By T. lkeda, R. S. Montgomery. A. Hara

Actual test specimens used in the previous laboratory wear investigation,' were fully characterized and the data is given in Table 1. Most of the carbides tested could be placed into groups of similar mean grain size. When the wear rates of the members of these groups were plotted as functions of their hardnesses, a family of curves resulted; curves for groups containing data from larger grained composites were at lower wear rates at the same hardnesses. Most specimens tested showed only A-1 porosity (ASTM Standard designa-

Jan 1, 1971

By J. J. Crowe, G. K. Burgess

PAGE, Theories of Allotropy of Iron........... 667 Previous Determinations of A2 and A3 in Iron........ 668 Critical Ranges as Determined by Expansion........ 669 Critical Ranges by Thermoelectric Observations........ Critical Ranges in Terms of Crystalline Structure....... 670 Critical Ranges as Detected by Mechanical Methods...... 670 Critical Ranges as Given by Electrical Resistance....... 670 Critical Ranges as Determined Magnetically........ 671 Critical Ranges as Determined Calorimetrically....... 673 Critical Ranges from Heating and Cooling Curves....... 673 Summary of Previous Determinations of A3 and A2 in Pure Iron.... 675 The Present Investigation............ 678 The Experimental Method........... 678 Arrangement of the Apparatus.......... 679 The Measurements of Temperaturc.......... 679 The Measurement of Time........... 679 The Thermocouples............ 681 Temperature Scale and Calibration of Thermocouples...... 681 Mounting of Thermocouples........... 682 The Differential Measurements.......... 682 The Furnace and Accessories........... 682 The Vacuum Pump............ 683 The Energy Supply............683 The Rheostat.............. 683 The Materials Investigated............ 685 Sources of Iron............. 685 Preparation and Description of Samples......... 685 Chemical Analyses............. 687 The Experimental Data............. 688 The Preliminary Observations.......... 688 The Definite Series............691 Description of the Plotted Curves........... 694 The Effect of Plotting at Different Intervals........ 694 The Curves of the Definite Series.......... 695 . The Curves of the Preliminary Series......... The Existence of Other Critical Ranges......... 696 The Microscopical Examination........... 697 Summary and Conclusions............ 698 Bibliography............... 701 Plates................ 704

Jan 1, 1914

By E. P. Haqyes, J. K. Butler

011, and gas development has continued unabated on the Texas Gulf Coast during 1937. Although the number of important new discoveries has not been great, the extensions in older fields, owing to discovery of new sands and the lateral extension of known sands, has been extensive. Twenty-four new producing fields were added during the year, and many of these areas give promise of developing into important producing districts in the future. Alta Mesa, Amelia, Aransas, Clara Driscoll, Five Corners, Hamman, Heyser, Old Ocean, Premont, Seabreeae, Segno and West Columbia have all had major extensions during 1937. The 1937 production for the Texas Gulf Coast was 120,141,429 bbl., or 32f per cent increase over the 1936 production of 90,865,293 bb1. t The total number of producing wells has increased from 6727 to 8968. Well abandonments have becn few and indications are that they will continue to be so. Rigid proration has been and continues to be in effect, and, as a result, wells in the Gulf Coast will have prolonged life. New Fields Tables 1 and 2 contain general information on all fields in this district. The following named fields were discovered in 1937: Aransas County.—Barnsdall Oil Company's No. 1-A Edwards was the discovery well for the Lamar field. It was drilled to a total depth of 9785 ft., plugged back and completed at 7530 ft. in the Frio as a gas and distillate well. Present indications are not very promising for a major field. Bee County.—The McMurray (Strauch) field was discovered by Dirks Bros. No. 1 Strauch at a total depth of 4577 ft. This is a Yegua producer, and had an initial production of 230 bbl. on a 3/16-in. choke. Brazoria County.—The Sandy Point field was discovered by Henry DeArmanls No. 1 Fite, which was completed as a producer at 6501 ft. in the Marginulina-Frio series. Galveston County.—Although the Hitchcock field was discovered in 1936, the first commercial oil producer was completed in 1937 when

Jan 1, 1938

The total estimated production of coal in the United States during the first century and a quarter of mining is shown in Table 20. This is the total of the production of the various states already shown in the various tables, and is believed to be the first statement of this sort made. No such table prepared from limited data can be accurate, but it is the writer's opinion that the totals shown are less than those actually produced. It was thought that this study would enable a reasonably accurate account of the movement of coal down the Ohio and Mississippi Rivers to be written. The searches made have shown that at this time the data do not exist from which such a study can be made, but some of the facts collected may be useful to future students.

