrin, cyanide

Sep 1, 2012

By B. McFadzean, S. Geldenhuys

"Dynamic froth stability tests have found widespread application to quantify froth performance. However, little to no attention has been given to scale parameters in the performance of these measurements. One of the most frequently changing scale parameters in the laboratory scale is the column diameter as this directly influences the amount of material needed for testing. Four different column diameters (50, 100, 200 and 300 mm) were used for this study. Column diameter experiments were done on an industrial scale by means of manual tracking of froth growth versus time. An increase in measured dynamic stability was seen with increasing froth column diameter, which reached a limiting value at large column sizes. It is thought that this behaviour is controlled by the differences in drainage rates of the bulk froth compared to froth in contact with the wall. The column diameter required to represent full-scale froth stability is proposed. A ratio of column surface area to total bubble surface area was used to correct for different column diameters.INTRODUCTIONThe froth phase in flotation contributes significantly to the overall performance of the process (Zanin, et al., 2009). Numerous parameters have been investigated to quantify froth performance, most notably froth recovery (Feteris, et al., 1987; Seaman, et al., 2004; Vera, et al., 1999). Experimentally gathering data to determine froth recovery is challenging and for this reason froth stability has been highlighted as a possible alternative.Froth/foam stability is defined as the time of persistence of the froth/foam and is affected by numerous factors, such as: drainage of the liquid in the lamellae (gravitational and capillary), viscosity at the bubble surface, thickness of the electrical double layer and gas diffusion through liquid films caused by pressure differences between bubbles (Aktas, et al., 2008; Beneventi, et al., 2001). It is well documented in both froth and foam literature that froth/foam stability will heavily influence the performance and appearance of the froth/foam phase (Ata, 2012; Farrokhpay, 2011; Weaire, et al., 2005). Experimentally this has been explicitly proven as an increase in froth stability, characterised by water recovery, usually results in an increase in both valuable mineral and solids recovery (Wiese, et al., 2011; Banford, et al., 1998)."

Jan 1, 2018

By E. Guerrini, M. Maccagni, J. Nielsen

"The solution for the treatment of the EAFD has not yet been fully achieved. Some of this dust has still not found an appropriate final destination. Large consortium treatment plants are quite expensive both in terms of investment and operating cost. Meanwhile, the tolling expenses for steel production companies are becoming very important, causing them to look for alternatives. Some steel plants are looking to close their production loop by internal treatment of their dust. Some years ago, Engitec began studying the coupling of the EZINEX® Process, an ammonium chloride electrolysis to recover the zinc contained in the EAFD, with the INDUTEC® Process, a pyro process based on an induction furnace that can convert EAFD into a C.Z.O. similar to the Waelz oxide. The combination of these two processes provides an alternative to the existing treatment options and is particularly interesting for relatively small capacities. In this paper, we would like to give the latest update about these two processes and their possible integration INTRODUCTION Zinc is contained in numerous wastes and secondary raw materials that can be thought of as high zinc concentrate mines. This is a very interesting source of Zn that is typically easily exploitable. Unfortunately, only a portion of these materials are currently processed to recover the metal value, while stabilized or unstabilized landfilling is often the final destination. Pyrometallurgical processes are mainly used to convert the zinc into crude zinc oxide (CZO). The various processes are very similar and characterized by the fact that the zinc bearing materials are usually submitted to a thermal treatment [1] in which the zinc is reduced, vaporized and re-oxidized producing CZO. This material not only contains zinc oxide, but also relatively high concentrations of heavy metals. Many potential CZO sources, such as electric arc furnace dust (EAF), galvanizing ashes, brass foundry and converters fumes also contain chlorides, fluorides and alkali metals that will transfer to the CZO. The classic example is the Waelz oxide [2]. This CZO is an intermediate product that must be transformed into zinc salts or zinc metal. Until now, the conversion to zinc metal is done through two main processes: the sulphate leaching and electrowinning system and the Imperial Smelting Process (ISP). ISP is facing a crisis for technical and economic reasons that has led to the closing of most of the existing plants. In any case, before being fed to one of these two processes, the CZO must be treated to eliminate or reduce some of the contained impurities. In particular, the halides are most harmful to these processes."

