By F. L. Mentg

The utilization of acid leaching tailings was studied. It is obvious that the Fe in acid leaching tailings can be leached into solutions as Fe2+. In this paper, the influence of conditions, including the concentration of ferrous sulfate, pH, temperature and velocity of air flow was investigated. The optimum conditions for preparing seed crystal are as follows: the concentration of ferrous sulfate is 20 g/L; pH is 9.5~10; reaction temperature is 10~20?; velocity of air flow is 0.4m3/h. The optimum conditions for preparing iron oxide red are as follows: the concentration of ferrous sulfate is 5 g/L; reaction temperature is 80~85?; velocity of air flow is 0.13m3/h. At last, the product of iron oxide red could be prepared by ammonia method.

Jan 1, 2014

By Jacob Masliyah, Zhenghe Xu, Lujie Yan

"Understanding adsorption mechanism of polymeric organic process modifierssuch as carboxymethyl cellulose (CMC) on talc hasbeen a major challenge due to anisotropic nature of talc basal planes and edge surfaces. The main objective of this study is to investigate the adsorption of CMC on the basal planes and edge surfaces of talc.Smooth basal plane and edge surfaces of talc were prepared successfully by simple cleavage and sophisticated ultramicrotome cutting method, respectively. The prepared surfaces were characterized by atomic force microscope (AFM) imaging to be sufficiently smooth for colloidal probe force measurements using AFM. Anisotropic surface charge characteristics were determined,with the basal planes to carry a permanent negative surface charge and edge surfaces featuring a pH-dependent charge characteristic. The adsorption of CMC on talc basal plane and edge surfaces at pH 9 in KClaqueous solutions of various ionic strengths wasinvestigated by in situ AFM imaging technique. Themorphology of adsorbed CMC on talc basal planes and edge surfaces was found to be significantly different, due to different binding mechanisms involved. Interaction of CMC with the talc basal plane was found to bedominated by hydrophobic interactions while its binding with the talc edge surface was mainly through chemical complexation and hydrogen bond. The amount of CMC adsorbed on both talc basal planes and edge surfaces increased with increasing ionic strengthof solutions. The methodology developed in our study opens the door to probe polymer adsorption on anisotropic phyllosilicate surfaces, which can help us better understand the mechanism of polymer adsorption on specific mineral faces."

Jan 1, 2014

By Avishan Atrafi, Marek Pawlik

"Gas dispersion properties of sodium salts of 6, 12 and 18-carbon fatty acids (hexanoic, lauric and oleic acid) were investigated as a function of pH. A strong effect of pH was observed on gas dispersion properties of fatty acids. At high pH for 12 and 18 carbon fatty acids, at which these surfactants formed a true solution, the gas dispersion properties were similar to those of MIBC. In the case of sodium hexanoate, which has a much higher solubility than the longer chain fatty acids and therefore does not form precipitates, the gas dispersion properties of this surfactant were strongly enhanced in the acidic pH range, where hexanoic acid was fully associated. This result is an indication that undissociated hexanoic acid is much more surface-active than anionic hexanoate. Only a small effect of the surfactant chain length on gas dispersion properties of the tested reagents was observed. The measured critical coalescence concentration (CCC95) values increase slightly by decreasing chain length and range from 5.8 x 10-5 mol/L (17.7 mg/L) for sodium oleate to 7.2 x 10-5 mol/L (16 mg/L) for sodium laurate at pH 10 and 1.9 x 10-4 mol/L (26 mg/L) for sodium hexanoate at pH 3.7. These are compared to CCC95 of MIBC, which is measured to be 8 x 10-5 mol/L (8 mg/L). The soluble molecular species were recognized as the most effective species in preventing bubble coalescence."