Jan 1, 1942

By D. Walton

The effect of small solute additions of Cu on the activation energies for creep A1 single crystals were determined over the range from 78° to 850° K. Below 240°K and above 800°K activation energies were unchanged. Between 240°K and 400°K strain aging causes the creep rate to become vanishingly small and the flow stress was independent of the temperature. Between 500° and 50°K the activation energy was increased to 41,000 cal per mole. NUMEROUS investigationsL have shown that solid solution alloying invariably increases the flow stress. A typical example is documented in Fig. 1. Such increases in flow stress can arise from two general effects: Alloying can increase the long-range stress fields through which dislocations must move by causing appropriate clustering; modification of dislocation densities, and so forth. Alloying can also modify the short-range stress fields that determine the activation energies for thermally stimulated migration of dislocations, such as occurs in some solute atom pinning processes, and so forth. Actually both long- and short-range stress-field effects can occur simultaneously. It was the purpose of this investigation to evaluate the effect of alloying on the short-range stress fields by determining the effect of alloying on the activation energies for creep. The resulting observations also shed some light on the effect of long-range stress fields on dislocation processes. EXPERIMENTAL TECHNIQUE Single-crystal bars (6 in. long 3/8 in. wide and l/4 in. thick) of dilute solutions of Cu in A1 were seeded, so as to provide extensive single slip, with the pole of the tensile axis located in the standard stereographic projection as shown in Fig. 2. Each crystal was grown under an argon atmosphere in a graphite mold containing a large reservoir of molten alloy for the purpose of obtaining rather uniform composition of Cu along the length of the bar. The nominal compositions of the alloys which were produced from 99.99 pct Cu and high-purity A1 containing 0.001 pct Fe and 0.001 pct Si, are given in Table I. Strains, measured by linear variable transformers attached by quartz rods to a 3 in. gage section were sensitive to and the stresses were ap- plied by direct loading of the specimen. Temperatures were determined by thermocouples attached to the gage section of the specimens. Below 400°K the apparent activation energies for creep, Q, were determined by the effect of small, rapid changes in temperature of about + 10°K from T1 to T2 on the corresponding creep rates ?1 and ?2 during primary creep according to where R is the gas constant.' Above 400°K, Q was evaluated from Eq. [1] for the secondary creep rate using temperature changes of about ±20K. A typical set of results is shown in Fig. 3. RESULTS AND DISCUSSION The previously obtained effect of temperature on the apparent activation energy for creep of single crystals of high-purity A12 is shown by the broken curve of Fig. 4. The datum points on the same graph illustrate the effect of dilute a solid solution alloying with Cu on the activation energy between 600" and 750°K. Each plotted point is the average of not less than five independent test values between 600° and 750°K and not less than three at other tempera-

Jan 1, 1962

By Leonard Logan

Production control in the petroleum industry may be discussed under three general heads: engineering, legal, and economic. Though the problems that fall under the respective heads of engineering, law, and economics are separate, they are dependent and interrelated. The present study will deal with the economic phases of production control and only incidentally with the legal phases as they affect the economics of the problem. No one of these forms of control is more important than the others. The engineers have performed their service well, and although there are many problems of engineering control yet to be solved, they are not pressing. Legal control is a problem for the legislatures and the courts to solve. The petroleum industry is such a comparatively young industry and the legal problems are of such recent origin that the courts have not yet been called on to settle all the issues and the legislatures still have before them bills concerned with the regulation of the industry. Economic control of production in the petroleum industry is a highly desirable goal but it has not yet been completely achieved. Since the first commercial well was drilled in 1859, there have been recurring periods of overproduction. (Over- production will be used here to describe a condition wherein so much crude oil is available that a satisfactory and reasonable price is not received for the product.) The production of oil in 1859 approximated only 2000 barrels. In the following year production jumped to 500,000 barrels, thus bringing into

