By W. C. Ellis, E. S. Greiner, M. E. Fine

Discontinuous changes of Young's modulus, internal friction, coefficient of expansion, electrical resistivity, and thermoelectric power are evidence for a transition in chromium near 37OC. Although the X-ray diffraction pattern gives no clue, a difference between the thermal expansivity and the temperature dependence of the lattice parameter suggests a crystal-lographic change. Young's modulus data disclosed another transition near THE thermal dependence of a number of proper- ties of chromium indicates a transition occurring over a temperature range near room temperature. Bridgman' noted this first from a minimum in the electrical resistivity near 12°C. In a sample of greater purity, Sochtig' observed the minimum at 41 °C. Erfling3 reported an inflection in the thermal expansivity curve at 36°C. These temperature-dependence curves are reversible with no hysteresis being detected. No discontinuity or inflection has been observed in the heat capacity' or the paramagnetic susceptibility.' Likewise, no one has noted a change in crystal symmetry. In the present investigation Young's modulus, internal friction, coefficient of expansion, electrical resistivity, illustrated in Fig. 1, lattice constant, Fig. 2, thermal electromotive force, Fig. 3, and paramagnetic susceptibility, Fig. 4, were measured over an extended temperature range. The samples were prepared in two ways: (1) By cold pressing a sintered electrolytic powder compact,' and (2) by electroforming from an aqueous solution. The electroformed samples were prepared by R. A. Ehrhardt and G. Bittrich by plating on copper or nickel tubes from an aqueous solution according to the method of Brenner, Burkhead, and Jennings.' The pressed powder samples (method 1) were finally annealed at 1400°C in purified helium: the electroformed samples, packed in powdered chromium, were vacuum-annealed at 1000°C. From the composition of the original powder' the purity of the pressed powder samples is estimated to be 99.8 pct Cr. Spectrochemical analysis furnished by E. K. Jaycox, revealed only slight traces of impurities in the electroformed sample (less than 0.001 pct), neither iron nor nickel being detected. Chromium deposited by this method is reported to contain approximately 0.05 pct 0.- Methods and Data Young's Modulus: For measurement of Young's modulus, an annealed, pressed powder sample, 0.114 x0.237x1.845 in., and an electroformed sample, 0.10 in. od, 0.01 in. id, and 1.86 in. long, were prepared. The resonant frequencies of the rod samples in forced longitudinal vibration were measured at a series of temperatures from —192" to 200°C by a method previously de~cribed.6,7 Because the samples were nonferromagnetic, iron- silicon or molybdenum permalloy tips (0.013 in. thick) were soldered to the ends. The softening temperature of the solder limited the temperature of measurement. Young's modulus, E,, of chromium at temperature, T, may be calculated from the resonant frequency of the composite rod, f,; the thickness of the tips, t; the length of the chromium sample at 25°C, l,.; the density of chromium at 25°C, pc (7.20 g per cc);5 and the thermal expansivity, Al/l25. Modulus differences for two temperatures, ET and E, are accurate to +0.002x10" dynes per cm2. ET = 4PAlc+2tyf Young's modulus at 25°C, Fig. la, is 28.2~10" dynes per cm' (40.8xlO" si) in wrought chromium (upper curve). The modulus of the electroformed sample is apparently lower due to cracks. From the modulus measurements two transitions were observed: one with a critical temperature at 37°C, the other at —152°C. Internal Friction: The internal friction, 1/Q, was determined from the width, Af, of the strain amplitude-frequency curve at 0.707 times the strain amplitude at resonance;' the internal friction, 1/Q, then equals Af/f. Fig. lb shows a sharp peak in internal friction at 38°C. The internal friction of the electroformed sample had a similar maximum. Thermal Expansion: The expansivity measurements, shown in Fig. 2, covering the temperature range —195" to +400°C were made by D. MacNair in an interferometric dilatometer8 sing a sample consisting of three pyramids 0.25 in. high prepared from wrought electrolytic chromium. Below —120°C the experimental points deviated up to ±2x10 from the drawn expansivity curve in Fig. 2 because of decreased precision of the quartz wedge thermometer at low temperatures. Near 38°C the thermal expansivity curve, Fig. 2, goes through an inflection corresponding to a minimum in the coefficient of expansion, Fig. ld, and a relative volume decrease on heating. Electrical Resistivity: The variation of electrical resistivity with temperature measured by the po-tentiometric method is also shown in Fig. l. The resistivity of the wrought chromium (upper curve) at 20°C is 13.6 microhm-cm; of electroformed chromium (lower curve) 12.8 microhm-cm. The lower value reflects higher purity and agrees closely with a published value." A minimum at 40°C occurs in the resistivity curves of both samples. No conclusive evidence for a transition near — 150°C was observed, but the points, Fig. 1, appear to deviate from a smooth curve between —120" and —160°C.

