By H. Warlimont

In recent investigations of the microstructure and crystallographic features of martensite by electgon microscopy,', '9 thin films (about 50 to l000A in thickness) have been used as specimens. It was found by W. Pitschl ,2 that the lattice relationships between the supefiaturated fcc matrix and the martensite formed in thin films were different from those observed after transformation in bulk material. Corresponding differences are to be expected in nucleation and in reaction kinetics in the formation of martensite in thin films, but have not yet been reported. In the course of the preparation of thin films of iron-base alloys for investigation by electron microscopy it was observed that films of alloys, whose martensite formation temperature (Ms) was below room temperature, formed martensite during the electrochemical thinning process conducted at or above room temperature. The chemical compositions and approximate bulkM,-temperatures of the three materials on which this observation was made are listed in Table I. The alloys were vacuum-melted from high-purity metals. It can be seen that the effect occurred in alloys that contain only sub-stitutional components as well as in alloys that contain carbon as an interstitial solute. The appearance of martensite formed in this manner is illustrated in Fig. 1, which represents a polished film of alloy No. 1 at XI0 magnification. The martensite plates can be recognized by their surface relief effects. In addition, heavily strained (owrinkledo) austenite can be seen near the edges of the film where it is thinnest and transformation stresses or strains can be accommodated by plastic deformation most easily. The nonuniform distribution of transformed regions is probably due to the varying thickness of the film. These observations were common to all materials listed in Table I. Because effects of supercooling or straining can

Jan 1, 1962

By John T., Ryan

THE subject assigned me, "Safety in Mining," is a very broad one and only the high spots can be covered in this short paper. As this is a meeting of the Coal Division, these remarks will be directed largely to coal mine safety, although the principles of safety and effective accident prevention methods are relatively the same in every branch of mining or industrial work. The coal mining industry should take pride in the part it has played in the development of the accident prevention movement, and there is ample proof for the statement that the first real organized accident prevention, work, both abroad and in this country, was con- ducted in the coal mining industry.

Jan 1, 1930

By B. DE MARE

THE No. 6 open-hearth furnace at the plant of the Worth Steel Co., Claymont, Del., is the first to be rebuilt according to the Kuehn system. This as well as the other five furnaces at Claymont, has a nominal capacity of 75 tons, but the actual charge is about 242,000 lb. No hot metal being available, the pig-iron is charged cold. Oil of low grade with an asphalt base is used as fuel. These two items have to be kept in mind when discussing the actual fuel consumption. Careful records have been kept covering a five weeks run and the following is a brief summary of them The time required to heat the furnace preparatory to charging from the time a wood fire was started until charging commenced was 36 hours. This, I understand, is much less than with furnaces of standard design. The draft of the furnace, as shown by a gage in the stack-flue, is 1.25 in. The maximum draft with new checkers on former runs was 1.50 in., this draft gradu¬ally decreasing as the checkers closed up. Both of the first helpers claim the present draft is all they need for the proper working of the furnace, and, as with the Kuehn regenerators the draft remains practically the same from beginning to end of a run, this is satisfactory.