Jan 1, 2018

By E. Guerrini, M. Maccagni, J. Nielsen

"The solution for the treatment of the EAFD has not yet been fully achieved. Some of this dust has still not found an appropriate final destination. Large consortium treatment plants are quite expensive both in terms of investment and operating cost. Meanwhile, the tolling expenses for steel production companies are becoming very important, causing them to look for alternatives. Some steel plants are looking to close their production loop by internal treatment of their dust. Some years ago, Engitec began studying the coupling of the EZINEX® Process, an ammonium chloride electrolysis to recover the zinc contained in the EAFD, with the INDUTEC® Process, a pyro process based on an induction furnace that can convert EAFD into a C.Z.O. similar to the Waelz oxide. The combination of these two processes provides an alternative to the existing treatment options and is particularly interesting for relatively small capacities. In this paper, we would like to give the latest update about these two processes and their possible integration INTRODUCTION Zinc is contained in numerous wastes and secondary raw materials that can be thought of as high zinc concentrate mines. This is a very interesting source of Zn that is typically easily exploitable. Unfortunately, only a portion of these materials are currently processed to recover the metal value, while stabilized or unstabilized landfilling is often the final destination. Pyrometallurgical processes are mainly used to convert the zinc into crude zinc oxide (CZO). The various processes are very similar and characterized by the fact that the zinc bearing materials are usually submitted to a thermal treatment [1] in which the zinc is reduced, vaporized and re-oxidized producing CZO. This material not only contains zinc oxide, but also relatively high concentrations of heavy metals. Many potential CZO sources, such as electric arc furnace dust (EAF), galvanizing ashes, brass foundry and converters fumes also contain chlorides, fluorides and alkali metals that will transfer to the CZO. The classic example is the Waelz oxide [2]. This CZO is an intermediate product that must be transformed into zinc salts or zinc metal. Until now, the conversion to zinc metal is done through two main processes: the sulphate leaching and electrowinning system and the Imperial Smelting Process (ISP). ISP is facing a crisis for technical and economic reasons that has led to the closing of most of the existing plants. In any case, before being fed to one of these two processes, the CZO must be treated to eliminate or reduce some of the contained impurities. In particular, the halides are most harmful to these processes."

Jan 1, 2018

By S. Groudev

Acid drainage waters generated in the uranium deposit Curilo, Bulgaria, were treated by means of a pilot-scale passive system consisting of a permeable reactive multibarrier and a constructed wetland connected in a series. The multibarrier had a total volume of 23 m3 and consisted of an alkalizing limestone drain and an anoxic section for microbial dissimilatory sulphate reduction, bio-sorption and additional chemical neutralization. The waters had a pH in the range of about 2.5 ~ 4.0 and contained radionuclides (uranium, radium), heavy metals (copper, zinc, cadmium, lead, nickel, cobalt, iron, manganese), arsenic and sulphates in concentrations usually much higher than the relevant permissible levels for waters intended for use in agriculture and/or industry. The water flow rate through the multibarrier varied in the range of about 1 ~ 17 m3/24 h, reflecting water residence times of about 300 ~ 18 hours. An efficient removal of pollutants was achieved by the multibarrier during different climatic seasons, even during cold winter days at external air and water temperatures close to 0oC. The multibarrier effluents were enriched in dissolved organic compounds and in some cases still contained manganese and iron in concentrations higher than the relevant permissible levels. These pollutants were removed in the constructed wetland as a result of the activity of different heterotrophic microorganisms, including some bacteria able to oxidize the bivalent manganese and iron ions to Mn4+ and Fe3+, respectively.

