Search Documents

By George M. Schwartz, Ian L. Reid

THE Soudan mine in the Vermilion district of northeastern Minnesota is the oldest iron mine in the state. It has shipped ore every year since 1884 and still contributes a yearly quota of high grade lump ore. No comprehensive report on the Vermilion iron-bearing district has appeared since Clements' monograph,' but Gruner2 discussed the possible origin of the ores in 1926, 1930, and 1932, and recently Reid and Hustad have added data on mining and geology .3, 4 For many years geologists of the Oliver Iron Mining Div., U. S. Steel Corp., have kept up to date a series of plans and vertical sections of the Soudan mine. In connection with mine operation considerable diamond drilling has been done, and this, together with the mine openings, has permitted a reasonably accurate picture of the structure of the orebodies and wall rocks. It has long been evident to geologists familiar with the mine that the ores were not a result of weathering, a point emphasized by Gruner in 1926 and 1930. As the deeper orebodies were developed it also became clear that replacement had played an important part in their development. In recent years it has been recognized that other iron ores were formed by replacement, as Roberts and Bartly5 have argued strongly for the deposits at Steep Rock Lake. On the basis of these facts G. M. Schwartz suggested to members of the Oliver staff that it would be desirable to study the evidence of replacement, particularly the possible alteration of the wall rock which would be expected if the replacement was a result of hypogene solutions. Rock Formations: The formations directly involved in the iron orebodies of the Soudan mine are few though far from simple. The country rock is largely the Ely greenstone of Keewatin age consisting of a mass of metamorphosed lava flows, tuffs, and intrusives which have been more or less altered by hydrothermal solutions. The predominant rock is chlorite schist. Interbedded with the original flows and tuffs are a series of beds and lenses of jasper to which the name Soudan formation has been applied. In the Vermilion district the term jaspilite has been used for interbanded jasper and hematite. According to modern usage these jasper or jaspilite beds do not comprise a formation separate from the Ely greenstone, inasmuch as the beds of jasper are interbedded with the flows and tuffs of the upper part of the greenstone. It would more nearly accord with modern usage to consider the Soudan beds a member of the upper part of the Ely formation. Because of incomplete rock exposure and exploration the number of interbedded jaspilite beds is unknown. In the mine, however, as many as nine major beds of jasper are known on a cross-section of one limb of the syncline, with an equal number on the other limb. In addition diamond drill cores show beds of greenstone down to half an inch in thickness. The thin beds are probably always tuffs. Structure: Rock structure in the Soudan area is complex, and because there are no recognizable horizons within the greenstone it is extremely difficult to work out the details. Generally speaking, the major regional structure is an anticlinorium, the axis trending east-west, with a westerly pitch. The Soudan mine is related to a synclinal structure on the north limb of the anticline about a mile from the west nose of the folded iron formation. The general structure at the mine is that of a closely folded minor syncline on the major regional anticline. A cross fault has dropped the east side so that the bottom of the syncline has not been reached, whereas to the west it is well shown by the mine openings and diamond drill exploration. Throughout the mine the beds of jasper, and ore-bodies that have replaced the jasper, normally dip northward at angles of 80" or steeper. In detail the jasper beds are extremely folded, probably as a result of deformation while they were still relatively unconsolidated. Orebodies: Ore in the Soudan mine is mainly a hard, dense, bluish hematite. Locally ore has been brecciated and cemented by quartz. The vugs commonly occurring near the borders of orebodies are lined with quartz crystals. They seem to have formed as part of the ore-forming process and are evidence that no folding or compression of the ore has taken place. The orebodies are numerous, varying greatly in size. Many lenses of high grade hematite are too small to be mined. Some of the larger orebodies have been followed vertically for as much as 2500 ft and horizontally up to 1500 ft. The large ore-bodies are extremely irregular in outline in the plane of the beds of jaspilite. In width they are more regular, as they are strictly governed by the width of the jaspilite beds and the greenstone wall rock, which seems to have resisted replacement by hematite. At many places the orebodies replace the jaspilite completely and have a footwall and hanging wall of greenstone. At other places either one or both walls may be jaspilite. Geologists who have studied the orebodies in recent years agree that evidence for the replacement origin of the hematite bodies seems conclusive. AS noted above, many of the orebodies replace jaspilite beds from wall to wall with no evidence whatever of compaction. The replacement origin is also supported by details of the banding which is characteristic of the

Jan 1, 1956

By Klaus Schwerdtfeger

In order to test the performance of ZrO, (CaO) and Tho,(Yz03) electrolytes in the electrochemical determination of oxygen activities in liquid metals at steel-rrzakitng temperatures , electromotive force measurements have been made with the following cells: The oxygen-- activities are calculated from the electmrnotive forces for the investigated systems. The standard free energy of- formation of MnO and the activity of manganese in Fe-Mn melts are derived. Indications are that the Zr 0z(Ca0) electrolyte exhibits little electronic conductivity at oxygen pressures as low as 10'a atnz at 1600°C; however, the partial electronic conductivity may become noticeable at lower oxygen activities. The Tho,(Yz03) electrolyte is found to be an ionic conductor at the oxygen pressure as low as that for the Mn + MnO equilibrium, but exhibits partial electronic conductivity at oxygen pressures higher than 10"1 atm (1500°C). fi. better control of oxidation and deoxidation reactions in steelmaking may be facilitated if the oxygen activity in the steel is known during various stages of the process. In the present work oxygen activities have been measured in liquid iron, manganese, and iron alloys with galvanic cells using ZrOz(CaO) and s solid electrolytes with the object of establishing the range of oxygen pressure in which these materials can be used as electrolytes at steelmaking temperatures. Calcia-stabilized zirconia and Tho2-Y203 solid solutions are oxygen ion conductors. Such electrolytes were first used by Kiukkola and Wagner1 and Peters and ~ann' in galvanic cells for the determination of thermodynamicquantities of oxide systems in the temperature range 700" to 1200°C. At these moderate temperatures calcia-stabilized zirconia has been found to exhibit predominantly ionic conductivity at oxygen pressures as low as those for the Cr + Crz03 equilibrium,394 but at lower oxygen pressures elec- tronic contribution to conductivity becomes significants4 The Th02-Y203 solid solutions are ionic conductors at oxygen pressures lower than those applicable to zirconia base electrolytes.5'6 At high oxygen pressures Thoz base electrolytes exhibit significant p-type semiconduction. At the time the present experiments were carried out several papers1'-* were published on the electrochemical determination of oxygen activities in liquid iron using the ZrOz(CaO) electrolyte. The results of different authors do not agree well. For instance, according to Fischer and ~ckermann" stabilized zirconia can be used to measure oxygen contents in liquid iron larger than 0.02 wt pct, but according to Baker and west1' ZrOz(CaO) cannot be used for the determination of oxygen content in liquid iron because of high electronic contribution to the conductivity. Fig. 1 is a schematic diagram of the apparatus used. About 500 g of liquid metal is contained in a crucible into which a stabilized zirconia or Th02(Y203) tube is immersed. A platinum contact wire is pressed (with a spring mechanism) against the inside bottom wall of the electrolyte tube. The tube is flushed continuously with a stream of air, CO-CO, (or Hz-C02) (at 0.96 atm and at a rate of about 300 cu cm per min), via an alumina tube inserted inside the electrolyte tube. This alumina tube also contains the Pt-Pt/10 pct Rh thermocouple. A capillary alumina tube shielding the other contact wire is immersed in the melt. The molybdenum contact wires were used mostly; in some cases platinum wire was employed. Molybdenum has the advantage that it dissolves more slowly in the melt than platinum. The whole cell was contained in the alumina reaction tube of a resistance furnace with molybdenum winding. The reaction tube was closed gas tight at both ends and flushed continuously with argon. Because of the poor thermal shock resistance of the electrolyte tubes the cell had to be assembled in the cold furnace. The electrolyte tube and alumina sheath