Jan 1, 2014

By Francisco Cubillos, Jorge Menacho, Cesar Gomez, Juan Rodríguez

Mineral flotation is the most used process to selectively separate particles of one or more minerals of interest. The process uses natural or induced hydrophobicity to collect particles on the surface of rising bubbles through collisions and formation of bubble-particle aggregates. Flotation machines must keep particles in suspension and well distributed, while at the same time, disperse a mass of air into a population of small bubbles. The efficiency of the separation depends primarily on the characteristics of the bubble population generated in the machine and its distribution and flow throughout its volume. The formation and separation of bubble-particle aggregates create two zones, with strong interactions between them, and with markedly different hydrodynamics conditions. A model describing two-phase hydrodynamics of the continuous and dispersed phases (frother solutions and bubbles, respectively), moving along the whole unit, is proposed. Bubble populations are characterized at the formation stage including the effect of the presence of frothers. Flow through the aggregates formation zone, where bubbles move freely and are closely spherical, is modeled using drift-flux analysis. In the aggregates separation zone, bubbles initially pack maintaining a water layer thick enough to prevent capillary forces to affect their shape. As water drainage proceeds, bubbles deform, capillary channels form, and a network of channels with a diameter size distribution develops; channels become narrower (permeability is reduced) as the distance from the interface increases. Froth hydrodynamics is characterized using models originally developed to describe unsaturated flow through porous solid particle beds. Effects of hydrostatic pressure are considered.

Jan 1, 2014

By Yimin Zhu

This paper introduces the sixteen mappings and rules of mineral flotation and the subgroup, period etc in periodic table of chemical element to provide mineral flotation workers to refer in theory and practice research. the nine mappings and rules of mineral flotation and the subgroup, period are Saline minerals including the first main groups and collectors of aliphatic acid and aliphatic amines, Minerals including the second main group elements and collector of aliphatic acid, Hydrated ion of the second main group elements and quartz flotation, The floatability of oxidized minerals including the four main group elements, Organic acid including the fifth main group elements and wolframe, tin flotation collectors, The floatability of sulfide minerals including the fifth main group elements, Inorganic compounds including the seventh main group elements and mineral flotation regulator, Oxidized minerals including the forth Subgroup elements and organic flotation agents with phosphorus and arsenic, Oxidized minerals including the fifth subgroup elements and organic floating agents including the fifth main group elements, Minerals including the first subgroup elements and CN-, Sulfide minerals including the second subgroup elements and CN-, The effect of the highest N-valency inorganic acids or salts including p area elements of the third period in mineral flotation, Oxidized minerals including transition elements of the forth period and 3# flocculating agent, The floatability of minerals including elements of the sixth period, Element area of generating compositions and the collecting theory of mineral flotation and so and. Keywords: mineral flotation, periodic table of chemical element, subgroup, period, regulator, coordination chemistry

Sep 1, 2012

By Takaaki Wajima

The slag was attempted to be converted into the adsorbent for phosphate removal from aqueous solution using the alkali fusion method. The slag was mixed with NaOH powder (NaOH / Slag = 1.6), and then the mixture was heated at 600 ? for 6 h to prepare the precursor. The precursor was stirred at room temperature in distilled water to synthesize the adsorbent, and the removal ability of the obtained adsorbent for phosphate from aqueous solution was investigated. The products, including hydrocalumite and calcite, were synthesized, and the removal efficiencies of the adsorbent for F- and PO43- showed higher than those of raw BF slag, especially removal of PO43- are excellent (99 %), while the removal of Cl- , SO42-, NO3- and Br- was minor. The adsorbent could remove PO43- selectively in the co-existing solution of Cl-, NO3-, F-, SO42- and Br-.The equilibrium adsorption capacity of the adsorbent for PO43- was extrapolated using Langmuir and Freundlich models, and experimental data are found to fit Langmuir than Freundlich. The calculated maximum adsorption capacity of the adsorbent for PO43- is higher than other adsorbent reported previously. The high affinity of the adsorbent for PO43- in aqueous solution was caused by the formation of hydroxyapatite [Ca5(PO4)3(OH)] and brushite [CaHPO4?2H2O]. The prepared adsorbent is expected to be anew inorganic adsorbent for the removal of phosphate ion from wastewater. Keywords: Blast furnace slag, Alkali fusion, Phosphate removal, High selectivity