Jan 1, 1952

By J. J. Pfeiffer, A. A. Oming, J. W. Myers

The method used to process washery refuse for use as a building material aggregate is described. Results of studies made in investigating this process are summarized. The Bureau of Mines, in cooperation with two commercial coal producers, studied the feasibility of using coal washery refuse in manufacturing lightweight aggregate for building materials. Lightweight aggregate is used in making masonry products of lower bulk density than can be produced from conventional aggregate such as sand, gravel, and crushed rock. Among the advantages of lightweight masonry are reduced deadweight loads which reduce materials cost, lower cost of construction labor, and improved thermal and sound insulation. A process for making lightweight concrete aggregate from coal-washery refuse appeared attractive because of the availability of raw material which contained sufficient fuel to carry out the processing. Vast quantities of such refuse have accumulated throughout the coal-producing areas of the U.S. Generally it is stored in unsightly piles, creating a problem of air pollution and using space that could be devoted to other purposes. Conversion of the refuse to lightweight aggregate could remedy these conditions and effectively utilize a material normally considered waste. The first part of the program was conducted in cooperation with the Truax-Traer Coal Co. to determine the feasibility of utilizing refuse from the company's coal preparation plant at Ceredo, W. Va., in manufacturing lightweight aggregate. The aggregate was to be used in making cement blocks comparable to those known in the building trades as cinder blocks. This project was completed in 1954. Based on the results of this work, the cooperator began commercial development and formed the Trulite Corp. for this purpose. A plant capable of handling 120 tpd of refuse was constructed for approximately $120,000. It began operating on June 1, 1955.' In 1959 a similar study was made, under a cooperative agreement with the Carbon Fuel Co. of Charleston, W. Va., to rrscertain the suitability of refuse from its plant for conversion to lightweight aggregate. Under this program various modifications of equipment were made, and the investigation of process variables begun in the previous project was extended. PROCESSING METHOD The formation of lightweight aggregate from coal-washery refuse js governed, in part, by the fusion characteristics of the mineral constituents of the refuse when heated above their softening temperatures. The heat required for this purpose is supplied by the combustihle matter in the refuse. Some of this combustible matter is coal with high ash content, but most of it is carbonaceous shale. Whereas the density of aggregate prepared from clay or shale depends largely on expansion, the density of aggregate made from refuse is reduced by burning out the combustible matter and, to a lesser extent, by expansion of the residue in the fuel bed. A chain-grate stoker with an updraft air system was chosen for the conversion process in preference to a downdraft sintering machine or a rotary kiln. In down-draft sintering, which operates on the overfeed burning principle, the volatile matter from the refuse would distill off without burning, resulting in inefficient combustion and interfering with proper operation of the equipment. The rotary kiln is designed primarily for processing material that lacks, or is low in, combustihle matter with the heat of reaction supplied from external sources. Washery refuse, which is relatively high in carbonaceous material, could burn at the wall of the kiln causing clinker formation with resultant decrease in throughput and increase in production cost. With an up-draft air stream on a chain or traveling-grate stoker, the volatile matter would be carried into the ignition and burning zones where the heat could be utilized more efficiently. The combustion procedure in this type of unit may be considered as consisting of four periods: 1) initial ignition of the top of the bed by furnace radiation, 2) ignition travel through the bed until the whole bed is ignited, 3) burnout of the combustible material with high air rates to fuse and expand the residue, 4) a cooling period. Investigation of the process required a study of the variables that affect both

