A survey was conducted so that the degree of corrosive, erosive, and abrasive attack on material-handling systems in the mining and mineral-processing industry could be assessed, and so that the areas of research and development that would be relevant to the needs of the industry could be determined. Of the 59 different mines that were invited to participate in the survey, 41 returned completed questionnaires, giving a return rate of 70 per cent. The total number of completed questionnaires amounted to 45. An analysis of the results shows that attack by erosion or abrasion is considered to occur more often than attack by corrosion. However, al three types of attack must be regarded as significant problems within the mining industry, since 52 per cent of the participating mines reported pump failures due to the inability of the materials of construction to withstand the operating conditions, and almost 90 per cent reported piping failures due to corrosion (22 per cent) or to erosion and abrasion (78 per cent).

Jan 1, 1986

By S. E. Olsen, M. Tangstad, G. Tranell, K. Berg, S. Gaal

In this study, the reduction behaviours of MnO and SiO2containing slags by solid carbonaceous materials was investigated in both small and larger-scale laboratory experiments. Five types of carbonaceous material were investigated: 2 graphites, industrial coke, anthracite and eucalyptus charcoal. The effects of the reductant type/properties on the reduction kinetics, metal composition and metal yield, have been quantified. Results show that the reduction rate is highly dependant on the type of carbon used. It was found that the reductant type significantly influenced the SiO2reduction while it did not seem to have a large effect on the MnO reduction. This may be due to the different CO2and SiO reactivities of the materials.

Jan 1, 2004

By T. S. Seleka

Laser surface melting has been conducted on a 304 stainless steel (SS) with the aim of enhancing pitting corrosion resistance of the material. This process involves rapid melting of the material?s surface followed by rapid solidification to refine the microstructure. This includes the dissolution of inclusions such as MnS, FeS, CrxCy, and other minor constituents. The microstructures as a result of laser treatment were observed by means of optical microscope and also confirmed by the XRD. The glow discharge optical emission spectroscopy (GDOES) was utilized for chemical analysis. Changes in hardness were observed by using a Vickers microhardness tester. Pitting corrosion tests on laser treated and untreated samples were conducted according to ASTM G48-92 to evaluate mass loss and pitting morphology. Laser surface melting improved the pitting corrosion resistance of this material in a chloride-containing environment.

Jan 1, 2007

The Gordonsville Operation of Pasminco US Inc. along with the Center for Advanced Mineral and Metallurgical Processing (CAMP) at Montana Tech studied, developed and implemented a pilot scale hydrometallurgical facility for the industrial recovery of germanium and gallium. This paper describes the joint testing and engineering program that culminated in this successful process. 1. Introduction The Pasminco US Inc. (PAS), Gordonsville Operation, has been producing zinc concentrate continuously since 1975. Within the zinc concentrate, several byproduct elements were found to be significantly concentrated including gallium and germanium. The gallium and germanium replace zinc and other metals within the crystal lattice structure of the zinc mineral (sphalerite) and are concentrated in the same manner as the zinc mineral. This concentrate is then sent to the Pasminco Clarksville Zinc Refinery for further processing. Within the hydrometallurgical zinc-processing plant at Clarksville, a residue is formed that contains a majority of the impurities that would otherwise contaminate or hinder the zinc process. Approximately 5,000 tons of residue is formed annually containing approximately 0.80% gallium and 0.60% germanium along with significant quantities of iron, zinc, silica, and lead. Pasminco currently sells this residue for the germanium value. Until recently, no revenue for the gallium was obtained from the sale of the residue.

Jan 1, 2008

By M. U. Ozbay

The stability of pillars is analysed on the assumption that pillars shed load in a stable manner if the slope the strata load-deformation relation is steeper than that of pillars in the post-peak regime. Concepts of local stiffness, mine structural stiffness, and critical stiffness are discussed. Procedures are described for the determination of strata stiffness for various pillar layouts by use of the available boundary-element computer programs. The postpeak stiffness of pillars is assessed from the available data relating to the post-peak load-deformation relationship and width-to-height ratio. Stability analyses are carried out by the contrasting of strata stiffness with post-peak pillar stiffness. It is shown that the strata stiffness becomes unacceptably small for a stable yield-pillar layout when the span exceeds about 5 times the depth. The strata stiffness is found to increase, thereby increasing the stability, as the span-to-depth ratio, number of pillars, and percentage extraction are decreased. It is also found that the stability in a yield pillar becomes difficult to achieve when al the pillars in a layout are in the descending part their post-peak load-deformation curve