Jan 1, 2014

By Yagmur Sirinyurt, Ayhan Ali Sirkeci, Gülay Bulut, Mustafa Özer, Tuncer Acar

"The basic requirement of glass industry for the silica sand is at least 99% SiO2 content. On the other hand, coloring impurities such as Fe and Ti, must be removed. Flotation is the most widely used method for the purification of silica sands from impurities. In this study experimental studies were carried out to reduce Fe content of Mersin (Turkey) district silica sands by flotation. Silica sand sample with a d80 particle size of 1.85 mm was reduced below 0.5 mm in size. Then the size fraction -0.5 +0.106 mm was subjected to flotation tests. In flotation tests, sulfonate-type R801-R825, fatty acid based DER NA 7 (Produced by a Turkish company) and HA110-HA150 a blend of various chemicals produced by Mersin Cam-Is Mining Company (producer of glass raw materials) were used as collectors. Flotation tests showed that sulfonate type R801-R825 collectors provided much better results in acidic medium (pH: 3). The optimum pH value for DER NA, HA150 and HA110 collectors was found to be 7. It was observed that the addition of collector at once caused an increase in the amount of floated product that resulted in a loss of silica to the tailings. In the case of multistage addition of the collector much better selectivity was achieved. As a result of flotation tests conducted under best conditions, a concentrate assaying 0.046% Fe was obtained with a weight percentage of 93.4 when DER NA 7 was used as a collector. In the case of R801-R825 a concentrate was produced with 0.058% Fe content with a yield of 98.4%. On the use of HA150-HA110 the concentrate was produced with 96% weight recovery and 0.052% Fe content."

Jan 1, 2014

By Tilak Raj Mankhand, Mudila Dhanunjaya Rao, Kamalesh K. Singh

"Zinc dust is used for the removal of primary impurities by cementation from the zinc sulphate electrolyte before electrowinning of zinc. However, the industrial zinc electrowinning plants has been reported that the zinc dust consumption is in large excess than the stoichiometric requirement. In the present investigation, morphology of the zinc dust has been altered by ball milling and utilized for the cementation of cadmium, which is one of the major impurity and compared the change in the rate of cementation with original zinc dust. Initially, 325 mesh size zinc dust was used for the optimization of the excess quantity of zinc dust to be used at a temperature of 50 °C. The chemical analysis of zinc dust before and after ball milling and morphology were studied by scanning electron microscopy (SEM), and the solution was characterized by Atomic Absorption Spectrophotometer. The rate of cementation increased with increase in ball milling time. The residual precipitate obtained after filtration was also characterized by X-ray diffraction analysis. Finally experiments were conducted to study the effect of temperature and kinetics of cadmium cementation using first order reaction kinetics. Based on the integral method, the calculated activation energy for the cadmium cementation with 4-hours ball milled zinc dust was found to be 3.39 KJ/mole. INTRODUCTION Primary production of zinc in the world is carried out by hydrometallurgical route. The primary impurities in the neutralized zinc sulphate solution that cause negative effect on electrowinning are copper, cadmium, cobalt, and nickel. Copper diminishes the current efficiency and cadmium contaminates the cathode zinc (Morgan, 1977) while electro winning. Nickel and cobalt lead to perforation in the zinc deposit and prevents the electro winning process (Abrasheva et al, 1984). Due to higher electro positivity of these metal impurities than zinc, they can co-deposit with cathode zinc at the time of electrolysis. In addition to that, some possible impurities (including cobalt) in the electrolysis may lower the hydrogen overvoltage, allowing deposition of hydrogen at cathode resulting in fall of current efficiency. The deposition of zinc on the cathode is possible only at higher hydrogen overvoltage which is practicable in the absence of such impurities (Raghavan et al., 1999). Cementation is one of the prominent purification technique, and in that less reactive metal can be replaced by highly reactive metal by allowing them into precipitation. Cementation of cadmium from zinc sulphate electrolyte is being done by the addition of zinc dust."

