By Tsuyoshi Miyashita

Onahama Refinery of Ryoho Recycle Company employs the electrothermic process for producing marketable zinc oxide from steelmaking dusts. The process comprises washing, filtration, drying, sintering and furnacing. Fume from the sinter machine is treated hydrometallurgically to recover zinc, cadmium and lead.

Jan 1, 1976

By J. H. Canterford

The adsorption of uranium onto Wyoming bentonite was measured in carbonate media over the pH range 8 to 11. Uranium was removed from solution onto the solids by a rapid reaction, proposed to be adsorption of the anionic uranyl tricarbonato complex onto edges of the clay platelets, and a slow reaction that may be precipitation of a hydroxide. The changes in uranium content of the aqueous and solid phases of a uranium ore carbonate leach slurry were also measured as the slurry was progressively diluted. There was an increase in the uranium content of the solids as the pH of the suspension was lowered, as observed with the Wyoming bentonite. Results indicate the conditions that should be met with respect to pH control to prevent the problem of excessive uranium adsorption in the counter-current decantation washing circuit of a conventional leaching process, as well as in the leaching and restoration phases of carbonate solution mining.

Jan 1, 1985

By R. E. Steiner, A. F. Weinberg, R. J. Van Thyne

Uranium solubility in molten bismuth was determined in the temperature range 350" to 600°C, varying from 0.09 wt pct to near 2 wl pct, respectively. Zirconium and magnesium, simulated fission products, and sodium were found to increase or decrease uranium solubility in bismuth in the temperature range 370° to 420°C, depending upon the addition or temperature. Data were obtained by both chemical analysis of samples obtained by filtration from saturated melts and by measurement of the variation of electrical resistance with temperature. IN a study for the United States Atomic Energy Commission, a Liquid Metal Fuel Reactor Experiment (LMFRE) was proposed in which a solution of uranium dissolved in molten bismuth served as both the fuel solution and the primary coolant. It was proven necessary to add other elements to this solution for certain desirable properties: 1) zirconium acts to prevent reaction of the fuel solution with the graphite core (which would result in the formation of uranium carbide) and also to inhibit mass transfer of iron and chromium from the walls of the reactor tubing to cold spots resulting in blockage; and 2) magnesium acts as a deoxidant and prevents loss of uranium. In addition to these intentional additives, other elements entering the solution are: 1) fission products which are a by-productof reactor operation, 2) sodium (the secondary coolant) through possible small leaks in the heat exchange system, and 3) iron and chromium from the container walls. Each of these elements may affect the solubility of uranium in the fuel solution. Since the concept of this reactor is based upon a liquid solution, the relatively low solubility of uranium in bismuth will dictate the minimum temperature at which the reactor heat exchanger can be operated. The solubility of uranium in liquid bismuth and the effect of some additives on this solubility have pre- viously been investigated1-' (more recent results6" became avaliable after initiation of this investigation). However, some discrepancies between the various results have been noted, and also the cumulative effect of the several additions or impurities was not known. This investigation was commenced to obtain definitive results. MATERIALS Analyses of the materials used are presented in Table I. Although ostensibly of extreme purity (99.999 wt pct), the bismuth was found to contain a significant amount of impurities, probably oxides. Except for determination of the binary system, Bi-U, prior to use all bismuth was hydrogen-refined and