Jan 1, 1932

By Pradeep K. Rohatgi, Clyde M. Adams

Structures produced upon solidification of the eu-tectic composition (33 wt pct Cu) aluminum copper alloy have been examined as a function of freezing rate dfs /d? , the rate of change of fraction solid (fs) with time (8). Slow (dfs/d? = 0.0016 sec-1), intermediate (dfs/d? = 0.02 sec-1) and rapid (dfs/d? = 0.4 to 7.30 sec-1) freezing rates were used. The lamellar Al-Cual2 eutectic is arranged in the form of rod-shaped colonies at rapid freezing rates. The colonies are aligned parallel to the direction of heat flow, whereas the lamellae within the colonies are aligned at various angles, as high as 90 deg, to the direction of heat flow. The colony spacing (C) is proportional to the square root of inverse freezihg rate. The relationship is C = 15.5(dfs/d?)-1/2 where C is in µ and 8 is in sec. The ratio of colony spacing to lamellar spacing is greater than 20.0 and increases with a decrease in the freezing rate. A duplex dendritic structure is produced at intermediate freezing rates. A fine lamellar eutectic is arranged within the dendrites (exhibiting side branches at an angle close to 60 deg from the main stem) and a coarse irregular eutectic appears in the interdendritic regions. The duplex eutectic structure is also produced at slow freezing rates. However, at slow freezing rates there is a Platelat of CuAl2, along the center of the main stem of each dendrite and the other lamellae are arranged perpendicular to the central platelet. THE eutectic between CuA12 and a! aluminum has been reported to freeze in a lamellar form by several workers.'-3 chadwick4 has measured the interlamel-lar spacing as a function of growth rate. Kraft and Albright2 have reported on irregularities in the lamellar structures, and have proposed growth models which account for the formation of faults during solidification. In certain instances the lamellar eutectic has been found to exist in colonies. The colony formation315 has been attributed to the breakdown of a planar liquid-solid interface due to rejection of impurities. The aim of the present work is to study the structures produced from the eutectic aluminum-copper alloy under relatively fast solidification rates, such as encountered in casting and welding operations. The solid-liquid interface presumably remains planar under conditions of slow unidirectional freezing which produce lamellae aligned parallel to the direction of heat flow. The local growth velocities are the same over the entire interface and are equal to the rate of growth of the all-solid region. The spacing between the eutectic lamellae is inversely proportional to the square root of the growth rate of the all-solid region. Under the freezing conditions used in the present study, the solid-liquid interface is cellular or dendritic and the local growth velocities are different in the different regions of the interface. The relationship between the growth rate of the all solid region and the local growth velocities varies with the location and the shape of the interface. The growth rate of the all-solid region is, therefore, an inadequate parameter to describe the eutectic micro-structures which depend upon the local growth velocities. For this reason the structures have been examined as a function of freezing rate, dfs/d?, where fs is the fraction solidified at time 0. The freezing rate was varied by a factor of 4000. The relationship between the freezing rate, dfs/d?, and the growth velocit of the all solid region depends upon the specimen geometry and the shape of the interface. EXPERIMENTAL PROCEDURES The A1-33 pct Cu alloy used throughout this study was made in an induction furnace, using electrolytic copper and aluminum of commercial purity (99.7 pct), the primary impurities being silicon (0.12 pct), iron (0.14 pct), and zinc (0.02 pct). Three ranges of freezing rates were investigated: 1) A spectrum of rapid freezing rates (ranging from 0.40 to 7.30 sec-1) was obtained in arc deposits made on 2-in. thick cast plates of the eutectic alloy. The arc was operated at constant power and was made to travel at constant velocity on the surface of the plate that was in contact with the chill surface during solidification. The pool of liquid metal formed under the moving tungsten arc solidified rapidly by heat extraction through the unmelted plate. Conditions of unidirectional heat flow were achieved near the fusion zone interface, especially in the center of the arc deposits. The great advantage of the arc technique is that rapid cooling and freezing rates can be varied in a qualitative way. The correlation between the arc parameters and the solidification rate is given by the following relationship:6-8

