By Lawrence H. Van Vlack, Otto K. Riegger, Gerald I. Madden

The microstructural variations of periclase (MgO) in the presence of oxide liquids are examined under the steelmaking variables of: 1) temperature, 2) liquid composition, and 3) FeO additions under different oxidation levels. Attention is given to the distribution of the phases, both liquid and solid, and to the growth of individual crystalline grains. Silicate liquids penetrate more extensively between individual periclase grains than do liquids containing high percentages of Fe2O3 Higher MgO solubilities in the liquid and lower MgO contents of the solid favor more rapid grain growth. The presence of a second solid phase reduces the periclase grain growth rate and increases the amount of the solid-to-solid contact within the oxide microstructures at high temperatures. The service suitability of a refractory depends on many factors. Two are of major importance and include 1) the thermal resistance to melting, and 2) the mechanical resistance to loads at service temperatures. Neither is a simple consequence of the service temperatures because service conditions will alter compositions, produce partial melting, and induee phase changes. Consequently, the equilibrium phase relationships have been rather thoroughly studied and give a knowledge of the thermal resistance to melting, but do not give full information about the mechanical properties because two refractories with the same types and quantities of phase may have different microstructures. Although variations of microstructures with time, temperature, and composition have been subjects for extensive investigation in metals, only a limited amount of comparable microstructural work has been performed for refractory materials.' This study was an attempt to evaluate some of the consequences of service parameters upon the microstructures of refractories so that bases may be established for the analyzing of high temperature mechanical properties. Periclase (MgO) was chosen as the refractory oxide; variables included those which are encountered under steelmaking conditions such as 1) temperature, 2) liquid composition, and 3) FeO additions under various oxidation levels. Specific attention was given to the distribution of the phases, both liquid and solid, and to the growth of individual crystalline grains. The most closely related work on microstructures of polyphase materials is that of Van Vlack and Rieg-ger2 on the microstructure of magnesiowüstite [(Mg,Fe)O] in the presence of silica. In that work which pertained to solid solutions with less than 40 pct MgO, most of the quantitative work was performed on FeO microstructures. The chief conclusions concerning these relatively low-melting oxide solids were as follows: 1) the rate of crystalline grain growth is inversely proportional to the grain diameter, 2) grain growth proceeds more rapidly at higher temperatures but is slightly retarded by additional liquid content, and 3) a Silicate-containing liquid penetrates as a film between the individual magnesiowüstite grains independent of time, temperature, amount of liquid, or the MgO/ FeO ratio. The above observations are in contrast to prior work3 on the microstructure of silica in the presence of iron oxide-containing liquids where the liquid does not penetrate as a complete film between solid grains. The phase relationships for the compositions of the present work are shown in Fig. 1 which is a summary of the work of several investigators.4 Of importance is the fact that CaO forms a more stable structure with SiO2 and Al2O3 than do either MgO or FeO. The oxygen potential has little effect on periclase unless iron oxide is also present. The iron oxide is ferrous at moderately low oxygen levels, changing to ferric as the Oxygen potential is increased so the spinels, magnetite, and magesioferrite are formed.5 These two phases are relatively stable in air at steelmaking temperatures. I) EXPERIMENTAL PROCEDURE ractory were made with reagent grade Oxides. The magnesium oxide used was 99 pct MgO after ignition, and the iron oxide raw material had a minimum content of 99 pet Fe2O3. The CaO, SiO2, and A12O3 were also reagent grade raw materials. After mixing, the required compositions were pressed into pellets at a minimum pressure of 5000 psi to insure compaction of the raw materials and prevent excess void content. A silicon carbide element tube furnace was used with thermocouple control for sin-

Jan 1, 1963

By Don M. Jackson, Robert W. Howard

Techniques for the epilaxial growth of single -crystal silicon carbide films on silicon were developed. The vapor-phase decomposition and bydrogen reduction of silicon tetrachloride (SiC14) and Propane (C3H8) resulted in clear films of silicon carbide, lip to seveval microns in thickness. The growth took place in a horizontal . silicon epilaxial reactor at 1100°C (pyrometer) at a rate of- 3000Å per minute. Electron diffraction and X-ray diffraction studies demonstrated that the films were single-cyrstal, ß -phase, or cubic silicon carbide. SiO2 film were used to mask areas of the silicon sur-lace in order that the silicon carbide might be grown in controlled geometries. Both n- and p-type films were grown on p-type silicon waters.. Heavily doped silicon films of the same conductivity type as the silicon carbide films were deposited over the silicon carbide in order to affect better probe contact to the structures. when n-type silicon carbide mesas were grown on p-type silicon substrates the de vollage-current relationships between films and substrates were that of junction diodes. These diodes showed a sensitivity to while light ill that the incident light increased forward- and reverse-satro,ation currents, P-type silicon carbide mesas grown on p-type silicon were ohmic rather than rectifying in their voltage -current relationship. No conclusions could he reached concerning heterojunc-tiou rectification in the structure. SILICON carbide is a semiconductor with many interesting properties. It decomposes at temperatures above 2200°C.1 It occurs in two general crys-tallographic forms—hexagonal (a Sic) and cubic (ß Sic)—with the cubic form having a forbidden-gap energy of 2.32 ev and the hexagonal form (specifically the 6H polytype) a gap energy of 2.86 ev.3 It behaves as an extrinsic semiconductor at temperatures approaching 5003C. It has been shown to have a high resistance to radiation damage4 and p-n junctions formed in Sic have been shown to radiate visible light under forward- or reverse-bias conditions. Epitaxial silicon carbide on silicon carbide has been successfully grown through the use of a variety of techniques, such as gaseous cracking of SiCL4 and CC4, nearly all of which require a deposition temperature above 1500°C.6 This paper will cover very recent work on the gas-phase deposition of highly ordered films of silicon carbide on high-quality silicon single-crystal substrates. The films have been shown to ex- hibit junction-rectification properties when geometrically isolated regions are electrically biased with reference to the silicon substrate. There will be no discussion of the mechanism of heterojunction rectification, but the methods of film fabrication, geometry control, and structural evaluations will be covered in detail. Electron diffraction, X-ray diffraction, and diode electrical properties were used to characterize the films and the junctions. GAS-PHASE DEPOSITION OF Sic The techniques for the deposition of silicon carbide films were a logical outgrowth of the standard silicon epitaxial process. The major premise followed was that, for any film to nucleate in an ordered fashion where there is considerable mismatch in lattice parameters (in this case 22 pct), an extremely clean, damage-free substrate surface must be presented to the gas stream. Thus a standard gas-phase HCl etching step was used to prepare the substrates for growth. A minimum of 5 µ of substrate-surface material was removed prior to the deposition of Sic overgrowth films. The techniques used for growing silicon carbide films were those of growing silicon alone, with the added injection of a hydrocarbon gas into the hydrogen and silicon tetrachloride gas stream. The hydrocarbon gases used thus far have been research-grade (99.99 pct) methane (CH4) and propane (C3H8). Propane ultimately gave the best results. The gas flows were controlled through a panel shown schematically in Fig. 1. A hydrogen main stream of 30 liters per min passed through the horizontal quartz-tube epitaxial reactor, while SiC14, C3H8, HC1, and doping gases were injected as side streams. The