Jan 1, 1962

By F. L. Kadey

The petrographic microscope is a well known tool in nonmetallic materials research. Its utility in the study of perlite is, therefore, not surprising. Valuable information has been derived on samples smaller than those needed by most other methods of analysis. Relatively little has been written about the petrographic analysis of perlite for two chief reasons: perlite is a material of relatively new commercial interest; and the independent prospector or expander, responsible for most studies, attacks the problem from an immediately practical viewpoint. Hence, petrographic studies of perlite have been limited to academic aspects. Rapid development of commercial interest in perlite has changed the situation. Mining and expanding companies now have effective research tools; and such instruments as the petrographic microscope have added materially to practical knowledge about this mineral. Petrographic techniques employed in the search for suitable deposits screen worthless samples rapidly and inexpensively compared with large-scale expanding tests. Hence, only samples of potential quality are selected for further testing. Field appearance of perlite reveals little about its true identity and practically nothing about its commercial significance. Consequently, any method that can be used to separate the "wheat from the chaff" is valuable. In addition to the conventional thin-section and immersion methods used in evaluation of crude perlite, petrographic microscope techniques have contributed to the study of expanded perlite. When apparently similar materials behave as differently in use as perlites, the internal structure of the individual particles becomes a subject of great interest. The purpose of this paper is to discuss some of the petrographic techniques used to characterize this material. WHAT IS PERLITE AND WHERE IS IT FOUND? Perlite was at first described as a glassy rhyolite possessing a pearl-like luster and exhibiting numerous concentric cracks resembling an onion skin appearance.' Fig. 1 is an illustration of perlite in this classical sense. Recently, its definition has taken on a commercial connotation: an acid volcanic containing 2 to 5% of combined water that, when heated rapidly to the softening point of the glass, coincident with the volatilization of the combined water, expands or "pops". Fig. 2, although hardly fitting the classical description given by Johannsen, is an excellent perlite in the commercial sense. It may occur as a breccia in rhyolite, (Fig. 3) and sometimes it is associated with obsidian nodules, as illustrated in Fig. 4. The term perlite includes the expanded product also. In the United States, perlitic rocks are restricted to the western part of the country. 2 Elsewhere in the northern hemisphere, European occurrences follow a belt beginning in Iceland and extending in a southeasterly direction through Scotland, County Antrim in Northern Ireland, and through the Massif Central of France, Germany, and Hungary; thence, into Italy and Sardinia, and through some of the Aegean Islands. A general oriental belt extends from Japan through Australia and New Zealand. Rhyolitic areas elsewhere in the world undoubtedly contain perlite.

Jan 1, 1963

By Mario L. Villa

During 1939 oil production experienced a new and important increase in Argentina in the productive areas of Comodoro Rivadavia (Territory of Chubut), Plaza Huincul (Territory of Neuquén), and those of the. Province of Mendoza. Production in the Standard Oil Company's field in the Province of Salta declined, but that of the Government oil fields in that province inereased 62.5 per cent.

Jan 1, 1940

By Mario L. Villa

During 1939 oil production experienced a new and important increase in Argentina in the productive areas of Comodoro Rivadavia (Territory of Chubut), Plaza Huincul (Territory of Neuquén), and those of the. Province of Mendoza. Production in the Standard Oil Company's field in the Province of Salta declined, but that of the Government oil fields in that province inereased 62.5 per cent.

Jan 1, 1940

By Francis Foley

IN examining steel under the microscope, one is constantly confronted with structures that are difficult to interpret. Recently, in a collection of samples for exhibition purposes, the writer found apiece of open-hearth runner metal, 2 in. (50 mm.) in diameter, that had been fractured for use as a sample of cast-steel structure. On polishing and etching a section for the purpose of photographing a field to typify the microstructure of steel in the "as cast" condition, a variety of structures was found (Fig. 1) so arranged as to arouse interest at once. For a distance of about 0.065 in. (1.6 mm.) from the skin of the runner, normal ingot structure was found (Fig. 2); this was followed by a zone, about 0.215 in. (5.5 mm.) wide, of considerably lower carbon content in which occurred a most pronounced Widmannstättian structure (Fig. 3); from this point on to the center of the runner, the metal was again of normal ingot structure (Fig. 4). Representative samples taken from the metal in the three zones showed the following analysis: C Ni Cr Metal from skin 0.34 1.26 0.63 Widmannstättian zone 0.21 1.18 0.63 Metal from center 0.34 1.32 0.67

Jan 7, 1919

By Russell Salter, Edwin J. King

SINCE 1950, when perhaps two or three cyclones were being tested in Arizona, the number in use has grown to about 100. Most of these have come into operation within the last two or three years, and according to information supplied by various mining companies, the number will continue to grow for several years more. In mills that have been recently constructed, cyclones dominate the fine classification field, removing grit from lime slurries, producing smelter flux, reducing concentrate thickener overloads, classifying molybdenite in grinding circuits, and conditioning flotation feed. Four major copper companies are now testing cyclones in primary grinding circuits, and one concentrator soon to begin operation will classify entirely with cyclones. In at least two instances these versatile machines have been given a vital role in the construction of tailings disposal systems.