Jan 1, 1970

By H. F. Easter

(San Francisco Meeting, September, 1915) THE lead department of the El Paso Smelting Works at El Paso, Tex., is operated strictly oil a custom basis. The ores treated are drawn from the surrounding territory, comprising New Mexico, Arizona, western Texas, and northern Mexico. Ores received from the last-named section originally amounted to a very large tonnage, but of recent years have dwindled into comparative insignificance so far as this plant is concerned. This has been clue partly to the establishment of a lead-smelting plant at Chihuahua, which is much closer than El Paso to most of the important mines, and partly to the recent revolutionary troubles in Mexico. There are no mines of either lead or copper in the immediate vicinity of El Paso. In general, it may be said that the lead-ore supply of recent years has been uncertain and precarious, with a general tendency toward an excess of silica and a shortage of iron. This latter requirement has been met in large part by the use in El Paso lead furnaces of considerable amounts of roasted heady copper matte from the Chihuahua smeltery and of converter slag from the El Paso converters. These two materials, coupled with complex lead-copper ores from Bisbee, Ariz., have introduced into the lead-smelting operations a most unusual amount of copper, which has had an important bearing upon the smelting practice of the plant. This matter will be discussed later. The ore, loaded in either box cars or gondolas, enters the storage yard on four tracks elevated about 8 ft. above the ground. As all unloading is clone by hand, unloading platforms at the height of the car floor parallel the tracks on each side to afford a runway for wheelbarrows. At frequent intervals these lengthwise platforms are joined together by others running crosswise to facilitate the distribution of the ores evenly over the beds, which are located below and between the tracks. At present much of the bedding space formerly used for lead ores is given over to the copper department, but 20 bins of various sizes are retained for the use of the lead furnaces and the Huntington & Heberlein roasting plant. The largest of these holds about 1,000 tons, while the smallest holds not over

Jan 8, 1915

By P. van Meurs, C. van der Poel

From observations of the linear displacement of oil by water from a porous medium as visualized in transparent models, new insight into the mechanism of vircous fingering, as occurring in the case of unfavorable oil-water viscosity ratios, has been obtained. A mathematical description of the observed phenomena leads to formulas. expressing both oil production and pressure drop across the formation as a func-tion of cumulative water injection with the oil-water viscosity ratio as a parameter. Theoretical results are compared with those obtained from scaled laboratory experiments in sand-filled rubes in which water was injected at the one end and production was obtained from the other end. In the second part of the paper the same principles are used to calculate a more realistic production scheme in which production of oil and water is obtained from wells regularly distributed over the field. Results show satisfactory agreement with production data of an actual oil field. Application of the theory is extremely simple as only a limited number of readily available parameters have to be known and results are presented in an analytical form. INTRODUCTION When oil is displaced from a porous medium by water having a viscosity lower than the oil. the oil-water interface is essentially unstable and has the tendency to break up into what are called "fingers" or "streamers". This Viscous fingering has been noted before by Engelberts and Klinkenberg' and has recently been demonstrated in transparent models by van Meurs-. It is highly questionable whether it is at all possible to perform relative permeability measurements In the laboratory reproducing the same distribution of water and oil in the cores as Present in practice. Therefore, we based our descriptive theory on an idealized model which was "tailored" to the fingering mechanism as observed in transparent models under scaled conditions. This approach was the more attractive, as a highly simplified model had already yielded an adequate description of the process. Though we are aware our theoretical approach can be extended in several ways, it is given here in its simplest form to explain the fundamental principles and to avoid complicated formulas. SIMPLEST CASE OF A LINEAR DRIVE Observations and Theoretical Model In Fig. 1 a series of photographs shows how water penetrates into a formation saturated with an oil which is considerably more viscous than the water. The technique for obtaining these photographs, using transparent models, has already been described?. The fingers can be clearly observed and are seen to be mainly parallel to the flow direction. Note that the contours of these fingers are not smooth but show protrusions of water enclosing oil pockets.