Jan 1, 1965

By T. H. Alden

BaCKOFEN, Avery, and Turner have shown"2 that the large tensile elongation in superplastic metals is correlated with a high strain-rate sensitivity of the flow stress. At present, the reported superplastic materials are complex eutectic or eutectoid systems with a large solubility range in at least one of the terminal phases. This note describes the behavior of a solid-solution alloy (at 22°C)5,= Sn-1 wt pct Bi, which has been processed in order to produce a fine grain size.2,3,6 The chill-cast, 1/2-in.-diam ingot was homogenized for 1 week at 130°C, extruded at O°C to 0.083 in. diam, quenched within 15 sec, and stored at -196°C. Samples were warmed to room temperature 16 hr prior to mechanical testing or metallography. During tension testing at room temperature, it was found that the flow stress reached a steady-state value which depended on the imposed elongation rate and was independent of strain to an error of about ±5 pct. In Fig. 1 is plotted log a vs log e where a is the measured steady-state flow stress and i the imposed strain rate. These quantities were calculated using "instantaneous" area and length to an accuracy in the sample diameter of ±5 x 10-4 in. The log a-log 1 curve is sigmoidal. The strain-rate sensitivity, which may be given by d log old log 6,' has a maximum value of about 0.48 between i = 5 x 10-4 and 5 x 10-3 per min. The value is well above frequently measured values for metals at creep temperatures (0.1 to 0.3) and comparable to the rate sensitivity for Pb-Sn solder: which has been shown to be superplastic.2,3 Note, however, that below or above the strain rate of 10-3 per min the rate sensitivity of Sn-1 pct Bi decreases and at high rates is more nearly like that of conventional metals. The grain size of this material is relatively uniform, Fig. 2, and may be specified by an average linear intercept i.' Grain growth occurs at room temperature but after 16 hr, L = 5. Tensile elongation was measured on finer-grain-size specimens, which had been at room temperature 15 min prior to testing. After 15 min, the samples are fully recrystallized. Three strain rates, 5 x 10-3, 10-2, and 2.5 x 10-2 per min, were employed for which the measured elongations varied from 425 to 500 pct. These results would seem to justify the term superplastic, applied to this alloy, although the ductility is inferior to that of the Sn-Bi eutectic.3 The Sn-1 pct Bi alloy, which is a single-phase material with equiaxed, fine grains, is an excellent one on which to make an estimate of the Nabarro-Herring9 creep rate. According to the model of Avery and Backofen2 a substantial part of the deformation must be accomplished by N-H creep in the strain rate-temperature regime in which d log a/d log 1 = 0.5. The maximum N-H creep rate is given by9 L2kT where v is the atomic volume and D the self-diffusion coefficient. For this test v = 3.O x 10-23 cu cm, D = 1.4 e-23,300/RT = 2.5 x 10-l7 sq cm per sec,7 L = 5x 10+4 cm, T = 295°K, and a = 2000 lb per sq in. = 1.38 x 10' dyne per sq cm. The calculated creep rate is E= 4 x 10-11 per sec which may be compared with the measured creep rate at this stress, Fig. 1, of 6.7 x 10-5 per sec. The N-H creep rate is seen to be negligible. Earlier consideration2 of this question was in error because incorrect diffusion coefficients were used. The assistance of R. R. Russell in metallography is acknowledged gratefully.

Jan 1, 1967

By R. E. Pray, M. C. Fuerstenau, J. D. Miller, B. F. Perinne

Quartz cannot be floated with potassium amyl xanthate as collector at any pH. Complete flotation is achieved with certain minimal additions of amyl xanthate and Pb from pH 5.8 to 8.5 and with amyl xanthate and Zn from pH 7.5 to 8.1. The active species of these metal ions responsible for activation are shown to be PbOH and ZnOH No flotation was effected when Cu and Mg were added as activators. Previous work1,2,3,4,5,6,7 has shown that quartz may be floated in the presence of sulfonate or soap when the following two criteria are met: 1) some portion of the added metal ion has hydro-lyzed to its first hydroxy complex, and 2) a precipitate of the metal-collector has formed. Since sulfonate and soap, two substantially different anionic collectors, conform to these criteria, this phenomenon may well be expected to be of a general nature. In this view then, it would appear that any anionic collector, including xanthates, should also float quartz when these two criteria are met. The object of this paper is to demonstrate the conditions under which quartz will respond to flotation in the presence of potassium amyl xanthate. EXPERIMENTAL MATERIALS AND TECHNIQUES Quartz was prepared by leaching the sized sample (48 x 150 mesh) with HC1 until no iron could be detected in the leach liquor. Conductivity water, made by passing distilled water through an ion exchange column, was used in the investigation. Potassium amyl xanthate was selected as collector. Purification of this reagent was effected with the following method: 1) a laboratory sample of potassium amyl xanthate was dissolved to saturation in hot ethyl alcohol and filtered several times while still hot, 2) the filtrate was cooled, during which time potassium amyl xanthate crystallized out of solution; the xanthate was then separated from the solution by filtration, 3) the amyl xanthate was dissolved in fresh hot ethyl alcohol and filtered, 4) step (2) was repeated, 5) the crystalline potassium amyl xanthate was washed with ethyl ether five times, and 6) the xanthate was dried for 24 hours under continuous vacuum. Inorganic impurities are insoluble in hot ethyl alcohol whereas dixanthogen is soluble in ethyl ether. Five-gram charges of 48x150 mesh quartz were conditioned for 3 min in 125 cc of solution containing the reagents and were floated with the small-scale cell and procedure described in previous papers.478 Reagent grade HCl and NaOH were used for pH adjustment, while reagent n-amyl alcohol was added as frother. Frother addition is necessary with this technique, but it should be mentioned that data, similar to those shown in Fig. 2 for 1 x10-4 mole per liter Pb++ and 1 X 10-4 mole per liter AX-, were also obtained with a Hallimond cell in the absence of frother. EXPERIMENTAL RESULTS Clean quartz could not be floated with amyl xanthate at any pH. Flotation was achieved under certain conditions, however, when various metal ions were added to the system. The activating ions used were lead, zinc, copper and magnesium, added as reagent grade chloride salts. Lead as Activator: The effect of Pb++ as activator was examined at five different additions of amyl xanthate (Fig. 1, 2 and 3). When 1x 10-5 mole per liter xanthate was added in the presence of 1 x 10"4 mole per liter Pb ++, no flotation was obtained at pH 6.5 or below, while a recovery of about 60% was effected at pH 7. When the pH was increased to 7.8, no flotation was again obtained, Complete depression was noted from pH 7.8 to about 10, at which point a recovery of about 30% was achieved. At about pH 11, the precipitate of lead amyl xanthate which was present below this pH dissolved and complete depression occurred. When 2.5x 10-5 mole per liter xanthate was added with the same lead addition, no flotation was obtained at pH 5.8 and below, whereas a recovery of

Jan 1, 1965

By R. V. Higgins, A. J. Leighton

Interest by petroleum engineers in the flow of three phases—oil, gas and water—in irregularly bounded porous media lies mostly in the performance calculation of water floods of reservoirs that have been partially depleted as the result of expansion of much of the originally dissolved gas. The authors present a method to forecast three-phase flow in complex geometry and explain the details by the use of a specific example of a five-spot water flood of a partially depleted stratified reservoir. In this example, the fluid and rock properties of a field given by Prats, et al,' were used. The computed results fit the field performance more accurately than Prats, et al, and Slider.' The time required for the high-speed digital computer to make the calculations, including the contributions from the different layered zones, is about one minute. INTRODUCTION The declining rate of discoveries of new oil fields in the United States makes the recovery of more oil from known reservoirs more attractive than previously. Water flooding has an excellent proved background for recovering additional oil economically. Accordingly, the main interest of this paper is in this type of recovery. In petroleum engineering studies, commercial interest in three-phase flow is mostly in the water flooding of reservoirs in which the oil has been partially produced by the expansion of dissolved gas. When water is pumped into these reservoirs, three-phase flow takes place. Although this paper is concerned with these conditions, the principles involved could be used for other conditions when and where they come to the fore. Many investigators have made contributions to non-empirical forecast methods using basic scientific engineering principles. Several of these used the oil in place at the start of the water flood and the oil remaining after a large quantity of water has passed through a core for key values in their calculations. Recently, Prats, et al,' and Slider have reduced assumptions by adding the third phase—gas—in their forecasting methods. Slider uses the mobilities in the immediate vicinity of inlet and outlet wells as an aid to simulate the resistance effect in the five-spat pattern of the flow of oil, gas and water. Prats, et al. minimize assumptions by using previously determined laboratory data for determining sweep efficiency in the five-spot pattern. In neither of these papers is the saturation profile continuously affected by permeability-saturation curves. Sheldon and Dougherty- recently described a method that employs continuously changing saturation profiles using permeability curves, has a minimum of assumptions and needs no prior sweep efficiency. The Higgins-Leighton method, described in this paper, has all of these features; however, many of the techniques are different from those of Sheldon and Dougherty. The Higgins-Leighton method, tested in May, 1961, is direct and easy to apply and requires very little computer time to calculate a forecast. The short computer time is especially helpful in the study of a reservoir containing many layers of different relative permeabilities. In the Higgins-Leighton method, the individual pressures do not have to be calculated, as the resistance to flow in each cell in the flow pattern is readily determined without the use of any iterative techniques. The saturation and permeability distributions are readily determined. These data and the shape factor, which is measured only once from the potentiometric model when mobility ratio is one, determine the resistance to flow in each cell. THEORY The authors showed in a previous paper4 that, as an aid to calculating performance, the reservoir can be divided into channels using the streamlines of a potentiometric model as a guide. See Fig. 1. This procedure also was used in this paper. The authors also showed that, by treating conduits as approximately one-dimensional and neglecting pressure gradients transverse to the main flow, the Buckley-Leverett equation may be expressed as The principles expressed by this equation are employed extensively in the three-phase flow, as they were in two-phase flow. In the three-phase flow, the channels (the size and shape of which are taken from a potentiometric model)