Jan 1, 1929

By H. E. Dunn, C. M. Cosman, J. H. Brennan

Up to the beginning of World War I, the American ferro-alloy industry was in its infancy and largely dependent on Europe. During that War, capacity was over expanded. Later recovery and commercial and scientific development have resulted in an industry which in 1957 produced 1.8 million tons of ferro-alloys. THE ferro-alloy industry is today an important element of the industrial structure of the United States. Its output is valued at almost half a billion dollars annually and its products are basic not only to National defense but also to the peacetime standard of living. This has not always been so. The ferro-alloy industry from late in the last century has grown from small beginnings, nurtured by the demand for stronger, tougher materials; by the search for steels capable of absorbing severe impact loads and resisting corrosive media and high temperatures; and also by the need for electrical and electronic specialties. Conversely, the ferro-alloy industry has grown because it developed improved steels and alloys by extensive research, and because it was able to show to steel makers the advantages accruing from the more extensive and the more economical use of alloying elements. The industry has grown in scope from producing a few grades of ferro-alloys of the more common metals-manganese, chromium, vanadium, silicon, titanium, tungsten, and molybdenum-until there are today some 150 compositions of ferro-alloys available to the steel maker, including such elements as columbium, zirconium, and boron. In 1912 the industry produced 360,000 tons of alloys valued at about $12,000,000, while 1957 production figures show an output of 1.8 million tons worth $440,000,000. In the United States, the history of an industry is largely the history of the companies making up this industry; hence, this paper will briefly trace the development of the most important ferro-alloy-producing companies. Quite varied have been the reasons that caused the different companies to move into the ferro-alloy field; the Willson Aluminum Co., seeking methods of producing aluminum, succeeded with the production of calcium carbide, and their developing electric furnace skills led them to the production of ferro-silicon and ferrochromium alloys. Willson was the predecessor of the Electro Metallurgical Co. of Union Carbide. Two Pittsburgh undertakers, interested in vanadium as an alloying agent for steel, set about to find a mine and, ranging as far as Peru, fathered American Vanadium Co., the predecessor of Vanadium Corp. of America Experiments of the

Jan 1, 1961

By E. T. Turkdogan

Jan 1, 1962

By J. H. Bain, D. C. Haigh, L. C. Parsons

Jan 1, 1964

By Edward J. Felten

THE oxidation resistance of chromium and Fe-Cr alloys is increased by small additions of yttrium or other rare earth metals.1,2 In addition, the presence of the additives increases the resistance of these alloys to spalling of the external oxide above 1000°C. This ability to prevent spalling appears to be related to the formation of an internal oxide in alloys containing yttrium or the other rare earth metals. The internal oxide is found in the form of a filamentary growth concentrated in the grain boundaries of the unoxidized metal. In alloys containing yttrium this internal oxide was found to be either Y2O3 Or YCrO3.' In an earlier report,' the growth of the external oxide was found to be controlled by diffusion through the oxide layer. Thermal balance studies were used to establish the kinetics of external oxide formation. In this related study the rate of growth of the internal filamentary oxide has also been studied. The results obtained indicate that the growth of the internal oxide is also diffusion controlled. Internal oxidation appears to occur in at least two ways. Using copper alloys containing small amounts of silicon, Rhines 3 found that between 600" and 1000oC a subscale was formed which consisted of particles of silica dispersed in the metallic matrix. The conditions requisite to internal oxidation as suggested by Rhines are: 1) a solubility of oxygen in the alloy, 2) the ability of oxygen to diffuse at an appreciable rate into the alloy, 3) the possibility of the formation by the alloying element of an oxide more stable than the oxide of the host metal, and 4) a relatively low solubility of this oxide in the metal. These conditions are fulfilled for a number of other copper alloys.3-5 Furthermore, the relationship between the depth to which the internal oxide is formed and the oxidation time follows the simple parabolic law.6 The activation energy for copper containing small amounts of silicon, germanium, iron, or manganese as calculated from Rhines data6 is about 48 kcal per mole. In some cases the internal oxide is found segregated at the grain boundaries, especially near the the surface. Observations of this type of oxide formation have been reported by stead,7 Rhines,* and Lustman. Evans" cites these cases as examples of the simultaneous movement of anions and cations during oxidation. Furthermore, Evans states that the presence of a minor constituent with a high

Jan 1, 1962

By Paul M. Tyler

MILITARY power stems from industrial power and industrial power in turn depends predominantly upon an ample and assured supply of mineral raw materials. It thus becomes the duty of mineral economists to collate the vast array of data and logical deductions in order to reach an unemotional judgment as to the ability of the Soviet economy to withstand the strain of prolonged military action on the modern scale. Russian publications, reports: and official speeches have been laboriously screened and analyzed. Since these are the sources of information for the lower echelons of the Soviet industrial organization itself, they carry factual data that can be pieced together to show the present-day pattern. Apparent contradictions and obvious distortions or omissions can often be rationalized on the basis of observations made by foreign engineers and consultants during the 1930'5 and by checking against the technical literature published before even so-called technical articles were riddled by bombastic and presumptuous claims.