By Philip S. Morse

THE Australian lead-smelting plants began to use charges carrying high zinc percentages somewhat earlier than was common with American plants. When lead smelting first started in Australia the immense deposits of oxidized lead at Broken Hill were available but later these oxidized ores became exhausted and were replaced by sulfides. This was before the days of flotation and these sulfides when concentrated carried about 1 per cent. of zinc to 6 per cent. of lead. The works of the Sulphide Corpn. at Cockle Creek was perhaps the pioneer in high-zinc slags but the Port Pirie plant of the Proprietary Co. was a close and very able second and has continued the work to the present time. The Cockle Creek lead furnaces remained in operation until shortly after the war when most of the Broken Hill companies combined and took over the Port Pirie plant to treat their concentrates. As it was the practice both at Cockle Creek and Port Pirie to carry 20 per cent. or more of lead on the charge, it was found that under these conditions of large amounts of zinc in the charge, good roasting was absolutely necessary and matte production was unwise. The Hunting-ton-Heberlein system of roasting was introduced and later the Dwight & Lloyd process. In this way, by roasting the sulfide portions of the charge as thoroughly as possible and making no matte, a method of smelting was developed where the slag over long periods carried as high as 20 per cent. ZnO without serious furnace troubles, and slags carrying even up to 33 per cent. ZnO have been reported. The zinc slags were not very different in appearance from the ordinary slags produced in American practice except that they gave off more smoke and fume on tapping. The slag usually ran hot and freely, coming from the tap in a full stream. Normally there was little crust on the sides of the furnace and the tuyeres gave no trouble though they were always rather dark. At the works of the Sulphide Corpn. it was the custom, on account of the labor situation, to shut down the furnaces during the Christmas holidays, thus giving a campaign of about 12 months. The furnaces at the end of the run usually showed no crust on the sides, though crusts always occurred at the back and front ends. A furnace campaign of 22 to 23 months has been made at this plant where both sides of the

Jan 1, 1929

By R. C. Wilmoth, R. D. Hill, R. B. Scott

A cost breakdown is given for reclamation and mine drainage abatement conducted by the Federal Water Quality Administration's demonstration project near Elkins, W. Va. Costs for construction of control measures have been developed and include backfilling strip mines, sealing subsidence areas, reconstructing stream channels, and installing mine seals to prevent the entrance of water and air.

Jan 1, 1973

By Paul R. La Pointe

GEOTECHNICAL OBJECTIVES OF UCG PROGRAM Underground coal gasification (UCG) is one of several in situ extraction technologies for utilizing deep, otherwise unmineable coal. This technology involves the injection of air or oxygen into the target coal seam, ignition of the coal and recovery of product gases. Geotechnical characteristics of the coal and enclosing rock strata strongly influence the success of this Process. The flame front follows the coal cleats (Hill, 1979), and cleating and bedding control the manner in which coal collapses into the cavity, thereby affecting recovery efficiency (Ramirez and others, 1982). Moreover, coal seams typically behave as fracture dominated aquifers in which cleat orientations govern subsequent contaminant dispersal. For these reasons, the Anaconda Minerals Co. undertook a detailed study of fracturing within the Wyodak-Anderson Coal in the eastern Powder River Basin (PRB) near its Rocky Hill UCG test site (Fig. 1). STRESS HISTORY AND FRACTURING IN THE POWDER RIVER BASIN Vertical jointing, or cleating, in coals may arise from shrinkage shortly after deposition under low confining pressures, or later in time, soon after burial but after the coalification process is well advanced (Ting, 1977). There is much evidence to support the formation of cleating after coalification (e.g. Hawkes and Mellor, 1970; McCulloch and others, 1974), which suggests that the stress state existing at that time strongly influences cleat formation. McCulloch and others (1974) argue that the typically better developed face cleat forms parallel to the plane containing [ol] and [o2]. Where the relation between cleats and stess has been studied (McCulloch and others, 1974; Stone and Snoeberger, 1977; Ward, 1977; Kulander and Dean, 1978), the highly systematic face cleat strongly parallels the [o1] direction. Stone and Snoeberger (1977) report face and butt cleat measurements of N70E and N29W for the Felix Coals 220 m stratigraphically above the Wyodak at the Hoe Creek UCG site (Fig. 1). Structural trends also indicate the past state of stress in the PRB. Glaze and Keller (1963) suggest that the NE-SW regional compression during the late Permian formed major N-S fold lines and basement magnetic anomalies. Mapel (1959) describes folds having N60W and N30W rends in the northern PRB, as well as a large normal fault trending northeast. Glass (1976) also describes normal faults trending northeast. Similarly, Olive (1957) mapped normal faults