Sep 1, 2012

By Urs Peuker, Thomas Mütze, Thomas Leißner, Inga Osbahr

"Mining in the Ore Mountains (Germany) has taken place for hundreds of years and in several stages. Each stage produced its typical tailing. According to the former state of the art of the processing much valuables could not be extracted. This was caused by complex interlocking of the minerals, low grades, or by upgrading processes not sensitive enough for small particle sizes. Thus the processing of these fractions was uneconomically. Modern technical possibilities and rising metal prices bring these tailings disposals into focus for the processing of strategic metals. Mining disposals can be classified in heaps with coarse, low grade rock, which did not undergo a processing, slags and fly ash from smelting, and tailing disposals from mineral processing. The latter is under investigation to integrate them into a geographic information system. The mineral processing of the material will be part of the database besides information about geographic location, structure, amount of valuables, and details of ownership of the heap. The tailings disposals are composed of coarse, low grade, interlocked particles from density separation processes, medium size particles, which are tailings from flotation, and fines with liberated valuables, which did not undergo flotation. Therefore mineral processing of these disposals comprises the separation of liberated gangue by classification, beneficiation of locked valuables with density separation, liberation of valuables by grinding, and beneficiation of liberated valuables with flotation. The presented work shows the results concerning the composition of one exemplary heap and results of the classification as well as of the preconcentration tests achieved with material from this heap."

Jan 1, 2014

By Emile Scheepers, Chris Aldrich, Jacques J. Eksteen

The pneumatic injection of CaC2 powder into molten iron has become a very reliable and effective way to carry out desulphurisation. The key variables that influence the kinetics of this process are the condition and composition of the top slag, the oxygen activity in the hot metal and the injection conditions. Notable injection parameters include carrier gas flowrate, reagent flowrate, lance depth and initial sulphur concentration. A one-dimensional, steady-state model for momentum, heat- and mass transfer in rising gasliquid- powder plumes was developed for conditions relevant to the CaC2 refining process at Saldanha Steel?, South Africa. Combined with a model that predicts the contribution of the topslag to the process, the overall rate of desulphurisation as a function of time was determined, thereby quantitatively demonstrating the influence of the above-mentioned injection parameters on the kinetics of the desulphurisation process.

Jan 1, 2003

By M. Q. Xu

During the flowsheet development for a potential commercial Cu/Ni separation plant at the In-co?s Sudbury operation, extensive laboratory and miniplant studies were carried out. There are two potential feed streams for Cu/Ni separation at the existing operation. It is shown that Cu/Ni separation from the rougher concentrate is relatively simple without need of regrind. However, Cu/Ni separation can be difficult from the bulk concentrate because of the presence of excess flotation reagents in the bulk concentrate slurry and locked particles. Excess flotation reagents created excess froth increasing entrainment. By replacing the slurry water with tap water and with addition of some hydrogen peroxide, entrainment is minimized and good Cu/Ni separation is achieved on the bulk concentrate. Fine regrind is required to increase liberation of the locked particles for ultimately high copper recovery at the minimal nickel content.

Jan 1, 2014

Incomplete liberation of mineral particles is one of the key factors limiting the performance of industrial flotation circuits. This work aims to quantify the relationship between different breakage modes and how these affect mineral liberation properties. A copper porphyry (bornite) ore sample was subjected to breakage using a piston-die compression unit and an impact mill. The particles produced as a result of each mode of breakage were then characterised using Mineral Liberation Analysis (MLA) to quantify the mineralogical and liberation properties of the progeny particles. The impact mill was found to produce bornite that was finer grained relative to the host particles. In con-trast, bornite discharged from the piston-die unit closely followed the size distribution of the host particles and was retained to a greater extent in the larger/intermediate size fractions. The results provide insight into what breakage methods are optimal for the purposes of downstream separation.