Jan 8, 1957

By Merton C. Flemings, Harold D. Brody

Analyses that include diffusion of solute in the solid phase are formulated to describe solute redistribution in dendritic solidification of metallic alloys. The analyses are based on conditions that include negligible undercooling before nucleation of solid phases, negligible increase of solute in advance of the tips of growing dendrites, complete diffusion within the liquid over distances the order of dendrite spacings, and a plate-like dendrite morphology. The classical nonequilibrium freezing equation, Cs = kCo(I - fS)k-l accurately describes solute redistribution between dendrite arms for the solidification processes considered, provided diffusion in the solid is negligible. To account for the effect of diffusion in the solid, an analytic expression is given which is similar inform to the classical expression. 172 addition, a numerical-analysis procedure is etnployed to examine in more detail the effect of diffusion both during and after solidification. The analyses are intended for application to solidification of castings and ingots to describe a) final solute distribution after solidification and cooling to room temperature (microsegregation) and b) local fraction solid as a function of ternperatcre within the solidifying casting or ingol. SOLUTE redistribution in cellular and dendritic solidification has been discussed quantitatively in recent papers'-3 and in a series of earlier work.4-6 However, none of the analyses developed have permitted close correlation of theory with final solute distribution (microsegregation) observed in castings and ingots. In this paper, discussion is given of approximations which may reasonably be made in mathematical treatment of microsegregation, and analyses are presented based on these approximations. Numerical results are given for Al-Cu alloys. In a second paper the analyses will be compared with exeriment.7 CLASSICAL ANALYSIS The classical quantitative treatment of solute redistribution within a closed "volume element" has been derived repeatedly, for example by Gulliver,4 Scheil,' and Pfann.' This "classical nonequilibrium solidification equation" is written for constant partition ratio: where Cs = interface composition of the solid when the weight-fraction solid within the "volume element" is fs (weight fraction, wt pct); k = equilibrium partition ratio; Co = initial alloy composition within the volume element (weight fraction, wt pct). Assumptions of Eq. [11 are: 1) There is negligible undercooling before nuclea-tion, or from curvature or kinetic effects. 2) There is no mass flow in or out of the volume

Jan 1, 1967

By Valentin R. Garfias

The production of petroleum in the Mexican fields during 1931 followed the downward trend of the past nine years, with a decline of close to 6,600,000 bbl., or about 17 per cent from the 1930 total. The output was close to 32,964,000 bbl., the Tampico-Tuxpam fields showing the largest actual and proportional decline, while the production of the fields in the Isthmus of Tehuantepec remained practically unchanged. Wildcatting along the international border was carried on more actively than in previous years, the only successful completion being the Alberca No. 1 well located about eight miles from the international boundary, across from Roma, Tex. This well, completed at a depth of 2015 ft. and plugged back to 1550, is rated at about 6,000,000 cu. ft. of gas per day from a horizon between 1330 to 1540 ft., and is now connected to the gas line from the Jennings gas field, Texas, supplying the city of Monterrey. Favorable oil indications have been encountered in other exploratory wells along the border and drilling will probably continue as these lands are largely held under government concessions which require continuous development work in order to retain title. Development in the Isthmus of Tehuantepec has progressed in a systematic manner, the number of successful completions during the year being considerably larger than in the South or Northern fields. The oil pipe line from the south fields to Mexico City has been completed and its operation and that of the Azcapotzalco refinery is expected to begin early in 1932. The construction of this line will Tevolutionize the transportation of petroleum and its products from the fields to the high plateau and seriously affect the revenues of the government-owned railroads. General conditions in the oil industry were reflected in Mexican operations. Low prices and the imminent threat of an American oil tariff discouraged development work necessary to maintain or increase production, and the curtailment of activities resulted in considerable reductions in personnel by all companies. Early in 1932 the Mexican Government announced its intention to create a surface tax or yearly rental on oil lands equivalent to about 31/4 U. S. cents per acre. Such additional burden on this already harassed industry will not only create little or no