Jan 1, 1984

By L. B. Underwood, C. J. Distefano

NORAD, when completed, will be housed in large chambers excavated out of the granite beneath the Cheyenne Mountain near Colorado Springs. A room and pillar layout for the chamber excavation was selected and executed. Many complex problems arose in designing a rock bolt system; this paper includes discussions on: rock strengthening following excavation, excavation and ground support problems, orienting rock bolts with respect to jointing systems, conducting pull tests, four-way chamber intersection problems, the need for grouting rock bolts, and loss of tension and permanency of anchorage in a rock bolt system. In the event of a sudden nuclear attack upon the United States, it is imperative that vital command and control centers have a high probability of survival. One such vital facility is the North American Air Defense Command Combat Operations Center at Colorado Springs, Colo. Known briefly as NORAD, this installation when completed will be housed in large chambers excavated out of granite beneath the eastern slope of Cheyenne Mountain (Fig. 1). The NORAD COC, a U.S. Air Force sponsored project, will serve as the primary collection and evaluation center for data concerning unknown aircraft, missiles, or space vehicles, which might bring destruction to North America. The data will be fed into high-speed computers and electronic equipment from outpost sources: radar, ballistic missile early warning stations and picket ships throughout the world. Electronically controlled display boards will make it possible to evaluate the tracking data instantaneously and to take appropriate defensive action.'

Jan 1, 1968

By F. W. Schaller

TETRAGONALITY is an important aspect of the models of transformation, strengthening, and tempering of ferrous martensite. When the c/a

Jan 1, 1963

By H. David Swain

On Bougainville Island in Papua New Guinea, Bougainville Copper Ltd. (BCL) has successfully applied electronic data processing (EDP) techniques to pit operations and mine planning. Though the EDP program is not complete, BCL has realized significant improvements in short and long range mine planning, and equipment and manpower utilization. About 80% of BCL's 4000 employees are Papua New Guinea nationals, and most have little education or training. The operational characteristics of the computer equipment, however, have been quickly adapted by users with low educational standards.

Jan 3, 1979

INTRODUCTION In the preceding chapters we have discussed the various elements of mineral economic analysis, their interrelationships, and the most accepted and advanced techniques by which these elements are manipulated to provide the decision maker quantitative measurements for judging alternate investment opportunities. Regardless of how carefully the economic evaluation is made, and how comprehensive the study of economic parameters has been, uncertainty still remains a significant factor in the outcome of the analysis. The investor or money manager is acutely aware of the uncertainty factor. Many of the economic parameters are functions of economic forecasts and value estimates that can- not be known with any degree of certainty. The postulated DCF-ROR is based upon certain estimates representing "best guess" values, and a single point parameter DCF-ROR analysis represents a combination of "best guesses." The wise decision maker looks at such an analysis and asks the "what if" questions. What if the production cost is 10% higher than the estimate? What if there is an overrun in construction costs? What if the mineral price falls lower than expected? What will be the effect of a higher royalty rate? Many more such questions may arise in trying to assess the total risk involved in funding a mineral project. Prior to the advent of the computer it was difficult to answer all such anticipated questions because of the many laborious calculations involved. Now, with the aid of the computer, most of these questions can be answered by the analyst at the same time the original computations are made by using the process of sensitivity analysis. Sensitivity analysis shows the effect of critical parameter changes upon the DCF-ROR or other profitability measure. When probability of occurrence can be associated with the various parameter value levels, sensitivity analysis becomes probabilistic analysis, and the risk factor can be quantitized in terms of total probability. SENSITIVITY ANALYSIS The determination of the sensitivity of the profitability index (usually the DCF-ROR) to changes in the various economic parameters, taking them one at a time, is called sensitivity analysis. The analysis may be performed for any number of parameters involved in the DCF-ROR computation. Generally, in mineral evaluations the most sensitive and most tested parameters are: the metal or mineral price, the operating cost, the annual production grade, and the initial capital invest-