By Henry R. Piehler

Continuous seven- and nine teen -filament close-packed silver-steel filamentary composites mere tested in tension. For purposes of comparison, the tensile behavior of the composite was predicted from the measured properties of the individual com-ponents. It was assumed that the axial strain is the same in both components and that the contribution of each component to the composite flow stress is proportional to its volume fraction. Good agreetnent was obtained between the observed and predicted tensile behavior. However, the composite elongation at fracture was about twice that observed when the individual steel wires were tested alone. Composites in which the filaments were widely spaced failed by the consecutive fracture of the filaments. In composites with closely spaced filaments, a composite instability preceded frachcre. These effects are explained in terms of a lateral restraint to the necking of the filaments which develops in the deforming composite. TWO-COMPONENT or composite materials are increasingly being developed and used as structural materials. Of all the composite geometries used, the filamentary configuration has proved to be the most successful. Polymer-bonded fiber-glas, the most common of the filamentary composites, has been investigated most extensively to date. One explanation of the behavior of fiberglas1 suggests that the load transfer between the glass fibers and the polymer matrix occurs primarily through friction. Bond separation between the fibers and the matrix is presumed to occur at very low stresses. Subsequently, only frictional bonding can provide for the transfer of load from the matrix to the fibers. The force normal to the fiber-matrix interface which gives rise to this friction is assumed to arise from the matrix shrinkage which occurs during solidification. The behavior of metallic filamentary-composite materials would be expected to differ from that of fiberglas in several significant aspects. Residual stresses resulting from differences in thermal contraction can be kept to a minimum by proper heat treatment. A strong wetted bond is formed between the two phases. In brazed joints,2 for example, the interphase bond is sufficiently strong that the weaker material will fail before separation occurs at the interface. Most metal filaments can undergo appreciable amounts of plastic deformation before failure. Failure by plastic instability or necking frequently occurs in metallic filaments, but not in glass fibers tested at room temperature. Differences between the behavior of fiberglas-polymer and metallic filamentary composites have indeed been observed in composites containing various types of metallic filaments in a silver matrix.3,4 At strains of the order of 10-2 pct, all the deformation was accommodated by the silver matrix. Hence, the strength of the composite depended only on the fiber concentration and not on the nature of the fiber. At higher strains, the strength of the composite increased when filaments with higher work-hardening rates were used. Surface slip line observations on a silver-mild steel composite that had been stretched 4 pct showed that an appreciable amount of deformation occurred in the filaments. Work on tungsten-copper filamentary composites5 has shown that the ultimate tensile strength for varying filament fractions followed a linear mixture rule. Assuming that the axial strains in both filaments and the matrix are equal, this linear mixture rule can be expressed as: The subscripts c, f, and m refer to the composite, filaments, and matrix, respectively. A and V are the area and volume fractions of each component. sc and of are the ultimate tensile strengths of the composite and the filaments. sm is the flow stress of matrix at a strain equal to the elongation at failure of the filaments. However, the tungsten filaments can undergo only a limited elongation before they fracture without an appreciable reduction in area. A composite containing more ductile filaments might indeed deviate from this linear mixture rule for the ultimate tensile strength, since filament failure by necking might be arrested by the matrix. SPECIMEN PREPARATION Specimens were prepared from 0.8 pct carbon steel piano wires of 0.015 in. initial diameter. The wires were given a thin nickel flash and a silver plate varying in thickness from 0.015 to 0.007 in., depending on the filament fraction desired. In order

Jan 1, 1965

By V. Koump, T. F. Perzak, R. G. Olsson

The rate of dissolution of recrystallized alumina in molten iron oxide in equilibrium with iron at 1450°C was studied by rotating alumina disks in the melt. The samples were rotated from 1 to 12 min at speeds from 54 to 3270 rpm. It is concluded from the experimental results that the process is limited by diffusion in the liquid boundary layer. The interdiffusion coefficient for the dissolution of alumina disks in pure molten iron oxide was estimated to be about 3 xl0-5= sq cm per sec. THE erosion of refractory materials is of considerable importance in iron- and steelmaking processes. Since many refractories contain alumina, this investigation was undertaken to develop a further understanding of the erosion mechanism. Shurygin et al.1-3 have investigated the rate of dissolution of alumina in molten silicates and molten fluorides by rotating alumina disks in various melts. The rates were reported to be limited by diffusion in the liquid boundary layer. In the present investigation the rate of dissolution of alumina in molten iron oxide in equilibrium with iron was studied in a similar manner; alumina disks were rotated at different speeds in molten iron oxide at 1450°C. The relationship between the rate of dissolution of the flat surface of the disk and the speed of rotation was used to determine whether the process is limited by diffusion in the liquid boundary layer or by some chemical reaction mechanism. APPARATUS AND EXPERIMENTAL PROCEDURE A schematic diagram of the experimental apparatus is shown in Fig. 1. The iron oxide melts were contained in 2-in.-diam high-purity iron crucibles that were centered in a cylindrical graphite susceptor. Prior to each sequence of experiments, sufficient reagent-grade ferric oxide was added to a crucible to form approximately 350 g of molten iron oxide; the depth of the melt was about 11/2 in. To prevent excessive erosion of the crucible, about 70 pct of the required iron was added to the crucible in the form of iron powder. The mixture was melted in an atmosphere of purified argon by induction heating with a 250-kc generator. After the oxide was molten, a Pt/Pt-10 pct Rh thermocouple at the exterior of the crucible was calibrated against an iron-sheathed thermocouple immersed in the melt and was thereafter used to regulate the melt temperature. All experiments were conducted at 1450°C with a probable error of 10°C. The alumina disks were constructed from pure re-crystallized alumina having a density of 3.7 g per cu cm (porosity approximately 6 pct). For each disk sample a 1-cm-diam alumina cylinder of known length (0.9 to 1.0 cm) was cemented into a ground seat at the end of a 1.27-cm-OD centerless ground alumina tube. The ends of the tube and cylinder were flush and served as the disk surface. When mounted in the apparatus the alumina tube was guided by tungsten carbide bearings and rotated by a variable-speed motor. The bearing and drive assembly could be raised and lowered in order to allow the sample to be quickly moved in and out of the melt. At the start of an experiment, a sample was preheated for several minutes directly above the melt, and then immersed in the middle of the melt to a depth of a in. and rotated for 1 to 12 min at speeds of 64 to 3270 rpm. The speed of rotation was measured by a hand tachometer. At the start and completion of each experiment, a melt sample was withdrawn with a cold copper rod and the alumina content was determined by chemical analysis. During individual experiments the alumina concentration of the melt changed by the order of 0.25 wt pct. Average melt compositions for individual experiments were used in the subsequent computations and were in the range between 0.12 and 4.3 wt pct alumina. The extent of dissolution was determined by sectioning the end of the sample and measuring the final length of the alumina cylinder with a microscope. Since the exposed end of the cylinder, i.e., the disk surface, was etched in a manner characteristic of this geometry, a number of measurements were made on

Jan 1, 1969

By C. W. Allen, B. D. Cullity

The proportional limit of iron crystals in torsion is governed by the resolved shear stress in the most highly stressed slip systems, averaged around the specimen circumference, and does not obey a critical resolved shear stress law. Crystals of most orientations exhibit a stage of easy plastic deformation, akin to easy glide in tensile or shear specimens. Transient deformation, similar to that which occurs in single crystals of other materials, is also observed. THE torsional deformation of single crystals of magnesium (hcp) and aluminum (fcc) has been described recently by Choi et al.,&apos; especially with respect to the criterion for the orientation dependence of the onset of plastic flow in these materials. The purpose of this paper is to present results of torsion tests of iron single crystals and thus to extend this yield criterion to a bcc metal. In addition to considering the variation of proportional limit with crystal orientation, this paper also briefly treats work hardening, transient deformation, and the mechanism of plastic flow in iron. The effects of the method of surface polishing and the chemical purity of the iron have been investigated. STRESS DISTRIBUTION It is convenient to express the stress at any point of a cylindrical crystal stressed in torsion in terms of t0, which is the shear stress acting at the surface on a plane normal to the axis of the cylinder and in a direction tangential to the cylinder. This stress is given by To = 2T/pr3 [1] where T is the applied torque and r the specimen radius. The shear stress t, resolved in any chosen slip system is given in terms of 7, by1 Ts/TO = sin 0, cos d sin (0, -) + cos , sin d sin d - ) [2] where 0 and d are the angles between the specimen axis and the slip plane normal and slip direction, respectively; h is the angular circumferential position on the specimen at which t, is being determined, measured from an arbitrary reference plane which includes the axis;o and d are the angular coordinates of the projections of the slip plane normal and slip direction on a transverse section with respect to this same reference plane. Slip in iron occurs in a <1ll> direction on the {ll0}, (1121, and (123) planes, which together comprise 48 slip systems. A complete evaluation of the stress distribution in an iron crystal stressed in torsion would therefore require a calculation of Ts/T0 as a function of for 48 different slip systems. Fortunately Gough,&apos;who studied the behavior of iron crystals in alternating torsion, was able to simplify this problem considerably. He showed that it was sufficient to consider a kind of average slip plane for each slip direction, namely the mathematical plane of maximum resolved shear stress containing the slip direction considered. This simplifying approximation is possible because, for each slip direction, the active slip plane or planes lie very near this mathematical plane of maximum shear stress. Vogel and rick&apos; have critically reviewed the early work of Taylor and Elam,13 Taylor,14 and Fahrenhorst and schmid8 from which the identification of the above crystallographic planes as slip planes in the bcc lattice largely stems. While their criticism is clearly justified, their own results do little to clarify the issue. The role of cross slip (screw dislocations changing glide planes) is evidently so important in this case, as Read3 has suggested, that methods for deducing slip systems from observations of gross slip traces are inadequate, such traces commonly arising from complex dislocation motion. Thus the treatment given here involving the plane of maximum resolved shear stress seems a logical simplification especially in view of Gough&apos;s2 study of a iron. There is, however, an assumption built into the subsequent treatment the comparative validity of which is difficult to assess, namely, that slip in all slip systems in iron may be characterized by a common critical resolved shear stress. The shear stress 7, resolved in a slip direction defined by d andd, and on the plane of maximum shear stress containing this direction, is found by first maximizing 7s/70 with respect to either Oo or 4,. The slip plane coordinates are then eliminated by using the relation between 0, ,o and d, d, namely,