Jan 1, 1962

By H. F. Moore

We have studied the simple case of repeated stress, without considering impact, which might bring in other factors. This investigation has shown that steel under repeated applications of stress, reversed from positive to negative, will not fail below some fairly clearly defined limiting stress that, so far we can see, does not bear any definite relation to the ordinary elastic limit, being as large as the elastic limit in some cases and about one-half the elastic limit in others. According to one theory, fatigue is the result of changes in crystalline structure by repeated stress. I do not know of any evidence in favor of this theory. The crystals are broken under repeated stress. According to Bauschinger, under repeated stress some inherent property of the material changes its elastic limit; possibly some property of the amorphous cement between the crystals. A third theory is that all fatigue of metals is the result of the spread of damage from little localized overstresses. While I do not feel justified in accepting the last theory rather than the second, I have yet to run across a case of failure of steel or other metal, either in the laboratory or in service, that could not be explained by the gradual spread of damage from some nucleus. We have found, for example, that it is possible to subject a homogeneous steel, like Armco iron or a 0.90 per cent. carbon steel, that has been thoroughly annealed, to one hundred million reversals of stress as high as the elastic limit of the steel with no sign of failure. On the other hand, a complex structured steel, like a chrome-nickel steel that has been hardened with very little drawing, will fail at a stress about 58 per cent. of its elastic limit. Between these two we get a variety of results. In the steel work of any building, there are undoubtedly many thousands of places where structural damage was done—where riveted members were bent into place cold and where the rivets were fitted with drift pins, etc. Locally the steel in the building was stressed beyond its yield point in many places. These little localized overstresses do no damage at all; the building is entirely safe. But if this building were subjected eight or ten times a day to a mild earthquake, these little localized overstresses might be nuclei from which damage would spread

Jan 1, 1922

By M. E. Nicholson

The effect of boron on the austenitic transformation rate of iron is smaller than on low carbon steels. The influence of austenitizing temperature on B-Fe is the reverse of its influence on steels. THERE have been many studies made of the influence of boron on the hardenability of steel, but apparently none has been made of its influence on the y-a transformation of pure iron. There are several facts suggesting that boron should have a pronounced effect on the transformation rate of iron. First, Simcoe et a1.l indicated that boron reduces the nucleation rate of ferrite and bainite. Second, they showed, along with others,', " that the lower the carbon content of steel the greater the influence of boron on hardenability. If this trend extends to pure iron, the influence on rate of ferrite formation should be considerably greater for iron than for medium carbon steels. According to Rahrer and Armstrong," the multiplying factor for boron in pure iron should be about 2.40, compared with 1.50 in a 0.35 pet C steel. According to an extrapolation made by Grange and Mitchell,' the effect should be even greater, and the multiplying factor should be about 3.5 in iron. Many investigations of the boron influence'.7, 2, 5 indicated that boron is effective only when in solid solution. On the other hand, Chandler and Bredig" suggested that boron increases hardenability by combining with nitrogen, thereby preventing formation of AlN, which catalyzes the decomposition of austenite. If their hypothesis is valid, boron should have no effect on an alloy free from nitrogen. Digges et al." showed that so far as low nitrogen high purity Fe-C alloys are concerned this is not the case. No experiments, however, have been made on low nitrogen iron. To determine whether or not boron has an effect on low nitrogen iron and, if an effect exists, to determine whether it is as large as predicted from the investigations of boron treated steels, the following work was performed. Because of the rapidity with which iron transforms from austenite to ferrite at even a moderate degree of supercooling, it was decided to study the influence of boron on the transformation rate of iron by determining the effect of quenching rate on the temperature of the beginning of transformation. The technique, essentially that used by Greninger' and Duwez,H consisted of heating small specimens, 0.1 in. sq and 0.010 in. thick, in an atmosphere of purified helium with a resistance heater coil, and then quenching the sample in a jet of helium gas. At the time the jet was applied, the heating coil was removed from around the sample. The sample was suspended in the furnace on 30 gage chrome1 and alumel wires, one welded to each side of the specimen, which also served as a thermocouple for measuring the specimen temperature. Specimens were prepared from vacuum-melted iron obtained from the National Research Corp. which was rolled to a thickness of 0.060 in. and then decarburized in wet hydrogen for 51/2 hr at 700°C. This treatment also removed any boron present in the iron. The resulting iron contained 0.001 pet C. 0.0002 pet N, and 0.005 pet 0. One half of the piece was then boronized by surrounding it with 325 mesh boron powder and heating it for about 2 hr at 900°C in H,. The boronized iron was then homogenized at 1100°C for 24 hr. The iron boride case formed by boronizing was removed by grinding 0.010 in. from each side of the plate, and the piece was finally rolled to a thickness of 0.010 in. The resulting alloy contained