Jan 1, 1932

By H. W. Bell

There was considerable prospecting for new supplies of oil in Arkansas during the past year, regardless of the overproduction affecting the industry throughout the country. Justification for this new work was not lacking, as the local markets more than threatened to absorb a declining production. There were, however, no important new discoveries in the state during 1929. The McDonald area in sec. 2515, S.-18 W., threatened to expand into a major producing area. Oil showings had been encountered here in wells drilled by the McDonald Oil Corpn. as early as the fall of 1928. In July, 1929, an initial production of 1000 bbl. of 32" oil was obtained in McDonald Bros. B-3 Wilson, from a sand at 2780 to 2786 ft., which is about 80 ft. higher than the sand previously tested in the neighboring wells. This production declined rapidly. At the end of the year there were six producers making about 200 bbl. per day total. Seven dry holes have temporarily stopped development in that area. The showing of B-3 was sufficient to cause considerable leasing activity. The area lies several miles west of the Louann portion of the Smackover field. The discovery well went to 2873 ft. and found Glen Rose lime in bottom. The age of the producing sand is in doubt; it seems closely related to the Tokio sand. During 1929, several paying wells were brought in, as a northeastern extension to the Smackover Heavy area, in sec. 34 and 35-15-15, from the Nacatoch sand. Over 20 new wells were drilled and resulted in at least 1500 bbl. production. The down-dip or off-structure territory contiguous to the Smackover uplift was further tested at various locations with the usual results; that is, a showing of "salt water gas," which soon blew off and in some cases a slight showing of oil. These gas showings, found further down the dip than oil, are the results of the ability of water to take gas into solution at the rate of about 3 per cent. by volume at atmospheric pressure and proportionally larger quantities, if available, at higher pressures (measured on the absolute scale). During the year no off-structure wrinkles sufficient to trap conlmercial quantities of oil have been found outside of the other known fields of

Jan 1, 1930

By David R. Hargis, John W. Harshbarger

The Upper Santa Cruz Basin lies in the drainage area of the Santa Cruz River in Arizona, and extends upstream from the community of Rillito to the international boundary [(Fig. 1)]. The principal water use area lies between, and includes, the cities of Tucson and Nogales. A subsurface geologic barrier near Rillito provides a reasonable dividing line between the ground waters of the upper and lower Santa Cruz basins. The upper basin contains the Tucson and Sahuarita-Continental critical ground water areas. The Tucson water use area encompasses the Tucson metropolitan area and extends from the northern boundary of the basin south to the boundary between the Tucson and Sahuarita-Continental critical ground water areas near San Xavier. The San Xavier use area is the San Xavier Indian Reservation. The north and south boundaries of the Continental use area coincide with the limits of the Sahuarita-Continental critical ground water area. The first study of ground water in this valley was initiated by Dr. G. E. P. Smith in 1905, and the results were published in 1910, followed by a series of bulletins of the Arizona Agricultural Experiment Station, University of Arizona, covering the general field of ground water development and utilization. Beginning in 1939, the ground water branch of the US Geologic Survey, in cooperation with the Arizona State Land Department and the Arizona Water Commission (AWC), published a series of bulletins concerning ground water occurrence and utilization in various areas of the state. In 1975 and 1977, the AWC published the Arizona State Water Plan (Arizona Water Commission, 1975) comprising a detailed inventory of water availability and use in Arizona and a study of alternative futures. The importance of ground water supplies in the Upper Santa Cruz Valley cannot be overemphasized. Metropolitan Tucson, surrounding agricultural areas, and the mineral industry are completely dependent upon ground water. Agriculture has been the largest user of ground water. The land distribution of the Upper Santa Cruz Basin is rural in character with large tracts of land included in national monuments and national forests. The Upper Santa Cruz is one of several state basins that does not depend upon one single industry as its major economic activity. Agriculture, mining, tourism, international commerce, and manufacturing all contribute to a viable economy. The city of Nogales, on the Mexican border, and the city of Tucson, to the North, are the centers of commerce in the basin.

Jan 1, 1982

By George W. Maynard Maynard

IN this paper I desire to embody the results of some personal observations of the working of the Siemens direct process as I witnessed it for a part of three days at the works of the Siemens-Anderson Company, in Pittsburgh. This preliminary investigation was to have been followed up by one extending over a considerable period of time, and would have embraced analytical and physical tests. Circumstances over which I had no control, resulting in the temporary suspension of work, have postponed the presentation of a complete paper. If the opportunity is afforded me, I purpose doing this at a future meeting of the Institute. To those interested in the development of the process, reference is made to the papers of Dr. Siemens in the Journal of the Iron and Steel Institute for the years 1873 and 1877, and to the paper of our late lamented brother, Holley, in the 8th volume of the Transactions of our own Institute. Dr. Siemens, in the introduction to his paper "On the Manufacture of Iron and Steel by Direct Process," read before the Iron and Steel Institute in September, 1877, says: " In mixing comparatively rich iron ore in powder with about 25 per cent. of its weight of pounded coal, and in exposing this mixture for some hours to the heat of a common stove or of a smith's fire, metallic iron is formed, which, on being heated to the welding-point on the same smith's hearth, may be forged into a horseshoe of excellent quality. The admixture with the ore of some fluxing materials, such as lime or clay, will, in most cases, be of advantage to rid the iron of adherent slag." This is the keynote of the Siemens direct process. Dr. Siemens says further: "If we regard the production of wrought iron from an abstract point of view, we perceive that we have to accomplish two things, viz., the deoxidation of the ore, and the fusion of the earthy matter .mixed with it; and if we calculate the amount of carbon necessary to accomplish this end, we shall find that in using, say, hematite ore, consisting of peroxide of iron with from 10 to 15 per cent. of silica, we shall require barely 40 per cent. of carbonaceous matter per ton of iron contained in the' ore to effect its reduction, and also the fusion of the slag."