Jan 1, 1968

By K. Takahashi, I. Iwasaki

The methyl stretching vibrations for a series of normal xanthates, isoxanthates and normal amines were determined with the aid of an infrared spectro-photometer, and the results were compared with published information on the corresponding alcohols. The frequency shifts of methyl stretching vibrations may be attributed to the inductive effect of polar groups. The hydrogens in the shorter chain alkyl groups are somewhat polar and can be expected to interact with water molecules by hydrogen bonding. Contact angle, surface tension lowering, solubility, and critical micelle concentration appear to be related to the induced polarity of the alkyl groups. Traube's rule states that in homologous series of compounds solubility decreases and surface activity increases regularly with the size of the hydrocarbon group. Analyzing the work of transfer of a solute from solution to surface, Langmuir' interpreted this rule to mean that each CH2 group added to a molecule produced its effect independently of the others. It is also well known2 that the maximum equilibrium contact angle with sulfhydryl collectors is independent of the polar groups and of the sulfide minerals, and that it increases to a certain limit with the number of carbon atoms in the alkyl group. This observation is thought to demonstrate the orientation of the collector molecules at the sulfide surfaces. The dependence on the hydrocarbon chain length is usually explained as due to the screening of the force field of polar mineral surfaces.3-5 Here again, Langmuir's principle of independent surface action appears to be implied. Heteropolar compounds consist of nonpolar and polar groups, the former being the hydrocarbon group and the latter containing such electronegative atoms as O, N, S, P, or halogens. According to Palit6 the hydrogens in the alkyl groups are more electroposi- tive than in the paraffins owing to the negative inductive effect of the polar groups and a possibility that a hydrogen bond with water molecules ensues. Goto and Takenaka7 provided direct evidence of the inductive effect by measuring the shift of the C-H stretching vibrations of alcohols, acids, and alkyl bromides with an infrared spectrophotometer. Their approach appeared to be directly applicable to the studies of surface activity both at air-water and water-mineral interfaces encountered in flotation systems. The present article attempts to relate the C-H stretching vibrations of alkyl xanthates, alcohols, and amines with such flotation chemistry parameters as contact angle, surface tension lowering, solubility, and critical micelle concentration. MATERIALS AND METHODS Normal xanthates from methyl to octyl inclusive and the isopropyl, isobutyl, and isoamyl xanthates used in this investigation were prepared in the usual manner.8 Normal amine hydrochlorides with carbon chain lengths of 1, 2, 4, and 6 were from Distillation Products Industries, of 8 from Archer-Daniels-Midland Co., and of 10, 12, 14 and 16 from Armour and Co. Normal propylamines, pentylamines and heptylamines from Distillation Products Industries were used both as received and as hydrochloride formed by converting the amines according to the procedure described by Li9 Perkin-Elmer Model 521 and 621 infrared spectro-photometers were used to investigate the spectra in the frequency region of 3050 to 2800 cm-' with frequency scale expansion. The accuracy of the frequency readings was within + 1 cm-1. The KBr micropellet technique was used to prepare the xan-thate samples for measurements, and the halocarbon mull technique was used for amines and amine hydrochlorides. EXPERIMENTAL RESULTS Fig. 1 shows the CH3 asymmetric stretching vibrations as a function of the number of carbons in the alkyl group for normal xanthates, isoxanthates and amines. Also included in the figure are data for normal alcohols and isoalcohols taken from the article

Jan 1, 1970

By William D. Klopp, Joseph R. Stephens

A substantial reduction in the 300°F ductile-to-brittle transition temperature for unalloyed chromium was achieved in alloys from systems which resemble the Cr-Re system. These alloy systems include Cr-Ru, Cr-Co, and Cr-Fe. Transition temperatures ranged from -300° F for Cr-35 at. pct Re to -75°F for 0-50 at. pct Fe. The ductile alloys have high grain gvowth rates at elevated temperatures. Also, Cr-24 at. pct Ru exhibited enhanced tensile ductility at elevated temperatures, characteristic of superplas-ticity. It is concluded that phase relations play an importarlt role in the rhenium ductilizing effect. The ductile alloys have compositions near the solubility limit in systems with a high terminal solubility and which contain an intermediate o phase. The importance of enhanced high-temperature ductility to the rhenium ductilizing effect is not well understood although both may have common basic features. CHROMIUM alloys are currently being investigated for advanced air-breathing engine applications, primarily as turbine buckets and/or stator vanes. The inherent advantages of chromium as a high-temperature structural material are well-known1 and include its high melting point relative to superalloys, moderately high modulus of elasticity, low density, good thermal shock resistance, and superior oxidation resistance as compared to the other refractory metals. Additionally, it is capable of being strengthened by conventional alloying techniques. The major disadvantage of chromium is its poor ductility at ambient temperatures, a problem which it shares with the other two Group VI-A metals, molybdenum and tungsten. For chromium, the problem is further amplified by its susceptibility to nitrogen em-brittlement during high-temperature air exposure. In cases of severe nitrogen embrittlement, the ductile-to-brittle transition temperature might exceed the steady-state operating temperature of the component. The low ductility of chromium would make stator vanes and turbine buckets prone to foreign object damage. The present work was directed towards improvement of the ductility of chromium through alloying, with the anticipation that any improvements so obtained might be additive to strengthening improvements achieved through different types of alloying. The alloying additions for ductility were selected on the basis of the similarity of their phase relations with chromium to that of Cr-Re. The reduction in the ductile-to-brittle transition temperatures of the Group VI-A metals as a result of alloying with 25 to 35 pct Re is well established.a4 the temperature range -300" to 750° F. This phenomenon is commonly referred to as the &apos;<rhenium ductilizing effect"; this term is also used to describe systems in which the ductilizing element is not rhenium. Other alloy systems which have recently been shown to exhibit the rhenium ductilizing effect include Cr-Co and c-Ru.= In order to explore the generality of this effect, alloys were selected from systems having phase relations similar to that of Cr-Re, primarily a high solubility in chromium and an intermediate o phase. The following compositions were prepared: Cr-35 and -40Re; Cr-10, -15, -18, -21, -24, and -27 pct Ru; Cr-25 and -30 pct Co; Cr-30, -40, and -50 pct Fe; Cr-45, -55, and -65 pct Mn. Seven other systems were also studied which partially resemble Cr-Re. These systems have extensive chromium solid solutions or a complex intermediate phase, not necessarily o. The compositions evaluated include the following: Cr-20 pct Ti; Cr-15, -30, and -45 pct V; Cr-2.5 pct Cb; Cr-2.5 pct Ta; Cr-20 pct Ni; Cr-6, -9, -12, and -15 pct 0s; Cr-10 pct Ir. The compositions of alloys in these systems were chosen near the solubility limit for the chromium-base solid solutions, since in the Group VI-A Re systems, the saturated alloys are the most ductile. These alloys were evaluated on the basis of hardness, fabricability, and ductile-to-brittle transition temperatures. In addition to the studies of alloying effects on ductility, an exploratory investigation was conducted on mechanical properties at high temperatures in Cr-Ru alloys EXPERIMENTAL PROCEDURE High-purity chromium prepared by the iodide deposition process was employed for all studies. An analysis of this chromium is given in Table I. Alloying elements were obtained in the following forms: Commercially pure powder — iridium, osmium, rhenium, and ruthenium. Arc-melted ingot — titanium and vanadium. Electrolytic flake — iron, manganese, and nickel. Sheet rolled from electron-bearn-melted ingot — columbium and tantalum. Electron-beam-melted ingot — cobalt. Sheet rolled from arc-melted ingot — rhenium. All alloys were initially consolidated by triple arc melting into 60-g button ingots on a water-cooled hearth using a nonconsumable tungsten electrode. The melting atmosphere was Ti-gettered Ar at a pressure of 20 torr. The ingots were drop cast into rectangular slabs and fabricated by heating at 1470" to 2800° F in argon followed by rolling in air. Bend specimens measuring 0.3 by 0.9 in. were cut from the 0.035-in. sheet parallel to the rolling direction. The specimens were annealed for 1 hr in argon, furnace cooled or water quenched, and electropolished prior to testing. Three-point loading bend tests were conducted at a crosshead speed of l-in. per min over