Jan 6, 1951

By Samuel Wyer

THE art of natural-gas compressing is now over 25 years old, and has grown at practically the same rate as the increase in domestic natural-gas consumers. There are now over 200 natural-gas compressing stations in North America, aggregating more than 320,000 hp. of compressor capacity and representing a property value of more than $22,000,000, and compressing more than 85 per cent. of all the gas used. The age and magnitude of the art make it evident that the use of gas compressors is a recognized integral part and universal custom of the natural-gas business. The public also is not without its rights and vital interests in this problem. Approximately 1,700,000 domestic natural-gas consumers in North America are dependent upon gas compressors for their natural-gas service. That is, if the use of compressors were to be prohibited, the majority of these consumers would be unable to secure adequate natural-gas service. Each consumer represents between four and five persons, and it therefore follows that the comfort and well-being-as far as natural-gas service is concerned-of at least 8,000,000 persons would be affected if the use of natural-gas compressors should be prohibited. These 1,700,000 consumers have invested, in services, house piping, fixtures, and appliances, an average of about $90 each, or an aggregate of $153,000,000, which is much more than the companies' investment in gas compressors. Furthermore, in all cases where the rate paid by the consumers is fair to the gas company-considering the value of the service rendered by the gas company-the consumers are entitled to continued service and protection of the investment they have made on the faith that the gas service would be continued in the future.

Jan 2, 1916

By R. N. Zitter

PRESENT work was done in connection with a program for obtaining a low energy gap semiconductor suitable for photodetection. The inter-metallic compound InSb, which is now being in-

Jan 1, 1959

By Fulton Flick

THE micrography and macrography of aluminum and its alloys present certain difficulties. Many of the difficulties attendant on the micrography have been removed by methods developed during the past few years, notably those of E. H. Dix, Jr.1 The development of grain size in aluminum and its alloys may be equally troublesome, yet comparatively little detailed attention appears to have been given to it. Satisfactory reagents. are available for the development of such structures in ferrous and most non-ferrous metals, but those applied to aluminum and its alloys, i. e., alcoholic or aqueous solutions of sodium hydroxide or hydrofluoric acid are not entirely satisfactory. Hanson and Archbutt,2 in speaking of these two reagents, state that "These two reagents give fairly satisfactory results, but they sometimes produce badly tarnished surfaces from which the surface deposit is difficult to remove." It has been our experience that neither of these reagents is to be entirely relied on for developing structures suitable for study or photography. This means that when the etch fails to produce satisfactory results the, specimen must be repolished, through the 000-paper at least, and then etched with another reagent. This procedure entails a con¬siderable loss of time, and the final results may not be all that might be desired. However, the reagent to be described, although not a panacea for all etching troubles, has improved results so markedly that it is felt that it is worth offering as a grain-size etch generally applicable to aluminum and aluminum alloys. Czochralski3 in 1915 mentioned the application of a solution of 10 to 20 c. c. concentrated hydrofluoric acid in 100 c.c. absolute alcohol, etching in this reagent being followed by dipping in concentrated hydrochloric-acid solution.