Jan 1, 1989

By K. S. Rao, R. P. Tiwari, V. K. Shrivastava

ABSRACT: In this paper numerical simulation of jointed block mass behaviour obtained in an experimental study has been presented. Singh et al. (2002) conducted extensive tests on the jointed model materials with several joint configurations. The results of this experimental study were used to validate the strength behaviour of numerical block mass model developed using professionally available software. This software basically contains different kinds of material models. From the results of numerical simulation the existence of strength anisotropy was observed. The strength anisotropy so obtained has been compared with the experimental values reported by Singh et al. (2002). The anisotropic curves in both cases are U-shaped with flat base. They show good agreement in sliding mode of failure zone in which inclination ß (= 90° - ?) of joint set-I lie between 20° to 40° for all cases of interlocking. ZUSAMMENFASSUNG: In dieser numerischen Papiersimulation des verbundenen Blockmasse Verhaltens, das in einer experimentellen Studie erhalten wird, ist dargestellt worden. Singh et al. (2002) leiteten umfangreiche Tests auf den verbundenen vorbildlichen Materialien mit einigen gemeinsamen Konfigurationen. Die Resultate dieser experimentellen Studie wurden verwendet, um das Stärke Verhalten des numerischen Blockmasse Modells zu validieren, das mit professionell vorhandener Software entwickelt wurde. Diese Software enthält im Allgemeinen unterschiedliche Arten der materiellen Modelle. Von den Resultaten der numerischen Simulation wurde das Bestehen von Stärke Anisotrophie beobachtet. Die Stärke Anisotrophie also erreicht ist mit den experimentellen Werten verglichen worden, die von Singh et al. (2002) berichtet werden. Die anisotropen Kurven in beiden Fällen sind mit flacher Unterseite u-förmig. Sie zeigen gute Vereinbarung in gleitender Erscheinungsform des Ausfalls Zone, in der Neigung ß (= 90° - ?) von der Verbindung stellenSie Lüge zwischen 20° auf 40° für alle Fälle vom Ineinandergreifen ein. RESUME: Dans cette simulation numérique de papier du comportement joint de la masse de bloc obtenu en étude expérimentale a été présenté. Singh et autres (2002) ont effectué les essais étendus sur les matériaux modèles joints avec plusieurs configurations communes. Les résultats de cette étude expérimentale ont été employés pour valider le comportement de résistance du modèle numérique de la masse de bloc développé en utilisant le logiciel professionnellement disponible. Ce logiciel contient fondamentalement différents genres de modèles matériels. Des résultats de la simulation numérique on a observé l'existence de l'anisotropie de force. L'anisotropie de force ainsi obtenu a été comparée aux valeurs expérimentales rapportées par Singh et autres (2002). Les courbes anisotropes dans les deux cas sont en U avec la base plate. Elles montrent la bonne concordance dans le mode coulissant de la zone d'échec en lequel la inclination ß (= 90° - ?) du joint placez-Je le mensonge entre 20° à 40° pour tous les cas d'enclencher.

Jan 1, 2003

By Deon van Tonder, Bert Van Hege

Comparison of various technologies for uranium recovery from sulphuric acid leach solutions shows that Resin-in-Pulp (RIP) and/or Solvent extraction (SX) based processing routes are usually cost effective (11). A combined RIP-SX recovery-purification route and a CCD-SX recovery-purification route were investigated and optimised. The design basis used for the investigation was a production rate of 200 kg/h U3O8 over a solution concentration range of 40 to 1500 mg/L U3O8. The OPEX for the RIP-SX processing route was found to be sensitive to the variation in uranium concentration in the leach liquor. One of the main drivers for this trend is the leach acid concentration. Conversely, the CAPEX of the CCD-SX processing route was sensitive to the uranium concentration in the leach liquor. The leach acid concentration only affected the OPEX of the CCD-SX processing route modestly, as the bulk of the acid is recovered in a pre-leach circuit. Contrary to expectation, the effect of extractant loss assumptions on the overall processing route economics was found to be modest to insignificant. It should be noted that the CCD-SX processing route OPEX was more sensitive to extractant loss assumptions than the RIP-SX processing route OPEX. Economic optimum wash ratios were determined for the CCD-SX processing route and increased with leach concentration ? the increase in wash ratio was less than proportional. A 5-stage CCD configuration was found optimal over the concentration range investigated.