Jan 1, 1969

By Klaus Schwerdtfeger

The rules of solution of oxygen from H2O-H2-He gas and of nitrogen from N2-H2 gas in shallow melts of liquid iron were measured at 1610o and 1600o C, respectiuely. Concentration profiles were detemined in the liquid iron. Tire rate data indicate that the solution process is controlled by diffusion in the iron melt. The diffusivities for oxygen and nitrogen in liquid iron, as calculated from the present data, are DFe-o = (12 ± 3) < 10-5 sq cm per sec and DFe-N = 11 ± 2) X 10-5 sq cm per sec at the temperatures employed. AN attempt was made by Shurygin and Kryukl to measure the diffusivity of oxygen in liquid iron. In their experiments a silica disc was rotated in liquid iron containing oxygen, and the rate of formation of liquid iron silicate was measured. Assuming that the rate of dissolution of silica is controlled by diffusion of oxygen in the iron, the oxygen diffusivity was computed from the rate data giving Dfe-0 = 6.1 X 5 sq cm per sec at 1600°C. Although this value seems to be of the right order of magnitude, there is no proof of the correctness of the assumptions involved in the interpretation of these rate data. The oxygen concentration in the iron at the iron-iron silicate interface was taken to be that in equilibrium with the silica-saturated silicate melt. That is, it was assumed that no concentration gradient existed in the liquid silicate. This is a questionable assumption, unless it is proved that the thickness of the silicate layer is very much smaller than that of the diffusion boundary layer in the iron. Furthermore, Shurygin et al.1 used the Levich equation2 to interpret their rate data. This equation was derived for mass transfer between a solid disc and a single-phase liquid. The hydrodynamic and diffusion boundary layers in the iron stirred by a disc, via coupling of the silicate melt, may be appreciably different from those predicted by Levich&apos;s derivations. In the present work the diffusivities of oxygen and nitrogen in liquid iron were measured at 1610" and 1600oC, respectively. EXPERIMENTAL METHOD Iron melts contained in high-purity gas-tight alumina crucibles were reacted with H2O-H2-He gas for the determination of the oxygen diffusivity and with N2-H2 gas for the determination of nitrogen diffusivity. At the end of the reaction period, the samples were quenched in a cold H2-He gas stream at the top of the furnace. Oxygen or nitrogen contents in the iron were determined by chemical analysis. Two different types of diffusion experiments were perforxed. To determine concentration profiles, a few rate measurements were made using 4-cm-deep melts. The solidified samples were sliced into discs and each disc was analyzed for oxygen or nitrogen. In another series of experiments, oxygen or nitrogen was diffused into shallow melts (about 0.5 to 1 cm in depth) and the total sample was analyzed to obtain an average concentration of the diffusate. In most experiments, 4- to 5-mm-ID alumina crucibles were used. Some experiments were also made in smaller (3 mm) and larger (7 mm) diam crucibles. This variation in diameter caused no difference in the reaction rate, within the limits of experimental uncertainty. To promote the establishment of a stable density profile in the melt, all the samples were suspended in the lower end of the hot zone so that the top of the melt was hotter by a few degrees. Molybdenum wire resistance heating was used. The reaction tube of the furnace was a gas-tight recrystal-lized alumina tube. In most experiments the furnace was heated by an ac power supply. To check the possibility of inductive stirring, some experiments were carried out in a dc operated furnace, with essentially the same results. The temperature of the furnace was controlled automatically in the usual manner. The temperature was measured with a Pt/Pt-10 pet Rh thermocouple and is estimated to be accurate within ±5°C. The iron used was prepared by melting and vacuum-carbon deoxidizing electrolytic "Plastiron" in a zir-conia crucible. The main impurities are: Si 0.004 pct P, S <0.002 pct Cr 0.005 pct N 0.001 pct Zr 0.002 pct O 0.003 pct Mn 0.004 pct C 0.002 pct The gas composition was controlled by constant pressure head capillary flowmeters. Oxygen was removed from the gas mixture by passing it through columns of platinized asbestos (450°C) and anhydrone. Selected H2O contents were obtained by passing the purified gas through oxalic acid dihydrate-anhydrous oxalic acid mixtures held at constant temperature in a water bath. Water vapor pressure data for the oxalic acid dihydrate-anhydrous oxalic acid equilibrium were taken from the 1iterature.3 The flow rate used was about 1.5 liters per min. The whole system was checked for tightness at regular intervals.

Jan 1, 1968

By E. Eichen, G. S. Ansell. L. R. Sefton

A Technique for the Preparation of Thin Films of Two-Phase Alloys Suitable for Use in Transmission Electron Microscopy In order to obtain foil sufficiently thin to permit transmission electron microscopy of two-phase alloys, particularly alloys in which the second phase is present as a very finely dispersed second phase, a technique has been developed to permit the thinning of these materials without either the large degree of pitting present in the electrochemical or chemical thinning process or the slicing of the second phase particles accompanying the mi-crotoming process. The metal or alloy to be thinned is first ground to initial sheet thickness of approximately 0.002 in. by hand grinding on 4/0 emery paper. This starting sheet of material is then reduced in cross section by an air-abrasion technique using an S. S. White dental abrasive unit. This unit consists of a supply of compressed CO, which provides a stream of high velocity gas impinging on the metal surface. Incorporated in the machine is a hopper-type of device in which fine abrasive particles of alumina are introduced into this high velocity gas stream. The abrasive particles are irregular in shape, approximately 30 across. If any particles are introduced into the sample during thinning, they should be readily observable. Impingement of this gas abrasive mixture on the metal surface causes rapid removal of the metal in a rather uniform manner. The rates of metal removal may be adjusted by both regulating the gas pressure and amount of abrasive material introduced into the gas stream. By moving the gas stream abrasive mixture slowly about the specimen or sheet surface, a large area of the sheet may be uniformly reduced to a thickness which is then suitable for use in transmission electron microscopy. Attendant with this metal removal is a result in cold working of the metal surface due to the impingement of the abrasive particles. The resultant foils, therefore, if made from materials which are desirable to view in the annealed condition, have to be subsequently heat treated. If the alloy from which these foils have been made has been initially heavily worked or deformed during manufacture, then no subsequent heat treatment is, necessary as in the case of the SAP-type alloys. Following this initial abrasive thinning technique, the material is then given a final electropolish which is just sufficient to remove any oxide which has formed on the metal surface during the abrasion technique. Care has to be exercised in this technique to make sure that none of the attendant problems associated with the chemical or electrochemical removal process are encountered. An electrolyte solution which has been found suitable for aluminum-aluminum oxide SAP materials is one containing 78 ml of perchloric acid, 120 ml of distilled water, 700 ml of ethanol, and 100 ml of butylcellosolve. The current density used is 1 amp per sq cm and a polishing time of 3 sec on each side of the foil is used. Extreme care must be used in choosing the current density and time to ensure that just the oxide film on the specimen is removed. Times or current density which are greater than this will lead to perforation of the film due to the removal of the A1,0, particles or a complete loss of the film due to complete solution of the matrix. Once the oxide film is removed the specimens must be kept in alcohol until placed in the microscope to prevent any further oxidation. Fig. 1 shows -an electron micrograph at X28,000 of a thin foil of an aluminum-aluminum oxide SAP-type alloy prepared using this technique. The alloy consists of a matrix of commercial purity aluminum containing a very finely dispersed second phase of aluminum oxide flakes. In the electron micrograph, the dark patches are the aluminum oxide particles. The lighter portions of the micrograph are the aluminum matrix. Within the aluminum matrix, the dislocation structure of the alloy is clearly visible. This structure consists of intersecting twin boundaries and single dislocations. No abrasive particles were observed in the samples. In addition, thin films of commercial purity aluminum were prepared using this method and observed in the electron microscope. Here also, there was no evidence of abrasive particles introduced in the samples. The technique presented provides a satisfactory method for the production of thin films of aluminum-aluminum oxide SAP-type alloys for use in transmission electron microscopy where none of the usual thinning techniques appears to be satisfactory.

Jan 1, 1962

By E. L. Claridge, K. S. Lee

Areal sweep efficiency of oil displacement by enhanced-viscosity water exhibiting pseudoplastic behavior was measured in a Hele-Shaw model representing one-quarter of a five-spot pattern. The pseudoplasticity of polymer solutions and the velocity distribution in the five-spot pattern produced a condition under which the mobility ratio between the displacing and the displaced fluid could not be assigned a single value. Instead, the movement of the displacement front is governed by local mobility ratios which are also time dependent. The areal sweep at breakthrough with polymer solutions was poorer than the sweep obtained with Newtonian fluids of comparable viscosity. However, the areal sweep at 1 PV throughput was greatly improved as compared to flood water without polymer. It was also demonstrated that, even after the oil-cut had declined to a low value during a regular waterflood, switching to polymer flood efficiently swept out the oil remaining in the model. INTRODUCTION The behavior of fluid displacements in isotropic porous media for various patterns of injection and production wells has been extensively investigated.1-7 These investigations all concerned Newtonian fluids, i.e., the viscosity of each fluid was constant regardless of flow rate. The generally unfavorable influence on areal sweep efficiency of higher mobility of the displacing fluid as compared to the mobility of the displaced fluid has been established for both miscible and immiscible fluids. The principle was also established that a close correspondence exists between miscible and immiscible flood front behavior,2, 3 although oil recovery in a waterflood at unfavorable mobility ratio may be less than that observed in a miscible displacement at the same mobility ratio. This is true even when oil recovery is expressed on the basis of movable oil. The reason is that oil saturation only slowly achieves its final value behind the water-flood front in accordance with the Buckley-Leverett8 simultaneous flow relations. It is convenient to use miscible displacements for laboratory simulation of waterflood frontal advance since the interfacial tension forces which are negligible in proportion to viscous forces on a reservoir scale9 are thus made nonoperative in the laboratory model. For miscible displacements, the Hele-Shaw type of model adequately represents a porous medium so long as the appropriate scaling rules5-10 are observed in its design and operation. During simulation of waterflood front behavior in the laboratory by using miscible displacements, the behavior of connate water may ordinarily be disregarded since it is usually indistinguishable from flood water in this process. However, when the flood water is deliberately thickened to improve the mobility ratio between water and oil. the effect on the sweep efficiency due to generation of a connate water bank during the process must be considered. In a uniform porous medium, such a bank is generated11 and efficiently displaced by injection of thickened water.l2 The oil originally in-place at the start of the waterflood is then displaced by connate water followed by thickened water. If the flood water must be thickened to obtain a favorable mobility ratio, the mobility of the oil phase is appreciably less than that of the connate water. Hence, the oil phase is inefficiently displaced by the connate water bank, and a considerable proportion of the oil comes in contact with and is displaced by the thickened waterflood front&apos; A recent study 12 of five-spot displacements using miscible Newtonian fluids in which connate water banks of various sizes were simulated shows that, for connate water banks as large as 40 percent of 1 PV, major improvements in sweep efficiency resulted from use of a thickened