Jan 1, 2018

By I. Nishkov, I. Grigorova, M. Ranchev, S. Dzhamyarov

"Chelopech concentrator (part of Dundee Precious Metals) is located in central-western Bulgaria. The current process plant utilizes conventional primary crushing and SAG mill grinding, copper and pyrite rougher and cleaner flotation stages to produce a marketable gold-rich copper and pyrite concentrates. As in the most processing plants, the pyrite depression is carried out alkaline media using lime. The subsequent activation of pyrite mineral is achieved by adding sulfuric acid, which has an adverse effect on the flotation equipment. Therefore, a series of laboratory flotation experiment for activation of lime depressed pyrite by ammonium salts, such as ammonium chloride (NH4Cl), ammonium sulfate (NH4)2SO4 and ammonium bicarbonate (NH4HCO3), have been conducted. The obtained results showed that ammonium bicarbonate proved to be the most appropriate reagent choice for pyrite mineral activation. These results are confirmed by X-ray photoelectron spectroscopy (XPS), performed to determine the surface chemistry of pyrite in its natural state, after lime treatment and subsequent treatment by NH4HCO3. The registered XPS spectra indicate that the hydrophilic phases on the pyrite surface could be efficiently removed by using the ammonium salt NH4HCO3. The industrial use of NH4HCO3 as an activator of lime-depressed pyrite is a possible alternative for sulfuric acid replacement as a most widely used pyrite activator. Flotation experiments with addition of 200, 400, 600 and 800 g/t from each of the studied ammonium salts have been conducted. Furthermore, the impact of the flotation pulp pH within the scope of 9.00 – 10.50 was also investigated. The obtained results from the laboratory flotation experiments, showed that the pyrite activation with ammonium bicarbonate is an excellent possibility for replacing the sulfuric acid as main pyrite activator reagent, in order to eliminate the gypsum accumulation during the flotation of pyrite in Chelopech concentrator.INTRODUCTION The Chelopech deposit, located about 60 km east of Sofia is one of the largest Cu-Au deposits in Europe. The ore have complicated mineralogical and chemical composition. The main ore minerals are represented by pyrite, enargite (luzonite), tennantite, chalcopyrite and bornite. The average copper content of the mined ore is about 1.1 % and the gold content is about 4.0 g/t."

Jan 1, 2018

By C. A. Acuña

Extensive literature exists on the motion of single bubbles and the behaviour of swarms of bubbles. This contribution describes work to track and reveal the motion of individual bubbles in a swarm. The technique is based on high speed cinematography and tracking of multiple moving objects. Image processing algorithms were implemented in Matlab to isolate and measure geometric proper-ties of the bubbles in image sequences recorded at 2 ms interval; and these properties were compiled into a data structure. To track a bubble, the geometric properties and a matching criterion were applied on consecutive pictures to identify the bubble. The bubble trajectory was reconstructed from the data structure for the matched objects. The methodology is briefly described. The new technique was tested for bubbles produced at slot-type spargers (i.e., approximately 2-D swarms) in the presence of two frother types ('strong' and 'weak'). Two observations are discussed: a) that bubble motion in a swarm describes a velocity-size relationship dictated by the dominant bubble size class; and b) that surfactant type influences bubble rise velocity for bubbles in the range 0.1 mm to 4 mm. The latter suggests surface viscosity rather than surface immobilization determines bubble rise velocity.

Jan 1, 2014

By Ritva Tuunila, Antti Häkkinen

"Wet stirred milling is one of the most effective grinding methods in producing very fine powders in large scale production, but it is a very energy-intensive process, especially when pigments or even nanosize particles are produced. Therefore, optimization of the process parameters is important. The specific energy consumption is a function of stress energy, which describes the effect of tip speed and media characteristics on grinding, and is related to the number of stress events during milling. In effective grinding, a large number of stress events are necessary. The stirrer configuration influences the number of stress events and their intensity, because the motion of the media and the suspension are caused by a rotating stirrer. The effect of three different stirrer types: a pin, disc and blade stirrer, on the grinding rate, i.e. product fineness and specific energy were investigated in this study with a batch laboratory stirred mill with two tip speeds. The material used in the experiments was calcium carbonate. The results obtained with the smaller tip speed showed approximately similar grinding rates and energy consumption for all stirrer types. When looking in closer detail, the blade stirrer seemed to give the finest product with all grinding times compared to the pin and disc stirrers, which both produced almost the same product fineness with the same grinding times. The specific energy consumption was the smallest with the disc stirrer, but not very big differences were obtained. With a higher tip speed, greater differences occurred both in grinding rates and specific energy consumption. The blade stirrer was the most effective in grinding, and the pin stirrer the next. The net energy consumption for the blade and pin stirrers was almost the same, but it was slightly higher for the disc stirrer."