Jan 1, 1963

By J. C. Fisher

Martensite transformations in steels and other alloys are characterized in part by the absence of composition changes during the growth of a new phase. Transformation occurs rapidly, and there is insufficient time for long range diffusion or partition of alloying elements to take place; martensite reactions in alloys thus are similar to phase transformations in single component systems. A fundamental understanding of martensite transformations in steels is impossible without knowledge of the free energy change upon transforming austenite (face centered cubic iron containing alloying elements) to ferrite (body centered cubic iron containing alloying elements) of the same chemical composition. The present paper assembles the best information available concerning the influence of temperature and composition on this free energy change. Most of the material has been taken from the work of Johansson,&apos; Mehl and Wells,2 Zener3,4 and Smith;5 and indirectly, through these authors, from the work of Austin.6 In agreement with the generally accepted viewpoint, martensite is assumed to be an ordered solution of carbon in ferrite of the same composition as the parent austenite; only at high temperatures and low carbon concentrations is the carbon in ferrite distributed at random. The properties of the disordered solution are estimated by extrapolating the known properties of iron-carbon solid solutions into the range of supersaturation, and the free energy change associated with ordering is estimated from the theory developed by Zener. By incorporating Smith&apos;s recent thermodynamic measurements and Zener&apos;s theory of ordering, the present analysis modifies previous estimates of the free energy change associ- ated with martensite transformations. Consider a two component system consisting of a solvent A and a solute B. Let Na and Nb represent mol fractions of A and B respectively, let aa = raNa and ab = YbNb represent activities, and let superscripts 1 and 2 refer to phases 1 and 2. The partial molal free energies of A and B in phases 1 and 2 can be summarized as follows: free energy standard state Fa&apos; - Fao1 = RT In an1 pure A&apos; Fa2 - Fa2 = RT In aa2 pure A2 Fb1 - Fbo = RT In ab1 pure B Fs2 - FB2 = RT In aB2 pure B. The free energy of a gram atom of phase 1 is* AF1 = Na&apos;Fa1 + Nb&apos;Fb1 and that of phase 2 is AF2 = NA2FA2 + NB2Fb2. A martensite transformation from phase 1 to phase 2 requires Na1 = Na2 = Na and NB1 = NB2 = Nb, and the free energy change per gram atom accompanying transformation is AFi-2 = NA(Fa2 - Fa1) + Nb(Fb2 - Fb1) = NA[RT In (aA2/aA1) + AFa1?2] + Nb RT In (aB2/aB1) = Na[RT In (ra2/ra1) + AFa1?2] + Nb RT In (TaVTB1). [1] where yn2, yn1, yB2, yB1 are activity coefficients, and where Ma&apos;+* is the free energy change upon transforming a gram atom of pure A from phase 1 to phase 2 at the temperature in question. For martensite transformations in plain carbon steels, A = iron (Fe), B = carbon (C), 1 = austenite (7). 2 = ferrite (a), and Eq 1 is AFr ?a= NFe[RT In (rf.a/rfer) + AFF.r?a] + TVc RT In (eca/rc1)- L2] Nothing is known concerning the values of yFea and yca for carbon concen- , trations in excess of 0.025 pct. However, the approximation rf.7 = 7f." = 1 cannot be appreciably in error for small carbon concentrations, and Eq 2 reduces to Afr-a = NfeFfer?a1 + NC RT In (rca/rcr)- [3] Johanssonl and Zenera have calculated MFfr?a from the specific heat measurements compiled by Austin.6* Their calculated values agree closely, and are summarized in Table 1. The activity coefficients relative to graphite for carbon dissolved in iron vary with temperature according to the relationships d In rcr/d(1/T) = AHcr-R dlnyca/d(l/T) = AHCa/R where AHc? and AHca are the heats of solution of graphite in y and a iron. Assuming the values of AH to be independent of carbon concentration and temperature, In rCr = AHcr/RT + I1 In rca = AHCa/RT + 12

Jan 1, 1950

By M. R. Tek, K. H. Coats, D. L. Katz

The nature and the limits of validity of Darcy&apos;s law US applied to the flow of natural gas through reservoirs has been considered in order to resolve some controversial aspects of the effect of turbulence on pressure drops. The equivalence between various concepts and viewpoints advanced in the past by several investigators to explain how and why a gas well does not necessarily perform according to Darcy&apos;s law is shown. Starting with generalized equations of flow of fluids through porous media, a partial differential equation has been derived which accurately represents the flow at all rates. This equation has been numerically solved using an IBM 704 digital computer. The results permit plots of unsteady radial pressure distribution curves from which specific isochronal backpressure curves may be constructed. These back-pressure curves show the effect of the ,8 factor on the slope of the back-pressure curve. The calculations further indicate that the drainage radius for a gas well in turbulent flow propagates at a rate dependent upon the rate of production at the wellbore. This is quite different from the case with liquid flow or natural-gas flow in laminar regime. Additionally, the effect of reservoir inhomogeneities and crossflow between layers of different permeability on the back-pressure performance of gas wells has been conridered. In light of the current numerical results the significance and linlitation of the rate of flow function Y proposed by Smith" has been discussed. INTRODUCTION The relationship between the pressure drop and flow rate in problems of fluid flow through porous media is known to be affected by the nature of flow through the porous matrix. It has been observed by many that, for a range of flow rates, the pressure drop remains proportional to the rate of flow. When some flow rate is reached, however, it is usually observed that the pressure drop gradually begins to increase more than proportionally to the flow rate. It is well known that this phenomenon was first observed by Osborne Reynolds in 1901 in experimenting with flow through pipes. In his classical experiments, Reynolds made visual observations on the condition of streamlines evidenced by injecting a dye into water flowing through glass tubes. In these experiments, the abrupt transition between steady, "streamline, laminar" flow and unsteady random turbulent flow was found to be a function of the dimensionless group (Dvp/u), now known as the Reynolds number. During these experiments, in addition to observations on the nature of flow regimes, the proportionality between flow rate and pressure drop in laminar flow was contrasted with the nonlinearity between these variables in turbulent flow. Fancher and Lewis&apos; reported data on various consolidated and unconsolidated sands in 1933. Their conclusions were that ". . . the flow of fluids through these porous materials closely resembles that through pipes; that there is a condition of flow in porous systems which resembles viscous flow, another which corresponds to turbulent; that the change from one type to the other takes place at a definite and reproducible condition for each system". In 1947, Brownell and Katz published a method to predict the laminar and turbulent flow behavior from the particle size, bed porosity and the particle sphericity, employing the friction factor-Reynolds number charts for pipes. Several investigators have verified the work of Fancher, Lewis and Barnes and presented their data as friction factor-vs-Reynolds number plots.&apos; The equation which would represent the pressure gradient over the whole range of velocity must have an added term over that represented by Darcy&apos;s law. Accordingly, the pressure gradient necessary to sustain flow at the velocity (v) through a porous medium may be represented by the following equation, suggested by Forscheimer." The nature and the range of validity of Darcy&apos;s law has been the subject of studies by many investigators over the past years. While everyone seemed to agree on the need for a quadratic correction term to Darcy&apos;s law to make it effective over the range of velocities, the concept of inception of turbulence and the use of the term "turbulent flow" remained controversial. Some fluid dynamicists define turbulence as a flow