Jan 1, 1969

By R. E. Ogilvie, A. R. Kaufmann, S. H. Gelles

The solid-solubility limits of iron in beryllium were determined between 850o and 1200oC by analysis of differential type multiphase diffusion couples, using an X-ray absorption technique. The maximum value of the solubility limit was found to be 0.92 ± 0.02 at. pct (5.46 wt pet) at the eutectic temperature 1225°C. The solubilities of nickel and beryllium were determined between 900°and 1200°C by the same technique and the maximum solubility was found to be 4.93 + 0.01 at. pct (25.2 wt pet) at the eutectoid temperature, 1065°C. A previously unreported high-temperature phase which decomposes eutectoidally at 1065 °C was found to exist in the beryllium-nickel system at a composition of approximately 8 at. pct Ni (36 wt pet) by diffision-couple analysis. The presence of this phase was confirmed by thermal analysis and metallo-graphic analysis of the structure resulting from the eutectoid decomposition. G. V. Raynor1 has treated the solid solubilities of some of the elements in beryllium on the basis of the "Hume-Rothery" rules2 which have been modified to include ionic size and ionic distortion effects. It was predicted that the solubility of iron and nickel in beryllium should be slightly less than that of copper. The lowering of the solubility, according to Raynor, is due to a more unfavorable relative valency effect and an ionic size effect. Kaufmann and corzine3 have compiled data on the solubilities of elements in beryllium and have discussed them in the light of the Raynor paper. These authors feel that, because the elements having the greatest solubility in beryllium systematically fall in the Group VIII and IB Columns of the periodic table, the electronic structure greatly influences the maximum solid solubility of elements in beryllium. The solubility of iron in beryllium was determined by Teitel and cohen4 as part of the study of the beryllium-iron phase diagram. The determination was carried out by X-ray and thermal analysis and according to the phase diagram presented, the maximum solubility of iron in beryllium is 0.41 at. pct (2.5 wt pct) at 1225oC. However, it is estimated that the uncertainty in the position of the a-beryllium primary solid-solution boundary is about 0.5 at. pct (3wtpct). Losana and Goria3 in studying the beryllium-nickel phase diagram, determined the solid solubility of nickel in beryllium by thermal analysis. They found the maximum solubility to be between 1.65 and 2.65 at. pct (10 to 15 wt pct) at 1240°C. This value decreased rapidly with decreasing temperature. In determining approximate ranges of solubilities for different elements in beryllium, Kaufmann, et al,8 reported a value of between 1.3 and 1.7 at. pct (7.9 to 10.1 wt pct) for the solubility of nickel in beryllium. The value was obtained by metallographic examination of quenched alloys and lattice-parameter measurements. However, the authors also noted a single-phase structure for a 1.7 at. pct Ni alloy (10 wt pct) on cooling from the liquid. This would indicate a higher solubility range than was reported. ~isch,&apos; in his X-ray studies of beryllium-copper, beryllium-nickel, and beryllium-iron intermetallic compounds, reports the disappearance of a second phase (Ni,Be2) in the beryllium primary solid solution at approximately 4 at. pct (20 wt pct). THEORY The analysis of concentration gradients in diffusion couples has proven to be a useful tool in determining phase equilibria.8-14 In this particular study the diffusion couples were chosen to straddle the expected composition range of the phase boundary, then heat treated at a given temperature and the concentration gradient evaluated. The composition of the phase boundary for a given temperature appears at a point of discontinuity of the composition gradient. Examples of typical phase diagrams and the concentration gradients which should be found in such systems are shown in Fig. 1. In the present work, gradients of the form of Fig. l(c) were obtained in diffusion couples made of pure beryllium and two-phase alloys of beryllium with either iron or nickel. The composition at the point where the gradient becomes discontinuous, Cs, corresponds to the solubility limit of either iron or nickel in beryllium. The analysis of the concentration gradients was carried out by an X-ra absorption method developed and applied by Ogilvie and later used by Moll13 and Hilliard.l4 It depends on the fact that the absorption of X-rays by matter is determined by the concentration and type of the various atomic species present. The relationship for the intensity, I, of a monochro-

Jan 1, 1960

By K. P. Mukherjee, K. P. Gupta, J. Bandyopadhyaya

Even though a lot of work has been done in the past to establish phase equilibrium in the Cu-Si system a re cent investigation casts some doubt about the existence and crystal structure of some of the phases that form in the composition range of 15 to 25 at. pct Si in Cu. The present investigation was carried out using high temperature X-ray diffraction technique along with other standard techniques to study the phases in this composition range. The high temperature 6 phase appears to be tetragonal with parameters a,, = 8.815A, c, = 7.903A, and co/ao = 0.896. The reported bcc E phase exists at room temperature and at least up to 780°C and appears to undergo a transformation near 600°C. The phase appears to be cubic but not of the bcc type. The ? phase appears to undergo a transformation, as has been indicated by earlier investigators, and the low temperature form of .? phase is tetragonal with parameters a, = 7.267A, co = 7.8924, and co/ao = 1.086. THE Cu-Si binary system has been investigated by several investigators1" and several intermediate phases,?,e,?&apos; at lower temperatures and ?,ß,0,e, and ? at higher temperatures, were observed between terminal solid solutions of copper and silicon. Even though the existence of the e phase and the transformation in the ? phase were reported in many early works, in a recent study of this system Nowotny and Bittner6 doubted the existence of the e phase and phase at 550°C. Among the high temperature phases, the 6 phase was reported to have a complex cubic structure with parameter a, = 8.805A.7 Nowotny and Bittner, however, suggested that the structure of the 6 phase might be of CsCl type. In order to check these contradictory reports the present study was taken up to investigate the Cu-Si binary system in the composition range of 17 to 25 at. pct Si. EXPERIMENTAL PROCEDURE Weighed amounts of copper (99.99 pct) and silicon (99.9 pct) were induction melted in recrystallized alumina crucibles under argon gas atmosphere. The alloys containing 17, 18, 20, 21, 21.2, 22, and 24 at. pct Si were annealed in evacuated and sealed quartz capsules at 700°C for 3 days and subsequently water quenched. Other than this annealing, the 21.2 at. pct Si and 24 at. pct Si alloys were annealed at 550°C for 10 days, the 17 at. pct Si alloy was annealed at 750°C for 3 days, and the 22 and 24 at. pct Si alloys were annealed at 780°C for 2 days. All annealing temperatures were controlled to within *l°C. Alloys after quenching were subjected to metallographic and X-ray diffraction investigation. A solution containing 5 g FeC13 + 10 cc HCl + 120 cc H2O diluted with six times its volume with water was used as etching reagent. A 114.6 mm diam Debye Scherrer camera was used for obtaining diffraction patterns. The 17, 21.2, and 24 at. pct Si alloys were subjected to high temperature diffractometry using a Tempress Research High temperature attachment and a GEXRD VI diffractometer. For the 6 phase (17 at. pct Si alloy) powder specimen from a 750°C annealed alloy was reheated to 750°C in the high temperature attachment for 1½ hr before taking a diffraction trace. A 550°C annealed and slowly cooled phase (24 at. pct Si) alloy was first reheated to 550°C. a diffraction trace was made after annealing it for 2 hr, and subsequently it was heated to 716OC and kept at this temperature for 2 hr before taking a diffraction trace. For the e phase (21.2 at. pct Si alloy) a 550°C annealed and slowly cooled specimen was heated first to 425°C and annealed at this temperature for 2 hr before taking a diffraction trace. Subsequently, the specimen temperature was raised to 495", 540°, 603", 635", 682", 720°, and 748°C and homogenized at each temperature for 1 hr before taking diffraction traces. The powder specimen temperature was controlled to within +2oC at each temperature and argon gas, purified by passing it at slow rate through a fused CaC12 column, hot (800°C) copper and titanium chips and finally through a P2O5 column, was used to prevent oxidation of the powder. For all X-ray work copper-radiations at 25 kv, 15 ma (for Debye Scherrer technique), and 40 kv, 20 ma (for diffractometer tech-nique) were used. RESULTS AND DISCUSSION At 700°C the alloys containing 17 to 21 at. pct Si showed two phases while the 21.2 at. pct Si alloy was found to be single phase. The X-ray diffraction patterns of the two-phase alloys were consistent with the phase (ßP-Mn type structure) and the phase (21.2 at. pct Si) patterns. The diffraction patterns of the 17 at. pct Si alloy quenched from 750" and 700°C were identical. According to the accepted Cu-Si phase dia-gram4,5,10 the 17 at. pct Si alloy at 750°C should be in the (k + 6) two-phase region and very close to the -phase boundary. The identical patterns possibly resulted from the decomposition of the 6 phase on