Jan 1, 2007

By H. A. D. Kirsten

Written contribution by L.J. Besaanst I am a Mechanical Engineering Technician (T3), and wish to further my education to at least NHD (T4) level. I read your paper in the Journal of The South African Institute of Mining and Metallurgy with great interest, and must compliment you on its brilliance. However, there are some questions I should like to ask, and certain points I should like to highlight. I should appreciate your comments. Written contribution by J.F. Curtis The comprehensive and finely detailed survey of, and proposals for, engineering education in South Africa reflects the author's wide experience in the needs for, and the provision of, such education. This paper wil make a major contribution to the enhancement of the profession of engineering and the improvement in quality of engineering activities in South Africa. Contribution by G.W. Annandalet I have studied your paper in some detail, and am of the opinion that it makes an important contribution to the topic of the development of technological manpower, which is currently being debated in South Africa at al levels. Debate on this topic has risen above the level of academic discussion; it has been discussed by the Economic Advisory Council of the President, and is being considered at Ministerial level. Author's reply to L.J. Besaans Thank you for your contribution and complimentary remarks. As you have pointed out, there are certainly many aspects that will have to be addressed in the resolution of the crisis in engineering education. I trust that the following comments satisfactorily answer the queries you have raised. Author's General Comments Since publication of the paper, attention has become focused on the provision of employment opportunities an aspect not dealt with specifically in the paper. The following comments serve to indicate some of the directions in which job opportunities will have to be developed in the numbers that will be required.

Jan 1, 1991

By R. M. Kear

Strategic and tactical planning are both required in the mining industry but have completely different objectives and require different environments. If these are not fully understood, then the best value for a mining operation may not be realized. This paper examines the differences in these approaches and how they interface in the mining environment. The objectives, content, skills required and the implied management issues for these two components are examined with the hope that this will assist management and the planning teams in defining their respective roles and expectations. The opinions are those of the author based on his experience on several mining operations and projects.

Jan 1, 2006

By X. Pan

Slag-metal equilibrium experiments were conducted at 1500ºC and 1580ºC under 0.03 atm, 0.05atm and 0.83 atm CO partial pressures using silica and Cr-oxide crucibles. The complex slags belonged to SiO2-CaO-Al2O3-MgO-FeOx-CrOxand the metal phase to the Cr-Fe-C-Si-(S)systems. The carbon saturation of the metal phase was avoided using oxide crucibles and thus the results are pertinent to ferrochromium refining slags and processes. From equilibrium data and thermodynamic calculations the CrO /(CrO+Cr2O3) ratio in the slag was determined as 0.75, 0.80and 0.86 under 0.83 atm and 0.05 atm of CO pressure at 1500ºC and 0.03 atm and CO pressure at1580ºC respectively. The results clearly demonstrated that a higher chromium content of the metal results in higher Cr in the slag, and chromium in slag decreases with increasing SiO2. The results were also sensitive to the crucibles used as these oxide crucibles saturated the slag either with respect to SiO2or Cr-oxides. It was also demonstrated that the relative amount of CrO in the slag was higher when SiO2crucibles were used in accord with thermodynamic calculations. Iso-concentration curves for carbon and chromium of the metal phase in equilibrium with the slag were drawn on pseudo ternary SiO2–(AI2O3+CaO+MgO)–(Cr2O3+Fe2O3) diagram. The activity coefficients and activities of carbon and chromium of the metal phase were also calculated from the experimental data and available thermodynamics information and were plotted as iso-activity curves in the same pseudo ternary diagram. Keywords: Chromium, slag, equilibrium

Jan 1, 2004

By Swapan Ghosh, Amitava Sengupta, Proloy Das

Ferro-alloys are very important ingredients used for making of quality steel with desired composition. In view of high demand in various types of ferro-alloys, it has become necessary to produce the same efficiently, safely and cost-effectively with consistent quality maintaining the anti-pollution norms. To achieve this goal, it is necessary to adopt latest process/equipment with the state-of-the-art instrumentation and automation system. A Programmable Logic Controller (PLC) based automation system with suitable Human Machine Interface(HMI) terminals along with intelligent field mounted sensing/control devices allows to monitor and control the complete plant effectively with optimum deployment of man-power. In association with this, use of process optimization controllers enables to achieve specialised functionalities of the submerged arc furnaces like material management, lining management, electrode management, power management, overall production management etc.

Jan 1, 2007

By M. Abdellatif

Keywords: Magnesium, pyrometallurgy, Mintek Extensive testwork on atmospheric thermal magnesium production has highlighted certain important fundamental and operational factors that have a major influence on magnesium extraction and its extraction rate, the condensation efficiency of magnesium, as well as on the quality of the condensed metal. The possible impact of these factors on the selection and preparation of raw materials, recipe choice, furnace electrical energy consumption, and on the refining requirements of the crude magnesium is discussed. Selected pilot plant operational and metallurgical data are also presented.