Jan 1, 1882

Herbert Moore Harbach was born in Lebanon, Pa., Apr. 4, 1891, graduated from the Lebanon High School in 1911, and entered State College, from which he received his degree of Bachelor of Science in Metallurgical Engineering in 1915. He was employed by the Lackawanna Iron Co., at Buffalo, N. Y., and was later transferred 'to their Lebanon plant to start up the newly erected benzol plant. He was later made foreman of the coke ovens, which position he held after it was bought by the Bethlehem Steel Co., and until he enlisted in the service of his country in September, 1917. He was stationed at Camp Meade, Md., until the spring of 1918, when he was transferred to the C. W. S., at Niagara Falls, as an expert chemist. There he was engaged in perfecting the various kinds of gases,

Jan 2, 1919

By Yoichi Ishida, Ching-Yao Cheng, John E. Dorn

Tile creep behavior of a iron was investigated over the range of temperatures from 375° to 1150°K. Apparent activation energies for creep, obtained by the effect of sudden changes in temperature on the creep rate, revealed the presence of- four distinguishable regions. The creep behavior of a iron in Regions II (480° to 774°K) and 111 (775° to 1045°K) was found to correlate well with a model where the creep rate is controlled by the nonconsevualive motion. of jogged screw dislocations. An anomalous increase in the apparent activation energy fur creep in Region III was found to be in harmony with the known decrease in the free activation energy for self-diffusion over the Curie transformation range. Furthermore, the creep rates in Regions II and III were found to increase with stress due not only to the effect of stress on the activation energy but also to an increase in density of mobile dislocations. The evidence suggests that pipe diffusion along moving dislocations could be a significant factor over the lower temperatures of Region II. ALTHOUGH the creep properties of iron and steel have been of interest to metallurgists for some time and an extensive literature is now available, most of the published information has not produced much toward understanding the fundamental dislocation processes controlling the creep behavior of these materials. Whereas the activation energy for high-temperature creep of metals usually agrees well with that for self-diffusion, Sherby, Orr, and Dorn1 deduced from the data of Tapsell -and c1enshaw2 that the activation energy for creep of Armco iron is about 78,000 cal per mole and more recently Lytton and sherby3 reviewed the data of Jenkins and Mellor4 and found an activation energy for creep of a iron of 80,000 cal per mole. Both values are substantially greater than the activation energy for self-diffusion in a iron. Because of the limited data suitable for purposes of identifying the controlling dislocation mechanisms of creep and the unusually high activation energies for creep quoted above, it was considered desirable to reinvestigate in detail the creep of a iron by more reliable techniques which would provide sufficient data for determination of the creep mechanisms. EXPERIMENTAL TECHNIQUE Creep specimens were prepared from 3/8 by 4 in. iron bar stock of the following composition by weight percent: 0.001 C, 0.0120 0, 0.001 N, 0.004 S, and 0.003 P. The as-received bars were cold-rolled to a thickness of 0.100 in., annealed under argon for 30 min at 1113°K, cold-rolled to a final thickness of 0.063 in., and machined into tensile specimens having gage section 0.250 in. wide and 1.70 in. long. Finally they were recrystallized under argon at 1113°K. Specimens to be crept above 1060°K were recrystallized at 1173°K. Both recrystallization treatments gave the same reproducible equiaxed ASTM No. 4 grain size. Creep testing was conducted in machines fitted with Andrade-Chalmers arms that maintained a constant stress to within ±0.2 pct of the reported values. Deformation over the specimen gage section was sensed with a linear differential transformer and recorded auto-graphically as a function of time. The strains deduced from these measurements were sensitive to ±5 x 10-5. During creep the specimens were contained in an argon-filled chamber which was immersed in a temperature-controlled molten tin bath. Creep temperatures, as measured by thermocouples attached to the specimen, were maintained to within ±10.25°K of the reported values. For activation-energy determinations rapid changes in temperature of about 12°K were obtained within 30 sec by direct resistance heating of the creep specimen, and maintained to ±1°K of the reported values. Observations of structural details of specimens before and after creep tests were made by electrolytic polishing and etching in acqueous ammonium persulfate. EXPERIMENTAL RESULTS A typical example of the determination of apparent activation energies, Q, by the effect of small changes in temperature is illustrated in Fig. 1. Q is defined by