Jan 2, 1925

By F. Keller, A. H. Geisler

ALTHOUGH the subject of precipitation from solid solution appears to be one of the more profitable fields in metallurgy for study with the electron microscope, few comprehensive studies have yet been made. Occasionally electron micrographs have been published that illustrated alleged precipitation in various alloys, but frequently the apparent size, shape and distribution of the particles do not fully agree with those expected from theory or from observations of the precipitate when the particles have grown to a size resolvable with the light microscope. The presence of a Widmanstätten pattern for submicroscopic precipitate particles has been demonstrated for only a few aged alloys.1 The initial problem has been the development of suitable techniques for applying the transmission-type instrument to a field that has been inherently associated with reflection-type microscopes. The various techniques have been the subjects of numerous publications, and instead of describing them individually here it will suffice to say that the oxide film method has proved to be the most satisfactory method yet found for studying the microstructure of aluminum alloys with the electron microscope. This method has the definite characteristic advantage that the actual surface layer of the specimen is examined and not a plastic or silica replica. Doubtless suitable methods for forming and removing the oxide film could be developed for alloys of other metals. The purpose of this report is to point out the characteristics of the oxide film method that have been observed during the studies of numerous aged aluminum alloys and to present the results of these studies. PREPARATION OF SPECIMENS The oxide film method for preparing specimens of aluminum alloys for examination in the electron microscope has been described in detail previously.1,2 Briefly, the procedure consists of preparing the metallographic specimen, forming the film by anodic oxidation and removing the film from the prepared surface of the oxidized specimen. The specimen is polished according to the usual procedure for microscopic examination.3 The specimen may then be etched to remove flowed metal but etching to attack the alloy constituents or to leave them in relief as in the replica processes is not necessary. Electrolytic polishing is not generally recommended. Deep-etched specimens are used frequently, however, since they provide information that is not revealed by polished specimens and frequently present the same information more clearly than do the polished specimens. The surface preparation of specimens to be deep-etched is not important, since specimens that have been subjected to the first wet polishing operation are generally used, but frequently the as-rolled surface is suitable. These specimens are then etched using a suitable macroetching reagent.

Jan 1, 1946

By Stewart Murray, Philip Klapwijk

INTRODUCTION Forecasting commodity markets is like predicting winners in a horse race: to get the answers right, one needs both luck and judgement. Commodity analysts bear some resemblance to racing tipsters as they try to convince interested parties that they have an inside track on which metal is going to win the great minerals race of the 1990s. Commodity analysts share some features with the gentlemen of the turf: • They influence other people in how to spend risk capital, • They don't put their own money at risk, and • If their tips consistently fail to deliver, then they end up looking elsewhere for employment. In order to find winners we need to know about the kind of race we are in and the strengths and weaknesses of all the runners. Miners are not interested in a five furlong sprint: their race is a long distance affair -- after all, the lead-times between discovery and start-up generally approach a decade for mines that will provide the staying power which leaders require in this industry. We need to look at the environment in which our commodities will be competing: in racing parlance, the going. Our equivalent is the economic background: just as some horses are at a relative advantage when the going is soft, so some commodities will do better than others if economic growth is sluggish. If we are going to pick the winners for the late 1990s, and as an industry, make the right investment decisions, nothing is more important than being able to forecast (with at least a semblance of accuracy) how and where the world's economy is going to develop in the next decade. In addressing the question of whether minerals are going to be leaders in the 1990s, this paper considers the idea that it will increasingly be the world outside the industrialised OECD that will provide the incremental growth in demand for mineral products. Economic growth in the Developing World is fundamentally different from that in the OECD, and the pattern of demand for materials in relation to economic output is much more favourable than in the OECD. If we are to forecast the future, we need to be able to understand the past, both in the boom times of the so called Golden Sixties and in the lean years that followed them. This should help us to decide whether the future is going to be like one or other of these extremes or, on the other hand, a return to normality. Having forecast the going, we can look at individual competitors. • Which are best placed to take advantage of the economic, social and industrial trends that we can now dimly foresee? • Which can resist the continued onslaught of the new materials and technologies? • Which of them will best weather the economic storms (assuming that recessions have not yet been abolished)? If we can provide answers to these questions, we will be well on our way to picking winners, i.e., the metals and minerals that will reward their owners with growing demand, steady (and high) prices leading to profits beyond the dreams of avarice.

Jan 1, 1990

By D. P. Harris

This paper examines recent developments and work in progress on the application of quantitative methods and computers to the appraisal of the mineral resource potential of discrete areas by employing reconnaissance geological information and general economic relationships. The perspective of this paper might be that of a firm planning a regional exploration program or of a legislative body seeking to choose between several alternative actions on the basis of their impact upon the regional resources. In addition to this general survey and commentary, an example is presented of the use of geostatistical analysis and computer simulation to evaluate the economic mineral resources of the Seward Peninsula of Alaska.