By Elmer Weber, W. M. Baldwin

Solid lead obeys a single parabolic weight increase vs. time law. In contrast, liquid lead undergoes three successive parabolic weight increases vs. time laws, the first of which has a low constant relative to the latter two. The conversion times for the change from one parabola to the next decrease with increasing temperature. IN recent reports on the subject,1,2 it was noted that zirconium and titanium scale in air by a complex mechanism. The scale first forming on the metal is protective to the extent that it gives a low constant, K, for Tammann&apos;s, and Pilling and Bedworth&apos;s parabolic equation: w² = Kt [1] relating weight increase, w, due to chemical reaction of the metal with the air, and time, t. After hundreds of hours of apparent stability in some cases the first scale yields to another that offers little protection to the metal. This transition from one scale to another, from a slow parabolic oxidation reaction to a fast one, was not due to impurities in the atmosphere or incidental effects (changing environment, etc.) but was a specific behavior of the metal itself, the transition occurring at definite times (dependent on temperature) and showing other reproducible traits. In view of this behavior how can long-time service behavior be predicted from short-time laboratory tests, not only in the case of these metals, but in any case? Certainly a systematic study of the type of scaling behavior described above—wherever it is found—would help to answer this question. The present paper is a report on the behavior as it is found in lead—the only metal to the authors&apos; knowledge for which the behavior has been described at all, if inadequately, for our present purpose.* At least four oxides of lead are known, of which one occurs in two allotropic forms. They are ß (red) tetragonal PbO stable up to 486°C;8 a (yellow) orthorhombic PbO stable from 486°C up to its dissociation temperature in air at about 2300°C;9 minium or Pb3O4 which from the dissociation pressure data given in Fig. 1 decomposes to PbO at 540°C in air; lead sesquioxide or Pb2O3,; and lead dioxide or PbO2 which, according to Fig. 1, decomposes in air at 400°C to minium. In view of the high dissociation temperature of PbO, lead will scale up to at least its boiling point. Further, it is known that oxygen is almost insoluble in liquid lead.&apos;V his implies a fair probability that an oxide scale would not dissolve in the molten metal and would afford the same protection to lead in the liquid state as in the solid. All of the oxides of lead for which specific gravity data are available are more voluminous than an equivalent weight of metal or a lower oxide from which they might form, hence the scales will be in compression. Lead oxides are known to be ductile, so it would be anticipated that they would form coherent nonporous scales. It is not surprising to learn, then, that both solid and liquid lead scale according to the Tammann, and Pilling and Bed-worth law.14,15 (Gruhl states that at 600°C and above lead oxidizes linearly with time because of "spitting" of the scale.) The parabolic constants K reported by various investigators3,14-16 are badly scattered, however, as shown in Fig. 2. The oxides formed on solid lead were described as being reddish-brown but were not chemically identified by Pilling and Bedworth.15 Gruhl&apos;s descripdin³ of the appearance of the scales On his liquid samples indicates that a (yellow orthorhombic) PbO is formed initially on the specimens but gives Way eventually—at least at temperatures below 486 °C— to .ß (red tetraunal) PbO, and that below 540°C minium—Pb3O4 :is firmed at an even later time as an overlay on either the red or yellow PbO. Fig. 3 is a graphical interpretation of Gruhl&apos;s description. Gruhl does not indicate any change in the parabolic scaling rate as yellow PbO converts to red. He does indicate that minium reduces the scaling rate, al-

Jan 1, 1953

By Lyman H. Hart

Some of the significant facts that will affect the supply and demand for metals during the next few decades are given in this presentation. This is important because the only hope for intelligent guidance of the national destiny depends upon presenting a consistent and accurate picture of basic problems. The metals problems now fomenting are only slightly less important than those precipitating the energy crisis. Admittedly, it is difficult to generate serious thinking on this subject when the world is enjoying easy access to all metals at modest prices. This is possible because of the current world capacity to over-produce, and United States credit standing, at least up to now, has permitted buying freely on world markets. Although both these vital conditions are subject to change, there is little doubt that if the U.S. financial house is kept in order, we can muddle along for a while on a generally expanding, metal-based economy. But should our credit standing be permitted to collapse, or should there be a tightening of world supplies of metals, the nation would immediately find itself in trouble. Unfortunately, clear signals indicate that both of these conditions are threatening. The metal age started many centuries ago, and with the exception of the noble metals, barely a dent was made in world reserves until the present century. Then, as a result of the pioneering ideas of D. C. Jackling and Paul Gemmel, and the willingness of the McNeals, Penroses and Guggenheims to back ideas with money, a virtual explosion of metal production was propagated throughout the world. It is important to examine the causes of this expansion to determine whether it is a trend that may be sustained or whether it is anomalous and therefore attributable to circumstances not likely to be repeated or continued. This period of plenty is a once only phenomenon. Vast metal resources have been sitting around here for eons, while the world was unaware of or unconcerned with their existence. But when population began to grow exponentially, and ways were discovered to use metals to develop machines to do the work of men and animals, the exploitation of raw materials increased at a staggering rate. And now the realization is dawning that minerals are a wasting asset and are beginning to present supply problems that should begin to be of concern. Two main factors have caused this condition; One is the population growth, and the other is the expanding demand for irreplaceable raw materials as nations become more developed. A group of systems analysts, at Massachusetts Institute of Technology in a book Limits of Growth, has warned that at present rates of population growth and resource consumption together with environmental constraints, a point will be reached within 100 years when the world population will become totally incapable of supporting itself. The authors conclude that this end result could be avoided if a planned equilibrium could be established at a lower rate of population growth and resource consumption. Fortunately, there is evidence that the population problem is moderating. The growth rate in the U.S. has decreased from 2.3% per year in 1900 to 1.1% in 1970. But, even at the lower rate, population will double in 70 years. The world rate is greater, and if it continues, world population will rise from 3.5 billion to nearly 10 billion in 50 years. All of these projections are questionable because the dangers of growing population are now being recognized. A marked decrease in growth rate has been noted in the more developed countries-in fact, it was zero in the U.S. in 1972. The other factor affecting consumption of raw materials is the increase in per capita use of most items as individuals become more affluent. Many economists believe that developing countries such as China and India represent a vast future potential market; but there are others, with whom the author agrees, who believe over-population tends to stagnate development. Nevertheless, it is a fact that vigorously developing societies increase consumption at a rate far above their population growth rate.

Jan 1, 1974

By R. Taggart, D. H. Polonis, W. C. Gallaugher

In the Ti-Cu system, the a&apos; phase can be produced over a wide range of alloy composition witJwut the retention of measurable amounts of the ß or ? phases. This paper reports on the decomposition of this hexagonal martensite phase front the standpoint of solute corzcentratiorz, tempering temperature, and coherency strain condition. The mechanism of precipitation during tempering comprises localized precipitation which is followed by discontinuous precipitation if sufficient coherency strains are present. The localized precipitation process in hypoeutectoid alloys is described by the generalized Johnson-hiehl equation and an activation energy of 46,000 cal per mole. In hypereutectoid alloys the corresponcEing activation energy is 51,000 cal per mole. The rate-controlling process has been proposed as the difision of copper along a&apos; platelet interfnces. SEVERAL investigations have been reported concerning the kinetics of decomposition of the mar-tensitic a&apos; phase in titanium binary alloys.&apos; In the Ti-Mo system,&apos; two modes of a&apos; decomposition have been observed in the presence of /3 phase; one of these involves the precipitation of fine a from a&apos;, and the other involves diffusion across the a&apos;-ß interface. In studies of the Ti-Cr system, Rostoker2 did not detect the formation of TiCr2 during tempering. In Ti-Ni alloys,3 the intermediate phase Ti2Ni has been found to precipitate directly from a&apos; along the interfaces between plates. With the exception of the study of Ti-Ni alloys the previous investigations of tempering phenomena in substitutional martensites are mainly qualitative and do not present a detailed description of the precipitation processes. The following limitations restrict the correlation of the microstruc-tural processes and reaction kinetics during tempering in most binary-alloy systems. 1) A mixture of at least two phases characterizes the constitution of quenched alloys. 2) Difficulties have been encountered in obtaining uniform structures throughout quenched samples. 3) The reaction products, and in particular their morphology. have not been clearly resolved. 4) The martensitic a&apos; phase forms over only a limited composition range for most titanium-base binary alloys. Gomez and polonis4 showed that the Ti-Cu system provides an excellent basis for investigating the tempering of a&apos; over a range of composition without the complication of retained P or the transition w phase. In the present work the effects of solute concentration, tempering temperature, and coherency strain conditions are considered with reference to the over-all precipitation process in quenched alloys of the Ti-Cu system. Both microstructural observations and kinetic data are correlated to define the rate-controlling processes which govern the observed localized and discontinuous precipitation reactions. An earlier paper5 was devoted to a discussion of the modes of heterogeneous nucleation of Ti2Cu from the martensitic a&apos; structure. The present paper will therefore emphasize the progress of the tempering reaction beyond the initial stages. EXPERIMENTAL METHODS The Ti-Cu alloys for this study were prepared by conventional arc-melting procedures. Chemical analysis revealed that the alloy buttons contained approximately 0.02 wt pct 0, 0.04 wt pct N, and within 0.1 wt pct of the intended copper concentration. The progress of the tempering reaction was followed by means of electrical-resistance measurements utilizing a Kelvin double bridge, microhard-ness readings with a 400-g load, and X-ray dif-fractometry patterns to reveal line-broadening effects. Metallographic specimens examined at magnifications greater than X1000 were shadowed with germanium to reveal fine structural details. Direct carbon replicas were prepared for the electron-microscopy studies. EXPERIMENTAL RESULTS Property Changes. The changes of microhardness that accompany the precipitation of Ti2Cu from a&apos; are shown in Figs. 1 and 2. As the solute concentration increases the peak hardness, for a given tempering temperature, increases. In alloys of given composition the time to reach the peak hardness agreed with the time to attain maximum X-ray diffraction peak breadth, as shown in Fig. 3. The maximum hardness and the maximum line breadth increased with lower tempering temperatures, and the time to reach the maximum also increased. The a&apos; peaks broadened during the initial stages of tem-