Jan 1, 1957

By G. Czupryna, S. Natansohn

Electrowinning is the prevalent technique for recovering silver from wastes generated in silver-tungsten electrical contact fabrication. Such scrap is placed in a permeable plastic basket, which constitutes the anode compartment, and is suspended in a larger cell where the cathode is mounted. A silver nitrate solution is used as the electrolyte and, upon application of an electric field, the silver migrates to the cathode where it deposits. At times, there is tungsten migration to the cathode compartment and consequent co-deposition with the silver. This W contamination, which may amount to several thousand mg/L (oz per gal), necessitates additional purification of the deposited Ag and its removal would, therefore, be advantageous. Eliminating the W impurity also extends the operating period of the cell with corresponding increases in the Ag output and savings in labor costs. The solution to this problem lies in the selective removal of the W from the AgNO3 electrolyte either by liquid-liquid or liquid-solid extraction. Although W extraction in the liquid-liquid mode with a quaternary amine or other reagents as extractants appears feasible, particularly in view of the low pH (about 1.5) of the system, this approach was not considered because it is essentially a batch-type process. It is a more elaborate industrial operation than extraction by ion exchange resins. Implementing the latter process consists of passing the electrolyte from the electrowinning cell through an ion exchange column which would extract the tungsten selectively and returning the tungsten-free stream to the cathode compartment. This process continues until the W extraction efficiency decreases (as a result of resin loading) below an acceptable value. The electrolyte is then directed through another, similar column while the W values are eluted off the first one and the resin is regenerated for another cycle. Thus, two columns in a parallel flow pattern provide the means for continuous processing of the electrolyte feedstock.

Jan 1, 1984

By C. H. Hitchcock

A brief resiclence in Virginia hasenabled me to examine some of its crystalline strata, and a few hints, concerning their correspondence with similar rocks elsewhere, may be of service to those who are studying them. In comparing the crystalline rocks of Virginin and New England, we may first recall the similarity of their geographical position. They constitute a continuous belt, being traceable through the Highlands of New York and yew Jersey, Southeastern Pennsylvania, in the counties of Bucks, Montgomery, Philadelphia, Delaware, and Chester, and Marylund. Thus the Green Mountains of Vermont and the White Mountains of New Hampshire seen] to be topographically continuous with the Blue Ridge and Midland districts of Virginia. This tract of country has been termed the Atlantic area in distinction from the Appalachian territory, whose eastern limit is the great, Lower Silurian limestone valley extending from the St. Lawrence and Champlain valleys to Alabama. The Appalachian formations were studied by the brothers Rogers, forty years since, and found to refit, unconformably upon the western flank of the Blue Ridge, the oldest of the series adjoining the gneisses, followed westerly by the other Palseozoic members in a regular ascending order, to which numercial designations were applied—Number 1 being the Cambrian, Number 2 the Lower Silurian Iimeqtones, etc?. In Vermont the same conclusion Was presented in the State reports: the Green Mountains were said to possess the anticlinal structure, and to underlie the quartzites and limestones. Inasmuch as this Atlantic area is' topgraphically continuous from the Middle to the Northern States, and is unconformably overlaid upon the west side by the same succession of strata, the presumption ii very strong that the history of bath sections has been the same, and that the entire area is of Eozoic age. Cross sections, in both districts, illustrate the existence of gigantic overturns, causing the strata of 'the Appalachian region to dip to wards the Atlantic gneisses. To the beginner it would appearthat tile Silurian group must dip beneath the crystallines, and hence many of the geologists in the beginning of the study of the stratigraphy of this easters border of the continent believed that