Jan 1, 2014

By Gabriel Barrios, Juan Pérez-Prim, Marcelo Tavares

"The application of High Pressure grinding Rolls (HPGR) has been growing in the mining industry for the last 10 to 15 years. The major benefits generally supporting this trend are better energy efficiency, improved grinding capacity, less sensitivity to ore grindability variations and higher metal recovery in downstream processes such as heap leaching and flotation. The HPGR machine comprises a pair of counter-rotating rolls mounted in a sturdy frame. One roll is fixed in the frame, while the other is allowed to float on rails and is positioned using pneumohydraulic springs. The feed material is introduced in the gap between the rolls and is crushed by the mechanism of interparticle breakage. Comminution performance is largely determined by the pressure exerted on the bed of particles by the floating roll hydraulic system. The operating bed pressure depends on the hydraulic system start-up parameters and the loading response of the feed material. The work describes how the coupling of the multi-body dynamic simulation with Discrete Element Method in which particle breakage is described using the particle replacement method, can be effectively used to predict the performance of the HPGR. The model considers important variables as the HPGR rolls geometry and design, the hydraulic spring system start-up parameters and the material loading response, to describe operational key outputs as material throughput, operating gap and roller pressure distribution. The preliminary version of the model has been used to predict the effect of material properties on the operating gap and the load distribution on the surface of the rolls, demonstrating that it can describe qualitatively the HPGR operation, indicating that the model will be a power full tool for the simulation and selection of industrial HPGR units."

Jan 1, 2014

By A. R. Videla, P. R. Brito-Parada, I. Mackay

"Linking results from laboratory scale experiments to industrial flotation behaviour is challenging. Typically, such experiments involve batch tests in which the system does not operate at steady-state, making it difficult to infer the effects that operating conditions have on flotation performance. In order to overcome this limitation a 4-litre recirculating tank was previously developed at Imperial College London. This tank is capable of reaching, and operating at, steady-state by recycling overflowing concentrate back into the feed. As well as instruments to control operating conditions, it is fitted with a system of sensors that allow the surface of the froth to be dynamically monitored. From this information, it is possible to measure the air recovery—a proxy for froth stability. Thus, this bench-scale tank can be used to understand the effect of differing operating conditions on flotation performance at steady state. However, so far, this cell has only been used to investigate idealised systems with only one or two species.Reprocessing of tailings dams is not only environmentally desirable but also increasingly economically feasible due to the declining head grades of primary deposits. There is also the added benefit of no further milling being required prior to flotation. However, the effects of fine and ultrafine particles on froth stability are not yet fully understood. In this work, the bench-scale continuous tank has been used for the first time to determine the flotation response of a complex feed, consisting of samples from a copper tailings dam, to changes in operating conditions. It was shown that the froth stability in the system is comparable to that of previous work and industrial tests, with a peak in air recovery being found at a superficial gas velocity of 1.13 cm/s. There is scope to optimize the froth stability of tailings flotation for enhanced metallurgical performance."

Jan 1, 2018

By F. Boylu

In this study, Ca-bentonite was subjected to a series of systematic hydrocyclone tests with the aim of developing separation procedures and in turn achieving optimum recoveries. In hydrocyclone tests, vortex and apex diameters and also feed pressures were investigated. In each hydrocyclone set, vortex diameter was kept constant while the other two parameters varied to produce bentonites con-centrates of various smectite contents. The separation efficiencies were evaluated based on the cation exchange capacity (CEC), particle size and swelling index. The detailed hydrocyclone tests showed that, upgrading of Ca-bentonites require procedures different from the bentonites reported in the literature. Sodium and mixed bentonites are easy- to-disperse and easy-to-separate whereas calcium types need to be scrubbed rigorously for disintegration. Scrubbing properties of ca-bentonite were investigated as a function of scrubbing time and percent solids by weight (PS). The scrubbing conditions at 700 rpm for 1.5 hours and percent solids of 30 % were found more effective for achieving a better quality bentonite. In addition to the parameters mentioned above, the effect of percent solids on hydrocyclone separation was also studied. Although Ca-bentonites permit studying at higher percent solids, increasing solids content of the pulp deteriorated the quality of the clean products. Application of an appropriate separation scheme enabled the development of a unique separation procedure involving stage wise scrubbing followed by hydrocycloning which yielded calcium bentonite concentrates with CEC of 90 meq/100 g and high swelling indexes of 12 mL from the original bentonite of 65 meq/100 g and 7.0 mL, respectively. These results indicate that upgraded bentonite products can be conveniently used in various diverse industrial applications including bleaching earth, desiccant, cat litter, paper etc.