Jan 1, 1967

By R. E. Ricksecker, W. M. Baldwin, R. McC. Baker

INTRODUCTION THE development of residual stress in strip during rolling has not been systematically studied. A few scattered papers1-3 mention the existence of residual stresses in rolled strip or touch upon some of their consequences,4 but there is no report of experimental studies in the literature describing the effect of roll diameter, strip thickness, reduction per pass, metal or metal temper on the magnitude of residual stresses developed in strip. A knowledge of the effect of these factors is of utmost importance since the present trend in some mills to roll thicker castings brings the rolling operation directly into that set of conditions which, as will be brought out in the present paper, can develop residual stresses of a high order of magnitude. Fundamentally, residual stresses are developed when a metal is inhomogeneously unloaded from a plastic stress state. A quantitative treatment of the problem requires a reasonably complete understanding of both the plastic stress state existing in the metal during deformation and the elastic stress state that would exist in the metal if the metal deformed as a perfectly elastic body. Our knowledge of either state during rolling is so meager that we can make no more than certain limited predictions. The external stress state* operating between the roll and the metal consists of compressive stresses acting almost perpendicularly to the strip surface but vary [ ] ing in intensity both across the width of the strip and along the length of contact between the roll and the strip. An example of such a stress distribution is shown in Fig I. The nature of the internal stress state, produced by this distribution, is not known. Various investigators,5-7 however, have felt that a qualitative similarity must exist between the internal stress state so produced and that produced in a wide strip that is compressed between two flat-nosed punches. In the latter case the external stress state is represented by a uniformly distributed compressive stress acting perpendicularly over the face of the tool. The elastic internal stress state in this case is complex-the principal stresses showing

Jan 1, 1948

By Charles Goodale

THE principles and theory on which the U. S. mining law of 1872 was based are well understood, and have been discussed at great length by many writers. The papers by Dr. R. W. Raymond1 in the Transactions of the American Institute of Mining Engineers have covered the subject very fully, with explanations of practical results in many adjudicated cases. It is believed that the following instance of the application of the law in recent years will have some weight in a discussion of proposed changes in our mining laws. The litigation between the St. Louis Mining & Milling Co., and the Montana Mining Co., Ltd., a British corporation, over portions of the Drumlummon lode covered more than 20 years, and resulted in a judgment for damages in favor of the St. Louis Co. of such an amount that the Montana Co. declined to pay the judgment, and therefore lost the entire property. The Drumlummon lode claim in the Marysville district, Mont., was located in 1876 by Thomas Cruse. When he staked out his claim, he assumed that the discovery on the Drumlummon vein, and another showing of mineral about 200 ft. distant, were on the same vein, and the center line of the claim was given a course of N. 57'2'E. Development of the Drumlummon vein soon showed that its strike was about N. 15 E., and that the other outcrop was on the North Star lode; so it was inevitable that the Drumlummon vein would cross one or both side lines of the location, and the Montana Co. found it advisable to acquire adjoining claims on both sides of the Drumlummon, in order to avoid possible litigation over apex rights. They bought the Marble Heart, but would not purchase the Hopeful (see Figs. 1 and 2), at the terms proposed for the reason that exploration in the Cruse level had shown the vein to be barren in that region. The owners of the Hopeful were sinking an incline from that claim in 1889, and the Montana Co. enjoined them, contending