Jan 1, 2014

By Sathyaprasad Nanjundaiah

The Paper intends to showcase a framework for spatial data collaboration from multiple sources of data, in order to create a single source of truth across the Organization. The framework is targeted to reduce the data duplicity, re-work, time loss due to search of required data and hindrances to fetch or transfer data from various data sources. The spatial data collaboration will provide a single window view of the entire organization with respect to its operations, management, sales, customers and competitors on a spatial reference across various regions in the World. Large Organizations with cross-country operations can standardize the use of spatial data through this framework for ease of data access, increasing the data reliability / integrity and better / on time decision making. Keywords: spatial data, GIS, collaboration, framework, mining, ESRI, tab files, shape files, ETL, reliability, integrity, interoperability, geo data, geo database, single source of truth

Sep 1, 2012

By P. Gao, J. W. Yu

"Magnetizing roasting-magnetic separation is an important route for the beneficiation of refractory iron ores. In this investigation, a pilot-scale fluidized magnetizing roasting reactor was introduced and used to study the effects of roasting temperature and the flow rates of reducing gas CO and fluidizing gas N2, on the magnetizing roasting performance of an Anshan-type carbonate-bearing fine iron ore. The results showed that the hematite was almost reduced to magnetite by a gas mixture of 4 m3/h CO and 1 m3/h N2 at a roasting temperature of 540 °C. Under the optimized conditions, a high-grade magnetic concentrate assaying 66.1 wt.% Fe with a recovery rate of 91.2% was achieved from an Anshan-type carbonate-bearing fine iron ore assaying 42.0 wt.% Fe. The XRD, VSM, and optical microscopy analyses revealed that the siderite was successfully converted to magnetite by roasting. Some coarse hematite particles were difficult to reduce to magnetite completely; however, these generated magnetite particles with a fine hematite core could also be effectively recovered by magnetic separation after liberation from gangue minerals due to their strong magnetism. INTRODUCTION Magnetizing roasting followed by low-intensity magnetic separation has been considered as an effective solution, both technologically and economically, when upgrading refractory iron ores (Zhang et al., 2012; Peng et al., 2012; Li and Zhu, 2012). According to the type of roasting reactor, the magnetization roasting can be divided into shaft furnace roasting, rotary kiln roasting, and fluidized bed roasting (Zhu and Li, 2014).Shaft furnace magnetization roasting system is mainly composed of heating and reduction processes. The hematite ore is first heated to 700~800 °C in the heating zone, then falls into reduction zone where the weakly magnetic hematite is reduced to magnetite by coke oven gas at 550~600 °C (Yan et al., 2012). However, several years of engineering practices indicate that the shaft furnace can only process the hematite ores with a granularity of 15 ~75 mm, and the shaft furnace roasting is also characterized by heterogeneity of roasted product. Hence, the shaft furnace magnetization roasting technology is gradually replaced by high-gradient magnetic separation with the development of high-gradient magnetic separator. The rotary kiln generally handles the hematite ores with a grain size of less than 30 mm (Zhu and Li, 2014), however the formation of clinker ring in the rotary kiln will affect the yield of iron resource. In the fluidized bed furnace, the hematite ore is shaken up by an upward current of gas which maintains the individual particles in suspension (Yu et al., 2018). The precise adjustment of the gas velocity to the particle size and the specific weight of the hematite ore, make it possible to generate a floating mixture of gas and solids which behaves almost like a liquid (Yu et al., 2017a). The process is reported to have the following advantages over the other roasting techniques: ease of control due to absence of moving parts within the reactor, homogeneity of roasted products, ability to handle fine particles, and high efficiency of heat transfer and mass transfer (Li et al., 2015; Yu et al., 2017b). However, the simultaneous heating and reductive magnetization of hematite ore occur at the same place in the conventional fluidized bed reactor. Therefore, the reductive atmosphere, as well as the safety and stability of anti-explosion are hard to be controlled. Besides, the roasting temperature for conventional fluidized bed furnace is usually up to 950~1150 °C (Liu et al., 2017). Thus, the formation of clinker ring caused by high temperature will affect the operating efficiency."