Jan 1, 1980

By E. O. Fromm, R. I. Jaffee, R. M. Evans

IN connection with a research on gallium alloys, a method for the thermal analysis of very low melting alloys was developed, which appeared to be worthy of more than passing interest. As used, the method was suitable for work in the temperature range, — 72° to 250°C. However, with suitable adjustment, the method could be adapted for use over broader temperature ranges. The Rosenhain temperature gradient furnace,' adapted for low-temperature use, was the basis for the method. The gradient was set up in a stainless steel tube. The specimens were lowered through it at a constant rate while time-temperature or inverse rate data were taken. It was essential to maintain careful control of the top and bottom temperatures of the gradient. Also essential was good heat transfer from the walls to the specimen. This was accomplished by a liquid heat-transfer medium.

Jan 1, 1953

By R. F. Lynch, J. D. Wood

The Al-1.0 pct Mg alloy 565 7 was studied using optical microscopy and electron microprobe X-ray analysis. Constituent particles were found to exist inter-dendritically in the as-cast material in a region of precipitate free a -aluminum. Five phases besides a fine precipitate and a-Al were identified in the cast structure: Fel3, Fe2Al7, Mg2Al3, CUMgAl2, and Cu2FeAl7. Thermal treatments conducted for 100 hr at 1180°, 1130°, 1080°, 1030°, 980°, and 880° F revealed a general dissolution and spheroidization of the in-terdendritic constituent network observed in the cast structure. The principal constituents present in the thermally treated structures were FeAl3 and Fe2Al7 with the relative amount of Fe2A17 to FeAl3 increasing with a decrease in the treatment temperature. The phases Present in the wrought structure were identical to those observed after the thermal treatments, with the constituent particles strung out in the direction of rolling. ALLOY 5657 is a nonheat-treatable commercial purity Al-1.0 pct Mg alloy utilized extensively because of its bright finishing characteristics. This investigation was conducted to determine the constituents present in 5657 alloy, and to study the effect of extended thermal treatments on morphology. Numerous studies have been carried out to establish the equilibrium diagrams for various aluminum systems,1-3 with phase identification based on X-ray analysis, morphology, and the etching response of relatively large particles. Phragmen4 conducted a study of the phases in aluminum eutectic systems and compiled a "corrected" table of etching responses, drawing on his work plus that of Schrader,5 Keller and Wilcox,6 and Mondolfo.7 A review of the original work of Keller and Wilcox, and Mondolfo, which was concerned with the constituents found in commercial alloys, reveals that in numerous cases their etching responses differ from those reported by Phragmen and from each other. These inconsistencies may occur because a specific constituent will react to a given etch in a varying manner depending upon its size, the elements dissolved in the phase, the other constituents surrounding a phase, and the solute content of the matrix. Work with a commercial orientation was conducted on alloys 2024 and 3003 by Sperry8,9 and on alloy 3003 by Barker,10 where the relationship between the phase diagram and the nonequilibrium structure of an alloy was examined. Backerud11 investigated the A1-Fe binary system and found that at high cooling rates the equilibrium eutectic reaction forming a-A1 and FeA13 is replaced by another lower temperature eutectic reaction forming a-A1 and metastable FeAl6, a constituent first identified by Hollingsworth et al.12 Most of the above mentioned studies were conducted on materials having a significantly greater alloy content than 5657 alloy, where the relatively small size and sparse distribution of second phase particles hinders the process of identifying constituents. EXPERIMENTAL PROCEDURE Material with a composition as given in Table I was examined in the as-direct chill cast, hot rolled and cold rolled conditions, and after thermal treatment of the cast structure. Thermal treatments were terminated by a water quench. Microscopic examination was conducted under various lighting conditions following the application of standard etchants as specified in Table 11. A semi-quantitative electron microprobe X-ray analysis was conducted for Al, Mg, Fe, Cu, Si, Zn, and Ti. RESULTS AND DISCUSSION Microstructure of the As-Cast Material. Particles of second phase material were found to exist inter-dendritically, principally in regions of precipitate free a-Al, as illustrated in Fig. 1. Adjacent to the ingot edge was a region of inverse segregation, resulting in an increased amount of second phase material containing large sized particles which aided in phase identification. Phase Identification. Cast Structure. Five phases besides a-Al and a fine precipitate were identified using optical microscopy and electron microprobe X-ray analysis, as presented in Tables II and III, respectively. FeA13 and Fe2A17 are often found with Fe2A17 forming a sheath around the core of FeAl3, resulting from an incomplete peritectoid reaction. These phases have a nearly identical appearance under white light, although they are easily differentiated under crossed polarizers, as characteristically illustrated in Figs. 2(a) and 2(b), respectively. Microprobe analysis con-