Jan 1, 1970

By Rex O. McLellan

The formation of a monovacancy in a metal is simulated in an elastic model by the displacement of the surface of a small spherical cavity in a large elastic continuum. The application of linear elasticity to this distortion results in a well- known formula for the energy and an expression for the concomitant entropy change due both to the shear strain in the continuum and also to the dilation of the solid resulting from the boundary conditions at the surface of the solid. Elastic data (the sliear modulus and its temperature coelficient) are used to calculate the entropy and energy of formation for many metals. Despite the simplicity of the assumptions involved, the agreement between the calculated entropies and energies and experimental values is remarkably good. In recent years there has been a large increase in measurements of the absolute concentration of mono-vacancies in metals as a function of temperature. Hence new data for both the energy and the noncon-figurational entropy of formation of monovacancies has become available. Recent measurements&apos; of the anomalous (non-Arrhenius) self-diffusion in many bcc metals has also focused interest on the prediction of the thermodynamic parameters of mono- and multi-vacancies in those metals for which no data are available. Damask and Dienes&apos; have discussed the various theoretical calculations of the energy of formation EL, of a monovacancy. These include simple models involving the breaking of atomic bonds on moving atoms from the interior of a crystal to the surface, models combining elastic calculations with surface-energy terms and detailed quantum mechanical calculations. The simler models give the correct order of magnitude of &, but tend to overestimate it by a factor of about two. The quantum mechanical calculations4"7 have been carried out for the noble and alkali metals with generally reasonably good agreement with the available Ef data. The calculation of entropy of formation Sfv14 lnvolves a fundamental calculation of the perturbation of the phonon spectrum caused by the creation of a vacancy. Huntington, Shirn. and wajda8 have given an approximate evaluation of sJV by considering an Einstein model for the localized vibrations in the immediate neighborhood of the defect and then using elastic theory to calculate the entropy associated with the shear stress field in the distorted crystal (as originally proposed by Zenerg). They also included a term due to the dilation of the crystal. They obtained a value of 1.47k for copper, in good agreement with the experimental value (1.50k). However, Nardelli and Tetta- manzi1° have recently shown that neglecting the coupling between atoms (Einstein Model) may lead to a serious error so the agreement may be somewhat fortuitous. In this work simple linear elastic theory is used to calculate the entropy and energy of formation of mono-vacancies. Despite the simplicity of some of the assumptions involved, the agreement with the available experimental data is remarkable. However. the reasonable degree of success in the application of linear elastic calculations to the excess entropy of a solute atom in a dilute solid solution1&apos; indicates that the application of elastic theory to vacancies. where the interaction of different atomic species is not involved, may not be inappropriate. THE ELASTIC MODEL The metal is assumed to be a spherical elastic continuum. A small spherical cavity of volume V = 4i;v:&apos;/3 is cut from the center. removed. and dissolved rever-sibly in the bulk of the material. TO a good approximation no net atomic bonds are broken and the material does not undergo a volume change although the externally measured volume of the body would increase by V. The radius of the sphere of metal is much larger than r Next a negative pressure is applied to the cavity causing its surface to be displaced inward by an amount simulating the relaxation of the lattice around a monovacancy. In this model the energy and entropy accompanying the distortion are taken as 4, and <. As a first approximation the equation of state for the solid is taken as: r = ro(i + *~D LiJ where K is the bulk modulus. P the hydrostatic pressure. Vo the volume of the material at 0°K and zero pressure. and d+/dT = 30. where 0 is the linear thermal expansion coefficient. The variation of entropy with hydrostatic pressure is given by the Maxwell equation: These equations give the entropy change resulting from increasing the hydrostatic pressure from 0 to P as: and since • we have: This is the entropy arising from the dilation resulting

Jan 1, 1970

By M. J. Marcinkowski, D. B. Crittenden, A. S. Sastri

A study co.mbining stress-strain .measurements in conjunction with transmission electron microscoPy has been made with near equiatomic Fe-Cr alloys which were aged for various times at 500°C. Associated with this aging is a marked increase in deformation twinning. The outstanding feature of these twins is that they generate stress fields sufficiently great so as to give rise to spontaneous dislocation loop nucleation nearly normal to the propagating twin. This observation is in agreement with the theoretically predicted elongation of the stress field of a dislocation Perpendicular to its direction of motion as it moves near the speed of sound. Dislocation loop nucleation is more difficult in the longer aged alloys so that this energy absorption mechanism is not effective in hindering twin propagation. Since crack nucleation can readily occur near the tip of a twin, the aged alloys become extremely brittle when deformed in tension. Iron-chromium alloys in the vicinity of the equiatomic compositions become severely embrittled when aged at about 500°C. Fisher et 01.&apos; have shown that this embrittlement is related to the decomposition of the original random Fe-Cr solid solution into a chromium-rich and an iron-rich phase. In addition, Mar-cinkowski et a1.&apos; have shown that twinning becomes an increasingly more important mode of deformation as the aging time is increased. These results have been recently corroborated by the transmission electron microscopy study of Mima and amauchi . The Fe-Cr alloy thus seems ideal for verifying the predictions made in Parts I4 and 115 of this investigation where the behavior of large static or blocked twins and those of large dynamic or propagating twins, respectively, were investigated numerically. It was thus decided to measure the stress-strain curves generated by embrittled alloys that were aged for various times and to examine sections by transmission electron microscopy. EXPERIMENTAL PROCEDURE Electrolytic iron and electrolytic chromium were vacuum-melted and poured into ingot form. The composition of the resulting alloy was found to contain 46.0 wt pct Cr (47.8 at. pct), the remainder being iron. The resulting ingot was swaged above 850°C into 0.250-and 0.400-in.-diam rounds. Compression samples of 0.250 in. diam and 0.400 in. long were cut from the smaller-diameter rounds. These samples were then sealed in evacuated quartz tubes and annealed for 30 min at 1150°C to produce a uniform and equiaxed grain size of mean diameter equal to 1.73 mm. They in turn were rapidly quenched from 850°C so as to preserve the condition of random solid-solution characteristic of the elevated temperature. The samples were then aged for various times up to 300 hr at 500°C in a massive Pb-Bi alloy bath. The samples were next polished and tested in compression at room temperature as described in Ref. 6 using an Instron tensile testing machine. The strain rate used was 0.05 in. per in. per min. The remaining larger round was converted into compression specimens of 0.325 in. diam and 0.500 in. long. This larger diameter enabled wafers of sufficient size to be prepared for examination by trans-mission electron microscopy techniques after subjecting them to a suitable strain. Foil preparation is described in some detail in Ref. 6. All foils were examined in a type HU-11A Hitachi electron microscope operating at 100 kv. RESULTS AND DISCUSSION Fig. 1 shows the effect of aging at 500°C on the room-temperature stress-strain curves of the FeCr alloys. For greater clarity the origin of each curve has been displaced upward. The same origin has been used for both the 0 and the 0.1 curves. It is apparent that with increased aging times a sharp drop in load is observed at the yield stress which becomes more pronounced as aging proceeds. A loud sonic burst accompanies this drop and subsequent metallographic examination shows the sample to contain numerous twins. For intermediate aging times, a number of smaller twin bursts follow the initial large one. The total plastic strain associated with the twinning mode of deformation can be obtained by adding up the contributions AE~ from all i twin bursts, i.e., £,¦££,-, in the manner illustrated schematically in Fig. 2. The contraction of the specimen, as measured from the strip chart of the Instron, after suitably correcting for the elasticity of the machine, was converted into true strain using the assumption that there was no volume change and that the sample remained cylindrical. The dashed lines are all drawn parallel to the