Jan 1, 2018

By Z. T. Yuan, S. L. Qi, Q. Y. Meng, G. X. Zou, L. X. Li, J. W. Lu

"The selective separation of pentlandite from serpentine was investigated using the magnetic coating-magnetic separation by conditioning slurry pH value, stirring speed, magnetic field intensity and controlling dosages of sodium hexametaphosphate (SHMP) and sodium oleate (SO). The optimal conditions were obtained as follows: the natural pH of 6.8-7.2, stirring speed of 2300 rpm, magnetic field intensity of 200 kA m-1, SHMP of 60 mg L-1, and SO of 400 mg L-1. Results showed that the Ni grade was 21.4% with the Ni recovery of 81.4% and MgO content of 3.8%. FTIR indicated that coagulant of SO preferentially adsorbed onto pentlandite and magnetite particles while hardly adsorbing onto serpentine particles when dispersant of SHMP was used. Thus, the selective magnetic coating of magnetite on pentlandite surfaces could be formed due to the formation of hydrophobic surfaces on pentlandite and magnetite particles. Calculations of DLVO (Derjaguin-Landau-Verwey-Overbeek) confirmed that interactions between magnetite and pentlandite particles were much stronger than that between magnetite and serpentine due to the existence of hydrophobic interactions with the addition of SO. Consequently, the pentlandite was successfully separated from serpentine. Therefore, this study exhibits the potential to separate pentlandite from serpentine minerals for practical applications and thus deserves further study.INTRODUCTION It has been well known that the separation of pentlandite from serpentine is a worldwide challenging issue in the processing of sulphide nickel-copper ores. Because the serpentine mainly causes the high pulp viscosity and slime coating on the pentlandite, which interferes with the flotation process of pentlandite (Cao et al., 2016; Feng et al., 2012). The fibrous mineral of serpentine preferentially attaches to the air bubble, forming bubble-macrofibers aggregates, which are easily floated into the nickel concentrates, resulting in the decline of Ni grade (Alvarez-Silva et al., 2016; Kusuma et al., 2014). In addition, the serpentine adheres to the pentlandite as hetero-aggregation or slime coating via the electrical interaction between a positively charged serpentine and a negatively charged pentlandite, which decreases the hydrophobicity of pentlandite and reduces the collector adsorption (Feng et al., 2013). In other words, the presence of serpentine or the occurrence of aggregates (including slime coating and bubble-macrofibers aggregates) seriously affects the flotation process and deteriorates the flotation of pentlandite. Therefore, we propose magnetic separation to recover pentlandite from serpentine with the magnetic coating technology, which is different from forth flotation."