Jan 1, 1882

By W. T. Jr. Thom

IN PREVIOUS classifications of coal, it has been customary to regard moisture eliminated from coal samples between 20° and 100° C. as extraneous matter, rather than as a constituent part of the coal. It seems, however, that the physical character and use properties of the low-rank coals are directly related to the amount of such moisture present, and recent chemical work has shown1 that such coals contain unstable groupings which decompose between 20° C. and temperatures somewhat above 100° C., with the splitting off of moisture. According to this view, the moisture eliminated from air-dried coal below boiling point is similar in all essential respects to moisture eliminated above 100° C., and is produced by analogous reactions; and inasmuch as the moisture given off above 100° C. has always been treated as a constituent of the volatile matter of coal, it would seem that consistent usage would include as a part of the volatile matter all moisture present as an essential component of the coal as it occurs in nature. As a matter of experience, it seems clear that the general physical and chemical characteristics of the low-rank coals are largely determined by or related to the moisture, whether chemically or physically combined, present in air-dried coal; it is also demonstrable by trial that the low-rank coals cannot be satisfactorily classified on a purely chemical basis by using the moisture free form of analysis. The low-rank coals of the western United States include numerous well-defined types, many of which were referred to in a classification proposed by Ashley,2 in which the physical and use properties of the coals were made the primary basis for their systematic grouping. When testing this classification by replotting analyses of these type coals according to the Seyler scheme of classification,3 a satisfactory parallelism between use properties and chemical constitution of the dry coal was found among

Jan 5, 1925

By W. T. Thom

In previous classifications of coal, it has been customary to regard moisture eliminated from coal samples between 20 and 100 C. as extraneous matter, rather than as a constituent part of the coal. It seems, however, that the physical character and use properties of the low-rank coals are directly related to the amount of such moisture present, and recent chemical work has shown' that such coals contain unstable groupings which decompose between 20 C. and temperatures somewhat above 100" C., with the splitting off of moisture. According to this view, the moisture eliminated from air-dried coal below boiling point is similar in all essential respects to moisture eliminated above 100" C., and is produced by analogous reactions; and inasmuch as the moisture given off above 100" C. has always been treated as a constituent of the volatile matter of coal, it would seem that consistent usage would include as a part of the volatile matter all moisture present as an essential component of the coal as it occurs in nature. As a matter of experience, it seems clear that the general physical and chemical characteristics of the low-rank coals are largely determined by or related to the moisture, whether chemically or physically combined, present in air-dried coal; it is also demonstrable by trial that the low-rank coals cannot be satisfactorily classified on a purely chemical basis by using the moisture free form of analysis. The low-rank coals of the western United States include numerous well-defined types, many of which were referred to in a classification proposed by Ashley,2 in which the physical and use properties of the coals were made the primary basis for their systematic grouping. When testing this classification by replotting analyses of these type coals according to the Seyler scheme of classification,3 a satisfactory parallelism between use properties and chemical constitution of the dry coal was found among

Jan 1, 1925

By D. D. Lambert, E. C. Simmons

Rare earth element (REE) analyses of cumulus plagioclase from the PGE ore zone of the Stillwater Complex indicate that pressure fluctuations in the magma chamber acting on a single magma cannot be responsible for features such as the reappearance of Mg-rich olivine on the liquidus. The data are more consistent with a model involving multiple injection and mixing of geochemically distinct magmas. The PGE-bearing sulfides of the J-M Reef are associated with such a reappearance of olivine, indicating that the unusual location of the ore zone may be related to the addition of new magma, compositionally distinct from magmas that produced cumulates in the Ultra- mafic zone of the complex.