Jan 1, 1965

By Klaus Schwerdtfeger

Activities of lead in Pt-Pb and Pd-Pb melts in the temperature range of 800° to 1200°C have been detev-mined from electromotive-. force measurements 202th the cells Both systems display strong negative deviations from Raoult&apos;s law. The data obtained with cell [1] were combined with available data on the activity of PbO in silica-satuvaterl PbO-SbO2 melts to calculate the standard free cnergy of formation 01- liquid PbO. FREE energies of formation of oxides and activities of components in metal and oxide melts can be determined with galvanic cells consisting of a metal phase, an electrolyte containing the oxide of one of the components of the metal phase, and an oxygen electrode. This technique has been used previously to measure the standard free energy of formation of solid sio2, 1 and activities in Fe-si, CO-si,2 Ni-Si,2 and CaO-P2O5 3 melts. The present paper reports activities in Pt-Pb and Pd-Pb melts as measured with the same experimental technique. EXPERIMENTAL METHOD General Considerations. The following cells were used: Pbl (PbO-SiO2)liquid, SiO2 Pt-Pb 1 (PbO-SiOz)liquid, SiO2solidO2 [2] Pd-Pb (PbO-SiOz)liquid, SiO2solid O2 [3] Liquid alloy and&apos; oxide melt were contained together in a silica glass crucible of essentially the same design as described previously.1&apos;2 The PbO-SiO2 melts are ionic conductors.&apos; During the experiment, the silica glass crystalizes in a layer adjacent to the electrolyte. The electrolyte equilibrates with solid silica and hence attains the composition of the Si02-liquidus curve in the system PbO-SiO2 at any particular temperature. Molybdenum wires were used to establish contact with the liquid metal. The oxygen electrode, which reaches the surface of the PbO-SiO, electrolyte from above, consists of a platinum wire inserted into a ceramic tube and provided with a 2-mm-diam platinum bead at its end. Gas of known oxygen partial pressure (pure oxygen of 1 atm: air, or N2 with 1.04 pct 0,) is blown through the ceramic tube onto the surface of the electrolyte. The cell reaction is Pb (metal) + 1/2O2 (gas) = PbO (electrolyte) [4] No oxidation of platinum or palladium ("displacement reaction") occurs. This is to be expected from the noble character of platinum and palladium, but was also shown experimentally, as described in the next section. The galvanic electromotive force of the cell is given by where AG is the change in free energy for Reaction [4], E(=2) is the number of electrical equivalents necessary to form 1 mole of PbO, and F is the Faraday constant. Formula [5] is valid only if no junction potential exists within the electrolyte. Junction potentials occur only when the compositions of the electrolyte are markedly different at the electrodes. Such differences are negligible in the PbO-SiO, electrolyte, as shown in the next section. Since molybdenum contact leads are used, appropriate corrections were made on the measured electromotive forces to account for the thermoelectric effect of the Mo-Pt couple. The thermoelec-tromotive forces were measured separately with a Mo-Pt couple, and were found to vary linearly from 19 mv at 740°C to 40 mv at 1310°C with molybdenum being positive and platinum negative (cold junction at 25°C). Extrapolation of these values to higher temperatures yields values which are in satisfactory agreement with those obtained previously in the temperature range 1440° to 1630°c.1,2 The change in free energy for Reaction [4] is expressed as where chemical potentials of the species. The value of constant for a given temperature because the slag composition is fixed. Inserting [6] into [5] and using appropriate expressions for upb and uO2 the relation

Jan 1, 1967

By W. O. Philbrook, R. S. Kaplan

Rates of oxidation were studied for levitation-melted samples of Fe-C, Fe-Si, Fe-C-Si, Fe-C-P, Fe-C-Mn, and Fe-C-S alloys oxidized by mixtures of either 5 or 10 pct O2, in helium at several temperatures in the range 1850o to 2050°C. The concentrations of the oxidized elements decreased linearly with time. Mass transport in the gas phase was found to be the rate-controlling step. Ilowever, a mulliple -film model was necessary to account for the flux of iron and manganese vapor counter to the oxygen flow. THE advent of the basic oxygen and spray-refining processes of steelmaking has generated considerable interest in the kinetics of reactions between oxygen-bearing gases and liquid iron alloys. The object of this research was the determination of the role of mass transport in the gas and metal phases and of surface chemical reactions in the overall oxidation process. Of the reactions for elimination of elements dissolved in liquid iron, the oxidation of carbon has been investigated most extensively. Studies by Fuji and Ura,1 Fuji,&apos; and Gunji et a1.,3 done with pilot-scale basic oxygen furnaces, indicated that mass transport of gaseous oxygen was rate controlling when the metal carbon content was greater than 0.15 to 0.30 pct. When the carbon content was less than this critical amount, diffusion of carbon dissolved in the iron was thought to be rate limiting. L. A. Baker et a1.4,5 levitated samples of iron-carbon alloys and oxidized them in CO-CO2, CO-C02-He, and O2-He atmospheres at 1660°C. These investigators found that the metal carbon concentration decreased linearly with time and their samples exploded when the carbon content fell below about 0.8 pct. They concluded that the rate-limiting step was the transfer of oxidant to the gas-metal interface. A model based on this rate-limiting step predicted decarburization rates within a factor of two of those experimentally observed. The explosion of the samples was attributed to a shift in rate-controlling step from gas-phase mass transport to transport of carbon dissolved in the metal. L. A. Baker and R. G. ward6 and R. Baker7 used freely falling droplets to investigate oxidation kinetics. In both papers, the authors speculated that flame fronts may have been partially responsible for the lack of better agreement between experiment and theory. Swisher and Turkdogan8 oxidized liquid iron having an initial carbon content of 0.97 pct with CO-CO2 and CO-C02-Ar mixtures at 1580°C. They concluded that a surface reaction was the rate controlling step. Iron-silicon alloys have been oxidized by R. Baker7 and Filipov and Martynov.9 R. Baker 7 also studied iron-carbon-silicon alloys falling as liquid droplets through oxygen. He found that the rate of both carbon and silicon oxidation varied inversely with the drop radius. When the initial silicon concentration was greater than 6 pct, the samples cooled during their fall. Manganese oxidation has been studied by R. Baker,7 and by Filipov and Martynov.9 ward10 investigated the loss of manganese from liquid iron under vacuum. He found that mass transport of manganese vapor was rate limiting in argon atmospheres of 0.02 torr to 700 torr pressure. Iron-sulfur alloys were desulfurized with H2-He and H2-Ar mixtures by Peters et al.11 A model based on the transport of H2S from the gas-metal interface into the bulk gas gave fair agreement between the predictions of the model and the experimental results. EXPERIMENTAL TECHNIQUE Essentially, the technique consisted of using helium-oxygen gas mixtures to oxidize levitated samples of liquid binary and ternary iron-base alloys. The fused silica reaction tube is shown in Fig. 1. The coil design is similar to that of L. A. Baker et al.4&apos;5 A Tef-lon-sheathed, ferritic stainless steel lifter (B) and an alumina pedestal (C) were used to support the sample in the coil prior to levitation and for the recovery of the sample. Samples were inserted into