Jan 1, 1970

By John W. Cahn, David A. Karlyn, Morris Cohen

The massive B(bcc) — am (fcc) transformation in Cu-Zn alloys has been studied isothermally by pulse-heating the retained ß phase from room temperature to the reaction temperatures. The transformation is found to occur only in the single-phase a region of the equilibrium diagram. The massive growth rate is of the order of 1 cm per sec and is constant at each temperature, usually after a delay time of some milliseconds. The delay time depends on the reaction temperature in C-curve fashion, while the growth rate increases monotonically with temperature over the single-phase range. The absence of isothermal massive transformation in the two-phase region does not arise from slow growth rates at such temperatures, but because the reaction cannot get started there. It is proposed that the massive transjormation initiates at small preexisting a particles which have rejected zinc into the surrounding 0 matrix. Only within the single-phase region can these particles consume the excess zinc during diffusion-controlled growth and thereby accelerate to the steady-state massive growth rate. The onset of massive growth marks the end of the delay time, and the growth rate then becomes interface-controlled. These isothermal transformation characteristics explain why the usual composition range for massive-kinetic studies by quenching is so limited. The same principles can be extended to more complex alloy systems by recognizing that the single-phase region in which the massive transformation can occur may not be stable with respect to phases not participating in the reaction. MASSWE transformations are now recognized as a regular class of solid-state reactions involving no compositional change (like martensitic transformations) and no shear displacements (unlike martensitic transformations). The name was first coined by Greninger1 in 1939 to describe the coarse grains of fcc a solid solution generated via a fast reaction from the parent bcc 0 solid solution in Cu-A1 alloys. However, some 9 years earlier, phillips2 had already described a similar transformation in the Cu-Zn system. The fact that the massive a formed as a single phase during drastic quenching from the 0 region of the equilibrium diagram signified that compositional changes were precluded. and the reaction was presumed to take place as in a one-component polymorphic transition by nucleation and growth. Phillips also observed that the occurrence of the massive transformation in the Cu-Zn system was extremely sensitive to alloy composition. For example. in a Cu-37.3 at. pct Zn alloy. the ß — am (am = massive transformation product) reaction was found to predominate and was not suppressed by iced-brine quenching from the 0 region. whereas at compositions greater than 38.3 at. pct Zn the massive reaction did not appear at all. Knowledge concerning massive transformations has bee11 substantially enhanced over the years by Massalski and his coworkers; an excellent summary of his papers and the current understanding of this type of reaction has been published recently by Barrett and ~assalski." he massive transformation product grows in roughly nodular form. often with irregular boundaries but sometimes with almost planar interfaces. The latter may have simple crys-tallographic indices relative to the 0 matrix. or the indices may be complex just as in the case of mar-tensites.&apos;1 Little is known about the existence of orientation relationships between the massive and parent phases. A striking feature of massive transformations is that the massive units start almost exclusively at grain boundaries of the parent phase and frequently propagate on a broad front across matrix grains and grain boundaries of various orientations. Because of the rapid growth rate, it is thought that the interface motion is controlled. not by long-range diffusion. but by thermally activated atom jumps across the transformation boundary.

Jan 1, 1970

The negative charges on diaphragms of quartz, tungstic oxides, stannic acid, acid dyestuffs, soaps, and glass have for a number of years been explained on the basis of chemical equilibria-a hydrogen ion or light metal ion passes into solution leaving the solid complex ion negatively charged. While there are a number of observations which indicate a proportionality between the ( potential and the streaming potential it should be recognized that all the experimental evidence thus far presented shows that if hydrogen ion concentration is kept at a constant value, electrokinetic phenomena are influenced by salts. The multivalent ions exert the greatest effect on the reduction of osmotic flow. In the interpretation of all electrokinetic data the assumption is made that the potential of the solid remains constant. That this is not true is evidenced by the values of ( potential for quartz in contact with conductivity water as reported by the several investigators and by the authors of this paper.

Sep 1, 1956

By R. H. Richman, F. Borik

A 0.3 pct C-12 pct Cr-6 pct Ni steel was rolled to 93 pct reduclion in area as austenite at 510°C, and then partially transformed as desired to ~rlartensite by qnenching to - 196°C. Pole figures for the austenitic matrix and for the martensitic product were separately determined by an X-ray transmission method. The deforitration texture of&apos; the warm-worked austenite is characlerized by (110)(225) components, and is thus closely similar to those produced in a brasses. The pole jigure of the martensite in partially transformed material agrees well with that which can be constructed by transfortnation of the {110)(225) orientations according to either the Kuvdjuniov- Sacks or the Nishi-yatuu relatiotship. Howeuer, an important result of this construction is that me-third of the predicted orientations are missing. A graphical analysis can then be used to show that in deformed austenite certain crystallographic variants of martensite (related to the most probable austenite slip systems) are suppressed, resulting in this preferred transformation. The evidence for preferred transformation is corroborated by the measured elastic anisotropy of warm-rolled and fully transformed H-11 steel. EXTENSIVE plastic deformation of a polycrystal-line aggregate in a manner that causes flow predominantly in one direction results in a preferred orientation of the constituent crystallites. The particular orientations that are produced depend upon the crystal structure and composition of the material, as well as upon the temperature, mode, and degree of deformation; in any case, the preferred crystallo-graphic orientations, or textures, are reflected in directionality of mechanical properties. Although such anisotropy may be exploited in certain specialized applications, it is more commonly diminished or eliminated by heat treatment lest it interfere undesirably in subsequent forming operations or in structural design. In the recently developed thermomechanical treatments that significantly enhance the strength of some steels,1,2 considerable deformation of the metastable austenite prior to the martensite transformation is essential to the strengthening process. If the austenite is textured by the deformation, and if the transformation to martensite proceeds according to one of the relationships established for transformation in annealed austenite, then it must be expected that the martensite will also possess a preferred orientation even though the multiplicity of martensite orientations possible in a given austen- ite crystal will tend to restore some degree of randomness. The existence of a residual anisotropy, both mechanical 3-6 and crystallographic,&apos; has been substantiated. In the latter crystallographic investigation, preferred orientations were determined for the martensitic structure of an SAE 4340 steel rolled 72 pct as austenite at 833°C and then quenched. However, the choice of a composition that transformed almost completely to martensite during the quench to room temperature did not permit direct measurement of the prior austenitic texture. In fact, when the "ideal orientations&apos;&apos; associated with well-known fcc rolling textures were converted, alone or in combination, to martensite according to the Kur-djumov-Sachs (K-s)&apos; or Nishiyama8 relations, the agreement obtained with the observed martensite texture was only fair at best. Recently a pertinent aspect of the austenite to martensite transformation was reported by Bokros and parker,10 who found that certain habit-plane variants of martensite were suppressed by tensile deformation of Fe-31.7 Ni single crystals prior to the necessary subzero cooling. It might be anticipated that the consequences of such preferred transformation are sustained during the formation of martensite in warm-worked austenite that has a well-developed deformation texture. The present investigation was undertaken first to establish more firmly the relation between preferred orientations in plastically deformed austenite and in the resulting martensite, and second to examine the textures for evidence of deformation-induced preferred transformation. EXPERIMENTAL PROCEDURES An alloy containing 0.3 pct C, 12 pct Cr, 6 pct Ni, and the balance iron, was selected because the mar-tensite-start temperature (M,) of about -100°C allowed convenient experimental manipulation of either austenite or martensite at room temperature. Furthermore, this composition can be readily deformed as metastable austenite at moderately elevated temperatures without intervention of appreciable isothermal or athermal decomposition products. The alloy was austenitized at 1150°C, aircooled to 510°C, rolled unidirectionally at this temperature to 93 pct reduction of cross-sectional area, and finally oil-quenched to room temperature. Partial transformation to martensite was accomplished by quenching to -196°C as needed. The rolled stock was reduced in thickness from 0.067 to 0.010 in. by etching in a solution of 5 pct HC1, 45 pct HNO3, and 50 pct water, and further thinned by careful mechanical polishing to maintain the two sides of the sheet parallel within 0.0003 in. After mechanical polishing to 0.005 in., electropolishing in 1:9 perchloric-acetic acid solution produced a final thickness of 0.002 in. The preferred orientations were determined from