Jan 1, 1970

By J. D. Shaw, E. B. Gebert, D. O. Noel

It is, of course, expected that manufacture of the various metal powders should involve numerous methods adapted to the specific characteristics of the metals themselves. Several methods for powdering a particular metal may be available, but the physical characteristics of the powder as produced by the several methods may be quite different. In the final analysis, the application of the metal powder dictates the physical properties that the metal powder must possess, and this, to a very large extent, will determine which of several possible methods of manufacture is adopted. Sometimes powder of the same metal is produced by more than one method, each powder having specific characteristics that make it particularly suitable for its application. For purposes of classification, the various methods of powdering metals can be grouped as follows: 1. Machining. 2. Milling (by ball mills, stamps, attrition mills, etc.). 3. Shotting (pouring molten metal into water, air, etc.). 4. Granulation (by stirring molten metal while solidifying). 5. Atomizing (disintegrating by steam, compressed air, etc.). 6. Condensation of metal vapor. 7. Reduction of oxide powders. 8. Chemical precipitation. 9. Electrolytic deposition. 10. Sintering (for producing alloy powders). 11. Formation of an alloy followed by dissolving or otherwise removing one of the alloying constituents. Machining Turnings, cuttings, filings, etc., are, of course, produced as by-products in machine work of various kinds, and find certain applications as metal powders. For example, iron powder so produced is used extensively as a reducing or precipitating agent and as a constituent in certain hard-finish cements.

Jan 1, 1938

By D. O. Noel, E. B. Gebert, J. D. Shaw

IT. is, of course, expected that manufacture of the various metal powders should involve numerous methods adapted to the specific characteristics of the metals themselves. Several methods for powdering a particular metal may be available, but the physical characteristics of the powder as produced by the several methods may be quite different. In the final analysis, the application of the metal powder dictates the physical properties that the metal powder must possess, and this, to a very large extent, will determine which of several possible methods of. manufacture is adopted. Sometimes powder of the same metal is produced by more than one method, each powder having specific characteristics .that make it particularly suitable for its application. For purposes of classification, the various methods of powdering metals can be grouped as follows: 1. Machining. 2. Milling (by ball mills, stamps, attrition mills, etc.). 3. Shotting (pouring molten metal into water, air, etc.). 4. Granulation (by stirring molten metal while solidifying). 5. Atomizing (disintegrating by steam, compressed air, etc.). 6. Condensation of metal vapor. 7. Reduction of oxide powders. 8. Chemical precipitation. 9. Electrolytic deposition. 10. Sintering (for producing alloy powders). 11. Formation of an alloy followed by dissolving or otherwise removing one of the alloying constituents. MACHINING Turnings, cuttings, filings, etc., are, of course, produced as by-products in machine work of various kinds, and find certain applications as metal powders. For example, iron powder so produced is used extensively as a reducing or precipitating agent and as a constituent in certain hard-finish cements.

Jan 1, 1938