Jan 1, 1984

By Henry M. Howe

1. The purpose of the National Research Council as organized for war purposes is twofold, to stimulate those outside its own personnel to conduct researches of importance for winning the war and to carry on such researches through its personnel to a limited extent. How this is done is explained in Section 10. "Research" is used here in a very broad sense, including, for instance, inventing and developing mechanical and physical devices. The need of this work arises from the inevitable concentration of most of the governmental war agencies on the production and transportation of war materials of the types now adopted, as distinguished from devising new kinds of instrumentalities, such as armor, guns, aircraft, and apparatus for detecting, locating, observing, signaling, transporting, and many other military purposes. But it is important that we should devise new agencies. The war came near being won by an invention, the submarine, and its course has been affected greatly by two other inventions, tanks and aircraft. In spite of our numerical superiority victory may well be snatched from us by an invention, if we allow Germany to outstrip us in inventing. Hence the importance of the Council's work in mobilizing and organizing the services of the patriotic civilian experts throughout the country, so as to bring their powers to bear on important war problems and on inventing war devices, as an adjunct to the development work of the regular governmental bodies. 2. Status of the Council.—Though President Wilson's request caused the Council to be created in 1916 by the National Academy of Sciences under its congressional charter; though his executive order of May 11, 1918, directs the heads of "Governmental departments immediately concerned" to "continue to co-operate with it in every way that may be required;" and though the Government has contributed largely to its financial support; it is not a department of the Government but an independent research body, aiming to evolve the necessary mechanism for the novel work of systematic stimulation and guidance of research. Thus the Government, which instigated the creation of the Council, recognizes and collaborates with it, and in part supports it. The Council acts moreover as the Department of Science and Research of the Council of National Defense.

Jan 1, 1919

US 4,192,852-Precipitation of iron values as a jarosite from a sulfate solution obtained as a byproduct in the hydrometallurgical processing of zinc sulfide ore The solution is cooled, partially neutralized, and clarified. The clarified solution is heated to a temperature of 80 to 100°C in the presence of sodium, potassium, or ammonium ions to precipitate substantially all of the ferric iron as jarosite The precipitate is thickened, filtered, and washed The residual solution may be processed for zinc or other nonferrous metal values R V. Pammenter and C J Haigh, assigned to Electrolytic Zinc Co of Australasia Ltd. Mar. 11, 1980. 16 pp. (423-42) Filed: 5-8-78 (903,524). Priority- Australia, 5-9-77 (PD0030) (Drawings below.)

Jan 1, 1982

By David A. Rice

This note describes a simple, rapid technique for measuring the apparent volume and density of individual bits of porous materials such as iron ore pellets or pieces of coke. The method consists of determining the weight recorded on a balance when a particle is depressed below the surface of mercury, and calculating the apparent volume from the known density of mercury. The apparent density is calculated after weighing the particle in air. The method is particularly well suited for applications where a great number of determinations are to be made. An additional benefit is the minimal handling of the mercury. In any event, the usual recommended safety precautions should be adhered to.