Jan 1, 1969

By Harry J. Evans

DURING the fury of the conflict it was believed quite generally that World War II was being fought for and would accomplish a permanent peace. Yet, before the guns were actually stilled on all fronts, the American people realized that the devastated world would continue to be dominated by suspicion and uncertainty. The misunderstandings which rapidly developed indicated that it may prove unwise to rely wholly on mutual international agreements and contracts to avoid war. Before the celebrations of V-Day died down serious thought was being given toward measures for preparedness for the next conflict. Along with a realization of the enormous loss of life caused by the destructive forces of war, the American people came to understand the seriousness of the rapid and unwarranted depletion of our natural resources. During the last half of 1945 the question of stock-piling strategic and critical raw materials for a future national emergency became an intensely live subject.

Jan 1, 1946

By J. J. Lillie

Sublevel stoping was first developed in the Michigan iron mines many years ago. Since that time this method, and modifications with long hole drilling, have been used in a number of non-ferrous mines and have been described in various papers and articles. With a few exceptions, the operations where sublevel methods have been applied are producers of large daily tonnages from ore bodies of considerable size. In selecting mining methods for small properties or relatively small detached ore bodies, sublevel methods often have been overlooked. The method has been used success- fully in relatively small operations at Copper Canyon, Nevada, and, more recently, in mining small ore bodies at Darwin, Calif. As a result of this experience, we believe that a review of the general procedure, the advantages noted, and the results obtained will be of interest to many operators of relatively small mines.

Jan 1, 1949

By W. G. Davenport, M. Paneni

Experiments in sheets of mercury and water have confirmed that the dynamics of bubble rise are simi-lur in Liquid metal and aqueous systems. RECOGNITION that bubble/metal interactions are important in pyrometallurgical refining processes (e.g., steelmaking, vacuum degassing, deoxidation of copper) has led to a number of investigations into the dynamic behavior of bubbles rising in liquid metals. Terminal velocities of bubbles rising in mercury (20°C)' and silver (1000" to 1050"c)1,2 have been measured. Good agreement between aqueous and liquid metal systems has been obtained. Shapes of air bubbles rising in mercury have been determined experimentally by Davenport, Bradshaw, and Richardsonl who used a system of electric probes to measure maximum horizontal and vertical dimensions, Fig. 5. In the present work the motion and shape of nitrogen bubbles rising in a thin sheet of mercury (i.e., a "two-dimensional" environment) have been studied with the view of confirming dynamic similarity between aqueous and metallic systems. The use of thin sheets of liquid permitted direct visual and photographic comparisons of bubble behavior in clear liquids and in mercury. EXPERIMENTAL METHOD The thin sheets of mercury or water were held in a clear acrylic plastic container, Fig. 1. The sheets of liquid were 80 cm high by 30 cm wide and 0.47 cm thick. Single bubbles were formed by injecting the desired volume of nitrogen into an inverted semicircular cup (stainless steel). The cup was then rotated into the upright position using an external handle thus releasing a single bubble of measured volume. Nitrogen was injected into the cup from a nitrogen cylinder through the external handle and a hollow rotating axle. The volume of a bubble (volume range 0.01 to 10 cu cm) at any instant was obtained by connecting a soap film meter to a small gas space above the liquid. By this technique any change in the volume of a gas bubble in the liquid (i.e., during cup filling or during rise) produces an equivalent displacement from gas space A into the buret B. This displacement is determined by measuring the movement of a horizontal soap film in the buret. Bubble shapes were determined using single-frame photography. Rising velocities were determined by cinephotography with a 1/100-sec stopwatch in the field of view. In both cases dimensions were referenced to a rule attached to the container surface, also in the field of view. Linear dimensions were measured on projections of the single-frame negatives. Rising velocities were calculated from measured heights of rise (10 to 20 cm) and times of rise. The effects of disturbances caused by cup rotation and by bubble release were minimized by photographing bubbles at a point not less than 25 cm above the cup. MATERIALS Mercury: Technical-grade purified: minimum 99 pct Hg; Johnson Matthey and Mallory Limited, Toronto. Nitrogen: Technical-grade purified nitrogen: 99.99 pct Nz, 0.01 pct 02, trace argon; Air Liquide Canada Limitee, Montreal.