Jan 1, 2014

By Kazutoshi Haga, Atsushi Shibayama, Altansukh Batnasan

The objectives of this study were to propose a viable alternative method for recovery of precious metals such as gold (Au), silver (Ag) and palladium (Pd) from waste printed circuit boards (WPCBs) and to regenerate the spent lixiviant solution for reuse. The proposed method generally consists of several steps as follows: 1). iodine-iodide leaching for metals extraction; 2). separation and recovery of precious metals and metal impurities from a pregnant leach solution; 3). regeneration of the spent iodine-iodide solution/lixiviant. In this method, more than 99% of Au leaching was achieved in the iodine-iodide solution from the solid residue of WPCBs that was obtained via sequential processes including incineration at 800 ?C and high pressure oxidative leaching with a diluted sulfuric acid at 120 ?C, while the leaching of Ag and Pd was less than 1%, respectively. Besides Ca, Cu, Ni, Co and Zn as main metal impurities, leaching efficiency of other metals did not exceed 1%. The precious metals and base metals as metal impurities present in the pregnant leach solution were separated and recovered by precipitation using L-AA and NaOH solutions. About 99.8% Au, 81.7% Ag and 72.8% Pd were recovered from the pregnant solution at pH of 2 with the addition of 0.1 M L-AA as precipitating agent. The remained small amounts of precious metals and metal impurities were precipitated at pH 13 using 1 M NaOH. The spent lixiviant after sequential precipitation was regenerated in the presence of hydrogen peroxide, hydrochloric acid and potassium iodide. It was revealed that over 90% of gold could be extracted from the residue of WPCBs with the regenerated lixiviant solution.

Jan 1, 2018

By Johan F. W. Kock

"Hearing loss due to excessive noise exposure is the most prevalent industrial disease. It is ranked on the World Health Organization’s (WHO) priority list for major work related injuries. Uncontrolled noise not only has a physical effect, but is also a psychological hazard affecting the performance and well being of man. Noise induced hearing loss (NIHL) is irreversible, yet it is preventable. The first defence against noise (noise control engineering) is a high priority in the mining industry. Second defences should be a last resort when the engineering control of noise is inadequate. Hearing conservation programs and the use of conventional hearing protection devices seem to have failed in the prevention of noise induced hearing loss. If compensation payouts that quadrupled in the past ten years are used as a barometer for the success of existing hearing conservation programs, then new strategies and technologies need to be investigated. The best practice Hearing Protection Device (HPD) may be seen as the minimum standard for second defence noise control.Conventional hearing protection is widely applied, but also misused in the industry as well as in the mining sector. Empirical research results, ownership, general attitudes of workers as well as qualitative aspects will be explored. The paper provides reasons, evidence, case studies and strategies regarding the best practice hearing protection philosophy (the Noise Clipper Model) as implemented in the Implats Mining Group. Worldwide tendencies towards custom-made HPD’s, findings that indicate improvements in hearing conservation programs and finally the successful application of Custom-made Hearing Protection Devices, will be outlined."