Jan 1, 1982

By S. Sumski, M. B. Panish, R. T. Lynch

The liquidus isotherms in the gallium-rich corner of the Ga-Al-P phase diagram have been determined from 1000" to 1200°C and at I100°C the corresponding solidus isotherm was obtained. A simple thermody-namic treatment which permits calculation of the solidus and liquidus isotherms is discussed. A technique which was previously used for the growth of GaxAl1-xAs was used for the preparation of solution epitaxial layers of GaxAl1-xP and ALP. An approximate value of 2.49 i 0.05 ev for the band gap of Alp at 300°K was obtained and the ternary phase data were used to estimate a value of 36 kcal per mole for the heat of formation 0f Alp at that temperature. The Gap-A1P crystalline solid solution is one in which there exists the possibility of obtaining crystals with selected energy gaps, within the limits imposed by the energy gaps of Gap and Alp. Such crystals are of considerable interest because of their potential value for optoelectronic and other solid-state devices. Furthermore, it has been amply demonstrated for GaAs and GaP,'-7 that device, or bulk materials grown from gallium solution generally have more efficient radiative recombination than materials prepared in other ways. This presumably due to the lower gallium vacancy concentration in such material.= Small crystals of GaXAl1-xP and A1P have been grown from solution,8-10 and A1P has been grown from the vapor," but neither have previously been grown by liquid epitaxy. In this paper we present the ternary liquidus-solidus phase diagram of the Ga-A1-P system in the region of primary interest for solution epitaxy, and discuss the thermodynamic implications of that phase diagram with particular reference to the liquidus and solidus isotherms in the gallium-rich corner of the GaxAl1-xP primary phase field and to the A1-P system. Several measurements of the absorption edge of GaxAl1-xP crystals have been made and the width of the forbidden gap of A1P has been estimated from these measurements. EXPERIMENTAL The differential thermal analysis technique used to determine the liquidus isotherms and the optical measurements used in this work are similar to those described previously12 for the Ga-Al-As system, ex- thermocouples in the thermopile for added sensitivity. The materials used were semiconductor grade Ga, Gap, and Al+ The composition and temperature range at which DTA studies could be done was quite restricted. The upper temperature was limited by the chrome l-alumel thermopile to about 1200°C, and the highest aluminum concentration to about 5 at. pct by low sensitivity caused by the reduced solubility of Gap with increasing aluminum concentration in the liquid. DTA studies were not possible at 1000°C and below because of the low sensitivity caused by low solubility of Gap in the Ga-A1-P system. The cooling rate for these studies was about 1°C per min. No heating studies were done because of limited sensitivity. Supercooling probably does occur, but our experience with other 111-V systems indicates that it is no greater than about 10 to 15.c. Solid solubilities were determined by analyzing epitaxial layers of GaxAl1-xP grown from the liquid, with an electron beam microprobe. The layers were grown on Gap seeds by a tipping technique in which the layer is grown over a short-temperature range (20" to 50°C) on the seed from a solution of known composition. The tipping technique reported by Nelsson1 for GaAs could not be used, particularly for solutions containing appreciable amounts of aluminum, because of the formation of an A1203 scum on the liquid surface. A system was therefore designed, which would effectively remove the oxides mechanically, so that uniform wetting and crystal growth could occur. This tipping technique has already been described in detail." The best control over the composition of the re-grown layer was obtained when the tipping was done at a temperature which corresponded to the temperature of first formation of solid for the solution being used. Generally, therefore, a solution was prepared by adding the amounts of Ga, Gap, and A1 required to yield a solution which would be completely liquid above the tipping temperature with solid precipitating below that temperature. For most of the work reported here, the 1100°C isotherm of the ternary was used. It was generally necessary to heat the solution to 50" to l00. C above the tipping temperature to dissolve all of the Gap in a reasonable length of time. The epitaxially grown layers were used both for optical transmission measurements to aid in the estimation of the way in which the absorption edge changed with aluminum concentration, and for the electron beam microprobe analyses to provide data for the determination of the solid solubility isotherm. RESULTS AND DISCUSSION Liquidus Isotherms in the Ga-A1-P Ternary Phase Diagram: Thermodynamic properties of the system. The only thermal effect studied in this work was that

Jan 1, 1970

By P. H. G. Durville

ANY metal which contains even a small percentage of aluminum possesses certain peculiarities of appearance and properties which are exhibited both when the metal is melted and after it solidifies. Pure aluminum, or an alloy containing a small proportion of aluminum, can be melted without flux-except for a layer of charcoal-because a film of aluminum oxide and metal forms at the surface of melted aluminum. Although very thin, this film is air-proof, and it prevents the metal underneath from oxidizing. This oxidized film does not move easily on account of its toughness and high surface tension. One very important point in connection with this process of still casting has not been strongly enough stressed, namely, that the same kind of surface film with the same peculiarities forms over the surface of all melted alloys that contain even a small proportion of aluminum. Experienced foundrymen know how desirable it is to cast aluminum under its "skin" or under the surface of the film which tends to remain still. In the case of red copper, when in fusion, the surface shows pure copper only. This is due to the fact that liquid copper constantly absorbs the copper oxide which forms on the surface. By closely examining melting copper the oxide can be seen dissolving in the bath, and going into solution just as pulverized sugar dissolves in water. When copper is cast in the open, either in wire bars or cakes, the surface of metal exposed to the air is covered by a film of black, oxide that cannot be absorbed by the metal.