Jan 1, 2006

By G. P. Dyke

With the removal of the majority of the shallow mineral reserves there has been an increase in the mining depths in the South African mining industry. This has, in turn, changed the industry?s and stakeholders? perceptions of risk associated with mining-induced instability. In recent years the increased mining depth, particularly in open pits, has led to an increase in pit slope failures, which has highlighted the need for appropriate and effective pit slope management programmes. Such a programme comprises many facets, including mine hazard plans, regular slope inspections, cleaning of interim and final pit faces, blasting practices, histories of failures, pit depressurization, stormwater control and evacuation procedures. However, it is arguably in the field of slope monitoring that the most significant strides have been made in terms of new technologies and best practice in open pit mining geotechnics, with the introduction of technologies such as laser scanners and slope stability radar. This paper seeks to illustrate the operational benefits associated with the implementation of new technologies into open pit mining, using AngloGold Ashanti?s Geita Gold Mine in Tanzania as an example.

Jan 1, 2009

By Haiping Sun, Samir Ganguly, Oleg Ostrovski, M. Yaser Lone

Wettability of graphite by synthetic SiO2-Al2O3-CaO-MnO slags with varied MnO content and by industrial slags was studied at 1350-1600 °C using sessile drop method under argon atmosphere. Initial contact angle was the lowest (110-115o) for the MnO-free slag. For slags with 10-40 wt% MnO, the initial contact angle was in the range 125-135o. The contact angle decreased with the contact time. The change in the contact angle with slag mass was found insignificant. The surface tension of slags obtained from the drop shape analyses was 500-800 mN/m and varied in a narrow range with temperature and MnO concentration. The reduction rate increased with increasing MnO content in the synthetic slag from 20 wt% to 40wt% and temperature. Increasing temperature also increased the rate of reduction. No correlation was observed between the reduction rate and MnO content in the synthetic slags in the range 0-20 wt% and in the industrial slags. The rate of SiO2 reduction from the molten slag was close to the rate of MnO reduction. The MnO-free slag had the largest contact area with graphite substrate. Keywords: reduction, wettability, graphite, slag, manganese, surface tension.

Jan 1, 2007

By N. Z. Jovanovic

Irrigation of agricultural crops may be a cost-effective option for the utilization of gypsiferous minewater as it may also create an opportunity to produce crops during the dry winter season on farm sin South Africa, such as in Mpumalanga. In this study, intensive field monitoring systems were developed and implemented to assess the feasibility and sustainability of irrigation with gypsiferous mine water. Soil water and salt balance components, as well as crop yields, were monitored in field trials carried out at Kleinkopjé and New Vaal Collieries (Anglo Coal), and at Syferfontein (Sasol). Field measurements indicated that high crop and pasture yields can be obtained, provided fertilization and irrigation water management are appropriate. Soil water and salt balances indicated that considerable amounts of minewater can be used and considerable masses of salts can be removed through precipitation of gypsum in the soil profile. With appropriate management, water and salt runoff and salt leaching can be intercepted, thereby minimizing the impact on groundwater. The SWB model is being validated through on-going monitoring. This will allow the use of the SWB model at other sites to predict the long-term impact of irrigation with mine water on soil and groundwater, as well as to run scenario simulations in order to recommend sustainable management of irrigation with minewater.

Jan 1, 2004

By G. Akdogan, S. M. Bradshaw, M. I. Isaacs, P. Van Wyk

In the mineral processing industry, Ni-Cu-Fe-S converter matte is leached in order to remove base metals from a concentrate containing platinum group metals (PGMs). This paper investigates the atmospheric leaching process, in order to develop a better understanding of the leaching behaviour of the base metals; in particular Cu, Fe, Ni, and the PGMs in particular Ru and Ir with key process variables, acid concentration, copper concentration under oxidative leaching conditions. Higher initial acid concentration resulted in a higher copper, iron and nickel extractions, as well as higher leaching rates together with faster Cu, Ru, Ir precipitation occurring. On the other hand, a higher initial copper concentration resulted in more nickel but less iron being extracted. Keywords: PGM, converter matte, leaching, precipitation