Jan 1, 1970

By Robin O. Williams

The increase in internal energy as the result of deformation has been measured for lead, aluminum, silver, nickel, iron, and zirconium by using rapid, adiabatic compression. The stored energy increase is roughly Proportional to the strain; the propor-tionality constant increases rapidly with increasing melting point. The fraction of the mechanical energy which is stored increases more slowly, since the strength of the metals also increases with melting point. The values of the stored energy are considered accurate to about 10 pet. The present values appear about 50 pet larger than the more reliable published results where comparisons are possible. It is possible that this difference is due to the high strain rate used in this investigation. Immediately after deformation all these metals release energy at a rate roughly proportional to (time)-&apos;. This release is considered to be associated with dislocation motion but in aluminum (and copper) some additional process seems to be present. This release can represent 20 pet or more of the stored energy. WHEN pure metals are plastically deformed, most of the mechanical energy is converted into heat. The energy remaining within the metal is significant in that it is the energy of the disorder produced and thus detailed knowledge of this energy is a powerful tool in understanding the nature of deformational disorder. While much effort has been expended on this problem, the amount of information available is limited. The situation as of 1958 has been carefully reviewed by Titchener and ever.&apos; The present results have been obtained by a new experimental approach to this problem. The method necessitates high-strain rates which make comparisons with published results less certain, but a high-strain rate is an advantage in that the energy release immediately after deformation can be followed. EXPERIMENTAL PROCEDURE In the experimental method used, the internal (stored) energy is given as the difference between the mechanical work used in deforming the sample and the heat which is released (the first law of thermodynamics). The work is supplied by two identical hammers swinging freely from a fixed height, the available energy being the product of the mass, the gravitational constant, and the distance through which the center of gravity moves. The initial temperature rise of the sample represents the heat produced by the deformation. The sample temperature is determined by a small thermocouple embedded in and supporting the sample. This process can be repeated over and over to produce increased strains. Most samples are run through about five cycles to a total strain of around 0.7. Further details are covered elsewhere. The determination of the heat is dependent upon the sample weight, its specific heat, the rise in temperature, and any gains or losses to the surroundings. One is dependent on published results for specific heals (the values were taken from a collection).3 The values must be accurate to about 0.1 pet in order that they not affect the results. The best values thus do not contribute to the uncertainty, but this is probably not always the case. The accuracy of the temperature rise is limited primarily by knowledge of the thermocouple characteristics over short temperature intervals, but careful calibration eliminates this as an important factor. One can calculate readily the heat flow between the sample and hammers if the time of contact and the sample temperature are known and if there were no oil at the interface. Assuming the maximum temperature difference, upper values for this interchange have been calculated (the time of contact is determined from the decrease in sample length) and it may or may not be significant. However, no correction is colnsidered necessary because of the presence of a thin oil film which has a thermal conductivity much less than the metals. Except for the possible uncertainty in specific heat, the heat is considered to be adequately known. The mechitnical losses which are recognized as important are: 1) friction between the sample and the hammer:;, 2) the kinetic energy in the hammer suspension system which may not be entirely usable, 3) the rebound energy of the hammers, and 4) the vibration of the hammer heads. All these have been covered in detail elsewhere2 and only the more significant points are made here. The friction turns out to be small except for soft materials (lead)

Jan 1, 1962

By R. A. Breitrick, J. N. Swinderman, J. J. Cooper, H. L. Bauer Jr.

The Robinson Mining District, near Ely, Nev., is one of the major porphyry copper districts in the world. Within the district is an eight mile long east-trending zone of altered porphyry, metamorphosed sedimentary rocks, and sulphide mineralization surrounded by Paleozoic limestone, dolomite, shale and sandstone, Tertiary volcanics, and Quaternary alluvium. Six major disseminated ore deposits have been exploited in this zone. About 20% of the district production has come from disseminated ore in metamorphosed sedimentary rocks found adjacent to altered quartz-monzonite porphyry. The following brief statements summarize some of the relations between porphyry alteration, metamor-phism, and mineralization: 1) Disseminated copper ore does not occur in unaltered porphyry or in m-metamorphosed sedimentary rocks. 2) Sedimentary rocks have been only weakly metamorphosed where intruded by unaltered porphyry. 3) Intensely metamorphosed sedimentary rocks are found only adjacent to altered porphyry. 4) Many hydrothermal minerals are common to both altered porphyry and adjacent metamorphosed sediments. 5) Disseminated ore is found in altered porphyry and adjacent metamorphosed sedimentary rocks. 6) In general, there is a direct correlation between grade of ore in porphyry and copper content in the adjacent rocks. 7) Chemical changes in the altered porphyry and metamorphosed rocks appear to be related. The foregoing relations support a hypothesis that the porphyry alteration, the metamorphism of the sedimentary rocks, and the ore deposition were all part of a continuous hydrothermal process which probably closely attended the porphyry intrusion. The Robinson Mining District, most often referred to as the Ruth or Ely District, is located in eastern Nev. and is one of the major porphyry copper districts of the world. Production from 1908 through 1962 was nearly 250 million tons of ore averaging a little over one percent copper with a total metal value of nearly one billion dollars. The ore has been produced from six major disseminated-type deposits with the Liberty Pit deposit accounting for 70% of the total district production. Less than one million tons of base metal and gold ores have been produced from the replacement-type deposits of the district. Approximately 20% of the district production has come from underground mining operations; the pit ore has been mined with shovels and removed by train haulage, truck-train haulage combinations, truck haulage, and presently by a combination truck-skip system. Many of the ore deposits formerly worked by underground methods have been and are being exploited by open pit methods. (See Fig. I.) Two co.&apos;s have accounted for virtually the entire production from the district. In 1958 Kennecott Copper Corp. acquired the district assets of Consolidated Coppermines Corp. and is now the sole ore producer in the district. Present operations are confined to the Liberty Pit where 22,500 tons of ore averaging a little less than 0.8% copper is mined per day. Cutoff grade is 0.4% copper, and the stripping ratio is three to one. The ore is hauled by rail 23 miles to the McGill Reduction Plant where it is concentrated to about 20% copper. Molybdenite is recovered as a by-product in the mill. The copper concentrates are smelted in McGill, and the blister copper is shipped for refining to Balt. where gold, silver, platinum and palladium are recovered. The Robinson Mining District has been well known as a porphyry copper district for the past fifty years, but many geologists are unaware of the fact that a large portion of the production has come from disseminated ore found in metamorphosed sedimentary rocks. The scope of this paper describes the occurrences of disseminated ore in the various metamorphosed sedimentary rocks, and presents evidence for the hypothesis that these ores are genetically, spacially, and coevally related to the disseminated ore in the porphyry rocks. Publication of this paper was granted by the management of Kennecott Copper Corp. A. H. James suggested and encouraged the writing of the manuscript. Special mineralogical and spectrographic analyses were performed by the Kennecott Research Center. The deposits of the district have been studied by many geologists since the turn of the century, and

Jan 1, 1964

By J. O. Edstrom, G. Bitsianes

Parabolic rate constants were determined for the formation of wiistite by the solid state reaction between magnetite and iron. The reaction was diffusion controlled and inert marker studies indicated that the mass transport through the wiistite layer was accomplished by means of iron migration. Relationships between rate constants and self-diffusivities are discussed. The transport capacity for iron through dense wustite layers was found to be sufficient to carry on reduction, even in gaseous reduction processes. REDUCTION of iron oxides has been the subject of many investigations. Most of the work, however, has been done on rather crude material and there have been difficulties in correlating the data on a quantitative basis. The reverse process of the oxidation of iron has been studied more thoroughly and usually by starting from the pure metal. As a result, the mechanisms of oxidation are now fairly well known.It has generally been found that the oxidation of metals follows the so-called parabolic 1aw;Q hat is, when the oxides are formed as dense layers, their thicknesses are proportional to the square root of the reaction time. This parabolic law follows directly from Fick&apos;s first law of diffusion The flux, J, is defined as the quantity of diffusing substance passing per unit time through unit area of a plane at right angles to the direction of diffusion. This flux is proportional to the concentration gradient of the diffusing substance, and the factor D, known as the diffusion coefficient, is introduced as the proportionality factor with dimensions of (length)&apos;/time. If the flux is measured as the increase of thickness of the oxide layer (Ax) per unit time (t) and the assumption is made that the concentrations of the reactants at the phase boundaries of the layer are independent of time, Eq. 1 reduces to Integration of this expression yields the parabolic function ax = k . t. [31 The product of the diffusion coefficient and the concentration difference across the oxide layer is included in the constant k. When iron is exposed to a highly oxidizing atmosphere, the oxide phases are formed normally in a topochemical fashion, i.e., the interfaces between the phases maintain parallel positions to the original surface of the specimen. Above 570°C, the phases are orientated usually in the order of iron, wiistite, magnetite, and hematite, a condition in conformance with the requirements of the Fe-0 system. Below 570°C, the wiistite phase is unstable and has not been found as a normal constituent in the oxidation products of iron. There is a strong probability that continuous layers of the solid oxides are formed as the specific volumes of the phases increase in direct order from iron to hematite.&apos; , &apos; Regarding mass transport through dense solid oxide layers, Wagner&apos; has postulated that diffusion in oxides generally may be interpreted as migration processes of ions and electrons. There must be normally a concentration gradient across the growing oxide layer for diffusion to occur. This condition requires that there be deviations from the ideal stoi-chiometric composition of the oxide and accordingly deviations from the strict order of an ideal lattice. Such "lattice defects" include interstitial ions, cation and anion vacancies, quasi-free electrons, and electron holes and are decisive for all migration processes.&apos; Cations, anions, and electrons all may have some mobility in the oxides but the movement of one of the particles generally far exceeds that of the others. Previous work&apos;, 1,2,7 has shown that during the oxidation of iron the migration through the wiistite layer, and probably also the magnetite layer, is confined to the movement of iron ions. Migration through hematite, however, has been found to take place by oxide ion movement. These behaviors are in direct agreement with the type of vacancies present in the respective oxides. Reduction of Iron Oxides The gaseous reduction of iron oxides, like the oxidation of iron, takes place in a topochemical fashion at distinct interfaces between the appearing phases."-&apos;" Porosities might be expected in these reaction products, since their specific volumes are less than that of the starting material. Frank and van Der Merwe" have shown, however, that it is theoretically possible for nonporous layers to form if the degree of misfit in specific volume is less than about 15 pct. These aspects on porosity formation