Jan 1, 2018

By X. H. Zhou

Column flotation is being widely adopted for fine particle treatment by the mineral processing industry due to its simplicity of structure, high efficiency and good separation performance. Cyclonic static micro-bubble column flotation (FCSMC) is an innovative column separation technology that has been successfully applied in the coal preparation industry in China. Recently, the application of this equipment has been further expanded to the separation of several minerals such as fluorite, copper, iron, etc. The bottom of the FCSMC is a cone in which cyclonic field is generated when circulating pump is injected tangentially into the column. The unique cyclonic structure is believed to help enhance the column separation performance. Since the FCSMC is a new flotation device, little work has been done to understand the fundamentals of this technology. In this research, a computational fluid dynamics software, ANSYS/ FLOTRAN, was employed to simulate the flow field of a lab FCSMC system (F0.2 m, F3.0 m by length.) The distribution patterns for velocity field and flow field were investigated under single phase condition. It has been found that axial velocity of the slurry decreases and becomes stable along the height of the column from bottom to top, and the slurry performs as a descending flow pattern. Another observation is the velocity fluctuates vigorously near the wall due to wall effect. Compared to axial velocity, the radial velocity distribution is smaller and more complicated. The basic pattern is that on a given cross section of the column radial velocity increases from the wall to the center and it the velocity changes greatly around the center. Under the condition of column height less than 0.8 m, the axial velocity is negative and it directs from the wall to the column axis. When column height is higher than 0.8 m a reverse pattern is obtained, i.e., axial velocity is positive while directing from column axis to the wall. Special efforts were directed to investigate the tangential velocity pattern. Results indicate that the tangential velocity patterns of different cross sections are similar and showed a symmetrical distribution. Tangential velocity distribution concluded two zones: outer whirlpool and inner whirl-pool. And, interestingly, it has been found that on different cross sections the highest tangential velocity always occurs at the same position of the cross sections.

Jan 1, 2014

By S. M. Narbekova, L. V. Semushkina, Zh. A. Aldybayeva, A. A. Mukhanova, D. K. Turysbekov, N. K. Tussupbayev

More complex and heavy-concentrating oxidized and mixed sulphidic oxidized ores are involved in production because of increasing needs for non-ferrous metals. Extraction of the oxidized minerals of non-ferrous metals general in current technologies. The problem is solved to oxidized polymetallic ores the preliminary selective sulphidization is the oxidized surface of the components by means of hydrogen sulphide, sulphide and calcium polysulphide, and also element sulphur, etc. The task was to study details of flotation of the oxidized lead-bearing ore of the Zarechnoe deposit (Kazakhstan) with calcium polysulphide as sulphidation. According to chemical analysis initial samples of the ore contain, %: lead – 4.8; zinc – 0.1; general iron – 0.81. Phase structure lead is characterized by the oxidized form of 57.76-64.5 %; by sulphidic status of 25.5-32.64 %, and by plyumboyarosite of 19.0-23.02 %. Researches on flotation beneficiation of oxidized lead-bearing ore are conducted. Sulfidizator gave to grinding, on flotations there were used the collector (butyl xanthogenate of sodium) and frother (T-80). Experiments were conducted with a new sulphidizator – calcium polysulphide. The latter is obtained by interaction of CaO calcium oxide with sulfur and water at high temperature with component mass the following ratio S:CaO:H2O =10:5:85. Extent of mill initial ore was optimised (88.42 % of - 0.071 mm grade). For the optimum mill mode the studies on matching of an optimized consumption of sulphidizators are performed. On basic technology with application of sulphide of sodium as a sulphidizator at optimum mill, the lead concentrate with the content of lead 64.4 % at extraction of 86.6 % was received. The content of cerussite in a concentrate was about 14.9 % at extraction of 82.1 %. With application of calcium polysulphide as a sulphidizator the lead concentrate with the content of lead 68.0 % at extraction of 88.0 % was received. The content of cerussite has made 16.0 % at extraction of 85.0 %. Application of a new sulphidizator allows to increase extraction of lead in a concentrate from 64.4% to 68% and cerussite extraction – from 82.1 % to 85.0 %. The possibility of application of calcium polysulphide as a sulphidizator instead of conventional sulphurous sodium was established.