Jan 1, 2020

By I. V. Lunkin, E. B. Rakishev, B. R. Rakishev

In mining the method of statistical tests is used by solving of problems, exposing to influence of random factors. Such problems are: rational selection of equipment set; co-ordination in time of different processes; interaction between some processes and kinds of works. Usually it is considered that Monte Carlo method proves its value in the first place in that problems, which allow theoretical-probabilistic description. Analysis of numerical solution of mining-economic problems shows that the method of statistical tests may be used successfully by solving of determinate problems, which are solved usually analytically or by the methods of mathematical programming. We are talking about the problems of optimal use of resources, expedient placing of equipment, effective use of investments, rational planning of stripping and extracting works, groups of mining enterprises and about different variants of transport problem. In the report possibility of the method use is studied at an example of typical technical-economic problems solving. By solving of these problems the variant of the method with uniform distribution of random quantity had been applied and built-in random number generator of visual modelling system VisSim had been used. By algorithms elaboration it seems very perspective to use combination of the Monte Carlo method with traditional methods of numerical solving of the problems (methods of linear, nonlinear and dynamic programming and so on). Keywords: method of statistical tests, mining-technical problems, diapason of random number sample, efficiency function and its extremum.

Jan 1, 2003

By P. L. Duncanson, J. D. Toth

Since 1995, when "freeze lining" refractory systems were introduced to the ferroalloy industry, they have gained in popularity, due to the freeze lining?s reputation for reliability, safety, and the contribution it makes to profitability. As with many popular and effective technologies, however, the freeze lining has spawned low-cost pretenders that claim the "freeze lining" name. On the surface they appear to contain some of the components of the technology, such as thermally conductive materials, but they fail to incorporate all of the principles that define a true Freeze Lining. The term "freeze lining" refers to the refractory system?s ability to maintain a temperature profile that is low enough to freeze a layer of process material on its hot face, which insulates the refractory and prevents direct contact with molten metal and slag. In doing so, the common wear mechanisms found in the submerged arc furnace - chemical attack, erosion, and thermal stress - can be prevented. These wear mechanisms are all related to high temperature; thus, they are prevented by maintaining low temperatures. Certain refractory properties and design concepts are absolutely necessary for the lining system to function as a true Freeze Lining. The paper explains these requirements and why they are important - the Truth of freeze linings - and further explains why systems that ignore one or more of these requirements cannot claim to be freeze linings, thereby exposing the Myths.

Jan 1, 2004

By N. Simpson

Low carbon 11.5% chromium stainless steels are finding increasing use in industry as square or rectangular tubing material for the construction of structures by welding. During processing, resistively welded circular pipes are bent into square or rectangular shapes. During this process longitudinal cracks can sometimes develop atone of the inner corners of the section. An investigation has shown that the processing of round into square tubing with very sharp corners can cause excessive cold working at the inner corners of the squared tube. This, together with the high tensile residual stresses and a susceptible microstructure due to the presence of grain boundary carbides, can result in brittle cleavage cracking. Measures that can be used to reduce the problem are described.

Jan 1, 2003

Viscosity measurements were carried out on slags in the CaO-Cu2O-CuO-MgO-SiO2systemcontaining ~ 63 wt% SiO2in air. The experimental work was carried out over a range of temperatures where the slags were completely liquid. Initial measurements were on a binary CaO-SiO2slag to which incremental additions of CuxO-MgO-SiO2slag with the same silica mole fraction were made. The viscosity-temperature relationship was measured for slags with‘Cu2O’contents of 0.02, 0.19, 0.38, 0.79, 1.69, 2.47, 3.01, 5.31 and 10.0 wt%. The proportions of Cu+and Cu2+in the slags were determined. The oxidation state of Cushifted from predominantly Cu+to Cu2+, with the Cu+/Cu2+ratio of approximately 0.3 for slag with a Cu content above 2 wt%. This is equivalent to Cu1.13O. The trends observed for changes of Cu2+/Cu+redox ratio with slag chemistry were consistent with the literature. Decreasing the CaO content by substituting copper oxide resulted in a decrease in the Cu+/Cu2+redox ratio. The change in ratio corresponded to a shift of the value of x in CuxO from an initial value of 1.8 to 1.1,when the slags contained 10% ‘Cu2O’. In this study, the SiO2content of the slags varied between 64 and 60 wt% as the Cu content increased. The viscosity of the slag containing 10 wt% CuxO was nearly 4.5 times lower than the binary CaO-SiO2slag. As the silica mole fraction (xSiO2) actually stayed constant (0.61±0.009),the results show that CuxO acted as a network breaker. Comparison with other ternary slags with similar silica mole fractions suggest that that addition of CuxO to silicate slags has a stronger effect on lowering the viscosity than FeO or MnO has on a molar basis. Keywords: viscosity, copper, silicate, slags

Jan 1, 2004