Jan 5, 1914

By S. J. Kidder

Application of shrinkage stoping methods, without filling, in the mining of large silver-gold orebodies in the Mogollon district, where the ore is hard and wall rocks stand well without timbering and where veins make little water. Vertical and inclined shafts in use with both surface and underground hoisting stations. Storage pockets used on main hoisting levels, with electric signals and telephones for communication. Power is generated by De La Vergne engines having a total sea-level rating of 1540 hp. On account of the remote location of the camp, transportation is an important item of expense, amounting in 1922 to $0.641 per ton of ore milled or $0.265 per ton-mile on all freight hauled. THE Mogollon mining district is in the southwestern part of New Mexico near the southern end of the Mogollon range, from which the district takes its name. The town of Mogollon is but 37 1/2 mi. in an air line northeast of Clifton, Ariz. The air-line distance from Silver City is 52 1/2 mi. and from Tyrone, 57 mi. Supplies are transported by motor truck from Silver City. The distance by road is 75 mi., half of which is an improved highway of modern construction. Transportation has always - been a large item of expense in carrying on operations in the district. Valuable ore is said to have been discovered in the Mogollon Mountains as early as 1870 but the first regular prospecting was carried on in 1875, by James C. Cooney, a sergeant from Fort Bayard. His discovery of rich silver-copper ores in the region of Mineral Creek led to the establishment of the Camp of Cooney. Remote from any settlements where there was a semblance of law and order, and harassed by the Apaches, development was slow and nearly 10 years elapsed before the village of Mogollon was established on Silver Creek. Prospecting in this section of the district had disclosed the outcrops of several promising veins containing silver-gold ores. Among the early claims located were the Last Chance, Top and Confidence, on what has proved to be the most productive vein in the district.

Jan 3, 1924

By W. R. Finney

THE formation of scale in boilers and other industrial equipment, and the corrosion of such equipment, are closely related problems. Since in the petroleum industry these problems cover a very broad field, this paper has been confined to the effects of scale and corrosion on gas engines, compressors, pipes and fittings, used in plants extracting gasoline from natural gas, and the steps taken in arriving at a workable plan for combating these evils at the Midwest Refining Co.'s plants in the Salt Creek field, Wyoming. Eliminating, or at least minimizing, the many deleterious effects occasioned by the use of bad water in jackets and cooling systems of gas engines and compressors has been the subject of much study for many years but no generally accepted plan has been evolved. The problem was unusually difficult at Salt Creek, as the severe winters of Wyoming bring operating conditions quite different from those encountered in warmer states, and the water available was especially bad. While the conditioning of water to prevent scale and to lessen corrosion may not be a particularly difficult problem in plants in large industrial centers, it becomes much more difficult when attempted at plants remote from railroads and by men without previous experience to guide them. In fact this difficulty has been so great in the Wyoming oil fields that until comparatively recently it has been the practice to allow much equipment to be ruined rather than to attempt corrective measures. At the Midwest plants this problem was given attention first by the plant men and later by both plant men and laboratory staff. To the latter it was simply one of many problems which arise in connection with field and plant operations, which must be studied and, if possible, solved. Many mistakes were made during the course of this investigation, but since mistakes, properly interpreted, are of value in guiding one's steps aright, it is believed that a review of the different stages of development which have led up to the present method of handling this problem will prove of interest to the industry.

Jan 12, 1926

Herbert C. Hoover, who became a member of this Institute in 1896 and who is now one of its Vice-Presidents, is the man who in 1914 extended a helping hand to Americans stranded in Europe at the outbreak of the war, and who made it possible for many such travelers to return safely to their homes. When his countrymen no longer needed his services, he turned to the Belgians, whose need of food had been presented to him. Engineers have been among his assistants from the first, and it is because we believe that members of his own profession will still be particularly interested in his work that we thus mention it in the Bulletin. A Minute adopted by the Board of Directors of the Institute, in which the Belgian Kiddies, Ltd., is recommended to the consideration of the members, immediately follows the Proceedings of the Meeting of the Board of Directors. With the thought that members of the Institute may be glad to read Mr. Hoover's own words in regard to his work, we print in full the speech

Jan 3, 1917

By ALBERT C. RUBEL

RECENT developments in the use of the core barrel in rotary drilling have led to its wide application in all types of development. Its use is essential to the wild-catter and a valuable guide and check even in the most closely developed areas. A perfect core would be an unbroken sample of formation whose length is equal to the amount of hole made by the core barrel, whose diameter is great enough to show the lithologic character, texture and attitude of the material encountered, whose formation is so unaltered in character and so free of contamination from outside sources that it represents a true and complete sample of the formation penetrated. From such a core it would be possible to determine the lithologic character and economic importance of the formation, whether it is oil bearing or barren, the nature and attitude of the sands and shale bodies, valuable fossil evidence and other points which would assist in the correlation or in the selection of suitable points for water shut off or production.

Jan 1, 1924