Jan 1, 1927

By Cyril Stanley Smith

ON the 6th of February 1684, Dr. Martin Lister mentioned at a meeting of the Royal Society1 that "brass is magnetical," and promised to give an account of that assertion at some other time. He repeated his promise but never fulfilled it, and it was left for William Arderon2 to show, in 1958, that brass could be made magnetic by hammering and that it would retain polarity after magnetizing. Twenty-seven years later Cavallo3,4 examined the matter in great detail. Working with cast calamine brass, he showed that it could be made magnetic by hammering and nonmagnetic by subsequent annealing at a red heat. He found that annealing at a very high temperature caused the samples to lose their magnetic quality permanently, even after subsequent cold-working, but that remelting and cold-working restored it. He encountered some samples of brass that could not be rendered magnetic by any treatment. Experiments in which these were remelted with iron additions gave negative results, and Cavallo concluded that iron impurity was not the cause of the magnetism. He worked with 50-grain (3-gram) samples melted under the blowpipe, hence cooled very quickly. Bennet5 made whole crucible charges from copper and zinc, and found the resulting brass ingots to be magnetic only when iron had been added and then only after cold-working. All these observations applied to material in the cast condition, in which coring would produce a continuous spectrum of composition and cooling would result in varying degrees of precipitation. This knowledge of the subject seems to have been forgotten in the nineteenth century. The older brass was made by the calamine process and frequently contained iron in amounts of 0.5 per cent or more, absorbed from the impure ore with which the copper and charcoal were heated in making the brass. When metallic zinc became available in commercial quantities, calamine brass gradually disappeared, and with it the knowledge of its curious magnetic properties. Only when sensitive apparatus replaced the compass needle of the earlier investigators could the effects be detected in relatively pure metal. The effect of cold-working in inducing ferromagnetism was rediscovered by Bitters in 1930 in a sample of impure copper, and this was confirmed by Lowance and Constant,9 Honda and Shimizu, 10,11 and others. In the same year, Tammann and Oelsen12 showed that copper-rich copper-iron alloys after certain heat-treatments could be rendered ferromagnetic or made more strongly ferromagnetic by cold-rolling. Kussman and Seeman13 showed that the change of susceptibility of relatively pure copper on cold-working was associated with the iron content, and concluded that actual precipitation of iron was caused by cold-working, which is a satisfactory theory until one considers the improbably high rate of diffusion that this would involve. When studying precipitation phenomena in

Jan 1, 1941

By Wheeler P. Davey

When metals are subjected to mechanical working, such as rolling, one of the phenomena that take place is a movement of the crystals of the metal into a system or systems of orientation which bear an angular relation to the direction of working. In rolled metal the crystals may orient themselves with respect to the rolling plane or the rolling direction, or both. Direct evidence of the existence of preferred orientations in rolled metal has been obtained by numerous investigators from X-ray patterns of the rolled metal. Most of these workers used a monochromatic pinhole method. Where the degree of preference for a single orientation is high the monochromatic pinhole pattern may be interpreted by a geometrical calculation based on the angular relationships of the planes in the crystal and the diffraction arcs on the X-ray pattern. This process may be aided by the geometrical construction of the locus sphere (Lagenkugel), and reflection circles of Polanyi,l Polanyi and Weissenberg,2 and Mark and Weissenberg,3 and of the plane polar figures (flachenpolfigur) of Franz Wever.4 R. M. Bozorth5 solves X-ray patterns from metals having a single preferred orientation by means of a series of charts which when placed over the X-ray pattern give directly certain angular relationships, between the crystal planes and the surface of the specimen.