Jan 1, 1956

By L. B. Harris

Continuous cyclic unloading during tensile work hardening of polycrystalline zinc at room temperature enables specimens to sustain greatly increased extension. Such enhanced ductility is associated with creep-type extension, during which the cyclic component appears to promote relaxation of internal strains. It is possible to trace the transitions from tension, through enhanced cyclic extension, to fatigue and relate the observed behavior to simpler types of deformation. DISTINCTIVE deformation behavior has been shown to occur when loading includes both cyclic and unidirectional components. For aluminum and copper extended by a sequence of progressively biased strain reversals, coffin1 observed greater fracture ductility and lower flow stresses than during monotonic tension. This may be compared with the reduction in hardness obtained from conventional fatigue softening. But fatigue softening is accompanied by enhanced fatigue life,&apos; whereas Benham3 found that fatigue life was reduced when copper continuously extended during axial load cycling. The corresponding specimen elongation, for large cyclic load amplitudes, was greater than during normal tension. Under different conditions, Bendler and wood4 found that torsional fatigue initiated extension in copper under low tensile loads previously in equilibrium with the specimen; fatigue life was again reduced. Thus there is a type of cyclic softening which is associated with reduced fatigue life and which occurs when the cyclic loading is accompanied by a unidirectional strain component. Further, the fracture ductility or extension obtained from the unidirectional component can exceed that obtained in the absence of cyclic load. Specimen extension was not initiated by axial fatigue at small load amplitudes;3 hence Benham&apos;s work distinguishes between fatigue at large and small amplitudes, the former often being linked with unidirectional deformation because of similarities in strain Structure. The initiation of tensile extension during torsional fatigue,4 however, occurred with small amplitudes. Comparable changes in behavior have been ob- served during creep. kennedy&apos; found that combined cyclic and creep stresses on lead at 32°C increased the rate of elongation over that for simple creep, the consequence being a reduction in creep life. It was also demonstrated that small cyclic stresses applied after creep deformation initially increased recovery, but that prolonged application produced only normal fatigue hardening. It is clear that physical properties can be changed by interaction between the cyclic and unidirectional deformations, but owing to the number of different ways in which the deformations can be combined and the large number of possible variables for each combination, trends of behavior become easily obscured. One definite conclusion is that enhanced ductility or increased extension can be obtained by cyclic action, and it is this process that has been investigated for the tensile test by measurements of the extra tensile strain produced by the addition of a cyclic tensile component. EXPERIMENTAL PROCEDURE Material. Specimens were 99.99 pct Zn wire of 1.6 and 2.0 mm diam. Mean grain diameter was 0.02 mm, sufficiently small to give a ductile necked-down fracture under all loading conditions. All experiments were conducted at an average temperature of 20°C. Normal Tension. Unidirectional tensile curves at different strain rates were obtained from an In-stron testing machine, on which load-time curves were recorded autographically, using gage lengths of 5 and 10 cm. Straining was at constant cross-head velocity, and quoted strain rates are with reference to initial specimen length. Measurements of total elongation under simple tension were also made on the tensile machine that had been modified to incorporate an added fluctuating load. Combined Tension and Rapid Cyclic Load. An electromagnetic vibrator was coupled to the elastic beam of a Hounsfield ensometer- and driven sinus-oidally from a power amplifier at frequencies from 20 to 360 cps, the flexible connecting links on the tensometer being replaced by rigid fixtures to eliminate lateral vibration in the specimen. One end of the specimen was pulled by the normal extension drive of the tensometer while the other end, fixed to the elastic beam and vibrator, was subjected to rapid oscillations of load. It was thus possible to apply cyclic load to a tensile test without altering the rate of extension of the specimen

Jan 1, 1964

By E. R. Buchanan, R. E. Reed-Hill

Cylindrical magnesium single crystals were deformed in torsion. The axis of torsion was the basal pole. Five crystals were deformed to different strains between 0.08 and 1.03 and then sectioned in order to determine their dislocation densities using the transmission electron microscope. The work hardening rate of all specimens was at least an order of magnitude higher than that normally associated with easy glide in a tension test and comparable to that obserzed in stage B of a tension test. The correspondence between stage B in a tension test and the initial stages of a torsion test is believed to result from the fact that in both cases deformation occurs in a structure containing roughly equivalent densities of the dislocations associated with the three basal slip vectors. THERE are three basic ways of changing the shape of a crystal using slip dislocations. The crystal can be sheared along a slip direction in a slip plane; it can be bent about an axis in the slip plane normal to the slip direction; and, if the slip plane contains multiple slip directions, it can be twisted or rotated about the slip plane normal. Of the three processes, generally known as translational, flexural, and rotational slip, only rotational slip has not been extensively investigated. The object of the present research was to obtain basic information about this phase of crystalline plasticity. This paper is concerned with some aspects of the stress-strain curves obtained by twisting magnesium crystals about their basal poles. Magnesium was selected for four reasons. One, its recovery rate at room temperature is relatively low. Two, single crystals may be easily grown. Three, at room temperature the critical resolved shear stress for basal slip is about two orders of magnitude lower than that for nonbasal slip, so that rotational slip might be expected to occur primarily by basal slip. Finally, relationships between flow stress, shear strain, and dislocation density have been determined for tensile deformation of magnesium crystals,&apos; thereby providing a basis of comparison for the torsional results. EXPERIMENTAL PROCEDURES Crystals were grown from 0.5 in. diam extruded sublimed magnesium rod furnished by the Dow Chemical Co. who reported that it contained in weight percent less than 0.0003 Al, 0.01 Ca, 0.01 Cu, 0.0012 Fe, 0.001 Mn, 0.0005 Ni, 0.003 Pb, 0.001 Si, 0.01 Sn, and 0.02 Zn, with the balance magnesium. All crystals were grown in a dried argon atmosphere using Jill-son&apos;s2 modified Bridgman technique. Two different methods were used to obtain crystals with the basal plane normal to the specimen axis. These included direct growth from seeds of the proper orientation, and spark machining (trepanning) of 0.5 in. diam cylinders from larger (1.5 in. diam) randomly grown crystals. The crystals thus produced were polished in a 20 pct HC1 water solution and then etched in a 1 pct HC1 water solution to develop etch pits lying in rows parallel to the basal plane trace. The crystals were then revolved about their axes on the stage of a low-powered microscope. Torsion specimens were prepared only from those crystals whose axes were normal to the rows of etch pits. It is estimated that this simple orientation method was accurate to about 51 deg. 1.625 in. long cylinders were next cut from these selected crystals and then acid machined in a 20 pct HC1 water solution into torsion specimens with a 1 in. long by 0.30 in. diam reduced gage section. Following this, they were annealed in air at 400°C and furnace cooled to room temperature. The specimens were given a final polish in a 10 pct HC1 water solution, rinsed in ethanol, dried, and cemented into brass grips with an epoxy resin. In addition to the torsion specimens, several tensile specimens with their basal planes at 45 deg to the stress axis were also prepared with similar dimensions except that the gage sections were increased to 4 in. in length. The torsion specimens were tested in the apparatus

Jan 1, 1970