Jan 1, 1970

By J. E. Johnson

OF the many items of information necessary to the successful management of the blast-furnace, few are more important than knowledge of the location and movement of the stock-line: whether the furnace is full and has. been kept so; whether the stock is settling regularly or slipping; and, if slipping, how often it has slipped, at what times, and how far at each time. To obtain these data, a man is sometimes stationed at the top of a. pair of mechanically-filled furnaces, simply to watch and gauge them by hand in the old-fashioned way. - A more recent practice is the suspension of test-rods from ropes leading over pulleys to the ground-level, where the ropes are wound on small drums with graduated peripheries and provided with crank-handles, whereby the skip-man or some other person can quickly and conveniently gauge the position of the stock-line in the furnace. I believe the credit for this great improvement belongs to Messrs. McClure & Phillips of Sharon, Pa., who were, as far as I know, the first to apply it, and who have a patent for it. The valuable indications gained by application of the Uehling pyrometer to the down-comer are Dot to be ignored; but the information thus furnished is somewhat indi¬rect, and there is no scale for the translation of "top-tempera¬tures " into " feet down." Moreover, this apparatus as a whole is delicate, and the cost of its installation and maintenance is high. If the record furnished by the Uehling pyrometer is not in the most desirable form, the test-rods, on the other hand, give no record at all, except through the memory, or notes of a man who, to say the least, is not gauging continuously, and who may omit to report an improperly low stock-line, if it be due to a fault of his own.

Mar 1, 1905

By T. K. Smith

The comments contained in the discussion of the paper concerning the prediction of fracture gradients are of considerable interest, since the subject is of a very controversial and timely nature. It is regrettable and Fairhurst2 contradicts the author's statement in the third paragraph of Other Applications. These references create significant doubt that Eaton's Eq. 1 predicts fracture pressure during the injection of fluid into old wells. 3. No evidence is presented in this paper to support the author's Conclusions 2 and 3. While an empirical coefficient related to back-calculated field data is correlated with depth (Eaton's Fig. 4), there is no reason to suspect that this coefficient might be the Poisson's ratio of the various formations involved. 4. Until the field data supporting the empirical approach proposed by the author are presented and evaluated, the accuracy claimed in Conclusion 5 is without substantiation. References 1. Geertsma, J.: "Problems of Rock Mechanics in Petroleum Production Engineering", Proc., First Intl. Symposium on Rock Mechanics, Lisbon (1966) 585. 2. Haimson, B. and Fairhurst, C.: "Hydraulic Fracturing in Porous-Permeable Materials", I. Pet Tech. (July, 1969) 811-817. that the comments are those of a critic and do not offer an alternative and better method for the prediction of fracture gradients. Nevertheless, a reply is in order.

Jan 1, 1970

By Richard H. Mote, W. C. Schroeder

The endlessly changing pattern of mineral supply and demand offers opportunity to the alert and can bring disaster to the unwary. The discovery of ore bodies, the invention of extractive processes, the provision of new transport facilities, the political stabilization of underdeveloped areas, and many other changes can increase supply dramatically. Such new outpourings of mineral wealth from ore bodies bring fortunes to their developers, and consumers frequently find their competitive positions decidedly improved by new and cheap sources of supply. On the other hand, operators of marginal properties can find competition from newly opened high-grade mines intolerable. Consumers that have depended on the products of nearby, high-cost mines may find new, remote, low-cost supplies advantageous only to their competitors. The invention of new prospecting methods can have spectacular effects. Shortly after World War I the discovery rate of petroleum pools began to decline. The leading prospecting technique of that day, the projection downward of surface reflections of geologic structure, was proving less rewarding. Prophets foretold an oil shortage in the near future. But at that very moment scientists were perfecting the application of seismic waves to reveal underground oil-bearing geologic structures. As these geophysical methods were put into commercial use the whole outlook changed-the problem of the 1930's became how to cope with the surplus from discovery, not how to meet the ever rising demand. Many lead mines were being abandoned as unprofitable about this same time because the penalties charged by smelters for the zinc in the ores and concentrates more than counterbalanced the payments for lead and silver. Then selective flotation (at the time called differential flotation) appeared,

Jan 1, 1959