Jan 1, 1930

By M. ROWE, H. E. Gilliland, L. BARNES

The authors of this paper are to be commended for a clear exposition of a timely subject. However, some important conclusions, in addition to those presented in the paper, can be drawn from the results of their elaborate and rather complete numerical computations. First of all, the major part of the calculations presented in the paper are for semi-infinite slabs of oil shale (the authors designate this as Model I) and a question must be posed — Are these elaborate computations needed to arrive at realistic estimates of the shale oil displaced. Consider the model of Lauwerier* that corresponds to the authors Model I if thermal conduction parallel to the fracture be neglected. If one also neglects the finite (but relatively small) heat capacity of the material in the fracture, it is easily shown from Lauwerier's solution that the cumulative oil production would be:

Jan 1, 1969

By Donald F. Irwin

Amid the violent economic changes of recent years that have affected Canadian gold-mining operations so deeply, the discovery and early developments of Kirkland Lake might easily be overlooked. There was more than one "false dawn" for the district before developments finally established the fact of a superb mineralized zone extending through the present operating properties. Never far from the railway, Kirkland Lake has had the benefit of direct rail service for many years. The pioneer discovery on which the first mill and cyanide plant was erected was the "Tough-Oakes," this property being on what is now the eastern end of the producing area; some time later, the "Lake Shore" was discovered at the present center of the district, and a small plant was built upon it also. Both of these early treatment plants were of pre-war design. Progress in gold metallurgy has caused a gradual change in cyanide practice since the early days at Kirkland Lake, which may be observed in the various plants now operating there. From the beginning, it was recognized that Kirkland Lake ores were more responsive to cyanidation than to alternative recovery methods, and that their mineralization contained gold in very finely divided form. Although sulfides and tellurides are present, the quantity is small, being in the order of 1 or 2 per cent by weight, so that gravity concentration is undesirable, since gold is not confined to the sulfides. Some complication is offered by the presence of tellurides, which have caused lengthy controversy over their importance in recovery methods, but which are now generally regarded as less harmful in the light of increasingly high recoveries being obtained. Nevertheless, finely divided gold intimately associated with sulfides in the presence of tellurides; and occurring in the hard Kirkland Lake porphyry ore, substantially free from natural slime-forming constituents, indicates fine grinding. This has been the universal practice although the degree of grinding has varied a little among the different mills and is considerably finer now than formerly. The natural condition as outlined caused the establishment of fine grinding at an early stage in the development of Kirkland Lake, during the period of valuation of gold at, $20.67 per ounce. With the arrival

Jan 1, 1935

By W. R. Toeplitz

Probably a more descriptive title would be "Much Ado About Nothing." By "nothing," of course, I refer to the porosity which is the main feature of this type of bearing. Porosity has a decided effect on the manufacturing techniques, the structure and physical properties, the oil content, and on the installation and service of oil-retaining porous bronze bearings. A simple curve can be drawn by plotting specific gravity along the abscissa and percentage of porosity by volume on the ordinate. A bronze composition, analyzing 89 Per cent copper, 9.75 Per cent tin, and 1.25 per cent graphite, has an absolute solid specific gravity of 8.5. At this specific gravity, of course, occurs the point of zero porosity. Conversely, at loo per cent porosity, the specific gravity is zero. A similar curve can be drawn for bearings impregnated with oil; the only change being that the specific gravity at loo per cent oil will be 0.89 if we assume that that is the specific gravity of the lubricant. The curve is useful in determining the oil content by volume for any specific gravity. The normal range of oil content for porous bronze bearings of this composition is from 35 to 16 per cent, which is in the specific gravity range of from 5.8 to 7.3. In addition to the amount of porosity, the type of porosity is important. The first consideration here is that the porosity must be intercommunicating. This can be determined by a number of simple tests. The first method, which is very accurate, is to extract the oil in the bearing by cycling

Jan 1, 1945