Jan 1, 2018

By I. V. Makarskii, D. N. Nikitin, L. G. Tarasova

"The extent and nature of the damage to diamonds at processing plant is largely determined by the design features of the equipment, the characteristics of the feed ore and the parameters of the ore disintegration process (change in the rotational speed of the autogenous mills, variations of the water supply to comminution process, choice of the optimum charge, etc.). To monitor the intactness of diamonds, an instrumental method using the X-ray tomography system and colored synthetic indicator diamonds was developed for identifying the process-related damage. The X-ray tomography system consists of a CT-Portable X-ray tomographic scanner, a crystal positioning device and customized software (developed by the Fraunhofer Institute and Aliud GmbH, Germany). The developed method enables improvement of the accuracy of the results, exclusion of the subjectivity of the mineralogical assessment, acceleration of data processing and promptly planning of the activities aimed at reducing the process-related damage to diamonds. KEYWORDS Diamonds, colored indicator diamonds, process-related damage, loss of mass, instrumental method, X-ray tomography system. INTRODUCTION Industrial tests of ore processing technology at the enterprises of ALROSA PJSC are accompanied by assessment of the process-related damage to diamonds. The assessment of the process-related damage to crystals is carried out for prompt elimination of factors contributing to the increase of impact forces in the process flow sheet of ore treatment plant. For this purpose a specially selected parcel of -4.0 + 2.0 mm sized natural indicator diamonds is used. The diamonds are exposed to ionizing radiation in order to turn them green and thus to create a distinctive feature. Colored natural indicator diamonds are described, photographed in several views and introduced into the process flow sheet of the processing plant, then extracted from the process flow, described and photographed again. The comparison of diamonds before and after their passing through the process flow sheet of the plant allows to find evidence of process-related impact on the crystal and to calculate the factor of process-related damage (the number of crystals damaged during liberation and recovery), the loss of crystal weight and the degree of damage to the crystals. The method of colored indicator diamonds is used to select processing methods, equipment or regime which would be the safest for diamonds based on the analysis of the factors of process-related damage. There are limitations of the method, such as:"

Jan 1, 2018

By F. J. Sotiuo

Variability of the quality of phosphate ore feed to the flotation plant has been of great concern for the industry. This variability sometimes resulted in 10% to 50% decrease of P2O5 recovery, a reduction of P2O5 concentrate grade and/or both due to depression of the system. For this investigation, samples of refractory ore and easy-to-float ore were obtained from the same mining area in Central Florida; and then submitted to bench flotation tests using fatty acids (FA). To understand the cause of difference in flotation behavior of these apparently similar ores (grade, mineralogy, and physical appearance), bulk and surface characterization studies were conducted. Based on the results of characterization studies and bench flotation tests on both refractory and easy-to-float samples, it was possible to determine FA surface coverage. It was found that the surface coverage for the refractory ore was between 6.9% and 9.8%, corresponding to 0% and 80% recovery, respectively; whereas the easy-to-float ore showed surface coverage of 17.2% (89% recovery) to 24.6% (98% recovery). Since size analysis, surface area and pore size measurements showed small differences, it was thought that the surface coverage differences could be caused by the ad-sorption of natural compounds onto the phosphate ore surfaces, depressing the system. SEM, EDS, and Leaching and Solvent Extraction (LSX) studies were performed on the phosphate ores to demonstrate the proposed mechanism. This paper summarized our characterization studies, flotation results, and findings. The study showed that the new identified compounds were responsible for the flotation behaviors of the Florida refractory phosphate ores.