Jan 1, 1968

By R. A. Vandermeer, J. C. Ogle

The preferred crystallographic orientations (texture) developed in randomly oriented, poly crystalline niobium during rolling were studied by means of X-ray diflraction techniques. The evolution of texture at both the surface and center regions of the rolled strip was carefully examined as a function of increasing defamation throughout the range 43 to 99.5 pct reduction in thickness. Certain aspects of the center texture development in niobium are in agreement with the predictions of a theory by Dillamore and Roberts, but others cannot be explained by the theory in its present form. Above 87 pct reduction by rolling, a distinctly different texture appeared in the surface layers which was unlike the center texture. The present results are compared with previous results obtained from other bcc metals and alloys. RANDOMLY oriented, poly crystalline metal aggregates when plastically deformed to a sufficiently large extent develop preferred orientations or textures. In a recent review article, Dillamore and Roberts1 pointed out that the nature of the developed texture may be influenced by a large number of variables. These include both material variables such as crystal structure and composition and treatment variables such as stress system, amount of deformation, deformation temperature, strain rate, prior thermal-mechanical history, and so forth. From a practical point of view, the control of preferred orientation may often be important for the successful fabrication of metals into usable components. During the past few decades many experiments have been devoted to the study of deformation textures. This work, however, has been confined in large part to metals and alloys that have an fcc crystal lattice. By comparison, bcc metals and alloys have received much less attention, and consequently our understanding of preferred orientations in these materials is only shallow. This state of affairs worsens when it is realized that almost all of our present howledge about this class of materials derives from studies on irons and steels.&apos; The bcc refractory metals, which are relative newcomers to the industrial world, have, on the other hand, been given at best only passing glances in the area of texture development. Our understanding of the evolution of preferred orientations in bcc metals can only remain fairly limited until systematic studies of metals and alloys other than the irons and steels have been carried out and the influence of the many variables has been determined. To that end a program was initiated to investigate in detail texture development in niobium. The present paper reports some of the results of this study. Textures were determined at both the center and surface of strips rolled variously to as much as 99.5 pct reduction in thickness at subzero temperatures. Emphasis in this paper is on texture description and on texture evolution during rolling to progressively heavier deformation. EXPERIMENTAL PROCEDURE The niobium was purchased from the Wah Chang Corp. as a 3-in.-diam electron-beam-melted billet. Chemical analysis indicated the impurities to be less than 300 ppm Ta, 40 ppm C, 10 ppm H, 170 ppm 0, and 110 ppm N. All other impurities were below the limits of detection by spectrochemical analysis. This large-grained billet was fabricated into specimen stock so that a fine-grained randomly oriented grain structure resulted. This was accomplished in three deformation steps alternated with recrystalli-zation anneals of 1 hr at 1200°C in a vacuum of low 10"6 Torr range after each deformation step. The first step was to alternately compress the billet 10 to 20 pct in each of three orthogonal directions. The second step was to compress in only two directions 90 deg apart to produce a 2-in.-sq bar. The final step was to roll this bar 50 pct to give a 1-in. by 2-in. cross section. After the final anneal, metallo-graphic examination showed the material to have an average grain size equivalent to ASTM No. 5 at 100 times (i.e., 0.065 in. diam). Specimens cut from the center and edges of this bar gave no indication of detectable preferred orientation when examined by X-ray diffraction. Samples 1.5 in. long, either 0.625 or 0.750 in. wide, and approximately 0.400 in. thick were machined from this fabricated ingot. The surfaces corresponding to the rolling planes were ground so as to be parallel. The samples were chemically polished in a solution of 60 pct nitric acid and 40 pct hydrofluoric acid (48 pct solution) prior to rolling to remove any cold work introduced in the machining operations. Rolling was accomplished with a 2-high hand-operated laboratory rolling mill that had 2.72-in.-diam rolls. Prior to operation, the rolls were polished with 600 grit paper, cleaned with acetone, and then soaked in a container of liquid nitrogen for several hours. The samples were also soaked in liquid nitrogen prior to rolling and were recooled between each pass. While some slight heating of the samples occurred during rolling, this procedure maintained the sample temperature well below 0°C at all times. The samples were rolled unidirectionally, and the rolling plane surfaces were not inverted during any phase of the operation. The draft per pass averaged between 0.010 to 0.012 in. After 96 or 97 pct reduction the draft was reduced to 0.001 to 0.002 in. per pass. Samples were rolled to various reductions in thickness between 43 and 99.5 pct.

Jan 1, 1969

By Curtis Wilson

FROM the results of his investigation of the hardenable copper-nickel-silicon and copper-cobalt-silicon alloys, M. G. Corson1 explained the dispersion-hardening effect by assuming the precipitation of the inter-metallic compounds nickel silicide and cobalt silicide, and on this basis he constructed diagrams for the pseudobinary systems copper-nickel silicide and copper-cobalt silicide. A consideration of these diagrams and of the factors that exert such an important influence upon the rate of precipitation, such as degree of supersaturation, nucleus number and rate of diffusion, leads to the expectation that the rate of precipitation of the silicides on reheating the quenched solid solutions at temperatures below the alpha-phase boundary should increase continuously as the reheating temperature is raised. The present investigation shows that while this rate does increase with the reheating temperature in a general way, it does not do so continuously. Supplements to Corson&apos;s diagrams are offered, showing the discontinuities, and slight modifications in the solubility curves are suggested.

Jan 1, 1933

By B. C. Allen

Grain-boundary gvoocing was studied irz chronziu?n. molybdenum, tungsten, and the solid-solution alloys, Cr-35Re. Mo-33Re, and W-25Re at 0.6 to 0.9 of the absolute liquidus temperature under an inevt atmosphere , foveign nzetal zlapor, and liquid metal. The controlling mechanism of matter transport was deduced frolr groove size and shape. kinetics of growth, and cotnparisoz with theoretical relatiotzships derived by Mullins. Grooves in chowzizon formed prittzarily by volume diffusion tkrongk kelium or argon at 1 atm pressure and by e1)apovation-condensatiotz in a static vacuum. Groozles in the other nzetals and alloys forrned priniarily by sirface diffusion, the coefficients of which were calculated. Carbon was found to decrease the acti7:ation energy for surface diffusion on molybdenun. Sitrface diffusizities weve sinzilav for iWo-0.0ZC and Mo-33Re. The presence of about 1 -?nm pressure of silver or tin vapor did not affect the neckanis)n of grooz;e formation. In liquid titz or silz:er, pain bolindary gvooves formed by zolume diffusion in the liquid. BASED on theories of ullins," the mechanisms of grain-boundary grooving have been determined for low-melting metals such as copper in an inert atmospheres or in liquid lead.4 The purpose of this investigation was to study grain-boundary grooving in the refractory Group VI-A metals, chromium, molybdenum, and tungsten, and the bcc solid-solution alloys, r-35e, 0-33e,= and -25e,&apos; at 0.6 to 0.9 of included to see whether Mullins&apos; theories were applicable to them as well. EXPERIMENTAL WORK The materials chromium, molybdenum, tungsten, Cr-35Re, Mo-33Re, and W-25Re were in the form of 0.050-cm-thick sheet assaying 99.98 pct or better. The nominal carbon level was generally 30 ppm. The oxygen + nitrogen + hydrogen content was -50 ppm. Mo-33Re and W-25Re were prepared by powder-metallurgy methods and supplied by Chase Brass and Copper Co. The remaining materials were arc-cast. Chromium and Cr-35Re were prepared at Battelle by arc melting, extruding, swaging, and rolling. Mo-0.003C was supplied by Climax Molybdenum Co., and Mo-0.02C and tungsten by Universal Cyclops Corp. As a source of liquid metals, tin and silver granules assaying 99.98 pct were used. Spectrographic analyses indicated the presence of -100 ppm each of iron and silicon. Vacuum melting reduced the combined gas content to c5 ppm (2.60,, 0.9N2, 0.4H2 in tin and l.602, 0.7N2, and c0.04H2 in silver). Specimens were prepared for grain-boundary grooving. Coupons 0.5 by 1.5 cm with a small hole in one end, or substrates 1.5 by 1.5 cm, were cut from sheet. The specimens were annealed in containers of the same material to provide a vapor-solid equilibrium as well as to protect them from gaseous impurities. Outgassing was done at 2 x 10"5 mm for 15 to 30 min at 1150°C for chromium and Cr-35Re, 1750°C for molybdenum and Mo-33Re, and 2600°C for tungsten and W-25Re. Then recrystallization to a stable grain size of about 0.5 mm was accomplished by annealing at least 1 hr at 1600°C for chromium, 1800°C for Cr-35Re, 2350°C for molybdenum, and 2300°C for Mo-33Re in a rhenium-element resistance furnace under 1 atm of static argon or helium. The atmosphere was gettered by tantalum radiation shielding. Tungsten and