Jan 1, 2003

By S. Fiore, M. C. Zanetti, C. Clerici

The processes and fluxes of a cast iron foundry plant located in the North of Italy were analyzed in order to determine the amount and kind of wastes produced from the different activities. The main fractions are the molding sands, furnace muds and powders coming from the dust abatement plant, the exhaust lime, the furnace refractory, the metallic shotting and the sludges and powders coming from the dust abatement plant of molding lines for a total production equal to 800 t/d. All wastes were sampled and particle-size and chemically characterized to evaluate the best recycling or reuse solutions. Wastes were sieved and divided in three categories according to the particle-size dimensions: below 0.1 mm, between 0.1 and 0.6 mm and above 0.6 mm. The fraction above 0.6 mm dimension underwent magnetic separation to recover and quantify the potentially available iron fraction. The fraction between 0.1 mm and 0.6 mm was chemically characterized in order to understand if it could be fed to the sand regeneration plant. The below 0.1 mm fraction was characterized to evaluate the following recycling and reuse solutions: additive for molding sands and/or raw material for the concrete industry.

Jan 1, 2003

By J. Y. Liu

The comminution in a high-pressure roller mill is modeled by an energy-based population balance approach considering three aspects of breakage taking place in the active zones of the mill: the interparticle breakage in the high-compression zone, the breakage at the edges of the rolls, and the pre-breakage in the acceleration zone. Together with an appropriate model of classification, this model can be used to simulate steady-state performance of closed-circuit grindings with high-pressure roller mill. After a brief description of the basic modeling approach, the algorithm of the steady-state calculation for a generalized grinding-classification circuit is presented, from which the circuit configurations commonly met in industrial practice can be derived. With an iron ore as feed material for example, simulation results are shown and discussed in respect of circulating load, specific energy consumption and product fineness for closed-circuit grindings under various operating conditions. The effects of stressing intensity, working gap, classifier parameters as well as circuit configuration on the overall circuit performance are investigated systematically by means of computer simulation.

Jan 1, 2014

By Shibayama A.

In this research, an investigation of a process to selectively remove arsenic (As) and antimony (Sb) contained in enargite (Cu3AsS4) and tennantite/tetrahedrite ((Cu1,Fe)12(As,Sb)4S13) copper resources by leaching and precipitation were performed. First in the leaching process, the target was to selectively leach As/Sb and reduce their contents in the ores to <0.5 wt% followed by a second process to remove As/Sb dissolved in solution for environmental control. Enargite ore contained 3.65 wt% As while tennantite/tetrahedrite ore contained 5.40 wt% As and 4.85 wt% Sb. Alkaline leaching using NaHS?NaOH media at varying experimental conditions (temperature, pulp density, time, reagent concentrations) were performed to investigate the process. As/Sb precipitation studies were also performed to control high As/Sb concentrations in leach solutions by using elemental sulphur (So). Results from leaching studies showed that over 99% of As/Sb in the impure copper ores can be removed and their contents in the final solids reduced to <0.5 wt%. It was also established that such very high leaching could be achieved at 80°C within 1?6 h and pulp densities as high as 1000 g/L. The study also revealed that leach solution containing very high As/Sb concentration ranging from 5 to 20 g/L can be used as fresh solution for leaching of fresh ores until concentrations exceeding 35 g/L when it was sent to precipitation circuit for As/Sb removal. Addition of elemental sulphur at 90°C and fast cooling to 30°C allowed over 60% As/Sb precipitation and removed as Na3AsS4 and solution with reduced As/Sb concentration to leaching circuit for continuous use. Keywords: Enargite; Tennantite/Tetrahedrite; Selective Leaching; Precipitation; Sodium hydrosulfide;

Sep 1, 2012

By Y. H. Tang

For its surface features, micro-sized hematite is usually difficult to recover by magnetic separation; especially, the existing high gradient magnetic separator in industry can not utilize collecting matrix with thin silky rods for its property of being easily blocked; the lower size limit for recovery of micro-sized weak magnetic minerals is about 0.019mm, some even is 0.037mm. This paper introduces the application of the combined new technique of water-air joint discharging of concentrate and collecting matrix with different diameter silky rods in the field of recovery of micro-sized hematite by high gradient magnetic separator. The commercial test result for recovery of a certain hematite with size about ?0.037mm shows that the recovery can be promoted by 16.81% with basically same concentrate grade.

Jan 1, 2014