Jan 1, 2014

By Jonas Addai-Mensah

Despite the fact that nickel (Ni) laterites accounts for about 60 % of the world?s nickel mineralization, commercial processing of complex, low grade Ni laterite ores by conventional beneficiation (e.g. magnetic, electrostatic and flotation separation) still presents intractable challenges, particularly in heap leaching. Invariably, low grade laterite ores require aggressive hydrometallurgical techniques (e.g., highly acidic lixiviant leaching at ambient or elevated temperatures) for Ni and cobalt (Co) extraction. As a precursor to heap leaching, agglomeration of the multi-mineral phase feed particles into robust and porous granules of 4-10 m permeable bed, is essential. In the present work, several basic and applied studies of the agglomeration behavior of real Ni laterite ores and selected oxides and clay minerals (hematite, quartz smectite and kaolinite) which constitute the predominant host gangue phases of typical laterite ores are performed. Isothermal, batch agglomeration tests involving sulphuric acid solution as a binder were carried out to produce coarse, narrow-sized (5 ? 40 mm) granules which were well characterized. The influential role of feed ore characteristics (e.g., mineralogy/chemistry and primary particle size distribution) and binder composition (30 vs. 44% w/w H2SO4) and dosage (15-25 wt.%) in agglomeration behavior and granule properties were examined through several characterization techniques including granule size, compressive strength, bed percolation and re-wetting stability and 3-dimensional micro-structure analyses. Links between feed mineralogy/chemistry and size, binder formulation, agglomeration behavior, curing conditions and final granule properties and structural characteristics are established. The implications of the findings to Ni laterite plant agglomeration for enhanced heap leaching are discussed. Keywords: nickel laterite, complex low-grade ores, agglomeration, heap leaching, micro-structure

Sep 1, 2012

By N. Pradhan

In the Sukinda valley, Orissa, India, a large quantity of overburden material is generated during the mining of chromite mineral (on average 10 tons for every ton of ore). The overburden hereby depicted as ?lateritic nickel ore? contains on an average 0.5% Ni. IMMT Bhubaneswar is working on this material for extraction of nickel and cobalt. But for better recovery of metal values, thermal activation or thermal reduction of ore is required. An alternative biotechnological route for reduction of ore is hereby attempted. An anaerobic dissimilatory Iron (III) reducing bacterial consortium (here denoted as IRB), capable of imparting iron phase changes in the lateritic nickel ore was established which improves the subsequent extraction of co-precipitated Co (III) and Ni (II) from the ore. In this study, properties of thermally and microbially reduced lateritic nickel ore are compared vis-à-vis original ore. Due to the phase changes, original light brown color of the lateritic nickel ore changes to dark brown on IRB treatment. This dissimilatory reduction of ore leads to formation of some magnetic particles, which were separable by hand held magnet. Roasting and IRB treated ore on acid leaching with H2SO4 show about 45 % and 36 % leaching of nickel ore compared to about 18 % leaching from the original lateritic ore. If bacterial reduction method is successful, cost intensive method of ore roasting process can be eliminated. Thus, it is possible to make use of dissimilatory iron reducing bacteria for recovery of valuable metals from off grade iron ore/ laterites. Keywords: lateritic nickel ore, bacterial reduction, thermal reduction, dissimilatory fe (iii) reducing bacteria

Sep 1, 2012

By Liu Jie

Refractory iron ore deposits in China have various genesis and complicated types, the nature of which is poor, fine-disseminated and complex. Therefore, refractory iron ore could scarcely be separated and utilized by traditional mineral processing technology at present. It is necessary to explore deep reduction technology to change the characteristics of refractory iron ore and to use effectively the iron resource. And deep reduction technology is that on the condition of higher reduction temperature than that of magnetic roasting and stronger reducing atmosphere, the iron oxides from iron ore was reduced to metallic iron particle that is easy to dissociate. And then production from deep reduction is easily separated by magnetic separation and iron powder production was obtained finally. Deep reduction technology for Lingyang iron ore from Jilin, China, as the refractory iron ore, was studied in this paper. The influences of such main factors as reduction temperature, time and coal content were investigated. The results showed that the Metallization rate of reduction product was up to more than 90% under optimum conditions, and then higher iron grade and recovery of reduction iron powder were obtained from subsequent magnetic separation. Furthermore, the deep reduction mechanism in the system was studied by the means of XRD and SEM analysis for reduction production and Physical Chemistry of Metallurgy. Analytical results indicated that during deep reduction, the size of iron particle from deep reduction materials was increasing as reduction temperature rising and reduction time extending. The growth of metallic iron particle from deep reduction production was divided into such three stages as reduction nucleation, deep reduction and growth of metallic iron particle.

Sep 1, 2012