Jan 1, 1967

By H. E. Cline, J. L. Walter

Grain boundary sliding and migration were studied in pure aluminum bicrystal and polycrystal samples with two-dimensional grain structure. Scratches, 50 P apart, were used for measurement of sliding and migration distanceso. Samples were deformed at constant rate at 315C and events recorded continuously on wrotion picture film. Electron micrograPhs of boundary-scratch intersections were obtained. Yield and flow stress values were measured. The sequence of sliding and migration events for a three-grain junction is described in detail. Sliding depended only on the resolved shear stress imparted to the boundary. Sliding was accowmodated by formation of shear zones in grains opposite triple points and adjacent to curved boundaries. These shear zones provided the driving force for grain boundary migration. Migration caused rumpling of the boundaries, decreasing the sliding rate. Sliding and migration generally began at the same time, occurred simultaneously and ended at the same time. In the bicrystal, sliding and migration rates were proportional. Initial sliding rules of 5 X joe cm per sec. were measured for the polycrystal and bicrystal samples. These sliding rates agree wilh the internal friction experirnents of K;. The observations seem consistent with a viscous boundary sliding nzechanism. GRAIN boundary sliding is the translation of one grain relative to its neighbor by a shear motion along their common boundary. Sliding is thought to be an important mode of deformation at elevated temperatures and at low strain rates such as prevail in creep,&apos; and perhaps in the area of superplastic behavior.2"4 Although much work has been done to investigate grain boundary sliding, the effort has not led to the identification of a mehanism. KG showed that grain boundaries in aluminum exhibit a viscous nature under very small displacements of internal friction measrements. Various dislocation mechanisms have been proposed but are without conclusive experimental support. Attempts to relate sliding to 6&apos;s viscous boundaries have been unsuccessful in that measured rates of sliding are always several orders of magnitude lower than KG&apos;S results would predict.= In bi crystals7and polycrystalsR of aluminum tested under constant load, the grain boundary sliding was found to be proportional to the total creep elongation which indicated that sliding might be controlled by deformation of the grains. Shear zones were observed to extend beyond grain boundaries at triple points to accommodate the sliding.8 Surface observations brought forth the opinion that sliding and migration occurred alternately, in sequence.&apos; Measurements of sliding at the surface have been criticized because they might not be representative of the interior of the sample. Generally speaking, it seemed that much of the previous work and knowledge was based on observations made at relatively low magnification and examination of samples after deformation had been accomplished. Thus, it was the purpose of the present study to continuously record, at high magnification, the events occurring during the deformation of pure aluminum. Samples with two-dimensional grain structures were used to simplify interpretation of the results. The sliding and migration of small areas of many samples were continuously recorded by time-lapse motion pictures. Replicas of the surface were used to provide high-resolution electron micrographs. These observations, coupled with tmsile strength data, provide sufficient information to arrive at an understanding of the phenomenon. EXPERIMENTAL PROCEDURE An ingot of 99.999 pct A1 was rolled to sheet, 0.127-cm thick. Tensile specimens, with a gage length of 0.85 cm, were machined from the sheet. Bicrystal tensile specimens, of the same dimensions, were spark cut from a large bicrystal ingot. The grain boundary was oriented at 45 deg to the tensile axis. The surfaces of the tensile samples were ground flat on fine metallographic paper and were then electropolished in a solution of 75 parts absolute alcohol and 25 parts of perchloric acid. The solution was cooled in an ice-water bath. Using a weighted sewing needle suspended from a small pivot on a precision milling machine, a grid of fine scratches, 50 p apart, was scribed on one surface of the sample. The polycrystalline samples were then annealed in hydrogen for 15 min at 350" to 400°C to produce a two-dimensional grain structure of about 0.2-cm average grain diameter which would not undergo further growth at the test temperature, 315OC. Examination of both surfaces of the samples showed that the grain boundaries were perpendicular to the surface of the polycrystal and bicrystal samples. A hot-stage tensile machine was constructed for use with an optical microscope as shown in Fig. 1. The specimen is shown mounted in the grips. The grips ride in V-ways so that the sample can be mounted without damage. The rear grip is free to slide so that when the sample expands during heating it is not put under a compressive stress. When the grips and samples are at temperature, the rear grip is locked in place by two set-screws. The other grip is connected to a synchronous drive motor which, through a worm gear and a fine-threaded rod, deforms the

Jan 1, 1969

By H. E. Elliott, R. S. Busk, A. T. Peters

One of the problems of the fabricator of metals and alloys is the propensity of some composition rarnges toward abnoermal grain growth during certain stages of fabrication. In this respect magnesium alloys are no exception among alloys. Fortunately, convenient foundry control methods have been developed by which the abnormal grain growth possible in certain magnesium-alloy castings can be suppressed. An unusual characteristic of magnesium alloys, however, is that castings of some composition ranges are subject to local grain growth during heat-treatment without the necessity of intentional mechanical stressing of the part prior to heat-treatment. This effect occurs only under certain critical casting conditions, and only in certain alloys of greater than about 8.5 per cent aluminum content, such as C alloy (Mg, 9 per cent A1, 2 Per cent Zn, 0.2 Per cent Mn) and G alloy (Mg, 10 per cent Al, 0.2 per cent Mn). The first observation of this phenomenon in cast magnesium alloys occasioned much surprise, since it is not observed in other meta1s- Jeffries and Archer1 have stated that "the grain size of cast metals, provided they have not been plastically deformed, cannot be changed by heating below the melting point." The study of the conditions leading to abnormal grain growth in cast magnesium alloys, and of the mechanism of this phenomenon, has led to some very interesting observations. Perhaps the most significant of these was the observation that stresses originating from cooling contraction in magnesium-alloy castings are the only stresses necessary, under certain conditions, to cause local recrystallization and subsequent grain growth in the casting during heat-treatment. Before recent developments, this phenomenon of abnormal local grain growth Was a definite problem in the production foundry on C alloy sand castings. Illustrated (Fig. I) is a picture of a casting scrapped because of this defect. A mottled effect is produced in coarse-grained areas by suitable etching solutions. The properties of metal in the affected area are much impaired by such grain coarsening. Ultimate tensile strengths of half the normal value have been measured in metal of this nature. In this paper are described the techniques that have been developed by The DOW Chemical Co. for studying, and in large measure solving, this production problem. Also discussed are studies of the mechanism by which excessive grain coarsening occurs, and the fundamental conditions that produce this effect. The abnormal grain growth discussed in this paper will be referred to as "germinasium since this term has been definedl as any process leading to an abnormally coarse grain size. This paper deals only with abnormal local grain growth that may occur during the solution heat-treatment of certain magnesium-alloy castings, as dis-

Jan 1, 1945

By Peter R. Morris

The effecl of preferred orienlation on X-vay dzffvaction measurements of retained austenzte was investigated for four precipitation-hardening staznless steels in sheet form. A method is preserzted for estimating the ervor in measurement associated with a given samplirig direction. The method was used to select an "optimum" sampling direclion in order to minimize errors in measurement due to preferred orientation. hleasuremenls of retained austenite content employing lhe proposed sampling direction are conzpaved to measuretnents enzploying the more commonly used normal direclion for a series of sawzples. THE first application of X-ray diffraction to the measurement of retained austenite in steels is due to Sekito, 1 who employed a photographic technique in which the (111) reflection from a thin strip of gold affixed to a cylindrical sample was employed as a standard. Averbach 2 introduced the "direct comparison" method in which the ratios of observed to calculated random intensity are assumed proportional to the austenite and/or martensite contents. Averbach&apos;s work forms the basis of most subsequent X-ray diffraction methods for the determination of retained austenite. Subsequent improvements are due to: Averbach and Cohen,3 who employed a sodium chloride crystal to monochromate cobalt radiation; Averbach et a1.,4 who introduced a bent sodium chloride monochromator; Mager,&apos; who used a bent quartz crystal to monochromate chromium radiation ; Littmam, who first used a geiger counter diffractometer for this purpose; Beu and Beu and Koistinen, 11,12 who studied effects of absorption factor, surface preparation, sample geometry, integrated intensity vs peak height, choice of radiation, monochromator, and filter. The possibility of errors in measured values due to orientation effects was noted by Miller,13 who suggested examination of a surface other than the plane of rolling. Lopata and Kula 14 have developed an experimental technique in which the preferred orientation is measured in each sample. They illustrated the method for a sample containing 42 pct retained austenite. Application of their technique to the 1 to 15 pct range typical for the precipitation-hardening stainless steels does not appear feasible. EXPERIMENTAL PROCEDURE The nominal compositions of the precipitation-hardening stainless steels investigated are listed in Table I. Ingots were solution-treated, hot-rolled to approximately 0.2 in., and reduced to 0.050 in. by a suc- cession of cold rolling and annealing operations. After this treatment the 17-4PH sample was in the marten-sitic condition, while the 17-7PH, PH 14-8Mo, and PH 15-7Mo samples were in the austenitic condition. Samples of 17-7PH and PH 15-7Mo steels in the mar-tensitic condition were obtained by heating to 1750&apos;F for 10 min and holding at -100°F for 8 hr. A sample of PH 14-8Mo steel in the martensitic condition was obtained by heating to 1700°F for 1 hr and holding at -100°F for 8 hr, followed by aging at 950" for 1 hr. POLE FIGURE DETERMINATIONS Samples were thinned to 0.003 to 0.005 in. by etching in a solution containing 250 ml reagent-grade phosphoric acid (85 to 87 pct H3PO4), 250 ml technical-grade hydrogen peroxide (30 to 35 pct H 2 O 2), and 50 to 100 ml reagent-grade hydrochloric acid (37 to 38 pct HCl). The specimens were placed in an "integrating" sample holder which provided a 1-in. oscillation in the plane of the sample. The diffractometer was aligned to measure the intensity diffracted by planes of the particular {hkl} type being studied. The sample was Set for a given latitude angle, a, measured from the plane of the sheet, and diffracted intensity recorded as the longitude angle, 0, measured in the plane of the sheet from the rolling direction, was increased from 0 to 360 deg. After a 360-deg scan of B, a was incremented by 5 deg, and the process repeated. Random standards obtained by spraying suspensions of powdered iron (bcc structure) and nickel (fcc structure) in lacquer were used to correct observed intensities for absorption and geometrical effects. Zirconium-filtered molybdenum radiation was used to determine the transmission regions of the (111) (0to 45 deg), (200) (0 to 60 deg), and (220) (0 to 45 deg) austenite and (110) (0 to 45 deg), (200) (0 to 50 deg), and (211) (0 to 35 deg) martensite pole figures. Vanadium-filtered chromium radiation was used to

Jan 1, 1968